This invention relates to razor blades and processes for manufacturing razor blades, and more particularly to colored razor blades.
Razor blades are typically formed of a suitable metallic sheet material such as stainless steel, which is slit to a desired width and heat-treated to harden the metal. The hardening operation utilizes a high temperature furnace, where the metal may be exposed to temperatures greater than 110° C. for up to 10 seconds, followed by quenching.
After hardening, a cutting edge is formed on the blade. The cutting edge typically has a wedge-shaped configuration with an ultimate tip having a radius less than about 1000 angstroms, e.g., about 200-300 angstroms.
Various coatings may be applied to the cutting edge. For example, hard coatings such as diamond, amorphous diamond, diamond-like carbon (DLC) material, nitrides, carbides, oxides or ceramics are often applied to the cutting edge or the ultimate tip to improve strength, corrosion resistance and shaving ability. Interlayers of niobium or chromium containing materials can aid in improving the binding between the substrate, typically stainless steel, and the hard coatings. A polytetrafluoroethylene (PTFE) outer layer can be used to provide friction reduction.
It is important that these coatings be applied, and any other post-hardening processing steps be performed, under sufficiently low temperature conditions so that the hardened, sharpened steel is not tempered. If the steel is tempered it will lose its hardness and may not perform properly during use.
Examples of razor blade cutting edge structures and processes of manufacture are described in U.S. Pat. Nos. 5,295,305; 5,232,568; 4,933,058; 5,032,243; 5,497,550; 5,940,975; 5,669,144; EP 0591334; and PCT 92/03330, which are hereby incorporated by reference.
The present invention provides razor blades that include a colored oxide layer, i.e., an oxide layer having a color different from the color of the underlying blade material, and methods of making such blades. The term “colored” as used herein, includes all colors, including black and white. The colored layer provides a desirable aesthetic effect, without deleteriously affecting the performance or physical properties of the blade. The color of the razor blades can be color-coordinated with the color of the housing of a razor cartridge or the handle or other components of a shaving system. In some preferred implementations, the layer covers substantially the entire blade surface, enhancing the aesthetic effect and simplifying manufacturing. The oxide layers described herein are durable, exhibit excellent adhesion to the blade material, and can be produced consistently and relatively inexpensively.
In one aspect, the invention features a razor blade for use in a wet shaving system, including a blade formed of a metallic sheet material and having a sharpened cutting edge, and a colored layer disposed on at least a portion of the blade.
The invention also features methods of producing colored layers. For example, in one aspect the invention features a method that includes subjecting a blade material to a hardening process; and, during the hardening process, oxidizing the blade material to form an oxide layer on the blade material. The method also includes quenching the blade material, after the oxidizing step, to initiate martensitic transformation of the blade material, and forming the hardened blade material into a razor blade, the oxide layer providing the razor blade with a colored surface. Preferred methods do not deleteriously affect the final properties of the blade.
Some methods may include one or more of the following features. The oxidizing step occurs after austenization of the blade material. The oxidizing step is conducted at a temperature of about 500 to 800° C. The hardening step includes reducing the temperature of the blade material from over 1100° C. during austenization to less than about 800° C. prior to the oxidizing step. Austenization of the blade material and the oxidizing step are conducted in separate chambers the ambient conditions of which can be independently controlled. The method further comprises controlling the ambient conditions under which the oxidizing step is performed. For example, the controlling step may include providing a chamber within which the oxidizing step is performed, and introducing one or more gases to the chamber during the oxidizing step. The gases may be selected from the group consisting of oxygen, mixtures of oxygen and nitrogen, nitrogen oxide, nitrogen dioxide, ozone (O3), water vapor, and mixtures thereof. It is generally preferred that the chamber in which austenization occurs be sufficiently free of oxygen so that the blade material is substantially oxide-free when the oxidizing step begins. By “substantially oxide-free,” we mean that the blade material has sufficiently little oxide on its surface so that a uniform oxidizing reaction, between the hydrogen, oxygen, and stainless steel surface can occur once the steel comes in contact with the oxygen as it enters the oxidation zone. In some implementations the chamber in which austenization occurs is substantially free of oxygen, i.e., contains less than about 500 ppm oxygen, preferably less than 100 ppm oxygen.
In some methods, the forming step includes sharpening the blade material to form a cutting edge. The forming step may also include breaking the slitted blade material into portions having substantially the same length as the razor blade.
The method may further include applying a coating to the cutting edge to enhance the shaving performance of the cutting edge. The coating may be selected, for example, from the group consisting of chromium containing materials, niobium containing materials, diamond coatings, diamond-like coatings (DLC), nitrides, carbides, oxides, and telomers.
In a further aspect, the invention features a wet shaving system that includes a razor including a blade formed of a metallic sheet material and having a sharpened cutting edge, the blade having a colored layer disposed on at least a portion of the blade. The blade may include any of the features discussed above.
The term “colored,” as used herein, refers to a layer having a color that is different from the color of the substrate material prior to oxidization.
The details of one or more embodiments of the invention are set forth in the accompanying drawings and the description below. Other features and advantages of the invention will be apparent from the description and drawings, and from the claims.
Referring to
Blade 10 includes a very thin, e.g., 300 to 2000 Angstrom, colored layer. This layer is not visible in
Referring to
As discussed above, the color of the blade may be coordinated with the color of the housing or handle, or a portion of the housing or handle, to create a pleasing and distinctive aesthetic effect. For example, the color of the oxide layer may be the same as, and/or contrasting or complementary with the color(s) of the housing and/or handle. The color of the oxide layer may also be coordinated with that of elastomeric portions of the cartridge, e.g., the guard.
Blade 10 can be used in other types of razors, for example razors having one, two or three or more blades, or double-sided blades. Blade 10 can be used in razors that do not have movable blades or pivoting heads. The cartridge may either be replaceable or be permanently attached to a razor handle.
A suitable process for forming the colored oxide layer and manufacturing the razor blade is shown diagrammatically in
When the desired sequence of pre-hardening steps has been completed, the blade material is subjected to a hardening process, which includes austenitization of the stainless steel. A typical temperature profile for the hardening process, which is conducted in a tunnel oven, is shown in
After austenization, the strips pass through an oxidation zone, in which the colored oxide layer is grown on the surface of the blade steel. The Forming Gas flows from the hardening furnace into the oxidation zone. An Oxidation Gas (e.g., including oxygen) is introduced to the Forming Gas at a desired point in the oxidation zone (a point at which the strips have reached a temperature suitable for oxidation), and drives the oxidation process. The oxygen may be provided in the form of dry air. The oxidation zone and oxidation conditions (e.g., hydrogen to oxygen ratio) will be discussed in detail below. After the material exits the oxidization zone, it is rapidly quenched, resulting in a martensitic transformation of the stainless steel. Quenching does not deleteriously affect the color of the oxide layer.
The processes described herein may be added to existing blade steel hardening processes, often with minimal changes to the existing process. For example, one existing blade steel hardening process utilizes a high temperature furnace (greater than 1100° C.) containing a flowing Forming Gas. Two parallel continuous stainless steel blade strips are pulled through this high temperature furnace at 36.6 m/min (120 ft/min) each. This high temperature treatment is used to austenitize the stainless steel strips. Near the exit of the high temperature furnace is a water-cooled jacketed tube (also referred to as the water-cooled muffle tube). This section is used to start the cooling process of the stainless steel blade strips. Just after the water-cooled zone, the stainless steel blade strips are pulled through a set of water-cooled quench blocks. The quench blocks initiate the martensitic transformation of the steel. This existing process may be modified to form a colored oxide layer by replacing the water-cooled muffle tube, between the high temperature furnace and the quench blocks, with the oxidization zone referred to above. It is also preferred that the temperature profile of the furnace be modified so that the strips exit the furnace at a temperature less than 800° C., more preferably about 400 to 750° C., e.g., about 600-700° C.
A suitable oxidization zone is shown diagramatically in
The desired color is generally obtained by controlling the thickness and composition of the oxide layer. The thickness and composition of the colored oxide layer will depend on several variables. For example, the thickness of the oxide layer will depend on the temperature of the stainless steel strip when the Oxidation Gas is introduced, and by the hydrogen-to-oxygen ratio of the mixture of Forming Gas and Oxidation Gas in the oxidation zone. The composition, or stoichiometry, of the oxide layer will depend on these same factors, and also on the morphology and surface composition of the strips. Generally, lower temperatures and flow rates will produce gold colors, and higher temperatures and flow rates will produce violet to blue colors. In some implementations, the hydrogen to oxygen ratio is from about 100:1 to 500:1. For a given type of blade material, with the hydrogen to oxygen ratio around the midpoint of this range, an aesthetic deep blue colored oxide will be obtained. Increasing the relative amount of oxygen will tend to result in light blue and light blue-green colors, while decreasing the relative amount of oxygen will tend to result in violet and then gold colors.
The speed at which the material travels through the oxidation zone and the length of the oxidation zone will also affect colorization. Suitable speeds may be, for example, in the range of 15 to 40 m/min.
In some cases, it may be necessary to adjust the process parameters of the hardening and/or oxidation process in order to obtain a consistent end product. The temperature of the strip as it enters the oxidation zone may be controlled by adjusting the temperature of the last zones in the hardening furnace, and/or by the use of heating elements in the oxidation zone. Increasing the temperature of the strip as it enters the oxidation zone will increase the oxide thickness produced in the oxidation zone. When the process is performed using most conventional furnaces, the temperature of the strip as it enters the oxidation zone can be adjusted only when first setting up the process. Since the gas composition of the Oxidizing Gas to the oxidation zone can be quickly adjusted, it is this parameter which is generally used to compensate for variations in the strip material and to fine-tune the oxide color. The exact temperature setting of the last zones of the hardening furnace and the exact composition of the Oxidizing Gas are selected based on, among other factors, the desired color, the size, shape, composition, and speed of the steel strip.
All of the processes described above allow a decorative oxide film to be grown on blade steel during the hardening process, after austenization and prior to the martensitic transformation. If, instead, the blade steel were colorized prior to the hardening process, the color would generally be degraded during the standard hardening process. If a thermal oxide coloration process were employed after the martensitic transformation, it would generally destroy the martensitic properties of the stainless steel strip. The processes described above generally provide highly adherent, protective oxides, while allowing excellent color control and without detrimentally impacting the metallurgic properties of the hardened stainless steel blade strips.
After the hardening process, the blade material is sharpened, to create the cutting edge shown in
In addition to the colored layer, the razor blade may include other features, such as performance enhancing coatings and layers, which may be applied between the sharpening and welding steps.
For example, the tip may be coated with one or more coatings, as discussed in the Background section above. Suitable tip coating materials include, but are not limited to, the following:
Suitable interlayer materials include niobium and chromium containing materials. A particular interlayer is made of niobium having a thickness of from about 100 to 500 angstroms. PCT 92/03330 describes use of a niobium interlayer.
Suitable hard coating materials include carbon-containing materials (e.g., diamond, amorphous diamond or DLC), nitrides (e.g., boron nitride, niobium nitride or titanium nitride), carbides (e.g., silicon carbide), oxides (e.g., alumina, zirconia) and other ceramic materials. Carbon containing hard coatings can be doped with other elements, such as tungsten, titanium or chromium by including these additives, for example, in the target during application by sputtering. The hard coating materials can also incorporate hydrogen, e.g., hydrogenated DLC. DLC layers and methods of deposition are described in U.S. Pat. No. 5,232,568.
Suitable overcoat layers include chromium containing materials, e.g., chromium or chromium alloys that are compatible with polytetrafluoroethylene, e.g., CrPt. A particular overcoat layer is chromium having a thickness of about 100-500 angstroms.
Suitable outer layers include polytetrafluoroethylene, sometimes referred to as a telomer. A particular polytetrafluoroethylene material is Krytox LW 1200 available from DuPont. This material is a nonflammable and stable dry lubricant that consists of small particles that yield stable dispersions. It is furnished as an aqueous dispersion of 20% solids by weight and can be applied by dipping, spraying, or brushing, and can thereafter be air-dried or melt coated. The layer is preferably 100 to 5,000 angstroms thick, e.g., 1,500 to 4,000 angstroms. Provided that a continuous coating is achieved, reduced telomer coating thickness can provide improved first shave results. U.S. Pat. Nos. 5,263,256 and 5,985,459, which are hereby incorporated by reference, describe techniques which can be used to reduce the thickness of an applied telomer layer.
For example, the razor blade tip may include a niobium interlayer, a DLC hard coating layer, a chromium overcoat layer, and a Krytox LW 1200 polytetrafluoroethylene outer coat layer.
The following example is intended to be illustrative and not limiting in effect.
Strips of a stainless steel blade material were heat treated in a high temperature furnace using the hardening temperature profile shown in
To obtain deep blue (minimum reflectivity between 640 nm and 660 nm), the last heated zone of the austenization (high temperature) furnace was lowered to a temperature of 740° C. The entry heated zone temperature, usually set near 1000° C., was increased to 1145° C., to maintain the desired length of higher temperatures within the furnace to obtain the correct amount of austenization. The oxidation zone was attached directly to the exit of the high temperature furnace (including high temperature gasket material). The water-cooled quench blocks (water temperature maintained at 32° C.) were nearly touching the exit of the oxidation zone. The Forming Gas flow rate into the entrance of the high temperature furnace was set at 18.9 L/min (40 scfh). The Oxidation Gas was introduced near the entry end of the oxidation zone as a mixture of air (0.45 L/min) and nitrogen (2.0 L/min). Two stainless steel blade strips were running through the furnace at 36.6 m/min (120 ft/min). The air flow rate was either increased or decreased to “dial-in” the desired oxide color.
To obtain a different color selection, the temperature of the last zone of the high temperature furnace was raised and lowered. The air flow rate was also modified to fine tune both the desired color and the color uniformity. The colors obtained ranged from, beginning with lower temperature and/or lower air flow rate and increasing the temperature and/or air flow rate: “straw” (light gold), to gold, to pink-gold, to deep blue (violet), to blue, to light blue. For lower temperatures and air flow rates (Tset=700° C., air flow at 0.30 L/min), “gold colors” were obtained. For higher temperatures and air flow rates (Tset=740° C., air flow at 0.45 L/min), “blues” were obtained.
Other embodiments are within the scope of the following claims.