Patent Application
20160115027
This invention generally relates to metal chalcogenide nanostructures, method for their preparation and methods of use.
Semiconductor nanorods are often considered as quasi-one-dimensional (1D) systems. They manifest linearly polarized emission, reduced lasing threshold and improved charge transport as compared with their counterpart spherical quantum dots. Present investigations of colloidal semiconductor nanorods are mainly based on the system of cadmium chalcogenides due to their facile synthetic accessibility.
However, it is still a challenge to fabricate quasi-1D zinc chalcogenide nanocrystals with controlled aspect ratios. Development of such nanocrystals are of high importance, as the availability of cadmium-free (or “green”) zinc chalcogenide nanorods, produced through this strategy, provides a desirable platform for eco-friendly components for use in, e.g., optics, photocatalysis, electronic devices and bio-labeling.
Selective monomer attachment and coalescence of particles are among the most important growth mechanisms of quasi-1D colloidal nanocrystals. On one hand, the growth rates of different facets of a nanocrystal are determined either by the internal growth behavior of these facets or the binding energy between the facet and the organic surfactant molecule. So monomers attach much faster to the high-energy facet than the others, leading to the formation of elongated nanostructures. On the other hand, nanorods can be produced by the co-alignment and coalescence from isolated individual building blocks via an oriented attachment process.
Compared with cadmium chalcogenide nanorods (CdS, CdSe and CdTe), which have been intensively studied, zinc chalcogenide nanorods (ZnS, ZnSe and ZnTe) are hardly investigated due to the difficulty in their synthesis, which is related to the stability of different crystal structures, not necessarily being compatible with anisotropic growth. The seeded growth approach in the presence of phosphonic acid as the surfactant in trioctylphosphine (TOP)/trioctylphosphine oxide (TOPO) solvents produces CdSe/CdS quantum rods with excellent size distribution and controlled aspect ratio [1-3]. However, attempts to use this approach to synthesize quasi-1D zinc chalcogenide nanorods have been unsuccessful, resulting in either polycrystalline or polypod-shaped zinc chalcogenide nanoparticles with poor size distributions [4-9].
It has been demonstrated that alkylamines, rather than TOP/TOPO, which act as both surfactant ligands and solvents, are more suitable for synthesizing zinc chalcogenide nanorods [10-14] due to the better compatibility between alkylamine ligands and zinc ions; yet the control of the diameter of the nanorods has not been achieved. In these cases, the thermal decomposition of organic precursors produces tiny ZnSe and ZnS spherical quantum dots. Instead of a dopting monomer attachment growth mechanism, the produced individual quantum dots co-align and coalesce into elongated nanowires. However, the diameters of the produced nanowires are mainly below 3 nm [11-12, 15-20], suggesting that the limitation of width control of zinc chalcogenide nanorods imposed by alkylamines is hard to be circumvented.
Recently, Achraya et al. [21] reported synthesizing metal Mn2+ doped ZnSe 1D nanorods via fragmentation. The ion doped 1D nanorods growth involved utilizing (crude) sample of nanowire precursors and swift injection to hot solutions.
High quality zinc chalcogenides based nanostructures, e.g., nanorods, are desirable, as they provide, on one hand, quasi-1D nanocrystals with improved and unique electro-optic characteristics, such as improved charge carrier transport, reduced lasing threshold and polarized photoluminescence with wavelength tunable by the dimensions, and in particular by the diameter of the nanorods through the quantum confinement effect, and, on the other hand, as they are less toxic or non-toxic, they enable “green” use in a variety of applications such as optics, displays, lighting, solar energy, photocatalysis and biological labeling.
However, the path to achieving high quality non-spherical zinc chalcogenide nanostructures has been hurdled by synthetic difficulties, as conventional synthetic routes, such as monomer attachment or coalescence, resulted in nanocrystals with either poor qualities (e.g. broad size distribution, broad shape distribution, polycrystalline nanorods, and polymorphic nanoparticles) or uncontrollable (unitary) aspect ratios. This is partially due to the stability of different crystal structures of zinc chalcogenide nanocrystals that are not necessarily compatible with anisotropic growth needed for the formation of quantum rods.
The inventors of the present invention have generally developed methodologies for the production of high quality quasi-1D zinc chalcogenide nanorods and high quality 2-D zinc chalcogenide quadrilateral nanostructures, “nanorod couples”, with controlled characteristics . The synthetic methodologies for both zinc chalcogenide nanorods and start with the synthesis of ultrathin nanowires. On one hand, the obtained ultrathin nanowires were purified by cleaning in order to remove all the unreacted monomers, enabling production of nanorods with controlled aspect ratios by a self-ripening process via thermal-activated material diffusion; and on the other hand, if zinc and chalcogen precursors were intentionally added to the reaction solution, or if the crude nanowires solution were not purified, a gradual heating of the reaction solution to an elevated temperature, e.g. 280° C., produced highly desirable and unique structures of the zinc chalcogenides quadrilateral nanostructures via twinning growth on the end facets of each two nanowire components.
The novel process of the invention permits the synthesis of zinc chalcogenide nanorods and nanorod couples from their respective nanowires.
Without wishing to be bound to theory, the methodology behind the manufacture of the zinc nanorods, which may also be employed as precursors for the production of the nanorod couples, involves mass redistribution in zinc chalcogenide nanowires to afford the nanorods; the mass distribution is induced by thermally-activated material diffusion. The mass redistribution (used herein interchangeably with mass/material diffusion) may be an inter-particle process or an intra-particle process.
As further demonstrated, the novel methodology can be applied to produce a great range and variety of zinc chalcogenide nanostructures including ZnS, ZnSe and ZnTe, suggesting that this strategy is general and could be instructive for synthesizing other quasi-1D and 2D nanostructures via colloidal synthesis.
The inventors have also been able to convert the zinc chalcogenide nanostructures of the invention into other metal chalcogenide nanostructures, thus opening the door for the efficient manufacture of metal chalcogenide nanostructures from precursor zinc nanostructures.
Thus, the invention generally provides zinc chalcogenide nanostructures selected from nanorods and quadrilateral nanostructures also termed herein nanorod couples.
In some embodiments, the nanorods and quadrilateral nanostructures are manufactured from the corresponding nanowires. In other embodiments, the quadrilateral zinc nanostructures are manufactured from the zinc nanorods of the invention.
The process of the invention for the preparation of zinc chalcogenide nanorods is generally depicted in
The nanowires utilized in the processes of the invention are typically ultrathin nanowires, as further disclosed herein below, which may be obtained by direct synthesis or may be used as available from a commercial source. The nanowires used in accordance with processes of the invention are generally referred to herein as “precursor nanowires”. In some embodiments, the nanowires are prepared immediately prior to the preparation of the nanorods or nanostructures of the invention, or may be prepared in advance and allowed to mature in the synthesis medium.
In some embodiments, prior to using the nanowires, the medium comprising the nanowires is purified, e.g., excess or residual amounts of monomer precursors are removed, to afford a nanowire solution which is free or substantially free of precursor monomers.
The “monomer precursors” or “monomers”, as used herein, are the precursors utilized in the manufacture of the nanowires. The monomers may be selected amongst (1) single source monomers containing both the zinc and the chalcogen, e.g. zinc diethyldithiocarbamate, and (2) monomers containing zinc precursors and chalcogen precursors.
The zinc precursors may be selected from zinc nitride, zinc chloride, zinc acetate, zinc oxide, dimethylzinc, zinc stearate, zinc oleate and zinc phosphonic compounds. The chalcogen precursors may be selected from chalcogen elements, selenourea, thiols, bis(trimethylsilyl)sulfide, trioctylphosphine-chalcogenides, tributylphosphine-chalcogenides, H2S, H2Se, H2Te, amine-chalcogenides compounds, and alkene-chalcogenide compounds.
In some embodiments, the monomers are selected amongst zinc precursors and chalcogen precursors.
In some embodiments, the purifying step may include precipitating and re-dispersing the nanowires in a fresh solution, e.g., chloroform, toluene, and alcohol such as methanol or ethanol. In some embodiments, said purification step may be performed several times. In further embodiments, the purification step may be performed in duplicate, triplicate or quadruplicate. The medium in which the nanowires are contained following purification is typically an organic solvent. According to one example, the purification is carried out by introducing into the medium in which the nanowires are grown in an organic solvent which is capable of fully dissolving the precursor materials (metal chalcogenide precursors, or monomers needed for the production of the nanowires, as detailed herein), centrifuging the medium in order to separate the nanowires from the organic medium and repeatedly washing, e.g., twice, three times, etc, the nanowires to remove as much of the precursors as possible to afford a precursor-free or substantially free nanowire medium.
Alternatively, the purifying step may be carried out by any other means for achieving complete elimination or reduction in the amount of the monomer precursors. The purification step may reduce the monomers precursors in 50% or 60% or 70% or 80% or 90% or 95% or 98% or 99%.
In some embodiments, the nanowire medium comprises 0, 0.1, 0.2, 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 0.9, 1, 2, 3, 4, 5, 6, 7, 8, 9, 10% higher monomer precursors subsequent to the purification step.
The nanowires solution or medium, as a precursor solution for the preparation of nanorods or quadrilateral nanostructures of the invention, may be treated prior to the gradual annealing step resulting in the nanorods or nanostructures of the invention. The treatment steps may encompass one or more of the following: dispersing, dissolving, purifying, precipitating, and re-dispersing in a clean solvent (medium) or another solvent, evaporation of solvent, adding chemical agents or ligands, exchanging ligands (attached to the nanowires), and any combination thereof.
Reference is now made to Scheme 1 below which provides a general and non-limiting scheme for processes and products of the invention.
The nanowires solution, either purified as above, or unpurified, namely containing an amount of the precursor monomers, is gradually annealed to afford either the nanorods of the invention or the quadrilateral nanostructures of the invention. Without wishing to be bound by theory, in the absence of monomers, namely when the nanowire solution is free from monomers, gradual annealing of the nanowires generates a controlled mass redistribution and formation of the nanorods, as depicted in
The size and final shape of the quadrilateral nanostructures of the invention may depend not only on the reaction conditions and the specific metal (e.g., zinc) chalcogenide employed, but also on the initial morphology of the starting nonmaterial, as depicted in
In view of the above, it is clear that the quadrilateral structures may be produced not only from zinc chalcogenides but also from other metal chalcogenides, as further disclosed and exemplified hereinbelow.
As used herein, the term “metal chalcogenide”, unless otherwise specifically referred to a specific metal species, refers to compounds of a metal with sulfur, selenium or tellurium or polonium. Exemplary metals include Ga, In, Ti, Sn, Pb, Bi, Zn, Cd, Hg, Cu, Ag, Au, Ni, Pd, Pt, Co, Rh, Ir, Fe, Ru, Os, Mn, Tc, Re, Cr, Mo, W, v, Nb, Ta, Ti, Zr, Hf, Sc and Y. Metal chalcogenides may be selected from Metal chalcogenides may be selected from CdS, CdSe, Sn2S6, Sn2Se6, In2Se4, In2Te3, Ga2Se3, CuInSe2, Cu7S4, Hg3Se4, Sb2Te3, ZnS, ZnSe, ZnTe, AgS, AgSe, AgTe, Cu2S, Cu2Se, CuInS2, PbS, PbSe, PbTe, ZnS, ZnSe and ZnTe.
In some embodiments, the metal is selected from Cd, Cu, Ag and Pb. The metal chalcogenide is thus selected from Cd-chalcogenides, Cu-chalcogenides, Ag-chalcogenides and Pb-chalcogenide.
In some embodiments, the metal chalcogenide is a zinc chalcogenide. The zinc chalcogenides may be selected from ZnS, ZnSe and ZnTe.
Thus, the invention provides a process for producing metal, e.g., zinc, chalcogenide nanostructures selected from nanorods and quadrilateral nanostructures having improved characteristics (as disclosed above), the process comprising heating/annealing a sample of ultrathin nanowires, in a medium (and under conditions) allowing mass redistribution or mass diffusion in said nanowires or fusion (coupling or twinning) of said nanowires.
In some embodiments, the process for the preparation of zinc chalcogenide nanorods comprises gradually annealing medium comprising nanowires under conditions allowing mass redistribution or mass diffusion to thereby form said nanorods; the nanorods being formed via controlled mass distribution and not via fragmentation or truncation of the nanowires into a plurality of nanorods.
In some embodiments, the process for the preparation of zinc chalcogenide nanorods comprises:
to thereby cause transformation of the nanowires in the medium into the respective nanorods.
In some embodiments, the process comprises a step of obtaining a sample of nanowires in a medium and purifying the sample prior to affecting gradual annealing.
Thus, the invention provides a process for the preparation of zinc chalcogenide nanorods, the process comprising:
to thereby cause transformation of the nanowires in the medium into the respective nanorods.
In other embodiments, the process comprises:
to thereby cause transformation of the nanowires in the solution into the respective nanorods.
As used herein, the expression “no more than a 5% amount of nanowire monomers relative to the original monomers concentration”, or any lingual variation thereof, refers to an amount of the nanowires monomers, also referred to as “metal chalcogenide monomers” or “monomers” used in the preparation of the metal nanowires, which is at most 5% of the original amount of the precursors originally used in the preparation of the monomers. Where the original amount of the nanowires monomers is not known, the amount of the monomers may be calculated considered as negligible or that no monomer amount is present.
In the process for preparing the nanowires used in the processes for making nanorods and nanostructures according to the invention, the nanowire monomers used may be (1) single source monomers containing both the zinc and the chalcogen, e.g. zinc diethyldithiocarbamate, and/or (2) monomers containing zinc precursors and chalcogen precursors.
The zinc precursors may be selected from zinc nitride, zinc chloride, zinc acetate, zinc oxide, dimethylzinc, zinc stearate, zinc oleate and zinc phosphonic compounds. The chalcogen precursors may be selected from chalcogen elements, selenourea, thiols, bis(trimethylsilyl)sulfide, trioctylphosphine-chalcogenides, tributylphosphine-chalcogenides, H2S, H2Se, H2Te, amine-chalcogenides compounds, and alkene-chalcogenide compounds.
In some embodiments, where the solution comprises nanowires is said to be substantially free of monomers or is purified to be substantially free of monomers, it typically contains (without purification or following purification) no more than 5%, 4%, 3%, 2%, 1%, 0.5%, 0.4%, 0.3%, 0.2% or 0.1% of the original monomer concentration.
In other embodiments, the solution consisting nanowires has been prepared by purifying a medium in which the nanowires were manufactured to remove all precursor monomers.
The amine compound may be any amine selected amongst alkylamines, alkenylamines (e.g., comprising one or more double bonds) and alkynylamines (e.g., comprising one or more triple bonds). In some embodiments, the nanowires are contained or comprised in a solution also containing at least one alkylamine
The alkylamine may be selected amongst C2-C25alkylamines, C10-C25alkylamines, C15-C25alkylamines, C20-C25alkylamines, as well from mono-alkylamines, dialklyamines and trialkylamines In some embodiments, the alkylamines are selected from C2-C25alkylamines In some embodiments, the alkylamines are selected from C10-C25alkylamines In some embodiments, the alkylamines are selected from C15-C25alkylamines In some embodiments, the alkylamines are selected from C20-C25alkylamines In some embodiments, the alkylamines are selected from C2, C3, C4, C5, C6, C7, C8, C9, C10, C11, C12, C13, C14, C15, C16, C17, C18, C19, C20, C21, C22, C23, C24 and C25-alkylamine. Where the alkylamine is a dialkylamine or a trialkylamine, namely in cases where the nitrogen (N) atom of the amine is covalently bound to two alkyl or three alkyl groups, respectively, each of the alkyl groups may or may not be the same and each may be selected amongst the above recited alkyl chains. For example, a dialkyl group may have two C9 alkyl chains, or one being a C9 alkyl and the other a C25 alkyl. In other words, a “C2-C25alkylamine” defines both a mono-alkylamine having a carbon chain of between C2 and C25 carbon atoms, or a di-alkylamine wherein each of the two alkyl groups is selected independently amongst C2 to C25 alkyls, or a tri-alkylamine wherein each of the three alkyl groups is selected independently amongst C2 to C25 alkyls.
The amine compound may be selected from dodecyl amine (DDA), tetradecyl amine (TDA), hexadecyl amine (HDA), octadecyl amine (ODA), oleic acid (OA), decylamine, dioctylamine, octylamine, oleylamine, tributylamine, trihexylamine and trioctylamine.
In some embodiments, the amine compound is oleylamine
As used herein, the term “solution” or “medium” refers to a liquid combination of at least one solvent, typically an organic solvent selected from alkylamines and a quantity of the nanowires, nanorods, or nanostructures of the invention. Where the solution is said to consist nanowires, nanorods, or nanostructures, it is said to contain the nanowires, nanorods, or nanostructures in at least one solvent (being a liquid medium).
Unlike processes such as that disclosed in the art [21], which involve addition of nanowires to an alkylamine at a high temperature (e.g., 260-300° C.) and by fast injection, the process of the invention involves the addition of the nanowires to an alkylamine at room temperature. According to the process of the invention, the solution of nanowires, e.g., in some embodiments as a mixture of nanowires in at least one type of alkylamine, optionally degassed, is heated gradually to a temperature ranging from 100 to 120° C. at a rate of between 5 and 30° C./minutes, or as further disclosed herein. Upon reaching the maximum temperature, the mixture is maintained for a period of time (e.g., a few minutes to one hour), thereafter the temperature is increased to a temperature ranging from 250 and 325° C., at a rate of 5 to 30° C./minute.
The process of the invention combining the step of mixing the nanowires with the alkylamine at room temperature, rather than at a high temperature, and the gradual annealing provides stable nanorods and prevents nanowires and nanorods from degradation or fragmentation. When the process was carried out under conditions involving fast injection of the nanowires, fragmentation occurred. The nanorods of the invention are not fragmented nanowires.
In further embodiments, the process for making the nanorods of the invention may further comprise a step of forming a coat or a shell around the zinc chalcogenide nanorods; the coat or shell thus producing a core/shell or a core/multishell nanostructure, wherein the core is a zinc chalcogenide nanorods and the shell being composed of a material which may or may not comprise zinc.
The multishell may comprise 1 to 10 or 1 to 5 or 3 or 2 shells. The thickness of the shell may range from about one monolayer to 50 monolayers. The thickness of the shell may range from about 0.3 to about 6 nm
In some embodiments, the shell material in a core/shell or multishell nanostructures according to the invention may be selected amongst any semiconductor material. The material of the semiconductor shell may be a II-VI, IV-VI2, III-V, IV-VI, I2-VI or I-III-VI2 semiconductor or combinations thereof. For example, the shell material may be selected from ZnS, ZnSe, ZnTe, ZnO, CdS, CdSe, CdTe, CdO, HgS, HgSe, HgTe, TiO2, SiO2, GaAs, GaP, GaAs, GaSb, GaN, InAs, InP, InSb, AlAs, AlP, AlSb, PbS, PbSe, PbTe, PbO, Cu2S, Cu2Se, CuInS2, CuInSe2, alloys thereof and mixtures thereof.
In some embodiments, the shell is another Zn-chalcogenide material. In some embodiments, the shell material is a material selected from ZnTe, ZnSe, ZnS, alloys thereof and mixture thereof.
In some embodiments, the core/shell systems are rods selected from ZnSe/ZnS, ZnTe/ZnSe, ZnTe/ZnSe/ZnS, and alloys thereof.
In some embodiments, the core/shell systems are selected from ZnTe/CdS, ZnSe/CdS.
In some embodiments, the core/multishells rods are selected from ZnTe/CdS/ZnS, ZnSe/CdS/ZnS, and ZnSe/CdSe/CdS.
The process of forming a coat or a shell around a nanorod of the invention may be selected, as known in the art, from slow addition of shell material precursors, or a successive ionic layer adsorption and reaction (SILAR) [22] or seeded growth method [1, 2].
In some embodiments, the medium comprising zinc chalcogenide nanorods is further used for the production of the quadrilateral nanostructures of the invention.
In some embodiments, the process further comprises:
In some embodiments, the monomers may be a single source containing both zinc and chalcogen, e.g. zinc diethyldithiocarbamate, and/or the monomers may be selected amongst to constitute both zinc precursors and chalcogen precursors.
In some embodiments, the zinc precursors may be selected from zinc nitride, zinc chloride, zinc acetate, zinc oxide, dimethylzinc, zinc stearate, zinc oleate, and zinc phosphonic compounds. The chalcogen precursors may be selected from chalcogen elements, selenourea, thiols, bis(trimethylsilyl)sulfide, trioctylphosphine-chalcogenides, tributylphosphine-chalcogenides, H2S, H2Se, H2Te, amine-chalcogenides compounds and alkene-chalcogenide compounds).
In some embodiments, the monomers are selected amongst single source monomers containing both zinc and a chalcogen, as defined above, and a mixture of zinc precursors and chalcogen precursors, each as defined.
In some embodiments, the nanorods are zinc chalcogenide nanorods according to the present invention.
In other embodiments, the nanorods are zinc chalcogenide nanorods prepared according to procedures known in the art such as [21].
In some embodiments, the amount of monomers, used for the preparation of nanowires, as detailed herein, added to the medium comprising the nanorods is equal or smaller than the amount of nanorods. In further embodiments, the ratio monomers:nanorods is between 1:1 and 1:6. In other embodiments, the ratio of monomers added to nanorods is 1:1, 1:2, 1:3, 1:4, 1:5 or 1:6 (monomers:nanorods). In other embodiments, the ratio monomers:nanorods is between 1:1 and 1:3. In further embodiments, the ratio monomers:nanorods is between 1:2 and 1:3.
Alternatively, the nanostructures may be prepared by gradually annealing a medium comprising zinc chalcogenide nanowires and an amount of monomers (namely an unpurified nanowire solution, as disclosed hereinabove), to cause transformation of the nanowires into quadrilateral nanostructures.
Thus, in such embodiments, the invention comprises:
The “nanowires” which are precursors in processes of the invention, for manufacturing nanorods and nanostructures, may be of a material selected amongst metal chalcogenide, e.g., zinc chalcogenides. The nanowires are typically ultrathin, namely having a diameter smaller than 2.5 nm; or in some embodiments smaller than 5 nm In some embodiments, the diameter of the nanowires is between 1 and 2.5 nm In other embodiments, the diameter is between 2.5 and 5.
The nanowires typically have a length in the nanometer to the micrometer regime (0.015 μm to 50 μm). The average length of the nanowires may be above 15 nm
In some embodiments the average length is above 30 nm In some embodiments the average length is above 100 nm In some embodiments, the average length is above 500 nm In other embodiments, the average length is above 1 μm. In some embodiments, the average length is above 10 pm. In further embodiments, the average length is above 50 μm.
In some embodiments, the average length is from 15 to 1000nm The aspect ratio of the nanowires is typically large. In some embodiments, the nanowires may have an aspect ratio (length/diameter) above 4. In some embodiments, the nanowires may have an aspect ratio (length/diameter) above 12. In some embodiments, the nanowires have an aspect ratio (length/diameter) above 50. In other embodiments, the nanowires may have an aspect ratio above 100. In further embodiments, the nanowires may have an aspect ratio between 50 and 200.
In some embodiments, the aspect ratio of the nanowires is 50 times larger than the aspect ratio of the nanorods produced therefrom. In some embodiments, the aspect ratio of the nanowires is 10 times larger than the aspect ratio of the nanorods produced therefrom. In some embodiments, the aspect ratio of the nanowires is 5 times larger than the aspect ratio of the nanorods produced therefrom. In some embodiments, the aspect ratio of the nanowires is 3 times larger than the aspect ratio of the nanorods produced therefrom.
In some embodiments, the nanowires have an average length ranging from 15 nm to 50 μm and an average diameter ranging from 1 nm to 2.5 nm
In some embodiments, the zinc chalcogenide nanowires have an average length ranging from 15 to 1000 nm and an average width ranging from 1 to 2.5 nm
In some embodiments, the nanowires may be associated (coated) with surface ligands, typically organic ligands. In some embodiments, each precursor nanowire is coated, partially or wholly with a plurality of ligands, selected in a non-limiting fashion from trioctylphosphine (TOP), tributylphosphine (TBP), trioctylphosphine oxide (TOPO), dodecyl amine (DDA), tetradecyl amine (TDA), hexadecyl amine (HDA), octadecyl amine (ODA), decylamine, dioctylamine, octylamine, oleylamine, tributylamine, trihexylamine, trioctylamin, oleic acid (OA), dodecylphosphonic acid (DDPA), tridecylphosphonic acid (TDPA), octadecylphosphonic acid (ODPA), hexylphosphonic acid (HPA) and thiols.
The gradual annealing of the nanowires in solution is carried out in a medium permitting nanorods formation, at an appropriate temperature. The medium permitting formation of the nanorods is typically a growth solution (or medium) comprising the nanowires, an appropriate solvent with optionally appropriate ligands and/or chemical agent. In some cases, the ligands solution serves also as the solvent solution. The growth solution may be the medium of the sample of the nanorods as obtained.
In some embodiments, the precursor nanowires are obtained in a powder form, therefore, the sample comprising them may be dispersed in a growth solution prior to the annealing step. In some embodiments, the sample comprising the precursor nanowires may be precipitated and re-dispersed into a growth solution prior to the gradual annealing step.
The growth solution provides the nanowires and may also provide ligands designed for assisting in mass re-distribution during nanorods synthesis, as well as, for assisting in dispersing and dissolving the nanowires in the growth solution.
Generally and without wishing to be bound by theory, promotion of mass redistribution and consequently nanorod formation is usually achieved by using ligands which are lightly attached to the precursor nanowire. In general, weak attaching ligands are organic ligands comprising a carbonaceous (organic) tail and a moiety, which may be selected from amines, and carboxylic acid. In some embodiments, the weak ligands are selected from dodecyl amine (DDA), tetradecyl amine (TDA), hexadecyl amine (HDA), octadecyl amine (ODA), oleic acid (OA), decylamine, dioctylamine, octylamine, oleylamine, tributylamine, trihexylamine and trioctylamine
In some embodiments, the weak ligands are selected from alkylamines In other embodiments, the ligand is oleylamine
In some cases, the required ligands (one or more) are present in the nanowire solution. In further embodiments, the nanowire solution is subjected to a ligand-exchange step (i.e., the ligands associated with surface of the precursor nanowires), prior to the gradual annealing step.
The gradual annealing step is carried out in a solution (medium) comprising the nanowires, by gradually elevating the temperature of the solution to an appropriate temperature while permitting formation of nanorods. The gradual annealing refers to increasing the temperature gradually in a way that does not involve a thermal shock; namely it does not involve an abrupt increase in the temperature. In some embodiments, the gradual elevation of the temperature may be at a rate of about several tenths of a degree Celsius per minute to about several tens of a degree Celsius per minute. In some other embodiments, the rate is above 0.1° C./minute. In some embodiments, the rate is above 1° C./minute. In some embodiments, the rate is above 5° C./minute. In some embodiments, the rate is above 10° C./minute.
In some embodiments, the rate ranges from 0.1° C./min to 50° C./min In further embodiments, the rate ranges from 1° C./minute to 50° C./min In other embodiments, the rate ranges from 0.1° C./minute to 10° C./minute.
In some embodiments, the temperature is elevated to a temperature being higher than 100° C. In other embodiments, the temperature is higher than 200° C. In some embodiments, the temperature is higher than 250° C. In some embodiments, the temperature is higher than 300° C.
In some embodiments, the temperature is the temperature at which the medium being gradually heated begins to boil. In other words, in such embodiments the temperature is the boiling point temperature of the reaction medium.
In some embodiments, the maximum temperature is between 100° C. to 400° C. In other embodiments, the maximum temperature is between 200° C. to 400° C. In further embodiments, the maximum temperature is between 250° C. to 350° C. In further embodiments, the maximum temperature is between 250° C. to 325° C. In still other embodiments, the maximum temperature is between 250° C. to 300° C.
In some embodiments, the annealing conditions (rate of gradual increase, starting temperature and maximum temperature) are identical both to the process of manufacturing nanorods from nanowires and to the process of manufacturing quadrilateral nanostructures from nanowires.
In other embodiments, the annealing conditions (maximum temperature) utilized in the process of manufacturing nanorods from nanowires are different from those utilized in the process of manufacturing quadrilateral nanostructures from nanowires. For example, the maximum temperature utilized in the process of manufacturing nanorods may be much higher than that for quadrilateral structures, e.g. between 280° C. to 325° C.
The process of the invention provides medium comprising nanorods of controllable size. The dimensions of the nanorods may be determined by the duration of reaction, e.g., the period of time the reaction solution is kept at an appropriate temperature of 280° C. to 300° C. The maximum temperature is 325° C. The dimensions of the nanorods are also determined by the length of the nanowires used as precursors for the synthesis. In some embodiments, the reaction is terminated immediately after reaching the rod formation temperature. In other embodiments, the reaction duration is above 1 minute. In some other embodiments, the reaction duration is above 5 minute. In some embodiments, the reaction duration is above 10 minute.
In some other embodiments, the reaction duration ranges from 5 seconds to 100 minutes. In some other embodiments, the reaction duration ranges from 1 minute to 60 minutes. In some other embodiments, the reaction duration ranges from 5 minute to 60 minutes.
In one of its additional aspects, the invention provides a medium comprising as-prepared zinc chalcogenide nanorods, wherein each zinc chalcogenides nanorod being a quasi-1D zinc chalcogenide nanorod; the medium has improved characteristics as follows:
1. it comprises a high yield of zinc chalcogenide nanorods having narrow distribution of shapes, structures and sizes;
2. it comprises a high yield of zinc chalcogenide nanorods that are single crystalline;
3. it exhibits high stability; high thermal and photo stability
4. it comprises a population of zinc chalcogenide nanorods having an average diameter above 2.5 nm; and
5. it comprises a population of zinc chalcogenide nanorods having controlled aspect ratios.
As noted above, the medium of the invention comprises “as-prepared zinc chalcogenide nanorods”. In other words, the nanorods comprised in the medium are the crude nanorods composition obtained directly in the specific medium in which their synthesis (e.g., colloidal) is carried out, with no (or substantially no) further purification treatments (e.g., size selective precipitation, purification, ligand exchange), i.e., a crude sample (solution/dispersion) of nanorods. The “medium of nanorods” comprising one or more nanorods (nanocrystals), typically a plurality of nanorods, may be in a form selected from a solution (or colloidal solution), a suspension or a dispersion of nanorods. In some embodiments, the medium is a liquid medium. In some embodiments, the liquid medium is a mixture of one or more organic solvents (liquids), which may or may not further contain solubilized materials. In some embodiments, the medium is an organic solution.
Thus, as the solution or medium comprises nanorods which are the direct product of mass redistribution, the invention also provides zinc chalcogenide nanorods manufactured by mass redistribution from the corresponding zinc chalcogenide nanowires.
In some embodiments, the zinc chalcogenide nanowires are present in the medium in which the nanorods are manufactured, with the medium comprising no excess of monomers.
The “nanorods” prepared according to the process of the invention and comprised in the medium are non-spherical nanoparticles exhibiting growth along the elongated axis of the nanoparticles, while maintaining small dimensions in the other axes, resulting in nanoparticles having one axis which is elongated (longer) relative to the other axes (or diameter). The nanorods of the invention are different in their dimensions from the nanowires from which they are manufactured.
The dimensions of all axes are in the nanoscale regime (1.5nm to 1,000 nm). The size of the nanorods is given as the length of the longest axis of the particle, its width (short axis or diameter) and/or its aspect ratio which is the ratio of length to diameter.
In some embodiments, the average (mean) length of the longest axis of the nanorods may range from about 5 nm to about 1,000 nm In some embodiments, the average (mean) length of the longest axis of the nanorods may range from about 5 nm to about 500 nm
In some embodiments, the average length of the longest axis is above 10 nm In some embodiments, the average length of the longest axis is above 50 nm In some embodiments, the average length of the longest axis is above 100 nm
In some embodiments, the average length of the longest axis is between 5 to 200 nm In some embodiments, the average length of the longest axis is between 10 to 200 nm In some embodiments, the average length of the longest axis is between 10 to 100 nm
The average width of the nanorods may be smaller than 100 times the Bohr radius of the Zn chalcogenide material. In some embodiments, the average length of the nanorods may be smaller than 50 times the Bohr radius of the Zn chalcogenide material. In further embodiments, the average length of the nanorods may be smaller than 40 times the Bohr radius of the Zn chalcogenide material; smaller than 30 times the Bohr radius of the Zn chalcogenide material; smaller than 20 times the Bohr radius of the Zn chalcogenide material; smaller than 15 times the Bohr radius of the Zn chalcogenide material; smaller than 10 times the Bohr radius of the Zn chalcogenide material; or smaller than 5 times Bohr radius of the Zn chalcogenide material.
The average (mean) width (or diameter) of the shortest axis of the nanorods may range from about 1.5 nm to about 100 nm In some embodiments, the average width ranges from about 1.5 nm to about 50 nm In other embodiments, the average width ranges from about 1.5 nm to about 20 nm In further embodiments, the average width ranges from 1.5 to 15 nm In some embodiments, the average width ranges from 1.5 to 12 nm In some embodiments, the average width ranges from 1.5 to 10 nm
In some embodiments, the average width ranges from about 2.5 nm to about 100 nm In some embodiments, the average width ranges from about 2.5 nm to about 50 nm In some embodiments, the average width ranges from about 2.5 nm to about 20 nm
In some embodiments, the average width ranges from 2.5 to 15 nm In some embodiments, the average width ranges from 2.5 to 12 nm In some embodiments, the average width ranges from 2.5 to 10 nm
In some embodiments, the average width ranges from 2.5 to 6 nm
In some embodiments, the average width ranges from about 4 nm to about 100 nm In some embodiments, the average width ranges from about 4 nm to about 50 nm In some embodiments, the average width ranges from about 4 nm to about 20 nm In some embodiments, the average width ranges from 4 to 15 nm In some embodiments, the average width ranges from 4 to 12 nm In some embodiments, the average width ranges from 4 to 10 nm
In some embodiments, the average width is above 10 nm In other embodiments, the average width is above 5 nm In other embodiments, the average width is above 4 nm In other embodiments, the average width is above 3 nm In other embodiments, the average width is above 2.5 nm
In some embodiments, the average width is below 100 nm In other embodiments, the average width is below 50 nm In other embodiments, the average width is below 40 nm In other embodiments, the average width is below 30 nm In other embodiments, the average width is below 20 nm
In other embodiments, the average width of the nanorods may range from about 3 to about 20 nm In other embodiments, the average width may range from about 5 to about 20 nm In other embodiments, the average width may range from about 3 to about 20 nm In other embodiments, the average width may range from about 4 to about 20 nm In other embodiments, the average width may range from about 5 to about 20 nm In further embodiments, the average width may be 2 5 nm, or 2 nm, or 3 nm, or 4 nm, or 5 nm, or 6 nm, or 7 nm, or 8 nm, or 9 nm, or 10 nm, or 11 nm, or 12 nm, or 13 nm, or 14 nm, or 15 nm, or 16 nm, or 17 nm, or 18 nm, or 19 nm, or 20 nm, or 21 nm, or 22 nm, or 23 nm, or 24 nm, or 25 nm, or 26 nm, or 27 nm, or 28 nm, or 29 nm or 30 nm
The average width of the nanorods may be smaller than 10 times the Bohr radius of the Zn chalcogenide material; smaller than 5 times the Bohr radius of the Zn chalcogenide material; smaller than 4 times the Bohr radius of the Zn chalcogenide material; smaller than 3 times the Bohr radius of the Zn chalcogenide material; smaller than 2 times the Bohr radius of the Zn chalcogenide material; or smaller than 1.5 times the Bohr radius of the Zn chalcogenide material.
In other embodiments, the nanorod may have an average aspect ratio (length/diameter) of between 2 and 200. In other embodiments, the nanorod may have an average aspect ratio of between 2 and 30. In other embodiments, the nanorod may have an average aspect ratio of between 2 and 20. In other embodiments, the nanorod may have an average aspect ratio of between 2 and 15. In other embodiments, the nanorod may have an average aspect ratio of between 2 and 10.
In some embodiments, the average aspect ratio is smaller than 30. In some embodiments, the average aspect ratio is smaller than 25. In further embodiments, the average aspect ratio is smaller than 20. In still further embodiments, the average aspect ratio is smaller than 15 and in further embodiments, the average aspect ratio is smaller than 10.
In some embodiments, the nanorods are an intermediate state between OD (quantum dot) and quasi-1D (nanowire), i.e., an intermediate state between confinement of carriers in three dimensions to confinement of carriers in two dimensions.
In some embodiments, the Zn chalcogenide material is ZnS, the average width of the nanorods may be between 2 nm and 6 nm In some embodiments, the Zn chalcogenide material is ZnS, the average width of the nanorods may be between 2 nm and 20 nm In some embodiments, the Zn chalcogenide material is ZnS, the average width of the nanorods may be between 2 nm and 30; between 2 and 40 nm; between 2 and 50 nm; between 2 and 60 nm; between 2 and 70 nm; between 2 and 80 nm; between 2 and 90 nm or between 2 and 100 nm
In further embodiments, the Zn chalcogenide material is ZnS, the average length of the nanorods may be between 5 nm and 50 nm In further embodiments, the Zn chalcogenide material is ZnS, the average length of the nanorods may be between 5 nm and 30; between 5 and 40 nm; between 5 and 60 nm; between 5 and 70 nm; between 5 and 80 nm; between 5 and 90 nm; between 5 and 100 nm; or between 5 nm and 200 nm In further embodiments, the Zn chalcogenide material is ZnS, the average length of the nanorods may be between 5 nm and 1000 nm
In some embodiments, the Zn chalcogenide material is ZnSe, the average width of the nanorods may be between 2.5 nm and 9 nm In some embodiments, the Zn chalcogenide material is ZnSe, the average width of the nanorods may be between 2.5 and 10 nm; between 2.5 nm and 20; between 2.5 nm and 30; between 2.5 nm and 40 or between 2.5 nm and 50 nm In some embodiments, the Zn chalcogenide material is ZnSe, the average width of the nanorods may be between 2.5 nm and 200 nm
In further embodiments, the Zn chalcogenide material is ZnSe, the average length of the nanorods may be between 5 nm and 100 nm In further embodiments, the average length of the nanorods may be between 5 nm and 30; between 5 and 40 nm; between 5 and 60 nm; between 5 and 70 nm; between 5 and 80 nm; or between 5 and 90 nm In further embodiments, the Zn chalcogenide material is ZnSe, the average length of the nanorods may be between 5 nm and 200 nm In further embodiments, the Zn chalcogenide material is ZnSe, the average length of the nanorods may be between 5 nm and 1000 nm
In some embodiments, the Zn chalcogenide material is ZnTe, the average width of the nanorods may be between 2.5 nm to 15 nm In some embodiments, the average width of the nanorods may be between 2.5 to 10 nm; between 2.5 nm to 20; between 2.5 nm to 30; between 2.5 nm to 40 or between 2.5 nm to 50 nm In some embodiments, the Zn chalcogenide material is ZnTe, the average width of the nanorods may be between 2.5 nm to 60 nm In some embodiments, the Zn chalcogenide material is ZnTe, the average width of the nanorods may be between 2.5 nm to 200 nm
In further embodiments, the Zn chalcogenide material is ZnTe, the average length of the nanorods may be between 5 nm and 150 nm In further embodiments, the average length of the nanorods may be between 5 nm and 30; between 5 and 40 nm; between 5 and 60 nm; between 5 and 70 nm; between 5 and 80 nm; between 5 and 90 nm; between 5 and 100 nm; between 5 and 110 nm; between 5 and 120 nm; between 5 and 130 nm; or between 5 and 140 nm In further embodiments, the Zn chalcogenide material is ZnSe, the average length of the nanorods may be between 5 nm and 200 nm In further embodiments, the Zn chalcogenide material is ZnTe, the average length of the nanorods may be between 5 nm and 1000 nm
The nanorods prepared and employed in accordance with the invention may be associated (coated) with surface ligands, typically organic ligands. Such organic ligands are selected to affect one or more physical or chemical characteristics, e.g., solubility of the nanorods. In some embodiments, each nanorod is coated, partially or wholly with a plurality of ligands. The ligands on the surface of the nanorods may be maintained or removed or exchanged depending on the specific application.
As stated above, the nanorods are constructed of zinc and a chalcogenide. The chalcogenide may be selected amongst elements of Group VIA of the periodic table. In some embodiments, the chalcogenide is selected from 0, S, Se and Te. In further embodiments, the chalcogenide is selected from S, Se and Te.
In some embodiments, the sample of nanorods of the invention comprises nanorods selected from ZnS, ZnSe and ZnTe.
In some embodiments, the nanorods of the invention comprise nanorods selected from selected from ZnTe, ZnSe, ZnS, alloys thereof, and mixture thereof.
In some embodiments, the sample of nanorods of the invention comprises Zn chalcogenide alloy nanorods of the general formula ZnSxSe1-x, ZnSexTe1-x and ZnSxTe1-x, wherein x being between 0 and 1. In some embodiments, x is zero. In other embodiments, x is one.
In some embodiments, the sample of nanorods comprises nanorods of Zn chalcogenide alloys comprising more than one chalcogenide.
In some embodiments, the nanorods comprise Zn chalcogenide alloys with at least one chalcogenide and at least one other element. The alloy nanorods may be selected from ZnSeS, ZnTeS and ZnTeSe.
The sample of nanorods of the invention comprises Zn chalcogenide and may further comprise a shell or multishell, i.e, have a core/shell or core/multishell structure. The multishell may comprise 1 to 10 or 1 to 5 or 3 or 2 shells. The thickness of the shell may range from about one monolayer to 50 monolayers. The thickness of the shell may range from about 0.3 to about 6 nm
In such core/shell or multishell systems, the core is a nanorod according to the invention and the shell may be selected amongst any semiconductor material.
The material of the semiconductor shell may be a II-VI, IV-VI2, III-V, IV-VI, I2-VI or I-III-VI2 semiconductor or combinations thereof. For example, the shell material may be selected from ZnS, ZnSe, ZnTe, ZnO, CdS, CdSe, CdTe, CdO, HgS, HgSe, HgTe, TiO2, SiO2, GaAs, GaP, GaAs, GaSb, GaN, InAs, InP, InSb, AlAs, AlP, AlSb, PbS, PbSe, PbTe, PbO, Cu2S, Cu2Se, CuInS2, CuInSe2, alloys thereof, and mixtures thereof.
In some embodiments, the shell is another Zn-chalcogenide material. In some embodiments, the shell material is a material selected from ZnTe, ZnSe, ZnS, alloys thereof, and mixture thereof.
In some embodiments, the core/shell systems are rods selected from ZnSe/ZnS, ZnTe/ZnSe, ZnTe/ZnSe/ZnS, and alloys thereof.
In some embodiments, the core/shell systems are selected from ZnTe/CdS, ZnSe/CdS.
In some embodiments, the core/multishells rods are selected from ZnTe/CdS/ZnS, ZnSe/CdS/ZnS, and ZnSe/CdSe/CdS.
The nanorods of the invention, either as is and/or when constructed as core/shell and/or core/multishell nanorods, may have an emission ranging from ultra-violet to infrared. In some embodiments, the emission ranges from ultra-violet to near infrared.
In further embodiments, the emission ranges from visible to near infrared. In some further embodiments, the emission is in the blue light regime.
As further stated above, the medium comprising zinc chalcogenide nanorods of the invention may be characterized by one or more of the following:
1. comprising a high yield of zinc chalcogenide nanorods having a narrow distribution of shapes, structures and sizes;
2. comprising a high yield of single crystalline zinc chalcogenide nanorods;
3. exhibiting high stability;
4. comprising a population of zinc chalcogenide nanorods having an average diameter above 2.5 nm; and
5. comprising a population of zinc chalcogenide nanorods having controllable aspect ratios.
In some embodiments, the medium comprises zinc chalcogenide nanocrystals of a narrow distribution of sizes in rod shape; namely, the majority of the nanoparticles are nanorods with only a small portion of the nanoparticles or none of the nanoparticles being of other shapes (such as, spherical nanoparticles). Additionally, amongst the population of nanorods, all or the majority thereof are straight nanorods, with the other minority thereof may be of a bent or branched structure.
In some embodiments, at least 70% of the nanoparticles are nanorods. In further embodiments, at least 80% of the nanoparticles are nanorods. In further embodiments, at least 90% of the nanoparticles are nanorods. In yet other embodiments, at least 95% of the nanoparticles are nanorods; in yet other embodiments, at least 98% of the nanoparticles are nanorods; and in other embodiments, between 95 and 98% of the nanoparticles are nanorods.
The nanorods are further said to have a narrow size distribution. The size of the nanorods may be defined by the following dimensions: diameter, length, and/or aspect ratio. Typically, for the nanorods in the medium, all size dimensions are narrowly distributed. In some embodiments, the size of the nanorods (diameter and/or length and/or aspect ratio) in the sample is ±30% of their mean value (as defined herein). In further embodiments, the size of the nanorods is ±20% of their mean value. In further embodiments, the size of the nanorods is ±10% of their mean value. In further embodiments, the size of the nanorods is ±5% of their mean value. In further embodiments, the size of the nanorods is ±2% of their mean value.
The width and/or length of the nanorods are further said to have a small standard deviation (σ) ranges. In some embodiments, the standard deviation (σ) of width and/or length of the nanorods in the sample is ±30% of their mean value (as defined herein). In further embodiments, the standard deviation (σ) of width and/or length of the nanorods is ±20% of their mean value. In further embodiments, the standard deviation (σ) of width and/or length of the nanorods is ±10% of their mean value. In further embodiments, the standard deviation (σ) of width and/or length of the nanorods is ±5% of their mean value. In further embodiments, the standard deviation (σ) of width and/or length of the nanorods is ±2% of their mean value.
The medium of the invention comprises a high yield of single crystalline nanorods. In other words, in the medium, the majority of nanorods are single crystalline nanorods with only a small portion of the nanorods or none of them are in an amorphous or polycrystalline or polymorphic form (phase).
In some embodiments, at least 70% of the nanorods are single crystals. In further embodiments, at least 80% of the nanorods are single crystals. In other embodiments, at least 90% of the nanorods are single crystals. In yet further embodiments, at least 95% of the nanorods are single crystals. In yet further embodiments, at least 98% of the nanorods are single crystals. In additional embodiments, between 95 to 99% of the nanorods are single crystals.
In some embodiments, the zinc chalcogenide nanorods are 2.5-20 nm in width and 5-500 nm in length.
The sample of nanorods substantially retains its characteristics even under various (one or more) treatments and/or applications (utilizations) such as precipitation steps, purification protocols (e.g., precipitation and re-dispersion in a clean solvent), ligand exchange, etc. In some embodiments, the sample may be subjected to illumination. The treatments and/or applications (utilizations) may be employed continuously or repetitively.
The medium of the invention is further characterized by comprising a plurality of nanorods produced by a process enabling control (tuning) of the nanorods size, length, diameter, and aspect ratio during the colloidal synthesis.
In another aspect, the invention provides medium comprising zinc chalcogenide nanorods obtainable by a process as disclosed herein above.
In a further aspect, the invention provides a medium of zinc chalcogenide nanorods obtained by a process as disclosed herein above.
The zinc chalcogenide quadrilateral nanostructures of the invention may be prepared, as described herein, from the following starting materials:
1. a mixture of zinc chalcogenide nanowires and one or more zinc chalcogenide nanowire monomer precursors;
2. zinc chalcogenide nanorods; and/or
3. zinc chalcogenide nanorods prepared according to the present invention.
The zinc chalcogenide quadrilateral nanostructure is characterized by a frame-like shape wherein each of two end facets of nanorods or nanowires are joined or fused so as to surround a space empty of the crystalline semiconductor material or material composing the nanostructure. It can contain ligands and/or solvent molecules. The quadrilateral nanostructure may be selected amongst a variety of four-sided substantially 2D nanostructures. Non-limiting examples include a square, a rhombus, a rectangle, a parallelogram, a trapezoid and a kite.
In some embodiments, the quadrilateral nanostructure is substantially a rectangle wherein at least two opposite faces, originating from the nanowires or nanorods, are parallel and/or have substantially the same length, width and/or aspect ratio.
Thus, the invention also provides zinc chalcogenide quadrilateral nanostructures, wherein each of the nanostructure four sides is of a zinc chalcogenide material, as defined hereinabove, and having the morphology and dimensions emerging from the starting material nanowires or nanorods.
As used herein with respect to the quadrilateral nanostructures, the precursors for making such systems may be any nanowires or nanorods as recited herein. As the quadrilateral nanostructures may also be prepared from other nanowires or nanorods, any known nanowire population or nanorod population may be utilized in their manufacture, as detailed herein.
Also as the methodology of manufacturing the zinc quadrilateral nanostructures may be extended to other metal chalcogenides starting from other metal chalcogenide nanowires or metal chalcogenide nanorods, the invention further contemplates metal quadrilateral nanostructures, the metal chalcogenide being selected from compounds of a metal with sulfur, selenium or tellurium or polonium. Exemplary metals include Ga, In, Ti, Sn, Pb, Bi, Zn, Cd, Hg, Cu, Ag, Au, Ni, Pd, Pt, Co, Rh, Ir, Fe, Ru, Os, Mn, Tc, Re, Cr, Mo, W, v, Nb, Ta, Ti, Zr, Hf, Sc and Y. Metal chalcogenides may be selected from CdS, CdSe, Sn2S6, Su2Se6, In2Se4, In2Te3, Ga2Se3, CuInSe2, Cu7S4, Hg3Se4, Sb2Te3, ZnS, ZnSe, ZnTe, AgS, AgSe, AgTe, Cu2S, Cu2Se, CuInS2, PbS, PbSe, PbTe ZnS, ZnSe and ZnTe.
In some embodiments, the metal is selected from Cd, Cu, Ag and Pb. The metal chalcogenide is thus selected from Cd-chalcogenides, Cu-chalcogenides, Ag-chalcogenides and Pb-chalcogenide.
Alternatively, the zinc nanorods and zinc quadrilateral nanostructures of the invention may be utilized as starting materials for the preparation of other metal chalcogenide nanorods and nanostructures according to the invention via cation exchange processes. Thus, the invention further contemplates a process for converting a zinc nanorod or zinc quadrilateral nanostructure, the process comprising treating a solution of zinc chalcogenide nanorods or quadrilateral nanostructures with a metal salt solution of under conditions permitting cation exchange and conversion of the zinc chalcogenide nanorod or nanostructure into the corresponding metal chalcogenide nanorod or nanostructure.
The nanorods or quadrilateral nanostructures of the invention may be utilized for a variety of electronic and optical applications, in different fields, such as lighting, flat panel displays, optics, biomedicine, solar energy and photocatalysis. In some embodiments, the nanorods are suitable for use in biomedicine. In further embodiments, the nanorods and/or quadrilateral nanostructures are used in medical imaging. In further embodiments, the nanorods and/or quadrilateral nanostructures are used in bio-tagging.
The invention also provides a device comprising the nanorods or quadrilateral nanostructure of the present invention. In some embodiments, the device is selected from a diode, a photodiode, a transmitter, a laser, a gain device, an amplifier, a switch, a marker, a bio-marker, a display, a large area display, liquid-crystal displays (LCDs), a detector, a photodetector, a sensor, a light emitting diode, a lighting system and a solar cell.
In order to better understand the subject matter that is disclosed herein and to exemplify how it may be carried out in practice, embodiments will now be described, by way of non-limiting example only, with reference to the accompanying drawings, in which:
A novel strategy is disclosed for synthesizing zinc chalcogenide quantum rods via a colloidal chemical synthetic approach Unlike the well-known growth mechanisms such as monomer attachment and particle coalescence often termed directed attachment, the formation of zinc chalcogenides quantum rods involves mass redistribution from their respective ultrathin long nanowires through the thermal-activated material diffusion. It is understood that the novel strategy is general and could be applied to other systems to fabricate anisotropic quasi-1D nanostructures.
The strategy of the invention uses a thermal-activated material diffusion approach to synthesize, e g , ZnSe, quantum rods by mass redistribution from their respective nanowire counterparts. Moreover, also demonstrated is the observation that this strategy can be applied to ZnS and ZnTe as well, and for synthesizing other quasi 1D colloidal nanostructures in nanorod form.
The synthetic approach is illustrated in the flowchart of Fig. IA. This strategy starts with the synthesis of ultrathin nanowires. In the second step, at an elevated temperature, the monomers dissolve into the solution from the end facets of the nanowires, which are the least stable region, and in the meanwhile grow onto the side facets of the nanowires, forming quantum rods via a self-ripening process.
ZnSe was used as an illustrative example for this strategy, to substantiate the proposed mechanism. The details of the synthesis of ZnSe nanowires are addressed herein. As demonsatrted, this synthetic approach produced nearly monodispersed ZnSe nanowires (
In the next step, the synthesis of ZnSe quantum rods was achieved, starting with long ZnSe nanowries (length=90±16 nm,
Starting with long ZnSe nanowires (length=90±16 nm, width=2.4±0 3 nm,
In addition to the sizing histograms on the width and length of the produced ZnSe quantum rods, those on the volume enabled a quantitative analysis to further support the mechanism of formation of ZnSe quantum rods from their nanowires (
The diameter of the final ZnSe quantum rods could be controlled by changing the reaction temperature. For a given nanowire synthesis, increasing the reaction temperature at this stage to 325° C. led to ZnSe quantum rods with an average diameter of 4 5 nm, compared to a diameter of 3 nm obtained when a temperature of 280° C. was used.
The synthesis of ZnSe quantum rods was also demonstrated starting with short ZnSe nanowires. For the synthesis starting with short ZnSe nanowires (length=45±14 nm, width=2.4±0 3 nm,
The XRD pattern (
Starting the synthesis of ZnSe quantum rods with the aged ZnSe nanowires, which have been kept in oleylamine at room temperature for 2-4 weeks, improved the size distribution of the produced ZnSe quantum rods (
High resolution TEM (HRTEM) measurements (
In addition to
To further demonstrate the generality of this methodology, it was employed to synthesize other zinc chalcogenides quantum rods, including ZnS and ZnTe, starting with their respective nanowires counterparts. ZnS (
Combining the results on the synthesis of ZnS and ZnTe quantum rods with those of ZnSe, it clearly demonstrated that the thermodynamically driven self-ripening based synthetic methodology was general and could successfully circumvent the limitation of the width control of quasi-1D nanocrystals imposed by alkylamines, generating zinc chalcogenides quantum rods with controlled aspect ratios.
Synthesis starting with a mixture containing both ZnSe nanowires and excess zinc precursor was also carried out. This synthesis was analogous to the purification and re-adding monomer approach used previously and which enableed control over the characteristics of the ZnSe nanorod couples. It was anticipated that the ripening of ZnSe nanowires would be inhibited in the presence of zinc monomer if the formation of quantum rods was based on a ripening process via the reaction solution.
The synthetic conditions were exactly the same as those addressed for the synthesis of ZnSe quantum rods, except that the starting material was a mixture containing both ZnSe nanowires and zinc oleylamine stock solution. As the reaction evolved for 10 minutes at 280° C., the diameter of the produced nanoparticles became slightly larger compared with that of the original ZnSe nanowires (
Self-assembly is a powerful bottom-up approach at the basis of supra-molecular and supra-nanocrystal chemistry, leading to formation of ordered self-assembled molecular monolayers, nanocrystal arrays and functional nanocrystal superstructures. Typically, self-assembly processes involve comparatively weak interactions between the components, such as hydrogen bonds and Van der Waals interactions, but this can also lead in a second step to covalently bound anisotropic nanostructures, as demonstrated in the growth of nanowires, rods, rings, sheets and platelets via a process of “oriented attachment”. In this mechanism, nanocrystals are formed first. Then, specific facets of the nanocrystals are attached via weak interactions. At a later stage, partial removal of the surface passivating ligands is followed by covalent bonding of two adjacent facets, leading to extended structures.
This type of powerful self-assembly mechanism is significantly and surprisingly expanded in the technology disclosed herein, to include a self-limited assembly process that leads to growth of “nanorod couples” combining precisely two anisotropic zinc chalcogenide nanorods or nanowires that fuse into a single nanostructure; the so called quadrilateral nanostructure of the invention. This self-limited process is attributed to the growth of the connecting twin structures between each two nanorod components, which reduces significantly the driving force for further reactions of a nanorod couple.
Nanorod couples present unique shape controlled properties and also provide a new platform for studying coupling effects in anisotropic rods, with relevance to applications in optics, photocatalysis and optoelectronic devices.
Single-crystal nanorod couples of ZnSe were synthesized by a high temperature colloidal chemical synthesis route.
The assignment of the observed structures to two connected rods is supported further by the high angle annular dark field scanning transmission electron microscopy (HAADF-STEM) characterization (
High-resolution TEM (HRTEM) characterization (
To study the nanorod couple growth mechanism, we characterized intermediate products by TEM and optical absorption spectroscopy. From this we propose the growth mechanism presented schematically in
During the early reaction stage, within the first 5 minutes at 230° C., a mixture of small and isolated ZnSe quantum dots and short rods was obtained (
ZnSe nanorod couples were obtained only when the temperature of the system was ramped up to 280° C. After 2 minutes at 280° C., the solution started to become turbid and the TEM image showed a mixture of nanorod couples and thin rods (
The end facets of the nanorods are more reactive compared to the side walls usually providing preferential elongation. At the lower temperature, the directed attachment process forming nanorods depletes the isolated dots and short rods from the reaction medium. Further directed attachment of rods to rods is then limited by the steric hindrance stopping the growth along the long axis via this process. Increasing the temperature of the system to 280° C. leads to the rod-couple formation, since the lability of the passivating ligands at the rod apexes is increased. This allows for reactivity of the apexes with the excess unreacted monomers growing onto these end facets, forming the connecting twin structures between the two nanorod components of a nanorod couple. Once the connections are formed, the driving force for further reactions of the rod couple is reduced significantly due to the presence of the thicker and more stable end portions. This provides the basis for the self-limited assembly process.
To further establish the mechanism proposed above and to provide additional control over the rod couples characteristics, a slightly different approach was employed for their synthesis. In this approach, purified ZnSe long nanorods were used and compare two experiments - one was conducted with adding zinc and selenium precursors while the other was carried out without them (
These comparative experiments clearly demonstrate that the unreacted monomers play a crucial role in the stabilization of the ZnSe long nanorods and also act as material sources for the fusion of ZnSe rods into rod couples. These results provide strong additional evidence for the proposed mechanism of formation of nanorod couples. This purification and re-adding monomer approach also can be used to gain further control over the nanorod couple characteristics as will be demonstrated below.
To create the rod couples structure, two rods need to couple together for the connection reaction to take place. The dipole-dipole (D-D), crystal-crystal (C-C), and ligand-ligand (L-L) interactions that are involved in the self-assembly of the nanorod couples from individual nanorods in solution were calculated (
The observed 2.1 nm spacing between the two rods within the couples is consistent with this explanation, considering that the side walls of ZnSe nanorods are densely packed by oleylamine capping ligands and are significantly less reactive compared with the end facets. The length of the surface ligands of two nanorod components of a nanorod couple leads to the observed spacing which is close to the length of an oleylamine ligand molecule. This offers also a route to control the rod distance within the rod-couples by using different ligands type and length. This is demonstrated by carrying out the ZnSe nanorod couples synthesis with other alkylamines including octadecylamine (ODA) and hexadecylamine (HDA) which also produced ZnSe nanorod couples (
The unique transition from single rods structure to rod couples leads to a significant change in the system's geometry, which is manifested in the envelope wave functions of the charge carriers and in the energy levels structure. In order to study the electronic structure of coupled rods, and in particular to probe the charge carriers' distribution throughout the nanoparticles, a finite well effective mass approximation approach was solved numerically for a frame architecture of appropriate dimensions, with the diameter of the short connecting arms larger than the rod components.
The wave functions of the band-edge states are predominantly confined to the short arms of the rod couples in accordance with their larger diameter. This leads to a red shift by ˜0.35 eV of the calculated band gap transition in the rod couple compared with the isolated rods. This is consistent with the observed red-shift in the absorption onset upon rod couple formation. Note that in rod couples there are two close lying edge states with either similar or opposite phases at each end. Even for a model of rod couples with the same diameter of the short and long arms, these were found to be the lowest lying states.
The higher excited states of the rod-couples occupy mostly the long edges of the structure, they resemble states in nanorods. However, unlike in nanorods, the wave functions in the two parallel rod couples can be either of similar phase (symmetric with respect to the yz plane), or of opposite phase (antisymmetric with respect to the yz plane). The symmetric and antisymmetric states are almost degenerate; indicating that within this model that includes a high potential barrier at the surface, coupling between the two arms is relatively low. However, in order to address the coupling more accurately, factors such as Coulomb interactions and level mixing should be taken into account, which are beyond the scope of the model used here.
The level structure points out to a distinct change in the polarization characteristics of the nanorod couples compared with rods. Because the band-edge state of the rod couples is a short-edge state, while in the single rod systems it is a long-edge state, a significant decrease in the photoluminescence polarization is expected to occur in these systems with respect to single nanorods. In order to measure the polarization of rod couples and nanorods, single particle photoluminescence polarization measurements were performed on ZnSe/CdS core/shell nanorod couples and ZnSe/CdS nanorods that were over-coated in a similar manner A few layers of CdS were grown in order to eliminate surface traps and to increase the emission quantum yields. TEM and HRTEM measurements (
Typical polarization dependence for single rod versus single rod couple is presented in
The synthetic procedure for ZnSe nanorod couples is based on an environmental compatible phosphine-free colloidal method prepared via a self-limited assembly process. There are various routes to achieve further control over the rod couples characteristics, leading to control over their properties, as illustrated in
In summary, a novel type of colloidal nanostructure, nanorod couple, formed via a self-limited self-assembly mechanism is provided. In this mechanism, initially, directed attachment leads to growth of nanorods. When this process saturates, raising the reaction temperature leads to formation of a rod couple consisting of precisely two nanorods connected by twinning structures. Upon the growth of the connecting regions, further reactivity is hindered providing a self-limited growth process. Furthermore, the electronic and optical properties are directly modified by the nanorod couple morphology leading to reduced emission polarization compared to nanorods. Using purified rods while adding proper precursors to form the rod couples in a second stage, opens the path also to realize rod-couples heterostructures with different composition of the short connecting arms (
Chemicals. Zn(NO3)2.6H2O (99%), zinc diethyldithiocarbamate (97%), ZnCl2 (99.995%), lithium triethylborohydride (1 M in tetrahydrofuran), cadmium (II) oxide (>99.99%), lead acetate trihydrate (99.999%), oleic acid (technical grade 90%), 1-Octadecene (ODE, technical grade, 90%), trioctylphosphine (TOP, 90%), trioctylphosphine oxide (TOPO, 99%), octadecylamine (ODA, 97%), hexadecylamine (HDA, 98%), chloroform (99% anhydrous), toluene (99% anhydrous) and methanol (99.8% anhydrous) were purchased from Sigma Aldrich. Selenium powder (99.999%) and tellurium powder (99.999%) were purchased from Strem Chemicals Inc. Oleylamine (approximate C18-content 80-90%) was purchased from Acros. Octadecylphosphonic acid (ODPA) and hexylphosphonic acid (HPA) were purchased from PCI Synthesis. All chemicals were used as received without further purification.
Instrument Specifications & Sample Preparation
UV-visible-near IR absorption spectroscopy: UV-Visible-Near IR absorption spectroscopy was performed on a JASCO V-570 spectrometer using quartz cuvettes.
Powder x-ray diffraction (XRD) patterns: XRD patterns were obtained using Cu Kα photons from a Phillips PW 1830/40 diffractometer operated at 40 kV and 30 mA. Samples were deposited as a thin layer on a low-background scattering quartz substrate.
Electron microscopy measurement: Transmission Electron Microscopy (TEM) grids were prepared by depositing one drop of a solution of purified nanoparticles onto a standard carbon coated grid. TEM was performed using a Tecnai G2 Spirit Twin T-12 transmission electron microscope with a tungsten filament running at an accelerating voltage of 120 keV. High Resolution Transmission Electron Microscopy (HRTEM) was performed using a Tecnai F20 G2 high resolution transmission electron microscope running at an accelerating voltage of 200 keV with a field emission gun as an electron source. This microscope was also used for the high angle annular dark field scanning transmission electron microscopy (HAADF-STEM) measurements.
Scanning electron microscopy (SEM) analysis: Samples for SEM measurement were prepared by dipping a piece of silicon wafer into a toluene solution containing nanorod couples such that the solution-substrate contact line sweeps down along the substrate slowly during the evaporation process'. Images were taken using Magellan (TM) 400L extra high resolution scanning electron microscope (XHR-SEM). The XHR-SEM was operated at an acceleration voltage of 1 KeV and a landing energy of 500 V to 50 V (by applying a positive bias to the stage). Samples were exposed to short cycles of oxygen plasma, using the built-in plasma cleaner, to remove organic contamination and improve image contrast.
Atomic force microscopy (AFM) analysis: AFM analysis of nanoparticles was carried out with a Nanowizard 3 AFM on quantitative imaging (QI) mode (JPK Instruments). Silicon nitride cantilevers (Appnano HYDRA AFM probes) with a resonance frequency of 49.8±0.1 kHz (in air) and an average spring constant of k=0.39±0.03 N/m (as determined by the thermal noise method) were used. Nanoparticles were imaged using the QI mode, which minimizes shearing forces acting on the sample and thus avoids dislocation of the nanoparticles by the tip.
Single particle photoluminescence polarization measurements: A dilute solution of purified nanoparticles in toluene is spin-coated onto a clean microscope cover glass. Excitation of the sample for photoluminescence measurements was done using an unpolarized light emitting diode (LED) at 470±20 nm (Prizmatix) in an Epi-illumination configuration and focused through a high numerical aperture oil immersion objective (X100 1.4 N.A. - Nikon). Photoluminescence emission is collected through the same objective, filtered spectrally and then passed through a rotating half wave plate which rotates the polarization vector of the emission. Following this, the emitted light passes through a polarizing beam displacer, that splits the light into two perpendicularly polarized beams (horizontal and vertical) and shifts them spatially one with respect to the other. The images of the two polarizations are collected simultaneously using an electron multiplying charge coupled device (EMCCD, Andor iXon3), yielding significant improvement in the signal to noise ratio for the polarization determination. The intensity of both polarization components is extracted from the different pairs of images, and the experimental polarization at different rotation angles of the half wave plate is calculated according to P=(Ill−I⊥)/(Ill+I⊥). These values are well fitted by a sinusoidal function which yields the degree of polarization for each particle. Measurements were performed under slow Ar flow for improved stability.
Synthesis of ZnSe nanowires. In a typical synthesis, 0.2 mmol (59.5 mg) Zn(NO3)2.6H2O and 10 mL oleylamine were mixed in a three-neck flask. The mixture was degassed and refilled with Ar three times at room temperature and then heated to 110° C. and kept at this temperature for 0.5 hr. At 160° C., 2 mL 0.1 M Se oleylamine solution was injected into the flask. After the injection, the temperature was set at 120° C. and the mixture was degassed for 10 minutes. Then the temperature was raised up to 230° C. in 6 minutes. After 20 minutes at 230° C., the reaction was quenched by removing the heating mantle
The synthesis of ZnSe nanowires were also carried out according to the above description with some modifications, such as: (i) variety of Zn:Se ratios; (ii) after degassing step, heating to 110° C. for up to 2 hr; (iii) omitting the step of setting the temperature to 120° C. after injection; (iv) the selenium solution is injected at different temperatures: 160° C. or 200° C. or 230° C. or 260° C.
Synthesis of ZnS nanowires. In a typical synthesis, 0.05 mmol (18 mg) zinc diethyldithiocarbamate and 10 mL oleylamine were mixed in a three-neck flask. The mixture was degassed and refilled with Ar three times at room temperature then it was heated to 110° C. and kept at this temperature for 0.5 hr. Then the temperature was raised up to 230° C. in 6 minutes from 110° C. After 20 minutes at 230° C., the reaction was quenched by removing the heating mantle
Synthesis of ZnTe nanowires. 0.2 mmol (27.3 mg) ZnCl2 and 10 mL oleylamine were mixed in a three-neck flask. The mixture was degassed and refilled with Ar three times at room temperature then it was heated to 110° C. and kept at this temperature for 0.5 hr. 0.5 M tellurium stock solution was prepared by dissolving tellurium powder into TOP at 280° C. 0.4 mL 0.5 M tellurium solution was mixed with 0.34 mL lithium triethylborohydride (1 M in tetrahydrofuran) and 1 mL oleylamine in the glove box and then the mixture was injected into the flask at 160° C. After the injection, the temperature was set at 120° C. and the mixture was degassed for 10 minutes. Then the temperature was raised up to 230° C. in 6 minutes from 120° C. After 20 minutes at 230° C., the reaction was quenched by removing the heating mantle
The synthesis of ZnSe nanowires were also carried out according to the above description with some modifications, such as: (i) use of 0.2 mmol (59.5 mg) Zn(NO3)2.6H2O instead of 0.2 mmol (27.3 mg) ZnCl2; (ii) Te stock solution was prepared by dissolving Te powder into trioctylphosphine (TOP) in the presence of lithium triethylborohydride (superhydri de).
Purification of zinc chalcogenides nanowires. The produced zinc chalcogenides nanowires crude solution was dissolved into chloroform and precipitated by adding methanol with the aid of centrifugation.
Aging of ZnSe nanowires. After the purification, ZnSe nanowires were redissolved into oleylamine and then the reaction solution was kept in the glove box at room temperature for 2-4 weeks prior to the synthesis of ZnSe quantum rods.
The aging of ZnSe nanowires were also carried out by redissolving purified ZnSe nanowires were redissolved into oleylamine and/or chloroform.
Synthesis of zinc chalcogenides quantum rods. Purified zinc chalcogenides nanowires were redissolved in oleylamine in a three-neck flask. The reaction mixture was degassed and refilled with Ar three times at room temperature. Then it was heated gradually (at a rate of 5-30° C./minute) to 110° C. and kept at this temperature for 10 minutes. Then the temperature the reaction solution was raised up gently (at a rate of 5-30° C./minute) to 280° C. in 10 minutes and kept at this temperature for 5-120 minutes. Aliquots were taken from time to time. The reaction was terminated by removing the heating mantle
The synthesis of zinc chalcogenides quantum rods were also carried out according to the above description with some modifications, such as: (i) chloroform was added to the solution of ZnSe nanowires in oleylamine in order to assist their solubilization in oleylamine; (ii) The reaction solution temperature (ripening temperature) was 290° C. or 305° C. or 325° C.
Preparation of zinc precursor stock solution. 0.067 M zinc stock solution was prepared by dissolving 0.2 mmol (27.3 mg) Zn(NO3)2.6H2O and 10 mL oleylamine in a three-neck flask. The mixture was degassed and refilled with Ar three times at room temperature then it was heated to 110° C. and kept at this temperature for 0.5 hr.
ZnSe Nanorod Couple Synthesis
The synthesis of ZnSe nanorod couples was carried out under inert atmosphere using standard Schlenck techniques. In a typical synthesis, 0.067 M selenium stock solution was prepared by dissolving 2 mmol (159 mg) selenium powder in 30 mL oleylamine at 220° C. Zn(NO3)2.6H2O (0.2 mmol, 59.5 mg) and oleylamine (15 mL) were added to a three-neck flask (50 mL). The mixture was placed under vacuum and purged with argon three times and then heated to 110° C. under vacuum and kept at this temperature for 1 hr. At 160° C., 3 mL selenium solution (0.067 M) was swiftly injected into the flask. After the injection, temperature was set at 120° C. and the mixture was degassed for 10 minutes at this temperature. Then the solution was heated up to 230° C. in 7 minutes and stabilized at this temperature for 20 minutes. The mixture was then heated up to 280° C. in 4 minutes and the solution became turbid in 3 minutes. The nanocrystals were allowed to grow for 15 minutes at 280° C. After cooling to 80° C., the crude reaction mixture was diluted with chloroform and oleic acid with a volume ratio of 4:1. Methanol was added in order to precipitate the nanocrystals with the aid of centrifugation, removing excess of organic materials and unreacted monomers.
ZnSe/CdS Core/Shell Nanorod Couples and Nanorods Synthesis
In a typical synthesis, trioctylphosphine (TOPO 2.0 g), octadecylphosphonic acid (ODPA 75 mg), hexylphosphonic acid (HPA 10 mg) and CdO (15 mg) were added to a three neck flask (50 mL). The mixture was placed under vacuum and purged with argon three times and then heated to 150° C. for 0.5 h under vacuum. The solution was heated under an argon atmosphere, to above 320° C. until it became colorless. Then the mixture was heated to 350° C. and 3 mL TOP was swiftly injected into the flask. After the temperature was stabilized at 365° C., a TOP (1.5 mL) solution containing ZnSe nanorod couples or nanorods (1×10−9 mol) and sulfur (30 mg) was injected into the flask. After the injection, the nanocrystals were allowed to grow for 30 seconds. The reaction was terminated by removing the heating mantle After cooling to 80° C., the crude reaction mixture was diluted with toluene. Methanol was added in order to precipitate the nanocrystals and remove excess surfactants.
Cation Exchange Procedures
From ZnSe to CdSe: 0.1 M cadmium oleate stock solution was prepared by dissolving CdO (0.32 g, 2.5 mmol) into a mixture of oleic acid (6.94 mL) and octadecene (ODE 18 mL) at 220° C. Cleaned 1.34×10−9 mol (containing 2.1×10−5 mol Zn2+) ZnSe nanorod couples were dissolved into anhydrous chloroform and then the solution was injected into 5 mL oleylamine solution in a three neck flask. The mixture was degassed at 110° C. for 10 minutes, and then it was heated up to 220° C. When the temperature was stabilized, 0.6 mL cadmium oleate stock solution (0.1 M) was swiftly injected into the flask while stirring. The solution in the flask was gradually changed from colorless to bright yellow and finally to yellow. After 25 minutes at this temperature the heating mantle was removed and the mixture was cooled down to room temperature.
From ZnSe to PbSe: 0.05 M lead oleate stock solution was prepared by dissolving lead acetate trihydrate (0.38 g, 1 mmol) in a mixture of oleic acid (0.88 mL) and ODE (19.12 mL) at 180° C. Purified 1.34×10−9 mol (containing 2.1×10−5 mol Zn2+) of cleaned ZnSe nanorod couples was dissolved into anhydrous chloroform and then the solution was injected into 5 mL oleylamine in a 20 mL vial sealed with a septum. After purging argon through the vial for 5 minutes, 0.8 mL lead oleate stock (0.05 M) solution was injected into the vial at room temperature. The colorless solution changed to dark brown at about 120° C. in 10 minutes. The solution was cooled down to room temperature.
Zinc stock solution preparation: 0.067 M zinc stock solution was prepared by dissolving 2 mmol (59.5 mg) Zn(NO3)2.6H2O in 30 mL oleylamine at 110° C.
Purification and re-adding monomer approach: This approach started with purified ZnSe long nanorods. The synthesis of ZnSe long nanorods is similar to that addressed in the Method in the main article (ZnSe nanorod couple synthesis). In a typical synthesis, Zn(NO3)2.6H2O (0.2 mmol, 59.5 mg) and oleylamine (15 mL) were added to a three-neck flask (50 mL). The mixture was placed under vacuum and purged with argon three times and then heated to 110° C. under vacuum and kept at this temperature for 1 hr. At 160° C., 3 mL selenium solution (0.067 M) was swiftly injected into the flask. After the injection, temperature was set at 120° C. and the mixture was degassed for 10 minutes at this temperature. Then the solution was heated up to 230° C. in 7 minutes and stabilized at this temperature for 20 minutes. Then the reaction was quenched by removing the heating mantle Then the long rods crude solution was purified, wherein it was diluted with chloroform and precipitated by methanol with the aid of centrifugation, in order to remove the unreacted monomers. Next, the purified ZnSe long nanorods (-3×10−-8 mol) were re-dissolved into 15 mL oleylamine solution into a three-neck flask. 1 mL 0.067 M zinc oleylamine and 1 mL 0.067 M selenium oleylamine stock solutions were added into the flask at room temperature. Then the reaction solution was gradually heated up to 280° C. in 15 minutes and stabilized at this temperature for 30 minutes. The reaction was quenched by removing the heating mantle
ZnSe nanorod couples synthesis using other alkylamines: The synthetic conditions of ZnSe nanorod couples using other alkylamines, such as ODA and HDA, are exactly the same as those using oleylamine except that the ODA or HDA solvent is used, rather than oleylamine
Reactions at Higher Temperatures above 280° C.
The synthesis was conducted at 300° C. and 320° C., below the boiling point of the oleylamine. TEM analysis (
Nanorod Couples Formed by the Purification and Re-Adding Monomer Approach
We performed two parallel comparative experiments starting with purified ZnSe long nanorods, one is conducted with adding the zinc and selenium monomers and the other is carried out without those monomers. In one of the experiment starting with purified ZnSe long nanorods (-3×10−8 mol) (
These comparative experiments clearly demonstrate that the unreacted monomers play a crucial role in the stabilization of the ZnSe long nanorods and also act as material sources for the fusion of ZnSe rods into rod couples. These results provide strong additional evidence for the proposed mechanism of formation of the nanorod couples.
Energetic Considerations for Interactions between Two Nanorods
Three types of interactions were considered to drive this initial pairing, including dispersion interactions between the crystal-crystal (C-C) and the ligand-ligand (L-L), as well as the dipole-dipole interactions between two rods (D-D).
The rod-rod dispersion interactions were calculated numerically. The crystalline core is treated as a cylindrical rod with the appropriate length and diameter (90×2.8 nm), and is coated by a ˜2 nm thick oleylamine shell. We use the expression:
where A is the appropriate Hamaker constant for the interaction being considered. The Hamaker value used for ZnSe is 1 eV3. For oleylamine, we used 0.34 eV.
Using this methodology and the values quoted above, the energetic contributions for the crystal-crystal (C-C) and ligand-ligand (L-L) dispersion interactions were found to be 0.050 eV and 0.53 eV, respectively, or around 1.1 kBT/11.2 kBT (@ 280° C.).
Regarding the D-D interaction, fairly large dipole moments are intrinsic to the wurtzite crystallographic lattices of CdSe and ZnSe due to the lack of inversion symmetry in these nanocrystals. The permanent dipole moment in nanorods has been shown to scale with the volume. We consider uniform distribution of point dipoles inside the nanorod. Dipole-dipole interactions for nanorods oriented antiparallel were calculated by numerically integrating the dipole distribution over the volumes V1,2 of both nanorods using:
where {circumflex over (μ)}1,2 are unit vectors along the c axis of the nanorods, {circumflex over (r)}1,2 are the positions of the point dipoles inside the nanorods, {right arrow over (r)}={right arrow over (r)}1−{right arrow over (r)}2, {circumflex over (r)}={right arrow over (r)}/r and r=|{right arrow over (r)}|. We use oleylamine6 (dielectric constant of ˜2) as both solvent and capping layer. Assuming a permanent dipole moment similar to that of CdSe (ρ=0.55 Debye/nm3)4,5,7 and a volume of 550 nm3, we calculate a dipole moment of 305 Debye per ZnSe nanorod. Therefore, the energetic gain from pulling together two opposite dipole moments from infinity to ds=2.1 nm (
ZnSe Nanorod Couples Synthesis using other alkylamines—Control over Inter-Rod Distance
We have employed the ZnSe nanorod couples synthetic route with other alkylamines, including ODA and HDA, instead of oleylamine (
Electronic Structure Calculation
In order to study the electronic structure of the ZnSe nanorod couples, and in particular to compare them to that of nanorods of similar length and diameter, we utilized a finite well effective mass approximation (EMA) approach. Within the EMA, the excited charge carrier confined to the particle is modeled as a particle in a box. Under this approximation, the Schrodinger equation for the electron (hole) envelope wave functions, φa, is defined as
where h is the reduced Planck constant, ma* is the reduced mass and Va is the potential energy exerted on the charge carrier in the medium. The total exciton energy is approximated by
E=E
bg
+E
e
E
h (4)
where Ebg is the bulk's band gap. The potential energy of the charge carriers within the particle is taken as zero. The potential energy outside the particle, which determines the height of the well's wall, was set to Vligands=[ELH(ligands)−Ebg(ZnSe)]/2, where ELH (ligands) is the energy difference between the LUMO and HOMO energies of the ligand. For oleylamine, ELH (ligands)=4.430 eV . In our calculations we neglected the Coulomb interaction term which is not easily obtained for elongated systems, and may further shift the exciton's energy.
Due to the relatively complex geometric structure of the nanorod couples, the solution for Schrodinger equation cannot be obtained analytically, and thus the electron and hole wave functions, co, and (Oh respectively, were solved numerically in a finite element numerical approach using the COMSOL software. Only few theoretical calculations and experimental measurements were performed regarding wurtzite ZnSe, and as a result the values of both the band gap for wurtzite ZnSe and for the effective masses of electrons and holes in the literature are quite scattered. The hole states correspond to the heavy hole, which dominates the valence band-edge states in this system.
Comparison between the electronic structure of nanorod couples and single nanorods was obtained for systems of similar dimensions. For both systems, particle length was set to 90 nm and rod diameter (long edge) to 2.8 nm The short edge diameter was set to 3.7 nm and the spacing between the two rods constructing the rod couples to 2.1 nm All geometric parameters were set according to the dimensions extracted from TEM images. The particles were embedded in an environment of organic material, with wave functions set to zero at the boundaries. The environment dimensions were increased until the difference in eigenvalues was lower than 10−4 eV, omitting boundary artifacts on the solution.
The band-edge states for both valence and conduction bands states are predominantly confined to the corners of the rod couples. Higher states are related to the “long edge” of the particles, and are corresponding to the single nanorod states. Due to the proximity of the corners connected by the short edge, the strong overlap between the wave functions confined in these corners results in the formation of “bonding” and “antibonding” short edge states. While both “bonding” and “antibonding” are obtained as the lowest states of the valence band, in the conduction band the “antibonding” state has a much higher energy due to the low effective mass of the electrons.
It should be accentuated that the model described above yields only a first approximation for the accurate energy values. In order to provide a more detailed picture of the electronic structure, including hole state mixing, electronic fine structure, and dipole moment induced effects, a more complex modeling is required, which is beyond the scope of the calculation described above.
Structural Characterization of ZnCdSe/CdS Nanorod Couples and Nanorods, and their Optical Spectroscopy
In order to increase the emission quantum yield of the systems and eliminate surface traps, ZnSe nanorod couples were reacted with Cd and S precursors at a high temperature using a seeded growth approach. TEM images provide evidence that after the reaction the dimensions of both the nanorod couples and nanorods were increased in comparison with their respective original counterparts. The spacing between each two nano-components of the nanorod couples is evident, indicating that the nanorod couple structural features are preserved upon the reaction.
The absorption spectra of the obtained nanorod couples and nanorods show a large red shift compared with the respective original ZnSe particles. This is attributed to a partial cation exchange, forming alloyed structure of ZnCdSe followed by the formation of a thin CdS shell. The nanoparticles have sharp absorption excitonic features, suggesting a relatively narrow size distribution, as was also confirmed by the TEM measurement. The obtained ZnCdSe/CdS nanorod couples and nanorods show sharp emission peaks associated with band gap transitions without significant trap state emissions.
HRTEM images and XRD of ZnCdSe/CdS nanorod couples and nanorods HRTEM images show that both ZnCdSe/CdS nanorod couples and nanorods preserve the respective distinct structural features upon reaction with Cd and S. The angles of the (002) and (110) peaks in the XRD patterns of the ZnCdSe/CdS nanorod couples and nanorods are slightly shifted to lower angle compared with the angles for CdS, which again indicates that a partial cation exchange process from ZnSe to CdSe takes place during the reaction with Cd and S, accompanied by thin CdS shell growth.
Control of the Nanorod Couples Features
I) Diameter control of the short arms of the nanorod couples: the diameters of the short arms of the rod couples can be tuned by the control of the amount of zinc and selenium precursors and the reaction time for short arm growth at 280° C. Nanorod couples were formed by ZnSe long nanorod purification and re-adding monomer approach.
After initial fusing of the two nanorods at 280° C., additional monomers were added into the reaction solution and they grow onto the short arms of the nanorod couples, making the short arms much thicker than the long arms, as evidenced by the TEM images wherein better contrast of the short arms of the nanorod couples is observed.
II) Diameter control of the long arms of the nanorod couples is performed by the purification and re-adding monomer approach, as described in another parallel comparative experiment in the absence of zinc and selenium monomers. Nanorod couples formed by ZnSe long nanorod purification and re-adding monomer approach. ZnSe nanorods with desirable diameter were produced with the control of reaction time at 280° C. in the absence of zinc and selenium monomers. Starting with ZnSe nanorods with large diameters, the purification and re-adding monomer approach produced nanorod couples with large diameter of the long arms.
III) Length control of the long arms of the nanorod couples: This can be tuned by choosing ZnSe nanorod with different lengths, wherein the length control of the ZnSe nanorods is successfully achieved by tuning the reaction time for growth at 230° C. Starting with ZnSe nanorods with different lengths, the purification and re-adding monomer approach can produce ZnSe nanorod couples with controlled lengths.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/IL2014/050591 | 7/1/2014 | WO | 00 |
| Number | Date | Country | |
|---|---|---|---|
| 61841628 | Jul 2013 | US | |
| 61921663 | Dec 2013 | US |