Patent Application
20180016497
This application claims the benefit of Korean Patent Application No. 10-2016-0088780, filed on Jul. 13, 2016, in the Korean Intellectual Property Office, the disclosure of which is incorporated herein in its entirety by reference.
The present invention relates to a nanophosphor that is applicable to anti-falsification, fluorescent contrast media, and transparent display and a method of synthesizing the same, and in particular, to a fluoride-based core/first shell/second shell/third shell nanophosphor that has a particle size of about 1 to about 50 nm, emits visible light when excited by infrared light, and has a tetragonal structure, wherein the nanophosphor emits blue, green, red, or white light due to energy transition between a core and a shell and energy transition among sensitizers constituting shell layers.
Nanophosphor includes an inorganic host having a size of 100 nm or less and lanthanide doped thereon. In the case of a nanophosphor doped with a trivalent lanthanide ion, its emission color depends on the doped lanthanide, not its host. This is because the emission of the nanophosphor occurs due to 4f-4f electron transition within the trivalent lanthanide ion doped on the host. Since electrons of the 4f orbital are located inner than 5s and 5p orbitals, the electrons are relatively less affected by external impacts, and even when lanthanide is doped on different hosts, light having a unique wavelength corresponding to the lanthanide may be emitted. Accordingly, unlike quantum dots, of which emission characteristics vary according to the size of particles, even with non-homogenous particle sizes, desired emission wavelengths may be maintained.
As for most phosphors including nanophosphors, when high-energy light, such as ultraviolet light or visible light, is radiated to a phosphor, an electron may transition from a ground energy level, and then, energy loss may occur, and visible light, having a wavelength longer than that of incident light, may be emitted. The difference between an absorption wavelength and an emission wavelength is referred to as stokes shift. In this regard, when some lanthanides are doped, electrons may be excited due to infrared light, and visible light, which has a shorter wavelength, that is, a higher energy level than exiting light, may be emitted: anti-stokes shift. This is referred to as up-conversion emission, which is distinguishable from down-conversion in which emission energy is lower than excitation energy. Phosphors showing up-conversion emission emit light when exposed to infrared light. Accordingly, such phosphors are suitable for use as fluorescent contrast media. This is because since, during cell imaging, the use of infrared light does not induce self-emission in cells, up-conversion phosphors may provide fluorescent images having a high signal-to-noise ratio. Unlike commercially available powder micro-phosphors, nanophosphors having a nanometer region may attach on the surface of cells or enter into cells. Accordingly, such nanophosphors are applicable to bio-imaging, such as cell imaging or in-vivo imaging. For use as contrast media for bio images, organic dyes are widely used. Organic dyes emit various colors of light having strong emission intensities. However, they have very weak photostability, and accordingly, even when the light-exposure time increases slightly, emission intensities are substantially decreased. This feature can be overcome by using an inorganic emission material, for example, quantum dots, as contrast media for bio images. In this case, however, quantum dots may cause flickering emission, and like CdSe, when heavy metal, such as Cd, is included, their applicability may be decreased.
In the case of nanophosphors, since nanophosphors are an inorganic material, excellent photostability may be obtained. Also, due to the absence of a toxic element, such as Cd, nanophosphors are an excellent alternative to fluorescent contrast media of the related art. However, up-conversion emission shows low emission efficiency, since after two photons having small energy are absorbed by phosphor, one photon having an energy intensity greater than the other emits light. In particular, in the case of a phosphor having a relatively small particle size, that is, a nanophosphor, surface defects may be serious per unit volume, leading to further lower up-conversion emission efficiency. Accordingly, for high-sensitivity fluorescent imaging, there is a need to develop a nanophosphor having a small, uniform particle size and strong up-conversion emission intensity. Conventionally, up-conversion emission effectively occurs in Tm, Er, and Ho. Accordingly, it is difficult to produce light having a wavelength region other than those of Tm, Er, and Ho. However, if an up-conversion nanophosphor that can emit light having a wavelength region other than those of Tm, Er, and Ho when exposed to infrared light as an exciting light source is developed, such an up-conversion nanophosphor may be applicable to bio imaging, such as multiplexing imaging, and imaging accuracy may be further improved. In addition, when the up-conversion nanophosphor emits various colors of visible light when exposed to a single infrared ray wavelength of light, it is applicable to transparent displays. Furthermore, since color other than the color embodied by Tm, Er, and Ho can be obtained, when the up-conversion nanophosphor is used for security applications using infrared rays, a security level may be increased.
Provided is an up-conversion nanophosphor having, as a host, LiGdF4 having a single tetragonal structure having a scheelite structure, which is known to have high emission efficiency, wherein the LiGdF4 is doped with Tm, Tb, and Eu to produce various colors of light. In detail, to embody a strong up-conversion emission, a core/first shell/second shell/third shell structure is introduced, the location where a sensitizer is doped is limited to shell layers, and the concentration of the sensitizer is controlled to emit various color of light. Also, the concentration of the co-sensitizer is controlled to emit white light. However, these embodiments are presented herein for illustrative purpose only, and the scope of the present disclosure is not limited thereto.
Additional aspects will be set forth in part in the description which follows and, in part, will be apparent from the description, or may be learned by practice of the presented embodiments.
According to an aspect of an embodiment, a nanophosphor includes an Yb3+-doped fluoride-based nanoparticle represented by Formula 1:
LiY1-x-yLyF4:Yb3+x. [Formula 1]
In Formula 1, x satisfies the condition of 0≦x≦1 and is a real number; y satisfies the condition of 0≦y≦1, is a real number, satisfies the condition of 0≦x+y≦1, and may be any real number that satisfies the condition of x+y≦1; and L may be any one selected from Y, Dy, Ho, Er, Tm, Lu, and a combination thereof.
The nanophosphor may include a core including the nanoparticle and a shell located on the surface of the core, and the shell may include a compound represented by Formula 2:
LiGd1-p-q-rMrF4:Yb3+p, Tm3+q. [Formula 2]
In Formula 2, p satisfies the condition of 0<p≦0.5 and is a real number, and q satisfies the condition of 0<q≦0.2 and is a real number.
In Formula 2, r satisfies the condition of 0≦r≦1 and is a real number, r may be any real number that satisfies the condition of 0<p+q+r<1, and M may be any one selected from a rare-earth element and a combination thereof.
The rare-earth element may be any one selected from Gd, Y, La, Ce, Pr, Nd, Pm, Sm, Eu, Tb, Dy, Ho, Er, and Lu.
The nanophosphor may include the core and the shell, and Yb3+, which is a co-sensitizer, absorbs infrared light and transfers the absorption energy to Tm3+, resulting in emission peaks in an ultraviolet light region and a blue light region.
The nanophosphor may include the nanoparticle-including core/first shell and a second shell located on the surface of the core/first shell, and the second shell may include a compound represented by Formula 3:
LiGd1-s-t-uNuF4:Tb3+s,Eu3+t. [Formula 3]
In Formula 3, s satisfies the condition of 0<s≦0.5 and is a real number, and t satisfies the condition of 0<t≦0.5 and is a real number.
In Formula 3, u satisfies the condition of 0≦u≦1 and is a real number, u may be any real number that satisfies the condition of 0<s+t+u<1, and N may be any one selected from a rare-earth element and a combination thereof.
The rare-earth element may be any one selected from Gd, Y, La, Ce, Pr, Nd, Pm, Sm, Dy, Ho, Er, Tm, Yb, and Lu.
The nanophosphor may include the nanoparticle-containing core/first shell/second shell, and a third shell located on the surface of the core/first shell/second shell, and the third shell may include a compound represented by Formula 4:
LiY1-vOvF4. [Formula 4]
In Formula 4, v satisfies the condition of 0≦v≦1 and is a real number, and O may be any one selected from a rare-earth element and a combination thereof.
The rare-earth element may be any one selected from Y, La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu.
The nanoparticle may have a size of about 2 nm to about 70 nm.
The nanoparticle may have up-conversion characteristics.
Embodiments of the inventive concept will be more clearly understood from the following detailed description taken in conjunction with the accompanying drawings in which:
Reference will now be made in detail to embodiments, examples of which are illustrated in the accompanying drawings, wherein like reference numerals refer to like elements throughout. In this regard, the present embodiments may have different forms and should not be construed as being limited to the descriptions set forth herein. Accordingly, the embodiments are merely described below, by referring to the figures, to explain aspects. For ease of description, in the drawings, the sizes of at least some elements are exaggerated for clarity. Like reference numbers in the drawings denote like elements.
Hereinafter, with reference to the attached drawings, a color-tunable core/first shell/second shell/third shell structure according to embodiments of the present disclosure will be described. The core/first shell/second shell/third shell structure may include a LiY1-x-yLyF4:Yb3+x/LiGd1-p-q-rMrF4:Yb3+p,Tm3+q/LiGd1-s-t-uNuF4:Tb3+s,Eu3+t/LiY1-vOvF4 structure. Regarding this structure, x satisfies the condition of 0≦x≦1 and is a real number; y satisfies the condition of 0≦y≦1, is a real number, satisfies the condition of 0≦x+y≦1, and may be any real number that satisfies the condition of x+y≦1; and L may be any one selected from Y, Dy, Ho, Er, Tm, Lu, and a combination thereof; p satisfies the condition of 0<p≦0.5 and is a real number, q satisfies the condition of 0<q≦0.2 and is a real number, r satisfies the condition of 0≦r≦1 and is a real number, r may be any real number that satisfies the condition of 0<p+q+r<1, and M may be any one selected from a rare-earth element and a combination thereof; s satisfies the condition of 0<s≦0.5 and is a real number, t satisfies the condition of 0<t≦0.5 and is a real number, u satisfies the condition of 0≦u≦1 and is a real number, u may be any real number that satisfies the condition of 0<s+t+u<1, and N may be any one selected from a rare-earth element and a combination thereof; and v satisfies the condition of 0≦v≦1 and is a real number, and O may be any one selected from a rare-earth element and a combination thereof. Hereinafter, up-conversion nanophosphors will be described. However, the concept of the present disclosure is not limited to embodiments to be presented below, and other embodiments may also be provided by, for example, the addition or substitution of constituting elements.
Embodiments explained in connection with the drawings are not interpreted as limiting the concept of the present disclosure, and shall be considered as to fully explain the present disclosure.
Hereinafter, examples of a method of preparing an up-conversion/down-conversion double emission fluoride-based nanophosphor having a core/first shell/second shell/third shell structure will be described.
0.74 mmol gadolinium chloride hexahydrate (GdCl3.6H2O), 0.25 mmol ytterbium chloride hexahydrate (YbCl3.6H2O), 0.01 mmol thulium chloride hexahydrate (TmCl3.6H2O), and 3.1 mmol oleic acid sodium (C18H33O2Na) were estimated, and a mixed solvent including water, ethanol, and hexane was added thereto in a predetermined amount. The mixture was heat-treated at a temperature of 70° C. to form a lanthanide complex compound (step of preparing a complex compound). The complex compound was mixed with a solution including an oleic acid and 1-octadecene, and then, heat-treated at a temperature of 150° C. for 30 minutes to prepare a mixed solution including the lanthanide complex compound (step of preparing a first mixed solution).
10 ml of a methanol solution including 2.5 mmol lithium hydroxide and 4 mmol ammonium fluoride was prepared (step of preparing a second mixed solution) and then mixed with the mixed solution including the lanthanide complex compound (step of preparing a reaction solution).
The resultant mixed solution was sufficiently mixed, and then, methanol was removed therefrom, followed by heat-treatment in inert gas atmosphere. In this regard, when the heat-treatment temperature is less than 200° C., single tetragonal nanocrystals are not completely formed, and thus, the formed phosphor may not have strong emission characteristics; and when the heat-treatment temperature exceeds 370° C., over-reaction may occur and thus, particles may agglomerate together to form larger particles, and the size distribution of formed particles is not uniform, leading to low luminance. Accordingly, the heat-treatment temperature was controlled to be in a range of 200 to 370° C., and the heat-treatment time was controlled to be in a range of 10 minutes to 4 hours (step of forming a nanoparticle). After the heat-treatment, the result was cooled to room temperature, thereby producing nanophosphor in the colloid state, having a particle diameter of 1 nm to 40 nm. The nanophosphor was washed with acetone or ethanol, and then, for storage purpose, dispersed in a non-polar solvent, for example, hexane, toluene, chloroform, or like.
0.2 mmol yttrium chloride hexahydrate (YCl3.6H2O), 0.8 mmol ytterbium chloride hexahydrate (YbCl3.6H2O), and 3.1 mmol oleic acid sodium (Cl18H33O2Na) were estimated, and a mixed solvent including water, ethanol, and hexane was added thereto in a predetermined amount. The mixture was heat-treated at a temperature of 70° C. to form a lanthanide complex compound (step of preparing a complex compound). The complex compound was mixed with a solution including an oleic acid and 1-octadecene, and then, heat-treated at a temperature of 150° C. for 30 minutes to prepare a first mixed solution including the lanthanide complex compound (step of preparing a first mixed solution).
10 ml of a methanol solution including 2.5 mmol lithium hydroxide and 4 mmol ammonium fluoride was prepared (step of preparing a second mixed solution), and then mixed with the first mixed solution including the lanthanide complex compound (step of preparing a reaction solution).
The resultant mixed solution was sufficiently mixed, and then, methanol was removed therefrom, followed by heat-treatment in inert gas atmosphere. In this regard, when the heat-treatment temperature is less than 200° C., single tetragonal nanocrystals are not completely formed, and thus, the formed phosphor may not have strong emission characteristics; and when the heat-treatment temperature exceeds 370° C., over-reaction may occur, and thus, particles may agglomerate together to form larger particles, and the size distribution of formed particles is not uniform, leading to low luminance. Accordingly, the heat-treatment temperature was controlled to be in a range of 200 to 370° C., and the heat-treatment time was controlled to be in a range of 10 minutes to 4 hours (step of forming a nanoparticle). After the heat-treatment, the result was cooled to room temperature, thereby producing nanophosphor in the colloid state, having a particle diameter of 1 nm to 40 nm. The nanophosphor prepared according to Example 1 included LiY0.2F4:Yb3+0.8 nanoparticle. The nanophosphor was washed with acetone or ethanol, and then, for storage purpose, dispersed in a non-polar solvent, for example, hexane, toluene, chloroform, or like.
A nanophosphor having a core/first shell structure was prepared by using the LiY0.2F4:Yb3+0.8 nanoparticle prepared according to Example 1, which is a core, and a Yb3+ and Tm3+-codoped fluoride-based compound.
0.74 mmol gadolinium chloride hexahydrate (GdCl3.6H2O), 0.25 mmol ytterbium chloride hexahydrate (YbCl3.6H2O), and 0.01 mmol thulium chloride hexahydrate (TmCl3.6H2O) were mixed with a solution including an oleic acid and 1-octadecene, and the resultant mixture was heat-treated at a temperature of 150° C. for 30 minutes to prepare a mixed solution including a lanthanide complex compound (step of preparing a first mixed solution).
The first mixed solution was mixed with a solution including the LiY0.2F4:Yb3+0.8 nanoparticle prepared according to Example 1 to prepare a second mixed solution.
10 ml of a methanol solution including 2.5 mmol lithium hydroxide and 4 mmol ammonium fluoride was prepared (step of preparing a third mixed solution), and then mixed with the second mixed solution including the lanthanide complex compound (step of preparing a reaction solution).
The resultant mixed solution was sufficiently mixed, and then, methanol was removed therefrom, followed by heat-treatment in inert gas atmosphere. In this regard, when the heat-treatment temperature is less than 200° C., single tetragonal nanocrystals are not completely formed, and thus, the formed phosphor may not have strong emission characteristics; and when the heat-treatment temperature exceeds 370° C., over-reaction may occur, and thus, particles may agglomerate together to form larger particles, and the size distribution of formed particles is not uniform, leading to low luminance. Accordingly, the heat-treatment temperature was controlled to be in a range of 200 to 370° C., and the heat-treatment time was controlled to be in a range of 10 minutes to 4 hours (step of forming a nanoparticle). After the heat-treatment, the result was cooled to room temperature, thereby producing nanophosphor in the colloid state, having a particle diameter of 1 nm to 30 nm. The nanophosphor prepared according to Example 2 included the LiY0.2F4:Yb3+0.8 core prepared according to Example 1 and a LiGdF4:Yb3+0.25,Tm3+0.01 shell. The nanophosphor was washed with acetone or ethanol, and then, for storage purpose, dispersed in a non-polar solvent, for example, hexane, toluene, chloroform, or like.
In a nanophosphor having a core/first shell/second shell/third shell structure according to an embodiment, the core corresponds to the ‘sensitizer-doped core’ illustrated in
Referring to the X-ray diffraction pattern of
A nanophosphor having a core/first shell/second shell structure was prepared by using the LiY0.2F4:Yb3+0.8/LiGdF4:Yb3+0.25,Tm3+0.01 nanoparticle prepared according to Example 2, as a core, and a LiGdF4:Tb3+ compound.
0.85 mmol gadolinium chloride hexahydrate (GdCl3.6H2O) and 0.15 mmol terbium chloride hexahydrate (TbCl3.6H2O) were mixed with a solution including an oleic acid and 1-octadecene, and the resultant mixture was heat-treated at a temperature of 150° C. for 30 minutes to prepare a mixed solution including a lanthanide complex compound (step of preparing a first mixed solution).
The first mixed solution was mixed with a solution including the LiY0.2F4:Yb3+0.8/LiGdF4:Yb3+0.25,Tm3+0.01 nanoparticle prepared according to Example 2 to prepare a second mixed solution.
10 ml of a methanol solution including 2.5 mmol lithium hydroxide and 4 mmol ammonium fluoride was prepared (step of preparing a third mixed solution), and then mixed with the second mixed solution including the lanthanide complex compound (step of preparing a reaction solution).
The resultant mixed solution was sufficiently mixed, and then, methanol was removed therefrom, followed by heat-treatment in inert gas atmosphere. In this regard, when the heat-treatment temperature is less than 200° C., single tetragonal nanocrystals are not completely formed, and thus, the formed phosphor may not have strong emission characteristics; and when the heat-treatment temperature exceeds 370° C., over-reaction may occur, and thus, particles may agglomerate together to form larger particles, and the size distribution of formed particles is not uniform, leading to low luminance. Accordingly, the heat-treatment temperature was controlled to be in a range of 200 to 370° C., and the heat-treatment time was controlled to be in a range of 10 minutes to 4 hours (step of forming a nanoparticle). After the heat-treatment, the result was cooled to room temperature, thereby producing nanophosphor in the colloid state, having a particle diameter of 1 nm to 50 nm. The nanophosphor was washed with acetone or ethanol, and then, for storage purpose, dispersed in a non-polar solvent, for example, hexane, toluene, chloroform, or like.
A nanophosphor having a core/first shell/second shell/third shell structure was prepared by using the LiY0.2F4:Yb3+0.8/LiGdF4:Yb3+0.25,Tm3+0.01/LiGdF4:Tb3+0.15 nanoparticle prepared according to Example 3, as a core, and a LiYF4 compound. 1 mmol yttrium chloride hexahydrate (YCl3.6H2O) was mixed with a solution including an oleic acid and 1-octadecene, and the resultant mixture was heat-treated at a temperature of 150° C. for 30 minutes to prepare a mixed solution including a yttrium complex compound (step of preparing a first mixed solution).
The first mixed solution was mixed with a solution including the LiY0.2F4:Yb3+0.8/LiGdF4:Yb3+0.25,Tm3+0.01/LiGdF4:Tb3+0.15 nanoparticle prepared according to Example 3 to prepare a second mixed solution.
10 ml of a methanol solution including 2.5 mmol lithium hydroxide and 4 mmol ammonium fluoride was prepared (step of preparing a third mixed solution), and then mixed with the second mixed solution including the yttrium complex compound (step of preparing a reaction solution).
The resultant mixed solution was sufficiently mixed, and then, methanol was removed therefrom, followed by heat-treatment in inert gas atmosphere. In this regard, when the heat-treatment temperature is less than 200° C., single tetragonal nanocrystals are not completely formed, and thus, the formed phosphor may not have strong emission characteristics; and when the heat-treatment temperature exceeds 370° C., over-reaction may occur, and thus, particles may agglomerate together to form larger particles, and the size distribution of formed particles is not uniform, leading to low luminance. Accordingly, the heat-treatment temperature was controlled to be in a range of 200 to 370° C., and the heat-treatment time was controlled to be in a range of 10 minutes to 4 hours (step of forming a nanoparticle). After the heat-treatment, the result was cooled to room temperature, thereby producing nanophosphor in the colloid state, having a particle diameter of 1 nm to 70 nm. The nanophosphor was washed with acetone or ethanol, and then, for storage purpose, dispersed in a non-polar solvent, for example, hexane, toluene, chloroform, or like.
A nanophosphor having a core/first shell/second shell structure was prepared by using the LiY0.2F4:Yb3+0.8/LiGdF4:Yb3+0.25,Tm3+0.01 nanoparticle prepared according to Example 2, as a core, and a LiGdF4:Eu3+ compound. 0.85 mmol gadolinium chloride hexahydrate (GdCl3.6H2O) and 0.15 mmol europium chloride hexahydrate (EuCl3.6H2O) were mixed with a solution including an oleic acid and 1-octadecene, and the resultant mixture was heat-treated at a temperature of 150° C. for 30 minutes to prepare a mixed solution including a lanthanide complex compound (step of preparing a first mixed solution).
The first mixed solution was mixed with a solution including the LiY0.2F4:Yb3+0.8/LiGdF4:Yb3+0.25,Tm3+0.01 nanoparticle prepared according to Example 2 to prepare a second mixed solution.
10 ml of a methanol solution including 2.5 mmol lithium hydroxide and 4 mmol ammonium fluoride was prepared (step of preparing a third mixed solution), and then mixed with the second mixed solution including the lanthanide complex compound (step of preparing a reaction solution).
The resultant mixed solution was sufficiently mixed, and then, methanol was removed therefrom, followed by heat-treatment in inert gas atmosphere. In this regard, when the heat-treatment temperature is less than 200° C., single tetragonal nanocrystals are not completely formed, and thus, the formed phosphor may not have strong emission characteristics; and when the heat-treatment temperature exceeds 370° C., over-reaction may occur, and thus, particles may agglomerate together to form larger particles, and the size distribution of formed particles is not uniform, leading to low luminance. Accordingly, the heat-treatment temperature was controlled to be in a range of 200 to 370° C., and the heat-treatment time was controlled to be in a range of 10 minutes to 4 hours (step of forming a nanoparticle). After the heat-treatment, the result was cooled to room temperature, thereby producing nanophosphor in the colloid state, having a particle diameter of 1 nm to 50 nm. The nanophosphor was washed with acetone or ethanol, and then, for storage purpose, dispersed in a non-polar solvent, for example, hexane, toluene, chloroform, or like.
A nanophosphor having a core/first shell/second shell/third shell structure was prepared by using the LiY0.2F4:Yb3+0.8/LiGdF4:Yb3+0.25,Tm3+0.01/LiGdF4:Eu3+0.15 nanoparticle prepared according to Example 5, as a core, and a LiYF4 compound.
1 mmol yttrium chloride hexahydrate (YCl3.6H2O) was mixed with a solution including an oleic acid and 1-octadecene, and the resultant mixture was heat-treated at a temperature of 150° C. for 30 minutes to prepare a mixed solution including a yttrium complex compound (step of preparing a first mixed solution).
The first mixed solution was mixed with a solution including the LiY0.2F4:Yb3+0.8/LiGdF4:Yb3+0.25,Tm3+0.01/LiGdF4:Eu3+0.15 nanoparticle prepared according to Example 3 to prepare a second mixed solution.
10 ml of a methanol solution including 2.5 mmol lithium hydroxide and 4 mmol ammonium fluoride was prepared (step of preparing a third mixed solution), and then mixed with the second mixed solution including the yttrium complex compound (step of preparing a reaction solution).
The resultant mixed solution was sufficiently mixed, and then, methanol was removed therefrom, followed by heat-treatment in inert gas atmosphere. In this regard, when the heat-treatment temperature is less than 200° C., single tetragonal nanocrystals are not completely formed, and thus, the formed phosphor may not have strong emission characteristics; and when the heat-treatment temperature exceeds 370° C., over-reaction may occur, and thus, particles may agglomerate together to form larger particles, and the size distribution of formed particles is not uniform, leading to low luminance. Accordingly, the heat-treatment temperature was controlled to be in a range of 200 to 370° C., and the heat-treatment time was controlled to be in a range of 10 minutes to 4 hours (step of forming a nanoparticle). After the heat-treatment, the result was cooled to room temperature, thereby producing nanophosphor in the colloid state, having a particle diameter of 1 nm to 70 nm. The nanophosphor was washed with acetone or ethanol, and then, for storage purpose, dispersed in a non-polar solvent, for example, hexane, toluene, chloroform, or like.
A nanophosphor having a core/first shell/second shell structure was prepared by using the LiY0.2F4:Yb3+0.8/LiGdF4:Yb3+0.25,Tm3+0.01 nanoparticle prepared according to Example 2, as a core, and a LiGdF4:Tb3+,Eu3+ compound.
0.83 mmol gadolinium chloride hexahydrate (GdCl3.6H2O), 0.15 mmol terbium chloride hexahydrate (TbCl3.6H2O), and 0.02 mmol europium chloride hexahydrate (EuCl3.6H2O) were mixed with a solution including an oleic acid and 1-octadecene, and the resultant mixture was heat-treated at a temperature of 150° C. for 30 minutes to prepare a mixed solution including a lanthanide complex compound (step of preparing a first mixed solution).
The first mixed solution was mixed with a solution including the LiY0.2F4:Yb3+0.8/LiGdF4:Yb3+0.25,Tm3+0.01 nanoparticle prepared according to Example 2 to prepare a second mixed solution.
10 ml of a methanol solution including 2.5 mmol lithium hydroxide and 4 mmol ammonium fluoride was prepared (step of preparing a third mixed solution), and then mixed with the second mixed solution including the lanthanide complex compound (step of preparing a reaction solution).
The resultant mixed solution was sufficiently mixed, and then, methanol was removed therefrom, followed by heat-treatment in inert gas atmosphere. In this regard, when the heat-treatment temperature is less than 200° C., single tetragonal nanocrystals are not completely formed, and thus, the formed phosphor may not have strong emission characteristics; and when the heat-treatment temperature exceeds 370° C., over-reaction may occur, and thus, particles may agglomerate together to form larger particles, and the size distribution of formed particles is not uniform, leading to low luminance. Accordingly, the heat-treatment temperature was controlled to be in a range of 200 to 370° C., and the heat-treatment time was controlled to be in a range of 10 minutes to 4 hours (step of forming a nanoparticle). After the heat-treatment, the result was cooled to room temperature, thereby producing nanophosphor in the colloid state, having a particle diameter of 1 nm to 50 nm. The nanophosphor was washed with acetone or ethanol, and then, for storage purpose, dispersed in a non-polar solvent, for example, hexane, toluene, chloroform, or like.
A nanophosphor having a core/first shell/second shell/third shell structure was prepared by using the LiY0.2F4:Yb3+0.8/LiGdF4:Yb3+0.25, Tm3+0.01/LiGdF4:Tb3+0.15,Eu3+0.02 nanoparticle prepared according to Example 7, as a core, and a LiYF4 compound.
1 mmol yttrium chloride hexahydrate (YCl3.6H2O) was mixed with a solution including an oleic acid and 1-octadecene, and the resultant mixture was heat-treated at a temperature of 150° C. for 30 minutes to prepare a mixed solution including a yttrium complex compound (step of preparing a first mixed solution).
The first mixed solution was mixed with a solution including the LiY0.2F4:Yb3+0.8/LiGdF4:Yb3+0.25, Tm3+0.01/LiGdF4:Tb3+0.15,Eu3+0.02 nanoparticle prepared according to Example 7 to prepare a second mixed solution.
10 ml of a methanol solution including 2.5 mmol lithium hydroxide and 4 mmol ammonium fluoride was prepared (step of preparing a third mixed solution), and then mixed with the second mixed solution including the yttrium complex compound (step of preparing a reaction solution).
The resultant mixed solution was sufficiently mixed, and then, methanol was removed therefrom, followed by heat-treatment in inert gas atmosphere. In this regard, when the heat-treatment temperature is less than 200° C., single tetragonal nanocrystals are not completely formed, and thus, the formed phosphor may not have strong emission characteristics; and when the heat-treatment temperature exceeds 370° C., over-reaction may occur, and thus, particles may agglomerate together to form larger particles, and the size distribution of formed particles is not uniform, leading to low luminance. Accordingly, the heat-treatment temperature was controlled to be in a range of 200 to 370° C., and the heat-treatment time was controlled to be in a range of 10 minutes to 4 hours (step of forming a nanoparticle). After the heat-treatment, the result was cooled to room temperature, thereby producing nanophosphor in the colloid state, having a particle diameter of 1 nm to 70 nm. The nanophosphor was washed with acetone or ethanol, and then, for storage purpose, dispersed in a non-polar solvent, for example, hexane, toluene, chloroform, or like.
A nanophosphor having a core/first shell/second shell structure was prepared by using the LiY0.2F4:Yb3+0.8/LiGdF4:Yb3+0.25,Tm3+0.01 nanoparticle prepared according to Example 2, as a core, and a LiYF4 compound.
1 mmol yttrium chloride hexahydrate (YCl3.6H2O) was mixed with a solution including an oleic acid and 1-octadecene, and the resultant mixture was heat-treated at a temperature of 150° C. for 30 minutes to prepare a mixed solution including a yttrium complex compound (step of preparing a first mixed solution).
The first mixed solution was mixed with a solution including the LiY0.2F4:Yb3+0.8/LiGdF4:Yb3+0.25,Tm3+0.01 nanoparticle prepared according to Example 2 to prepare a second mixed solution.
10 ml of a methanol solution including 2.5 mmol lithium hydroxide and 4 mmol ammonium fluoride was prepared (step of preparing a third mixed solution), and then mixed with the second mixed solution including the yttrium complex compound (step of preparing a reaction solution).
The resultant mixed solution was sufficiently mixed, and then, methanol was removed therefrom, followed by heat-treatment in inert gas atmosphere. In this regard, when the heat-treatment temperature is less than 200° C., a single tetragonal nanocrystal is not completely formed, and thus, the formed phosphor may not have strong emission characteristics; and when the heat-treatment temperature exceeds 370° C., over-reaction may occur, and thus, particles may agglomerate together to form larger particles, and the size distribution of formed particles is not uniform, leading to low luminance. Accordingly, the heat-treatment temperature was controlled to be in a range of 200 to 370° C., and the heat-treatment time was controlled to be in a range of 10 minutes to 4 hours (step of forming a nanoparticle). After the heat-treatment, the result was cooled to room temperature, thereby producing nanophosphor in the colloid state, having a particle diameter of 1 nm to 50 nm. The nanophosphor was washed with acetone or ethanol, and then, for storage purpose, dispersed in a non-polar solvent, for example, hexane, toluene, chloroform, or like.
As shown in the emission image of
A silica composite including the LiY0.2F4:Yb3+0.8/LiGdF4:Yb3+0.25,Tm3+0.01/LiGdF4:Eu3+0.15/LiYF4 nanoparticle prepared according to Example 6 was prepared
1.00 ml of a solution of the red emission up-conversion nanophosphor having the core/first shell/second shell/third shell structure prepared according to Example 6 was added to 2.00 ml of a perhydropolysilazane solution (Samsung SDI model number: CISD-15001, 18.6 wt % dibutyl ether solution), and then, annealed at room temperature in the atmosphere condition for 24 hours. The obtained product was milled by using a mortar and a pestle, and then, dried at a temperature of 60° C. for 7 hours and 30 minutes to prepare an up-conversion nanophosphor-silica composite.
This experiment has been explained in connection with the nanophosphor having the core/first shell/second shell/third shell structure. However, the nanophosphor according to the inventive concept is not limited thereto, and various other examples of the nanophosphor are also applicable herein. For example, the nanophosphor according to the inventive concept may have the core/first shell structure alone, the core/first shell/second shell structure alone, or the core/first shell/third shell structure alone.
An inorganic nanophosphor having the core/first shell/second shell/third shell structure according to embodiments of the present disclosure shows up-conversion emission having emission peaks in blue, green, and red wavelength regions corresponding to Tm, Tb, and Eu, has increased up-conversion emission intensity due to the formation of a shell on the outermost shell, enabling color-tunable high luminance up-conversion emission, and has white light emission characteristics in addition to mono-color light emission characteristics.
An inorganic nanophosphor according to embodiments of the present disclosure uses up-conversion emission. Accordingly, the inorganic nanophosphor can be used as contrast media for bio imaging, and also used in disease diagnosis fields. Various wavelength regions of emission may contribute to accuracy of fluorescent imaging. Also, due to the strong up-conversion emission from the core/first shell/second shell/third shell structure, the inorganic nanophosphor can be used as a sensor that detects infrared light that is not detectable by the human eye.
The increased efficiency of light emission characteristics may lead to a greater level of sensitivity of an infrared-ray sensor. The conversion of the infrared light, which is not used in a solar cell, into visible light may result in a greater efficiency of the solar cell.
The up-conversion nanophosphor having the core and core/first shell/second shell/third shell structure according to embodiments of the present disclosure uses infrared light that is not detectable by the human eye. Accordingly, the up-conversion nanophosphor can be used in security-related fields, for example, in a counterfeit prevention code. Since particles of the up-conversion nanophosphor have a size of 50 nm or less, it is difficult to detect the up-conversion nanophosphor. Also, since the up-conversion nanophosphor can show an emission characteristic that is not obtainable from bulk powder phosphor, it can be used in high-grade security code. Due to the uniform and small size thereof, a transparent polymer composite can be manufactured, and since the manufactured polymer composite can emit various wavelengths of color, it can be applied in a transparent display device.
The up-conversion nanophosphor can emit white light. In this case, the up-conversion nanophosphor can be used in, for example, an illuminating device using infrared light. However, these effects thereof are an example only, and do not limit the scope of the inventive concept.
As described above, the inventive concept has been described in connection with example embodiments. However, it is obvious to one of ordinary skill in the art that the embodiments described above may be modified or changed in various manners as long as within the inventive concept or region recited in the following claims.
One of ordinary skill in the art may improve or change the inventive concept in various manners, and as long as being obvious to one of ordinary skill in the art, the improvement and change may be within the claimed scope of the inventive concept.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2016-0088780 | Jul 2016 | KR | national |