Patent Grant
11918676
This disclosure is in the field of colloidal dispersions. Specifically, this disclosure pertains to using poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan in colloidal dispersions.
Driven by a desire to find new structural polysaccharides using enzymatic syntheses or genetic engineering of microorganisms or plant hosts, researchers have discovered polysaccharides that are biodegradable, and that can be made economically from renewable resource-based feedstocks. One such polysaccharide is poly alpha-1,3-glucan, a glucan polymer characterized by having alpha-1,3-glycosidic linkages. This polymer has been isolated by contacting an aqueous solution of sucrose with a glucosyltransferase enzyme isolated from Streptococcus salivarius (Simpson et al., Microbiology 141:1451-1460, 1995). Films prepared from poly alpha-1,3-glucan tolerate temperatures up to 150° C. and provide an advantage over polymers obtained from beta-1,4-linked polysaccharides (Ogawa et al., Fiber Differentiation Methods 47:353-362, 1980).
U.S. Pat. No. 7,000,000 disclosed the preparation of a polysaccharide fiber comprising hexose units, wherein at least 50% of the hexose units within the polymer were linked via alpha-1,3-glycosidic linkages using a Streptococcus salivarius gtfJ enzyme. This enzyme utilizes sucrose as a substrate in a polymerization reaction producing poly alpha-1,3-glucan and fructose as end-products (Simpson et al., 1995). The disclosed glucan triacetate polymer formed a liquid crystalline solution when it was dissolved above a critical concentration in a solvent or in a mixture comprising a solvent. From this solution continuous, strong fibers were spun. After regeneration back to glucan cotton-like fibers, highly suitable for use in textiles, were created and used.
Development of new colloidal dispersions are desirable given their potential utility in various applications, including food, oil field, pharmaceutical, personal care and specialty industries.
In a first embodiment, the disclosure concerns a colloidal dispersion comprising: (a) poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan; and (b) a solvent.
In a second embodiment, the poly alpha-1,3-1,6-glucan has alpha-1,3 and alpha-1,6-glycosidic linkages comprising: (a) at least 30% of the glycosidic linkages are alpha-1,3 linkages; and (b) at least 30% of the glycosidic linkages are alpha-1,6 linkages.
In a third embodiment, the poly alpha-1,3-glucan and the poly alpha-1,3-1,6-glucan comprise particles with an average particle diameter size of between 5 nm and 200 nm.
In a fourth embodiment, the particles have a spherical or cylindrical shape.
In a fifth embodiment, the particles form aggregates with an average aggregate diameter size of between 10 nm and 200 μm.
In a sixth embodiment, the solvent is water.
In a seventh embodiment, the poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan constitutes between 0.1% by wt. and 15% by wt. of the total colloidal dispersion.
In an eighth embodiment, the colloidal dispersion has a viscosity of at least 10 cPs.
In a ninth embodiment, the colloidal dispersion has a pH between 1 and 14.
In a tenth embodiment, the colloidal dispersion has a viscosity and a pH wherein the viscosity changes less than 10% while the pH is changed over a range between 2 and 11.
In an eleventh embodiment, the colloidal dispersion further comprises a salt or surfactant wherein the colloidal dispersion has a viscosity that changes less than 10% after the addition of the salt or surfactant.
In a twelfth embodiment, the colloidal dispersion has shear thinning behavior or shear thickening behavior.
In a thirteenth embodiment, the colloidal dispersion is in the form of a personal care product, pharmaceutical product, food product, household product, or industrial product.
In a fourteenth embodiment, the disclosure concerns a personal care product comprising a colloidal dispersion comprising: (a) poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan; and (b) a solvent.
In a fifteenth embodiment, the disclosure concerns a food product comprising a colloidal dispersion comprising: (a) poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan; and (b) a solvent.
In a sixteenth embodiment, the disclosure concerns a process for making a poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan colloidal dispersion comprising: (a) heating an enzyme reaction solution comprising an aqueous basic buffered solution of an enzyme, sucrose and, optionally, antimicrobial agent to make a slurry containing poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan; (b) filtering the slurry to isolate the poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan in the form of a wet cake; (c) washing the wet cake with water; and (d) dispersing the wet cake in water to form a poly alpha-1,3-glucan colloidal dispersion.
In a seventeenth embodiment, the disclosure concerns a process for making a poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan colloidal dispersion can have at least one of the following: (a) heating the enzyme reaction solution at 20-25° C. for 24 hours; (b) the enzyme for making poly alpha-1,3-glucan is Streptococcus salivarius gtfJ; (c) the enzyme for making poly alpha-1,3-1,6-glucan is Streptococcus oralis gtf 4297, Streptococcus sp. C150 gtf 3298 or Streptococcus mutans gtf 0544; (d) the aqueous basic buffered solution has a pH buffering agent of an alkali metal phosphate buffer; (e) the alkali metal phosphate buffer wherein the alkali metal is potassium; (f) the aqueous basic buffered solution has a pH between 7 and 5; (g) the antimicrobial agent is FERMASURE®; and (h) the wet cake contains between 60 to 80% wt % water.
In an eighteenth embodiment, the disclosure concerns a poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan colloidal dispersion prepared according to a process comprising: (a) heating an enzyme reaction solution comprising an aqueous basic buffered solution of an enzyme, sucrose and, optionally, antimicrobial agent to make a slurry containing poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan; (b) filtering the slurry to isolate the poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan in the form of a wet cake; (c) washing the wet cake with water; and (d) dispersing the wet cake in water to form a poly alpha-1,3-glucan colloidal dispersion.
The disclosures of all patent and non-patent literature cited herein are incorporated herein by reference in their entirety.
As used herein, the term “colloidal dispersion” refers to a heterogeneous system having a dispersed phase and a dispersion medium, i.e., microscopically dispersed insoluble particles are suspended throughout another substance. An example of a colloidal dispersion in water is a hydrocolloid. The colloidal dispersion may be a stable colloidal dispersion or an unstable colloidal dispersion. The stable colloidal dispersion is stable at room temperature and/or at elevated temperature, for example, between 40 and 50° C. for a period of at least one month with no visible settling. The unstable dispersion, under the same conditions, may see at least a portion of the poly alpha-1,3-glucan and/or poly alpha-1,3-1,6-glucan settle out of the dispersion. Agitation of the settled material will generally re-form the colloidal dispersion. In some embodiments, the colloidal dispersion is a stable dispersion. In other embodiments, the colloidal dispersion is an unstable dispersion.
The terms “poly alpha-1,3-glucan”, “alpha-1,3-glucan polymer” and “glucan polymer” are used interchangeably herein. Poly alpha-1,3-glucan is a polymer comprising glucose monomeric units linked together by glycosidic linkages, wherein at least 50% of the glycosidic linkages are alpha-1,3-glycosidic linkages. Poly alpha-1,3-glucan is a type of polysaccharide. The structure of poly alpha-1,3-glucan can be illustrated as follows:
Poly alpha-1,3-glucan can be prepared using chemical methods. Alternatively, it can be prepared by extracting it from various organisms, such as fungi, that produce poly alpha-1,3-glucan. Alternatively still, poly alpha-1,3-glucan can be enzymatically produced from sucrose using one or more glucosyltransferase (gtf) enzymes (e.g., gtfJ), such as described in U.S. Pat. No. 7,000,000, and U.S. Patent Appl. Publ. Nos. 2013/0244288 and 2013/0244287 (all of which are incorporated herein by reference), for example.
The terms “poly alpha-1,3-1,6-glucan”, “alpha-1,3-1,6-glucan polymer”, and “poly (alpha-1,3)(alpha-1,6) glucan” are used interchangeably herein (note that the order of the linkage denotations “1,3” and “1,6” in these terms is of no moment). Poly alpha-1,3-1,6-glucan herein is a polymer comprising glucose monomeric units linked together by glycosidic linkages (i.e., glucosidic linkages), wherein at least 30% of the glycosidic linkages are alpha-1,3-glycosidic linkages, and at least 30% of the glycosidic linkages are alpha-1,6-glycosidic linkages. Poly alpha-1,3-1,6-glucan is a type of polysaccharide containing a mixed glycosidic linkage content. The meaning of the term poly alpha-1,3-1,6-glucan in certain embodiments herein excludes “alternan,” which is a glucan containing alpha-1,3 linkages and alpha-1,6 linkages that consecutively alternate with each other (U.S. Pat. No. 5,702,942, U.S. Pat. Appl. Publ. No. 2006/0127328). Alpha-1,3 and alpha-1,6 linkages that “consecutively alternate” with each other can be visually represented by . . . G-1,3-G-1,6-G-1,3-G-1,6-G-1,3-G-1,6-G-1,3-G- . . . , for example, where G represents glucose.
The percentage of glycosidic linkages between the glucose monomer units of poly alpha-1,3-glucan used to prepare poly alpha-1,3-glucan compounds herein that are alpha-1,3 is at least 50%, 60%, 70%, 80%, 90%, 95%, 96%, 97%, 98%, 99%, or 100% (or any integer value between 50% and 100%). In such embodiments, accordingly, poly alpha-1,3-glucan has less than 50%, 40%, 30%, 20%, 10%, 5%, 4%, 3%, 2%, 1%, or 0% (or any integer value between 0% and 50%) of glycosidic linkages that are not alpha-1,3.
A glucan wet cake is formed from a glucan colloidal dispersion by removing water by filtration. Water remains on the surface of glucan solid particles and trapped between particles. Whereas the glucan colloidal dispersion is a pourable liquid, the wet cake has a soft solid-like consistency.
The term “poly alpha-1,3-glucan slurry” herein refers to an aqueous mixture comprising the components of a glucosyltransferase enzymatic reaction such as poly alpha-1,3-glucan, sucrose, one or more glucosyltransferase enzymes, glucose and fructose.
The term “poly alpha-1,3-glucan wet cake” herein refers to poly alpha-1,3-glucan that has been separated from a slurry and washed with water or an aqueous solution. Poly alpha-1,3-glucan is not dried when preparing a wet cake.
The term “viscosity” as used herein refers to the measure of the extent to which a fluid or an aqueous composition such as a hydrocolloid resists a force tending to cause it to flow. Various units of viscosity that can be used herein include centipoise (cPs) and Pascal-second (Pa·s). A centipoise is one one-hundredth of a poise; one poise is equal to 0.100 kg·m−1·s−1. Thus, the terms “viscosity modifier” and “viscosity-modifying agent” as used herein refer to anything that can alter/modify the viscosity of a fluid or aqueous composition.
The term “shear thinning behavior” as used herein refers to a decrease in the viscosity of the colloidal dispersion as shear rate increases. The term “shear thickening behavior” as used herein refers to an increase in the viscosity of the colloidal dispersion as shear rate increases. “Shear rate” herein refers to the rate at which a progressive shearing deformation is applied to the colloidal dispersion. A shearing deformation can be applied rotationally.
The “molecular weight” of the poly alpha-1,3-glucan and poly alpha-1,3-glucan compounds herein can be represented as number-average molecular weight (Mn) or as weight-average molecular weight (Mw). Alternatively, molecular weight can be represented as Daltons, grams/mole, DPw (weight average degree of polymerization), or DPn (number average degree of polymerization). Various means are known in the art for calculating these molecular weight measurements, such as high-pressure liquid chromatography (HPLC), size exclusion chromatography (SEC), or gel permeation chromatography (GPC).
The terms “percent by volume”, “volume percent”, “vol %” and “v/v %” are used interchangeably herein. The percent by volume of a solute in a solution can be determined using the formula: [(volume of solute)/(volume of solution)]×100%.
The terms “percent by weight (% by wt.)”, “weight percentage (wt %)” and “weight-weight percentage (% w/w)” are used interchangeably herein. Percent by weight refers to the percentage of a material on a mass basis as it is comprised in a composition, mixture or solution.
Viscosity can be measured with the colloidal dispersion at any temperature between 3° C. to 110° C. (or any integer between 3 and 110° C.). Alternatively, viscosity can be measured at a temperature between 4° C. to 30° C., or 20° C. to 25° C. Viscosity can be measured at atmospheric pressure (about 760 torr) or any other higher or lower pressure.
The viscosity of a colloidal dispersion disclosed herein can be measured using a viscometer or rheometer, or using any other means known in the art. It would be understood by those skilled in the art that a rheometer can be used to measure the viscosity of those hydrocolloids and aqueous solutions of the disclosure that exhibit shear thinning behavior or shear thickening behavior (i.e., liquids with viscosities that vary with flow conditions). The viscosity of such embodiments can be measured at a rotational shear rate of 10 to 1000 rpm (revolutions per minute) (or any integer between 10 and 1000 rpm), for example. Alternatively, viscosity can be measured at a rotational shear rate of 10, 60, 150, 250, or 600 rpm.
The pH of a colloidal dispersion disclosed herein can be between 2.0 to 12.0. Alternatively, pH can be 2.0, 3.0, 4.0, 5.0, 6.0, 7.0, 8.0, 9.0, 10.0, 11.0, 12.0; or between 4.0 to 8.0; or between 3.0 and 11.0. In certain embodiments, the viscosity of the colloidal dispersion does not largely fluctuate at a pH between 3.0 and 11.0.
A poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan compound disclosed herein can be present in a colloidal dispersion at a weight percentage (wt %) of at least 0.01%, 0.05%, 0.1%, 0.2%, 0.3%, 0.4%, 0.5%, 0.6%, 0.7%, 0.8%, 0.9%, 1.0%, 1.2%, 1.4%, 1.6%. 1.8%, 2.0%, 2.5%. 3.0%, 3.5%, 4.0%. 4.5%, 5%, 6%, 7%, 8%, 9%, 10%, 11%, 12%, 13%, 14% or 15%.
A colloidal dispersion disclosed herein can be in the form of, and/or comprised in, a personal care product, pharmaceutical product, food product, household product, or industrial product. Poly alpha-1,3-glucan compounds herein can be used as thickening agents in each of these products. Such a thickening agent may be used in conjunction with one or more other types of thickening agents if desired, such as those disclosed in U.S. Pat. No. 8,541,041, the disclosure of which is incorporated herein by reference in its entirety.
Personal care products herein are not particularly limited and include, for example, skin care compositions, cosmetic compositions, antifungal compositions, and antibacterial compositions. Personal care products herein may be in the form of, for example, lotions, creams, pastes, balms, ointments, pomades, gels, liquids, combinations of these and the like. The personal care products disclosed herein can include at least one active ingredient. An active ingredient is generally recognized as an ingredient that causes the intended pharmacological effect.
In certain embodiments, the colloidal dispersion comprising the poly alpha-1,3-glucan and/or the poly alpha-1,3-1,6-glucan can be a skin care product that can be applied to skin for addressing skin damage related to a lack of moisture. A skin care product may also be used to address the visual appearance of skin (e.g., reduce the appearance of flaky, cracked, and/or red skin) and/or the tactile feel of the skin (e.g., reduce roughness and/or dryness of the skin while improved the softness and subtleness of the skin). In addition to the colloidal dispersion, the skin care product may further comprise one or more one active ingredient for the treatment or prevention of skin ailments, providing a cosmetic effect, or for providing a moisturizing benefit to skin, such as zinc oxide, petrolatum, white petrolatum, mineral oil, cod liver oil, lanolin, dimethicone, hard fat, vitamin A, allantoin, calamine, kaolin, glycerin, or colloidal oatmeal, and combinations of these. A skin care product may include one or more natural moisturizing factors such as ceramides, hyaluronic acid, glycerin, squalane, amino acids, cholesterol, fatty acids, triglycerides, phospholipids, glycosphingolipids, urea, linoleic acid, glycosaminoglycans, mucopolysaccharide, sodium lactate, or sodium pyrrolidone carboxylate, for example. Other ingredients that may be included in a skin care product include, without limitation, glycerides, apricot kernel oil, canola oil, squalane, squalene, coconut oil, corn oil, jojoba oil, jojoba wax, lecithin, olive oil, safflower oil, sesame oil, shea butter, soybean oil, sweet almond oil, sunflower oil, tea tree oil, shea butter, palm oil, cholesterol, cholesterol esters, wax esters, fatty acids, and orange oil. In some embodiments, the skin care product comprising the colloidal dispersion can further comprise one or more of an oil, a wax, a fragrance, UV absorber, a pigment, an amino acid, a fatty acid, a dye, an antioxidant, vitamins, retinol, alpha hydroxy acids, salicylic acid or any of the ingredients listed above.
The poly alpha-1,3-glucan and/or the poly alpha-1,3-1,6-glucan can be present in the personal care product in the range of from 0.05 to 15% by weight, based on the total weight of the personal care product composition. In other embodiments, the poly alpha-1,3-glucan and/or the poly alpha-1,3-1,6-glucan can be present in the range of from 0.1 to 10% by weight or from 0.1 to 5% by weight, all percentages by weight are based on the total amount of the personal care product.
In some embodiments, the personal care product comprises or consists essentially of the colloidal dispersion comprising the poly alpha-1,3-glucan and/or the poly alpha-1,3-1,6-glucan, one or more oils, one or more emulsifiers, water and one or more preservatives. In other embodiments, the personal care product comprises or consists essentially of the colloidal dispersion comprising the poly alpha-1,3-glucan and/or the poly alpha-1,3-1,6-glucan, one or more oils, one or more emulsifiers, water, one or more emollients and one or more preservatives. In still further embodiments, the personal care product comprises or consists essentially of the colloidal dispersion comprising the poly alpha-1,3-glucan and/or the poly alpha-1,3-1,6-glucan, one or more oils, one or more emulsifiers, water, one or more emollients, one or more fragrances and one or more preservatives.
A personal care product herein can also be in the form of makeup or other product including, but not limited to, a lipstick, mascara, rouge, foundation, blush, eyeliner, lip liner, lip gloss, other cosmetics, sunscreen, sun block, nail polish, mousse, hair spray, styling gel, nail conditioner, bath gel, shower gel, body wash, face wash, shampoo, hair conditioner (leave-in or rinse-out), cream rinse, hair dye, hair coloring product, hair shine product, hair serum, hair anti-frizz product, hair split-end repair product, lip balm, skin conditioner, cold cream, moisturizer, body spray, soap, body scrub, exfoliant, astringent, scruffing lotion, depilatory, permanent waving solution, antidandruff formulation, antiperspirant composition, deodorant, shaving product, pre-shaving product, after-shaving product, cleanser, skin gel, rinse, toothpaste, or mouthwash, for example. In some embodiments, the personal care product comprising the colloidal dispersion can further comprise one or more of an oil, a wax, a fragrance, a UV absorber, UV absorber, a pigment, an amino acid, a fatty acid, a dye, an antioxidant, vitamins, retinol, alpha hydroxy acids, salicylic acid or any of the ingredients listed above.
A pharmaceutical product herein can be in the form of an emulsion, liquid, elixir, gel, suspension, solution, cream, or ointment, for example. Also, a pharmaceutical product herein can be in the form of any of the personal care products disclosed herein. A pharmaceutical product can further comprise one or more pharmaceutically acceptable carriers, diluents, and/or pharmaceutically acceptable salts. A poly alpha-1,3-glucan compound disclosed herein can also be used in capsules, encapsulants, tablet coatings, and as an excipients for medicaments and drugs. In some embodiments, the pharmaceutical product comprising the colloidal dispersion can further comprise one or more of active ingredients, sweeteners, coloring agents, lactose, lecithin, flavoring agents, magnesium oxide, malic acid, benzoic acid, benzyl alcohol, parabens, carbonates, waxes, oils, cellulose, corn starch or a combination thereof. The inactive ingredients that can be part of a pharmaceutical product are carefully controlled by the United States Food and Drug Administration (FDA). Any of those ingredients that are known and recognized by the FDA can be used as a part of the pharmaceutical product.
Non-limiting examples of food products herein include vegetable, meat, and soy patties; reformed seafood; reformed cheese sticks; cream soups; gravies and sauces; salad dressing; mayonnaise; onion rings; jams, jellies, and syrups; pie filling; potato products such as French fries and extruded fries; batters for fried foods, pancakes/waffles and cakes; pet foods; beverages; frozen desserts; ice cream; cultured dairy products such as cottage cheese, yogurt, cheeses, and sour creams; cake icing and glazes; whipped topping; leavened and unleavened baked goods; and the like.
The the colloidal dispersion comprising the poly alpha-1,3-glucan and/or the poly alpha-1,3-1,6-glucan can be used as a filler in the food product or, in other embodiments, can be used as a replacement for at least a portion of an oil or fat in a food product, thus producing a low fat version of the food product.
A non-limiting example of a household product or industrial product is a liquid detergent. The glucan colloidal dispersion can be used as a structuring agent or thickener to stabilize the components in liquid detergent formulation. In some embodiments, the household product comprising the colloidal dispersion can further comprise one or more of alcohols, surfactants, polymers, pigments, dyes, fragrances, enzymes, builders, chelating agents, pH regulators, amines, oils, waxes or combinations thereof. A number of ingredients are known for household products can be used along with the colloidal dispersions. Any of those known ingredients can be used.
The present disclosure is directed toward a colloidal dispersion comprising: (a) poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan; and (b) a solvent. In some embodiments, the colloidal dispersion consists essentially of (a) poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan; and (b) a solvent. In other embodiments, the colloidal dispersion comprises less than 1% by weight of sucrose and/or fructose, wherein the percentage by weight is based on the total amount of the colloidal dispersion. The poly alpha-1,3-1,6-glucan has alpha-1,3 and alpha-1,6-glycosidic linkages comprising: (a) at least 30%, 40% or 50% of the glycosidic linkages are alpha-1,3 linkages; and (b) at least 30%, 40% or 50% of the glycosidic linkages are alpha-1,6 linkages.
The poly alpha-1,3-glucan and the poly alpha-1,3-1,6-glucan comprise particles with an average particle diameter size of between 5 nm, 10 nm or 20 nm and 100 nm, 150 nm or 200 nm. Preferably the particles have an average particle diameter size of between 5 nm and 200 nm and more preferably between 10 nm and 100 nm. The particles can have a spherical or cylindrical shape. Typically, the particles are substantially spherical in shape. By substantially is meant that greater than 50% of the particles are spherical in shape. The particles can form aggregates with an average aggregate diameter size of between 10 nm, 100 nm, 1 μm or 10 μm and 100 μm, 150 μm or 300 μm. Preferably the aggregates have an average aggregate diameter size of between 10 nm and 250 μm and more preferably between 10 μm and 225 μm. In all cases, the average size refers to the D50 particle size, or the particle size in which 50% of the particles are larger and 50% of the particles are smaller than the D50 value.
The solvent for the colloidal dispersion can be water. In other embodiments, the solvent can be a combination of water and less than 50% by weight of one or more water-miscible organic solvents, for example, methanol, ethanol, isopropanol, propanol, acetone, ethylene glycol, acetic acid, tetrahydrofuran, dimethyl sulfoxide, dimethyl formamide or a combination thereof, wherein the percentage by weight is based on the total amount of the solvent.
The poly alpha-1,3-glucan characterized by having alpha-1,3-glycosidic linkages or the poly alpha-1,3-1,6-glucan characterized by having alpha-1,3 and alpha-1,6-glycosidic linkages of the colloidal dispersion constitutes between 0.1, 1 or 5% by wt. and 10, 15, 20, 40 or 60% by wt. of the total colloidal dispersion. Preferably the poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan of the colloidal dispersion constitutes between 0.1% by wt. and 15% by wt. and more preferably between 0.1% by wt. and 10% by wt.
The colloidal dispersion has a viscosity of at least 10, 100, 1,000, 10,000, 100,000 or 1,000,000 cPs.
The colloidal dispersion has a pH between 1 or 2 and 11, 12, 13 or 14. The pH is preferably between 1 and 14 and more preferably between 2 and 11.
The colloidal dispersion has a viscosity and a pH wherein the viscosity changes less than 10, 20, 30, 40 or 50% while the pH is changed over a range between 1 or 2 and 11, 12, 13 or 14. Preferably the viscosity changes less than 50% while the pH changes over a range between 1 and 14 and more preferably the viscosity changes less than 10% while the pH changes over a range between 2 and 11.
The colloidal dispersion can further comprise a salt or surfactant wherein the colloidal dispersion has a viscosity that changes less than 10% after the addition of the salt or surfactant.
The colloidal dispersion has shear thinning behavior or shear thickening behavior.
The colloidal dispersion can be used in the form of a personal care product, pharmaceutical product, food product, household product, or industrial product.
The present disclosure is further directed toward a personal care product comprising a colloidal dispersion comprising: (a) poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan; and (b) a solvent.
The present disclosure is still further directed toward a food product comprising a colloidal dispersion comprising: (a) poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan; and (b) a solvent.
The present disclosure is still further directed toward a process for making a poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan colloidal dispersion comprising: (a) heating an enzyme reaction solution comprising an aqueous basic buffered solution of an enzyme, sucrose and, optionally, antimicrobial agent to make a slurry containing poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan; (b) filtering the slurry to isolate the poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan in the form of a wet cake; (c) washing the wet cake with water; and (d) dispersing the wet cake in water to form the poly alpha-1,3-glucan or the poly alpha-1,3-1,6-glucan colloidal dispersion. The process can have at least one of the following: (a) heating the enzyme reaction solution at 20-25° C. for 24 hours; (b) the enzyme for making poly alpha-1,3-glucan is Streptococcus salivarius gtfJ; (c) the enzyme for making poly alpha-1,3-1,6-glucan is Streptococcus oralis gtf 4297, Streptococcus sp. C150 gtf 3298 or Streptococcus mutans gtf 0544; (d) the aqueous basic buffered solution has a pH buffering agent of an alkali metal phosphate buffer; (e) the alkali metal phosphate buffer wherein the alkali metal is potassium; (f) the aqueous basic buffered solution has a pH between 7 and 5; (g) the antimicrobial agent is FERMASURE® sodium chlorite; and (h) the wet cake contains between 60 to 80 wt % water.
The present disclosure is still further directed toward a poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan colloidal dispersion prepared according to a process comprising: (a) heating an enzyme reaction solution comprising an aqueous basic buffered solution of an enzyme, sucrose and, optionally, antimicrobial agent to make a slurry containing poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan; (b) filtering the slurry to isolate the poly alpha-1,3-glucan or poly alpha-1,3-1,6-glucan in the form of a wet cake; (c) washing the wet cake with water; and (d) dispersing the wet cake in water to form a poly alpha-1,3-glucan colloidal dispersion.
Particle Size was measured by Primary particle size was analyzed using a slurry of poly alpha-1,3-glucan with Atomic Force Microscopy (AFM). 10 uL of a slurry of poly alpha-1,3-glucan was placed on a freshly cleaved mica surface, spun at 6000 r/s for 10 seconds, dried at room temperature and imaged by AFM tapping mode. AFM images were obtained using a Dimensional Icon scanning probe Dimensional Icon scanning probe microscope (Bruker, Santa Barbara, Calif.). The microscope was operated in the Tapping Mode, in which the cantilever is oscillated at resonance and the feedback control adjusts for constant tapping amplitude. Typically, tapping mode was used to provide both topographic and phase images. The topography image is a quantitative three-dimensional image of the surface, and the color or brightness of any pixel in the image represents height. Scanning was carried out in air using commercially available 125-/m-long silicon OTESP tips, with 37-55 N/m spring constant, and over 300 kH frequencies with a moderate tapping ratio from 0.85 to 0.65.
Particle Aggregate Size was measured with a Beckman Coulter LS13320 which uses laser diffraction to determine the volume distribution of a field of particles in the range of 0.4 to 2000 um. A standard Fraunhofer regression model was used for the particle size distribution measurements. Three repeat runs are made as a check on sample stability and on instrument reproducibility.
Viscosity was measured by a Brookfield DV3T Rheometer equipped with a recirculating bath to control temperature (20° C.) and a YULA15-E(Z) spindle. The shear rate was increased using a gradient program which increased from 0.01-250 rpm and then shear rate was increased by 7.05 (1/s) every 20 seconds.
pH was measured by VWR symphony H10P.
Determination of Glycosidic Linkages was determined by NMR (nuclear magnetic resonance). Twenty glycosidic linkages in glucan products synthesized by a gtf enzyme were determined by 13C NMR or 1H NMR.
For 13C NMR, dry glucan polymer (25-30 mg) was dissolved in 1 mL of deuterated DMSO containing 3% by weight of LiCl with stirring at 50° C. Using a glass pipette, 0.8 mL of the solution was transferred into a 5-mm NMR tube. A 25 quantitative 13C NMR spectrum was acquired using a Bruker Avance 500-MHz NMR spectrometer (Billerica, Mass.) equipped with a CPDUL cryoprobe at a spectral frequency of 125.76 MHz, using a spectral window of 26041.7 Hz. An inverse-gated decoupling pulse sequence using waltz decoupling was used with an acquisition time of 0.629 second, an inter-pulse delay of 5 seconds, and 6000 30 pulses. The time domain data was transformed using an exponential multiplication of 2.0 Hz.
For 1H NMR, approximately 20 mg of a glucan polymer sample was weighed into a vial on an analytical balance. The vial was removed from the balance and 0.8 mL of deuterated DMSO (DMSO-d6), containing 3% by weight of LiCl, was added to the vial. The mixture was stirred with a magnetic stir bar 5 and warmed to 90° C. until the glucan sample dissolved. The solution was allowed to cool to room temperature. While stirring at room temperature, 0.2 mL of a 20% by volume solution of trifluoroacetic acid (TFA) in DMSO-d6 was added to the polymer solution. The TFA was added in order to move all hydroxyl proton signals out of the region of the spectrum where carbohydrate ring proton signals 10 occur. A portion, 0.8 mL, of the final solution was transferred, using a glass pipette, into a 5-mm NMR tube. A quantitative 1H NMR spectrum was acquired using an NMR spectrometer with a proton frequency of 500 MHz or greater. The spectrum was acquired using a spectral window of 11.0 ppm and a transmitter offset of 5.5 ppm. A 90° pulse was applied for 32 pulses with an inter-pulse 15 delay of 10 seconds and an acquisition time of 1.5 seconds. The time domain data were transformed using an exponential multiplication of 0.15 Hz.
The disclosure is further defined in the following Examples. It should be understood that these Examples, while indicating certain preferred aspects of the disclosure, are given by way of illustration only. From the above discussion and these Examples, one skilled in the art can ascertain the essential characteristics of this disclosure, and without departing from the spirit and scope thereof, can make various changes and modifications of the disclosure to adapt it to various uses and conditions.
U.S. Pat. No. 7,000,000 disclosed a polysaccharide fiber comprising hexose units wherein at least 50% of the hexose units within the polymer were linked via alpha-1,3-glycosidic linkages using a Streptococcus salivarius gtfJ enzyme. This enzyme utilizes sucrose as a substrate in a polymerization reaction producing poly alpha-1,3-glucan and fructose as end-products.
A slurry of poly alpha-1,3-glucan was prepared from an aqueous solution (0.5 L) containing Streptococcus salivarius gtfJ enzyme (100 unit/L) described in U.S. Patent Appl. Publ. No. 2013/0244288, which is incorporated herein by reference in its entirety, sucrose (100 g/L) obtained from OmniPur Sucrose (EM8550), potassium phosphate buffer (10 mM) obtained from Sigma Aldrich, and FermaSure®, an antimicrobial agent, (100 ppm) obtained from DuPont adjusted to pH 5.5. The resulting enzyme reaction solution was maintained at 20-25° C. for 24 hours. A slurry was formed since the poly alpha-1,3-glucan synthesized in the reaction was aqueous insoluble. The poly alpha-1,3-glucan solids produced in the reaction were collected using a Buchner funnel fitted with a 325-mesh screen over 40 micrometer filter paper, forming the wet cake which contains about 60-80 wt % of water. The poly alpha-1,3-glucan wet cake is then dispersed in water using conventional agitators without high shear, high temperature, long mixing time or separate mixing steps. For example, dispersing in water using an Ika Ultra-Turrax® T25 digital disperser, typically at 8000 rpm for 5 min at ambient temperature.
Poly alpha-1,3-1,6-glucan was made from a slurry of poly alpha-1,3-1,6-glucan. A slurry of poly alpha-1,3-1,6-glucan was prepared from an aqueous solution (0.5 L) containing an enzyme of Streptococcus oralis gtf 4297, Streptococcus sp. C150 gtf 3298 or Streptococcus mutans gtf 0544 for Examples 2a-c, respectively, (100 unit/L) described in U.S. Patent Appl. Publ. No. 2014/0087431, which is incorporated herein by reference in its entirety, sucrose (100 g/L) obtained from OmniPur Sucrose (EM8550), potassium phosphate buffer (50 mM) obtained from Sigma Aldrich, and FermaSure® (100 ppm) obtained from DuPont adjusted to pH 6.5. The resulting enzyme reaction solution was maintained at 22-25° C. for 24-30 hours. A slurry was formed since the poly alpha-1,3-1,6-glucan synthesized in the reaction was aqueous insoluble. The poly alpha-1,3-1,6-glucan solids produced in the reaction were collected using a Buchner funnel fitted with a 325-mesh screen over 40 micrometer filter paper, forming the wet cake which contains about 60-80 wt % of water. The poly alpha-1,3; 1,6-glucan wet cake is then dispersed in water using an Ika Ultra-Turrax® T25 digital disperser, typically at 8000 rpm for 5 min. Different enzymes yielded different ratios of 1,3 to 1,6 glycosidic linkages. Enzyme Streptococcus oralis gtf 4297 produced 31% alpha-1,3 linkages and 67% alpha-1,6 linkages, Streptococcus sp. C150 gtf 3298 produced 50% alpha-1,3 linkages and 50% alpha-1,6 linkages and Streptococcus mutans gtf 0544 produced 62% alpha-1,3 linkages and 36% alpha-1,6 linkages.
Primary particle size was analyzed using a slurry of poly alpha-1,3-glucan described in Example 1 with Atomic Force Microscopy (AFM). 10 uL of a slurry of poly alpha-1,3-glucan was placed on a freshly cleaved mica surface, spun at 6000 r/s for 10 seconds, dried at room temperature and imaged by AFM tapping mode. AFM images were obtained using a Dimensional Icon scanning probe Dimensional Icon scanning probe microscope (Bruker, Santa Barbara, Calif.). The microscope was operated in the Tapping Mode, in which the cantilever is oscillated at resonance and the feedback control adjusts for constant tapping amplitude. Typically, tapping mode was used to provide both topographic and phase images. The topography image is a quantitative three-dimensional image of the surface, and the color or brightness of any pixel in the image represents height. Scanning was carried out in air using commercially available 125-/m-long silicon OTESP tips, with 37-55 N/m spring constant, and over 300 kH frequencies with a moderate tapping ratio from 0.85 to 0.65. The AFM images indicate that the average diameter of primary particles are 20-30 nm.
Particle size distribution was measured using the samples described in Example 1 and Example 2 with a Beckman Coulter LS13320 which uses laser diffraction to determine the volume distribution of a field of particles in the range of 0.4 to 2000 um. A standard Fraunhofer regression model was used for the particle size distribution measurements. Three repeat runs are made as a check on sample stability and on instrument reproducibility. In Table 1, D10, D50 and D90 indicate the diameter of particle or cluster at 10%, 50% and 90% in the cumulative distribution, respectively. D50 indicates the median diameter or the medium value of the particle size distribution.
While most particles have a generally spherical shape, some particles have a cylindrical or rod-like shape. For purposes of measuring size of cylindrical shapes, the diameter is calculated as an effective diameter after the mass of the cylindrical shaped particle is adjusted as if it had a spherical shape.
To prepare 5 wt % poly alpha-1,3-glucan dispersion, 8.6 g of poly alpha-1,3-glucan wet cake (L6B1C6, 29 wt %) was dispersed in 50 mL of deionized water as described in Example 1. To determine the viscosity of poly alpha-1,3-glucan dispersed in water at various shear rates, the hydrocolloid samples were subjected to various shear rates using a Brookfield DV3T Rheometer equipped with a recirculating bath to control temperature (20° C.) and a YULA15-E(Z) spindle. The shear rate was increased using a gradient program which increased from 0.01-250 rpm and then shear rate was increased by 7.05 (1/s) every 20 seconds. The results summarized in Table 2 indicate that the viscosity of poly alpha-1,3-glucan dispersed in water is reduced as the shear rate is increased. This observation means that the hydrocolloids demonstrate significant shear thinning behavior.
Six aliquots of aqueous dispersion of 5 wt % poly alpha-1,3-glucan was prepared as described in Example 1. The pH of aqueous dispersion was 5.5. Two aliquots were adjusted to pH 2.0 and pH 4.0 using 1 N of nitric acid. Three aliquots were adjusted to pH 7.0, pH 9.0 and pH 11.0 using 1 N sodium hydroxide. One aliquot was used without adjusting pH. Viscosity measurements were made as described above. The results summarized in Table 3 indicate that pH has no significant impact on the viscosity of glucan dispersed in water.
To prepare 5 wt % poly alpha-1,3-glucan dispersion with 15 wt % aluminum chloride. 8.6 g of poly alpha-1,3-glucan wet cake (L6B1C6, 29 wt %) and 7.5 g of aluminum chloride were dispersed in 50 mL of deionized water as described in Example 1 using the homogenization method. 5 wt % poly alpha-1,3-glucan dispersion was prepared as described in Example 6. Viscosity measurements were made, as described in Example 6. The results summarized in Table 4 indicate that the presence of aluminum chloride did not have a significant impact on the viscosity of glucan in water.
To prepare 5 wt % poly alpha-1,3-glucan dispersion with 2 wt % surfactant, 8.6 g of poly alpha-1,3-glucan wet cake (L6B1C6, 29 wt %) and 1 g of surfactant were dispersed in 50 mL of deionized water, as described in Example 1. Four samples were prepared with four different surfactants, including CTAB (centrimonium bromide), sorbitan monoolate, Tween20 (or polysorbate 20) and Zelec AN (amine neutralized phosphate ester). 5 wt % poly alpha-1,3-glucan dispersion was prepared as described in Example 6. Viscosity measurements were made, as described in Example 6. The results summarized in Table 5 indicate that the presence of surfactant did not have a significant impact on the viscosity of glucan in water.
To prepare the prototype skin care formulation, (A) and (B) in Table 6 were placed in two separate vessels and were mixed using a propeller stirrer at 75° C. After 5 min, (A) was added to (B) and they were mixed using a propeller stirrer at 75° C. for 1 min. Then (C) was added to the mixture of (A) and (B) at 45° C. During the mixing, the propeller stirrer was set to 500 rpm.
To prepare the prototype acne treatment formulation, (D) and (E) in Table 7 were placed in two separate vessels and were mixed using a propeller stirrer at 75° C. After 5 min, (D) was added to (E) and they were mixed using a propeller stirrer at 75° C. for 1 min. Then (F) was added to the mixture of (D) and (E) at 45° C. During the mixing, the propeller stirrer was set to 500 rpm.
To prepare the prototype roll-on antiperspirant formulation, (G) and (H) in Table 8 were placed in two separate vessels and were mixed using a propeller stirrer at 75° C. After 5 min, (G) was added to (H) and they were mixed using a propeller stirrer at 75° C. for 1 min. Then (C) was added to the mixture of (G) and (H) at 45° C. During the mixing, the propeller stirrer was set to 500 rpm.
To prepare the prototype hair care formulation, (J) and (K) in Table 9 were placed in two separate vessels and were mixed using a propeller stirrer at 75° C. After 5 min, (J) was added to (K) and they were mixed using a propeller stirrer at 75° C. for 1 min. Then (L) was added to the mixture of (J) and (K) at 45° C. During the mixing, the propeller stirrer was set to 500 rpm.
Various hand lotions were prepared for sensory evaluations. The hand lotions were prepared according to the general procedure given below, using the ingredients of TABLE 10.
At room temperature, the ingredients of Phase A were agitated until the mixture was homogeneous. The ingredients of Phase B were combined in a separate vessel and were mixed by hand until homogeneous. The homogeneous compositions of Phase B was slowly added to the homogenous mixture of Phase A with stirring. When the addition was complete, the mixture was homogenized by mixing at 5000-9000 revolutions per minute (rpm) for 5-10 minutes. The ingredient of Phase C was then added with stirring to form the desired hand lotions. For Comparative Example B, the pH of the lotion was adjusted to 5.5 by adding a 20 wt % aqueous solution of sodium hydroxide. DI water means deionized water. % Activity means the percentage of ingredient in the composition as added in each example. The Wt % is the weight percentage of the ingredient in the final formulation.
Skinfeel Results: A double-blind, skinfeel analysis was performed according to ASTM E1490-3. The primary attributes evaluated in this study were; rub-out sliminess, afterfeel stickiness, pick-up stringiness and pick-up stickiness. Panelists assessed attributes on a scale from 1-5, where 1 exhibits the least of the attribute and 5 exhibits the most of the attribute. The results are reported in table 11 below as an average value of the panelists' ratings for each attribute. The sum average of these values indicates that the overall sensory experience for the lotions produced with the Poly alpha-1,3-glucans exceed the results of similar lotions produced with either Xanthan Gum or Carbopol Ultrez 10.
The low fat mayonnaise was prepared with poly alpha-1,3-glucan by mixing all ingredients in Table 12 using a Silverson homogenizer at 6500 rpm for 5 min. The resulting formulation restored texture of low fat mayonnaise to similar level to full fat product.
This application is a continuation of Application No. 15/548,916 (filed Aug. 4, 2017, now U.S. Pat. No. 11,351,104), which is the National Stage application of International Application No. PCT/US2016/16136 (filed Feb. 2,2016), which claims the benefit of U.S. Provisional Application No. 62/112,960 (filed Feb. 6, 2015), all of which prior applications are incorporated herein by reference in their entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4306059 | Yokobayashi | Dec 1981 | A |
| 4501886 | O'Brien | Feb 1985 | A |
| 4946700 | Taguchi | Aug 1990 | A |
| 4963298 | Allen | Oct 1990 | A |
| 5248712 | Takeuchi | Sep 1993 | A |
| 5296286 | Allen | Mar 1994 | A |
| 5702942 | Leathers | Dec 1997 | A |
| 5712107 | Nichols | Jan 1998 | A |
| 5985666 | Loiselle | Nov 1999 | A |
| 6087559 | Nichols | Jul 2000 | A |
| 6127602 | Nichols | Oct 2000 | A |
| 6127603 | Nichols | Oct 2000 | A |
| 6284479 | Nichols | Sep 2001 | B1 |
| 6410025 | Lander | Jun 2002 | B1 |
| 6465203 | Nichols | Oct 2002 | B2 |
| 6967027 | Heux | Nov 2005 | B1 |
| 7000000 | O'Brien | Feb 2006 | B1 |
| 8076279 | Brand | Dec 2011 | B2 |
| 8197641 | Esser | Jun 2012 | B2 |
| 8551378 | Velev | Oct 2013 | B2 |
| 8642757 | O'Brien | Feb 2014 | B2 |
| 8828689 | Caimi | Sep 2014 | B2 |
| 8835374 | Guida | Sep 2014 | B2 |
| 8871474 | Payne | Oct 2014 | B2 |
| 8962282 | Caimi | Feb 2015 | B2 |
| 9034092 | O'Brien | May 2015 | B2 |
| 9080195 | O'Brien | Jul 2015 | B2 |
| 9096956 | Shiflett | Aug 2015 | B2 |
| 9139718 | Paullin | Sep 2015 | B2 |
| 9175423 | O'Brien | Nov 2015 | B2 |
| 9212301 | O'Brien | Dec 2015 | B2 |
| 9278988 | Kasat | Mar 2016 | B2 |
| 9334584 | O'Brien | May 2016 | B2 |
| 9365955 | Opper | Jun 2016 | B2 |
| 9403917 | Kasat | Aug 2016 | B2 |
| 9540747 | O'Brien | Jan 2017 | B2 |
| 9562112 | Landschütze | Feb 2017 | B2 |
| 9644322 | Massouda | May 2017 | B2 |
| 9670290 | Landschütze | Jun 2017 | B2 |
| 9695253 | Nambiar | Jul 2017 | B2 |
| 9701800 | Dümberger | Jul 2017 | B2 |
| 9708417 | Cormier | Jul 2017 | B2 |
| 9714403 | Nagy | Jul 2017 | B2 |
| 9771548 | Nagy | Sep 2017 | B2 |
| 9957334 | Dennes | May 2018 | B2 |
| 9982284 | Nagy | May 2018 | B2 |
| 10005850 | Kasat | Jun 2018 | B2 |
| 10030323 | Dürnberger | Jul 2018 | B2 |
| 10072100 | Nambiar | Sep 2018 | B2 |
| 10087479 | Fake | Oct 2018 | B2 |
| 10117937 | Yao | Nov 2018 | B2 |
| 20040091581 | Joly | May 2004 | A1 |
| 20050059633 | Van Geel-Schuten | Mar 2005 | A1 |
| 20060127328 | Monsan | Jun 2006 | A1 |
| 20080095731 | Mitra | Apr 2008 | A1 |
| 20100122378 | Frohberg | May 2010 | A1 |
| 20110014345 | Pilling | Jan 2011 | A1 |
| 20110189346 | Pilling | Aug 2011 | A1 |
| 20110319310 | Labeque | Dec 2011 | A1 |
| 20130087938 | O'Brien | Apr 2013 | A1 |
| 20130157316 | Caimi | Jun 2013 | A1 |
| 20130161562 | O'Brien | Jun 2013 | A1 |
| 20130161861 | O'Brien | Jun 2013 | A1 |
| 20130168895 | Opper | Jul 2013 | A1 |
| 20130196384 | Caimi | Aug 2013 | A1 |
| 20130214443 | Shiflett | Aug 2013 | A1 |
| 20130244287 | O'Brien | Sep 2013 | A1 |
| 20130244288 | O'Brien | Sep 2013 | A1 |
| 20130313737 | O'Brien | Nov 2013 | A1 |
| 20140087431 | Payne | Mar 2014 | A1 |
| 20140113821 | Gu | Apr 2014 | A1 |
| 20140179913 | Paullin | Jun 2014 | A1 |
| 20140187766 | Kasat | Jul 2014 | A1 |
| 20140187767 | Kasat | Jul 2014 | A1 |
| 20140323715 | Kasat | Oct 2014 | A1 |
| 20150080220 | Yao | Mar 2015 | A1 |
| 20150126730 | O'Brien | May 2015 | A1 |
| 20150191550 | Mishra | Jul 2015 | A1 |
| 20150225877 | O'Brien | Aug 2015 | A1 |
| 20150232785 | Paullin | Aug 2015 | A1 |
| 20150240278 | Nagy | Aug 2015 | A1 |
| 20150299339 | Shibakami | Oct 2015 | A1 |
| 20150353649 | Paullin | Dec 2015 | A1 |
| 20160053061 | Dürnberger | Feb 2016 | A1 |
| 20160053406 | Dürnberger | Feb 2016 | A1 |
| 20160060792 | Dürnberger | Mar 2016 | A1 |
| 20160122445 | Nambiar | May 2016 | A1 |
| 20160138195 | Kraft | May 2016 | A1 |
| 20160138196 | Röder | May 2016 | A1 |
| 20160144065 | Röder | May 2016 | A1 |
| 20160175811 | Behabtu | Jun 2016 | A1 |
| 20160177471 | Kraft | Jun 2016 | A1 |
| 20160230348 | Massouda | Aug 2016 | A1 |
| 20160251453 | Kasat | Sep 2016 | A1 |
| 20160304629 | Kasat | Oct 2016 | A1 |
| 20160311935 | Dennes | Oct 2016 | A1 |
| 20160326268 | Cormier | Nov 2016 | A1 |
| 20160326269 | Dennes | Nov 2016 | A1 |
| 20160333117 | Massouda | Nov 2016 | A1 |
| 20160333157 | Massouda | Nov 2016 | A1 |
| 20170167063 | Behabtu | Jun 2017 | A1 |
| 20170196231 | Massouda | Jul 2017 | A1 |
| 20170198108 | Mishra | Jul 2017 | A1 |
| 20170198109 | Mishra | Jul 2017 | A1 |
| 20170198322 | Cheng | Jul 2017 | A1 |
| 20170198323 | Cheng | Jul 2017 | A1 |
| 20170198324 | Cheng | Jul 2017 | A1 |
| 20170204203 | Massouda | Jul 2017 | A1 |
| 20170204232 | Mishra | Jul 2017 | A1 |
| 20170204442 | Dicosimo | Jul 2017 | A1 |
| 20170208823 | Massouda | Jul 2017 | A1 |
| 20170218093 | Cheng | Aug 2017 | A1 |
| 20170267787 | Nambiar | Sep 2017 | A1 |
| 20170298303 | Nagy | Oct 2017 | A1 |
| 20170362345 | Behabtu | Dec 2017 | A1 |
| 20180049457 | Cheng | Feb 2018 | A1 |
| 20180066214 | Nagy | Mar 2018 | A1 |
| 20180273731 | Opietnik | Sep 2018 | A1 |
| 20190186049 | Dürnberger | Jun 2019 | A1 |
| 20190218373 | Opietnik | Jul 2019 | A1 |
| 20210130504 | Kim | May 2021 | A1 |
| Number | Date | Country |
|---|---|---|
| WO-2005053765 | Jun 2005 | WO |
| WO-2006036092 | Apr 2006 | WO |
| WO-2013036918 | Mar 2013 | WO |
| WO-2013036968 | Mar 2013 | WO |
| WO-2013052730 | Apr 2013 | WO |
| WO-2013096502 | Jun 2013 | WO |
| WO-2013096511 | Jun 2013 | WO |
| WO-2013101854 | Jul 2013 | WO |
| WO-2013177348 | Nov 2013 | WO |
| WO-2014052386 | Apr 2014 | WO |
| WO-2014077340 | May 2014 | WO |
| WO-2014099724 | Jun 2014 | WO |
| WO-2014105696 | Jul 2014 | WO |
| WO-2014105698 | Jul 2014 | WO |
| WO-2014161018 | Oct 2014 | WO |
| WO-2014161019 | Oct 2014 | WO |
| WO-2014165881 | Oct 2014 | WO |
| WO-2014201479 | Dec 2014 | WO |
| WO-2014201480 | Dec 2014 | WO |
| WO-2014201481 | Dec 2014 | WO |
| WO-2014201482 | Dec 2014 | WO |
| WO-2014201483 | Dec 2014 | WO |
| WO-2014201484 | Dec 2014 | WO |
| WO-2015069828 | May 2015 | WO |
| WO-2015094402 | Jun 2015 | WO |
| WO-2015095046 | Jun 2015 | WO |
| WO-2015095358 | Jun 2015 | WO |
| WO-2015103531 | Jul 2015 | WO |
| WO-2015109064 | Jul 2015 | WO |
| WO-2015109066 | Jul 2015 | WO |
| WO-2015109164 | Jul 2015 | WO |
| WO-2015123323 | Aug 2015 | WO |
| WO-2015123327 | Aug 2015 | WO |
| WO-2015130881 | Sep 2015 | WO |
| WO-2015138283 | Sep 2015 | WO |
| WO-2015183721 | Dec 2015 | WO |
| WO-2015183724 | Dec 2015 | WO |
| WO-2015195777 | Dec 2015 | WO |
| WO-2015195960 | Dec 2015 | WO |
| WO-2015200589 | Dec 2015 | WO |
| WO-2015200590 | Dec 2015 | WO |
| WO-2015200593 | Dec 2015 | WO |
| WO-2015200596 | Dec 2015 | WO |
| WO-2015200605 | Dec 2015 | WO |
| WO-2015200612 | Dec 2015 | WO |
| WO 2015183714 | Dec 2015 | WO |
| WO 2015183722 | Dec 2015 | WO |
| WO 2015183726 | Dec 2015 | WO |
| WO 2015183729 | Dec 2015 | WO |
| WO-2016073732 | May 2016 | WO |
| WO-2016105971 | Jun 2016 | WO |
| WO-2016106011 | Jun 2016 | WO |
| WO-2016106068 | Jun 2016 | WO |
| Entry |
|---|
| Ogawa et al, “X-ray Diffraction Data for (1->3)-alpha-d-glucan Triacetate”, Carbohydrate Polymers, vol. 3, No. 4, Jan. 1, 1983, pp. 287-297. |
| “Applied Fibre Science”, F. Happey, Ed, Chapter 8, Academic Press, New York, 1979 (Book not included). |
| International Preliminary Report on Patentability, PCT/US16/16136, Agnes Wittmann Regis, Authorized Officer, IB, dated Aug. 17, 2017. |
| Ogawa et al: “Crystal Structure of (1->3)-alpha-d-glucan”, Water-soluble Polymers: Synthesis, Solution Properties and Applications, American Chemical Society, vol. 141, Jan. 1, 1980, pp. 353-362. |
| PCT International Search Report and Written Opinion for International Application No. PCT/US2015/011546, dated May 28, 2015. |
| Ogawa et al., ‘X-ray Diffraction Data for (1>3)-alpha-d-glucan,’ Carbohydrate Research, Oct. 1, 1979, vol. 75, pp. CI3-CI6. |
| Ogawa et al: “Molecular and Crystal Structure of the Regenerated Form of (1->3)-alpha-d-glucan”, International Journal of Biological Macromolecules, vol. 3, No. 1, Feb. 1, 1981, pp. 31-36. |
| PCT International Search Report and Written Opinion for International Application No. PCT/US2015/037622, dated Sep. 22, 2015. |
| PCT International Search Report and Written Opinion for International Application No. PCT/US2015/066317, dated Mar. 30, 2016. |
| PCT International Search Report and Written Opinion for International Application No. PCT/US2015/011551, dated Jul. 9, 2015. |
| PCT International Search Report and Written Opinion for International Application No. PCT/US2015/037646, dated Oct. 7, 2015. |
| PCT International Search Report and Written Opinion for International Application No. PCT/US2015/037656, dated Oct. 7, 2015. |
| Simpson et al., “Four glucosyltransferases, Gtfj, GTFK, GtfL and GtfM, from Streptococcus salivarius ATCC 25975”, Microbiology, vol. 141, 1995, pp. 1451-1460. |
| PCT International Search Report and Written Opinion for International Application No. PCT/US2016/016136, dated Apr. 4, 2016. |
| PCT International Search Report and Written Opinion for International Application No. PCT/US2015/010139, dated Apr. 29, 2015. |
| PCT International Search Report and Written Opinion for International Application No. PCT/US2015/011724, dated May 15, 2015. |
| Simpson et al.(Four glucosyltransferases, GtfJ, Gtfk, GtfL and GtfM, from Streptococcus salivarius ATTC 25975, Microbiologgy , 1995, 141, 1451-60). (Year: 1995). |
| “Food: Filtration fulfils important role in starch production” by Trevor Sparks, 2012 (Year: 2012). |
| Striegel et al., “An SEC/MALS study of alternan degradation during size-exclusion chromatographic analysis”, Anal Bioanal Chem 394: 1887-1893 (2009) (Year: 2009). |
| Tanford, C., “Physical Chemistry of Macromolecules”, section 18c (1961), John Wiley & Sons (New York) (Year: 1961). |
| Behabtu et al., Enzymatic Polymerization Routes to Synthetic-Natural Materials: A Review ACS Sustainable Chem. Eng., vol. 8, pp. 9947-9954 (2020). |
| PCT International Search Report and Written Opinion for International Application No. PCT/US2014/044281, dated Sep. 11, 2014. |
| PCT International Search Report and Written Opinion for International Application No. PCT/US2015/037628, dated Sep. 22, 2015. |
| PCT International Search Report and Written Opinion for International Application No. PCT/US2013/076905, dated Mar. 4, 2014. |
| PCT International Search Report and Written Opinion for International Application No. PCT/US2015/037624, dated Oct. 12, 2015. |
| PCT International Search Report and Written Opinion for International Application No. PCT/US2013/076919, dated Mar. 3, 2014. |
| PCT International Search Report and Written Opinion for International Application No. PCT/US2015/037634, dated Sep. 22, 2015. |
| Number | Date | Country | |
|---|---|---|---|
| 20230000752 A1 | Jan 2023 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62112960 | Feb 2015 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15548916 | US | |
| Child | 17746183 | US |