Patent Grant
11698567
This application is the U.S. National Stage of PCT/FR2018/052295, filed Sep. 20, 2018, which in turn claims priority to French patent application number 1759138 filed Sep. 29, 2017. The content of these applications are incorporated herein by reference in their entireties.
The present invention relates to the field of electrochemical devices with electrically controllable optical and/or energy properties, which devices are commonly referred to as “electrochromic devices”. More particularly, the invention relates to optical systems incorporating such electrochromic devices and to the associated manufacturing processes. Lastly, the invention relates to processes for modifying the color of such optical devices.
Electrochromic devices have certain characteristics that can be modified under the effect of a suitable electrical supply, between a clear state and a tinted state; more particularly transmission, absorption, reflection of electromagnetic radiation at certain wavelengths, in particular in the visible and/or in the infrared, or even the scatter of light may be modified. The variation in transmission generally occurs in the optical domain (infrared, visible, ultraviolet) and/or in other domains of the electromagnetic spectrum, and hence such devices are said to have variable optical and/or energy properties, the optical domain not necessarily being the only domain concerned.
From the thermal point of view, glazings the absorption of which in at least one portion of the solar spectrum may be modified allow solar flux into the interior of rooms or passenger compartments/cockpits to be controlled when they are employed as exterior architectural glazings or windows of transportation means such as automobiles, trains, airplanes, etc. and excessive heating thereof in the case of bright sunshine to be avoided.
From the optical point of view, they allow degree of vision to be controlled, this allowing glare to be avoided when they are employed as exterior glazings in the case of bright sunshine. They may also have a particularly advantageous shutter effect, both when they are employed as exterior glazings and when they are used as interior glazings, for example as part of interior partitions between rooms (offices in a building) or to isolate compartments in trains or airplanes for example.
In this context, it is known to employ an optical system incorporating an electrochromic device. Despite their advantageous properties, optical systems provided with electrochromic devices have the drawback of having a residual color in transmission, generally a yellow-green hue when the electrochromic device is in the clear state. This color is mainly due to the residual absorption of the electrochromic device, although other components of the optical system also participate in the absorption of incident light.
To mitigate this drawback, there is described in the prior art, which includes patent document WO2012/064510A1, an optical system equipped with an electrochromic device, wherein a layer of a hue substantially complementary to that of the electrochromic material is added. According to the principle of subtracting synthesis of colors, this layer allows the residual color in transmission of the optical device to be at least partially attenuated or, in other words, neutralized.
However, at least one underlying problem remains: the added attenuating layer generates losses in light transmission that, in certain configurations, may significantly decrease the clearness in transmission of the optical system, on account of the substantial amount of light absorbed by the latter. Such as described above, the ability of such a layer to transmit light is directly related to its absorption spectrum and not necessarily to its color. Thus, although there are an infinity of absorption spectra allowing a given chromaticity in transmission to be obtained, the light-transmission values associated with each of these absorption spectra may differ substantially from one spectrum to the next.
More precisely, the visual appearance of a color is a result of three psychosensorial parameters corresponding to the subjective sensations of hue, saturation and brightness. Hue is defined by words such as blue, green, red, etc. Saturation expresses degree of chroma, as opposed to how much white radiation the colored emission contains; the whiter a color appears the lower its saturation. Brightness or lightness is an achromatic factor that is related to the level of the colored stimulus. It varies from a non-dazzling maximum value to the absence of light (black). It is quite easy to understand that by varying these three parameters independently of one another, it is possible to produce any imaginable color sensation. In this context, the various systems for describing a color, for example the CIE 1931 or CIELAB 76 color spaces, are merely different ways of defining the three parameters that describe said color.
In the human eye, these color sensations are described by “integral quantities”. In this respect, perceived chromaticity, a notion encompassing hue and saturation, is the combination of three signals corresponding to three types of color photoreceptors, i.e. the three types of cones, that are present in the retina. Such as illustrated in
The same principles apply to the description of the sensation of light intensity. In this case, the photoreceptors called rods also enter into play. An overall sensitivity to light intensity has been determined for an average human eye. Such as illustrated in
In the rest of the text, for the sake of the description, the visual appearance of the color in transmission and the values of light transmission (TL) are measured according to standard NF EN 410, which is commonly used to determine the luminous and solar properties of glazings employed in the construction industry. Alternatively, the data may also be measured according to other known experimental protocols without however departing from the spirit of the invention.
Confronted with substantial losses in light transmission, a person skilled in the art would be incited to decrease the tint percentage of the attenuating layer, in order to maintain the amount of light absorbed by the latter below an acceptable threshold. This partial solution however remains unsatisfactory since it tends to decrease the chromatic attenuation of the optical system, this remaining the effect first sought.
There is therefore a need to provide an optical system incorporating an electrochromic device the color in transmission of which is modified effectively and reliably, while preserving a satisfactory light-transmission value.
The present invention meets this need. More particularly, in at least one embodiment, the proposed technique relates to a process for modifying the color in transmission of an optical system from an initial state having an initial color (L*i; a*i; b*i) to a final state having a final color (L*f; a*f; b*f), said process being characterized in that it comprises at least one step of modifying the absorbance properties of an optical element of said optical system so that at least 50% of the total absorption of this element occurs in an effective absorption range defined so that a variation in absorption by the optical system of any amount of light at a wavelength λ comprised in said effective absorption range generates a variation ΔC(λ) in chromaticity distance (Ci, C(λ)) smaller than 0, where:
ΔC(λ)=C(λ)−Ci=√{square root over ((a*(λ)−a*ref)2+(b*(λ)−b*ref)2)}−√{square root over ((a*i−a*ref)2+(b*i−b*ref)2)}
In the present text, the notion of color encompasses the three psychosensorial parameters employed in the establishment of its visual appearance, namely brightness, hue and saturation, the latter two parameters possibly being grouped together in the notion of chromaticity. The expression “optical element” is understood to mean an element that is at least partially transparent and that is intended to be arranged on the optical path of an incident ray passing through the optical system. This optical system may consist of a succession of transparent sheets of vitrified or plastic material, that include a substrate and a counter substrate. According to particular embodiments, certain of these sheets are separated from each other by a closed space filled with inert gas.
The invention is based on a novel and inventive concept consisting in providing a process allowing the initial color in transmission of an optical system to be modified, while preserving a satisfactory value of light transmission or in other words, clearness.
Concretely, such a process for adapting an optical system to particular transmission conditions may take the form of a process for modifying an already existing optical system, by modifying the absorbance properties of one of its optical elements. It will be noted that this modification of the absorbance properties may be achieved by replacing the targeted optical element, by modifying its intrinsic properties and/or by adding a colored coating. Alternatively, the subject matter of the invention may take the form of a process for manufacturing an optical system in which the absorbance properties of at least one of its optical elements have already been modified, compared to a known prior-art optical system.
A process according to the invention allows the initial color of an optical system to be modified, this initial color having as components an initial lightness and an initial chromaticity, with the objective of obtaining a reference color having, in particular, a reference chromaticity value. The color finally obtained after implementation of the process is called the “final color”.
In the present text, the chromaticity distance C is the distance between the chromaticity of the reference color, also called the “objective”, and the chromaticity of a color in question, called the “counter-objective”, for example the initial color or the color obtained after any variation in the amount of light absorbed at a wavelength λ. The variation ΔC(λ) in this chromaticity distance generated by this variation in the amount of light absorbed by the optical system at the wavelength λ expresses the capacity of the optical system to get closer to the desired chromaticity in transmission, i.e. to the reference chromaticity, by absorbing light at a wavelength λ. A negative ΔC(λ) value expresses a variation in chromaticity, after absorption of light at a wavelength λϵ[λmin; λmax], allowing the initial chromaticity to be brought closer to the one desired, the obtained chromaticity being “closer” to the desired chromaticity than the initial chromaticity. In contrast, the obtainment of a positive ΔC(λ) value, after absorption of light at a given wavelength λ not comprised in [λmin; λmax], expresses an increase in the distance between the desired chromaticity, i.e. the reference chromaticity, and the initial chromaticity.
A process according to the invention is based on the use of an effective absorption range [λmin; λmax] defined using the variation ΔC(λ) in chromaticity distances of the optical system, i.e. the variation generated by the variation in absorption, at a wavelength λ, of any amount of light. More precisely, this effective absorption range [λmin; λmax] is defined so that ΔC(λ) is lower than 0, and therefore corresponds to an absorption wavelength range in which the variation in color of the optical system corresponds to the sought after effect, at least from a chromatic point of view.
A process according to the invention is in addition based on the notion of total absorption of the optical element in question. This total absorption is an integral value corresponding to the amount of light absorbed by the optical element in question over the entirety of its absorption spectrum. The criterion according to which “at least 50% of the total absorption of the optical element in question is comprised in the effective absorption range” therefore corresponds to a requirement of “color purity”, according to which at least 50% of the absorption achieved by the optical element such as modified is dedicated to a chromatic variation tending towards the reference color. It is to be noted that any absorption achieved outside of this effective absorption range will necessarily need to be corrected with the objective of obtaining the desired chromaticity, for example by adding additional filters, this possibly generating additional losses in transmission that it is quite rightly desired to avoid. Taking into consideration the aforementioned criterion therefore makes it possible to combine the notions of effectiveness of the chromatic variation of an optical system on the one hand, and of limitation of losses in light transmission on the other hand.
According to one particular embodiment, said optical system comprises at least one electrochemical functional system with electrically controllable optical and/or energy properties, which preferably comprises at least one ionically conductive layer arranged between a first electrode coating and a second electrode coating, the at least one electrochemically active layer being suitable for passing reversibly between a first state and a second state having optical and/or energy transmission properties different from the first state.
According to one particular embodiment, said ionically conductive layer is said optical element of said optical system the absorbance properties of which are modified.
According to one particular embodiment, said optical system comprises at least the following optical elements:
a functional assembly comprising a substrate of glazing function, on which substrate said electrochemical functional system with electrically controllable optical and/or energy properties is formed, and
a lamination interlayer, which is preferably made of polymer and more preferably of PVB, and which is interposed between the functional assembly and a counter-substrate of glazing function.
It is to be noted that the interposition of the lamination interlayer between the functional assembly and the counter-substrate does not necessarily mean that these three elements make direct contact with one another. The term “between” here refers to the order of arrangement of these various optical elements. Thus, the latter may for example be physically separated by one or more layers, for example forming the electrochemical functional system. When used as an exterior glazing, the counter-substrate is intended to be positioned toward the exterior of a building, on the side of the incident solar light.
According to one particular embodiment, said process comprises a step of determining said effective absorption range [λmin; λmax], preferably using a representation of the chromatic variations (Δa*(λ); Δb*(λ)) in transmission and of the variations ΔTL(λ) in losses in light transmission generated as a function of the wavelength λ at which said optical system undergoes a variation in the amount of light absorbed.
According to one particular embodiment, said reference chromaticity value (a*ref; b*ref) has a saturation value of zero.
Such a process aims to decrease the saturation of a color or, in other words, to attenuate it. A point having a saturation value of zero will be grey, white or black, depending on the lightness. In the context of an application to an optical system of glazing function, a zone of zero saturation in transmission has no hue, and therefore the advantage of not adversely affecting the hue of the light rays transmitted from the exterior.
According to one alternative embodiment, the targeted chromaticity value has a non-zero saturation and therefore corresponds to one particular color to be obtained in transmission, whether this be for reasons of technical and/or esthetic nature.
According to one particular embodiment, said optical element is modified so that its absorption spectrum is substantially centered on a wavelength at which the ratio ΔC(λ)/ΔTL(λ) is maximal, where:
The spectral transmittance of the optical system varies with the ratio ΔC(λ)/ΔTL(λ). Thus, assuming that the variation ΔTL(λ) is smaller than 0, the higher the value of ΔC(λ)/ΔTL(λ), the better the system transmits the incident light at an absorption wavelength λ. In other words, the increase in ΔC(λ)/ΔTL(λ) allows the losses in transmission generated by the optical system to be decreased.
Thus, surprisingly, it has been established that the overall loss in transmission may be minimal for an absorption achieved at an absorption wavelength located in the wavelength range in which the eye is the most sensitive. This result goes against a technical prejudice accepted up to now, namely that it is recommended to avoid absorbing transmitted light in a spectral region in which the human eye is the most sensitive, in order to limit losses ΔTL in light transmission. Contrary to received ideas, it has therefore been established by the inventors that, with a view to modifying the color in transmission of an optical system while preserving a satisfactory clearness, it is more important to take into account the ratio ΔC(λ)/ΔTL(λ) than to consider in isolation solely the variation in light transmission TL(λ) of the system.
According to one particular embodiment, said optical element is modified so that at least 55%, preferably at least 60%, preferably at least 65%, and preferably at least 70% of its total absorption is comprised in said effective absorption range [λmin; λmax].
An optical system obtained by means of such a process has a higher spectral transmittance, and therefore allows losses in transmission to be decreased.
According to one particular embodiment, the modifying step comprises coloring the bulk of said optical element to be modified and/or depositing a colored coating on at least one of the faces of said optical element to be modified.
According to one particular embodiment, said process comprises at least one preliminary step of measuring the spectrum in transmission of said optical system.
Such a spectrum measurement is for example carried out using a spectrophotometer. On the basis of this measurement, it is possible to determine the initial chromaticity value of the optical system, for example using a color space such as the CIE XYZ (1931) system.
According to one particular embodiment, the invention also relates to an optical system the color of which has been modified by a process such as described above.
According to one particular embodiment, the invention also relates to an optical system comprising:
a first optical element that has what is called an “initial” color (L*i; a*i; b*i) in transmission,
a second optical element that is such that the optical system (1) has what is called a “final” color (L*f; a*f; b*f) in transmission, and that is characterized in that at least 50% of the total absorption of this second optical element is comprised in an effective absorption range [λmin; λmax] defined so that a variation in absorption by the optical system of any amount of light at a wavelength λ comprised in said effective absorption range [λmin; λmax] generates a variation ΔC(λ) in chromaticity distance (Ci, C(λ)) smaller than 0, where:
ΔC(λ)=C(λ)−Ci=√{square root over ((a*(λ)−a*ref)2+(b*(λ)−b*ref)2)}−√{square root over ((a*i−a*ref)2+(b*i−b*ref)2)}
According to one particular embodiment, said optical system comprises at least one electrochemical functional system with electrically controllable optical and/or energy properties, which preferably comprises at least one ionically conductive layer arranged between a first electrode coating and a second electrode coating, the at least one electrochemically active layer being suitable for passing reversibly between a first state and a second state having optical and/or energy transmission properties different from the first state.
According to one particular embodiment, said electrochemical functional system with electrically controllable optical and/or energy properties is formed on that face of the substrate which is opposite the lamination interlayer.
According to one particular embodiment, said optical system comprises at least the following optical elements:
a functional assembly comprising a substrate of glazing function, on which substrate an electrochemical functional system with electrically controllable optical and/or energy properties, preferably an electrochromic device, is formed, and
a lamination interlayer, which is preferably made of polymer and more preferably of PVB, and which is interposed between the functional assembly and a counter-substrate of glazing function.
According to one particular embodiment, said optical system comprises a reflection-controlling coating, which is preferably made of silicon nitride (SiNx), in order to modify, and preferably attenuate, the color of the optical system in reflection toward one of the sides of said optical system.
The adaptation of the optical system with a view to modifying its color in transmission, or that of a constituent first optical element, generally generates a modification of its color in reflection. The use of a coating for controlling this color in reflection allows the characteristics thereof to be modified, and preferably it to be attenuated, from the point of view of an of the observer positioned opposite the electrochromic system, with respect to said coating.
According to one particular embodiment, said reflection-controlling coating is arranged between said functional assembly and said counter substrate.
Thus arranged, said reflection-controlling coating not only allows the color of the optical system in reflection to be modified from the point of view of an observer positioned on the exterior, but also the amount of exterior light transmitted by the optical system to be increased or, in other words, the overall losses in transmission to be decreased. In this configuration, an interference effect between said optical element suitable for modifying the color in transmission of said optical system and said reflection-controlling coating allows reflection to be decreased, and therefore transmission to be increased, in particular at the wavelengths at which the eye is most sensitive.
The invention also relates to a process for manufacturing an optical system such as described above.
The invention in addition relates to the use of such an optical system as an architectural glazing, in particular an exterior glazing of an internal partition or glazed door, as a glazing in the windows or the internal partitions of transportation means such as trains, airplanes, automobiles, boats and ships, as glazings for display screens such as computer screens or television screens, for spectacles or the objectives of cameras or to protect solar panels.
Other features and advantages of the invention will become apparent on reading the following description of particular embodiments, which are given by way of simple nonlimiting illustrative examples, and the appended figures, in which:
In the various figures, unless otherwise indicated, the same reference numbers have been used to reference elements that are similar or identical.
The various elements illustrated by the figures are not necessarily shown to actual scale, the accent more being placed on the representation of the general operation of the invention.
A plurality of particular embodiments of the invention are described below. It will be understood that the present invention is in no way limited by these particular embodiments and that other embodiments may perfectly well be implemented.
According to one particular embodiment and such as illustrated in
a functional assembly 2 comprising a substrate 3 of glazing function, on which substrate a functional electrochemical system 4 with electrically controllable optical and/or energy properties is formed, said electrochemical functional system 4 comprising at least one ionically conductive layer arranged between a first electrode coating and a second electrode coating, the least one ionically conductive layer being suitable for reversibly passing between a first state and a second state having different optical and/or energy transmission properties from the first state, and
a lamination interlayer 5 made of PVB, interposed between the functional assembly 2 and a counter-substrate 6 of glazing function.
In particular, this optical system 1 comprises:
a first optical element that has what is called an “initial” color (L*i; a*i; b*i) in transmission,
a second optical element that is such that the optical system 1 has what is called a “final” color (L*f; a*f; b*f) in transmission, and that is characterized in that at least 50% of the total absorption of this second optical element is comprised in an effective absorption range (λmin; λmax) defined so that a variation in absorption by the optical system 1 of any amount of light at a wavelength λ comprised in the effective absorption range [λmin; ×max] generates a variation ΔC(λ) in chromaticity distance (Ci, C(λ)) smaller than 0.
According to this particular embodiment, the electrochemical functional system 4 with electrically controllable optical and/or energy properties is formed on that face of the substrate 3 which is opposite the lamination interlayer 5. According to one alternative embodiment, this functional system may be interposed between the substrate 3 and the lamination interlayer 5.
According to one particular embodiment and such as illustrated in
According to alternative embodiments, the optical system 1 may adopt various glazing configurations in which the various optical elements are organized along the optical axis X:
single glazing in which two sheets of glazing function, the substrate 3 and the counter-substrate 6, are laminated into a single glazing: (exterior of a building) counter-substrate 6/lamination interlayer 5/functional assembly 2 comprising the substrate 3 (building interior);
double glazing, shown in
triple glazing in which two among four glass sheets, the substrate 3 and the counter-substrate 6, are laminated together: (exterior of a building) counter-substrate 6/lamination interlayer 5/functional assembly 2 comprising the substrate 3/cavity filled with an inert gas/glass sheet/cavity filled with an inert gas/low-E layer/glass sheet (building interior).
Generally, the glazing comprises a laminated glazing. This laminated glazing is intended to be placed on the exterior side of the building. By double glazing what is meant is an assembly of two glazings spaced apart and separated by a gas-filled or vacuum-filled cavity, and by triple glazing what is meant is an assembly of three glazings spaced apart and separated by two respective gas- or vacuum-filled cavities. As described above, at least one of the spaced-apart glazings of a multiple glazing may be laminated. In all these configurations, the counter-substrate 6 is intended to be positioned toward the exterior.
It will be noted that the electrochromic device included in the optical system 1 according to the invention may include one or more transparent conductive coatings such as SnO2:F or ITO and/or one or more networks of conductors such as metal wires. The electrochemically active layer and the one or more layers of electrolyte may take the form of a gel solution and/or of an ionically conductive polymer and/or of one or more mineral layers deposited by magnetron cathode sputtering, CVD or the sol-gel process, without departing from the spirit of the invention.
An optical system 1 according to the invention makes it possible to combine the notions of effectiveness of the chromatic variation on the one hand, and of limitation of losses in light transmission on the other hand. This advantageous optical system 1 may in particular be obtained by implementing a process for modifying its color in transmission, from an initial color (L*i; a*i; b*i) to a final color (L*f; a*f; b*f), such as described in more detail in the rest of the text and illustrated in
In a first step (S1), the spectrum in transmission of the optical system 1 is measured using a spectrophotometer or any other known device of equivalent function.
On the basis of this measurement, the initial chromaticity value (a*i; b*i) in transmission of the optical system is determined (step S2), for example using a known color space such as the CIE XYZ (1931) system.
According to one particular embodiment, and such as illustrated in
Thus, in the example illustrated in
Subsequently, the initial chromaticity distance Ci, between this initial chromaticity value (a*i; b*i) in transmission and a given reference chromaticity value (a*ref; b*ref) is determined (step S3). This given reference value relates to a reference color that it is sought to obtain. It differs from the “final color” that is obtained at the end of the modifying process. The initial chromaticity distance Ci, corresponds to the norm of the vector extending from the initial chromaticity point (a*i; b*i) to the chosen reference chromaticity point (a*ref; b*ref).
According to the particular embodiment illustrated in
Ci=√{square root over ((a*i)2+(b*i)2)}
According to one alternative embodiment, the chosen reference chromaticity value (a*ref; b*ref) has a non-zero saturation and therefore corresponds to a particular color to be obtained in transmission, whether this be for reasons of technical and/or esthetic nature. According to this alternative embodiment, the initial chromaticity distance Ci satisfies the following equation:
Ci=√{square root over ((a*i−a*ref)2+(b*i−b*ref)2)}
The variation ΔC(λ) in this chromaticity distance between the initial chromaticity value (a*i; b*i) and a chromaticity value (a*(λ); b*(λ)) in transmission obtained following a variation in absorption at the wavelength λ, which value is represented by a triangle, expresses the capacity of the optical system 1 to get closer to the desired chromaticity in transmission, i.e. to the reference chromaticity. Thus, this variation ΔC satisfies the following equation:
ΔC(λ)=C(λ)−Ci=√{square root over ((a*(λ)−a*ref)2+(b*(λ)−b*ref)2)}−√{square root over ((a*i−a*ref)2+(b*i−b*ref)2)}
A negative ΔC(λ) value expresses a variation in chromaticity, after absorption of light at a wavelength λ, allowing the initial chromaticity to be brought closer to the one desired, the obtained chromaticity being “closer” to the desired chromaticity than the initial chromaticity. In contrast, the obtainment of a positive ΔC(λ) value, after absorption of light at a given wavelength λ, expresses an increase in the distance between the desired chromaticity, i.e. the reference chromaticity, and the initial chromaticity.
It will be noted that the choice of a SAGE™ electrochromic double glazing is purely arbitrary. Thus, a graphical representation similar to that of
To return to the subject of
With regard to the CIE L*a*b* color space illustrated in
The chromatic variations in transmission (Δa*(λ); Δb*(λ)) may respectively be defined using the following equations:
Δa*(λ)=a*(λ)−a*i
Δb*(λ)=b*(λ)−b*i
With regard to these two equations, to the aforementioned one defining ΔC(λ), and to the known values of a*i, a*ref, b*i and b*ref, it is easy to calculate the variation ΔC(λ) in chromaticity distance affecting the optical system 1.
In a following step (S4), using
With regard to the chromatic variations Δa*(λ); Δb*(λ)) in transmission of an optical device 1 as a function of absorption wavelengths, such as illustrated in
According to one particular embodiment, the effective absorption range [λmin; λmax] is determined so that the value of the ratio ΔC(λ)/ΔTL(λ) is maximal. The spectral transmittance of the optical system varies with the ratio ΔC(λ)/ΔTL(λ). Thus, assuming that the variation ΔTL(λ) is smaller than 0, the higher the value of ΔC(λ)/ΔTL(λ), the better the transmission of the incident light by the system at an absorption wavelength λ. In other words, the increase in ΔC(λ)/ΔTL(λ) allows the losses in transmission generated by the optical system to be decreased.
Surprisingly, it has been determined in the case of the example illustrated in
Following the determination of the effective absorption range [λmin; λmax] (step S4), the absorbance properties of an optical element of said optical system 1 are modified (step S5) so that at least 50% of the total absorption (A) of this element is achieved in an effective absorption range [λmin; λmax] defined so that a variation in absorption by the optical system 1 of any amount of light at a wavelength λ comprised in said effective absorption range [λmin; λmax] generates a variation ΔC(λ) in chromaticity distance (Ci, C(λ)) smaller than 0.
It will be noted that this modification of the absorbance properties may be achieved by replacing the targeted optical element, by modifying its intrinsic properties and/or by adding a colored coating. Alternatively, the subject matter of the invention may take the form of a process for manufacturing an optical system in which the absorbance properties of one of its optical elements have already been modified, compared to a known prior-art optical system. Thus, according to this particular embodiment, the invention relates to a process for manufacturing an optical system 1 that comprises:
a first optical element that has what is called an “initial” color (L*i; a*i; b*i) in transmission,
a second optical element that is such that the optical system 1 has what is called a “final” color (L*f; a*f; b*f) in transmission, and that is characterized in that at least 50% of the total absorption of this second optical element is comprised in an effective absorption range (λmin; λmax) defined so that a variation in absorption by the optical system 1 of any amount of light at a wavelength λ comprised in the effective absorption range [λmin; λmax] generates a variation ΔC(λ) in chromaticity distance (Ci, C(λ)) smaller than 0.
It will be noted that tinting a PVB so that at least one preset portion of its total absorption (A) is comprised in a preset wavelength range presents no particular technical difficulty, providing of course that these two parameters are judiciously determined/chosen beforehand, this being, inter alia, the crux of the invention.
Alternatively or in combination, the modification (S5) of the absorbance properties of an optical element of the optical system 1 is achieved via the addition, to the material, of semiconductor or metal nanoparticles and/or the deposition of a colored coating on at least one of the faces of the optical element 1 to be modified.
It will be noted that according to particular embodiments, the absorbance properties of one or more elements of the optical system 1 may alternatively or in combination be modified.
Thus, and according to one particular embodiment, the ionically conductive layer integrated into the electrochromic device is or forms part of the optical elements the absorbance properties of which are modified.
In addition, the choice of the desired portion of the total absorption (A) comprised in the effective absorption range [λmin; λmax] may differ from one embodiment to the next without however departing from the spirit of the invention.
In order to observe the reproduction of the present invention by an optical system 1 comprising at least one optical element the absorbance properties of which have been modified, it is possible to proceed as follows:
It will be noted that the spectrum in transmission of said optical system before modification may already be known, since it is that of a standard optical system, and/or be determinable by replacement of said modified optical element with a standard optical element and subsequent measurement of the spectrum in transmission of the optical system incorporating this standard replacement element. By “standard optical element” what is meant is an optical element having a negligible influence on the obtained spectrum in transmission of the optical system.
The values described in the present text must not be understood as being strictly limited to the mentioned numerical values. Rather, unless otherwise indicated, each value designates both the exactly mentioned value and a range of functionally equivalent values encompassing this value.
Although particular embodiments of the present invention have been illustrated and described, it is obvious that various other changes and modifications may be made within the spirit and scope of the invention. The present text is therefore intended to cover in the appended claims any modification falling within the scope of the present invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 1759138 | Sep 2017 | FR | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/FR2018/052295 | 9/20/2018 | WO |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2019/063911 | 4/4/2019 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 5792559 | Heithoff et al. | Aug 1998 | A |
| 20170192257 | Branda et al. | Jul 2017 | A1 |
| Number | Date | Country |
|---|---|---|
| WO 2012064510 | May 2012 | WO |
| Entry |
|---|
| International Search Report as issued in International Patent Application No. PCT/FR2018/052295, dated Jan. 18, 2019. |
| Number | Date | Country | |
|---|---|---|---|
| 20200225550 A1 | Jul 2020 | US |