COLORED GLASS ARTICLES HAVING IMPROVED MECHANICAL DURABILITY

Abstract

A colored glass article may include 50-80 mol % SiO2; 7-20 mol % Al2O3; 1-35 mol % R2O, wherein R2O comprises at least one of Li2O, Na2O, and K2O; 1×10−6-10 mol % of a colorant, wherein the colorant comprises at least one of Cr2O3, Au, Ag, CuO, NiO, Co3O4, TiO2, CeO2; and 12-24 mol % of Al2O3+MgO+CaO+ZnO. The colored glass article may have a transmittance color coordinate in the CIELAB color space with an L*value of 55 to 96.5. The colored glass article may have a compressive stress profile with a depth of compression ≥0.15t a thickness t from 0.4 mm-5 mm, a compressive stress ≥200 MPa, and a central tension ≥60 MPa. The colored glass article may have a dielectric constant from 5.6 to 6.4 over the frequency range from 10 GHz to 60 GHz.

Description

FIELD

The present specification generally relates to glass compositions and glass articles and, in particular, to glass compositions and ion-exchangeable, colored glass articles formed therefrom.

TECHNICAL BACKGROUND

Aluminosilicate glass articles may exhibit superior ion-exchangeability and drop performance. Various industries, including the consumer electronics industry, desire colored materials with the same or similar strength and fracture toughness properties as existing, non-colored, ion-exchange strengthened glasses. However, simply including colorants in conventional aluminosilicate glass compositions may not produce the desired color.

Accordingly, a need exists for an alternative colored glass articles having high strength and fracture toughness.

SUMMARY

Aspect A1 includes a colored glass article comprising: greater than or equal to 50 mol % and less than or equal to 80 mol % SiO₂; greater than or equal to 7 mol % and less than or equal to 20 mol % Al₂O₃; greater than or equal to 1 mol % and less than or equal to 35 mol % R₂O, wherein R₂O comprises at least one of Li₂O, Na₂O, and K₂O; greater than 1×10⁻⁶ mol % and less than or equal to 10 mol % of a colorant, wherein the colorant comprises at least one of Cr₂O₃, Au, Ag, CuO, NiO, Co₃O₄, TiO₂, CeO₂; and greater than or equal to 12 mol % and less than or equal to 24 mol % of Al₂O₃+MgO+CaO+ZnO, wherein the colored glass article comprises: a transmittance color coordinate in the CIELAB color space comprising an L*value greater than or equal to 55 and less than or equal to 96.5 as measured under F2 illumination and a 10° standard observer angle; a compressive stress profile with a depth of compression greater than or equal to 0.15t where t is a thickness of the colored glass article, a compressive stress greater than or equal to 200 MPa, and a central tension greater than or equal to 60 MPa; a dielectric constant from 5.6 to 6.4 over a frequency range from 10 GHz to 60 GHz; and the thickness t is greater than or equal to 0.4 mm and less than or equal to 5 mm.

Aspect A2 includes the colored glass article of aspect A1, wherein the thickness t is greater than or equal to 0.5 mm and less than or equal to 5 mm.

Aspect A3 includes the colored glass article of any preceding aspect, wherein a colored glass article having the same composition and microstructure as a center of the colored glass article has a fracture toughness K_IC greater than or equal to 0.7 MPa·m^1/2.

Aspect A4 includes the colored glass article of any preceding aspect comprising an average transmittance of greater than or equal to 10% and less than or equal to 92% over the wavelength range of 380 nm to 750 nm.

Aspect A5 includes the colored glass article of any preceding aspect further comprising at least one crystalline phase.

Aspect A6 includes the colored glass article of any preceding aspect comprising a crystallinity of less than 10 wt %.

Aspect A7 includes the colored glass article of any preceding aspect, wherein the depth of compression is less than or equal to 0.3t.

Aspect A8 includes the colored glass article of any preceding aspect, wherein the surface compressive stress is greater than or equal to 400 MPa.

Aspect A9 includes the colored glass article of any preceding aspect, wherein the central tension is greater than or equal to 70 MPa.

Aspect A10 includes the colored glass article of any preceding aspect, wherein the transmittance color coordinate in the CIELAB color space comprises an a* value and |a*| is ≥0.3.

Aspect A11 includes the colored glass article of any preceding aspect, wherein the transmittance color coordinate in the CIELAB color space comprises a b* value and |b*| is ≥0.5.

Aspect A12 includes the colored glass article of any preceding aspect, wherein the transmittance color coordinate in the CIELAB color space comprises an a* value and a b* value, wherein |a*| is ≥0.3 and |b*| is ≥0.5.

Aspect A13 includes the colored glass article of any preceding aspect, wherein the transmittance color coordinate in the CIELAB color space comprises a* and b* values within a region of a plot of a* vs. b* bound by the intersection of lines: b*=0.2879·a*+27.818; b*=7.0833·a*−94.5; b*=0.45·a*+104.5; and b*=15.3·a*+253.

Aspect A14 includes the colored glass article of aspect A13, wherein the colorant comprises Ag.

Aspect A15 includes the colored glass article of any of aspects A1-A12, wherein the transmittance color coordinate in the CIELAB color space comprises a* and b* values within a region of a plot of a* vs. b* bound by the intersection of lines: b*=7.0833·a*−94.5; b*−0.9583·a*+146.75; b*=2.6957·a*−50.565; and b*=33.

Aspect A16 includes the colored glass article of aspect A15 wherein the colorant comprises Ag.

Aspect A17 includes the colored glass article of any of aspects A1-A12, wherein the transmittance color coordinate in the CIELAB color space comprises a* and b* values within a region of a plot of a* vs. b* bound by the intersection of lines: b*=2.6957·a*−50.565; a*=54; b*=1.0769·a*−17.154; and b*=6.6667·a*−173.67.

Aspect A18 includes the colored glass article of aspect A17 wherein the colorant comprises Ag.

Aspect A19 includes the colored glass article of any of aspects A1-A12, wherein the transmittance color coordinate in the CIELAB color space comprises a* and b* values within a region of a plot of a* vs. b* bound by the intersection of lines: b*=0.2879·a*+27.818; a*=0; b*=−1.375·a*+1; and b*=9.333·a*+86.667, exclusive of a* greater than −0.3 and less than 0.3 and exclusive of b* greater than −0.5 and less than 0.5.

Aspect A20 includes the colored glass article of aspect A19, wherein the colorant comprises Ag.

Aspect A21 includes the colored glass article of any of aspects A1-A12, wherein the transmittance color coordinate in the CIELAB color space comprises a* and b* values within a region of a plot of a* vs. b* bound by the intersection of lines: b*=0.0833·a*+20.833; b*=2.1182·a*−32.073; b*=−0.3; and b*=1.5929·a*−0.3, exclusive of a* greater than −0.3 and less than 0.3 and exclusive of b* greater than −0.5 and less than 0.5.

Aspect A22 includes the colored glass article of aspect A21, wherein the colorant comprises Ag.

Aspect A23 includes the colored glass article of any of aspects A1-A12, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −18 and less than or equal to 0.3 and b* values greater than or equal to 0.5 and less than or equal to 82.

Aspect A24 includes the colored glass article of claim A23, wherein the colorant comprises Cr₂O₃.

Aspect A25 includes the colored glass article of any of aspects A1-A12, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −18 and less than or equal to 18, exclusive of a* greater than −0.3 and less than 0.3, and b* greater than or equal to 0.5 and less than or equal to 82.

Aspect A26 includes the colored glass article of aspect A25, wherein the colorant comprises Cr₂O₃ and NiO.

Aspect A27 includes the colored glass article of any of aspects A1-A12, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −20 and less than or equal to 60, exclusive of a* greater than −0.3 and less than 0.3, and b* greater than or equal to −90 and less than or equal to 85, exclusive of b* values greater than −0.5 and less than 0.5.

Aspect A28 includes the colored glass article of aspect A27, wherein the colorant comprises Cr₂O₃ and Co₃O₄.

Aspect A29 includes the colored glass article of any of aspects A1-A12, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −35 and less than or equal to −0.3, and b* values greater than or equal to 0.5 and less than or equal to 82.

Aspect A30 includes the colored glass article of aspect A29, wherein the colorant comprises Cr₂O₃ and CuO.

Aspect A31 includes the colored glass article of any of aspects A1-A12, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −35 and less than or equal to 20, exclusive of a* greater than −0.3 and less than 0.3, and b* values greater than or equal to 0.5 and less than or equal to 75.

Aspect A32 includes the colored glass article of aspect A31, wherein the colorant comprises Cr₂O₃, NiO, and CuO.

Aspect A33 includes the colored glass article of any of aspects A1-A12, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −15 and less than or equal to 65, exclusive of a* greater than −0.3 and less than 0.3, and b* values greater than or equal to −90 and less than or equal to 80, exclusive of b* greater than −0.5 and less than 0.5.

Aspect A34 includes the colored glass article of aspect A33, wherein the colorant comprises Cr₂O₃, NiO, and Co₃O₄.

Aspect A35 includes the colored glass article of any of aspects A1-A12, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −35 and less than or equal to 60, exclusive of a* greater than −0.3 and less than 0.3, and b* values greater than or equal to −90 and less than or equal to 80, exclusive of b* greater than −0.5 and less than 0.5.

Aspect A36 includes the colored glass article of aspect A35, wherein the colorant comprises Cr₂O₃, CuO, and Co₃O₄.

Aspect A37 includes the colored glass article of any of aspects A1-A12, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −35 and less than or equal to 60, exclusive of a* greater than −0.3 and less than 0.3, and b* values greater than or equal to −90 and less than or equal to 80, exclusive of b* greater than −0.5 and less than 0.5.

Aspect A38 includes the colored glass article of aspect A37, wherein the colorant comprises Cr₂O₃, NiO, CuO, and Co₃O₄.

Aspect A39 includes the colored glass article of any of aspects A1-A12, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −15 and less than or equal to −0.3 and b* values greater than or equal to −10 and less than or equal to 10, exclusive of b* greater than −0.5 and less than 0.5.

Aspect A40 includes the colored glass article of aspect A39, wherein the colorant comprises at least one of NiO, CuO, TiO₂, Co₃O₄, Cr₂O₃, and CeO₂.

Aspect A41 includes the colored glass article of any of aspects A1-A12, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −5 and less than or equal to 25, exclusive of a* greater than −0.3 and less than 0.3, and b* greater than or equal to −20 and less than or equal to 5, exclusive of b* greater than −0.5 and less than 0.5.

Aspect A42 includes the colored glass article of aspect A41, wherein the colorant comprises Au.

Aspect A43 includes the colored glass article of any of aspects A1-A12, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −10 and less than or equal to 25, exclusive of a* greater than −0.3 and less than 0.3, and b* values greater than or equal to −20 and less than or equal to 5, exclusive of b* greater than −0.5 and less than 0.5.

Aspect A44 includes the colored glass article of aspect A43, wherein the colorant comprises Au.

Aspect A45 includes the colored glass article of any of aspects A1-A12, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −15 and less than or equal to −0.3, and b* values greater than or equal to −10 and less than or equal to 10, exclusive of b* greater than −0.5 and less than 0.5.

Aspect A46 includes the colored glass article of aspect A45, wherein the colorant comprises at least one of Cr₂O₃, Au, Ag, CuO, NiO, Co₃O₄, TiO₂, and CeO₂.

Aspect A47 includes an electronic device comprising a housing, the housing comprising a colored glass article according to any preceding aspect.

Aspect A48 includes a colored glass article comprising: greater than or equal to 50 mol % and less than or equal to 80 mol % SiO₂; greater than or equal to 7 mol % and less than or equal to 20 mol % Al₂O₃; greater than or equal to 1 mol % and less than or equal to 35 mol % R₂O, wherein R₂O comprises at least one of Li₂O, Na₂O, and K₂O; greater than 1×10⁻⁶ mol % and less than or equal to 10 mol % of a colorant, wherein the colorant comprises at least one of Cr₂O₃, Au, Ag, CuO, NiO, Co₃O₄, TiO₂, CeO₂; and greater than or equal to 10 mol % and less than or equal to 30 mol % of Al₂O₃+MgO+CaO+ZnO, wherein the colored glass article comprises: a transmittance color coordinate in the CIELAB color space comprising an L*value greater than or equal to 55 and less than or equal to 96.5 as measured under F2 illumination and a 10° standard observer angle; a compressive stress profile with a depth of compression greater than or equal to 0.15t where t is a thickness of the colored glass article, a compressive stress greater than or equal to 200 MPa, and a central tension greater than or equal to 60 MPa; a dielectric constant from 5.6 to 6.4 over a frequency range from 10 GHz to 60 GHz; and the thickness t is greater than or equal to 0.4 mm and less than or equal to 5 mm.

Aspect A49 includes the colored glass article of aspect A48, wherein the thickness t is greater than or equal to 0.5 mm and less than or equal to 5 mm.

Aspect A50 includes the colored glass article of any preceding aspect, wherein a colored glass article having the same composition and microstructure as a center of the colored glass article has a fracture toughness K_IC greater than or equal to 0.7 MPa·m^1/2.

Aspect A51 includes the colored glass article of any preceding aspect comprising an average transmittance of greater than or equal to 10% and less than or equal to 92% over the wavelength range of 380 nm to 750 nm.

Aspect A52 includes the colored glass article of any preceding aspect further comprising at least one crystalline phase.

Aspect A53 includes the colored glass article of any preceding aspect comprising a crystallinity of less than 10 wt %.

Aspect A54 includes the colored glass article of any preceding aspect, wherein the depth of compression is less than or equal to 0.3t.

Aspect A55 includes the colored glass article of any preceding aspect, wherein the surface compressive stress is greater than or equal to 400 MPa.

Aspect A56 includes the colored glass article of any preceding aspect, wherein the central tension is greater than or equal to 70 MPa.

Aspect A57 includes the colored glass article of any preceding aspect, wherein the transmittance color coordinate in the CIELAB color space comprises an a* value and |a*| is ≥0.3.

Aspect A58 includes the colored glass article of any preceding aspect, wherein the transmittance color coordinate in the CIELAB color space comprises a b* value and |b*| is ≥0.5.

Aspect A59 includes the colored glass article of any preceding aspect, wherein the transmittance color coordinate in the CIELAB color space comprises an a* value and a b* value, wherein |a*| is ≥0.3 and |b*| is ≥0.5.

Aspect A60 includes the colored glass article of any preceding aspect, wherein the transmittance color coordinate in the CIELAB color space comprises a* and b* values within a region of a plot of a* vs. b* bound by the intersection of lines: b*=0.2879·a*+27.818; b*=7.0833·a*−94.5; b*=0.45·a*+104.5; and b*=15.3·a*+253.

Aspect A61 includes the colored glass article of aspect A60, wherein the colorant comprises Ag.

Aspect A61 includes the colored glass article of any of aspects A48-A59, wherein the transmittance color coordinate in the CIELAB color space comprises a* and b* values within a region of a plot of a* vs. b* bound by the intersection of lines: b*=7.0833·a*−94.5; b*=−0.9583·a*+146.75; b*=2.6957·a*−50.565; and b*=33.

Aspect A62 includes the colored glass article of aspect A61 wherein the colorant comprises Ag.

Aspect A63 includes the colored glass article of any of aspects A48-A59, wherein the transmittance color coordinate in the CIELAB color space comprises a* and b* values within a region of a plot of a* vs. b* bound by the intersection of lines: b*=2.6957·a*−50.565; a*=54; b*=1.0769·a*−17.154; and b*=6.6667·a*−173.67.

Aspect A64 includes the colored glass article of aspect A63 wherein the colorant comprises Ag.

Aspect A65 includes the colored glass article of any of aspects A48-A59, wherein the transmittance color coordinate in the CIELAB color space comprises a* and b* values within a region of a plot of a* vs. b* bound by the intersection of lines: b*=0.2879·a*+27.818; a*=0; b*=−1.375·a*+1; and b*=9.333·a*+86.667, exclusive of a* greater than −0.3 and less than 0.3 and exclusive of b* greater than −0.5 and less than 0.5.

Aspect A66 includes the colored glass article of aspect A65, wherein the colorant comprises Ag.

Aspect A67 includes the colored glass article of any of aspects A48-A59, wherein the transmittance color coordinate in the CIELAB color space comprises a* and b* values within a region of a plot of a* vs. b* bound by the intersection of lines: b*=0.0833·a*+20.833; b*=2.1182·a*−32.073; b*=−0.3; and b*=1.5929·a*−0.3, exclusive of a* greater than −0.3 and less than 0.3 and exclusive of b* greater than −0.5 and less than 0.5.

Aspect A68 includes the colored glass article of aspect A67, wherein the colorant comprises Ag.

Aspect A69 includes the colored glass article of any of aspects A58-A59, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −18 and less than or equal to 0.3 and b* values greater than or equal to 0.5 and less than or equal to 82.

Aspect A70 includes the colored glass article of claim A69, wherein the colorant comprises Cr₂O₃.

Aspect A71 includes the colored glass article of any of aspects A48-A59, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −18 and less than or equal to 18, exclusive of a* greater than −0.3 and less than 0.3, and b* greater than or equal to 0.5 and less than or equal to 82.

Aspect A72 includes the colored glass article of aspect A71, wherein the colorant comprises Cr₂O₃ and NiO.

Aspect A73 includes the colored glass article of any of aspects A48-A59, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −20 and less than or equal to 60, exclusive of a* greater than −0.3 and less than 0.3, and b* greater than or equal to −90 and less than or equal to 85, exclusive of b* values greater than −0.5 and less than 0.5.

Aspect A74 includes the colored glass article of aspect A73, wherein the colorant comprises Cr₂O₃ and Co₃O₄.

Aspect A75 includes the colored glass article of any of aspects A48-A59, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −35 and less than or equal to −0.3, and b* values greater than or equal to 0.5 and less than or equal to 82.

Aspect A76 includes the colored glass article of aspect A75, wherein the colorant comprises Cr₂O₃ and CuO.

Aspect A77 includes the colored glass article of any of aspects A48-A59, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −35 and less than or equal to 20, exclusive of a* greater than −0.3 and less than 0.3, and b* values greater than or equal to 0.5 and less than or equal to 75.

Aspect A78 includes the colored glass article of aspect A77, wherein the colorant comprises Cr₂O₃, NiO, and CuO.

Aspect A79 includes the colored glass article of any of aspects A48-A59, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −15 and less than or equal to 65, exclusive of a* greater than −0.3 and less than 0.3, and b* values greater than or equal to −90 and less than or equal to 80, exclusive of b* greater than −0.5 and less than 0.5.

Aspect A80 includes the colored glass article of aspect A79, wherein the colorant comprises Cr₂O₃, NiO, and Co₃O₄.

Aspect A81 includes the colored glass article of any of aspects A48-A59, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −35 and less than or equal to 60, exclusive of a* greater than −0.3 and less than 0.3, and b* values greater than or equal to −90 and less than or equal to 80, exclusive of b* greater than −0.5 and less than 0.5.

Aspect A82 includes the colored glass article of aspect A81, wherein the colorant comprises Cr₂O₃, CuO, and Co₃O₄.

Aspect A83 includes the colored glass article of any of aspects A48-A59, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −35 and less than or equal to 60, exclusive of a* greater than −0.3 and less than 0.3, and b* values greater than or equal to −90 and less than or equal to 80, exclusive of b* greater than −0.5 and less than 0.5.

Aspect A84 includes the colored glass article of aspect A83, wherein the colorant comprises Cr₂O₃, NiO, CuO, and Co₃O₄.

Aspect A84 includes the colored glass article of any of aspects A48-A59, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −15 and less than or equal to −0.3 and b* values greater than or equal to −10 and less than or equal to 10, exclusive of b* greater than −0.5 and less than 0.5.

Aspect A85 includes the colored glass article of aspect A84, wherein the colorant comprises at least one of NiO, CuO, TiO₂, Co₃O₄, Cr₂O₃, and CeO₂.

Aspect A86 includes the colored glass article of any of aspects A48-A59, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −5 and less than or equal to 25, exclusive of a* greater than −0.3 and less than 0.3, and b* greater than or equal to −20 and less than or equal to 5, exclusive of b* greater than −0.5 and less than 0.5.

Aspect A87 includes the colored glass article of aspect A86, wherein the colorant comprises Au.

Aspect A88 includes the colored glass article of any of aspects A48-A59, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −10 and less than or equal to 25, exclusive of a* greater than −0.3 and less than 0.3, and b* values greater than or equal to −20 and less than or equal to 5, exclusive of b* greater than −0.5 and less than 0.5.

Aspect A89 includes the colored glass article of aspect A88, wherein the colorant comprises Au.

Aspect A90 includes the colored glass article of any of aspects A48-A59, wherein the transmittance color coordinate in the CIELAB color space comprises a* values greater than or equal to −15 and less than or equal to −0.3, and b* values greater than or equal to −10 and less than or equal to 10, exclusive of b* greater than −0.5 and less than 0.5.

Aspect A91 includes the colored glass article of aspect A90, wherein the colorant comprises at least one of Cr₂O₃, Au, Ag, CuO, NiO, Co₃O₄, TiO₂, and CeO₂.

Aspect A92 includes an electronic device comprising a housing, the housing comprising a colored glass article according to any preceding aspect.

Additional features and advantages of the colored glass articles described herein will be set forth in the detailed description that follows, and in part will be readily apparent to those skilled in the art from that description or recognized by practicing the embodiments described herein, including the detailed description which follows, the claims, as well as the appended drawings.

It is to be understood that both the foregoing general description and the following detailed description describe various embodiments and are intended to provide an overview or framework for understanding the nature and character of the claimed subject matter. The accompanying drawings are included to provide a further understanding of the various embodiments, and are incorporated into and constitute a part of this specification. The drawings illustrate the various embodiments described herein, and together with the description serve to explain the principles and operations of the claimed subject matter.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a plan view of an electronic device incorporating any of the colored glass articles according to one or more embodiments described herein;

FIG. 2 is a perspective view of the electronic device of FIG. 1;

FIG. 3A is a plot of a* vs. b* CIELAB space (x-axis: a*; y-axis: b*) as a function of a heat treatment temperature of a colored glass article made from a glass composition according to one or more embodiments described herein;

FIG. 3B is a plot of a projected a* vs. L*CIELAB space (x-axis: a*; y-axis: L*) of the colored glass article of FIG. 3A;

FIG. 3C is a plot of a projected b* vs. L*CIELAB space (x-axis: b*; y-axis: L*) of the colored glass article of FIG. 3A;

FIG. 4A is a plot of a* vs. b* CIELAB space (x-axis: a*; y-axis: b*) as a function of a heat treatment temperature of a colored glass article made from a glass composition according to one or more embodiments described herein;

FIG. 4B is a plot of a projected a* vs. L*CIELAB space (x-axis: a*; y-axis: L*) of the colored glass article of FIG. 4A;

FIG. 4C is a plot of a projected b* vs. L*CIELAB space (x-axis: b*; y-axis: L*) of the colored glass article of FIG. 4A;

FIG. 5A is a plot of a* vs. b* CIELAB space (x-axis: a*; y-axis: b*) as a function of a heat treatment temperature of a colored glass article made from a glass composition according to one or more embodiments described herein;

FIG. 5B is a plot of a projected a* vs. L*CIELAB space (x-axis: a*; y-axis: L*) of the colored glass article of FIG. 5A;

FIG. 5C is a plot of a projected b* vs. L*CIELAB space (x-axis: b*; y-axis: L*) of the colored glass article of FIG. 5A;

FIG. 6A is a plot of a* vs. b* CIELAB space (x-axis: a*; y-axis: b*) as a function of a heat treatment temperature of a colored glass article made from a glass composition according to one or more embodiments described herein;

FIG. 6B is a plot of a projected a* vs. L*CIELAB space (x-axis: a*; y-axis: L*) of the colored glass article of FIG. 6A;

FIG. 6C is a plot of a projected b* vs. L*CIELAB space (x-axis: b*; y-axis: L*) of the colored glass article of FIG. 6A;

FIG. 7 is a plot of R₂O—Al₂O₃ vs. a* CIELAB space (x-axis: R₂O—Al₂O₃; y-axis: a*) of colored glass articles made from glass compositions and subjected to a heat treatment according to one or more embodiments described herein;

FIG. 8 is a plot of R₂O—Al₂O₃ vs. b* CIELAB space (x-axis: R₂O—Al₂O₃; y-axis: b*) of colored glass articles made from glass compositions and subjected to a heat treatment according to one or more embodiments described herein;

FIG. 9 is a plot of a projected a* vs. b* CIELAB space (x-axis: a*; y-axis: b*) of a colored glass article made from a glass composition according to one or more embodiments described herein;

FIG. 10 is a plot of a projected a* vs. L*CIELAB space (x-axis: a*; y-axis: L*) of the colored glass article of FIG. 9;

FIG. 11 is a plot of a projected b* vs. L*CIELAB space (x-axis: b*; y-axis: L*) of the colored glass article of FIG. 9;

FIG. 12 is a plot of a projected a* vs. b* CIELAB space (x-axis: a*; y-axis: b*) of a colored glass article made from a glass composition according to one or more embodiments described herein;

FIG. 13 is a plot of a projected a* vs. L*CIELAB space (x-axis: a*; y-axis: L*) of the colored glass article of FIG. 12;

FIG. 14 is a plot of a projected b* vs. L*CIELAB space (x-axis: b*; y-axis: L*) of the colored glass article of FIG. 12;

FIG. 15 is a plot of a projected a* vs. b* CIELAB space (x-axis: a*; y-axis: b*) of a colored glass article made from a glass composition according to one or more embodiments described herein;

FIG. 16 is a plot of a projected a* vs. L*CIELAB space (x-axis: a*; y-axis: L*) of the colored glass article of FIG. 15;

FIG. 17 is a plot of a projected b* vs. L*CIELAB space (x-axis: b*; y-axis: L*) of the colored glass article of FIG. 15;

FIG. 18 is a plot of a projected a* vs. b* CIELAB space (x-axis: a*; y-axis: b*) of a colored glass article made from a glass composition according to one or more embodiments described herein;

FIG. 19 is a plot of a projected a* vs. L*CIELAB space (x-axis: a*; y-axis: L*) of the colored glass article of FIG. 18;

FIG. 20 is a plot of a projected b* vs. L*CIELAB space (x-axis: b*; y-axis: L*) of the colored glass article of FIG. 18;

FIG. 21 is a plot of a projected a* vs. b* CIELAB space (x-axis: a*; y-axis: b*) of a colored glass article made from a glass composition according to one or more embodiments described herein;

FIG. 22 is a plot of a projected a* vs. L*CIELAB space (x-axis: a*; y-axis: L*) of the colored glass article of FIG. 21;

FIG. 23 is a plot of a projected b* vs. L*CIELAB space (x-axis: b*; y-axis: L*) of the colored glass article of FIG. 21;

FIG. 24 is a plot of a projected a* vs. b* CIELAB space (x-axis: a*; y-axis: b*) of a colored glass article made from a glass composition according to one or more embodiments described herein;

FIG. 25 is a plot of a projected a* vs. L*CIELAB space (x-axis: a*; y-axis: L*) of the colored glass article of FIG. 24;

FIG. 26 is a plot of a projected b* vs. L*CIELAB space (x-axis: b*; y-axis: L*) of the colored glass article of FIG. 24;

FIG. 27 is a plot of a projected a* vs. b* CIELAB space (x-axis: a*; y-axis: b*) of a colored glass article made from a glass composition according to one or more embodiments described herein;

FIG. 28 is a plot of a projected a* vs. L*CIELAB space (x-axis: a*; y-axis: L*) of the colored glass article of FIG. 27;

FIG. 29 is a plot of a projected b* vs. L*CIELAB space (x-axis: b*; y-axis: L*) of the colored glass article of FIG. 27;

FIG. 30 is a plot of a projected a* vs. b* CIELAB space (x-axis: a*; y-axis: b*) of a colored glass article made from a glass composition according to one or more embodiments described herein;

FIG. 31 is a plot of a projected a* vs. L*CIELAB space (x-axis: a*; y-axis: L*) of the colored glass article of FIG. 30;

FIG. 32 is a plot of a projected b* vs. L*CIELAB space (x-axis: b*; y-axis: L*) of the colored glass article of FIG. 30;

FIG. 33A graphically depicts a plot of projected a* vs. L*CIELAB spaces (y-axis: a*; x-axis: L*) of colored glass articles according to one or more embodiments of the present disclosure;

FIG. 33B graphically depicts a plot of projected b* vs. L*CIELAB spaces (y-axis: b*; x-axis: L*) of colored glass articles according to one or more embodiments of the present disclosure;

FIG. 33C graphically depicts a plot of projected a* vs. b* CIELAB spaces (y-axis: b*; x-axis: a*) of colored glass articles according to one or more embodiments of the present disclosure;

FIG. 34A graphically depicts a plot of projected a* vs. L*CIELAB spaces (y-axis: a*; x-axis: L*) of colored glass articles according to one or more embodiments of the present disclosure;

FIG. 34B graphically depicts a plot of projected b* vs. L*CIELAB spaces (y-axis: b*; x-axis: L*) of colored glass articles according to one or more embodiments of the present disclosure;

FIG. 34C graphically depicts a plot of projected a* vs. b* CIELAB spaces (y-axis: b*; x-axis: a*) of colored glass articles according to one or more embodiments of the present disclosure;

FIG. 35 graphically depicts absorbance spectra (y-axis) as a function of wavelength (x-axis) of colored glass articles according to one or more embodiments of the present disclosure;

FIG. 36 graphically depicts absorbance spectra (y-axis) as a function of wavelength (x-axis) of colored glass articles according to one or more embodiments of the present disclosure;

FIG. 37 graphically depicts absorbance spectra (y-axis) as a function of wavelength (x-axis) of colored glass articles according to one or more embodiments of the present disclosure;

FIG. 38 graphically depicts absorbance spectra (y-axis) as a function of wavelength (x-axis) of colored glass articles according to one or more embodiments of the present disclosure;

FIG. 39 graphically depicts absorbance (y-axis) as a function of wavelength (x-axis) spectra of colored glass articles according to one or more embodiments of the present disclosure;

FIG. 40A graphically depicts a plot of a projected a* vs. L*CIELAB space (y-axis: a*; x-axis: L*) of a colored glass article according to one or more embodiments of the present disclosure;

FIG. 40B graphically depicts a plot of a projected b* vs. L*CIELAB space (y-axis: b*; x-axis: L*) of a colored glass article according to one or more embodiments of the present disclosure;

FIG. 40C graphically depicts a plot of a projected a* vs. b* CIELAB space (y-axis: b*; x-axis: a*) of a colored glass article according to one or more embodiments of the present disclosure;

FIG. 41 graphically depicts an absorbance spectra (y-axis) as a function of wavelength (x-axis) of colored glass articles according to one or more embodiments of the present disclosure;

FIG. 42A graphically depicts a plot of a projected b* vs. L*CIELAB space (y-axis: b*; x-axis: L*) of a colored glass article according to one or more embodiments of the present disclosure;

FIG. 42B graphically depicts a plot of a projected a* vs. b* CIELAB space (y-axis: b*; x-axis: a*) of a colored glass article according to one or more embodiments of the present disclosure;

FIG. 42C graphically depicts a plot of a projected a* vs. L*CIELAB space (y-axis: a*; x-axis: L*) of a colored glass article according to one or more embodiments of the present disclosure;

FIG. 43 graphically depicts an absorbance spectra (y-axis) as a function of wavelength (x-axis) of a colored glass article according to one or more embodiments of the present disclosure;

FIG. 44A is a transmission electron microscopy (TEM) micrograph of anisotropic silver particles in a colored glass article according to one or more embodiments of the present disclosure;

FIG. 44B is a magnified view of a portion of the TEM micrograph of FIG. 44A showing an anisotropic silver particle in a colored glass article according to one or more embodiments of the present disclosure;

FIG. 44C is a magnified view of a portion of the TEM micrograph of FIG. 44B showing an anisotropic silver particle in a colored glass article according to one or more embodiments of the present disclosure;

FIG. 45 graphically depicts a transmittance spectra (y-axis) as a function of wavelength (x-axis) of a colored glass article heat treated at the same temperature for different heat treatment times, according to one or more embodiments of the present disclosure;

FIG. 46 graphically depicts a transmittance spectra (y-axis) as a function of wavelength (x-axis) of a colored glass article according to one or more embodiments of the present disclosure;

FIG. 47 graphically depicts a transmittance spectra (y-axis) as a function of wavelength (x-axis) of a colored glass article according to one or more embodiments of the present disclosure;

FIG. 48 is graphically depicts a plot of a projected a* vs. b* CIELAB space (y-axis: b*; x-axis: a*) of colored glass articles according to one or more embodiments of the present disclosure;

FIG. 49 is a schematic representation of a sample utilized in the double cantilever beam (DCB) procedure to determine the fracture toughness K_IC and a cross-section thereof;

FIG. 50 graphically depicts the results of an incremental face drop on sandpaper (i.e., a “drop test”) for select inventive examples and a comparative example;

FIG. 51 schematically depicts a drop test conducted on ion exchange strengthened colored glass articles;

FIG. 52 is a plot of b* as a function of Fe₂O₃ content for a variety of glass compositions according to one or more embodiments of the present disclosure;

FIG. 53 is a plot of b* as a function of a* for glass compositions with various SnO₂ contents as labelled according to one or more embodiments of the present disclosure;

FIG. 54 is a plot of titanium oxidation state content as measured by XPS for glass articles subjected to various heat treatments; and

FIG. 55 is a plot of Ti³⁺ oxidation state fraction as detected by XPS as a function of function of Fe₂O₃ content for a variety of glass compositions and annealing treatments according to one or more embodiments of the present disclosure.

DETAILED DESCRIPTION

Reference will now be made in detail to various embodiments of glass compositions and colored glass articles formed therefrom having a desired color. According to embodiments, a colored glass article includes: greater than or equal to 50 mol % and less than or equal to 80 mol % SiO₂; greater than or equal to 7 mol % and less than or equal to 20 mol % Al₂O₃; greater than or equal to 1 mol % and less than or equal to 35 mol % R₂O, wherein R₂O comprises at least one of Li₂O, Na₂O, and K₂O; greater than 1×10⁻⁶ mol % and less than or equal to 10 mol % of a colorant, wherein the colorant comprises at least one of Cr₂O₃, Au, Ag, CuO, NiO, Co₃O₄, TiO₂, CeO₂; and greater than or equal to 12 mol % and less than or equal to 24 mol % of Al₂O₃+MgO+CaO+ZnO. The colored glass article may further include a transmittance color coordinate in the CIELAB color space comprising an L*value greater than or equal to 55 and less than or equal to 96.5 as measured under F2 illumination and a 10° standard observer angle; a compressive stress profile with a depth of compression greater than or equal to 0.15t where t is a thickness of the colored glass article, a compressive stress greater than or equal to 200 MPa, and a central tension greater than or equal to 60 MPa; a dielectric constant from 5.6 to 6.4 over a frequency range from 10 GHz to 60 GHz; and the thickness t is greater than or equal to 0.4 mm and less than or equal to 5 mm. Various embodiments of colored glass articles will be described herein with specific reference to the appended drawings.

Ranges may be expressed herein as from “about” one particular value, and/or to “about” another particular value. When such a range is expressed, another embodiment includes from the one particular value and/or to the other particular value. Similarly, when values are expressed as approximations, by use of the antecedent “about,” it will be understood that the particular value forms another embodiment. It will be further understood that the endpoints of each of the ranges are significant both in relation to the other endpoint, and independently of the other endpoint.

Directional terms as used herein—for example up, down, right, left, front, back, top, bottom—are made only with reference to the figures as drawn and are not intended to imply absolute orientation.

Unless otherwise expressly stated, it is in no way intended that any method set forth herein be construed as requiring that its steps be performed in a specific order, nor that with any apparatus specific orientations be required. Accordingly, where a method claim does not actually recite an order to be followed by its steps, or that any apparatus claim does not actually recite an order or orientation to individual components, or it is not otherwise specifically stated in the claims or description that the steps are to be limited to a specific order, or that a specific order or orientation to components of an apparatus is not recited, it is in no way intended that an order or orientation be inferred, in any respect. This holds for any possible non-express basis for interpretation, including: matters of logic with respect to arrangement of steps, operational flow, order of components, or orientation of components; plain meaning derived from grammatical organization or punctuation, and; the number or type of embodiments described in the specification.

As used herein, the singular forms “a,” “an” and “the” include plural referents unless the context clearly dictates otherwise. Thus, for example, reference to “a” component includes aspects having two or more such components, unless the context clearly indicates otherwise.

In the embodiments of the glass compositions and the resultant colored glass articles described herein, the concentrations of constituent components in oxide form (e.g., SiO₂, Al₂O₃, and the like) are specified in mole percent (mol %) on an oxide basis, unless otherwise specified.

In embodiments of the glass compositions and the resultant colored glass articles described herein, the concentrations of Au and Cl are specified in mole percent (mol %), unless otherwise specified.

In embodiments of the glass compositions and the resultant colored glass articles described herein, the concentration of a cation “M” is specified in mole percent (mol %), unless otherwise specified.

The term “substantially free,” when used to describe the concentration and/or absence of a particular constituent component in a glass composition and the resultant colored glass article, means that the constituent component is not intentionally added to the glass composition and the resultant colored glass article. However, the glass composition and the resultant colored glass article may contain traces of the constituent component as a contaminant or tramp in amounts of less than 200 ppm unless specified otherwise herein. It is noted that the definition of “substantially free” is exclusive of gold (Au) which may be intentionally added to the glass composition in relatively small amounts such as, for example and without limitation, amounts less than 200 ppm (or the equivalent in mol %) to achieve a desired color in the resultant colored glass article.

The terms “0 mol %” and “free,” when used to describe the concentration and/or absence of a particular constituent component in a glass composition, means that the constituent component is not present in the glass composition.

Fracture toughness (K_IC) represents the ability of a glass composition to resist fracture. Fracture toughness is measured on a non-strengthened glass article, such as measuring the K_IC value prior to ion exchange (IOX) treatment of the glass article, thereby representing a feature of a glass substrate prior to IOX. The fracture toughness test methods described herein are not suitable for glasses that have been exposed to IOX treatment. Accordingly, where the fracture toughness of an ion exchanged article is referred to, it means the fracture toughness of a non-ion exchanged article with the same composition and microstructure (when present) as the center (i.e., a point located at least 0.5t from every surface of the article or substrate where t is the thickness of the article or substrate) of the ion exchanged article (which corresponds to the portion of the ion exchanged article least affected by the ion exchange process and, hence, a composition and microstructure comparable to a non-ion exchanged glass). Fracture toughness is measured by the chevron notched short bar method. The chevron notched short bar (CNSB) method is disclosed in Reddy, K. P. R. et al, “Fracture Toughness Measurement of Glass and Ceramic Materials Using Chevron-Notched Specimens,” J. Am. Ceram. Soc., 71 [6], C-310-C-313 (1988) except that Y*_m is calculated using equation 5 of Bubsey, R. T. et al., “Closed-Form Expressions for Crack-Mouth Displacement and Stress Intensity Factors for Chevron-Notched Short Bar and Short Rod Specimens Based on Experimental Compliance Measurements,” NASA Technical Memorandum 83796, pp. 1-30 (October 1992). Unless otherwise specified, all fracture toughness values were measured by chevron notched short bar (CNSB) method.

Alternative K_IC fracture toughness measurements were performed on some samples with the double cantilever beam (DCB) procedure. The DCB specimen geometry is shown in FIG. 49 with parameters being the crack length a, applied load P, cross-sectional dimensions w and 2 h, and the thickness of the crack-guiding groove b. The samples were cut into rectangles of width 2 h=1.25 cm and a thickness ranging from, w=0.3 mm to 1 mm, with the overall length of the sample, which is not a critical dimension, varying from 5 cm to 10 cm. A hole was drilled on both ends with a diamond drill to provide a means of attaching the sample to a sample holder and to the load. A crack “guiding groove” was cut down the length of the sample on both flat faces using a wafer dicing saw with a diamond blade, leaving a “web” of material, approximately half the total plate thickness (dimension b in FIG. 49), with a height of 180 m corresponding to the blade thickness. The high precision dimensional tolerances of the dicing saw allow for minimal sample-to-sample variation. The dicing saw was also used to cut an initial crack where a=15 mm. As a consequence of this final operation a very thin wedge of material was created near the crack tip (due to the blade curvature) allowing for easier crack initiation in the sample. The samples were mounted in a metal sample holder with a steel wire in the bottom hole of the sample. The samples were also supported on the opposite end to keep the samples level under low loading conditions. A spring in series with a load cell (FUTEK, LSB200) was hooked to the upper hole which was then extended, to gradually apply load, using rope and a high precision slide. The crack was monitored using a microscope having a 5 μm resolution attached to a digital camera and a computer. The applied stress intensity, K_P, was calculated using the following equation:

$K_P=\left[\frac{P·a}{{\left(w·b\right)}^{0.5}{h}^{1.5}}\right]\left[3.47+2.32\frac{h}{a}\right]$

For each sample, a crack was first initiated at the tip of the web, and then the starter crack was carefully sub-critically grown until the ratio of dimensions a/h was greater than 1.5 to accurately calculate stress intensity. At this point the crack length, a, was measured and recorded using a traveling microscope with 5 μm resolution. A drop of toluene was then placed into the crack groove and wicked along the length of the groove by capillary forces, pinning the crack from moving until the fracture toughness is reached. The load was then increased until sample fracture occurred, and the critical stress intensity K_IC calculated from the failure load and sample dimensions, with K_P being equivalent to K_IC due to the measurement method.

The viscosity of the glass composition, as described herein, is measured according to ASTM C965-96.

The term “melting point,” as used herein, refers to the temperature at which the viscosity of the glass composition is 200 poise.

The term “softening point,” as used herein, refers to the temperature at which the viscosity of the glass composition is 1×10^7.6 poise. The softening point is measured according to the parallel plate viscosity method which measures the viscosity of inorganic glass from 10⁷ to 109 poise as a function of temperature, similar to ASTM C1351M.

The term “annealing point” as used herein, refer to the temperature at which the viscosity of the glass composition is 1×10^13.18 poise.

The term “strain point,” as used herein, refers to the temperature at which the viscosity of the glass composition is 1×10^14.68 poise.

The term “coefficient of thermal expansion” and “CTE,” as described herein, is measured in accordance with ASTM E228-85 over the temperature range of 25° C. to 300° C. and is expressed in terms of “×10⁻⁷/° C.” as an average over the temperature range.

The term “liquidus viscosity,” as used herein, refers to the viscosity of the glass composition at the onset of devitrification (i.e., at the liquidus temperature as determined with the gradient furnace method according to ASTM C829-81).

The term “liquidus temperature,” as used herein, refers to the temperature at which the glass composition begins to devitrify as determined with the gradient furnace method according to ASTM C829-81.

Surface compressive stress is measured with a surface stress meter (FSM) such as commercially available instruments such as the FSM-6000, manufactured by Orihara Industrial Co., Ltd. (Japan). Surface stress measurements rely upon the measurement of the stress optical coefficient (SOC), which is related to the birefringence of the glass article. SOC, in turn, is measured according to Procedure C (Glass Disc Method) described in ASTM standard C770-16, entitled “Standard Test Method for Measurement of Glass Stress-Optical Coefficient,” the contents of which are incorporated herein by reference in their entirety. Depth of compression (DOC) is also measured with the FSM. The maximum central tension (CT) values are measured using a scattered light polariscope (SCALP) technique known in the art.

The term “depth of compression” (DOC), as used herein, refers to the position in the article where compressive stress transitions to tensile stress.

Transmittance data (total transmittance and diffuse transmittance) in the visible spectrum is measured with a Lambda 950 UV/Vis/NIR Spectrophotometer manufactured by PerkinElmer Inc. (Waltham, Massachusetts USA). The Lambda 950 apparatus was fitted with a 150 mm integrating sphere. Data was collected using an open beam baseline and a Spectralon® reference reflectance disk. For total transmittance (Total Tx), the sample is fixed at the integrating sphere entry point.

The term “average transmittance,” as used herein with respect to the visible spectrum, refers to the average of transmittance measurements made within a given wavelength range with each whole numbered wavelength weighted equally. In embodiments described herein, the “average transmittance” with respect to the visible spectrum is reported over the wavelength range from 380 nm to 750 nm (inclusive of endpoints). Unless otherwise specified, the average transmittance is indicated for article thicknesses from 0.4 mm to 5 mm, inclusive of endpoints. Unless otherwise specified, when average transmittance is indicated, this means that each thickness within the range of thicknesses from 0.4 mm to 5 mm has an average transmittance as specified. For example, colored glass articles having average transmittances of 10% to 92% over the wavelength range from 380 nm to 750 nm means that each thickness within the range of 0.4 mm to 5 mm (e.g., 0.6 mm, 0.9 mm, 2 mm, etc.) has an average transmittance in the range of 10% to 92% for the wavelength range from 380 nm to 750 nm.

The term “CIELAB color space,” as used herein, refers to a color space defined by the International Commission on Illumination (CIE) in 1976. It expresses color as three values: L*for the lightness from black (0) to white (100), a* from green (−) to red (+), and b* from blue (−) to yellow (+). Unless otherwise specified, the L*, a*, and b* values are indicated for article thicknesses of 0.4 mm to 5 mm (inclusive of endpoints) in the thickness direction of the sample under F2 illumination and a 100 standard observer angle. Unless otherwise specified, this means that each thickness within the range of thicknesses has L*, a*, and b* coordinates falling within the specified range(s) for L*, a*, and b* coordinates. For example, a colored glass article having an L*value within the range from 55 to 96.5 means that each thickness within the range of 0.4 mm to 5 mm (e.g., 0.6 mm, 0.9 mm, 2 mm, etc.) has an L*in the range of 55 to 96.5.

The term “color gamut,” as used herein, refers to the pallet of colors that may be achieved by the colored glass articles within the CIELAB color space.

The “optical transmission spectra,” described herein, were obtained using an Agilent Cary 60 spectrophotometer with a scan range of 250 nm to 800 nm, a scan step of 2 nm, a signal average of 0.5 s, and a spot size of 2 mm. The optical transmission data obtained were used to plot coordinates in the CIELAB color space as described in R. S. Berns, Billmeyer and Saltzman's Principles of Color Technology, 3rd. Ed., John Wiley & Sons, New York (2000).

The term “projected color gamut,” as used herein, refers to the line, surface, volume, or overlapping volume occupied by the colored glass article within the three-dimensional CIELAB color space and represents the pallet of colors that may be achieved by the colored glass articles within the CIELAB color space based upon the concentration of colorant(s) present in the colored glass article. The projected color gamuts shown herein were produced using the plotting routine Gnuplot Version 5.4. Specifically, Gnuplot was used to display projections of the CIELAB color coordinates for the transmitted colors under F2 illumination for the CIE 1976 10° Standard Observer. The transmittance spectrum through a flat sheet of glass is given by the following expression:

$T\left(\lambda \right)=\frac{{\left[1-R\left(\lambda \right)\right]}^2\times \exp \left[-{\sum }_i{N}_i{\sigma }_i\left(\lambda \right)t\right]}{1-{R\left(\lambda \right)}^2\times \exp \left[-2{\sum }_i{N}_i{\sigma }_i\left(\lambda \right)t\right]},$

where R is the Fresnel intensity reflection coefficient of the glass, N_i and σ_i represent the number density and absorption cross section, respectively, for the individual dopants, λ is the optical wavelength, and t is the thickness of the glass. The color coordinates were calculated from the transmittance spectra through 1.5 mm of the colored glass article. The expression for the transmittance was evaluated by varying the dopant concentrations (N_i) for the combinations of the colorants from 0 to a maximum value. As described herein, the maximum values for Cr₂O₃, NiO, CuO, and Co₃O₄ were set to 2 mol %, 4 mol %, 20 mol %, and 2 mol %, respectively for purposes of determining the projected color gamut.

The dielectric constant of the colored glass articles may be measured using a split post dielectric resonator (SPDR), as is known in the art, at a frequency of 10 GHz. The dielectric constant was measured on samples of the colored glass article having a length of 3 inches (76.2 mm), a width of 3 inches (76.2 mm), and a thickness of less than 0.9 mm.

The dielectric constant of the colored glass articles may also be measured over a range of frequencies from 10 GHz to 60 GHz using a double concave reflecting mirror Fabry-Perot open resonator, as is known in the art. The dielectric constant can be measured at different frequencies by adjusting the mirror spacing in the open resonator. The dielectric constant may be measured on samples of the colored glass article having a length of 120 mm, a width of 120 mm, and a thickness of 2 mm or less. While not wishing to be bound by theory, it is believed that the dielectric constant of the colored glass articles measured at 10 GHz approximates the dielectric constant at each frequency in the range from 10 GHz to 60 GHz.

The dielectric constant Dk of the colored glass article may be calculated according to the equation:

$\mathrm{Dk}=3.802946+0.01747*B_2{O}_3\left(\mathrm{mol}\%\right)+0.058769*{\mathrm{Al}}_2{O}_3\left(\mathrm{mol}\%\right)+0.080876*{\mathrm{Li}}_{2}O\left(\mathrm{mol}\%\right)+0.148433*{\mathrm{Na}}_{2}O\left(\mathrm{mol}\%\right)+0.153264*K_{2}O\left(\mathrm{mol}\%\right)+0.045179*\mathrm{MgO}\left(\mathrm{mol}\%\right)+0.080113*\mathrm{CaO}\left(\mathrm{mol}\%\right).$

Colorants have been added to conventional aluminosilicate glass compositions to achieve glass articles having a desired color. However, such glass articles may not have the desired mechanical or electrical properties suitable for some end user applications. For example, glasses used in the housings of consumer electronic devices may require robust mechanical properties to withstand the rigors of day-to-day use and/or dielectric properties to allow for reception of wireless signals by the device.

Moreover, it may be desirable to have colored glass articles having mechanical and dielectric properties such that the glass article is suitable for use with consumer electronic devices while also providing the same colored glass articles in a range of different colors. However, simply including colorants in aluminosilicate glass compositions may not produce the desired color. For example, some colorants may have relatively low vaporization temperatures and may vaporize and diffuse out of the glass during manufacturing. The relatively low retention of the colorant limits the color gamut that may be achieved.

Disclosed herein are glass compositions and colored glass articles formed therefrom having superior ion-exchange performance. The colored glass articles also have dielectric properties, such as dielectric constants, such that the glass articles are suitable for use as enclosures for consumer electronic devices such as smart phones, tablets, and computers. The use of various colorants and combinations of colorants expands the color gamut that may be achieved in the resultant colored glass articles

The glass compositions and colored glass articles described herein may be described as aluminoborosilicate glass compositions and colored glass articles and comprise SiO₂, Al₂O₃, and B₂O₃. In addition to SiO₂, Al₂O₃, and B₂O₃, the glass compositions and colored glass articles described herein include one or more colorants in a colorant package to impart a desired color to the resultant colored glass article. The glass compositions and colored glass articles described herein also include alkali oxides, such as Li₂O and Na₂O, to enable the ion-exchangeability of the colored glass articles. In embodiments, the glass compositions and colored glass articles described herein may further include other components to improve colorant retention and produce colored glass articles having the desired color. In embodiments, the difference between R₂O and Al₂O₃ (i.e. R₂O (mol %)—Al₂O₃ (mol %)) in the glass compositions and resultant colored glass articles described herein may be adjusted to produce a desired observable color (e.g., pink, purple, red, orange, or blue). In embodiments, the viscosity of the glass composition may be adjusted to prevent devitrification of the glass composition.

SiO₂ is the primary glass former in the glass compositions described herein and may function to stabilize the network structure of the colored glass articles. The concentration of SiO₂ in the glass compositions and resultant colored glass articles should be sufficiently high (e.g., greater than or equal to 40 mol %) to enhance the chemical durability of the glass composition and, in particular, the resistance of the glass composition to degradation upon exposure to acidic solutions, basic solutions, and in water. The amount of SiO₂ may be limited (e.g., to less than or equal to 80 mol %) to control the melting point of the glass composition, as the melting point of pure SiO₂ or high SiO₂ glasses is undesirably high. Thus, limiting the concentration of SiO₂ may aid in improving the meltability and the formability of the resultant colored glass article.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 40 mol % and less than or equal to 80 mol % SiO₂ or even 50 mol % and less than or equal to 80 mol % SiO₂. In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 45 mol % and less than or equal to 67 mol % SiO₂ or even greater than or equal to 53 mol % and less than or equal to 67 mol % SiO₂. In embodiments, the concentration of SiO₂ in the glass composition and the resultant colored glass article may be greater than or equal to 40 mol %, greater than or equal to 45 mol %, greater than or equal to 50 mol %, greater than or equal to 52 mol %, greater than or equal to 53 mol %, greater than or equal to 54 mol %, greater than or equal to 55 mol %, greater than or equal to 56 mol %, greater than or equal to 57 mol %, greater than or equal to 58 mol %, or even greater than or equal to 60 mol %. In embodiments, the concentration of SiO₂ in the glass composition and the colored resultant glass article may be less than or equal to 80 mol %, less than or equal to 75 mol %, less than or equal to 73 mol %, less than or equal to 71 mol %, less than or equal to 70 mol %, less than or equal to 68 mol %, less than or equal to 67 mol %, less than or equal to 66 mol %, less than or equal to 65 mol %, less than or equal to 64 mol %, less than or equal to 63 mol %, less than or equal to 62 mol %, less than or equal to 61 mol %, less than or equal to 60 mol %, or even less than or equal to 59 mol %. In embodiments, the concentration of SiO₂ in the glass composition and the resultant colored glass article may be greater than or equal to 40 mol % and less than or equal to 70 mol %, greater than or equal to 40 mol % and less than or equal to 67 mol %, greater than or equal to 40 mol % and less than or equal to 65 mol % greater than or equal to 40 mol % and less than or equal to 63 mol %, greater than or equal to 40 mol % and less than or equal to 62 mol %, greater than or equal to 40 mol % and less than or equal to 61 mol %, greater than or equal to 40 mol % and less than or equal to 60 mol %, greater than or equal to 45 mol % and less than or equal to 70 mol %, greater than or equal to 45 mol % and less than or equal to 67 mol %, greater than or equal to 45 mol % and less than or equal to 65 mol % greater than or equal to 45 mol % and less than or equal to 63 mol %, greater than or equal to 45 mol % and less than or equal to 62 mol %, greater than or equal to 45 mol % and less than or equal to 61 mol %, greater than or equal to 45 mol % and less than or equal to 60 mol %, greater than or equal to 50 mol % and less than or equal to 70 mol %, greater than or equal to 50 mol % and less than or equal to 67 mol %, greater than or equal to 50 mol % and less than or equal to 65 mol %, greater than or equal to 50 mol % and less than or equal to 63 mol %, greater than or equal to 50 mol % and less than or equal to 62 mol %, greater than or equal to 50 mol % and less than or equal to 61 mol %, greater than or equal to 50 mol % and less than or equal to 60 mol %, greater than or equal to 50 mol % and less than or equal to 59 mol %, greater than or equal to 53 mol % and less than or equal to 70 mol %, greater than or equal to 53 mol % and less than or equal to 67 mol %, greater than or equal to 53 mol % and less than or equal to 65 mol % greater than or equal to 53 mol % and less than or equal to 63 mol %, greater than or equal to 53 mol % and less than or equal to 62 mol %, greater than or equal to 53 mol % and less than or equal to 61 mol %, greater than or equal to 53 mol % and less than or equal to 60 mol %, greater than or equal to 53 mol % and less than or equal to 59 mol %, greater than or equal to 55 mol % and less than or equal to 70 mol %, greater than or equal to 55 mol % and less than or equal to 67 mol %, greater than or equal to 55 mol % and less than or equal to 65 mol % greater than or equal to 55 mol % and less than or equal to 63 mol %, greater than or equal to 55 mol % and less than or equal to 62 mol %, greater than or equal to 55 mol % and less than or equal to 61 mol %, greater than or equal to 55 mol % and less than or equal to 60 mol %, greater than or equal to 55 mol % and less than or equal to 59 mol %, greater than or equal to 56 mol % and less than or equal to 70 mol %, greater than or equal to 56 mol % and less than or equal to 67 mol %, greater than or equal to 56 mol % and less than or equal to 65 mol % greater than or equal to 56 mol % and less than or equal to 63 mol %, greater than or equal to 56 mol % and less than or equal to 62 mol %, greater than or equal to 56 mol % and less than or equal to 61 mol %, greater than or equal to 56 mol % and less than or equal to 60 mol %, greater than or equal to 56 mol % and less than or equal to 59 mol %, greater than or equal to 57 mol % and less than or equal to 70 mol %, greater than or equal to 57 mol % and less than or equal to 67 mol %, greater than or equal to 57 mol % and less than or equal to 65 mol % greater than or equal to 57 mol % and less than or equal to 63 mol %, greater than or equal to 57 mol % and less than or equal to 62 mol %, greater than or equal to 57 mol % and less than or equal to 61 mol %, greater than or equal to 57 mol % and less than or equal to 60 mol %, or even greater than or equal to 57 mol % and less than or equal to 59 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the concentration of SiO₂ in the glass composition and the resultant colored glass article may be greater than or equal to 50 mol % and less than or equal to 80 mol %, greater than or equal to 50 mol % and less than or equal to 75 mol %, greater than or equal to 50 mol % and less than or equal to 73 mol %, greater than or equal to 50 mol % and less than or equal to 71 mol %, greater than or equal to 50 mol % and less than or equal to 69 mol %, greater than or equal to 52 mol % and less than or equal to 80 mol %, greater than or equal to 52 mol % and less than or equal to 75 mol %, greater than or equal to 52 mol % and less than or equal to 73 mol %, greater than or equal to 52 mol % and less than or equal to 71 mol %, greater than or equal to 52 mol % and less than or equal to 69 mol %, greater than or equal to 54 mol % and less than or equal to 80 mol %, greater than or equal to 54 mol % and less than or equal to 75 mol %, greater than or equal to 54 mol % and less than or equal to 73 mol %, greater than or equal to 54 mol % and less than or equal to 71 mol %, greater than or equal to 54 mol % and less than or equal to 69 mol %, greater than or equal to 56 mol % and less than or equal to 80 mol %, greater than or equal to 56 mol % and less than or equal to 75 mol %, greater than or equal to 56 mol % and less than or equal to 73 mol %, greater than or equal to 56 mol % and less than or equal to 71 mol %, greater than or equal to 56 mol % and less than or equal to 69 mol %, greater than or equal to 58 mol % and less than or equal to 80 mol %, greater than or equal to 58 mol % and less than or equal to 75 mol %, greater than or equal to 58 mol % and less than or equal to 73 mol %, greater than or equal to 58 mol % and less than or equal to 71 mol %, greater than or equal to 58 mol % and less than or equal to 69 mol %, greater than or equal to 50 mol % and less than or equal to 80 mol %, greater than or equal to 60 mol % and less than or equal to 75 mol %, greater than or equal to 60 mol % and less than or equal to 73 mol %, greater than or equal to 60 mol % and less than or equal to 71 mol %, or even greater than or equal to 60 mol % and less than or equal to 69 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the concentration of SiO₂ in the glass composition and the resultant colored glass article may be greater than or equal to 52 mol % and less than or equal to 70 mol %, greater than or equal to 52 mol % and less than or equal to 68 mol %, greater than or equal to 52 mol % and less than or equal to 66 mol %, greater than or equal to 52 mol % and less than or equal to 65 mol %, greater than or equal to 52 mol % and less than or equal to 64 mol %, greater than or equal to 53 mol % and less than or equal to 70 mol %, greater than or equal to 53 mol % and less than or equal to 68 mol %, greater than or equal to 53 mol % and less than or equal to 66 mol %, greater than or equal to 53 mol % and less than or equal to 65 mol %, or greater than or equal to 53 mol % and less than or equal to 64 mol %, greater than or equal to 54 mol % and less than or equal to 70 mol %, greater than or equal to 54 mol % and less than or equal to 68 mol %, greater than or equal to 54 mol % and less than or equal to 66 mol %, greater than or equal to 54 mol % and less than or equal to 65 mol %, or greater than or equal to 54 mol % and less than or equal to 64 mol %, or any and all sub-ranges formed from these endpoints.

Like SiO₂, Al₂O₃ may also stabilize the glass network and additionally provides improved mechanical properties and chemical durability to the glass composition and the resultant colored glass article. The amount of Al₂O₃ may also be tailored to control the viscosity of the glass composition. Al₂O₃ may be included such that the resultant glass composition has the desired fracture toughness (e.g., greater than or equal to 0.7 MPa·m^1/2). However, if the amount of Al₂O₃ is too high (e.g., greater than 25 mol %), the viscosity of the glass melt may increase, thereby diminishing the formability of the colored glass article. In embodiments, if the amount of Al₂O₃ is too high, the solubility of one or more colorants of the colorant package in the glass melt may decrease, resulting in the formation of undesirable crystal phases in the glass. For example and without limitation, when the colorant package includes Cr₂O₃, the solubility of Cr₂O₃ in the glass melt may decrease with increasing Al₂O₃ concentrations (e.g., concentrations greater than or equal to 17.5 mol %), leading to the precipitation of undesirable crystal phases. Without wishing to be bound by theory, it is hypothesized that similar behavior may occur with colorants other than Cr₂O₃.

Accordingly, in embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 7 mol % and less than or equal to 25 mol % Al₂O₃, greater than or equal to 7 mol % and less than or equal to 20 mol % Al₂O₃, or even greater than or equal to 8 mol % and less than or equal to 20 mol % Al₂O₃. In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 10 mol % and less than or equal to 20 mol % Al₂O₃, greater than or equal to 10 mol % and less than or equal to 17.5 mol % Al₂O₃, or even greater than or equal to 12 mol % and less than or equal to 17.25 mol % Al₂O₃. In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 11 mol % and less than or equal to 19 mol % Al₂O₃ or greater than or equal to 14 mol % and less than or equal to 17 mol % Al₂O₃. In embodiments, the concentration of Al₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 7 mol %, greater than or equal to 8 mol %, greater than or equal to 9 mol %, greater than or equal to 10 mol %, greater than or equal to 11 mol %, greater than or equal to 12 mol %, greater than or equal to 12.5 mol %, greater than or equal to 13 mol %, greater than or equal to 13.5 mol %, greater than or equal to 14 mol %, greater than or equal to 14.5 mol %, greater than or equal to 15 mol %, greater than or equal to 15.5 mol %, or even greater than or equal to 16 mol %. In embodiments, the concentration of Al₂O₃ in the glass composition and the resultant colored glass article may be less than or equal to 25 mol %, less than or equal to 23 mol %, less than or equal to 20 mol %, less than or equal to 19 mol %, less than or equal to 18 mol %, less than or equal to 17.5 mol %, less than or equal to 17.25 mol %, less than or equal to 17 mol %, less than or equal to 16.75 mol %, or even less than or equal to 16 mol %. In embodiments, the concentration of Al₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 8 mol % and less than or equal to 20 mol %, greater than or equal to 8 mol % and less than or equal to 18 mol % greater than or equal to 8 mol % and less than or equal to 17.5 mol %, greater than or equal to 8 mol % and less than or equal to 17 mol %, greater than or equal to 10 mol % and less than or equal to 20 mol %, greater than or equal to 10 mol % and less than or equal to 18 mol % greater than or equal to 10 mol % and less than or equal to 17.5 mol %, greater than or equal to 10 mol % and less than or equal to 17 mol %, greater than or equal to 12 mol % and less than or equal to 20 mol %, greater than or equal to 12 mol % and less than or equal to 18 mol % greater than or equal to 12 mol % and less than or equal to 17.5 mol %, greater than or equal to 12 mol % and less than or equal to 17 mol %, greater than or equal to 12.5 mol % and less than or equal to 20 mol %, greater than or equal to 12.5 mol % and less than or equal to 18 mol % greater than or equal to 12.5 mol % and less than or equal to 17.5 mol %, greater than or equal to 12.5 mol % and less than or equal to 17 mol %, greater than or equal to 13 mol % and less than or equal to 20 mol %, greater than or equal to 13 mol % and less than or equal to 18 mol % greater than or equal to 13 mol % and less than or equal to 17.5 mol %, greater than or equal to 13 mol % and less than or equal to 17 mol %, greater than or equal to 13.5 mol % and less than or equal to 20 mol %, greater than or equal to 13.5 mol % and less than or equal to 18 mol % greater than or equal to 13.5 mol % and less than or equal to 17.5 mol %, greater than or equal to 13.5 mol % and less than or equal to 17 mol %, greater than or equal to 14 mol % and less than or equal to 20 mol %, greater than or equal to 14 mol % and less than or equal to 18 mol % greater than or equal to 14 mol % and less than or equal to 17.5 mol %, or even greater than or equal to 14 mol % and less than or equal to 17 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the concentration of Al₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 7 mol % and less than or equal to 25 mol %, greater than or equal to 7 mol % and less than or equal to 23 mol %, greater than or equal to 7 mol % and less than or equal to 20 mol %, greater than or equal to 7 mol % and less than or equal to 17 mol %, greater than or equal to 9 mol % and less than or equal to 25 mol %, greater than or equal to 9 mol % and less than or equal to 23 mol %, greater than or equal to 9 mol % and less than or equal to 20 mol %, greater than or equal to 9 mol % and less than or equal to 17 mol %, greater than or equal to 11 mol % and less than or equal to 25 mol %, greater than or equal to 11 mol % and less than or equal to 23 mol %, greater than or equal to 11 mol % and less than or equal to 20 mol %, greater than or equal to 11 mol % and less than or equal to 17 mol %, greater than or equal to 13 mol % and less than or equal to 25 mol %, greater than or equal to 13 mol % and less than or equal to 23 mol %, greater than or equal to 13 mol % and less than or equal to 20 mol %, greater than or equal to 13 mol % and less than or equal to 17 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the concentration of Al₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 10 mol % and less than or equal to 17.5 mol %, greater than or equal to 10 mol % and less than or equal to 17.25 mol %, greater than or equal to 10 mol % and less than or equal to 17 mol %, greater than or equal to 10 mol % and less than or equal to 16.75 mol %, greater than or equal to 12 mol % and less than or equal to 17.5 mol %, greater than or equal to 12 mol % and less than or equal to 17.25 mol %, greater than or equal to 12 mol % and less than or equal to 17 mol %, greater than or equal to 12 mol % and less than or equal to 16.75 mol %, greater than or equal to 14 mol % and less than or equal to 17.5 mol %, greater than or equal to 14 mol % and less than or equal to 17.25 mol %, greater than or equal to 14 mol % and less than or equal to 17 mol %, greater than or equal to 14 mol % and less than or equal to 16.75 mol %, greater than or equal to 14.5 mol % and less than or equal to 17.5 mol %, greater than or equal to 14.5 mol % and less than or equal to 17.25 mol %, greater than or equal to 14.5 mol % and less than or equal to 17 mol %, greater than or equal to 14.5 mol % and less than or equal to 16.75 mol %, greater than or equal to 15 mol % and less than or equal to 17.5 mol %, greater than or equal to 15 mol % and less than or equal to 17.25 mol %, greater than or equal to 15 mol % and less than or equal to 17 mol %, greater than or equal to 15 mol % and less than or equal to 16.75 mol %, greater than or equal to 15.5 mol % and less than or equal to 17.5 mol %, greater than or equal to 15.5 mol % and less than or equal to 17.25 mol %, greater than or equal to 15.5 mol % and less than or equal to 17 mol %, greater than or equal to 15.5 mol % and less than or equal to 16.75 mol %, greater than or equal to 16 mol % and less than or equal to 17.5 mol %, greater than or equal to 16 mol % and less than or equal to 17.25 mol %, greater than or equal to 16 mol % and less than or equal to 17 mol %, or even greater than or equal to 16 mol % and less than or equal to 16.75 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the concentration of Al₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 10 mol % and less than or equal to 20 mol %, greater than or equal to 10 mol % and less than or equal to 19 mol %, greater than or equal to 10 mol % and less than or equal to 18 mol %, greater than or equal to 10 mol % and less than or equal to 17 mol %, greater than or equal to 10 mol % and less than or equal to 16 mol %, greater than or equal to 11 mol % and less than or equal to 20 mol %, greater than or equal to 11 mol % and less than or equal to 19 mol %, greater than or equal to 11 mol % and less than or equal to 18 mol %, greater than or equal to 11 mol % and less than or equal to 17 mol %, greater than or equal to 11 mol % and less than or equal to 16 mol %, greater than or equal to 12 mol % and less than or equal to 20 mol %, greater than or equal to 12 mol % and less than or equal to 19 mol %, greater than or equal to 12 mol % and less than or equal to 18 mol %, greater than or equal to 12 mol % and less than or equal to 17 mol %, greater than or equal to 12 mol % and less than or equal to 16 mol %, greater than or equal to 13 mol % and less than or equal to 20 mol %, greater than or equal to 13 mol % and less than or equal to 19 mol %, greater than or equal to 13 mol % and less than or equal to 18 mol %, greater than or equal to 13 mol % and less than or equal to 17 mol %, greater than or equal to 13 mol % and less than or equal to 16 mol %, greater than or equal to 14 mol % and less than or equal to 20 mol %, greater than or equal to 14 mol % and less than or equal to 19 mol %, greater than or equal to 14 mol % and less than or equal to 18 mol %, greater than or equal to 14 mol % and less than or equal to 17 mol %, greater than or equal to 14 mol % and less than or equal to 16 mol %, or any and all sub-ranges formed from any of these endpoints.

B₂O₃ decreases the melting point of the glass composition, which may improve retention of certain colorants in the glass, such as, for example and without limitation, Au. Without wishing to be bound by theory, it is hypothesized that similar behavior may occur with colorants other than Au. B₂O₃ may also improve the damage resistance of the resultant colored glass article. In addition, B₂O₃ may be added to reduce the formation of non-bridging oxygen, the presence of which may reduce fracture toughness. The concentration of B₂O₃ should be sufficiently high (e.g., greater than or equal to 1 mol %) to reduce the melting point of the glass composition, improve the formability, and increase the fracture toughness of the colored glass article. However, if B₂O₃ is too high (e.g., greater than 15 mol %), the annealing point and strain point may decrease, which increases stress relaxation and reduces the overall strength of the colored glass article.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 1 mol % and less than or equal to 15 mol % B₂O₃, greater than or equal to 1 mol % and less than or equal to 10 mol % B₂O₃, greater than or equal to 3 mol % and less than or equal to 10 mol % B₂O₃, greater than or equal to 3.5 mol % and less than or equal to 9 mol % B₂O₃. In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 2 mol % and less than or equal to 12 mol % B₂O₃ or even greater than or equal to 2 mol % and less than or equal to 8 mol % B₂O₃. In embodiments, the concentration of B₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 1 mol %, greater than or equal to 2 mol %, greater than or equal to 3 mol %, greater than or equal to 3.5 mol %, greater than or equal to 4 mol %, greater than or equal to 4.5 mol %, greater than or equal to 5 mol %, or even greater than or equal to 5.5 mol %. In embodiments, the concentration of B₂O₃ in the glass composition and the resultant colored glass article may be less than or equal to 15 mol %, less than or equal to 12 mol %, less than or equal to 10 mol %, less than or equal to 9 mol %, less than or equal to 8 mol %, less than or equal to 7.5 mol %, less than or equal to 7 mol %, less than or equal to 6.5 mol %, or even less than or equal to 6 mol %. In embodiments, the concentration of B₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 1 mol % and less than or equal to 15 mol %, greater than or equal to 1 mol % and less than or equal to 12 mol %, greater than or equal to 1 mol % and less than or equal to 10 mol %, greater than or equal to 1 mol % and less than or equal to 9 mol %, greater than or equal to 1 mol % and less than or equal to 8 mol %, greater than or equal to 1 mol % and less than or equal to 7.5 mol %, greater than or equal to 1 mol % and less than or equal to 7 mol %, greater than or equal to 1 mol % and less than or equal to 6.5 mol %, greater than or equal to 1 mol % and less than or equal to 6 mol %, greater than or equal to 2 mol % and less than or equal to 15 mol %, greater than or equal to 2 mol % and less than or equal to 12 mol %, greater than or equal to 2 mol % and less than or equal to 10 mol %, greater than or equal to 2 mol % and less than or equal to 9 mol %, greater than or equal to 2 mol % and less than or equal to 8 mol %, greater than or equal to 2 mol % and less than or equal to 7.5 mol %, greater than or equal to 2 mol % and less than or equal to 7 mol %, greater than or equal to 2 mol % and less than or equal to 6.5 mol %, greater than or equal to 2 mol % and less than or equal to 6 mol %, greater than or equal to 3 mol % and less than or equal to 15 mol %, greater than or equal to 3 mol % and less than or equal to 12 mol %, greater than or equal to 3 mol % and less than or equal to 10 mol %, greater than or equal to 3 mol % and less than or equal to 9 mol %, greater than or equal to 3 mol % and less than or equal to 8 mol %, greater than or equal to 3 mol % and less than or equal to 7.5 mol %, greater than or equal to 3 mol % and less than or equal to 7 mol %, greater than or equal to 3 mol % and less than or equal to 6.5 mol %, greater than or equal to 3 mol % and less than or equal to 6 mol %, greater than or equal to 3.5 mol % and less than or equal to 15 mol %, greater than or equal to 3.5 mol % and less than or equal to 12 mol %, greater than or equal to 3.5 mol % and less than or equal to 10 mol %, greater than or equal to 3.5 mol % and less than or equal to 9 mol %, greater than or equal to 3.5 mol % and less than or equal to 8 mol %, greater than or equal to 3.5 mol % and less than or equal to 7.5 mol %, greater than or equal to 3.5 mol % and less than or equal to 7 mol %, greater than or equal to 3.5 mol % and less than or equal to 6.5 mol %, greater than or equal to 3.5 mol % and less than or equal to 6 mol %, greater than or equal to 4 mol % and less than or equal to 15 mol %, greater than or equal to 4 mol % and less than or equal to 12 mol %, greater than or equal to 4 mol % and less than or equal to 10 mol %, greater than or equal to 4 mol % and less than or equal to 9 mol %, greater than or equal to 4 mol % and less than or equal to 8 mol %, greater than or equal to 4 mol % and less than or equal to 7.5 mol %, greater than or equal to 4 mol % and less than or equal to 7 mol %, greater than or equal to 4 mol % and less than or equal to 6.5 mol %, greater than or equal to 4 mol % and less than or equal to 6 mol %, greater than or equal to 4.5 mol % and less than or equal to 10 mol %, greater than or equal to 4.5 mol % and less than or equal to 9 mol %, greater than or equal to 4.5 mol % and less than or equal to 8 mol %, greater than or equal to 4.5 mol % and less than or equal to 7.5 mol %, greater than or equal to 4.5 mol % and less than or equal to 7 mol %, greater than or equal to 4.5 mol % and less than or equal to 6.5 mol %, greater than or equal to 5 mol % and less than or equal to 10 mol %, greater than or equal to 5 mol % and less than or equal to 9 mol %, greater than or equal to 5 mol % and less than or equal to 8 mol %, greater than or equal to 5 mol % and less than or equal to 7.5 mol %, greater than or equal to 5 mol % and less than or equal to 7 mol %, greater than or equal to 5 mol % and less than or equal to 6.5 mol %, greater than or equal to 5.5 mol % and less than or equal to 10 mol %, greater than or equal to 5.5 mol % and less than or equal to 9 mol %, greater than or equal to 5.5 mol % and less than or equal to 8 mol %, greater than or equal to 5.5 mol % and less than or equal to 7.5 mol %, greater than or equal to 5.5 mol % and less than or equal to 7 mol %, or even greater than or equal to 5.5 mol % and less than or equal to 6.5 mol %, or any and all sub-ranges formed from any of these endpoints.

As described hereinabove, the glass compositions and the resultant colored glass articles may contain alkali oxides, such as Li₂O, Na₂O, and K₂O, to enable the ion-exchangeability of the colored glass articles.

Li₂O aids in the ion-exchangeability of the colored glass article and also reduces the softening point of the glass composition, thereby increasing the formability of the colored glass articles. The addition of Li₂O facilitates the exchange of both Na⁺ and K⁺ cations into the glass for strengthening the glass and also facilitates producing a relatively high surface compressive stress and relatively deep depth of compression, improving the mechanical characteristics of the resultant colored glass article. In addition, Li₂O decreases the melting point of the glass composition, which may improve retention of colorants in the glass, such as, for example and without limitation, Au. Without wishing to be bound by theory, it is hypothesized that similar behavior may occur with colorants other than Au. The concentration of Li₂O in the glass compositions and resultant colored glass articles should be sufficiently high (e.g., greater than or equal to 1 mol %) to reduce the melting point of the glass composition and achieve the desired maximum central tension (e.g., greater than or equal to 40 MPa) following ion exchange. However, if the amount of Li₂O is too high (e.g., greater than 20 mol %), the liquidus temperature may increase, thereby diminishing the manufacturability of the colored glass article.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 1 mol % and less than or equal to 20 mol % Li₂O or even greater than or equal to 1 mol % and less than or equal to 18 mol % Li₂O. In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 3 mol % and less than or equal to 18 mol % Li₂O, greater than or equal to 7 mol % and less than or equal to 18 mol % Li₂O, greater than or equal to 8.8 mol % and less than or equal to 14 mol % Li₂O, or even greater than or equal to 9 mol % and less than or equal to 13.5 mol % Li₂O. In embodiments, the concentration of Li₂O in the glass composition and the resultant colored glass article may be greater than or equal to 1 mol %, greater than or equal to 3 mol %, greater than or equal to 5 mol %, greater than or equal to 7 mol %, greater than or equal to 7.5 mol %, greater than or equal to 8 mol %, greater than or equal to 8.5 mol %, greater than or equal to 8.8 mol %, greater than or equal to 9 mol %, greater than or equal to 9.2 mol %, greater than or equal to 9.4 mol %, greater than or equal to 9.6 mol %, greater than or equal to 9.8 mol %, greater than or equal to 10 mol %, greater than or equal to 11 mol %, greater than or equal to 11.5 mol %, or even greater than or equal to 12 mol %. In embodiments, the concentration of Li₂O in the glass composition and the resultant colored glass article may be less than or equal to 20 mol %, less than or equal to 18 mol %, less than or equal to 17 mol %, less than or equal to 16 mol %, less than or equal to 15 mol %, less than or equal to 14 mol %, less than or equal to 13.5 mol %, less than or equal to 13 mol %, less than or equal to 12.5 mol %, less than or equal to 12 mol %, less than or equal to 11.5 mol %, or even less than or equal to 11 mol %. In embodiments, the concentration of Li₂O in the glass composition and the resultant colored glass article may be greater than or equal to 1 mol % and less than or equal to 20 mol %, greater than or equal to 1 mol % and less than or equal to 18 mol %, greater than or equal to 1 mol % and less than or equal to 16 mol %, greater than or equal to 1 mol % and less than or equal to 14 mol %, greater than or equal to 1 mol % and less than or equal to 12.5 mol %, greater than or equal to 1 mol % and less than or equal to 12 mol %, greater than or equal to 1 mol % and less than or equal 11.5 mol %, greater than or equal to 1 mol % and less than or equal to 11 mol %, greater than or equal to 3 mol % and less than or equal to 20 mol %, greater than or equal to 3 mol % and less than or equal to 18 mol %, greater than or equal to 3 mol % and less than or equal to 16 mol %, greater than or equal to 3 mol % and less than or equal to 14 mol %, greater than or equal to 3 mol % and less than or equal to 12.5 mol %, greater than or equal to 3 mol % and less than or equal to 12 mol %, greater than or equal to 3 mol % and less than or equal 11.5 mol %, greater than or equal to 3 mol % and less than or equal to 11 mol %, greater than or equal to 5 mol % and less than or equal to 20 mol %, greater than or equal to 5 mol % and less than or equal to 18 mol %, greater than or equal to 5 mol % and less than or equal to 16 mol %, greater than or equal to 5 mol % and less than or equal to 14 mol %, greater than or equal to 5 mol % and less than or equal to 12.5 mol %, greater than or equal to 5 mol % and less than or equal to 12 mol %, greater than or equal to 5 mol % and less than or equal 11.5 mol %, greater than or equal to 5 mol % and less than or equal to 11 mol %, greater than or equal to 7 mol % and less than or equal to 20 mol %, greater than or equal to 7 mol % and less than or equal to 18 mol %, greater than or equal to 7 mol % and less than or equal to 16 mol %, greater than or equal to 7 mol % and less than or equal to 15 mol %, greater than or equal to 7 mol % and less than or equal to 14 mol %, greater than or equal to 7 mol % and less than or equal to 13 mol %, greater than or equal to 7 mol % and less than or equal to 12.5 mol %, greater than or equal to 7 mol % and less than or equal to 12 mol %, greater than or equal to 7 mol % and less than or equal 11.5 mol %, greater than or equal to 7 mol % and less than or equal to 11 mol %, greater than or equal to 7.5 mol % and less than or equal to 20 mol %, greater than or equal to 7.5 mol % and less than or equal to 18 mol %, greater than or equal to 7.5 mol % and less than or equal to 16 mol %, greater than or equal to 7.5 mol % and less than or equal to 14 mol %, greater than or equal to 7.5 mol % and less than or equal to 12.5 mol %, greater than or equal to 7.5 mol % and less than or equal to 12 mol %, greater than or equal to 7.5 mol % and less than or equal 11.5 mol %, greater than or equal to 7.5 mol % and less than or equal to 11 mol %, greater than or equal to 8 mol % and less than or equal to 20 mol %, greater than or equal to 8 mol % and less than or equal to 18 mol %, greater than or equal to 8 mol % and less than or equal to 16 mol %, greater than or equal to 8 mol % and less than or equal to 15 mol %, greater than or equal to 8 mol % and less than or equal to 14 mol %, greater than or equal to 8 mol % and less than or equal to 13 mol %, greater than or equal to 8 mol % and less than or equal to 12.5 mol %, greater than or equal to 8 mol % and less than or equal to 12 mol %, greater than or equal to 8 mol % and less than or equal 11.5 mol %, greater than or equal to 8 mol % and less than or equal to 11 mol %, greater than or equal to 8.5 mol % and less than or equal to 20 mol %, greater than or equal to 8.5 mol % and less than or equal to 18 mol %, greater than or equal to 8.5 mol % and less than or equal to 16 mol %, greater than or equal to 8.5 mol % and less than or equal to 14 mol %, greater than or equal to 8.5 mol % and less than or equal to 12.5 mol %, greater than or equal to 8.5 mol % and less than or equal to 12 mol %, greater than or equal to 8.5 mol % and less than or equal 11.5 mol %, greater than or equal to 8.5 mol % and less than or equal to 11 mol %, greater than or equal to 9 mol % and less than or equal to 20 mol %, greater than or equal to 9 mol % and less than or equal to 18 mol %, greater than or equal to 9 mol % and less than or equal to 16 mol %, greater than or equal to 9 mol % and less than or equal to 15 mol %, greater than or equal to 9 mol % and less than or equal to 14 mol %, greater than or equal to 9 mol % and less than or equal to 13 mol %, greater than or equal to 9 mol % and less than or equal to 12.5 mol %, greater than or equal to 9 mol % and less than or equal to 12 mol %, greater than or equal to 9 mol % and less than or equal 11.5 mol %, or even greater than or equal to 9 mol % and less than or equal to 11 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the concentration of Li₂O in the glass composition and the resultant colored glass article may be greater than or equal to 8.8 mol % and less than or equal to 14 mol %, greater than or equal to 8.8 mol % and less than or equal to 13.5 mol %, greater than or equal to 8.8 mol % and less than or equal to 13 mol %, greater than or equal to 8.8 mol % and less than or equal to 12.5 mol %, greater than or equal to 8.8 mol % and less than or equal to 12 mol %, greater than or equal to 8.8 mol % and less than or equal to 11.5 mol %, greater than or equal to 9 mol % and less than or equal to 14 mol %, greater than or equal to 9 mol % and less than or equal to 13.5 mol %, greater than or equal to 9 mol % and less than or equal to 13 mol %, greater than or equal to 9 mol % and less than or equal to 12.5 mol %, greater than or equal to 9 mol % and less than or equal to 12 mol %, greater than or equal to 9 mol % and less than or equal to 11.5 mol %, greater than or equal to 9.2 mol % and less than or equal to 14 mol %, greater than or equal to 9.2 mol % and less than or equal to 13.5 mol %, greater than or equal to 9.2 mol % and less than or equal to 13 mol %, greater than or equal to 9.2 mol % and less than or equal to 12.5 mol %, greater than or equal to 9.2 mol % and less than or equal to 12 mol %, greater than or equal to 9.2 mol % and less than or equal to 11.5 mol %, greater than or equal to 9.4 mol % and less than or equal to 14 mol %, greater than or equal to 9.4 mol % and less than or equal to 13.5 mol %, greater than or equal to 9.4 mol % and less than or equal to 13 mol %, greater than or equal to 9.4 mol % and less than or equal to 12.5 mol %, greater than or equal to 9.4 mol % and less than or equal to 12 mol %, greater than or equal to 9.4 mol % and less than or equal to 11.5 mol %, greater than or equal to 9.6 mol % and less than or equal to 14 mol %, greater than or equal to 9.6 mol % and less than or equal to 13.5 mol %, greater than or equal to 9.6 mol % and less than or equal to 13 mol %, greater than or equal to 9.6 mol % and less than or equal to 12.5 mol %, greater than or equal to 9.6 mol % and less than or equal to 12 mol %, greater than or equal to 9.6 mol % and less than or equal to 11.5 mol %, greater than or equal to 9.8 mol % and less than or equal to 14 mol %, greater than or equal to 9.8 mol % and less than or equal to 13.5 mol %, greater than or equal to 9.8 mol % and less than or equal to 13 mol %, greater than or equal to 9.8 mol % and less than or equal to 12.5 mol %, greater than or equal to 9.8 mol % and less than or equal to 12 mol %, greater than or equal to 9.8 mol % and less than or equal to 11.5 mol %, greater than or equal to 10 mol % and less than or equal to 14 mol %, greater than or equal to 10 mol % and less than or equal to 13.5 mol %, greater than or equal to 10 mol % and less than or equal to 13 mol %, greater than or equal to 10 mol % and less than or equal to 12.5 mol %, greater than or equal to 10 mol % and less than or equal to 12 mol %, or even greater than or equal to 10 mol % and less than or equal to 11.5 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the concentration of Li₂O in the glass composition and the resultant colored glass article may be greater than or equal to 10 mol % and less than or equal to 17 mol %, greater than or equal to 10 mol % and less than or equal to 16 mol %, greater than or equal to 10 mol % and less than or equal to 15 mol %, greater than or equal to 10 mol % and less than or equal to 14 mol %, greater than or equal to 10 mol % and less than or equal to 13 mol %, greater than or equal to 10 mol % and less than or equal to 12 mol %, greater than or equal to 11 mol % and less than or equal to 17 mol %, greater than or equal to 11 mol % and less than or equal to 16 mol %, greater than or equal to 11 mol % and less than or equal to 15 mol %, greater than or equal to 11 mol % and less than or equal to 14 mol %, greater than or equal to 11 mol % and less than or equal to 13 mol %, greater than or equal to 11 mol % and less than or equal to 12 mol %, greater than or equal to 11.1 mol % and less than or equal to 17 mol %, greater than or equal to 11.1 mol % and less than or equal to 16 mol %, greater than or equal to 11.1 mol % and less than or equal to 15 mol %, greater than or equal to 11.1 mol % and less than or equal to 14 mol %, greater than or equal to 11.1 mol % and less than or equal to 13 mol %, greater than or equal to 11.1 mol % and less than or equal to 12 mol %, greater than or equal to 11.5 mol % and less than or equal to 17 mol %, greater than or equal to 11.5 mol % and less than or equal to 16 mol %, greater than or equal to 11.5 mol % and less than or equal to 15 mol %, greater than or equal to 11.5 mol % and less than or equal to 14 mol %, greater than or equal to 11.5 mol % and less than or equal to 13 mol %, greater than or equal to 11.5 mol % and less than or equal to 12 mol %, greater than or equal to 12 mol % and less than or equal to 17 mol %, greater than or equal to 12 mol % and less than or equal to 16 mol %, greater than or equal to 12 mol % and less than or equal to 15 mol %, greater than or equal to 12 mol % and less than or equal to 14 mol %, greater than or equal to 12 mol % and less than or equal to 13 mol %, greater than or equal to 13 mol % and less than or equal to 17 mol %, greater than or equal to 13 mol % and less than or equal to 16 mol %, greater than or equal to 13 mol % and less than or equal to 15 mol %, greater than or equal to 13 mol % and less than or equal to 14 mol %, or any and all sub-ranges formed from any of these endpoints.

Na₂O improves diffusivity of alkali ions in the glass and thereby reduces ion-exchange time and helps achieve the desired surface compressive stress (e.g., greater than or equal to 300 MPa). The addition of Na₂O also facilitates the exchange of K⁺ cations into the glass for strengthening and improving the mechanical characteristics of the resultant colored glass article. Na₂O also improves the formability of the colored glass article. In addition, Na₂O decreases the melting point of the glass composition, which may improve retention of certain colorants in the glass, such as, for example, Au. Without wishing to be bound by theory, it is hypothesized that similar behavior may occur with colorants other than Au. However, if too much Na₂O is added to the glass composition, the melting point may be too low. In embodiments, the concentration of Li₂O present in the glass composition and the resultant colored glass article may be greater than the concentration of Na₂O present in the glass composition and the resultant colored glass article.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than 0 mol % or greater than or equal to 0.01 mol % and less than or equal to 15 mol % Na₂O, greater than or equal to 0.5 mol % and less than or equal to 15 mol % Na₂O or even greater than or equal to 1 mol % and less than or equal to 15 mol % Na₂O. In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 1 mol % and less than or equal to 12 mol % Na₂O or even greater than or equal to 2 mol % and less than or equal to 10 mol % Na₂O. In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0.01 mol % and less than or equal to 4 mol % Na₂O. In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 1.5 mol % and less than or equal to 8 mol % Na₂O or even greater than or equal to 2 mol % and less than or equal to 7.5 mol % Na₂O. In embodiments, the concentration of Na₂O in the glass composition and the resultant colored glass article may be greater than 0 mol %, greater than or equal to 0.01 mol %, greater than or equal to 0.5 mol %, greater than or equal to 1 mol %, greater than or equal to 1.5 mol %, greater than or equal to 2 mol %, greater than or equal to 2.5 mol %, greater than or equal to 3 mol %, greater than or equal to 3.5 mol %, greater than or equal to 4 mol %, or even greater than or equal to 4.5 mol %. In embodiments, the concentration of Na₂O in the glass composition and the resultant colored glass article may be less than or equal to 15 mol %, less than or equal to 12 mol %, less than or equal to 10 mol %, less than or equal to 9 mol %, less than or equal to 8.5 mol %, less than or equal to 8 mol %, less than or equal to 7.5 mol %, less than or equal to less than or equal to 7 mol %, less than or equal to 6.5 mol %, less than or equal to 6 mol %, less than or equal to less than or equal to 5.5 mol %, less than or equal to 5 mol %, less than or equal to 4.5 mol %, or even less than or equal to 4 mol %. In embodiments, the concentration of Na₂O in the glass composition and the resultant colored glass article may be greater than 0 mol % and less than or equal to 15 mol %, greater than 0 mol % and less than or equal to 12 mol %, greater than 0 mol % and less than or equal to 10 mol %, greater than 0 mol % and less than or equal to 8 mol %, greater than 0 mol % and less than or equal to 6 mol %, greater than 0 mol % and less than or equal to 5.5 mol %, greater than 0 mol % and less than or equal to 5 mol %, greater than 0 mol % and less than or equal to 4.5 mol %, greater than 0 mol % and less than or equal to 4 mol %, greater than or equal to 0.01 mol % and less than or equal to 15 mol %, greater than or equal to 0.01 mol % and less than or equal to 12 mol %, greater than or equal to 0.01 mol % and less than or equal to 10 mol %, greater than or equal to 0.01 mol % and less than or equal to 8 mol %, greater than or equal to 0.01 mol % and less than or equal to 6 mol %, greater than or equal to 0.01 mol % and less than or equal to 5.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 5 mol %, greater than or equal to 0.01 mol % and less than or equal to 4.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 4 mol %, greater than or equal to 0.5 mol % and less than or equal to 15 mol %, greater than or equal to 0.5 mol % and less than or equal to 12 mol %, greater than or equal to 0.5 mol % and less than or equal to 10 mol %, greater than or equal to 0.5 mol % and less than or equal to 8 mol %, greater than or equal to 0.5 mol % and less than or equal to 6 mol %, greater than or equal to 1 mol % and less than or equal to 15 mol %, greater than or equal to 1 mol % and less than or equal to 12 mol %, greater than or equal to 1 and less than or equal to 10 mol %, greater than or equal to 1 and less than or equal to 9 mol %, greater than or equal to 1 mol % and less than or equal to 8 mol %, greater than or equal to 1 mol % and less than or equal to 7.5 mol %, greater than or equal to 1 mol % and less than or equal to 7 mol %, greater than or equal to 1 mol % and less than or equal to 6.5 mol %, greater than or equal to 1 mol % and less than or equal to 6 mol %, greater than or equal to 1 mol % and less than or equal to 5.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 15 mol %, greater than or equal to 1.5 mol % and less than or equal to 12 mol %, greater than or equal to 1.5 and less than or equal to 10 mol %, greater than or equal to 1.5 and less than or equal to 9 mol %, greater than or equal to 1.5 mol % and less than or equal to 8 mol %, greater than or equal to 1.5 mol % and less than or equal to 7.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 7 mol %, greater than or equal to 1.5 mol % and less than or equal to 6.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 6 mol %, greater than or equal to 1.5 mol % and less than or equal to 5.5 mol %, greater than or equal to 2 mol % and less than or equal to 15 mol %, greater than or equal to 2 mol % and less than or equal to 12 mol %, greater than or equal to 2 and less than or equal to 10 mol %, greater than or equal to 2 and less than or equal to 9 mol %, greater than or equal to 2 mol % and less than or equal to 8 mol %, greater than or equal to 2 mol % and less than or equal to 7.5 mol %, greater than or equal to 2 mol % and less than or equal to 7 mol %, greater than or equal to 2 mol % and less than or equal to 6.5 mol %, greater than or equal to 2 mol % and less than or equal to 6 mol %, greater than or equal to 2 mol % and less than or equal to 5.5 mol %, greater than or equal to 2.5 mol % and less than or equal to 15 mol %, greater than or equal to 2.5 mol % and less than or equal to 12 mol %, greater than or equal to 2.5 and less than or equal to 10 mol %, greater than or equal to 2.5 and less than or equal to 9 mol %, greater than or equal to 2.5 mol % and less than or equal to 8 mol %, greater than or equal to 2.5 mol % and less than or equal to 7.5 mol %, greater than or equal to 2.5 mol % and less than or equal to 7 mol %, greater than or equal to 2.5 mol % and less than or equal to 6.5 mol %, greater than or equal to 2.5 mol % and less than or equal to 6 mol %, greater than or equal to 2.5 mol % and less than or equal to 5.5 mol %, greater than or equal to 3 mol % and less than or equal to 15 mol %, greater than or equal to 3 mol % and less than or equal to 12 mol %, greater than or equal to 3 and less than or equal to 10 mol %, greater than or equal to 3 and less than or equal to 9 mol %, greater than or equal to 3 and less than or equal to 8.5 mol %, greater than or equal to 3 mol % and less than or equal to 8 mol %, greater than or equal to 3 mol % and less than or equal to 7.5 mol %, greater than or equal to 3 mol % and less than or equal to 7 mol %, greater than or equal to 3 mol % and less than or equal to 6.5 mol %, greater than or equal to 3 mol % and less than or equal to 6 mol %, greater than or equal to 3 mol % and less than or equal to 5.5 mol %, greater than or equal to 3.5 mol % and less than or equal to 15 mol %, greater than or equal to 3.5 mol % and less than or equal to 12 mol %, greater than or equal to 3.5 and less than or equal to 10 mol %, greater than or equal to 3.5 and less than or equal to 9 mol %, greater than or equal to 3.5 mol % and less than or equal to 8 mol %, greater than or equal to 3.5 mol % and less than or equal to 7.5 mol %, greater than or equal to 3.5 mol % and less than or equal to 7 mol %, greater than or equal to 3.5 mol % and less than or equal to 6.5 mol %, greater than or equal to 3.5 mol % and less than or equal to 6 mol %, greater than or equal to 3.5 mol % and less than or equal to 5.5 mol %, greater than or equal to 4 mol % and less than or equal to 15 mol %, greater than or equal to 4 mol % and less than or equal to 12 mol %, greater than or equal to 4 and less than or equal to 10 mol %, greater than or equal to 4 and less than or equal to 9 mol %, greater than or equal to 4 mol % and less than or equal to 8 mol %, greater than or equal to 4 mol % and less than or equal to 7.5 mol %, greater than or equal to 4 mol % and less than or equal to 7 mol %, greater than or equal to 4 mol % and less than or equal to 6.5 mol %, greater than or equal to 4 mol % and less than or equal to 6 mol %, greater than or equal to 4 mol % and less than or equal to 5.5 mol %, greater than or equal to 4.5 mol % and less than or equal to 15 mol %, greater than or equal to 4.5 mol % and less than or equal to 12 mol %, greater than or equal to 4.5 and less than or equal to 10 mol %, greater than or equal to 4.5 mol % and less than or equal to 8 mol %, greater than or equal to 4.5 mol % and less than or equal to 7.5 mol %, greater than or equal to 4.5 mol % and less than or equal to 7 mol %, greater than or equal to 4.5 mol % and less than or equal to 6.5 mol %, greater than or equal to 4.5 mol % and less than or equal to 6 mol %, or even greater than or equal to 4.5 mol % and less than or equal to 5.5 mol %, or any and all sub-ranges formed from any of these endpoints.

The concentration of Li₂O+Na₂O in the glass composition and the resultant colored glass article may determine the ability of the glass composition and the colored glass article to be strengthened through an ion exchange process. Generally, the ion exchange process strengthens the glass by replacing alkali ions in the glass with larger alkali ions. For example, a glass containing Li₂O and/or Na₂O may be strengthened by ion exchange such that potassium ions (K⁺) replace the Li⁺ or Na⁺ ions in the glass. In this manner, the ability of the colored glass article to be strengthened by an ion exchange process relates directly to the content of Li₂O+Na₂O, and if the Li₂O+Na₂O content is too low (e.g., less than about 8 mol %) the resultant colored glass article may not be able to be sufficiently strengthened by ion exchange processes.

In embodiments, the concentration of Li₂O+Na₂O in the glass composition and the resultant colored glass article may be greater than or equal to than or equal to 8 mol %, such as greater than or equal to 10 mol % and less than or equal to than or equal to 19 mol %. In embodiments, the concentration of Li₂O+Na₂O in the glass composition and the resultant colored glass article may be greater than or equal to than or equal to 9 mol %, greater than or equal to 10 mol %, greater than or equal to 12 mol %, greater than or equal to 14 mol %, greater than or equal to 16 mol %, or more. In embodiments, the concentration of Li₂O+Na₂O in the glass composition and the colored glass article is less than or equal to than or equal to 20 mol %, less than or equal to than or equal to 18 mol %, less than or equal to than or equal to 16 mol %, less than or equal to than or equal to 14 mol %, less than or equal to than or equal to 12 mol %, less than or equal to than or equal to 10 mol %, or less. In embodiments, the concentration of Li₂O+Na₂O in the glass composition and the colored glass article may be greater than or equal to 8 mol % and less than or equal to than or equal to 20 mol %, greater than or equal to 9 mol % and less than or equal to than or equal to 19 mol %, greater than or equal to 10 mol % and less than or equal to than or equal to 18 mol %, greater than or equal to 11 mol % and less than or equal to than or equal to 17 mol %, greater than or equal to 12 mol % and less than or equal to than or equal to 16 mol %, greater than or equal to 13 mol % and less than or equal to than or equal to 15 mol %, greater than or equal to 8 mol % and less than or equal to than or equal to 14 mol %, or any and all sub-ranges formed from any of these endpoints.

K₂O, when included, promotes ion-exchange and may increase the depth of compression and decrease the melting point to improve the formability of the colored glass article. However, adding too much K₂O may cause the surface compressive stress and melting point to be too low. Accordingly, in embodiments, the amount of K₂O added to the glass composition may be limited.

In embodiments, the glass composition and the resultant colored glass article may optionally comprise greater than or equal to 0 mol % and less than or equal to 3 mol % K₂O, greater than or equal to 0 mol % and less than or equal to 1 mol % K₂O, greater than or equal to 0.01 mol % and less than or equal to 1 mol % K₂O or even greater than or equal to 0.1 mol % and less than or equal to 1 mol % K₂O. In embodiments, the glass composition and the resultant colored glass article may optionally comprise greater than 0.1 mol % and less than or equal to 0.5 mol % K₂O. In embodiments, the concentration of K₂O in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol %, greater than or equal to 0.01 mol %, greater than or equal to 0.1 mol %, greater than or equal to 0.2 mol %, greater than or equal to 0.25 mol %, greater than or equal to 0.4 mol %, or even greater than or equal to 0.5 mol %. In embodiments, the concentration of K₂O in the glass composition and the resultant colored glass article may be less than or equal to 3 mol %, less than or equal to 2.5 mol %, less than or equal to 2 mol %, less than or equal to 1.5 mol %, less than or equal to 1 mol %, less than or equal to 0.75 mol %, less than or equal to 0.5 mol %, or even less than or equal to 0.25 mol %. In embodiments, the concentration of K₂O in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 3 mol %, greater than or equal to 0 mol % and less than or equal to 2.5 mol %, greater than or equal to 0 mol % and less than or equal to 2 mol %, greater than or equal to 0 mol % and less than or equal to 1.5 mol %, greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0 mol % and less than or equal to 0.75 mol %, greater than or equal to 0 mol % and less than or equal to 0.7 mol %, greater than or equal to 0 mol % and less than or equal to 0.5 mol %, greater than or equal to 0 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.01 mol % and less than or equal to 3 mol %, greater than or equal to 0.01 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 2 mol %, greater than or equal to 0.01 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 1 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.7 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 3 mol %, greater than or equal to 0.1 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 2 mol %, greater than or equal to 0.1 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 1 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.7 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.2 mol % and less than or equal to 3 mol %, greater than or equal to 0.2 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.2 mol % and less than or equal to 2 mol %, greater than or equal to 0.2 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.2 mol % and less than or equal to 1 mol %, greater than or equal to 0.2 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.2 mol % and less than or equal to 0.7 mol %, greater than or equal to 0.2 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.25 mol % and less than or equal to 3 mol %, greater than or equal to 0.25 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.25 mol % and less than or equal to 2 mol %, greater than or equal to 0.25 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.25 mol % and less than or equal to 1 mol %, greater than or equal to 0.25 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.25 mol % and less than or equal to 0.7 mol %, greater than or equal to 0.25 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.3 mol % and less than or equal to 3 mol %, greater than or equal to 0.3 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.3 mol % and less than or equal to 2 mol %, greater than or equal to 0.3 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.3 mol % and less than or equal to 1 mol %, greater than or equal to 0.3 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.3 mol % and less than or equal to 0.7 mol %, greater than or equal to 0.3 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.4 mol % and less than or equal to 3 mol %, greater than or equal to 0.4 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.4 mol % and less than or equal to 2 mol %, greater than or equal to 0.4 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.4 mol % and less than or equal to 1 mol %, greater than or equal to 0.4 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.4 mol % and less than or equal to 0.7 mol %, or even greater than or equal to 0.4 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 1 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the glass composition and the resultant colored glass article may be substantially free or free of K₂O.

In embodiments, the concentration of K₂O in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol %, greater than or equal to 0.01 mol %, greater than or equal to 0.1 mol %, greater than or equal to 0.2 mol %, greater than or equal to 0.25 mol %, greater than or equal to 0.4 mol %, or even greater than or equal to 0.5 mol %. In embodiments, the concentration of K₂O in the glass composition and the resultant colored glass article may be less than or equal to 5 mol %, less than or equal to 4 mol %, less than or equal to 3 mol %, less than or equal to 2 mol %, or even less than or equal to 1 mol %. In embodiments, the concentration of K₂O in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 5 mol %, greater than or equal to 0 mol % and less than or equal to 4 mol %, greater than or equal to 0 mol % and less than or equal to 3 mol %, greater than or equal to 0 mol % and less than or equal to 2 mol %, greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0.01 mol % and less than or equal to 5 mol %, greater than or equal to 0.01 mol % and less than or equal to 4 mol %, greater than or equal to 0.01 mol % and less than or equal to 3 mol %, greater than or equal to 0.01 mol % and less than or equal to 2 mol %, greater than or equal to 0.01 mol % and less than or equal to 1 mol %, greater than or equal to 0.1 mol % and less than or equal to 5 mol %, greater than or equal to 0.1 mol % and less than or equal to 4 mol %, greater than or equal to 0.1 mol % and less than or equal to 3 mol %, greater than or equal to 0.1 mol % and less than or equal to 2 mol %, greater than or equal to 0.1 mol % and less than or equal to 1 mol %, greater than or equal to 0.2 mol % and less than or equal to 5 mol %, greater than or equal to 0.2 mol % and less than or equal to 4 mol %, greater than or equal to 0.2 mol % and less than or equal to 3 mol %, greater than or equal to 0.2 mol % and less than or equal to 2 mol %, greater than or equal to 0.2 mol % and less than or equal to 1 mol %, greater than or equal to 0.25 mol % and less than or equal to 5 mol %, greater than or equal to 0.25 mol % and less than or equal to 4 mol %, greater than or equal to 0.25 mol % and less than or equal to 3 mol %, greater than or equal to 0.25 mol % and less than or equal to 2 mol %, greater than or equal to 0.25 mol % and less than or equal to 1 mol %, greater than or equal to 0.3 mol % and less than or equal to 5 mol %, greater than or equal to 0.3 mol % and less than or equal to 5 mol %, greater than or equal to 0.3 mol % and less than or equal to 3 mol %, greater than or equal to 0.3 mol % and less than or equal to 2 mol %, greater than or equal to 0.3 mol % and less than or equal to 1 mol %, greater than or equal to 0.4 mol % and less than or equal to 5 mol %, greater than or equal to 0.4 mol % and less than or equal to 4 mol %, greater than or equal to 0.4 mol % and less than or equal to 3 mol %, greater than or equal to 0.4 mol % and less than or equal to 2 mol %, greater than or equal to 0.4 mol % and less than or equal to 1 mol %, greater than or equal to equal to 0.5 mol % and less than or equal to 5 mol %, greater than or equal to equal to 0.5 mol % and less than or equal to 4 mol %, greater than or equal to equal to 0.5 mol % and less than or equal to 3 mol %, greater than or equal to equal to 0.5 mol % and less than or equal to 2 mol %, or even greater than or equal to equal to 0.5 mol % and less than or equal to 1 mol %, or any and all sub-ranges formed from any of these endpoints.

R₂O, as used herein, is the sum (in mol %) of Li₂O, Na₂O, and K₂O present in the glass composition and the resultant colored glass article (i.e., R₂O═Li₂O (mol %)+Na₂O (mol %)+K₂O (mol %). Like B₂O₃, the alkali oxides aid in decreasing the softening point and molding temperature of the glass composition, thereby offsetting the increase in the softening point and molding temperature of the glass composition due to higher amounts of SiO₂ in the glass composition, for example. The softening point and molding temperature may be further reduced by including combinations of alkali oxides (e.g., two or more alkali oxides) in the glass composition, a phenomenon referred to as the “mixed alkali effect.” However, it has been found that if the amount of alkali oxide is too high, the average coefficient of thermal expansion of the glass composition increases to greater than 100×10⁻⁷/° C., which may be undesirable.

In embodiments, the concentration of R₂O in the glass composition and the resultant colored glass article may be greater than or equal to 1 mol % and less than or equal to 35 mol %. In embodiments, the concentration of R₂O in the glass composition and the resultant colored glass article may be greater than or equal to 6 mol % and less than or equal to 25 mol % or even greater than or equal to 8 mol % and less than or equal to 23 mol %. In embodiments, the concentration of R₂O in the glass composition and the resultant colored glass article may be greater than or equal to 2 mol %, greater than or equal to 4 mol %, greater than 6 mol %, greater than or equal to 8 mol %, greater than or equal to 10 mol %, greater than or equal to 10.3 mol %, greater than or equal to 11 mol %, greater than or equal to 12 mol %, greater than or equal to 13 mol %, greater than or equal to 12 mol %, or even greater than or equal to 14 mol %. In embodiments, the concentration of R₂O in the glass composition and the resultant colored glass article may be less than or equal to 35 mol %, less than or equal to 30 mol %, less than or equal to 25 mol %, less than or equal to 23 mol %, less than or equal to 22 mol %, less than or equal to 21 mol %, less than or equal to 20 mol %, less than or equal to 19 mol %, less than or equal to 18 mol %, less than or equal to 17 mol %, or even less than or equal to 16 mol %. In embodiments, the concentration of R₂O in the glass composition and the resultant colored glass article may be greater than or equal to 1 mol % and less than or equal to 35 mol %, greater than or equal to 1 mol % and less than or equal to 30 mol %, greater than or equal to 1 mol % and less than or equal to 25 mol %, greater than or equal to 1 mol % and less than or equal to 23 mol %, greater than or equal to 1 mol % and less than or equal to 22 mol %, greater than or equal to 1 mol % and less than or equal to 21 mol %, greater than or equal to 1 mol % and less than or equal to 20 mol %, greater than or equal to 1 mol % and less than or equal to 19 mol %, greater than or equal to 1 mol % and less than or equal to 18 mol %, greater than or equal to 1 mol % and less than or equal to 17 mol %, greater than or equal to 1 mol % and less than or equal to 16 mol %, greater than or equal to 2 mol % and less than or equal to 35 mol %, greater than or equal to 2 mol % and less than or equal to 30 mol %, greater than or equal to 2 mol % and less than or equal to 25 mol %, greater than or equal to 2 mol % and less than or equal to 23 mol %, greater than or equal to 2 mol % and less than or equal to 22 mol %, greater than or equal to 2 mol % and less than or equal to 21 mol %, greater than or equal to 2 mol % and less than or equal to 20 mol %, greater than or equal to 2 mol % and less than or equal to 19 mol %, greater than or equal to 2 mol % and less than or equal to 18 mol %, greater than or equal to 2 mol % and less than or equal to 17 mol %, greater than or equal to 2 mol % and less than or equal to 16 mol %, greater than or equal to 4 mol % and less than or equal to 35 mol %, greater than or equal to 4 mol % and less than or equal to 30 mol %, greater than or equal to 4 mol % and less than or equal to 25 mol %, greater than or equal to 4 mol % and less than or equal to 23 mol %, greater than or equal to 4 mol % and less than or equal to 22 mol %, greater than or equal to 4 mol % and less than or equal to 21 mol %, greater than or equal to 4 mol % and less than or equal to 20 mol %, greater than or equal to 4 mol % and less than or equal to 19 mol %, greater than or equal to 4 mol % and less than or equal to 18 mol %, greater than or equal to 4 mol % and less than or equal to 17 mol %, greater than or equal to 4 mol % and less than or equal to 16 mol %, greater than or equal to 6 mol % and less than or equal to 35 mol %, greater than or equal to 6 mol % and less than or equal to 30 mol %, greater than or equal to 6 mol % and less than or equal to 25 mol %, greater than or equal to 6 mol % and less than or equal to 23 mol %, greater than or equal to 6 mol % and less than or equal to 22 mol %, greater than or equal to 6 mol % and less than or equal to 21 mol %, greater than or equal to 6 mol % and less than or equal to 20 mol %, greater than or equal to 6 mol % and less than or equal to 19 mol %, greater than or equal to 6 mol % and less than or equal to 18 mol %, greater than or equal to 6 mol % and less than or equal to 17 mol %, greater than or equal to 6 mol % and less than or equal to 16 mol %, greater than or equal to 8 mol % and less than or equal to 35 mol %, greater than or equal to 8 mol % and less than or equal to 30 mol %, greater than or equal to 8 mol % and less than or equal to 25 mol %, greater than or equal to 8 mol % and less than or equal to 23 mol %, greater than or equal to 8 mol % and less than or equal to 22 mol %, greater than or equal to 8 mol % and less than or equal to 21 mol %, greater than or equal to 8 mol % and less than or equal to 20 mol %, greater than or equal to 8 mol % and less than or equal to 19 mol %, greater than or equal to 8 mol % and less than or equal to 18 mol %, greater than or equal to 8 mol % and less than or equal to 17 mol %, greater than or equal to 8 mol % and less than or equal to 16 mol %, greater than or equal to 10 mol % and less than or equal to 35 mol %, greater than or equal to 10 mol % and less than or equal to 30 mol %, greater than or equal to 10 mol % and less than or equal to 25 mol %, greater than or equal to 10 mol % and less than or equal to 23 mol %, greater than or equal to 10 mol % and less than or equal to 22 mol %, greater than or equal to 10 mol % and less than or equal to 21 mol %, greater than or equal to 10 mol % and less than or equal to 20 mol %, greater than or equal to 10 mol % and less than or equal to 19 mol %, greater than or equal to 10 mol % and less than or equal to 18 mol %, greater than or equal to 10 mol % and less than or equal to 17 mol %, greater than or equal to 10 mol % and less than or equal to 16 mol %, greater than or equal to 11 mol % and less than or equal to 35 mol %, greater than or equal to 11 mol % and less than or equal to 30 mol %, greater than or equal to 11 mol % and less than or equal to 25 mol %, greater than or equal to 11 mol % and less than or equal to 23 mol %, greater than or equal to 11 mol % and less than or equal to 22 mol %, greater than or equal to 11 mol % and less than or equal to 21 mol %, greater than or equal to 11 mol % and less than or equal to 20 mol %, greater than or equal to 11 mol % and less than or equal to 19 mol %, greater than or equal to 11 mol % and less than or equal to 18 mol %, greater than or equal to 11 mol % and less than or equal to 17 mol %, greater than or equal to 11 mol % and less than or equal to 16 mol %, greater than or equal to 12 mol % and less than or equal to 35 mol %, greater than or equal to 12 mol % and less than or equal to 30 mol %, greater than or equal to 12 mol % and less than or equal to 25 mol %, greater than or equal to 12 mol % and less than or equal to 23 mol %, greater than or equal to 12 mol % and less than or equal to 22 mol %, greater than or equal to 12 mol % and less than or equal to 21 mol %, greater than or equal to 12 mol % and less than or equal to 20 mol %, greater than or equal to 12 mol % and less than or equal to 19 mol %, greater than or equal to 12 mol % and less than or equal to 18 mol %, greater than or equal to 12 mol % and less than or equal to 17 mol %, greater than or equal to 12 mol % and less than or equal to 16 mol %, greater than or equal to 13 mol % and less than or equal to 35 mol %, greater than or equal to 13 mol % and less than or equal to 30 mol %, greater than or equal to 13 mol % and less than or equal to 25 mol %, greater than or equal to 13 mol % and less than or equal to 23 mol %, greater than or equal to 13 mol % and less than or equal to 22 mol %, greater than or equal to 13 mol % and less than or equal to 21 mol %, greater than or equal to 13 mol % and less than or equal to 20 mol %, greater than or equal to 13 mol % and less than or equal to 19 mol %, greater than or equal to 13 mol % and less than or equal to 18 mol %, greater than or equal to 13 mol % and less than or equal to 17 mol %, greater than or equal to 13 mol % and less than or equal to 16 mol %, greater than or equal to 14 mol % and less than or equal to 35 mol %, greater than or equal to 14 mol % and less than or equal to 30 mol %, greater than or equal to 14 mol % and less than or equal to 25 mol %, greater than or equal to 14 mol % and less than or equal to 23 mol %, greater than or equal to 14 mol % and less than or equal to 22 mol %, greater than or equal to 14 mol % and less than or equal to 21 mol %, greater than or equal to 14 mol % and less than or equal to 20 mol %, greater than or equal to 14 mol % and less than or equal to 19 mol %, greater than or equal to 14 mol % and less than or equal to 18 mol %, greater than or equal to 14 mol % and less than or equal to 17 mol %, or even greater than or equal to 14 mol % and less than or equal to 16 mol %, or any and all sub-ranges formed from any of these endpoints.

In embodiments, the difference between R₂O and Al₂O₃ (i.e. R₂O (mol %)—Al₂O₃ (mol %)) in the glass composition may be adjusted to produce a desired observable color (e.g., pink, purple, red, orange, or blue). The analyzed R₂O—Al₂O₃ of the resultant colored glass article, along with the added colorant package, may correlate with the observable color of the colored glass article after heat treatment, as discussed herein. In embodiments, R₂O—Al₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to −5 mol % and less than or equal to 7 mol % or even greater than or equal to −3 mol % and less than or equal to 2 mol %. In embodiments, R₂O—Al₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to −3 mol % and less than or equal to 6 mol %. In embodiments, R₂O—Al₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to −1 mol % and less than or equal to 5 mol %. In embodiments, R₂O—Al₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to −5 mol % and less than or equal to 1.5 mol %. In embodiments, R₂O—Al₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to −3 mol % and less than or equal to 1.5 mol %. In embodiments, R₂O—Al₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 1.5 mol % and less than or equal to 7 mol %. In embodiments, R₂O—Al₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 1.5 mol % and less than or equal to 5 mol %. In embodiments, R₂O—Al₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to −5 mol %, greater than or equal to −4 mol %, greater than or equal to −3 mol %, greater than or equal to −2.5 mol %, greater than or equal to −2 mol %, greater than or equal to −1.5 mol %, greater than or equal to 0.2 mol %, greater than or equal to 0.5 mol %, greater than or equal to 1 mol %, greater than or equal to 1.5 mol %, or even greater than or equal to 2 mol %. In embodiments, R₂O—Al₂O₃ in the glass composition and the resultant colored glass article may be less than or equal to 7 mol %, less than or equal to 6.5 mol %, less than or equal to 6 mol %, less than or equal to 5.5 mol %, less than or equal to 5 mol %, less than or equal to 4.5 mol %, less than or equal to 4 mol %, less than or equal to 3.5 mol %, less than or equal to 3 mol %, less than or equal to 2.5 mol %, less than or equal to 2 mol %, less than or equal to 1.5 mol %, less than or equal to 1 mol %, or even less than or equal to 0.5 mol %. In embodiments, R₂O—Al₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to −5 mol % and less than or equal to 7 mol %, greater than or equal to −5 mol % and less than or equal to 5 mol %, greater than or equal to −5 mol % and less than or equal to 3 mol %, greater than or equal to −5 mol % and less than or equal to 1.5 mol %, greater than or equal to −3 mol % and less than or equal to 7 mol %, greater than or equal to −3 mol % and less than or equal to 5 mol %, greater than or equal to −3 mol % and less than or equal to 3 mol %, greater than or equal to −3 mol % and less than or equal to 1.5 mol %, greater than or equal to −1 mol % and less than or equal to 7 mol %, greater than or equal to −1 mol % and less than or equal to 5 mol %, greater than or equal to −1 mol % and less than or equal to 3 mol %, greater than or equal to −1 mol % and less than or equal to 1.5 mol %, greater than or equal to 0 mol % and less than or equal to 7 mol %, greater than or equal to 0 mol % and less than or equal to 5 mol %, greater than or equal to 0 mol % and less than or equal to 3 mol %, greater than or equal to 0 mol % and less than or equal to 1.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 7 mol %, greater than or equal to 1.5 mol % and less than or equal to 5 mol %, or even greater than or equal to 1.5 mol % and less than or equal to 3 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, R₂O—Al₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to −3 mol % and less than or equal to 2 mol %, greater than or equal to −3 mol % and less than or equal to 1.5 mol %, greater than or equal to −3 mol % and less than or equal to 1 mol %, greater than or equal to −3 mol % and less than or equal to 0.5 mol %, greater than or equal to −2.5 mol % and less than or equal to 2 mol %, greater than or equal to −2.5 mol % and less than or equal to 1.5 mol %, greater than or equal to −2.5 mol % and less than or equal to 1 mol %, greater than or equal to −2.5 mol % and less than or equal to 0.5 mol %, greater than or equal to −2 mol % and less than or equal to 2 mol %, greater than or equal to −2 mol % and less than or equal to 1.5 mol %, greater than or equal to −2 mol % and less than or equal to 1 mol %, greater than or equal to −2 mol % and less than or equal to 0.5 mol %, greater than or equal to −1.5 mol % and less than or equal to 2 mol %, greater than or equal to −1.5 mol % and less than or equal to 1.5 mol %, greater than or equal to −1.5 mol % and less than or equal to 1 mol %, or even greater than or equal to −1.5 mol % and less than or equal to 0.5 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the difference between the concentrations of R₂O and Al₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 0.2 mol % and less than or equal to 5 mol %, greater than or equal to 0.2 mol % and less than or equal to 4.5 mol %, greater than or equal to 0.2 mol % and less than or equal to 4 mol %, greater than or equal to 0.2 mol % and less than or equal to 3.5 mol %, greater than or equal to 0.2 mol % and less than or equal to 3 mol %, greater than or equal to 0.5 mol % and less than or equal to 5 mol %, greater than or equal to 0.5 mol % and less than or equal to 4.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 4 mol %, greater than or equal to 0.5 mol % and less than or equal to 3.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 3 mol %, greater than or equal to 1 mol % and less than or equal to 5 mol %, greater than or equal to 1 mol % and less than or equal to 4.5 mol %, greater than or equal to 1 mol % and less than or equal to 4 mol %, greater than or equal to 1 mol % and less than or equal to 3.5 mol %, greater than or equal to 1 mol % and less than or equal to 3 mol %, greater than or equal to 1.5 mol % and less than or equal to 5 mol %, greater than or equal to 1.5 mol % and less than or equal to 4.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 4 mol %, greater than or equal to 1.5 mol % and less than or equal to 3.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 3 mol %, greater than or equal to 2 mol % and less than or equal to 5 mol %, greater than or equal to 2 mol % and less than or equal to 4.5 mol %, greater than or equal to 2 mol % and less than or equal to 4 mol %, greater than or equal to 2 mol % and less than or equal to 3.5 mol %, greater than or equal to 2 mol % and less than or equal to 3 mol %, or any and all sub-ranges formed from any of these endpoints.

In embodiments, the glass compositions and the resultant colored glass articles described herein further include MgO and/or ZnO to improve retention of colorants in the glass, such as Au or the like, by lowering the melting point of the glass composition. Decreasing the melting point of the glass composition may help improve colorant retention because the glass compositions may be melted at relatively lower temperatures and the evaporation of colorants from the glass, such as gold, may be reduced. While not wishing to be bound by theory, it is also believed that partially replacing Li₂O and/or Na₂O with MgO and/or ZnO may also help improve retention of the colorants. Specifically, Li₂O and/or Na₂O is included in the batch glass composition as lithium carbonate and sodium carbonate, respectively. Upon melting the glass composition, carbonate gas is released from the glass composition. Colorants such as Au escape from the glass composition within the carbonate gas. Therefore, the improved colorant retention may be due to the reduced amount of carbonate. Further, it is believed that MgO and/or ZnO may improve the solubility of some colorants in the glass (such as Cr₂O₃, for example), thereby avoiding the formation of undesirable crystal phases (such as Cr-spinel crystals) and expanding the color gamut that may be achieved by the resultant colored glass articles. For example, in embodiments where the colorant includes Cr₂O₃, the sum of MgO and ZnO present in the glass composition and the resultant colored glass article (i.e., MgO (mol %)+ZnO (mol %)) may be greater than or equal to 0 mol % and less than or equal to 6 mol % or even less than or equal to 4.5 mol %. Without wishing to be bound by theory, it is hypothesized that similar behavior may occur with colorants other than Au and Cr₂O₃.

In embodiments, the sum (in mol %) of MgO and ZnO present in the glass composition and the resultant colored glass article (i.e., MgO (mol %)+ZnO (mol %)) may be greater than or equal to 0 mol % and less than or equal to 8 mol %, greater than or equal to 0.1 mol % and less than or equal to 8 mol %, greater than or equal to 0 mol % and less than or equal to 6 mol %, greater than or equal to 0.1 mol % and less than or equal to 6 mol %, or even greater than or equal to 0 mol % and less than or equal to 4.5 mol %. In embodiments, the sum of MgO and ZnO in the glass composition and the resultant colored glass article may be greater than or equal to 0.5 mol % and less than or equal to 5.5 mol %. In embodiments, the sum of MgO and ZnO in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol %, greater than or equal to 0.01 mol %, greater than or equal to 0.1 mol %, greater than or equal to 0.5 mol %, greater than or equal to 1 mol %, greater than or equal to 1.5 mol %, greater than or equal to 2 mol %, greater than or equal to 2.5 mol %, greater than or equal to 3 mol %, or even greater than or equal to 3.5 mol %. In embodiments, the sum of MgO and ZnO in the glass composition and the resultant colored glass article may be less than or equal to 8 mol %, less than or equal to 7 mol %, less than or equal to 6 mol %, less than or equal to 5.5 mol %, less than or equal to 5 mol %, less than or equal to 4.5 mol %, less than or equal to 4.25 mol %, or even less than or equal to 4 mol %. In embodiments, the sum of MgO and ZnO in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 8 mol %, greater than or equal to 0 mol % and less than or equal to 7 mol %, greater than or equal to 0 mol % and less than or equal to 6 mol %, greater than or equal to 0 mol % and less than or equal to 5.5 mol %, greater than or equal to 0 mol % and less than or equal to 5 mol %, greater than or equal to 0 mol % and less than or equal to 4.5 mol %, greater than or equal to 0 mol % and less than or equal to 4.25 mol %, greater than or equal to 0 mol % and less than or equal to 4 mol %, greater than or equal to 0.1 mol % and less than or equal to 8 mol %, greater than or equal to 0.1 mol % and less than or equal to 7 mol %, greater than or equal to 0.1 mol % and less than or equal to 6 mol %, greater than or equal to 0.1 mol % and less than or equal to 5.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 5 mol %, greater than or equal to 0.1 mol % and less than or equal to 4.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 4.25 mol %, greater than or equal to 0.1 mol % and less than or equal to 4 mol %, greater than or equal to 0.5 mol % and less than or equal to 8 mol %, greater than or equal to 0.5 mol % and less than or equal to 7 mol %, greater than or equal to 0.5 mol % and less than or equal to 6 mol %, greater than or equal to 0.5 mol % and less than or equal to 5.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 5 mol %, greater than or equal to 0.5 mol % and less than or equal to 4.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 4.25 mol %, greater than or equal to 0.5 mol % and less than or equal to 4 mol %, greater than or equal to 1 mol % and less than or equal to 8 mol %, greater than or equal to 1 mol % and less than or equal to 7 mol %, greater than or equal to 1 mol % and less than or equal to 6 mol %, greater than or equal to 1 mol % and less than or equal to 5.5 mol %, greater than or equal to 1 mol % and less than or equal to 5 mol %, greater than or equal to 1 mol % and less than or equal to 4.5 mol %, greater than or equal to 1 mol % and less than or equal to 4.25 mol %, greater than or equal to 1 mol % and less than or equal to 4 mol %, greater than or equal to 1.5 mol % and less than or equal to 8 mol %, greater than or equal to 1.5 mol % and less than or equal to 7 mol %, greater than or equal to 1.5 mol % and less than or equal to 6 mol %, greater than or equal to 1.5 mol % and less than or equal to 5.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 5 mol %, greater than or equal to 1.5 mol % and less than or equal to 4.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 4.25 mol %, greater than or equal to 1.5 mol % and less than or equal to 4 mol %, greater than or equal to 2 mol % and less than or equal to 8 mol %, greater than or equal to 2 mol % and less than or equal to 7 mol %, greater than or equal to 2 mol % and less than or equal to 6 mol %, greater than or equal to 2 mol % and less than or equal to 5.5 mol %, greater than or equal to 2 mol % and less than or equal to 5 mol %, greater than or equal to 2 mol % and less than or equal to 4.5 mol %, greater than or equal to 2 mol % and less than or equal to 4.25 mol %, greater than or equal to 2 mol % and less than or equal to 4 mol %, greater than or equal to 2.5 mol % and less than or equal to 8 mol %, greater than or equal to 2.5 mol % and less than or equal to 7 mol %, greater than or equal to 2.5 mol % and less than or equal to 6 mol %, greater than or equal to 2.5 mol % and less than or equal to 5.5 mol %, greater than or equal to 2.5 mol % and less than or equal to 5 mol %, greater than or equal to 2.5 mol % and less than or equal to 4.5 mol %, greater than or equal to 2.5 mol % and less than or equal to 4.25 mol %, greater than or equal to 2.5 mol % and less than or equal to 4 mol %, greater than or equal to 3 mol % and less than or equal to 8 mol %, greater than or equal to 3 mol % and less than or equal to 7 mol %, greater than or equal to 3 mol % and less than or equal to 6 mol %, greater than or equal to 3 mol % and less than or equal to 5.5 mol %, greater than or equal to 3 mol % and less than or equal to 5 mol %, greater than or equal to 3 mol % and less than or equal to 4.5 mol %, greater than or equal to 3 mol % and less than or equal to 4.25 mol %, greater than or equal to 3 mol % and less than or equal to 4 mol %, greater than or equal to 3 mol % and less than or equal to 8 mol %, greater than or equal to 3 mol % and less than or equal to 7 mol %, greater than or equal to 3.5 mol % and less than or equal to 6 mol %, greater than or equal to 3.5 mol % and less than or equal to 5.5 mol %, greater than or equal to 3.5 mol % and less than or equal to 5 mol %, or even greater than or equal to 3.5 mol % and less than or equal to 4.5 mol %, greater than or equal to 3.5 mol % and less than or equal to 4.25 mol %, greater than or equal to 3.5 mol % and less than or equal to 4 mol %, or any and all sub-ranges formed from any of these endpoints.

In addition to improving colorant retention, MgO lowers the viscosity of the glass compositions, which enhances the formability, the strain point, and the Young's modulus, and may improve ion-exchangeability. However, when too much MgO is added to the glass composition, the diffusivity of sodium and potassium ions in the glass composition decreases which, in turn, adversely impacts the ion-exchange performance (i.e., the ability to ion-exchange) of the resultant colored glass article.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0 mol % and less than or equal to 8 mol % MgO or even greater than or equal to 0 mol % and less than or equal to 4.5 mol % MgO. In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0.5 mol % and less than or equal to 7 mol % MgO. In embodiments, the concentration of MgO in the glass composition may be greater than or equal to 0 mol %, greater than or equal to 0.5 mol %, greater than or equal to 1 mol %, greater than or equal to 1.5 mol %, greater than or equal to 2 mol %, or even greater than or equal to 2.5 mol %. In embodiments, the concentration of MgO in the glass composition may be less than or equal to 8 mol %, less than or equal to 7 mol %, less than or equal to 6 mol %, less than or equal to 5.5 mol %, less than or equal to 5 mol %, less than or equal to 4.5 mol %, less than or equal to 4 mol %, less than or equal to 3.5 mol %, less than or equal to 3 mol %, less than or equal to 2.5 mol %, less than or equal to 2 mol %, less than or equal to 1.5 mol %, or even less than or equal to 1 mol %. In embodiments, the concentration of MgO in the glass composition may be greater than or equal to 0 mol % and less than or equal to 8 mol %, greater than or equal to 0 mol % and less than or equal to 7 mol %, greater than or equal to 0 mol % and less than or equal to 6 mol %, greater than or equal to 0 mol % and less than or equal to 5.5 mol %, greater than or equal to 0 mol % and less than or equal to 5 mol %, greater than or equal to 0 mol % and less than or equal to 4.5 mol %, greater than or equal to 0 mol % and less than or equal to 4 mol %, greater than or equal to 0 mol % and less than or equal to 3.5 mol %, greater than or equal to 0 mol % and less than or equal to 3 mol %, greater than or equal to 0 mol % and less than or equal to 2.5 mol %, greater than or equal to 0 mol % and less than or equal to 2 mol %, greater than or equal to 0 mol % and less than or equal to 1.5 mol %, greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 8 mol %, greater than or equal to 0.5 mol % and less than or equal to 7 mol %, greater than or equal to 0.5 mol % and less than or equal to 6 mol %, greater than or equal to 0.5 mol % and less than or equal to 5.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 5 mol %, greater than or equal to 0.5 mol % and less than or equal to 4.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 4 mol %, greater than or equal to 0.5 mol % and less than or equal to 3.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 3 mol %, greater than or equal to 0.5 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 2 mol %, greater than or equal to 0.5 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 1 mol %, greater than or equal to 1 mol % and less than or equal to 8 mol %, greater than or equal to 1 mol % and less than or equal to 7 mol %, greater than or equal to 1 mol % and less than or equal to 6 mol %, greater than or equal to 1 mol % and less than or equal to 5.5 mol %, greater than or equal to 1 mol % and less than or equal to 5 mol %, greater than or equal to 1 mol % and less than or equal to 4.5 mol %, greater than or equal to 1 mol % and less than or equal to 4 mol %, greater than or equal to 1 mol % and less than or equal to 3.5 mol %, greater than or equal to 1 mol % and less than or equal to 3 mol %, greater than or equal to 1 mol % and less than or equal to 2.5 mol %, greater than or equal to 1 mol % and less than or equal to 2 mol %, greater than or equal to 1 mol % and less than or equal to 1.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 8 mol %, greater than or equal to 1.5 mol % and less than or equal to 7 mol %, greater than or equal to 1.5 mol % and less than or equal to 6 mol %, greater than or equal to 1.5 mol % and less than or equal to 5.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 5 mol %, greater than or equal to 1.5 mol % and less than or equal to 4.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 4 mol %, greater than or equal to 1.5 mol % and less than or equal to 3.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 3 mol %, greater than or equal to 1.5 mol % and less than or equal to 2.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 2 mol %, greater than or equal to 2 mol % and less than or equal to 8 mol %, greater than or equal to 2 mol % and less than or equal to 7 mol %, greater than or equal to 2 mol % and less than or equal to 6 mol %, greater than or equal to 2 mol % and less than or equal to 5.5 mol %, greater than or equal to 2 mol % and less than or equal to 5 mol %, greater than or equal to 2 mol % and less than or equal to 4.5 mol %, greater than or equal to 2 mol % and less than or equal to 4 mol %, greater than or equal to 2 mol % and less than or equal to 3.5 mol %, greater than or equal to 2 mol % and less than or equal to 3 mol %, greater than or equal to 2 mol % and less than or equal to 2.5 mol %, greater than or equal to 0 mol % and less than or equal to 8 mol %, greater than or equal to 2.5 mol % and less than or equal to 7 mol %, greater than or equal to 2.5 mol % and less than or equal to 6 mol %, greater than or equal to 2.5 mol % and less than or equal to 5.5 mol %, greater than or equal to 2.5 mol % and less than or equal to 5 mol %, greater than or equal to 2.5 mol % and less than or equal to 4.5 mol %, greater than or equal to 2.5 mol % and less than or equal to 4 mol %, greater than or equal to 2.5 mol % and less than or equal to 3.5 mol %, or even greater than or equal to 2.5 mol % and less than or equal to 3 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the glass composition and the resultant colored glass article may be substantially free or free of MgO.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0 mol % and less than or equal to 6 mol % MgO. In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0.1 mol % and less than or equal to 5 mol % MgO. In embodiments, the concentration of MgO in the glass composition may be greater than or equal to 0 mol %, greater than or equal to 0.1 mol %, or even greater than or equal to 0.5 mol %. In embodiments, the concentration of MgO in the glass composition may be less than or equal to 6 mol %, less than or equal to 5 mol %, less than or equal to 4 mol %, less than or equal to 3 mol %, less than or equal to 2 mol %, or even less than or equal to 1 mol %. In embodiments, the concentration of MgO in the glass composition may be greater than or equal to 0 mol % and less than or equal to 6 mol %, greater than or equal to 0 mol % and less than or equal to 5 mol %, greater than or equal to 0 mol % and less than or equal to 4 mol %, greater than or equal to 0 mol % and less than or equal to 3 mol %, greater than or equal to 0 mol % and less than or equal to 2 mol %, greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0.1 mol % and less than or equal to 6 mol %, greater than or equal to 0.1 mol % and less than or equal to 5 mol %, greater than or equal to 0.1 mol % and less than or equal to 4 mol %, greater than or equal to 0.1 mol % and less than or equal to 3 mol %, greater than or equal to 0.1 mol % and less than or equal to 2 mol %, greater than or equal to 0.1 mol % and less than or equal to 1 mol %, greater than or equal to 0.5 mol % and less than or equal to 6 mol %, greater than or equal to 0.5 mol % and less than or equal to 5 mol %, greater than or equal to 0.5 mol % and less than or equal to 4 mol %, greater than or equal to 0.5 mol % and less than or equal to 3 mol %, greater than or equal to 0.5 mol % and less than or equal to 2 mol %, or even greater than or equal to 0.5 mol % and less than or equal to 1 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the glass composition and the resultant colored glass article may be substantially free or free of MgO.

In addition to improving colorant retention, ZnO lowers the viscosity of the glass compositions, which enhances the formability, the strain point, and the Young's modulus, and may improve ion-exchangeability. However, when too much ZnO is added to the glass composition, the diffusivity of sodium and potassium ions in the glass composition decreases which, in turn, adversely impacts the ion-exchange performance (i.e., the ability to ion-exchange) of the resultant colored glass article.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0 mol % and less than or equal to 5 mol % ZnO or even greater than or equal to 0 mol % and less than or equal to 4.5 mol % ZnO. In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0.1 mol % and less than or equal to 4 mol % ZnO. In embodiments, the concentration of ZnO in the glass composition may be greater than or equal to 0 mol %, greater than or equal to 0.1 mol %, greater than or equal to 0.25 mol %, greater than or equal to 0.5 mol %, greater than or equal to 0.75 mol %, greater than or equal to 1 mol %, greater than or equal to 1.5 mol %, or even greater than or equal to 2 mol %. In embodiments, the concentration of ZnO in the glass composition may be less than or equal to 5 mol %, less than or equal to 4.5 mol %, less than or equal to 4 mol %, less than or equal to 3.5 mol %, less than or equal to 3 mol %, less than or equal to 2.5 mol %, less than or equal to 2 mol %, less than or equal to 1.75 mol %, less than or equal to 1.5 mol %, less than or equal to 1.25 mol %, or even less than or equal to 1 mol %. In embodiments, the concentration of ZnO in the glass composition may be greater than or equal to 0 mol % and less than or equal to 5 mol %, greater than or equal to 0 mol % and less than or equal to 4.5 mol %, greater than or equal to 0 mol % and less than or equal to 4 mol %, greater than or equal to 0 mol % and less than or equal to 3.5 mol %, greater than or equal to 0 mol % and less than or equal to 3 mol %, greater than or equal to 0 mol % and less than or equal to 2.5 mol %, greater than or equal to 0 mol % and less than or equal to 2 mol %, greater than or equal to 0 mol % and less than or equal to 1.75 mol %, greater than or equal to 0 mol % and less than or equal to 1.5 mol %, greater than or equal to 0 mol % and less than or equal to 1.25 mol %, greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0.1 mol % and less than or equal to 5 mol %, greater than or equal to 0.1 mol % and less than or equal to 4.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 4 mol %, greater than or equal to 0.1 mol % and less than or equal to 3.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 3 mol %, greater than or equal to 0.1 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 2 mol %, greater than or equal to 0.1 mol % and less than or equal to 1.75 mol %, greater than or equal to 0.1 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 1.25 mol %, greater than or equal to 0.1 mol % and less than or equal to 1 mol %, greater than or equal to 0.25 mol % and less than or equal to 5 mol %, greater than or equal to 0.25 mol % and less than or equal to 4.5 mol %, greater than or equal to 0.25 mol % and less than or equal to 4 mol %, greater than or equal to 0.25 mol % and less than or equal to 3.5 mol %, greater than or equal to 0.25 mol % and less than or equal to 3 mol %, greater than or equal to 0.25 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.25 mol % and less than or equal to 2 mol %, greater than or equal to 0.25 mol % and less than or equal to 1.75 mol %, greater than or equal to 0.25 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.25 mol % and less than or equal to 1.25 mol %, greater than or equal to 0.25 mol % and less than or equal to 1 mol %, greater than or equal to 0.5 mol % and less than or equal to 5 mol %, greater than or equal to 0.5 mol % and less than or equal to 4.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 4 mol %, greater than or equal to 0.5 mol % and less than or equal to 3.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 3 mol %, greater than or equal to 0.5 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 2 mol %, greater than or equal to 0.5 mol % and less than or equal to 1.75 mol %, greater than or equal to 0.5 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 1.25 mol %, greater than or equal to 0.5 mol % and less than or equal to 1 mol %, greater than or equal to 0.75 mol % and less than or equal to 5 mol %, greater than or equal to 0.75 mol % and less than or equal to 4 mol %, greater than or equal to 0.75 mol % and less than or equal to 3 mol %, greater than or equal to 0.75 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.75 mol % and less than or equal to 2 mol %, greater than or equal to 0.75 mol % and less than or equal to 1.75 mol %, greater than or equal to 0.75 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.75 mol % and less than or equal to 1.25 mol %, greater than or equal to 1 mol % and less than or equal to 1 mol %, greater than or equal to 1 mol % and less than or equal to 5 mol %, greater than or equal to 1 mol % and less than or equal to 4.5 mol %, greater than or equal to 1 mol % and less than or equal to 4 mol %, greater than or equal to 1 mol % and less than or equal to 3.5 mol %, greater than or equal to 1 mol % and less than or equal to 3 mol %, greater than or equal to 1 mol % and less than or equal to 2.5 mol %, greater than or equal to 1 mol % and less than or equal to 2 mol %, greater than or equal to 1 mol % and less than or equal to 1.75 mol %, greater than or equal to 1 mol % and less than or equal to 1.5 mol %, greater than or equal to 1 mol % and less than or equal to 1.25 mol %, greater than or equal to 1.5 mol % and less than or equal to 5 mol %, greater than or equal to 1.5 mol % and less than or equal to 4.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 4 mol %, greater than or equal to 1.5 mol % and less than or equal to 3.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 3 mol %, greater than or equal to 1.5 mol % and less than or equal to 2.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 2 mol %, greater than or equal to 1.5 mol % and less than or equal to 1.75 mol %, greater than or equal to 2 mol % and less than or equal to 5 mol %, greater than or equal to 2 mol % and less than or equal to 4.5 mol %, greater than or equal to 2 mol % and less than or equal to 4 mol %, greater than or equal to 2 mol % and less than or equal to 3.5 mol %, greater than or equal to 2 mol % and less than or equal to 3 mol %, or even greater than or equal to 2 mol % and less than or equal to 2.5 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the glass composition and the resultant colored glass article may be substantially free or free of ZnO.

Like ZnO and the alkaline earth oxide MgO, other alkaline earth oxides, such as CaO, SrO and BaO, decrease the melting point of the glass composition. Accordingly, CaO, SrO, and/or BaO may be included in the glass composition and the resultant colored glass articles to lower the melting point of the glass composition, which may help improve colorant retention.

In embodiments, the glass compositions and the resultant colored glass articles described herein may further comprise CaO. CaO lowers the viscosity of a glass composition, which enhances the formability, the strain point and the Young's modulus, and may improve the ion-exchangeability. However, when too much CaO is added to the glass composition, the diffusivity of sodium and potassium ions in the glass composition decreases which, in turn, adversely impacts the ion-exchange performance (i.e., the ability to ion-exchange) of the resultant glass.

In embodiments, the concentration of CaO in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol %, greater than or equal to 0.25 mol %, greater than or equal to 0.5 mol %, or even greater than or equal to 0.75 mol %. In embodiments, the concentration of CaO in the glass composition and the resultant colored glass article may be less than or equal to 7 mol %, less than or equal to 6.5 mol %, less than or equal to 6 mol %, less than or equal to 5.5 mol %, less than or equal to 5 mol %, less than or equal to 4.5 mol %, less than or equal to 4 mol %, less than or equal to 3.5 mol %, less than or equal to 3 mol %, less than or equal to 2.5 mol %, less than or equal to 2 mol %, less than or equal to 1.75 mol %, less than or equal to 1.5 mol %, less than or equal to 1.25 mol %, or even less than or equal to 1 mol %. In embodiments, the concentration of CaO in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 7 mol %, greater than or equal to 0 mol % and less than or equal to 6.5 mol %, greater than or equal to 0 mol % and less than or equal to 6 mol %, greater than or equal to 0 mol % and less than or equal to 5.5 mol %, greater than or equal to 0 mol % and less than or equal to 5 mol %, greater than or equal to 0 mol % and less than or equal to 4.5 mol %, greater than or equal to 0 mol % and less than or equal to 4 mol %, greater than or equal to 0 mol % and less than or equal to 3.5 mol %, greater than or equal to 0 mol % and less than or equal to 3 mol %, greater than or equal to 0 mol % and less than or equal to 2.5 mol %, greater than or equal to 0 mol % and less than or equal to 2 mol %, greater than or equal to 0 mol % and less than or equal to 1.75 mol %, greater than or equal to 0 mol % and less than or equal to 1.5 mol %, greater than or equal to 0 mol % and less than or equal to 1.25 mol %, greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0.25 mol % and less than or equal to 7 mol %, greater than or equal to 0.25 mol % and less than or equal to 6.5 mol %, greater than or equal to 0.25 mol % and less than or equal to 6 mol %, greater than or equal to 0.25 mol % and less than or equal to 5.5 mol %, greater than or equal to 0.25 mol % and less than or equal to 5 mol %, greater than or equal to 0.25 mol % and less than or equal to 4.5 mol %, greater than or equal to 0.25 mol % and less than or equal to 4 mol %, greater than or equal to 0.25 mol % and less than or equal to 3.5 mol %, greater than or equal to 0.25 mol % and less than or equal to 3 mol %, greater than or equal to 0.25 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.25 mol % and less than or equal to 2 mol %, greater than or equal to 0.25 mol % and less than or equal to 1.75 mol %, greater than or equal to 0.25 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.25 mol % and less than or equal to 1.25 mol %, greater than or equal to 0.25 mol % and less than or equal to 1 mol %, greater than or equal to 0.5 mol % and less than or equal to 7 mol %, greater than or equal to 0.5 mol % and less than or equal to 6.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 6 mol %, greater than or equal to 0.5 mol % and less than or equal to 5.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 5 mol %, greater than or equal to 0.5 mol % and less than or equal to 4.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 4 mol %, greater than or equal to 0.5 mol % and less than or equal to 3.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 3 mol %, greater than or equal to 0.5 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 2 mol %, greater than or equal to 0.5 mol % and less than or equal to 1.75 mol %, greater than or equal to 0.5 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 1.25 mol %, greater than or equal to 0.5 mol % and less than or equal to 1 mol %, greater than or equal to 0.75 mol % and less than or equal to 7 mol %, greater than or equal to 0.75 mol % and less than or equal to 6.5 mol %, greater than or equal to 0.75 mol % and less than or equal to 6 mol %, greater than or equal to 0.75 mol % and less than or equal to 5.5 mol %, greater than or equal to 0.75 mol % and less than or equal to 5 mol %, greater than or equal to 0.75 mol % and less than or equal to 4.5 mol %, greater than or equal to 0.75 mol % and less than or equal to 4 mol %, greater than or equal to 0.75 mol % and less than or equal to 3.5 mol %, greater than or equal to 0.75 mol % and less than or equal to 3 mol %, greater than or equal to 0.75 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.75 mol % and less than or equal to 2 mol %, greater than or equal to 0.75 mol % and less than or equal to 1.75 mol %, greater than or equal to 0.75 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.75 mol % and less than or equal to 1.25 mol %, or even greater than or equal to 0.75 mol % and less than or equal to 1 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the glass composition and the resultant colored glass article may be substantially free or free of CaO.

In embodiments, the concentration of SrO in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol %, greater than or equal to 0.25 mol %, greater than or equal to 0.5 mol %, or even greater than or equal to 0.75 mol %. In embodiments, the concentration of SrO in the glass composition and the resultant colored glass article may be less than or equal to 2 mol %, less than or equal to 1.75 mol %, less than or equal to 1.5 mol %, less than or equal to 1.25 mol %, or even less than or equal to 1 mol %. In embodiments, the concentration of SrO in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 2 mol %, greater than or equal to 0 mol % and less than or equal to 1.75 mol %, greater than or equal to 0 mol % and less than or equal to 1.5 mol %, greater than or equal to 0 mol % and less than or equal to 1.25 mol %, greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0.25 mol % and less than or equal to 2 mol %, greater than or equal to 0.25 mol % and less than or equal to 1.75 mol %, greater than or equal to 0.25 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.25 mol % and less than or equal to 1.25 mol %, greater than or equal to 0.25 mol % and less than or equal to 1 mol %, greater than or equal to 0.5 mol % and less than or equal to 2 mol %, greater than or equal to 0.5 mol % and less than or equal to 1.75 mol %, greater than or equal to 0.5 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 1.25 mol %, greater than or equal to 0.5 mol % and less than or equal to 1 mol %, greater than or equal to 0.75 mol % and less than or equal to 2 mol %, greater than or equal to 0.75 mol % and less than or equal to 1.75 mol %, greater than or equal to 0.75 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.75 mol % and less than or equal to 1.25 mol %, or even greater than or equal to 0.75 mol % and less than or equal to 1 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the glass composition and the resultant colored glass article may be substantially free or free of SrO.

In embodiments, the concentration of BaO in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol %, greater than or equal to 0.25 mol %, greater than or equal to 0.5 mol %, or even greater than or equal to 0.75 mol %. In embodiments, the concentration of BaO in the glass composition and the resultant colored glass article may be less than or equal to 2 mol %, less than or equal to 1.75 mol %, less than or equal to 1.5 mol %, less than or equal to 1.25 mol %, or even less than or equal to 1 mol %. In embodiments, the concentration of BaO in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 2 mol %, greater than or equal to 0 mol % and less than or equal to 1.75 mol %, greater than or equal to 0 mol % and less than or equal to 1.5 mol %, greater than or equal to 0 mol % and less than or equal to 1.25 mol %, greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0.25 mol % and less than or equal to 2 mol %, greater than or equal to 0.25 mol % and less than or equal to 1.75 mol %, greater than or equal to 0.25 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.25 mol % and less than or equal to 1.25 mol %, greater than or equal to 0.25 mol % and less than or equal to 1 mol %, greater than or equal to 0.5 mol % and less than or equal to 2 mol %, greater than or equal to 0.5 mol % and less than or equal to 1.75 mol %, greater than or equal to 0.5 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 1.25 mol %, greater than or equal to 0.5 mol % and less than or equal to 1 mol %, greater than or equal to 0.75 mol % and less than or equal to 2 mol %, greater than or equal to 0.75 mol % and less than or equal to 1.75 mol %, greater than or equal to 0.75 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.75 mol % and less than or equal to 1.25 mol %, or even greater than or equal to 0.75 mol % and less than or equal to 1 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the glass composition and the resultant colored glass article may be substantially free or free of BaO.

R′O, as used herein, is the sum (in mol %) of MgO, ZnO, CaO, BaO, and SrO (i.e. R′O=MgO (mol %)+ZnO (mol %)+CaO (mol %)+BaO (mol %)+SrO (mol %)). In embodiments, the concentration of R′O in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol %, greater than or equal to 0.5 mol %, greater than or equal to 1 mol %, greater than or equal to 1.5 mol %, greater than or equal to 2 mol %, or even greater than or equal to 2.5 mol %. In embodiments, the concentration of R′O in the glass composition and the resultant colored glass article may be less than or equal to 8 mol %, less than or equal to 7.5 mol %, less than or equal to 7 mol %, less than or equal to 6.5 mol %, less than or equal to 6 mol %, less than or equal to 5 mol %, less than or equal to 5 mol %, less than or equal to 4.5 mol %, less than or equal to 4 mol %, or even less than or equal to 3.5 mol %. In embodiments, the concentration of R′O in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 8 mol %, greater than or equal to 0 mol % and less than or equal to 7.5 mol %, greater than or equal to 0 mol % and less than or equal to 7 mol %, greater than or equal to 0 mol % and less than or equal to 6.5 mol %, greater than or equal to 0 mol % and less than or equal to 6 mol %, greater than or equal to 0 mol % and less than or equal to 5.5 mol %, greater than or equal to 0 mol % and less than or equal to 5 mol %, greater than or equal to 0 mol % and less than or equal to 4.5 mol %, greater than or equal to 0 mol % and less than or equal to 4 mol %, greater than or equal to 0 mol % and less than or equal to 3.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 8 mol %, greater than or equal to 0.5 mol % and less than or equal to 7.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 7 mol %, greater than or equal to 0.5 mol % and less than or equal to 6.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 6 mol %, greater than or equal to 0.5 mol % and less than or equal to 5.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 5 mol %, greater than or equal to 0.5 mol % and less than or equal to 4.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 4 mol %, greater than or equal to 0.5 mol % and less than or equal to 3.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 8 mol %, greater than or equal to 1 mol % and less than or equal to 7.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 7 mol %, greater than or equal to 1 mol % and less than or equal to 6.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 6 mol %, greater than or equal to 1 mol % and less than or equal to 5.5 mol %, greater than or equal to 1 mol % and less than or equal to 5 mol %, greater than or equal to 1 mol % and less than or equal to 4.5 mol %, greater than or equal to 1 mol % and less than or equal to 4 mol %, greater than or equal to 1 mol % and less than or equal to 3.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 8 mol %, greater than or equal to 1.5 mol % and less than or equal to 7.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 7 mol %, greater than or equal to 1.5 mol % and less than or equal to 6.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 6 mol %, greater than or equal to 1.5 mol % and less than or equal to 5.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 5 mol %, greater than or equal to 1.5 mol % and less than or equal to 4.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 4 mol %, greater than or equal to 1.5 mol % and less than or equal to 3.5 mol %, greater than or equal to 2 mol % and less than or equal to 8 mol %, greater than or equal to 2 mol % and less than or equal to 7.5 mol %, greater than or equal to 2 mol % and less than or equal to 7 mol %, greater than or equal to 2 mol % and less than or equal to 6.5 mol %, greater than or equal to 2 mol % and less than or equal to 6 mol %, greater than or equal to 2 mol % and less than or equal to 5.5 mol %, greater than or equal to 2 mol % and less than or equal to 5 mol %, greater than or equal to 2 mol % and less than or equal to 4.5 mol %, greater than or equal to 2 mol % and less than or equal to 4 mol %, greater than or equal to 2 mol % and less than or equal to 3.5 mol %, greater than or equal to 2.5 mol % and less than or equal to 8 mol %, greater than or equal to 2.5 mol % and less than or equal to 7.5 mol %, greater than or equal to 2.5 mol % and less than or equal to 7 mol %, greater than or equal to 2.5 mol % and less than or equal to 6.5 mol %, greater than or equal to 2.5 mol % and less than or equal to 6 mol %, greater than or equal to 2.5 mol % and less than or equal to 5.5 mol %, greater than or equal to 2.5 mol % and less than or equal to 5 mol %, greater than or equal to 2.5 mol % and less than or equal to 4.5 mol %, greater than or equal to 2.5 mol % and less than or equal to 4 mol %, or even greater than or equal to 2.5 mol % and less than or equal to 3.5 mol %, or any and all sub-ranges formed from any of these endpoints.

In embodiments, the sum of R₂O, CaO, MgO, and ZnO (R₂O (mol %)+CaO (mol %)+MgO (mol %)+ZnO (mol %) may be less than or equal to 35 mol %. While not wishing to be bound by theory, it is believed that minimizing the combination of R₂O, CaO, MgO, and ZnO in the glass composition may provide the resultant colored glass article with a desirable dielectric constant, such as when the colored glass article is used as a portion of a housing for an electronic device. In embodiments, R₂O (mol %)+CaO (mol %)+MgO (mol %)+ZnO (mol %) may be greater than or equal to 1 mol % and less than or equal to 35 mol %, greater than or equal to 1 mol % and less than or equal to 30 mol %, greater than or equal to 1 mol % and less than or equal to 25 mol %, greater than or equal to 1 mol % and less than or equal to 20 mol %, greater than or equal to 1 mol % and less than or equal to 15 mol %, greater than or equal to 1 mol % and less than or equal to 10 mol %, greater than or equal to 2 mol % and less than or equal to 35 mol %, greater than or equal to 2 mol % and less than or equal to 30 mol %, greater than or equal to 2 mol % and less than or equal to 25 mol %, greater than or equal to 2 mol % and less than or equal to 20 mol %, greater than or equal to 2 mol % and less than or equal to 15 mol %, greater than or equal to 2 mol % and less than or equal to 10 mol %, greater than or equal to 3 mol % and less than or equal to 35 mol %, greater than or equal to 3 mol % and less than or equal to 30 mol %, greater than or equal to 3 mol % and less than or equal to 25 mol %, greater than or equal to 3 mol % and less than or equal to 20 mol %, greater than or equal to 3 mol % and less than or equal to 15 mol %, greater than or equal to 3 mol % and less than or equal to 10 mol %, greater than or equal to 4 mol % and less than or equal to 35 mol %, greater than or equal to 4 mol % and less than or equal to 30 mol %, greater than or equal to 4 mol % and less than or equal to 25 mol %, greater than or equal to 4 mol % and less than or equal to 20 mol %, greater than or equal to 4 mol % and less than or equal to 15 mol %, greater than or equal to 4 mol % and less than or equal to 10 mol %, greater than or equal to 4 mol % and less than or equal to 35 mol %, greater than or equal to 5 mol % and less than or equal to 30 mol %, greater than or equal to 5 mol % and less than or equal to 25 mol %, greater than or equal to 5 mol % and less than or equal to 20 mol %, greater than or equal to 5 mol % and less than or equal to 15 mol %, greater than or equal to 5 mol % and less than or equal to 10 mol %, greater than or equal to 6 mol % and less than or equal to 35 mol %, greater than or equal to 6 mol % and less than or equal to 30 mol %, greater than or equal to 6 mol % and less than or equal to 25 mol %, greater than or equal to 6 mol % and less than or equal to 20 mol %, greater than or equal to 6 mol % and less than or equal to 15 mol %, greater than or equal to 6 mol % and less than or equal to 10 mol %, greater than or equal to 7 mol % and less than or equal to 35 mol %, greater than or equal to 7 mol % and less than or equal to 30 mol %, greater than or equal to 7 mol % and less than or equal to 25 mol %, greater than or equal to 7 mol % and less than or equal to 20 mol %, greater than or equal to 7 mol % and less than or equal to 15 mol %, greater than or equal to 7 mol % and less than or equal to 10 mol %, greater than or equal to 8 mol % and less than or equal to 35 mol %, greater than or equal to 8 mol % and less than or equal to 30 mol %, greater than or equal to 8 mol % and less than or equal to 25 mol %, greater than or equal to 8 mol % and less than or equal to 20 mol %, greater than or equal to 8 mol % and less than or equal to 15 mol %, or even greater than or equal to 8 mol % and less than or equal to 10 mol %.

In embodiments, the sum of Al₂O₃, MgO, and ZnO present in the glass composition and the resultant colored glass article (i.e., Al₂O₃ (mol %)+MgO (mol %)+ZnO (mol %)) may be greater than or equal to 12 mol % and less than or equal to 22 mol %. While not wishing to be bound by theory, it is believed that combinations of Al₂O₃, MgO, and ZnO within this range may aid in avoiding the formation of undesired crystal phases in the resultant colored glass articles. For example and without limitation, when the colorant package in the glass composition and the resultant colored glass article includes Cr₂O₃, combinations of Al₂O₃, MgO, and ZnO within this range may avoid the formation of Cr-spinel crystals by increasing the solubility of the Cr₂O₃ colorant and thereby expanding the color gamut that may be achieved in the resultant colored glass articles. Without wishing to be bound by theory, it is hypothesized that similar behavior may occur with colorants other than Cr₂O₃.

In embodiments, the sum of Al₂O₃, MgO, and ZnO in the glass composition and the resultant colored glass article may be greater than or equal to 13 mol % and less than or equal to 21.5 mol %. In embodiments, the sum of Al₂O₃, MgO, and ZnO in the glass composition and the resultant colored glass article may be greater than or equal to 12 mol %, greater than or equal to 13 mol %, greater than or equal to 14 mol %, greater than or equal to 15 mol %, or even greater than or equal to 16 mol %. In embodiments, the sum of Al₂O₃, MgO, and ZnO in the glass composition and the resultant colored glass article may be less than or equal to 22 mol %, less than or equal to 21.5 mol %, less than or equal to 21 mol %, less than or equal to 20.5 mol %, or even less than or equal to 20 mol %. In embodiments, the sum of Al₂O₃, MgO, and ZnO in the glass composition and the resultant colored glass article may be greater than or equal to 12 mol % and less than or equal to 22 mol %, greater than or equal to 12 mol % and less than or equal to 21.5 mol %, greater than or equal to 12 mol % and less than or equal to 21 mol %, greater than or equal to 12 mol % and less than or equal to 20.5 mol %, greater than or equal to 12 mol % and less than or equal to 20 mol %, greater than or equal to 13 mol % and less than or equal to 22 mol %, greater than or equal to 13 mol % and less than or equal to 21.5 mol %, greater than or equal to 13 mol % and less than or equal to 21 mol %, greater than or equal to 13 mol % and less than or equal to 20.5 mol %, greater than or equal to 13 mol % and less than or equal to 20 mol %, greater than or equal to 14 mol % and less than or equal to 22 mol %, greater than or equal to 14 mol % and less than or equal to 21.5 mol %, greater than or equal to 14 mol % and less than or equal to 21 mol %, greater than or equal to 14 mol % and less than or equal to 20.5 mol %, greater than or equal to 15 mol % and less than or equal to 20 mol %, greater than or equal to 15 mol % and less than or equal to 22 mol %, greater than or equal to 15 mol % and less than or equal to 21.5 mol %, greater than or equal to 15 mol % and less than or equal to 21 mol %, greater than or equal to 15 mol % and less than or equal to 20.5 mol %, greater than or equal to 15 mol % and less than or equal to 20 mol %, greater than or equal to 16 mol % and less than or equal to 22 mol %, greater than or equal to 16 mol % and less than or equal to 21.5 mol %, greater than or equal to 16 mol % and less than or equal to 21 mol %, greater than or equal to 16 mol % and less than or equal to 20.5 mol %, or even greater than or equal to 16 mol % and less than or equal to 20 mol %, or any and all sub-ranges formed from any of these endpoints.

In embodiments, the sum of Al₂O₃, MgO, CaO, and ZnO present in the glass composition and the resultant colored glass article (i.e., Al₂O₃ (mol %)+MgO (mol %)+CaO (mol %)+ZnO (mol %)) may be greater than or equal to 12 mol % and less than or equal to 24 mol %. While not wishing to be bound by theory, it is believed that combinations of Al₂O₃, MgO, CaO and ZnO within this range may aid in avoiding the formation of undesired crystal phases in the resultant colored glass articles. In addition, a relatively high concentration of high field strength modifiers, such as Mg, Ca, and Zn cations, may also improve the mechanical properties, such as fracture toughness, elastic modulus and drop test performance, of the resultant colored glass article.

In embodiments, the sum of Al₂O₃, MgO, CaO and ZnO in the glass composition and the resultant colored glass article may be greater than or equal to 12 mol % and less than or equal to 24 mol %. In embodiments, the sum of Al₂O₃, MgO, CaO and ZnO in the glass composition and the resultant colored glass article may be greater than or equal to 12 mol %, greater than or equal to 13 mol %, greater than or equal to 14 mol %, greater than or equal to 15 mol %, or even greater than or equal to 16 mol %. In embodiments, the sum of Al₂O₃, MgO, CaO and ZnO in the glass composition and the resultant colored glass article may be less than or equal to 24 mol %, less than or equal to 23 mol %, less than or equal to 22 mol %, less than or equal to 21.5 mol %, less than or equal to 21 mol %, less than or equal to 20.5 mol %, or even less than or equal to 20 mol %. In embodiments, the sum of Al₂O₃, MgO, CaO and ZnO in the glass composition and the resultant colored glass article may be greater than or equal to 12 mol % and less than or equal to 24 mol %, greater than or equal to 12 mol % and less than or equal to 23 mol %, greater than or equal to 12 mol % and less than or equal to 22 mol %, greater than or equal to 12 mol % and less than or equal to 21.5 mol %, greater than or equal to 12 mol % and less than or equal to 21 mol %, greater than or equal to 12 mol % and less than or equal to 20.5 mol %, greater than or equal to 12 mol % and less than or equal to 20 mol %, greater than or equal to 13 mol % and less than or equal to 24 mol %, greater than or equal to 13 mol % and less than or equal to 23 mol %, greater than or equal to 13 mol % and less than or equal to 22 mol %, greater than or equal to 13 mol % and less than or equal to 21.5 mol %, greater than or equal to 13 mol % and less than or equal to 21 mol %, greater than or equal to 13 mol % and less than or equal to 20.5 mol %, greater than or equal to 13 mol % and less than or equal to 20 mol %, greater than or equal to 14 mol % and less than or equal to 24 mol %, greater than or equal to 14 mol % and less than or equal to 23 mol %, greater than or equal to 14 mol % and less than or equal to 22 mol %, greater than or equal to 14 mol % and less than or equal to 21.5 mol %, greater than or equal to 14 mol % and less than or equal to 21 mol %, greater than or equal to 14 mol % and less than or equal to 20.5 mol %, greater than or equal to 15 mol % and less than or equal to 24 mol %, greater than or equal to 15 mol % and less than or equal to 23 mol %, greater than or equal to 15 mol % and less than or equal to 22 mol %, greater than or equal to 15 mol % and less than or equal to 21.5 mol %, greater than or equal to 15 mol % and less than or equal to 21 mol %, greater than or equal to 15 mol % and less than or equal to 20.5 mol %, greater than or equal to 15 mol % and less than or equal to 20 mol %, greater than or equal to 16 mol % and less than or equal to 24 mol %, greater than or equal to 16 mol % and less than or equal to 23 mol %, greater than or equal to 16 mol % and less than or equal to 22 mol %, greater than or equal to 16 mol % and less than or equal to 21.5 mol %, greater than or equal to 16 mol % and less than or equal to 21 mol %, greater than or equal to 16 mol % and less than or equal to 20.5 mol %, or even greater than or equal to 16 mol % and less than or equal to 20 mol %, or any and all sub-ranges formed from any of these endpoints.

In embodiments, the sum of Al₂O₃, MgO, CaO and ZnO in the glass composition and the resultant colored glass article may be greater than or equal to 10 mol %, greater than or equal to 11 mol %, or even greater than or equal to 12 mol %. In embodiments, the sum of Al₂O₃, MgO, CaO and ZnO in the glass composition and the resultant colored glass article may be less than or equal to 30 mol %, less than or equal to 27 mol %, or even less than or equal to 24 mol %. In embodiments, the sum of Al₂O₃, MgO, CaO and ZnO in the glass composition and the resultant colored glass article may be greater than or equal to 10 mol % and less than or equal to 30 mol %, greater than or equal to 10 mol % and less than or equal to 27 mol %, greater than or equal to 10 mol % and less than or equal to 24 mol %, greater than or equal to 11 mol % and less than or equal to 30 mol %, greater than or equal to 11 mol % and less than or equal to 27 mol %, greater than or equal to 11 mol % and less than or equal to 24 mol %, greater than or equal to 12 mol % and less than or equal to 30 mol %, greater than or equal to 12 mol % and less than or equal to 27 mol %, or even greater than or equal to 12 mol % and less than or equal to 24 mol %, or any and all sub-ranges formed form any of these endpoints.

In embodiments, the glass composition and the resultant colored glass article may optionally include Cl, which may enable growth of particular crystal phases containing colorant. For example, when the colorant package included in the glass comprises Au, the inclusion of Cl may enable the growth of certain Au crystals. In embodiments, the concentration of Cl in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % or even greater than or equal to 0.1 mol %. In embodiments, the concentration of Cl in the glass composition and the resultant colored glass article may be less than or equal to 0.5 mol % or even less than or equal to 0.25 mol %. In embodiments, the concentration of Cl in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 0.5 mol %, greater than or equal to 0 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.5 mol %, or even greater than or equal to 0.1 mol % and less than or equal to 0.25 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the glass composition and the resultant colored glass article may be substantially free or free of Cl. In embodiments where the colorant package comprises Ag, the glass composition and resultant colored glass article include less than 100 ppm of halides, including Cl.

In embodiments, the glass compositions and the resultant colored glass articles described herein may further comprise ZrO₂. While not wishing to be bound by theory, it is believed that ZrO₂ may act as a multivalent species that serves as redox couples to supply oxygen to certain colorants, for example Au, during relatively low-temperature heat treatment, which helps improve retention of the colorant. Without wishing to be bound by theory, it is hypothesized that similar behavior may occur with colorants other than Au. ZrO₂ may also act as an additional colorant, producing colored glass articles that may be, for example, red in color. In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0.01 mol % and less than or equal to 2 mol % ZrO₂. In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0.01 mol % and less than or equal to 2 mol % ZrO₂. In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0.1 mol % and less than or equal to 1.5 mol % ZrO₂. In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0.25 mol % and less than or equal to 1.5 mol % ZrO₂. In embodiments, the concentration of ZrO₂ in the glass composition may be greater than or equal to 0 mol %, greater than or equal to 0.01 mol %, greater than or equal to 0.1 mol %, or even greater than or equal to 0.2 mol %. In embodiments, the concentration of ZrO₂ in the glass composition may be less than or equal to 2 mol %, less than or equal to 1.5 mol %, less than or equal to 1 mol %, less than or equal to 0.75 mol %, or even less than or equal to 0.5 mol %. In embodiments, the concentration of ZrO₂ in the glass composition may be greater than or equal to 0 mol % and less than or equal to 2 mol %, greater than or equal to 0 mol % and less than or equal to 1.5 mol %, greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0 mol % and less than or equal to 0.75 mol %, greater than or equal to 0 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 2 mol %, greater than or equal to 0.01 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 1 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 2 mol %, greater than or equal to 0.1 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 1 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.2 mol % and less than or equal to 2 mol %, greater than or equal to 0.2 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.2 mol % and less than or equal to 1 mol %, greater than or equal to 0.2 mol % and less than or equal to 0.75 mol %, or even greater than or equal to 0.2 mol % and less than or equal to 0.5 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the glass composition and the resultant colored glass article may be substantially free or free of ZrO₂.

In embodiments, the glass compositions and the resultant colored glass articles described herein may further comprise Fe₂O₃, which may help improve colorant retention. Fe₂O₃ is a multivalent species that serves as redox couples to supply oxygen to certain colorants, for example Au, during relatively low-temperature heat treatment, which helps improve retention of the colorant. Without wishing to be bound by theory, it is hypothesized that similar behavior may occur with colorants other than Au. Fe₂O₃ may also act as a colorant, producing colored glass articles that may, for example, be pink or red in color. In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0.01 mol % and less than or equal to 1 mol % Fe₂O₃ or even greater than or equal to 0.1 mol % and less than or equal to 1 mol % Fe₂O₃. In embodiments, the concentration of Fe₂O₃ in the glass composition may be greater than or equal to 0 mol %, greater than or equal to 0.01 mol %, or even greater than or equal to 0.1 mol %. In embodiments, the concentration of Fe₂O₃ in the glass composition may be less than or equal to 1 mol %, less than or equal to 0.75 mol %, less than or equal to 0.5 mol %, or even less than or equal to 0.25 mol %. In embodiments, the concentration of Fe₂O₃ in the glass composition may be greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0 mol % and less than or equal to 0.75 mol %, greater than or equal to 0 mol % and less than or equal to 0.5 mol %, greater than or equal to 0 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.01 mol % and less than or equal to 1 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.05 mol % and less than or equal to 1 mol %, greater than or equal to 0.05 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.05 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.05 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.1 mol % and less than or equal to 1 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.25 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the glass composition and the resultant colored glass article may be substantially free or free of Fe₂O₃.

In embodiments, the concentration of Fe₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol %, greater than or equal to 0.001 mol %, or even greater than or equal to 0.005 mol %. In embodiment, the concentration of Fe₂O₃ in the glass composition and the resultant colored glass article may be less than or equal to 0.5 mol %, less than or equal to 0.1 mol %, less than or equal to 0.05 mol %, or even less than or equal to 0.01 mol %. In embodiments, the composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 0.5 mol %, greater than or equal to 0 mol % and less than or equal to 0.1 mol %, greater than or equal to 0 mol % and less than or equal to 0.05 mol %, greater than or equal to 0 mol % and less than or equal to 0.01 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.1 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.05 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.01 mol %, greater than or equal to 0.005 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.005 mol % and less than or equal to 0.1 mol %, greater than or equal to 0.005 mol % and less than or equal to 0.05 mol %, or even greater than or equal to 0.005 mol % and less than or equal to 0.01 mol %, or any and all sub-ranges formed from any of these endpoints.

In embodiments, the glass compositions and the resultant colored glass articles described herein may further comprise SnO₂, Sb₂O₃, and/or Bi₂O₃. Like MgO and ZnO, SnO₂, Sb₂O₃, and Bi₂O₃ may help lower the melting point of the glass composition. Accordingly, SnO₂, Sb₂O₃, and/or Bi₂O₃ may be included in the glass composition and the resultant colored glass articles to lower the melting point and improve colorant retention. In embodiments in which the colorant package includes Ag, SnO₂ also aids in the reduction of Ag in the glass leading to the formation of silver particles in the glass. While not wishing to be bound by theory, in embodiments where the colorant package includes Au, it is believed that additions of SnO₂ may also aid in the reduction of Au in the glass, leading to the formation of gold particles. In embodiments that include SnO₂ and/or Sb₂O₃, the SnO₂ and/or Sb₂O₃ may also function as a fining agent.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0.01 mol % and less than or equal to 1 mol % SnO₂. In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0.05 mol % and less than or equal to 0.75 mol % SnO₂, greater than or equal to 0.05 mol % and less than or equal to 0.5 mol % SnO₂, or even greater than or equal to 0.1 mol % and less than or equal to 0.25 mol % SnO₂. In embodiments, the concentration of SnO₂ in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol %, greater than or equal to 0.01 mol %, greater than or equal to 0.05 mol %, or even greater than or equal to 0.1 mol %. In embodiments, the concentration of SnO₂ in the glass composition and the resultant colored glass article may be less than or equal to 1 mol %, less than or equal to 0.75 mol %, less than or equal to 0.5 mol %, or even less than or equal to 0.25 mol %. In embodiments, the concentration of SnO₂ in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0 mol % and less than or equal to 0.75 mol %, greater than or equal to 0 mol % and less than or equal to 0.5 mol %, greater than or equal to 0 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.01 mol % and less than or equal to 1 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.05 mol % and less than or equal to 1 mol %, greater than or equal to 0.05 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.05 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.05 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.1 mol % and less than or equal to 1 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.5 mol %, or even greater than or equal to 0.1 mol % and less than or equal to 0.25 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the glass composition and the resultant colored glass article may be substantially free or free of SnO₂.

In embodiments, the concentration of Sb₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol %, greater than or equal to 0.01 mol %, greater than or equal to 0.05 mol %, or even greater than or equal to 0.1 mol %. In embodiments, the concentration of Sb₂O₃ in the glass composition and the resultant colored glass article may be less than or equal to 1 mol %, less than or equal to 0.75 mol %, less than or equal to 0.5 mol %, or even less than or equal to 0.25 mol %. In embodiments, the concentration of Sb₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0 mol % and less than or equal to 0.75 mol %, greater than or equal to 0 mol % and less than or equal to 0.5 mol %, greater than or equal to 0 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.01 mol % and less than or equal to 1 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.05 mol % and less than or equal to 1 mol %, greater than or equal to 0.05 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.05 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.05 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.1 mol % and less than or equal to 1 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.5 mol %, or even greater than or equal to 0.1 mol % and less than or equal to 0.25 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the glass composition and the resultant colored glass article may be substantially free or free of Sb₂O₃.

The glass composition and the resultant colored glass article may comprise Bi₂O₃ as an additional component in the color package for the purposes of achieving a desired color, such as a yellow color. In embodiments, the concentration of Bi₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol %, greater than or equal to 0.01 mol %, greater than or equal to 0.05 mol %, or even greater than or equal to 0.1 mol %. In embodiments, the concentration of Bi₂O₃ in the glass composition and the resultant colored glass article may be less than or equal to 1 mol %, less than or equal to 0.75 mol %, less than or equal to 0.5 mol %, or even less than or equal to 0.25 mol %. In embodiments, the concentration of Bi₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0 mol % and less than or equal to 0.75 mol %, greater than or equal to 0 mol % and less than or equal to 0.5 mol %, greater than or equal to 0 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.01 mol % and less than or equal to 1 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.05 mol % and less than or equal to 1 mol %, greater than or equal to 0.05 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.05 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.05 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.1 mol % and less than or equal to 1 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.5 mol %, or even greater than or equal to 0.1 mol % and less than or equal to 0.25 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the glass composition and the resultant colored glass article may be substantially free or free of Bi₂O₃.

The glass compositions and the resultant colored glass articles described herein may further comprise SO₃ as a fining agent. SO₃ may be utilized as a fining agent without impacting the color or color stability of the colored glass article. In embodiments, the concentration of SO₃ in the glass composition and the resultant colored glass article may be less than or equal to 0.1 mol %, less than or equal to 0.01 mol %, or even less than or equal to 0.001 mol %. In embodiments, the glass composition and the resultant colored glass article may be substantially free or free of SO₃. In embodiments, the glass composition and the resultant glass colored article may comprise greater than or equal to 0 mol % to less than or equal to 1 mol % SO₃.

The glass composition and the resultant colored glass article may comprise WO₃ as an additional component in the color package for the purposes of achieving a desired color, such as a yellow color. In embodiments, the concentration of WO₃ in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 1 mol %, such as greater than or equal to 0 mol % and less than or equal to 0.5 mol %, greater than 0 mol % and less than or equal to 0.1 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.01 mol %, and all sub-ranges formed from any of these endpoints. In embodiments, the glass composition and the resultant colored glass article may be substantially free or free of WO₃.

The glass composition and the resultant colored glass article may comprise Nb₂O₅ as an additional component in the color package for the purposes of achieving a desired color, such as a yellow color. In embodiments, the concentration of Nb₂O₅ in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 1 mol %, such as greater than or equal to 0 mol % and less than or equal to 0.5 mol %, greater than 0 mol % and less than or equal to 0.1 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.01 mol %, and all sub-ranges formed from any of these endpoints. In embodiments, the glass composition and the resultant colored glass article may be substantially free or free of Nb₂O₅.

The glass composition and the colored glass article may comprise MoO₃ as an additional component in the color package for the purposes of achieving a desired color, such as a yellow color. In embodiments, the concentration of MoO₃ in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 1 mol %, such as greater than or equal to 0 mol % and less than or equal to 0.5 mol %, greater than 0 mol % and less than or equal to 0.1 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.01 mol %, and all sub-ranges formed from any of these endpoints. In embodiments, the glass composition and the resultant colored glass article may be substantially free or free of MoO₃.

The glass composition and the colored glass article may comprise La₂O₃ as an additional component in the color package for the purposes of achieving a desired color, such as a yellow color. In embodiments, the concentration of La₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 3 mol %, such as greater than or equal to 0 mol % and less than or equal to 2 mol %, greater than 0 mol % and less than or equal to 1 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.1 mol %, and all sub-ranges formed from any of these endpoints. In embodiments, the glass composition and the colored glass article may be substantially free or free of La₂O₃.

In embodiments, the glass compositions and the resultant colored glass articles described herein may further comprise a reduced concentration or be substantially free or free of P₂O₅. In embodiments where P₂O₅ is included, the P₂O₅ may enhance the ion exchange characteristics of the resultant colored glass article. However, an increased concentration (i.e., greater than 1 mol %) of P₂O₅ may reduce the retention of one or more colorants in the colorant package. While not wishing to be bound by theory, it is believed that P₂O₅ may be more volatile than other glass network formers, such as SiO₂, which may contribute to reduced retention of colorants in the colorant package. In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0.1 mol % and less than or equal to 1 mol % P₂O₅. In embodiments, the concentration of P₂O₅ in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol %, greater than or equal to 0.1 mol %, greater than or equal to 0.25 mol %, or even greater than or equal to 0.5 mol %. In embodiments, the concentration of P₂O₅ in the glass composition and the resultant colored glass article may be less than or equal to 1 mol % or even less than or equal to 0.75 mol %. In embodiments, the concentration of P₂O₅ in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.1 mol % and less than or equal to 1 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.25 mol % and less than or equal to 1 mol %, greater than or equal to 0.25 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.5 mol % and less than or equal to 1 mol %, or even greater than or equal to 0.5 mol % and less than or equal to 0.75 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the glass composition and the resultant colored glass article may be substantially free or free of P₂O₅.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0 mol % and less than or equal to 3 mol % P₂O₅. In embodiments, the concentration of P₂O₅ in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol %, greater than or equal to 0.1 mol %, greater than or equal to 0.25 mol %, or even greater than or equal to 0.5 mol %. In embodiments, the concentration of P₂O₅ in the glass composition and the resultant colored glass article may be less than or equal to 3 mol %, less than or equal to 2, or even less than or equal to 1 mol %. In embodiments, the concentration of P₂O₅ in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 3 mol %, greater than or equal to 0 mol % and less than or equal to 2 mol %, greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0.1 mol % and less than or equal to 3 mol %, greater than or equal to 0.1 mol % and less than or equal to 2 mol %, greater than or equal to 0.1 mol % and less than or equal to 1 mol %, greater than or equal to 0.25 mol % and less than or equal to 3 mol %, greater than or equal to 0.25 mol % and less than or equal to 2 mol %, greater than or equal to 0.25 mol % and less than or equal to 1 mol %, greater than or equal to 0.5 mol % and less than or equal to 3 mol %, greater than or equal to 0.5 mol % and less than or equal to 2 mol %, or even greater than or equal to 0.5 mol % and less than or equal to 1 mol %, or any and all sub-ranges formed from any of these endpoints.

In the embodiments described herein, the glass compositions and resultant colored glass articles further comprise at least one colorant in a colorant package that functions to impart a desired color to the resultant colored glass article. In embodiments, the colorant package may comprise at least one of Au, Ag, Cr₂O₃, transition metal oxides (e.g., CuO, NiO, Co₃O₄, TiO₂, Cr₂O₃), rare earth metal oxides (e.g., CeO₂), and/or combinations thereof as colorants in the colorant package. In embodiments, the colorants in the colorant package may be selected from the group consisting of Au, Ag, Cr₂O₃, transition metal oxides (e.g., CuO, NiO, Co₃O₄, TiO₂, Cr₂O₃), rare earth metal oxides (e.g., CeO₂), and combinations thereof. In embodiments, the glass compositions and resultant colored glass articles may include greater than or equal to 1×10⁻⁶ mol % and less than or equal to 10 mol % of colorant (i.e., the sum of all colorants in the colorant package). In embodiments, the concentration of the colorant package in the glass compositions and resultant colored glass articles may be greater than or equal to 1×10⁻⁶ mol % and less than or equal to 9.5 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 9 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 8.5 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 8 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 7.5 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 7 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 6.5 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 6 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 5.5 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 5 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 4.5 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 4 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 3.5 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 3 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 2.5 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 2 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 1.5 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 1 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 0.5 mol %, greater than or equal to 0.0005 mol % and less than or equal to 10 mol %, greater than or equal to 0.0005 mol % and less than or equal to 9.5 mol %, greater than or equal to 0.0005 mol % and less than or equal to 9 mol %, greater than or equal to 0.0005 mol % and less than or equal to 8.5 mol %, greater than or equal to 0.0005 mol % and less than or equal to 8 mol %, greater than or equal to 0.0005 mol % and less than or equal to 7.5 mol %, greater than or equal to 0.0005 mol % and less than or equal to 7 mol %, greater than or equal to 0.0005 mol % and less than or equal to 6.5 mol %, greater than or equal to 0.0005 mol % and less than or equal to 6 mol %, greater than or equal to 0.0005 mol % and less than or equal to 5.5 mol %, greater than or equal to 0.0005 mol % and less than or equal to 5 mol %, greater than or equal to 0.0005 mol % and less than or equal to 4.5 mol %, greater than or equal to 0.0005 mol % and less than or equal to 4 mol %, greater than or equal to 0.0005 mol % and less than or equal to 3.5 mol %, greater than or equal to 0.0005 mol % and less than or equal to 3 mol %, greater than or equal to 0.0005 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.0005 mol % and less than or equal to 2 mol %, greater than or equal to 0.0005 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.0005 mol % and less than or equal to 1 mol %, greater than or equal to 0.0005 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.001 mol % and less than or equal to 9.5 mol %, greater than or equal to 0.001 mol % and less than or equal to 9 mol %, greater than or equal to 0.001 mol % and less than or equal to 8.5 mol %, greater than or equal to 0.001 mol % and less than or equal to 8 mol %, greater than or equal to 0.001 mol % and less than or equal to 7.5 mol %, greater than or equal to 0.001 mol % and less than or equal to 7 mol %, greater than or equal to 0.001 mol % and less than or equal to 6.5 mol %, greater than or equal to 0.001 mol % and less than or equal to 6 mol %, greater than or equal to 0.001 mol % and less than or equal to 5.5 mol %, greater than or equal to 0.001 mol % and less than or equal to 5 mol %, greater than or equal to 0.001 mol % and less than or equal to 4.5 mol %, greater than or equal to 0.001 mol % and less than or equal to 4 mol %, greater than or equal to 0.001 mol % and less than or equal to 3.5 mol %, greater than or equal to 0.001 mol % and less than or equal to 3 mol %, greater than or equal to 0.001 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.001 mol % and less than or equal to 2 mol %, greater than or equal to 0.001 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.001 mol % and less than or equal to 1 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 9.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 9 mol %, greater than or equal to 0.01 mol % and less than or equal to 8.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 8 mol %, greater than or equal to 0.01 mol % and less than or equal to 7.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 7 mol %, greater than or equal to 0.01 mol % and less than or equal to 6.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 6 mol %, greater than or equal to 0.01 mol % and less than or equal to 5.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 5 mol %, greater than or equal to 0.01 mol % and less than or equal to 4.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 4 mol %, greater than or equal to 0.01 mol % and less than or equal to 3.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 3 mol %, greater than or equal to 0.01 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 2 mol %, greater than or equal to 0.01 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 1 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.5 mol %, or any and all sub-ranges formed from any of these endpoints.

Colorant: Transition Metal Oxides and/or Rare Earth Oxides

In embodiments, the colorant package in the glass compositions and the resultant colored glass articles may include colorants that comprise or consist of transition metal oxides, rare earth oxides, or combinations thereof, to achieve a desired color. In embodiments, transition metal oxides and/or rare earth oxides may be included in the glass compositions as the sole colorant or in combination with other colorants. In embodiments, colorants based on transition metal oxides and/or rare earth oxides may include NiO, Co₃O₄, Cr₂O₃, CuO, CeO₂, TiO₂ and/or combinations thereof. In embodiments, colorants based on transition metal oxides and/or rare earth oxides may further include oxides of V, Mn, Fe, Cu, Zr, Nb, Mo, Tc, Ru, Rh, Pd, Cd, Hf, Ta, W, Re, Os, Ir, Pt, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, and Er.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0.001 mol %, such as greater than or equal to 0.001 mol % and less than or equal to 10 mol %, NiO+Co₃O₄+Cr₂O₃+CuO+CeO₂+TiO₂. In embodiments, the concentration of NiO+Co₃O₄+Cr₂O₃+CuO+CeO₂+TiO₂ in the glass composition and the resultant colored glass article may be greater than or equal to 0.001 mol % and less than or equal to 5 mol %, greater than or equal to 0.001 mol % and less than or equal to 4 mol %, greater than or equal to 0.001 mol % and less than or equal to 3 mol %, greater than or equal to 0.001 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.001 mol % and less than or equal to 2 mol %, greater than or equal to 0.001 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 5 mol %, greater than or equal to 0.01 mol % and less than or equal to 4 mol %, greater than or equal to 0.01 mol % and less than or equal to 3 mol %, greater than or equal to 0.01 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 2 mol %, greater than or equal to 0.01 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.02 mol % and less than or equal to 5 mol %, greater than or equal to 0.02 mol % and less than or equal to 4 mol %, greater than or equal to 0.02 mol % and less than or equal to 3 mol %, greater than or equal to 0.02 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.02 mol % and less than or equal to 2 mol %, greater than or equal to 0.02 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 5 mol %, greater than or equal to 0.1 mol % and less than or equal to 4 mol %, greater than or equal to 0.1 mol % and less than or equal to 3 mol %, greater than or equal to 0.1 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 2 mol %, greater than or equal to 0.1 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 5 mol %, greater than or equal to 0.5 mol % and less than or equal to 4 mol %, greater than or equal to 0.5 mol % and less than or equal to 3 mol %, greater than or equal to 0.5 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 2 mol %, greater than or equal to 0.5 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.7 mol % and less than or equal to 5 mol %, greater than or equal to 0.7 mol % and less than or equal to 4 mol %, greater than or equal to 0.7 mol % and less than or equal to 3 mol %, greater than or equal to 0.7 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.7 mol % and less than or equal to 2 mol %, greater than or equal to 0.7 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.9 mol % and less than or equal to 5 mol %, greater than or equal to 0.9 mol % and less than or equal to 4 mol %, greater than or equal to 0.9 mol % and less than or equal to 3 mol %, greater than or equal to 0.9 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.9 mol % and less than or equal to 2 mol %, greater than or equal to 0.9 mol % and less than or equal to 1.5 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the glass composition and resultant glass article may comprise 0 mol % of one or more of NiO, Co₃O₄, Cr₂O₃, CuO, CeO₂, and/or TiO₂.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0.001 mol %, such as greater than or equal to 0.001 mol % and less than or equal to 3 mol %, NiO+Co₃O₄+Cr₂O₃+CuO. In embodiments, the concentration of NiO+Co₃O₄+Cr₂O₃+CuO in the glass composition and the resultant colored glass article may be greater than or equal to 0.001 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.001 mol % and less than or equal to 2 mol %, greater than or equal to 0.001 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.001 mol % and less than or equal to 1 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.4 mol %, greater than or equal to 0.01 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 2 mol %, greater than or equal to 0.01 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 1 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.4 mol %, greater than or equal to 0.02 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.02 mol % and less than or equal to 2 mol %, greater than or equal to 0.02 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.02 mol % and less than or equal to 1 mol %, greater than or equal to 0.02 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.02 mol % and less than or equal to 0.4 mol %, greater than or equal to 0.1 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 2 mol %, greater than or equal to 0.1 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 1 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.4 mol %, greater than or equal to 0.2 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.2 mol % and less than or equal to 2 mol %, greater than or equal to 0.2 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.2 mol % and less than or equal to 1 mol %, greater than or equal to 0.2 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.2 mol % and less than or equal to 0.4 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the glass composition and resultant glass article may comprise 0 mol % of one or more of NiO, Co₃O₄, Cr₂O₃, and/or CuO.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0 mol % TiO₂, such as greater than or equal to 0 mol % and less than or equal to 2 mol % or even greater than or equal to 0.01 mol % and less than or equal to 2 mol %, TiO₂. In embodiments, the concentration of TiO₂ in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 2 mol %, greater than or equal to 0 mol % and less than or equal to 1.5 mol %, greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0 mol % and less than or equal to 0.75 mol %, greater than or equal to 0 mol % and less than or equal to 0.5 mol %, greater than or equal to 0 mol % and less than or equal to 0.4 mol %, greater than or equal to 0.01 mol % and less than or equal to 2 mol %, greater than or equal to 0.01 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 1 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.4 mol %, greater than or equal to 0.1 mol % and less than or equal to 2 mol %, greater than or equal to 0.1 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 1 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.4 mol %, greater than or equal to 0.2 mol % and less than or equal to 2 mol %, greater than or equal to 0.2 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.2 mol % and less than or equal to 1 mol %, greater than or equal to 0.2 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.2 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.2 mol % and less than or equal to 0.4 mol %, greater than or equal to 0.3 mol % and less than or equal to 2 mol %, greater than or equal to 0.3 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.3 mol % and less than or equal to 1 mol %, greater than or equal to 0.3 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.3 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.3 mol % and less than or equal to 0.4 mol %, or any and all sub-ranges formed from any of these endpoints.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0.1 mol %, such as greater than or equal to 0.1 mol % and less than or equal to 2 mol %, CeO₂. In embodiments, the concentration of CeO₂ in the glass composition and the resultant colored glass article may be greater than or equal to 0.1 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 1 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.4 mol %, greater than or equal to 0.2 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.2 mol % and less than or equal to 1 mol %, greater than or equal to 0.2 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.2 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.2 mol % and less than or equal to 0.4 mol %, greater than or equal to 0.3 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.3 mol % and less than or equal to 1 mol %, greater than or equal to 0.3 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.3 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.3 mol % and less than or equal to 0.4 mol %, or any and all sub-ranges formed from any of these endpoints. In embodiments, the glass composition and the resultant colored glass article may comprise greater than 0 mol % and less than or equal to 2 mol % CeO₂.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0 mol %, such as greater than or equal to 0.01 mol % and less than or equal to 0.05 mol %, NiO. In embodiments, the concentration of NiO in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 0.05 mol %, greater than or equal to 0 mol % and less than or equal to 0.04 mol %, greater than or equal to 0 mol % and less than or equal to 0.035 mol %, greater than or equal to 0 mol % and less than or equal to 0.03 mol %, greater than or equal to 0 mol % and less than or equal to 0.025 mol %, greater than or equal to 0 mol % and less than or equal to 0.02 mol %, greater than or equal to 0 mol % and less than or equal to 0.015 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.05 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.04 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.035 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.03 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.025 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.02 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.015 mol %, greater than or equal to 0.015 mol % and less than or equal to 0.05 mol %, greater than or equal to 0.015 mol % and less than or equal to 0.04 mol %, greater than or equal to 0.015 mol % and less than or equal to 0.035 mol %, greater than or equal to 0.015 mol % and less than or equal to 0.03 mol %, greater than or equal to 0.015 mol % and less than or equal to 0.025 mol %, or even greater than or equal to 0.015 mol % and less than or equal to 0.02 mol %, and all sub-ranges formed from any of these endpoints.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0 mol %, such as greater than or equal to 0.1 mol % and less than or equal to 0.5 mol %, CuO. In embodiments, the concentration of CuO in the glass composition and the resultant colored glass article may be greater than or equal to 0.1 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.4 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.35 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.3 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.2 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.15 mol %, greater than or equal to 0.15 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.15 mol % and less than or equal to 0.4 mol %, greater than or equal to 0.15 mol % and less than or equal to 0.35 mol %, greater than or equal to 0.15 mol % and less than or equal to 0.3 mol %, greater than or equal to 0.15 mol % and less than or equal to 0.25 mol %, or even greater than or equal to 0.15 mol % and less than or equal to 0.2 mol %, and all sub-ranges formed from any of these endpoints.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0 mol %, such as greater than or equal to 0.0001 mol % and less than or equal to 0.01 mol %, Co₃O₄. In embodiments, the concentration of Co₃O₄ in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 0.01 mol %, greater than or equal to 0 mol % and less than or equal to 0.0095 mol %, greater than or equal to 0 mol % and less than or equal to 0.009 mol %, greater than or equal to 0 mol % and less than or equal to 0.0085 mol %, greater than or equal to 0 mol % and less than or equal to 0.0075 mol %, greater than or equal to 0 mol % and less than or equal to 0.007 mol %, greater than or equal to 0 mol % and less than or equal to 0.0065 mol %, greater than or equal to 0 mol % and less than or equal to 0.006 mol %, greater than or equal to 0 mol % and less than or equal to 0.0055 mol %, greater than or equal to 0 mol % and less than or equal to 0.005 mol %, greater than or equal to 0 mol % and less than or equal to 0.0045 mol %, greater than or equal to 0 mol % and less than or equal to 0.004 mol %, greater than or equal to 0 mol % and less than or equal to 0.0035 mol %, greater than or equal to 0 mol % and less than or equal to 0.003 mol %, greater than or equal to 0 mol % and less than or equal to 0.0025 mol %, greater than or equal to 0 mol % and less than or equal to 0.002 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.01 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.0095 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.009 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.0085 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.0075 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.007 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.0065 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.006 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.0055 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.005 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.0045 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.004 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.0035 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.003 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.0025 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.002 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.01 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.0095 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.009 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.0085 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.0075 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.007 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.0065 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.006 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.0055 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.005 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.0045 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.004 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.0035 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.003 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.0025 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.002 mol %, and all sub-ranges formed from any of these endpoints.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0 mol %, such as greater than or equal to 0.01 mol % and less than or equal to 0.05 mol %, Cr₂O₃. In embodiments, the concentration of Cr₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 0.05 mol %, greater than or equal to 0 mol % and less than or equal to 0.04 mol %, greater than or equal to 0 mol % and less than or equal to 0.035 mol %, greater than or equal to 0 mol % and less than or equal to 0.03 mol %, greater than or equal to 0 mol % and less than or equal to 0.025 mol %, greater than or equal to 0 mol % and less than or equal to 0.02 mol %, greater than or equal to 0 mol % and less than or equal to 0.015 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.05 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.04 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.035 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.03 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.025 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.02 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.015 mol %, greater than or equal to 0.015 mol % and less than or equal to 0.05 mol %, greater than or equal to 0.015 mol % and less than or equal to 0.04 mol %, greater than or equal to 0.015 mol % and less than or equal to 0.035 mol %, greater than or equal to 0.015 mol % and less than or equal to 0.03 mol %, greater than or equal to 0.015 mol % and less than or equal to 0.025 mol %, or even greater than or equal to 0.015 mol % and less than or equal to 0.02 mol %, and all sub-ranges formed from any of these endpoints.

In embodiments, the glass composition and the resultant colored glass article may comprise at least one of: greater than or equal to 0.001 mol % NiO+Co₃O₄+Cr₂O₃+CuO, such as greater than or equal to 0.001 mol % and less than or equal to 3 mol % NiO+Co₃O₄+Cr₂O₃+CuO (or any of the ranges of NiO+Co₃O₄+Cr₂O₃+CuO described herein); greater than or equal to 0.1 mol % CeO₂, such as greater than or equal to 0.1 mol % and less than or equal to 1.5 mol % CeO₂ (or any of the ranges of CeO₂ described herein); and greater than or equal to 0.1 mol % TiO₂, such as greater than or equal to 0.1 mol % and less than or equal to 2 mol % TiO₂ (or any of the ranges of TiO₂ described herein).

The glass composition and the resultant colored glass article may include sufficient TiO₂+CeO₂ to provide a desired yellow color. In embodiments, the concentration of TiO₂+CeO₂ in the glass composition and the resultant colored glass article may be greater than or equal to 0.2 mol %, greater than or equal to 0.3 mol %, greater than or equal to 0.4 mol %, greater than or equal to 0.5 mol %, greater than or equal to 0.6 mol %, greater than or equal to 0.7 mol %, greater than or equal to 0.8 mol %, or more. In embodiments, the concentration of TiO₂+CeO₂ in the glass composition and the resultant colored glass article may be less than or equal to 3 mol %, less than or equal to 2.5 mol %, less than or equal to 2 mol %, less than or equal to 1.5 mol %, less than or equal to 1 mol %, or less. In embodiments, the concentration of TiO₂+CeO₂ in the glass composition and the resultant colored glass article may be greater than or equal to 0.2 mol % and less than or equal to 3 mol %, such as greater than or equal to 0.3 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.4 mol % and less than or equal to 2 mol %, greater than or equal to 0.5 mol % and less than or equal to 2.0 mol %, greater than or equal to 0.5 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.6 mol % and less than or equal to 1 mol %, greater than or equal to 0.7 mol % and less than or equal to 0.9 mol %, greater than or equal to 0.8 mol % and less than or equal to 1.5 mol %, or any and all sub-ranges formed from any of these endpoints.

In embodiments, the glass composition and the resultant colored glass article may include at least one of Er₂O₃ and Nd₂O₃ as colorants for the purposes of providing the desired color. The inclusion of Er₂O₃ and Nd₂O₃ in the glass compositions may allow for colors to be achieved that are not possible with other transition metal colorants and do not require a post-forming heat treatment to achieve the desired colors, unlike some glasses that utilize Au, Ag, or Cu as colorants. The Er₂O₃ and Nd₂O₃ may also be combined with other colorants to tune the color of the colored glass article.

In embodiments, the glass compositions and the resultant colored glass articles may include Er₂O₃ in an amount greater than or equal to 0 mol % to less than or equal to 4 mol %, such as greater than 0 mol % to less than or equal to 4 mol %, or greater than or equal to 0.1 mol % to less than or equal to 2 mol %. In embodiments, the glass compositions and the resultant colored glass articles may include Er₂O₃ in an amount greater than or equal to 0 mol %, greater than 0 mol %, greater than or equal to 0.1 mol %, greater than or equal to 0.2 mol %, greater than or equal to 0.5 mol %, greater than or equal to 1 mol %, or more. In embodiments, the glass compositions and the resultant colored glass articles include Er₂O₃ in an amount less than or equal to 4 mol %, less than or equal to 3 mol %, less than or equal to 2 mol %, less than or equal to 1 mol %, less than or equal to 0.5 mol %, or less. In embodiments, the glass compositions and the resultant colored glass articles include Er₂O₃ in an amount greater than or equal to 0 mol % to less than or equal to 4 mol %, greater than 0 mol % to less than or equal to 3.5 mol %, greater than or equal to 0.1 mol % to less than or equal to 3 mol %, greater than or equal to 0.2 mol % to less than or equal to 2.5 mol %, greater than or equal to 0.3 mol % to less than or equal to 2 mol %, greater than or equal to 0.4 mol % to less than or equal to 1.9 mol %, greater than or equal to 0.5 mol % to less than or equal to 1.8 mol %, greater than or equal to 0.6 mol % to less than or equal to 1.7 mol %, greater than or equal to 0.7 mol % to less than or equal to 1.6 mol %, greater than or equal to 0.8 mol % to less than or equal to 1.5 mol %, greater than or equal to 0.9 mol % to less than or equal to 1.4 mol %, greater than or equal to 1.0 mol % to less than or equal to 1.3 mol %, greater than or equal to 1.1 mol % to less than or equal to 1.2 mol %, or any and all sub-ranges formed from the foregoing endpoints. In embodiments, the glass compositions and the resultant colored glass articles may be substantially free or free of Er₂O₃.

In embodiments, the glass compositions and the resultant colored glass articles may include Nd₂O₃ in an amount greater than or equal to 0 mol % to less than or equal to 4 mol %, such as greater than 0 mol % to less than or equal to 4 mol %, or greater than or equal to 0.1 mol % to less than or equal to 3 mol %. In embodiments, the glass compositions and the resultant colored glass articles may include Nd₂O₃ in an amount greater than or equal to 0 mol %, greater than 0 mol %, greater than or equal to 0.1 mol %, greater than or equal to 0.2 mol %, greater than or equal to 0.5 mol %, greater than or equal to 1 mol %, or more. In embodiments, the glass compositions and the resultant colored glass articles may include Nd₂O₃ in an amount less than or equal to 4 mol %, less than or equal to 3 mol %, less than or equal to 2 mol %, less than or equal to 1 mol %, less than or equal to 0.5 mol %, or less. In embodiments, the glass compositions and the resultant colored glass articles include Nd₂O₃ in an amount greater than or equal to 0 mol % to less than or equal to 4 mol %, greater than 0 mol % to less than or equal to 3.5 mol %, greater than or equal to 0.1 mol % to less than or equal to 3 mol %, greater than or equal to 0.2 mol % to less than or equal to 2.5 mol %, greater than or equal to 0.3 mol % to less than or equal to 2 mol %, greater than or equal to 0.4 mol % to less than or equal to 1.9 mol %, greater than or equal to 0.5 mol % to less than or equal to 1.8 mol %, greater than or equal to 0.6 mol % to less than or equal to 1.7 mol %, greater than or equal to 0.7 mol % to less than or equal to 1.6 mol %, greater than or equal to 0.8 mol % to less than or equal to 1.5 mol %, greater than or equal to 0.9 mol % to less than or equal to 1.4 mol %, greater than or equal to 1.0 mol % to less than or equal to 1.3 mol %, greater than or equal to 1.1 mol % to less than or equal to 1.2 mol %, or any and all sub-ranges formed from the foregoing endpoints. In embodiments, the glass compositions and the resultant colored glass articles may be substantially free or free of Nd₂O₃.

Colorant: Gold

In embodiments, the colorant package in the glass compositions and the resultant colored glass articles may comprise or consist of Au as a colorant to achieve a desired color. In embodiments, Au may be included in the glass compositions as the sole colorant or in combination with other colorants. As described herein, in embodiments, the glass compositions and the resultant colored glass articles may be formulated to improve the retention of Au, thereby expanding the color gamut achievable in the resultant colored glass articles.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than 0.0005 mol % and less than or equal to 1 mol % Au. In embodiments, the glass composition and the resultant colored glass article may comprise greater than 0.001 mol % and less than or equal to 0.5 mol % Au. In embodiments, the concentration of Au in the glass composition and the resultant colored glass article may be greater than or equal to 0.0005 mol %, greater than or equal to 0.001 mol %, greater than or equal to 0.002 mol % Au, greater than or equal to 0.005 mol %, or even greater than or equal to 0.01 mol %. In embodiments, the concentration of Au in the glass composition and the resultant colored glass article may be less than or equal to 1 mol %, less than or equal to 0.75 mol %, less than or equal to 0.5 mol %, less than or equal to 0.25 mol %, less than or equal to 0.1 mol %, or even less than or equal to 0.05 mol %. In embodiments, the concentration of Au in the glass composition and the resultant colored glass article may be greater than or equal to 0.0005 mol % and less than or equal to 1 mol %, greater than or equal to 0.0005 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.0005 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.0005 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.0005 mol % and less than or equal to 0.1 mol %, greater than or equal to 0.0005 mol % and less than or equal to 0.05 mol %, greater than or equal to 0.001 mol % and less than or equal to 1 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.1 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.05 mol %, greater than or equal to 0.002 mol % and less than or equal to 1 mol %, greater than or equal to 0.002 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.002 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.002 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.002 mol % and less than or equal to 0.1 mol %, greater than or equal to 0.002 mol % and less than or equal to 0.05 mol %, greater than or equal to 0.005 mol % and less than or equal to 1 mol %, greater than or equal to 0.005 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.005 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.005 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.005 mol % and less than or equal to 0.1 mol %, greater than or equal to 0.005 mol % and less than or equal to 0.05 mol %, greater than or equal to 0.01 mol % and less than or equal to 1 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.1 mol %, or even greater than or equal to 0.01 mol % and less than or equal to 0.05 mol %, or any and all sub-ranges formed from any of these endpoints.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 1×10⁻⁶ mol % and less than or equal to 1 mol % Au. In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 1×10⁻⁶ mol % and less than or equal to 0.01 mol % Au. In embodiments, the concentration of Au in the glass composition and the resultant colored glass article may be greater than or equal to 1×10⁻⁶ mol %, greater than or equal to 1×10⁻⁵ mol %, greater than or equal to 0.0001 mol %, greater than or equal to 0.0005 mol %, or even greater than or equal to 0.001 mol %. In embodiments, the concentration of Au in the glass composition and the resultant colored glass article may be less than or equal to 1 mol %, less than or equal to 0.75 mol %, less than or equal to 0.5 mol %, less than or equal to 0.25 mol %, less than or equal to 0.1 mol %, less than or equal to 0.05 mol %, or even less than or equal to 0.01. In embodiments, the concentration of Au in the glass composition and the resultant colored glass article may be greater than or equal to 1×10⁻⁶ mol % and less than or equal to 0.75 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 0.5 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 0.25 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 0.1 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 0.05 mol %, greater than or equal to 1×10⁻⁶ mol % and less than or equal to 0.01 mol %, greater than or equal to 1×10⁻⁵ mol % and less than or equal to 1 mol %, greater than or equal to 1×10⁻⁵ mol % and less than or equal to 0.75 mol %, greater than or equal to 1×10⁻⁵ mol % and less than or equal to 0.5 mol %, greater than or equal to 1×10⁻⁵ mol % and less than or equal to 0.25 mol %, greater than or equal to 1×10⁻⁵ mol % and less than or equal to 0.1 mol %, greater than or equal to 1×10⁻⁵ mol % and less than or equal to 0.05 mol %, greater than or equal to 1×10⁻⁵ mol % and less than or equal to 0.01 mol %, greater than or equal to 0.0001 mol % and less than or equal to 1 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.1 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.05 mol %, greater than or equal to 0.0001 mol % and less than or equal to 0.01 mol %, greater than or equal to 0.0005 mol % and less than or equal to 1 mol %, greater than or equal to 0.0005 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.0005 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.0005 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.0005 mol % and less than or equal to 0.1 mol %, greater than or equal to 0.0005 mol % and less than or equal to 0.05 mol %, greater than or equal to 0.0005 mol % and less than or equal to 0.01 mol %, greater than or equal to 0.001 mol % and less than or equal to 1 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.1 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.05 mol %, or even greater than or equal to 0.001 mol % and less than or equal to 0.01 mol %, or any and all sub-ranges formed from any of these endpoints.

A different color gamut may be achieved by including secondary colorants in addition to Au. For example, in embodiments, the glass composition and resultant colored glass article may comprise greater than or equal to 0 mol % and less than or equal to 1 mol % of a cation “M”, wherein “M” is at least one of F, Cl, Br, Ti, V, Cr, Mn, Fe, Co, Ni, Cu, Se, Nb, Mo, Ru, Rh, Pd, Ag, Cd, In, Te, W, Ir, Pt, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, and Er.

Colorant: Cr₂O₃

In embodiments, the colorant package used in the glass compositions and the resultant colored glass articles described herein may comprise or consist of Cr₂O₃ as a colorant to achieve a desired color. In embodiments, Cr₂O₃ may be included in the glass compositions as the sole colorant or in combination with other colorants. For example, in embodiments where Cr₂O₃ is utilized as a colorant, other transition metal oxides may be included in the glass composition to modify the color imparted to the glass, including, for example and without limitation, CuO, NiO, and/or Co₃O₄. As described herein, in embodiments, the glass compositions and the resultant colored glass articles may be formulated to improve the solubility of Cr₂O₃, thereby expanding the color gamut achievable in the resultant colored glass articles.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0 mol % and less than or equal to 2 mol % Cr₂O₃. In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0.001 mol % and less than or equal to 1.5 mol % Cr₂O₃. In embodiments, the concentration of Cr₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol %, greater than or equal to 0.001 mol %, greater than or equal to 0.005 mol %, greater than or equal to 0.01 mol %, or even greater than or equal to 0.05 mol %. In embodiments, the concentration of Cr₂O₃ in the glass composition and the resultant colored glass article may be less than or equal to 2 mol %, less than or equal to 1.5 mol %, less than or equal to 1 mol %, less than or equal to 0.5 mol %, or even less than or equal to 0.1 mol %. In embodiments, the concentration of Cr₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 2 mol %, greater than or equal to 0 mol % and less than or equal to 1.5 mol %, greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0 mol % and less than or equal to 0.5 mol %, greater than or equal to 0 mol % and less than or equal to 0.1 mol %, greater than or equal to 0.001 mol % and less than or equal to 2 mol %, greater than or equal to 0.001 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.001 mol % and less than or equal to 1 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.1 mol %, greater than or equal to 0.005 mol % and less than or equal to 2 mol %, greater than or equal to 0.005 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.005 mol % and less than or equal to 1 mol %, greater than or equal to 0.005 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.005 mol % and less than or equal to 0.1 mol %, greater than or equal to 0.01 mol % and less than or equal to 2 mol %, greater than or equal to 0.01 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 1 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.1 mol %, greater than or equal to 0.05 mol % and less than or equal to 2 mol %, greater than or equal to 0.05 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.05 mol % and less than or equal to 1 mol %, greater than or equal to 0.05 mol % and less than or equal to 0.5 mol %, or even greater than or equal to 0.05 mol % and less than or equal to 0.1 mol %, or any and all sub-ranges formed from any of these endpoints.

In embodiments where the colorant package includes Cr₂O₃ as a colorant, the glass compositions and the resultant colored glass articles are per-alkali (i.e., R₂O (mol %)+R′O (mol %)—Al₂O₃ (mol %) is greater than or equal to 0.5 mol %) to increase the solubility of Cr₂O₃ and avoid Cr-spinel crystal formation. However, when the glass composition has an excessive amount of alkali after charge balancing Al₂O₃, the alkali may form non-bridging oxygen around SiO₂, which degrades fracture toughness. Accordingly, in embodiments, R₂O+R′O—Al₂O₃ in the glass composition and the resultant colored glass article may be limited (e.g., less than or equal to 6 mol %) to prevent a reduction in fracture toughness.

In embodiments, R₂O+R′O—Al₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 0.5 mol % and less than or equal to 6 mol %. In embodiments, R₂O+R′O—Al₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 1 mol % and less than or equal to 5.5 mol %. In embodiments, R₂O+R′O—Al₂O₃ in the glass composition and the colored resultant glass article may be greater than or equal to 0.5 mol %, greater than or equal to 1 mol %, greater than or equal to 1.5 mol %, or even greater than or equal to 2 mol %. In embodiments, R₂O+R′O—Al₂O₃ in the glass composition and the resultant colored glass article may be less than or equal to 6 mol %, less than or equal to 5.5 mol %, less than or equal to 5 mol %, less than or equal to 4.5 mol %, less than or equal to 4 mol %, less than or equal to 3.5 mol %, or even less than or equal to 3 mol %. In embodiments, R₂O+R′O—Al₂O₃ in the glass composition and the resultant colored glass article may be greater than or equal to 0.5 mol % and less than or equal to 6 mol %, greater than or equal to 0.5 mol % and less than or equal to 5.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 5 mol %, greater than or equal to 0.5 mol % and less than or equal to 4.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 4 mol %, greater than or equal to 0.5 mol % and less than or equal to 3.5 mol %, greater than or equal to 0.5 mol % and less than or equal to 3 mol %, greater than or equal to 1 mol % and less than or equal to 6 mol %, greater than or equal to 1 mol % and less than or equal to 5.5 mol %, greater than or equal to 1 mol % and less than or equal to 5 mol %, greater than or equal to 1 mol % and less than or equal to 4.5 mol %, greater than or equal to 1 mol % and less than or equal to 4 mol %, greater than or equal to 1 mol % and less than or equal to 3.5 mol %, greater than or equal to 1 mol % and less than or equal to 3 mol %, greater than or equal to 1.5 mol % and less than or equal to 6 mol %, greater than or equal to 1.5 mol % and less than or equal to 5.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 5 mol %, greater than or equal to 1.5 mol % and less than or equal to 4.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 4 mol %, greater than or equal to 1.5 mol % and less than or equal to 3.5 mol %, greater than or equal to 1.5 mol % and less than or equal to 3 mol %, greater than or equal to 2 mol % and less than or equal to 6 mol %, greater than or equal to 2 mol % and less than or equal to 5.5 mol %, greater than or equal to 2 mol % and less than or equal to 5 mol %, greater than or equal to 2 mol % and less than or equal to 4.5 mol %, greater than or equal to 2 mol % and less than or equal to 4 mol %, greater than or equal to 2 mol % and less than or equal to 3.5 mol %, or even greater than or equal to 2 mol % and less than or equal to 3 mol %, or any and all sub-ranges formed from any of these endpoints.

In embodiments where the colorant package comprises Cr₂O₃ as a colorant, the glass compositions and the resultant colored glass articles may satisfy at least one of the following conditions and achieve the desired color: (1) less than or equal to 17.5 mol % Al₂O₃ and/or R₂O+R′O—Al₂O₃ greater than or equal to 0.5 mol %; (2) Al₂O₃+MgO+ZnO less than or equal to 22 mol %; and (3) MgO+ZnO less than or equal to 4.5 mol %.

In embodiments where the colorant comprises Cr₂O₃, different color gamuts may be achieved by including other colorants in addition to Cr₂O₃. For example, in embodiments, the glass composition and resultant colored glass article may comprise NiO, Co₃O₄, CuO, or combinations thereof in addition to Cr₂O₃.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0 mol % and less than or equal to 4 mol % NiO as a colorant in addition to Cr₂O₃. In embodiments, the concentration of NiO in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol %, greater than or equal to 0.01 mol %, or even greater than or equal to 0.05 mol %. In embodiments, the concentration of NiO in the glass composition and the resultant colored glass article may be less than or equal to 4 mol %, less than or equal to 3 mol %, less than or equal to 2 mol %, less than or equal to 1 mol %, less than or equal to 0.5 mol %, less than or equal to 0.25 mol %, or even less than or equal to 0.1 mol %. In embodiments, the concentration of NiO in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 4 mol %, greater than or equal to 0 mol % and less than or equal to 3 mol %, greater than or equal to 0 mol % and less than or equal to 2 mol %, greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0 mol % and less than or equal to 0.5 mol %, greater than or equal to 0 mol % and less than or equal to 0.25 mol %, greater than or equal to 0 mol % and less than or equal to 0.1 mol %, greater than or equal to 0.01 mol % and less than or equal to 4 mol %, greater than or equal to 0.01 mol % and less than or equal to 3 mol %, greater than or equal to 0.01 mol % and less than or equal to 2 mol %, greater than or equal to 0.01 mol % and less than or equal to 1 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.1 mol %, greater than or equal to 0.05 mol % and less than or equal to 4 mol %, greater than or equal to 0.05 mol % and less than or equal to 3 mol %, greater than or equal to 0.05 mol % and less than or equal to 2 mol %, greater than or equal to 0.05 mol % and less than or equal to 1 mol %, greater than or equal to 0.05 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.05 mol % and less than or equal to 0.25 mol %, or even greater than or equal to 0.05 mol % and less than or equal to 0.1 mol %, or any and all sub-ranges formed between any of these endpoints.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0 mol % and less than or equal to 2 mol % Co₃O₄ as a colorant in addition to Cr₂O₃. In embodiments, the concentration of Co₃O₄ in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol %, greater than or equal to 0.001 mol %, greater than or equal to 0.005 mol %, or even greater than or equal to 0.01 mol %. In embodiments, the concentration of Co₃O₄ in the glass composition and the resultant colored glass article may be less than or equal to 2 mol %, less than or equal to 1.5 mol %, less than or equal to 1 mol %, less than or equal to 0.5 mol %, less than or equal to 0.1 mol %, or even less than or equal to 0.05 mol %. In embodiments, the concentration of Co₃O₄ in the glass composition and the resultant colored glass article may greater than or equal to 0 mol % and less than or equal to 2 mol %, greater than or equal to 0 mol % and less than or equal to 1.5 mol %, greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0 mol % and less than or equal to 0.5 mol %, greater than or equal to 0 mol % and less than or equal to 0.1 mol %, greater than or equal to 0 mol % and less than or equal to 0.05 mol %, greater than or equal to 0.001 mol % and less than or equal to 2 mol %, greater than or equal to 0.001 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.001 mol % and less than or equal to 1 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.1 mol %, greater than or equal to 0.001 mol % and less than or equal to 0.05 mol %, greater than or equal to 0.005 mol % and less than or equal to 2 mol %, greater than or equal to 0.005 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.005 mol % and less than or equal to 1 mol %, greater than or equal to 0.005 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.005 mol % and less than or equal to 0.1 mol %, greater than or equal to 0.005 mol % and less than or equal to 0.05 mol %, greater than or equal to 0.01 mol % and less than or equal to 2 mol %, greater than or equal to 0.01 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 1 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.1 mol %, or even greater than or equal to 0.01 mol % and less than or equal to 0.05 mol %, or any and all sub-ranges formed from any of these endpoints.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or 0 mol % and less than or equal to 5 mol % CuO as a colorant in addition to Cr₂O₃. In embodiments, the concentration of CuO in the glass composition and the resultant colored glass article may be greater than or equal 0 mol %, greater than or equal to 0.05 mol %, greater than or equal to 0.1 mol %, greater than or equal to 0.5 mol %, or even greater than or equal to 1 mol %. In embodiments, the concentration of CuO in the glass composition and the resultant colored glass article may be less than or equal to 5 mol %, less than or equal to 4 mol %, less than or equal to 3 mol %, or even less than or equal to 2 mol %. In embodiments, the concentration of CuO in the glass composition and the resultant colored glass article may be greater than or equal to 0 mol % and less than or equal to 5 mol %, greater than or equal to 0 mol % and less than or equal to 4 mol %, greater than or equal to 0 mol % and less than or equal to 3 mol %, greater than or equal to 0 mol % and less than or equal to 2 mol, greater than or equal to 0.05 mol % and less than or equal to 5 mol %, greater than or equal to 0.05 mol % and less than or equal to 4 mol %, greater than or equal to 0.05 mol % and less than or equal to 3 mol %, greater than or equal to 0.05 mol % and less than or equal to 2 mol %, greater than or equal to 0.1 mol % and less than or equal to 5 mol %, greater than or equal to 0.1 mol % and less than or equal to 4 mol %, greater than or equal to 0.1 mol % and less than or equal to 3 mol %, greater than or equal to 0.1 mol % and less than or equal to 2 mol %, greater than or equal to 0.5 mol % and less than or equal to 5 mol %, greater than or equal to 0.5 mol % and less than or equal to 4 mol %, greater than or equal to 0.5 mol % and less than or equal to 3 mol %, greater than or equal to 0.5 mol % and less than or equal to 2 mol %, greater than or equal to 1 mol % and less than or equal to 5 mol %, greater than or equal to 1 mol % and less than or equal to 4 mol %, greater than or equal to 1 mol % and less than or equal to 3 mol %, or even greater than or equal to 1 mol % and less than or equal to 2 mol %, or any and all sub-ranges formed from any of these endpoints.

Colorant: Silver

In embodiments, the colorant package used in the glass compositions and the resultant colored glass articles may comprise or consist of Ag as a colorant to achieve a desired color. As described herein, in embodiments, the glass compositions and the resultant colored glass articles may be formulated to improve the retention of Ag, thereby expanding the color gamut achievable in the resultant colored glass articles. In embodiments, Ag may be included in the glass compositions as the sole colorant or in combination with other colorants. In embodiments where Ag is utilized as a colorant in the glass composition, the color is created by the presence of anisotropic silver particles in the colored glass article that are formed from the reduction of silver ions in the glass composition.

Accordingly, in embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0.01 mol % and less than or equal to 5 mol % Ag. In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 0.05 mol % and less than or equal to 2.5 mol % Ag, greater than or equal to 0.1 mol % and less than or equal to 1 mol % Ag, greater than or equal to 0.1 mol % and less than or equal to 0.75 mol % Ag, greater than or equal to 0.1 mol % and less than or equal to 0.5 mol % Ag, or greater than or equal to 0.1 mol % and less than or equal to 0.25 mol % Ag. In embodiments, the concentration of Ag in the glass composition and the resultant colored glass article may be greater than or equal to 0.01 mol %, greater than or equal to 0.05 mol %, or greater than or equal to 0.1 mol %. In embodiments, the concentration of Ag in the glass composition and the resultant colored glass article may be less than or equal to 5 mol %, less than or equal to 2.5 mol %, less than or equal to 1 mol %, less than or equal to 0.75 mol %, less than or equal to 0.5 mol %, or less than or equal to 0.25 mol %. In embodiments, the concentration of Ag in the glass composition and the resultant colored glass article may be greater than or equal to 0.01 mol % and less than or equal to 5 mol %, greater than or equal to 0.01 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 1 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.01 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.05 mol % and less than or equal to 5 mol %, greater than or equal to 0.05 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.05 mol % and less than or equal to 1 mol %, greater than or equal to 0.05 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.05 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.05 mol % and less than or equal to 0.25 mol %, greater than or equal to 0.1 mol % and less than or equal to 5 mol %, greater than or equal to 0.1 mol % and less than or equal to 2.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 1 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.75 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 0.25 mol %, or any and all sub-ranges formed from any of these endpoints.

Conventionally, halide-free colored glass articles that comprise silver in as-formed condition (i.e., colored glass articles that have not been subjected to mechanical stretching) produce only yellow, orange, and red colors upon a suitable heat treatment applied to the glass article in as-formed condition. These colors are generated by the formation of isotropic (i.e., nominally spherical) silver particles in the conventional, halide-free colored glass article. These isotropic silver particles support a single localized surface plasmon resonance. Isotropic silver particles are the most energetically favorable to form because they have the lowest surface area to volume ratio and, as a result, they are the most common geometry observed in colored glass articles that comprise silver.

In contrast, colored glass articles that comprise anisotropic silver particles can produce a much broader range of colors, such as pink, purple, blue, green, brown and black. As used herein, anisotropic silver particles refer to silver particles having an aspect ratio greater than 1, where the aspect ratio is the ratio of longest dimension of the particle to the shortest dimension of the particle (e.g., a ratio of the length of the particle to the width of the particle is greater than 1). This is in contrast to an isotropic silver particle in which the aspect ratio is 1. The broader color gamut produced in glasses having anisotropic silver particles is because anisotropic silver particles support two distinct plasmonic modes: a higher energy transverse mode, and a lower energy longitudinal mode. These two distinct plasmonic modes can be observed via absorption spectra of the colored glass articles, which typically have at least two distinct peaks when anisotropic silver particles are present in the glass. By varying the aspect ratio of anisotropic particles, the resonant absorption of these two plasmonic modes can be tuned and, as a result, the color shifted.

Conventionally, the formation of anisotropic metallic silver particles in glass can be either induced by elongating spherical particles of silver through shear forces (e.g., by stretching the colored glass article via re-draw) using mechanical stretching processes. The mechanical stretching process results in a glass article having silver particles that are generally aligned in parallel with one another along the stretching direction (i.e., the glass is polarized).

A conventional alternative to mechanical stretching processes for creating anisotropic metallic particles in a glass article is the incorporation of halides (e.g., F, Cl, and Br) in the glass composition. In halide-containing colored glass articles, anisotropic silver particles are formed by templating the particles on elongated and/or pyramidal-shaped halide crystals. However, the inclusion of halides in the glass composition may be undesirable.

In contrast, the colored glass articles comprising Ag as a colorant described herein may generate a broad range of colors, such as yellow, orange, red, green, pink, purple, brown, and black without the inclusion of halides in the glass composition or the use of mechanical stretching processes. Without being bound by any particular theory, it is believed that anisotropic silver particles may form in the colored glass articles of the present disclosure due to a mechanism similar to the template growth caused by the inclusion of halides in the glass composition. However, instead of templating on a halide-containing crystal or mechanically stretching isotropic silver particles, it has been unexpectedly found that anisotropic silver crystals may form on nano-sized crystals of spodumene, lithium silicate, and/or beta quartz during heat treatment of the glass article in its as formed condition. Additionally and/or alternatively, it is believed that anisotropic silver particles may precipitate at the interfaces between phase separated regions of the colored glass article and/or regions that are only partially crystalized. Further, these crystals and/or phase separated regions may form a nucleation site for the growth of anisotropic silver particles.

Accordingly, in embodiments, the glass composition and the resultant colored glass article including silver as a colorant may comprise less than 100 parts per million (ppm) of halides. For example, the glass compositions and the resultant colored glass articles comprising Ag as a colorant may comprise less than 100 ppm halides, such as less than 50 ppm halides, less than 25 ppm halides, less than 10 ppm halides, or even 0 ppm halides.

As noted previously, colored glass articles comprising Ag produced using mechanical stretching processes generally include anisotropic silver particles similar to those of the colored glass article of the present application. However, it should be noted that these mechanical stretching processes also result in the anisotropic silver particles being ordered and aligned (e.g., the longer dimensions of each anisotropic silver particles are facing in the same direction, such as in the direction of mechanical stretching). Put more simply, the colored glass articles produced using mechanical stretching processes are polarized due to the alignment of the anisotropic silver particles in the glass as a result of mechanical stretching.

In contrast, in the embodiments described herein, the colored glass articles comprising Ag as a colorant, which are not subjected to mechanical stretching processes, are non-polarized. In embodiments, the anisotropic silver particles of the colored glass article are not aligned (e.g., the longer dimensions of two or more anisotropic silver particles are facing in different directions) and, instead, the anisotropic silver particles are randomly aligned in the glass.

The term “length,” as used herein, refers to the longest dimension of the anisotropic silver particles. In embodiments, the anisotropic silver particles in the colored glass articles described herein have a length greater than or equal to 10 nm, greater than or equal to 12 nm, greater than or equal to 14 nm, greater than or equal to 16 nm, greater than or equal to 18 nm, greater than or equal to 10 nm, greater than or equal to 22 nm, greater than or equal to 24 nm, greater than or equal to 26 nm, greater than or equal to 28 nm, greater than or equal to 30 nm, greater than or equal to 32 nm, greater than or equal to 34 nm, greater than or equal to 36 nm, or even greater than or equal to 38 nm. The length of the anisotropic silver particles may be measured using image analysis on electron micrographs obtained from samples of the colored glass articles using software such as ImageJ software. To obtain the length and width of the anisotropic silver particles, a calibration is set by measuring the scale bar on the electron micrograph, converting each pixel to the appropriate unit length. The image is then converted into a grayscale image. A software measuring tool is then used to measure the number of pixels from one end to the other of each particle as well as the number of pixels across the greatest width of the particle. In embodiments an automated script is run to measure the length and aspect ratios of multiple particles automatically. In embodiments, the anisotropic silver particles in the colored glass articles described herein have a length less than or equal to 40 nm, less than or equal to 38 nm, less than or equal to 36 nm, less than or equal to 34 nm, less than or equal to 32 nm, less than or equal to 30 nm, less than or equal to 28 nm, less than or equal to 26 nm, less than or equal to 24 nm, less than or equal to 22 nm, or even less than or equal to 20 nm. In embodiments, the anisotropic silver particles in the colored glass articles described herein have a length greater than or equal to 10 nm and less than or equal to 40 nm, greater than or equal to 12 nm and less than or equal to 36 nm, greater than or equal to 14 nm and less than or equal to 34 nm, greater than or equal to 14 nm and less than or equal to 32 nm, greater than or equal to 14 nm and less than or equal to 28 nm, greater than or equal to 14 nm and less than or equal to 26 nm, greater than or equal to 16 nm and less than or equal to 26 nm, greater than or equal to 16 nm and less than or equal to 24 nm, greater than or equal to 16 nm and less than or equal to 22 nm, greater than or equal to 16 nm and less than or equal to 20 nm, or any and all sub-ranges formed from any of these endpoints.

The term “width,” as used herein, refers to the dimension of the anisotropic particles in a direction perpendicular to the longest dimension of the anisotropic particles (i.e., the dimension in a direction perpendicular to the length). In embodiments, the anisotropic silver particles in the colored glass articles described herein have a width greater than or equal to 6 nm, greater than or equal to 8 nm, greater than or equal to 10 nm, greater than or equal to 12 nm, or even greater than or equal to 14 nm. In embodiments, the anisotropic silver particles in the colored glass articles described herein have a width less than or equal to 20 nm, less than or equal to 18 nm, less than or equal to 16 nm, less than or equal to 12 nm, or even less than or equal to 10 nm. In embodiments, the anisotropic silver particles in the colored glass articles described herein have a width greater than or equal to 6 nm and less than or equal to 20 nm, greater than or equal to 6 nm and less than or equal to 18 nm, greater than or equal to 6 nm and less than or equal to 16 nm, greater than or equal to 8 nm and less than or equal to 20 nm, greater than or equal to 8 nm and less than or equal to 18 nm, greater than or equal to 8 nm and less than or equal to 16 nm, greater than or equal to 10 nm and less than or equal to 20 nm, greater than or equal to 10 nm and less than or equal to 18 nm, greater than or equal to 10 nm and less than or equal to 16 nm, greater than or equal to 10 nm and less than or equal to 14 nm, or any and all sub-ranges formed from any of these endpoints.

In embodiments, the anisotropic silver particles in the colored glass articles described herein have an aspect ratio (i.e., the ratio of the length to the width of the anisotropic silver nanoparticles) greater than 1, greater than or equal to 1.5, greater than or equal to 2, or even greater than or equal to 2.5. In embodiments, the anisotropic silver particles in the colored glass articles described herein have an aspect ratio less than or equal to 3, less than or equal to 2.5, less than or equal to 2, or even less than or equal to 1.5. In embodiments, the anisotropic silver particles in the colored glass articles described herein have an aspect ratio greater than 1 and less than or equal to 3, greater than 1 and less than or equal to 2.5, greater than 1 and less than or equal to 2, greater than 1 and less than or equal to 1.5, greater than or equal to 1.5 and less than or equal to 3, greater than or equal to 1.5 and less than or equal to 2.5, greater than or equal to 1.5 and less than or equal to 2, greater than or equal to 2 and less than or equal to 3, greater than or equal to 2 and less than or equal to 2.5, or any and all sub-ranges formed from any of these endpoints.

The glass compositions and the resultant colored glass articles that include Ag as a colorant may further comprise one or more rare-earth oxides, such as CeO₂, Nd₂O₃, Er₂O₃. Rare-earth oxides may be added to provide additional visible light absorbance to the glass (in addition to that imparted by the silver) to further alter the color of the glass. Rare-earth oxides may also be added to increase the Young's modulus and/or the annealing point of the resultant glass.

In embodiments, the glass compositions and the resultant colored glass articles that include Ag as a colorant may further comprise greater than or equal to 0 mol % and less than or equal to 4 mol % of CeO₂, In embodiments, the glass compositions and the resultant colored glass articles that include Ag as a colorant may further comprise greater than or equal to 0 mol % and less than or equal to 3 mol % CeO₂, greater than or equal to 0 mol % and less than or equal to 1 mol % of CeO₂, greater than or equal to 0.05 mol % and less than or equal to 1 mol % of CeO₂, or greater than or equal to 0.05 mol % and less than or equal to 0.5 mol % of CeO₂. In embodiments, the concentration of CeO₂ in the glass compositions and the resultant colored glass articles that comprise Ag as a colorant may be greater than or equal to 0 mol %, or even greater than or equal to 0.05 mol %. In embodiments, the concentration of CeO₂ in the glass compositions and the resultant colored glass articles that comprise Ag as a colorant may be less than or equal to 4 mol %, less than or equal to 3 mol %, less than or equal to 2 mol %, less than or equal to 1 mol % or less than or equal to 0.5 mol %. In embodiments, the concentration of CeO₂ in the glass compositions and the resultant colored glass articles that include Ag as a colorant may be greater than or equal to 0 mol % and less than or equal to 4 mol %, greater than or equal to 0 mol % and less than or equal to 3 mol %, greater than or equal to 0 mol % and less than or equal to 2 mol %, greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.05 mol % and less than or equal to 4 mol %, greater than or equal to 0.05 mol % and less than or equal to 3 mol %, greater than or equal to 0.05 mol % and less than or equal to 2 mol %, greater than or equal to 0.05 mol % and less than or equal to 1 mol %, or even greater than or equal to 0.05 mol % and less than or equal to 0.5 mol %, or any and all sub-ranges formed from any of these endpoints.

In embodiments, the glass compositions and the resultant colored glass articles that include Ag as a colorant may comprise greater than or equal to 0 mol % and less than or equal to 4 mol % of Nd₂O₃, In embodiments, the glass compositions and the resultant colored glass articles that include Ag as a colorant may comprise greater than or equal to 0 mol % and less than or equal to 3 mol % Nd₂O₃, greater than or equal to 0 mol % and less than or equal to 1 mol % of Nd₂O₃, greater than or equal to 0 mol % and less than or equal to 1 mol % of Nd₂O₃, greater than or equal to 0.1 mol % and less than or equal to 1 mol % of Nd₂O₃, greater than or equal to 0.1 mol % and less than or equal to 1.5 mol % of Nd₂O₃, or greater than or equal to 0.1 mol % and less than or equal to 0.5 mol % of Nd₂O₃. In embodiments, the concentration of Nd₂O₃ in the glass compositions and the resultant colored glass articles that include Ag as a colorant may be greater than or equal to 0 mol %, or even greater than or equal to 0.1 mol %. In embodiments, the concentration of Nd₂O₃ in the glass compositions and the resultant colored glass articles that include Ag as a colorant may be less than or equal to 4 mol %, less than or equal to 3 mol %, less than or equal to 2 mol %, less than or equal to 1 mol % or less than or equal to 0.5 mol %. In embodiments, the concentration of one or more of Nd₂O₃ in the glass compositions and the resultant colored glass articles that include Ag as a colorant may be greater than or equal to 0 mol % and less than or equal to 4 mol %, greater than or equal to 0 mol % and less than or equal to 3 mol %, greater than or equal to 0 mol % and less than or equal to 2 mol %, greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0 mol % and less than or equal to 1.5 mol %, greater than or equal to 0 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 4 mol %, greater than or equal to 0.1 mol % and less than or equal to 3 mol %, greater than or equal to 0.1 mol % and less than or equal to 2 mol %, greater than or equal to 0.1 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 1 mol %, or even greater than or equal to 0.1 mol % and less than or equal to 0.5 mol %, or any and all sub-ranges formed from any of these endpoints.

In embodiments, the glass compositions and the resultant colored glass articles that include Ag as a colorant may comprise greater than or equal to 0 mol % and less than or equal to 4 mol % of Er₂O₃. In embodiments, the glass compositions and the resultant colored glass articles that include Ag as a colorant may comprise greater than or equal to 0 mol % and less than or equal to 3 mol % Er₂O₃, greater than or equal to 0 mol % and less than or equal to 1.5 mol % of Er₂O₃, greater than or equal to 0 mol % and less than or equal to 1 mol % of Er₂O₃, greater than or equal to 0.1 mol % and less than or equal to 1.5 mol % of Er₂O₃, greater than or equal to 0.1 mol % and less than or equal to 1 mol % of Er₂O₃, or greater than or equal to 0.1 mol % and less than or equal to 0.5 mol % of Er₂O₃. In embodiments, the concentration of Er₂O₃ in the glass compositions and the resultant colored glass articles that include Ag as a colorant may be greater than or equal to 0 mol %, or even greater than or equal to 0.1 mol %. In embodiments, the concentration of Er₂O₃ in the glass compositions and the resultant colored glass articles that include Ag as a colorant may be less than or equal to 4 mol %, less than or equal to 3 mol %, less than or equal to 2 mol %, less than or equal to 1 mol % or less than or equal to 0.5 mol %. In embodiments, the concentration of one or more of Er₂O₃ in the glass compositions and the resultant colored glass articles that include Ag as a colorant may be greater than or equal to 0 mol % and less than or equal to 4 mol %, greater than or equal to 0 mol % and less than or equal to 3 mol %, greater than or equal to 0 mol % and less than or equal to 2 mol %, greater than or equal to 0 mol % and less than or equal to 1.5 mol %, greater than or equal to 0 mol % and less than or equal to 1 mol %, greater than or equal to 0 mol % and less than or equal to 0.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 4 mol %, greater than or equal to 0.1 mol % and less than or equal to 3 mol %, greater than or equal to 0.1 mol % and less than or equal to 2 mol %, greater than or equal to 0.1 mol % and less than or equal to 1.5 mol %, greater than or equal to 0.1 mol % and less than or equal to 1 mol %, or even greater than or equal to 0.1 mol % and less than or equal to 0.5 mol %, or any and all sub-ranges formed from any of these endpoints.

In embodiments, the glass compositions and the resultant colored glass articles described herein may further include tramp materials such as TiO₂, MnO, MoO₃, WO₃, Y₂O₃, CdO, As₂O₃, sulfur-based compounds, such as sulfates, halogens, or combinations thereof. In embodiments, the glass composition and the resultant colored glass article may be substantially free or free of tramp materials such as TiO₂, MnO, MoO₃, WO₃, Y₂O₃, CdO, As₂O₃, sulfur-based compounds, such as sulfates, halogens, or combinations thereof.

In embodiments described herein, decreasing the melting point of the glass composition may help improve colorant retention because the glass compositions may be melted at relatively lower temperatures and colorant evaporation may be reduced. Accordingly, the glass compositions and the resultant colored glass articles described herein may optionally include MgO and/or ZnO, which help lower the melting point of the glass composition. B₂O₃, Li₂O, and Na₂O also decrease the melting point of the glass composition. As described herein, other components may be added to the glass composition to lower the melting point thereof, such as SnO₂, Sb₂O₃, and Bi₂O₃. In embodiments, the glass composition may have a melting point less than or equal to 1550° C. In embodiments, the glass composition may have a melting point greater than or equal to 1300° C., greater than or equal to 1325° C., greater than or equal to 1350° C., greater than or equal to 1375° C., or even greater than or 1400° C. In embodiments, the glass composition may have a melting point less than or equal to 1550° C., less than or equal to 1525° C., less than or equal 1500° C., less than or equal to 1475° C., or even less than or equal to 1450° C. In embodiments, the melting point of the glass composition may be greater than or equal to 1300° C. and less than or equal to 1550° C., greater than or equal to 1300° C. and less than or equal to 1525° C., greater than or equal to 1300° C. and less than or equal to 1500° C., greater than or equal to 1300° C. and less than or equal to 1475° C., greater than or equal to 1300° C. and less than or equal to 1450° C., greater than or equal to 1325° C. and less than or equal to 1550° C., greater than or equal to 1325° C. and less than or equal to 1525° C., greater than or equal to 1325° C. and less than or equal to 1500° C., greater than or equal to 1325° C. and less than or equal to 1475° C., greater than or equal to 1325° C. and less than or equal to 1450° C., greater than or equal to 1350° C. and less than or equal to 1550° C., greater than or equal to 1350° C. and less than or equal to 1525° C., greater than or equal to 1350° C. and less than or equal to 1500° C., greater than or equal to 1350° C. and less than or equal to 1475° C., greater than or equal to 1350° C. and less than or equal to 1450° C., greater than or equal to 1375° C. and less than or equal to 1550° C., greater than or equal to 1375° C. and less than or equal to 1525° C., greater than or equal to 1375° C. and less than or equal to 1500° C., greater than or equal to 1375° C. and less than or equal to 1475° C., greater than or equal to 1375° C. and less than or equal to 1450° C., greater than or equal to 1400° C. and less than or equal to 1550° C., greater than or equal to 1400° C. and less than or equal to 1525° C., greater than or equal to 1400° C. and less than or equal to 1500° C., greater than or equal to 1400° C. and less than or equal to 1475° C., or even greater than or equal to 1400° C. and less than or equal to 1450° C., or any and all sub-ranges formed from any of these endpoints.

In embodiments, a liquidus temperature of the glass composition may be greater than or equal to 1000° C., greater than or equal to 1050° C., or even greater than or equal to 1100° C. In embodiments, a liquidus temperature of the precursor glass composition may be less than or equal to 1400° C., less than or equal to 1350° C. or even less than or equal to 1300° C. In embodiments, a liquidus temperature of the glass composition may be greater than or equal to 1000° C. and less than or equal to 1400° C., greater than or equal to 1000° C. and less than or equal to 1350° C., greater than or equal to 1000° C. and less than or equal to 1300° C., greater than or equal to 1050° C. and less than or equal to 1400° C., greater than or equal to 1050° C. and less than or equal to 1350° C., greater than or equal to 1000° C. and less than or equal to 1300° C., greater than or equal to 1100° C. and less than or equal to 1400° C., greater than or equal to 1100° C. and less than or equal to 1350° C., or even greater than or equal to 1100° C. and less than or equal to 1300° C., or any and all sub-ranges formed from any of these endpoints.

In embodiments, the viscosity of the glass composition may be adjusted to prevent devitrification of the glass composition and formation of colorant particles, such as Au particles, during melting and forming. Formation of colorant particles during melting and forming may limit the color gamut that may be achieved by heat treatment. In embodiments, to achieve the desired viscosity and thereby prevent formation of colorant particles before melting, the glass compositions and the resultant glass articles described herein may satisfy the relationship 5.72*Al₂O₃ (mol %)−21.4*ZnO (mol %)−2.5*P₂O₅ (mol %)−35*Li₂O (mol %)−16.6*B₂O₃ (mol %)−20.5*MgO (mol %)−23.3*Na₂O (mol %)−27.9*SrO (mol %)−18.5*K₂O (mol %)−26.3*CaO (mol %) is greater than −609 mol %. While not wishing to be bound by theory, it is believe that this relationship may also hold true for glass compositions containing colorants other than Au, such as when the colorant comprises Ag (which may also form colorant particles in the glass). In embodiments, the glass compositions and the resultant glass articles described herein may satisfy the relationship 5.72*Al₂O₃ (mol %)−21.4*ZnO (mol %)−2.5*P₂O₅ (mol %)−35*Li₂O (mol %)−16.6*B₂O₃ (mol %)−20.5*MgO (mol %)−23.3*Na₂O (mol %)−27.9*SrO (mol %)−18.5*K₂O (mol %)−26.3*CaO (mol %) is greater than −609 mol %, greater than or equal to −575 mol %, greater than or equal to −550 mol %, or even greater than or equal to −525 mol %. In embodiments, the glass compositions and the resultant glass articles described herein may satisfy the relationship 5.72*Al₂O₃ (mol %)−21.4*ZnO (mol %)−2.5*P₂O₅ (mol %)−35*Li₂O (mol %)−16.6*B₂O₃ (mol %)−20.5*MgO (mol %)−23.3*Na₂O (mol %)−27.9*SrO (mol %)−18.5*K₂O (mol %)−26.3*CaO (mol %) is less than or equal to −400 mol %, less than or equal to −425 mol %, or even less than or equal to −450 mol %. In embodiments, the glass compositions and the resultant glass articles described herein may satisfy the relationship 5.72*Al₂O₃ (mol %)−21.4*ZnO (mol %)−2.5*P₂O₅ (mol %)−35*Li₂O (mol %)−16.6*B₂O₃ (mol %)−20.5*MgO (mol %)−23.3*Na₂O (mol %)−27.9*SrO (mol %)−18.5*K₂O (mol %)−26.3*CaO (mol %) is greater than −609 mol % and less than or equal to −400 mol %, greater than −609 mol % and less than or equal to −425 mol %, greater than −609 mol % and less than or equal to −450 mol %, greater than or equal to −575 mol % and less than or equal to −400 mol %, greater than or equal to −575 mol % and less than or equal to −425 mol %, greater than or equal to −575 mol % and less than or equal to −450 mol %, greater than or equal to −550 mol % and less than or equal to −400 mol %, greater than or equal to −550 mol % and less than or equal to −425 mol %, greater than or equal to −550 mol % and less than or equal to −450 mol %, greater than or equal to −525 mol % and less than or equal to −400 mol %, greater than or equal to −525 mol % and less than or equal to −425 mol %, or even greater than or equal to −525 mol % and less than or equal to −450 mol %, or any and all sub-ranges formed from any of these endpoints.

In embodiments, the colored glass articles may be formed by first melting a glass composition comprising a combination of constituent glass components as described herein and one or more colorants in a colorant package. Thereafter, the molten glass is formed into a precursor glass article using conventional forming techniques and, thereafter, cooled. The precursor glass article may take on any number of forms including, without limitation, sheets, tubes, rods, containers (e.g., vials, bottles, jars, etc.) or the like. In embodiments, the precursor glass article may be exposed to a heat treatment to produce color in the glass. For example and without limitation, the heat treatment may induce the formation of colorant particles in the glass which, in turn, cause the glass to become colored. In some embodiments, the glass may appear clear (i.e., colorless) prior to heat treatment. Examples of colorant particles may include, for example and without limitation, Au particles (such as when the colorant package in the glass comprises Au), randomly oriented, anisotropic silver particles (such as when the colorant package comprises Ag) and/or the like, thereby forming a colored glass article. The time and/or temperature of the heat treatment may be specifically selected to produce a colored glass article having a desired color. Without wishing to be bound by theory, it is believed that a desired color is a result of the morphology of the particles precipitated in the glass which, in turn, is dependent on the time and/or temperature of the heat treatment. Accordingly, it should be understood that a single glass composition can be used to form colored glass articles having different colors based on the time and/or temperature of the applied heat treatment in addition to the composition of the colorant package included in the glass.

Specifically, different color coordinates within the color gamut may be achieved by altering the heat treatment cycle of the glass composition used to produce the resultant colored glass articles. The heat treatment cycle is characterized by the temperature of the environment (i.e., the oven) and the duration of the cycle (i.e., the time exposed to the heated environment). As used herein, the phrase “temperature of the heat treatment cycle” refers to the temperature of the environment (i.e., the oven). In embodiments, glass articles formed from the glass compositions described herein are heat treated in an isothermal oven to produce the resultant colored glass articles.

In embodiments, the temperature of the heat treatment cycle is greater than or equal to 500° C., greater than or equal to 550° C., greater than or equal to 575° C., greater than or equal to 600° C., greater than or equal to 625° C., or even greater than or equal to 650° C. In embodiments, the temperature of the heat treatment cycle is less than or equal to 800° C., less than or equal to 775° C., less than or equal to 750° C., less than or equal to 725° C., or even less than or equal to 700° C. In embodiments, the temperature of the heat treatment cycle is greater than or equal to 500° C. and less than or equal to 800° C., greater than or equal to 500° C. and less than or equal to 775° C., greater than or equal to 500° C. and less than or equal to 750° C., greater than or equal to 500° C. and less than or equal to 725° C., greater than or equal to 550° C. and less than or equal to 700° C., greater than or equal to 550° C. and less than or equal to 800° C., greater than or equal to 550° C. and less than or equal to 775° C., greater than or equal to 550° C. and less than or equal to 750° C., greater than or equal to 550° C. and less than or equal to 725° C., greater than or equal to 550° C. and less than or equal to 700° C., greater than or equal to 575° C. and less than or equal to 800° C., greater than or equal to 575° C. and less than or equal to 775° C., greater than or equal to 575° C. and less than or equal to 750° C., greater than or equal to 575° C. and less than or equal to 725° C., greater than or equal to 575° C. and less than or equal to 700° C., greater than or equal to 600° C. and less than or equal to 800° C., greater than or equal to 600° C. and less than or equal to 775° C., greater than or equal to 600° C. and less than or equal to 750° C., greater than or equal to 600° C. and less than or equal to 725° C., greater than or equal to 600° C. and less than or equal to 700° C., greater than or equal to 625° C. and less than or equal to 800° C., greater than or equal to 625° C. and less than or equal to 775° C., greater than or equal to 625° C. and less than or equal to 750° C., greater than or equal to 625° C. and less than or equal to 725° C., greater than or equal to 625° C. and less than or equal to 700° C., greater than or equal to 650° C. and less than or equal to 800° C., greater than or equal to 650° C. and less than or equal to 775° C., greater than or equal to 650° C. and less than or equal to 750° C., greater than or equal to 650° C. and less than or equal to 725° C., or even greater than or equal to 650° C. and less than or equal to 700° C., or any and all sub-ranges formed from any of these endpoints.

In embodiments, the duration of the heat treatment cycle is greater than or equal to 0.15 hour, greater than or equal to 0.25 hour, greater than or equal to 0.5 hour, greater than or equal 1 hour, or even greater than or equal to 2 hours. In embodiments, the durations of the heat treatment cycle is less than or equal to 24 hours, less than or equal to 16 hours, less than or equal to 8 hours, less than or equal to 6 hours, less than or equal to 4 hours, or even less than or equal to 3 hours. In embodiments, the duration of the heat treatment cycle is greater than or equal to 0.25 hour and less than or equal to 24 hours, greater than or equal to 0.25 hour and less than or equal to 16 hours, greater than or equal to 0.25 hour and less than or equal to 8 hours, greater than or equal to 0.25 hour and less than or equal to 4 hours, greater than or equal to 0.5 hour and less than or equal to 24 hours, greater than or equal to 0.5 hour and less than or equal to 16 hours, greater than or equal to 0.5 hour and less than or equal to 8 hours, greater than or equal to 0.5 hour and less than or equal to 4 hours, greater than or equal to 1 hour and less than or equal to 24 hours, greater than or equal to 1 hour and less than or equal to 16 hours, greater than or equal to 1 hour and less than or equal to 8 hours, greater than or equal to 1 hour and less than or equal to 4 hours, greater than or equal to 2 hours and less than or equal to 24 hours, greater than or equal to 2 hours and less than or equal to 16 hours, greater than or equal to 2 hours and less than or equal to 8 hours, or even greater than or equal to 2 hours and less than or equal to 4 hours, or any and all sub-ranges formed from any of these endpoints.

In embodiments, the heat treatment may comprise ramping up to a heat treatment temperature at a heating rate and cooling down from the heat treatment temperature at a cooling rate. In embodiments, the selected heating rate and cooling rate may effect the color coordinates of the resultant colored glass articles.

In embodiments, the heating rate of the heat treatment may be greater than or equal to 2° C./min or even greater than or equal to 3° C./min. In embodiments, the heating rate of the heat treatment may be less than equal to 10° C./min, less than or equal to 7° C./min, or even less than or equal to 5° C./min. In embodiments, the heating rate of the heat treatment may be greater than or equal to 2° C./min and less than or equal to 10° C./min, greater than or equal to 2° C./min and less than or equal to 7° C./min, greater than or equal to 2° C./min and less than or equal to 5° C./min, greater than or equal to 3° C./min and less than or equal to 10° C./min, greater than or equal to 3° C./min and less than or equal to 7° C./min, or even greater than or equal to 3° C./min and less than or equal to 5° C./min, or any and all sub-ranges formed from any of these endpoints.

In embodiments, the cooling rate of the heat treatment may be greater than or equal to 1° C./min or even greater than or equal to 2° C./min. In embodiments, the cooling rate of the heat treatment may be less than or equal to 10° C./min, less than or equal to 8° C./min, less than or equal to 6° C./min, or even less than or equal to 4° C./min. In embodiments, the cooling rate of the heat treatment may be greater than or equal to 1° C./min and less than or equal to 10° C./min, greater than or equal to 1° C./min and less than or equal to 8° C./min, greater than or equal to 1° C./min and less than or equal to 6° C./min, greater than or equal to 1° C./min and less than or equal to 4° C./min, greater than or equal to 2° C./min and less than or equal to 10° C./min, greater than or equal to 2° C./min and less than or equal to 8° C./min, greater than or equal to 2° C./min and less than or equal to 6° C./min, or even greater than or equal to 2° C./min and less than or equal to 4° C./min, or any and all sub-ranges formed from any of these endpoints.

For example and without limitation, in embodiments in which the glass composition comprises Ag, colored glass articles having an orange color may be formed by heat treating the precursor glass article at a heat treatment temperature from about 590° C. to about 610° C. for a heat treatment time from about 45 minutes to about 180 minutes.

For example and without limitation, in embodiments in which the glass composition comprises Ag, colored glass articles having a red color may be formed by heat treating the precursor glass article at a heat treatment temperature from about 600° C. to about 615° C. for a heat treatment time from about 180 minutes to about 300 minutes.

For example and without limitation, in embodiments in which the glass composition comprises Ag, colored glass articles having a green color may be formed by heat treating the precursor glass article at a heat treatment temperature from about 620° C. to about 640° C. for a heat treatment time from about 20 minutes to about 40 minutes.

For example and without limitation, in embodiments in which the glass composition comprises Ag, colored glass articles having a brown color may be formed by heat treating the precursor glass article at a heat treatment temperature from about 640° C. to about 660° C. for a heat treatment time from about 30 minutes to about 90 minutes.

For example and without limitation, in embodiments in which the glass composition comprises Ag, colored glass articles having a purple color may be formed by heat treating the precursor glass article at a heat treatment temperature from about 625° C. to about 650° C. for a heat treatment time from about 30 minutes to about 90 minutes.

While some embodiments of the glasses described herein require a heat treatment to impart color to the glass, it is noted that other embodiments of glasses described herein do not require a heat treatment to impart color to the glass. For example, some glasses containing transition metal oxides and/or rare earth oxides may not require a heat treatment to impart color to the glass. As such, it should be understood that the heat treatment is optional.

Following heat treatment (if required), the glasses described herein are colored and, as such, are referred to as colored glass articles. In embodiments, the colored glass articles are predominantly glass (i.e., predominantly non-crystalline), but may include particles (such as colorant particles) that have crystalline morphology. As such, the colored glass articles may include at least one crystalline phase. In embodiments, the crystalline phase may be, for example and without limitation, an Au crystalline phase and/or a Ag crystalline phase. However, it should be understood that other crystalline phases are possible and may be present as an alternative to an Au crystalline phase and/or an Ag crystalline phase or instead of an Au crystalline phase and/or an Ag crystalline phase. In embodiments, the crystallinity of the colored glass article is less than or equal to 10 wt. %, less than or equal to 9 wt. %, less than or equal to 8 wt. %, less than or equal to 7 wt. %, less than or equal to 6 wt. %, less than or equal to 5 wt. %, less than or equal to 4 wt. %, less than or equal to 3 wt. %, less than or equal to 2 wt. %, or even less than or equal to 1 wt. % by weight of the glass article.

In embodiments, the colored glass articles may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 20 and less than or equal to 96.5. In embodiments, the colored glass articles may have a transmittance color coordinate in the CIELAB color space of absolute value of a* (i.e., |a*|) greater than or equal to 0.3. In embodiments, the colored glass articles may have a transmittance color coordinate in the CIELAB color space of absolute value of b* (i.e., |b*|) greater than or equal to 0.5. In embodiments, the colored glass articles may have a transmittance color coordinate in the CIELAB color space of: L*greater than or equal to 20 and less than or equal to 96.5; absolute value of a* (i.e., |a*|) greater than or equal to 0.3; and absolute value of b* (i.e., |b*|) greater than or equal to 0.5. In these embodiments, L*may be greater than or equal to 25, greater than or equal to 30, greater than or equal to 35, greater than or equal to 40, greater than or equal to 45, greater than or equal to 50, or even greater than or equal to 55. As noted herein, unless otherwise specified, the transmittance color coordinates in the CIELAB color space are specified for article thicknesses of 0.4 to 5 mm (inclusive of endpoints) under F2 illumination and a 100 standard observer angle.

Without wishing to be bound by theory, it is believed that glasses having CIELAB color coordinates within the range of L*greater than or equal to 20 and less than or equal to 96.5 are transparent to wavelengths of visible light (i.e., wavelengths of light from 380 nm to 750 nm, inclusive of endpoints) rather than opaque. However, as the value of L*decreases, the color of the colored glass articles becomes more saturated and the glasses become more opaque (i.e., less transparent). As the value for L*increases, the color of the colored glass articles becomes less saturated and, when the L*value exceeds 96.5, the colored glass article may appear colorless.

In embodiments, the colored glass articles may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −5 and less than or equal to 25 (exclusive of a* greater than −0.3 and less than 0.3), and b* greater than or equal to −20 and less than or equal to 5 (exclusive of b* greater than −0.5 and less than 0.5).

In embodiments, the colored glass articles may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −10 and less than or equal to 25 (exclusive of a* greater than −0.3 and less than 0.3), and b* greater than or equal to −20 and less than or equal to 5 (exclusive of b* greater than −0.5 and less than 0.5).

In embodiments, the colored glass articles may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −18 and less than or equal to 0.3, and b* greater than or equal to 0.5 and less than or equal to 82.

In embodiments, the colored glass articles may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −18 and less than or equal to 18 (exclusive of a* greater than −0.3 and less than 0.3), and b* greater than or equal to 0.5 and less than or equal to 82.

In embodiments, the colored glass articles may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −20 and less than or equal to 60 (exclusive of a* greater than −0.3 and less than 0.3), and b* greater than or equal to −90 and less than or equal to 85 (exclusive of b* greater than −0.5 and less than 0.5).

In embodiments, the colored glass articles may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −35 and less than or equal to −0.3, and b* greater than or equal to 0.5 and less than or equal to 82.

In embodiments, the colored glass articles may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −35 and less than or equal to 20 (exclusive of a* greater than −0.3 and less than 0.3), and b* greater than or equal to 0.5 and less than or equal to 75.

In embodiments, the colored glass articles may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −15 and less than or equal to 65 (exclusive of a* greater than −0.3 and less than 0.3), and b* greater than or equal to −90 and less than or equal to 80 (exclusive of b* greater than −0.5 and less than 0.5).

In embodiments, the colored glass articles may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −35 and less than or equal to 60 (exclusive of a* greater than −0.3 and less than 0.3), and b* greater than or equal to −90 and less than or equal to 80 (exclusive of b* greater than −0.5 and less than 0.5).

In embodiments, the colored glass articles may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −35 and less than or equal to 60 (exclusive of a* greater than −0.3 and less than 0.3), and b* greater than or equal to −90 and less than or equal to 80 (exclusive of b* greater than −0.5 and less than 0.5).

In embodiments, the colored glass articles may have a transmitted color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −11.12 and less than or equal to 60 (exclusive of a* greater than −0.3 and less than 0.3), and b* greater than or equal to −20 and less than or equal to 120 (exclusive of b* greater than −0.5 and less than 0.5).

In embodiments, the transmitted color coordinates of the CIELAB color space may be described in terms of a range of L*values and a region of the a* (horizontal axis or x-axis) and b* (vertical axis or y-axis) color space. The region of the a* vs. b* color space may be defined by the intersection of a plurality of lines defined by a* and b*.

In embodiments, colored glass articles that appear yellow in color may have a transmitted color coordinate in the CIELAB color space of L*greater than or equal to 20 and less than or equal to 90 and a* and b* values within a region of the a* vs. b* color space bound by the intersection of the lines: b*=0.2879·a*+27.818; b*=7.0833·a*−94.5; b*=0.45·a*+104.5; and b*=15.3·a*+253. This region is graphically depicted in FIG. 20 as the region being bound by lines A, B, C, and D.

In embodiments, colored glass articles that appear orange in color may have a transmitted color coordinate in the CIELAB color space of L*greater than or equal to 20 and less than or equal to 90 and a* and b* values within a region of the a* vs. b* color space bound by the intersection of the lines: b*=7.0833·a*−94.5; b*=−0.9583·a*+146.75; b*=2.6957a*−50.565; and b*=33. This region is graphically depicted in FIG. 20 as the region being bound by lines B, E, F and G.

In embodiments, colored glass articles that appear red in color may have a transmitted color coordinate in the CIELAB color space of L*greater than or equal to 20 and less than or equal to 90 and a* and b* values within a region of the a* vs. b* color space bound by the intersection of the lines: b*=2.6957·a*−50.565; a*=54; b*=1.0769·a*−17.154; and b*=6.6667·a*−173.67. This region is graphically depicted in FIG. 20 as the region being bound by lines F, H, I and J.

In embodiments, colored glass articles that appear green in color may have a transmitted color coordinate in the CIELAB color space of L*greater than or equal to 4 and less than or equal to 80 and a* and b* values within a region of the a* vs. b* color space bound by the intersection of the lines: b*=0.2879·a*+27.818; a*=0; b*=−1.375·a*+1; and b*=9.333·a*+86.667, exclusive of a* greater than −0.3 and less than 0.3 and exclusive of b* greater than −0.5 and less than 0.5. This region is graphically depicted in FIG. 20 as the region being bound by lines A, K, L, and M.

In embodiments, colored glass articles that appear pink/purple in color may have a transmitted color coordinate in the CIELAB color space of L*greater than or equal to 10 and less than or equal to 80 and a* and b* values within a region of the a* vs. b* color space bound by the intersection of the lines: b*=0.0833·a*+20.833; b*=2.1182·a*−32.073; b*=−0.3; and b*=1.5929·a*−0.3, exclusive of a* greater than −0.3 and less than 0.3 and exclusive of b* greater than −0.5 and less than 0.5. This region is graphically depicted in FIG. 20 as the region being bound by lines N, O, P and Q.

In embodiments, colored glass articles may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −15 and less than or equal to −0.3, and b* greater than or equal to −10 and less than or equal to 10 (exclusive of b* greater than −0.5 and less than 0.5).

In embodiments, colored glass articles may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 85 and less than or equal to 96.5, a* greater than or equal to −10 and less than −0.3, and b* greater than or equal to −5 and less than or equal to 5 (exclusive of b* greater than −0.5 and less than 0.5).

In embodiments of the colored glass articles described herein in which the colorant package includes Au, the concentrations of R₂O and Al₂O₃ may be adjusted such that the difference R₂O—Al₂O₃, in combination with Au, produces colored glass articles having the desired color (e.g., pink, purple, red, orange, etc.). In embodiments, the colored glass article may have a transmittance color coordinate in the CIELAB color space of: L*greater than or equal to 55 and less than or equal to 96.5; a* greater than or equal to −15 and less than or equal to 25; and b* greater than or equal to −25 and less than or equal to 25, exclusive of a* greater than −0.3 and less than 0.3 and exclusive of b* greater than −0.5 and less than 0.5.

In embodiments where the colorant package comprises Au, relatively smaller concentrations of R₂O—Al₂O₃ (e.g., less than or equal to 1.5 mol %) may result in a blue or purple glass article. Relatively higher concentrations of R₂O—Al₂O₃ (e.g., greater than 1.5 mol %) may result in an orange or red glass article.

For example, in embodiments in which the colorant package includes Au, R₂O—Al₂O₃ may be greater than or equal to −5 mol % and less than or equal to 1.5 mol % and b* may be greater than or equal to −25 and less than or equal to 10, exclusive of b* greater than −0.5 and less than 0.5. In embodiments, R₂O—Al₂O₃ may greater than or equal to −3 mol % and less than or equal to 1.5 mol % and b* may be greater than or equal to −15 and less than or equal to 7, exclusive of b* greater than −0.5 and less than 0.5. In embodiments, R₂O—Al₂O₃ may be greater than or equal to −5 mol % and less than or equal to 1.5 mol %, greater than or equal to −3 mol % and less than or equal to 1.5 mol %, greater than or equal to −1 mol % and less than or equal to 1.5 mol %, or even greater than or equal to 0 mol % and less than or equal to 1.5 mol %, or any and all sub-ranges formed from any of these endpoints; and b* may be greater than or equal to −25 and less than or equal to 10 (exclusive of b* greater than −0.5 and less than 0.5), greater than or equal to −25 and less than or equal to 7, greater than or equal to −25 and less than or equal to 5 (exclusive of b* greater than −0.5 and less than 0.5), greater than or equal to −15 and less than or equal to 10 (exclusive of b* greater than −0.5 and less than 0.5), greater than or equal to −15 and less than or equal to 7 (exclusive of b* greater than −0.5 and less than 0.5), greater than or equal to −15 and less than or equal to 5 (exclusive of b* greater than −0.5 and less than 0.5), greater than or equal to −10 and less than or equal to 10 (exclusive of b* greater than −0.5 and less than 0.5), greater than or equal to −10 and less than or equal to 7 (exclusive of b* greater than −0.5 and less than 0.5), or even greater than or equal to −10 and less than or equal to 5 (exclusive of b* greater than −0.5 and less than 0.5), or any and all sub-ranges formed from any of these endpoints.

In embodiments in which the colorant package includes Au, R₂O—Al₂O₃ may be greater than 1.5 mol % and less than or equal to 7 mol % and b* may be greater than or equal to 0.5 and less than or equal to 25. In embodiments, R₂O—Al₂O₃ may be greater than 1.5 mol % and less than or equal to 5 mol % and b* may be greater than or equal to 0.5 and less than or equal to 15. In embodiments, R₂O—Al₂O₃ may be greater than 1.5 mol % and less than or equal to 7 mol %, greater than 1.5 mol % and less than or equal to 5 mol %, or even greater than 1.5 mol % and less than or equal to 3 mol %, or any and all sub-ranges formed from any of these endpoints; and b* may be greater than or equal to 0.5 and less than or equal to 25, greater than or equal to 0.5 and less than or equal to 15, greater than or equal to 0.5 and less than or equal to 10, greater than or equal to 2.5 and less than or equal to 25, greater than or equal to 2.5 and less than or equal to 15, greater than or equal to 2.5 and less than or equal to 10, greater than or equal to 5 and less than or equal to 25, greater than or equal to 5 and less than or equal to 15, or even greater than or equal to 5 and less than or equal to 10, or any and all sub-ranges formed from any of these endpoints.

In embodiments, the colored glass articles including Au as a colorant may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −5 and less than or equal to 25 (exclusive of a* greater than −0.3 and less than 0.3), and b* greater than or equal to −20 and less than or equal to 5 (exclusive of b* greater than −0.5 and less than 0.5).

In embodiments, the colored glass articles including Au as a colorant may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −10 and less than or equal to 25 (exclusive of a* greater than −0.3 and less than 0.3), and b* greater than or equal to −20 and less than or equal to 5 (exclusive of b* greater than −0.5 and less than 0.5).

In embodiments, the colored glass articles including Cr₂O₃ as a colorant may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −18 and less than or equal to 0.3, and b* greater than or equal to 0.5 and less than or equal to 82.

In embodiments, the colored glass articles including Cr₂O₃ and NiO as a colorant may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −18 and less than or equal to 18 (exclusive of a* greater than −0.3 and less than 0.3), and b* greater than or equal to 0.5 and less than or equal to 82.

In embodiments, the colored glass articles including Cr₂O₃ and Co₃O₄ as a colorant may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −20 and less than or equal to 60 (exclusive of a* greater than −0.3 and less than 0.3), and b* greater than or equal to −90 and less than or equal to 85 (exclusive of b* greater than −0.5 and less than 0.5).

In embodiments, the colored glass articles including Cr₂O₃ and CuO as a colorant may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −35 and less than or equal to −0.3, and b* greater than or equal to 0.5 and less than or equal to 82.

In embodiments, the colored glass articles including Cr₂O₃, NiO, and CuO as a colorant may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −35 and less than or equal to 20 (exclusive of a* greater than −0.3 and less than 0.3), and b* greater than or equal to 0.5 and less than or equal to 75.

In embodiments, the colored glass articles including Cr₂O₃, NiO, and Co₃O₄ as a colorant may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −15 and less than or equal to 65 (exclusive of a* greater than −0.3 and less than 0.3), and b* greater than or equal to −90 and less than or equal to 80 (exclusive of b* greater than −0.5 and less than 0.5).

In embodiments, the colored glass articles including Cr₂O₃, CuO, and Co₃O₄ as a colorant may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −35 and less than or equal to 60 (exclusive of a* greater than −0.3 and less than 0.3), and b* greater than or equal to −90 and less than or equal to 80 (exclusive of b* greater than −0.5 and less than 0.5).

In embodiments, the colored glass articles including Cr₂O₃, NiO, CuO, and Co₃O₄ as a colorant may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −35 and less than or equal to 60 (exclusive of a* greater than −0.3 and less than 0.3), and b* greater than or equal to −90 and less than or equal to 80 (exclusive of b* greater than −0.5 and less than 0.5).

In embodiments, the colored glass articles including Ag as a colorant may have a transmitted color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −11.12 and less than or equal to 60 (exclusive of a* greater than −0.3 and less than 0.3), and b* greater than or equal to −20 and less than or equal to 120 (exclusive of b* greater than −0.5 and less than 0.5).

In embodiments, the transmitted color coordinates of the CIELAB color space may be described in terms of a range of L*values and a region of the a* (horizontal axis or x-axis) and b* (vertical axis or y-axis) color space. The region of the a* vs. b* color space may be defined by the intersection of a plurality of lines defined by a* and b*.

For example, in embodiments, colored glass articles comprising Ag as a colorant that appear yellow in color may have a transmitted color coordinate in the CIELAB color space of L*greater than or equal to 20 and less than or equal to 90 and a* and b* values within a region of the a* vs. b* color space bound by the intersection of the lines: b*=0.2879·a*+27.818; b*=7.0833·a*−94.5; b*=0.45·a*+104.5; and b*=15.3·a*+253. This region is graphically depicted in FIG. 20 as the region being bound by lines A, B, C, and D.

In embodiments, colored glass articles comprising Ag as a colorant that appear orange in color may have a transmitted color coordinate in the CIELAB color space of L*greater than or equal to 20 and less than or equal to 90 and a* and b* values within a region of the a* vs. b* color space bound by the intersection of the lines: b*=7.0833·a*−94.5; b*=−0.9583·a*+146.75; b*=2.6957·a*−50.565; and b*=33. This region is graphically depicted in FIG. 20 as the region being bound by lines B, E, F and G.

In embodiments, colored glass articles comprising Ag as a colorant that appear red in color may have a transmitted color coordinate in the CIELAB color space of L*greater than or equal to 20 and less than or equal to 90 and a* and b* values within a region of the a* vs. b* color space bound by the intersection of the lines: b*=2.6957·a*−50.565; a*=54; b*=1.0769·a*−17.154; and b*=6.6667·a*−173.67. This region is graphically depicted in FIG. 20 as the region being bound by lines F, H, I and J.

In embodiments, colored glass articles comprising Ag as a colorant that appear green in color may have a transmitted color coordinate in the CIELAB color space of L*greater than or equal to 4 and less than or equal to 80 and a* and b* values within a region of the a* vs. b* color space bound by the intersection of the lines: b*=0.2879·a*+27.818; a*=0; b*=−1.375·a*+1; and b*=9.333·a*+86.667, exclusive of a* greater than −0.3 and less than 0.3 and exclusive of b* greater than −0.5 and less than 0.5. This region is graphically depicted in FIG. 20 as the region being bound by lines A, K, L, and M.

In embodiments, colored glass articles comprising Ag as a colorant that appear pink/purple in color may have a transmitted color coordinate in the CIELAB color space of L*greater than or equal to 10 and less than or equal to 80 and a* and b* values within a region of the a* vs. b* color space bound by the intersection of the lines: b*=0.0833·a*+20.833; b*=2.1182·a*−32.073; b*=−0.3; and b*=1.5929·a*−0.3, exclusive of a* greater than −0.3 and less than 0.3 and exclusive of b* greater than −0.5 and less than 0.5. This region is graphically depicted in FIG. 20 as the region being bound by lines N, O, P and Q.

In embodiments, colored glass articles that include a transition metal oxides and/or rare earth metal oxides as a colorant (such as NiO, CuO, TiO₂, Co₃O₄, Cr₂O₃, and/or CeO₂) may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −15 and less than or equal to −0.3, and b* greater than or equal to −10 and less than or equal to 10 (exclusive of b* greater than −0.5 and less than 0.5).

In embodiments, colored glass articles that include a transition metal oxides and/or rare earth metal oxides as a colorant (such as NiO, CuO, TiO₂, Co₃O₄, Cr₂O₃, and/or CeO₂) may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 85 and less than or equal to 96.5, a* greater than or equal to −10 and less than −0.3, and b* greater than or equal to −5 and less than or equal to 5 (exclusive of b* greater than −0.5 and less than 0.5).

In some embodiments, the colored glass articles have an average transmittance of greater than or equal to 10% and less than or equal to 92% of light over the wavelength range from 380 nm to 750 nm. As noted herein, unless otherwise specified, the average transmittance is indicated for article thicknesses of 0.4 to 5 mm, inclusive of endpoints. In embodiments, the colored glass articles have an average transmittance greater than or equal to 15% and less than or equal to 92% over the wavelength range of 380 nm to 750 nm. In embodiments, the colored glass articles have an average transmittance greater than or equal to 20% and less than or equal to 92% for light over the wavelength range of 380 nm to 750 nm. In embodiments, the colored glass articles have an average transmittance greater than or equal to 25% and less than or equal to 92% for light over the wavelength range of 380 nm to 750 nm. In embodiments, the colored glass articles have an average transmittance greater than or equal to 30% and less than or equal to 92% for light over the wavelength range of 380 nm to 750 nm. In embodiments, the colored glass articles have an average transmittance greater than or equal to 19% and less than or equal to 88% over the wavelength range of 380 nm to 750 nm. In embodiments, the colored glass articles have an average transmittance greater than or equal to 15% and less than or equal to 88% over the wavelength range of 380 nm to 750 nm. In embodiments, the colored glass articles have an average transmittance greater than or equal to 20% and less than or equal to 88% for light over the wavelength range of 380 nm to 750 nm. In embodiments, the colored glass articles have an average transmittance greater than or equal to 25% and less than or equal to 88% for light over the wavelength range of 380 nm to 750 nm. In embodiments, the colored glass articles have an average transmittance greater than or equal to 30% and less than or equal to 88% for light over the wavelength range of 380 nm to 750 nm.

In embodiments, the colored glass articles described herein may have a dielectric constant Dk at 10 GHz of less than or equal to 6.4, such as less than or equal to 6.4 and greater than or equal to 5.6. In embodiments, the dielectric constant of the colored glass article may be less than or equal to 6.4 and greater than or equal to 5.7, less than or equal to 6.4 and greater than or equal to 5.8, less than or equal to 6.4 and greater than or equal to 5.9, less than or equal to 6.4 and greater than or equal to 6.0, less than or equal to 6.4 and greater than or equal to 6.2, less than or equal to 6.3 and greater than or equal to 5.6, less than or equal to 6.3 and greater than or equal to 5.7, less than or equal to 6.3 and greater than or equal to 5.8, less than or equal to 6.3 and greater than or equal to 5.9, less than or equal to 6.3 and greater than or equal to 6.0, less than or equal to 6.3 and greater than or equal to 6.2, less than or equal to 6.2 and greater than or equal to 5.7, less than or equal to 6.2 and greater than or equal to 5.8, less than or equal to 6.2 and greater than or equal to 5.9, less than or equal to 6.2 and greater than or equal to 6.0, or even less than or equal to 6.2 and greater than or equal to 6.1. As noted herein, while not wishing to be bound by theory, it is believed that the dielectric constant of the colored glass articles measured at 10 GHz approximates the dielectric constant at each frequency in the range from 10 GHz to 60 GHz. Accordingly, a dielectric constant reported for a colored glass article at a frequency of 10 GHz approximates the dielectric constant of the colored glass article at each frequency over the frequency range of 10 GHz to 60 GHz, inclusive of endpoints.

The colored glass articles formed from the glass compositions described herein may be any suitable thickness, which may vary depending on the particular application of the colored glass article. In embodiments, the colored glass articles may have a thickness greater than or equal to 200 μm and less than or equal to 6 mm, greater than or equal to 200 μm and less than or equal to 4 mm, greater than or equal to 200 μm and less than or equal to 2 mm, greater than or equal to 200 μm and less than or equal to 1 mm, greater than or equal to 200 μm and less than or equal to 750 μm, greater than or equal to 200 μm and less than or equal to 650 μm, greater than or equal to 200 μm and less than or equal to 600 μm, greater than or equal to 200 μm and less than or equal to 550 μm, greater than or equal to 200 μm and less than or equal to 500 μm, greater than or equal to 250 μm and less than or equal to 6 mm, greater than or equal to 250 μm and less than or equal to 4 mm, greater than or equal to 250 μm and less than or equal to 2 mm, greater than or equal to 250 μm and less than or equal to 1 mm, greater than or equal to 250 μm and less than or equal to 750 μm, greater than or equal to 250 μm and less than or equal to 650 μm, greater than or equal to 250 μm and less than or equal to 600 μm, greater than or equal to 250 μm and less than or equal to 550 μm, greater than or equal to 250 μm and less than or equal to 500 μm, greater than or equal to 300 μm and less than or equal to 6 mm, greater than or equal to 300 μm and less than or equal to 4 mm, greater than or equal to 300 μm and less than or equal to 2 mm, greater than or equal to 300 μm and less than or equal to 1 mm, greater than or equal to 300 μm and less than or equal to 750 μm, greater than or equal to 300 μm and less than or equal to 650 μm, greater than or equal to 300 μm and less than or equal to 600 μm, greater than or equal to 300 μm and less than or equal to 550 μm, greater than or equal to 300 μm and less than or equal to 500 μm, greater than or equal to 350 μm and less than or equal to 6 mm, greater than or equal to 350 μm and less than or equal to 4 mm, greater than or equal to 350 μm and less than or equal to 2 mm, greater than or equal to 350 μm and less than or equal to 1 mm, greater than or equal to 350 μm and less than or equal to 750 μm, greater than or equal to 350 μm and less than or equal to 650 μm, greater than or equal to 350 μm and less than or equal to 600 μm, greater than or equal to 350 μm and less than or equal to 550 μm, greater than or equal to 350 μm and less than or equal to 500 μm, greater than or equal to 400 μm and less than or equal to 6 mm, greater than or equal to 400 μm and less than or equal to 4 mm, greater than or equal to 400 μm and less than or equal to 2 mm, greater than or equal to 400 μm and less than or equal to 1 mm, greater than or equal to 400 μm and less than or equal to 750 μm, greater than or equal to 400 μm and less than or equal to 650 μm, greater than or equal to 400 μm and less than or equal to 600 μm, greater than or equal to 400 μm and less than or equal to 550 μm, greater than or equal to 400 μm and less than or equal to 500 μm, greater than or equal to 450 μm and less than or equal to 6 mm, greater than or equal to 450 μm and less than or equal to 4 mm, greater than or equal to 450 μm and less than or equal to 2 mm, greater than or equal to 450 μm and less than or equal to 1 mm, greater than or equal to 450 μm and less than or equal to 750 μm, greater than or equal to 450 μm and less than or equal to 650 μm, greater than or equal to 450 μm and less than or equal to 600 μm, greater than or equal to 450 μm and less than or equal to 550 μm, greater than or equal to 450 μm and less than or equal to 500 μm, greater than or equal to 500 μm and less than or equal to 6 mm, greater than or equal to 500 μm and less than or equal to 4 mm, greater than or equal to 500 μm and less than or equal to 2 mm, greater than or equal to 500 μm and less than or equal to 1 mm, greater than or equal to 500 μm and less than or equal to 750 μm, greater than or equal to 750 μm and less than or equal to 6 mm, greater than or equal to 750 μm and less than or equal to 4 mm, greater than or equal to 750 μm and less than or equal to 2 mm, greater than or equal to 750 μm and less than or equal to 1 mm, greater than or equal to 1 mm and less than or equal to 6 mm, greater than or equal to 1 mm and less than or equal to 4 mm, greater than or equal to 1 mm and less than or equal to 2 mm, greater than or equal to 2 mm and less than or equal to 6 mm, greater than or equal to 2 mm and less than or equal to 4 mm, or even greater than or equal to 4 mm and less than or equal to 6 mm, or any and all sub-ranges formed from any of these endpoints.

As discussed hereinabove, colored glass articles formed from the glass compositions described herein may have an increased fracture toughness such that the colored glass articles are more resistant to damage. In embodiments, the colored glass article may have a K_IC fracture toughness as measured by a CNSB method, prior to ion exchange, greater than or equal to 0.7 MPa·m^1/2. In embodiments, the colored glass article may have a K_IC fracture toughness, prior to ion exchange as measured by a CNSB method greater than or equal to 0.7 MPa·m^1/2, greater than or equal to 0.8 MPa·m^1/2, greater than or equal to 0.9 MPa·m^1/2, or even greater than or equal to 1.0 MPa·m^1/2.

As discussed hereinabove, colored glass articles formed from the glass compositions described herein may have an increased fracture toughness such that the colored glass articles are more resistant to damage. In embodiments, the colored glass article may have a K_IC fracture toughness as measured by a DCB method, prior to ion exchange, greater than or equal to 0.7 MPa·m^1/2. In embodiments, the colored glass article may have a K_IC fracture toughness, prior to ion exchange as measured by a DCB method greater than or equal to 0.7 MPa·m^1/2, greater than or equal to 0.8 MPa·m^1/2, greater than or equal to 0.9 MPa·m^1/2, or even greater than or equal to 1.0 MPa·m^1/2

In embodiments, the glass compositions described herein are ion-exchangeable to facilitate strengthening the colored glass articles made from the glass compositions. In typical ion-exchange processes, smaller metal ions in the glass compositions are replaced or “exchanged” with larger metal ions of the same valence within a layer that is close to the outer surface of the colored glass article made from the glass composition. The replacement of smaller ions with larger ions creates a compressive stress within the layer of the colored glass article made from the glass composition. In embodiments, the metal ions are monovalent metal ions (e.g., Li⁺, Na⁺, K⁺, and the like), and ion-exchange is accomplished by immersing the glass article made from the glass composition in a bath comprising at least one molten salt of the larger metal ion that is to replace the smaller metal ion in the colored glass article. Alternatively, other monovalent ions such as Ag⁺, Tl⁺, Cu⁺, and the like may be exchanged for monovalent ions. The ion-exchange process or processes that are used to strengthen the colored glass article made from the glass composition may include contacting the colored glass article with an ion-exchange medium. In embodiments, the ion-exchange medium may be a molten salt bath. For example, the ion-exchange process may include, but is not limited to, immersion in a single bath or multiple baths of like or different compositions with optional washing and/or annealing steps between immersions.

Upon exposure to the colored glass article, the ion-exchange solution (e.g., KNO₃ and/or NaNO₃ molten salt bath) may, according to embodiments, be at a temperature greater than or equal to 350° C. and less than or equal to 500° C., greater than or equal to 360° C. and less than or equal to 450° C., greater than or equal to 370° C. and less than or equal to 440° C., greater than or equal to 360° C. and less than or equal to 420° C., greater than or equal to 370° C. and less than or equal to 400° C., greater than or equal to 375° C. and less than or equal to 475° C., greater than or equal to 400° C. and less than or equal to 500° C., greater than or equal to 410° C. and less than or equal to 490° C., greater than or equal to 420° C. and less than or equal to 480° C., greater than or equal to 430° C. and less than or equal to 470° C., or even greater than or equal to 440° C. and less than or equal to 460° C., or any and all sub-ranges between the foregoing values. In embodiments, the colored glass article may be exposed to the ion-exchange solution for a duration greater than or equal to 2 hours and less than or equal to 24 hours, greater than or equal to 2 hours and less than or equal to 12 hours, greater than or equal to 2 hours and less than or equal to 6 hours, greater than or equal to 8 hours and less than or equal to 24 hours, greater than or equal to 6 hours and less than or equal to 24 hours, greater than or equal to 6 hours and less than or equal to 12 hours, greater than or equal to 8 hours and less than or equal to 24 hours, or even greater than or equal to 8 hours and less than or equal to 12 hours, or any and all sub-ranges formed from any of these endpoints.

In embodiments, a colored glass article made from a glass composition may be ion-exchanged to achieve a depth of compression of 10 μm or greater, 20 μm or greater, 30 μm or greater, 40 μm or greater, 50 μm or greater, 60 μm or greater, 70 μm or greater, 80 μm or greater, 90 μm or greater, or 100 μm or greater. In embodiments, the colored glass article made from the glass composition may have a thickness “t” and may be ion-exchanged to achieve a depth of compression greater than or equal to 0.15t, greater than or equal to 0.17t, or even greater than or equal to 0.2t. In embodiments, the colored glass article made from the glass composition may have a thickness “t” and may be ion-exchanged to achieve a depth of compression less than or equal to 0.3t, less than or equal to 0.27t, or even less than or equal to 0.25t. In embodiments, the colored glass article made from the glass composition described herein may have a thickness “t” and may be ion-exchanged to achieve a depth of compression greater than or equal to 0.15t and less than or equal to 0.3t, greater than or equal to 0.15t and less than or equal to 0.27t, greater than or equal to 0.15t and less than or equal to 0.25t, greater than or equal to 0.17t and less than or equal to 0.3t, greater than or equal to 0.17t and less than or equal to 0.27t, greater than or equal to 0.17t and less than or equal to 0.25t, greater than or equal to 0.2t and less than or equal to 0.3t, greater than or equal to 0.2t and less than or equal to 0.27t, or even greater than or equal to 0.2t and less than or equal to 0.25t, or any and all sub-ranges formed from any of these endpoints.

The development of this surface compression layer is beneficial for achieving a better crack resistance and higher flexural strength compared to non-ion-exchanged materials. The surface compression layer has a higher concentration of the ions exchanged into the colored glass article in comparison to the concentration of the ions exchanged into the colored glass article for the body (i.e., the area not including the surface compression) of the colored glass article. In embodiments, the colored glass article made from the glass composition may have a surface compressive stress after ion-exchange strengthening greater than or equal to 300 MPa, greater than or equal to 400 MPa, greater than or equal to 500 MPa, or even greater than or equal to 600 MPa. In embodiments, the colored glass article made from the glass composition may have a surface compressive stress after ion-exchange strengthening less than or equal to 1 GPa, less than or equal to 900 MPa, or even less than or equal to 800 MPa. In embodiments, the colored glass article made from the glass composition may have a surface compressive stress after ion-exchange strengthening greater than or equal to 300 MPa and less than or equal to 1 GPa, greater than or equal to 300 MPa and less than or equal to 900 MPa, greater than or equal to 300 MPa and less than or equal to 800 MPa, greater than or equal to 400 MPa and less than or equal to 1 GPa, greater than or equal to 400 MPa and less than or equal to 900 MPa, greater than or equal to 400 MPa and less than or equal to 800 MPa, greater than or equal to 500 MPa and less than or equal to 1 GPa, greater than or equal to 500 MPa and less than or equal to 900 MPa, greater than or equal to 500 MPa and less than or equal to 800 MPa, greater than or equal to 600 MPa and less than or equal to 1 GPa, greater than or equal to 600 MPa and less than or equal to 900 MPa, greater than or equal to 600 MPa and less than or equal to 800 MPa.

In embodiments, the colored glass articles made from the glass composition may have a maximum central tension after ion-exchange strengthening greater than or equal to 40 MPa, greater than or equal to 60 MPa, greater than or equal to 80 MPa, or even greater than or equal to 100 MPa. In embodiments, the colored glass article made from the glass composition may have a maximum central tension after ion-exchange strengthening less than or equal to 250 MPa, less than or equal to 200 MPa, or even less than or equal to 150 MPa. In embodiments, the colored glass article made from the glass composition may have a maximum central tension after ion-exchange strengthening greater than or equal to 40 MPa and less than or equal to 250 MPa, greater than or equal to 40 MPa and less than or equal to 200 MPa, greater than or equal to 40 MPa and less than or equal to 150 MPa, greater than or equal to 60 MPa and less than or equal to 250 MPa, greater than or equal to 60 MPa and less than or equal to 200 MPa, greater than or equal to 60 MPa and less than or equal to 150 MPa, greater than or equal to 80 MPa and less than or equal to 250 MPa, greater than or equal to 80 MPa and less than or equal to 200 MPa, greater than or equal to 80 MPa and less than or equal to 150 MPa, greater than or equal to 100 MPa and less than or equal to 250 MPa, greater than or equal to 100 MPa and less than or equal to 200 MPa, or even greater than or equal to 100 MPa and less than or equal to 150 MPa, or any and all sub-ranges formed from any of these endpoints. As utilized herein, central tension refers to a maximum central tension value unless otherwise indicated.

As described herein, in embodiments, the glass compositions described herein may be formulated to increase the retention of Au, which increases the concentration of Au in the resultant colored glass articles, thereby expanding the color gamut achievable by the colored glass articles. In embodiments, a colored glass article having greater than or equal to 0.01 mol % and less than or equal to 1 mol % Au may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −5 and less than or equal to 25, exclusive of a* greater than −0.3 and less than 0.3, and b* greater than or equal to −20 and less than or equal to 5, exclusive of b* greater than −0.5 and less than 0.5. In embodiments, colored glass article having greater than or equal to 1×10⁻⁶ mol % and less than or equal to 1 mol % Au may have a transmittance color coordinate in the CIELAB color space of L*greater than or equal to 55 and less than or equal to 96.5, a* greater than or equal to −10 and less than or equal to 25 exclusive of a* greater than −0.3 and less than 0.3, and b* greater than or equal to −20 and less than or equal to 5 exclusive of b* greater than −0.5 and less than 0.5.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 60 mol % and less than or equal to 70 mol % SiO₂; greater than or equal to 11 mol % and less than or equal to 17 mol % Al₂O₃; greater than or equal to 2 mol % and less than or equal to 8 mol % B₂O₃; greater than or equal to 9 mol % and less than or equal to 14 mol % Li₂O; greater than or equal to 2 mol % and less than or equal to 6 mol % Na₂O; greater than or equal to 0.1 mol % and less than or equal to 2 mol % MgO; greater than or equal to 0.1 mol % and less than or equal to 2 mol % ZnO; and greater than or equal to 1×10⁻⁶ mol % and less than or equal to 0.01 mol % Au. In these embodiments, MgO+ZnO is greater than or equal to 0.1 mol % and less than or equal to 4.5 mol %.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 60 mol % and less than or equal to 70 mol % SiO₂; greater than or equal to 11 mol % and less than or equal to 17 mol % Al₂O₃; greater than or equal to 2 mol % and less than or equal to 8 mol % B₂O₃; greater than or equal to 9 mol % and less than or equal to 14 mol % Li₂O; greater than or equal to 2 mol % and less than or equal to 6 mol % Na₂O; greater than or equal to 0.1 mol % and less than or equal to 0.5 mol % K₂O; and greater than or equal to 1×10⁻⁶ mol % and less than or equal to 0.05 mol % Au. In these embodiments, R₂O—Al₂O₃ is greater than or equal to 0 mol % and less than or equal to 3 mol %, R₂O being the sum of Li₂O, Na₂O, and K₂O.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 40 mol % and less than or equal to 70 mol % SiO₂; greater than or equal to 8 mol % and less than or equal to 20 mol % Al₂O₃; greater than or equal to 1 mol % and less than or equal to 10 mol % B₂O₃; greater than or equal to 1 mol % and less than or equal to 20 mol % Li₂O; greater than or equal to 1 mol % and less than or equal to 15 mol % Na₂O; greater than or equal to 0 mol % and less than or equal to 8 mol % MgO; greater than or equal to 0 mol % and less than or equal to 5 mol % ZnO; and greater than or equal to 0.0005 mol % and less than or equal to 1 mol % Au, wherein: MgO+ZnO is greater than or equal to 0.1 mol % and less than or equal to 6 mol %.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 40 mol % and less than or equal to 70 mol % SiO₂; greater than or equal to 8 mol % and less than or equal to 20 mol % Al₂O₃; greater than or equal to 1 mol % and less than or equal to 10 mol % B₂O₃; greater than or equal to 1 mol % and less than or equal to 20 mol % Li₂O; greater than or equal to 1 mol % and less than or equal to 15 mol % Na₂O; greater than or equal to 0 mol % and less than or equal to 6 mol % MgO; greater than or equal to 0 mol % and less than or equal to 5 mol % ZnO; and greater than or equal to 1×10⁻⁶ mol % and less than or equal to 1 mol % Au, wherein: MgO+ZnO is greater than or equal to 0.1 mol % and less than or equal to 6 mol %.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 50 mol % and less than or equal to 80 mol % SiO₂; greater than or equal to 7 mol % and less than or equal to 25 mol % Al₂O₃; greater than or equal to 1 mol % and less than or equal to 15 mol % B₂O₃; greater than or equal to 5 mol % and less than or equal to 20 mol % Li₂O; greater than or equal to 0.5 mol % and less than or equal to 15 mol % Na₂O; greater than 0 mol % and less than or equal to 1 mol % K₂O; and greater than or equal to 1×10⁻⁶ mol % and less than or equal to 1 mol % Au, wherein: R₂O—Al₂O₃ is greater than or equal to −5 mol % and less than or equal to 7 mol %, R₂O being the sum of Li₂O, Na₂O, and K₂O.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 50 mol % and less than or equal to 70 mol % SiO₂; greater than or equal to 10 mol % and less than or equal to 17.5 mol % Al₂O₃; greater than or equal to 3 mol % and less than or equal to 10 mol % B₂O₃; greater than or equal to 8.8 mol % and less than or equal to 14 mol % Li₂O; greater than or equal to 1.5 mol % and less than or equal to 8 mol % Na₂O; and greater than 0 mol % and less than or equal to 2 mol % Cr₂O₃, wherein: R₂O+R′O—Al₂O₃ is greater than or equal to 0.5 mol % and less than or equal to 6 mol %, wherein R₂O is the sum of Li₂O, Na₂O, and K₂O and R′O is the sum of MgO, ZnO, and CaO; and Al₂O₃+MgO+ZnO is greater than or equal to 12 mol % and less than or equal to 22 mol %.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 50 mol. % and less than or equal to 70 mol. % SiO₂; greater than or equal to 10 mol. % and less than or equal to 20 mol. % Al₂O₃; greater than or equal to 4 mol. % and less than or equal to 10 mol. % B₂O₃; greater than or equal to 7 mol. % and less than or equal to 17 mol. % Li₂O; greater than or equal to 1 mol. % and less than or equal to 9 mol. % Na₂O; greater than or equal to 0.01 mol. % and less than or equal to 1 mol. % SnO₂; and greater than or equal to 0.01 mol. % and less than or equal to 5 mol. % Ag, wherein R₂O—Al₂O₃ is greater than 0.2 mol. % and less than or equal to 5.00 mol. % and R₂O is the sum of Li₂O, Na₂O, and K₂O.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 50 mol % and less than or equal to 70 mol % SiO₂; greater than or equal to 10 mol % and less than or equal to 20 mol % Al₂O₃; greater than or equal to 1 mol % and less than or equal to 10 mol % B₂O₃; greater than or equal to 7 mol % and less than or equal to 14 mol % Li₂O; greater than or equal to 0.01 mol % and less than or equal to 8 mol % Na₂O; greater than or equal to 0.01 mol % and less than or equal to 1 mol % K₂O; greater than or equal to 0 mol % and less than or equal to 7 mol % CaO; and greater than or equal to 0 mol % and less than or equal to 8 mol % MgO, wherein Li₂O+K₂O+Na₂O+CaO+MgO+ZnO is less than or equal to 25 mol % and at least one of: CuO+NiO+Co₃O₄+Cr₂O₃ is greater than or equal to 0.001 mol %, CeO₂ is greater than or equal to 0.1 mol %, and TiO₂ is greater than or equal to 0.1 mol %.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 53 mol % to less than or equal to 66 mol % SiO₂; greater than or equal to 9 mol % to less than or equal to 18 mol % Al₂O₃; greater than or equal to 0 mol % to less than or equal to 15 mol % B₂O₃; greater than or equal to 0 mol % to less than or equal to 3 mol % P₂O₅; greater than or equal to 0 mol % to less than or equal to 16 mol % Li₂O; greater than or equal to 0 mol % to less than or equal to 15 mol % Na₂O; greater than or equal to 0 mol % to less than or equal to 5 mol % K₂O; greater than or equal to 0 mol % to less than or equal to 6 mol % MgO; greater than or equal to 0 mol % to less than or equal to 6 mol % CaO; greater than or equal to 0 mol % to less than or equal to 3 mol % ZnO; greater than or equal to 0 mol % to less than or equal to 2 mol % TiO₂; greater than 0 mol % to less than or equal to 2 mol % CeO₂; greater than or equal to 0 mol % to less than or equal to 1 mol % Fe₂O₃; greater than or equal to 0 mol % to less than or equal to 0.5 mol % SnO₂; greater than or equal to 0 mol % to less than or equal to 0.05 mol % SO₃; greater than or equal to 0 mol % to less than or equal to 1 mol % WO₃; greater than or equal to 0 mol % to less than or equal to 1 mol % Nb₂O₅; greater than or equal to 0 mol % to less than or equal to 1 mol % Bi₂O₃; greater than or equal to 0 mol % to less than or equal to 1 mol % MoO₃; and greater than or equal to 0 mol % to less than or equal to 3 mol % La₂O₃, wherein: TiO₂+CeO₂ is greater than or equal to 0.2 mol %; and Li₂O+Na₂O is greater than or equal to 8 mol %.

In embodiments, the glass composition and the resultant colored glass article may comprise greater than or equal to 50 mol % and less than or equal to 70 mol % SiO₂; greater than or equal to 10 mol % and less than or equal to 20 mol % Al₂O₃; greater than or equal to 1 mol % and less than or equal to 10 mol % B₂O₃; greater than or equal to 7 mol % and less than or equal to 14 mol % Li₂O; greater than 0 mol % and less than or equal to 8 mol % Na₂O; greater than or equal to 0 mol % and less than or equal to 1 mol % K₂O; greater than or equal to 0 mol % and less than or equal to 7 mol % CaO; greater than or equal to 0 mol % and less than or equal to 8 mol % MgO; and at least one of: greater than 0 mol % to less than or equal to 4 mol % Er₂O₃, and greater than 0 mol % to less than or equal to 4 mol % Nd₂O₃.

In embodiments, the colored glass articles may have an average CTE of less than about 85×10⁻⁷ C⁻¹, less than about 80×10⁻⁷ C⁻¹, less than about 75×10⁻⁷ C⁻¹, less than about 70×10⁻⁷ C⁻¹, less than about 65×10⁻⁷ C⁻¹, or even less than about 60×10⁻⁷ C⁻¹. These relatively low CTE values improve the survivability of the glass to thermal cycling or thermal stress conditions relative to articles with higher CTEs.

In embodiments, the colored glass articles described herein may generally have a strain point greater than or equal to about 400° C. and less than or equal to about 550° C.

In embodiments, the colored glass articles described herein may generally have an anneal point greater than or equal to about 450° C. and less than or equal to about 650° C.

In embodiments, the colored glass articles described herein may generally have a softening point greater than or equal to about 700° C. and less than or equal to about 900° C.

The colored glass articles described herein may be used for a variety of applications including, for example, for housings for consumer electronic devices; for architectural glass applications; for automotive or vehicular glass applications; or for commercial or household appliance applications. In embodiments, a consumer electronic device (e.g., smartphones, tablet computers, watches, personal computers, ultrabooks, televisions, and cameras), an architectural glass, and/or an automotive glass may comprise a colored glass article as described herein.

An example article incorporating any of the colored glass articles disclosed herein is shown in FIGS. 1 and 2. Specifically, FIGS. 1 and 2 show a consumer electronic device 100 including a housing 102 having front 104, back 106, and side surfaces 108; electrical components (not shown) that are at least partially inside or entirely within the housing and including at least a controller, a memory, and a display 110 at or adjacent to the front surface of the housing; and a cover substrate 112 at or over the front surface of the housing such that it is over the display. In embodiments, at least a portion of housing 102, such as the back 106, may include any of the colored glass articles disclosed herein.

EXAMPLES

In order that various embodiments be more readily understood, reference is made to the following examples, which illustrate various embodiments of the colored glass articles described herein.

Heat Treatment—The heat treatment of the Examples below included placing the glass articles between a SiC setter, placing the glass articles in an oven and heating the oven to the indicated heat treatment temperature at a rate of 4° C./min, and cooling from the heat treatment temperature after the heat treatment time had lapsed at a cooling rate of 3° C./min.

Table 1 shows comparative examples Comp. 1 and Comp. 2 and examples 1-30, with the batch compositions utilized to form each example reported (in terms of mol %). Table 1 also reports the heat treatment used to produce colored glass articles from the batch compositions and the analyzed Au concentration (in terms of mol %) of the resultant colored glass articles.

TABLE 1
	Example
	1	2	3	Comp. 1	Comp. 2	4
SiO2	58.8	58.8	58.8	58.5	58.5	58.5
Al2O3	16.5	16.5	16.5	16.5	16.5	16.5
B2O3	6.0	6.0	6.0	6.0	6.0	6.0
Li2O	10.0	10.0	10.0	12.0	12.0	10.0
Na2O	4.5	4.5	4.5	6.5	6.5	4.5
K2O	0.2	0.2	0.2	0.5	0.5	0.5
MgO	3.0	3.0	3.0	—	—	3.0
ZnO	1.0	1.0	1.0	—	—	1.0
ZrO2	—	—	—	—	—	—
P2O5	—	—	—	—	—	—
SnO2	—	—	—	—	—	—
Fe2O3	—	—	—	—	—	—
Au	0.005	0.005	0.005	0.010	0.020	0.010
R2O	14.7	14.7	14.7	19.0	19.0	15.0
MgO + ZnO	4.0	4.0	4.0	0.0	0.0	4.0
R2O − Al2O3	−1.8	−1.8	−1.8	2.5	2.5	−1.5
5.72*Al2O3 −	−546.7	−546.7	−546.7	−585.9	−585.9	−552.2
21.4*ZnO −
2.5*P2O5 −
35*Li2O −
16.6*B2O3 −
20.5*MgO −
23.3*Na2O −
27.9*SrO −
18.5*K2O −
26.3*CaO
HEAT TREATMENT
Meltingtem-	1550	1500	1450	1450	1450	1450
perature
(° C.)
Meltingtime	18	18	18	18	18	18
(hours)
Analyzed	0.0009	0.0017	0.0018	0.0013	0.0023	0.0030
Au (mol %)
% of Au	18.0	34.0	36.0	13.0	11.5	30.0
retained
Example	5	6	7	8	9	10
SiO2	58.5	60.7	60.7	60.7	60.7	60.7
Al2O3	16.5	14.5	14.5	14.5	14.5	14.5
B2O3	6.0	6.0	6.0	6.0	6.0	6.0
Li2O	10.0	10.0	10.0	10.0	10.0	10.0
Na2O	4.5	4.5	4.5	4.5	4.5	4.5
K2O	0.5	0.5	0.5	0.5	0.5	0.2
MgO	3.0	3.0	3.0	3.0	3.0	3.0
ZnO	1.0	1.0	1.0	1.0	1.0	1.0
ZrO2	—	—	0.5	—	0.5	0.5
P2O5	—	—	—	1.0	1.0	—
SnO2	—	0.10	0.10	0.10	0.10	0.05
Fe2O3	—	—	—	—	—	—
Au	0.020	0.005	0.005	0.005	0.005	0.005
R2O	15.0	15.0	15.0	15.0	15.0	14.7
MgO + ZnO	4.0	4.0	4.0	4.0	4.0	4.0
R2O − Al2O3	−1.5	0.5	0.5	0.5	0.5	0.2
5.72*Al2O3 −	−552.2	−563.7	−563.7	−566.2	−566.2	−558.1
21.4*ZnO −
2.5*P2O5 −
35*Li2O −
16.6*B2O3 −
20.5*MgO −
23.3*Na2O −
27.9*SrO −
18.5*K2O −
26.3*CaO
Meltingtem-	1450	1550	1550	1550	1550	1550
perature
(° C.)
Meltingtime	18	18	18	18	18	18
(hours)
Analyzed	0.0043	0.0013	0.0018	0.0006	0.0007	0.0019
Au (mol %)
% of Au	21.5	26.0	36.0	12.0	14.0	38.0
retained
	Example
	11	12	13	14	15	16
SiO2	60.7	60.7	60.7	61.8	61.8	61.8
Al2O3	14.5	14.5	14.5	14.5	14.5	14.5
B2O3	6.0	6.0	6.0	6.0	6.0	6.0
Li2O	10.0	10.0	10.0	6.5	6.5	6.5
Na2O	4.5	4.5	4.5	8.0	8.0	8.0
K2O	0.2	0.2	0.2	0.2	0.2	0.2
MgO	3.0	3.0	3.0	2.0	2.0	2.0
ZnO	1.0	1.0	1.0	1.0	1.0	1.0
ZrO2	0.2	0.3	0.5	—	—	0.2
P2O5	—	—	—	—	—	—
SnO2	0.01	0.03	0.05	—	0.05	0.05
Fe2O3	—	—	—	—	—	—
Au	0.005	0.005	0.005	0.005	0.005	0.005
R2O	14.7	14.7	14.7	14.7	14.7	14.7
MgO + ZnO	4.0	4.0	4.0	3.0	3.0	3.0
R2O − Al2O3	0.2	0.2	0.2	0.2	0.2	0.2
5.72*Al2O3 −	−558.1	−558.1	−558.1	−496.7	−496.7	−496.7
21.4*ZnO −
2.5*P2O5 −
35*Li2O −
16.6*B2O3 −
20.5*MgO −
23.3*Na2O −
27.9*SrO −
18.5*K2O −
26.3*CaO
HEAT TREATMENT
Meltingtem-	1550	1550	1550	1500	1500	1500
perature
(° C.)
Meltingtime	18	18	18	18	18	18
(hours)
Analyzed	0.0013	0.0016	0.0017	0.0009	0.0010	0.0012
Au (mol %)
% of Au	26.0	32.0	34.0	18.0%	20.0%	24.0%
retained
	Example
	17	18	19	20	21	22
SiO2	61.8	61.8	61.8	60.8	60.8	60.8
Al2O3	14.5	14.5	14.5	15.5	15.5	15.5
B2O3	6.0	6.0	6.0	6.0	6.0	6.0
Li2O	6.5	6.5	6.5	6.5	6.5	6.5
Na2O	8.0	8.0	8.0	8.0	8.0	8.0
K2O	0.2	0.2	0.2	0.2	0.2	0.2
MgO	2.0	2.0	2.0	2.0	2.0	2.0
ZnO	1.0	1.0	1.0	1.0	1.0	1.0
ZrO2	—	—	0.2	—	—	0.2
P2O5	—	—	—	—	—	—
SnO2	—	0.05	0.05	—	0.05	0.05
Fe2O3	—	—	—	—	—	—
Au	0.005	0.005	0.005	0.005	0.005	0.005
R2O	14.7	14.7	14.7	14.7	14.7	14.7
MgO + ZnO	3.0	3.0	3.0	3.0	3.0	3.0
R2O − Al2O3	0.2	0.2	0.2	−0.8	−0.8	−0.8
5.72*Al2O3 −	−496.7	−496.7	−496.7	−490.9	−490.9	−490.9
21.4*ZnO −
2.5*P2O5 −
35*Li2O −
16.6*B2O3 −
20.5*MgO −
23.3*Na2O −
27.9*SrO −
18.5*K2O −
26.3*CaO
HEAT TREATMENT
Meltingtem-	1500	1500	1500	1500	1500	1500
perature
(° C.)
Meltingtime	18	18	18	18	18	18
(hours)
Analyzed	0.0010	0.0011	0.0014	0.0012	0.0012	0.0012
Au (mol %)
% of Au	20.0%	22.0%	28.0%	24.0%	24.0%	24.0%
retained
	Example
	23	24	25	26	27	28
SiO2	61.2	61.2	60.7	60.7	60.7	60.7
Al2O3	14.5	14.5	14.5	14.5	14.5	14.5
B2O3	6.0	6.0	6.0	6.0	6.0	6.0
Li2O	6.5	6.5	8.0	9.0	9.0	9.0
Na2O	8.0	8.0	4.5	4.5	4.5	4.5
K2O	0.8	0.8	0.2	0.2	0.2	0.2
MgO	2.0	2.0	4.0	4.0	3.0	4.0
ZnO	1.0	1.0	2.0	1.0	2.0	1.0
ZrO2	—	—	—	—	—	—
P2O5	—	—	—	—	—	—
SnO2	0.10	0.10	0.05	0.05	0.05	0.05
Fe2O3	0.05	0.05	0.10	0.05	0.05	0.10
Au	0.005	0.005	0.005	0.005	0.005	0.005
R2O	15.3	15.3	12.7	13.7	13.7	13.7
MgO + ZnO	3.0	3.0	6.0	5.0	5.0	5.0
R2O − Al2O3	0.8	0.8	−1.8	−0.8	−0.8	−0.8
5.72*Al2O3 −	−506.8	−506.8	−530.0	−543.6	−544.5	−543.6
21.4*ZnO −
2.5*P2O5 −
35*Li2O −
16.6*B2O3 −
20.5*MgO −
23.3*Na2O −
27.9*SrO −
18.5*K2O −
26.3*CaO
HEAT TREATMENT
Meltingtem-	1500	1500	1500	1500	1500	1500
perature
(° C.)
Meltingtime	16	16	18	18	18	18
(hours)
Analyzed	0.0016	0.0017	0.0005	0.0009	0.0005	0.0006
Au (mol %)
% of Au	32.0%	34.0%	10.0%	18.0%	10.0%	12.0%
retained
	Example
	29	30
SiO2	61.2	61.2
Al2O3	14.5	14.5
B2O3	6.0	6.0
Li2O	6.5	6.5
Na2O	8.0	8.0
K2O	0.8	0.8
MgO	2.0	2.0
ZnO	1.0	1.0
ZrO2	—	—
P2O5	—	—
SnO2	0.10	0.10
Fe2O3	0.05	0.05
Au	0.005	0.005
R20	15.3	15.3
MgO + ZnO	3.0	3.0
R2O − Al2O3	−0.8	−0.8
5.72*Al2O3 −
21.4*ZnO −
2.5*P2O5 −
35*Li2O −
16.6*B2O3 −	−544.5	−544.5
20.5*MgO −
23.3*Na2O −
27.9*SrO −
18.5*K2O −
26.3*CaO
HEAT TREATMENT
Meltingtem-	1500	1500
perature
(° C.)
Meltingtime	18	18
(hours)
Analyzed	0.0006	0.0013
Au (mol %)
% of Au	12.0%	26.0%
retained

Referring to Table 1, Examples 1-3 were formed from the same glass composition, but melted at different temperatures. Example 1, which was melted at 1550° C., had an Au retention of 18.0%. Examples 2 and 3, which were melted at 1500° C. and 1450° C., respectively, had Au retentions of 34.0% and 36.0%, respectively. As indicated by Examples 1-3, a lower melting temperature favors Au retention. Therefore, it may be desirable to form a glass composition having a lower melting point such that Au retention during processing may be improved.

Comparative Examples Comp. 1 and Comp. 2 had an Au retention of 13.0% and 11.5%, respectively, after being melted at 1450° C. for 18 hours. Examples 4 and 5, which were similar to Comparative Examples Comp. 1 and Comp. 2, respectively, but included MgO and ZnO, had Au retentions of 30.0% and 21.5%, respectively, after being melted at 1450° C. for 18 hours. As indicated by Comparative Examples Comp. 1 and Comp. 2 and Examples 4 and 5, including MgO and ZnO in the glass composition improves Au retention of the resultant colored glass article.

Example 6 had an Au retention of 26.0% after being melted at 1550° C. for 18 hours. Example 7, which was similar to Example 3 but included ZrO₂, had an Au retention of 36.0% after being melted at 1550° C. for 18 hours. As indicated by Examples 6 and 7, including ZrO₂ in addition to MgO and ZnO in the glass composition improves Au retention of the resultant colored glass article.

Examples 8 and 9, which were similar to Examples 6 and 7, respectively, but included P₂O₅, had lower Au retentions of 12.0% and 14.0%, respectively, after being melted at 1550° C. for 18 hours. As indicated by Examples 6-9, including P₂O₅ in the glass composition impairs Au retention of the resultant colored glass article.

Examples 10-13, which included ZrO₂ and SnO₂, had relatively higher Au retentions of 38.0%, 26.0%, 32.0%, and 34%, respectively, after being melted at 1550° C. for 18 hours. As indicated by Examples 10-13, including SnO₂ in addition to MgO, ZnO, and ZrO₂ in the glass compositions improves Au retention of the resultant colored glass article.

Examples 14 and 17 had an Au retention of 18.0% and 20.0%, respectively, after being melted at 1550° C. for 18 hours. Examples 15 and 18, which were similar to Examples 14 and 17, but included SnO₂, had an Au retention of 20.0% and 22%, respectively, after being melted at 1550° C. for 18 hours. As indicated by Examples 15 and 18, including SnO₂ in addition to MgO and ZnO in the glass composition improves Au retention of the resultant colored glass article.

Examples 16 and 19, which included ZrO₂ and SnO₂, had relatively higher Au retentions of 24.0% and 28.0%, respectively, after being melted at 1550° C. for 18 hours. As indicated by Examples 16 and 19, including SnO₂ in addition to MgO, ZnO, and ZrO₂ in the glass compositions improves Au retention of the resultant colored glass article.

Examples 23 and 24, which included Fe₂O₃, had relatively higher Au retentions of 32.0% and 34.0%, respectively, after being melted at 1550° C. for 18 hours. As indicated by Examples 23 and 24, including Fe₂O₃ in addition to MgO, ZnO, and ZrO₂ in the glass compositions improves Au retention of the resultant colored glass article.

Referring now to FIGS. 3A-3C, 4A-4C, 5A-5C, and 6A-6C, a gradient-temperature approach was used to identify the heat treatment cycle parameters (i.e., temperature and duration) to achieve the desired color coordinates. Specifically, a 12 cm long and 1.5 mm thick sample formed from the glass composition of Example 11 was placed in a gradient-temperature oven and held at a heat treatment temperature, which varied along the length of the sample, for the prescribed duration. The sample was then rapidly cooled to quench the sample and the precipitated Au particles therein. Optical transmission spectra were then measured every 2 mm along the direction of the gradient. The coordinates in the CIELAB color space were plotted, as measured under F2 illumination and a 10⁰ standard observer angle, in which the heat treatment temperature moved through the color space with separate plots for the four different heat treatment durations: 0.25 hour (FIGS. 3A-3C), 0.5 hour (FIGS. 4A-4C), 1 hour (FIGS. 5A-5C), and 1.5 hour (FIGS. 6A-6C). As indicated by FIGS. 3A-3C, 4A-4C, 5A-5C, and 6A-6C, different heat treatment temperatures and durations may be used to achieve the desired color.

Note that, as described herein, processing of the glass compositions to produce the resultant colored glass articles may occur in an isothermal oven. However, a gradient-temperature oven was used in these examples to investigate a range of temperatures simultaneously. A gradient-temperature oven produces similar results as an isothermal oven at the desired temperature.

Table 2 shows examples 31-65, with the analyzed concentration (in terms of mol %) of the resultant colored glass articles.

TABLE 2
Example	31	32	33	34	35	36
SiO2	61.09	61.03	61.08	60.99	60.87	60.73
Al2O3	14.51	14.50	14.51	14.49	14.44	14.58
B2O3	6.00	6.00	5.86	5.93	5.91	5.94
Li2O	9.94	9.94	10.07	10.10	10.01	10.10
Na2O	4.30	4.33	4.28	4.28	4.25	4.31
K2O	0.19	0.19	0.19	0.19	0.45	0.19
MgO	2.89	2.90	2.89	2.89	2.89	2.93
ZnO	1.00	1.00	0.99	0.99	0.99	1.05
ZrO2	0.22	0.30	0.45	0.50	0.03	0.00
P2O5	—	—	—	—	—	—
SnO2	0.02	0.03	0.05	0.07	0.11	0.11
Fe2O3	0.02	0.02	0.02	0.02	0.02	0.00
Au	0.0013	0.0015	0.0017	0.0019	0.0013	0.0009
R2O	14.43	14.46	14.54	14.57	14.71	14.60
MgO + ZnO	3.89	3.90	3.88	3.88	3.88	3.98
R2O − Al2O3	−0.08	−0.04	0.03	0.08	0.27	0.02
5.72*Al2O3 −	−548.9	−549.8	−550.4	−552.7	−553.6	−555.2
21.4*ZnO −
2.5*P2O5 −
35*Li2O −
16.6*B2O3 −
20.5*MgO −
23.3*Na2O −
27.9*SrO −
18.5*K2O −
26.3*CaO
Example	37	38	39	40	41	42
SiO2	61.26	60.71	59.87	60.15	59.28	61.36
Al2O3	14.38	14.65	14.86	15.43	15.07	15.72
B2O3	5.89	5.95	5.95	5.88	5.70	6.00
Li2O	10.00	10.05	10.14	10.01	9.80	10.21
Na2O	4.28	4.30	4.31	4.27	6.03	4.34
K2O	0.19	0.19	0.19	0.19	0.18	0.20
MgO	2.86	2.93	3.11	2.89	2.80	0.97
ZnO	1.01	1.06	1.09	1.02	0.99	1.05
ZrO2	0.00	0.00	0.32	0.00	0.00	0.00
P2O5	—	—	—	—	—	—
SnO2	0.06	0.05	0.05	0.11	0.10	0.11
Fe2O3	0.00	0.07	0.07	0.00	0.00	0.00
Au	0.0007	0.0005	0.0007	0.0008	0.0005	0.0010
R2O	14.47	14.54	14.64	14.47	16.01	14.75
MgO + ZnO	3.87	3.99	4.20	3.91	3.79	2.02
R2O − Al2O3	0.09	−0.11	−0.22	−0.96	0.94	−0.97
5.72*Al2O3 −	−549.0	−553.2	−559.7	−543.8	−573.8	−514.2
21.4*ZnO −
2.5*P2O5 −
35*Li2O −
16.6*B2O3 −
20.5*MgO −
23.3*Na2O −
27.9*SrO −
18.5*K2O −
26.3*CaO
Example	43	44	45	46	47	48
SiO2	60.94	59.36	60.40	60.59	60.56	60.64
Al2O3	16.51	16.42	15.52	15.32	15.23	15.08
B2O3	5.89	5.78	6.05	6.04	6.04	6.01
Li2O	10.05	9.90	10.66	10.65	10.63	10.74
Na2O	4.27	4.22	4.77	4.79	4.89	4.90
K2O	0.19	0.19	0.19	0.19	0.20	0.20
MgO	0.97	2.94	0.97	0.97	0.98	0.97
ZnO	1.03	1.03	1.02	1.02	1.05	1.05
ZrO2	0.00	0.00	0.31	0.32	0.31	0.32
P2O5	—	—	—	—	—	—
SnO2	0.10	0.11	0.05	0.06	0.06	0.05
Fe2O3	—	—	—	—	—	—
Au	0.0010	0.0006	0.0008	0.0008	0.0008	0.0007
R2O	14.51	14.31	15.62	15.63	15.72	15.84
MgO + ZnO	2.00	3.97	1.99	1.99	2.03	2.02
R2O − Al2O3	−2.00	−2.11	0.10	0.31	0.49	0.76
5.72*Al2O3 −	−500.0	−532.7	−541.1	−542.2	−545.4	−549.6
21.4*ZnO −
2.5*P2O5 −
35*Li2O −
16.6*B2O3 −
20.5*MgO −
23.3*Na2O −
27.9*SrO −
18.5*K2O −
26.3*CaO
Example	49	50	51	52	53	54
SiO2	60.94	59.36	60.40	60.59	62.14	62.08
Al2O3	16.51	16.42	15.52	15.32	14.95	14.98
B2O3	5.89	5.78	6.05	6.04	6.06	5.93
Li2O	10.05	9.90	10.66	10.65	10.51	10.69
Na2O	4.27	4.22	4.77	4.79	4.29	4.31
K2O	0.19	0.19	0.19	0.19	0.14	0.14
MgO	0.97	2.94	0.97	0.97	0.50	0.50
ZnO	1.03	1.03	1.02	1.02	1.03	1.00
ZrO2	0.00	0.00	0.31	0.32	0.29	0.29
P2O5	—	—	—	—	—	—
SnO2	0.10	0.11	0.05	0.06	0.04	0.04
Fe2O3	—	—	—	—	0.04	0.04
Au	0.0008	0.0010	0.0012	0.0015	0.0014	0.0011
R2O	14.51	14.31	15.62	15.63	14.94	15.14
MgO + ZnO	2.00	3.97	1.99	1.99	1.54	1.51
R2O − Al2O3	−2.00	−2.11	0.10	0.31	−0.01	0.16
5.72*Al2O3 −	−556.1	−558.4	−557.7	−558.9	−517.8	−521.6
21.4*ZnO −
2.5*P2O5 −
35*Li2O −
16.6*B2O3 −
20.5*MgO −
23.3*Na2O −
27.9*SrO −
18.5*K2O −
26.3*CaO
Example	55	56	57	58	59	60
SiO2	62.06	61.95	61.95	61.67	61.01	60.66
Al2O3	14.92	14.87	14.88	14.88	14.96	15.03
B2O3	5.92	5.91	5.92	5.93	6.04	6.06
Li2O	10.86	11.03	11.04	11.06	11.18	11.21
Na2O	4.25	4.24	4.24	4.25	4.26	4.28
K2O	0.14	0.14	0.14	0.14	0.14	0.14
MgO	0.50	0.50	0.49	0.50	0.50	0.50
ZnO	1.01	1.02	1.01	1.02	1.03	1.03
ZrO2	0.28	0.28	0.28	0.28	0.28	0.28
P2O5	—	—	—	0.21	0.56	0.76
SnO2	0.04	0.04	0.04	0.04	0.04	0.04
Fe2O3	0.02	0.01	—	—	—	—
Au	0.0010	0.0010	0.0011	0.0010	0.0010	0.0010
R2O	15.25	15.41	15.42	15.46	15.58	15.63
MgO + ZnO	1.51	1.52	1.50	1.52	1.53	1.54
R2O − Al2O3	0.33	0.54	0.55	0.58	0.62	0.60
5.72*Al2O3 −	−526.5	−532.6	−532.8	−534.9	−541.5	−543.7
21.4*ZnO −
2.5*P2O5 −
35*Li2O −
16.6*B2O3 −
20.5*MgO −
23.3*Na2O −
27.9*SrO −
18.5*K2O −
26.3*CaO
	Example
	61	62	63	64	65
SiO2	60.51	60.49	60.80	60.94	61.47
Al2O3	15.06	15.02	14.76	14.61	14.60
B2O3	6.06	6.07	6.05	5.97	5.91
Li2O	11.21	11.22	11.20	11.17	11.12
Na2O	4.30	4.30	4.29	4.29	4.27
K2O	0.14	0.14	0.14	0.15	0.15
MgO	0.51	0.51	0.51	0.51	0.50
ZnO	1.03	1.04	1.03	1.03	1.04
ZrO2	0.28	0.28	0.28	0.48	0.50
P2O5	0.86	0.89	0.90	0.81	0.40
SnO2	0.04	0.04	0.04	0.04	0.04
Fe2O3	—	—	—	—	—
Au	0.0009	0.0010	0.0009	0.0011	0.0010
R2O	15.65	15.67	15.63	15.61	15.53
MgO + ZnO	1.54	1.54	1.53	1.54	1.54
R2O − Al2O3	0.59	0.65	0.87	1.00	0.93
5.72*Al2O3 −	−544.2	−545.2	−545.1	−543.6	−539.3
21.4*ZnO −
2.5*P2O5 −
35*Li2O −
16.6*B2O3 −
20.5*MgO −
23.3*Na2O −
27.9*SrO −
18.5*K2O −
26.3*CaO

Referring now to Table 3, example glass articles 31-35 having the concentrations shown in Table 2 were subjected to isothermal heat treatment between 600° C. and 660° C. The observable colors of the resultant colored glass articles are shown in Table 3. Heat treating example glass articles 31, 32, and 33 having an analyzed R₂O—Al₂O₃ of −0.08 mol %, −0.04 mol %, and 0.03 mol %, respectively, resulted in observably pink, purple, and red colored glass articles. Heat treating example glass articles 34 and 35, having an analyzed R₂O—Al₂O₃ of 0.08 mol % and 0.27 mol %, respectively, resulted in observably red and orange colored glass articles. As indicated by Tables 2 and 3, the analyzed R₂O—Al₂O₃ of a glass article may be adjusted and the glass article may be subjected to a certain heat treatment to provide a desired colored glass article.

	TABLE 3
		Example
		31	32	33	34	35
	Observable	pink,	pink,	pink,	pink,	orange,
	colors	purple	purple	purple	red,	red
					purple

Referring now to Table 4, example glass articles 36-48 having the analyzed concentrations shown in Table 2 were subjected to heat treatment at the temperature and for the period of time shown in Table 4. The observable colors of the resultant colored glass articles are shown in Table 4.

TABLE 4
Heat	550° C.	575° C.	600° C.	625° C.	650° C.
treatment	for 2 hrs.	for 2 hrs.	for 2 hrs.	for 2 hrs.	for 2 hrs.
36	purple	purple	purple	purple	—
37	clear,	purple	purple	red	—
	purple
38	pink	pink	pink	pink	—
39	red	red	red	red	—
40	clear,	purple	purple	purple	—
	purple
41	orange	orange	orange	orange	—
42	clear,	purple	purple	purple	—
	purple
43	clear	clear	purple	purple	—
44	clear	clear	purple	purple	—
45	purple	purple	purple	red	red
46	clear,	purple	purple	red	red
	purple
47	purple	purple	red	red	red
48	purple	purple	red	red	red

Example glass article 41, having an analyzed R₂O—Al₂O₃ of 0.94 mol %, was the only glass article to result in an observably orange colored glass article after heat treatment. Example glass articles 36-40 and 42-48 had an R₂O—Al₂O₃ of 0.76 mol % or less. Heat treating glass article 38, including Fe₂O₃, resulted in an observably pink colored glass article. Heat treating glass articles 39 and 45-48, including ZrO₂, resulted in red colored glass articles. As indicated by Tables 2 and 4, the analyzed R₂O—Al₂O₃ may be adjusted, additional components may be added to the glass composition, and the glass article may be subjected to a certain heat treatment to provide a desired colored glass article.

Table 5 shows examples 66-75, with the analyzed concentration (in terms of mol %) of the resultant colored glass articles.

TABLE 5
Example	66	67	68	69	70	71
SiO2	62.15	62.27	62.22	62.19	62.08	61.95
Al2O3	14.93	14.97	14.90	14.95	14.98	14.87
B2O3	6.09	5.98	6.03	6.03	5.93	5.91
Li2O	10.50	10.45	10.53	10.50	10.69	11.03
Na2O	4.30	4.30	4.28	4.27	4.31	4.24
K2O	0.14	0.14	0.14	0.14	0.14	0.14
MgO	0.50	0.50	0.50	0.50	0.50	0.50
ZnO	1.03	1.00	1.03	1.04	1.00	1.02
ZrO2	0.28	0.29	0.28	0.29	0.29	0.28
P2O5	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.04	0.04	0.04	0.04	0.04	0.04
Fe2O3	0.04	0.04	0.04	0.04	0.04	0.01
Au	6.0 × 10−6	9.0 × 10−6	1.2 × 10−5	1.1 × 10−5	8.0 × 10−6	1.0 × 10−5
R2O	14.94	14.89	14.95	14.91	15.14	15.41
MgO + ZnO	1.53	1.50	1.53	1.54	1.50	1.52
R2O − Al2O3	0.01	−0.08	0.05	−0.04	0.16	0.54
5.72*Al2O3 −	−518.27	−513.82	−518.03	−516.67	−521.57	−532.56
21.4*ZnO −
2.5*P2O5 −
35*Li2O −
16.6*B2O3 −
20.5*MgO−
23.3*Na2O −
27.9*SrO −
18.5*K2O −
26.3*CaO
Example	72	73	74	75
SiO2	61.67	61.47	62.75	61.67
Al2O3	14.88	14.60	14.47	14.88
B2O3	5.93	5.91	5.88	5.93
Li2O	11.06	11.12	11.07	11.06
Na2O	4.25	4.27	4.27	4.25
K2O	0.14	0.15	0.15	0.14
MgO	0.50	0.50	0.29	0.50
ZnO	1.02	1.04	0.47	1.02
ZrO2	0.28	0.50	0.52	0.28
P2O5	0.21	0.40	0.08	0.21
SnO2	0.04	0.04	0.04	0.04
Fe2O3	0.00	0.00	0.00	0.00
Au	8.3 × 10−6	8.3 × 10−6	8.3 ×10−6	8.3 ×10−6
R2O	15.45	15.54	15.49	15.45
MgO + ZnO	1.52	1.54	0.76	1.52
R2O − Al2O3	0.57	0.94	1.02	0.57
5.72*Al2O3 −
21.4*ZnO −
2.5*P2O5 −	−534.64	−539.57	−520.76	−534.64
35*Li2O −
16.6*B2O3 −
20.5*MgO −
23.3*Na2O −
27.9*SrO −
18.5*K2O −
26.3*CaO

Referring now to Table 6, example glass articles 66 and 68-75 having the analyzed concentrations shown in Table 5 were subjected to heat treatment at the temperature and for the period of time shown in Table 6. The observable colors of the resultant colored glass articles are shown in Table 6.

TABLE 6
Heat	550° C.	575° C.	600° C.	625° C.	650° C.	550° C.	575° C.
treatment	for 2 hrs.	for 2 hrs.	for 2 hrs.	for 2 hrs.	for 2 hrs.	for 8 hrs.	for 8 hrs.
66	—	blue	blue	blue	—	—	—
68	—	blue	blue	red	—	—	—
69	—	purple	purple	red	—	—	—
70	red	purple	blue	blue	—	—	—
71	clear,	blue	blue	purple	—	—	—
	purple
72	clear,	purple	purple	purple	—	—	—
	purple
73	clear,	purple	purple	purple	—	—	—
	purple
74	clear,	purple	purple	red	red	red	red
	purple
75	—	—	purple	red	red	purple	red

Example glass articles 71-75, having an analyzed R₂O—Al₂O₃ of greater than or equal to 0.54 mol %, had a relatively limited achievable color gamut after being subjected to different heat treatments. As indicated by Table 6, a relatively increased R₂O—Al₂O₃ may limit the achievable color gamut of the colored glass article.

Referring now to Table 7, example glass article 66 having the analyzed concentrations shown in Table 5 and the thicknesses shown in Table 7 were subjected to heat treatment at the temperature and for the period of time shown in Table 7. The transmittance color coordinate in the CIELAB color space, as measured at the indicated article thickness under F2 illumination and a 100 standard observer angle, and the observable color of the resultant colored glass articles are shown in Table 7.

TABLE 7
Thick-		525° C.	535° C.	535° C.	545° C.	575° C.
ness		for 6 hrs.	for 6 hrs.	for 10 hrs.	for 10 hrs.	for 2 hrs.
	L*	96.39	95.09	92.01	91.06	92.75
	a*	0.15	1.68	4.21	2.53	−0.60
	b*	0.27	−0.12	−2.12	−3.64	−2.62
	Observable	clear	pink	pink	purple	blue
	color
1.33 mm	L*	96.14	94.18	86.80	84.96	87.95
	a*	0.31	2.60	8.81	3.50	−1.67
	b*	0.42	−0.09	−4.55	−7.99	−5.86
	Observable	clear	pink	pink	purple	blue
	color
2.06 mm	L*	95.69	90.65	83.19	78.95	83.25
	a*	0.55	6.37	13.52	6.58	−3.01
	b*	0.63	−0.97	−4.53	−11.46	−8.40
	Observable	clear	pink	pink	purple	blue
	color
Thick-		600° C.	625° C.
ness		for 2 hrs.	for 2 hrs.
0.6 mm	L*	93.60	92.21
	a*	−0.61	−0.12
	b*	−0.60	−1.91
	Observable	blue	blue
	color
1.33 mm	L*	90.23	87.41
	a*	−1.34	−0.15
	b*	−1.72	−4.02
	Observable	blue	blue
	color
	L*	86.49	82.29
	a*	−2.05	−0.24
	b*	−2.30	−5.93
	Observable	blue	blue
	color

Referring now to Table 8, example glass article 68 having the analyzed concentrations shown in Table 5 and the thicknesses shown in Table 8 were subjected to heat treatment at the temperature and for the period of time shown in Table 8. The transmittance color coordinate in the CIELAB color space, as measured at the indicated article thickness under F2 illumination and a 100 standard observer angle, and the observable color of the resultant colored glass articles are shown in Table 8.

TABLE 8
		545° C.	550° C.	555° C.	535° C.	545° C.
Thickness		for 2 hrs.	for 2 hrs.	for 1.5 hrs.	for 10 hrs.	for 4 hrs.
0.6 mm	L*	93.11	92.14	91.56	91.16	90.79
	a*	3.74	4.82	4.74	6.02	5.90
	b*	−0.62	−1.31	−2.06	−0.27	−1.33
	Observable	pink	pink	pink	red	pink
	color
1.33 mm	L*	89.09	87.26	86.79	85.12	84.78
	a*	7.98	9.84	9.46	12.00	11.74
	b*	−1.42	−2.58	−3.64	−0.72	−2.32
	Observable	pink	purple	pink	red	pink
	color
2.06 mm	L*	84.41	81.51	81.40	79.52	78.50
	a*	12.63	15.29	14.09	17.14	17.21
	b*	−2.25	−4.01	−5.39	−0.26	−3.16
	Observable	pink	purple	pink	red	red
	color
		560° C.	555° C.	570° C.	625° C.	600° C.
Thickness		for 0.75 hrs.	for 4 hrs.	for 0.75 hrs.	for 3 hrs.	for 2 hrs.
0.6 mm	L*	92.14	89.13	88.96	88.74	89.18
	a*	4.61	5.00	4.90	2.75	−1.05
	b*	−1.57	−3.95	−4.51	−4.49	−4.32
	Observable	pink	purple	purple	purple	purple
	color
1.33 mm	L*	85.56	81.32	79.76	80.41	79.58
	a*	10.56	10.79	7.38	5.66	−2.04
	b*	−4.34	−7.51	−10.45	−9.10	−9.85
	Observable	pink	purple	purple	purple	purple
	color
2.06 mm	L*	77.01	74.55	70.91	71.91	71.33
	a*	16.22	16.05	8.60	8.16	−2.76
	b*	−8.50	−9.19	−15.68	−13.36	−14.14
	Observable	pink	pink	purple	purple	purple
	color
		575° C.	575° C.
Thickness		for 2 hrs.	for 4 hrs.
0.6 mm	L*	88.09	88.92
	a*	−01.8	1.77
	b*	−5.64	−4.80
	Observable	blue	blue
	color
1.33 mm	L*	78.27	80.57
	a*	0.17	3.42
	b*	−11.89	−9.88
	Observable	blue	blue
	color
2.06 mm	L*	70.17	72.06
	a*	−0.58	4.74
	b*	−16.48	−14.79
	Observable	blue	blue
	color

Referring now to Table 9, example glass article 68 having the analyzed concentrations shown in Table 5 and the thicknesses shown in Table 9 were subjected to heat treatment at the temperature and for the period of time shown in Table 9. The transmittance color coordinate in the CIELAB color space, as measured at the indicated article thickness under F2 illumination and a 10° standard observer angle, and the observable color of the resultant colored glass articles are shown in Table 9.

TABLE 9
		530° C.	535° C.	545° C.	550° C.	555° C.
Thick-		for	for	for	for	for
ness		3 hrs.	6 hrs.	2 hrs.	2 hrs.	1.5 hrs.
0.6	L*	94.72	90.50	89.99	88.79	88.58
mm	a*	1.96	6.78	7.30	7.58	7.50
	b*	0.34	0.18	−0.85	−1.80	−2.57
	Obser-	pink	pink	pink	pink	pink
	vable
	color
1.33	L*	92.64	84.15	83.50	80.52	79.57
mm	a*	3.99	13.49	14.01	14.51	14.41
	b*	0.62	0.67	−0.95	−3.71	−5.60
	Obser-	pink	red	red	pink	pink
	vable
	color
2.06	L*	90.49	77.92	74.81	72.37	71.79
mm	a*	6.07	19.65	21.74	20.56	21.07
	b*	0.97	1.59	−1.98	−5.27	−6.54
	Obser-	pink	red	pink	pink	pink
	vable
	color
		555° C.	650° C.	540° C.	565° C.	585° C.
Thick-		for	for	for	for	for
ness		4 hrs.	2 hrs.	3 hrs.	1.75 hrs.	2 hrs.
0.6	L*	88.59	87.25	88.03	86.62	87.36
mm	a*	6.20	7.01	4.98	3.98	2.37
	b*	−2.50	−4.14	−4.41	−5.65	−5.52
	Obser-	purple	purple	purple	purple	purple
	vable
	color
1.33	L*	80.63	77.89	78.78	76.92	77.59
mm	a*	13.13	13.81	10.10	8.92	5.17
	b*	−3.71	−7.35	−8.78	−10.22	−10.98
	Obser-	purple	purple	purple	purple	purple
	vable
	color
2.06	L*	71.87	68.47	70.21	67.15	68.17
mm	a*	18.44	19.71	14.96	12.94	7.47
	b*	−6.46	−10.62	−12.00	−14.54	−15.73
	Obser-	purple	purple	purple	purple	purple
	vable
	color
Thick-		560° C. for	600° C. for
ness		0.75 hrs.	2 hrs.
0.6	L*	87.04	87.56
mm	a*	0.99	1.39
	b*	−6.09	−5.32
	Obser-	blue	blue
	vable
	color
1.33	L*	77.03	77.57
mm	a*	3.32	2.56
	b*	−11.99	−10.84
	Obser-	blue	blue
	vable
	color
2.06	L*	67.17	68.30
mm	a*	3.12	4.07
	b*	−17.38	−15.38
	Obser-	blue	blue
	vable
	color

As indicated in Tables 7-9, colored glass articles including Au may be subjected to different heat treatment to achieve a desired observable color.

Table 10 shows the surface compressive stress CS, depth of layer DOL, and maximum central tension CT of example glass article 67 after being subjected to heat treatment at 545° C. for 2 hrs. and then being subjected to ion-exchange under the conditions listed in Table 10.

TABLE 10
IOX temp. (° C.)	400	400	400	400	400	400	400
IOX time (hrs.)	5	6	7	8	6	6.5	6.5
KNO3 in	83.0	83.0	83.0	83.0	83.0	83.0	80.0
IOX bath (wt %)
NaNO3 in	15.4	15.4	15.4	15.4	15.6	15.0	18.0
IOX bath (wt %)
LiNO3 in	1.6	1.6	1.6	1.6	1.4	2.0	2.0
IOX bath (wt %)
CS (MPa)	720	643	632	623	657	621	611
DOL (μm)	4.46	4.86	5.36	5.44	5.00	5.04	4.85
CT (MPa)	111.1	117.4	116.3	115.6	119.2	109.1	118.2

Table 11 shows example compositions C1-C26, with the analyzed concentration (in terms of mol %) of the resultant colored glass articles.

TABLE 11
Composition	C1	C2	C3	C4	C5	C6
SiO2	61.21	61.94	62.86	61.81	61.91	61.36
Al2O3	14.46	14.48	14.52	15.56	15.54	15.75
B2O3	5.84	5.95	5.92	5.88	5.89	5.91
Li2O	11.79	10.95	11.01	11.05	11.02	11.17
Na2O	6.34	6.32	5.34	5.34	5.34	5.42
K2O	0.19	0.19	0.19	0.19	0.19	0.19
MgO	0.01	0.02	0.01	0.02	0.02	0.02
CaO	—	—	—	—	—	—
ZnO	—	—	—	—	—	—
ZrO2	—	—	—	—	—	—
SnO2	0.11	0.11	0.10	0.11	0.05	0.06
Fe2O3	—	—	—	—	—	0.07
Cl	0.02	0.03	0.02	0.03	0.02	0.02
Au	0.0005	0.0007	0.0009	0.0008	0.0007	0.0005
R2O	18.32	17.46	16.54	16.58	16.55	16.78
R2O—Al2O3	3.86	2.98	2.02	1.02	1.01	1.03
5.72*Al2O3-	−578.32	−550.38	−528.71	−523.70	−522.93	−529.18
21.4*ZnO-
2.5*P2O5-35*Li2O-
16.6*B2O3-
20.5*MgO-
23.3*Na2O-
27.9*SrO-18.5*K2O-
26.3*CaO
Composition	C7	C8	C9	C10	C11	C12
SiO2	61.24	60.87	60.67	60.54	60.56	60.70
Al2O3	15.66	16.54	16.47	16.52	16.36	16.27
B2O3	5.89	5.85	5.84	5.99	6.04	6.01
Li2O	11.15	11.08	10.97	11.06	11.13	11.12
Na2O	5.38	5.34	5.35	5.27	5.28	5.28
K2O	0.19	0.19	0.19	0.20	0.20	0.19
MgO	0.01	0.02	0.02	0.02	0.02	0.02
CaO	—	—	—	—	—	—
ZnO	—	—	—	—	—	—
ZrO2	0.32	—	0.31	0.32	0.32	0.32
SnO2	0.05	0.06	0.05	0.05	0.05	0.05
Fe2O3	0.07	—	0.07	—	—	—
Cl	0.02	0.02	0.02	—	—	—
Au	0.0005	0.0007	0.0005	0.0007	0.0008	0.0008
R2O	16.72	16.61	16.51	16.53	16.61	16.59
R2O—Al2O3	1.06	0.07	0.04	0.01	0.25	0.32
5.72*Al2O3-	−527.52	−518.65	−515.27	−518.94	−523.37	−522.85
21.4*ZnO-
2.5*P2O5-35*Li2O-
16.6*B2O3-
20.5*MgO-
23.3*Na2O-
27.9*SrO-18.5*K2O-
26.3*CaO
Composition	C13	C14	C15	C16	C17	C18
SiO2	60.64	60.64	63.76	65.01	65.86	67.01
Al2O3	16.07	15.42	14.39	14.29	14.28	13.47
B2O3	6.01	6.04	5.86	5.09	4.36	4.13
Li2O	11.37	11.50	11.02	10.96	10.95	10.92
Na2O	5.28	5.76	4.24	4.23	4.22	4.20
K2O	0.19	0.19	0.14	0.14	0.14	0.14
MgO	0.02	0.02	0.04	0.03	0.02	0.02
CaO	—	—	—	—	0.01	0.01
ZnO	—	—	0.02	—	—	—
ZrO2	0.32	0.32	0.48	0.20	0.10	0.04
SnO2	0.05	0.05	0.04	0.04	0.04	0.04
Fe2O3	—	—	—	—	—	—
Cl	—	—	—	—	—	—
Au	0.0008	0.0008	0.0011	0.0010	0.0010	0.0010
R2O	16.84	17.45	15.41	15.33	15.31	15.26
R2O—Al2O3	0.77	2.03	1.01	1.04	1.03	1.79
5.72*Al2O3-	−532.74	−552.69	−503.22	−488.03	−475.55	−474.86
21.4*ZnO-
2.5*P2O5-35*Li2O-
16.6*B2O3-
20.5*MgO-
23.3*Na2O-
27.9*SrO-18.5*K2O-
26.3*CaO
Composition	C19	C20	C21	C22	C23
SiO2	67.59	67.75	67.84	67.89	67.63
Al2O3	13.13	13.01	12.96	12.99	13.15
B2O3	3.93	3.92	3.92	3.92	3.94
Li2O	10.94	10.91	10.88	10.77	10.69
Na2O	4.17	4.17	4.17	4.20	4.21
K2O	0.14	0.14	0.14	0.14	0.15
MgO	0.02	0.02	0.01	0.01	0.01
CaO	0.01	0.01	0.01	0.01	0.10
ZnO	0.00	0.00	0.00	0.00	0.00
ZrO2	0.02	0.02	0.01	0.01	0.02
SnO2	0.04	0.04	0.04	0.04	0.04
Fe2O3	0.00	0.00	0.00	0.00	0.00
Cl	0.00	0.00	0.00	0.00	0.00
Au	0.0011	0.0014	0.0016	0.0006	0.0001
R2O	15.25	15.22	15.20	15.11	15.04
R2O—Al2O3	2.13	2.21	2.24	2.12	1.90
5.72*Al2O3-	−473.41	−473.02	−472.32	−468.73	−468.03
21.4*ZnO-
2.5*P2O5-35*Li2O-
16.6*B2O3-
20.5*MgO-
23.3*Na2O-
27.9*SrO-18.5*K2O-
26.3*CaO
Composition	C24	C25	C26
SiO2	63.76	65.86	67.59
Al2O3	14.39	14.28	13.13
B2O3	5.86	4.36	3.93
Li2O	11.02	10.95	10.94
Na2O	4.24	4.22	4.17
K2O	0.14	0.14	0.14
MgO	0.04	0.02	0.02
CaO	0.00	0.00	0.00
ZnO	0.02	0.00	0.00
ZrO2	0.48	0.10	0.02
SnO2	0.04	0.04	0.04
Fe2O3	0.00	0.00	0.00
Cl	0.00	0.00	0.00
Au	8.3 × 10−6	7.7× 10−6	8.0 × 10−6
R2O	15.40	15.31	15.25
R2O—Al2O3	1.01	1.03	2.12
5.72*Al2O3-	−503.30	−475.27	−473.20
21.4*ZnO-
2.5*P2O5-35*Li2O-
16.6*B2O3-
20.5*MgO-
23.3*Na2O-
27.9*SrO-18.5*K2O-
26.3*CaO

Referring now to Table 12, example glass articles A1-A52 were formed from example compositions C2-C9 and C15-C23 shown in Table 11 and were subjected to heat treatment at the temperature and for the period of time shown in Table 12. The transmittance color coordinate in the CIELAB color space, as measured at an article thickness of 1.33 mm under F2 illumination and a 10° standard observer angle, and the observable color of the resultant colored glass articles are shown in Table 12.

TABLE 12
Glass Article	A1	A2	A3	A4	A5	A6
Composition	C18	C19	C20	C21	C22	C23
Heat treatment	550	550	550	550	550	550
temp. (° C.)
Heat treatment	8	8	8	8	8	8
time (hr.)
L*	87.39	88.12	86.98	86.12	91.39	96.68
a*	7.72	7.34	8.39	9.23	4.78	0.00
b*	1.87	4.93	8.07	9.58	3.81	0.80
Observable color	orange	orange	orange	orange	orange	light
						yellow
Glass Article	A7	A8	A9	A10	A11	A12
Composition	C15	C16	C17	C18	C18	C19
Heat treatment	575	575	575	575	575	575
temp. (° C.)
Heat treatment	2	2	2	8	2	8
time (hr.)
L*	83.48	92.46	85.94	88.08	91.19	88.2
a*	0.19	0.98	1.68	8.15	3.07	7.80
b*	−6.06	−0.93	−4.63	5.71	−0.47	6.51
Observable color	blue	purple	purple	orange	pink	orange
Glass Article	A13	A14	A15	A16	A17	A18
Composition	C19	C20	C20	C21	C22	C22
Heat treatment	575	575	575	575	575	575
temp. (° C.)
Heat treatment	2	8	2	8	8	2
time (hr.)
L*	89.96	86.7	86.9	85.72	90.59	90.98
a*	4.42	8.49	8.50	8.98	5.51	4.33
b*	−0.06	9.06	6.59	10.40	4.77	1.19
Observable color	pink	orange	orange	orange	orange	red
Glass Article	A19	A20	A21	A22	A23	A24
Composition	C23	C23	C15	C16	C17	C18
Heat treatment	575	575	600	600	600	600
temp. (° C.)
Heat treatment	2	8	2	2	2	2
time (hr.)
L*	96.73	95.89	82.63	83	83.43	88.03
a*	0.03	0.63	3.35	4.27	5.48	8.35
b*	0.75	1.84	−6.62	−6.11	−5.49	4.10
Observable color	yellow	peach	purple	purple	purple	orange
Glass Article	A25	A26	A27	A28	A29	A30
Composition	C19	C20	C22	C23	C2	C3
Heat treatment	600	600	600	600	625	625
temp. (° C.)
Heat treatment	2	2	2	2	2	2
time (hr.)
L*	87.99	86.66	90.23	96.4	89.29	87.6
a*	8.34	8.91	5.53	0.28	5.14	7.22
b*	5.45	8.48	3.52	1.24	9.97	10.51
Observable color	orange	orange	orange	light	orange	red
				orange
Glass Article	A31	A32	A33	A34	A35	A36
Composition	C4	C5	C6	C7	C8	C9
Heat treatment	625	625	625	625	625	625
temp. (° C.)
Heat treatment	2	2	2	2	2	2
time (hr.)
L*	83	86.74	88.94	87.28	78.03	80.49
a*	11.39	9.76	6.92	9.09	5.04	6.25
b*	2.59	2.60	4.75	3.44	−9.39	−8.92
Observable color	red	red	red	red	purple	purple
Glass Article	A37	A38	A39	A40	A41	A42
Composition	C15	C16	C17	C18	C19	C20
Heat treatment	625	625	625	625	625	625
temp. (° C.)
Heat treatment	2	2	2	2	2	2
time (hr.)
L*	84.25	85.21	85.58	87.5	87.39	86.09
a*	10.89	10.87	10.81	8.98	8.76	9.27
b*	−0.89	0.55	0.90	4.56	5.39	8.00
Observable color	magenta	red	red	orange	orange	orange
Glass Article	A43	A44	A45	A46	A47	A48
Composition	C22	C23	C15	C16	C17	C18
Heat treatment	625	625	650	650	650	650
temp. (° C.)
Heat treatment	2	2	2	2	2	2
time (hr.)
L*	90.31	95.7	84.63	85.69	86.23	87.42
a*	5.73	0.89	11.19	11.18	10.85	9.14
b*	3.85	1.49	−0.12	1.22	1.47	4.40
Observable color	orange	orange	magenta	red	red	orange
Glass Article	A49	A50	A51	A52
Composition	C19	C20	C22	C23
Heat treatment	650	650	650	650
temp. (° C.)
Heat treatment	2	2	2	2
time (hr.)
L*	87.42	86.18	90.14	95.53
a*	8.84	9.28	6.00	1.04
b*	5.24	8.10	3.89	1.42
Observable color	orange	orange	orange	orange

Referring now to Table 13, example glass articles A53-A114 were formed from example compositions C1-C14 and C24-C26 shown in Table 11 and were subjected to heat treatment at the temperature and for the period of time shown in Table 13. The observable colors of the resultant colored glass articles are shown in Table 13.

TABLE 13
Glass Article	A53	A54	A55	A56	A57	A58
Composition	C1	C2	C3	C4	C5	C6
Heat treatment	550	550	550	550	550	550
temp. (° C.)
Heat treatment	2	2	2	2	2	2
time (hr.)
Observable color	red	clear,	clear,	clear	clear	red
		red	red
Glass Article	A59	A60	A61	A62	A63	A64
Composition	C7	C8	C9	C10	C11	C12
Heat treatment	550	550	550	550	550	550
temp. (° C.)
Heat treatment	2	2	2	2	2	2
time (hr.)
Observable color	red	clear	clear,	clear	clear	clear
			pink
Glass Article	A65	A66	A67	A68	A69	A70
Composition	C13	C14	C24	C1	C2	C3
Heat treatment	550	550	550	575	575	575
temp. (° C.)
Heat treatment	2	2	8	2	2	2
time (hr.)
Observable color	clear	clear,	purple	orange	orange	red
		purple
Glass Article	A71	A72	A73	A74	A75	A76
Composition	C4	C5	C6	C7	C8	C9
Heat treatment	575	575	575	575	575	575
temp. (° C.)
Heat treatment	2	2	2	2	2	2
time (hr.)
Observable color	purple	purple	red	red	clear,	clear,
					red	pink
Glass Article	A77	A78	A79	A80	A81	A82
Composition	C10	C11	C12	C13	C14	C24
Heat treatment	575	575	575	575	575	575
temp. (° C.)
Heat treatment	2	2	2	2	2	2
time (hr.)
Observable color	clear,	clear,	clear,	clear,	clear,	purple
	purple	purple	purple	purple	red
Glass Article	A83	A84	A85	A86	A87	A88
Composition	C25	C26	C24	C25	C1	C2
Heat treatment	575	575	575	575	600	600
temp. (° C.)
Heat treatment	2	2	8	8	2	2
time (hr.)
Observable color	purple	red	red	red	orange	orange
Glass Article	A89	A90	A91	A92	A93	A94
Composition	C3	C4	C5	C6	C7	C8
Heat treatment	600	600	600	600	600	600
temp. (° C.)
Heat treatment	2	2	2	2	2	2
time (hr.)
Observable color	red	purple	purple	red	red	purple
Glass Article	A95	A96	A97	A98	A99	A100
Composition	C9	C10	C11	C12	C13	C14
Heat treatment	600	600	600	600	600	600
temp. (° C.)
Heat treatment	2	2	2	2	2	2
time (hr.)
Observable color	purple	purple	purple	purple	purple	orange
Glass Article	A101	A102	A103	A104	A105	A106
Composition	C24	C25	C26	C24	C25	C26
Heat treatment	600	600	600	625	625	625
temp. (° C.)
Heat treatment	2	2	2	2	2	2
time (hr.)
Observable color	purple	red	red	red	red	red
Glass Article	A107	A108	A109	A110	A111	A112
Composition	C10	C11	C12	C13	C14	C24
Heat treatment	650	650	650	650	650	650
temp. (° C.)
Heat treatment	2	2	2	2	2	2
time (hr.)
Observable color	purple	purple	clear,	purple	orange	red
			purple
Glass Article	A113	A114
Composition	C25	C26
Heat treatment	650	650
temp. (° C.)
Heat treatment	2	2
time (hr.)
Observable color	red	red

Referring now to FIGS. 7 and 8, plots show the relationship of R₂O—Al₂O₃ and a* and b*, respectively, of example glass articles A29-A44. As shown in FIG. 7, a* was a positive number, regardless of the R₂O—Al₂O₃ value, thereby resulting in observable colors towards red side of the CIELAB color space. As shown in FIG. 8, as R₂O—Al₂O₃ increased, b* increased, thereby shifting the observable colors from blue to yellow. For example, example glass articles A35 and A36, formed from example compositions C8 and C9 having an analyzed R₂O—Al₂O₃ of 0.07 mol % and 0.04 mol %, respectively, had a b* of −9.39 and −8.92, respectively, resulting in observably purple glass articles. Example glass articles A29 and A30, formed from example glass compositions C2 and C3 having an analyzed R₂O—Al₂O₃ of 2.98 mol % and 2.02 mol %, respectively, had a b* of 9.97 and 10.51, respectively, resulting in an observably orange glass article and an observably red glass article.

Moreover, example glass articles A33 and A34, formed from example glass compositions C6 and C7 including Fe₂O₃ and ZrO₂, respectively, had an observable red color.

As indicated by Tables 12 and 13 and FIGS. 7 and 8, the analyzed R₂O—Al₂O₃ may be adjusted, additional components may be added to the glass composition, and the glass article may be subjected to a certain heat treatment to provide a desired colored glass article.

Table 14 shows example glass compositions (in terms of mol %) containing Cr₂O₃ as a colorant and the transmittance color coordinate in the CIELAB color space, as measured at an article thickness of 1.5 mm under F2 illumination and a 100 standard observer angle, of the resultant colored glass articles.

TABLE 14
Example	Cr-1	Cr-2	Cr-3	Cr-4	Cr-5	Cr-6
SiO2	58.78	58.30	58.52	58.97	58.26	58.52
Al2O3	16.68	16.35	16.50	16.41	16.38	16.56
B2O3	5.93	5.93	6.01	5.98	5.93	6.04
Li2O	11.74	9.86	9.93	9.89	9.85	9.89
Na2O	6.26	4.25	4.27	4.27	4.26	4.30
K2O	0.48	0.48	0.48	0.49	0.48	0.49
MgO	0.02	2.91	2.95	2.91	2.94	2.93
CaO	0.01	0.01	0.01	0.01	0.01	0.02
ZnO	—	1	1.01	1	1	1.05
TiO2	0.01	0.01	0.01	0.01	0.01	0.01
NiO	—	—	0.023	0.012	0.043	0.089
Co3O4	—	0.001	0.002	0.002	0.03	0.048
CuO	—	0.83	0.233	0.037	0.785	0.044
Cr2O3	0.098	0.068	0.038	0.002	0.016	0.008
R2O	18.48	14.59	14.68	14.65	14.59	14.68
R′O	0.03	3.92	3.97	3.92	3.95	4
R2O + R′O − Al2O3	1.83	2.16	2.15	2.16	2.16	2.12
MgO + ZnO	0.02	3.91	3.96	3.91	3.94	3.98
Al2O3 + MgO + ZnO	16.7	20.26	20.46	20.32	20.32	20.54
Transmittance Color Coordinate
L*	83.78	77.06	85.88	94.99	66.99	62.17
a*	−12.60	−26.24	−9.49	−0.45	−10.12	−2.12
b*	62.26	8.74	6.26	0.17	−14.19	−20.39
Example	Cr-7	Cr-8	Cr-9	Cr-10	Cr-11	Cr-12
SiO2	57.09	59.21	58.44	58.12	59.20	58.36
Al2O3	16.10	16.64	16.21	16.56	16.58	16.11
B2O3	5.90	5.62	5.70	6.07	5.67	5.69
Li2O	9.68	11.75	11.56	11.83	11.82	11.6
Na2O	4.21	6.18	6.09	6.21	6.16	6.07
K2O	0.47	0.47	0.47	0.48	0.45	0.46
MgO	2.86	0.02	0.02	0.02	0.02	0.02
CaO	0.02	0.01	0.01	0.01	0.01	0.01
ZnO	0.98	—	—	—	—	—
TiO2	—	0.01	—	0.01	0.01	—
NiO	0.014	0.078	0.039	0.071	—	—
Co3O4	0.058	0.001	0.001	0.002	0.002	0.038
CuO	2.598	0.002	1.351	0.563	0.086	1.583
Cr2O3	0.006	0.009	0.102	0.051	0.002	0.051
R2O	14.36	18.4	18.12	18.52	18.43	18.13
R′O	3.86	0.03	0.03	0.03	0.03	0.03
R2O + R′O − Al2O3	2.12	1.79	1.94	1.99	1.88	2.05
MgO + ZnO	3.84	0.02	0.02	0.02	0.02	0.02
Al2O3 + MgO + ZnO	19.94	16.66	16.23	16.58	16.6	16.13
Transmittance Color Coordinate
L*	38.41	89.31	89.27	76.84	94.52	41.28
a*	−14.36	−0.65	−0.77	−14.83	−1.14	−18.17
b*	−13.36	17.15	17.45	11.73	−2.04	−13.89
Example	Cr-13	Cr-14	Cr-15	Cr-16	Cr-17	Cr-18
SiO2	58.03	58.39	58.48	58.45	58.58	58.71
Al2O3	16.57	16.49	16.53	16.49	16.42	16.54
B2O3	6.03	6.01	6.09	6.04	5.97	5.99
Li2O	11.93	10.02	10.08	10.04	10.5	10.48
Na2O	6.23	4.28	4.26	4.25	4.71	4.76
K2O	0.48	0.48	0.49	0.48	0.48	0.49
MgO	0.02	2.95	2.94	2.94	0.96	0.97
CaO	0.01	0.02	0.01	0.02	0.98	0.98
ZnO	—	1.01	1.01	1.01	0.99	1.02
TiO2	0.01	0.01	0.01	0.01	0.01	0.01
NiO	0.093	0.021	—	0.082	0.019	—
Co3O4	0.072	0.002	0.002	0.048	0.002	0.002
CuO	0.516	0.278	0.091	0.137	0.339	0.054
Cr2O3	0.012	0.036	0.001	0.006	0.039	0.001
R2O	18.64	14.78	14.83	14.77	15.69	15.73
R′O	0.03	3.98	3.96	3.97	2.93	2.97
R2O + R′O − Al2O3	2.1	2.27	2.26	2.25	2.2	2.16
MgO + ZnO	0.02	3.96	3.95	3.95	1.95	1.99
Al2O3 + MgO + ZnO	16.59	20.45	20.48	20.44	18.37	18.53
Transmittance Color Coordinate
L*	38.93	85.89	95.05	62.68	85.25	95.29
a*	1.10	−9.54	−0.84	−2.13	−10.39	−0.68
b*	−44.38	5.68	−0.62	−20.72	6.20	−0.90
Example	Cr-19
SiO2	58.51
Al2O3	16.49
B2O3	6.06
Li2O	10.47
Na2O	4.76
K2O	0.49
MgO	0.97
CaO	0.99
ZnO	1.01
TiO2	0.01
NiO	0.085
Co3O4	0.048
CuO	0.111
Cr2O3	0.005
R2O	15.72
R′O	2.97
R2O + R′O − Al2O3	2.2
MgO + ZnO	1.98
Al2O3 + MgO + ZnO	18.47
Transmittance Color Coordinate
L*	61.08
a*	−2.34
b*	−22.51

As indicated by the example glass compositions and colored glass articles in Table 14, the glass compositions described herein improve Cr₂O₃ solubility to form colored glass articles having the desired color. For example, example glass composition Cr-1 including 0.098 mol % Cr₂O₃ formed a colored glass article having a transmittance color coordinate in the CIELAB color space of L*=83.78, a*=−12.60, and b*=62.26.

As further indicated by the example glass compositions and colored glass articles in Table 14, adding other colorants in addition to Cr₂O₃ as described herein allows different color gamuts to be achieved. For example, example glass composition Cr-2 including 0.068 mol % Cr₂O₃, 0.001 mol % Co₃O₄, and 0.83 mol % CuO formed a colored glass article have a transmittance color coordinate in the CIELAB color space of L*=77.06, a*=−26.24, and b*=8.74. Example glass composition Cr-3, including 0.038 mol % Cr₂O₃, 0.023 mol % NiO, 0.002 mol % Co₃O₄, and 0.233 mol % CuO formed a colored glass article have a transmittance color coordinate in the CIELAB color space of L*=85.88, a*=−9.40, and b*=6.26.

Referring now to FIGS. 9-32, projected color gamuts were modeled for glass compositions containing Cr₂O₃ as a colorant. The modeled compositions included Cr₂O₃ as the sole colorant as well as Cr₂O₃ in combination with NiO, Co₃O₄, CuO, and various combinations thereof.

Referring now to FIGS. 9-11, a projected color gamut for a glass composition including only Cr₂O₃ as a colorant is shown. As illustrated, a single colorant generates a line in the CIELAB color space. The points along the line correspond to different levels of Cr₂O₃ concentration from 0 mol % to 2 mol %. The arrows indicate the directions of increasing concentration. The Cr₂O₃ color gamut projects that a colored glass article having greater than or equal to 0 mol % and less than or equal to 2 mol % Cr₂O₃ may have a transmittance color coordinate in the CIELAB color space, as measured at an article thickness of 1.5 mm under F2 illumination and a 100 standard observer angle, of L*greater than or equal to 0 and less than or equal to 100, a* greater than or equal to −18 and less than or equal to 0, and b* greater than or equal to 0 and less than or equal to 82.

Different color gamuts may be achieved by including other colorants in addition to Cr₂O₃. Referring now to FIGS. 12-14, a projected color gamut for a glass composition including Cr₂O₃ and NiO as colorants is shown. As illustrated, two colorants generate a surface in the CIELAB color space. The Cr₂O₃/NiO color gamut projects that a colored glass article having greater than or equal to 0 mol % and less than or equal to 2 mol % Cr₂O₃ and greater than or equal to 0 mol % and less than or equal to 4 mol % NiO may have a transmittance color coordinate in the CIELAB color space, as measured at an article thickness of 1.5 mm under F2 illumination and a 10° standard observer angle, of L*greater than or equal to 0 and less than or equal to 100, a* greater than or equal to −18 and less than or equal to 18, and b* greater than or equal to 0 and less than or equal to 82.

Referring now to FIGS. 15-17, a projected color gamut for a glass composition including Cr₂O₃ and Co₃O₄ as colorants is shown. As illustrated, two colorants generate a surface in the CIELAB color space. The Cr₂O₃/Co₃O₄ color gamut projects that a colored glass article having greater than or equal to 0 mol % and less than or equal to 2 mol % Cr₂O₃ and greater than or equal to 0 mol % and less than or equal to 2 mol % Co₃O₄ may have a transmittance color coordinate in the CIELAB color space, as measured at an article thickness of 1.5 mm under F2 illumination and a 100 standard observer angle, of L*greater than or equal to 0 and less than or equal to 100, a* greater than or equal to −20 and less than or equal to 60, and b* greater than or equal to −90 and less than or equal to 85.

Referring now to FIGS. 18-20, a projected color gamut for a glass composition including Cr₂O₃ and CuO as colorants is shown. As illustrated, two colorants generate a surface in the CIELAB color space. The Cr₂O₃/CuO color gamut projects that a colored glass article having greater than or equal to 0 mol % and less than or equal to 2 mol % Cr₂O₃ and greater than or equal to 0 mol % and less than or equal to 20 mol % CuO may have a transmittance color coordinate in the CIELAB color space, as measured at an article thickness of 1.5 mm under F2 illumination and a 10° standard observer angle, of L*greater than or equal to 0 and less than or equal to 100, a* greater than or equal to −35 and less than or equal to 0, and b* greater than or equal to 0 and less than or equal to 82.

Referring now to FIGS. 21-23, a projected color gamut for a glass composition including Cr₂O₃, NiO, and CuO as colorants is shown. As illustrated, three colorants create a volume in the CIELAB color space. The Cr₂O₃/NiO/CuO color gamut projects that a colored glass article having greater than or equal to 0 mol % and less than or equal to 2 mol % Cr₂O₃, greater than or equal to 0 mol % and less than or equal to 4 mol % NiO, and greater than or equal to 0 mol % and less than or equal to 20 mol % CuO may have a transmittance color coordinate in the CIELAB color space, as measured at an article thickness of 1.5 mm under F2 illumination and a 10° standard observer angle, of L*greater than or equal to 0 and less than or equal to 100, a* greater than or equal to −35 and less than or equal to 20, and b* greater than or equal to 0 and less than or equal to 75.

Referring now to FIGS. 24-26, a projected color gamut for a glass composition including Cr₂O₃, NiO, and Co₃O₄ as colorants is shown. As illustrated, three colorants create a volume in the CIELAB color space. The Cr₂O₃/NiO/Co₃O₄ color gamut projects that a colored glass article having greater than or equal to 0 mol % and less than or equal to 2 mol % Cr₂O₃, greater than or equal to 0 mol % and less than or equal to 4 mol % NiO, and greater than or equal to 0 mol % and less than or equal to 2 mol % Co₃O₄ may have a transmittance color coordinate in the CIELAB color space, as measured at an article thickness of 1.5 mm under F2 illumination and a 100 standard observer angle, of L*greater than or equal to 0 and less than or equal to 100, a* greater than or equal to −15 and less than or equal to 65, and b* greater than or equal to −90 and less than or equal to 80.

Referring now to FIGS. 27-29, a projected color gamut for a glass composition including Cr₂O₃, CuO, and Co₃O₄ as colorants is shown. As illustrated, three colorants create a volume in the CIELAB color space. The Cr₂O₃/CuO/Co₃O₄ color gamut projects that a colored glass article having greater than or equal to 0 mol % and less than or equal to 2 mol % Cr₂O₃, greater than or equal to 0 mol % and less than or equal to 20 mol % CuO, and greater than or equal to 0 mol % and less than or equal to 2 mol % Co₃O₄ may have a transmittance color coordinate in the CIELAB color space, as measured at an article thickness of 1.5 mm under F2 illumination and a 10° standard observer angle, of L*greater than or equal to 0 and less than or equal to 100, a* greater than or equal to −35 and less than or equal to 60, and b* greater than or equal to −90 and less than or equal to 80.

Referring now to FIGS. 30-32, a projected color gamut for a glass composition including Cr₂O₃, NiO, CuO, and Co₃O₄ as colorants is shown. As illustrated, four colorants create an overlapping volume in the CIELAB color space. The Cr₂O₃/NiO/CuO/Co₃O₄ color gamut projects that a colored glass article having greater than or equal to 0 mol % and less than or equal to 2 mol % Cr₂O₃, greater than or equal to 0 mol % and less than or equal to 4 mol % NiO, greater than or equal to 0 mol % and less than or equal to 20 mol % CuO, and greater than or equal to 0 mol % and less than or equal to 2 mol % Co₃O₄ may have a transmittance color coordinate in the CIELAB color space, as measured at an article thickness of 1.5 mm under F2 illumination and a 10° standard observer angle, of L*greater than or equal to 0 and less than or equal to 100, a* greater than or equal to −35 and less than or equal to 60, and b* greater than or equal to −90 and less than or equal to 80.

Tables 15 and 16 show example glass compositions (in terms of mol %) containing Ag as a colorant.

TABLE 15
Example
(mol %)	Ag-1	Ag-2	Ag-3	Ag-4	Ag-5	Ag-6	Ag-7	Ag-8	Ag-9	Ag-10	Ag-11	Ag-12	Ag-13	Ag-14	Ag-15
SiO2	59.55	60.05	60.55	60.00	59.95	59.90	60.10	60.00	59.85	60.16	60.09	59.79	59.47	59.45	57.55
Al2O3	16.50	16.50	16.50	16.50	16.50	16.50	16.50	16.50	16.50	15.90	15.93	15.89	15.82	16.50	16.50
B2O3	6.00	6.00	6.00	6.00	6.00	6.00	6.00	6.00	6.00	6.08	6.06	6.04	5.99	6.00	6.00
Li2O	12.00	12.00	12.00	12.00	12.00	12.00	12.00	12.00	12.00	11.99	11.97	11.97	11.92	12.00	12.00
Na2O	5.70	5.20	4.70	5.20	5.20	5.20	5.20	5.20	5.20	5.41	5.41	5.89	6.37	5.50	6.50
K2O	—	—	—	—	—	—	—	—	—	0.20	0.20	0.20	0.19	0.20	0.20
SnO2	0.10	0.10	0.10	0.10	0.10	0.10	0.10	0.10	0.10	0.11	0.11	0.11	0.10	0.20	0.10
Ag	0.15	0.15	0.15	0.15	0.15	0.15	0.10	0.10	0.25	0.15	0.25	0.12	0.13	0.15	0.15
CeO2	—	—	—	0.05	0.10	0.15	—	0.10	0.10	—	—	—	—	—	—
Nd2O3	—	—	—	—	—	—	—	—	—	—	—	—	—	—	1.00
Er2O3	—	—	—	—	—	—	—	—	—	—	—	—	—	—	—
R2O—Al2O3	1.20	0.70	0.20	0.70	0.70	0.70	0.70	0.70	0.70	1.70	1.64	2.16	2.66	1.20	2.20

TABLE 16
Example
(mol %)	Ag-16	Ag-17	Ag-18	Ag-19	Ag-20	Ag-21	Ag-22	Ag-23	Ag-24	Ag-25	Ag-26	Ag-27	Ag-28	Ag-29
SiO2	57.55	59.1	59.05	59.41	59.31	59.36	59.26	58.91	58.81	59.41	59.01	58.55	58.7	59.7
Al2O3	16.50	16.00	16.00	15.97	15.97	15.97	15.97	15.97	15.97	15.97	15.89	16.5	16.4	16.5
B2O3	6.00	6.00	6.00	6.00	6.00	6.00	6.00	6.00	6.00	6.00	6.00	6	6	6
Li2O	12.00	12.00	12.00	12.00	12.00	12.00	12.00	12.00	12.00	12.00	12.00	12	12	12
Na2O	6.50	6.50	6.50	6.17	6.17	6.17	6.17	6.67	6.67	6.17	6.65	6.5	6.5	5.5
K2O	0.20	0.20	0.20	0.20	0.20	0.20	0.20	0.20	0.20	0.20	0.20	0.2	0.2	0.2
SnO2	0.10	0.10	0.10	0.10	0.20	0.10	0.20	0.10	0.20	0.10	0.10	0.1	0.1	0.1
Ag	0.15	0.10	0.15	0.15	0.15	0.20	0.20	0.15	0.15	0.15	0.15	0.15	0.15	0.15
CeO2	—	—	—	—	—	—	—	—	—	—	—	—	—
Nd2O3	—	—	—	—	—	—	—	—	—	—	—	—	—
Er2O3	1.00	—	—	—	—	—	—	—	—	—	—	—	—
R2O—Al2O3	2.20	2.70	2.70	2.40	2.40	2.40	2.40	2.90	2.90	2.40	2.96	2.2	2.3	1.2

The exemplary glass compositions of Tables 15 and 16 were used to produce glass coupons. These glass coupons were inserted into pre-heated, ambient-air electric ovens, held for a desired amount of time, and cooled in air to produce colored glass coupons. It should be noted that some glasses were heated at a particular ramp rate and/or cooled at a controlled rate; however, it was determined that neither the ramp rate nor cooling rate affected color generation.

Plots of CIELAB spaces of colored glass coupons produced from Examples Ag-1 and Ag-9 are depicted in FIG. 33A (a* vs. L*), FIG. 33B (b* vs. L*), and FIG. 33C (a* vs. b*). Sample sets having thicknesses of 0.6 mm, 1.33 mm, and 2.06 mm were made from each composition and the samples were heat treated at various heat treatment times (575° C., 600° C., 625° C., 650° C.) and various heat treatment times (1 hour, 2 hours) to produce colored glass articles having the CIELAB L*, a*, b* values indicated in FIGS. 33A-33C.

Plots of projected CIELAB spaces of colored glass coupons produced from Examples Ag-10-Ag-12 are depicted in FIG. 34A (a* vs. L*), FIG. 34B (b* vs. L*), and FIG. 34C (a* vs. b*). Sample sets having thicknesses of 0.6 mm, 1.33 mm, and 2.06 mm were made from each composition and the samples were heat treated at various heat treatment times (575° C., 600° C., 625° C., 650° C.) and various heat treatment times (1 hour, 2 hours) to produce colored glass articles having the CIELAB L*, a*, b* values indicated in FIGS. 34A-34C.

FIGS. 35 and 36 depict the absorbance spectra (determined from the transmittance spectra T where the absorbance A=log₁₀ (1/T)) of colored glass coupons produced from Examples Ag-1 and Ag-9, respectively. Specifically, the absorbance spectra of glass coupons formed from the compositions of Examples Ag-1 and Ag-9 were collected from coupons in: as-made condition (no heat treatment); after exposure to a heat treatment of 600° C. for 2 hours; after exposure to a heat treatment of 600° C. for 3 hours; after exposure to a heat treatment of 625° C. for 2 hours; after exposure to a heat treatment of 625° C. for 3 hours; and after exposure to a heat treatment of 650° C. for 3 hours. As shown in FIGS. 35 and 36, the absorbance spectra varied considerably with changes in heat treatment temperature and heat treatment time.

FIGS. 37, 38 and 39 depict the absorbance spectra of colored glass coupons produced from Examples Ag-10-Ag-12, respectively. Specifically, the absorbance spectra of glass coupons formed from the compositions of examples Ag-10-Ag-12 were collected from coupons in: after exposure to a heat treatment of 575° C. for 2 hours; after exposure to a heat treatment of 600° C. for 1 hours; after exposure to a heat treatment of 600° C. for 2 hours; after exposure to a heat treatment of 600° C. for 3 hours; after exposure to a heat treatment of 625° C. for 1 hour; after exposure to a heat treatment of 630° C. for 4 hours; and after exposure to a heat treatment of 650° C. for 0.5 hour. As shown in FIGS. 37-39, the absorbance spectra varied considerably with changes in heat treatment temperature and heat treatment time.

FIGS. 40A-40C are plots of CIELAB spaces of colored glass coupons produced from Example Ag-16 containing erbium. Specifically FIG. 40A is a plot of a* vs. L*, FIG. 40B is a plot b* vs. L*, and FIG. 40C is a plot of a* vs. b*. Sample sets having thicknesses of −0.6 mm, −1.33 mm, and −2.06 mm were made from the composition and heat treated at various heat treatment temperatures and various heat treatment times (as indicated in Table 17) to produce colored glass articles having the CIELAB L*, a*, b* values indicated in FIGS. 40A-40C. The CIELAB space plots indicate that an entirely new range of colors can be achieved by adding erbium to the composition. FIG. 41 depicts the absorbance spectra of example Ag-16 in as-made condition (priorto heat treatment); after heattreatment at 565° C. for 15 minutes; and after heat treatment at 575° C. after 20 minutes.

TABLE 17
	Heat Treatment
	(Temp (° C.)/
	Time (minutes)/
	Ramp Rate	Thickness
Example	(° C./min))	(mm)	L*	a*	b*
Ag-16	as made	0.60	95.09	4.58	−1.73
Ag-16	575/20/10	0.57	94.76	3.32	1.91
Ag-16	565/15/10	0.60	95	4.26	−0.83
Ag-16	as made	1.34	93.7	8.44	−3.23
Ag-16	575/20/10	1.32	92.03	3.62	13.15
Ag-16	565/15/10	1.32	93.51	7.83	−1.61
Ag-16	as made	2.06	92.66	10.98	−4.12
Ag-16	575/20/10	2.03	91.28	7.96	6.77
Ag-16	565/15/10	2.04	92.25	9.9	−0.62

FIGS. 42A-42C are plots of CIELAB spaces of colored glass coupons produced from Example Ag-13. In particular, coupons of glass formed from the composition of Example Ag-13 includes R₂O—Al₂O₃ values in the range between 2.5 and 3 mol %, specifically 2.66 mol %. The samples were heat treated at various heat treatment temperatures and heat treatment times to produce colored glass articles having a range of colors including green, brown, maroon, purple and pink, as indicated in the CIELAB spaces of FIGS. 42A-42C.

FIG. 43 is the absorbance spectra of Example Ag-13 for heat treatments at 635° C. for 20 minutes; 635° C. for 30 minutes; and 635° C. for 40 minutes. The heat treatment conditions produced a colored glass article that was green in color. As shown in FIG. 43 the absorbance spectra had two distinct peaks arising from the formation of anisotropic silver particles that support two distinct plasmon resonances. FIGS. 44A-44C are TEM micrographs of the anisotropic silver particles in the green glass formed from Example Ag-13 and show the random orientation of the anisotropic particles (FIG. 44A) and that the silver particles have an aspect ratio greater than 1 (FIGS. 44B and 44C).

As discussed herein, the R₂O—Al₂O₃ value of a composition influences both isotropic and anisotropic particle formation during heat treatment and hence the color of the resultant glass. When R₂O—Al₂O₃<<1 (i.e., 0.2 mol % or less), virtually no color is formed in the glass upon heat treatment. This is demonstrated by Example Ag-3, which has an R₂O—Al₂O₃ value of 0.2 mol %. Irrespective of heat treatment, the glass of Example Ag-3 remained nearly colorless and transparent after heat treatment. However, when the R₂O—Al₂O₃ value is increased to 0.7 mol % (as with glasses formed from Example Ag-2) and then to 1.2 mol % (as with glasses formed from Example Ag-1), a progressively broader and more saturated range of colors were produced by heat treatment.

Referring now to FIG. 45, a transmittance spectrum is shown for 1.3 mm coupons of glass formed from Example Ag-1 and heat treated at the same heat treatment temperature (600° C.) for different heat treatment times (1, 2, or 3 hours). The different heat treatment conditions yielded colored glass articles of different colors (yellow (solid line in FIG. 45), orange (dotted line in FIG. 45), and red (dashed line in FIG. 45), respectively), each of which had different transmittance spectra over the visible light range, as indicated in FIG. 45, with yellow samples being the most transparent and the red samples the least.

Referring now to FIG. 46, a transmittance spectrum is shown for a 1.3 mm coupon of glass formed from Example Ag-1 and heat treated at a heat treatment temperature of 650° C. for a heat treatment time of 1 hour, producing a colored glass article that was brown in color. As noted herein, colored glass articles that are brown in color can be produced by heat treatment at temperatures between 640° C. and 660° C. for heat treatment times between 30 and 90 minutes.

Referring now to FIG. 47, a transmittance spectrum is shown for a 1.3 mm coupon of glass formed from Example Ag-21 and heat treated with an initial heat treatment of 450° C. for 1 our followed by a second heat treatment of 635° C. for 1 hour, producing a colored glass article that was purple in color. It was determined that the initial heat treatment was not needed to produce color in the sample. As noted herein, colored glass articles that are purple in color can be produced by heat treatment at temperatures between 625° C. and 650° C. for heat treatment times between 30 and 90 minutes.

Referring now to Table 18 and FIG. 48, colored glass articles in the form of glass coupons were produced from the glass compositions of Tables 15 and 16. The glass coupons had thicknesses from ˜0.5 mm to ˜1.4 mm and were heat treated at various times and temperatures (as specified in Table 18) to produce colored glass articles with different color hues. PHCFR means that the glass coupon was placed directly into a pre-heated furnace, held for the indicated time, at which point the furnace was switched off and the glass coupon was cooled in the furnace at the cooling rate of the furnace (typically 2-3° C./minute). PHAC means that the glass coupon was placed directly into a pre-heated furnace, held for the indicated time, then removed and allowed to cool back to room temperature in ambient air. The CIELAB L*, a*, and b* coordinates of each colored glass article were determined and the a*, b* color coordinates were plotted as depicted in FIG. 48, where the x-axis is the a* coordinate and the y-axis is the b* coordinate. For reference, the L*coordinate (not depicted) is along an axis orthogonal to both the x-axis and the y-axis of FIG. 48 and extends through the point a*=0 and b*=0.

TABLE 18
	Heat Treatment
	(Temp (° C.)/
	Time (hours)/
	Ramp Rate	Thickness
Example	(° C./min))	(mm)	L*	a*	b*
Ag-10	600/3/10	1.33	88.3	−2.26	65.85
Ag-10	600/3/10	1.29	90.44	−3.88	51.15
Ag-11	575/2/10	1.29	80.43	5.3	94.46
Ag-11	575/2/10	1.32	81.29	3.96	93.62
Ag-10	600/2/10	1.31	92.72	−2.81	29.07
Ag-10	600/2/10	1.28	92.55	−3.22	30.79
Ag-10	625/2/10	1.32	83.97	7.32	53.78
Ag-10	625/2/10	1.32	79.43	12.07	62
Ag-27	600/0.5/PHCFR	1.26	89.41	−8.22	57.36
Ag-27	600/0.75/PHCFR	1.35	83.95	−2.24	85.2
Ag-27	600/1/PHCFR	1.32	79.51	4.83	96
Ag-9	600/1/PHAC	1.31	77.86	12.16	106.74
Ag-9	600/2/PHAC	1.31	73.48	18.67	108.37
Ag-1	600/1/10	1.29	78.31	13	104.03
Ag-13	635/0.3/10	0.61	78.07	16.01	101.22
Ag-11	635/0.5/10	0.59	76.1	18.64	111.37
Ag-23	625/0.5/10	1.28	86.72	−2.66	91.23
Ag-23	450/1/10	1.25	81.15	6.31	103.91
Ag-21	575/2/10	1.16	90.82	−7.55	56.94
Ag-23	575/2/10	1.23	90.94	−9.74	52.14
Ag-23	575/3/10	1.35	83.93	−2.13	87.35
Ag-23	600/1/10	1.33	88.97	−7.73	76.89
Ag-23	625/0.75/10	1.37	77.37	13.14	107.83
Ag-23	650/0.3/10	1.32	83.6	3.6	98.53
Ag-23	615/0.5/10	1.33	90.72	−11.12	66.64
Ag-23	615/1/10	1.29	78.19	13.1	108.41
Ag-23	640/0.5/10	1.25	73.27	21.82	101.59
Ag-23	650/0.5/10	1.29	77.89	7.06	92.68
Ag-22	575/3/10	1.34	78.23	13.57	100.58
Ag-24	575/3/10	1.34	89.53	1.16	40.46
Ag-20	625/2/10	1.37	83.21	9.05	39.01
Ag-19	575/4/10	1.35	83.86	10.63	45.29
Ag-22	600/1/10	1.31	83.83	10.63	46.05
Ag-21	615/0.5/10	1.35	63.83	21.26	79.15
Ag-23	635/0.6/10	1.26	69.96	24.92	104.44
Ag-27	600/1.25/PHCFR	1.31	69.76	24.11	109.37
Ag-21	575/3/10	1.35	75.48	20.79	106.6
Ag-11	600/1/10	1.32	71.5	21.65	110.29
Ag-11	600/1/10	1.33	70.48	23.07	110.67
Ag-9	625/1/PHAC	1.31	79.96	15.43	62.16
Ag-22	575/2/10	1.20	91.99	−4.71	37.28
Ag-11	650/0.5/10	1.35	93.59	−10.87	39.72
Ag-1	600/2/PHAC	1.31	81.94	14.76	45.2
Ag-12	600/2/10	1.34	82.02	14.23	39.93
Ag-12	600/2/10	1.31	82.6	12.96	41.47
Ag-27	600/0.25/PHCFR	1.31	93.01	−7.93	33.76
Ag-11	600/3/10	1.34	53.38	36.16	89.47
Ag-12	600/3/10	1.32	71.89	26.88	63.17
Ag-12	600/3/10	1.33	72.44	26.28	61.16
Ag-11	600/2/10	1.30	61.58	30.81	101
Ag-11	600/2/10	1.32	60.37	32.13	100.26
Ag-11	625/1/10	1.33	56.78	40.08	95.88
Ag-11	625/1/10	1.35	58.43	38.04	98.02
Ag-1	600/3/PHAC	1.32	60.97	36.89	57.26
Ag-9	625/2/PHAC	1.32	61.72	41.44	100.95
Ag-9	650/1/PHAC	1.32	57.39	33.25	43.5
Ag-1	600/2/10	1.33	54.05	46.56	90.95
Ag-1	600/3/10	1.32	57.71	37.75	53.96
Ag-9	600/3/10	1.32	49.88	47.94	84.03
Ag-11	635/0.3/10	1.36	63.67	36.89	105.88
Ag-11	635/0.5/10	1.32	60	39.32	100.53
Ag-11	630/0.6/10	0.59	67.2	32.97	110.25
Ag-11	650/0.5/10	0.56	61.12	27.94	74.46
Ag-21	600/1/10	1.33	74.55	21.53	41.51
Ag-22	625/1/10	1.35	57.25	32.53	43.57
Ag-22	625/2/10	1.35	39.71	34.72	46.35
Ag-22	575/4/10	1.37	66.13	32.1	107.91
Ag-23	575/4/10	1.37	61.84	37.63	102.88
Ag-22	600/2/10	1.28	64.47	34.95	82.43
Ag-23	600/2/10	1.25	58.86	39.89	98.15
Ag-22	600/3/10	1.24	62.11	37.06	96.27
Ag-22	635/1/10	1.27	54.92	30.14	34.44
Ag-22	635/2/10	1.28	42.76	29.96	47.39
Ag-22	650/30/10	1.31	47.96	24.34	42.2
Ag-11	600/3/10	1.32	43.41	41.48	73.52
Ag-9	600 0.5/10	1.33	72.32	25.62	43.19
Ag-24	575/4/10	1.35	73.2	19.64	35.14
Ag-11	625/2/10	1.31	21.62	46.36	36.66
Ag-11	625/2/10	1.30	28.68	48.69	48.74
Ag-27	600/1.5/PHCFR	1.31	46.01	53.51	77.81
Ag-9	600/3/PHAC	1.31	37.09	48.11	62.4
Ag-9	625/3/PHAC	1.29	27.58	50.33	46.01
Ag-11	650/0.5/10	1.35	34.47	49.12	57.71
Ag-21	600/2/10	1.27	25.15	38.39	41.98
Ag-23	600/3/10	1.23	35.28	29.5	16.99
Ag-23	635/1/10	1.27	29.58	37.33	46.53
Ag-9	600/2/10	1.31	40.56	48.66	68.35
Ag-21	575/4/10	1.36	46	51.36	75.97
Ag-11	630/0.6/10	1.35	43.57	50.81	73.87
Ag-22	615/1/10	1.31	45.53	48.19	73.96
Ag-23	625/1/10	1.35	32.52	37.79	42.15
Ag-12	625/2/10	1.31	40.9	42.34	45.72
Ag-12	625/2/10	1.31	40.92	34.87	38.77
Ag-10	575/2/10	1.28	95.61	−2.57	10.47
Ag-10	575/2/10	1.33	95.5	−2.51	10.73
Ag-12	575/2/10	1.30	95.46	−4.72	15.2
Ag-12	575/2/10	1.31	95.21	−4.78	16.2
Ag-10	600/1/10	1.29	94.06	−0.93	15.68
Ag-10	600/1/10	1.29	95.27	−1.08	9.58
Ag-1	575/1/PHAC	1.30	96.33	−2.88	7.92
Ag-9	575/1/PHAC	1.33	96.22	−1.88	6.36
Ag-13	635/0.5/10	0.59	65.97	−1.78	6.53
Ag-11	635/0.5/10	1.34	95.37	−0.8	8.8
Ag-11	635/0.5/10	0.61	95.46	−0.63	8.11
Ag-11	630/0.7/10	1.36	94.65	−1.36	13.6
Ag-11	630/0.7/10	0.57	96.13	−0.64	4.96
Ag-13	630/0.7/10	1.34	17.64	−0.13	9.52
Ag-10	650/0.5/10	0.57	93.1	−2.63	16.08
Ag-11	650/0.5/10	0.58	95.83	−6.92	18.3
Ag-13	635/0.6/10	0.50	68.86	−5.21	8.63
Ag-13	635/0.6/10	0.50	69.02	−4.23	10.36
Ag-19	625/0.6/10	1.28	91.48	−0.24	1.94
Ag-19	575/2/10	1.19	96.2	−1.67	5.92
Ag-20	575/2/10	1.18	96.23	−1.37	6.17
Ag-20	575/3/10	1.36	95.79	−1.76	8.63
Ag-20	575/4/10	1.35	94.03	−2.99	21.48
Ag-20	600/2/10	1.28	95.38	−0.5	8.66
Ag-20	635/2/10	1.29	93.27	−5.41	22.51
Ag-24	650/0.5/10	1.29	62.01	−3.99	25.51
Ag-24	645/0.5/10	1.22	53.04	−2.71	16.67
Ag-1	600/1/PHAC	1.30	94.18	−1.61	17.89
Ag-20	650/0.5/10	1.31	93.44	−5.26	21.04
Ag-24	575/2/10	1.21	94.46	−5.08	22.99
Ag-20	635/2/10	1.29	93.27	−5.41	22.51
Ag-19	575/3/10	1.33	94.25	−5.38	25.07
Ag-12	625/1/10	1.34	65.54	23.63	19.56
Ag-12	625/1/10	1.32	71.17	21.05	19.63
Ag-12	635/0.5/10	1.35	71.32	13.82	13.62
Ag-1	625/3/PHAC	1.32	65.21	24.02	22.49
Ag-12	635/0.5/10	1.35	64.18	18.22	17.04
Ag-12	635/0.3/10	1.35	79.6	9.04	7.31
Ag-13	635/0.3/10	1.34	38.54	15.27	11
Ag-12	635/0.5/10	1.34	80.09	10.51	7.99
Ag-12	630/0.7/10	1.37	72.96	14.97	10.44
Ag-12	630/0.7/10	0.57	87.75	6.18	4.56
Ag-13	650/0.5/10	1.36	4.61	15.13	5.16
Ag-22	625/0.5/10	1.29	74.16	17.2	20.72
Ag-21	(450/1/10) + (635/0.6/10)	1.26	60.75	10.74	2.34
Ag-24	(450/1/10) + (635/0.6/10)	1.26	81.63	5.11	0.83
Ag-21	625/1/10	1.33	21.04	16.09	2.81
Ag-24	625/1/10	1.35	69.03	7.33	0.15
Ag-20	635/0.6/10	1.28	89.93	6.67	9.6
Ag-21	635/0.6/10	1.28	51.58	13.43	4.69
Ag-24	635/0.6/10	1.27	78.17	7.73	2.76
Ag-21	600/3/10	1.27	24.57	12.39	7.72
Ag-19	635/1/10	1.28	84.58	3.58	3.24
Ag-21	635/1/10	1.26	40.14	10.14	−0.13
Ag-24	635/1/10	1.29	78.27	4.37	−0.11
Ag-20	640/0.5/10	1.27	89.29	7.12	9.32
Ag-21	640/0.5/10	1.28	39.19	13.64	0.14
Ag-22	640/0.5/10	1.26	67.68	20.56	21.8
Ag-13	650/0.5/10	0.55	50.65	20.25	15.66

As indicated in FIG. 48, the resultant colored glass articles may be grouped into regions of the a*-b* plot according to the hue of the colored glass article. That is, colored glass articles having similar color hues have combinations of discrete a* and b* values that fall within the same region of the a*-b* plot. In particular, colored glass articles that appear yellow have a*, b* values that fall within the region defined by the intersection of four lines: b*=0.2879·a*+27.818 (line A); b*=7.0833·a*−94.5 (line B); b*=0.45·a*+104.5 (line C); and b*=15.3·a*+253 (line D). The region defined by the intersection lines A, B, C, and D can be referred to as the “yellow region” and colored glass articles having combinations of discrete a* and b* values falling within this region will generally appear yellow.

Similarly, colored glass articles that appear orange have a*, b* values that fall within the region defined by the intersection of four lines: b*=7.0833·a*−94.5 (line B); b*=−0.9583·a*+146.75 (line E); b*=2.6957·a*−50.565 (line F); and b*=33 (line G). The region defined by the intersection lines B, E, F, and G can be referred to as the “orange region” and colored glass articles having combinations of discrete a* and b* values falling within this region will generally appear orange.

Still referring to FIG. 48, colored glass articles that appear red have a*, b* values that fall within the region defined by the intersection of four lines: b*=2.6957·a*−50.565 (line F); a*=54 (line H); b*=1.0769·a*−17.154 (line I); and b*=6.6667·a*−173.67 (line J). The region defined by the intersection lines F, H, I, and J can be referred to as the “red region” and colored glass articles having combinations of discrete a* and b* values falling within this region will generally appear orange.

Colored glass articles that appear green have a*, b* values that fall within the region defined by the intersection of four lines: b*=0.2879·a*+27.818 (line A); a*=0 (line K); b*=−1.375·a*+1 (line L); and b*=9.333·a*+86.667 (line M), exclusive of a* greater than −0.3 and less than 0.3 and exclusive of b* greater than −0.5 and less than 0.5. The region defined by the intersection lines A, L, K, and M can be referred to as the “green region” and colored glass articles having combinations of discrete a* and b* values falling within this region will generally appear green.

Colored glass articles that appear pink/purple have a*, b* values that fall within the region defined by the intersection of four lines: b*=0.0833·a*+20.833 (line N); b*=2.1182·a*−32.073 (line O); b*=−0.3 (line P); and b*=1.5929·a*−0.3 (line Q), exclusive of a* greater than −0.3 and less than 0.3 and exclusive of b* greater than −0.5 and less than 0.5. The region defined by the intersection lines N, O, P, and Q can be referred to as the “pink/purple region” and colored glass articles having combinations of discrete a* and b* values falling within this region will generally appear pink/purple.

Referring now to Table 19, colored glass articles in the form of glass coupons were produced from the glass compositions of Tables 15 and 16. The glass coupons had thicknesses from ˜0.5 mm to ˜1.4 mm and were heat treated at various times and temperatures (as specified in Table 19) to produce colored glass articles with different color hues. PHCFR means that the glass coupon was placed directly into a pre-heated furnace, held for the indicated time, at which point the furnace was switched off and the glass coupon was cooled in the furnace at the cooling rate of the furnace (typically 2-3° C./minute). PHAC means that the glass coupon was placed directly into a pre-heated furnace, held for the indicated time, then removed and allowed to cool back to room temperature in ambient air. The CIELAB L*, a*, and b* coordinates of each colored glass article were determined. The average transmittance (%) for each sample over the wavelength range from 380 nm to 750 nm was also determined. The results are reported in Table 19.

TABLE 19
	Heat		Average
	Treatment		Visible
	(Temp (° C.)/		Trans-
	Time (hours)/	Thick-	mittance
	Ramp Rate	ness	% (380-
Example	(° C./min))	(mm)	750 nm)	L*	a*	b*
Ag-10	575/2/10	1.28	86.1	95.61	−2.57	10.47
Ag-10	575/2/10	1.33	85.8	95.5	−2.51	10.73
Ag-12	575/2/10	1.30	83.4	95.46	−4.72	15.2
Ag-12	575/2/10	1.31	82.5	95.21	−4.78	16.2
Ag-10	600/1/10	1.29	82.6	94.06	−0.93	15.68
Ag-10	600/1/10	1.29	86.2	95.27	−1.08	9.58
Ag-11	600/1/10	1.32	44.0	71.5	21.65	110.29
Ag-11	600/1/10	1.33	43.1	70.48	23.07	110.67
Ag-12	600/2/10	1.34	62.0	82.02	14.23	39.93
Ag-12	600/2/10	1.31	62.3	82.6	12.96	41.47
Ag-10	600/3/10	1.33	64.4	88.3	−2.26	65.85
Ag-10	600/3/10	1.29	69.5	90.44	−3.88	51.15
Ag-11	600/3/10	1.32	24.6	43.41	41.48	73.52
Ag-11	600/3/10	1.34	30.5	53.38	36.16	89.47
Ag-12	600/3/10	1.32	49.3	71.89	26.88	63.17
Ag-12	600/3/10	1.33	50.0	72.44	26.28	61.16
Ag-11	575/2/10	1.29	51.8	80.43	5.3	94.46
Ag-11	575/2/10	1.32	52.6	81.29	3.96	93.62
Ag-12	600/1/10	1.36	76.5	89.88	5.59	16.84
Ag-12	600/1/10	1.30	76.2	90.36	4.53	20.01
Ag-10	600/2/10	1.31	77.1	92.72	−2.81	29.07
Ag-10	600/2/10	1.28	76.4	92.55	−3.22	30.79
Ag-11	600/2/10	1.30	36.2	61.58	30.81	101
Ag-11	600/2/10	1.32	35.4	60.37	32.13	100.26
Ag-10	625/1/10	1.33	74.6	90.4	3.5	27.63
Ag-10	625/1/10	1.34	70.9	88.67	5.26	33.93
Ag-11	625/1/10	1.33	34.4	56.78	40.08	95.88
Ag-11	625/1/10	1.35	35.2	58.43	38.04	98.02
Ag-12	625/1/10	1.34	45.9	65.54	23.63	19.56
Ag-12	625/1/10	1.32	52.4	71.17	21.05	19.63
Ag-10	635/0.5/10	1.32	76.2	89.49	7.4	15.81
Ag-12	635/0.5/10	1.35	50.0	71.32	13.82	13.62
Ag-10	625/2/10	1.32	59.4	83.97	7.32	53.78
Ag-10	625/2/10	1.32	53.9	79.43	12.07	62
Ag-11	625/2/10	1.31	16.8	21.62	46.36	36.66
Ag-11	625/2/10	1.30	19.2	28.68	48.69	48.74
Ag-12	625/2/10	1.31	24.2	40.92	34.87	38.77
Ag-12	625/2/10	1.31	26.3	40.9	42.34	45.72
Ag-16	as made	0.60	88.7	95.09	4.58	−1.73
Ag-16	575/0.33/10	0.57	86.5	94.76	3.32	1.91
Ag-16	565/0.25/10	0.60	88.1	95	4.26	−0.83
Ag-16	as made	1.34	86.3	93.7	8.44	−3.23
Ag-16	575/0.33/10	1.32	77.1	92.03	3.62	13.15
Ag-16	565/0.25/10	1.32	85.2	93.51	7.83	−1.61
Ag-16	as made	2.06	84.4	92.66	10.98	−4.12
Ag-16	575/0.33/10	2.03	77.6	91.28	7.96	6.77
Ag-16	565/0.25/10	2.04	82.1	92.25	9.9	−0.62
Ag-28	600/0.5/	1.26	63.2	89.41	−8.22	57.36
	PHCFR
Ag-28	600/0.25/	1.31	72.2	93.01	−7.93	33.76
	PHCFR
Ag-28	600/0.75/	1.35	54.9	83.95	−2.24	85.2
	PHCFR
Ag-28	600/1/	1.32	50.1	79.51	4.83	96
	PHCFR
Ag-28	600/1.25/	1.31	42.4	69.76	24.11	109.37
	PHCFR
Ag-28	600/1.5/	1.31	31.2	46.01	53.51	77.81
	PHCFR
Ag-1	600/1/PHAC	1.30	81.9	94.18	−1.61	17.89
Ag-9	600/1/PHAC	1.31	49.3	77.86	12.16	106.74
Ag-1	600/2/PHAC	1.31	61.0	81.94	14.76	45.2
Ag-9	600/2/PHAC	1.31	45.5	73.48	18.67	108.37
Ag-1	600/3/PHAC	1.32	41.6	60.97	36.89	57.26
Ag-9	600/3/PHAC	1.31	22.8	37.09	48.11	62.4
Ag-1	625/1/PHAC	1.27	68.7	84.18	6.08	9.04
Ag-9	625/1/PHAC	1.31	56.5	79.96	15.43	62.16
Ag-1	625/2/PHAC	1.33	26.8	43.55	32.19	26.91
Ag-9	625/2/PHAC	1.32	39.5	61.72	41.44	100.95
Ag-1	625/3/PHAC	1.32	45.8	65.21	24.02	22.49
Ag-9	625/3/PHAC	1.29	20.9	27.58	50.33	46.01
Ag-9	650/1/PHAC	1.32	37.5	57.39	33.25	43.5
Ag-1	650/1/PHAC	1.31	44.7	72.34	1.09	29.03
Ag-9	as made	1.30	92.2	96.88	−0.02	−0.01
Ag-1	as made	1.31	92.2	96.92	−0.01	0.09
Ag-1	575/1/PHAC	1.30	86.9	96.33	−2.88	7.92
Ag-9	575/1/PHAC	1.33	87.9	96.22	−1.88	6.36
Ag-1	600/0.5/10	1.32	80.0	92.34	2.78	16.14
Ag-9	600/0.5/10	1.33	52.2	72.32	25.62	43.19
Ag-1	600/1/10	1.29	50.2	78.31	13	104.03
Ag-9	600/1/10	1.31	70.1	86.43	9.77	25.5
Ag-1	600/2/10	1.33	33.9	54.05	46.56	90.95
Ag-9	600/2/10	1.31	25.0	40.56	48.66	68.35
Ag-1	600/3/10	1.32	39.4	57.71	37.75	53.96
Ag-9	600/3/10	1.32	31.1	49.88	47.94	84.03
Ag-12	635/0.5/10	1.35	41.5	64.18	18.22	17.04
Ag-13	635/0.5/10	0.59	41.4	65.97	−1.78	6.53
Ag-10	635/0.33/10	1.34	74.0	87.67	9.78	15.76
Ag-10	635/0.33/10	0.62	84.3	93.14	3.83	6.38
Ag-11	635/0.33/10	1.36	39.5	63.67	36.89	105.88
Ag-11	635/0.33/10	0.59	50.1	69.96	15.42	24.46
Ag-29	635/0.33/10	1.34	85.1	94.52	0.48	9.73
Ag-29	635/0.33/10	0.61	87.4	95.33	0.21	6.61
Ag-12	635/0.33/10	1.35	61.6	79.6	9.04	7.31
Ag-12	635/0.33/10	0.61	78.5	89.9	3.47	3.3
Ag-13	635/0.33/10	1.34	20.6	38.54	15.27	11
Ag-13	635/0.33/10	0.61	50.9	78.07	16.01	101.22
Ag-10	635/0.5/10	1.34	74.7	88.54	8.59	17.4
Ag-10	635/0.5/10	0.59	80.1	91.15	5.96	10.8
Ag-11	635/0.5/10	1.32	36.8	60	39.32	100.53
Ag-11	635/0.5/10	0.59	48.5	76.1	18.64	111.37
Ag-29	635/0.5/10	1.34	86.7	95.37	−0.8	8.8
Ag-29	635/0.5/10	0.61	87.2	95.46	−0.63	8.11
Ag-12	635/0.5/10	1.34	63.3	80.09	10.51	7.99
Ag-12	635/0.5/10	0.60	80.3	90.61	4.01	3.43
Ag-10	630/0.66/10	1.35	72.0	87.8	8.65	22.02
Ag-10	630/0.66/10	0.59	76.8	89.84	7.04	15.34
Ag-11	630/0.66/10	1.35	27.9	43.57	50.81	73.87
Ag-11	630/0.66/10	0.59	42.0	67.2	32.97	110.25
Ag-29	630/0.66/10	1.36	83.9	94.65	−1.36	13.6
Ag-29	630/0.66/10	0.57	89.2	96.13	−0.64	4.96
Ag-12	630/0.66/10	1.37	53.7	72.96	14.97	10.44
Ag-12	630/0.66/10	0.57	75.6	87.75	6.18	4.56
Ag-13	630/0.66/10	1.34	3.2	17.64	−0.13	9.52
Ag-13	630/0.66/10	0.57	18.2	48.85	1.57	10.55
Ag-10	650/0.5/10	1.35	65.2	85.98	3.06	28.27
Ag-10	650/0.5/10	0.57	77.8	93.1	−2.63	16.08
Ag-11	650/0.5/10	1.35	24.5	34.47	49.12	57.71
Ag-11	650/0.5/10	0.56	38.4	61.12	27.94	74.46
Ag-29	650/0.5/10	1.35	71.1	93.59	−10.87	39.72
Ag-29	650/0.5/10	0.58	80.9	95.83	−6.92	18.3
Ag-12	650/0.5/10	1.33	35.2	61.52	12.86	25.33
Ag-12	650/0.5/10	0.57	59.8	80.08	6.11	13.24
Ag-13	650/0.5/10	1.36	2.1	4.61	15.13	5.16
Ag-13	650/0.5/10	0.55	26.0	50.65	20.25	15.66
Ag-13	635/0.6/10	0.50	39.8	68.86	−5.21	8.63
Ag-13	635/0.6/10	0.50	38.1	69.02	−4.23	10.36
Ag-19	625/0.5/10	1.28	81.6	91.48	−0.24	1.94
Ag-20	625/0.5/10	1.28	89.1	95.5	1.16	2.16
Ag-21	625/0.5/10	1.28	18.7	40.92	11.24	24.65
Ag-22	625/0.5/10	1.29	55.2	74.16	17.2	20.72
Ag-23	625/0.5/10	1.28	58.9	86.72	−2.66	91.23
Ag-24	625/0.5/10	1.27	75.7	89.09	2.7	2.71
Ag-19	(450/1 + 635/	1.25	66.2	85.08	1.93	7.48
	0.6)/10
Ag-20	(450/1 + 635/	1.23	80.2	90.59	5.45	5.91
	0.6)/10
Ag-21	(450/1 + 635/	1.26	34.5	60.75	10.74	2.34
	0.6)/10
Ag-22	(450/1 + 635/	1.26	29.2	48.41	27.84	24.6
	0.6)/10
Ag-23	(450/1 + 635/	1.25	52.3	81.15	6.31	103.91
	0.6)/10
Ag-24	(450/1 + 635/	1.26	64.8	81.63	5.11	0.83
	0.6)/10
Ag-19	575/2/10	1.19	88.5	96.2	−1.67	5.92
Ag-20	575/2/10	1.18	88.8	96.23	−1.37	6.17
Ag-21	575/2/10	1.16	67.3	90.82	−7.55	56.94
Ag-22	575/2/10	1.20	73.4	91.99	−4.71	37.28
Ag-23	575/2/10	1.23	65.7	90.94	−9.74	52.14
Ag-24	575/2/10	1.21	80.3	94.46	−5.08	22.99
Ag-19	575/3/10	1.33	79.0	94.25	−5.38	25.07
Ag-20	575/3/10	1.36	87.2	95.79	−1.76	8.63
Ag-21	575/3/10	1.35	48.1	75.48	20.79	106.6
Ag-22	575/3/10	1.34	50.3	78.23	13.57	100.58
Ag-23	575/3/10	1.35	54.8	83.93	−2.13	87.35
Ag-24	575/3/10	1.34	69.8	89.53	1.16	40.46
Ag-19	600/1/10	1.31	87.2	94.83	1.61	4.63
Ag-20	600/1/10	1.32	88.3	95.72	−0.04	5.54
Ag-21	600/1/10	1.33	54.1	74.55	21.53	41.51
Ag-22	600/1/10	1.31	62.5	83.83	10.63	46.05
Ag-23	600/1/10	1.33	61.7	88.97	−7.73	76.89
Ag-24	600/1/10	1.31	81.0	91.25	4.02	7.41
Ag-19	625/0.75/10	1.35	67.6	83.95	3.26	8.39
Ag-20	625/0.75/10	1.37	83.2	93.23	2.8	9.89
Ag-21	625/0.75/10	1.37	7.7	14.26	16.11	14.63
Ag-22	625/0.75/10	1.37	54.0	73.76	18.6	26.67
Ag-23	625/0.75/10	1.37	49.0	77.37	13.14	107.83
Ag-24	625/0.75/10	1.36	76.2	89.09	3.18	2.61
Ag-19	625/1/10	1.34	71.6	86.86	3.84	2.74
Ag-20	625/1/10	1.34	81.7	91.97	4.78	9
Ag-21	625/1/10	1.33	6.9	21.04	16.09	2.81
Ag-22	625/1/10	1.35	37.4	57.25	32.53	43.57
Ag-23	625/1/10	1.35	17.4	32.52	37.79	42.15
Ag-24	625/1/10	1.35	46.9	69.03	7.33	0.15
Ag-19	625/2/10	1.36	56.7	77.84	3.78	3.15
Ag-20	625/2/10	1.37	61.3	83.21	9.05	39.01
Ag-21	625/2/10	1.36	1.7	6.03	5.89	6.3
Ag-22	625/2/10	1.35	24.2	39.71	34.72	46.35
Ag-23	625/2/10	1.37	1.0	0.84	1.4	−0.02
Ag-24	625/2/10	1.37	20.6	49.68	7.22	18.91
Ag-19	635/0.6/10	1.27	78.4	90.97	0.85	2.76
Ag-20	635/0.6/10	1.28	78.5	89.93	6.67	9.6
Ag-21	635/0.6/10	1.28	24.9	51.58	13.43	4.69
Ag-22	635/0.6/10	1.28	47.7	67.94	22.47	27.95
Ag-23	635/0.6/10	1.26	44.4	69.96	24.92	104.44
Ag-24	635/0.6/10	1.27	58.0	78.17	7.73	2.76
Ag-19	650/0.33/10	1.31	48.7	75.06	5.45	37.69
Ag-20	650/0.33/10	1.32	69.6	86.53	4.09	15.65
Ag-21	650/0.33/10	1.31	15.4	40.77	8.5	13.14
Ag-22	650/0.33/10	1.32	38.6	61.55	16.07	24.77
Ag-23	650/0.33/10	1.32	55.2	83.6	3.6	98.53
Ag-24	650/0.33/10	1.31	60.4	79.86	1.57	0.06
Ag-19	575/4/10	1.35	62.5	83.86	10.63	45.29
Ag-20	575/4/10	1.35	80.8	94.03	−2.99	21.48
Ag-21	575/4/10	1.36	31.9	46	51.36	75.97
Ag-22	575/4/10	1.37	40.8	66.13	32.1	107.91
Ag-23	575/4/10	1.37	38.5	61.84	37.63	102.88
Ag-24	575/4/10	1.35	53.1	73.2	19.64	35.14
Ag-19	600/2/10	1.27	65.2	81.77	8.74	17.89
Ag-20	600/2/10	1.28	86.8	95.38	−0.5	8.66
Ag-21	600/2/10	1.27	19.1	25.15	38.39	41.98
Ag-22	600/2/10	1.28	41.8	64.47	34.95	82.43
Ag-23	600/2/10	1.25	37.3	58.86	39.89	98.15
Ag-24	600/2/10	1.27	67.2	83.23	7.5	10.6
Ag-19	600/3/10	1.26	52.0	71.68	13.7	17.07
Ag-20	600/3/10	1.29	84.2	94.77	−1.5	14.51
Ag-21	600/3/10	1.27	9.3	24.57	12.39	7.72
Ag-22	600/3/10	1.24	39.5	62.11	37.06	96.27
Ag-23	600/3/10	1.23	21.5	35.28	29.5	16.99
Ag-24	600/3/10	1.27	61.5	79.25	9.59	9.6
Ag-19	615/0.5/10	1.33	86.3	94.4	1.3	5.3
Ag-20	615/0.5/10	1.31	88.3	95.29	1.21	3.5
Ag-21	615/0.5/10	1.35	40.0	63.83	21.26	79.15
Ag-22	615/0.5/10	1.34	65.7	82.74	12.56	22.42
Ag-23	615/0.5/10	1.33	64.2	90.72	−11.12	66.64
Ag-24	615/0.5/10	1.36	83.7	92.44	1.04	2.52
Ag-19	615/1/10	1.27	80.4	90.96	0.89	3.45
Ag-20	615/1/10	1.28	87.9	95.27	1.06	4.77
Ag-21	615/1/10	1.30	25.5	48.52	11.08	17.34
Ag-22	615/1/10	1.31	30.2	45.53	48.19	73.96
Ag-23	615/1/10	1.29	50.1	78.19	13.1	108.41
Ag-24	615/1/10	1.28	79.9	90.88	2.5	3.31
Ag-19	635/1/10	1.28	67.1	84.58	3.58	3.24
Ag-20	635/1/10	1.30	80.7	91.4	5.14	8.57
Ag-21	635/1/10	1.26	17.2	40.14	10.14	−0.13
Ag-22	635/1/10	1.27	35.1	54.92	30.14	34.44
Ag-23	635/1/10	1.27	15.8	29.58	37.33	46.53
Ag-24	635/1/10	1.29	59.5	78.27	4.37	−0.11
Ag-19	635/2/10	1.27	36.9	65.94	−0.53	17.41
Ag-20	635/2/10	1.29	76.6	93.27	−5.41	22.51
Ag-21	635/2/10	1.26	0.4	1.28	1.76	1.45
Ag-22	635/2/10	1.28	25.2	42.76	29.96	47.39
Ag-23	635/2/10	1.27	1.4	3.97	1.91	−0.02
Ag-24	635/2/10	1.30	44.3	71.69	3.05	12.22
Ag-19	640/0.5/10	1.30	49.2	72.62	5.98	9.06
Ag-20	640/0.5/10	1.27	77.5	89.29	7.12	9.32
Ag-21	640/0.5/10	1.28	14.4	39.19	13.64	0.14
Ag-22	640/0.5/10	1.26	47.6	67.68	20.56	21.8
Ag-23	640/0.5/10	1.25	47.4	73.27	21.82	101.59
Ag-24	640/0.5/10	1.28	71.6	86.14	4.05	0.38
Ag-19	650/0.5/10	1.31	59.2	81.01	3.36	10.21
Ag-20	650/0.5/10	1.31	76.7	93.44	−5.26	21.04
Ag-21	650/0.5/10	1.32	5.3	20.93	4.42	17.31
Ag-22	650/0.5/10	1.31	27.8	47.96	24.34	42.2
Ag-23	650/0.5/10	1.29	48.8	77.89	7.06	92.68
Ag-24	650/0.5/10	1.29	29.3	62.01	−3.99	25.51
Ag-24	645/0.5/10	1.22	22.6	53.04	−2.71	16.67

Tables 20A-20E show example glass compositions (in terms of mol %) containing transition metal oxides and/or rare earth oxides as colorant(s), including the total amount of transition metal oxides and/or rare earth oxides present (i.e., Sum “TM+RE”).

TABLE 20A
Example
(mol %)	TM-1	TM-2	TM-3	TM-4	TM-5	TM-6	TM-7	TM-8	TM-9	TM-10
SiO2	61.74	60.04	61.06	61.24	61.20	60.38	59.54	61.59	61.62	61.34
Al2O3	15.04	15.86	15.39	15.39	15.42	15.51	15.98	15.28	15.09	15.32
B2O3	6.06	6.19	6.05	5.95	5.9	5.93	5.9	6.01	5.94	5.94
Li2O	9.03	8.93	8.94	9.93	9.95	8.65	8.69	9.28	9.3	9.39
Na2O	1.41	1.4	1.4	1.5	1.5	1.41	1.52	1.38	1.47	1.46
K2O	0.2	0.2	0.2	0.2	0.2	0.2	0.19	0.2	0.2	0.2
CaO	5.25	6.12	3.84	1.32	2.53	3.83	1.88	4.16	4.19	4.25
MgO	0.99	1	2.88	4.24	3.08	2.88	5.05	1.89	1.9	1.93
NiO	0.0154	0.0178	0.0170	0.0161	0.0154	0.0000	0.0000	0.0163	0.0000	0.0234
Co3O4	0.0001	0.0001	0.0001	0.0000	0.0000	0.0000	0.0000	0.0000	0.0023	0.0094
Cr2O3	0.0297	0.0287	0.0272	0.0280	0.0266	0.0008	0.0008	0.0256	0.0000	0.0000
CuO	0.2207	0.1959	0.1906	0.1750	0.1758	0.0008	0.0000	0.1638	0.2810	0.1165
CeO2	0.0000	0.0000	0.0000	0.0000	0.0000	0.2100	0.2100	0.0000	0.0000	0.0000
TiO2	0.01	0.01	0.01	0.01	0.01	0.99	1.02	0.01	0.01	0.01
Sum	0.2759	0.2525	0.2449	0.2291	0.2278	1.2016	1.2308	0.2157	0.2933	0.1593
TM + RE

TABLE 20B
Example
(mol %)	TM-11	TM-12	TM-13	TM-14	TM-15	TM-16	TM-17	TM-18	TM-19	TM-20
SiO2	61.06	61.24	61.14	61.48	61.47	61.13	61.11	61.32	61.1	61.18
Al2O3	15.39	15.39	15.41	15.58	14.54	14.65	15.75	15.29	14.87	14.65
B2O3	6.05	5.95	5.91	6.03	5.92	5.9	5.79	5.84	5.95	6.14
Li2O	8.94	9.93	9.96	9.69	9.92	10	9.24	9.35	9.96	10.05
Na2O	1.4	1.5	1.49	1.48	1.83	1.83	1.36	1.47	1.86	1.86
K2O	0.2	0.2	0.2	0.2	0.19	0.19	0.17	0.2	0.2	0.19
CaO	3.84	1.32	3.74	1.31	1.99	2.03	4.31	4.23	2.06	2.02
MgO	2.88	4.24	1.92	4.22	1.92	1.94	2.01	1.99	1.98	1.94
NiO	0.0170	0.0161	0.0164	0.0000	0.0000	0.0000	0.0215	0.0000	0.0000	0.0000
Co3O4	0.0001	0.0000	0.0000	0.0000	0.0000	0.0000	0.0000	0.0025	0.0000	0.0000
Cr2O3	0.0272	0.0280	0.0269	0.0000	0.0000	0.0000	0.0270	0.0000	0.0000	0.0000
CuO	0.1906	0.1750	0.1693	0.0000	0.0000	0.0000	0.1761	0.2642	0.0000	0.0000
CeO2	0.0000	0.0000	0.0000	0.0000	0.2000	0.2100	0.0000	0.0000	0.4200	0.4100
TiO2	0.01	0.01	0.01	0.01	0.99	0.99	0.01	0.05	1.01	1
Sum	0.2449	0.2291	0.2226	0.0100	1.1900	1.2000	0.2346	0.3167	1.4300	1.4100
TM + RE

	TABLE 20C
	Example	TM-21	TM-22	TM-23
	SiO2	61.42	61.39	61.04
	Al2O3	14.92	14.87	14.73
	B2O3	5.62	5.78	5.8
	Li2O	9.91	9.85	9.94
	Na2O	1.87	1.86	1.84
	K2O	0.2	0.2	0.19
	CaO	2.06	2.06	2.03
	MgO	1.99	1.97	1.95
	NiO	0.0000	0.0000	0.0000
	Co3O4	0.0000	0.0000	0.0000
	Cr2O3	0.0000	0.0000	0.0000
	CuO	0.0000	0.0000	0.0000
	CeO2	0.4200	0.4200	0.4200
	TiO2	1.02	1.02	1.01
	Sum	1.4400	1.4400	1.4300
	TM + RE

TABLE 20D
Example
(mol %)	TM-24	TM-25	TM-26	TM-27	TM-28	TM-29	TM-30	TM-31	TM-32	TM-33
SiO2	58.63	59.17	58.78	58.51	58.74	59.71	60.28	60.15	59.03	61.64
Al2O3	16.38	16.61	16.52	16.52	16.30	16.46	16.48	15.79	16.35	15.05
B2O3	6.05	5.71	5.95	6.06	6.09	5.95	6.08	6.14	5.85	5.87
Li2O	9.95	11.13	10.91	10.50	10.05	10.45	10.24	8.95	11.86	12.03
Na2O	4.28	5.76	5.23	4.77	4.27	4.78	4.29	1.41	6.32	3.93
K2O	0.20	0.19	0.19	0.20	0.19	0.20	0.20	0.20	0.19	0.39
MgO	0.04	0.02	0.03	0.04	0.05	0.03	0.03	1.98	0.08	0.02
ZnO	3.96	0.99	2.00	3.01	3.92	1.99	2.00	5.01	0.00	0.75
SnO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.00	0.01
Fe2O3	0.0044	0.0040	0.0044	0.0044	0.0044	0.0040	0.0044	0.0052	0.0132	0.0040
NiO	0.00	0.0138	0.0147	0.0147	0.0146	0.0147	0.0147	0.0176	0.0112	0.0116
Co3O4	0.0027	0.0024	0.0021	0.0024	0.0021	0.0021	0.0021	0.0001	0.0027	0.0118
Cr2O3	0.0004	0.0258	0.0267	0.0267	0.0262	0.0263	0.0268	0.0291	0.0274	0.0240
CuO	0.3340	0.2222	0.1944	0.2130	0.2046	0.2305	0.2183	0.1987	0.1659	0.1673
Sum	0.3371	0.2653	0.2380	0.2568	0.2476	0.2736	0.2619	0.2455	0.2072	0.2047
TM + RE

	TABLE 20E
	Example	TM-34	TM-35	TM-36
	SiO2	60.95	61.66	60.89
	Al2O3	15.44	15.11	15.61
	B2O3	5.80	5.94	6.12
	Li2O	9.78	11.97	9.49
	Na2O	1.56	3.94	1.52
	K2O	0.20	0.39	0.19
	CaO	4.28	0.76	4.17
	MgO	1.97	0.03	1.99
	NiO	0.0000	0.0173	0.0000
	Co3O4	0.0017	0.0025	0.0010
	Cr2O3	0.0034	0.0277	0.0000
	CuO	0.0000	0.1380	0.0000
	CeO2	0.00	0.00	0.00
	TiO2	0.01	0.01	0.01
	Sum	0.0052	0.1855	0.0010
	TM + RE

Tables 21A-21C show the dielectric constant (calculated) and dielectric constant (as measured at 10 GHz) for select examples from Tables 20A-20E. When calculated, the dielectric constant was calculated according to the formula: Dk=3.802946+0.01747*B₂O₃ (mol %)+0.058769*Al₂O₃ (mol %)+0.080876*Li₂O (mol %)+0.148433*Na₂O (mol %)+0.153264*K₂O (mol %)+0.045179*MgO (mol %)+0.080113*CaO (mol %). Where measured, the dielectric constant was measured using a split post dielectric resonator (SPDR at a frequency of 10 GHz. Tables 21A-21C also show the CIELAB L*, a*, and b* coordinates for select examples from Tables 20A-2E at the indicated thickness.

TABLE 21A
Example	TM-1	TM-2	TM-3	TM-4	TM-5	TM-6	TM-7	TM-8	TM-9	TM-10
Dk	6.2283	6.3393	6.2123	6.1651	6.2121	6.1945	6.1815	6.2106	6.2161	6.2415
Relationship
(calculated)
Dk	6.13	6.23	6.18	6.15	6.19	6.29	6.21	6.22
(measured
at 10 GHz)
L*								90.61	92.48	88.24
a*								−8.02	−4.39	−1.61
b*								4.61	−3.85	−4.42
Thickness								1.32	1.38	1.36
(mm)

TABLE 21B
Example	TM-11	TM-12	TM-13	TM-14	TM-15	TM-16	TM-17	TM-18	TM-19	TM-20
Dk	6.2123	6.1651	6.2555	6.1535	6.1101	6.1268	6.2410	6.2374	6.1475	6.1387
Relationship
(calculated)
Dk
(measured at
10 GHz)
L*	90.14	90.81	90.81	96.81	96.68	96.63	89.23	92.76	96.11	96.11
a*	−8.48	−7.43	−7.6	−0.02	−0.4	−0.39	−7.87	−4.26	−1.36	−1.36
b*	4.91	4.98	4.79	0.2	1.28	1.47	3.88	−3.53	4.76	4.76
Thickness	1.38	1.34	1.34	1.32	1.34	1.34	1.32	1.37	1.34	1.34
(mm)

TABLE 21C
Example	TM-21	TM-22	TM-23	TM-24	TM-28	TM-34	TM-35	TM-36
Dk	6.1426	6.1352	6.1268			5.95	6.41	5.94
Relationship
(calculated)
Dk				6.42	6.52	6.23	6.41	6.24
(measured at
10 GHz)
L*	96.11	96.11	96.22
a*	−1.36	−1.36	−1.3
b*	4.76	4.76	4.44
Thickness	1.34	1.34	1.36
(mm)

Tables 22A and 22B show the ion exchange characteristic (CS, DOL, and CT) for select glass articles from Tables 20A-20D at different thicknesses and ion exchange conditions (temperature, time, and ion exchange bath compositions).

TABLE 22A
	Thickness	Temp	Time	KNO3	NaNO3	LiNO3	CS	DOL	CT
Example	(mm)	(° C.)	(hrs.)	(wt. %)	(wt. %)	(wt. %)	(MPa)	(μm)	(MPa)
TM-24	0.6	440	6.5	79.2	19.4	1.4	599	5.62	104.67
TM-25	0.6	430	4	79	19.4	1.6	633	6.02	129.51
TM-26	0.6	430	4	79	19.4	1.6	661	5.03	124.41
TM-27	0.6	430	4	79	19.4	1.6	700	3.83	119.67
TM-28	0.6	430	4	79	19.4	1.6	684	3.97	117.14
TM-28	0.6	430	8	79	19.4	1.6	615	4.79	131.67
TM-28	0.6	430	16	79	19.4	1.6	559	6.82	97.64
TM-28	0.6	440	6	79	19.4	1.6	600	5.29	109.95
TM-28	0.6	440	6	79.2	19.4	1.4	651	4.67	108.80
TM-28	0.6	440	7	79.2	19.4	1.4	600	5.40	110.20
TM-28	0.6	440	6.5	79.2	19.4	1.4	589	5.56	105.80
TM-29	0.6	430	4	79	19.4	1.6	643	5.56	142.52
TM-30	0.6	430	4	79	19.4	1.6	681	5.24	127.46
TM-31	0.6	450	4	90	10	0	902	3.52	110
TM-31	0.6	450	8	90	10	0	832	4.52	160
TM-31	0.6	450	12	90	10	0	758	5.62	191
TM-31	0.6	450	8	89	10	1	773	3.54	110
TM-31	0.6	450	12	89	10	1	673	4.65	138
TM-31	0.6	450	8	88.5	10	1.5	695	3.64	96
TM-31	0.6	450	12	88.5	10	1.5	639	4.17	109
TM-13	0.6	450	4	90	10	0	900	3.99	133
TM-13	0.6	450	8	90	10	0	786	5.61	187
TM-13	0.6	450	12	90	10	0	721	7.55	174
TM-13	0.6	450	8	89	10	1	721	4.89	139
TM-13	0.6	450	12	89	10	1	661	5.76	143
TM-13	0.6	450	8	88.5	10	1.5	704	4.39	114
TM-13	0.6	450	12	88.5	10	1.5	636	5.69	113

TABLE 22B
	Thickness	Temp	Time	KNO3	NaNO3	LiNO3	CS	DOL	CT
Example	(mm)	(° C.)	(hrs.)	(wt. %)	(wt. %)	(wt. %)	(MPa)	(μm)	(MPa)
TM-32	1.33	400	16	89	10	1	672	9.1	72
TM-32	1.33	400	24	89	10	1	627	11.2	78
TM-32	1.33	430	8	80	20	0	518	11.6	97
TM-32	0.6	380	8	79	18.7	2.3	641	4.1	100
TM-32	0.6	380	10	79	18.7	2.3	612	4.7	102
TM-32	0.6	380	12	79	18.7	2.3	599	5.2	100
TM-32	0.6	410	4	79	19.5	1.5	633	5.3	109
TM-32	0.6	410	5	79	19.5	1.5	612	5.9	108
TM-32	0.6	410	6	79	19.5	1.5	601	6.1	107
TM-32	0.6	400	5	79	19.8	1.2	695	5.0	112
TM-32	0.6	400	5	79	20.1	0.9	671	5.3	116
TM-32	0.6	400	5	79	19.4	1.6	645	5.0	107
TM-32	0.6	430	2.5	79	19.4	1.6	591	6.0	101
TM-32	0.6	430	3	79	19.4	1.6	569	6.1	98
TM-32	0.6	430	3.5	79	19.4	1.6	557	6.8	96
TM-32	0.6	430	2.5	75.6	24	0.4	609	6.41	126
TM-32	0.6	430	2.5	76	24	0	602	7.57	129
TM-32	0.55	400	3	79	19.8	1.2	749	3.69	108
TM-8	0.6	450	4	89.8	10	0.2	693	5.54	139
TM-8	0.6	450	4	89.8	10	0.2	637	7.54	134
TM-8	0.6	450	8	89.5	10	0.5	664	5.56	134
TM-8	0.6	450	8	88.5	11	0.5	661	5.59	138
TM-8	0.6	450	8	87.5	12	0.5	645	5.69	142
TM-8	0.6	450	8	86.5	13	0.5	636	5.74	145
TM-8	0.6	450	8	89.5	10	0.5	667	5.52	136
TM-8	0.55	450	6.75	87.3	12.5	0.2	668	5.64	140
TM-8	0.55	450	6.75	87.5	12.5	0	686	5.63	157
TM-8	0.6	440	8	88	11	1	667	4.32	121
TM-8	0.6	440	10	88	11	1	638	5.10	127
TM-8	0.6	440	12	88	11	1	614	5.64	129

Table 23 shows the fracture toughness (K_IC) for select examples from Tables 20A-20D and a comparative example of a non-colored glass article comprising 58.41 mol % SiO₂, 6.07 mol % B₂O₃, 17.84 mol % Al₂O₃, 1.73 mol % Na₂O, 0.20 mol % K₂O, 4.43 mol % MgO, 0.57 mol % CaO, 0.01 mol % SnO₂, and 10.71 mol % Li₂O. The fracture toughness was measured using the chevron notch short bar method and the dual cantilever beam method.

	TABLE 23
		KIC CNSB	KIC DCB
	Example	(MPa · m1/2)	(MPa · m1/2)
	TM-32	0.774	0.816
	TM-8	0.8	0.839
	TM-33	0.794	0.813
	Comparative	0.786	0.877
	Example

FIG. 50 shows the results of an incremental face drop on sandpaper (i.e., a “drop test”) for two different sandpaper conditions (180 grit) and (80 grit) for select examples from Tables 20A-20D and a comparative example of a non-colored glass article comprising 58.41 mol % SiO₂, 6.07 mol % B₂O₃, 17.84 mol % Al₂O₃, 1.73 mol % Na₂O, 0.20 mol % K₂O, 4.43 mol % MgO, 0.57 mol % CaO, 0.01 mol % SnO₂, and 10.71 mol % Li₂O. Prior to performing the drop test, the TM-33 samples were ion exchanged in a molten salt batch comprising 89.3 wt % KNO₃, 10 wt. % NaNO₃, and 0.7 wt. % LiNO₃ at 440° C. for 9 hours. The TM-8 samples were ion exchanged in a molten salt batch comprising 79 wt % KNO₃, 19.9 wt. % NaNO₃, and 1.6 wt. % LiNO₃ at 400° C. for 5 hours. The comparative examples were ion exchanged in a molten salt batch comprising 90.3 wt % KNO₃, 9 wt. % NaNO₃, and 0.7 wt. % LiNO₃ at 450° C. for 5 hours.

The circles in FIG. 50 indicate at what height the sample fractured. The diamonds represent samples that were dropped incrementally all the way to 220 cm and did not fracture. As exemplified by FIG. 50, Examples 8 and 32, colored glass articles exhibited similar drop performance as compared to a comparative example of a non-colored glass article.

A typical drop test is schematically shown in FIG. 51. Each sample 1310 was affixed to a standard test vehicle 1320, which approximates the size, mass, and balance of a generic “smart” phone, and dropped from a drop height h onto a sheet of sandpaper 1330 having an abrasive surface 1335. The drop height h ranged from about 0.2 meter to 2.2 meters in incremental heights of 0.1 meter. Drop testing was carried out using a 180-grit silicon carbide sandpaper surface and an 80 grit silicon carbide sandpaper surface. The drop performance is reported in terms of the maximum drop height in cm before failure of the colored glass article.

Tables 24A and 24B show example glass compositions (in terms of mol %) containing transition metal oxides and/or rare earth oxides as colorant(s). Tables 24A and 24B also show the dielectric constant (Dk, as measured at 10 GHz) for the example compositions.

TABLE 24A
Example
(mol %)	TM-37	TM-38	TM-39	TM-40	TM-41	TM-42	TM-42	TM-44	TM-45
SiO2	58.5	59.5	59.6	59.2	59.1	61.1	61.5	59.1	59.3
Al2O3	16.4	16.4	16.3	16.4	16.5	15.6	15.2	16.4	16.5
B2O3	5.8	5.8	5.6	5.9	5.9	5.8	6.0	6.0	5.7
P2O5	0.0	0.0	0.0	0.0	0.0	0.0	0.0	0.0	0.0
Li2O	11.8	9.2	8.7	9.4	9.0	9.3	8.2	9.4	8.8
Na2O	6.1	3.8	3.3	3.8	3.3	3.8	1.2	3.7	3.3
K2O	0.2	0.2	0.2	0.2	0.2	0.2	0.2	0.2	0.2
MgO	0.0	0.0	0.1	0.9	1.9	0.0	0.1	0.1	0.1
CaO	0.0	4.9	5.9	3.9	4.0	4.0	7.4	4.9	6.0
TiO2	1.0	0.0	0.0	0.0	0.0	0.0	0.0	0.0	0.0
Fe2O3	0.00	0.00	0.00	0.00	0.00	0.00	0.01	0.00	0.00
CeO2	0.20	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
NiO	0.00	0.02	0.01	0.02	0.02	0.02	0.02	0.03	0.03
Co3O4	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.01	0.01
Cr2O3	0.00	0.03	0.03	0.03	0.03	0.03	0.03	0.00	0.00
CuO	0.00	0.16	0.16	0.16	0.16	0.16	0.16	0.12	0.13
Cl	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
Dk	6.7	6.44	6.44	6.43	6.39	6.37	6.23	6.47	6.46
(measured
at 10 GHz)

TABLE 24B
Example
(mol %)	TM-46	TM-47	TM-48	TM-49	TM-50	TM-51	TM-52	TM-52	TM-54
SiO2	59.7	58.9	61.1	61.8	62.5	62.5	62.5	62.1	60.2
Al2O3	16.3	16.7	15.5	15.2	14.8	14.7	14.8	15.2	15.9
B2O3	5.8	5.9	5.9	5.6	6.0	6.0	6.0	5.9	6.0
P2O5	0.0	0.0	0.0	0.0	0.0	0.0	0.0	0.0	0.0
Li2O	9.3	8.9	9.4	8.3	8.9	8.9	9.0	8.9	8.8
Na2O	3.7	3.3	3.8	1.2	1.4	1.4	1.4	1.4	1.4
K2O	0.2	0.2	0.2	0.2	0.2	0.2	0.2	0.2	0.2
MgO	0.9	1.9	0.0	0.1	1.9	2.9	3.9	5.1	0.1
CaO	3.9	4.0	3.9	7.5	4.1	3.1	2.1	1.1	7.2
TiO2	0.0	0.0	0.0	0.0	0.0	0.0	0.0	0.0	0.0
Fe2O3	0.00	0.00	0.00	0.01	0.00	0.00	0.01	0.00	0.01
CeO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
NiO	0.03	0.03	0.03	0.03	0.02	0.02	0.02	0.02	0.02
Co3O4	0.01	0.01	0.01	0.01	0.00	0.00	0.00	0.00	0.00
Cr2O3	0.00	0.00	0.00	0.00	0.03	0.03	0.03	0.03	0.03
CuO	0.12	0.12	0.12	0.13	0.18	0.17	0.18	0.20	0.19
Cl	0.01	0.01	0.01	0.01	0.00	0.00	0.00	0.00	0.00
Dk	6.44	6.38	6.34	6.18	6.44	6.44	6.43	6.39	6.37
(measured
at 10 GHz)

Tables 25A-25BJ show example colored glass articles (in terms of mol %) containing transition metal oxides and/or rare earth oxides as colorant(s) and properties thereof. Examples TM476-TM442 were annealed at at 600° C. for 1 hour prior to analysis.

TABLE 25A
Example	TM-55	TM-56	TM-57	TM-58	TM-59	TM-60	TM-61	TM-62	TM-63	TM-64
SiO2	61.002	60.927	60.970	61.007	61.010	60.948	61.004	61.073	61.062	61.035
Al2O3	15.489	15.485	15.422	15.381	15.380	15.350	15.307	15.296	15.263	15.237
B2O3	6.051	6.055	6.050	6.048	6.007	6.008	6.006	6.011	6.013	6.015
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.486	9.491	9.483	9.481	9.396	9.397	9.394	9.317	9.319	9.323
Na2O	1.581	1.601	1.608	1.612	1.655	1.700	1.673	1.680	1.695	1.710
K2O	0.196	0.197	0.199	0.196	0.197	0.202	0.196	0.196	0.196	0.197
MgO	1.959	1.949	1.921	1.902	1.867	1.861	1.846	1.833	1.828	1.808
CaO	4.201	4.214	4.211	4.204	4.229	4.237	4.240	4.246	4.258	4.259
ZnO	0.000	0.000	0.000	0.001	0.001	0.001	0.001	0.001	0.000	0.000
SnO2	0.001	0.002	0.002	0.003	0.002	0.003	0.002	0.003	0.002	0.003
Fe2O3	0.007	0.007	0.007	0.007	0.008	0.007	0.007	0.007	0.007	0.007
TiO2	0.016	0.048	0.088	0.108	0.172	0.199	0.223	0.233	0.248	0.281
CeO2	0.009	0.020	0.037	0.045	0.073	0.084	0.096	0.102	0.105	0.122
ZrO2	0.002	0.003	0.004	0.004	0.004	0.003	0.003	0.004	0.003	0.004
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	0.025	0.068	0.125	0.153	0.244	0.283	0.319	0.334	0.353	0.403
R2O	11.262	11.289	11.290	11.289	11.248	11.299	11.263	11.192	11.211	11.230
Li2O + Na2O	11.067	11.092	11.091	11.093	11.051	11.097	11.067	10.996	11.014	11.033
R2O − Al2O3	−4.227	−4.196	−4.132	−4.092	−4.132	−4.052	−4.044	−4.104	−4.052	−4.007
R′O	6.160	6.163	6.131	6.107	6.097	6.099	6.087	6.080	6.086	6.067
Thickness	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400
(mm)
L*	96.82	96.83	96.86	96.87	96.88	96.87	96.87	96.84	96.87	96.85
a*	−0.07	−0.07	−0.06	−0.05	−0.06	−0.08	−0.1	−0.1	−0.11	−0.14
b*	0.29	0.29	0.3	0.32	0.4	0.49	0.57	0.62	0.66	0.81
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25B
Example	TM-65	TM-66	TM-67	TM-68	TM-69	TM-70	TM-71	TM-72	TM-73	TM-74
SiO2	60.976	60.958	60.918	60.830	60.802	60.816	60.779	60.702	60.716	60.696
Al2O3	15.190	15.176	15.147	15.121	15.063	14.993	14.977	14.982	14.810	14.781
B2O3	6.021	6.020	6.021	6.050	6.051	6.005	6.006	6.008	6.010	6.011
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.382	9.380	9.382	9.290	9.293	9.335	9.337	9.340	9.343	9.344
Na2O	1.716	1.729	1.742	1.786	1.814	1.829	1.843	1.850	1.893	1.908
K2O	0.200	0.198	0.199	0.197	0.199	0.198	0.199	0.197	0.200	0.200
MgO	1.788	1.780	1.769	1.729	1.699	1.666	1.658	1.651	1.581	1.567
CaO	4.255	4.256	4.275	4.321	4.323	4.334	4.335	4.359	4.360	4.372
ZnO	0.001	0.000	0.001	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SnO2	0.003	0.003	0.003	0.002	0.003	0.003	0.003	0.003	0.003	0.003
Fe2O3	0.007	0.007	0.007	0.007	0.006	0.006	0.006	0.006	0.006	0.006
TiO2	0.321	0.345	0.371	0.466	0.522	0.570	0.602	0.635	0.763	0.788
CeO2	0.137	0.145	0.161	0.197	0.221	0.241	0.250	0.263	0.312	0.320
ZrO2	0.003	0.003	0.004	0.004	0.004	0.004	0.004	0.005	0.004	0.005
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	0.458	0.489	0.532	0.663	0.743	0.811	0.853	0.897	1.075	1.107
R2O	11.298	11.308	11.323	11.274	11.306	11.362	11.379	11.387	11.435	11.452
Li2O + Na2O	11.098	11.110	11.124	11.076	11.106	11.164	11.180	11.190	11.235	11.252
R2O − Al2O3	−3.893	−3.868	−3.824	−3.848	−3.757	−3.630	−3.597	−3.595	−3.375	−3.329
R′O	6.044	6.036	6.046	6.050	6.022	5.999	5.993	6.010	5.941	5.939
Thickness	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400
(mm)
L*	96.84	96.82	96.81	96.78	96.75	96.71	96.69	96.67	96.57	96.53
a*	−0.18	−0.2	−0.23	−0.33	−0.39	−0.47	−0.51	−0.56	−0.74	−0.79
b*	0.97	1.08	1.22	1.72	2.05	2.46	2.65	2.96	3.99	4.26
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25C
Example	TM-75	TM-76	TM-77	TM-78	TM-79	TM-80	TM-81	TM-82	TM-83	TM-84
SiO2	60.631	60.704	60.669	60.654	60.659	60.639	60.654	60.777	60.742	60.733
Al2O3	14.741	14.741	14.749	14.758	14.738	14.739	14.725	14.647	14.654	14.635
B2O3	6.012	6.041	6.042	6.040	6.040	6.040	5.987	5.986	5.987	5.986
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.347	9.104	9.106	9.103	9.103	9.103	9.128	9.126	9.127	9.127
Na2O	1.931	1.972	1.966	1.971	1.976	1.975	1.991	1.981	1.982	1.995
K2O	0.201	0.202	0.203	0.200	0.201	0.199	0.201	0.201	0.202	0.199
MgO	1.544	1.537	1.529	1.530	1.527	1.519	1.513	1.489	1.490	1.491
CaO	4.396	4.427	4.439	4.438	4.438	4.449	4.451	4.427	4.434	4.439
ZnO	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.001	0.000
SnO2	0.003	0.003	0.003	0.003	0.003	0.003	0.003	0.003	0.003	0.003
Fe2O3	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006
TiO2	0.844	0.902	0.918	0.926	0.934	0.950	0.958	0.966	0.979	0.991
CeO2	0.338	0.359	0.365	0.367	0.370	0.373	0.379	0.387	0.388	0.391
ZrO2	0.005	0.004	0.004	0.004	0.005	0.004	0.004	0.004	0.004	0.005
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.182	1.261	1.283	1.292	1.304	1.323	1.337	1.353	1.367	1.381
R2O	11.479	11.278	11.275	11.274	11.281	11.278	11.320	11.309	11.312	11.320
Li2O + Na2O	11.277	11.076	11.072	11.074	11.079	11.079	11.119	11.107	11.109	11.122
R2O − Al2O3	−3.262	−3.463	−3.474	−3.483	−3.458	−3.461	−3.405	−3.338	−3.343	−3.315
R′O	5.940	5.963	5.968	5.968	5.964	5.968	5.964	5.916	5.926	5.929
Thickness	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400
(mm)
L*	96.44	96.37	96.36	96.34	96.3	96.32	96.3	96.27	96.26	96.24
a*	−0.89	−0.99	−1.01	−1.03	−1.05	−1.07	−1.1	−1.12	−1.15	−1.17
b*	4.9	5.52	5.65	5.78	5.91	6.05	6.2	6.36	6.54	6.67
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25D
Example	TM-85	TM-86	TM-87	TM-88	TM-89	TM-90	TM-91	TM-92	TM-93	TM-94
SiO2	60.647	60.851	60.921	60.845	60.809	60.660	60.650	60.706	60.692	60.684
Al2O3	14.685	14.689	14.621	14.656	14.674	14.606	14.621	14.595	14.584	14.598
B2O3	5.989	6.014	6.012	6.014	6.016	6.038	6.039	6.038	6.039	6.040
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.130	8.904	8.901	8.903	8.906	9.099	9.101	9.100	9.101	9.102
Na2O	1.995	1.991	2.005	2.013	2.009	2.015	2.006	1.995	2.006	2.008
K2O	0.200	0.201	0.203	0.202	0.200	0.203	0.201	0.200	0.200	0.202
MgO	1.490	1.492	1.481	1.488	1.485	1.481	1.479	1.472	1.474	1.474
CaO	4.455	4.446	4.433	4.445	4.447	4.436	4.436	4.425	4.425	4.414
ZnO	0.001	0.001	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SnO2	0.003	0.003	0.003	0.003	0.003	0.003	0.003	0.003	0.003	0.003
Fe2O3	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006
TiO2	0.998	1.000	1.008	1.016	1.025	1.022	1.022	1.022	1.022	1.022
CeO2	0.395	0.397	0.400	0.405	0.415	0.426	0.431	0.433	0.443	0.442
ZrO2	0.004	0.004	0.004	0.004	0.005	0.005	0.005	0.004	0.005	0.005
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.393	1.397	1.408	1.421	1.440	1.448	1.453	1.455	1.465	1.464
R2O	11.326	11.096	11.109	11.118	11.115	11.317	11.308	11.295	11.307	11.312
Li2O + Na2O	11.126	10.895	10.906	10.916	10.915	11.114	11.107	11.095	11.107	11.110
R2O − Al2O3	−3.359	−3.593	−3.512	−3.538	−3.560	−3.289	−3.313	−3.299	−3.277	−3.286
R′O	5.946	5.939	5.914	5.933	5.932	5.917	5.915	5.897	5.899	5.888
Thickness	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400
(mm)
L*	96.26	96.24	96.25	96.21	96.17	96.13	96.11	96.1	96.09	96.05
a*	−1.18	−1.18	−1.2	−1.22	−1.27	−1.31	−1.32	−1.33	−1.35	−1.37
b*	6.75	6.76	6.86	7.03	7.34	7.65	7.77	7.86	7.97	8.15
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25E
Example	TM-95	TM-96	TM-97	TM-98	TM-99	TM-100	TM-101	TM-102	TM-103	TM-104
SiO2	60.676	60.627	60.659	60.557	60.488	60.462	60.525	60.517	60.541	60.560
Al2O3	14.658	14.671	14.658	14.704	14.707	14.707	14.666	14.666	14.647	14.641
B2O3	5.992	5.992	5.992	5.995	6.001	6.002	6.000	6.000	6.000	6.000
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	8.998	8.998	8.998	9.003	9.013	9.013	9.011	9.011	9.011	9.011
Na2O	2.020	2.027	2.017	2.033	2.029	2.027	2.024	2.030	2.025	2.023
K2O	0.203	0.204	0.201	0.201	0.203	0.202	0.203	0.204	0.204	0.202
MgO	1.480	1.483	1.475	1.479	1.477	1.489	1.485	1.485	1.485	1.479
CaO	4.449	4.461	4.461	4.475	4.468	4.480	4.467	4.468	4.463	4.455
ZnO	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SnO2	0.004	0.003	0.003	0.003	0.003	0.003	0.003	0.003	0.003	0.003
Fe2O3	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006
TiO2	1.033	1.041	1.041	1.042	1.043	1.043	1.043	1.043	1.043	1.043
CeO2	0.476	0.481	0.484	0.498	0.558	0.562	0.562	0.563	0.568	0.572
ZrO2	0.006	0.005	0.004	0.004	0.004	0.005	0.005	0.004	0.005	0.005
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.509	1.522	1.525	1.540	1.601	1.605	1.604	1.606	1.611	1.615
R2O	11.221	11.229	11.217	11.237	11.244	11.241	11.238	11.245	11.239	11.236
Li2O + Na2O	11.018	11.025	11.015	11.036	11.041	11.040	11.035	11.041	11.036	11.034
R2O − Al2O3	−3.436	−3.442	−3.442	−3.467	−3.463	−3.466	−3.428	−3.421	−3.407	−3.405
R′O	5.929	5.944	5.936	5.954	5.946	5.968	5.952	5.953	5.948	5.933
Thickness	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400
(mm)
L*	95.95	95.92	95.9	95.86	95.6	95.6	95.46	95.44	95.46	95.46
a*	−1.45	−1.48	−1.49	−1.52	−1.67	−1.66	−1.66	−1.67	−1.68	−1.68
b*	8.86	9.08	9.2	9.44	10.94	10.9	11.05	11.13	11.2	11.28
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25F
Example	TM-105	TM-106	TM-107	TM-108	TM-109	TM-110	TM-111	TM-112	TM-113	TM-114
SiO2	60.513	60.470	60.471	60.487	60.502	60.460	60.459	60.385	60.465	60.434
Al2O3	14.673	14.696	14.696	14.680	14.667	14.697	14.697	14.715	14.659	14.675
B2O3	6.003	6.005	6.005	6.031	6.031	6.033	6.033	6.054	6.051	6.053
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.015	9.018	9.018	8.994	8.994	8.996	8.997	8.978	8.975	8.977
Na2O	2.018	2.016	2.014	2.023	2.020	2.029	2.025	2.029	2.028	2.023
K2O	0.201	0.202	0.203	0.201	0.203	0.202	0.201	0.203	0.202	0.201
MgO	1.484	1.491	1.484	1.484	1.484	1.480	1.487	1.477	1.476	1.469
CaO	4.456	4.459	4.465	4.473	4.471	4.474	4.468	4.475	4.455	4.453
ZnO	0.000	0.000	0.002	0.002	0.002	0.002	0.002	0.002	0.002	0.002
SnO2	0.004	0.003	0.004	0.003	0.003	0.003	0.003	0.003	0.003	0.004
Fe2O3	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006
TiO2	1.043	1.044	1.042	1.028	1.028	1.028	1.031	1.081	1.087	1.106
CeO2	0.578	0.585	0.585	0.584	0.586	0.585	0.588	0.589	0.586	0.591
ZrO2	0.005	0.005	0.005	0.004	0.004	0.005	0.004	0.004	0.005	0.005
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.622	1.629	1.627	1.611	1.614	1.613	1.619	1.670	1.674	1.698
R2O	11.234	11.236	11.235	11.218	11.217	11.227	11.222	11.210	11.205	11.201
Li2O + Na2O	11.033	11.034	11.032	11.017	11.014	11.025	11.021	11.006	11.003	11.000
R2O − Al2O3	−3.439	−3.461	−3.461	−3.462	−3.450	−3.469	−3.475	−3.505	−3.454	−3.474
R′O	5.940	5.950	5.950	5.959	5.956	5.956	5.956	5.954	5.933	5.924
Thickness	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400
(mm)
L*	95.38	95.38	95.45	95.4	95.43	95.44	95.42	95.4	95.39	95.38
a*	−1.7	−1.7	−1.72	−1.72	−1.73	−1.73	−1.73	−1.79	−1.8	−1.83
b*	11.45	11.52	11.59	11.74	11.76	11.76	11.8	12.13	12.24	12.42
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25G
Example	TM-115	TM-116	TM-117	TM-118	TM-119	TM-120	TM-121	TM-122	TM-123	TM-124
SiO2	60.414	60.401	60.373	60.387	60.323	60.339	60.319	60.321	60.332	60.332
Al2O3	14.673	14.662	14.685	14.665	14.700	14.681	14.696	14.696	14.696	14.701
B2O3	6.052	6.053	6.054	6.054	6.055	5.988	5.989	5.989	5.989	5.988
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	8.976	8.977	8.979	8.979	8.981	9.020	9.022	9.021	9.022	9.020
Na2O	2.026	2.022	2.028	2.023	2.031	2.026	2.023	2.023	2.017	2.021
K2O	0.200	0.202	0.202	0.201	0.202	0.203	0.202	0.204	0.202	0.203
MgO	1.484	1.480	1.472	1.465	1.468	1.478	1.480	1.478	1.476	1.473
CaO	4.470	4.461	4.455	4.464	4.474	4.487	4.484	4.485	4.484	4.488
ZnO	0.002	0.002	0.002	0.002	0.000	0.002	0.000	0.002	0.000	0.002
SnO2	0.004	0.004	0.003	0.004	0.003	0.004	0.004	0.003	0.003	0.004
Fe2O3	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006
TiO2	1.101	1.135	1.144	1.152	1.158	1.171	1.174	1.171	1.174	1.171
CeO2	0.587	0.591	0.593	0.594	0.594	0.592	0.597	0.596	0.594	0.586
ZrO2	0.005	0.004	0.005	0.005	0.005	0.005	0.005	0.005	0.005	0.005
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.688	1.727	1.737	1.746	1.751	1.763	1.771	1.767	1.768	1.757
R2O	11.202	11.201	11.209	11.203	11.214	11.249	11.247	11.249	11.241	11.245
Li2O + Na2O	11.002	10.999	11.007	11.002	11.012	11.046	11.045	11.045	11.039	11.042
R2O − Al2O3	−3.471	−3.462	−3.476	−3.462	−3.486	−3.432	−3.449	−3.447	−3.456	−3.456
R′O	5.956	5.942	5.928	5.930	5.942	5.966	5.965	5.965	5.960	5.963
Thickness	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400
(mm)
L*	95.35	95.29	95.28	95.27	95.27	95.27	95.27	95.27	95.24	95.3
a*	−1.84	−1.91	−1.92	−1.93	−1.93	−1.97	−1.97	−1.96	−1.96	−1.95
b*	12.51	13.06	13.2	13.27	13.21	13.47	13.49	13.47	13.49	13.25
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25H
Example	TM-125	TM-126	TM-127	TM-128	TM-129	TM-130	TM-131	TM-132	TM-133	TM-134
SiO2	60.295	60.290	60.285	60.395	60.350	60.436	60.382	60.449	60.481	60.565
Al2O3	14.728	14.745	14.743	14.679	14.719	14.678	14.724	14.692	14.681	14.678
B2O3	5.979	5.979	5.978	5.975	5.976	5.972	5.973	5.970	5.968	5.967
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.021	9.020	9.019	9.015	9.016	9.011	9.011	9.007	9.005	9.003
Na2O	2.028	2.023	2.025	2.014	2.025	2.034	2.032	2.020	2.021	2.020
K2O	0.202	0.202	0.201	0.203	0.202	0.203	0.201	0.202	0.202	0.199
MgO	1.480	1.477	1.482	1.476	1.472	1.467	1.471	1.473	1.478	1.472
CaO	4.496	4.507	4.506	4.492	4.492	4.479	4.491	4.477	4.484	4.463
ZnO	0.000	0.000	0.000	0.000	0.002	0.000	0.000	0.000	0.001	0.000
SnO2	0.004	0.004	0.004	0.004	0.004	0.004	0.004	0.003	0.003	0.003
Fe2O3	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006
TiO2	1.174	1.173	1.181	1.181	1.182	1.180	1.188	1.188	1.172	1.131
CeO2	0.583	0.570	0.565	0.556	0.550	0.525	0.514	0.506	0.493	0.488
ZrO2	0.005	0.005	0.005	0.004	0.004	0.005	0.004	0.005	0.005	0.005
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.756	1.744	1.747	1.737	1.732	1.705	1.702	1.694	1.665	1.619
R2O	11.251	11.245	11.245	11.231	11.243	11.248	11.244	11.230	11.227	11.222
Li2O + Na2O	11.049	11.043	11.044	11.028	11.041	11.045	11.043	11.028	11.025	11.023
R2O − Al2O3	−3.476	−3.500	−3.498	−3.448	−3.476	−3.430	−3.480	−3.462	−3.454	−3.456
R′O	5.976	5.984	5.988	5.969	5.966	5.946	5.961	5.950	5.963	5.936
Thickness	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400
(mm)
L*	95.33	95.36	95.41	95.42	95.45	95.57	95.64	95.66	95.65	95.81
a*	−1.93	−1.91	−1.9	−1.89	−1.88	−1.8	−1.78	−1.75	−1.7	−1.58
b*	13.03	12.84	12.63	12.52	12.4	11.57	11.3	11.03	10.61	9.76
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25I
Example	TM-135	TM-136	TM-137	TM-138	TM-139	TM-140	TM-141	TM-142	TM-143	TM-144
SiO2	60.576	60.566	60.579	60.603	60.735	60.761	60.731	60.660	60.607	60.663
Al2O3	14.676	14.702	14.695	14.690	14.628	14.622	14.646	14.681	14.746	14.719
B2O3	5.966	5.966	6.031	6.026	6.024	6.024	6.027	6.028	6.006	6.005
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.001	9.002	9.023	9.016	9.013	9.013	9.016	9.018	8.984	8.983
Na2O	2.013	2.026	2.010	2.016	2.015	2.008	2.017	2.008	2.018	2.006
K2O	0.201	0.199	0.202	0.200	0.199	0.200	0.200	0.199	0.199	0.201
MgO	1.483	1.487	1.487	1.488	1.470	1.475	1.474	1.499	1.503	1.505
CaO	4.474	4.474	4.474	4.468	4.452	4.446	4.448	4.465	4.499	4.476
ZnO	0.000	0.000	0.000	0.002	0.002	0.000	0.000	0.002	0.000	0.000
SnO2	0.003	0.003	0.003	0.004	0.003	0.003	0.004	0.003	0.003	0.003
Fe2O3	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006
TiO2	1.106	1.074	0.985	0.974	0.938	0.920	0.911	0.904	0.906	0.905
CeO2	0.488	0.489	0.501	0.501	0.509	0.515	0.516	0.522	0.521	0.524
ZrO2	0.005	0.005	0.005	0.005	0.005	0.005	0.004	0.006	0.004	0.004
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.594	1.563	1.486	1.475	1.447	1.435	1.427	1.426	1.426	1.429
R2O	11.215	11.227	11.235	11.233	11.227	11.222	11.233	11.226	11.200	11.190
Li2O + Na2O	11.014	11.028	11.033	11.032	11.028	11.021	11.034	11.027	11.001	10.989
R2O − Al2O3	−3.461	−3.475	−3.461	−3.457	−3.402	−3.400	−3.413	−3.455	−3.546	−3.529
R′O	5.958	5.961	5.961	5.958	5.924	5.922	5.922	5.965	6.002	5.981
Thickness	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400
(mm)
L*	95.81	95.81	95.86	95.86	95.84	95.82	95.82	95.84	95.84	95.83
a*	−1.59	−1.53	−1.49	−1.47	−1.53	−1.42	−1.41	−1.42	−1.42	−1.41
b*	9.81	9.45	9.28	9.2	9.44	9.04	8.99	9.03	9.07	9.03
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25J
Example	TM-145	TM-146	TM-147	TM-148	TM-149	TM-150	TM-151	TM-152	TM-153	TM-154
SiO2	60.726	60.601	60.720	60.707	60.668	60.678	60.673	60.696	60.659	60.668
Al2O3	14.705	14.758	14.696	14.703	14.697	14.703	14.703	14.666	14.706	14.704
B2O3	6.005	6.008	6.006	6.006	6.013	6.013	6.013	6.011	6.014	6.013
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	8.982	8.987	8.985	8.985	9.024	9.024	9.024	9.021	9.026	9.024
Na2O	2.009	2.018	2.010	2.008	2.016	2.009	2.013	2.009	2.005	2.008
K2O	0.200	0.199	0.199	0.200	0.198	0.198	0.201	0.199	0.199	0.199
MgO	1.498	1.519	1.508	1.509	1.509	1.511	1.506	1.550	1.527	1.527
CaO	4.441	4.469	4.442	4.448	4.440	4.440	4.440	4.427	4.418	4.417
ZnO	0.000	0.002	0.000	0.002	0.000	0.000	0.000	0.000	0.000	0.000
SnO2	0.003	0.003	0.003	0.003	0.003	0.003	0.004	0.004	0.003	0.004
Fe2O3	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006
TiO2	0.902	0.901	0.896	0.894	0.888	0.887	0.884	0.883	0.900	0.897
CeO2	0.519	0.524	0.524	0.525	0.532	0.524	0.528	0.522	0.533	0.528
ZrO2	0.004	0.004	0.004	0.005	0.005	0.005	0.004	0.004	0.005	0.005
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.421	1.426	1.420	1.418	1.420	1.411	1.411	1.406	1.433	1.425
R2O	11.191	11.205	11.193	11.193	11.238	11.230	11.238	11.229	11.229	11.231
Li2O + Na2O	10.991	11.006	10.994	10.993	11.040	11.032	11.037	11.030	11.030	11.032
R2O − Al2O3	−3.514	−3.553	−3.503	−3.510	−3.459	−3.472	−3.466	−3.437	−3.476	−3.473
R′O	5.939	5.990	5.950	5.959	5.949	5.951	5.946	5.978	5.945	5.944
Thickness	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400
(mm)
L*	95.85	95.84	95.84	95.85	95.85	95.87	95.85	95.87	95.85	95.87
a*	−1.41	−1.41	−1.41	−1.41	−1.4	−1.4	−1.4	−1.39	−1.4	−1.39
b*	9.01	9.03	8.99	9.02	8.97	8.93	8.93	8.89	8.93	8.84
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25K
Example	TM-155	TM-156	TM-157	TM-158	TM-159	TM-160	TM-161	TM-162	TM-163	TM-164
SiO2	60.669	60.684	60.652	60.705	60.708	60.663	60.672	60.718	60.695	60.765
Al2O3	14.704	14.681	14.707	14.679	14.679	14.692	14.728	14.714	14.720	14.679
B2O3	6.014	6.021	6.022	6.018	6.018	6.018	6.007	6.006	6.006	6.004
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.025	9.022	9.023	9.017	9.017	9.017	8.963	8.962	8.962	8.960
Na2O	2.010	2.008	2.015	2.005	2.003	2.003	2.006	2.007	2.010	2.007
K2O	0.199	0.199	0.198	0.199	0.198	0.198	0.199	0.197	0.200	0.199
MgO	1.525	1.533	1.536	1.541	1.538	1.554	1.550	1.543	1.540	1.538
CaO	4.418	4.416	4.417	4.409	4.414	4.421	4.431	4.419	4.430	4.418
ZnO	0.000	0.000	0.000	0.001	0.000	0.002	0.000	0.000	0.000	0.000
SnO2	0.004	0.003	0.003	0.004	0.003	0.004	0.004	0.004	0.003	0.003
Fe2O3	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006
TiO2	0.894	0.893	0.893	0.889	0.888	0.894	0.897	0.889	0.897	0.891
CeO2	0.528	0.527	0.524	0.523	0.525	0.524	0.533	0.530	0.527	0.525
ZrO2	0.004	0.004	0.004	0.005	0.004	0.005	0.005	0.004	0.004	0.004
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.422	1.420	1.417	1.411	1.413	1.418	1.430	1.419	1.424	1.416
R2O	11.234	11.230	11.235	11.221	11.218	11.218	11.168	11.167	11.172	11.166
Li2O + Na2O	11.035	11.031	11.038	11.022	11.020	11.021	10.970	10.970	10.972	10.967
R2O − Al2O3	−3.470	−3.451	−3.472	−3.458	−3.460	−3.474	−3.560	−3.547	−3.548	−3.513
R′O	5.943	5.949	5.953	5.952	5.952	5.976	5.981	5.962	5.970	5.956
Thickness	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400
(mm)
L*	95.87	95.87	95.87	95.85	95.87	95.86	95.87	95.88	95.87	95.81
a*	−1.38	−1.38	−1.38	−1.38	−1.38	−1.38	−1.38	−1.38	−1.38	−1.37
b*	8.83	8.81	8.83	8.82	8.84	8.82	8.79	8.78	8.81	8.8
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25L
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	165	166	167	168	169	170	171	172	173	174
SiO2	60.799	60.679	60.695	60.729	60.761	60.660	60.675	60.669	60.706	60.775
Al2O3	14.665	14.730	14.714	14.693	14.672	14.721	14.707	14.688	14.671	14.680
B2O3	6.004	6.007	6.015	6.014	6.013	6.015	6.015	6.010	6.008	5.974
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	8.959	8.964	8.962	8.961	8.960	8.963	8.962	9.041	9.037	9.000
Na2O	2.007	2.008	2.010	2.002	2.009	2.016	2.010	2.002	2.004	2.006
K2O	0.199	0.199	0.199	0.199	0.198	0.199	0.199	0.200	0.198	0.199
MgO	1.535	1.546	1.551	1.552	1.548	1.558	1.551	1.536	1.525	1.504
CaO	4.406	4.425	4.417	4.413	4.406	4.430	4.442	4.426	4.425	4.439
ZnO	0.000	0.002	0.002	0.002	0.000	0.000	0.000	0.000	0.000	0.000
SnO2	0.003	0.003	0.003	0.003	0.004	0.003	0.004	0.003	0.003	0.004
Fe2O3	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006
TiO2	0.889	0.891	0.890	0.889	0.889	0.889	0.889	0.880	0.880	0.888
CeO2	0.524	0.534	0.531	0.532	0.530	0.534	0.535	0.535	0.533	0.521
ZrO2	0.004	0.005	0.005	0.004	0.004	0.005	0.005	0.004	0.004	0.005
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.413	1.425	1.422	1.422	1.419	1.423	1.424	1.415	1.412	1.409
R2O	11.165	11.171	11.171	11.162	11.166	11.178	11.171	11.243	11.239	11.204
Li2O + Na2O	10.966	10.972	10.972	10.963	10.968	10.978	10.972	11.043	11.041	11.006
R2O − Al2O3	−3.501	−3.559	−3.543	−3.531	−3.506	−3.544	−3.536	−3.446	−3.431	−3.475
R′O	5.941	5.973	5.970	5.967	5.954	5.988	5.993	5.962	5.950	5.943
Thickness	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400
(mm)
L*	95.87	95.86	95.87	95.86	95.86	95.84	95.85	95.85	95.85	95.91
a*	−1.37	−1.38	−1.38	−1.38	−1.38	−1.38	−1.38	−1.38	−1.38	−1.36
b*	8.77	8.8	8.79	8.8	8.81	8.86	8.84	8.84	8.83	8.58
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25M
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	175	176	177	178	179	180	181	182	183	184
SiO2	60.747	60.799	60.778	60.734	60.742	60.783	60.797	60.807	60.903	60.905
Al2O3	14.692	14.685	14.688	14.699	14.705	14.689	14.693	14.692	14.633	14.672
B2O3	5.974	5.974	5.975	5.991	5.990	5.989	5.988	5.988	5.984	6.001
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	8.999	8.999	9.001	9.018	9.018	9.016	9.014	9.013	9.008	8.984
Na2O	2.011	2.003	2.011	2.009	2.008	2.004	2.010	2.013	2.001	2.008
K2O	0.201	0.199	0.201	0.201	0.201	0.200	0.200	0.199	0.200	0.200
MgO	1.510	1.493	1.494	1.492	1.487	1.492	1.485	1.485	1.486	1.493
CaO	4.450	4.441	4.450	4.465	4.460	4.450	4.447	4.447	4.444	4.431
ZnO	0.000	0.002	0.002	0.002	0.000	0.002	0.000	0.001	0.000	0.000
SnO2	0.004	0.004	0.004	0.004	0.004	0.004	0.004	0.004	0.004	0.003
Fe2O3	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006
TiO2	0.888	0.884	0.884	0.887	0.888	0.883	0.887	0.884	0.887	0.887
CeO2	0.513	0.508	0.503	0.489	0.486	0.479	0.464	0.457	0.441	0.408
ZrO2	0.005	0.004	0.005	0.004	0.005	0.004	0.004	0.004	0.004	0.004
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.401	1.392	1.386	1.376	1.374	1.362	1.352	1.341	1.328	1.294
R2O	11.211	11.201	11.213	11.228	11.226	11.220	11.223	11.225	11.209	11.191
Li2O + Na2O	11.011	11.002	11.012	11.027	11.026	11.019	11.024	11.026	11.009	10.991
R2O − Al2O3	−3.481	−3.484	−3.475	−3.471	−3.479	−3.470	−3.470	−3.467	−3.423	−3.482
R′O	5.961	5.936	5.945	5.958	5.947	5.944	5.932	5.933	5.930	5.924
Thickness	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400	2.400
(mm)
L*	95.91	95.95	95.96	96.05	96.03	96.08	95.85	96.15	96.19	96.29
a*	−1.34	−1.33	−1.32	−1.29	−1.28	−1.27	−1.22	−1.22	−1.19	−1.1
b*	8.44	8.32	8.21	7.88	7.86	7.67	7.4	7.26	6.97	6.29
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25N
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	185	186	187	188	189	190	191	192	193	194
SiO2	60.915	60.903	61.594	61.212	61.723	61.723	61.723	61.723	61.566	61.654
Al2O3	14.675	14.680	15.016	14.863	14.763	14.763	14.763	14.763	14.849	14.808
B2O3	5.999	5.999	5.254	5.238	5.275	5.275	5.275	5.275	5.271	5.266
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	8.982	8.981	9.695	9.665	9.147	9.147	9.147	9.147	9.142	9.132
Na2O	2.011	2.013	3.772	2.563	2.244	2.244	2.244	2.244	2.094	2.153
K2O	0.199	0.199	0.066	0.154	0.181	0.181	0.181	0.181	0.194	0.190
MgO	1.496	1.496	0.477	1.178	1.334	1.334	1.334	1.334	1.429	1.375
CaO	4.428	4.441	3.499	4.167	4.313	4.313	4.313	4.313	4.423	4.400
ZnO	0.001	0.000	0.000	0.008	0.016	0.016	0.016	0.016	0.024	0.024
SnO2	0.003	0.004	0.115	0.087	0.046	0.046	0.046	0.046	0.026	0.038
Fe2O3	0.006	0.006	0.007	0.005	0.004	0.004	0.004	0.004	0.004	0.004
TiO2	0.886	0.886	0.188	0.474	0.549	0.549	0.549	0.549	0.587	0.562
CeO2	0.395	0.389	0.113	0.292	0.344	0.344	0.344	0.344	0.368	0.352
ZrO2	0.004	0.004	0.202	0.089	0.058	0.058	0.058	0.058	0.024	0.037
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.281	1.275	0.301	0.766	0.893	0.893	0.893	0.893	0.955	0.914
R2O	11.192	11.193	13.533	12.383	11.572	11.572	11.572	11.572	11.429	11.476
Li2O + Na2O	10.993	10.994	13.467	12.229	11.391	11.391	11.391	11.391	11.235	11.286
R2O − Al2O3	−3.484	−3.487	−1.483	−2.480	−3.191	−3.191	−3.191	−3.191	−3.419	−3.332
R′O	5.925	5.937	3.976	5.353	5.662	5.662	5.662	5.662	5.876	5.799
Thickness	2.400	2.400	4.127	4.024	4.354	3.967	4.238	4.057	4.025	4.010
(mm)
L*	96.32	96.21	96.54	96.42	96.22	96.19	96.3	96.28	96.1	96.19
a*	−1.06	−1.03	−0.14	−0.39	−0.71	−0.69	−0.7	−0.71	−0.95	−0.76
b*	6.06	5.92	0.72	2.2	4.11	3.99	4.02	4.06	5.52	4.33
Density			2.419		2.429	2.429	2.429	2.429
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25O
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	195	196	197	198	199	200	201	202	203	204
SiO2	61.220	61.167	61.145	61.056	61.074	60.985	60.554	60.376	60.288	60.985
Al2O3	14.708	14.714	14.714	14.757	14.730	14.689	14.728	14.704	14.690	14.689
B2O3	5.980	5.975	5.975	5.975	5.976	6.003	6.012	6.012	6.051	6.003
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.074	9.066	9.066	9.066	9.068	9.109	9.122	9.123	9.083	9.109
Na2O	2.136	2.017	1.988	1.976	1.979	2.005	2.003	1.985	1.983	2.005
K2O	0.186	0.196	0.200	0.200	0.200	0.201	0.202	0.200	0.202	0.201
MgO	1.368	1.457	1.459	1.488	1.496	1.516	1.500	1.497	1.504	1.516
CaO	4.357	4.436	4.443	4.467	4.450	4.471	4.491	4.492	4.493	4.471
ZnO	0.008	0.016	0.016	0.016	0.016	0.024	0.016	0.024	0.016	0.024
SnO2	0.043	0.012	0.013	0.012	0.023	0.025	0.015	0.016	0.017	0.025
Fe2O3	0.004	0.004	0.004	0.004	0.003	0.004	0.003	0.003	0.003	0.004
TiO2	0.547	0.581	0.592	0.597	0.597	0.595	0.962	1.172	1.271	0.595
CeO2	0.329	0.341	0.367	0.368	0.366	0.368	0.385	0.391	0.390	0.368
ZrO2	0.041	0.014	0.014	0.014	0.019	0.005	0.002			0.005
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	0.876	0.922	0.960	0.966	0.963	0.963	1.347	1.563	1.661	0.963
R2O	11.396	11.279	11.254	11.242	11.247	11.316	11.327	11.308	11.267	11.316
Li2O + Na2O	11.210	11.083	11.054	11.042	11.047	11.115	11.125	11.108	11.066	11.115
R2O − Al2O3	−3.312	−3.435	−3.459	−3.515	−3.483	−3.373	−3.401	−3.396	−3.423	−3.373
R′O	5.733	5.909	5.917	5.970	5.961	6.010	6.007	6.013	6.012	6.010
Thickness	4.063	4.071	4.177	4.123	4.387	4.114	4.191	4.286	3.986	2.441
(mm)
L*	96.26	96.07	96.05	96.04	96.07	96.1	95.79	95.61	95.64	96.29
a*	−0.71	−0.92	−1.02	−1.02	−0.99	−1.01	−1.5	−1.81	−1.92	−0.63
b*	3.98	5.31	5.94	5.94	5.73	5.8	8.64	10.49	11.13	3.67
Density	2.427	2.427		2.429	2.430	2.430		2.437	2.439	2.430
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25P
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	205	206	207	208	209	210	211	212	213	214
SiO2	60.554	60.376	60.288	60.152	60.135	60.130	60.007	60.152	60.135	60.130
Al2O3	14.728	14.704	14.690	14.713	14.694	14.683	14.684	14.713	14.694	14.683
B2O3	6.012	6.012	6.051	6.063	6.061	6.061	6.075	6.063	6.061	6.061
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.122	9.123	9.083	9.101	9.097	9.098	9.199	9.101	9.097	9.098
Na2O	2.003	1.985	1.983	1.987	1.986	1.973	1.954	1.987	1.986	1.973
K2O	0.202	0.200	0.202	0.201	0.204	0.203	0.202	0.201	0.204	0.203
MgO	1.500	1.497	1.504	1.504	1.501	1.487	1.491	1.504	1.501	1.487
CaO	4.491	4.492	4.493	4.499	4.486	4.485	4.491	4.499	4.486	4.485
ZnO	0.016	0.024	0.016	0.024	0.024	0.024	0.016	0.024	0.024	0.024
SnO2	0.015	0.016	0.017	0.015	0.019	0.022	0.018	0.015	0.019	0.022
Fe2O3	0.003	0.003	0.003	0.003	0.003	0.004	0.004	0.003	0.003	0.004
TiO2	0.962	1.172	1.271	1.343	1.399	1.433	1.462	1.343	1.399	1.433
CeO2	0.385	0.391	0.390	0.390	0.384	0.389	0.389	0.390	0.384	0.389
ZrO2	0.002				0.003	0.004	0.003		0.003	0.004
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.347	1.563	1.661	1.733	1.783	1.822	1.852	1.733	1.783	1.822
R2O	11.327	11.308	11.267	11.289	11.287	11.273	11.355	11.289	11.287	11.273
Li2O + Na2O	11.125	11.108	11.066	11.088	11.083	11.070	11.153	11.088	11.083	11.070
R2O − Al2O3	−3.401	−3.396	−3.423	−3.424	−3.407	−3.410	−3.329	−3.424	−3.407	−3.410
R′O	6.007	6.013	6.012	6.027	6.011	5.996	5.997	6.027	6.011	5.996
Thickness	2.453	2.444	2.451	4.294	4.203	4.375	4.076	2.400	2.421	2.420
(mm)
L*	96.14	96.07	96.02	95.56	95.62	95.61	95.49	96.03	96.04	96.01
a*	−0.99	−1.16	−1.26	−2.08	−2.06	−2.16	−2.25	−1.32	−1.37	−1.41
b*	5.6	6.53	7.12	12.16	11.93	12.57	13.31	7.4	7.63	7.84
Density		2.437	2.439	2.440		2.440		2.440		2.440
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25Q
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	215	216	217	218	219	220	221	222	223	224
SiO2	60.007	60.059	59.947	59.925	59.694	60.059	59.947	59.925	59.694	59.634
Al2O3	14.684	14.657	14.686	14.672	14.706	14.657	14.686	14.672	14.706	14.690
B2O3	6.075	6.064	6.079	6.070	6.078	6.064	6.079	6.070	6.078	6.082
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.199	9.182	9.204	9.191	9.195	9.182	9.204	9.191	9.195	9.201
Na2O	1.954	1.959	1.981	1.980	1.967	1.959	1.981	1.980	1.967	1.964
K2O	0.202	0.201	0.203	0.206	0.205	0.201	0.203	0.206	0.205	0.203
MgO	1.491	1.491	1.495	1.493	1.502	1.491	1.495	1.493	1.502	1.483
CaO	4.491	4.464	4.492	4.481	4.496	4.464	4.492	4.481	4.496	4.485
ZnO	0.016	0.024	0.016	0.032	0.048	0.024	0.016	0.032	0.048	0.056
SnO2	0.018	0.022	0.019	0.012	0.014	0.022	0.019	0.012	0.014	0.015
Fe2O3	0.004	0.003	0.003	0.003	0.002	0.003	0.003	0.003	0.002	0.002
TiO2	1.462	1.468	1.482	1.490	1.497	1.468	1.482	1.490	1.497	1.504
CeO2	0.389	0.394	0.391	0.439	0.586	0.394	0.391	0.439	0.586	0.681
ZrO2	0.003	0.006	0.001	0.001		0.006	0.001	0.001
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.852	1.862	1.873	1.929	2.083	1.862	1.873	1.929	2.083	2.184
R2O	11.355	11.342	11.388	11.378	11.367	11.342	11.388	11.378	11.367	11.368
Li2O + Na2O	11.153	11.141	11.185	11.171	11.162	11.141	11.185	11.171	11.162	11.165
R2O − Al2O3	−3.329	−3.315	−3.298	−3.294	−3.340	−3.315	−3.298	−3.294	−3.340	−3.322
R′O	5.997	5.979	6.003	6.006	6.046	5.979	6.003	6.006	6.046	6.024
Thickness	2.423	4.163	4.353	4.547	4.077	2.444	2.459	2.448	2.425	4.414
(mm)
L*	95.98	95.39	95.46	95.07	94.15	95.94	95.92	95.74	95.14	93.33
a*	−1.46	−2.28	−2.27	−2.59	−3	−1.49	−1.53	−1.73	−2.17	−3.15
b*	8.19	13.49	13.41	16.27	21.96	8.33	8.57	10.16	14.23	26.17
Density		2.441		2.443		2.441		2.443		2.456
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25R
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	225	226	227	228	229	230	231	232	233	234
SiO2	59.620	59.511	59.558	59.634	59.620	59.511	59.558	59.578	59.529	59.531
Al2O3	14.682	14.725	14.762	14.690	14.682	14.725	14.762	14.727	14.766	14.745
B2O3	6.083	6.086	6.072	6.082	6.083	6.086	6.072	6.084	6.073	6.078
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.204	9.207	9.084	9.201	9.204	9.207	9.084	9.102	9.086	9.093
Na2O	1.986	1.974	1.974	1.964	1.986	1.974	1.974	1.971	1.970	1.986
K2O	0.202	0.200	0.201	0.203	0.202	0.200	0.201	0.204	0.205	0.207
MgO	1.469	1.497	1.482	1.483	1.469	1.497	1.482	1.490	1.510	1.490
CaO	4.470	4.496	4.507	4.485	4.470	4.496	4.507	4.503	4.504	4.507
ZnO	0.048	0.048	0.064	0.056	0.048	0.048	0.064	0.048	0.056	0.064
SnO2	0.023	0.015	0.021	0.015	0.023	0.015	0.021	0.022	0.021	0.019
Fe2O3	0.002	0.002	0.002	0.002	0.002	0.002	0.002	0.002	0.001	0.001
TiO2	1.501	1.505	1.504	1.504	1.501	1.505	1.504	1.509	1.512	1.506
CeO2	0.704	0.729	0.757	0.681	0.704	0.729	0.757	0.756	0.763	0.769
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	2.205	2.234	2.261	2.184	2.205	2.234	2.261	2.265	2.274	2.275
R2O	11.392	11.382	11.259	11.368	11.392	11.382	11.259	11.277	11.261	11.286
Li2O + Na2O	11.190	11.181	11.058	11.165	11.190	11.181	11.058	11.073	11.056	11.079
R2O − Al2O3	−3.289	−3.343	−3.503	−3.322	−3.289	−3.343	−3.503	−3.450	−3.504	−3.459
R′O	5.987	6.041	6.053	6.024	5.987	6.041	6.053	6.041	6.070	6.061
Thickness	4.551	4.166	4.152	2.482	2.478	2.454	2.423	4.194	4.282	4.847
(mm)
L*	93.19	92.97	92.74	94.62	94.58	94.36	94.27	92.73	92.66	92.63
a*	−3.19	−3.17	−3.2	−2.4	−2.42	−2.48	−2.5	−3.19	−3.21	−3.2
b*	27.13	28.08	29.2	17.11	17.47	18.53	18.96	29.21	29.67	29.65
Density		2.459	2.461	2.456		2.459	2.461	2.461		2.462
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25S
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	235	236	237	238	239	240	241	242	243	244
SiO2	59.645	59.578	59.529	59.531	59.645	59.759	59.810	60.264	60.495	60.007
Al2O3	14.728	14.727	14.766	14.745	14.728	14.750	14.715	14.777	14.795	14.684
B2O3	6.084	6.084	6.073	6.078	6.084	6.080	6.079	6.075	6.062	6.075
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.037	9.102	9.086	9.093	9.037	9.031	9.029	9.024	9.047	9.199
Na2O	1.958	1.971	1.970	1.986	1.958	1.962	1.976	1.996	1.983	1.954
K2O	0.205	0.204	0.205	0.207	0.205	0.204	0.205	0.206	0.202	0.202
MgO	1.487	1.490	1.510	1.490	1.487	1.489	1.481	1.493	1.491	1.491
CaO	4.497	4.503	4.504	4.507	4.497	4.505	4.494	4.524	4.521	4.491
ZnO	0.064	0.048	0.056	0.064	0.064	0.064	0.056	0.056	0.056	0.016
SnO2	0.019	0.022	0.021	0.019	0.019	0.025	0.030	0.021	0.013	0.018
Fe2O3	0.001	0.002	0.001	0.001	0.001	0.001	0.001	0.001	0.001	0.004
TiO2	1.501	1.509	1.512	1.506	1.501	1.358	1.358	0.793	0.558	1.462
CeO2	0.765	0.756	0.763	0.769	0.765	0.768	0.766	0.769	0.771	0.389
ZrO2										0.003
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	2.267	2.265	2.274	2.275	2.267	2.126	2.124	1.563	1.329	1.852
R2O	11.200	11.277	11.261	11.286	11.200	11.197	11.210	11.225	11.232	11.355
Li2O + Na2O	10.994	11.073	11.056	11.079	10.994	10.993	11.005	11.020	11.030	11.153
R2O − Al2O3	−3.528	−3.450	−3.504	−3.459	−3.528	−3.553	−3.505	−3.552	−3.562	−3.329
R′O	6.048	6.041	6.070	6.061	6.048	6.058	6.031	6.073	6.068	5.997
Thickness	4.210	2.386	2.393	2.375	2.410	4.140	4.393	4.160	4.192	4.248
(mm)
L*	92.66	94.28	94.27	94.27	94.28	92.93	93.19	93.99	94.22	94.67
a*	−3.21	−2.48	−2.48	−2.47	−2.47	−3.07	−2.97	−2.05	−1.72	−2.94
b*	29.76	18.74	18.77	18.73	18.72	27.63	25.82	17.53	15.2	20.12
Density	2.461	2.461		2.462	2.461	2.459		2.453	2.449
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25T
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	245	246	247	248	249	250	251	252	253	254
SiO2	60.007	59.645	59.645	59.759	59.810	60.264	60.495	60.539	60.584	60.764
Al2O3	14.684	14.728	14.728	14.750	14.715	14.777	14.795	14.803	14.774	14.751
B2O3	6.075	6.084	6.084	6.080	6.079	6.075	6.062	6.047	6.048	6.030
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.199	9.037	9.037	9.031	9.029	9.024	9.047	9.025	9.027	8.941
Na2O	1.954	1.958	1.958	1.962	1.976	1.996	1.983	1.992	2.004	1.980
K2O	0.202	0.205	0.205	0.204	0.205	0.206	0.202	0.204	0.205	0.204
MgO	1.491	1.487	1.487	1.489	1.481	1.493	1.491	1.492	1.476	1.464
CaO	4.491	4.497	4.497	4.505	4.494	4.524	4.521	4.530	4.511	4.502
ZnO	0.016	0.064	0.064	0.064	0.056	0.056	0.056	0.056	0.051	0.055
SnO2	0.018	0.019	0.019	0.025	0.030	0.021	0.013	0.014	0.018	0.015
Fe2O3	0.004	0.001	0.001	0.001	0.001	0.001	0.001	0.001	0.002	0.002
TiO2	1.462	1.501	1.501	1.358	1.358	0.793	0.558	0.526	0.526	0.518
CeO2	0.389	0.765	0.765	0.768	0.766	0.769	0.771	0.768	0.772	0.771
ZrO2	0.003
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.852	2.267	2.267	2.126	2.124	1.563	1.329	1.295	1.297	1.289
R2O	11.355	11.200	11.200	11.197	11.210	11.225	11.232	11.220	11.235	11.125
Li2O + Na2O	11.153	10.994	10.994	10.993	11.005	11.020	11.030	11.016	11.030	10.921
R2O − Al2O3	−3.329	−3.528	−3.528	−3.553	−3.505	−3.552	−3.562	−3.582	−3.539	−3.626
R′O	5.997	6.048	6.048	6.058	6.031	6.073	6.068	6.077	6.038	6.021
Thickness	4.242	4.220	4.685	2.420	2.403	2.365	2.406	4.160	4.388	4.256
(mm)
L*	94.23	88.92	86.3	94.38	94.5	95.05	95.18	94.17	94.21	94.28
a*	−3.04	−2.7	−1.69	−2.33	−2.25	−1.44	−1.19	−1.68	−1.64	−1.63
b*	22.54	45.61	53.12	17.56	16.74	11.04	9.5	15.04	14.7	14.59
Density		2.461	2.461	2.459		2.453	2.449		2.449	2.448
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25U
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	255	256	257	258	259	260	261	262	263	264
SiO2	60.539	60.584	60.764	60.726	60.727	60.722	60.582	60.726	60.727	60.722
Al2O3	14.803	14.774	14.751	14.753	14.741	14.746	14.729	14.753	14.741	14.746
B2O3	6.047	6.048	6.030	6.034	6.034	6.033	6.085	6.034	6.034	6.033
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.025	9.027	8.941	8.947	8.947	8.946	9.005	8.947	8.947	8.946
Na2O	1.992	2.004	1.980	1.993	2.014	2.003	2.023	1.993	2.014	2.003
K2O	0.204	0.205	0.204	0.204	0.205	0.201	0.203	0.204	0.205	0.201
MgO	1.492	1.476	1.464	1.466	1.466	1.473	1.662	1.466	1.466	1.473
CaO	4.530	4.511	4.502	4.505	4.498	4.507	4.330	4.505	4.498	4.507
ZnO	0.056	0.051	0.055	0.054	0.056	0.058	0.065	0.054	0.056	0.058
SnO2	0.014	0.018	0.015	0.018	0.015	0.013	0.014	0.018	0.015	0.013
Fe2O3	0.001	0.002	0.002	0.002	0.001	0.001	0.001	0.002	0.001	0.001
TiO2	0.526	0.526	0.518	0.519	0.514	0.513	0.513	0.519	0.514	0.513
CeO2	0.768	0.772	0.771	0.775	0.775	0.780	0.783	0.775	0.775	0.780
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.295	1.297	1.289	1.293	1.289	1.293	1.295	1.293	1.289	1.293
R2O	11.220	11.235	11.125	11.143	11.166	11.149	11.231	11.143	11.166	11.149
Li2O + Na2O	11.016	11.030	10.921	10.939	10.960	10.949	11.028	10.939	10.960	10.949
R2O − Al2O3	−3.582	−3.539	−3.626	−3.610	−3.575	−3.596	−3.498	−3.610	−3.575	−3.596
R′O	6.077	6.038	6.021	6.025	6.020	6.038	6.057	6.025	6.020	6.038
Thickness	2.417	2.418	2.444	4.380	4.072	4.378	4.870	2.426	2.421	2.347
(mm)
L*	95.22	95.18	95.19	94.18	94.14	94.12	94.17	95.15	95.12	95.14
a*	−1.16	−1.15	−1.16	−1.65	−1.67	−1.67	−1.67	−1.16	−1.15	−1.13
b*	9.3	9.35	9.39	15.04	15.31	15.34	15.23	9.48	9.53	9.33
Density		2.449	2.448	2.449		2.449	2.448	2.449		2.449
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25V
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	265	266	267	268	269	270	271	272	273	274
SiO2	60.582	60.596	60.718	60.784	60.787	60.748	60.743	60.678	60.746	61.209
Al2O3	14.729	14.743	14.739	14.704	14.740	14.736	14.755	14.736	14.767	14.903
B2O3	6.085	6.072	6.052	5.995	5.981	5.992	5.989	6.019	6.029	6.048
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.005	8.986	8.956	9.047	9.027	9.043	9.039	9.092	9.107	9.136
Na2O	2.023	2.005	1.996	1.989	1.991	1.995	1.980	1.985	1.995	2.007
K2O	0.203	0.205	0.201	0.200	0.195	0.198	0.200	0.201	0.200	0.200
MgO	1.662	2.519	3.593	3.986	4.249	4.247	4.344	4.313	4.194	3.537
CaO	4.330	3.495	2.393	1.943	1.685	1.672	1.600	1.613	1.595	1.580
ZnO	0.065	0.059	0.051	0.051	0.046	0.047	0.049	0.053	0.054	0.055
SnO2	0.014	0.019	0.011	0.013	0.012	0.020	0.011	0.016	0.023	0.019
Fe2O3	0.001	0.001	0.002	0.001	0.002	0.002	0.002	0.002	0.002	0.001
TiO2	0.513	0.513	0.509	0.506	0.506	0.508	0.508	0.506	0.505	0.509
CeO2	0.783	0.781	0.779	0.770	0.775	0.782	0.775	0.777	0.776	0.790
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.295	1.294	1.288	1.277	1.281	1.290	1.283	1.283	1.282	1.299
R2O	11.231	11.195	11.154	11.236	11.212	11.236	11.219	11.278	11.303	11.344
Li2O + Na2O	11.028	10.991	10.952	11.036	11.017	11.038	11.019	11.077	11.103	11.143
R2O − Al2O3	−3.498	−3.548	−3.585	−3.469	−3.529	−3.500	−3.535	−3.459	−3.464	−3.559
R′O	6.057	6.073	6.037	5.980	5.980	5.966	5.993	5.979	5.844	5.171
Thickness	2.421	4.189	4.423	4.260	4.165	4.146	4.190	4.170	4.180	4.194
(mm)
L*	95.13	94.35	94.58	94.8	94.76	94.78	94.75	94.75	94.71	94.51
a*	−1.16	−1.72	−1.77	−1.78	−1.83	−1.81	−1.85	−1.82	−1.79	−1.74
b*	9.58	14.79	14.19	13.48	13.89	13.69	14.02	13.79	13.72	14.37
Density	2.448		2.439		2.436		2.436		2.436
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25W
	Example
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
	275	276	277	278	279	280	281	282	283	284
SiO2	61.198	60.698	60.742	60.693	60.701	60.455	60.382	60.392	60.334	60.509
Al2O3	14.923	14.833	14.825	14.844	14.835	14.859	14.835	14.829	14.841	14.837
B2O3	6.064	5.985	5.976	5.986	5.990	6.176	6.201	6.198	6.203	6.048
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.160	9.918	9.904	9.920	9.927	9.930	9.969	9.966	9.974	9.971
Na2O	2.012	1.985	1.982	1.983	1.979	1.978	1.994	1.980	1.975	1.973
K2O	0.206	0.201	0.203	0.199	0.200	0.203	0.206	0.201	0.206	0.203
MgO	3.493	3.468	3.454	3.461	3.090	2.719	1.422	1.269	0.981	0.909
CaO	1.577	1.552	1.547	1.546	1.910	2.307	3.613	3.782	4.101	4.149
ZnO	0.045	0.050	0.049	0.053	0.050	0.054	0.051	0.055	0.059	0.069
SnO2	0.020	0.022	0.017	0.017	0.014	0.018	0.018	0.020	0.020	0.018
Fe2O3	0.001	0.001	0.001	0.001	0.001	0.001	0.001	0.001	0.001	0.001
TiO2	0.512	0.510	0.511	0.512	0.510	0.512	0.520	0.519	0.518	0.520
CeO2	0.783	0.772	0.784	0.779	0.786	0.782	0.784	0.782	0.785	0.788
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.294	1.281	1.295	1.291	1.296	1.294	1.303	1.302	1.303	1.308
R2O	11.379	12.104	12.089	12.103	12.106	12.112	12.169	12.147	12.155	12.147
Li2O + Na2O	11.173	11.903	11.886	11.904	11.906	11.908	11.963	11.946	11.949	11.943
R2O − Al2O3	−3.544	−2.730	−2.736	−2.741	−2.728	−2.747	−2.666	−2.682	−2.686	−2.691
R′O	5.116	5.070	5.049	5.061	5.051	5.081	5.087	5.106	5.141	5.127
Thickness	4.614	4.276	4.301	5.387	4.217	4.340	4.301	4.267	4.995	4.099
(mm)
L*	94.55	94.54	94.45	94.45	94.36	94.19	93.92	93.74	93.84	93.72
a*	−1.72	−1.74	−1.76	−1.75	−1.69	−1.72	−1.63	−1.59	−1.58	−1.56
b*	14.15	14.3	14.68	14.51	14.61	15.38	15.74	16.03	16.09	16.23
Density	2.431	2.431	2.431		2.433	2.436	2.442		2.444	2.445
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25X
	Example
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
	285	286	287	288	289	290	291	292	293	294
SiO2	60.571	60.555	60.483	60.662	60.562	60.471	60.403	60.151	60.028	60.072
Al2O3	14.776	14.799	14.849	14.790	14.811	14.820	14.761	14.736	14.724	14.661
B2O3	6.049	6.051	6.053	5.923	5.924	5.920	5.917	6.009	5.998	5.993
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.972	9.975	9.979	9.994	9.995	9.989	9.983	10.074	10.057	10.048
Na2O	2.004	1.986	1.988	2.000	1.991	1.995	1.997	1.985	2.043	2.026
K2O	0.203	0.203	0.203	0.203	0.205	0.204	0.203	0.205	0.205	0.205
MgO	0.824	0.701	0.626	0.597	0.593	0.559	0.524	0.517	0.510	0.516
CaO	4.212	4.348	4.433	4.443	4.476	4.517	4.549	4.555	4.564	4.527
ZnO	0.056	0.055	0.062	0.053	0.052	0.060	0.052	0.036	0.000	0.000
SnO2	0.022	0.019	0.018	0.022	0.021	0.020	0.015	0.014	0.015	0.009
Fe2O3	0.001	0.002	0.002	0.001	0.001	0.002	0.002	0.002	0.006	0.006
TiO2	0.518	0.517	0.520	0.519	0.605	0.715	0.955	1.148	1.342	1.510
CeO2	0.787	0.784	0.783	0.787	0.753	0.717	0.631	0.558	0.484	0.399
ZrO2									0.011	0.011
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.305	1.301	1.303	1.306	1.359	1.432	1.585	1.705	1.826	1.910
R2O	12.179	12.164	12.170	12.197	12.191	12.188	12.183	12.264	12.305	12.280
Li2O + Na2O	11.976	11.961	11.966	11.994	11.986	11.984	11.980	12.060	12.100	12.074
R2O − Al2O3	−2.597	−2.635	−2.679	−2.592	−2.620	−2.633	−2.578	−2.472	−2.418	−2.381
R′O	5.092	5.104	5.121	5.093	5.122	5.136	5.125	5.108	5.074	5.044
Thickness	4.197	4.298	4.167	4.363	4.125	4.122	4.158	4.281	4.159	3.964
(mm)
L*	93.75	93.71	93.64	93.7	93.88	93.95	94.17	94.36	94.69	95.1
a*	−1.56	−1.55	−1.56	−1.54	−1.69	−1.85	−2.2	−2.45	−2.6	−2.52
b*	16.22	16.4	16.57	16.29	16.68	16.98	17.87	18.42	18.03	16.21
Density	2.444		2.446	2.445	2.446		2.443	2.442	2.441
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25Y
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	295	296	297	298	299	300	301	302	303	304
SiO2	60.087	60.055	60.095	60.116	60.153	60.168	60.145	60.118	60.140	60.190
Al2O3	14.651	14.728	14.688	14.686	14.656	14.675	14.666	14.690	14.688	14.665
B2O3	5.989	5.983	5.987	5.984	5.985	5.974	5.973	5.959	5.969	5.961
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	10.042	9.961	9.968	9.963	9.963	9.933	9.931	9.909	9.925	9.926
Na2O	2.027	2.036	2.031	2.036	2.040	2.032	2.044	2.049	2.032	2.032
K2O	0.203	0.205	0.206	0.203	0.204	0.203	0.204	0.203	0.201	0.203
MgO	0.518	0.516	0.517	0.517	0.508	0.510	0.511	0.512	0.510	0.506
CaO	4.523	4.545	4.531	4.521	4.510	4.521	4.524	4.535	4.533	4.527
ZnO	0.000	0.000	0.000	0.000	0.001	0.001	0.001	0.000	0.000	0.000
SnO2	0.012	0.012	0.015	0.017	0.017	0.016	0.028	0.034	0.024	0.020
Fe2O3	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006
TiO2	1.512	1.525	1.531	1.526	1.526	1.536	1.535	1.540	1.539	1.537
CeO2	0.401	0.398	0.394	0.392	0.398	0.395	0.396	0.402	0.397	0.399
ZrO2	0.014	0.014	0.015	0.017	0.019	0.015	0.021	0.027	0.020	0.015
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.913	1.923	1.925	1.918	1.924	1.932	1.931	1.943	1.937	1.936
R2O	12.272	12.202	12.205	12.202	12.207	12.168	12.180	12.161	12.159	12.161
Li2O + Na2O	12.069	11.997	11.999	11.999	12.003	11.965	11.975	11.958	11.957	11.958
R2O—Al2O3	−2.379	−2.526	−2.482	−2.484	−2.449	−2.507	−2.486	−2.529	−2.529	−2.504
R′O	5.042	5.061	5.049	5.038	5.019	5.031	5.036	5.048	5.043	5.033
Thickness	3.999	4.433	4.017	4.131	4.050	3.900	3.906	3.979	3.972	4.132
(mm)
L*	95.13	95.17	95.14	95.18	95.17	95.16	95.3	95.27	95.2	95.11
a*	−2.51	−2.5	−2.51	−2.49	−2.46	−2.49	−2.44	−2.49	−2.46	−2.5
b*	16.02	15.9	15.93	15.76	15.57	15.79	15.18	15.49	15.49	15.87
Density	2.438									2.438
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25Z
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	305	306	307	308	309	310	311	312	313	314
SiO2	58.199	58.058	58.609	58.469	58.775	58.630	58.676	59.307	58.477	58.759
Al2O3	16.223	16.266	16.263	16.460	16.189	16.387	16.250	16.526	16.342	16.414
B2O3	5.981	5.921	5.875	5.985	5.920	5.870	5.954	5.580	5.840	5.601
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	12.137	12.097	11.826	11.595	11.599	11.584	11.725	11.691	11.860	11.821
Na2O	6.086	6.085	6.114	6.176	6.115	6.149	6.084	6.079	6.163	6.141
K2O	0.189	0.187	0.194	0.189	0.195	0.194	0.194	0.186	0.198	0.193
MgO	0.014	0.011	0.013	0.014	0.014	0.014	0.016	0.014	0.016	0.014
CaO	0.009	0.009	0.005	0.010	0.009	0.009	0.010	0.009	0.013	0.013
ZnO	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Fe2O3	0.002	0.001	0.003	0.003	0.002	0.003	0.003	0.003	0.003	0.004
TiO2	0.952	0.955	0.987	0.982	0.971	0.982	0.973	0.493	0.977	0.977
CeO2	0.200	0.400	0.103	0.106	0.199	0.161	0.103	0.102	0.100	0.054
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.152	1.355	1.090	1.088	1.170	1.143	1.076	0.595	1.077	1.031
R2O	18.412	18.369	18.134	17.960	17.908	17.927	18.003	17.956	18.221	18.155
Li2O + Na2O	18.223	18.182	17.940	17.771	17.714	17.733	17.809	17.770	18.022	17.962
R2O—Al2O3	2.190	2.104	1.871	1.500	1.719	1.540	1.753	1.429	1.879	1.742
R′O	0.023	0.020	0.017	0.025	0.024	0.024	0.026	0.024	0.029	0.027
Thickness	1.307		1.336	1.318	1.307	1.336	1.342		1.322	1.343
(mm)
L*	95.05		96.71	96.69	96.05	96.61	96.59		96.74	96.66
a*	−0.8		−0.26	−0.28	−0.73	−0.44	−0.33		−0.28	−0.14
b*	8.89		1.46	1.5	5.28	2.41	1.41		1.51	1.16
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25AA
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	315	316	317	318	319	320	321	322	323	324
SiO2	58.511	58.511	58.538	58.515	58.649	58.452	58.373	58.402	58.367	57.989
Al2O3	16.356	16.330	16.277	16.326	16.377	16.319	16.322	16.363	16.369	16.383
B2O3	5.827	5.914	6.003	5.950	5.818	5.878	5.951	5.933	5.998	6.042
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	11.808	11.823	11.749	11.818	11.767	11.840	11.791	11.210	10.681	10.423
Na2O	6.093	6.113	6.125	6.137	6.125	6.101	6.142	5.696	5.193	4.738
K2O	0.192	0.192	0.194	0.193	0.193	0.192	0.196	0.193	0.195	0.195
MgO	0.013	0.016	0.014	0.016	0.014	0.016	0.019	0.021	0.031	0.035
CaO	0.011	0.011	0.011	0.011	0.011	0.011	0.013	0.978	1.963	2.970
ZnO	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.016	0.016	0.032
SnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.003	0.003	0.001
Fe2O3	0.002	0.004	0.004	0.004	0.004	0.003	0.003	0.003	0.003	0.003
TiO2	0.976	0.977	0.973	0.972	0.981	0.978	0.978	0.973	0.974	0.975
CeO2	0.199	0.099	0.100	0.050	0.049	0.200	0.201	0.198	0.201	0.201
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.176	1.076	1.073	1.022	1.030	1.177	1.179	1.171	1.174	1.176
R2O	18.093	18.128	18.068	18.147	18.085	18.133	18.129	17.099	16.069	15.356
Li2O + Na2O	17.901	17.936	17.874	17.954	17.892	17.941	17.933	16.906	15.874	15.161
R2O—Al2O3	1.738	1.799	1.791	1.820	1.708	1.814	1.807	0.736	−0.300	−1.027
R′O	0.024	0.027	0.026	0.027	0.026	0.027	0.032	1.015	2.009	3.037
Thickness	1.347	1.272	1.336	1.274				0.712	0.722	0.692
(mm)
L*	95.59	96.76	96.77	96.5				96.48	96.57	96.59
a*	−0.76	−0.27	−0.29	−0.59				−0.37	−0.32	−0.28
b*	7.04	1.42	1.52	3.58				2.57	1.68	1.54
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25AB
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	325	326	327	328	329	330	331	332	333	334
SiO2	57.677	59.209	59.955	58.314	60.377	59.543	60.528	60.314	61.472	60.280
Al2O3	16.598	16.296	16.473	16.409	15.513	15.983	15.053	15.076	14.543	15.163
B2O3	6.075	6.018	6.029	5.942	5.928	5.900	5.913	6.022	5.921	5.811
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.908	10.380	9.937	9.702	8.653	8.692	10.037	10.078	9.924	9.955
Na2O	4.237	4.716	4.177	4.237	1.410	1.522	1.842	1.855	1.831	1.865
K2O	0.195	0.197	0.193	0.197	0.195	0.194	0.196	0.196	0.193	0.197
MgO	0.045	0.029	0.031	0.044	2.883	5.050	2.025	2.023	1.916	2.022
CaO	4.039	1.960	1.985	3.959	3.826	1.878	2.095	2.114	1.992	2.131
ZnO	0.016	0.016	0.024	0.000	0.000	0.000	1.065	1.073	1.005	1.102
SnO2	0.002	0.002	0.003	0.000	0.000	0.000	0.002	0.002	0.005	0.003
Fe2O3	0.004	0.003	0.003	0.003	0.003	0.003	0.003	0.004	0.004	0.002
TiO2	0.987	0.969	0.978	0.976	0.993	1.015	1.015	1.015	0.986	1.024
CeO2	0.203	0.199	0.199	0.202	0.209	0.213	0.216	0.218	0.201	0.424
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.191	1.168	1.177	1.178	1.202	1.228	1.230	1.233	1.187	1.448
R2O	14.339	15.292	14.307	14.137	10.258	10.407	12.075	12.130	11.948	12.017
Li2O + Na2O	14.145	15.096	14.114	13.940	10.063	10.213	11.879	11.933	11.756	11.820
R2O—Al2O3	−2.259	−1.003	−2.166	−2.272	−5.255	−5.576	−2.979	−2.946	−2.594	−3.146
R′O	4.100	2.004	2.039	4.003	6.709	6.928	5.185	5.210	4.913	5.255
Thickness	0.675	0.627	1.378	0.675	1.322	1.332	1.349	1.333	1.343	1.349
(mm)
L*	96.59	96.63	96.68	96.59	96.62	96.64	96.6	96.61	96.68	96.25
a*	−0.25	−0.23	−0.35	−0.25	−0.33	−0.32	−0.38	−0.38	−0.28	−0.83
b*	1.34	1.29	1.79	1.34	1.63	1.56	1.95	2	1.45	4.74
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25AC
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	335	336	337	338	339	340	341	342	343	344
SiO2	61.125	60.995	60.539	60.743	59.214	59.453	61.006	61.358	60.911	60.803
Al2O3	14.651	14.714	15.081	14.925	15.593	15.651	14.781	15.141	14.731	14.640
B2O3	5.896	5.860	5.892	5.885	6.096	6.051	5.953	5.253	5.980	5.979
P2O5	0.000	0.050	0.000	0.000	0.000	0.000	0.000	0.005	0.000	0.050
Li2O	10.003	9.977	9.977	9.982	10.145	9.941	9.813	9.591	9.903	9.987
Na2O	1.833	1.840	1.866	1.859	1.807	1.835	1.760	1.798	1.811	1.741
K2O	0.193	0.190	0.192	0.195	0.176	0.179	0.175	0.184	0.186	0.171
MgO	1.938	1.959	2.011	1.495	2.228	2.243	2.090	2.014	2.007	2.048
CaO	2.029	2.049	2.110	2.094	2.289	2.258	2.136	2.121	2.088	2.133
ZnO	1.017	1.034	1.068	1.591	1.189	1.113	1.072	1.067	1.055	1.133
SnO2	0.104	0.101	0.002	0.003	0.000	0.000	0.001	0.001	0.102	0.101
Fe2O3	0.004	0.004	0.004	0.003	0.004	0.004	0.004	0.002	0.003	0.003
TiO2	0.994	1.002	1.016	1.007	1.034	1.041	0.995	1.031	1.005	0.993
CeO2	0.206	0.208	0.214	0.208	0.219	0.218	0.209	0.427	0.210	0.212
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.201	1.210	1.230	1.215	1.253	1.259	1.203	1.458	1.214	1.204
R2O	12.028	12.007	12.035	12.036	12.128	11.954	11.748	11.573	11.900	11.899
Li2O + Na2O	11.835	11.817	11.843	11.841	11.952	11.775	11.572	11.389	11.713	11.728
R2O—Al2O3	−2.623	−2.707	−3.046	−2.889	−3.466	−3.698	−3.034	−3.568	−2.831	−2.741
R′O	4.984	5.042	5.190	5.180	5.705	5.615	5.298	5.202	5.150	5.314
Thickness	1.339	1.371	1.381	1.369	1.354	1.375	1.414	1.411	1.401	1.404
(mm)
L*	96.63	96.59	96.64	96.57	96.56	96.59	96.57	96.26	96.6	96.63
a*	−0.27	−0.31	−0.29	−0.41	−0.42	−0.41	−0.32	−0.87	−0.32	−0.31
b*	1.67	1.88	1.56	2.15	2.15	2.11	2.01	4.96	1.91	1.83
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25AD
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	345	346	347	348	349	350	351	352	353	354
SiO2	59.468	60.460	64.701	64.666	64.271	64.556	64.764	64.074	63.986	63.749
Al2O3	15.686	15.286	12.988	12.996	12.892	13.024	12.961	12.946	12.937	12.770
B2O3	6.026	5.992	5.829	5.809	5.719	5.828	5.744	5.642	5.779	5.715
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.952	9.668	11.984	12.021	11.714	12.066	10.021	9.964	9.946	9.646
Na2O	1.796	1.815	2.807	2.803	2.732	2.821	1.837	1.822	1.821	1.783
K2O	0.178	0.185	0.195	0.196	0.186	0.198	0.196	0.198	0.197	0.188
MgO	2.212	1.561	0.009	0.009	0.008	0.009	0.034	0.030	0.033	0.030
CaO	2.233	2.157	0.009	0.012	0.010	0.010	2.935	2.978	2.964	2.915
ZnO	1.152	1.616	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SnO2	0.001	0.000	0.050	0.052	0.044	0.051	0.047	0.049	0.048	0.040
Fe2O3	0.004	0.003	0.002	0.002	0.002	0.002	0.003	0.003	0.003	0.003
TiO2	1.041	1.030	0.980	0.984	0.972	0.981	0.982	0.983	0.976	0.966
CeO2	0.223	0.219	0.201	0.205	0.200	0.207	0.200	0.203	0.206	0.195
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.264	1.249	1.181	1.188	1.172	1.187	1.182	1.185	1.182	1.161
R2O	11.926	11.669	14.985	15.020	14.632	15.085	12.053	11.984	11.964	11.617
Li2O + Na2O	11.748	11.484	14.791	14.824	14.446	14.887	11.857	11.786	11.767	11.429
R2O—Al2O3	−3.760	−3.617	1.997	2.024	1.740	2.061	−0.908	−0.962	−0.974	−1.153
R′O	5.597	5.333	0.018	0.022	0.018	0.019	2.969	3.008	2.997	2.945
Thickness	1.315	1.332	1.263	1.324	1.272	1.261	1.263	1.304	1.321	1.327
(mm)
L*	96.66	96.61	96.73	96.77	96.79	96.8	96.77	96.77	96.77	96.78
a*	−0.27	−0.41	−0.34	−0.36	−0.34	−0.33	−0.26	−0.28	−0.28	−0.23
b*	1.44	2.11	1.83	1.89	1.81	1.75	1.43	1.51	1.56	1.4
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25AE
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	355	356	357	358	359	360	361	362	363	364
SiO2	63.775	62.413	58.673	57.445	59.730	58.759	60.601	61.581	62.137	61.463
Al2O3	12.781	14.797	17.014	16.961	16.736	16.344	14.931	14.390	14.227	14.564
B2O3	5.553	5.933	5.551	6.208	5.451	6.259	5.818	5.932	5.692	5.707
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.666	8.872	8.827	9.475	8.846	9.693	10.043	9.657	9.644	9.999
Na2O	1.784	1.356	1.414	1.390	1.407	1.399	1.862	1.852	1.855	1.837
K2O	0.189	0.003	0.190	0.186	0.193	0.190	0.195	0.195	0.197	0.186
MgO	0.030	2.804	2.224	2.225	2.132	2.070	1.986	1.871	1.894	2.013
CaO	2.932	1.938	4.900	4.803	4.724	4.534	2.068	1.982	1.964	1.994
ZnO	0.000	0.984	0.000	0.000	0.000	0.000	1.044	1.001	0.996	1.022
SnO2	0.040	0.005	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Fe2O3	0.003	0.002	0.005	0.004	0.004	0.004	0.002	0.001	0.002	0.003
TiO2	0.964	0.587	1.079	1.066	0.543	0.518	1.015	0.980	0.983	0.999
CeO2	0.198	0.303	0.116	0.228	0.225	0.222	0.425	0.552	0.402	0.203
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.162	0.890	1.195	1.294	0.768	0.740	1.441	1.531	1.384	1.202
R2O	11.639	10.231	10.431	11.051	10.447	11.282	12.100	11.704	11.696	12.023
Li2O + Na2O	11.450	10.228	10.241	10.865	10.253	11.092	11.905	11.509	11.499	11.837
R2O—Al2O3	−1.142	−4.566	−6.583	−5.910	−6.289	−5.062	−2.831	−2.686	−2.530	−2.541
R′O	2.961	5.726	7.124	7.028	6.856	6.604	5.099	4.853	4.854	5.029
Thickness	1.28	1.299					1.362		1.335	1.322
(mm)
L*	96.79	96.55					96.22		96.11	96.44
a*	−0.21	−0.31					−0.87		−0.91	−0.38
b*	1.32	1.69					5.01		5.37	2.02
Density										2.426
(g/cm3)
Liquidus										1140
Temp.
(° C.)

TABLE 25AF
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	365	366	367	368	369	370	371	372	373	374
SiO2	60.804	60.576	60.231	61.469	62.340	61.703	60.724	61.098	62.294	61.677
Al2O3	14.714	14.504	14.428	14.810	14.326	14.629	14.698	14.431	14.644	14.862
B2O3	5.689	5.677	5.662	5.655	5.495	5.395	5.497	5.644	5.810	5.787
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	10.162	10.324	10.089	10.236	10.071	9.945	9.983	10.156	10.125	10.095
Na2O	1.841	1.828	1.807	1.873	1.841	1.839	1.829	1.816	1.867	1.902
K2O	0.187	0.179	0.182	0.191	0.183	0.189	0.189	0.186	0.191	0.191
MgO	2.067	2.025	2.019	2.052	1.960	2.001	2.049	1.991	2.043	2.114
CaO	2.041	2.000	1.995	2.039	1.961	2.024	2.036	1.972	2.007	2.088
ZnO	1.057	1.074	1.083	1.040	1.018	1.043	1.053	1.005	0.994	1.047
SnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Fe2O3	0.002	0.002	0.002	0.002	0.001	0.002	0.002	0.002	0.004	0.003
TiO2	1.011	0.991	0.988	0.206	0.394	0.806	1.514	1.490	0.008	0.008
CeO2	0.416	0.811	1.505	0.417	0.400	0.413	0.416	0.204	0.002	0.210
ZrO2
La2O3
SO3					0.002					0.005
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.427	1.802	2.493	0.623	0.794	1.219	1.930	1.694	0.010	0.218
R2O	12.190	12.332	12.078	12.299	12.096	11.973	12.001	12.158	12.184	12.189
Li2O + Na2O	12.002	12.152	11.895	12.108	11.912	11.783	11.811	11.972	11.993	11.998
R2O—Al2O3	−2.524	−2.172	−2.350	2.510	−2.230	−2.656	2.697	−2.273	−2.460	−2.673
R′O	5.165	5.099	5.098	5.131	4.939	5.069	5.138	4.968	5.045	5.248
Thickness	1.317	1.3	1.302	1.317	1.306	1.297	1.294	1.306	1.303	1.305
(mm)
L*	96.16	95.24	78.05	96.40	96.39	96.26	91.74	96.35	96.69	96.61
a*	−0.76	−1.27	1.20	−0.28	−0.34	−0.59	−1.67	−0.67	0.00	−0.11
b*	4.40	9.54	50.71	1.90	2.25	3.50	24.78	3.67	0.20	0.78
Density	2.442	2.46	2.497	2.432	2.437	2.435	2.447	2.434
(g/cm3)
Liquidus	1155	1165	1160	1155	1160	1150	1165	1155
Temp.
(° C.)

TABLE 25AG
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	375	376	377	378	379	380	381	382	383	384
SiO2	61.698	61.353	61.076	61.998	61.764	61.536	61.663	61.249	60.429	61.303
Al2O3	14.856	14.696	14.518	14.656	14.822	14.693	14.631	14.539	14.544	14.612
B2O3	5.763	5.805	5.715	5.892	5.795	5.770	5.640	5.794	5.777	5.777
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.914	10.046	9.942	10.168	9.987	9.985	9.823	9.855	9.910	9.933
Na2O	1.896	1.870	1.850	1.874	1.884	1.923	1.896	1.867	1.868	1.888
K2O	0.193	0.187	0.185	0.187	0.193	0.195	0.194	0.187	0.191	0.189
MgO	2.093	2.078	2.037	2.032	2.085	2.073	2.067	2.058	2.064	2.030
CaO	2.083	2.058	2.036	1.999	2.051	2.018	2.039	2.013	2.029	2.006
ZnO	1.060	1.063	1.094	0.978	0.999	0.998	1.021	1.012	1.021	1.006
SnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Fe2O3	0.002	0.001	0.001	0.004	0.004	0.004	0.003	0.001	0.001	0.001
TiO2	0.007	0.008	0.007	0.199	0.405	0.593	0.593	0.583	0.588	0.198
CeO2	0.417	0.823	1.527	0.003	0.001	0.198	0.415	0.827	1.565	1.041
ZrO2
La2O3
SO3	0.002						0.001			0.001
WO3
Nb2O5						0.004	0.003
Bi2O3
MoO3
CeO2 + TiO2	0.424	0.831	1.534	0.202	0.406	0.791	1.008	1.411	2.153	1.238
R2O	12.004	12.103	11.977	12.229	12.063	12.103	11.913	11.910	11.968	12.011
Li2O + Na2O	11.811	11.916	11.792	12.042	11.870	11.908	11.719	11.722	11.778	11.821
R2O—Al2O3	−2.852	−2.593	−2.540	−2.428	−2.759	−2.590	−2.718	−2.629	−2.576	−2.601
R′O	5.237	5.199	5.167	5.010	5.135	5.089	5.126	5.083	5.113	5.042
Thickness	1.3	1.304	1.286	1.309	1.305	1.319	1.328	1.326	1.321	1.314
(mm)
L*	96.45	95.83	94.16	96.67	96.73	96.53	96.30	95.50	88.89	95.31
a*	−0.22	−0.34	−0.22	−0.01	0.00	−0.20	−0.45	−0.82	−0.98	−0.49
b*	1.63	4.04	8.95	0.21	0.21	1.27	2.86	6.82	21.58	6.20
Density						2.423	2.432	2.457	2.489	2.462
(g/cm3)
Liquidus						1190	1170	1140	1155	1150
Temp.
(° C.)

TABLE 25AH
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	385	386	387	388	389	390	391	392	393	394
SiO2	61.406	60.866	60.079	61.338	62.505	62.054	60.320	62.899	62.147	59.768
Al2O3	14.507	14.529	14.559	14.593	14.503	14.478	14.321	14.494	14.610	14.583
B2O3	5.685	5.727	5.761	5.850	5.737	5.791	5.779	5.725	5.652	5.703
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.875	9.927	9.953	9.969	8.673	9.182	11.182	9.853	9.914	9.943
Na2O	1.878	1.870	1.869	1.877	1.855	1.849	1.829	0.390	0.975	3.299
K2O	0.186	0.186	0.184	0.188	0.191	0.191	0.190	0.190	0.193	0.192
MgO	2.025	2.035	2.043	2.050	2.049	2.031	2.001	2.027	2.042	2.040
CaO	1.999	2.006	2.002	1.994	2.020	1.985	1.964	1.987	2.004	2.018
ZnO	0.993	1.009	1.004	1.002	1.048	1.029	1.011	1.019	1.037	1.029
SnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Fe2O3	0.001	0.001	0.001	0.001	0.003	0.003	0.003	0.003	0.003	0.003
TiO2	0.387	0.781	1.468	0.294	0.999	0.993	0.991	0.996	1.000	0.999
CeO2	1.039	1.040	1.043	0.834	0.407	0.406	0.400	0.408	0.414	0.408
ZrO2
La2O3
SO3	0.004	0.010	0.020
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.426	1.821	2.511	1.128	1.406	1.398	1.391	1.404	1.414	1.407
R2O	11.939	11.982	12.006	12.034	10.719	11.221	13.200	10.433	11.082	13.434
Li2O + Na2O	11.754	11.796	11.822	11.846	10.528	11.031	13.011	10.243	10.889	13.243
R2O—Al2O3	−2.567	−2.547	−2.553	−2.559	−3.784	−3.257	−1.121	−4.061	−3.528	−1.148
R′O	5.017	5.050	5.050	5.045	5.118	5.044	4.976	5.033	5.083	5.088
Thickness	1.316	1.299	1.317	1.328	1.318	1.321	1.358	1.31	1.309	1.314
(mm)
L*	94.98	93.05	78.73	95.79	96.36	96.27	96.05	96.35	96.26	95.50
a*	−0.71	−1.51	3.11	−0.50	−0.53	−0.61	−0.87	−0.53	−0.61	−1.11
b*	8.07	15.87	66.05	4.71	2.96	3.51	5.36	2.86	3.37	7.62
Density	2.465	2.463	2.477	2.454	2.434	2.438	2.451	2.43	2.435	2.452
(g/cm3)
Liquidus	1185	1145	1150	1150
Temp.
(° C.)

TABLE 25AI
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	395	396	397	398	399	400	401	402	403	404
SiO2	62.861	63.118	63.125	61.304	61.305	61.386	60.739	60.354	60.167	60.820
Al2O3	14.549	14.510	14.461	14.333	14.155	14.179	14.661	14.740	14.708	14.725
B2O3	5.958	5.797	5.918	5.931	5.988	5.932	5.856	6.086	6.048	5.857
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	10.097	10.044	10.014	9.879	10.270	10.157	10.088	10.193	10.326	10.041
Na2O	1.857	1.858	1.850	1.880	1.890	1.868	1.857	1.901	1.944	1.911
K2O	0.193	0.192	0.190	0.193	0.192	0.194	0.375	0.191	0.197	0.192
MgO	0.030	2.051	1.523	1.999	1.869	1.938	1.988	2.034	2.067	1.972
CaO	2.014	0.023	1.501	2.066	1.968	1.970	2.009	2.066	2.087	2.042
ZnO	1.032	1.011	0.016	1.011	0.977	0.990	1.002	1.007	1.019	0.998
SnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Fe2O3	0.003	0.002	0.003	0.003	0.003	0.003	0.003	0.003	0.003	0.003
TiO2	0.989	0.983	0.988	0.978	0.970	0.968	0.994	1.000	1.002	1.002
CeO2	0.406	0.404	0.401	0.406	0.397	0.398	0.410	0.410	0.417	0.411
ZrO2
La2O3
SO3										0.007
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.396	1.388	1.389	1.384	1.367	1.366	1.404	1.410	1.418	1.414
R2O	12.147	12.094	12.055	11.953	12.352	12.218	12.319	12.285	12.467	12.144
Li2O + Na2O	11.954	11.902	11.864	11.759	12.160	12.024	11.945	12.094	12.269	11.952
R2O—Al2O3	−2.401	−2.416	−2.406	−2.380	−1.802	−1.961	−2.342	−2.455	−2.241	−2.582
R′O	3.076	3.084	3.040	5.076	4.814	4.898	4.999	5.107	5.173	5.013
Thickness	1.307	1.318	1.321	1.288	1.298	1.292	1.305	1.299	1.294	1.299
(mm)
L*	96.47	96.44	96.39	96.21	96.09	96.06	96.06	96.04	96.11	96.12
a*	−0.64	−0.51	−0.56	−0.76	−0.85	−0.87	−0.83	−0.86	−0.79	−0.75
b*	3.59	2.75	3.15	4.47	5.11	5.18	4.90	5.09	4.70	4.50
Density	2.419	2.408	2.402
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25AJ
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	405	406	407	408	409	410	411	412	413	414
SiO2	60.732	60.871	62.547	61.554	63.613	61.314	61.240	61.373	62.031	60.955
Al2O3	14.501	14.581	13.795	14.167	14.152	14.505	14.493	14.270	13.888	14.442
B2O3	6.170	5.856	5.721	6.035	5.296	5.761	5.742	5.772	5.861	5.942
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	10.077	10.205	10.024	10.419	9.319	9.960	10.022	10.060	10.080	10.205
Na2O	1.923	1.890	1.723	1.610	1.395	1.888	1.900	2.033	1.887	1.898
K2O	0.198	0.192	0.191	0.190	0.187	0.190	0.188	0.188	0.196	0.196
MgO	1.964	1.964	1.815	1.861	1.841	1.974	2.007	1.964	1.852	1.975
CaO	2.030	2.016	1.899	1.911	1.928	1.983	1.996	1.964	1.904	1.988
ZnO	0.977	1.008	0.944	0.865	0.905	0.986	0.980	0.976	0.937	0.983
SnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Fe2O3	0.003	0.003	0.003	0.003	0.003	0.003	0.003	0.003	0.003	0.003
TiO2	0.993	0.986	0.936	0.955	0.949	0.986	0.985	0.966	0.951	0.986
CeO2	0.413	0.408	0.374	0.381	0.375	0.409	0.410	0.398	0.392	0.411
ZrO2
La2O3
SO3			0.011	0.029	0.023	0.025	0.017	0.016
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.406	1.394	1.310	1.336	1.323	1.394	1.395	1.364	1.343	1.396
R2O	12.198	12.288	11.938	12.218	10.901	12.037	12.110	12.281	12.163	12.299
Li2O + Na2O	12.000	12.096	11.748	12.028	10.714	11.847	11.922	12.093	11.967	12.103
R2O—Al2O3	−2.303	−2.293	−1.857	−1.949	−3.251	−2.468	−2.383	−1.989	−1.725	−2.144
R′O	4.971	4.988	4.659	4.637	4.674	4.944	4.984	4.904	4.693	4.946
Thickness	1.295	1.258	1.266	1.241	1.263	1.275	1.268	1.265	1.275	1.287
(mm)
L*	96.02	96.13	95.00	94.27	94.24	96.26	96.25	96.25	96.12	96.10
a*	−0.76	−0.79	−0.34	−0.15	−0.14	−0.67	−0.69	−0.69	−0.81	−0.80
b*	4.55	4.71	3.46	3.17	3.16	3.89	4.07	4.09	4.88	4.87
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25AK
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	415	416	417	418	419	420	421	422	423	424
SiO2	61.158	61.060	60.634	61.106	61.744	61.589	61.061	61.621	61.673	61.634
Al2O3	14.319	14.694	14.390	14.826	14.594	14.535	14.435	14.574	14.682	14.321
B2O3	6.075	5.747	5.425	5.681	5.710	5.565	5.561	5.555	5.156	5.664
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	10.166	9.815	9.929	10.187	10.079	10.078	9.998	9.954	9.968	10.075
Na2O	1.885	1.899	1.835	1.894	1.855	1.841	1.842	1.867	1.813	1.880
K2O	0.193	0.196	0.183	0.191	0.190	0.183	0.186	0.188	0.180	0.187
MgO	1.887	2.059	2.030	2.102	2.034	2.030	2.038	2.016	2.057	2.000
CaO	1.950	2.052	2.037	2.083	2.009	2.004	2.027	2.006	2.031	2.001
ZnO	0.962	1.028	1.059	1.080	0.972	0.966	1.046	1.002	1.004	1.035
SnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Fe2O3	0.003	0.003	0.001	0.001	0.004	0.003	0.002	0.002	0.002	0.002
TiO2	0.976	1.009	1.466	0.006	0.797	0.992	0.985	0.797	0.603	0.197
CeO2	0.410	0.422	1.004	0.833	0.001	0.207	0.806	0.409	0.826	1.001
ZrO2
La2O3
SO3				0.002			0.009
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.386	1.431	2.470	0.840	0.798	1.199	1.790	1.206	1.429	1.197
R2O	12.244	11.910	11.947	12.271	12.124	12.101	12.025	12.009	11.961	12.141
Li2O + Na2O	12.051	11.714	11.764	12.080	11.934	11.919	11.839	11.821	11.781	11.954
R2O—Al2O3	−2.075	−2.785	−2.443	−2.554	−2.470	−2.433	−2.410	−2.565	−2.721	−2.180
R′O	4.799	5.139	5.125	5.265	5.016	5.001	5.112	5.025	5.092	5.036
Thickness	1.307	1.31	1.361	1.287	1.344	1.337	1.343	1.327	1.348	1.335
(mm)
L*	96.08	96.06	76.71	96.21	96.60	96.56	91.80	96.44	96.06	95.80
a*	−0.86	−0.86	8.60	−0.17	−0.03	−0.27	−1.71	−0.47	−0.68	−0.36
b*	5.17	5.19	86.33	2.30	0.48	1.43	23.03	2.69	4.71	4.28
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25AL
Example	TM-425	TM-426	TM-427	TM-428	TM-429	TM-430	TM-431	TM-432	TM-433	TM-434
SiO2	61.677	60.200	60.730	60.788	60.355	62.197	60.801	61.427	61.484	60.057
Al2O3	14.558	14.755	14.881	15.062	15.208	14.409	15.150	14.397	14.684	15.049
B2O3	5.047	6.116	6.167	6.152	5.901	5.743	6.238	6.058	6.037	6.175
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.853	10.333	10.417	10.130	10.624	9.987	10.105	10.383	10.303	10.407
Na2O	1.799	1.918	1.973	1.951	1.981	1.899	1.989	1.886	1.928	1.945
K2O	0.182	0.196	0.195	0.196	0.196	0.197	0.198	0.191	0.197	0.197
MgO	2.023	2.024	2.078	2.082	2.131	1.971	2.133	1.901	2.024	2.100
CaO	2.012	2.029	2.081	2.084	2.094	2.045	2.118	1.948	2.045	2.099
ZnO	1.026	0.994	1.022	1.034	1.029	1.022	1.013	0.958	0.997	1.028
SnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Fe2O3	0.002	0.003	0.014	0.065	0.024	0.091	0.016	0.012	0.064	0.063
TiO2	0.796	0.998	0.008	0.007	0.007	0.008	0.007	0.007	0.007	0.007
CeO2	1.019	0.419	0.419	0.432	0.433	0.416	0.217	0.818	0.207	0.856
ZrO2
La2O3
SO3									0.008
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.816	1.416	0.427	0.439	0.440	0.423	0.225	0.825	0.214	0.863
R2O	11.834	12.447	12.584	12.277	12.801	12.082	12.292	12.460	12.428	12.549
Li2O + Na2O	11.652	12.251	12.389	12.081	12.605	11.885	12.094	12.269	12.231	12.352
R2O − Al2O3	−2.725	−2.309	−2.297	−2.785	−2.407	−2.326	−2.858	−1.936	−2.256	−2.499
R′O	5.061	5.047	5.181	5.201	5.255	5.038	5.264	4.806	5.065	5.227
Thickness	1.334	1.409	1.403	1.389	1.389	1.396	1.38	1.4	1.385	1.397
(mm)
L*	95.32	96.15	96.35	96.36	96.17	95.77	96.55	95.64	96.15	95.61
a*	−1.27	−0.79	−0.20	−0.18	−0.14	−0.22	−0.06	−0.39	−0.15	−0.32
b*	9.58	4.64	1.71	1.67	1.91	2.31	0.61	4.71	1.14	4.83
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25AM
Example	TM-435	TM-436	TM-437	TM-438	TM-439	TM-440	TM-441	TM-442	TM-443	TM-444
SiO2	59.613	60.633	61.035	60.100	60.869	60.983	60.730	60.650	62.003	63.308
Al2O3	14.360	14.719	14.773	14.452	14.701	14.630	14.721	14.573	13.538	12.544
B2O3	5.628	5.754	5.457	5.752	5.759	5.730	5.869	5.768	5.719	5.557
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.937	9.964	10.013	10.067	9.839	9.975	10.077	9.971	10.095	10.014
Na2O	1.876	1.913	1.925	1.887	1.921	1.867	1.889	1.842	1.902	1.914
K2O	0.188	0.189	0.194	0.187	0.192	0.193	0.193	0.189	0.192	0.192
MgO	2.027	2.092	2.081	2.033	2.071	2.065	2.100	2.057	2.053	2.021
CaO	2.003	2.069	2.053	2.012	2.043	2.042	2.073	2.032	2.055	2.026
ZnO	1.002	1.026	1.009	0.989	1.010	1.072	1.106	1.074	1.019	1.000
SnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Fe2O3	0.002	0.002	0.004	0.002	0.003	0.001	0.001	0.001	0.003	0.003
TiO2	1.447	0.006	0.990	0.971	0.790	0.606	0.202	0.799	0.989	0.991
CeO2	1.025	0.843	0.205	0.828	0.417	0.825	1.029	1.027	0.412	0.415
ZrO2
La2O3
SO3			0.010			0.002		0.007
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	2.471	0.849	1.195	1.798	1.207	1.430	1.231	1.826	1.401	1.407
R2O	12.001	12.066	12.131	12.141	11.952	12.035	12.159	12.003	12.190	12.120
Li2O + Na2O	11.813	11.877	11.938	11.954	11.760	11.842	11.966	11.814	11.998	11.927
R2O − Al2O3	−2.359	−2.653	−2.642	2.311	−2.749	−2.594	−2.562	−2.570	−1.349	−0.424
R′O	5.032	5.188	5.143	5.034	5.124	5.179	5.279	5.163	5.128	5.046
Thickness	1.208	1.187	1.205	1.217	1.221	1.301	1.308	1.294	1.33	1.305
(mm)
L*	75.42	95.92	96.39	90.40	96.13	95.26	95.24	93.27	95.86	94.41
a*	5.59	−0.29	−0.37	−1.24	−0.60	−0.86	−0.49	−1.13	−0.98	−1.42
b*	71.57	3.76	2.56	24.31	4.30	8.13	6.74	15.33	6.22	12.10
Density									2.439	2.431
(g/cm3)
Liquidus									1160	1170
Temp.
(° C.)

TABLE 25AN
Example	TM-445	TM-446	TM-447	TM-448	TM-449	TM-450	TM-451	TM-452	TM-453	TM-454
SiO2	63.846	61.725	61.403	61.676	62.297	62.861	64.138	60.358	61.846	59.290
Al2O3	11.995	13.120	12.434	11.536	14.470	14.471	14.495	14.603	13.810	15.265
B2O3	5.535	5.839	5.796	5.627	4.743	3.915	2.828	6.123	6.166	5.972
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	10.169	10.534	11.632	12.150	10.019	10.236	10.024	10.395	10.165	10.420
Na2O	1.960	2.056	2.169	2.375	1.894	1.891	1.886	1.896	1.876	1.990
K2O	0.190	0.193	0.189	0.188	0.192	0.192	0.193	0.194	0.192	0.196
MgO	1.956	2.054	2.002	2.020	1.992	2.015	2.016	2.014	1.808	2.186
CaO	1.975	2.045	1.985	2.013	1.996	2.009	2.014	2.019	1.876	2.130
ZnO	0.969	1.004	0.978	0.992	0.986	0.995	0.991	0.984	0.908	1.047
SnO2								0.000	0.000	0.000
Fe2O3	0.003	0.003	0.003	0.003	0.003	0.003	0.003	0.003	0.013	0.040
TiO2	0.978	0.998	0.980	0.988	0.982	0.983	0.984	0.985	0.936	1.016
CeO2	0.407	0.410	0.409	0.416	0.410	0.412	0.411	0.412	0.391	0.434
ZrO2
La2O3
SO3					0.002
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.385	1.408	1.389	1.404	1.392	1.395	1.395	1.398	1.327	1.450
R2O	12.320	12.783	13.991	14.713	12.104	12.320	12.103	12.486	12.233	12.606
Li2O + Na2O	12.130	12.590	13.802	14.525	11.912	12.128	11.910	12.292	12.042	12.410
R2O − Al2O3	0.325	−0.337	1.556	3.177	−2.366	−2.151	−2.391	−2.117	−1.577	−2.660
R′O	4.900	5.103	4.966	5.025	4.974	5.019	5.021	5.017	4.591	5.364
Thickness	1.334	1.325	1.336	1.329	1.343	1.336	1.334	1.287	1.282	1.293
(mm)
L*	94.98	95.45	95.91	96.06	95.96	95.97	95.97	96.09	96.11	95.96
a*	−1.33	−1.15	−1.00	−0.81	−0.87	−0.84	−0.91	−0.79	−0.74	−0.73
b*	10.46	8.02	6.34	4.98	5.43	5.27	5.73	4.71	4.51	4.83
Density	2.432	2.44	2.448	2.455	2.442	2.445	2.45
(g/cm3)
Liquidus	1135	1160	1165	1135	1195	1215	1245
Temp.
(° C.)

TABLE 25AO
Example	TM-455	TM-456	TM-457	TM-458	TM-459	TM-460	TM-461	TM-462	TM-463	TM-464
SiO2	59.744	59.186	60.509	60.421	60.579	60.333	61.608	63.053	61.230	61.869
Al2O3	15.020	15.187	14.713	14.848	14.672	15.126	14.624	13.534	14.809	14.514
B2O3	6.099	6.202	5.894	5.827	6.032	6.294	5.872	6.222	5.827	5.947
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	10.340	10.557	10.257	10.063	10.197	10.361	9.941	10.267	10.019	10.253
Na2O	1.911	1.926	1.879	1.919	1.842	1.858	1.868	1.772	1.863	1.825
K2O	0.194	0.194	0.191	0.192	0.193	0.192	0.196	0.196	0.198	0.191
MgO	2.099	2.166	2.033	2.090	2.000	2.176	2.046	1.735	2.036	1.937
CaO	2.060	2.086	2.043	2.081	2.018	2.085	1.995	1.816	2.051	1.965
ZnO	1.021	1.010	1.003	1.026	1.046	1.069	1.024	0.950	1.051	1.024
SnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Fe2O3	0.064	0.023	0.056	0.090	0.003	0.002	0.002	0.002	0.002	0.002
TiO2	1.009	1.012	0.991	1.000	1.006	0.012	0.011	0.011	0.011	0.011
CeO2	0.425	0.433	0.417	0.423	0.407	0.426	0.410	0.379	0.421	0.396
ZrO2
La2O3
SO3		0.004		0.006		0.009		0.007	0.049
WO3						0.052	0.396
Nb2O5								0.049	0.423
Bi2O3									0.001	0.059
MoO3
CeO2 + TiO2	1.434	1.446	1.408	1.423	1.413	0.438	0.421	0.390	0.433	0.407
R2O	12.445	12.677	12.327	12.174	12.232	12.410	12.006	12.235	12.081	12.268
Li2O + Na2O	12.252	12.483	12.136	11.982	12.039	12.219	11.810	12.039	11.883	12.078
R2O − Al2O3	−2.575	−2.510	−2.386	−2.674	−2.441	−2.716	−2.619	−1.299	−2.728	−2.246
R′O	5.180	5.263	5.079	5.196	5.064	5.330	5.064	4.501	5.138	4.925
Thickness	1.287	1.342	1.37	1.345	1.31	1.301	1.293	1.307	1.284	1.277
(mm)
L*	95.79	95.98	95.92	95.15	96.09	96.36	96.41	96.33	96.20	96.38
a*	−0.72	−0.81	−0.70	−0.79	−0.80	−0.23	−0.27	−0.25	−0.41	−0.22
b*	5.53	5.05	5.12	7.39	4.80	1.80	1.84	1.90	2.50	1.74
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25AP
Example	TM-465	TM-466	TM-467	TM-468	TM-469	TM-470	TM-471	TM-472	TM-473	TM-474
SiO2	59.713	61.525	61.538	58.525	60.939	60.714	60.727	61.761	61.367	60.720
Al2O3	15.337	14.475	14.604	16.084	14.420	14.467	15.292	14.234	14.109	14.621
B2O3	6.242	6.186	5.924	5.610	6.037	6.081	5.891	6.159	5.959	5.925
P2O5	0.000	0.000	0.000	0.002	0.026	0.050	0.027	0.049	0.002	0.002
Li2O	10.607	10.347	10.039	10.018	10.108	10.056	10.045	10.377	10.291	10.116
Na2O	1.892	1.864	1.877	2.003	1.879	1.898	1.965	1.900	1.877	1.915
K2O	0.179	0.195	0.192	0.199	0.192	0.193	0.194	0.190	0.191	0.195
MgO	2.128	1.943	2.024	2.554	1.958	1.997	2.152	1.909	1.876	1.994
CaO	1.961	1.975	1.978	2.298	1.999	2.037	2.141	1.940	1.931	2.048
ZnO	1.038	1.016	0.987	1.168	0.978	0.985	1.046	0.949	0.955	0.987
SnO2	0.000	0.000	0.000	0.002	0.048	0.097	0.051	0.097	0.053	0.053
Fe2O3	0.003	0.002	0.002	0.003	0.003	0.003	0.003	0.003	0.003	0.003
TiO2	0.010	0.011	0.012	1.060	0.983	0.988	0.007	0.006	0.968	0.993
CeO2	0.387	0.408	0.411	0.458	0.413	0.416	0.441	0.407	0.402	0.412
ZrO2
La2O3
SO3		0.002	0.017
WO3
Nb2O5
Bi2O3	0.500
MoO3		0.045	0.381
CeO2 + TiO2	0.397	0.420	0.423	1.518	1.396	1.403	0.448	0.413	1.370	1.405
R2O	12.678	12.405	12.108	12.219	12.178	12.147	12.205	12.468	12.359	12.226
Li2O + Na2O	12.499	12.211	11.916	12.020	11.987	11.954	12.011	12.278	12.168	12.031
R2O − Al2O3	−2.659	−2.070	−2.496	−3.865	−2.242	−2.320	−3.088	−1.766	−1.750	−2.395
R′O	5.126	4.934	4.989	6.020	4.935	5.019	5.339	4.799	4.763	5.029
Thickness	1.297	1.328	1.333	1.348	1.335	1.341	1.355	1.346	1.354	1.35
(mm)
L*	96.30	96.38	96.41	96.11	96.19	96.39	96.46	96.52	96.19	96.20
a*	−0.28	−0.23	−0.28	−0.80	−0.74	−0.57	−0.11	−0.06	−0.69	−0.72
b*	1.96	1.78	2.02	4.64	4.25	3.12	1.06	0.71	4.05	4.18
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25AQ
Example	TM-475	TM-476	TM-477	TM-478	TM-479	TM-480	TM-481	TM-482	TM-483	TM-484
SiO2	59.486	60.630	60.210	60.621	60.457	61.483	60.402	62.960	61.721	64.109
Al2O3	15.281	14.950	15.185	14.934	15.052	14.394	15.135	13.779	14.375	13.328
B2O3	6.085	5.820	5.908	5.873	5.911	5.920	5.788	5.728	5.972	5.796
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	9.288	9.005	9.134	9.094	9.147	9.097	9.535	9.781	9.879	10.038
Na2O	1.521	1.367	1.359	1.842	1.841	1.828	1.358	1.647	1.367	1.455
K2O	0.194	0.166	0.165	0.165	0.162	0.167	0.168	0.165	0.166	0.166
MgO	5.002	4.692	4.755	4.560	4.693	4.289	3.108	3.321	3.897	2.914
CaO	1.759	1.936	1.840	1.487	1.511	1.420	3.059	1.196	1.204	0.790
ZnO	0.000	0.008	0.008	0.008	0.008	0.000	0.016	0.016	0.008	0.008
SnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Fe2O3	0.001	0.002	0.002	0.002	0.002	0.002	0.002	0.002	0.002	0.002
TiO2	0.976	1.011	1.016	0.997	0.803	1.080	1.012	0.999	0.998	0.990
CeO2	0.398	0.413	0.419	0.418	0.413	0.320	0.418	0.408	0.411	0.405
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.374	1.424	1.434	1.414	1.216	1.400	1.429	1.406	1.408	1.395
R2O	11.004	10.538	10.658	11.102	11.150	11.091	11.061	11.593	11.413	11.659
Li2O + Na2O	10.809	10.372	10.494	10.937	10.988	10.925	10.893	11.428	11.246	11.493
R2O − Al2O3	−4.277	−4.411	−4.527	−3.832	−3.902	−3.303	−4.074	−2.186	−2.963	−1.669
R′O	6.761	6.636	6.602	6.054	6.212	5.709	6.182	4.532	5.109	3.712
Thickness	0.57	1.295	1.282	1.309	1.305	1.301	1.277	1.289	1.287	1.286
(mm)
L*	96.38	96.34	96.35	96.38	96.37	96.39	96.34	96.28	96.35	96.29
a*	−0.29	−0.57	−0.53	−0.52	−0.47	−0.52	−0.52	−0.65	−0.58	−0.68
b*	1.68	3.13	2.92	2.88	2.63	2.80	2.98	3.83	3.28	3.91
Density
(g/cm3)
Liquidus	1140
Temp.
(° C.)

TABLE 25AR
Example	TM-485	TM-486	TM-487	TM-488	TM-489	TM-490	TM-491	TM-492	TM-493	TM-494
SiO2	59.283	59.636	59.706	59.455	59.392	59.737	59.476	59.673	59.593	60.312
Al2O3	14.546	14.386	14.531	14.696	14.568	14.718	14.658	14.710	14.781	14.488
B2O3	4.841	4.902	4.734	4.835	4.826	4.789	4.812	4.734	4.864	5.668
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	13.885	13.143	11.778	12.419	8.785	10.985	13.119	11.672	12.316	9.953
Na2O	0.879	0.864	2.169	0.872	5.816	0.858	0.870	2.187	0.870	1.822
K2O	0.171	0.814	0.765	1.309	0.166	2.465	0.811	0.775	1.286	0.166
MgO	2.026	1.939	1.998	2.030	2.064	2.040	2.060	2.044	2.062	2.000
CaO	1.987	1.958	1.970	2.002	2.002	2.010	2.015	2.010	2.031	1.999
ZnO	0.972	0.951	0.940	0.958	0.975	0.971	0.965	0.973	0.972	1.083
SnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Fe2O3	0.002	0.002	0.002	0.002	0.002	0.002	0.003	0.003	0.003	0.002
TiO2	0.997	0.994	0.997	1.010	0.997	1.015	1.008	1.012	1.014	1.485
CeO2	0.411	0.410	0.410	0.412	0.407	0.410	0.205	0.206	0.206	1.014
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.408	1.404	1.407	1.422	1.404	1.425	1.213	1.218	1.221	2.499
R2O	14.935	14.821	14.712	14.600	14.767	14.308	14.799	14.634	14.472	11.940
Li2O + Na2O	14.764	14.007	13.947	13.291	14.601	11.843	13.989	13.859	13.186	11.775
R2O − Al2O3	0.388	0.435	0.181	−0.096	0.199	−0.411	0.142	−0.075	−0.310	−2.548
R′O	4.985	4.849	4.908	4.990	5.041	5.021	5.039	5.028	5.065	5.081
Thickness	1.221	1.223	1.217	1.17	1.227	1.237	1.281	1.253	1.24	1.352
(mm)
L*	96.03	96.00	95.41	95.90	94.89	92.22	96.32	96.29	96.34	70.36
a*	−0.78	−0.83	−1.06	−0.92	−1.28	−1.52	−0.47	−0.55	−0.46	8.58
b*	4.89	5.26	7.73	5.69	10.18	19.29	2.37	2.51	2.52	76.71
Density	2.447	2.448	2.453	2.447	2.46	2.447	2.436	2.444	2.437
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25AS
Example	TM-495	TM-496	TM-497	TM-498	TM-499	TM-500	TM-501	TM-502	TM-503	TM-504
SiO2	61.349	62.180	61.549	60.736	61.636	61.225	61.051	60.582	59.100	59.100
Al2O3	14.663	14.334	14.333	14.536	14.206	14.525	14.611	14.511	14.500	14.500
B2O3	5.943	5.761	5.893	5.760	5.984	5.717	5.837	5.949	5.000	5.000
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	10.028	10.030	10.084	10.028	10.114	10.038	10.118	10.011	13.800	12.396
Na2O	1.861	1.868	1.850	1.837	1.858	1.841	1.860	1.819	1.000	2.404
K2O	0.168	0.168	0.165	0.165	0.168	0.167	0.165	0.160	0.200	0.200
MgO	2.051	1.965	1.982	2.028	1.945	2.018	2.031	2.052	3.000	2.579
CaO	2.029	1.943	1.954	2.013	1.929	2.003	2.023	2.009	0.500	1.202
ZnO	1.061	0.948	0.994	1.071	0.973	1.046	1.072	1.095	1.500	1.219
SnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Fe2O3	0.002	0.002	0.002	0.002	0.002	0.002	0.002	0.002
TiO2	0.010	0.790	0.978	0.995	0.778	0.598	0.199	0.788	1.000	1.000
CeO2	0.826	0.001	0.206	0.815	0.395	0.813	1.024	1.013	0.400	0.400
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	0.837	0.791	1.184	1.810	1.173	1.412	1.223	1.801	1.400	1.400
R2O	12.057	12.066	12.099	12.030	12.140	12.046	12.143	11.990	15.000	15.000
Li2O + Na2O	11.889	11.898	11.934	11.865	11.972	11.879	11.978	11.830	14.800	14.800
R2O − Al2O3	−2.606	−2.268	−2.234	−2.506	−2.066	−2.479	−2.468	−2.520	0.500	0.500
R′O	5.142	4.856	4.930	5.113	4.848	5.067	5.125	5.157	5.000	5.000
Thickness	1.372	1.367	1.383	1.358	1.388	1.377	1.364	1.159
(mm)
L*	95.90	96.57	96.46	89.22	96.26	95.55	95.29	94.42
a*	−0.31	−0.01	−0.33	−1.81	−0.57	−0.83	−0.52	−1.22
b*	3.62	0.35	1.84	28.72	3.37	6.58	6.23	11.32
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25AT
Example	TM-505	TM-506	TM-507	TM-508	TM-509	TM-510	TM-511	TM-512	TM-513	TM-514
SiO2	59.100	59.100	59.100	59.100	59.100	59.100	59.100	59.100	59.100	59.100
Al2O3	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500
B2O3	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000
P2O5
Li2O	13.026	11.341	11.765	12.437	10.270	10.737	11.184	11.835	8.800	9.423
Na2O	1.000	3.459	2.314	1.000	4.530	3.338	2.328	1.000	6.000	4.585
K2O	0.974	0.200	0.921	1.563	0.200	0.926	1.488	2.165	0.200	0.993
MgO	2.309	2.262	1.962	1.783	1.941	1.651	1.452	1.246	1.500	1.217
CaO	0.777	1.730	1.414	0.987	2.265	1.928	1.624	1.202	3.000	2.575
ZnO	1.915	1.008	1.623	2.230	0.794	1.421	1.924	2.552	0.500	1.208
SnO2
Fe2O3
TiO2	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000
CeO2	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400
R2O	15.000	15.000	15.000	15.000	15.000	15.000	15.000	15.000	15.000	15.000
Li2O + Na2O	14.026	14.800	14.079	13.437	14.800	14.074	13.512	12.835	14.800	14.007
R2O − Al2O3	0.500	0.500	0.500	0.500	0.500	0.500	0.500	0.500	0.500	0.500
R′O	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000
Thickness
(mm)
L*
a*
b*
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25AU
Example	TM-515	TM-516	TM-517	TM-518	TM-519	TM-520	TM-521	TM-522	TM-523	TM-524
SiO2	59.100	59.100	59.100	61.100	61.100	61.100	61.100	61.100	61.100	61.100
Al2O3	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500
B2O3	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000
P2O5
Li2O	9.889	10.358	11.000	11.960	10.749	11.277	9.835	10.196	10.764	8.907
Na2O	3.526	2.458	1.000	0.870	2.081	0.870	2.995	1.997	0.870	3.923
K2O	1.585	2.184	3.000	0.170	0.170	0.853	0.170	0.807	1.366	0.170
MgO	1.005	0.792	0.500	2.000	2.000	2.000	2.000	2.000	2.000	2.000
CaO	2.258	1.937	1.500	2.000	2.000	2.000	2.000	2.000	2.000	2.000
ZnO	1.737	2.271	3.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000
SnO2
Fe2O3
TiO2	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000
CeO2	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400
R2O	15.000	15.000	15.000	13.000	13.000	13.000	13.000	13.000	13.000	13.000
Li2O + Na2O	13.415	12.816	12.000	12.830	12.830	12.147	12.830	12.193	11.634	12.830
R2O − Al2O3	0.500	0.500	0.500	−1.500	−1.500	−1.500	−1.500	−1.500	−1.500	−1.500
R′O	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000
Thickness
(mm)
L*
a*
b*
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25AV
Example	TM-525	TM-526	TM-527	TM-528	TM-529	TM-530	TM-531	TM-532	TM-533	TM-534
SiO2	61.100	61.100	61.100	61.100	61.100	61.100	61.100	61.100	63.100	63.100
Al2O3	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500
B2O3	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000
P2O5
Li2O	9.311	9.693	10.243	7.630	8.178	8.583	8.987	9.530	10.120	9.072
Na2O	2.878	2.004	0.870	5.200	3.950	3.028	2.108	0.870	0.730	1.778
K2O	0.812	1.303	1.887	0.170	0.871	1.389	1.905	2.600	0.150	0.150
MgO	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000
CaO	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000
ZnO	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000
SnO2
Fe2O3
TiO2	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000
CeO2	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400
R2O	13.000	13.000	13.000	13.000	13.000	13.000	13.000	13.000	11.000	11.000
Li2O + Na2O	12.188	11.697	11.113	12.830	12.129	11.611	11.095	10.400	10.850	10.850
R2O − Al2O3	−1.500	−1.500	−1.500	−1.500	−1.500	−1.500	−1.500	−1.500	−3.500	−3.500
R′O	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000
Thickness
(mm)
L*
a*
b*
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25AW
Example	TM-535	TM-536	TM-537	TM-538	TM-539	TM-540	TM-541	TM-542	TM-543	TM-544
SiO2	63.100	63.100	63.100	63.100	63.100	63.100	63.100	63.100	63.100	63.100
Al2O3	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500
B2O3	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000
P2O5
Li2O	9.537	8.293	8.609	9.102	7.511	7.859	8.189	8.665	6.450	6.914
Na2O	0.730	2.557	1.701	0.730	3.339	2.450	1.704	0.730	4.400	3.350
K2O	0.733	0.150	0.690	1.168	0.150	0.691	1.107	1.605	0.150	0.737
MgO	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000
CaO	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000
ZnO	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000
SnO2
Fe2O3
TiO2	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000
CeO2	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400
R2O	11.000	11.000	11.000	11.000	11.000	11.000	11.000	11.000	11.000	11.000
Li2O + Na2O	10.267	10.850	10.310	9.832	10.850	10.309	9.893	9.395	10.850	10.263
R2O − Al2O3	−3.500	−3.500	−3.500	−3.500	−3.500	−3.500	−3.500	−3.500	−3.500	−3.500
R′O	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000
Thickness
(mm)
L*
a*
b*
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25AX
Example	TM-545	TM-546	TM-547	TM-548	TM-549	TM-550	TM-551	TM-552	TM-553	TM-554
SiO2	63.100	63.100	63.100	61.100	61.100	61.100	61.100	61.100	61.100	61.100
Al2O3	14.500	14.500	14.500	12.500	12.500	12.500	12.500	12.500	12.500	12.500
B2O3	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000
P2O5
Li2O	7.258	7.603	8.070	13.800	12.383	13.009	11.324	11.749	12.417	10.256
Na2O	2.570	1.788	0.730	1.000	2.417	1.000	3.476	2.317	1.000	4.544
K2O	1.172	1.609	2.200	0.200	0.200	0.991	0.200	0.934	1.583	0.200
MgO	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000
CaO	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000
ZnO	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000
SnO2
Fe2O3
TiO2	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000
CeO2	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400
R2O	11.000	11.000	11.000	15.000	15.000	15.000	15.000	15.000	15.000	15.000
Li2O + Na2O	9.828	9.391	8.800	14.800	14.800	14.009	14.800	14.066	13.417	14.800
R2O − Al2O3	−3.500	−3.500	−3.500	2.500	2.500	2.500	2.500	2.500	2.500	2.500
R′O	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000
Thickness
(mm)
L*
a*
b*
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25AY
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	555	556	557	558	559	560	561	562	563	564
SiO2	61.100	61.100	61.100	61.100	61.100	61.100	61.100	61.100	61.100	61.100
Al2O3	12.500	12.500	12.500	12.500	12.500	12.500	12.500	12.500	14.500	14.500
B2O3	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000
P2O5
Li2O	10.727	11.173	11.818	8.800	9.430	9.897	10.366	11.000	13.800	12.394
Na2O	3.336	2.323	1.000	6.000	4.568	3.506	2.441	1.000	1.000	2.406
K2O	0.937	1.504	2.182	0.200	1.002	1.597	2.193	3.000	0.200	0.200
MgO	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	1.800	1.547
CaO	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	0.300	0.722
ZnO	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	0.900	0.731
SnO2
Fe2O3
TiO2	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000
CeO2	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400
R2O	15.000	15.000	15.000	15.000	15.000	15.000	15.000	15.000	15.000	15.000
Li2O + Na2O	14.063	13.496	12.818	14.800	13.998	13.403	12.807	12.000	14.800	14.800
R2O − Al2O3	2.500	2.500	2.500	2.500	2.500	2.500	2.500	2.500	0.500	0.500
R′O	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	3.000	3.000
Thickness
(mm)
L*
a*
b*
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25AZ
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	565	566	567	568	569	570	571	572	573	574
SiO2	61.100	61.100	61.100	61.100	61.100	61.100	61.100	61.100	61.100	61.100
Al2O3	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500
B2O3	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000
P2O5
Li2O	13.013	11.337	11.759	12.421	10.267	10.736	11.180	11.822	8.800	9.432
Na2O	1.000	3.463	2.309	1.000	4.533	3.328	2.317	1.000	6.000	4.564
K2O	0.987	0.200	0.932	1.579	0.200	0.937	1.502	2.178	0.200	1.004
MgO	1.378	1.357	1.172	1.061	1.164	0.986	0.865	0.740	0.900	0.728
CaO	0.469	1.039	0.850	0.595	1.360	1.156	0.974	0.724	1.800	1.542
ZnO	1.153	0.604	0.978	1.343	0.476	0.858	1.161	1.536	0.300	0.731
SnO2
Fe2O3
TiO2	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000
CeO2	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400
R2O	15.000	15.000	15.000	15.000	15.000	15.000	15.000	15.000	15.000	15.000
Li2O + Na2O	14.013	14.800	14.068	13.421	14.800	14.063	13.498	12.822	14.800	13.996
R2O − Al2O3	0.500	0.500	0.500	0.500	0.500	0.500	0.500	0.500	0.500	0.500
R′O	3.000	3.000	3.000	3.000	3.000	3.000	3.000	3.000	3.000	3.000
Thickness
(mm)
L*
a*
b*
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25BA
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	575	576	577	578	579	580	581	582	583	584
SiO2	61.100	61.100	61.100	63.100	63.100	63.100	63.100	63.100	63.100	63.100
Al2O3	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500
B2O3	5.000	5.000	5.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000
P2O5
Li2O	9.899	10.368	11.000	13.800	12.391	13.015	11.334	11.757	12.424	10.264
Na2O	3.501	2.437	1.000	1.000	2.409	1.000	3.466	2.313	1.000	4.536
K2O	1.599	2.195	3.000	0.200	0.200	0.985	0.200	0.930	1.576	0.200
MgO	0.600	0.472	0.300	2.000	2.000	2.000	2.000	2.000	2.000	2.000
CaO	1.350	1.159	0.900	2.000	2.000	2.000	2.000	2.000	2.000	2.000
ZnO	1.050	1.369	1.800	1.000	1.000	1.000	1.000	1.000	1.000	1.000
SnO2
Fe2O3
TiO2	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000
CeO2	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400
R2O	15.000	15.000	15.000	15.000	15.000	15.000	15.000	15.000	15.000	15.000
Li2O + Na2O	13.401	12.805	12.000	14.800	14.800	14.015	14.800	14.070	13.424	14.800
R2O − Al2O3	0.500	0.500	0.500	0.500	0.500	0.500	0.500	0.500	0.500	0.500
R′C	3.000	3.000	3.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000
Thickness
(mm)
L*
a*
b*
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25BB
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	585	586	587	588	589	590	591	592	593	594
SiO2	63.100	63.100	63.100	63.100	63.100	63.100	63.100	63.100	55.100	55.100
Al2O3	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500
B2O3	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	9.000	9.000
P2O5
Li2O	10.733	11.179	11.824	8.800	9.429	9.896	10.364	11.000	13.800	12.391
Na2O	3.333	2.322	1.000	6.000	4.571	3.510	2.444	1.000	1.000	2.409
K2O	0.934	1.499	2.176	0.200	1.000	1.595	2.191	3.000	0.200	0.200
MgO	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000
CaO	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000
ZnO	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000
SnO2
Fe2O3
TiO2	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000
CeO2	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MOO3
CeO2 + TiO2	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400
R2O	15.000	15.000	15.000	15.000	15.000	15.000	15.000	15.000	15.000	15.000
Li2O + Na2O	14.066	13.501	12.824	14.800	14.000	13.405	12.809	12.000	14.800	14.800
R2O − Al2O3	0.500	0.500	0.500	0.500	0.500	0.500	0.500	0.500	0.500	0.500
R′O	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000
Thickness
(mm)
L*
a*
b*
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25BC
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	595	596	597	598	599	600	601	602	603	604
SiO2	55.100	55.100	55.100	55.100	55.100	55.100	55.100	55.100	55.100	55.100
Al2O3	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500	14.500
B2O3	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000
P2O5
Li2O	13.016	11.333	11.757	12.425	10.264	10.732	11.179	11.825	8.800	9.428
Na2O	1.000	3.467	2.314	1.000	4.536	3.335	2.323	1.000	6.000	4.573
K2O	0.984	0.200	0.929	1.575	0.200	0.933	1.498	2.175	0.200	0.999
MgO	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000
CaO	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000
ZnO	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000
SnO2
Fe2O3
TiO2	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000
CeO2	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400
R2O	15.000	15.000	15.000	15.000	15.000	15.000	15.000	15.000	15.000	15.000
Li2O + Na2O	14.016	14.800	14.071	13.425	14.800	14.067	13.502	12.825	14.800	14.001
R2O − Al2O3	0.500	0.500	0.500	0.500	0.500	0.500	0.500	0.500	0.500	0.500
R′O	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000	5.000
Thickness
(mm)
L*
a*
b*
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25BD
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	605	606	607	608	609	610	611	612	613	614
SiO2	55.100	55.100	55.100	60.700	60.700	60.700	60.700	60.700	60.700	60.700
Al2O3	14.500	14.500	14.500	14.700	14.700	14.700	14.700	14.700	14.700	14.700
B2O3	9.000	9.000	9.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000
P2O5
Li2O	9.895	10.364	11.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000
Na2O	3.511	2.446	1.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000
K2O	1.594	2.190	3.000	0.200	0.200	0.200	0.200	0.200	0.200	0.200
MgO	2.000	2.000	2.000	5.500	4.060	4.357	2.996	3.112	3.508	1.933
CaO	2.000	2.000	2.000	0.500	1.940	0.786	3.004	2.097	0.998	4.067
ZnO	1.000	1.000	1.000	0.000	0.000	0.857	0.000	0.791	1.494	0.000
SnO2
Fe2O3
TiO2	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000
CeO2	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400
R2O	15.000	15.000	15.000	11.200	11.200	11.200	11.200	11.200	11.200	11.200
Li2O + Na2O	13.406	12.810	12.000	11.000	11.000	11.000	11.000	11.000	11.000	11.000
R2O − Al2O3	0.500	0.500	0.500	−3.500	−3.500	−3.500	−3.500	−3.500	−3.500	−3.500
R′O	5.000	5.000	5.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000
Thickness
(mm)
L*
a*
b*
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25BE
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	615	616	617	618	619	620	621	622	623	624
SiO2	60.700	60.700	60.700	60.700	60.700	60.700	60.700	60.700	60.700	60.804
Al2O3	14.700	14.700	14.700	14.700	14.700	14.700	14.700	14.700	14.700	14.704
B2O3	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.002
P2O5
Li2O	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.003
Na2O	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.001
K2O	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200
MgO	2.091	2.298	2.655	0.500	0.785	0.997	1.210	1.500	4.500	3.634
CaO	3.118	2.302	1.211	5.500	4.360	3.511	2.658	1.500	1.500	2.368
ZnO	0.791	1.400	2.133	0.000	0.855	1.492	2.131	3.000
SnO2
Fe2O3
TiO2	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	1.000	0.885
CeO2	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400	0.400
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.400	1.285
R2O	11.200	11.200	11.200	11.200	11.200	11.200	11.200	11.200	11.200	11.203
Li2O + Na2O	11.000	11.000	11.000	11.000	11.000	11.000	11.000	11.000	11.000	11.003
R2O − Al2O3	−3.500	−3.500	−3.500	−3.500	−3.500	−3.500	−3.500	−3.500	−3.500	−3.501
R′O	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.002
Thickness
(mm)
L*
a*
b*
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25BF
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	625	626	627	628	629	630	631	632	633	634
SiO2	62.143	60.881	62.128	63.193	60.958	62.199	63.132	64.227	61.061	62.392
Al2O3	13.463	14.707	13.562	12.563	14.711	13.567	12.700	11.677	14.715	13.479
B2O3	6.000	6.003	6.002	6.000	6.004	6.003	6.002	6.000	6.006	6.004
P2O5
Li2O	9.589	9.005	9.546	10.018	9.006	9.547	9.956	10.440	9.009	9.593
Na2O	1.853	2.001	1.865	1.746	2.001	1.865	1.762	1.640	2.002	1.855
K2O	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200
MgO	3.174	2.996	2.484	2.210	2.359	1.880	1.567	1.261	1.502	1.061
CaO	2.236	3.008	2.974	2.772	3.646	3.580	3.481	3.300	4.505	4.357
ZnO
SnO2
Fe2O3
TiO2	1.000	0.800	0.894	1.000	0.715	0.814	0.895	1.000	0.601	0.718
CeO2	0.341	0.400	0.346	0.298	0.400	0.346	0.305	0.256	0.400	0.342
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.341	1.200	1.240	1.298	1.115	1.160	1.200	1.256	1.001	1.059
R2O	11.642	11.206	11.611	11.963	11.208	11.612	11.919	12.280	11.211	11.648
Li2O + Na2O	11.442	11.006	11.411	11.763	11.008	11.412	11.718	12.080	11.011	11.447
R2O − Al2O3	−1.821	−3.502	−1.951	−0.600	−3.502	−1.954	−0.782	0.603	−3.503	−1.832
R′O	5.411	6.003	5.458	4.982	6.004	5.460	5.047	4.560	6.006	5.418
Thickness
(mm)
L*
a *
b*
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25BG
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	635	636	637	638	639	640	6411	642	643	644
SiO2	63.363	64.322	65.600	60.700	60.817	61.571	60.902	61.607	62.195	60.987
Al2O3	12.578	11.687	10.500	14.700	13.823	13.139	13.182	12.468	12.019	12.547
B2O3	6.003	6.002	6.000	6.000	6.877	6.901	7.518	7.625	7.547	8.153
P2O5
Li2O	10.019	10.439	11.000	9.000	9.000	9.600	9.000	9.552	10.031	9.000
Na2O	1.747	1.641	1.500	2.000	2.000	1.850	2.000	1.862	1.742	2.000
K2O	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200
MgO	0.740	0.423	0.000	4.500	3.623	4.050	2.982	3.289	3.727	2.347
CaO	4.249	4.142	4.000	1.500	2.377	1.350	3.018	2.159	1.242	3.653
ZnO
SnO2
Fe2O3
TiO2	0.803	0.888	1.000	1.000	0.883	1.000	0.798	0.894	1.000	0.713
CeO2	0.299	0.256	0.200	0.400	0.400	0.340	0.400	0.345	0.297	0.400
ZrO2
La2O3
SO
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.102	1.144	1.200	1.400	1.283	1.340	1.198	1.239	1.297	1.113
R2O	11.966	12.281	12.700	11.200	11.200	11.650	11.200	11.614	11.973	11.200
Li2O + Na2O	11.766	12.081	12.500	11.000	11.000	11.450	11.000	11.414	11.773	11.000
R2O − Al2O3	−0.611	0.594	2.200	−3.500	−2.623	−1.489	−1.982	−0.854	−0.046	−1.347
R′O	4.989	4.565	4.000	6.000	6.000	5.400	6.000	5.448	4.969	6.000
Thickness
(mm)
L*
a*
b*
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25BH
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	645	646	647	648	649	650	651	652	653	654
SiO2	61.683	62.202	62.803	61.100	61.838	62.374	62.901	63.600	60.661	62.068
Al2O3	11.870	11.409	10.929	11.700	11.051	10.579	10.115	9.500	14.715	13.849
B2O3	8.226	8.232	8.176	9.000	9.000	9.000	9.000	9.000	6.006	5.113
P2O5
Li2O	9.549	9.963	10.451	9.000	9.590	10.019	10.441	11.000	9.009	9.600
Na2O	1.863	1.759	1.637	2.000	1.852	1.745	1.640	1.500	2.002	2.001
K2O	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200
MgO	2.686	2.991	3.412	1.500	1.943	2.264	2.581	3.000	4.505	4.503
CaO	2.764	2.046	1.137	4.500	3.467	2.717	1.978	1.000	1.502	1.501
ZnO
SnO2
Fe2O3
TiO2	0.813	0.895	1.000	0.600	0.718	0.804	0.888	1.000	1.001	0.852
CeO2	0.345	0.304	0.255	0.400	0.341	0.298	0.256	0.200	0.400	0.311
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.158	1.199	1.255	1.000	1.059	1.102	1.144	1.200	1.401	1.163
R2O	11.612	11.922	12.288	11.200	11.643	11.964	12.281	12.700	11.211	11.802
Li2O + Na2O	11.412	11.722	12.088	11.000	11.443	11.764	12.081	12.500	11.011	11.602
R2O − Al2O3	−0.258	0.514	1.359	−0.500	0.592	1.385	2.166	3.200	−3.503	−2.047
R′O	5.451	5.037	4.549	6.000	5.410	4.981	4.559	4.000	6.006	6.004
Thickness
(mm)
L*
a*
b*
Density
(g/cm3)
Liquidus
Temp.
(° C.)

TABLE 25BI
	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-	TM-
Example	655	656	657	658	659	660	661	662	663	664
SiO2	62.777	63.086	63.874	64.293	64.083	64.816	65.297	65.769	65.400	66.069
Al2O3	13.448	13.223	12.770	12.540	12.610	12.190	11.918	11.656	11.800	11.422
B2O3	5.102	4.468	4.369	4.455	3.835	3.767	3.764	3.825	3.000	3.000
P2O5
Li2O	9.908	10.028	10.368	10.553	10.447	10.764	10.973	11.179	11.000	11.291
Na2O	2.001	2.001	2.001	2.001	2.001	2.001	2.001	2.001	2.000	2.000
K2O	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200
MgO	4.052	4.502	4.090	3.728	4.501	4.093	3.782	3.413	4.500	4.064
CaO	1.351	1.501	1.363	1.243	1.500	1.364	1.261	1.138	1.500	1.355
ZnO
SnO2
Fe2O3
TiO2	0.850	0.745	0.728	0.742	0.639	0.628	0.627	0.637	0.500	0.500
CeO2	0.310	0.247	0.237	0.245	0.183	0.177	0.176	0.182	0.100	0.100
ZrO2
La2O3
SO3
WO3
Nb2O5
Bi2O3
MoO3
CeO2 + TiO2	1.160	0.991	0.965	0.988	0.823	0.805	0.804	0.820	0.600	0.600
R2O	12.110	12.229	12.569	12.754	12.647	12.965	13.173	13.380	13.200	13.491
Li2O + Na2O	11.910	12.029	12.369	12.553	12.447	12.765	12.973	13.180	13.000	13.291
R2O − Al2O3	−1.338	−0.995	−0.201	0.214	0.038	0.774	1.255	1.724	1.400	2.069
R′O	5.403	6.003	5.453	4.971	6.002	5.457	5.043	4.550	6.000	5.418
Thickness
(mm)
L*
a*
b*
Density
(g/cm3)
Liquidus
Temp.
(° C.)

	TABLE 25BJ
	Example	TM-665	TM-666	TM-667
	SiO2	66.560	67.047	67.700
	Al2O3	11.144	10.869	10.500
	B2O3	3.000	3.000	3.000
	P2O
	Li2O	11.504	11.716	12.000
	Na2O	2.000	2.000	2.000
	K2O	0.200	0.200	0.200
	MgO	3.743	3.426	3.000
	CaO	1.248	1.142	1.000
	ZnO
	SnO2
	Fe2O3
	TiO2	0.500	0.500	0.500
	CeO2	0.100	0.100	0.100
	ZrO2
	La2O3
	SO3
	WO3
	Nb2O5
	Bi2O3
	MoO3
	CeO2 + TiO2	0.600	0.600	0.600
	R2O	13.704	13.916	14.200
	Li2O + Na2O	13.504	13.716	14.000
	R2O—Al2O3	2.560	3.047	3.700
	R′O	4.991	4.567	4.000
	Thickness
	(mm)
	L*
	a*
	b*
	Density
	(g/cm3)
	Liquidus
	Temp.
	(° C.)

The change in b* value experienced as a result of the annealing process for Examples TM-476 to TM-502 was calculated, and is reported in Table 26 below.

TABLE 26
Example Delta b*
TM-476  0.28
TM-477  0.20
TM-478  0.30
TM-479  0.39
TM-480  0.62
TM-481  0.11
TM-482  0.92
TM-483  0.45
TM-484  1.22
TM-485  1.26
TM-486  1.41
TM-487  4.01
TM-488  2.00
TM-489  6.06
TM-490  15.85
TM-491  0.42
TM-492  0.19
TM-493  0.56
TM-494  58.97
TM-495  −0.07
TM-496  0.05
TM-497  0.22
TM-498  20.43
TM-499  0.46
TM-500  1.39
TM-501  −0.07
TM-502  4.78

To investigate the impact of Fe₂O₃ content in the glass composition on the color and color stability of the colored glass articles, the b* value was plotted for a number of glass compositions with different Fe₂O₃ contents, as shown in FIG. 52. The solid box in FIG. 52 identifies a Fe₂O₃ content regime that minimizes the color sensitivity of the colored glass article while not significantly affecting the b* value. The dashed box in FIG. 52 identifies Fe₂O₃ contents that produced stable colors after 20 hours at a temperature of 600° C.

The effect of SnO₂ content on b* was investigated by plotting the a* and b* values for glass compositions with various analyzed SnO₂ contents, as shown in FIG. 53. In FIG. 53 the data points are labeled with the analyzed SnO₂ content. As shown in FIG. 53, increasing SnO₂ content decreases the b* value and increases the a* value of the colored glass article.

To investigate the impact of CeO₂ on the stability of titanium oxidation states in the colored glass articles, and the associated color stability of the colored glass articles, XPS analysis was performed. Glass bars with a size of 3 mm×3 mm×10 mm were formed from the glass composition of Example TM-361 that includes CeO₂ and TiO₂, and a comparative composition that contains TiO₂ in the absence of CeO₂ was formed into bars of the same dimensions. The comparative composition as analyzed included 61.5 mol % SiO₂, 14.5 mol % Al₂O₃, 5.7 mol % B₂O₃, 9.8 mol % Li₂O, 1.8 mol % Na₂O, 0.2 mol % K₂O, 2.0 mol % MgO, 2.0 mol % CaO, 1.0 mol % ZnO, 1.5 mol % TiO₂, and 0.004 mol % Fe₂O₃. The Example TM-361 glass bars were fractured under ultra-high vacuum in as formed condition, after annealing at 600° C. for 24 hours, and after annealing at 600° C. for 48 hours. The oxidation state of titanium and cerium was determined by XPS analysis at the fracture site, with the predominant oxidation state for titanium being Ti⁴⁺ and for cerium being Ce³⁺. The results indicated that the content of Ti³⁺ increased with increasing annealing time as shown in FIG. 54, and suggests that an observed color change may be due to the change of titanium oxidation state. In contrast, the XPS results for the comparative composition indicated that the titanium oxidation state did not change as a function of anneal time. XPS results also indicated that the presence of Fe₂O₃ in the glass compositions inhibits the transition of Ti⁴¹ to Ti³⁺ when heat treated, as shown in FIG. 55, improving color stability.

Tables 27A-27Z show example colored glass articles (in terms of mol %) containing transition metal oxides and/or rare earth oxides as colorant(s). The density, thickness, and transmittance color coordinates in the CIELAB color space, as measured under F2 illumination and a 100 standard observer angle are also reported in Tables 27A-27Z.

TABLE 27A
Example	TM-668	TM-669	TM-670	TM-671	TM-672	TM-673	TM-674	TM-675	TM-676
SiO2	59.628	59.304	59.086	59.387	59.413	59.364	59.216	59.208	59.194
Al2O3	14.591	14.557	14.528	14.630	14.585	14.562	14.536	14.495	14.316
B2O3	5.954	5.938	5.941	5.818	5.810	5.808	5.812	5.961	6.000
Li2O	9.971	9.943	9.949	9.452	9.439	9.436	9.444	9.266	9.327
Na2O	2.056	2.041	2.026	2.038	2.025	2.035	2.068	2.078	2.106
K2O	0.201	0.198	0.202	0.204	0.206	0.202	0.209	0.207	0.208
MgO	0.815	1.079	1.240	1.327	1.372	1.422	1.463	1.467	1.442
CaO	4.520	4.507	4.493	4.527	4.514	4.504	4.524	4.523	4.499
ZnO
SnO2	0.023	0.020	0.020	0.020	0.022	0.020	0.019	0.022	0.034
Fe2O3	0.062	0.040	0.026	0.019	0.016	0.011	0.009	0.008	0.008
ZrO2	0.023	0.022	0.023	0.020	0.020	0.019	0.015	0.016	0.045
TiO2	1.841	2.120	2.282	2.396	2.432	2.488	2.524	2.531	2.501
CeO2	0.310	0.225	0.177	0.153	0.140	0.121	0.114	0.113	0.119
Er2O3	0.001	0.001	0.001	0.001	0.001	0.001	0.040	0.097	0.196
Nd2O3
NiO
CO3O4
Cr2O3
CuO
Density
(g/cc)
Thickness	4.240	4.008	4.078	4.120	4.284	4.319	4.212	4.128	4.357
(mm)
L*	94.25	94.90	95.51	95.65	95.81	95.94	95.64	95.15	94.35
a *	−2.21	−2.07	−1.82	−1.68	−1.57	−1.46	−0.24	0.95	2.63
b*	19.13	16.05	12.60	11.21	10.08	9.06	8.17	8.08	8.97
Liquidus
(° C.)

TABLE 27B
Example	TM-677	TM-678	TM-679	TM-680	TM-681	TM-682	TM-683	TM-684	TM-685
SiO2	58.988	58.833	58.882	58.986	58.980	58.925	59.071	59.214	59.356
Al2O3	14.288	14.198	14.241	14.164	14.147	14.160	14.164	14.182	14.152
B2O3	6.028	6.066	5.965	5.972	5.978	5.989	5.998	5.988	5.982
Li2O	9.371	9.430	9.325	9.335	9.345	9.362	9.124	9.110	9.099
Na2O	2.123	2.128	2.110	2.098	2.081	2.075	2.103	2.098	2.114
K2O	0.205	0.206	0.203	0.206	0.200	0.197	0.206	0.207	0.206
MgO	1.479	1.482	1.521	1.504	1.510	1.509	1.506	1.508	1.505
CaO	4.512	4.514	4.550	4.521	4.518	4.521	4.527	4.543	4.531
ZnO
SnO2	0.027	0.028	0.023	0.029	0.026	0.023	0.034	0.033	0.043
Fe2O3	0.007	0.007	0.006	0.006	0.006	0.006	0.006	0.006	0.006
ZrO2	0.024	0.041	0.029	0.029	0.026	0.023	0.033	0.029	0.031
TiO2	2.539	2.539	2.561	2.551	2.555	2.560	2.568	2.426	2.316
CeO2	0.109	0.113	0.112	0.112	0.110	0.110	0.112	0.109	0.109
Er2O3	0.291	0.409	0.463	0.482	0.513	0.532	0.542	0.541	0.542
Nd2O3
NiC
CO3O4
Cr2O3
CuO
Density			2.499		2.504		2.508		2.505
(g/cc)
Thickness	4.289	4.124	4.216	4.072	4.195	4.134	4.132	3.935	3.869
(mm)
L*	93.94	93.12	92.96	92.83	92.72	92.63	92.46	92.83	92.95
a*	4.03	5.21	5.66	5.85	6.15	6.14	6.29	6.57	6.60
b*	8.24	9.81	9.99	10.56	10.50	10.82	11.66	7.99	6.61
Liquidus
(° C.)

TABLE 27C
Example	TM-686	TM-687	TM-688	TM-689	TM-690	TM-691	TM-692	TM-693	TM-694
SiO2	59.941	60.557	60.916	61.013	61.055	61.063	61.043	61.151	61.284
Al2O3	14.150	14.180	14.183	14.178	14.200	14.155	14.295	14.326	14.311
B2O3	5.980	5.986	5.985	5.985	5.976	5.997	5.988	5.993	5.987
Li2O	9.098	9.151	9.149	9.150	9.135	9.162	9.147	9.155	9.146
Na2O	2.148	2.137	2.126	2.115	2.086	2.102	2.095	2.113	2.126
K2O	0.202	0.200	0.207	0.209	0.204	0.208	0.207	0.205	0.205
MgO	1.520	1.525	1.528	1.524	1.528	1.511	1.512	1.517	1.515
CaO	4.554	4.561	4.549	4.545	4.550	4.540	4.523	4.550	4.541
ZnO
SnO2	0.021	0.019	0.023	0.019	0.019	0.023	0.019	0.019	0.018
Fe2O3	0.006	0.006	0.005	0.005	0.006	0.006	0.006	0.006	0.006
ZrO2	0.016	0.012	0.016	0.018	0.016	0.017	0.015	0.014	0.013
TiO2	1.695	1.005	0.651	0.575	0.561	0.552	0.489	0.285	0.179
CeO2	0.107	0.106	0.107	0.106	0.106	0.106	0.105	0.105	0.106
Er2O3	0.558	0.551	0.551	0.554	0.555	0.555	0.552	0.558	0.562
Nd2O3
NiO
Co3O4
Cr2O3
CuO
Density		2.489		2.485		2.485		2.482
(g/cc)
Thickness	3.785	3.863	3.978	4.104	4.137	4.114	4.165	4.009	4.515
(mm)
L*	93.47	93.69	93.80	93.82	93.81	93.80	93.89	93.94	93.86
a*	7.16	7.38	7.47	7.46	7.52	7.52	7.39	7.36	7.46
b*	1.91	−0.29	−0.89	−0.95	−1.00	−1.06	−1.10	−1.37	−1.45
Liquidus
(° C.)

TABLE 27D
Example	TM-695	TM-696	TM-697	TM-698	TM-699	TM-700	TM-701	TM-702	TM-703
SiO2	61.374	61.330	61.313	61.341	61.095	60.891	60.838	60.750	60.691
Al2O3	14.288	14.325	14.252	14.228	14.287	14.314	14.292	14.303	14.349
B2O3	5.960	5.959	5.963	5.991	6.005	6.011	6.021	5.959	5.962
Li2O	9.147	9.146	9.153	9.057	9.077	9.086	9.101	9.197	9.201
Na2O	2.110	2.109	2.119	2.107	2.117	2.137	2.126	2.116	2.092
K2O	0.206	0.207	0.208	0.210	0.207	0.205	0.205	0.204	0.200
MgO	1.518	1.533	1.528	1.500	1.500	1.513	1.501	1.505	1.515
CaO	4.544	4.550	4.531	4.508	4.535	4.542	4.521	4.519	4.536
ZnO
SnO2	0.021	0.021	0.013	0.015	0.014	0.018	0.017	0.017	0.015
Fe2O3	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006
ZrO2	0.014	0.015	0.012	0.014	0.013	0.019	0.022	0.017	0.017
TiO2	0.147	0.133	0.119	0.127	0.121	0.132	0.129	0.123	0.116
CeO2	0.104	0.104	0.218	0.336	0.459	0.564	0.656	0.715	0.734
Er2O3	0.558	0.559	0.562	0.557	0.560	0.559	0.561	0.565	0.563
Nd2O3
NiO
Co3O4
Cr2O3
CuO
Density	2.481
(g/cc)
Thickness	4.487	3.840	4.025	4.194	3.908	4.157	3.992	3.894	4.001
(mm)
L*	93.91	93.94	93.62	93.53	93.15	92.80	92.47	92.20	92.17
a*	7.45	7.39	7.18	6.86	6.57	6.38	6.14	6.13	6.02
b*	−1.51	−1.55	0.06	1.83	3.97	5.85	7.67	8.57	8.73
Liquidus
(° C.)

TABLE 27E
Example	TM-704	TM-705	TM-706	TM-707	TM-708	TM-709	TM-710	TM-711	TM-712
SiO2	60.652	60.743	60.892	60.628	61.227	61.093	60.899	60.944	60.957
Al2O3	14.363	14.328	14.294	14.583	14.330	14.589	14.631	14.542	14.555
B2O3	5.962	5.956	5.884	5.870	5.835	5.800	5.927	5.938	5.932
Li2O	9.202	9.192	9.156	9.132	9.079	9.024	9.127	9.143	9.135
Na2O	2.091	2.086	2.098	2.064	2.096	2.097	2.057	2.055	2.052
K2O	0.202	0.199	0.199	0.198	0.210	0.210	0.200	0.204	0.201
MgO	1.525	1.502	1.493	1.554	1.444	1.463	1.495	1.497	1.499
CaO	4.532	4.524	4.514	4.617	4.508	4.557	4.541	4.550	4.547
ZnO
SnO2	0.017	0.021	0.028	0.018	0.010	0.009	0.011	0.014	0.014
Fe2O3	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006
ZrO2	0.017	0.023	0.026	0.012	0.010	0.015	0.014	0.016	0.014
TiO2	0.116	0.116	0.117	0.113	0.109	0.111	0.111	0.112	0.112
CeO2	0.749	0.745	0.739	0.774	0.776	0.792	0.780	0.781	0.782
Er2O3	0.563	0.555	0.551	0.429	0.357	0.232	0.198	0.196	0.192
Nd2O3
NiO
Co3O4
Cr2O3
CuO
Density	2.512		2.511				2.470		2.468
(g/cc)
Thickness	3.805	3.844	3.954	3.868	4.114	4.092	3.929	4.050	4.004
(mm)
L*	92.07	92.15	92.12	92.40	92.54	93.01	93.28	93.33	93.35
a*	6.04	5.99	6.06	5.00	4.34	2.88	2.45	2.38	2.37
b*	9.06	8.87	8.67	9.61	10.34	10.88	10.43	10.35	10.27
Liquidus
(° C.)

TABLE 27F
Example	TM-713	TM-714	TM-715	TM-716	TM-717	TM-718	TM-719	TM-720	TM-721
SiO2	60.805	60.511	60.539	60.398	60.465	60.305	60.237	60.087	60.440
Al2O3	14.567	14.567	14.473	14.452	14.399	14.360	14.248	14.199	14.056
B2O3	5.940	5.959	5.952	5.961	5.953	6.029	6.057	6.097	6.121
Li2O	9.147	9.147	9.136	9.151	9.138	9.256	9.299	9.360	9.398
Na2O	2.047	2.030	2.027	2.050	2.062	2.065	2.075	2.069	2.083
K2O	0.203	0.199	0.201	0.205	0.208	0.208	0.209	0.207	0.206
MgO	1.496	1.496	1.487	1.500	1.494	1.501	1.511	1.504	1.495
CaO	4.551	4.528	4.521	4.548	4.535	4.531	4.525	4.545	4.565
ZnO
SnO2	0.020	0.021	0.016	0.012	0.017	0.016	0.013	0.015	0.018
Fe2O3	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.005
ZrO2	0.019	0.014	0.011	0.015	0.014	0.013	0.013	0.012	0.023
TiO2	0.290	0.840	1.167	1.280	1.296	1.312	1.323	1.330	0.843
CeO2	0.701	0.433	0.188	0.136	0.125	0.113	0.112	0.111	0.190
Er2O3	0.206	0.246	0.273	0.281	0.284	0.283	0.369	0.453	0.550
Nd2O3
NiO
Co3O4
Cr2O3
CuO
Density		2.466				2.460		2.481
(g/cc)
Thickness	4.449	4.060	4.161	4.106	4.139	4.138	4.038	4.251	4.149
(mm)
L*	93.59	94.24	94.63	94.69	94.70	94.68	94.28	93.97	93.56
a*	2.43	3.00	4.10	4.41	4.52	4.64	5.58	6.44	7.07
b*	9.90	7.73	2.95	1.94	1.54	1.28	1.07	0.81	1.45
Liquidus
(° C.)

TABLE 27G
Example	TM-722	TM-723	TM-724	TM-725	TM-726	TM-727	TM-728	TM-729	TM-730
SiO2	60.497	60.632	60.782	60.845	60.918	60.910	60.982	60.980	61.257
Al2O3	14.125	14.089	14.039	14.031	14.046	14.087	14.045	14.045	14.042
B2O3	6.194	6.207	6.211	6.213	6.238	6.236	6.232	6.232	6.212
Li2O	9.290	9.309	9.315	9.318	9.207	9.204	9.198	9.198	9.183
Na2O	2.090	2.095	2.078	2.077	2.083	2.083	2.085	2.083	2.093
K2O	0.205	0.207	0.205	0.205	0.202	0.202	0.200	0.202	0.205
MgO	1.505	1.502	1.500	1.500	1.491	1.507	1.500	1.498	1.508
CaO	4.612	4.595	4.575	4.576	4.572	4.579	4.567	4.575	4.583
ZnO
SnO2	0.024	0.022	0.022	0.021	0.026	0.022	0.028	0.034	0.029
Fe2O3	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006
ZrO2	0.022	0.023	0.023	0.023	0.031	0.021	0.026	0.023	0.014
TiO2	0.624	0.448	0.347	0.262	0.251	0.199	0.200	0.197	0.082
CeO2	0.226	0.252	0.268	0.282	0.284	0.291	0.276	0.272	0.112
Er2O3	0.578	0.611	0.627	0.640	0.642	0.651	0.652	0.652	0.671
Nd2O3
NiO
Co3O4
Cr2O3
CuO
Density	2.495
(g/cc)
Thickness	4.061	4.177	4.091	4.171	4.052	4.578	4.049	4.253	3.997
(mm)
L*	93.49	93.39	93.40	93.28	93.32	93.34	93.37	93.39	93.54
a*	7.06	7.32	7.46	7.46	7.54	7.53	7.65	7.68	8.17
b*	1.32	1.36	1.24	1.20	1.01	1.04	0.67	0.44	−1.79
Liquidus
(° C.)

TABLE 27H
Example	TM-731	TM-732	TM-733	TM-734	TM-735	TM-736	TM-737	TM-738	TM-739
SiO2	61.394	61.473	61.524	61.457	61.632	61.793	61.891	61.878	62.038
Al2O3	14.054	14.021	13.983	14.191	14.178	14.318	14.341	14.535	14.516
B2O3	6.215	6.212	6.212	6.191	6.166	6.113	6.095	6.094	6.073
Li2O	9.187	9.182	9.183	9.146	9.108	9.030	9.005	8.963	8.932
Na2O	2.077	2.078	2.088	2.089	2.082	2.067	2.071	2.068	2.046
K2O	0.207	0.207	0.209	0.207	0.210	0.203	0.203	0.198	0.200
MgO	1.525	1.509	1.515	1.525	1.525	1.504	1.505	1.488	1.476
CaO	4.557	4.551	4.526	4.588	4.543	4.565	4.538	4.565	4.549
ZnO
SnO2	0.018	0.020	0.022	0.019	0.015	0.019	0.013	0.017	0.021
Fe2O3	0.006	0.006	0.006	0.006	0.005	0.006	0.006	0.006	0.006
ZrO2	0.011	0.015	0.017	0.009	0.011	0.010	0.008	0.008	0.009
TiO2	0.026	0.017	0.014	0.011	0.010	0.013	0.011	0.011	0.011
CeO2	0.036	0.022	0.018	0.012	0.010	0.008	0.006	0.005	0.004
Er2O3	0.685	0.683	0.679	0.547	0.501	0.351	0.305	0.162	0.118
Nd2O3
NiO
Co3O4
Cr2O3
CuO
Density				2.472				2.425
(g/cc)
Thickness	3.886	4.061	3.923	4.245	3.768	3.894	3.894	3.870	3.841
(mm)
L*	93.53	93.56	93.58	93.92	94.15	94.67	94.82	95.59	95.85
a*	8.34	8.29	8.21	7.36	6.93	5.59	5.16	3.13	2.42
b*	−2.07	−2.09	−2.06	−1.91	−1.83	−1.51	−1.38	−0.79	−0.55
Liquidus
(° C.)

TABLE 27I
Example	TM-740	TM-741	TM-742	TM-743	TM-744	TM-745	TM-746	TM-747	TM-748
SiO2	62.017	62.079	60.560	60.560	60.610	60.610	60.660	60.660	60.710
Al2O3	14.531	14.513	14.740	14.740	14.740	14.740	14.740	14.740	14.740
B2O3	6.074	6.066	6.000	6.000	6.000	6.000	6.000	6.000	6.000
Li2O	8.934	8.923	9.000	9.000	9.000	9.000	9.000	9.000	9.000
Na2O	2.041	2.043	2.000	2.000	2.000	2.000	2.000	2.000	2.000
K2O	0.200	0.201	0.200	0.200	0.200	0.200	0.200	0.200	0.200
MgO	1.479	1.482	1.500	1.500	1.500	1.500	1.500	1.500	1.500
CaO	4.553	4.535	4.500	4.500	4.500	4.500	4.500	4.500	4.500
ZnO
SnO2	0.021	0.019
Fe2O3	0.006	0.006
ZrO2	0.017	0.014
TiO2	0.011	0.011	0.900	0.900	0.800	0.800	0.700	0.700	0.600
CeO2	0.004	0.004	0.354	0.354	0.391	0.391	0.428	0.428	0.465
Er2O3	0.109	0.102	0.250	0.250	0.262	0.262	0.275	0.275	0.287
Nd2O3
NiO
Co3O4
Cr2O3
CuO
Density
(g/cc)
Thickness	3.893	4.004	0.626	2.458	0.606	2.463	0.604	2.456	0.616
(mm)
L*	95.89	95.92	96.15	95.04	96.15	94.78	96.11	94.75	96.17
a*	2.31	2.19	0.61	2.00	0.63	2.13	0.67	2.24	0.74
b*	−0.50	−0.47	1.75	5.39	1.68	6.12	1.70	5.91	1.46
Liquidus
(° C.)

TABLE 27J
Example	TM-749	TM-750	TM-751	TM-752	TM-753	TM-754	TM-755	TM-756	TM-757
SiO2	60.710	60.760	60.760	60.810	60.810	60.860	60.860	60.910	60.910
Al2O3	14.740	14.740	14.740	14.740	14.740	14.740	14.740	14.740	14.740
B2O3	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000
Li2O	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000
Na2O	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000
K2O	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200
MgO	1.500	1.500	1.500	1.500	1.500	1.500	1.500	1.500	1.500
CaO	4.500	4.500	4.500	4.500	4.500	4.500	4.500	4.500	4.500
ZnO
SnO2
Fe2O3
ZrO2
TiO2	0.600	0.500	0.500	0.400	0.400	0.300	0.300	0.200	0.200
CeO2	0.465	0.503	0.503	0.540	0.540	0.577	0.577	0.614	0.614
Er2O3	0.287	0.299	0.299	0.312	0.312	0.324	0.324	0.336	0.336
Nd2O3
NiO
Co3O4
Cr2O3
CuO
Density								2.478
(g/cc)
Thickness	2.444	0.622	2.436	0.602	2.441	0.621	2.454	0.603	2.430
(mm)
L*	94.51	96.03	94.64	96.14	94.30	95.98	94.34	95.93	94.25
a*	2.35	0.81	2.52	0.81	2.67	0.88	2.83	0.99	2.99
b*	6.48	1.68	5.44	1.32	6.26	1.67	5.64	1.54	5.40
Liquidus
(° C.)

TABLE 27K
Example	TM-758	TM-759	TM-760	TM-761	TM-762	TM-763	TM-764	TM-765	TM-766
SiO2	60.960	60.960	60.890	60.890	60.920	60.920	60.960	60.960	61.000
Al2O3	14.740	14.740	14.740	14.740	14.740	14.740	14.740	14.740	14.740
B2O3	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000
Li2O	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000
Na2O	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000
K2O	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200
MgO	1.500	1.500	1.500	1.500	1.500	1.500	1.500	1.500	1.500
CaO	4.500	4.500	4.500	4.500	4.500	4.500	4.500	4.500	4.500
ZnO
SnO2
Fe2O3
ZrO2
TiO2	0.100	0.100	0.752	0.752	0.691	0.691	0.610	0.610	0.529
CeO2	0.652	0.652			0.023	0.023	0.053	0.053	0.083
Er2O3	0.349	0.349	0.423	0.423	0.430	0.430	0.440	0.440	0.450
Nd2O3
NiO
Co3O4
Cr2O3
CuO
Density		2.482
(g/cc)
Thickness	0.617	2.448	0.528	2.425	0.530	2.392	0.531	2.389	0.542
(mm)
L*	96.08	93.98	96.24	94.92	96.22	95.00	96.20	94.97	96.20
a*	0.99	3.26	1.28	4.62	1.30	4.62	1.32	4.61	1.34
b*	1.14	5.64	−0.23	−0.98	−0.23	−1.02	−0.17	−0.78	−0.14
Liquidus
(° C.)

TABLE 27L
Example	TM-767	TM-768	TM-769	TM-770	TM-771	TM-772	TM-773	TM-774	TM-775
SiO2	61.000	61.040	61.040	61.080	61.080	61.120	61.120	61.160	61.160
Al2O3	14.740	14.740	14.740	14.740	14.740	14.740	14.740	14.740	14.740
B2O3	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000
Li2O	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000
Na2O	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000
K2O	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200
MgO	1.500	1.500	1.500	1.500	1.500	1.500	1.500	1.500	1.500
CaO	4.500	4.500	4.500	4.500	4.500	4.500	4.500	4.500	4.500
ZnO
SnO2
Fe2O3
ZrO2
TiO2	0.529	0.448	0.448	0.367	0.367	0.286	0.286	0.205	0.205
CeO2	0.083	0.113	0.113	0.143	0.143	0.174	0.174	0.204	0.204
Er2O3	0.450	0.460	0.460	0.470	0.470	0.480	0.480	0.490	0.490
Nd2O3
NiO
Co3O4
Cr2O3
CuO
Density
(g/cc)
Thickness	2.387	0.539	2.425	0.481	2.347	0.492	2.349	0.518	2.369
(mm)
L*	94.91	96.20	94.81	96.22	94.90	96.22	94.84	96.19	94.65
a*	4.62	1.34	4.67	1.19	4.51	1.24	4.60	1.35	4.65
b*	−0.47	−0.08	−0.15	−0.01	−0.18	0.00	−0.04	0.00	0.29
Liquidus
(° C.)

TABLE 27M
Example	TM-776	TM-777	TM-778	TM-779	TM-780	TM-781	TM-782	TM-783	TM-784
SiO2	61.200	61.200	60.360	60.360	60.360	60.360	59.760	59.760	60.360
Al2O3	14.740	14.740	14.740	14.740	14.740	14.740	14.740	14.740	14.740
B2O3	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000
Li2O	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000
Na2O	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000
K2O	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200
MgO	1.500	1.500	1.500	1.500	1.500	1.500	1.500	1.500	1.500
CaO	4.500	4.500	4.500	4.500	4.500	4.500	4.500	4.500	4.500
ZnO
SnO2
Fe2O3
ZrO2
TiO2	0.124	0.124	0.400	0.400	0.900	0.900	1.500	1.500	0.500
CeO2	0.234	0.234	0.800	0.800	0.300	0.300	0.600	0.600	1.000
Er2O3	0.500	0.500	0.500	0.500	0.500	0.500	0.200	0.200	0.200
Nd2O3
NiO
Co3O4
Cr2O3
CuO
Density				2.527		2.516		2.500	2.480
(g/cc)
Thickness	0.529	2.530	0.556	2.386	0.557	2.382	0.591	2.387
(mm)
L*	96.10	94.64	95.65	92.55	96.04	94.22	92.85	80.58
a*	1.41	4.71	1.11	3.67	1.23	4.15	−1.03	3.09
b*	0.06	0.38	2.47	11.15	1.07	4.68	18.74	59.89
Liquidus			1140	1140	1130	1130	1110	1110
(° C.)

TABLE 27N
Example	TM-785	TM-786	TM-787	TM-788	TM-789	TM-790	TM-791	TM-792	TM-793
SiO2	61.560	61.560	61.660	61.660	61.760	61.760	61.860	61.860	61.960
Al2O3	14.740	14.740	14.740	14.740	14.740	14.740	14.740	14.740	14.740
B2O3	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000
Li2O	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000
Na2O	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000
K2O	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200
MgO	1.500	1.500	1.500	1.500	1.500	1.500	1.500	1.500	1.500
CaO	4.500	4.500	4.500	4.500	4.500	4.500	4.500	4.500	4.500
ZnO
SnO2
Fe2O3
ZrO2
TiO2
CeO2
Er2O3	0.500	0.500	0.400	0.400	0.300	0.300	0.200	0.200	0.100
Nd2O3
NiO
Co3O4
Cr2O3
CuO
Density		2.469		2.459		2.458		2.441
(g/cc)
Thickness	0.562	2.396	0.573	2.389	0.548	2.388	0.550	2.388	0.581
(mm)
L*	96.22	94.94	96.27	95.19	96.41	95.55	96.53	95.88	96.64
a*	1.45	4.94	1.17	4.25	0.85	3.33	0.58	2.39	0.31
b*	−0.30	−1.30	−0.26	−1.07	−0.10	−0.81	−0.02	−0.53	0.07
Liquidus	1120	1120	1120	1120	1125	1125	1110	1110	1125
(° C.)

TABLE 27O
Example	TM-794	TM-795	TM-796	TM-797	TM-798	TM-799	TM-800	TM-801	TM-802
SiO2	61.960	61.380	61.380	61.380	61.380	61.380	61.340	61.340	61.340
Al2O3	14.740	14.700	14.700	14.700	14.700	14.700	14.700	14.700	14.700
B2O3	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000
Li2O	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000
Na2O	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000
K2O	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200
MgO	1.500	1.500	1.500	1.500	1.500	1.500	1.500	1.500	1.500
CaO	4.500	4.500	4.500	4.500	4.500	4.500	4.500	4.500	4.500
ZnO
SnO2
Fe2O3
ZrO2
TiO2		0.358	0.358	0.358	0.358	0.358	0.320	0.320	0.320
CeO2		0.120	0.120	0.120	0.120	0.120	0.030	0.030	0.030
Er2O3	0.100	0.237	0.237	0.237	0.237	0.237	0.409	0.409	0.409
Nd2O3
NiO
Co3O4
Cr2O3
CuO
Density	2.431
(g/cc)
Thickness	2.392		0.562	2.402	0.535	2.374		0.561	2.408
(mm)
L*	96.26		96.49	95.65	96.51	95.70		96.30	95.14
a*	1.28		0.68	2.65	0.65	2.58		1.19	4.30
b*	−0.20		0.08	0.12	0.10	0.11		−0.19	−0.97
Liquidus	1125	1115					1125
(° C.)

TABLE 27P
	Example
	TM-803	TM-804	TM-805	TM-806	TM-807	TM-808	TM-809	TM-810	TM-811
SiO2	58.830	58.830	59.370	59.370	60.430	60.430	58.560	58.560	59.730
Al2O3	14.700	14.700	14.700	14.700	14.700	14.700	14.700	14.700	14.700
B2O3	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000
Li2O	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000
Na2O	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000
K2O	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200
MgO	1.500	1.500	1.500	1.500	1.500	1.500	1.500	1.500	1.500
CaO	4.500	4.500	4.500	4.500	4.500	4.500	4.500	4.500	4.500
ZnO
SnO2
Fe2O3
ZrO2
TiO2	2.551	2.551	1.852	1.852	0.507	0.507	3.130	3.130	1.624
CeO2	0.707	0.707	0.795	0.795	0.964	0.964	0.003	0.003	0.192
Er2O3	0.010	0.010	0.080	0.080	0.200	0.200	0.410	0.410	0.550
Nd2O3
NiO
Co3O4
Cr2O3
CuO
Density		2.483		2.487		2.495		2.502
(g/cc)
Thickness	0.565	2.476	0.591	2.430	0.575	2.435	0.559	2.406	0.565
(mm)
L*	87.33	64.75	92.00	78.90	95.85	93.09	95.41	91.78	95.74
a*	0.33	15.46	−1.61	3.33	0.23	1.12	1.56	5.49	1.20
b*	45.88	90.85	24.64	67.66	3.28	13.25	0.97	4.52	2.75
Liquidus		1125		1155		1135		1110
(° C.)

TABLE 27Q
	Example
	TM-812	TM-813	TM-814	TM-815	TM-816	TM-817	TM-818	TM-819	TM-820
SiO2	59.730	60.570	60.570	60.638	60.638	58.787	58.787	59.878	59.878
Al2O3	14.700	14.700	14.700	14.700	14.700	14.700	14.700	14.700	14.700
B2O3	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000
Li2O	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000
Na2O	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000
K2O	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200
MgO	1.500	1.500	1.500	1.500	1.500	1.500	1.500	1.500	1.500
CaO	4.500	4.500	4.500	4.500	4.500	4.500	4.500	4.500	4.500
ZnO
SnO2
Fe2O3
ZrO2
TiO2	1.624	0.548	0.548	0.594	0.594	2.071	2.071	1.212	1.212
CeO2	0.192	0.327	0.327	0.808	0.808	0.988	0.988	0.875	0.875
Er2O3	0.550	0.650	0.650	0.060	0.060	0.254	0.254	0.135	0.135
Nd2O3
NiO
Co3O4
Cr2O3
CuO
Density	2.510	2.510
(g/cc)
Thickness	2.402	2.404	0.560	0.578	2.414	0.578	2.404	0.586	2.399
(mm)
L*	93.48	94.01	95.87	96.22	94.48	85.96	60.04	93.85	87.70
a*	3.59	5.22	1.70	−0.17	−0.52	0.43	15.34	−1.03	−0.49
b*	11.00	3.02	0.65	2.75	11.35	47.04	85.82	13.22	38.02
Liquidus	1105	1125
(° C.)

TABLE 27R
	Example
	TM-821	TM-822	TM-823	TM-824	TM-825	TM-826	TM-827	TM-828	TM-829
SiO2	59.963	59.963	57.421	57.421	58.991	58.991	61.419	61.419	61.419
Al2O3	14.700	14.700	14.700	14.700	14.700	14.700	14.700	14.700	14.700
B2O3	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000
Li2O	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000
Na2O	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000
K2O	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200
MgO	1.500	1.500	1.500	1.500	1.500	1.500	1.500	1.500	1.500
CaO	4.500	4.500	4.500	4.500	4.500	4.500	4.500	4.500	4.500
ZnO
SnO2
Fe2O3
ZrO2
TiO2	1.633	1.633	4.104	4.104	2.575	2.575	0.350	0.350	0.350
CeO2	0.067	0.067	0.077	0.077	0.072	0.072	0.080	0.080	0.080
Er2O3	0.437	0.437	0.498	0.498	0.462	0.462	0.251	0.251	0.251
Nd2O3
NiO
Co3O4
Cr2O3
CuO
Density	2.484				2.501		2.451
(g/cc)
Thickness	0.580	2.430	0.638	2.447	0.550	2.408	0.542	2.410	0.551
(mm)
L*	96.06	94.61	87.69	80.63	95.26	91.27	96.45	95.61	96.47
a*	1.24	4.21	1.92	6.64	0.89	3.57	0.75	2.89	0.73
b*	0.74	2.71	20.46	48.88	6.33	27.02	0.02	−0.27	0.02
Liquidus	1105				1095		1130
(° C.)

TABLE 27S
	Example
	TM-830	TM-831	TM-832	TM-833	TM-834	TM-835	TM-836	TM-837	TM-838
SiO2	61.419	61.326	61.326	61.326	61.326	61.655	61.655	61.598	61.598
Al2O3	14.700	14.700	14.700	14.700	14.700	14.700	14.700	14.700	14.700
B2O3	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000	6.000
Li2O	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000	9.000
Na2O	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000	2.000
K2O	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.200
MgO	1.500	1.500	1.500	1.500	1.500	1.500	1.500	1.500	1.500
CaO	4.500	4.500	4.500	4.500	4.500	4.500	4.500	4.500	4.500
ZnO
SnO2
Fe2O3
ZrO2
TiO2	0.350	0.419	0.419	0.419	0.419	0.030	0.030	0.003	0.003
CeO2	0.080	0.104	0.104	0.104	0.104	0.010	0.010	0.094	0.094
Er2O3	0.251	0.251	0.251	0.251	0.251	0.405	0.405	0.405	0.405
Nd2O3
NiO
Co3O4
Cr2O3
CuO
Density		2.454				2.461		2.465
(g/cc)
Thickness	2.370	0.551	2.413	0.559	2.371	0.565	2.416	0.549	2.400
(mm)
L*	95.65	96.43	95.60	96.46	95.62	96.31	95.22	96.31	95.17
a*	2.80	0.75	2.84	0.73	2.74	1.23	4.22	1.18	4.18
b*	−0.19	0.09	0.02	0.07	0.15	−0.23	−1.08	−0.15	−0.75
Liquidus		1140				1105		1135
(° C.)

TABLE 27T
	Example
	TM-839	TM-840	TM-841	TM-842	TM-843	TM-844	TM-845	TM-846	TM-847
SiO2	61.581	61.581	61.318	61.318	60.750	60.750	60.692	60.692	60.865
Al2O3	14.700	14.700	14.700	14.700	15.437	15.437	15.420	15.420	15.465
B2O3	6.000	6.000	6.000	6.000	5.979	5.979	5.972	5.972	5.991
Li2O	9.000	9.000	9.000	9.000	9.462	9.462	9.452	9.452	9.471
Na2O	2.000	2.000	2.000	2.000	1.535	1.535	1.540	1.540	1.539
K2O	0.200	0.200	0.200	0.200	0.201	0.201	0.201	0.201	0.198
MgO	1.500	1.500	1.500	1.500	1.988	1.988	1.995	1.995	1.999
CaO	4.500	4.500	4.500	4.500	4.229	4.229	4.232	4.232	4.242
ZnO
SnO2
Fe2O3
ZrO2
TiO2	0.100	0.100	0.372	0.372
CeO2	0.010	0.010	0.001	0.001
Er2O3	0.409	0.409	0.409	0.409	0.420	0.420	0.496	0.496	0.204
Nd2O3
NiO									0.026
Co3O4
Cr2O3
CuO
Density	2.462		2.465
(g/cc)
Thickness	0.541	2.399	0.537	2.405	0.546	2.418	0.527	2.354	0.573
(mm)
L*	96.34	95.16	96.30	95.11	96.24	95.11	96.23	94.80	96.10
a*	1.16	4.24	1.19	4.30	1.17	4.33	1.32	4.79	0.56
b*	−0.20	−1.06	−0.18	−0.95	−0.17	−0.95	−0.13	−0.63	1.43
Liquidus	1125		1125
(° C.)

TABLE 27U
	Example
	TM-848	TM-849	TM-850	TM-851	TM-852	TM-853	TM-854	TM-855	TM-856
SiO2	60.865	60.865	60.865	60.883	60.883	60.478	60.478	60.599	60.599
Al2O3	15.465	15.465	15.465	15.473	15.473	15.366	15.366	15.396	15.396
B2O3	5.991	5.991	5.991	5.986	5.986	5.946	5.946	5.963	5.963
Li2O	9.471	9.471	9.471	9.492	9.492	9.428	9.428	9.446	9.446
Na2O	1.539	1.539	1.539	1.546	1.546	1.533	1.533	1.539	1.539
K2O	0.198	0.198	0.198	0.198	0.198	0.205	0.205	0.203	0.203
MgO	1.999	1.999	1.999	1.995	1.995	1.978	1.978	1.992	1.992
CaO	4.242	4.242	4.242	4.243	4.243	4.218	4.218	4.224	4.224
ZnO
SnO2
Fe2O3
ZrO2
TiO2
CeO2
Er2O3	0.204	0.204	0.204	0.160	0.160	0.828	0.828	0.626	0.626
Nd2O3
NiO	0.026	0.026	0.026	0.024	0.024	0.020	0.020	0.012	0.012
Co3O4
Cr2O3
CuO
Density
(g/cc)
Thickness	2.354	0.541	2.370	0.589	2.415	0.549	2.448	0.550	2.386
(mm)
L*	93.89	96.12	93.98	96.13	94.08	95.61	92.62	95.91	93.67
a*	2.29	0.58	2.24	0.44	1.87	2.13	6.69	1.69	5.60
b*	6.03	1.47	6.13	1.45	5.99	0.65	3.68	0.37	1.87
Liquidus
(° C.)

TABLE 27V
	Example
	TM-857	TM-858	TM-859	TM-860	TM-861	TM-862	TM-863	TM-864	TM-865
SiO2	60.750	60.692	60.865	60.883	60.478	60.599	58.500	58.500	58.500
Al2O3	15.437	15.420	15.465	15.473	15.366	15.396	16.420	16.420	16.420
B2O3	5.979	5.972	5.991	5.986	5.946	5.963	5.970	5.970	5.970
Li2O	9.462	9.452	9.471	9.492	9.428	9.446	11.940	11.940	11.940
Na2O	1.535	1.540	1.539	1.546	1.533	1.539	6.470	6.470	6.470
K2O	0.201	0.201	0.198	0.198	0.205	0.203	0.200	0.200	0.200
MgO	1.988	1.995	1.999	1.995	1.978	1.992
CaO	4.229	4.232	4.242	4.243	4.218	4.224
ZnO
SnO2
Fe2O3
ZrO2
TiO2
CeO2
Er2O3	0.420	0.496	0.204	0.160	0.828	0.626	0.500	0.500	0.500
Nd2O3
NiO			0.026	0.024	0.020	0.012	0.025	0.025	0.025
Co3O4
Cr2O3
CuO
Density
(g/cc)
Thickness	2.384	2.412	2.410	2.403	2.391	2.423	0.540	0.549	2.415
(mm)
L*	95.08	94.81	93.75	93.98	92.61	93.57	95.38	95.68	92.56
a*	4.26	4.89	2.31	1.90	6.58	5.62	1.29	1.30	4.63
b*	−0.95	−0.97	6.25	6.01	3.77	1.94	2.40	1.55	6.03
Liquidus
(° C.)

TABLE 27W
	Example
	TM-866	TM-867	TM-868	TM-869	TM-870	TM-871	TM-872	TM-873	TM-874
SiO2	58.500	58.500	58.500	58.500	58.500	59.180	58.830	59.120	58.950
Al2O3	16.420	16.420	16.420	16.420	16.420	15.950	14.570	15.930	15.900
B2O3	5.970	5.970	5.970	5.970	5.970	5.890	5.970	5.830	6.030
Li2O	11.940	11.940	11.940	11.940	11.940	12.010	12.200	12.100	12.160
Na2O	6.470	6.470	6.470	6.470	6.470	6.270	6.310	6.230	6.220
K2O	0.200	0.200	0.200	0.200	0.200	0.200	0.200	0.190	0.200
MgO						0.020	0.020	0.020	0.020
CaO						0.010	0.010	0.010	0.010
ZnO
SnO2
Fe2O3						0.004	0.005	0.004	0.004
ZrO2
TiO2
CeO2
Er2O3	0.500	0.500	0.500	0.500	0.500	0.450	1.850	0.450	0.450
Nd2O3
NiO	0.025					0.001	0.010	0.086	0.040
Co3O4								0.009	0.003
Cr2O3						0.001	0.003	0.001	0.001
CuO						0.002	0.015	0.002	0.001
Density
(g/cc)
Thickness	2.386	0.567	0.562	2.415	2.427	1.348	1.349	1.350	1.350
(mm)
L*	92.64	96.29	96.29	95.04	95.03	95.76	93.70	91.72	93.92
a*	4.59	1.32	1.31	4.77	4.78	3.04	7.94	3.05	3.00
b*	5.86	−0.23	−0.22	−1.28	−1.28	−0.87	−1.71	10.60	4.49
Liquidus		1100
(° C.)

TABLE 27X
	Example
	TM-875	TM-876	TM-877	TM-878	TM-879	TM-880	TM-881	TM-882	TM-883
SiO2	58.940	59.090	60.890	60.890	61.410	60.940	61.950	60.940	58.670
Al2O3	15.160	15.910	14.880	14.930	15.340	15.430	14.760	15.300	16.520
B2O3	5.960	5.950	5.950	5.620	5.720	5.820	5.610	5.710	5.920
Li2O	12.160	12.020	9.610	9.490	9.440	9.550	9.390	9.490	11.850
Na2O	6.280	6.270	1.510	1.530	1.480	1.480	1.500	1.500	6.240
K2O	0.200	0.200	0.200	0.210	0.200	0.200	0.200	0.200	0.190
MgO	0.020	0.020	2.010	2.040	1.960	2.010	1.920	2.040	0.010
CaO	0.010	0.010	4.300	4.420	4.260	4.340	4.170	4.390	0.020
ZnO									0.040
SnO2
Fe2O3	0.004	0.004	0.006	0.006	0.006	0.006	0.006	0.006	0.005
ZrO2
TiO2
CeO2
Er2O3	1.170	0.460	0.620	0.830	0.160	0.200	0.480	0.420
Nd2O3									0.520
NiO	0.053	0.003	0.012	0.020	0.023	0.025	0.001
Co3O4		0.012	0.002	0.002	0.001	0.001	0.002	0.002
Cr2O3	0.002	0.001
CuO	0.009	0.025
Density
(g/cc)
Thickness	1.336	1.348	2.423	2.391	2.403	2.410	2.412	2.384	1.230
(mm)
L*	93.39	87.55	93.57	92.61	93.98	93.75	94.81	95.08	90.96
a*	5.72	2.01	5.62	6.58	1.90	2.31	4.89	4.26	−2.23
b*	3.16	−11.44	1.94	3.77	6.01	6.25	−0.97	−0.95	−8.98
Liquidus
(° C.)

TABLE 27Y
	Example
	TM-884	TM-885	TM-886	TM-887	TM-888	TM-889	TM-890	TM-891	TM-892
SiO2	58.510	57.810	58.000	57.880	57.740	57.520	57.600	57.570	59.130
Al2O3	16.390	16.210	16.250	16.110	16.080	16.330	16.370	16.070	16.500
B2O3	5.840	5.810	5.600	5.690	5.760	5.830	5.740	5.990	5.890
Li2O	11.760	11.720	11.620	11.740	11.790	11.780	11.760	10.970	11.890
Na2O	6.210	6.110	6.080	6.050	6.040	5.190	4.270	4.230	6.200
K2O	0.190	0.190	0.180	0.190	0.180	0.190	0.190	0.190	0.190
MgO							0.930	1.850	0.010
CaO	0.020	0.020	0.020	0.020	0.020	0.020	0.020	0.020	0.010
ZnO	0.010					1.010	1.030	1.000
SnO2
Fe2O3	0.006	0.009	0.009	0.009	0.009	0.009	0.009	0.009	0.004
ZrO2
TiO2
CeO2
Er2O3
Nd2O3	1.040	2.090	2.110	2.080	2.060	2.100	2.070	2.090	0.160
NiO			0.112	0.214	0.307				0.003
Co3O4									0.001
Cr2O3									0.001
CuO
Density
(g/cc)
Thickness	1.260	1.270	1.290	1.300	1.280	1.310	1.310	1.250	1.361
(mm)
L*	87.17	82.21	79.65	77.99	76.39	81.84	81.50	81.59	94.46
a*	−2.88	−2.53	−3.97	−4.64	−5.20	−2.50	−2.50	−2.62	−0.94
b*	−14.35	−20.64	−10.21	−0.58	6.85	−21.17	−21.72	−21.75	−3.02
Liquidus
(° C.)

	TABLE 27Z
	Example	TM-893	TM-894	TM-895
	SiO2	58.920	58.640	58.970
	Al2O3	16.400	16.470	16.540
	B2O3	5.900	5.960	5.910
	Li2O	12.050	12.050	11.780
	Na2O	6.160	6.200	6.160
	K2O	0.190	0.190	0.190
	MgO	0.010	0.010	0.010
	CaO	0.010	0.010	0.010
	ZnO
	SnO2
	Fe2O3	0.004	0.005	0.005
	ZrO2
	TiO2
	CeO2
	Er2O3
	Nd2O3	0.320	0.410	0.390
	NiO	0.006	0.013	0.004
	Co3O4	0.001	0.002	0.002
	Cr2O3	0.001	0.001	0.001
	CuO	0.011	0.024	0.011
	Density
	(g/cc)
	Thickness	1.373	1.368	1.381
	(mm)
	L*	92.34	91.24	91.58
	a*	−1.73	−2.11	−2.05
	b*	−5.70	−7.32	−7.47
	Liquidus
	(° C.)

Tables 28A-28C show example glass compositions (in terms of mol %) containing gold (Au) as a colorant.

TABLE 28A
	Ex. (mol %)
	SPR-1	SPR-2	SPR-3	SPR-4	SPR-5	SPR-6	SPR-7	SPR-8	SPR-9
SiO2	60.610	60.886	60.779	60.735	60.801	59.984	59.847	60.214	60.910
Al2O3	14.400	14.464	14.443	14.430	14.427	14.765	14.715	14.608	14.544
B2O3	5.896	5.974	5.969	5.829	5.899	6.133	6.082	6.027	5.850
P2O5	0.031	0.027	0.027	0.031	0.031	0.000	0.000	0.000	0.000
Li2O	10.074	9.955	9.947	10.047	10.037	10.424	10.479	10.415	9.760
Na2O	4.254	4.283	4.315	4.259	4.249	4.239	4.235	4.224	4.274
K2O	0.189	0.188	0.190	0.188	0.454	0.197	0.199	0.195	0.204
MgO	2.872	2.881	2.891	2.874	2.890	2.959	2.975	2.917	3.006
CaO	0.034	0.034	0.033	0.034	0.031	0.016	0.017	0.016	0.014
ZnO	0.985	0.999	0.993	0.985	0.994	1.045	1.020	1.012	1.015
TiO2	0.006	0.006	0.006	0.006	0.004	0.007	0.007	0.007	0.006
ZrO2	0.501	0.223	0.300	0.448	0.027	0.000	0.000	0.000	0.000
SnO2	0.071	0.016	0.035	0.054	0.105	0.053	0.052	0.052	0.050
Fe2O3	0.024	0.024	0.024	0.024	0.025	0.146	0.096	0.047	0.048
NiO	0.000	0.000	0.000	0.000	0.000	0.000	0.233	0.229	0.000
Co3O4	0.000	0.000	0.000	0.000	0.000	0.001	0.002	0.002	0.000
HfO2	0.006	0.003	0.006	0.006	0.000	0.000	0.000	0.000	0.000
MnO2	0.019	0.000	0.000	0.021	0.000	0.000	0.000	0.000	0.000
As2O3	0.002	0.001	0.001	0.002	0.001	0.000	0.000	0.000	0.001
Au	0.000000	0.004966	0.004973	0.000000	0.000000	0.001997	0.001770	0.001802	0.000677
SO3	0.000	0.003	0.008	0.000	0.000	0.000	0.010	0.005	0.005
Cl	0.025	0.027	0.029	0.027	0.025	0.029	0.030	0.029	0.314

TABLE 28B
Ex.
(mol %)	SPR-10	SPR-11	SPR-12	SPR-13	SPR-14	SPR-15	SPR-16	SPR-17	SPR-18
SiO2	60.874	61.382	60.006	61.945	62.849	61.812	61.880	61.363	61.235
Al2O3	14.545	14.424	14.896	14.480	14.514	15.558	15.478	15.755	15.656
B2O3	5.794	5.826	5.882	5.946	5.984	5.879	5.985	5.914	5.887
P2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Li2O	8.957	9.890	10.033	10.946	10.972	11.048	10.969	11.170	11.146
Na2O	4.264	4.299	4.326	6.323	5.323	5.337	5.379	5.421	5.382
K2O	0.200	0.193	0.194	0.191	0.196	0.193	0.196	0.194	0.194
MgO	2.941	2.862	3.102	0.016	0.011	0.018	0.016	0.018	0.014
CaO	0.014	0.015	0.016	0.007	0.007	0.006	0.008	0.006	0.006
ZnO	1.990	1.011	1.074	0.000	0.000	0.000	0.000	0.000	0.000
TiO2	0.007	0.007	0.008	0.007	0.006	0.006	0.006	0.006	0.008
ZrO2	0.000	0.000	0.316	0.001	0.000	0.001	0.001	0.001	0.320
SnO2	0.051	0.057	0.052	0.109	0.110	0.108	0.056	0.055	0.054
Fe2O3	0.048	0.004	0.068	0.003	0.004	0.003	0.004	0.069	0.069
NiO	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Co3O4	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.003
MnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
As2O3	0.001	0.001	0.001	0.000	0.001	0.001	0.001	0.000	0.001
Au	0.000488	0.000357	0.000000	0.001297	0.000261	0.001960	0.000000	0.000327	0.000655
SO3	0.000	0.009	0.000	0.000	0.000	0.002	0.000	0.007	0.003
Cl	0.312	0.020	0.025	0.025	0.022	0.025	0.022	0.022	0.020

TABLE 28C
Ex.
(mol %)	SPR-19	SPR-20	SPR-21	SPR-22
SiO2	60.872	60.616	62.173	61.281
Al2O3	16.544	16.474	14.974	14.343
B2O3	5.853	5.964	5.722	5.820
P2O5	0.000	0.000	0.000	0.018
Li2O	11.078	10.927	9.237	6.759
Na2O	5.336	5.358	2.332	7.465
K2O	0.193	0.195	0.182	0.589
MgO	0.019	0.016	2.433	2.027
CaO	0.007	0.008	1.555	0.542
ZnO	0.000	0.000	0.976	0.973
TiO2	0.007	0.007	0.010	0.006
ZrO2	0.001	0.309	0.302	0.000
SnO2	0.055	0.054	0.042	0.104
Fe2O3	0.003	0.047	0.043	0.044
NiO	0.000	0.000	0.000	0.000
Co3O4	0.000	0.000	0.000	0.000
HfO2	0.000	0.000	0.000	0.000
MnO2	0.000	0.000	0.000	0.000
As2O3	0.000	0.001	0.000	0.000
Au	0.000987	0.000157	0.000563	0.002166
SO3	0.006	0.002	0.006	0.005
Cl	0.024	0.022	0.011	0.020

Referring now to Table 29, colored glass articles in the form of glass coupons were produced from the glass compositions of Tables 28A-28C. The glass coupons had the indicated thicknesses and were heat treated at various times and temperatures (as indicated) to produce colored glass articles with different color hues. The CIELAB L*, a*, and b* coordinates of each colored glass article were determined. The average transmittance (%) for each sample over the wavelength range from 380 nm to 750 nm was also determined. The results are reported in Table 29.

TABLE 29
							Average
	Thickness	Temp	Time				transmittance
Example	(mm)	(° C.)	(Hr.)	L*	a*	b*	(380 nm-750 nm)
SPR-1	1.32	620	10	80.8	15	10.88	62.083
SPR-2	1.31	632	0.25	69.7	1.33	−15.5	53.986
SPR-2	1.35	545	2	88	8.84	−1.45	77.737
SPR-2	1.36	553	1.5	88.9	7.79	−1.3	79.081
SPR-2	1.36	630	6	77.1	19.7	2.28	61.052
SPR-2	1.42	603	1.5	69.1	9.07	−12.3	54.353
SPR-2	1.39	632	0.5	69.7	6.74	−12.2	54.045
SPR-2	1.29	705	0.25	73.7	20	−5.76	60.047
SPR-2	1.35	655	1.5	75.2	20.5	−1.62	60.186
SPR-2	1.38	630	6	76.9	20.1	2.43	60.776
SPR-2	1.34	545	1	88.3	8.75	−1.28	78.270
SPR-2	1.36	553	2	89.2	7.76	−1.14	79.523
SPR-2	1.36	630	1.5	77.2	20	2.26	61.288
SPR-2	1.4	632	6	69.5	7.02	−12.4	54.092
SPR-2	1.43	603	0.5	69	9.22	−12.6	54.475
SPR-2	1.32	632	0.25	69.4	1.26	−15.9	53.842
SPR-2	1.29	705	0.25	73.9	20	−5.92	60.530
SPR-2	1.35	655	1.5	75.2	20.6	1.95	60.438
SPR-2	1.37	630	6	77	20.2	2.07	61.092
SPR-2	1.29	560	0.25	91.9	4.36	−0.78	83.484
SPR-2	1.29	580	0.25	92	4.2	−0.87	83.677
SPR-2	1.22	600	0.25	76.4	8.13	−12.5	65.670
SPR-2	1.22	560	0.50	91.4	5	−0.94	82.705
SPR-2	1.21	580	0.50	75.5	11.5	−12.3	64.875
SPR-2	1.2	600	0.50	70.9	2.8	−15.7	57.149
SPR-2	1.26	560	0.75	87.3	9	−2.33	77.093
SPR-2	1.28	580	0.75	70.3	10.9	−14.8	58.437
SPR-2	1.3	600	0.75	70.3	4.83	−13.4	55.255
SPR-2	1.27	560	2	75.2	15.9	4.84	61.011
SPR-2	1.47	620	0.25	66.7	−1.17	−19	51.231
SPR-2	1.45	630	0.25	66.6	−1.27	−18.7	50.691
SPR-2	1.45	640	0.25	66.3	−0.3	−18.2	50.110
SPR-2	1.48	650	0.25	66.3	1.82	16.9	49.961
SPR-2	1.48	660	0.25	67.4	4.84	−14.3	51.179
SPR-2	1.49	670	0.25	67.9	6.81	−13	51.865
SPR-2	1.33	680	0.25	70.7	8.42	−11.5	55.644
SPR-2	1.3	690	0.25	72.3	13.3	−9.69	58.346
SPR-2	1.3	700	0.25	72.7	14.9	−8.33	58.842
SPR-2	1.32	710	0.25	74.9	18	−3.59	60.103
SPR-2	1.29	620	0.50	70.7	4.6	12.7	55.193
SPR-2	1.31	640	0.50	70.7	10.4	−11.8	56.589
SPR-2	0.9	660	0.50	81.5	13.6	−2.27	68.459
SPR-2	0.87	680	0.50	83	14.2	0	69.595
SPR-2	0.86	700	0.50	83.3	13.9	0.36	69.916
SPR-2	0.81	620	0.75	79.8	5.56	−7.92	67.047
SPR-2	0.69	640	0.75	83.7	9.69	−3.81	72.165
SPR-2	0.72	660	0.75	85.4	11.4	−0.42	73.325
SPR-2	1.28	680	0.75	78.3	17.9	0.24	62.902
SPR-2	1.29	700	0.75	78.4	17.6	0.44	62.728
SPR-2	1.29	620	2.00	75.3	17.7	−3.72	60.833
SPR-2	1.42	580	2	89.9	5.08	1.36	80.246
SPR-2	1.3	600	2	70.6	11.1	−12	56.982
SPR-2	1.34	640	2	76.3	20.2	0.48	60.676
SPR-2	1.35	660	2	76.6	19.3	0.15	60.827
SPR-2	1.18	680	2	79.4	17.7	1.36	64.066
SPR-2	1.35	550	1	85.4	11.2	2.58	74.328
SPR-2	1.34	550	1.25	80	16.2	4.65	67.893
SPR-2	1.27	540	1.25	92.1	4.47	−0.39	83.614
SPR-2	1.27	710	2.5	78.8	19.2	3.29	62.662
SPR-2	1.34	625	1.25	72.1	15.3	8.48	58.196
SPR-2	1.39	540	1.5	87	9.82	−1.71	76.314
SPR-2	1.35	590	0.917	70.8	8.23	−10.7	55.681
SPR-2	1.34	555	1	92.7	4.09	0.34	84.664
SPR-2	1.335	635	1	70	11.7	−12.7	56.278
SPR-2	1.365	595	1	70.9	9.62	−10.6	56.159
SPR-2	1.279	615	1	70.9	6.71	−12.2	55.936
SPR-2	1.331	580	0.5	68.7	3.09	−17.4	55.139
SPR-2	0.641	525	2	94.3	2.41	−0.16	87.417
SPR-2	2.077	525	2	89	7.39	0.62	78.548
SPR-2	0.64	545	2	94.5	2.23	−0.11	87.779
SPR-2	2.06	545	2	89.7	6.76	−0.51	79.648
SPR-3	1.3	630	6	77.6	18.6	1.33	61.990
SPR-3	1.31	575	1	74	16.2	−7.99	61.103
SPR-3	1.29	632	0.5	72.7	7.67	−9.49	57.240
SPR-3	1.25	603	1.5	73.2	8.79	−9.7	58.809
SPR-3	1.26	655	1.5	77.1	18.5	−0.67	62.079
SPR-3	1.37	575	1	73.3	17.7	−8.38	60.550
SPR-3	1.33	635	1	72.5	13.9	−8.58	58.373
SPR-3	1.37	615	1	70.7	8.26	−11.1	55.575
SPR-3	1.34	595	1	72.6	9.35	−8.15	57.204
SPR-3	1.27	555	1	93.2	3.16	−0.23	85.431
SPR-3	1.367	575	1	73	17.5	−8.56	60.095
SPR-3	1.33	635	1	72.7	14.9	−7.76	58.572
SPR-3	1.336	595	1	72.6	9.13	−8.28	57.195
SPR-3	1.242	603	1.5	73.1	8.86	−9.73	58.626
SPR-3	1.293	632	0.5	72.7	7.74	−9.49	57.192
SPR-3	1.356	615	1	70.8	8.14	−11.1	55.630
SPR-3	0.565	632	0.5	85.6	4.05	−4.57	74.432
SPR-3	1.512	632	0.5	69.3	8.38	−10.7	53.145
SPR-4	1.33	580	0.25	91.1	4.08	−1.11	82.311
SPR-4	1.34	600	0.25	73.9	9.69	−11.7	61.448
SPR-4	1.32	560	0.50	91.9	3.7	0.66	83.379
SPR-4	1.34	580	0.50	73.1	12.9	−10.7	60.597
SPR-4	1.23	600	0.50	73.6	3.67	−11.4	58.393
SPR-4	1.23	560	0.75	88.4	6.93	−1.86	78.551
SPR-4	1.24	580	0.75	74.3	9.95	−8.94	60.566
SPR-4	1.23	600	0.75	74.4	5.31	−8.99	58.880
SPR-4	1.3	560	2.00	77.7	13.3	−0.84	62.143
SPR-4	1.3	580	2.00	74.4	10.8	−6.76	59.556
SPR-4	1.32	600	2.00	74.7	13.4	−5.8	60.238
SPR-4	1.28	560	0.25	72.4	10.6	−9.29	57.846
SPR-4	1.28	620	2	78.8	17.2	1.61	63.224
SPR-4	1.32	640	2	78.8	17.6	4.07	62.054
SPR-4	1.32	660	2	78.7	17.7	3.8	62.119
SPR-4	1.2	680	2	80.6	16.3	4.42	64.227
SPR-4	1.342	660	6	76.9	18.6	1.38	60.789
SPR-4	1.389	600	1	72.8	9.91	−6.88	56.945
SPR-4	1.285	600	10	79.1	17.3	3.94	62.620
SPR-4	1.289	620	10	78.7	17.7	3.31	62.257
SPR-4	1.295	640	10	78.3	17.9	2.64	62.079
SPR-4	1.308	660	2	77.6	18.3	1.83	61.500
SPR-4	0.528	710	2.5	89.7	7.57	2.52	78.250
SPR-4	2.043	710	2.5	73.1	22.9	9.92	53.254
SPR-5	1.348	660	6	83.1	9.17	10.21	64.324
SPR-5	1.32	600	10	82.4	9.71	9.07	63.785
SPR-5	1.293	620	10	82.8	9.49	8.88	64.444
SPR-5	1.35	640	10	82.6	9.48	9.53	63.931
SPR-5	1.315	660	2	82.8	9.65	9.27	64.280
SPR-6	1.31	600	1	64.6	24.8	−4.62	48.155
SPR-7	1.36	600	1	64.1	23.1	23.31	44.240
SPR-8	1.27	600	1	69.2	13.3	34.5	45.285
SPR-9	1.33	600	1	87.3	10.2	−3.02	77.166
SPR-10	1.303	600	1	88.1	6.56	−4.17	78.834
SPR-11	1.302	625	2	81.4	15.7	6.6	65.169
SPR-12	1.307	600	2	84.2	12.7	1.32	69.833
SPR-13	1.306	625	2	89.3	5.14	9.97	74.122
SPR-14	1.291	575	2	87.4	9.35	8.2	72.514
SPR-14	1.321	625	2	87.6	7.22	10.51	71.412
SPR-14	0.502	625	2	92.7	3.39	4.56	82.163
SPR-14	1.304	625	2	85.3	9.75	11.19	67.746
SPR-14	2.015	625	2	82.9	10.7	15.3	62.880
SPR-14	0.612	625	2	92.1	3.93	12.8	78.141
SPR-14	2.063	625	2	85.8	8.06	34.2	62.357
SPR-15	1.298	625	2	83	11.4	2.59	68.255
SPR-16	1.327	625	2	86.7	9.76	2.6	73.863
SPR-16	0.6	625	2	90	6.98	1.73	79.393
SPR-16	1.97	625	2	79.4	13.9	1.64	63.678
SPR-16	0.62	625	2	90.3	6.77	1.82	79.780
SPR-16	2.039	625	2	80.4	15.3	3.72	64.446
SPR-16	0.623	625	2	91.5	6.22	7.06	79.380
SPR-16	2.089	625	2	81.6	17.2	20.79	60.538
SPR-17	1.325	625	2	88.9	6.92	4.75	75.258
SPR-18	1.318	625	2	87.3	9.09	3.44	73.391
SPR-19	1.308	625	2	78	5.04	−9.39	63.809
SPR-20	1.332	625	2	80.5	6.25	−8.92	68.187
SPR-20	0.632	625	2	87.7	2.61	−5.06	77.726
SPR-20	1.353	625	2	79	5.44	−9.99	65.901
SPR-20	0.632	625	2	69	8.35	−14.9	53.661
SPR-20	0.622	625	2	88.1	1.98	−5.62	78.812
SPR-20	2.058	625	2	68	6.29	−18	53.414
SPR-14	1.291	575	2	87.4	9.35	8.2	72.514
SPR-14	1.321	625	2	87.6	7.22	10.51	71.412
SPR-14	0.502	625	2	92.7	3.39	4.56	82.163
SPR-14	1.304	625	2	85.3	9.75	11.19	67.746
SPR-14	2.015	625	2	82.9	10.7	15.3	62.880
SPR-14	0.612	625	2	92.1	3.93	12.8	78.141
SPR-14	2.063	625	2	85.8	8.06	34.2	62.357
SPR-14	1.291	575	2	87.4	9.35	8.2	72.514
SPR-14	1.321	625	2	87.6	7.22	10.51	71.412
SPR-14	0.502	625	2	92.7	3.39	4.56	82.163
SPR-14	1.304	625	2	85.3	9.75	11.19	67.746
SPR-14	2.015	625	2	82.9	10.7	15.3	62.880
SPR-14	0.612	625	2	92.1	3.93	12.8	78.141
SPR-14	2.063	625	2	85.8	8.06	34.2	62.357
SPR-16	1.327	625	2	86.7	9.76	2.6	73.863
SPR-16	0.6	625	2	90	6.98	1.73	79.393
SPR-16	1.97	625	2	79.4	13.9	1.64	63.678
SPR-16	0.62	625	2	90.3	6.77	1.82	79.780
SPR-16	2.039	625	2	80.4	15.3	3.72	64.446
SPR-16	0.623	625	2	91.5	6.22	7.06	79.380
SPR-16	2.089	625	2	81.6	17.2	20.79	60.538
SPR-20	1.332	625	2	80.5	6.25	−8.92	68.187
SPR-20	0.632	625	2	87.7	2.61	−5.06	77.726
SPR-20	1.353	625	2	79	5.44	−9.99	65.901
SPR-20	0.632	625	2	69	8.35	−14.9	53.661
SPR-20	0.622	625	2	88.1	1.98	−5.62	78.812
SPR-20	2.058	625	2	68	6.29	−18	53.414
SPR-16	1.327	625	2	86.7	9.76	2.6	73.863
SPR-16	0.6	625	2	90	6.98	1.73	79.393
SPR-16	1.97	625	2	79.4	13.9	1.64	63.678
SPR-16	0.62	625	2	90.3	6.77	1.82	79.780
SPR-16	2.039	625	2	80.4	15.3	3.72	64.446
SPR-16	0.623	625	2	91.5	6.22	7.06	79.380
SPR-16	2.089	625	2	81.6	17.2	20.79	60.538
SPR-20	1.332	625	2	80.5	6.25	−8.92	68.187
SPR-20	0.632	625	2	87.7	2.61	−5.06	77.726
SPR-20	1.353	625	2	79	5.44	−9.99	65.901
SPR-20	0.632	625	2	69	8.35	−14.9	53.661
SPR-20	0.622	625	2	88.1	1.98	−5.62	78.812
SPR-20	2.058	625	2	68	6.29	−18	53.414
SPR-21	1.381	620	8	84.2	−3.45	−7.17	70.463
SPR-22	3.069	640	8	72.6	16.9	68.63	40.945
SPR-22	3.085	660	8	71.9	17.5	66.16	40.588
SPR-22	3.1	680	8	71	17.9	65.27	39.780
SPR-22	3.15	700	8	72.3	17.5	64.89	41.003
SPR-22	3.4	620	2	72	18.4	67.51	40.834
SPR-22	3.07	640	2	71	18.5	66.03	40.098

Tables 30A-30NN show example glass compositions (in terms of mol %) containing transition metal oxides and/or rare earth oxides as colorants.

TABLE 30A
Ex.
(mol %)	ORA-1	ORA-2	ORA-3	ORA-4	ORA-5	ORA-6	ORA-6	ORA-7	ORA-8
SiO2	60.93	61.53	58.99	57.22	57.78	58.75	58.75	59.03	58.53
Al2O3	16.20	15.91	16.99	18.71	17.54	16.67	16.67	16.52	16.50
B2O3	5.66	5.59	6.15	5.68	5.96	5.92	5.92	5.86	5.58
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	10.49	10.61	11.02	10.75	10.92	11.78	11.78	11.65	11.55
Na2O	1.67	1.68	1.74	1.71	1.68	6.26	6.26	6.22	6.17
K2O	0.30	0.30	0.30	0.29	0.29	0.48	0.48	0.48	0.47
MgO	3.78	3.65	3.98	4.67	4.31	0.02	0.02	0.02	0.02
CaO	0.52	0.50	0.55	0.61	0.57	0.01	0.01	0.01	0.01
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.01	0.00
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.005	0.005	0.005	0.006	0.005	0.004	0.004	0.004	0.004
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.127	0.042	0.153	0.243	0.206	0.000	0.000	0.177	0.000
Co3O4	0.055	0.068	0.025	0.049	0.001	0.000	0.000	0.001	0.001
Cr2O3	0.000	0.000	0.000	0.000	0.000	0.098	0.098	0.000	0.000
CuO	0.247	0.104	0.088	0.034	0.724	0.000	0.000	0.000	1.151
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
As2O3	0.001	0.000	0.001	0.001	0.001	0.001	0.001	0.001	0.001
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.000	0.002	0.002	0.000	0.000	0.002	0.000
Cl	0.007	0.007	0.009	0.007	0.007	0.011	0.011	0.011	0.011
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30B
Ex
(mol %)	ORA-9	ORA-10	ORA-11	ORA-11	ORA-12	ORA-14	ORA-15	ORA-16
SiO2	58.95	60.10	57.65	57.65	56.77	58.04	59.63	57.80
Al2O3	16.55	15.85	16.16	16.16	16.65	17.65	16.71	17.65
B2O3	5.97	5.74	5.95	5.95	5.90	6.20	6.16	5.87
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	11.70	9.81	11.61	11.61	9.84	11.04	10.94	10.85
Na2O	6.22	4.23	6.10	6.10	4.24	1.68	1.67	1.69
K2O	0.48	0.47	0.47	0.47	0.48	0.29	0.29	0.29
MgO	0.02	2.69	0.02	0.02	2.98	4.34	3.95	4.35
CaO	0.01	0.02	0.01	0.01	0.02	0.57	0.54	0.58
ZnO	0.02	0.96	0.00	0.00	1.04	0.00	0.00	0.00
TiO2	0.01	0.01	1.91	1.91	1.95	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.004	0.005	0.004	0.004	0.004	0.006	0.005	0.005
CeO2	0.000	0.000	0.100	0.100	0.102	0.000	0.000	0.000
NiO	0.000	0.000	0.000	0.000	0.000	0.000	0.058	0.048
Co3O4	0.046	0.001	0.001	0.001	0.001	0.001	0.011	0.013
Cr2O3	0.000	0.098	0.000	0.000	0.000	0.000	0.000	0.000
CuO	0.000	0.010	0.000	0.000	0.000	0.155	0.020	0.845
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
As2O3	0.001	0.001	0.001	0.001	0.000	0.001	0.001	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.000	0.000	0.015	0.009	0.002	0.000
Cl	0.011	0.007	0.011	0.011	0.011	0.007	0.007	0.007
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30C
Ex.
(mol %)	ORA-17	ORA-18	ORA-21	ORA-22	ORA-23	ORA-24	ORA-25
SiO2	56.37	58.62	58.27	58.49	58.94	58.49	57.45
Al2O3	18.99	17.25	16.34	16.49	16.40	16.55	18.22
B2O3	6.02	5.97	5.92	6.01	5.98	6.04	5.91
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	11.02	10.73	9.89	9.97	9.93	9.93	10.77
Na2O	1.69	1.68	4.25	4.26	4.26	4.30	1.69
K2O	0.28	0.29	0.48	0.48	0.49	0.49	0.29
MgO	4.81	4.17	2.91	2.95	2.90	2.93	4.45
CaO	0.61	0.59	0.01	0.01	0.01	0.02	0.60
ZnO	0.00	0.00	1.00	1.01	1.00	1.05	0.00
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.006	0.005	0.004	0.005	0.005	0.005	0.006
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.141	0.108	0.000	0.023	0.012	0.089	0.053
CO3O4	0.029	0.001	0.001	0.002	0.002	0.048	0.013
Cr2O3	0.000	0.000	0.068	0.038	0.002	0.008	0.000
CuO	0.006	0.576	0.829	0.233	0.037	0.044	0.525
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000
As2O3	0.001	0.001	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.001	0.006	0.003	0.000	0.000
Cl	0.007	0.009	0.011	0.011	0.011	0.009	0.005
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30D
Ex.
(mol %)	ORA-26	ORA-27	ORA-28	ORA-29	ORA-30	ORA-31	ORA-32	ORA-33	ORA-34
SiO2	57.72	57.57	57.20	56.72	56.18	59.18	58.40	58.81	58.08
Al2O3	17.62	17.48	17.51	17.36	17.14	16.63	16.20	16.54	16.54
B2O3	6.01	5.97	5.91	5.90	5.81	5.62	5.70	5.76	6.07
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	10.85	10.80	10.79	10.68	10.55	11.79	11.60	11.86	11.87
Na2O	1.67	1.67	1.67	1.68	1.65	6.18	6.09	6.17	6.20
K2O	0.29	0.29	0.29	0.28	0.28	0.46	0.47	0.47	0.48
MgO	4.25	4.22	4.23	4.19	4.15	0.02	0.02	0.02	0.02
CaO	0.58	0.58	0.58	0.58	0.56	0.01	0.01	0.01	0.01
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.00	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.006	0.006	0.006	0.006	0.006	0.004	0.003	0.004	0.004
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.057	0.057	0.053	0.052	0.052	0.077	0.039	0.127	0.071
Co3O4	0.012	0.012	0.012	0.011	0.012	0.001	0.001	0.032	0.002
Cr2O3	0.000	0.000	0.000	0.000	0.000	0.009	0.101	0.000	0.051
CuO	0.905	1.330	1.735	2.536	3.586	0.002	1.350	0.176	0.563
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.000	0.000	0.000	0.000	0.005	0.004	0.006	0.004
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.005	0.004	0.006	0.000	0.000	0.001	0.011	0.000	0.000
Cl	0.005	0.005	0.004	0.005	0.004	0.009	0.009	0.013	0.015
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30E
Ex.
(mol %)	ORA-35	ORA-36	ORA-37	ORA-38	ORA-39	ORA-40	ORA-41	ORA-42	ORA-43
SiO2	59.17	58.32	58.74	57.99	57.84	58.16	58.35	58.45	58.41
Al2O3	16.57	16.10	16.54	16.56	17.76	17.85	16.48	16.52	16.48
B2O3	5.67	5.69	5.75	6.03	6.08	6.00	6.00	6.09	6.04
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	11.86	11.64	11.91	11.97	11.03	10.89	10.06	10.12	10.07
Na2O	6.16	6.07	6.13	6.22	1.69	1.69	4.28	4.26	4.25
K2O	0.45	0.46	0.46	0.48	0.29	0.29	0.48	0.49	0.48
MgO	0.02	0.02	0.02	0.02	4.35	4.37	2.94	2.94	2.93
CaO	0.01	0.01	0.01	0.01	0.58	0.58	0.02	0.01	0.02
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	1.01	1.01	1.01
TiO2	0.01	0.00	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.004	0.003	0.004	0.004	0.005	0.005	0.004	0.004	0.004
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.000	0.000	0.242	0.093	0.252	0.051	0.021	0.000	0.082
Co3O4	0.002	0.038	0.068	0.072	0.053	0.001	0.002	0.002	0.048
Cr2O3	0.002	0.051	0.000	0.012	0.001	0.001	0.036	0.001	0.006
CuO	0.086	1.582	0.092	0.515	0.022	0.066	0.278	0.091	0.137
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.006	0.005	0.004	0.007	0.006	0.005	0.004	0.005	0.004
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.003	0.000	0.010	0.012	0.002	0.005	0.014
Cl	0.009	0.007	0.013	0.015	0.009	0.009	0.013	0.013	0.013
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30F
Ex.
(mol %)	ORA-44	ORA-45	ORA-46	ORA-47	ORA-48	ORA-49	ORA-50	ORA-51	ORA-52
SiO2	58.30	58.71	58.54	58.67	58.47	58.47	58.61	58.63	57.36
Al2O3	16.45	16.46	16.41	16.53	16.48	16.43	16.48	16.55	17.09
B2O3	6.08	5.98	5.96	5.99	6.05	6.03	6.04	6.10	6.18
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	10.10	10.05	10.53	10.51	10.50	10.52	10.53	9.94	10.16
Na2O	4.26	4.24	4.71	4.75	4.76	4.74	4.76	4.29	4.32
K2O	0.48	0.48	0.48	0.49	0.49	0.48	0.49	0.29	0.49
MgO	2.91	2.93	0.96	0.97	0.97	0.98	0.97	2.93	3.12
CaO	0.02	0.02	0.98	0.98	0.99	0.99	0.99	0.02	0.02
ZnO	1.00	1.01	0.99	1.02	1.01	1.01	1.01	1.02	1.08
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.004	0.004	0.005	0.005	0.005	0.005	0.005	0.004	0.004
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.250	0.053	0.019	0.000	0.085	0.250	0.053	0.086	0.025
Co3O4	0.053	0.001	0.002	0.002	0.048	0.053	0.001	0.049	0.010
Cr2O3	0.001	0.000	0.039	0.001	0.005	0.000	0.000	0.005	0.001
CuO	0.058	0.036	0.339	0.054	0.111	0.010	0.036	0.060	0.103
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.006	0.005	0.005	0.004	0.006	0.005	0.004	0.003	0.000
As2O3	0.000	0.001	0.001	0.001	0.001	0.001	0.001	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.001	0.002	0.006	0.002	0.007	0.000	0.009	0.000	0.005
Cl	0.013	0.011	0.011	0.015	0.013	0.013	0.013	0.013	0.013
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30G
Ex.
(mol %)	ORA-53	ORA-54	ORA-56	ORA-57	ORA-58	ORA-59	ORA-60	ORA-61	ORA-62
SiO2	57.87	58.57	58.46	58.81	57.89	59.54	59.30	54.94	61.12
Al2O3	17.10	16.44	16.41	16.50	16.88	16.00	16.52	18.22	15.01
B2O3	5.76	5.80	5.84	5.78	5.98	6.02	5.63	6.53	5.46
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	9.89	9.90	9.84	9.82	10.00	10.04	9.71	10.84	9.12
Na2O	4.33	4.22	4.21	4.22	4.30	4.23	4.27	4.68	3.84
K2O	0.49	0.47	0.47	0.47	0.49	0.29	0.29	0.31	0.26
MgO	3.08	2.90	2.91	2.93	3.05	2.75	2.86	3.21	2.66
CaO	0.02	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZnO	1.06	0.99	0.99	1.03	1.06	0.95	1.00	1.10	0.90
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.004	0.004	0.004	0.004	0.004	0.004	0.004	0.004	0.004
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.084	0.048	0.049	0.037	0.097	0.023	0.090	0.049	0.050
Co3O4	0.048	0.002	0.035	0.016	0.053	0.010	0.046	0.002	0.032
Cr2O3	0.001	0.001	0.001	0.001	0.001	0.000	0.000	0.000	0.000
CuO	0.241	0.633	0.735	0.336	0.172	0.114	0.245	0.084	1.500
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.003	0.007	0.000	0.002	0.005	0.000	0.002
Cl	0.013	0.007	0.009	0.013	0.013	0.011	0.011	0.011	0.011
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30H
Ex
(mol %)	ORA-63	ORA-64	ORA-65	ORA-66	ORA-67	ORA-68	ORA-69	ORA-70	ORA-71
SiO2	56.53	55.78	58.58	58.56	57.21	57.93	58.24	57.46	58.16
Al2O3	17.59	17.97	16.59	16.88	16.96	17.01	16.43	16.92	16.96
B2O3	6.17	6.34	5.92	5.97	6.16	5.96	6.05	6.19	5.86
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	10.10	10.32	9.82	9.88	9.97	9.92	9.84	10.02	9.82
Na2O	4.35	4.34	4.27	4.29	4.30	4.31	4.24	4.32	4.35
K2O	0.29	0.29	0.48	0.29	0.29	0.29	0.29	0.29	0.30
MgO	3.25	3.42	2.94	2.98	3.04	3.03	2.93	3.02	3.02
CaO	0.02	0.02	0.02	0.02	0.02	0.02	0.02	0.02	0.02
ZnO	1.07	1.11	1.02	1.03	1.05	1.06	1.02	1.04	1.05
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.004	0.005	0.005	0.004	0.005	0.004	0.004	0.004	0.004
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.037	0.112	0.034	0.063	0.476	0.000	0.063	0.057	0.232
Co3O4	0.017	0.057	0.002	0.002	0.018	0.005	0.033	0.039	0.057
Cr2O3	0.000	0.000	0.030	0.000	0.000	0.000	0.000	0.000	0.000
CuO	0.548	0.232	0.260	0.008	0.487	0.444	0.824	0.595	0.145
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.000	0.003	0.001	0.000	0.002	0.001	0.003	0.002
As2O3	0.000	0.000	0.001	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.006	0.000	0.012	0.000	0.006	0.000	0.000	0.000	0.005
Cl	0.013	0.013	0.011	0.011	0.011	0.009	0.009	0.011	0.013
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30I
Ex
(mol %)	ORA-72	ORA-73	ORA-74	ORA-75	ORA-76	ORA-77	ORA-78	ORA-79	ORA-80
SiO2	57.12	59.37	58.01	55.88	59.19	55.91	57.08	59.16	59.23
Al2O3	17.20	16.56	16.75	17.76	16.28	17.42	17.50	16.52	16.54
B2O3	6.36	5.79	6.24	6.48	5.92	5.76	6.14	5.82	5.86
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	10.08	9.75	10.06	10.29	9.77	9.68	9.98	11.85	11.83
Na2O	4.35	4.27	4.31	4.36	4.24	4.26	4.37	6.18	6.21
K2O	0.29	0.29	0.29	0.29	0.29	0.29	0.29	0.19	0.20
MgO	3.11	2.90	2.90	3.39	2.79	3.37	3.20	0.02	0.02
CaO	0.02	0.02	0.02	0.02	0.02	0.02	0.02	0.01	0.01
ZnO	1.06	1.02	1.02	1.17	1.00	1.25	1.13	0.00	0.00
TiO2	0.01	0.01	0.01	0.01	0.49	2.04	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.005	0.004	0.004	0.005	0.004	0.005	0.004	0.004	0.004
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.106	0.015	0.291	0.200	0.000	0.000	0.000	0.083	0.000
Co3O4	0.047	0.001	0.057	0.050	0.001	0.001	0.054	0.048	0.001
Cr2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.005	0.000
CuO	0.238	0.000	0.013	0.077	0.000	0.000	0.215	0.093	0.061
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.002	0.000	0.004	0.002	0.000	0.001	0.001	0.003	0.005
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.000	0.000	0.000	0.000	0.003	0.000	0.005
Cl	0.011	0.009	0.013	0.011	0.009	0.009	0.011	0.011	0.015
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30J
Ex
(mol %)	ORA-81	ORA-82	ORA-83	ORA-84	ORA-85	ORA-86	ORA-87	ORA-88	ORA-89
SiO2	59.07	59.29	59.35	59.18	59.52	59.10	58.23	58.92	58.45
Al2O3	16.48	16.51	16.56	16.41	16.38	16.53	16.16	16.40	16.34
B2O3	5.81	5.83	5.82	6.00	5.84	5.96	5.74	6.02	6.02
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	11.88	11.80	11.84	11.95	11.82	11.88	11.68	11.83	11.82
Na2O	6.19	6.18	6.19	6.18	6.17	6.19	6.05	6.20	6.19
K2O	0.19	0.19	0.19	0.19	0.19	0.19	0.19	0.19	0.19
MgO	0.02	0.02	0.02	0.02	0.02	0.02	0.02	0.02	0.02
CaO	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	1.91	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.004	0.004	0.004	0.036	0.025	0.003	0.004	0.004	0.058
CeO2	0.000	0.000	0.001	0.001	0.003	0.099	0.002	0.000	0.000
NiO	0.249	0.026	0.000	0.000	0.000	0.000	0.000	0.000	0.057
Co3O4	0.053	0.010	0.001	0.001	0.001	0.001	0.001	0.015	0.035
Cr2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
CuO	0.009	0.106	0.000	0.000	0.000	0.000	0.000	0.370	0.791
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.004	0.005	0.001	0.000	0.001	0.000	0.001	0.001	0.004
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.001	0.001
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Cl	0.011	0.011	0.007	0.009	0.007	0.011	0.007	0.011	0.013
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30K
Ex.
(mol %)	ORA-90	ORA-91	ORA-92	ORA-93	ORA-94	ORA-95	ORA-96	ORA-97	ORA-98
SiO2	58.93	58.59	58.63	58.78	58.92	58.98	58.92	59.17	58.67
Al2O3	16.35	16.35	16.56	16.41	16.34	16.42	16.52	16.45	16.52
B2O3	5.98	6.07	6.13	6.10	5.99	6.04	6.01	5.97	5.92
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	11.84	11.80	11.87	11.82	11.77	11.87	11.87	11.88	11.85
Na2O	6.20	6.21	6.24	6.21	6.18	6.22	6.24	6.21	6.24
K2O	0.20	0.20	0.20	0.20	0.19	0.20	0.19	0.19	0.19
MgO	0.02	0.02	0.02	0.02	0.02	0.02	0.02	0.02	0.01
CaO	0.00	0.01	0.00	0.01	0.00	0.00	0.00	0.00	0.02
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.04
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.003	0.003	0.003	0.003	0.003	0.003	0.003	0.003	0.005
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.000	0.061	0.006	0.013	0.014	0.011	0.014	0.018	0.000
Co3O4	0.031	0.034	0.035	0.035	0.034	0.002	0.001	0.000	0.000
Cr2O3	0.016	0.000	0.048	0.029	0.015	0.055	0.037	0.047	0.000
CuO	0.411	0.628	0.229	0.364	0.504	0.147	0.142	0.015	0.000
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.007	0.004	0.004	0.004	0.003	0.004	0.004	0.005	0.000
As2O3	0.001	0.001	0.001	0.001	0.001	0.001	0.001	0.001	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.001	0.000	0.000	0.000	0.005	0.002	0.000	0.006	0.000
Cl	0.011	0.013	0.013	0.015	0.011	0.013	0.013	0.013	0.015
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.517
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30L
Ex.		ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	ORA-99	100	101	102	103	104	105	106	107
SiO2	58.51	57.81	58.00	57.88	57.74	57.52	57.60	57.57	58.73
Al2O3	16.39	16.21	16.25	16.11	16.08	16.33	16.37	16.07	16.47
B2O3	5.84	5.81	5.60	5.69	5.76	5.83	5.74	5.99	6.09
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	11.76	11.72	11.62	11.74	11.79	11.78	11.76	10.97	11.98
Na2O	6.21	6.11	6.08	6.05	6.04	5.19	4.27	4.23	6.24
K2O	0.19	0.19	0.18	0.19	0.18	0.19	0.19	0.19	0.19
MgO	0.00	0.00	0.00	0.00	0.00	0.00	0.93	1.85	0.02
CaO	0.02	0.02	0.02	0.02	0.02	0.02	0.02	0.02	0.01
ZnO	0.01	0.00	0.00	0.00	0.00	1.01	1.03	1.00	0.00
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.006	0.009	0.009	0.009	0.009	0.009	0.009	0.009	0.004
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.000	0.000	0.112	0.214	0.306	0.000	0.000	0.000	0.015
Co3O4	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.003
Cr2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.028
CuO	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.200
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.001
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.003	0.000	0.005	0.008	0.000	0.000	0.001	0.000
Cl	0.017	0.018	0.014	0.016	0.014	0.016	0.016	0.016	0.013
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	1.042	2.094	2.105	2.077	2.055	2.101	2.069	2.087	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30M
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	108	109	110	111	112	113	114	115	116
SiO2	59.04	58.88	59.31	59.45	60.14	60.08	60.58	59.80	59.18
Al2O3	16.49	16.45	16.59	16.60	16.68	16.98	16.85	17.22	15.95
B2O3	5.75	5.91	6.10	5.88	6.10	6.18	6.08	6.24	5.89
P2O5	0.03	0.02	0.02	0.02	0.02	0.02	0.04	0.00	0.00
Li2O	11.98	12.01	12.09	12.08	12.25	12.27	12.27	12.29	12.01
Na2O	6.18	5.68	5.27	4.78	4.34	3.87	3.86	3.89	6.27
K2O	0.18	0.19	0.19	0.19	0.19	0.19	0.20	0.19	0.20
MgO	0.02	0.02	0.02	0.02	0.03	0.02	0.02	0.02	0.02
CaO	0.03	0.02	0.02	0.02	0.02	0.02	0.03	0.01	0.01
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.00	0.01	0.00	0.01	0.00	0.01	0.00	0.01	0.01
ZrO2	0.00	0.51	0.00	0.51	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.027	0.016	0.016	0.016	0.016	0.016	0.028	0.004	0.004
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.018	0.017	0.019	0.014	0.016	0.017	0.000	0.018	0.001
Co3O4	0.003	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Cr2O3	0.028	0.029	0.030	0.031	0.029	0.030	0.000	0.030	0.001
CuO	0.181	0.219	0.294	0.343	0.160	0.284	0.000	0.271	0.002
HfO2	0.000	0.006	0.000	0.006	0.000	0.000	0.000	0.000	0.000
MnO2	0.024	0.015	0.012	0.012	0.016	0.013	0.022	0.001	0.001
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.001
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.001	0.004	0.000	0.000	0.000	0.004	0.000	0.002
Cl	0.011	0.013	0.011	0.011	0.009	0.009	0.009	0.007	0.009
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.451

TABLE 30N
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	117	118	119	120	121	122	123	124	125
SiO2	58.83	59.12	58.95	58.94	59.09	58.96	59.27	58.89	59.84
Al2O3	14.57	15.93	15.90	15.16	15.91	17.23	17.31	17.36	17.03
B2O3	5.97	5.83	6.03	5.96	5.95	6.10	6.00	6.03	6.00
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	12.20	12.10	12.16	12.16	12.02	10.39	10.34	11.33	11.12
Na2O	6.31	6.23	6.22	6.28	6.27	2.80	2.79	2.82	2.81
K2O	0.20	0.19	0.20	0.20	0.20	0.10	0.10	0.10	0.10
MgO	0.02	0.02	0.02	0.02	0.02	0.99	0.99	1.00	0.98
CaO	0.01	0.01	0.01	0.01	0.01	2.03	2.04	1.02	0.99
ZnO	0.00	0.00	0.00	0.00	0.00	1.04	1.06	1.06	1.02
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.004	0.004	0.004	0.004	0.004	0.005	0.005	0.004	0.005
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.010	0.086	0.040	0.053	0.003	0.000	0.000	0.000	0.000
Co3O4	0.000	0.009	0.002	0.000	0.012	0.037	0.048	0.038	0.047
Cr2O3	0.003	0.001	0.001	0.002	0.001	0.049	0.000	0.052	0.000
CuO	0.015	0.002	0.001	0.009	0.025	0.253	0.024	0.271	0.037
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.000	0.002	0.000	0.002	0.004	0.005	0.007	0.004
As2O3	0.002	0.001	0.001	0.001	0.001	0.001	0.001	0.001	0.001
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.007	0.000	0.000	0.011	0.000	0.000	0.000	0.004
Cl	0.016	0.009	0.013	0.014	0.013	0.011	0.009	0.011	0.009
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	1.850	0.447	0.453	1.168	0.460	0.000	0.000	0.000	0.000

TABLE 30O
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	126	127	128	129	130	131	132	133	134
SiO2	58.98	58.50	58.20	58.36	58.82	58.06	58.50	58.41	58.97
Al2O3	16.66	17.08	16.22	16.36	16.60	16.27	16.29	16.43	16.39
B2O3	6.03	6.12	5.98	6.00	5.85	5.92	5.96	6.08	5.91
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	11.18	11.27	12.14	12.00	12.03	12.10	12.08	12.33	12.05
Na2O	2.79	2.80	6.09	6.11	6.18	6.09	6.14	6.17	6.15
K2O	0.10	0.10	0.19	0.20	0.19	0.19	0.20	0.20	0.19
MgO	0.95	0.97	0.01	0.02	0.01	0.01	0.02	0.01	0.01
CaO	1.94	2.00	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZnO	1.01	1.03	0.00	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.01	0.01	0.95	0.01	0.01	0.96	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.005	0.005	0.002	0.048	0.004	0.001	0.051	0.004	0.004
CeO2	0.000	0.000	0.200	0.002	0.000	0.400	0.000	0.002	0.004
NiO	0.000	0.000	0.000	0.000	0.037	0.000	0.000	0.000	0.000
Co3O4	0.035	0.047	0.000	0.001	0.000	0.001	0.000	0.000	0.002
Cr2O3	0.049	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
CuO	0.246	0.042	0.000	0.182	0.232	0.000	0.000	0.044	0.279
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.001	0.007	0.000	0.687	0.000	0.000	0.737	0.000	0.001
As2O3	0.001	0.001	0.000	0.001	0.000	0.001	0.001	0.001	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.299	0.000
SO3	0.007	0.000	0.000	0.000	0.010	0.000	0.001	0.000	0.000
Cl	0.009	0.011	0.007	0.009	0.009	0.009	0.009	0.011	0.009
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30P
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	135	136	137	138	139	140	141	142	143
SiO2	58.37	58.70	57.48	58.61	56.91	57.48	58.88	58.26	58.47
Al2O3	16.51	16.37	16.31	16.26	16.71	16.60	16.55	16.75	16.46
B2O3	6.14	6.07	5.90	5.88	5.94	5.97	5.98	6.09	5.98
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	12.18	12.14	11.91	11.83	11.83	11.87	11.96	12.09	11.59
Na2O	6.19	6.20	6.08	6.11	6.16	6.17	6.19	6.25	6.18
K2O	0.19	0.20	0.20	0.19	0.20	0.22	0.19	0.20	0.19
MgO	0.02	0.01	0.02	0.01	0.01	0.02	0.02	0.02	0.01
CaO	0.01	0.01	0.01	0.00	0.01	0.01	0.01	0.01	0.01
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.01	0.01	1.98	0.99	2.00	0.01	0.01	0.01	0.98
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.004	0.004	0.003	0.003	0.002	0.107	0.099	0.101	0.003
CeO2	0.000	0.002	0.101	0.103	0.214	0.000	0.103	0.212	0.106
NiO	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Co3O4	0.006	0.004	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Cr2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
CuO	0.359	0.269	0.000	0.000	0.000	0.000	0.000	0.000	0.000
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.000	0.001	0.000	0.001	1.514	0.003	0.000	0.000
As2O3	0.001	0.001	0.000	0.000	0.000	0.000	0.000	0.000	0.001
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.012	0.000	0.000	0.008	0.000	0.005	0.000
Cl	0.013	0.011	0.013	0.009	0.013	0.013	0.011	0.015	0.011
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30Q
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	144	145	146	147	148	149	150	151	152
SiO2	58.78	58.63	59.36	59.68	60.20	60.62	61.26	61.65	59.16
Al2O3	16.19	16.39	16.55	16.53	16.44	16.49	16.37	16.41	16.55
B2O3	5.92	5.87	5.78	5.78	5.85	5.88	5.89	5.93	5.92
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	11.60	11.58	11.67	11.82	11.81	11.82	11.78	11.80	11.85
Na2O	6.11	6.15	6.20	5.69	5.22	4.74	4.25	3.77	6.17
K2O	0.19	0.19	0.19	0.19	0.19	0.19	0.19	0.19	0.19
MgO	0.01	0.01	0.01	0.02	0.02	0.01	0.02	0.02	0.02
CaO	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.97	0.98	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.002	0.003	0.004	0.004	0.004	0.004	0.004	0.004	0.004
CeO2	0.199	0.161	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.000	0.000	0.019	0.020	0.018	0.020	0.020	0.020	0.105
Co3O4	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Cr2O3	0.000	0.000	0.028	0.034	0.030	0.030	0.028	0.029	0.000
CuO	0.000	0.000	0.158	0.196	0.192	0.154	0.163	0.157	0.000
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.001	0.000	0.001
As2O3	0.001	0.001	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.006	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Cl	0.011	0.011	0.009	0.009	0.009	0.009	0.007	0.007	0.009
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30R
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	153	154	155	156	157	158	159	160	161
SiO2	59.09	59.33	58.93	59.20	59.10	58.51	59.65	58.74	58.81
Al2O3	16.57	16.52	16.51	16.48	16.68	16.44	16.41	16.72	16.49
B2O3	5.93	5.85	6.02	5.92	5.87	6.05	5.91	6.00	6.01
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	11.95	11.83	12.04	11.94	11.67	11.97	11.68	11.98	11.85
Na2O	6.17	6.19	6.20	6.16	6.20	6.18	6.10	6.28	6.20
K2O	0.19	0.19	0.20	0.19	0.19	0.19	0.19	0.20	0.19
MgO	0.02	0.02	0.02	0.01	0.01	0.02	0.01	0.02	0.01
CaO	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.004	0.004	0.004	0.004	0.004	0.004	0.004	0.004	0.004
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.058	0.033	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Co3O4	0.001	0.000	0.004	0.019	0.000	0.000	0.000	0.000	0.000
Cr2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.014	0.030	0.000
CuO	0.000	0.010	0.058	0.046	0.244	0.617	0.000	0.000	0.402
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.000	0.000	0.001	0.000	0.000	0.000	0.000	0.000
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.000	0.000	0.006	0.000	0.000	0.007	0.000
Cl	0.009	0.009	0.011	0.009	0.009	0.011	0.007	0.013	0.011
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30S
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	162	163	164	165	166	167	168	169	170
SiO2	58.68	58.44	58.49	58.71	59.24	58.85	58.57	58.74	59.78
Al2O3	16.47	16.41	16.39	16.49	16.63	16.54	16.54	16.51	16.48
B2O3	6.01	5.89	5.79	6.02	5.72	5.96	6.07	6.02	5.96
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	11.98	11.80	11.83	9.89	11.15	10.92	10.51	9.98	10.47
Na2O	6.21	6.11	6.12	4.28	5.77	5.24	4.77	4.28	4.78
K2O	0.20	0.21	0.21	0.20	0.19	0.20	0.20	0.20	0.20
MgO	0.02	0.02	0.02	0.04	0.02	0.03	0.04	0.05	0.03
CaO	0.01	0.01	0.01	4.00	1.00	2.00	3.01	3.99	1.99
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.01
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.004	0.072	0.071	0.004	0.004	0.004	0.004	0.005	0.004
CeO2	0.000	0.001	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.000	0.000	0.000	0.000	0.014	0.015	0.015	0.016	0.015
Co3O4	0.000	0.000	0.000	0.003	0.002	0.002	0.002	0.002	0.002
Cr2O3	0.000	0.000	0.000	0.000	0.026	0.027	0.027	0.027	0.026
CuO	0.410	0.000	0.000	0.338	0.224	0.195	0.213	0.185	0.231
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	1.030	1.031	0.001	0.000	0.000	0.000	0.001	0.000
As2O3	0.000	0.000	0.000	0.001	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.002	0.000	0.000	0.000	0.000	0.000	0.006
Cl	0.011	0.009	0.013	0.009	0.007	0.009	0.009	0.009	0.007
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30T
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	171	172	173	174	175	176	177	178	179
SiO2	60.35	59.09	59.09	59.24	58.84	58.90	59.35	58.51	58.20
Al2O3	16.50	16.38	16.40	16.33	16.50	16.51	16.27	16.30	16.50
B2O3	6.09	5.92	5.97	5.95	5.98	5.97	5.91	5.92	5.89
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	10.25	9.97	9.90	9.91	10.02	9.95	9.92	9.72	9.77
Na2O	4.29	4.26	4.25	4.25	4.25	4.25	4.24	4.22	4.22
K2O	0.20	0.20	0.20	0.20	0.20	0.20	0.20	0.21	0.21
MgO	0.03	0.04	0.04	0.04	0.04	0.05	0.04	0.05	0.05
CaO	2.00	3.93	3.95	3.92	4.00	3.98	3.89	3.92	3.97
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.004	0.004	0.004	0.004	0.004	0.004	0.004	0.074	0.075
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.015	0.029	0.029	0.000	0.000	0.000	0.000	0.000	0.000
Co3O4	0.002	0.009	0.009	0.006	0.006	0.006	0.006	0.000	0.000
Cr2O3	0.027	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
CuO	0.219	0.132	0.129	0.132	0.130	0.160	0.155	0.000	0.000
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.001	0.001	0.000	0.000	0.000	0.000	1.056	1.081
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.000	0.000	0.004	0.000	0.000	0.000	0.006
Cl	0.007	0.009	0.009	0.011	0.009	0.011	0.009	0.009	0.011
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30U
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	180	181	182	183	184	185	186	187	188
SiO2	58.69	58.89	58.60	58.69	57.79	57.28	57.43	57.09	57.38
Al2O3	16.22	16.37	16.48	16.37	17.33	17.18	17.16	17.37	17.30
B2O3	5.96	6.02	6.05	6.08	6.04	6.31	6.21	6.13	6.17
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	10.10	10.06	10.15	10.20	9.91	10.07	9.97	10.08	10.17
Na2O	4.22	4.31	4.30	4.28	4.32	4.34	4.32	4.34	4.31
K2O	0.21	0.20	0.20	0.20	0.20	0.20	0.20	0.20	0.20
MgO	0.05	0.04	0.04	0.04	0.05	0.05	0.05	0.05	0.05
CaO	3.88	3.94	3.98	3.95	4.31	4.22	4.26	4.27	4.26
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.57	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.075	0.004	0.004	0.004	0.005	0.004	0.004	0.004	0.004
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.000	0.029	0.030	0.028	0.000	0.000	0.000	0.000	0.000
Co3O4	0.001	0.009	0.009	0.009	0.000	0.000	0.000	0.000	0.000
Cr2O3	0.000	0.000	0.000	0.000	0.015	0.015	0.010	0.010	0.005
CuO	0.001	0.113	0.120	0.119	0.001	0.321	0.370	0.420	0.135
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.000	0.000	0.000	0.000	0.001	0.002	0.002	0.001
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.008	0.000	0.000	0.000	0.000	0.000	0.006
Cl	0.011	0.013	0.015	0.013	0.011	0.009	0.009	0.011	0.011
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30V
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	189	190	191	192	193	194	195	196	197
SiO2	58.03	58.38	58.51	57.61	59.47	59.58	59.21	59.10	61.08
Al2O3	16.91	16.78	16.62	17.18	16.37	16.35	16.41	16.46	15.56
B2O3	6.14	6.05	6.18	6.16	5.81	5.65	5.93	5.93	5.79
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	10.13	10.06	10.08	10.16	9.22	8.75	9.38	8.95	9.29
Na2O	4.30	4.28	4.28	4.35	3.76	3.28	3.77	3.27	3.79
K2O	0.20	0.20	0.20	0.20	0.19	0.20	0.20	0.20	0.20
MgO	0.04	0.05	0.05	0.05	0.05	0.06	0.95	1.91	0.05
CaO	4.11	4.07	3.99	4.19	4.89	5.91	3.94	3.95	4.01
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.004	0.004	0.004	0.004	0.004	0.005	0.004	0.005	0.005
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.000	0.004	0.000	0.000	0.016	0.015	0.016	0.017	0.016
Co3O4	0.008	0.009	0.004	0.004	0.000	0.000	0.000	0.000	0.000
Cr2O3	0.019	0.039	0.019	0.039	0.030	0.029	0.028	0.028	0.029
CuO	0.090	0.053	0.045	0.028	0.162	0.164	0.157	0.162	0.160
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.007	0.002	0.001	0.004	0.003	0.004	0.001	0.004
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.002	0.000	0.000	0.000	0.000	0.000	0.001	0.000	0.000
Cl	0.009	0.009	0.009	0.011	0.007	0.007	0.009	0.007	0.009
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30W
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	198	199	200	201	202	203	204	205	206
SiO2	61.52	59.08	59.30	59.66	58.87	61.10	61.75	58.14	58.87
Al2O3	15.16	16.42	16.47	16.33	16.67	15.45	15.23	16.87	16.53
B2O3	5.98	5.95	5.73	5.77	5.85	5.89	5.57	6.08	5.91
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.02
Li2O	8.24	9.44	8.83	9.31	8.94	9.43	8.33	9.92	9.92
Na2O	1.20	3.75	3.26	3.74	3.29	3.77	1.20	4.34	4.29
K2O	0.20	0.19	0.19	0.19	0.20	0.20	0.20	0.20	0.19
MgO	0.07	0.05	0.06	0.93	1.94	0.05	0.07	0.05	0.05
CaO	7.41	4.92	5.96	3.89	4.05	3.95	7.46	4.19	3.99
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.005	0.005	0.005	0.004	0.005	0.005	0.005	0.004	0.025
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.016	0.031	0.030	0.032	0.033	0.034	0.030	0.029	0.030
Co3O4	0.000	0.008	0.008	0.008	0.008	0.008	0.008	0.009	0.009
Cr2O3	0.028	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
CuO	0.160	0.122	0.132	0.116	0.124	0.117	0.128	0.146	0.124
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.004	0.000	0.004	0.000	0.002	0.002	0.000	0.020
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.005	0.000	0.000	0.000	0.000	0.005	0.000	0.000
Cl	0.007	0.009	0.007	0.007	0.009	0.009	0.005	0.000	0.000
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30X
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	207	208	209	210	211	211	212	213	214
SiO2	58.64	58.03	58.01	59.08	59.03	59.03	58.05	59.09	62.20
Al2O3	16.67	16.82	16.91	16.49	16.44	16.44	16.96	16.53	14.80
B2O3	5.97	6.11	6.09	5.87	5.90	5.90	6.03	6.09	6.05
P2O5	0.02	0.00	0.00	0.03	0.02	0.02	0.00	0.00	0.00
Li2O	9.82	10.05	10.04	9.96	9.94	9.94	9.97	11.78	8.89
Na2O	4.29	4.36	4.35	4.24	4.28	4.28	4.36	6.21	1.41
K2O	0.19	0.20	0.20	0.19	0.19	0.19	0.20	0.19	0.20
MgO	0.05	0.04	0.05	0.05	0.05	0.05	0.05	0.01	0.06
CaO	4.13	4.17	4.22	3.95	4.02	4.02	4.23	0.01	6.18
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.020	0.020	0.005	0.025	0.019	0.019	0.020	0.004	0.005
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.034	0.030	0.018	0.018	0.017	0.017	0.017	0.019	0.016
Co3O4	0.009	0.009	0.002	0.002	0.002	0.002	0.002	0.002	0.000
Cr2O3	0.000	0.000	0.027	0.026	0.026	0.026	0.029	0.026	0.029
CuO	0.141	0.136	0.061	0.038	0.045	0.045	0.079	0.028	0.157
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.015	0.002	0.003	0.022	0.014	0.014	0.002	0.001	0.001
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Cl	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30Y
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	215	216	217	218	219	220	221	222	223
SiO2	61.74	62.49	62.52	62.48	62.06	60.17	60.04	60.22	61.06
Al2O3	15.04	14.77	14.73	14.78	15.15	15.89	15.86	15.81	15.39
B2O3	6.06	5.96	5.99	5.99	5.88	6.03	6.19	6.14	6.05
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	9.03	8.90	8.91	8.96	8.90	8.81	8.93	8.96	8.94
Na2O	1.41	1.40	1.41	1.40	1.41	1.40	1.40	1.41	1.40
K2O	0.20	0.20	0.20	0.20	0.20	0.20	0.20	0.20	0.20
MgO	0.99	1.94	2.92	3.90	5.06	0.07	1.00	1.98	2.88
CaO	5.25	4.10	3.08	2.06	1.07	7.19	6.12	5.02	3.84
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.005	0.005	0.005	0.005	0.005	0.006	0.005	0.005	0.005
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.015	0.017	0.018	0.021	0.018	0.017	0.018	0.018	0.017
Co3O4	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Cr2O3	0.030	0.028	0.029	0.028	0.029	0.029	0.029	0.029	0.027
CuO	0.221	0.181	0.172	0.181	0.197	0.193	0.196	0.199	0.191
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.001	0.001	0.000	0.000	0.001	0.001	0.001	0.002	0.001
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Cl	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30Z
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	224	225	226	227	228	229	230	231	232
SiO2	60.16	60.87	58.66	59.73	61.24	61.20	61.14	59.00	59.98
Al2O3	15.99	15.63	17.75	16.64	15.39	15.42	15.41	17.77	16.87
B2O3	5.99	5.96	6.06	6.05	5.95	5.90	5.91	5.86	6.19
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	8.89	8.88	10.62	10.31	9.93	9.95	9.96	10.51	9.96
Na2O	1.43	1.42	1.58	1.54	1.50	1.50	1.49	1.60	1.51
K2O	0.20	0.20	0.20	0.19	0.20	0.20	0.20	0.20	0.20
MgO	4.06	4.91	4.28	4.32	4.24	3.08	1.92	4.28	4.31
CaO	2.99	1.86	0.61	0.97	1.32	2.53	3.74	0.62	0.97
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.005	0.005	0.004	0.004	0.005	0.004	0.005	0.004	0.004
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.001
NiO	0.017	0.017	0.017	0.018	0.016	0.015	0.016	0.033	0.000
Co3O4	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.009	0.000
Cr2O3	0.029	0.028	0.028	0.027	0.028	0.027	0.027	0.000	0.000
CuO	0.230	0.212	0.187	0.175	0.175	0.176	0.169	0.123	0.000
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.003	0.000	0.001	0.001	0.001	0.001	0.001	0.001	0.000
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Cl	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.007
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30AA
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	233	234	235	236	237	238	239	240	241
SiO2	61.48	60.82	61.59	60.38	59.54	58.78	58.67	58.87	58.93
Al2O3	15.58	15.90	15.28	15.51	15.98	16.53	16.55	16.50	16.41
B2O3	6.03	5.95	6.01	5.93	5.90	6.31	6.19	6.27	6.25
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	9.69	9.52	9.28	8.65	8.69	9.66	9.62	9.59	9.69
Na2O	1.48	1.44	1.38	1.41	1.52	1.45	1.46	1.46	1.45
K2O	0.20	0.20	0.20	0.20	0.19	0.19	0.19	0.19	0.19
MgO	4.22	3.17	1.89	2.88	5.05	2.18	2.16	2.17	2.16
CaO	1.31	2.86	4.16	3.83	1.88	4.75	4.78	4.78	4.78
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.01	0.01	0.01	0.99	1.02	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.004	0.004	0.004	0.003	0.003	0.005	0.005	0.006	0.005
CeO2	0.004	0.001	0.000	0.209	0.213	0.000	0.000	0.000	0.000
NiO	0.000	0.008	0.016	0.000	0.000	0.009	0.039	0.040	0.000
Co3O4	0.000	0.000	0.000	0.000	0.000	0.001	0.004	0.004	0.004
Cr2O3	0.000	0.013	0.026	0.001	0.001	0.014	0.036	0.024	0.035
CuO	0.000	0.098	0.164	0.001	0.000	0.106	0.281	0.101	0.091
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.001	0.003
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Cl	0.005	0.007	0.005	0.009	0.007	0.000	0.000	0.000	0.000
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30BB
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	242	243	244	245	246	247	248	249	250
SiO2	58.94	59.48	58.54	58.48	58.76	60.53	60.31	61.47	60.28
Al2O3	16.76	16.21	16.48	16.62	16.48	15.05	15.08	14.54	15.16
B2O3	5.90	6.16	6.32	6.27	6.24	5.91	6.02	5.92	5.81
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	9.32	9.56	9.85	9.80	9.71	10.04	10.08	9.92	9.95
Na2O	1.47	1.47	1.45	1.45	1.45	1.84	1.86	1.83	1.86
K2O	0.19	0.20	0.19	0.19	0.19	0.20	0.20	0.19	0.20
MgO	2.20	2.07	2.17	2.18	2.16	2.03	2.02	1.92	2.02
CaO	4.89	4.69	4.73	4.76	4.74	2.09	2.11	1.99	2.13
ZnO	0.00	0.00	0.00	0.00	0.00	1.07	1.07	1.01	1.10
TiO2	0.01	0.01	0.01	0.01	0.01	1.01	1.02	0.99	1.02
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.005	0.005	0.005	0.005	0.005	0.003	0.004	0.004	0.002
CeO2	0.000	0.000	0.000	0.000	0.000	0.216	0.218	0.201	0.424
NiO	0.000	0.036	0.022	0.021	0.019	0.000	0.000	0.000	0.000
Co3O4	0.001	0.001	0.003	0.003	0.002	0.000	0.000	0.000	0.000
Cr2O3	0.025	0.034	0.029	0.030	0.031	0.000	0.000	0.000	0.000
CuO	0.279	0.101	0.212	0.193	0.187	0.000	0.000	0.000	0.000
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.004	0.001	0.000	0.000	0.001	0.000	0.000	0.000	0.000
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.014
Cl	0.000	0.000	0.000	0.000	0.000	0.011	0.009	0.007	0.007
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30CC
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	251	252	253	254	255	256	257	258	259
SiO2	61.13	60.99	60.54	60.74	59.21	59.45	61.01	61.36	60.91
Al2O3	14.65	14.71	15.08	14.92	15.59	15.65	14.78	15.14	14.73
B2O3	5.90	5.86	5.89	5.89	6.10	6.05	5.95	5.25	5.98
P2O5	0.00	0.05	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	10.00	9.98	9.98	9.98	10.15	9.94	9.81	9.59	9.90
Na2O	1.83	1.84	1.87	1.86	1.81	1.83	1.76	1.80	1.81
K2O	0.19	0.19	0.19	0.19	0.18	0.18	0.18	0.18	0.19
MgO	1.94	1.96	2.01	1.49	2.23	2.24	2.09	2.01	2.01
CaO	2.03	2.05	2.11	2.09	2.29	2.26	2.14	2.12	2.09
ZnO	1.02	1.03	1.07	1.59	1.19	1.11	1.07	1.07	1.05
TiO2	0.99	1.00	1.02	1.01	1.03	1.04	0.99	1.03	1.00
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.10	0.10	0.00	0.00	0.00	0.00	0.00	0.00	0.10
Fe2O3	0.004	0.004	0.004	0.003	0.004	0.004	0.004	0.002	0.003
CeO2	0.206	0.208	0.214	0.208	0.219	0.218	0.209	0.427	0.210
NiO	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Co3O4	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Cr2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
CuO	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.021	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.009	0.000	0.000	0.000	0.007	0.000	0.000	0.002
Cl	0.007	0.009	0.007	0.007	0.007	0.005	0.005	0.007	0.007
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30DD
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	260	261	262	263	264	265	266	267	268
SiO2	60.80	59.47	60.46	64.70	64.67	64.27	64.56	64.76	64.07
Al2O3	14.64	15.69	15.29	12.99	13.00	12.89	13.02	12.96	12.95
B2O3	5.98	6.03	5.99	5.83	5.81	5.72	5.83	5.74	5.64
P2O5	0.05	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	9.99	9.95	9.67	11.98	12.02	11.71	12.07	10.02	9.96
Na2O	1.74	1.80	1.82	2.81	2.80	2.73	2.82	1.84	1.82
K2O	0.17	0.18	0.18	0.19	0.20	0.19	0.20	0.20	0.20
MgO	2.05	2.21	1.56	0.01	0.01	0.01	0.01	0.03	0.03
CaO	2.13	2.23	2.16	0.01	0.01	0.01	0.01	2.93	2.98
ZnO	1.13	1.15	1.62	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.99	1.04	1.03	0.98	0.98	0.97	0.98	0.98	0.98
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.10	0.00	0.00	0.05	0.05	0.04	0.05	0.05	0.05
Fe2O3	0.003	0.004	0.003	0.002	0.002	0.002	0.002	0.003	0.003
CeO2	0.212	0.223	0.219	0.201	0.205	0.200	0.207	0.200	0.203
NiO	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Co3O4	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Cr2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
CuO	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.021	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.003
Cl	0.007	0.007	0.005	0.012	0.014	1.019	0.016	0.011	0.012
F	0.000	0.000	0.000	0.231	0.231	0.230	0.231	0.266	1.093
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30EE
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	269	270	271	272	273	274	275	276	277
SiO2	63.99	63.75	63.77	61.32	60.98	63.28	62.41	63.31	62.35
Al2O3	12.94	12.77	12.78	15.29	15.41	14.67	14.80	14.64	15.09
B2O3	5.78	5.72	5.55	5.84	6.08	5.87	5.93	5.67	5.93
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	9.95	9.65	9.67	9.35	9.57	8.88	8.87	8.78	8.95
Na2O	1.82	1.78	1.78	1.47	1.42	1.35	1.36	1.36	1.36
K2O	0.20	0.19	0.19	0.20	0.20	0.00	0.00	0.00	0.00
MgO	0.03	0.03	0.03	1.99	1.96	2.78	2.80	2.75	2.89
CaO	2.96	2.92	2.93	4.23	4.22	1.91	1.94	1.91	2.00
ZnO	0.00	0.00	0.00	0.00	0.00	0.95	0.98	0.97	1.01
TiO2	0.98	0.97	0.96	0.05	0.01	0.01	0.59	0.29	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.05	0.04	0.04	0.00	0.00	0.00	0.00	0.00	0.10
Fe2O3	0.003	0.003	0.003	0.005	0.005	0.002	0.002	0.002	0.002
CeO2	0.206	0.195	0.198	0.000	0.000	0.299	0.303	0.305	0.308
NiO	0.000	0.000	0.000	0.000	0.022	0.000	0.000	0.000	0.000
Co3O4	0.000	0.000	0.000	0.002	0.009	0.000	0.000	0.000	0.000
Cr2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
CuO	0.000	0.000	0.000	0.264	0.113	0.000	0.000	0.000	0.000
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.000	0.000	0.001	0.000	0.000	0.000	0.000	0.000
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.000	0.000	0.000	0.000	0.001	0.000	0.000
Cl	0.011	1.011	1.064	0.000	0.009	0.004	0.004	0.005	0.005
F	1.094	0.989	1.022	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30FF
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	278	279	280	281	282	283	285	286
SiO2	61.95	63.09	58.67	60.98	61.10	60.60	58.94	60.54
Al2O3	15.17	15.05	17.01	17.21	14.87	14.93	14.50	15.63
B2O3	5.83	5.88	5.55	4.81	5.95	5.82	5.75	6.08
P2O5	0.51	0.50	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	8.90	8.97	8.83	8.11	9.96	10.04	13.39	9.65
Na2O	1.36	1.36	1.41	1.45	1.86	1.86	1.39	1.47
K2O	0.00	0.00	0.19	0.20	0.20	0.19	0.19	0.20
MgO	2.92	2.87	2.22	2.19	1.98	1.99	1.79	1.96
CaO	2.00	0.96	4.90	4.90	2.06	2.07	3.99	4.38
ZnO	1.02	1.00	0.00	0.00	0.00	1.04	0.00	0.00
TiO2	0.01	0.01	1.08	0.01	1.01	1.02	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.57	0.00	0.00	0.00
Fe2O3	0.003	0.002	0.005	0.005	0.002	0.002	0.005	0.005
CeO2	0.316	0.309	0.116	0.122	0.416	0.425	0.000	0.000
NiO	0.000	0.000	0.000	0.000	0.000	0.000	0.003	0.005
Co3O4	0.000	0.000	0.000	0.000	0.000	0.000	0.001	0.001
Cr2O3	0.000	0.000	0.001	0.001	0.000	0.000	0.000	0.000
CuO	0.000	0.000	0.000	0.000	0.000	0.000	0.045	0.071
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.001
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.002	0.000	0.000	0.022	0.000	0.000	0.000
Cl	0.005	0.004	0.007	0.007	0.005	0.007	0.000	0.000
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30GG
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	287	288	289	290	291	292	293	294	295
SiO2	60.42	61.34	59.26	59.32	59.30	59.57	59.31	59.28	58.55
Al2O3	15.76	15.32	16.06	16.19	16.14	16.03	16.28	16.36	16.45
B2O3	6.15	5.94	6.27	6.18	6.25	6.16	6.03	6.10	6.20
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	9.52	9.39	9.69	9.52	9.61	9.59	9.45	9.36	9.72
Na2O	1.46	1.46	1.48	1.47	1.47	1.47	1.49	1.48	1.46
K2O	0.20	0.20	0.19	0.19	0.19	0.19	0.19	0.19	0.19
MgO	1.99	1.93	2.17	2.21	2.18	2.15	2.25	2.26	2.34
CaO	4.43	4.25	4.63	4.67	4.60	4.59	4.73	4.74	4.80
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.006	0.005	0.006	0.006	0.006	0.006	0.006	0.006	0.006
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.006	0.023	0.018	0.018	0.018	0.017	0.017	0.018	0.021
Co3O4	0.001	0.009	0.002	0.002	0.002	0.002	0.002	0.002	0.002
Cr2O3	0.000	0.000	0.030	0.030	0.031	0.029	0.029	0.026	0.028
CuO	0.053	0.116	0.179	0.185	0.190	0.188	0.193	0.188	0.219
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.001	0.001	0.002	0.001	0.000	0.001	0.003	0.000	0.001
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Cl	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30HH
Ex	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	296	297	298	299	300	301	302	303	304
SiO2	59.81	60.62	59.28	59.05	59.84	60.24	60.81	61.20	61.86
Al2O3	15.83	15.58	16.34	16.45	15.99	15.84	14.91	14.79	14.33
B2O3	6.23	6.09	5.99	6.02	6.09	6.04	6.13	6.11	6.06
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	9.63	9.44	11.71	11.72	9.46	10.42	10.64	12.51	10.59
Na2O	1.50	1.55	6.22	6.25	1.59	2.57	2.57	2.59	4.49
K2O	0.20	0.19	0.19	0.20	0.20	0.20	0.19	0.20	0.20
MgO	2.07	1.99	0.02	0.02	2.11	0.05	0.05	0.03	0.03
CaO	4.48	4.26	0.01	0.01	4.40	4.33	4.39	2.28	2.17
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.006	0.007	0.003	0.003	0.005	0.004	0.004	0.004	0.004
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.016	0.008	0.011	0.008	0.009	0.009	0.011	0.008	0.010
Co3O4	0.002	0.003	0.000	0.001	0.002	0.001	0.002	0.001	0.001
Cr2O3	0.029	0.027	0.024	0.027	0.028	0.028	0.029	0.028	0.027
CuO	0.189	0.222	0.173	0.219	0.243	0.239	0.249	0.235	0.219
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.003	0.001	0.004	0.000	0.003	0.004	0.001	0.000	0.000
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.000	0.000	0.010	0.000	0.000	0.000	0.002
Cl	0.000	0.000	0.011	0.011	0.009	0.013	0.011	0.009	0.011
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30II
Ex	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	305	306	307	308	309	310	311	312	313
SiO2	61.95	61.15	60.57	61.14	61.00	60.47	60.78	60.81	61.72
Al2O3	14.34	14.82	14.66	14.53	14.33	14.61	14.55	14.61	14.54
B2O3	6.01	6.02	6.06	5.91	6.04	6.02	6.01	5.97	5.97
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	10.57	10.62	11.00	12.82	11.15	11.14	11.10	11.03	11.15
Na2O	2.53	2.57	2.88	2.88	4.80	2.91	2.88	2.87	2.84
K2O	1.17	0.20	0.19	0.19	0.19	1.18	0.20	0.48	0.19
MgO	0.04	2.07	0.05	0.03	0.03	0.04	1.98	1.69	1.06
CaO	3.12	2.27	4.33	2.24	2.17	3.30	2.23	2.26	2.25
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.004	0.004	0.004	0.004	0.004	0.004	0.004	0.004	0.004
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.008	0.008	0.009	0.008	0.008	0.009	0.008	0.008	0.007
Co3O4	0.001	0.002	0.001	0.002	0.001	0.001	0.002	0.001	0.002
Cr2O3	0.027	0.028	0.028	0.027	0.026	0.027	0.027	0.027	0.027
CuO	0.219	0.238	0.209	0.208	0.222	0.260	0.212	0.212	0.219
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.003	0.001	0.000	0.000	0.000	0.000	0.000	0.000	0.000
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.000	0.000	0.011	0.000	0.000	0.000	0.000
Cl	0.011	0.007	0.009	0.011	0.009	0.013	0.007	0.009	0.009
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30JJ
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	314	315	316	317	318	319	320	321	322
SiO2	61.88	61.90	59.24	58.96	58.61	59.56	58.58	58.78	58.94
Al2O3	14.54	14.59	16.01	16.03	16.22	16.07	16.18	16.41	16.13
B2O3	6.00	5.90	6.00	6.26	6.25	5.89	6.25	5.95	6.12
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	11.95	11.43	10.10	10.11	10.07	9.74	10.08	9.86	10.05
Na2O	2.87	3.34	1.47	1.47	1.47	1.48	1.47	1.47	1.49
K2O	0.19	0.19	0.19	0.19	0.19	0.20	0.19	0.19	0.19
MgO	0.03	0.03	2.15	2.15	2.24	2.16	2.31	2.30	2.22
CaO	2.25	2.28	4.55	4.57	4.67	4.62	4.67	4.78	4.62
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.004	0.004	0.006	0.006	0.006	0.006	0.006	0.006	0.006
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.010	0.009	0.020	0.020	0.019	0.017	0.020	0.016	0.018
Co3O4	0.001	0.001	0.002	0.002	0.002	0.002	0.002	0.002	0.002
Cr2O3	0.027	0.028	0.030	0.029	0.031	0.029	0.030	0.023	0.029
CuO	0.203	0.262	0.214	0.187	0.197	0.203	0.191	0.193	0.183
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.000	0.000	0.003	0.001	0.002	0.002	0.002	0.001
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.010	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Cl	0.009	0.009	0.000	0.000	0.000	0.000	0.000	0.000	0.000
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30KK
Ex	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	323	324	325	326	327	328	329	330	331
SiO2	60.45	60.59	60.02	60.41	59.73	60.46	60.17	60.03	61.68
Al2O3	15.53	15.42	15.80	15.59	16.01	15.63	15.79	15.79	15.01
B2O3	5.89	5.98	6.00	6.00	6.01	6.00	6.00	5.99	5.96
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	9.95	9.47	9.51	9.51	9.52	9.50	9.51	9.49	9.44
Na2O	1.45	1.41	1.30	1.42	1.40	1.40	1.26	1.40	1.38
K2O	0.19	0.18	0.18	0.19	0.19	0.19	0.18	0.19	0.19
MgO	1.98	2.14	2.22	2.12	2.22	2.07	2.19	2.18	1.95
CaO	4.28	4.57	4.71	4.52	4.67	4.52	4.65	4.67	4.16
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.006	0.005
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.018	0.018	0.018	0.017	0.019	0.012	0.019	0.015	0.017
Co3O4	0.002	0.002	0.002	0.002	0.002	0.002	0.002	0.002	0.002
Cr2O3	0.028	0.030	0.031	0.030	0.030	0.029	0.029	0.029	0.028
CuO	0.209	0.180	0.185	0.181	0.187	0.182	0.185	0.185	0.173
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.002	0.002	0.003	0.001	0.001	0.001	0.000	0.001	0.001
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Cl	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30LL
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	332	333	334	335	336	337	338	339	340
SiO2	61.47	61.47	61.51	61.27	61.46	61.87	61.25	61.30	61.64
Al2O3	15.03	15.11	15.06	15.13	15.05	14.90	15.13	15.02	14.94
B2O3	5.96	5.99	5.97	5.97	5.98	5.92	6.04	5.90	5.84
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	12.21	12.11	12.06	12.22	12.23	12.02	12.17	12.35	12.33
Na2O	3.92	3.95	3.94	3.95	3.92	3.93	3.95	3.93	3.90
K2O	0.39	0.39	0.39	0.39	0.39	0.40	0.39	0.39	0.39
MgO	0.02	0.02	0.02	0.02	0.02	0.02	0.02	0.02	0.02
CaO	0.77	0.77	0.77	0.77	0.77	0.75	0.77	0.77	0.75
ZnO	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.004	0.004	0.004	0.004	0.004	0.004	0.004	0.004	0.004
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.014	0.007	0.005	0.005	0.004	0.019	0.021	0.024	0.023
Co3O4	0.002	0.001	0.001	0.002	0.002	0.001	0.001	0.002	0.002
Cr2O3	0.025	0.023	0.029	0.024	0.027	0.023	0.030	0.023	0.028
CuO	0.181	0.154	0.234	0.232	0.137	0.134	0.209	0.251	0.136
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.000	0.000	0.002	0.000	0.000	0.000	0.001	0.000	0.000
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Cl	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30MM
Ex.	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-	ORA-
(mol %)	341	342	343	344	345	346	347	348	349
SiO2	61.24	58.93	58.82	58.94	58.90	61.76	62.65	63.64	64.54
Al2O3	15.06	16.47	16.44	16.45	16.45	15.01	15.08	14.99	15.05
B2O3	6.06	5.91	5.95	5.92	5.92	5.81	4.87	3.93	2.96
P2O5	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Li2O	12.33	10.13	10.23	12.25	12.30	12.33	12.32	12.36	12.30
Na2O	3.92	4.26	4.26	6.19	6.19	3.78	3.78	3.79	3.82
K2O	0.39	0.29	0.29	0.20	0.20	0.39	0.38	0.39	0.39
MgO	0.02	2.98	2.97	0.02	0.02	0.03	0.03	0.03	0.04
CaO	0.76	0.03	0.03	0.01	0.01	0.61	0.62	0.62	0.64
ZnO	0.00	0.99	0.99	0.00	0.00	0.00	0.00	0.00	0.00
TiO2	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.004	0.004	0.004	0.003	0.003	0.004	0.004	0.004	0.004
CeO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
NiO	0.018	0.000	0.000	0.000	0.000	0.019	0.022	0.022	0.021
Co3O4	0.002	0.000	0.000	0.000	0.000	0.002	0.002	0.002	0.002
Cr2O3	0.025	0.000	0.000	0.000	0.000	0.021	0.021	0.022	0.022
CuO	0.145	0.000	0.000	0.000	0.000	0.206	0.199	0.184	0.203
HfO2	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
MnO2	0.004	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
As2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
SO3	0.000	0.000	0.000	0.000	0.000	0.021	0.000	0.002	0.000
Cl	0.000	0.011	0.011	0.014	0.014	0.007	0.007	0.007	0.011
F	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000	0.000

TABLE 30NN
Ex.
(mol %)	ORA-350	ORA-351	ORA-352	ORA-353	ORA-354
SiO2	65.24	66.43	61.57	61.66	61.64
Al2O3	15.13	15.10	15.07	15.16	15.12
B2O3	2.02	1.03	5.87	5.82	5.81
P2O5	0.00	0.00	0.00	0.00	0.00
Li2O	12.43	12.27	12.38	12.29	12.38
Na2O	3.81	3.82	3.82	3.79	3.78
K2O	0.41	0.40	0.39	0.39	0.38
MgO	0.04	0.03	0.03	0.03	0.03
CaO	0.64	0.64	0.63	0.65	0.67
ZnO	0.00	0.00	0.00	0.00	0.00
TiO2	0.01	0.01	0.01	0.01	0.01
ZrO2	0.00	0.00	0.00	0.00	0.00
WO3	0.00	0.00	0.00	0.00	0.00
SnO2	0.00	0.00	0.00	0.00	0.00
Fe2O3	0.004	0.004	0.004	0.004	0.004
CeO2	0.000	0.000	0.000	0.000	0.000
NiO	0.020	0.022	0.023	0.023	0.022
Co3O4	0.002	0.002	0.002	0.002	0.001
Cr2O3	0.022	0.022	0.021	0.022	0.021
CuO	0.219	0.212	0.174	0.137	0.123
HfO2	0.000	0.000	0.000	0.000	0.000
MnO2	0.001	0.000	0.004	0.000	0.001
As2O3	0.000	0.000	0.000	0.000	0.000
Sb2O3	0.000	0.000	0.000	0.000	0.000
V2O5	0.000	0.000	0.000	0.000	0.000
SO3	0.004	0.000	0.000	0.007	0.000
Cl	0.011	0.011	0.009	0.007	0.007
F	0.000	0.000	0.000	0.000	0.000
Nd2O3	0.000	0.000	0.000	0.000	0.000
Er2O3	0.000	0.000	0.000	0.000	0.000

Referring now to Table 31, colored glass articles in the form of glass coupons were produced from the glass compositions of Tables 30A-30NN. The glass coupons had the indicated thicknesses. The CIELAB L*, a*, and b* coordinates of each colored glass article were determined. The average transmittance (%) for each sample over the wavelength range from 380 nm to 750 nm was also determined. The results are reported in Table 31.

TABLE 31
					Average
					transmittance
				Thickness	(380 nm-
Example	L*	a*	b*	(mm)	750 nm )
ORA-1	54.3	−2.25	−23.3	1.496	38.08
ORA-2	53.5	5.59	−47.3	1.504	45.89
ORA-3	73.5	−1.65	3.45	1.518	56.14
ORA-4	58.6	−2.44	−0.74	1.355	42.35
ORA-5	81.6	−6.19	26.71	1.503	48.95
ORA-6	80.9	−10.9	60.97	1.551	44.81
ORA-6	82.2	−11.5	61.28	1.52	46.21
ORA-7	84	2.38	24.44	1.51	67.97
ORA-8	86	−9.09	−0.48	1.499	56.39
ORA-8	85.7	−9.4	−0.84	1.502	55.96
ORA-8	85.7	−9.37	−0.86	1.5	55.85
ORA-9	60.3	2.68	46.7	1.5	52.41
ORA-10	81.4	−12.9	44.23	1.496	45.38
ORA-11	96.2	1.07	6.85	1.534	82.97
ORA-11	96.1	1.08	7	1.53	82.78
ORA-12	96.6	−0.46	2.3	1.34	87.06
ORA-14	96.3	−0.49	0.14	1.516	89.66
ORA-15	85.6	−1.05	2.82	1.504	72.58
ORA-16	80	−7.58	−2.04	1.51	52.17
ORA-17	74.4	−1.63	2.16	1.509	58.32
ORA-18	88.8	−3.39	17.58	1.505	66.53
ORA-21	77.1	−17.9	8.2	1.453	39.68
ORA-22	87	−8.47	5.42	1.33	64.68
ORA-23	95.3	−0.43	0.29	1.34	88.58
ORA-23	95.3	−0.43	0.43	1.34	88.58
ORA-24	65.9	−2.01	−18.5	1.33	51.58
ORA-25	81.5	−5.99	−3.18	1.535	58.24
ORA-26	77.9	−9.15	−1.49	1.537	47.20
ORA-27	73.6	11.9	1.72	1.526	37.11
ORA-28	68.3	−14.4	6.15	1.538	27.56
ORA-29	55.7	−17.4	17.39	1.554	13.76
ORA-30	41.5	16.8	27.15	1.553	5.89
ORA-31	89.8	−0.72	16.26	1.4	72.68
ORA-32	26.9	−12	15.29	1.32	3.08
ORA-33	65.6	−2.29	−12.4	1.31	50.51
ORA-34	79.1	−13.5	10.74	1.31	46.61
ORA-35	95	−1.05	−1.88	1.32	87.51
ORA-36	46.4	−17.7	−13.5	1.3	13.49
ORA-37	42.9	−1.87	−22.3	1.34	33.01
ORA-38	43.4	−0.37	−42	1.33	28.23
ORA-39	60.9	−2.38	0.5	1.32	44.34
ORA-40	94.3	−0.51	8.43	1.34	84.53
ORA-41	87.1	−8.58	5.19	1.32	64.68
ORA-42	95.2	−0.73	−0.52	1.31	88.13
ORA-43	65.5	2.16	−19.2	1.35	50.85
ORA-44	59.3	−2.83	−0.51	1.34	42.93
ORA-45	94.5	−0.38	9.12	1.31	85.15
ORA-46	86.6	−9.29	5.62	1.31	62.94
ORA-47	95.4	−0.61	0.79	1.34	88.84
ORA-48	65.2	−2.41	20.2	1.29	50.75
ORA-49	57.6	−3.12	−2.32	1.34	41.79
ORA-50	94.3	−0.35	9.09	1.33	84.83
ORA-51	66.3	−1.99	−18.3	1.32	51.94
ORA-52	90	−1.31	−2.91	1.31	79.81
ORA-52	89.2	−1.62	−3.62	1.29	78.10
ORA-53	66.3	1.99	−19.6	1.33	51.11
ORA-53	66.6	−2.1	−19.5	1.33	51.36
ORA-54	88.8	−6.42	4.63	1.33	65.58
ORA-54	88.8	−6.54	4.6	1.35	65.42
ORA-56	68.8	−6.69	−18.2	1.32	43.78
ORA-56	69.6	−6.37	−17.8	1.29	45.12
ORA-57	83	−4	7.77	1.29	65.47
ORA-57	83.6	3.74	7.38	1.29	66.76
ORA-58	64.6	−2.21	−20.4	1.29	49.14
ORA-58	64.1	−2.17	−20.6	1.29	48.62
ORA-59	89	−1.7	−3.4	1.3	77.55
ORA-60	67	−1.93	−18.2	1.29	51.74
ORA-61	93.4	−0.84	7.53	1.34	83.00
ORA-62	63.5	−11.9	−9.2	1.31	28.70
ORA-63	83.1	−3.99	−6.93	1.27	65.15
ORA-64	62.7	−2.12	−21.6	1.31	46.93
ORA-65	87.2	−8.3	5.82	1.33	65.10
ORA-66	93.7	−0.3	9.8	1.36	83.86
ORA-67	74.4	−2.49	32.99	1.14	46.62
ORA-68	90.5	4.5	−5.85	1.34	74.29
ORA-69	68.8	−7.32	−15.8	1.33	42.51
ORA-70	68	−4.44	−20.9	1.35	47.23
ORA-71	57	−2.73	−5.3	1.37	41.30
ORA-72	63.6	−2.73	−18.7	1.42	46.95
ORA-73	96.1	−0.12	3.25	1.35	89.72
ORA-74	55.7	−2.73	0.04	1.36	39.84
ORA-75	62.8	−2.25	−5.79	1.36	47.14
ORA-76	96.8	−0.02	0.27	1.35	91.59
ORA-77	95.9	0.01	0.7	1.33	88.60
ORA-78	65.4	0.92	−37.5	1.36	53.47
ORA-79	76.6	−2.14	−16.2	0.621	63.69
ORA-79	76.6	−2.14	−16.2	0.621	63.69
ORA-79	76.6	−2.14	−16.2	0.621	63.69
ORA-80	96.7	−0.25	−0.13	0.62	91.23
ORA-80	96.7	−0.25	−0.13	0.62	91.23
ORA-80	96.7	−0.25	−0.13	0.62	91.23
ORA-81	71.2	−2.05	−7.46	0.643	56.43
ORA-81	71.2	−2.05	−7.46	0.643	56.43
ORA-81	71.2	−2.05	−7.46	0.643	56.43
ORA-82	86.6	−1.81	−6.31	1.33	74.45
ORA-83	96.9	−0.02	0.12	1.24	92.02
ORA-84	96.7	−0.11	0.25	1.3	91.05
ORA-85	96.8	−0.07	0.21	1.32	91.52
ORA-86	96.9	−0.03	0.21	1.28	91.43
ORA-87	96.7	−0.02	0.47	1.25	91.39
ORA-88	79.3	−4.44	−11.8	1.26	60.21
ORA-89	60.4	−8.61	−17.1	1.34	31.09
ORA-90	67.8	−6.25	−30.3	1.34	46.93
ORA-91	62.4	−6.04	−26.3	1.35	38.76
ORA-92	63	−10.3	−24.5	1.35	38.11
ORA-93	64.1	−8.04	−28.3	1.33	41.34
ORA-94	65.3	−6.48	−29.5	1.33	43.18
ORA-95	84.5	−12.4	12.15	1.29	52.71
ORA-96	83	13.6	13.11	1.35	49.38
ORA-97	90.1	−8.32	29.93	1.3	61.02
ORA-98	91	−2.23	−8.98	1.23	85.94
ORA-99	87.2	−2.88	−14.4	1.26	81.26
ORA-100	82.2	−2.53	−20.6	1.27	74.80
ORA-101	79.7	−3.97	−10.2	1.29	68.13
ORA-102	78	−4.64	−0.58	1.3	62.62
ORA-103	76.4	−5.2	6.85	1.28	58.13
ORA-104	81.8	−2.5	−21.2	1.31	74.47
ORA-105	81.5	−2.5	−21.7	1.31	74.29
ORA-106	81.6	−2.62	−21.8	1.25	74.67
ORA-107	88.2	−6.98	0.45	1.2	69.06
ORA-108	88.5	−6.04	2.77	1.22	69.99
ORA-109	90.6	−5.74	6.05	1.2	71.88
ORA-110	90.6	−5.52	7.3	1.2	72.19
ORA-111	90.3	−5.35	9.22	1.28	70.83
ORA-112	90.5	−5.31	8.41	1.28	70.71
ORA-113	90.8	4.31	9.47	1.28	72.44
ORA-114	96.8	−0.06	0.39	1.27	91.19
ORA-115	90	−5.24	7.76	1.29	70.45
ORA-116	95.8	3.04	−0.87	1.348	88.26
ORA-117	93.7	7.94	−1.71	1.349	81.56
ORA-118	91.7	3.05	10.6	1.35	79.00
ORA-119	93.9	3	4.49	1.35	83.88
ORA-120	93.4	5.72	3.16	1.336	81.16
ORA-121	87.6	2.01	−11.4	1.348	77.16
ORA-122	68.3	−2.07	−0.58	1.348	51.93
ORA-123	69.5	−8.73	−13	1.341	45.19
ORA-124	68.1	−1.99	−0.92	1.348	51.96
ORA-125	70.4	8.27	−13.1	1.315	46.55
ORA-126	68	−9.3	−15.1	1.32	43.43
ORA-127	65.6	−2.31	−3.05	1.346	49.46
ORA-128	95.1	−0.8	8.89	1.307	79.31
ORA-129	95.2	−0.91	5.02	1.324	83.78
ORA-130	93.2	−1.14	3.86	1.327	81.89
ORA-131	78.2	4.27	62.38	1.258	45.39
ORA-132	96.1	−0.4	3.04	1.297	87.72
ORA-133	95	−1.08	5.27	1.299	79.59
ORA-134	92.2	−3.32	−5.34	1.252	79.12
ORA-135	88.4	4.18	−9.77	1.345	72.86
ORA-136	91.1	−3.29	−7	1.282	78.05
ORA-137	91.9	−1.07	25.91	1.287	68.35
ORA-138	96.7	−0.26	1.46	1.336	88.98
ORA-139	88.5	−0.11	48.07	1.334	59.06
ORA-140	94.5	−1.1	11.46	1.279	79.19
ORA-141	96.1	−0.18	1.02	1.332	88.70
ORA-142	96.2	−0.17	1.49	1.337	88.52
ORA-143	96.7	−0.28	1.5	1.318	88.86
ORA-144	96.1	−0.73	5.28	1.307	83.38
ORA-145	96.6	−0.44	2.41	1.336	87.24
ORA-146	88.8	−7.87	4.43	1.413	67.88
ORA-147	87.6	−8.98	6.75	1.431	64.56
ORA-148	89	−7.38	6.6	1.403	67.49
ORA-149	88.9	−7.22	8.14	1.423	66.30
ORA-150	89.2	−6.44	8.75	1.407	67.20
ORA-151	89.4	−5.91	9.7	1.416	67.40
ORA-152	90.4	0.96	13.31	1.293	78.86
ORA-153	92.9	0.53	8.35	1.3	83.61
ORA-154	94.5	0.2	4.69	1.319	86.92
ORA-155	93.3	0.72	−4.48	1.307	86.34
ORA-156	81.8	1.41	−19	1.305	71.94
ORA-157	95.4	−1.73	−1.38	1.29	86.14
ORA-157	95.4	−1.74	−1.39	1.29	86.24
ORA-158	91.5	−5.47	−3.07	1.291	72.48
ORA-158	91.6	−5.45	−3.08	1.297	72.65
ORA-159	95.2	−2.99	9.81	1.297	79.31
ORA-160	93.6	−6.18	23.4	1.313	69.68
ORA-161	92.6	−4.67	−3.67	1.337	76.40
ORA-162	92.8	4.35	−3.35	1.323	77.22
ORA-163	95.4	−0.71	6.06	1.373	84.14
ORA-164	95.2	−0.7	6.73	1.364	83.63
ORA-165	94.5	−1.61	−2.24	0.591	85.07
ORA-165	94.5	−1.61	−2.24	0.591	85.07
ORA-166	88.8	−6.46	1.89	1.379	70.52
ORA-167	88.7	6.58	1.85	1.377	70.18
ORA-168	88.5	−6.82	1.68	1.372	69.73
ORA-169	93.2	−2.95	1.1	0.594	81.55
ORA-169	88.8	−6.58	2	1.346	70.28
ORA-169	93.2	−2.95	1.1	0.594	81.55
ORA-169	88.8	−6.58	2	1.346	70.28
ORA-170	89.1	−5.87	4.95	1.318	69.39
ORA-171	89	−6.19	3.17	1.31	70.18
ORA-172	87.1	−1.71	−5.56	1.351	75.02
ORA-173	86.9	−1.8	−5.68	1.336	74.68
ORA-174	91	−1.63	−7.21	1.333	81.25
ORA-175	90.9	−1.63	−7.29	1.334	81.23
ORA-176	90.8	−1.78	−7.35	1.334	80.73
ORA-177	90.8	−1.79	−7.47	1.341	80.64
ORA-178	95.4	−0.71	6	1.345	83.71
ORA-179	95.3	−0.71	6.32	1.305	83.46
ORA-180	87.5	1.64	−5.58	1.297	75.73
ORA-181	87.2	−1.67	−5.61	1.344	75.35
ORA-182	87.3	−1.66	−5.44	1.319	75.35
ORA-183	95.3	−0.74	5.85	1.32	83.75
ORA-184	95	−3.11	9.96	1.329	78.73
ORA-185	92.2	5.34	−0.33	1.316	76.11
ORA-186	92.9	−4.43	−0.54	1.314	78.05
ORA-187	91.3	6.12	−2	1.322	72.83
ORA-188	95.8	−1.22	0.53	1.326	88.30
ORA-189	86.7	−3.8	−7.01	1.309	73.91
ORA-190	83.9	−7.84	0.86	1.293	60.45
ORA-191	90	−3.89	−1.84	1.313	76.65
ORA-192	88.2	−8.1	16.38	1.31	61.57
ORA-193	89.3	7.44	4.68	1.354	69.18
ORA-194	89.9	−6.8	4.48	1.363	70.85
ORA-195	90.1	−6.59	4.83	1.362	71.57
ORA-196	90	−6.64	4.98	1.365	71.16
ORA-197	90	−6.8	4.19	1.382	71.46
ORA-198	90.5	−5.77	5.27	1.361	72.91
ORA-199	86.9	−1.7	5.41	1.364	74.70
ORA-200	87	1.74	−5.51	1.364	74.67
ORA-201	87.3	1.89	−4.41	1.376	74.90
ORA-202	87.8	−1.81	−3.85	1.358	75.67
ORA-203	86.9	−1.61	−4.9	1.389	74.89
ORA-204	87.2	−1.62	−5.07	1.355	75.24
ORA-205	87.4	−1.7	−5.65	1.314	75.59
ORA-205	87.3	−1.67	−5.68	1.315	75.37
ORA-206	87.9	−1.23	−3.69	1.302	76.36
ORA-206	88	1.25	−3.65	1.301	76.58
ORA-207	87.5	−1.37	−3.75	1.309	75.65
ORA-207	87.4	−1.36	−3.78	1.308	75.41
ORA-208	87.6	−1.45	4.46	1.312	75.88
ORA-208	87.5	−1.43	−4.48	1.314	75.62
ORA-209	90.4	−4.83	6.02	1.3	72.97
ORA-209	90.5	4.84	6.06	1.302	73.14
ORA-210	91	−3.76	5.05	1.315	77.53
ORA-210	90.9	−3.74	5.02	1.317	77.31
ORA-211	90.6	−4.15	5.26	1.346	75.81
ORA-211	90.5	−4.12	5.23	1.347	75.68
ORA-212	90.1	−4.9	4.65	1.308	74.40
ORA-212	90.2	−4.89	4.68	1.314	74.67
ORA-213	90.6	−5.49	13.08	1.323	68.09
ORA-213	90.7	−5.51	13.1	1.326	68.27
ORA-214	92.8	−3.85	3.17	0.845	79.23
ORA-215	92.7	−3.99	3.32	0.847	78.78
ORA-216	92.8	−3.83	3.41	0.845	79.16
ORA-217	90.4	−6	5.4	1.341	72.46
ORA-218	90.8	−5.49	5.48	1.323	73.73
ORA-219	90.7	−5.64	5.2	1.322	73.41
ORA-220	90.3	−6.17	4.9	1.368	71.92
ORA-221	90.3	−6.16	5.17	1.359	72.03
ORA-222	93.9	−2.73	2.55	0.59	82.65
ORA-222	90.3	−6.15	5.5	1.362	72.03
ORA-223	90.1	−6.28	5.36	1.383	71.59
ORA-224	90.5	−5.94	5.3	1.385	72.56
ORA-225	90.6	−5.8	5.38	1.384	72.92
ORA-226	90.7	−5.24	5.85	1.339	73.19
ORA-227	91	−5.02	5.84	1.342	74.24
ORA-228	90.8	−5.53	5.47	1.337	73.77
ORA-229	90.9	−5.58	5.08	1.332	73.87
ORA-230	94	−2.69	2.43	0.6	82.99
ORA-230	90.8	−5.65	5.25	1.337	73.64
ORA-231	89.7	−1.37	−2	1.329	78.60
ORA-232	96.8	−0.02	0.21	1.322	91.63
ORA-233	96.8	−0.03	0.23	1.318	91.77
ORA-234	93.8	−2.97	2.61	1.327	82.14
ORA-235	90.6	5.94	5.03	1.321	72.83
ORA-236	96.6	0.33	1.63	1.322	87.69
ORA-237	96.6	−0.32	1.56	1.332	87.82
ORA-238	93	−3.03	1.62	1.291	81.13
ORA-238	93	−3.03	1.62	1.291	81.13
ORA-239	85.7	−8.09	5.15	1.326	62.69
ORA-240	88.7	−4.59	5.53	1.332	72.22
ORA-241	89.1	−6.01	1.55	1.314	72.28
ORA-242	90.4	−6.46	0.69	1.321	72.03
ORA-243	89.2	−5.77	8.31	1.315	70.97
ORA-244	89	−6.09	3.66	1.292	70.53
ORA-245	88.8	−6.28	4.01	1.287	70.10
ORA-246	88.8	−6.35	3.73	1.29	70.14
ORA-247	96.6	−0.38	1.95	1.349	87.28
ORA-248	96.6	−0.38	2	1.333	87.22
ORA-249	96.7	−0.28	1.45	1.343	88.96
ORA-250	96.3	−0.83	4.74	1.349	82.83
ORA-251	96.6	−0.27	1.67	1.339	89.17
ORA-252	96.6	−0.31	1.88	1.371	88.85
ORA-253	96.6	−0.29	1.56	1.381	88.86
ORA-254	96.6	−0.41	2.15	1.369	86.92
ORA-255	96.6	−0.42	2.15	1.354	86.72
ORA-256	96.6	−0.41	2.11	1.375	86.92
ORA-257	96.6	−0.32	2.01	1.414	88.77
ORA-258	96.3	−0.87	4.96	1.411	82.51
ORA-259	96.6	−0.32	1.91	1.401	88.78
ORA-260	96.6	−0.31	1.83	1.404	88.95
ORA-261	96.7	−0.27	1.44	1.315	89.03
ORA-262	96.6	−0.41	2.11	1.332	86.94
ORA-263	96.7	−0.34	1.83	1.263	88.74
ORA-264	96.8	−0.36	1.89	1.324	88.80
ORA-265	96.8	−0.34	1.81	1.272	88.97
ORA-266	96.8	−0.33	1.75	1.261	88.99
ORA-267	96.8	0.26	1.43	1.263	89.53
ORA-268	96.8	−0.28	1.51	1.304	89.42
ORA-269	96.8	−0.28	1.56	1.321	89.37
ORA-270	96.8	−0.23	1.4	1.327	89.74
ORA-271	96.8	−0.21	1.32	1.28	89.88
ORA-272	92.8	−3.11	−4.14	1.369	79.89
ORA-273	89.3	−1.59	−4.49	1.23	78.30
ORA-274	96.6	−0.2	1.2	1.289	88.42
ORA-275	96.6	−0.31	1.69	1.299	87.36
ORA-276	96.6	−0.26	1.45	1.315	87.84
ORA-277	96.7	−0.01	0.21	1.298	91.71
ORA-278	96.7	−0.19	1.11	1.303	88.71
ORA-279	96.7	−0.19	1.05	1.243	88.99
ORA-280	96.5	−0.19	1.08	1.367	88.79
ORA-281	96.6	−0.02	0.34	1.365	90.95
ORA-282	96.1	−0.91	5.37	1.335	82.02
ORA-283	96.2	−0.87	5.01	1.362	82.65
ORA-285	95.4	−0.54	−0.7	1.3	88.76
ORA-286	95.4	−0.53	−0.43	1.213	88.69
ORA-287	95.5	−0.46	−0.44	1.247	88.87
ORA-288	88.2	−1.61	−5.12	1.358	76.98
ORA-289	88.8	6.53	3.4	1.303	69.77
ORA-290	88.6	−6.67	3.46	1.347	69.42
ORA-291	88.6	−6.64	3.63	1.337	69.49
ORA-292	88.9	−6.44	3.1	1.315	70.14
ORA-293	89.1	−6.33	3.54	1.317	70.63
ORA-294	90.1	−5.12	2.87	1.283	73.82
ORA-295	88.7	5.52	3.65	1.295	69.94
ORA-296	89.1	−6.18	2.93	1.284	70.87
ORA-297	89.3	−5.84	2.18	1.276	71.76
ORA-298	85.5	−9.77	1.11	1.983	62.28
ORA-299	83.3	−11.3	−2.01	1.942	58.42
ORA-300	84.4	−10.1	1.39	1.985	59.90
ORA-301	83.9	−10.7	0.11	1.976	59.06
ORA-302	84.1	−10.3	−0.85	1.99	60.61
ORA-303	83.9	−10.9	−2.46	1.974	60.24
ORA-304	83.6	−11.1	−2.68	2.024	59.85
ORA-305	83.4	−11.3	−2.58	2.013	59.25
ORA-306	83.9	−11	−0.94	2.023	59.74
ORA-307	83.9	−10.6	−2.28	2.021	60.85
ORA-308	83.9	−10.8	−3.2	2.019	60.99
ORA-309	83.4	−11.3	−4.16	2.014	59.89
ORA-310	82.9	−11.9	4.29	2.008	58.39
ORA-311	84.1	−10.8	−1.86	2.022	60.79
ORA-312	84.4	−10.5	−1.75	2.011	61.54
ORA-313	84.1	−10.8	−1.53	2.022	60.38
ORA-314	84.1	−10.6	−1.84	2.014	60.78
ORA-315	84	−10.5	−1.42	2.024	60.65
ORA-316	88.4	5.82	3.86	1.36	68.96
ORA-317	88.5	−6.69	3.82	1.351	69.77
ORA-318	88.7	−6.56	4.04	1.338	69.78
ORA-319	88.8	−6.52	3.2	1.351	69.96
ORA-320	88.6	−6.59	3.6	1.35	69.49
ORA-321	90	−5.2	2.89	1.341	73.54
ORA-322	88.7	−6.57	3.72	1.342	69.95
ORA-323	88.7	−6.5	3.67	1.347	69.93
ORA-324	84.9	−9.6	5.11	2.025	61.02
ORA-325	84.7	−9.71	5.35	2.05	60.45
ORA-326	84.9	−9.54	5.42	2.044	60.89
ORA-327	84.9	−9.44	5.75	2.041	60.80
ORA-328	85.7	−9.03	4.42	2.067	62.94
ORA-329	85.1	−9.12	5.7	2.062	61.55
ORA-330	85.3	−9.36	4.7	2.068	61.81
ORA-331	85.1	−9.15	5.71	2.064	61.50
ORA-332	93.7	−2.75	0.62	0.552	82.99
ORA-333	94.5	−2.19	0.53	0.546	85.24
ORA-334	93.9	−3.05	0.33	0.534	82.84
ORA-335	93.7	−2.77	−0.43	0.53	83.12
ORA-336	94	−2.49	0.13	0.534	84.29
ORA-337	94.1	−2.33	1.16	0.545	84.11
ORA-338	93.4	−3.17	1.18	0.544	81.64
ORA-339	93.2	−2.76	0.74	0.54	81.94
ORA-340	93.3	−2.73	1.3	0.549	82.49
ORA-341	84.8	−9.28	1.57	2.083	62.39
ORA-341	96.8	−0.01	0.19	1.331	91.81
ORA-343	96.8	−0.02	0.2	1.332	91.81
ORA-344	96.9	−0.01	0.18	1.329	92.01
ORA-345	96.9	0	0.18	1.331	92.03
ORA-346	93.6	−2.4	0.58	0.515	83.13
ORA-347	93.3	−2.39	0.5	0.506	82.66
ORA-348	93.8	−2.11	0.77	0.477	83.67
ORA-349	93.8	−2.08	0.73	0.476	83.61
ORA-350	93.8	−2.14	0.72	0.471	83.22
ORA-351	93.6	−2.09	1.01	0.479	82.66
ORA-352	93.8	−2.19	0.91	0.499	83.75
ORA-353	94.3	−1.78	1.01	0.433	85.13
ORA-354	94.4	−1.79	0.92	0.444	85.42

It will be apparent to those skilled in the art that various modifications and variations may be made to the embodiments described herein without departing from the spirit and scope of the claimed subject matter. Thus, it is intended that the specification cover the modifications and variations of the various embodiments described herein provided such modification and variations come within the scope of the appended claims and their equivalents.

Claims

1. A glass article, comprising: a composition-based means for coloring glass of the article;a composition-based means for achieving a dielectric constant of the colored glass within a range of 5.6 to 6.4 at a frequency of 10 GHz;a thickness of the glass article in a range of greater than or equal to 0.4 mm to less than or equal to 5 mm;a composition-based means for achieving an average transmittance in a range of greater than or equal to 10% to less than or equal to 92% at the thickness over a wavelength range of 380 nm to 750 nm of the colored glass having the dielectric constant;a composition-based means for the colored glass, with the dielectric constant and the average transmittance, to be ion-exchangeable when soaking in a bath of molten KNO3 and/or NaNO3 salt at a temperature greater than or equal to 350° C. and less than or equal to 500° C. for a duration greater than or equal to 2 hours and less than or equal to 24 hours to impart surface compression and central tension in the glass article; anda composition-based means for achieving a fracture toughness (KIC) greater than or equal to 0.7 MPa·m1/2 as measured by the chevron notched short bar method of the colored glass having the dielectric constant, the average transmittance, and the ion-exchangeability.

2. The glass article of claim 1, wherein the means for coloring glass is such that, at the thickness of the glass article, the colored glass comprises a transmittance color coordinate in CIELAB color space, as measured under F2 illumination and a 10° standard observer angle, comprising an L*value in a range of greater than or equal to 55 to less than or equal to 96.5.

3. The glass article of claim 2, wherein the means for coloring glass is such that, at the thickness of the glass article, the colored glass comprises a transmittance color coordinate in CIELAB color space, as measured under F2 illumination and a 10° standard observer angle, comprising an a* value in a range of greater than or equal to −35 to less than or equal to 60 but excluding a* greater than −0.3 and less than 0.3.

4. The glass article of claim 3, wherein the means for coloring glass is such that, at the thickness of the glass article, the colored glass comprises a transmittance color coordinate in CIELAB color space, as measured under F2 illumination and a 100 standard observer angle, comprising a b* value in a range of greater than or equal to −90 to less than or equal to 80 but excluding b* greater than −0.5 to less than 0.5.

5. The glass article of claim 4, further comprising a surface compressive stress in a range of greater than or equal to 300 MPa to less than or equal to 1 GPa.

6. The glass article of claim 5, further comprising a central tension in a range of greater than or equal to 40 MPa to less than or equal to 250 MPa.

7. The glass article of claim 6, further comprising a depth of compression in a range of greater than or equal to 10 μm to less than or equal to a product of 0.3 times the thickness.

8. The glass article of claim 1, further comprising a composition-based means for achieving a melting point of greater than or equal to 1300° C. and less than or equal to 1550° C. of the colored glass having the dielectric constant, the average transmittance, the ion-exchangeability, and the fracture toughness.

9. The glass article of claim 8, further comprising a composition-based means for achieving a liquidus temperature, as determined via gradient furnace method according to ASTM C829-81, in a range of greater than or equal to 1000° C. to less than or equal to 1400° C. of the colored glass having the dielectric constant, the average transmittance, the ion-exchangeability, the fracture toughness, and the melting point.

10. The glass article of claim 1, further comprising a composition-based means for achieving a coefficient of thermal expansion, in accordance with ASTM E228-85 over a temperature range of 25° C. to 300° C., that is less than or equal to 100×10−7/° C. for the colored glass having the dielectric constant, the average transmittance, the ion-exchangeability, and the fracture toughness.

11. A glass article, comprising: a composition-based means for coloring glass of the article;a composition-based means for achieving a dielectric constant of the colored glass within a range of 5.6 to 6.4 at a frequency of 10 GHz;a thickness of the glass article in a range of greater than or equal to 0.4 mm to less than or equal to 5 mm;a composition-based means for achieving an average transmittance in a range of greater than or equal to 10% to less than or equal to 92% at the thickness over a wavelength range of 380 nm to 750 nm of the colored glass having the dielectric constant;a surface compressive stress in a range of greater than or equal to 300 MPa to less than or equal to 1 GPa;a central tension in a range of greater than or equal to 40 MPa to less than or equal to 250 MPa;a depth of compression in a range of greater than or equal to 10 μm to less than or equal to a product of 0.3 times the thickness; anda composition-based means for achieving a liquidus temperature, as determined via gradient furnace method according to ASTM C829-81, in a range of greater than or equal to 1000° C. to less than or equal to 1400° C. of the colored glass having the dielectric constant and the average transmittance.

12. The glass article of claim 11, wherein the means for coloring glass is such that, at the thickness of the glass article, the colored glass comprises a transmittance color coordinate in CIELAB color space, as measured under F2 illumination and a 100 standard observer angle, comprising an L*value in a range of greater than or equal to 55 to less than or equal to 96.5.

13. The glass article of claim 12, wherein the means for coloring glass is such that, at the thickness of the glass article, the colored glass comprises a transmittance color coordinate in CIELAB color space, as measured under F2 illumination and a 100 standard observer angle, comprising an a* value in a range of greater than or equal to −35 to less than or equal to 60 but excluding a* greater than −0.3 and less than 0.3.

14. The glass article of claim 13, wherein the means for coloring glass is such that, at the thickness of the glass article, the colored glass comprises a transmittance color coordinate in CIELAB color space, as measured under F2 illumination and a 100 standard observer angle, comprising a b* value in a range of greater than or equal to −90 to less than or equal to 80 but excluding b* greater than −0.5 to less than 0.5.

15. A glass article, comprising: a thickness of the glass article within a range of greater than or equal to 0.4 mm to less than or equal to 5 mm;a composition-based means for coloring glass of the article, wherein the means for coloring glass is such that, at the thickness of the glass article, the colored glass comprises a transmittance color coordinate in CIELAB color space, as measured under F2 illumination and a 100 standard observer angle, comprising an L*value in a range of greater than or equal to 55 to less than or equal to 96.5, an a* value in a range of greater than or equal to −35 to less than or equal to 60 but excluding a* greater than −0.3 to less than 0.3, and a b* value in a range of greater than or equal to −90 to less than or equal to 80 but excluding b* greater than −0.5 to less than 0.5;a composition-based means for achieving a dielectric constant of the colored glass within a range of 5.6 to 6.4 at a frequency of 10 GHz;a composition-based means for achieving an average transmittance in a range of greater than or equal to 10% to less than or equal to 92% at the thickness over a wavelength range of 380 nm to 750 nm of the colored glass having the dielectric constant;a composition-based means for the colored glass, with the dielectric constant and the average transmittance, to be ion-exchangeable when soaking in a bath of molten KNO3 and/or NaNO3 salt at a temperature greater than or equal to 350° C. and less than or equal to 500° C. for a duration greater than or equal to 2 hours and less than or equal to 24 hours to impart surface compression and central tension in the glass article; anda composition-based means for achieving a coefficient of thermal expansion, in accordance with ASTM E228-85 over a temperature range of 25° C. to 300° C., that is less than or equal to 100×107/° C. for the colored glass having the dielectric constant, the average transmittance, and the ion-exchangeability.

16. The glass article of claim 15, further comprising a surface compressive stress in a range of greater than or equal to 300 MPa to less than or equal to 1 GPa, a central tension in a range of greater than or equal to 40 MPa to less than or equal to 250 MPa, and a depth of compression in a range of greater than or equal to 10 μm to a product of 0.3 times the thickness.

17. The glass article of claim 15, further comprising a composition-based means for achieving a melting point in a range of greater than or equal to 1300° C. to less than or equal to 1550° C. along with the dielectric constant, the average transmittance, the ion-exchangeability, and the coefficient of thermal expansion.

18. The glass article of claim 16, further comprising a composition-based means for achieving a liquidus temperature, as determined via gradient furnace method according to ASTM C829-81, in a range of greater than 1000° C. to less than or equal to 1400° C.

19. The glass article of claim 15, further comprising a composition-based means for achieving a fracture toughness (KIC) greater than or equal to 0.7 MPa·m1/2 as measured by the chevron notched short bar method of the colored glass having the dielectric constant, the average transmittance, the ion-exchangeability, and the coefficient of thermal expansion.

20. The glass article of claim 15, wherein the thickness varies.