Patent Application
20120075771
This application claims priority under 35 U.S.C. §119 to Korean Patent Application No. 10-2010-0093721, filed on Sep. 28, 2010, in the Korean Intellectual Property Office, the disclosure of which is incorporated herein by reference in its entirety.
The present invention relates to a coin type lithium ion capacitor, and more particularly, to a coin type lithium ion capacitor having a high capacity coin type structure which has high energy density and output density and improves stability.
In recent years, a battery in which carbon material such as graphite is used as a negative electrode material and a lithium-containing metallic oxide such as LiCoO2 is used as a positive electrode material has been suggested. The battery is called a rocking chair battery in which after assembling cells, lithium ions are supplied from the lithium-containing metallic oxide of the positive electrode to the negative electrode by charging the cells and during discharge, the lithium ions of the negative electrode are transferred back to the positive electrode. In other words, the battery is called a lithium-ion rechargeable battery in which only the lithium ions are involved in the charge and discharge without using metallic lithium in the negative electrode, and is distinguished from a lithium battery using the metallic lithium. The battery is characterized by high voltage, capacity, and stability.
With environmental issues coming to the forefront, a storage system for clean energy obtained by photovoltaic power generation or wind power generation or a power supply for an electric vehicle or hybrid electric vehicle substituting for a gasoline vehicle is being developed. As vehicle mounted apparatuses or equipment such as power windows or IT-related machines recently have high performance and high function, a new power supply is needed in view of energy density and output density.
As an electric storage device that responds to such applications that necessitate high energy density and high output characteristics, recently, an electric storage device called a hybrid capacitor in which electric storage principles of a lithium ion rechargeable battery and an electric double layer capacitor s gathering attention. As one of the hybrid capacitors, an organic electrolyte capacitor has been suggested, which uses for a negative electrode a carbon material capable of significantly increasing energy density by allowing the carbon material that can store and release lithium ions to store and carry (hereinafter, in some cases, referred to as “pre-doping”) the lithium ions chemically or electrochemically in advance to thereby lower a negative electrode potential.
Recently, the demand for a high capacity organic electrolyte capacitor with improved stability which has higher energy density and output density gradually increases, and particularly, the demand for a lithium ion capacitor which may be used in the range of 4.2 V to 4.4 V has gradually increased, but a research on the capacitor is not actively being conducted.
Therefore, it is urgent to develop a 4.2 V to 4.4 V lithium ion capacitor having high energy density and output density.
A coin type battery is useful in terms of utilization and basically has a two-electrode structure. Therefore, there is a problem in that after a complicated pre-doping process, a process of disassembling a battery to remove a lithium metallic electrode and reassembling the other electrode is required in a manufacturing process.
An exemplary embodiment of the present invention provides a coin type lithium ion capacitor, including: a positive electrode made of an activated carbon based positive active material; and a negative electrode opposite to the positive electrode with a first separator interposed therebetween. The negative electrode may include a graphite electrode including a first current collector and a graphite based negative active material coated onto the first current collector; and a lithium metal member opposite to the graphite electrode with a second separator interposed therebetween and including a second current collector and a lithium metal coated on the second current collector, in which lithium ions of the lithium metal move from the lithium metal to the positive electrode through the graphite electrode during discharge and are carried in the graphite electrode from the positive electrode during charge.
Another exemplary embodiment of the present invention provides a coin type lithium ion capacitor, including: a positive electrode including an activated carbon based positive active material; and a negative electrode opposite to the positive electrode with a first separator interposed therebetween, in which the negative electrode includes a graphite electrode including a first current collector and a graphite based negative active material coated onto the first current collector; and a lithium metal member opposite to the graphite electrode with a second separator interposed therebetween and including a second current collector and a lithium metal coated on the second current collector, in which lithium ions of the lithium metal move from the lithium metal to the positive electrode through the graphite electrode during discharge and are carried in the graphite electrode from the positive electrode during charge.
Other features and aspects will be apparent from the following detailed description, the drawings, and the claims.
Hereinafter, exemplary embodiments will be described in detail with reference to the accompanying drawings. Throughout the drawings and the detailed description, unless otherwise described, the same drawing reference numerals will be understood to refer to the same elements, features, and structures. The relative size and depiction of these elements may be exaggerated for clarity, illustration, and convenience. The following detailed description is provided to assist the reader in gaining a comprehensive understanding of the methods, apparatuses, and/or systems described herein. Accordingly, various changes, modifications, and equivalents of the methods, apparatuses, and/or systems described herein will be suggested to those of ordinary skill in the art. Also, descriptions of well-known functions and constructions may be omitted for increased clarity and conciseness.
The present invention provides a lithium ion capacitor without the need for a pre-doping process, particularly, a lithium ion capacitor with a two-electrode structure which has a stable charge and discharge characteristic in a wide range of voltage by a self-discharge process and a cell-activation process instead of the pre-doping process.
To this end, the lithium ion capacitor according to the present invention has a two-electrode structure including a positive electrode made of an activated carbon based positive active material and a negative electrode formed of a graphite electrode capable of carrying lithium ions and a lithium metal member connected to the graphite electrode by a wire. The two-electrode structure does not need a pre-doping process of allowing a graphite to carry lithium ions which is used in a lithium ion capacitor of the related art.
The lithium ion capacitor of the present invention has a charge and discharge characteristic by a potential difference between the positive electrode and the negative electrode which is created through a self-discharge process (or an initial self-discharge process) and a cell-activation process and as a result, the pre-doping process is not needed. Therefore, the lithium ion capacitor can be manufactured without the additional pre-doping process because of the two-electrode structure and particularly, manufactured in a coin type which has wide applicability.
Herein, the self-discharge process refers to a process in which lithium ions naturally move from the lithium metal to the graphite electrode by the potential difference by electrochemical contact between the graphite electrode constituting the negative electrode and the lithium metal.
The cell-activation process refers to a process in which the lithium ions discharged during repeated charge/discharge between the graphite electrode and the activated carbon based positive electrode are not deposited as lithium metal but carried in the graphite when the lithium ions are charged in the graphite electrode after the self-discharge process.
Therefore, the present invention may provide the coin type lithium capacitor having high output and high capacity like the coin type cell of the related art used as a primary battery and a lithium rechargeable battery by the two-electrode structure having the negative electrode including the graphite electrode effectively carrying the lithium ions, and the activated carbon based positive electrode through the self-discharge process and the cell-activation process.
Meanwhile, during the cell-activation process, when the discharged lithium ions are not completely charged in the graphite electrode, the problem in that the lithium ions which are not charged but left are deposited may occur. In this case, there may be problems such as generation of gas due to a side reaction of the deposited lithium ions with an electrolytic solution filled in the lithium ion capacitor.
In the present invention, two methods for preventing the lithium ions from being deposited are suggested.
In the first method, a lithium metal member constituting the negative electrode includes a lithium metal current collector and lithium metal coated on the lithium metal current collector, in which the lithium metal is coated on the current collector at the amount of less than acceptable capacity of the graphite based negative active material constituting the graphite electrode. As a result, it is possible to prevent the lithium ions from being deposited. That is, when a full discharge between the lithium metal and the activated carbon based positive electrode is made, the lithium metal is coated on the lithium metal current collector at the amount obtained by analyzing the actually acceptable capacity so that no lithium metal is left.
In the second method, a current collector structurally constituting a graphite electrode is formed in a mesh type to allow lithium ions to diffuse through the graphite electrode coated on the mesh type current collector. In the negative electrode structure including the lithium metal member and the graphite electrode according to the present invention, since the lithium metal coated on the lithium metal current collector is provided at a lower portion of the graphite electrode, the lithium ions diffuse through the mesh type graphite electrode during discharge between the lithium metal and the activated carbon based positive electrode. Therefore, a predetermined amount of lithium ions diffuse to the activated carbon based positive electrode while being intercalated into the graphite electrode and as a result, the lithium ions are not deposited as the lithium metal again but carried into the graphite electrode during charge, that is, the lithium ions structurally exists in an LiC6 form.
In the present invention, in order to minimize the deposition of the lithium metal, the respective electrodes are coated so that the electrodes have capacity in order of an activated carbon electrode (positive electrode), a graphite electrode (negative electrode), and lithium metal in designing the electrodes.
Hereinafter, an exemplary embodiment of the present invention will be described in detail with reference to the accompanying drawings.
Referring to
The electrochemical cell ES is received in the receiving space and an electrolytic solution is filled in the rest of the receiving space. The electrolytic solution may be composed of a non-protonic organic solvent and an electrolyte of a lithium salt and as the organic solvent, one or two kinds or more of ethylene carbonate, propylene carbonate, butylene carbonate, γ-butyrolactone, 1,2-dimethoxyethane, 1,3-dioxolane, dimethyl carbonate, ethyl methyl carbonate, and diethyl carbonate may be mixed and as the lithium salt, one of LiBF4, LiClO4, LiPF6, LiCF3SO3, Li(CF3SO2)2N may be used.
The electrochemical cell ES includes a positive electrode 240 made of an activated carbon based positive active material and a negative electrode 260 opposite to the positive electrode 240 with a first separator 250 interposed therebetween.
The positive electrode 240 is made of a positive active material that is coated on a current collector (not shown) (hereinafter, referred to as “cathode current collector”) to reversibly carry lithium ions and anions and an activated carbon may be used as the positive active material. A conductive material such as acetylene black and a metal powder may be used as a conducting material used in manufacturing the positive electrode. The conducting material may be applied at the ratio of 1% to 50% of the positive active material. In the case where the activated carbon is in a powder form, a binder material may be used to coat the activated carbon in a powder form onto the cathode current collector. For example, rubber binders such as SBR, fluorine-containing resins such as polytetrafluoroethylene (PTEE) and polyvinylidene fluoride (PVDF), acrylic resins, and thermoplastic resins may be used.
The negative electrode 260 includes a graphite electrode 262, a second separator 264, and a lithium metal member 266.
Specifically, as shown in
The mesh type shape allows the lithium ions generated from the lithium metal member 266 to smoothly move (or diffuse) to the positive electrode through the first current collector 262A. The negative active material 262B can reversibly carry the lithium ions generated from the lithium metal member 266 and may use a graphite material such as graphite and hard carbon. The graphite based negative active material is coated onto the mesh type first current collector 262A to constitute the graphite electrode 262.
The lithium metal member 266 is provided opposite to the graphite electrode with the second separator 264 interposed therebetween. The lithium metal member 266 includes a second current collector 266A and lithium metal 266B coated onto the second current collector 266A. As described above, in order to prevent the lithium ions generated from the lithium metal 266B from being completely carried in the graphite electrode 262 and deposited as lithium metal, the lithium metal 266B may be coated on the second current collector 266A at the amount of less than the acceptable capacity of the graphite based negative active material 262B.
As described above, according to the exemplary embodiment of the present invention, in order to design the lithium ion capacitor in a coin type having a two-electrode structure, the graphite electrode 262 and the lithium metal member 266 are electrically connected by a wire 268 to constitute a single cell, in which the single cell acts as a negative electrode.
After assembling cells, the lithium ions repeatedly diffuse to the cathode and the anode (for example, 5 cycles) through charge and discharge processes as the initial high-temperature self-discharge process and the cell-activation process and finally are carried in the graphite as the anode.
The coin type lithium ion capacitor of the present invention can prevent gas from being generated by a side reaction of the activated carbon as the positive active material and the lithium metal with the electrolytic solution at 4.2 V or more.
The reason is that all the lithium metal 266B engaging with the graphite electrode 260 constituting the negative electrode is intercalated into the cathode to be consumed and as a result, the gas is prevented from being generated by the side reaction with the electrolytic solution, which makes it possible to stably drive cells even at 4.2 V or more.
As such, the lithium ion capacitor of the present invention has the two-electrode structure with the positive electrode and the negative electrode opposite to the positive electrode, in which the negative electrode is formed in a structure having the graphite electrode and the lithium metal which are connected by the wire.
By having the structure, the lithium ion capacitor can provide stability and very high energy density and output density by the self-discharge process and the cell-activation process without the pre-doping process in manufacturing the capacitor.
Meanwhile, the lithium ion capacitor can be charged and discharged even in a structure having the lithium metal and the positive electrode without the graphite electrode shown in
As shown in
Based on the fact, the present invention provides a charge and discharge characteristic which is stable even at 4.2 V or more by including the graphite electrode carrying the lithium ions generated from the lithium metal between the positive electrode and the lithium metal.
Cells were manufactured to have a weight ratio of a cathode to an anode of 1:1, 2:1, and 3:1, respectively and were subjected to a test. In self-discharge and activation processes of cells, coin cells were manufactured and allowed to be left in an oven of 60° C. for 48 hours so that lithium ions were self-discharged to the anode by a physical contact in the manufactured cell. The lithium ions were diffused by electrochemically bringing the cathode into contact with the anode/lithium metal electrode so that in the coin cell subjected to the self-discharge process, the lithium ions from the lithium metal as a lithium ion source are carried in the anode. In the initial activation process, an electrochemical activation step was performed by 1.5 to 4.5 V.
The lithium metal was completely consumed after performing the initial charge and discharge processes ten times and intercalated into the graphite based negative active material. Consequently, no lithium metal was left.
The coin type lithium ion capacitor subjected to the cell activation step showed a stable charge and discharge curve. That is, as shown in
However, as shown in
It was confirmed that the case where the weight ratio of cathode to anode is 3:1 had higher capacity compared to the cases where the weight ratios are 2:1 and 1:1 and consequently, it can be seen that the capacity of the coin type lithium ion capacitor is determined by the cathode.
According to the exemplary embodiment of the present invention, it is possible to provide a coin type lithium ion capacitor having stability of a coin type typified by a two-electrode structure and high energy density and output density by a self-discharge process and a cell-activation process without a pre-doping process.
From the foregoing, it will be appreciated that various embodiments of the present disclosure have been described herein for purposes of illustration, and that various modifications and changes may be made without departing from the scope and spirit of the present disclosure. For example, in the exemplary embodiment, the coin type lithium ion capacitor having the two-electrode structure is mainly described, but the present invention may include another type of lithium ion capacitor in addition to the coin type. Accordingly, the various embodiments disclosed herein are not intended to be limiting, with the true scope and spirit being indicated by the following claims.