Patent Application
20130011270
This disclosure generally relates to coatings and surface treatments for gas turbine components.
Certain gas turbine components operate in a harsh environment that may expose the component to high temperatures, high mechanical stresses, and potentially reactive combustion gases. The possible effects of this type of operating environment may be considered when selecting turbine component materials. For example, material characteristics such as resistance to heat, stress, fatigue, corrosion, erosion, and/or oxidation may be considered. Material costs and manufacturability may be considered as well, along with numerous other factors.
In accordance with one embodiment, a gas turbine component for use in a gas turbine engine includes a substrate and a non-aluminide protective coating. The substrate includes a Ni-based superalloy base material, and the non-aluminide protective coating is disposed over at least a portion of the base material. The protective coating includes a platinum-group metal.
In accordance with another embodiment, a gas turbine blade includes a platform having an underside and an opposite topside and an airfoil portion that includes an airfoil and the topside of the platform. The gas turbine blade further has a shank portion that includes a shank and the underside of the platform. A platinum-group metal is interdiffused with at least a portion of both of the airfoil portion and the shank portion, and the shank portion is non-aluminized.
In accordance with another embodiment, a method of coating a gas turbine blade for use in a gas turbine engine includes the step of interdiffusing a platinum-group metal with a base material of at least a portion of a shank portion of a turbine blade substrate.
In accordance with another embodiment, a non-aluminide corrosion-resistant coating comprises a platinum-group metal and a gamma/gamma prime microstructure.
Preferred exemplary embodiments of the invention will hereinafter be described in conjunction with the appended drawings, wherein like designations denote like elements, and wherein:
The protective coatings described herein may be used on gas turbine blades or other gas turbine components such as compressor blades, turbine or compressor vanes, seals, rotors or hubs, shafts, or any other component that may encounter the harsh environment present in a gas turbine or other type of combustion engine. Coatings arranged, produced, or used as taught herein may protect underlying component materials from corrosion and oxidation without substantially changing the ductility of the underlying materials, thereby improving the service life of the component by helping to improve its fatigue strength compared to components that include other less ductile coatings. These coatings may also be used in other non-turbine applications with components that may operate under high stress conditions, at elevated temperatures, and/or in a corrosive environment. As used herein, the term “corrosion” may be used to refer to oxidation, which is a specific form of corrosion, along with other types of corrosion.
Referring to
Platform 16 lies between the airfoil 12 and the shank 14, generally dividing the blade into an upper boundary portion 18 and a lower boundary region 20. The upper boundary region 18, also referred to as the gas path region, is exposed to combustion gases during operation and includes the airfoil 12 and a topside 22 of the platform 16. The lower boundary region 20 is generally not exposed to combustion gases during operation and includes an underside 24 of the platform 16 and any other blade components under the platform 16 or on the shank side of the platform 16. Blade 10 may include some relatively high stress regions near platform 16 when in operation. For example, a high stress region may be located where shank 14 meets the underside 24 of the platform 16 or where airfoil 12 meets the topside 22 of the platform 16, due to the transitions in the shape of the blade in those regions. This arrangement of components in turbine blade 10 may also result in the lower boundary region 20 operating at temperatures lower than those at which the gas path region 18 operates. For example, the lower boundary region 20 may operate at temperatures that range from about 1200-1600° F., while the gas path region 18 may operate at higher temperatures that may range from about 1900-2100° F. For purposes of this disclosure, the gas path region 18 may also be referred to as the airfoil portion, and the lower boundary region 20 may be referred to as the shank portion.
In the illustrated embodiment, turbine blade 10 also includes internal cooling channels 26, the ends of some of which are shown along the airfoil surface. Channels 26 may extend from one or more surfaces of the shank portion 20 to one or more surfaces of the airfoil portion 18 to facilitate the flow of a cooling fluid such as air therethrough. Various blade cooling arrangements are known in the art, and the cooling channels may be omitted entirely in some cases.
Due to the earlier-described harsh environment in and around an operating gas turbine engine, engine components are sometimes constructed using superalloy materials that have high strength, ductility, and creep resistance at high temperatures and relatively high resistance to corrosion. Superalloy materials may be based on nickel (Ni), cobalt (Co), or Ni-Iron. Examples of superalloys include alloys available under the trade names Hastelloy, Inconel, and René, such as René N4, René N5 or others. While the corrosion-resistance of superalloys may generally be considered very good as metal alloys are concerned, the elevated temperatures and stresses, corrosive combustion gases, and other elements (e.g., atmospheric pollutants or particulates, fuel additives and impurities, salts, etc.) in the gas turbine operating environment can accelerate the corrosion of even the most corrosion-resistant superalloys.
Various types of coatings or surface treatments have been developed in attempt to improve the corrosion-resistance of superalloy components for use in gas turbines. One type of coating that has been used for this purpose is an aluminide coating. Aluminide coatings generally include aluminum interdiffused with an underlying base material that is to be protected. Certain aluminide coatings, some of them including additional metal and/or metalloid components, are known to exhibit excellent resistance to high temperature corrosion and oxidation in gas turbine applications. But aluminide coatings may have the side effect of embrittling the surface of an otherwise sufficiently ductile base material, such as a superalloy material. Such embrittlement can lead to cracks in the surface of the coated component in high stress areas and/or in high fatigue areas, thereby exposing the underlying base material to accelerated corrosion or initiating mechanical failure.
Chromide coatings have also been proposed to improve the corrosion-resistance of superalloy components. Chromide coatings generally include chromium interdiffused with an underlying base material that is to be protected. Chromide coatings may not negatively affect the ductility of the base material to the degree that aluminide coatings do, but chromide coatings may be limited in their ability to resist corrosion at the high end of the range of gas turbine operating temperatures. As gas turbine engines are developed to have higher efficiency or power output, operating temperatures may generally increase. Thus, the available coatings for gas turbine components may be insufficient to provide the desired protection from corrosion, particularly in portions of the components that are subjected to high stresses or fatigue.
Referring to
Protective coating 40 is a layer of material that includes an increased resistance to corrosion relative to base material 35. A coating may be classified as either an overlay coating or an interdiffused coating. Both types of coatings may be at least partially interdiffused with an underlying material, but any interdiffusion that is present with an overlay coating is in the form of a relatively thin layer at the interface of the overlay coating and the underlying material. An interdiffused coating has a substantial portion of its thickness interdiffused with the underlying material, and may be entirely interdiffused with the underlying material. For example, a chromide coating may include a layer of material that is more chromium-rich than the underlying material and further includes the constituent elements of the underlying material.
In one embodiment, the protective coating 40 is a non-aluminide interdiffused coating. That is to say that no aluminum or aluminum-containing material is coated over the substrate 30 to form the protective coating 40, or that the base material has not been aluminized. Thus the only aluminum that may be present in the protective coating 40 may be from the base material 35, for example in the form of a gamma prime phase such as Ni3Al. Protective coating 40 may also include a platinum-group metal. One type of platinum-group metal is platinum (Pt). Pt-group metals include platinum, iridium, osmium, palladium, ruthenium, rhodium, and any combination thereof. In one embodiment, protective coating 40 includes Pt metal interdiffused with the base material 35 or other underlying material. In this instance, protective coating 40 may be described as a Pt-rich gamma/gamma prime coating. The Pt-rich gamma/gamma prime coating has increased resistance to corrosion compared to the base material 35 and may have higher corrosion-resistance than chromide coatings at some temperatures and/or to certain elements or compounds. When such a coating is produced by the methods described below, and possibly by other methods, the Pt-group metal is thought to reside primarily in the gamma prime phase of the base material 35 so that the protective coating 40 comprises a Ni-based solid solution gamma phase and a Ni3Al and/or Ni3Ti gamma prime precipitate phase that is rich in Pt-group metal. Additionally, a gamma/gamma prime coating rich in a Pt-group metal (also referred to herein as a Pt-group coating) such as platinum may have little to no effect on the ductility of the base material 35, thus offering the base material 35 superior protection from corrosion without substantially compromising its fatigue properties and/or other mechanical properties. The superior mechanical properties may also be accompanied by reduced weight compared to other coatings. For example, a non-aluminide Pt-group coating as described adds less weight to the coated component that a comparable Pt-aluminide coating and may thus be particularly advantageous in weight-sensitive applications such as smaller business class jet engines, helicopter turbines, and certain small engine military applications.
A gas turbine component including the gamma/gamma prime protective coating described above may be produced by the following illustrative method. A gas turbine component substrate that is constructed from the base material may be provided. A Pt-group metal is coated over the substrate by electroplating or other known techniques. The Pt-group metal is then interdiffused with the underlying material to form the Pt-group coating. The interdiffusion may be accomplished by heat treating the coated substrate. For example, the coated substrate may be placed in an inert or substantially evacuated environment at a temperature of about 1900° F. for 1 to 2 hours to interdiffuse the Pt-group metal with the underlying material at the substrate surface. Of course, these temperatures and times are non-limiting and may depend on several other factors. In one embodiment, Pt metal is electroplated over at least a portion of the substrate so that it has a thickness that ranges from about 0.1 to about 0.3 mils (2.5 to 7.5 μm). The plated substrate is then heat treated at the above-described conditions to interdiffuse the Pt and with the underlying material. The resulting protective coating may have a thickness that ranges from about 0.3 to about 2.0 mils (7.5 to 50 μm). The Pt-group metal may be coated and/or interdiffused with the base material using other methods. For example, the Pt-group metal may be coated onto the base material by ion-sputtering, CVD, PVD, slurry coating, molten dip-coating, or other suitable process. Interdiffusion may occur simultaneously in any deposition process that is performed at elevated temperatures in a range near the above-noted heat treating temperature.
Protective coating 40 may also include a chromide coating, though it is not required. A chromide coating is not shown separately in
Protective coating 40 may also include a dopant interdiffused therewith in a relatively small concentration, such as about 1.0 wt % or less, to promote coating adhesion and/or to form an oxide that further inhibits corrosion. One example of a suitable dopant is hafnium (Hf), though other transitional metals similar to Hf or Yttrium (Y) may also be used. Other examples include one or more rare earth metals. The dopant may be interdiffused with the protective coating in a separate process such as a vapor phase, CVD, or pack cementation process. Or the dopant may be simultaneously coated over the substrate with the chromate coating and/or the Pt-group coating and interdiffused therewith.
Referring again to
As shown in
Supplemental coating 50 may optionally include a thermal barrier coating, such as a ceramic coating. In such an instance, supplemental coating 50 may itself be a multi-layer coating that includes a bond coating and an overlying ceramic coating. Any bond coating known in the art may be used. One such bond coating is a Pt-aluminide bond coating, which may be formed by aluminizing or applying an aluminide coating on the protective coating 40. Various ceramic coatings for use as thermal barriers with turbine blades and methods of applying them, such as electron-beam PVD and solution plasma spray (SPS), are known and may be suitable for use over protective layer 40.
According to one or more of the structures and methods described above, one specific embodiment of turbine blade 10 includes a turbine blade substrate coated with a platinum-rich gamma/gamma prime coating 40 over the shank portion 20, and further includes a Pt-aluminide coating over the airfoil portion 18. This particular embodiment of a turbine blade may be formed by an exemplary method that includes providing a turbine blade substrate that includes a Ni-based super alloy base material, electroplating platinum metal over the base material, heat treating the Pt-coated substrate to at least partially interdiffuse the Pt with the base material, coating an aluminide coating over the Pt coating at the airfoil portion of the substrate, and heat treating the coated substrate again for formation of the gamma prime phase in the base material and/or in the protective coating. In another embodiment, a chromide coating is coated over substantially the entire surface of the base material of the turbine blade substrate prior to the platinum plating. In yet another embodiment, a thermal barrier coating is coated over the airfoil portion of the blade after the gamma prime phase formation.
It is to be understood that the foregoing is a description of one or more preferred exemplary embodiments of the invention. The invention is not limited to the particular embodiment(s) disclosed herein, but rather is defined solely by the claims below. Furthermore, the statements contained in the foregoing description relate to particular embodiments and are not to be construed as limitations on the scope of the invention or on the definition of terms used in the claims, except where a term or phrase is expressly defined above. Various other embodiments and various changes and modifications to the disclosed embodiment(s) will become apparent to those skilled in the art. All such other embodiments, changes, and modifications are intended to come within the scope of the appended claims.
As used in this specification and claims, the terms “for example,” “e.g.,” “for instance,” “such as,” and “like,” and the verbs “comprising,” “having,” “including,” and their other verb forms, when used in conjunction with a listing of one or more components or other items, are each to be construed as open-ended, meaning that that the listing is not to be considered as excluding other, additional components or items. Other terms are to be construed using their broadest reasonable meaning unless they are used in a context that requires a different interpretation.
This application claims the benefit of U.S. Provisional Ser. No. 61/505,724 filed on Jul. 8, 2011, the entire contents of which are incorporated herein by reference.