Claims
- 1. A cutting tool insert comprising a substrate and a plurality of coatings on at least a portion of said substrate, said plurality of coatings including:a first coating of at least 2 microns deposited on said substrate, said first coating comprising at least one of a metal carbide, a metal nitride, and a metal carbonitride of a metal selected from the group consisting of zirconium and hafnium; and a second coating comprising at least one of a metal nitride and metal oxide of a metal selected from groups VB and VIB of the periodic table.
- 2. The cutting tool insert of claim 1, wherein a thickness of said first coating is at least 2 microns and is no greater than 5 microns.
- 3. The cutting tool insert of claim 1, wherein:said first coating is selected from the group consisting of zirconium nitride and hafnium nitride; and said second coating is one of aluminum oxide and titanium nitride and is 1 to 10 microns thick.
- 4. The cutting tool insert of claim 1, further comprising:a third coating that is a coating of a metal carbonitride 2 to 6 microns thick, said third coating intermediate said first coating and said second coating and in contact with said second coating.
- 5. The cutting tool insert of claim 4, wherein said metal carbonitride of said third coating has a nitrogen to carbon atomic ratio between 0.7 and 0.95 which causes said metal carbonitride of said third coating to form projections into said second coating to thereby improve adherence and crater resistance of said second coating.
- 6. The cutting tool insert of claim 4, wherein:said first coating is a coating of hafnium nitride at least 4 microns thick; said second coating is a coating of aluminum oxide 2 to 4 microns thick; and said third coating is a coating of titanium carbonitride 3 to 4 microns thick.
- 7. The cutting tool insert of claim 6, wherein said plurality of coatings further comprises:a fourth coating that is a coating of titanium nitride at least 1 micron thick, said fourth coating overlying said second coating.
- 8. A cutting tool insert comprising a substrate and a plurality of coatings on at least a portion of said substrate, said plurality of coatings including:a first coating deposited on said substrate and comprising at least one of a metal carbide, a metal nitride, and a metal carbonitride, wherein said metal is selected from the group consisting of zirconium and hafnium; and a second coating comprising a ceramic; and a third coating, intermediate said first coating and said second coating and in contact with said second coating, said third coating comprising a metal carbonitride having a nitrogen to carbon atomic ratio between 0.7 and 0.95 which causes said metal carbonitride in said third coating to form projections into said second coating to thereby improve adherence and crater resistance of said second coating.
- 9. The cutting tool insert of claim 8, wherein said first coating is 2 to 5 microns thick.
- 10. The cutting tool insert of claim 8, wherein said third coating is a coating of titanium carbonitride.
- 11. The cutting tool insert of claim 10, wherein said third coating is 2 to 5 microns thick.
- 12. The cutting tool insert of claim 8, wherein said metal carbonitride of said third coating has a nitrogen content of 70% to 90% based upon the total nitrogen and carbon content of said metal carbonitride layer.
- 13. The cutting tool insert of claim 8, wherein said metal carbonitride of said third coating has a nitrogen to carbon atomic ratio of 0.75 to 0.95 as determined by x-ray diffraction.
- 14. The cutting tool insert of claim 8, wherein:said first coating is a coating of hafnium nitride 2 to 5 microns thick; said second coating is a coating of aluminum oxide 1 to 10 microns thick; and said third coating is a coating of titanium carbonitride 2 to 4 microns thick.
- 15. The cutting tool insert of claim 14, wherein:said second coating is about 6 microns thick; and said third coating is about 3 microns thick.
- 16. The cutting tool insert of claim 14, further comprising a fourth coating having a thickness of 1 up to 4 microns and consisting of at least one of titanium nitride ad titanium carbide, said fourth coating overlying and in contact with said second coating.
- 17. The cutting tool insert of claim 16, wherein:said second coating is about 6 microns thick; said third coating is about 3 microns thick; and said fourth coating is about 2 microns thick.
- 18. The cutting too insert of claim 8, wherein said metal carbonitride in said third coating is of a metal selected from the elements of groups IVB, VB, and VIB of the periodic table.
- 19. The cutting tool insert of claim 16, wherein said substrate comprises 3 to 30 weight percent binder and 70 to 97 weight percent of a carbide selected from the group consisting of tungsten carbide, titanium carbide, tantalum carbide, niobium carbide, molybdenum carbide, zirconium carbide, and hafnium carbide.
- 20. The cutting tool insert of claim 19, wherein said substrate further comprises a nitride selected from the group consisting of titanium nitride, tantalum nitride, niobium nitride, molybdenum nitride, zirconium nitride, and hafnium nitride.
- 21. The cutting tool insert of claim 19, wherein a surface layer of said substrate is enriched in said binder relative to a remainder of said substrate.
- 22. A cutting tool insert comprising a substrate and a plurality of coatings on at least a portion of said substrate, said plurality of coatings including:a first coating of at least 2 microns deposited on said substrate, said first coating comprising at least one of a metal carbide, a metal nitride, and a metal carbonitride of a metal selected from the group consisting of zirconium and hafnium; and a second coating comprising at least one nitride of a metal selected from groups IIIA, IVB, VB, and VIB of the periodic table.
- 23. The cutting tool insert of any of claim 1 or 8 wherein the substrate is a metal-containing substrate.
- 24. The cutting tool insert of claim 23, wherein the substrate is cemented carbide.
- 25. The cutting tool insert of claim 24, wherein the cemented carbide comprises:3 up to 30 weight percent of a binder metal selected from the group consisting of iron, nickel, cobalt, and a material consisting of at least two of iron, nickel, and cobalt; and 79 up to 97 weight percent of a material selected from the group consisting of tungsten carbide, titanium carbide, tantalum carbide, niobium carbide, molybdenum carbide, zirconium carbide, and hafnium carbide.
RELATED APPLICATION(S)
This application is a continuation-in-part of Ser. No. 08/390,570 filed Sep. 3, 1999, now abandoned, which is a continuation-in-part of U.S. applications Ser. No. 08/860,163, filed Jun. 16, 1997, now U.S. Pat. No. 5,958,569, granted Sep. 28, 1999.
US Referenced Citations (22)
Foreign Referenced Citations (2)
Number |
Date |
Country |
1291387 |
Feb 1969 |
GB |
1291388 |
Feb 1969 |
GB |
Non-Patent Literature Citations (3)
Entry |
US 5,143,488, 9/1992, Santhanam et al. (withdrawn) |
Article entitled “A Look at the Hafnium Nitride Coatings”, authored by Roy V. Leverenz. |
Teledyne Firth Sterling Catalog, No. EM-86A, entitled EX Mill M-Series Positive/Negative. |
Continuations (1)
|
Number |
Date |
Country |
Parent |
08/860163 |
Jun 1997 |
US |
Child |
09/390570 |
|
US |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
09/390570 |
Sep 1999 |
US |
Child |
09/467936 |
|
US |