This invention relates generally to waterproof coating systems, and more particularly to a coating system that changes color in response to ambient temperature changes to assist in the heating or cooling of underlying structures as well as ascertaining defects in the underlying structures.
Exterior coatings are exposed to the vicissitudes of weather from the very moment they are applied to protect an exterior surface. Water-based coatings are favored over solvent borne coatings for a number of well known reasons. They offer ease of application, reduced toxic solvent emission, lower raw material and application costs, and easy cleanup of site and equipment.
In more recent years, white water-based coatings have become extremely popular and in some areas are required due to their ability to protect a roof against excessive temperatures by reflecting solar radiation, to thereby significantly reduce cooling costs of the underlying building. The temperature of the roof surface is dependent on its ability to reflect solar energy (solar reflectance), absorb solar energy (solar absorbance) and to release absorbed energy in the form of infrared radiation (emissivity). The peak surface temperature of the roof strongly depends on the peak solar radiation and the solar reflectance of the surface, and the ability to remove heat from the roof depends on its emissivity. On a sunny day in August in California, with an ambient temperature of 90° as shown in
Although white reflective roof coatings are ideal for summer conditions, they also block much desired solar radiation during cooler periods. In some areas, relatively hot day-time temperatures are replaced by relatively cool night-time temperatures. Although it may be desirous to seasonably or even daily replace the roof surface from reflective white to absorptive black depending on the ambient temperature, such a practice would be impractical to implement and extremely expensive.
In an effort to provide a color-changing roof surface, U.S. Pat. No. 6,500,555 to Khaldi and Japanese Laid-Open Application No. 08-226211 to Sumiko disclose laminates of thermochromic material that can be adhered to the roof of a building. Such laminates become light in color to stop absorption of solar heat as the temperature rises and become dark in color to absorb more solar heat as the temperature falls. However, the inelastic nature of such laminates (the Khaldi patent for example discloses an aluminum foil base) do not lend well to large roof areas where expansion and contraction of the underlying structure due to extreme temperature fluctuations, wind or other weather conditions may occur. In addition, the provision of separate laminates are not only difficult to store, transport and lift to the roof surface, they also must be manually installed with roof-penetrating mechanical fasteners and/or adhesives and joined together at their seams through appropriate sealers, thus increasing the amount of material, time and labor for installing such laminates. Such systems are also prone to leakage and separation, especially during extreme weather conditions. It would therefore be desirable to provide a seamless, stretchable color changing membrane that can be directly applied to the roof surface, including any pre-existing roof materials and roof-related equipment or features, without the use of mechanical fasteners, adhesives or joints.
Another challenge associated with thermochromic materials is their normally quick deterioration when exposed to ultraviolet (UV) rays. Although a clear top layer would be desirable to maximize the effectiveness of the lower thermochromic layer, many materials with UV blocking or absorbing additives are unfortunately too opaque to allow effective use of the thermochromic layer.
In order to further minimize costs for heating and cooling buildings or other structures, an infrared scanner can be used to determine underlying areas where moisture may accumulate, since such areas are typically at a lower temperature than the surrounding roof surface, as well as areas of missing or inadequate insulation. However, such scanners can be expensive, have a limited field of view, and require significant labor to operate, especially over large area roofs on manufacturing buildings or the like. It would therefore be desirable to readily detect, without the aid of infrared scanners or the like, one or more defects in an underlying structure.
According to one aspect of the invention, a method of passively heating or cooling an underlying structure includes applying a solar reflective base layer over the underlying structure to form a first seamless membrane; applying a color changing layer over the base layer to form a second seamless membrane that is contiguous with the first seamless membrane, the color changing layer having a clear state above a first transition temperature and an opaque state below a second transition temperature; reflecting radiant energy from the base layer by exposing the color changing layer to a temperature above the first transition temperature to thereby prevent absorption of heat into the underlying structure; and absorbing radiant energy into the base layer by exposing the color changing layer to a temperature below the second transition temperature to thereby heat the underlying structure.
According to a further aspect of the invention, a coating system for assisting in the heating or cooling of an underlying structure includes a first seamless, elastic membrane comprising a solar reflective material and a second seamless, elastic membrane that is contiguous with the first membrane. The second membrane has a color changing material with a clear state above a first transition temperature to thereby permit transmission of solar radiation to the first membrane and an opaque state below a second transition temperature to thereby absorb radiant energy.
According to yet a further aspect of the invention, a method of detecting defects in a structure includes applying a layer of thermochromic material to the structure; observing a localized area of non-uniform color associated with the thermochromic layer; and ascertaining whether a defect is associated with the localized area.
The foregoing summary as well as the following detailed description of the preferred embodiments of the present invention will be best understood when considered in conjunction with the accompanying drawings, wherein like designations denote like elements throughout the drawings, and wherein:
It is noted that the drawings are not necessarily to scale and are only intended to depict typical embodiments of the invention. Accordingly, the drawings should not be considered as limiting the scope of the invention. The invention will now be described in greater detail with reference to the accompanying drawings.
Referring to the drawings, and to
The base layer 14 preferably comprises a thermally insulative flexible material such as a water-based acrylic elastomer with a relatively high solar reflectivity value and a relatively high heat emittance value for maximum effectiveness. The high solar reflectivity value may be obtained by adding metal oxides to the acrylic elastomer. Preferably, the base layer material is substantially white in color to maximize solar reflectivity. However, it will be understood that the base layer may be of any other color and/or shade with varying degrees of effectiveness. The base layer is also preferably formulated to have a high elasticity to accommodate expansion and contraction of the underlying structure, laminates, coatings and other materials through extreme hot and cold temperature cycles. A suitable single component material with the above-described features is supplied by Neptune Coatings Corp. of Grass Valley, Calif. under the trademark Reflex®. Such a material may be cured at room temperature and is capable of reflecting over 90% of impinging solar radiation when provided in white or beige colors and up to about 50% when provided in darker colors.
It will be understood that a wide variety of different colors, tints, shades, materials, metal oxides and/or other heat reflecting additives may be used for the base layer 14. By way of example, and without limitation, water-based or oil-based single or two-part polymers such as epoxies, polyurethanes, silicones, styrene butadiene, polyvinyl acetate, bituminous or polymer-modified bituminous materials, and so on, containing aluminum pigments, ceramic nano-particles, glass, ceramic or polymeric micro-spheres, extender pigments with low conductivity such as calcined clay, radiation reflective metal oxides such as red iron oxide, titanium oxide or silver oxide, various combinations thereof, as well as any other material or combination of materials and additives that assist in reflecting the sun's radiant energy and/or emitting absorbed energy from the base layer 14.
The color changing layer 16 preferably comprises a flexible thermochromic material that is located between the source of solar radiation and the base layer 14. The color changing layer 16 preferably changes color between a substantially clear (translucent or transparent) condition over a predetermined temperature range to thereby passively expose the base layer 14 to solar radiation above a first transition temperature, and an opaque condition at a second transition temperature below the first transition temperature to thereby passively conceal the base layer 14 below the second transition temperature. Depending on the particular formulation of the thermochromic material, it is contemplated that the first and second transition temperatures may be substantially equal. When the base layer 14 is constructed of an acrylic elastomer, the color changing layer 16 preferably comprises a thermochromic ink, such as a micro-encapsulated leuco dye material, in a clear polyvinyl acrylic emulsion polymer. For maximum effectiveness, the color changing layer 16 is preferably substantially black in color below the first temperature and substantially clear above the second temperature so that effective heating and cooling of the structure 12 can be enhanced. As with the base layer 14, the color changing layer 16 is also preferably formulated to have a high elasticity to accommodate expansion and contraction of the underlying structure, laminates, coatings and other materials through extreme hot and cold temperature cycles.
By way of example only, when the temperature of the ambient air and/or structure 12 is above approximately 66° F. (19° C.), the layer 16 is substantially clear to expose the base layer 14 to the sun's radiant energy. Likewise, when the temperature of the ambient air and/or structure 12 is below about 52° F. (11° C.), for example, the layer 16 is substantially opaque to absorb the sun's radiant energy. It will be understood that the color changing layer 16 can be formulated for other temperature ranges, such as between 68° F. and 84° F., 72° F. and 88° F., and so on, and/or for shorter or longer temperature ranges, since the ideal temperature or temperature range for one location may be different than the ideal temperature or temperature range for another location due to local seasonal conditions and variations.
It will be further understood that the color changing layer may be constructed of a wide variety of different formulations and colors. For example, different coating products such as lacquers, enamels, epoxies, acrylics, latexes, polyurethanes, silicones, and so on, may be combined with different colored thermochromic materials such as blue, red, green, brown, orange, and so on, and/or different thermochromic formulations such as micro-encapsulated leuco dye systems, liquid crystals in the nematic mesophase, phase shifting semi-conductor materials such as Vanadium dioxide that selectively block or conduct radiation in the infrared range at a predetermined phase change temperature, as well as other phase shifting materials and the like.
The protective layer 18 preferably comprises a two component, solvent based, high solids fluorinated polyurethane (FPU) material composed of closely packed trifluoromethyl groups, with a 2:1 ratio of base to activator. Preferably, the protective layer 18 is clear so that solar radiation will reach the color changing layer 16. The FPU material prevents the transmission of UV radiation to the color changing layer 16 and protects the color changing layer against UV degradation, moisture, oxygen permeation, weathering, and other degrading environmental conditions to thereby prolong the useful life of the color changing layer. The FPU material also exhibits a lower surface energy than Polytetrafluoroethylene (PTFE) at about 6 MJ/m2 for easy cleaning and maintenance, as well as hydrophobic and oleophobic properties to shed water, oils and other contaminants that may be present on its surface.
It will be understood that the protective layer 18 may be constructed of a wide variety of different materials such as lacquers, enamels, epoxies, acrylics, latex, silicones, and so on, with well-known additives for blocking UV radiation and protecting the color changing layer from direct exposure to environmental conditions.
Referring now to
Likewise, when the color changing layer 16 is below a second transition temperature lower than the first transition temperature (depending on the particular thermochromic formulation), it will be substantially opaque so that a substantial amount of radiant energy is absorbed by the layer 16, as shown by arrows 34 in
Referring now to
Once the underlying surface has been properly prepared, the base layer 14 is applied over the surface as shown at block 44, preferably through the use of high pressure, airless spray equipment capable of supplying at least one-half gallon per minute (GPM) of the base layer material. Preferably, the thickness of the cured base layer is in the range of about 10 mils to about 40 mils, and more preferably about 20 mils. It will be understood that the base layer 14 can alternatively be applied using brushes, rollers, conventional air atomization equipment, high velocity low pressure (HVLP) systems, and so on. In some instances, it may be desirable to apply two or more coats to build up to the desired layer thickness. Application of the base layer 14 using one or more of the above-described techniques creates a seamless, flexible, highly elastic, weather impenetrable and heat reflective first membrane that eliminates the problems associated with rolled laminates or other roofing systems.
When the base layer 14 has sufficiently cured, the color changing layer 16 is applied over the base layer as shown at block 46, preferably through the use of high pressure, airless spray equipment capable of supplying at least one-half GPM. When the atmospheric and/or base layer temperature is above the clear transition temperature, the thermochromic material is preferably cooled through a refrigerated holding tank and insulated delivery hoses (not shown) so that the material can be seen as it is applied over the base layer 14. In this manner, uniform application of the color changing layer 16 at temperatures above the clear transition temperature can be verified. The thickness of the cured color changing layer is in the range of about 1 to 10 mils, and more preferably in the range of about 2-3 mils. It will be understood that the color changing layer 16 can alternatively be applied using brushes, rollers, conventional air atomization equipment, high velocity low pressure (HVLP) systems, and so on. Application of the color changing layer 14 using one or more of the above-described techniques creates a seamless, flexible, highly elastic, and heat responsive second membrane that eliminates the problems associated with rolled laminates or other roofing systems. When it has been determined that the existing roof structure has a radiant energy reflective surface in good condition, the color changing layer may be directly applied to the reflective surface without applying the base layer.
When the color changing layer 16 has sufficiently cured, the protective layer 18 is applied over the color changing layer as shown at block 48. For high volume applications using the afore-mentioned two-component fluorinated polyurethane material, plural component airless spray equipment for mixing the base and activator at the correct ratio during application is preferred. Such a system can be pneumatically or hydraulically driven. The thickness of the cured protective layer 18 is preferably in the range of about two to ten mils, and more preferably about five mils. For low volume applications, the two components may be mixed together and applied over the color changing layer 16 by brush, roller, conventional atomized spray equipment, or HVLP equipment. Application of the protective layer 18 using one or more of the above-described techniques creates a seamless, flexible, highly elastic, weather impenetrable and heat reflective third membrane that eliminates the problems associated with rolled laminates or other roofing systems.
Once installed, the coating system 10 can be scanned or observed, as shown at block 50, to determine whether there are localized color changes and thus underlying structural defects, as shown in
Likewise, when the temperature of the roof is below the transition temperature as shown in
When the base layer 14 is white and the color changing layer is black below the lower transition temperature, the combined layers may exhibit varying shades of gray to indicate varying degrees of structural defects. Since the localized color changes lie within the visible range of the electromagnetic spectrum, the roofing defects may be readily ascertained by the naked eye without relying on the expensive and time consuming thermal imaging equipment of the prior art.
Accordingly, it is determined at decision block 56 (
The coating system 10 of the present invention can thus be advantageously applied as a seamless monolithic membrane over the entire area of a roof, wall or other structure, including structure protuberances, accessories or fixtures that must be sealed to the structure against moisture and other environmental conditions, in a quick and efficient manner without the time consuming, labor intensive, and error prone installation of prior art laminate materials, including the inherently weak seam interface between laminate strips.
It will be understood that the terms “opaque”, “translucent”, “transparent” and “clear” as used throughout the specification denote relative, rather than absolute conditions. By way of example, when the color changing layer is “clear” or “transparent”, it may allow the transmission of certain wavelengths while inhibiting the transmission of other wavelengths through the layer. Thus, a transparent material may be transparent to certain wavelengths and yet opaque to other wavelengths. In addition, the terms “translucent”, “transparent” and “clear” may refer to a colorless condition or a colored condition different from the “opaque” color condition. It will be further understood that the term “preferably” as used throughout the specification refers to one or more exemplary embodiments of the invention and therefore is not to be interpreted in any limiting sense. Also, it will be understood that the term “contiguous” and its various derivatives as may be used throughout the specification refer to components that may be joined together either directly or through one or more intermediate members. Accordingly, intermediate layers of material may be located between or on at least one side of one or more of the layers 14, 16 and 18 and/or between the underlying structure 12 and the layer 14. Accordingly, it is not necessary that the structure 12 and layers 14, 16, and 18 be in immediate contact with each other to reap the benefits of the present invention.
It will be appreciated by those skilled in the art that changes could be made to the embodiments described above without departing from the broad inventive concept thereof. For example, although the color changing system of the present invention has been shown and described for use with structures such as walls and roofs of buildings, it will be understood that the system of the invention can be used with other enclosed spaces such as vehicles, trailers, temperature-controlled enclosures, and so on. It will be further understood that the base layer, color changing layer and protective layer, if used, can be formed as single ply roofing membranes during the manufacturing process and installed separately on roof structures or the like. It will be understood, therefore, that this invention is not limited to the particular embodiments disclosed, but is intended to cover modifications within the spirit and scope of the present invention as defined by the appended claims.