Patent Application
20140145117
The present invention relates to a solid Gd promoted mesoporous Ni-ZSM-5 catalyst, process for the preparation thereof and a process for vapours phase dry reforming of methane with carbon dioxide for the production of syngas (mixture of carbon monoxide and hydrogen). Particularly, the present invention relates to a process for the carbon dioxide reforming of methane to syngas over a Gd promoted Ni-ZSM-5 solid catalysts. More particularly, the present invention relates to a process for the vapour phase carbon dioxide reforming of methane to syngas by using a coke resistant Gd promoted Ni-ZSM-5 catalyst.
The world's demand for energy continues to grow due to population growth and improving standards of living. At the same time, the days of fossil fuel and gas are diminishing constantly. Although, the existing resources will be able to meet the global demand of fuel and chemicals for next two decades. Time has come to discover alternative resources for potential future fuel and more efficient up gradation of natural fuel resources. Globally, there are abundant supplies of natural gas, much of which can be developed at relatively low cost. The current mean projection of global remaining recoverable resource of natural gas is 16,200 Trillion cubic feet (Tcf), 150 times current annual global gas consumption, with low and high projections of 12,400 Tcf and 20, 800 Tcf, respectively. Natural gas is basically having a methane conc. of up to 85% alongside impurities such as sulphur and carbon dioxide as the chief impurities. Some time, it may contain sizeable amount of CO2 (upto 25%) as impurity. Hence, any transformation requiring direct conversion of natural gas must be having robust catalytic system with least possible time bound deactivation.
The up gradation of methane or natural gas to valuable chemical feedstock proceeds through indirect routs by initial conversion to syngas (a mixture of carbon monoxide and hydrogen). The production of syngas can be carried out by steam reforming (SR) (very large scale process) and even through partial oxidation of methane (PDX). Although partial oxidation of methane have high methane conversion with excellent syngas selectivity and extremely fast reaction kinetics, but is suffer from local heat generation over the catalyst and safety issues. Whereas the SR do not suffer from those safety issues but steam reforming of methane produce CO2 along with syngas which need to remove before its downstream GTL applications.
However, despite of unfavorable thermodynamics dry reforming of methane has some unique advantages; it can generate syngas at unite CO/H2 ratio, moreover it becomes advantageous because of the use of two greenhouse gases at a time. Low quality natural gas can be utilized for syngas production in near future; even the source gas does not need any further purification. A fundamental option currently explored is to reduce CO2 to chemicals and energy carriers using reduction equivalents from renewable resources. From this perspective the dry reforming of methane over metal based solid catalyst has drawn much attention in recent years and is now viewed as an area to produce ultra pure hydrogen or syngas for future fuel alternatives. As this would conceptually allow the efficient valuation of methane and the reforming technology requires the preparation of thermally stable and coke resistant CO2 reforming catalyst. The conventional supported nickel catalyst used for methane reforming are very active for carbon formation leads to rapid deactivation of catalyst, while coke-resistance alternatives (Rh, Ru, Pt etc) are bounded by its availability and high cost. So economic boundary conditions dictate the use of Ni based catalysts. There are reports on dry reforming of methane over different solid catalyst but to the best of our knowledge there is no reference for the use of gadolinium (Gd) promoted Ni-ZSM-5 catalyst for this purpose.
ZSM-5 (ZEOLITE SOCONY MOBIL-5) is an aluminosilicate zeolite belonging to the pentasil family of zeolites. Its chemical formula is NanAlnSi96-nO192.16H2O (0<n<27).
Reference may be made to article in the Catalysis Today, 2011, 171, 132-139 by I. Sarusi et al. where they got about 19% methane conversion with CO/H2 ration of over doped Rh/Al2O3 catalyst.
Reference may be made to article in the Green Chemistry, 2007, 9, 577-581 by S. Williams and his group reported the use of O2 permeable ceramic membrane for the CO2 reforming of methane to syngas. On this article they described a very high concentration of feed gas (notably 80% feed concentration) to get 28% methane conversion. The meanwhile it is been observed that the membrane reactor which catalyses the reaction itself get deactivated (50%) after 14 h.
Reference may be made to US patent no US2007/0253886A by Abatzoglou and his group. Where they used active metal (mainly Ni) deposited on non-porous metallic and ceramic support; the catalyst shows very high methane conversion of 98% at 800° C. with CO/H2 ratio of 0.98. But the catalyst stability was limited up to 18 h time on stream.
Reference may be made to article in the Chem Cat Chem, 2011, 3, 593-606, in which Glaser et al and his group reported a highly stable and porous zirconia as support. With 5% Ni supported on ZrO2 they achieved 75% methane conversion at 750° C. with a comparatively slow GHSV of 7.2×104 ml h−1 g−1.
Reference may be made to article in the Chemical Communication, 2001, 415-416 in which Japanese worker Fujimoto and his group reported the production of syngas by pulse irradiation technique on a mixture of CH4 and CO2 at low temperature and atmospheric pressure. They achieved almost 42% methane conversion with H2/CO ratio of 1.5 with 1:1.5 CH4 to CO2 feed ratio at 180° C. while in presence of NiMgO catalyst the same technique gives almost 69% methane conversion while the H2/CO ration goes down to 0.86 with 1:1 CH4 to CO2 feed ratio.
Reference may also be made to article in the ACS Catalysis, 2012, 2, 1331-1342, which Chou et al. reported a mesoporous tri-metallic composite of NiO—CaO—Al2O3 in the dry reforming of methane. In this report they found 89% of methane conversion at 750° C. whereas the GHSV is 15000 ml g−1 h−1. But the H2/CO ratio is only able to rise up to 0.88 at 750° C.
Reference may be made to article in the Catalysis Communication, 2001, 2, 255-260, in which Aika et al reported the use Ru supported titania catalyst over dry reforming of methane. At industrial condition, at 0.1 MPa and 800° C. the catalyst shows a stable activity for 25 h time on stream with CO2 conversion of −46%.
The drawback of the processes reported so far is that although they exhibit sufficiently high conversions of methane for high selectivity of syngas of unit H2/CO ratio but the rapid formation of coke causes deactivation of reforming catalyst. To overcome the deactivation many researchers used novel metals such as Pt, Ru, Rh etc but the rising cost and relatively poor availability desiccates the use of those catalyst in industrial purpose. On this economic boundation, Ni based catalyst will be the holy grail for methane reforming in coming future. There is, therefore, an evident necessity for further improvements in the Ni based catalyst and process for the dry reforming of methane with carbon dioxide.
The main object of the present invention is to provide a solid Gd promoted mesoporous Ni-ZSM-5 catalyst and a process for the preparation thereof and a process for vapours phase reforming of methane with carbon dioxide for the production of syngas.
Another object of the present invention is to provide a process which selectively gives syngas from methane and carbon dioxide with CO/H2 ratio equal to 1.
Yet another object of the present invention is to provide a process and catalyst which uses two greenhouse gases at a time to produce syngas for future fuel alternatives.
Yet another object of the present invention is to provide a process which works continuously more than 40 h without any deactivation of reforming catalyst under continuous process for the production of syngas from dry reforming of methane.
Yet another object of the present invention is to provide a catalyst promoted by Gd and which can be prepared easily and also very economical to produce syngas from dry reforming of methane.
Accordingly the present invention provides solid Gd promoted mesoporous Ni-ZSM-5 catalyst which comprises Gd in the range of 0.01-0.5%, Ni in the range of 3-15% and the remaining being ZSM-5.
In one embodiment of the present invention solid Gd promoted mesoporous Ni-ZSM-5 catalyst is coke resistant up to 40 h under the reaction condition.
In an embodiment of the present invention a process for the preparation of solid Gd promoted mesoporous Ni-ZSM-5 catalyst, wherein the said process comprising the steps of;
In another embodiment of the present invention the weight ratio of Gd to Ni varied the range of 0.01 to 0.5%.
Still in another embodiment of the present invention weight ratio of Ni to ZSM-5 varied in the range of 3 to 15%.
Still in another embodiment of the present invention a process for vapours phase reforming of methane with carbon dioxide for the production of syngas using Solid Gd promoted mesoporous Ni-ZSM-5 catalyst, wherein the said process comprising the steps of;
Still in another embodiment of the present invention molar ratio of CH4:CO2:He is 1:1:8.
Still in another embodiment of the present invention reactor used in step (a) is a fixed bed reactor.
Still in another embodiment of the present invention the conversion of methane is in the range of 1-95%.
Still in another embodiment of the present invention the H2/CO ratio of syngas obtained in the range of 0.82-1.0.
The present invention provides a catalyst and process for the production of syngas from dry reforming of methane under atmospheric pressure over Gd promoted mesoporous Ni-ZSM-5 catalyst which involves the following steps
Synthesis of mesoporous ZSM-5 using adequate amount of NaAlO2, tetrapropylammonium hydroxide (TPAOH), tetraethyl orthosilicate (TEOS), cationic copolymer Poly (diallyldimethylammonium chloride) with sufficient amount of water hydrothermally treated at 180° C. for 7 days for crystallization and finally filtered and washed with cold water; dried overnight and calcined at 650° C. for 3 hrs to remove the template.
Synthesis of Gd promoted Ni-ZSM-5 catalyst using the colloidal route of synthesis of Gd—Ni nanoparticle followed by successful dispersion over previously prepared mesoporous ZSM-5 (Na form) where the weight ratio of Gd to Ni varied the range of 0.01 to 0.5.
The dry reforming of methane was carried out in a fixed-bed down flow reactor at atmospheric pressure. Typically 200 mg of catalyst was placed in between two quartz wool plugged in the centre of the 6 mm quartz reactor. The catalyst was reduced in H2 (10% H2 in He) with the flow rate of 10 ml/min for 3 h at 700° C. After the reduction the temperature was changed and dry reforming of methane was carried out at different temperature (650-900° C.). The gas hourly space velocity (GHSV) was varied between 10000 ml g−1 h−1 to 30000 ml g−1 h−1 with a molar ratio of CH4:CO2:He of 1:1:8. The reaction products were analysed using an online gas chromatography (Agilent 7890A) fitted with a TCD detector using two different columns Molecular sieves (for analysing H2) and PoraPack-Q (for analysing CH4, CO2 and CO).
The following examples are given by way of illustration of working of the invention in actual practice and should not be constructed to limit the scope of the present invention in any way.
An aqueous solution of NaAlO2 (0.08 g) was added with 7 ml 25% tetrapropylammonium hydroxide (TPAOH). Subsequently, 7.0 ml tetraethyl orthosilicate (TEOS) was added and the mixture was aged at 100° C. under vigorously stirring for 2 h. The pH of the solution was observed in between 9-10. Then a cationic copolymer Poly (diallyldimethylammonium chloride) (PDDAM) was added (4 g) into the precursors. The resultant mixture was kept for at stirring for 12 h at 35° C. Finally the content was transferred in to stainless steel lined autoclave for hydrothermal synthesis at 180° C. for 7 days.
The resultant mixed species was washed with ethanol, and dried at 110° C., for 24 hours, followed by calcination at 650° C. for 5 h to obtain ZSM-5. (Reference: 21. F. S. Xiao, L. Wang, C. Yin, K. Lin, Y. Di, J. Li, R. Xu, D. S. Su, R. Schlogl, T. Yokoi, and T. Tatsumi, Angew. Chem. Int. Ed., 45, (2006), 3090)
The impregnation of Gd—Ni was done following colloidal method. Where a given amount of Gd(NO3)3.6H2O (0.0115 g) was taken with given amount of Ni(NO3)3.6H2O (0.98 g) into 20 ml ethylene glycol and reduced at 160° C. for 3 h. The reagents were added maintaining the following molar ratio:
The content was added into previously prepared ZSM-5 (2 g) and continuously stirred for 30 min. Then the mixture was evaporated to dryness at 100° C. and kept for drying at 120° C. for 6 hrs. Then the material was calcined in air atmosphere at 750° C. for 4 h.
The catalyst can be denoted as % Gd-% Ni-ZSM-5 (0.2 wt % Gd, 10% Ni). The catalyst was characterized by PXRD, SEM, TEM.
An aqueous solution of NaAlO2 (0.08 g) was added with 7 ml 25% tetrapropylammonium hydroxide (TPAOH). Subsequently, 7.0 ml tetraethyl orthosilicate (TEOS) was added and the mixture was aged at 100° C. under vigorously stirring for 2 h. The pH of the solution was observed in between 9-10. Then a cationic copolymer Poly (diallyldimethylammonium chloride) (PDDAM) was added (4.0 g) into the precursors. The resultant mixture was kept for at stirring for 12 h at 35° C. Finally the content was transferred in to stainless steel lined autoclave for hydrothermal synthesis at 180° C. for 7 days.
The resultant mixed species was washed with ethanol, and dried at 110° C., for 24 hours, followed by calcination at 650° C. for 5 h to obtain ZSM-5. (Reference: 21. F. S. Xiao, L. Wang, C. Yin, K. Lin, Y. Di, J. Li, R. Xu, D. S. Su, R. Schlogl, T. Yokoi, and T. Tatsumi, Angew. Chem. Int. Ed., 45, (2006), 3090)
The impregnation of Gd—Ni was done following colloidal method. Where a given amount of Gd(NO3)3.6H2O (0.0115 g) was taken with given amount of Ni(NO3)3.6H2O (0.49 g) into 20 ml ethylene glycol and reduced at 160° C. for 3 h. The reagents were added maintaining the following molar ratio:
The content was added into previously prepared ZSM-5 (2 g) and continuously stirred for 30 min. Then the mixture was evaporated to dryness at 100° C. and kept for drying at 120° C. for 6 hrs. Then the material was calcined in air atmosphere at 750° C. for 4 h.
The catalyst can be denoted as % Gd-% Ni-ZSM-5 (0.2 wt % Gd, 5% Ni). The catalyst was characterized by PXRD, SEM, TEM.
This example describes the production of syngas from dry reforming of methane by gas phase reaction in presence of Gd promoted mesoporous Ni-ZSM-5 as catalyst.
Gd:Ni weight ratio in the catalyst=0.2:5
Process pressure: 1 atm
Gas hourly space velocity (GHSV): 10000 ml g−1 h−1
Reaction time: 1 h
Methane conversion: 95.1%
H2/CO ratio: 0.96
The example describes the effect of temperature on conversion and H2/CO ratio of dry reforming of methane. The product analysis presented in Table-1.
Gd:Ni weight ratio in the catalyst=0.2:5
Process pressure=1 atmosphere
Gas hourly space velocity (GHSV): 10000 ml g−1 h−1
Reaction time: 1 h
The example describes the effect of time on stream on conversion of methane and H2/CO ratio of dry reforming of methane. The product analysis presented in Table 2
Gd:Ni weight ratio in the catalyst=0.2:5
Process pressure: 1 atm
Gas hourly space velocity (GHSV): 10000 ml g−1 h−1
Reaction temperature: 800° C.
The example describes the effect of gas hourly space velocity on the conversion of methane and H2/CO ratio of dry reforming of methane. The product analysis presented in Table-3.
Gd:Ni weight ratio in the catalyst=0.2:5.
Process pressure: 1 atm
Reaction time: 1 h
The main advantages of the present invention are:
| Number | Date | Country | Kind |
|---|---|---|---|
| 3614/DEL/2012 | Nov 2012 | IN | national |