Component for machine structural use and method for making the same

Abstract

A component for machine structural use having improved fatigue strength. The component for machine structural use is produced by subjecting at least a part of a steel material to hardening, and the hardened structure is controlled such that the average grain diameter of former austenitic grains is 12 μm or less and the maximum grain diameter does not exceed four times the average grain diameter.

Description

TECHNICAL FIELD

The present invention relates to components for machine structural use, components having hardened layers formed by high-frequency hardening in at least part of the components. Examples of the components for machine structural use described herein include drive shafts, input shafts, output shafts, crankshafts, inner and outer races of constant velocity joints, hubs, and gears for automotive vehicles.

BACKGROUND ART

Components for machine structural use, e.g., drive shafts and constant velocity joints for automotive vehicles, have been manufactured by the following method: A hot-rolled steel bar is processed into a predetermined shape by hot-forging, cutting, cold forging, or the like, followed by high-frequency hardening and tempering. In general, by this method, the fatigue strengths important for the components for machine structural use, e.g., torsional fatigue strength, bending fatigue strength, rolling fatigue strength, and sliding-rolling contact fatigue strength are attained.

Meanwhile, the demand for light-weight automobile components is on an increase in recent years because of the environmental concerns, and thus a further improvement on the fatigue strengths of automobile components is required.

There have been many proposed methods for improving the fatigue strength such as one described above.

For example, one possible approach for increasing the torsional fatigue strength is to increase the depth of hardening by the high-frequency hardening. Although the depth of hardening may be increased, the fatigue strength is saturated at a certain depth.

It is also effective to increase the grain boundary strength to increase the torsional fatigue strength. From this standpoint, a technology has been suggested which reduces the former austenitic grain diameter by dispersion of TiC. For example, the technology set forth in Patent Document 1 reduces the former austenitic grain diameter by dispersing a large amount of fine TiC during heating for high-frequency hardening. However, this technology requires solid solution treatment of TiC prior to the hardening and includes a hot-rolling step of heating the workpiece to a temperature of not less than 1,100° C. Thus, the heating temperature needs to be high during the hot rolling, and the production efficiency is disadvantageously low.

Moreover, the technology disclosed in Patent Document 1 above cannot sufficiently comply with the recent requirements on the fatigue strengths.

Patent Document 2 sets forth a shaft component for machine structural use, in which the torsional fatigue strength is increased by limiting the ratio (CD/R) of the depth CD of the hardened layer to the radius R of the shaft component subjected to the high-frequency hardening to 0.3 to 0.7 and then by adjusting the value A according to the amount of carbon, the value A being defined by the austenitic grain diameter γf within a depth of 1 mm from the surface after the high-frequency hardening, the average Vickers hardness Hf within (CD/R)=0.1 before the high-frequency hardening, and the average Vickers hardness Hc of the central portion of the shaft after the high-frequency hardening.

However, even when the CD/R is controlled, there is a limit to the improvement of the fatigue properties. This technology also fails to sufficiently comply with the recent requirement on the torsional fatigue strength.

Patent Document 1: Japanese Unexamined Patent Application Publication No. 2000-154819 (Claims)

Patent Document 2: Japanese Unexamined Patent Application Publication No. 8-53714 (Claims)

DISCLOSURE OF INVENTION

The present invention has been made based on the above-described situations and aims to provide a component for machine structural use with a higher fatigue strength and an advantageous method for manufacturing the component.

The inventors have vigorously pursued studies particularly on high-frequency hardened structures to effectively improve the above-described fatigue properties.

The inventors have focused attention on the grain diameter distribution of the former austenitic grains of a high-frequency hardened structure and found that the fatigue properties, such as torsional fatigue strength, bending fatigue strength, and rolling fatigue strength, can be improved by reducing the average grain diameter and the maximum grain diameter of the former austenitic grains.

The structure of the present invention can be summarized as follows:

1. A component for machine structural use, including a steel material at least part of which is subjected to hardening, wherein the hardened structure has an average diameter of former austenitic grains of 12 μm or less and a maximum grain diameter not exceeding four times the average grain diameter.

2. The component for machine structural use according to item 1, including a composition containing, in terms of percent by mass:

C: 0.3% to 1.5%

Si: 0.05% to 3.0%

Mn: 0.2% to 2.0%

and satisfying formula (1): C^1/2(1+0.7Si)(1+3Mn)>2.0   (1) wherein the balance is Fe and inevitable impurities.

3. The component for machine structural use according to item 2, the composition further containing, in terms of percent by mass:

Al: 0.25% or less.

4. The component for machine structural use according to item 2 or 3, the composition further containing, in terms of percent by mass, at least one selected from among:

Cr: 0.03% to 2.5%

Mo: 0.05% to 1.0%

Cu: 0.03% to 1.0%

Ni: 0.05% to 2.5%

Co: 0.01% to 1.0%

V: 0.01% to 0.5%

W: 0.005% to 1.0%

and satisfying formula (2): C^1/2(1+0.7Si)(1+3Mn)(1+2.1Cr)(1+3.0 Mo)(1+0.4 Cu)(1+0.3Ni)(1+5.0V)(1+0.5W)>2.0   (2) instead of formula (1).

5. The component for machine structural use according to item 2, 3, or 4, the composition containing, in terms of percent by mass, at least one selected from among:

Ti: 0.005% to 0.1%

Nb: 0.005% to 0.1%

Zr: 0.005% to 0.1%

B: 0.0003% to 0.01%

Ta: 0.02% to 0.5%

Hf: 0.02% to 0.5%

Sb: 0.005% to 0.015%

and satisfying formula (3): C^1/2(1+0.7Si)(1+3Mn)(1+2.1Cr)(1+3.0 Mo)(1+0.4 Cu)(1+0.3Ni)(1+5.0V)(1+1000B)(1+0.5W)>2.0   (3) instead of formula (1) or (2).

6. The component for machine structural use according to item 2, 3, 4, or 5, the composition further containing, in terms of percent by mass, at least one selected from among:

S: 0.1% or less

Pb: 0.01% to 0.1%

Bi: 0.01% to 0.1%

Se: 0.003% to 0.1%

Te: 0.003% to 0.1%

Ca: 0.0001% to 0.01%

Mg: 0.0001% to 0.01%

REM: 0.0001% to 0.1%.

7. A method for making a component for machine structural use, including subjecting at least part of a steel material to high-frequency heating at least once, the steel material containing one or both of a fine bainite structure and a fine martensite structure in a total of 10 percent by volume, wherein the high-frequency heating is conducted at a heating rate of at least 400° C./s and an ultimate temperature of 1,000° C. or less.

8. The method for making the component for machine structural use according to item 7, wherein the steel material is worked through: a hot-working step in which a total processing ratio at 800° C. to 1,000° C. is 80% or more; a cooling step subsequent to the hot-working step, in which the cooling rate is 0.2° C./s or more in the temperature range of 700° C. to 500° C.; and a secondary working step of either effecting 20% or more of working in a temperature range of 700° C. to less than 800° C. before the cooling step or effecting 20% or more of working in a temperature range of up to the A₁ transformation temperature subsequent to the cooling step.

9. The method for making the component for machine structural use according to item 7 or 8, wherein a retention time at 800° C. or more in the high-frequency heating is 5 seconds or less at a time.

10. The method for making the component for machine structural use according to any one of items 7 to 9, the steel material including, in terms of percent by mass,

C: 0.3% to 1.5%

Si: 0.05% to 3.0%

Mn: 0.2% to 2.0%

and satisfying formula (1): C^1/2(1+0.7Si)(1+3Mn)>2.0   (1) wherein the balance is Fe and inevitable impurities.

11. The method for making the component for machine structural use according to item 10, the steel material further including:

Al: 0.25% or less.

12. The method for making the component for machine structural use according to item 10 or 11, the steel material further including, in terms of percent by mass, at least one selected from among:

Cr: 0.03% to 2.5%

Mo: 0.05% to 1.0%

Cu: 0.03% to 1.0%

Ni: 0.05% to 2.5%

Co: 0.01% to 1.0%

V: 0.01% to 0.5%

W: 0.005% to 1.0%

and satisfying formula (2): C^1/2(1+0.7Si)(1+3Mn)(1+2.1Cr)(1+3.0 Mo)(1+0.4 Cu)(1+0.3Ni)(1+5.0V)(1+0.5W)>2.0   (2) instead of formula (1).

13. The method for making the component for machine structural use according to item 10, 11, or 12, the steel material further including, in terms of percent by mass, at least one selected from among:

Ti: 0.005% to 0.1%

Nb: 0.005% to 0.1%

Zr: 0.005% to 0.1%

B: 0.0003% to 0.01%

Ta: 0.02% to 0.5%

Hf: 0.02% to 0.5%

Sb: 0.005% to 0.015%

and satisfying formula (3): C^1/2(1+0.7Si)(1+3Mn)(1+2.1Cr)(1+3.0 Mo)(1+0.4 Cu)(1+0.3Ni)(1+5.0V)(1+1000B)(1+0.5W)>2.0   (3) instead of formula (1) or (2).

14. The method for making the component for machine structural use according to item 10, 11, 12, or 13, the steel material further including, in terms of percent by mass, at least one selected from among:

S: 0.1% or less

Pb: 0.01% to 0.1%

Bi: 0.01% to 0.1%

Se: 0.003% to 0.1%

Te: 0.003% to 0.1%

Ca: 0.0001% to 0.01%

Mg: 0.0001% to 0.01%

REM: 0.0001% to 0.1%.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a front view of a representative example of a shaft.

FIG. 2 shows schemes of fatigue test and includes FIG. 2(a) showing a scheme of shaft torsional fatigue test and FIG. 2(b) showing a scheme of rolling fatigue test.

FIG. 3 is an optical microscope image of a hardened structure.

FIG. 4(a) and FIG. 4(b) are each a graph showing the relationship between the average former austenitic grain diameter and the torsional fatigue strength.

FIG. 5(a) and FIG. 5(b) are each a graph showing the effect of the former austenitic grain diameter and the maximum former austenitic grain diameter/average former austenitic grain diameter of the hardened layer on the torsional fatigue strength.

FIG. 6(a) and FIG. 6(b) are each a graph showing the effect of the processing ratio at temperatures lower than 800° C. and the conditions of the high-frequency hardening on the torsional fatigue strength.

FIG. 7(a) and FIG. 7(b) are each a graph showing the effect of the former austenitic grain diameter and the maximum former austenitic grain diameter/average former austenitic grain diameter of the hardened layer on the rolling fatigue strength.

FIG. 8 is a schematic diagram of a crankshaft.

FIG. 9 is a diagram showing the position of the crankshaft subjected to the high-frequency hardening.

FIG. 10 is a diagram showing the scheme of the endurance test.

FIG. 11 is a partial cross-sectional view of a constant velocity joint.

FIG. 12 is a cross-sectional view of a hardened structure in a constant velocity joint outer race.

FIG. 13 is another cross-sectional view of a hardened structure in a constant velocity joint outer race.

FIG. 14 is a partial cross-sectional view of a constant velocity joint.

FIG. 15 is a cross-sectional view of a hardened structure in a constant velocity joint inner race.

FIG. 16 is another cross-sectional view of a hardened structure in a constant velocity joint inner race.

FIG. 17 is a diagram showing a hub and a hub bearing unit.

FIG. 18 is another diagram showing a hub and a hub bearing unit.

FIG. 19 is a diagram showing the scheme of sliding rolling contact fatigue test.

FIG. 20 is a perspective view of a gear.

FIG. 21 is a cross-sectional view showing a hardened surface layer of tooth and bottoms of the gear.

Denotations of reference numerals in FIGS. 1 to 21 are as follows:

• 1: shaft
• 2: spline
• 3: chuck
• 4: crankshaft
• 5: journal
• 6: crank pin
• 7: crank web
• 8: counter weight
• 9: hardened structure layer
• 10: drive shaft
• 11: hub
• 12: constant velocity joint
• 13: outer race
• 13a: mouse
• 13b: stem
• 14: inner race
• 15: ball
• 16: hardened structure layer
• 17: hub
• 18: shaft of hub
• 19: spacer
• 20: outer race of hub
• 21: ball
• 22: contact rolling surface
• 23: fitting portion
• 24: shaft of constant velocity joint
• 25: gear
• 26: teeth
• 27: bottom
• 28: hardened structure layer
• 29: shaft hole

BEST MODE FOR CARRYING OUT THE INVENTION

The present invention will now be described in specific details.

A component for machine structural use according to the present invention may take various shapes and structures, such as a drive shaft, an input shaft, an output shaft, a crankshaft, an inner or outer race of a constant velocity joint, a hub, and a gear for automobiles. In any case, it is essential that the component have a hardened layer over the entirety or part of the portion that particularly requires a fatigue strength, that the average grain diameter of the former austenitic grains be 12 μm or less, and that the maximum grain diameter does not exceed four times the average grain diameter.

The research results that led to this knowledge will now be explained.

A steel material (150 kg) having a composition indicated as steel a or steel b below was melted in a vacuum melting furnace- and hot-forged into a 150 mm square bar, from which dummy billets were made. Then, rolled steel bar materials were manufactured under various hot-working conditions.

[Steel a]: C: 0.48 mass %, Si: 0.55 mass %, Mn: 0.78 mass %, P: 0.011 mass %, S: 0.019 mass %, Al: 0.024 mass %, N: 0.0043 mass %, balance: Fe and inevitable impurities

[Steel b]: C: 0.48 mass %, Si: 0.51 mass %, Mn: 0.79 mass %, P: 0.011 mass %, S: 0.021 mass %, Al: 0.024 mass %, N: 0.0039 mass %, Mo: 0.45 mass %, Ti: 0.021 mass %, B: 0.0024 mass %, balance: Fe and inevitable impurities

Next, the steel bar was cut to a predetermined length and subjected to surface cutting and partly to cold-drawing to adjust the diameter. At the same time, the steel bar was rolled to form splines. A shaft 1 with splines 2 having a dimension and the shape shown in FIG. 1 was manufactured as a result.

The shaft was heated and hardened under various conditions in a high-frequency hardening device (frequency: 10 to 200 kHz), tempered in a heating furnace at 170° C. for 30 minutes, and then analyzed to determine the torsional fatigue strength.

The torsional fatigue strength was evaluated in terms of torque (N·m) when the number of cycles to fracture was 1×10⁵ in the shaft torsional fatigue test. In the torsional fatigue test, a hydraulic fatigue tester was used, and as shown in FIG. 2(a), splines 2a and 2b were respectively fit into disk-shaped chucks 3a and 3b and torsional torque was repeatedly applied between the chucks 3a and 3b at a frequency of 1 to 2 Hz.

The structure of the hardened layer of the same shaft was observed with an optical microscope to determine the average former austenitic grain diameter and the maximum former austenitic grain diameter.

The average former austenitic grain diameter was determined as follows. A specimen was observed with an optical microscope at three positions, namely, at ⅕, ½, and ⅘ of the thickness of the hardened layer from the surface, and from five field of views for each position under a magnification of ×400 (the area of one field of view: 0.25 mm×0.225 mm) to ×1,000 (the area of one field of view: 0.10 mm×0.09 mm). The average former austenitic grain diameter was measured at each position, and the highest average was defined as the average former austenitic grain diameter. The thickness of the hardened layer was assumed to be the depth of the region from the surface at which the area ratio of the martensitic structure decreased to 98%.

The maximum former austenitic grain diameter was determined as follows. A specimen was observed at the same three positions in the hardened layer thickness direction from five fields of view at each position under a magnification of ×400 (the area of one field of view: 0.25 mm×0.225 mm), so that the areas corresponding to the total of 15 fields of view can be observed. The grain diameter distributions in all the fields of view were applied to the equation below to determine the maximum grain diameter: Maximum grain diameter=average grain diameter+3σ (σ: standard deviation)

In observing the former austenitic grains, the cross-section taken in the thickness direction of the hardened layer was reacted with a corrosive liquid containing an aqueous picrinic acid solution (50 g of picrinic acid dissolved in 500 g of water), 11 g of sodium dodecylbenzenesulfonate, 1 g of ferrous chloride, and 1.5 g of oxalic acid so as to expose the former austenitic grain boundaries as shown in FIG. 3.

FIG. 4 shows the relationship between the average former austenitic grain diameter and the torsional fatigue strength. As shown in FIG. 4(a), the fatigue strength increased with the decrease in average grain diameter. However, at a former austenitic grain diameter of 12 μm or less, the fatigue strength differed although the grain diameter was substantially the same. It was found that the cause of this is the grain diameter distribution, in particular, the maximum grain diameter. Further investigations were pursued on this issue and it was found that at a maximum grain diameter of not exceeding four times the average grain diameter, the fatigue strength improves significantly by reducing the average grain diameter. Plotted points in FIG. 4(a) were re-plotted in FIG. 4(b) as open squares and rhombuses for a maximum grain diameter/average grain diameter of 4 or less and solid squares and rhombuses for a ratio grain diameter/average grain diameter exceeding 4.

The factors that cause the average grain diameter and the maximum grain diameter to affect the fatigue strength are presumably as follows.

The impurity elements that cause fatigue fracture tend to segregate at the former austenitic boundaries. Thus, as the former austenitic grains become smaller, the area in which segregation occurs increases. This decreases the impurity concentration in the individual segregation sites and thereby increases the fatigue strength. Furthermore, stress concentration to the former austenitic grain boundaries due to cutout or the like is dispersed when the grain diameter is small, thereby decreasing the stress applied onto the individual grain boundaries and increasing the fatigue strength. Such effects are affected not only by the average grain diameter but also by the maximum grain diameter. In other words, in the vicinity of a large grain, the area of the grain boundary is small and the impurity concentration easily increases. Moreover, dispersion of stresses does not readily occur.

It can be presumed that the presence of a large grain with a diameter exceeding four times the average grain diameter increases the possibility of decreasing the fatigue strength due to the above-described effects.

In particular, when the maximum grain diameter of the former austenitic grains is 20 μm or less, the fatigue strength is expected to improve significantly and stably for a wide range of component shape. More preferably, the average grain diameter is 5 μm or less. Most preferably the average grain diameter is 4 μm or less.

FIG. 5(a) and FIG. 5(b) are each a graph showing the effect of the average former austenitic grain diameter and the maximum former austenitic grain diameter/average former austenitic grain diameter in the hardened layer on the torsional fatigue strength. At an average former austenitic grain diameter of 12 μm or less, the fatigue strength can be notably increased by adjusting the maximum former austenitic grain diameter/average former austenitic grain diameter to 4 or less. Moreover, at an average austenitic grain diameter of 5 μm or less, particularly 3 μm or less, the fatigue strength can be further significantly increased by adjusting the maximum former austenitic grain diameter/average former austenitic grain diameter to 4 or less.

FIG. 6(a) and FIG. 6(b) show the effect of processing ratio at temperatures less than 800° C., the maximum ultimate temperature (heating temperature) during high-frequency heating, and the heating rate on the torsional fatigue strength. FIG. 6(a) and FIG. 6(b) show that excellent fatigue properties can be obtained at a processing ratio in the temperature zone less than 800° C. of 25% or more, a maximum ultimate temperature during the high-frequency hardening of 1,000° C. or less, and a heating rate of 400° C./s or more.

The effect of the average former austenitic grain diameter and the maximum former austenitic grain diameter/average former austenitic grain diameter on the rolling fatigue resistance was also studied. A steel material (150 kg) having a composition indicated as steel a or steel b above was melted in a vacuum melting furnace and hot-forged into a 150 mm square bar, from which dummy billets were manufactured. The billet was hot-worked and cold-drawn under various conditions and cut to make a steel bar 12 mm in diameter. The surface of the steel bar was subjected to high-frequency hardening under various conditions, and the resulting steel bar was cut to a predetermined length to make a specimen for rolling fatigue test. Radial-type rolling fatigue test shown in FIG. 2(b) was conducted using this specimen.

FIG. 7(a) and FIG. 7(b) show the results of the test. As with the torsional fatigue described above, the fatigue strength can be notably increased by adjusting the maximum former austenitic grain diameter/average former austenitic grain diameter to 4 or less at an average former austenitic grain diameter of 12 μm or less. Moreover, at an average austenitic grain diameter of 5 μm or less, particularly 3 μm or less, the fatigue strength can be further significantly increased by adjusting the maximum former austenitic grain diameter/average former austenitic grain diameter to 4 or less.

The experimental results used for obtaining FIG. 4(a), FIGS. 4(b) to FIG. 6(a), and FIG. 6(b) are set forth in Tables 1-1 and 1-2, and the results used for obtaining FIG. 7(a) and FIG. 7(b) are set forth in Tables 2-1 and 2-2. The rolling fatigue property is indicated as the ratio of the time to fracture to the time to fracture of Sample No. 1 in Table 2-1 which corresponds to an example of the existing related art.

	TABLE 1-1
	Hot-working conditions
	Total		Working		HF hardening conditions
		processing	Cooling	(cold-working)	Pre-hardening			Retention
		ratio (%) at	rate (° C./s)	ratio (%) at	structure		Heating	time (sec) at
	Steel	800° C. to	after	less than	Proportion (vol. %) of	Heating	temperature	800° C. or
No.	type	1000° C.	working	800° C.	bainite structure	rate(° C./s)	(° C.)	more
1	a	80	0.1	0	0	800	870	1
2	a	80	0.8	50	82	2000	870	1
3	a	80	0.8	40	82	800	870	1
4	a	80	0.8	25	82	2000	870	1
5	a	80	0.8	10	82	2000	870	1
6	a	80	0.8	0	82	2000	870	1
7	a	80	0.8	25	82	800	870	1
8	a	30	0.8	25	82	400	870	1
9	a	80	0.8	10	82	800	870	1
10	a	80	0.8	0	82	800	870	1
11	a	80	0.8	0	82	400	870	1
12	a	80	0.8	50	82	800	950	1
13	a	80	0.8	25	82	800	950	1
14	a	80	0.8	25	82	400	950	1
15	a	80	0.8	25	82	100	950	1
16	a	80	0.8	0	82	400	950	1
17	a	80	0.8	25	82	800	1050	1
18	a	80	0.8	10	82	800	1050	1
19	a	80	0.8	0	82	800	1050	1
20	a	80	0.8	0	82	100	1050	1
21	a	80	0.8	25	82	100	980	1
22	a	80	0.8	60	82	100	870	1
23	a	80	0.8	70	82	100	870	1
24	a	80	0.8	30	82	100	870	1
25	b	80	0.8	50	82	2000	870	1
26	b	80	0.8	40	82	800	870	1
27	b	80	0.8	25	82	2000	870	1
28	b	80	0.8	10	82	2000	870	1
29	b	80	0.8	0	82	2000	870	1
30	b	80	0.8	25	82	800	870	1
31	b	80	0.8	25	82	400	870	1
32	b	80	0.8	10	82	800	870	1
33	b	80	0.8	0	82	800	870	1
34	b	80	0.8	0	82	400	870	1
	Hardened layer structure		Torsional
		Average former	Maximum former		fatigue
		austenitic grain	austenitic grain		strength
	No.	diameter (μm)	diameter (μm)	Max./Ave.	(1 × 105) (MPa)	Reference
	1	17	72	4.2	500	Rel. Ex.
	2	4	8.7	2.2	844	Inv. Ex.
	3	4.4	15	3.4	826	Inv. Ex.
	4	4.8	18	3.8	808	Inv. Ex.
	5	12.2	49	4.0	525	Comp. Ex.
	6	13	53	4.1	520	Comp. Ex.
	7	5.8	12	2.1	772	Inv. Ex.
	8	6.2	18	2.9	754	Inv. Ex.
	9	12.5	50	4.0	523	Comp. Ex.
	10	13.9	60	4.3	512	Comp. Ex.
	11	14	80	5.7	510	Comp. Ex.
	12	8.5	16	1.9	727	Inv. Ex.
	13	9.5	23	2.4	709	Inv. Ex.
	14	9.6	35	3.6	673	Inv. Ex.
	15	11	50	4.5	592	Comp. Ex.
	16	13	61	4.7	500	Comp. Ex.
	17	14	35	2.5	511	Comp. Ex.
	18	15	60	4.0	502	Comp. Ex.
	19	16	80	5.0	493	Comp. Ex.
	20	15	120	8.0	484	Comp. Ex.
	21	11.8	70	5.9	592	Comp. Ex.
	22	4	18	4.5	620	Comp. Ex.
	23	4.4	32	7.3	600	Comp. Ex.
	24	8	40	5.0	600	Comp. Ex.
	25	1.9	3.8	2.0	960	Inv. Ex.
	26	2.4	8	3.3	940	Inv. Ex.
	27	2.8	10.8	3.9	920	Inv. Ex.
	28	2.6	14	5.4	750	Comp. Ex.
	29	2.7	21	7.8	690	Comp. Ex.
	30	3.9	7.9	2.0	880	Inv. Ex.
	31	4.1	12	2.9	860	Inv. Ex.
	32	4.2	18.5	4.4	730	Comp. Ex.
	33	4.3	22	5.1	690	Comp. Ex.
	34	4.4	26	5.9	680	Comp. Ex.
	Rel. Ex.: Example of related art,
	Inv. Ex.: Example of the present invention
	Comp. Ex.: Comparative example

	TABLE 1-2
	Hot-working conditions
	Total		Working		HF hardening conditions
		processing	Cooling	(cold-working)	Pre-hardening			Retention
		ratio (%) at	rate (° C./s)	ratio (%) at	structure		Heating	time (sec) at
	Steel	800° C. to	after	less than	Proportion (vol. %) of	Heating	temperature	800° C. or
No.	type	1000° C.	working	800° C.	bainite structure	rate(° C./s)	(° C.)	more
35	b	80	0.8	50	82	800	1000	1
36	b	80	0.8	25	82	800	1020	1
37	b	80	0.8	25	82	400	1030	1
38	b	80	0.8	25	82	100	950	1
39	b	80	0.8	0	82	400	1030	1
40	b	80	0.8	25	82	800	1050	1
41	b	80	0.8	10	82	800	1050	1
42	b	80	0.8	0	82	800	1050	1
43	b	80	0.8	0	82	100	1050	1
44	b	80	0.8	50	82	800	950	1
45	b	80	0.8	25	82	800	950	1
46	b	80	0.8	25	82	400	950	1
	Hardened layer structure		Torsional
		Average former	Maximum former		fatigue
		austenitic grain	austenitic grain		strength(1 × 105)
	No.	diameter (μm)	diameter (μm)	Max./Ave.	(MPa)	Reference
	35	6	11	1.8	800	Inv. Ex.
	36	8.6	15	2.1	750	Inv. Ex.
	37	10	30	3.5	700	Inv. Ex.
	38	9	40	4.4	600	Comp. Ex.
	39	9	48	5.3	595	Comp. Ex.
	40	13	38	2.9	590	Comp. Ex.
	41	14	56	4.0	580	Comp. Ex.
	42	15	75	5.0	570	Comp. Ex.
	43	14	110	7.9	560	Comp. Ex.
	44	3	7.9	2.6	950	Inv. Ex.
	45	5	11	2.2	810	Inv. Ex.
	46	3.4	13	3.8	850	Inv. Ex.
	Rel. Ex.: Example of related art,
	Inv. Ex.: Example of the present invention
	Comp. Ex.: Comparative example

	TABLE 2-1
	Hot-working conditions
	Total		Working		HF hardening conditions
		processing	Cooling	(cold-working)	Pre-hardening			Retention
		ratio (%) at	rate (° C./s)	ratio (%) at	structure		Heating	time (sec) at
	Steel	800° C. to	after	less than	Proportion (vol. %) of	Heating	temperature	800° C. or
No.	type	1000° C.	working	800° C.	bainite structure	rate(° C./s)	(° C.)	more
1	a	80	0.1	0	0	800	870	1
2	a	80	0.8	50	82	2000	870	1
3	a	80	0.8	40	82	800	870	1
4	a	80	0.8	25	82	2000	870	1
5	a	80	0.8	10	82	2000	870	1
6	a	80	0.8	0	82	2000	870	1
7	a	80	0.8	25	82	800	870	1
8	a	30	0.8	25	82	400	870	1
9	a	80	0.8	10	82	800	870	1
10	a	80	0.8	0	82	800	870	1
11	a	80	0.8	0	82	400	870	1
12	a	80	0.8	50	82	800	950	1
13	a	80	0.8	25	82	800	950	1
14	a	80	0.8	25	82	400	950	1
15	a	80	0.8	25	82	100	950	1
16	a	80	0.8	0	82	400	950	1
17	a	80	0.8	25	82	800	1050	1
18	a	80	0.8	10	82	800	1050	1
19	a	80	0.8	0	82	800	1050	1
20	a	80	0.8	0	82	100	1050	1
21	a	80	0.8	25	82	100	980	1
22	a	80	0.8	60	82	100	870	1
23	a	80	0.8	70	82	100	870	1
24	a	80	0.8	30	82	100	870	1
25	b	80	0.8	50	82	2000	870	1
26	b	80	0.8	40	82	800	870	1
27	b	80	0.8	25	82	2000	870	1
28	b	80	0.8	10	82	2000	870	1
29	b	80	0.8	0	82	2000	870	1
30	b	80	0.8	25	82	800	870	1
31	b	80	0.8	25	82	400	870	1
32	b	80	0.8	10	82	800	870	1
33	b	80	0.8	0	82	800	870	1
34	b	80	0.8	0	82	400	870	1
	Hardened layer structure
		Average former	Maximum former		Rolling fatigue
		austenitic grain	austenitic grain		(ratio based on
	No.	diameter (μm)	diameter (μm)	Max./Ave.	related art)	Reference
	1	17	72	4.2	1.0	Rel. Ex.
	2	4	8.7	2.2	10.0	Inv. Ex.
	3	4.4	15	3.4	9.8	Inv. Ex.
	4	4.8	18	3.8	9.5	Inv. Ex.
	5	12.2	49	4.0	1.5	Comp. Ex.
	6	13	53	4.1	1.4	Comp. Ex.
	7	5.8	12	2.1	6.4	Inv. Ex.
	8	6.2	18	2.9	6.3	Inv. Ex.
	9	12.5	50	4.0	1.5	Comp. Ex.
	10	13.9	60	4.3	1.4	Comp. Ex.
	11	14	80	5.7	1.3	Comp. Ex.
	12	8.5	16	1.9	4.4	Inv. Ex.
	13	9.5	23	2.4	4.2	Inv. Ex.
	14	9.6	35	3.6	3.4	Inv. Ex.
	15	11	50	4.5	2.2	Comp. Ex.
	16	13	61	4.7	1.0	Comp. Ex.
	17	14	35	2.5	1.4	Comp. Ex.
	18	15	60	4.0	1.1	Comp. Ex.
	19	16	80	5.0	0.9	Comp. Ex.
	20	15	120	8.0	0.9	Comp. Ex.
	21	11.8	70	5.9	2.2	Comp. Ex.
	22	4	18	4.5	3.0	Comp. Ex.
	23	4.4	32	7.3	2.9	Comp. Ex.
	24	8	40	5.0	2.1	Comp. Ex.
	25	1.9	3.8	2.0	12.1	Inv. Ex.
	26	2.4	8	3.3	12.0	Inv. Ex.
	27	2.8	10.8	3.9	11.0	Inv. Ex.
	28	2.6	14	5.4	6.5	Comp. Ex.
	29	2.7	21	7.8	5.5	Comp. Ex.
	30	3.9	7.9	2.0	10.7	Inv. Ex.
	31	4.1	12	2.9	10.8	Inv. Ex.
	32	4.2	18.5	4.4	4.5	Comp. Ex.
	33	4.3	22	5.1	4.3	Comp. Ex.
	34	4.4	26	5.9	4.3	Comp. Ex.
	Rel. Ex.: Example of related art,
	Inv. Ex.: Example of the present invention
	Comp. Ex.: Comparative example

	TABLE 2-2
	Hot-working conditions		HF hardening conditions
		Total		Working				Retention
		processing		(cold-	Pre-hardening			time
		ratio (%) at	Cooling rate	working) ratio	structure			(sec) at
	Steel	800° C. to	(° C./s) after	(%) at less	Proportion (vol. %) of	Heating rate	Heating	800° C. or
No.	type	1000° C.	working	than 800° C.	bainite structure	(° C./s)	temperature(° C.)	more
35	b	80	0.8	50	82	800	1000	1
36	b	80	0.8	25	82	800	1020	1
37	b	80	0.8	25	82	400	1030	1
38	b	80	0.8	25	82	100	950	1
39	b	80	0.8	0	82	400	1030	1
40	b	80	0.8	25	82	800	1050	1
41	b	80	0.8	10	82	800	1050	1
42	b	80	0.8	0	82	800	1050	1
43	b	80	0.8	0	82	100	1050	1
44	b	80	0.8	50	82	800	950	1
45	b	80	0.8	25	82	800	950	1
46	b	80	0.8	25	82	400	950	1
	Hardened layer structure		Rolling
		Average former	Maximum former		fatigue (ratio
		austenitic grain	austenitic grain		based on
	No.	diameter (μm)	diameter (μm)	Max./Ave.	related art)	Reference
	35	6	11	1.8	10.4	Inv. Ex.
	36	8.6	15	2.1	10.2	Inv. Ex.
	37	10	30	3.5	9.9	Inv. Ex.
	38	9	40	4.4	3.5	Comp. Ex.
	39	9	48	5.3	3.5	Comp. Ex.
	40	13	38	2.9	2.3	Comp. Ex.
	41	14	56	4.0	2.6	Comp. Ex.
	42	15	75	5.0	2.3	Comp. Ex.
	43	14	110	7.9	2.4	Comp. Ex.
	44	3	7.9	2.6	10.6	Inv. Ex.
	45	5	11	2.2	10.3	Inv. Ex.
	46	3.4	13	3.8	10.8	Inv. Ex.
	Rel. Ex.: Example of related art,
	Inv. Ex.: Example of the present invention
	Comp. Ex.: Comparative example

In order for the average grain diameter of former austenitic grains to be 12 μm or less and for the maximum grain diameter to be not more than four times the average grain diameter, it is advantageously suitable to use an approach of allowing the structure before high-frequency hardening to contain homogeneous, fine bainite structure and/or martensite structure. This approach is described below.

That is, the structure before the high-frequency hardening preferably contains 10 vol % or more and more preferably 25 vol % or more of a bainite structure and/or a martensite structure. Since the bainite structure and the martensite structure are each a structure containing finely dispersed carbides, inclusion of large amounts of bainite structure or martensite structure in the pre-hardening structure will increase the area of the ferrite/carbide boundaries, which are nucleation sites for austenite, during hardening by heating and finer austenite is generated as a result. Thus, this approach effectively contributes to reducing the former austenitic grain diameter of the hardened layer. Since the austenitic grain diameter decreases during the hardening by heating, the grain boundary strength increases and the fatigue strength improves.

In order to adjust the proportion of the homogeneous, fine bainite structure and/or martensite structure to 10 vol % or more, a steel having the composition described below is preferably hot-worked such that the total processing ratio at temperatures of 800° C. to 1,000° C. is 80% or more, followed by cooling at a cooling rate of 0.2° C./s or more for the temperature range of 700° C. to 500° C. This is because, at a total processing ratio at 800° C. to 1,000° C. of less than 80%, a sufficiently homogenous, fine bainite or martensite structure cannot be obtained. The total proportion of the bainite structure and/or the martensite structure cannot be adjusted to 10 vol % or more unless the cooling rate in the temperature range of 700° C. to 500° C. is 0.2° C./s or more after the hot-working.

Moreover, in order to reduce the average grain diameter and the maximum grain diameter of former austenite of the hardened layer after the high-frequency hardening, it is necessary to effect 20% or more of working (second working step) in the temperature range less than 800° C. before the high-frequency hardening. The working in the temperature range less than 800° C. may be effected in the hot-working step before the cooling at the above-described cooling rate, i.e., may be effected in the temperature range of 700° C. to less than 800° C. Alternatively, a separate cold-working may be effected after the cooling or a hot-working may be effected by heating the workpiece at the A₁ transformation temperature or less. The processing ratio at temperatures lower than 800° C. is more preferably 30% or more.

Examples of the working method include cold forging, cold ironing, forming rolling, and shotblasting.

A preferable steel composition for obtaining such a pre-structure will now be described.

• C: 0.3 to 1.5 mass %

Carbon is the element having the greatest influence on the hardenability. Carbon effectively contributes to increasing the hardness and the depth of the hardened layer and to improving the fatigue strength. However, at a C content less than 0.3 mass %, the depth of the hardened layer must be significantly increased to securely achieve the required fatigue strength, and this leads to occurrence of significant quenching cracks and difficulties in generating the bainite structure. Thus, 0.3 mass % or more of carbon is contained. At a C content exceeding 1.5 mass %, the grain boundary strength decreases, the fatigue strength decreases, and the machinability, cold-forgeability, and resistance to quenching crack decrease. Therefore, the C content is limited to the range of 0.3 to 1.5 mass %, preferably 0.4 to 0.6 mass %.

• Si: 3.0 mass % or less

Silicon not only serves as a deoxidizer but also contributes to effectively improving the strength. At a Si content exceeding 3.0 mass %, the machinability and the forgeability decrease. Thus, the Si content is preferably 3.0 mass % or less.

In order to increase the strength, Si content is preferably 0.05 mass % or more.

• Mn: 2.0 mass % or less

Manganese is added for its effects of improving the hardenability and securing the depth of the hardened layer during the hardening. At a Mn content less than 0.2 mass %, the effect of addition is not sufficient. The Mn content is preferably 0.2 mass % or more, and more preferably 0.3 mass % or more. On the other hand, at a Mn content exceeding 2.0 mass %, the residual austenite after hardening increases, thereby decreasing the surface hardness and the fatigue strength. Thus, the Mn content is preferably 2.0 mass % or less. At an excessively large Mn content, the base material hardens and the machinability may be adversely affected. Thus, the Mn content is preferably 1.2 mass % or less and more preferably 1.0 mass % or less.

Al: 0.25 mass % or less

Aluminum is effective for deoxidization. It is also effective for reducing the grain diameter of the hardened layer since it restrains the growth of the austenitic grains during the heating for hardening. At an Al content exceeding 0.25 mass %, however, the effect is saturated and the cost for the composition is disadvantageously increased. Thus, the Al content is preferably 0.25 mass % or less, and more preferably 0.001 to 0.10 mass %.

In the present invention, the above-described four components are the main components. The main components must satisfy formula (1) below: C^1/2(1+0.7Si)(1+3Mn)>2.0   (1)

By adjusting the C, Si, and Mn contents to satisfy formula (1), it becomes possible to bring the total proportion of the bainite and martensite in the pre-high-frequency hardening structure to 10 vol % or more and to produce a hardened layer having the structure of the present invention by the high-frequency hardening. Moreover, when the value of the left side of formula (1) is 2.0 or less, the hardness of the hardened layer after the high-frequency hardening is low, and it becomes difficult to sufficiently maintain the depth of the hardened layer.

Although the main components are described above, at least one of the following six components may also be incorporated according to the present invention.

• Cr: 2.5 mass % or more

Chromium is effective for improving the hardenability and for ensuring the hardening depth. An excessive amount of Cr stabilizes the carbides and promotes generation of the residual carbides, thereby decreasing the grain boundary strength and the fatigue strength. Accordingly, the Cr content is preferably as low as possible, but can be up to 2.5 mass %. Preferably, the Cr content is 1.5 mass % or less. In order to improve the hardenability, the Cr content is preferably 0.03 mass % or more.

• Mo: 1.0 mass % or less

Molybdenum is effective for inhibiting the growth of the austenitic grains. For this effect, the Mo content is preferably 0.05 mass % or more. At a Mo content exceeding 1.0 mass %, the machinability is degraded. The Mo content is preferably 1.0 mass % or less.

• Cu: 1.0 mass % or less

Copper is effective for improving the hardenability. Copper forms solid solution in the ferrite, and this solid-solution hardening increases the fatigue strength. Copper also inhibits generation carbides, prevents a decrease in grain boundary strength caused by the carbide, and improves the fatigue strength. However, at a Cu content exceeding 1.0 mass %, cracks occur during hot-working. Thus, the Cu content is preferably 1.0 mass % or less, and more preferably 0.5 mass % or less. At a Cu content less than 0.03 mass %, the effect of improving the hardenability and the effect of preventing the decrease in grain boundary strength are small. Thus, the Cu content is preferably 0.03 mass % or more.

• Ni: 2.5 mass % or less

Nickel improves the hardenability and is used to adjust the hardenability. It also inhibits generation of carbides, prevents a decrease in grain boundary strength caused by carbides, and increases the fatigue strength. However, Ni is very expensive and increases the cost of steel material if added in an amount exceeding 2.5 mass %. Thus, the Ni content is preferably 2.5 mass % or less. At an Ni content less than 0.05 mass %, the effect of improving the hardenability and inhibiting the decrease in brain boundary strength are small. Thus, the Ni content is preferably 0.05 mass % or more, and more preferably 0.1 to 1.0 mass %.

• Co: 1.0 mass % or less

Cobalt inhibits generation of carbides, inhibits a decrease in grain boundary strength caused by carbides, and increases the fatigue strength. However, Co is a very expensive element, and incorporation of 1.0 mass % or more of Co will increase the cost of the steel material. Thus, the Co content is 1.0 mass % or less. At a Co content less than 0.01 mass %, the effect of inhibiting the decrease in grain boundary strength is small. Thus, the Co content is preferably 0.01 mass % or more and more preferably 0.02 to 0.5 mass %.

• V: 0.5 mass % or less

Vanadium bonds with C and N in the steel to function as a deposition strengthening element. It also increases the resistance to temper softening. These effects increase the fatigue strength. At a V content exceeding 0.5 mass %, these effects are saturated. Thus, the V content is preferably 0.5 mass % or less. At a V content of less than 0.01 mass %, the effect of improving the fatigue strength is small; thus, the V content is preferably 0.01 mass % or more and more preferably 0.03 to. 0.3 mass %.

• W: 1.0 mass % or less

Tungsten is useful for inhibiting the growth of austenitic grains. For this effect, the W content is preferably 0.005 mass % or more. At a W content exceeding 1.0 mass %, the machinability will be degraded. Thus, the W content is preferably 1.0 mass % or less.

In adding one or more of the six components to the main components, formula (2) below must be satisfied for the same reason as for formula (1): C^1/2(1+0.7Si)(1+3Mn)(1+2.1Cr)(1+3.0 Mo)(1+0.4 Cu)(1+0.3Ni)(1+5.0V)(1+0.5W)>2.0   (2)

In the present invention, at least one selected from Ti: 0.1 mass % or less, Nb: 0.1 mass % or less, Zr: 0.1 mass % or less, B: 0.01 mass % or less, Ta: 0.5 mass % or less, Hf: 0.5 mass % or less, and Sb: 0.015 mass % or less may be further contained.

• Ti: 0.1 mass % or less

Titanium bonds with N, which is an inevitable impurity, and prevents B from forming BN and from losing the effect of increasing the hardenability, thereby fully enhancing the hardenability increasing effect of B. To achieve this effect, the Ti content is preferably 0.005 mass % or more. At a Ti content exceeding 0.1 mass %, large amounts of TiN are generated, and this starts fatigue fracture and thus causes a significant decrease in fatigue strength. Thus, the Ti content is preferably 0.1 mass % or less and more preferably in the range of 0.01 to 0.07 mass %.

• Nb: 0.1 mass % or less

Niobium not only has hardenability enhancing effect but also serves as a deposition strengthening element by bonding with C and N in the steel. It is also an element that increases the temper softening resistance. These effects improve the fatigue strength. However, at a Nb content exceeding 0.1 mass %, these effects are saturated. Thus, the Nb content is preferably 0.1 mass % or less. At a Nb content less than 0.005 mass %, the effect of deposition strengthening and the effect of enhancing the temper softening resistance are small; thus, the Nb content is preferably 0.005 mass % or more, and more preferably 0.01 to 0.05 mass %.

• Zr: 0.1 mass % or less

Zirconium not only has a hardenability improvement effect but also serves as a deposition strengthening element by bonding with C and N in the steel. It is also an element that increases the temper softening resistance. These effects improve the fatigue strength. However, at a Zr content exceeding 0.1 mass %, these effects are saturated. Thus, the Zr content is preferably 0.1 mass % or less. At a Zr content less than 0.005 mass %, the effect of deposition strengthening and the effect of enhancing the temper softening resistance are small; thus, the Zr content is preferably 0.005 mass % or more, and more preferably 0.01 to 0.05 mass %.

• B: 0.01 mass % or less

Boron not only improves the fatigue properties by strengthening the grain boundaries but also improves the strength. The B content is preferably 0.0003 mass % or more. Since the effect is saturated at a content exceeding 0.01 mass %, the B content is limited to 0.01 mass % or less.

• Ta: 0.5 mass % or less

Tantalum may be contained since it is effective against delay of microstructural changes and prevents degradation of fatigue strength, in particular, rolling fatigue strength. However, Ta does not contribute to further strength improvements even when the Ta content is increased over 0.5 mass %. Thus, the Ta content is set to 0.5 mass % or less. In order to achieve the effect of improving the fatigue strength, the Ta content is preferably 0.02 mass % or more.

• Hf: 0.5 mass % or less

Hafnium may be contained since it is effective against delay of microstructural changes and prevents degradation of fatigue strength, in particular, rolling fatigue strength. However, Hf does not contribute to further strength improvements even when the Hf content is increased over 0.5 mass %. Thus, the Hf content is 0.5 mass % or less. In order to achieve the effect of improving the fatigue strength, the Hf content is preferably 0.02 mass % or more.

• Sb: 0.015 mass % or less

Antimony may be contained since it is effective against delay of microstructural changes and prevents degradation of fatigue strength, in particular, rolling fatigue strength. However, when the Sb content is increased to exceed 0.015 mass %, the toughness is decreased. The Sb content is thus 0.015 mass % or less and preferably 0.010 mass % or less. The Sb content is preferably 0.005 mass % or more to allow Sb to exhibit an effect of improving the fatigue strength.

In adding one or more of the above-described seven components to the main components, formula (3) below must be satisfied for the same reason as that for formula (1) above: C^1/2(1+0.7Si)(1+3Mn)(1+2.1Cr)(1+3.0 Mo)(1+0.4 Cu)(1+0.3Ni)(1+5.0V)(1+1000B)(1+0.5W)>2.0   (3)

In this invention, Si: 0.1 mass % or less, Pb: 0.1 mass % or less, Bi: 0.1 mass % or less, Se: 0.1 mass % or less, Te: 0.1 mass % or less, Ca: 0.01 mass % or less, Mg: 0.01 mass % or less, and REM: 0.1 mass % or less may be further contained.

• S: 0.1 mass % or less

Sulfur is a useful element that forms MnS in the steel and improves the machinability. At a S content exceeding 0.1 mass %, however, S segregates in the grain boundaries and thereby decreases the grain boundary strength. Thus, the S content is limited to 0.1 mass %or less and preferably 0.04 mass % or less.

• Pb: 0.1 mass % or less
• Bi: 0.1 mass % or less

Both Pb and Bi improve machinability since they melt during machining to provide lubricating and embrittlement effects. Thus they may be added for these effects. However, at a Pb content exceeding 0.1 mass % and a Bi content exceeding 0.1 mass %, the effects are saturated and the cost of the components increases. Thus, the Pb and Bi contents are set to be within the above-described ranges. In order to improve the machinability, the Pb content is preferably 0.01 mass % or more and the Bi content is preferably 0.01 mass % or more.

• Se: 0.1 mass % or less
• Te: 0.1 mass % or less

Se and Te each bond with Mn to form MnSe and MnTe, which function as chip-breakers and thereby improve the machinability. However, at a content exceeding 0.1 mass %, the effects are saturated and the cost for the component increases. Thus, the content is set to be 0.1 mass % or less for both the elements. In order to improve the machinability, the Se content is preferably 0.003 mass % or more and the Te content is preferably 0.003 mass % or more.

• Ca: 0.01 mass % or less
• REM: 0.1 mass % or less

Ca and REM each bond with MnS to form sulfides, which function as chip-breakers and thereby improve the machinability. However, at a Ca content exceeding 0.01 mass % and a REM content exceeding 0.1 mass %, the effects are saturated, and the cost for the component increases. Thus, their contents are set to be within the above-described ranges. In order to improve the machinability, the Ca content is preferably 0.0001 mass % or more and the REM content is preferably 0.0001 mass % or more.

• Mg: 0.01 mass % or less

Magnesium is not only an oxidizer but also functions as the stress concentration source thereby improving the machinability. Thus, Mg may added as necessary. However, at an excessively large Mg content, the effects are saturated and the cost for the component increases. Thus, the Mg content is set to be 0.01 mass % or less. In order to improve the machinability the Mg content is preferably 0.0001 mass % or more.

The balance excluding the above-described elements is preferably Fe and inevitable impurities. Examples of the inevitable impurities are P, 0, and N. A P content up to 0.10 mass %, a N content up to 0.01 mass %, and an 0 content of up to 0.008 mass % are acceptable.

Next, the production method of the present invention is explained.

A steel material having a particular composition described above is subjected to bar-mill rolling and then to hot-working such as hot-forging to form a component-shaped product. The component is at least partially subjected to high-frequency hardening at a heating temperature of 800° C. to 1,000° C. This portion of the component subjected to the hardening is set to be the site where fatigue strength is required.

In this series of steps, a hardened structure having an average former austenitic grain diameter of 12 μm or less and a maximum grain diameter not more than four times the average diameter can be obtained by conducting the hot-working such that the total processing ratio in the temperature range of 800° C. to 1,000° C. is at least 80%, cooling at a rate of at least 0.2° C./s in the temperature range of 700° C. to 500° C., and then effecting at least 20% or processing in the temperature range of below 800° C. or by conducting the hot-working such that the total processing ratio in the temperature range of 800° C. to 1,000° C. is at least 80%, effecting 20% or more of processing in the temperature range of below 800° C., and then cooling at a rate of 0.2° C./s or more in the temperature range of 700° C. to 500° C.; and then employing the high-frequency hardening conditions described in detail below.

Each of the limitations will now be described in detail.

[Working Conditions]

The total processing ratio in the range of 800° C. to 1,000° C. during the hot-working is set to be at least 80%, and the cooling rate in the temperature range of 700° C. to 500° C. is set to be at least 0.2° C./s. Under these conditions, the pre-hardening structure can be obtained as homogeneous, fine bainite and/or martensitic structure, and the austenitic grains become finer during the subsequent heating for high-frequency hardening. Preferably, the cooling rate is at least 0.5° C./s.

Before the high-frequency hardening, 20% or more of processing is effected in the temperature range below 800° C. The working in the temperature range of 800° C. or lower may be conducted in the hot-working step and before the cooling at the above-described cooling ratio (the temperature range from 700° C. to less than 800° C.); alternatively, a separate cold working may be effected after the cooling or a hot-working may be effected by re-heating the workpiece at the A₁ transformation temperature or less. The processing ratio at a temperature below 800° C. is preferably at least 30%. Examples of the working methods include cold forging, cold ironing, forming rolling, and shotblasting. By working at a temperature of 800° C. or less, the bainite or martensitic structure before the high-frequency hardening becomes finer; therefore, the average former austenitic grain diameter in the hardened layer obtained by the high-frequency hardening will be 12 μm or less and the maximum grain diameter does not exceed four times the average grain diameter. As a result, the fatigue strength is improved.

The term “processing ratio” used herein is defined as the reduction ratio of the cross-sectional area before and after working for the cases concerning rolling, forging, and drawing. For the cases such as shotblasting where the processing ratio cannot be defined in terms of the reduction-ratio of the cross-sectional area, the processing ratio is determined by the change in hardness corresponding to the reduction ratio.

[High-Frequency Hardening Conditions]

The heating temperature is set to be 800° C. to 1,000° C., and the range 600° C. to 800° C. is heated at a rate of 400° C./s or more. If the heating temperature is less than 800° C., generation of the austenitic structure is insufficient, and a hardened layer cannot be obtained. On the other hand, when the heating temperature exceeds 1,000° C., the rate of austenitic grain growth increases substantially. This increases the average grain diameter and, at the same time, the individual grains frequently grow at rates significantly different from one another in the temperature region where rapid growth occurs. As a result, the maximum grain diameter exceeds four times the average grain diameter, thereby inflicting a decrease in fatigue strength.

When the heating ratio in the range of 600° C. to 800° C. is less than 400° C./s, the austenitic grain growth is promoted and the size of the individual grains becomes nonuniform. Thus, the maximum grain diameter exceeds four times the average grain diameter, which results in a decreased fatigue strength. This is presumably due to the fact that when the heating rate is low, reverse transformation from ferrite to austenite starts at a lower temperature and nonuniform grain growth tends to occur depending on the position of the grains.

The heating temperature is preferably 800° C. to 950° C., and the heating rate in the range of 600° C. to 800° C. is preferably at least 700° C./s and more preferably at least 1,000° C./s.

During the high-frequency heating, if the retention time at 800° C. or more is excessively long, the austenitic grains grow and the maximum grain diameter tends to exceed four times the average grain diameter as a result. Thus, the retention time at 800° C. or more is preferably 5 sec or less.

EXAMPLES

Example 1

As an example of the component for machine structural use, shafts simulating a drive shaft, an output shaft, and an input shaft of automobiles were prepared. In particular, each of the steel materials having compositions shown in Table 3 was melted in a converter and cast into a cast slab by continuous casting. The size of the cast slab was 300×400 [mm]. The cast slab was subjected to a breakdown step and rolled into a 150 mm square billet. The billet was rolled into a steel bar under the hot-working conditions shown in Tables 4-1 and 4-2 while setting the finishing temperature to 800° C. or more. Here, the total processing ratio in the range of 800° C. to 1,000° C. is the ratio of reduction of the cross section in this temperature range. After the rolling, cooling was conducted under the conditions described in Tables 4-1 and 4-2.

Next, the steel bar was cut to a predetermined length and subjected to surface cutting and partly cold-drawing to adjust the diameter. Simultaneously, splines of the steel bar are formed by rolling to prepare a shaft 1 having splines 2 with dimensions and a shape shown in FIG. 1. The cold-working ratio is the ratio of reduction of the cross-section.

This shaft was hardened under conditions shown in Tables 4-1 and 4-2 using a high-frequency hardening apparatus with a frequency of 15 kHz and then tempered at 170° C. for 30 minutes in a heating furnace. The torsional fatigue strength was tested. For some of the shafts, tempering was omitted and their torsional fatigue strength was tested.

The torsional fatigue strength was evaluated in terms of torque (N·m) when the number of cycles to fracture was 1×10⁵ in the shaft torsional fatigue test. In the torsional fatigue test, a hydraulic fatigue tester was used, and as shown in FIG. 2, splines 2a and 2b were respectively fit into disk-shaped chucks 3a and 3b and torsional torque was repeatedly applied between the chucks 3a and 3b at a frequency of 1 to 2 Hz.

The hardened layer of the same shaft was etched using an etchant whose main component is picric acid, e.g., a mixture of an aqueous picric acid solution prepared by dissolving 50 g of picric acid in 500 g of water, 11 g of sodium dodecylbenzenesulfonate, 1 g of ferrous chloride, and 1.5 g of oxalic acid. Subsequently, its structure was observed with an optical microscope to determine the average diameter and maximum diameter of the former austenitic grains. The average diameter and the maximum diameter were determined by the same method as one described above.

The resistance to quenching crack was also tested for the same shaft.

The resistance to quenching crack was evaluated in terms of the number of quenching cracks observed, with an optical microscope (magnification: ×100 to ×200), in five polished C-cross-sections of the splines after the high-frequency hardening.

The results are shown in Tables 4-1 and 4-2.

	TABLE 3
	Chemical composition (mass %)	Value of left
Steel type	C	Si	Mn	P	S	Al	N	Others	part of formula (1)-(3)
A	0.48	0.55	0.78	0.011	0.019	0.024	0.0043	—	3.2
B	0.45	0.51	0.81	0.013	0.022	0.029	0.0041	0.3Mo, 0.4Ni	6.6
C	0.43	0.51	0.79	0.011	0.021	0.024	0.0039	0.45Mo, 0.021Ti, 0.0024B	22.6
D	0.43	0.21	0.91	0.011	0.022	0.025	0.0041	0.9Cr, 0.003Ca	8.1
E	0.25	0.21	0.92	0.011	0.022	0.024	0.0042	—	2.2
F	1.52	0.19	0.45	0.012	0.015	0.025	0.0042	1.32Cr	11.5
G	0.45	0.22	2.55	0.011	0.018	0.025	0.0045	—	6.7
H	0.32	0.21	0.55	0.012	0.015	0.025	0.0045	—	1.7
I	0.43	0.21	0.91	0.011	0.022	0.025	0.0041	1.1Cr	9.3
J	0.45	0.21	0.92	0.011	0.022	0.026	0.0041	0.4Mo	6.4
K	0.43	0.22	0.91	0.011	0.022	0.025	0.0042	0.8Cu	3.7
L	0.43	0.21	0.91	0.011	0.022	0.025	0.0041	0.8Ni	3.5
M	0.43	0.21	0.91	0.011	0.022	0.023	0.0043	0.15V	4.9
N	0.44	0.23	0.92	0.011	0.022	0.025	0.0041	0.7W	3.9
O	0.43	0.21	0.91	0.012	0.022	0.025	0.0039	0.06Ti	2.8
P	0.44	0.21	0.91	0.011	0.019	0.025	0.0041	0.03Nb	2.8
Q	0.43	0.21	0.91	0.011	0.022	0.024	0.0042	0.05Zr	2.8
R	0.43	0.21	0.91	0.011	0.022	0.024	0.0042	0.003B	2.8
S	0.48	0.55	0.78	0.011	0.004	0.024	0.0043	—	3.2
T	0.48	0.55	0.78	0.011	0.004	0.024	0.0043	0.02Pb	3.2
U	0.48	0.55	0.78	0.011	0.004	0.024	0.0043	0.02Pb	3.2
V	0.48	0.55	0.78	0.011	0.004	0.024	0.0043	0.01Se	3.2
W	0.48	0.55	0.78	0.011	0.004	0.024	0.0043	0.01Te	3.2
X	0.48	0.55	0.78	0.011	0.004	0.024	0.0043	0.003Ca	3.2
Y	0.48	0.55	0.78	0.011	0.022	0.024	0.0043	0.002Mg	3.2
Z	0.48	0.55	0.78	0.011	0.022	0.024	0.0043	0.002REM	3.2
AA	0.45	0.21	0.92	0.012	0.022	0.026	0.0041	0.4Mo, 0.02Ti	6.4
AB	0.45	0.22	0.92	0.011	0.022	0.026	0.0041	0.02Ti, 0.003B	11.6
AC	0.45	0.21	0.92	0.011	0.004	0.026	0.0041	0.4Mo	6.4
AD	0.43	0.21	0.91	0.012	0.004	0.025	0.0039	0.06Ti	2.8
AE	0.45	0.21	0.92	0.011	0.004	0.026	0.0041	0.4Mo, 0.02Ti	6.4
AF	0.46	0.23	0.92	0.011	0.022	0.026	0.0041	0.02Pb	3.0
AG	0.45	0.21	0.92	0.011	0.019	0.026	0.0041	0.4Mo, 0.02Pb	6.4
AH	0.46	0.21	0.91	0.011	0.019	0.025	0.0041	0.03Nb, 0.02Pb	2.9
AI	0.45	0.21	0.92	0.011	0.019	0.026	0.0041	0.4Mo, 0.02Ti, 0.02Pb	6.4
AJ	0.45	0.45	0.82	0.011	0.031	0.002	0.004	0.4Mo, 0.02Ti, 0.0020B, 0.003Ca	26.9
AK	0.43	0.51	0.79	0.011	0.06	0.002	0.0039	0.45Mo, 0.021Ti, 0.0020B, 0.003Ca	22.6
AL	0.43	0.51	0.79	0.011	0.06	<0.001	0.0039	0.45Mo, 0.021Ti, 0.0020B, 0.003Ca	22.6

	TABLE 4-1
			Pre-hardening
	Hot-working conditions	Working (cold-	structure	HF hardening conditions
		Total processing	Cooling rate	working) ratio	Proportion		Heating	Retention time
	Steel	ratio (%) at	(° C./s) after	(%) at less than	(vol. %)	Heating	temperature	(sec) at 800° C.
No.	type	800° C. to 1000° C.	working	800° C.	of bainite structure	rate (° C./s)	(° C.)	or more
1	A	30	0.7	20	73	800	880	1
2	A	80	0.8	20	71	800	890	1
3	A	80	0.7	50	72	800	870	1
4	A	80	0.06	20	4	800	910	1
5	A	80	0.8	0	72	800	890	1
6	B	80	0.8	20	75	800	870	1
7	C	30	0.7	20	84	800	880	1
8	C	80	0.8	0	83	800	880	1
9	C	80	0.7	20	85	800	880	1
10	C	80	0.8	50	82	800	880	1
11	C	80	0.08	20	7	800	880	1
12	C	80	0.8	0	86	3000	880	1
13	C	80	0.8	10	84	200	900	1
14	C	80	0.8	20	85	800	700	0
15	C	80	0.8	20	86	800	1050	1
16	D	80	0.8	20	79	800	890	1
17	E	80	0.7	20	9	800	890	1
18	F	80	0.7	20	75	800	890	1
19	G	80	0.7	20	70	800	890	1
20	H	80	0.7	20	10	800	890	1
21	A	80	0.8	20	75	2000	800	1
22	I	80	0.8	20	68	800	890	1
23	J	80	0.8	20	82	800	890	1
				Torsional
	Hardened layer structure			fatigue
		Average former	Maximum former	Number (N) of		strength
		austenitic grain	austenitic grain	quenching		(1 × 105)
	No.	diameter (μm)	diameter (μm)	cracks	Tempering	(MPa)	Reference
	1	6.5	35	0	Yes	559	Comp. Ex.
	2	4.8	9.5	0	Yes	845	Inv. Ex.
	3	2.5	5.3	0	Yes	891	Inv. Ex.
	4	13.5	40	5	Yes	560	Comp. Ex.
	5	7.5	48	0	Yes	570	Comp. Ex.
	6	4.8	11	0	Yes	888	Inv. Ex.
	7	5.6	30	0	Yes	680	Comp. Ex.
	8	4.8	35	0	Yes	670	Comp. Ex.
	9	2.5	7	0	Yes	880	Inv. Ex.
	10	1.7	5	0	Yes	925	Inv. Ex.
	11	6.5	35	0	Yes	670	Comp. Ex.
	12	3.5	20	2	Yes	620	Comp. Ex.
	13	8.9	45	0	Yes	622	Comp. Ex.
	14	Undetectable	Undetectable	0	Yes	320	Comp. Ex.
		due to	due to
		incomplete	incomplete
		hardening	hardening
	15	15.5	50	0	Yes	610	Comp. Ex.
	16	4.5	15	0	Yes	889	Inv. Ex.
	17	7.5	45	5	Yes	542	Comp. Ex.
	18	4.5	35	3	Yes	615	Comp. Ex.
	19	4.8	32	0	Yes	720	Comp. Ex.
	20	4.2	35	2	Yes	535	Comp. Ex.
	21	2.8	9	0	Yes	790	Inv. Ex.
	22	4.2	12	0	Yes	845	Inv. Ex.
	23	4.3	12	0	Yes	847	Inv. Ex.
	Rel. Ex.: Example of related art,
	Inv. Ex.: Example of the present invention
	Comp. Ex.: Comparative example

	TABLE 4-2
	Hot-working conditions	Working (cold-
	Total processing		working) ratio (%)
	ratio (%) at		at less than	Pre-	HF hardening conditions
		800° C. to 1000° C.		800° C.	hardening		Retention
		Cooling rate		Proportion (vol. %)	structure	Heating	time (sec) at	Average former
	Steel	(° C./s) after		of bainite	Heating	temperature	800° C. or	austenitic grain
No.	type	working		structure(vol. %)	rate(° C./s)	(° C.)	more	diameter (μm)
24	K	80	0.8	20	79	800	890	1
25	L	80	0.8	20	79	800	890	1
26	M	80	0.8	20	79	800	890	1
27	N	80	0.8	20	79	800	890	1
28	O	80	0.8	20	72	800	890	1
29	p	80	0.8	20	79	800	890	1
30	Q	80	0.8	20	79	800	890	1
31	R	80	0.8	20	79	800	890	1
32	S	80	0.8	20	70	800	890	1
33	T	80	0.8	20	79	800	890	1
34	U	80	0.8	20	79	800	890	1
35	V	80	0.8	20	79	800	890	1
36	W	80	0.8	20	79	800	890	1
37	X	80	0.8	20	79	800	890	1
38	Y	80	0.8	20	79	800	890	1
39	Z	80	0.8	20	79	800	890	1
40	AA	80	0.8	20	85	800	890	1
41	AB	80	0.8	20	79	800	890	1
42	AC	80	0.8	20	80	800	890	1
43	AD	80	0.8	20	79	800	890	1
44	AE	80	0.8	20	79	800	890	1
45	AF	80	0.8	20	79	800	890	1
46	AG	80	0.8	20	79	800	890	1
47	AH	80	0.8	20	79	800	890	1
48	AI	80	0.8	20	85	800	890	1
49	C	80	0.8	50	82	800	880	1
50	AJ	80	0.8	20	83	800	930	2
51	AK	80	0.8	20	81	500	930	3
52	AL	80	0.8	20	81	500	930	3
	Hardened			Torsional
	layer structure	Number (N)		fatigue
		Maximum former		of		strength
		austenitic grain		quenching		(1 × 105)
	No.	diameter (μm)		cracks	Tempering	(MPa)	Reference
	24	3.9	11	0	Yes	849	Inv. Ex.
	25	4.3	12	0	Yes	851	Inv. Ex.
	26	4.2	12	0	Yes	852	Inv. Ex.
	27	4.3	12	0	Yes	855	Inv. Ex.
	28	3.9	11	0	Yes	858	Inv. Ex.
	29	4.3	12	0	Yes	861	Inv. Ex.
	30	3.8	10	0	Yes	864	Inv. Ex.
	31	4.3	12	0	Yes	867	Inv. Ex.
	32	4.2	12	0	Yes	846	Inv. Ex.
	33	4.3	12	0	Yes	873	Inv. Ex.
	34	4.5	13	0	Yes	845	Inv. Ex.
	35	4.3	12	0	Yes	865	Inv. Ex.
	36	3.8	10	0	Yes	889	Inv. Ex.
	37	4.3	12	0	Yes	855	Inv. Ex.
	38	4.2	12	0	Yes	858	Inv. Ex.
	39	4.3	12	0	Yes	861	Inv. Ex.
	40	3.9	11	0	Yes	864	Inv. Ex.
	41	4.3	12	0	Yes	867	Inv. Ex.
	42	3.8	10	0	Yes	846	Inv. Ex.
	43	4.3	12	0	Yes	873	Inv. Ex.
	44	3.9	11	0	Yes	855	Inv. Ex.
	45	4.3	12	0	Yes	858	Inv. Ex.
	46	3.8	10	0	Yes	861	Inv. Ex.
	47	4.2	12	0	Yes	864	Inv. Ex.
	48	3.7	10	0	Yes	867	Inv. Ex.
	49	1.7	5	0	No	1000	Inv. Ex.
	50	3.1	10	0	No	900	Inv. Ex.
	51	3.9	10	0	No	910	Inv. Ex.
	52	4.0	10	0	Yes	905	Inv. Ex.
	Rel. Ex.: Example of related art,
	Inv. Ex.: Example of the present invention
	Comp. Ex.: Comparative example

Tables 4-1 and 4-2 clearly show that every shaft with a hardened structure in which the average former austenitic grain diameter was 12 μm or less and the maximum grain diameter did not exceed four times the average grain diameter exhibited high torsional fatigue strength and excellent resistance to quench cracking, i.e., the number of quench cracking being zero.

In contrast, shafts with hardened structures in which the average former austenitic grain diameter was 12 μm or more and the maximum grain diameter exceeded four times the average grain diameter all exhibited low fatigue strength.

Example 2

A crankshaft shown in FIG. 8 was prepared as a component for machine structural use of the present invention. A crankshaft 4 has journals 5 to a cylinder, crank pins 6, which are bearings for a piston connecting rod, crank webs 7, and counter weights 8. The journals 5 and the crank pins 6 are subjected to high-frequency hardening to increase the fatigue strength.

Each of steel materials having compositions shown in Table 3 was melted in a converter and cast into a cast slab by continuous casting. The size of the cast slab was 300×400 [mm]. The cast slab was hot-rolled to prepare a steel bar having a diameter of 90 mm. The steel bar was cut to a predetermined length, hot-forged in the temperature range of 700° C. to 1,100° C. from bending to finish, deburred, and formed into a shape of a crankshaft, followed by cooling at a rate shown in Tables 5-1 and 5-2. During the hot-forging, the hot-forging process was divided into a plurality of steps. The last stage of the hot-forging was conducted at 700° C. to less than 800° C., and all other steps were conducted at 800° C. to 1,000° C. In each of the steps, the diameter of the crank pins was adjusted to control the total processing ratio at 800° C. to 1,000° C. and the total processing ratio at 700° C. to less than 800° C.

Subsequently, as shown in a cross-sectional view of the crankshaft in FIG. 9, the surfaces of the crank pins and journals of the crankshaft were subjected to high-frequency hardening under the conditions set forth in Tables 5-1 and 5-2 to form hardened structure layers 9. The crankshaft was then tempered at 170° C. for 30 min and subjected to finishing to prepare a product. Some of the crankshafts were not subjected to tempering.

The bending fatigue life of the crankshaft obtained thereby was tested. The results are shown in Tables 5-1 and 5-2.

The bending fatigue life of the crankshaft was evaluated as follows.

As shown in FIG. 10, while fixing the ends of the crankshaft, an endurance test was conducted by repeatedly applying a predetermined load (5,000 N) to each connecting rod. The number of cycles of load application before breaking of the pin or journal was used for evaluating the bending fatigue life.

The average diameter and the maximum grain diameter of the former austenitic grains in the hardened layer of the same crankshaft were determined by the same method as one described above.

The results are also described in Tables 5-1 and 5-2.

	TABLE 5-1
	Hot-working conditions	Pre-hardening	HF hardening conditions
		Total processing	Cooling rate	Total processing	structure		Heating	Retention time
	Steel	ratio (%) at	(° C./s) after	ratio (%) at less	Proportion (vol. %)	Heating	temperature	(sec) at 800° C.
No.	type	800° C. to 1000° C.	working	than 800° C.	of bainite structure	rate (° C./s)	(° C.)	or more
1	A	30	0.7	20	73	800	880	1
2	A	80	0.8	20	71	800	890	1
3	A	80	0.7	50	72	800	870	1
4	A	80	0.06	20	4	800	910	1
5	A	80	0.8	0	72	800	890	1
6	B	80	0.8	20	75	800	870	1
7	C	30	0.7	20	84	800	880	1
8	C	80	0.8	0	83	800	880	1
9	C	80	0.7	20	85	800	880	1
10	C	80	0.8	50	82	800	880	1
11	C	80	0.08	20	7	800	880	1
12	C	80	0.8	0	86	3000	880	1
13	C	80	0.8	10	84	200	900	1
14	C	80	0.8	20	85	800	700	0
15	C	80	0.8	20	86	800	1050	1
16	D	80	0.8	20	79	800	890	1
17	E	80	0.7	20	9	800	890	1
18	F	80	0.7	20	75	800	890	1
19	G	80	0.7	20	70	800	890	1
20	H	80	0.7	20	10	800	890	1
21	A	80	0.8	20	75	2000	800	1
22	I	80	0.8	20	68	800	890	1
23	J	80	0.8	20	82	800	890	1
	Hardened layer structure
		Average former	Maximum former		Bending
		austenitic grain	austenitic grain		fatigue life
	No.	diameter (μm)	diameter (μm)	Tempering	(×106)	Reference
	1	6.5	35	Yes	2.2	Comp. Ex.
	2	4.8	9.5	Yes	9.5	Inv. Ex.
	3	2.5	5.3	Yes	12.0	Inv. Ex.
	4	13.5	40	Yes	2.2	Comp. Ex.
	5	7.5	48	Yes	2.3	Comp. Ex.
	6	4.8	11	Yes	11.8	Inv. Ex.
	7	5.6	30	Yes	4.1	Comp. Ex.
	8	4.8	35	Yes	3.9	Comp. Ex.
	9	2.5	7	Yes	11.4	Inv. Ex.
	10	1.7	5	Yes	14.3	Inv. Ex.
	11	6.5	35	Yes	3.9	Comp. Ex.
	12	3.5	20	Yes	3.0	Comp. Ex.
	13	8.9	45	Yes	3.1	Comp. Ex.
	14	Undetectable	Undetectable	Yes	0.7	Comp. Ex.
		due to	due to
		incomplete	incomplete
		hardening	hardening
	15	15.5	50	Yes	2.9	Comp. Ex.
	16	4.5	15	Yes	11.9	Inv. Ex.
	17	7.5	45	Yes	2.0	Comp. Ex.
	18	4.5	35	Yes	2.9	Comp. Ex.
	19	4.8	32	Yes	5.0	Comp. Ex.
	20	4.2	35	Yes	2.0	Comp. Ex.
	21	2.8	9	Yes	9.4	Inv. Ex.
	22	4.2	12	Yes	9.5	Inv. Ex.
	23	4.3	12	Yes	9.6	Inv. Ex.
	Rel. Ex.: Example of related art,
	Inv. Ex.: Example of the present invention
	Comp. Ex.: Comparative example

	TABLE 5-2
	Hot-working conditions	Pre-hardening	HF hardening conditions
		Total processing	Cooling rate	Total processing	structure		Heating	Retention time
	Steel	ratio (%) at	(° C./s) after	ratio (%) at less	Proportion (vol. %)	Heating	temperature	(sec) at 800° C.
No.	type	800° C. to 1000° C.	working	than 800° C.	of bainite structure	rate (° C./s)	(° C.)	or more
24	K	80	0.8	20	79	800	890	1
25	L	80	0.8	20	79	800	890	1
26	M	80	0.8	20	79	800	890	1
27	N	80	0.8	20	79	800	890	1
28	O	80	0.8	20	72	800	890	1
29	P	80	0.8	20	79	800	890	1
30	Q	80	0.8	20	79	800	890	1
31	R	80	0.8	20	79	800	890	1
32	S	80	0.8	20	70	800	890	1
33	T	80	0.8	20	79	800	890	1
34	U	80	0.8	20	79	800	890	1
35	V	80	0.8	20	79	800	890	1
36	W	80	0.8	20	79	800	890	1
37	X	80	0.8	20	79	800	890	1
38	Y	80	0.8	20	79	800	890	1
39	Z	80	0.8	20	79	800	890	1
40	AA	80	0.8	20	85	800	890	1
41	AB	80	0.8	20	79	800	890	1
42	AC	80	0.8	20	80	800	890	1
43	AD	80	0.8	20	79	800	890	1
44	AE	80	0.8	20	79	800	890	1
45	AF	80	0.8	20	79	800	890	1
46	AG	80	0.8	20	79	800	890	1
47	AH	80	0.8	20	79	800	890	1
48	AI	80	0.8	20	85	800	890	1
49	C	80	0.8	50	82	800	880	1
50	AJ	80	0.8	20	83	800	930	2
51	AK	80	0.8	20	81	500	930	3
52	AK	80	0.8	20	81	500	930	3
	Hardened layer structure
		Average former	Maximum former		Bending
		austenitic grain	austenitic grain		fatigue life
	No.	diameter (μm)	diameter (μm)	Tempering	(×106)	Reference
	24	3.9	11	Yes	9.7	Inv. Ex.
	25	4.3	12	Yes	9.8	Inv. Ex.
	26	4.2	12	Yes	9.9	Inv. Ex.
	27	4.3	12	Yes	10.0	Inv. Ex.
	28	3.9	11	Yes	10.2	Inv. Ex.
	29	4.3	12	Yes	10.3	Inv. Ex.
	30	3.8	10	Yes	10.5	Inv. Ex.
	31	4.3	12	Yes	10.6	Inv. Ex.
	32	4.2	12	Yes	9.6	Inv. Ex.
	33	4.3	12	Yes	11.0	Inv. Ex.
	34	4.5	13	Yes	9.5	Inv. Ex.
	35	4.3	12	Yes	10.5	Inv. Ex.
	36	3.8	10	Yes	11.9	Inv. Ex.
	37	4.3	12	Yes	10.0	Inv. Ex.
	38	4.2	12	Yes	10.2	Inv. Ex.
	39	4.3	12	Yes	10.3	Inv. Ex.
	40	3.9	11	Yes	10.5	Inv. Ex.
	41	4.3	12	Yes	10.6	Inv. Ex.
	42	3.8	10	Yes	9.6	Inv. Ex.
	43	4.3	12	Yes	11.0	Inv. Ex.
	44	3.9	11	Yes	10.0	Inv. Ex.
	45	4.3	12	Yes	10.2	Inv. Ex.
	46	3.8	10	Yes	10.3	Inv. Ex.
	47	4.2	12	Yes	10.5	Inv. Ex.
	48	3.7	10	Yes	10.6	Inv. Ex.
	49	1.7	5	No	15.2	Inv. Ex.
	50	3.1	10	Yes	10.5	Inv. Ex.
	51	3.9	10	Yes	10.5	Inv. Ex.
	52	4.0	10	Yes	10.5	Inv. Ex.
	Rel. Ex.: Example of related art,
	Inv. Ex.: Example of the present invention
	Comp. Ex.: Comparative example

Tables 5-1 and 5-2 clearly show that every shaft with a hardened structure where an average grain diameter of former austenitic grains in the hardened layer was 12 μm or less and a maximum grain diameter did not exceed four times the average diameter exhibited excellent bending fatigue life, i.e., the number of times of application of the load to breaking being 9×10⁶ or more.

In contrast, those having an average grain diameter of former austenitic grains of 12 μm or less and a maximum grain diameter exceeding four times the average grain diameter exhibited low bending life strength.

Example 3

A constant velocity joint 12 for transmitting power from a drive shaft 10 to a hub 11 of a wheel was prepared as a component for machine structural use of the present invention.

The constant velocity joint 12 is a combination of an outer race 13 and an inner race 14. In particular, the inner race 14 is movably fixed to the inner side of a mouth 13a of the outer race 13 via balls 15 fit in a ball track groove in the inner surface of the mouth 13a and is connected to the drive shaft 10; meanwhile, a stem 13b of the outer race 13 is for example splined to the hub 11 to transmit power from the drive shaft 10 to the hub 11 of the wheel.

Each of steel materials having compositions shown in Table 3 was melted in a converter and cast into a cast slab by continuous casting. The size of the cast slab was 300×400 [mm]. The cast slab was subjected to a breakdown step and rolled into a 150 mm square billet. The billet was then rolled to prepare a steel bar having a diameter of 50 mm.

Next, the steel bar was cut to a predetermined length, hot-forged under the conditions set forth in Table 6-1, 6-2, 7-1, or 7-2 at a temperature 800° C. or more, and formed such that the mouth (outer diameter: 600 mm) and the stem (diameter: 20 mm) of the constant velocity joint outer race were integrally combined. Subsequently, the tracking groove for balls is formed in the inner surface of the mouth of the constant velocity joint outer race by cutting or cold forging, and, at the same time, the stem of the constant velocity joint outer race was formed into a spline shaft by cutting or rolling. The cooling after the hot-forging were conducted under the conditions set forth in Tables 6-1, 6-2, 7-1, and 7-2. The total processing ratio in the hot-forging and the forming by rolling was adjusted by controlling the rate of change in cross-sectional area of a cross section taken in the direction orthogonal to the axis direction of the component to which the high-frequency hardening was effected.

As shown in FIG. 12 or 13, the inner surface of the mouth 13a or the outer surface of the stem 13b of the constant velocity joint outer race 13 was hardened using a 15 kHz high-frequency hardening apparatus to form a hardened structure layer 16 and then tempered at 180° C. for 2 hours in a heating furnace to prepare a product. The conditions for the tempering were set forth in Tables 6-1, 6-2, 7-1, and 7-2. The tempering was omitted for some of the constant velocity joint outer races. The resulting constant velocity joint outer race was attached, via balls (steel balls) in the mouth, to the inner race connected to the drive shaft, and the stem was fit into the hub to prepare a constant velocity joint unit (see FIG. 11). The specifications for the balls, the inner race, and the hub were as follows:

balls: hardened and tempered high-carbon chromium bearing steel SUJ2

inner race: carburized, hardened, and tempered chromium steel SCr

hub: carburized steel for machine structural use

Next, using this constant velocity joint unit, the endurance test for determining rolling fatigue strength was conducted for those units in which the inner surface of the mouth was subjected to high-frequency hardening and the endurance test for determining torsional fatigue strength was conducted for those units in which the outer surface of the stem was subjected to high-frequency hardening, both the tests being conducted in a power transmission system for transmitting the rotary action of the drive shaft to the hub through the inner race and the outer race of the constant velocity joint.

In the rolling fatigue strength test, power transmission was conducted at a torque of 900 N·m, a working angle (the angle defined by the axis line of the outer race and the axis line of the drive shaft) of 20°, and a number of revolution of 300 rpm. The time taken until the inner surface of the mouth was broken by rolling fatigue was evaluated as the rolling fatigue strength.

In this power transmission system, the endurance test for determining the torsional fatigue strength was conducted. In the torsional fatigue test, the working angle of the constant velocity joint unit (the angle defined by the axis line of the outer race and the axis line of the drive shaft) was set to 0° and a torsional fatigue tester with a maximum torque of 4900 N·m was used to apply torsional force between the hub and the drive shaft, and the maximum torque of the stem was changed so that the stress conditions are fully reversed. The stress at which the number of cycles to fracture was 1×10⁵ was evaluated as the torsional fatigue strength.

In the torsional fatigue test, the shape and dimensions of the hub and the drive shaft were adjusted so that the strength of the hub and the drive shaft were large enough for the evaluation of the torsional fatigue of the outer race of the constant velocity joint.

Likewise, in the rolling fatigue test, the shape and dimensions of the constant velocity joint inner race, steel balls, and the like were adjusted so that the inner surface of the constant velocity joint outer race was the weakest part in the endurance test.

The constant velocity joint outer races prepared under the same conditions were analyzed to determine the average diameter and the maximum diameter of the former austenitic grains in the hardened layer by the above-described process.

The results are shown in Tables 6-1, 6-2, 7-1, and 7-2.

	TABLE 6-1
	Hot-working conditions
	Total			Pre-hardening	HF hardening conditions
		processing ratio	Cooling rate	Total processing	structure		Heating	Retention time
	Steel	(%) at 800° C. to	(° C./s) after	ratio (%) at less	Proportion (vol. %)	Heating	temperature	(sec) at 800° C.
No.	type	1000° C.	working	than 800° C. *1	of bainite structure	rate ° C./s)	(° C.)	or more
1	A	30	0.7	20	73	800	880	1
2	A	80	0.8	20	71	800	890	1
3	A	80	0.7	50	72	800	870	1
4	A	80	0.06	20	4	800	910	1
5	A	80	0.8	0	72	800	890	1
6	B	80	0.8	20	75	800	870	1
7	C	30	0.7	20	84	800	880	1
8	C	80	0.8	0	83	800	880	1
9	C	80	0.7	20	85	800	880	1
10	C	80	0.8	50	82	800	880	1
11	C	80	0.08	20	7	800	880	1
12	C	80	0.8	0	86	3000	880	1
13	C	80	0.8	10	84	200	900	1
14	C	80	0.8	20	85	800	700	0
15	C	80	0.8	20	86	800	1050	1
16	D	80	0.8	20	79	800	890	1
17	E	80	0.7	20	9	800	890	1
18	F	80	0.7	20	75	800	890	1
19	G	80	0.7	20	70	800	890	1
20	H	80	0.7	20	10	800	890	1
21	A	80	0.8	20	75	2000	800	1
22	I	80	0.8	20	68	800	890	1
23	J	80	0.8	20	82	800	890	1
24	K	80	0.8	20	79	800	890	1
25	L	80	0.8	20	79	800	890	1
26	M	80	0.8	20	79	800	890	1
27	N	80	0.8	20	79	800	890	1
	Hardened layer structure
		Average former	Maximum former
		austenitic grain	austenitic grain		Rolling fatigue
	No.	diameter (μm)	diameter (μm)	Tempering	life (hr)	Reference
	1	6.5	35	Yes	79	Comp. Ex.
	2	4.8	9.5	Yes	136	Inv. Ex.
	3	2.5	5.3	Yes	148	Inv. Ex.
	4	13.5	40	Yes	79	Comp. Ex.
	5	7.5	48	Yes	81	Comp. Ex.
	6	4.8	11	Yes	147	Inv. Ex.
	7	5.6	30	Yes	99	Comp. Ex.
	8	4.8	35	Yes	97	Comp. Ex.
	9	2.5	7	Yes	145	Inv. Ex.
	10	1.7	5	Yes	158	Inv. Ex.
	11	6.5	35	Yes	97	Comp. Ex.
	12	3.5	20	Yes	89	Comp. Ex.
	13	8.9	45	Yes	89	Comp. Ex.
	14	Undetectable	Undetectable	Yes	50	Comp. Ex.
		due to	due to
		incomplete	incomplete
		hardening	hardening
	15	15.5	50	Yes	87	Comp. Ex.
	16	4.5	15	Yes	148	Inv. Ex.
	17	7.5	45	Yes	76	Comp. Ex.
	18	4.5	35	Yes	88	Comp. Ex.
	19	4.8	32	Yes	98	Comp. Ex.
	20	4.2	35	Yes	75	Comp. Ex.
	21	2.8	9	Yes	139	Inv. Ex.
	22	4.2	12	Yes	136	Inv. Ex.
	23	4.3	12	Yes	136	Inv. Ex.
	24	3.9	11	Yes	137	Inv. Ex.
	25	4.3	12	Yes	137	Inv. Ex.
	26	4.2	12	Yes	138	Inv. Ex.
	27	4.3	12	Yes	139	Inv. Ex.
	*1: If value in the column is zero, the inner surface of the mouth is formed by cutting. Otherwise, the inner surface of the mouth is formed by cold-forging and the figure in the column indicates the processing ratio.
	Rel. Ex.: Example of related art,
	Inv. Ex.: Example of the present invention
	Comp. Ex.: Comparative example

	TABLE 6-2
	Hot-working				Hardened
	conditions	Total	Pre-		layer structure
	Total		processing	hardening	HF hardening conditions	Average	Maximum
		processing	Cooling	ratio (%)	structure			Retention	former	former
		ratio (%)	rate	at less	Proportion			time	austenitic	austenitic
		at	(° C./s)	than	(vol. %)	Heating	Heating	(sec) at	grain	grain		Rolling
	Steel	800° C. to	after	800° C.	of bainite	rate	temperature	800° C.	diameter	diameter	Tem-	fatigue
No.	type	1000° C.	working	*1	structure	(° C./s)	(° C.)	or more	(μm)	(μm)	pering	life (hr)	Reference
28	O	80	0.8	20	72	800	890	1	3.9	11	Yes	139	Inv. Ex.
28	O	80	0.8	20	72	800	890	1	3.9	11	Yes	139	Inv. Ex.
29	P	80	0.8	20	79	800	890	1	4.3	12	Yes	140	Inv. Ex.
30	Q	80	0.8	20	79	800	890	1	3.8	10	Yes	141	Inv. Ex.
31	R	80	0.8	20	79	800	890	1	4.3	12	Yes	142	Inv. Ex.
32	S	80	0.8	20	70	800	890	1	4.2	12	Yes	136	Inv. Ex.
AJ	0.45	0.45	0.82	0.011	0.031	0.002	0.004	0.4Mo,	26.9	12	Yes	143	Inv. Ex.
								0.02Ti,
								0.0020B,
								0.003Ca
AK	0.43	0.51	0.79	0.011	0.06	0.002	0.0039	0.45Mo,	22.6	13	Yes	136	Inv. Ex.
								0.021Ti,
								0.0020B,
								0.003Ca
35	V	80	0.8	20	79	800	890	1	4.3	12	Yes	141	Inv. Ex.
36	W	80	0.8	20	79	800	890	1	3.8	10	Yes	148	Inv. Ex.
37	X	80	0.8	20	79	800	890	1	4.3	12	Yes	139	Inv. Ex.
38	Y	80	0.8	20	79	800	890	1	4.2	12	Yes	139	Inv. Ex.
39	Z	80	0.8	20	79	800	890	1	4.3	12	Yes	140	Inv. Ex.
40	AA	80	0.8	20	85	800	890	1	3.9	11	Yes	141	Inv. Ex.
41	AB	80	0.8	20	79	800	890	1	4.3	12	Yes	142	Inv. Ex.
42	AC	80	0.8	20	80	800	890	1	3.8	10	Yes	136	Inv. Ex.
43	AD	80	0.8	20	79	800	890	1	4.3	12	Yes	143	Inv. Ex.
44	AE	80	0.8	20	79	800	890	1	3.9	11	Yes	139	Inv. Ex.
45	AF	80	0.8	20	79	800	890	1	4.3	12	Yes	139	Inv. Ex.
46	AG	80	0.8	20	79	800	890	1	3.8	10	Yes	140	Inv. Ex.
47	AH	80	0.8	20	79	800	890	1	4.2	12	Yes	141	Inv. Ex.
48	AI	80	0.8	20	85	800	890	1	3.7	10	Yes	142	Inv. Ex.
49	C	80	0.8	50	82	800	880	1	1.7	5	No	172	Inv. Ex.
50	AJ	80	0.8	20	83	800	930	2	3.1	10	Yes	140	Inv. Ex.
51	AK	80	0.8	20	81	500	930	3	3.9	10	Yes	138	Inv. Ex.
52	AL	80	0.8	20	81	500	930	3	4.0	10	Yes	135	Inv. Ex.
*1: If value in the column is zero, the inner surface of the mouth is formed by cutting. Otherwise, the inner surface of the mouth is formed by cold-forging and the figure in the column indicates the processing ratio.
Rel. Ex.: Example of related art,
Inv. Ex.: Example of the present invention
Comp. Ex.: Comparative example

	TABLE 7-1
	Hot-working				Hardened
	conditions	Total	Pre-		layer structure
	Total		processing	hardening	HF hardening conditions	Average	Maximum
		processing	Cooling	ratio (%)	structure			Retention	former	former		Torsional
		ratio (%)	rate	at less	Proportion		Heating	time	austenitic	austenitic		fatigue
		at	(° C./s)	than	(vol. %)	Heating	temper-	(sec) at	grain	grain		strength
	Steel	800° C. to	after	800° C.	of bainite	rate	ature	800° C.	diameter	diameter	Tem-	(×105)
No.	type	1000° C.	working	*2	structure	(° C./s)	(° C.)	or more	(μm)	(μm)	pering	(MPa)	Reference
1	A	30	0.7	20	73	800	880	1	6.5	35	Yes	481	Comp. Ex.
2	A	80	0.8	20	71	800	890	1	4.8	9.5	Yes	783	Inv. Ex.
3	A	80	0.7	50	72	800	870	1	2.5	5.3	Yes	832	Inv. Ex.
4	A	80	0.06	20	4	800	910	1	13.5	40	Yes	482	Comp. Ex.
5	A	80	0.8	0	72	800	890	1	7.5	48	Yes	493	Comp. Ex.
6	B	80	0.8	20	75	800	870	1	4.8	11	Yes	829	Inv. Ex.
7	C	30	0.7	20	84	800	880	1	5.6	30	Yes	609	Comp. Ex.
8	C	80	0.8	0	83	800	880	1	4.8	35	Yes	598	Comp. Ex.
9	C	80	0.7	20	85	800	880	1	2.5	7	Yes	820	Inv. Ex.
10	C	80	0.8	50	82	800	880	1	1.7	5	Yes	868	Inv. Ex.
11	C	80	0.08	20	7	800	880	1	6.5	35	Yes	598	Comp. Ex.
12	C	80	0.8	0	86	3000	880	1	3.5	20	Yes	545	Comp. Ex.
13	C	80	0.8	10	84	200	900	1	8.9	45	Yes	548	Comp. Ex.
14	C	80	0.8	20	85	800	700	0	Un-	Un-	Yes	229	Comp. Ex.
									detectable	detectable
									due to in-	due to in-
									complete	complete
									hardening	hardening
15	C	80	0.8	20	86	800	1050	1	15.5	50	Yes	535	Comp. Ex.
16	D	80	0.8	20	79	800	890	1	4.5	15	Yes	830	Inv. Ex.
17	E	80	0.7	20	9	800	890	1	7.5	45	Yes	463	Comp. Ex.
18	F	80	0.7	20	75	800	890	1	4.5	35	Yes	540	Comp. Ex.
19	G	80	0.7	20	70	800	890	1	4.8	32	Yes	651	Comp. Ex.
20	H	80	0.7	20	10	800	890	1	4.2	35	Yes	456	Comp. Ex.
21	A	80	0.8	20	75	2000	800	1	2.8	9	Yes	789	Inv. Ex.
22	I	80	0.8	20	68	800	890	1	4.2	12	Yes	783	Inv. Ex.
23	J	80	0.8	20	82	800	890	1	4.3	12	Yes	785	Inv. Ex.
24	K	80	0.8	20	79	800	890	1	3.9	11	Yes	787	Inv. Ex.
25	L	80	0.8	20	79	800	890	1	4.3	12	Yes	789	Inv. Ex.
26	M	80	0.8	20	79	800	890	1	4.2	12	Yes	791	Inv. Ex.
27	N	80	0.8	20	79	800	890	1	4.3	12	Yes	794	Inv. Ex.
*2: If value in the column is zero, the spline is formed by cutting. Otherwise, the spline is formed by rolling and the figure in the column indicates the processing ratio.
Rel. Ex.: Example of related art,
Inv. Ex.: Example of the present invention
Comp. Ex.: Comparative example

	TABLE 7-2
	Hot-working				Hardened
	conditions	Total	Pre-		layer structure
	Total		processing	hardening	HF hardening conditions	Average	Maximum
		processing	Cooling	ratio (%)	structure			Retention	former	former		Torsional
		ratio (%)	rate	at less	Proportion		Heating	time	austenitic	austenitic		fatigue
		at	(° C./s)	than	(vol. %)	Heating	temper-	(sec) at	grain	grain		strength
	Steel	800° C. to	after	800° C.	of bainite	rate	ature	800° C.	diameter	diameter	Tem-	(×105)
No.	type	1000° C.	working	*2	structure	(° C./s)	(° C.)	or more	(μm)	(μm)	pering	(MPa)	Reference
28	O	80	0.8	20	72	800	890	1	3.9	11	Yes	797	Inv. Ex.
29	P	80	0.8	20	79	800	890	1	4.3	12	Yes	800	Inv. Ex.
30	Q	80	0.8	20	79	800	890	1	3.8	10	Yes	803	Inv. Ex.
31	R	80	0.8	20	79	800	890	1	4.3	12	Yes	806	Inv. Ex.
32	S	80	0.8	20	70	800	890	1	4.2	12	Yes	784	Inv. Ex.
AJ	0.45	0.45	0.82	0.011	0.031	0.002	0.004	0.4Mo,	26.9	12	Yes	813	Inv. Ex.
								0.02Ti,
								0.0020B,
								0.003Ca
AK	0.43	0.51	0.79	0.011	0.06	0.002	0.0039	0.45Mo,	22.6	13	Yes	783	Inv. Ex.
								0.021Ti,
								0.0020B,
								0.003Ca
35	V	80	0.8	20	79	800	890	1	4.3	12	Yes	804	Inv. Ex.
36	W	80	0.8	20	79	800	890	1	3.8	10	Yes	830	Inv. Ex.
37	X	80	0.8	20	79	800	890	1	4.3	12	Yes	794	Inv. Ex.
38	Y	80	0.8	20	79	800	890	1	4.2	12	Yes	797	Inv. Ex.
39	Z	80	0.8	20	79	800	890	1	4.3	12	Yes	800	Inv. Ex.
40	AA	80	0.8	20	85	800	890	1	3.9	11	Yes	803	Inv. Ex.
41	AB	80	0.8	20	79	800	890	1	4.3	12	Yes	806	Inv. Ex.
42	AC	80	0.8	20	80	800	890	1	3.8	10	Yes	784	Inv. Ex.
43	AD	80	0.8	20	79	800	890	1	4.3	12	Yes	813	Inv. Ex.
44	AE	80	0.8	20	79	800	890	1	3.9	11	Yes	794	Inv. Ex.
45	AF	80	0.8	20	79	800	890	1	4.3	12	Yes	797	Inv. Ex.
46	AG	80	0.8	20	79	800	890	1	3.8	10	Yes	800	Inv. Ex.
47	AH	80	0.8	20	79	800	890	1	4.2	12	Yes	803	Inv. Ex.
48	AI	80	0.8	20	85	800	890	1	3.7	10	Yes	806	Inv. Ex.
49	C	80	0.8	50	82	800	880	1	1.7	5	No	950	Inv. Ex.
50	AJ	80	0.8	20	83	800	930	2	3.1	10	Yes	810	Inv. Ex.
51	AK	80	0.8	20	81	500	930	3	3.9	10	Yes	780	Inv. Ex.
52	AL	80	0.8	20	81	500	930	3	4.0	10	Yes	770	Inv. Ex.
*2: If value in the column is zero, the spline is formed by cutting. Otherwise, the spline is formed by rolling and the figure in the column indicates the processing ratio.
Rel. Ex.: Example of related art,
Inv. Ex.: Example of the present invention
Comp. Ex.: Comparative example

Tables 6-1, 6-2, 7-1, and 7-2 clearly show that every constant velocity joint outer race with a hardened structure in which the average former austenitic grain diameter was 12 μm or less and the maximum grain diameter did not exceed four times the average grain diameter exhibited excellent rolling fatigue properties and torsional fatigue strength.

In contrast, the constant velocity joint outer races with an average former austenitic grain diameter exceeding 12 μm and a maximum grain diameter exceeding four times the average grain diameter exhibited poor rolling fatigue and torsional fatigue properties.

Example 4

A constant velocity joint 12 shown in FIG. 14 for transmitting power from a drive shaft 10 to a hub 11 of a wheel was prepared as the component for a machine structural use according to the present invention.

The constant velocity joint 12 was a combination of an outer race 13 and an inner race 14. In particular, the inner race 14 was movably fixed to the inner side of a mouth 13a of the outer race 13 via balls 15 fit in a ball tracking groove in the inner surface of the mouth 13a and was connected to the drive shaft 10; meanwhile, a stem 13b of the outer race 13 was for example splined to the hub 11 to transmit power from the drive shaft 10 to the hub 11 of the wheel.

Each of steel materials having compositions shown in Table 3 was melted in a converter and cast into a cast slab by continuous casting. The size of the cast slab was 300×400 [mm]. The cast slab was subjected to a breakdown step and rolled into a 150 mm square billet. The billet was then rolled to prepare a steel bar having a diameter of 55 mm.

Next, the steel bar was cut to a predetermined length and formed into a constant velocity joint inner race (outer diameter: 45 mm, inner diameter: 20 mm) by hot-forging. The fitting surface thereof was cut or rolled to form riffles for splining. A surface for contact rolling with balls was formed by cutting or cold forging. The cooling conditions after the hot-forging are shown in Tables 8-1, 8-2, 9-1, and 9-2. The total processing ratio in the hot-forging and cold forging was adjusted by controlling the reduction ratio of area of a cross-section taken in the direction orthogonal to the axis direction of the contact rolling surface.

As shown in FIG. 15 or 16, a fitting surface 14b of the constant velocity joint inner race into which the drive shaft fits and a contact rolling surface 14a onto which the balls interposed between the inner race and the constant velocity joint outer race make rolling contact were hardened with a 15 Hz high-frequency hardening apparatus under the conditions set forth in Tables 8-1, 8-2, 9-1, and 9-2 to thereby form a hardened structure layer 16. Subsequently, tempering at 180° C. was conducted for 2 hours in a heating furnace to harden the layer. The tempering was omitted for some of the constant velocity joints. The drive shaft was fitted to the fitting surface of the resulting constant velocity joint inner race, and the constant velocity joint inner race was attached to the mouth of the constant velocity joint outer race via balls (steel balls). The stem of the constant velocity joint outer race was fit to the hub to prepare a constant velocity joint unit (see FIG. 11). The specifications for the balls, the outer race, the drive shaft, and the hub were as follows:

balls: hardened and tempered high-carbon chromium bearing steel SUJ2

outer race: high-frequency hardened, tempered carburized steel for machine structural use

hub: high-frequency hardened, tempered carburized steel for machine structural use

drive shaft: high-frequency hardened, tempered carburized steel for machine structural use

Next, using this constant velocity joint, the endurance test for determining rolling fatigue strength was conducted for those in which the fitting surface with the drive shaft was subjected to high-frequency hardening, and the endurance test for determining torsional fatigue strength was conducted for those in which the contact rolling surface with the balls was subjected to high-frequency hardening, both the tests being conducted in a power transmission system for transmitting the rotary action of the drive shaft to the hub through the inner race of the constant velocity joint.

In the rolling fatigue test, power transmission was conducted at a torque of 900 N·m, a working angle (the angle defined by the axis line of the inner race and the axis line of the drive shaft) of 20°, and a number of revolution of 300 rpm. The time taken until separation occurred in the contact rolling surface of the constant velocity joint inner race was evaluated as the rolling fatigue strength. The dimensions and shape of the drive shaft, the constant velocity joint outer race, and the like were adjusted so that the constant velocity joint inner race was the weakest portion in the endurance test.

The constant velocity joint inner races prepared under the same conditions were analyzed to determine the average diameter and the maximum diameter of the former austenitic grains in the hardened layers by the above-described process.

The results are shown in Tables 8-1, 8-2, 9-1, and 9-2.

	TABLE 8-1
	Hot-working				Hardened
	conditions	Total	Pre-		layer structure
	Total		processing	hardening	HF hardening conditions	Average	Maximum
		processing	Cooling	ratio (%)	structure			Retention	former	former		Sliding
		ratio (%)	rate	at less	Proportion		Heating	time	austenitic	austenitic		rolling
		at	(C. °/s)	than	(vol. %)	Heating	temper-	(sec) at	grain	grain		contact
	Steel	800° C. to	after	800° C.	of bainite	rate	ature	800° C.	diameter	diameter	Tem-	fatigue
No.	type	1000° C.	working	*3	structure	(° C./s)	(° C.)	or more	(μm)	(μm)	pering	life (hr)	Reference
1	A	30	0.7	20	73	800	880	1	6.5	35	Yes	79	Comp. Ex.
2	A	80	0.8	20	71	800	890	1	4.8	9.5	Yes	136	Inv. Ex.
3	A	80	0.7	50	72	800	870	1	2.5	5.3	Yes	147	Inv. Ex.
4	A	80	0.06	20	4	800	910	1	13.5	40	Yes	79	Comp. Ex.
5	A	80	0.8	0	72	800	890	1	7.5	48	Yes	80	Comp. Ex.
6	B	80	0.8	20	75	800	870	1	4.8	11	Yes	147	Inv. Ex.
7	C	30	0.7	20	84	800	880	1	5.6	30	Yes	97	Comp. Ex.
8	C	80	0.8	0	83	800	880	1	4.8	35	Yes	95	Comp. Ex.
9	C	80	0.7	20	85	800	880	1	2.5	7	Yes	146	Inv. Ex.
10	C	80	0.8	50	82	800	880	1	1.7	5	Yes	145	Inv. Ex.
11	C	80	0.08	20	7	800	880	1	6.5	35	Yes	95	Comp. Ex.
12	C	80	0.8	0	86	3000	880	1	3.5	20	Yes	89	Comp. Ex.
13	C	80	0.8	10	84	200	900	1	8.9	45	Yes	88	Comp. Ex.
14	C	80	0.8	20	85	800	700	0	Undetectable	Undetect-	Yes	49	Comp. Ex.
									due to	able due
									incomplete	to in-
									hardening	complete
										hardening
15	C	80	0.8	20	86	800	1050	1	15.5	50	Yes	86	Comp. Ex.
16	D	80	0.8	20	79	800	890	1	4.5	15	Yes	148	Inv. Ex.
17	E	80	0.7	20	9	800	890	1	7.5	45	Yes	76	Comp. Ex.
18	F	80	0.7	20	75	800	890	1	4.5	35	Yes	87	Comp. Ex.
19	G	80	0.7	20	70	800	890	1	4.8	32	Yes	93	Comp. Ex.
20	H	80	0.7	20	10	800	890	1	4.2	35	Yes	73	Comp. Ex.
21	A	80	0.8	20	75	2000	800	1	2.8	9	Yes	135	Inv. Ex.
22	I	80	0.8	20	68	800	890	1	4.2	12	Yes	136	Inv. Ex.
23	J	80	0.8	20	82	800	890	1	4.3	12	Yes	135	Inv. Ex.
24	K	80	0.8	20	79	800	890	1	3.9	11	Yes	137	Inv. Ex.
25	L	80	0.8	20	79	800	890	1	4.3	12	Yes	137	Inv. Ex.
26	M	80	0.8	20	79	800	890	1	4.2	12	Yes	139	Inv. Ex.
27	N	80	0.8	20	79	800	890	1	4.3	12	Yes	139	Inv. Ex.
*3: If value in the column is zero, the spline is formed by cutting. Otherwise, the spline is formed by rolling and the figure in the column indicates the processing ratio.
Rel. Ex.: Example of related art,
Inv. Ex.: Example of the present invention
Comp. Ex.: Comparative example

	TABLE 8-2
	Hot-working				Hardened
	conditions	Total	Pre-		layer structure
	Total		processing	hardening	HF hardening conditions	Average	Maximum
		processing	Cooling	ratio (%)	structure			Retention	former	former		Sliding
		ratio (%)	rate	at less	Proportion		Heating	time	austenitic	austenitic		rolling
		at	(° C./s)	than	(vol. %)	Heating	temper-	(sec) at	grain	grain		contact
	Steel	800° C. to	after	800° C.	of bainite	rate	ature	800° C.	diameter	diameter	Tem-	fatigue
No.	type	1000° C.	working	*3	structure	(° C./s)	(° C.)	or more	(μm)	(μm)	pering	life (hr)	Reference
28	O	80	0.8	20	72	800	890	1	3.9	11	Yes	139	Inv. Ex.
29	P	80	0.8	20	79	800	890	1	4.3	12	Yes	140	Inv. Ex.
30	Q	80	0.8	20	79	800	890	1	3.8	10	Yes	141	Inv. Ex.
31	R	80	0.8	20	79	800	890	1	4.3	12	Yes	142	Inv. Ex.
32	S	80	0.8	20	70	800	890	1	4.2	12	Yes	142	Inv. Ex.
AJ	0.45	0.45	0.82	0.011	0.031	0.002	0.004	0.4Mo,	26.9	12	Yes	143	Inv. Ex.
								0.02Ti,
								0.0020B,
								0.003Ca
AK	0.43	0.51	0.79	0.011	0.06	0.002	0.0039	0.45Mo,	22.6	13	Yes	136	Inv. Ex.
								0.021Ti,
								0.0020B,
								0.003Ca
35	V	80	0.8	20	79	800	890	1	4.3	12	Yes	139	Inv. Ex.
36	W	80	0.8	20	79	800	890	1	3.8	10	Yes	149	Inv. Ex.
37	X	80	0.8	20	79	800	890	1	4.3	12	Yes	139	Inv. Ex.
38	Y	80	0.8	20	79	800	890	1	4.2	12	Yes	140	Inv. Ex.
39	Z	80	0.8	20	79	800	890	1	4.3	12	Yes	140	Inv. Ex.
40	AA	80	0.8	20	85	800	890	1	3.9	11	Yes	141	Inv. Ex.
41	AB	80	0.8	20	79	800	890	1	4.3	12	Yes	143	Inv. Ex.
42	AC	80	0.8	20	80	800	890	1	3.8	10	Yes	136	Inv. Ex.
43	AD	80	0.8	20	79	800	890	1	4.3	12	Yes	143	Inv. Ex.
44	AE	80	0.8	20	79	800	890	1	3.9	11	Yes	140	Inv. Ex.
45	AF	80	0.8	20	79	800	890	1	4.3	12	Yes	139	Inv. Ex.
46	AG	80	0.8	20	79	800	890	1	3.8	10	Yes	140	Inv. Ex.
47	AH	80	0.8	20	79	800	890	1	4.2	12	Yes	141	Inv. Ex.
48	AI	80	0.8	20	85	800	890	1	3.7	10	Yes	140	Inv. Ex.
49	C	80	0.8	50	82	800	880	1	1.7	5	No	160	Inv. Ex.
50	AJ	80	0.8	20	83	800	930	2	3.1	10	Yes	145	Inv. Ex.
51	AK	80	0.8	20	81	500	930	3	3.9	10	Yes	138	Inv. Ex.
52	AL	80	0.8	20	81	500	930	3	4.0	10	Yes	135	Inv. Ex.
*3: If value in the column is zero, the spline is formed by cutting. Otherwise, the spline is formed by rolling and the figure in the column indicates the processing ratio.
Rel. Ex.: Example of related art,
Inv. Ex.: Example of the present invention
Comp. Ex.: Comparative example

	TABLE 9-1
	Hot-working				Hardened
	conditions	Total	Pre-		layer structure
	Total		processing	hardening	HF hardening conditions	Average	Maximum
		processing	Cooling	ratio (%)	structure			Retention	former	former
		ratio (%)	rate	at less	Proportion		Heating	time	austenitic	austenitic
		at	(° C./s)	than	(vol. %)	Heating	temper-	(sec) at	grain	grain		Rolling
	Steel	800° C. to	after	800° C.	of bainite	rate	ature	800° C.	diameter	diameter	Tem-	fatigue
No.	type	1000° C.	working	*4	structure	(° C./s)	(° C.)	or more	(μm)	(μm)	pering	life (hr)	Reference
1	A	30	0.7	20	73	800	880	1	6.5	35	Yes	79	Comp. Ex.
2	A	80	0.8	20	71	800	890	1	4.8	9.5	Yes	136	Inv. Ex.
3	A	80	0.7	50	72	800	870	1	2.5	5.3	Yes	147	Inv. Ex.
4	A	80	0.06	20	4	800	910	1	13.5	40	Yes	79	Comp. Ex.
5	A	80	0.8	0	72	800	890	1	7.5	48	Yes	81	Comp. Ex.
6	B	80	0.8	20	75	800	870	1	4.8	11	Yes	145	Inv. Ex.
7	C	30	0.7	20	84	800	880	1	5.6	30	Yes	99	Comp. Ex.
8	C	80	0.8	0	83	800	880	1	4.8	35	Yes	97	Comp. Ex.
9	C	80	0.7	20	85	800	880	1	2.5	7	Yes	145	Inv. Ex.
10	C	80	0.8	50	82	800	880	1	1.7	5	Yes	155	Inv. Ex.
11	C	80	0.08	20	7	800	880	1	6.5	35	Yes	96	Comp. Ex.
12	C	80	0.8	0	86	3000	880	1	3.5	20	Yes	89	Comp. Ex.
13	C	80	0.8	10	84	200	900	1	8.9	45	Yes	88	Comp. Ex.
14	C	80	0.8	20	85	800	700	0	Undetectable	Undetect-	Yes	48	Comp. Ex.
									due to	able due
									incomplete	to in-
									hardening	complete
										hardening
15	C	80	0.8	20	86	800	1050	1	15.5	50	Yes	87	Comp. Ex.
16	D	80	0.8	20	79	800	890	1	4.5	15	Yes	147	Inv. Ex.
17	E	80	0.7	20	9	800	890	1	7.5	45	Yes	76	Comp. Ex.
18	F	80	0.7	20	75	800	890	1	4.5	35	Yes	88	Comp. Ex.
19	G	80	0.7	20	70	800	890	1	4.8	32	Yes	97	Comp. Ex.
20	H	80	0.7	20	10	800	890	1	4.2	35	Yes	75	Comp. Ex.
21	A	80	0.8	20	75	2000	800	1	2.8	9	Yes	136	Inv. Ex.
22	I	80	0.8	20	68	800	890	1	4.2	12	Yes	136	Inv. Ex.
23	J	80	0.8	20	82	800	890	1	4.3	12	Yes	136	Inv. Ex.
24	K	80	0.8	20	79	800	890	1	3.9	11	Yes	137	Inv. Ex.
25	L	80	0.8	20	79	800	890	1	4.3	12	Yes	137	Inv. Ex.
26	M	80	0.8	20	79	800	890	1	4.2	12	Yes	138	Inv. Ex.
27	N	80	0.8	20	79	800	890	1	4.3	12	Yes	139	Inv. Ex.
28	O	80	0.8	20	72	800	890	1	3.9	11	Yes	139	Inv. Ex.
29	P	80	0.8	20	79	800	890	1	4.3	12	Yes	139	Inv. Ex.
*4: If the value in the column is zero, the rolling-contact surface for balls is formed by cutting. Otherwise, the rolling-contact surface for balls is formed by cold-forging and the figure in the column indicates the processing ratio.
Rel. Ex.: Example of related art,
Inv. Ex.: Example of the present invention
Comp. Ex.: Comparative example

	TABLE 10-2
	Hot-working	Working			Hardened
	conditions	(cold-	Pre-		layer structure
	Total		working)	hardening	HF hardening conditions	Average	Maximum
		processing	Cooling	ratio (%)	structure			Retention	former	former
		ratio (%)	rate	at less	Proportion		Heating	time	austenitic	austenitic
		at	(° C./s)	than	(vol. %)	Heating	temper-	(sec) at	grain	grain		Rolling
	Steel	800° C. to	after	800° C.	of bainite	rate	ature	800° C.	diameter	diameter	Tem-	fatigue
No.	type	1000° C.	working	*5	structure	(° C./s)	(° C.)	or more	(μm)	(μm)	pering	life	Reference
29	O	80	0.8	20	72	800	890	1	3.9	11	Yes	10.7	Inv. Ex.
30	P	80	0.8	20	79	800	890	1	4.3	12	Yes	10.9	Inv. Ex.
31	Q	80	0.8	20	79	800	890	1	3.8	10	Yes	11.1	Inv. Ex.
32	R	80	0.8	20	79	800	890	1	4.3	12	Yes	11.3	Inv. Ex.
AJ	0.45	0.45	0.82	0.011	0.031	0.002	0.004	0.4Mo,	26.9	12	Yes	11.3	Inv. Ex.
								0.02Ti,
								0.0020B,
								0.003Ca
AK	0.43	0.51	0.79	0.011	0.06	0.002	0.0039	0.45Mo,	22.6	12	Yes	11.5	Inv. Ex.
								0.021Ti,
								0.0020B,
								0.003Ca
35	U	80	0.8	20	79	800	890	1	4.5	13	Yes	10.1	Inv. Ex.
36	V	80	0.8	20	79	800	890	1	4.3	12	Yes	10.7	Inv. Ex.
37	W	80	0.8	20	79	800	890	1	3.8	10	Yes	12.7	Inv. Ex.
38	X	80	0.8	20	79	800	890	1	4.3	12	Yes	10.6	Inv. Ex.
39	Y	80	0.8	20	79	800	890	1	4.2	12	Yes	10.9	Inv. Ex.
40	Z	80	0.8	20	79	800	890	1	4.3	12	Yes	10.9	Inv. Ex.
41	AA	80	0.8	20	85	800	890	1	3.9	11	Yes	11.1	Inv. Ex.
42	AB	80	0.8	20	79	800	890	1	4.3	12	Yes	11.5	Inv. Ex.
43	AC	80	0.8	20	80	800	890	1	3.8	10	Yes	10.1	Inv. Ex.
44	AD	80	0.8	20	79	800	890	1	4.3	12	Yes	11.5	Inv. Ex.
45	AE	80	0.8	20	79	800	890	1	3.9	11	Yes	10.9	Inv. Ex.
46	AF	80	0.8	20	79	800	890	1	4.3	12	Yes	10.7	Inv. Ex.
47	AG	80	0.8	20	79	800	890	1	3.8	10	Yes	10.9	Inv. Ex.
48	AH	80	0.8	20	79	800	890	1	4.2	12	Yes	11.1	Inv. Ex.
49	AI	80	0.8	20	85	800	890	1	3.7	10	Yes	10.9	Inv. Ex.
49	C	80	0.8	50	82	800	880	1	1.7	5	No	13.5	Inv. Ex.
50	AJ	80	0.8	20	83	800	930	2	3.1	10	Yes	11.1	Inv. Ex.
51	AK	80	0.8	20	81	500	930	3	3.9	10	Yes	10.4	Inv. Ex.
52	AL	80	0.8	20	81	500	930	3	4.0	10	Yes	10.3	Inv. Ex..
*5: If the value in the column is zero, the rolling-contact surface for balls is formed by cutting. Otherwise, the rolling-contact surface for balls is formed by cold-forging and the figure in the column indicates the processing ratio.
Rel. Ex.: Example of related art,
Inv. Ex.: Example of the present invention
Comp. Ex.: Comparative example

	TABLE 9-2
	Hot-working				Hardened
	conditions	Total	Pre-		layer structure
	Total		processing	hardening	HF hardening conditions	Average	Maximum
		processing	Cooling	ratio (%)	structure			Retention	former	former
		ratio (%)	rate	at less	Proportion		Heating	time	austenitic	austenitic
		at	(° C./s)	than	(vol. %)	Heating	temper-	(sec) at	grain	grain		Rolling
	Steel	800° C. to	after	800° C.	of bainite	rate	ature	800° C.	diameter	diameter	Tem-	fatigue
No.	type	1000° C.	working	*4	structure	(° C./s)	(° C.)	or more	(μm)	(μm)	pering	life (hr)	Reference
30	Q	80	0.8	20	79	800	890	1	3.8	10	Yes	141	Inv. Ex.
31	R	80	0.8	20	79	800	890	1	4.3	12	Yes	141	Inv. Ex.
32	S	80	0.8	20	70	800	890	1	4.2	12	Yes	136	Inv. Ex.
AJ	0.45	0.45	0.82	0.011	0.031	0.002	0.004	0.4Mo,	26.9	12	Yes	143	Inv. Ex.
								0.02Ti,
								0.0020B,
								0.003Ca
AK	0.43	0.51	0.79	0.011	0.06	0.002	0.0039	0.45Mo,	22.6	13	Yes	136	Inv. Ex.
								0.021Ti,
								0.0020B,
								0.003Ca
35	V	80	0.8	20	79	800	890	1	4.3	12	Yes	141	Inv. Ex.
36	W	80	0.8	20	79	800	890	1	3.8	10	Yes	147	Inv. Ex.
37	X	80	0.8	20	79	800	890	1	4.3	12	Yes	139	Inv. Ex.
38	Y	80	0.8	20	79	800	890	1	4.2	12	Yes	139	Inv. Ex.
39	Z	80	0.8	20	79	800	890	1	4.3	12	Yes	140	Inv. Ex.
40	AA	80	0.8	20	85	800	890	1	3.9	11	Yes	141	Inv. Ex.
41	AB	80	0.8	20	79	800	890	1	4.3	12	Yes	142	Inv. Ex.
42	AC	80	0.8	20	80	800	890	1	3.8	10	Yes	136	Inv. Ex.
43	AD	80	0.8	20	79	800	890	1	4.3	12	Yes	143	Inv. Ex.
44	AE	80	0.8	20	79	800	890	1	3.9	11	Yes	138	Inv. Ex.
45	AF	80	0.8	20	79	800	890	1	4.3	12	Yes	139	Inv. Ex.
46	AG	80	0.8	20	79	800	890	1	3.8	10	Yes	139	Inv. Ex.
47	AH	80	0.8	20	79	800	890	1	4.2	12	Yes	141	Inv. Ex.
48	AI	80	0.8	20	85	800	890	1	3.7	10	Yes	141	Inv. Ex.
49	C	80	0.8	50	82	800	880	1	1.7	5	No	170	Inv. Ex.
50	AJ	80	0.8	20	83	800	930	2	3.1	10	Yes	142	Inv. Ex.
51	AK	80	0.8	20	81	500	930	3	3.9	10	Yes	137	Inv. Ex.
52	AL	80	0.8	20	81	500	930	3	4.0	10	Yes	135	Inv. Ex.
*4: If the value in the column is zero, the rolling-contact surface for balls is formed by cutting. Otherwise, the rolling-contact surface for balls is formed by cold-forging and the figure in the column indicates the processing ratio.
Rel. Ex.: Example of related art,
Inv. Ex.: Example of the present invention
Comp. Ex.: Comparative example

Tables 8-1, 8-2, 9-1, and 9-2 clearly show that every constant velocity joint inner race with a hardened structure in which the average former austenitic grain diameter was 12 μm or less and the maximum grain diameter did not exceed four times the average grain diameter exhibited excellent fatigue properties.

In contrast, the constant velocity joint inner races with an average former austenitic grain diameter exceeding 12 μm and a maximum grain diameter exceeding four times the average grain diameter exhibited poor fatigue properties.

Example 5

A hub shown in FIG. 17 for an automobile wheel was prepared as a component for machine structural use according to the present invention.

A hub 17 for an automobile wheel has a shaft 18 also serving as the inner race of a bearing and constitutes the bearing via balls 21 interposed between an outer race 20 and the outer surface of the shaft 18. In FIG. 17, reference numeral 19 denotes a spacer for retaining the balls 21 between the shaft 18 of the hub and the outer race 20. In the illustration of FIG. 17, the outer surface (contact rolling surface) 22 onto which the balls serving as a bearing for the hub make rolling contact requires improved rolling fatigue life.

Each of steel materials having compositions shown in Table 3 was melted in a converter and cast into a cast slab by continuous casting. The size of the cast slab was 300×400 [mm]. The cast slab was subjected to a breakdown step and rolled into a 150 mm square billet. The billet was then rolled to prepare a steel bar having a diameter of 24 mm. The steel bar was then cut to a predetermined length, formed into the shape of a hub by hot-forging, and cooled at a cooling rate set forth in Tables 10-1 and 10-2. The outer surface onto which the bearing balls for the hub shaft make rolling contact was formed by cutting or cold forging and subjected to high-frequency hardening under the conditions set forth in Tables 10-1 and 10-2 to form a hardened structure layer. Then the hub was tempered at 170° C. for 30 minutes in a heating furnace and subjected to finishing to prepare a product. Tempering was omitted for some of the hubs. The total processing ratio in the hot-forging and cold forging was controlled by adjusting the ratio of change in area of the cross-section taken in the direction orthogonal to the axis direction of the contact rolling surface.

The rolling fatigue life of each resulting hub was analyzed and the results are shown in Tables 10-1 and 10-2.

The rolling fatigue life of the hub was evaluated as follows.

Bearing balls were arranged on the outer surface of the shaft of the hub, and an outer race was attached. While fixing the hub, a predetermined load (900 N) was applied onto the outer race 20 of the hub as shown in FIG. 17 and the outer race 20 of the hub was rotated at a predetermined rate (300 rpm) to conduct the endurance test. The time taken until occurrence of the rolling fatigue fracture of a high-frequency hardened structure layer 22 was evaluated as the rolling fatigue life.

The rolling fatigue life was indicated in terms of the ratio with respect to the rolling fatigue life of Sample No. 22, which is a related-art sample prepared under the hot working and high-frequency hardening conditions outside the range of the present invention, in Tables 10-1 and 10-2, the rolling fatigue life of the related-art sample being defined as 1.

Here, the dimensions and shape of the outer race, steel balls, and the like were adjusted so that the shaft contact rolling surface of the hub was the weakest part in the endurance test.

The same hub was analyzed to determine the average diameter and the maximum diameter of the former austenitic grains in the hardened structure layer by the above-described process.

The results are also shown in Tables 10-1 and 10-2.

	TABLE 10-1
	Hot-working	Working			Hardened
	conditions	(cold-	Pre-		layer structure
	Total		working)	hardening	HF hardening conditions	Average	Maximum
		processing	Cooling	ratio (%)	structure			Retention	former	former
		ratio (%)	rate	at less	Proportion		Heating	time	austenitic	austenitic
		at	(° C./s)	than	(vol. %)	Heating	temper-	(sec) at	grain	grain		Rolling
	Steel	800° C. to	after	800° C.	of bainite	rate	ature	800° C.	diameter	diameter	Tem-	fatigue
No.	type	1000° C.	working	*5	structure	(° C./s)	(° C.)	or more	(μm)	(μm)	pering	life	Reference
1	A	30	0.7	20	73	800	880	1	6.5	35	Yes	2.5	Comp. Ex.
2	A	80	0.8	20	71	800	890	1	4.8	9.5	Yes	10.1	Inv. Ex.
3	A	80	0.7	50	72	800	870	1	2.5	5.3	Yes	12.3	Inv. Ex.
4	A	80	0.06	20	4	800	910	1	13.5	40	Yes	2.6	Comp. Ex.
5	A	80	0.8	0	72	800	890	1	7.5	48	Yes	2.6	Comp. Ex.
6	B	80	0.8	20	6	800	870	1	4.8	11	Yes	12.4	Inv. Ex.
7	C	30	0.7	20	84	800	880	1	5.6	30	Yes	4.3	Comp. Ex.
8	C	80	0.8	0	83	800	880	1	4.8	35	Yes	4.1	Comp. Ex.
9	C	80	0.7	20	85	800	880	1	2.5	7	Yes	12.1	Inv. Ex.
10	C	80	0.8	50	82	800	880	1	1.7	5	Yes	12.3	Inv. Ex.
11	C	80	0.08	20	7	800	880	1	6.5	35	Yes	4.1	Comp. Ex.
12	C	80	0.8	0	86	3000	880	1	3.5	20	Yes	3.4	Comp. Ex.
13	C	80	0.8	10	84	200	900	1	8.9	45	Yes	3.4	Comp. Ex.
14	C	80	0.8	20	85	800	700	0	Undetectable	Undetect-	Yes	0.8	Comp. Ex.
									due to	able due
									incomplete	to in-
									hardening	complete
										hardening
15	C	80	0.8	20	86	800	1050	1	15.5	50	Yes	3.2	Comp. Ex.
16	D	80	0.8	20	79	800	890	1	4.5	15	Yes	12.5	Inv. Ex.
17	E	80	0.7	20	9	800	890	1	7.5	45	Yes	2.3	Comp. Ex.
18	F	80	0.7	20	75	800	890	1	4.5	35	Yes	3.3	Comp. Ex.
19	G	80	0.7	20	70	800	890	1	4.8	32	Yes	3.9	Comp. Ex.
20	H	80	0.7	20	10	800	890	1	4.2	35	Yes	2.1	Comp. Ex.
21	A	80	0.8	20	75	2000	800	1	2.8	9	Yes	4.0	Comp. Ex.
22	A	80	0.1	0	0	200	1050	7	17	88	Yes	1.0	Rel. Ex.
23	I	80	0.8	20	68	800	890	1	4.2	12	Yes	10.1	Inv. Ex.
24	J	80	0.8	20	82	800	890	1	4.3	12	Yes	10.1	Inv. Ex.
25	K	80	0.8	20	79	800	890	1	3.9	11	Yes	10.3	Inv. Ex.
26	L	80	0.8	20	79	800	890	1	4.3	12	Yes	10.4	Inv. Ex.
27	M	80	0.8	20	79	800	890	1	4.2	12	Yes	10.7	Inv. Ex.
28	N	80	0.8	20	79	800	890	1	4.3	12	Yes	10.6	Inv. Ex.
*5: If the value in the column is zero, the rolling-contact surface for balls is formed by cutting. Otherwise, the rolling-contact surface for balls is formed by cold-forging and the figure in the column indicates the processing ratio.
Rel. Ex.: Example of related art,
Inv. Ex.: Example of the present invention
Comp. Ex.: Comparative example

Tables 10-1 and 10-2 clearly show that every hub with a hardened structure in which the average former austenitic grain diameter was 12 μm or less and the maximum grain diameter did not exceed four times the average grain diameter exhibited a rolling fatigue life at least 10 times that of the related art sample.

In contrast, Comparative Examples with an average former austenitic grain diameter exceeding 12 μm and a maximum grain diameter exceeding four times the average grain diameter exhibited short rolling fatigue life.

Example 6

A hub shown in FIG. 18 was prepared as in EXAMPLE 5 as an component for machine structural use according to the present invention. In particular, each of steel materials having compositions shown in Table 3 was melted in a converter and cast into a cast slab by continuous casting. The size of the cast slab was 300×400 [mm]. The cast slab was subjected to a breakdown step, rolled into a 150 mm square billet, and rolled to prepare a steel bar having a diameter of 24 mm. The steel bar was cut to a predetermined length, formed into a shape of a hub by hot-forging, and cooled at a rate shown in Tables 11-1 and 11-2. Subsequently, the hub shaft was cut or rolled for splining for fitting with the shaft of the constant velocity joint.

The inner surface (fitting portion 23 in FIG. 18) of the hub shaft that fits with the shaft of the constant velocity joint was subjected to high-frequency hardening under the conditions set forth in Tables 10-1 and 10-2 to form a hardened structure layer. The hub was then tempered at 170° C. for 30 minutes in a heating furnace and subjected to finishing to prepare a product. Tempering was omitted for some of the hubs. The total processing ratio in the hot-forging and forming rolling was adjusted by controlling the ratio of change in cross-section in the axis direction of the fitting portion of the hub shaft with the constant velocity joint.

The resulting hub was analyzed to determine the sliding rolling contact fatigue life of the inner surface that fits with the constant velocity joint. The results are shown in Tables 11-1 and 11-2.

The sliding rolling contact fatigue life of the hub was evaluated as follows:

Sliding Rolling Contact Fatigue Life

As shown in FIG. 19, a shaft 24 of the constant velocity joint was fit into the inner surface of the shaft of the hub, and while fixing the hub, fully reversed cycles of torsional force were applied to the shaft of the constant velocity joint (maximum torque: 700 N, 2 cycles per second). The number of cycles until occurrence of fracture of the hub spline due to the sliding rolling contact fatigue was evaluated as the fatigue life.

The sliding rolling contact fatigue life was indicated in terms of the ratio with respect to the sliding rolling contact fatigue life of Sample No. 22, which is a related art sample prepared under the hot-working and high-frequency hardening conditions outside the range of the present invention), in Tables 11-1 and 11-2, the sliding rolling contact fatigue life of the related-art sample being defined as 1.

The same hub was analyzed to determine the average diameter and the maximum diameter of the former austenitic grains in the hardened structure layer by the above-described process.

The results are also set forth in Tables 11-1 and 11-2.

	TABLE 11-1
	Hot-working	Working			Hardened
	conditions	(cold-	Pre-		layer structure
	Total		working)	hardening	HF hardening conditions	Average	Maximum
		processing	Cooling	ratio (%)	structure			Retention	former	former		Sliding
		ratio (%)	rate	at less	Proportion		Heating	time	austenitic	austenitic		rolling
		at	(° C./s)	than	(vol. %)	Heating	temper-	(sec) at	grain	grain		contact
	Steel	800° C. to	after	800° C.	of bainite	rate	ature	800° C.	diameter	diameter	Tem-	fatigue
No.	type	1000° C.	working	*6	structure	(° C./s)	(° C.)	or more	(μm)	(μm)	pering	life	Reference
1	A	30	0.7	20	73	800	880	1	6.5	35	Yes	2.5	Comp. Ex.
2	A	80	0.8	20	71	800	890	1	4.8	9.5	Yes	10.3	Inv. Ex.
3	A	80	0.7	50	72	800	870	1	2.5	5.3	Yes	12.3	Inv. Ex.
4	A	80	0.06	20	4	800	910	1	13.5	40	Yes	2.6	Comp. Ex.
5	A	80	0.8	0	72	800	890	1	7.5	48	Yes	2.6	Comp. Ex.
6	B	80	0.8	20	75	800	870	1	4.8	11	Yes	12.6	Inv. Ex.
7	C	30	0.7	20	84	800	880	1	5.6	30	Yes	3.9	Comp. Ex.
8	C	80	0.8	0	83	800	880	1	4.8	35	Yes	3.9	Comp. Ex.
9	C	80	0.7	20	85	800	880	1	2.5	7	Yes	12.1	Inv. Ex.
10	C	80	0.8	50	82	800	880	1	1.7	5	Yes	12.3	Inv. Ex.
11	C	80	0.08	20	7	800	880	1	6.5	35	Yes	3.8	Comp. Ex.
12	C	80	0.8	0	86	3000	880	1	3.5	20	Yes	3.4	Comp. Ex.
13	C	80	0.8	10	84	200	900	1	8.9	45	Yes	3.3	Comp. Ex.
14	C	80	0.8	20	85	800	700	0	Undetectable	Undetect-	Yes	0.5	Comp. Ex.
									due to	able due
									incomplete	to in-
									hardening	complete
										hardening
15	C	80	0.8	20	86	800	1050	1	15.5	50	Yes	3.2	Comp. Ex.
16	D	80	0.8	20	79	800	890	1	4.5	15	Yes	12.5	Inv. Ex.
17	E	80	0.7	20	9	800	890	1	7.5	45	Yes	2.3	Comp. Ex.
18	F	80	0.7	20	75	800	890	1	4.5	35	Yes	3.3	Comp. Ex.
19	G	80	0.7	20	70	800	890	1	4.8	32	Yes	3.9	Comp. Ex.
20	H	80	0.7	20	10	800	890	1	4.2	35	Yes	2.1	Comp. Ex.
21	A	80	0.8	20	75	2000	800	1	2.8	9	Yes	4.0	Comp. Ex.
22	A	80	0.1	0	0	200	1050	7	17	88	Yes	1.0	Rel. Ex.
23	I	80	0.8	20	68	800	890	1	4.2	12	Yes	10.1	Inv. Ex.
24	J	80	0.8	20	82	800	890	1	4.3	12	Yes	10.1	Inv. Ex.
*6: If the value in the column is zero, the spline is formed by cutting. Otherwise, the spline is formed by rolling and the figure in the column indicates the processing ratio
Rel. Ex.: Example of related art,
Inv. Ex.: Example of the present invention
Comp. Ex.: Comparative example

	TABLE 11-2
			Pre-hardening
	Hot-working conditions	Working (cold-	structure	HF hardening conditions
		Total processing	Cooling rate	working) ratio	Proportion		Heating	Retention time
	Steel	ratio (%) at	(° C./s) after	(%) at less than	(vol. %) of bainite	Heating	temperature	(sec) at 800° C.
No.	type	800° C. to 1000° C.	working	800° C. *6	structure	rate(° C./s)	(° C.)	or more
25	K	80	0.8	20	79	800	890	1
26	L	80	0.8	20	79	800	890	1
27	M	80	0.8	20	79	800	890	1
28	N	80	0.8	20	79	800	890	1
29	O	80	0.8	20	72	800	890	1
30	P	80	0.8	20	79	800	890	1
31	Q	80	0.8	20	79	800	890	1
32	R	80	0.8	20	79	800	890	1
AJ	0.45	0.45	0.82	0.011	0.031	0.002	0.004	0.4Mo, 0.02Ti,
								0.0020B, 0.003Ca
AK	0.43	0.51	0.79	0.011	0.06	0.002	0.0039	0.45Mo,
								0.021Ti,
								0.0020B, 0.003Ca
35	U	80	0.8	20	79	800	890	1
36	V	80	0.8	20	79	800	890	1
37	W	80	0.8	20	79	800	890	1
38	X	80	0.8	20	79	800	890	1
39	Y	80	0.8	20	79	800	890	1
40	Z	80	0.8	20	79	800	890	1
41	AA	80	0.8	20	85	800	890	1
42	AB	80	0.8	20	79	800	890	1
43	AC	80	0.8	20	80	800	890	1
44	AD	80	0.8	20	79	800	890	1
45	AE	80	0.8	20	79	800	890	1
46	AF	80	0.8	20	79	800	890	1
47	AG	80	0.8	20	79	800	890	1
48	AH	80	0.8	20	79	800	890	1
49	AI	80	0.8	20	85	800	890	1
50	C	80	0.8	50	82	800	880	1
51	AJ	80	0.8	20	83	800	930	2
52	AK	80	0.8	20	81	500	930	3
53	AL	80	0.8	20	81	500	930	3
			Sliding
	Hardened layer structure		rolling
		Average former	Maximum former		contact
		austenitic grain	austenitic grain		fatigue
	No.	diameter (μm)	diameter (μm)	Tempering	life	Reference
	25	3.9	11	Yes	10.3	Inv. Ex.
	26	4.3	12	Yes	10.4	Inv. Ex.
	27	4.2	12	Yes	10.7	Inv. Ex.
	28	4.3	12	Yes	10.6	Inv. Ex.
	29	3.9	11	Yes	10.3	Inv. Ex.
	30	4.3	12	Yes	10.4	Inv. Ex.
	31	3.8	10	Yes	10.7	Inv. Ex.
	32	4.3	12	Yes	10.6	Inv. Ex.
	AJ	26.9	12	Yes	11.3	Inv. Ex.
	AK	22.6	12	Yes	11.5	Inv. Ex.
	35	4.5	13	Yes	10.1	Inv. Ex.
	36	4.3	12	Yes	10.7	Inv. Ex.
	37	3.8	10	Yes	12.7	Inv. Ex.
	38	4.3	12	Yes	10.7	Inv. Ex.
	39	4.2	12	Yes	10.6	Inv. Ex.
	40	4.3	12	Yes	11.3	Inv. Ex.
	41	3.9	11	Yes	11.5	Inv. Ex.
	42	4.3	12	Yes	10.1	Inv. Ex.
	43	3.8	10	Yes	10.1	Inv. Ex.
	44	4.3	12	Yes	11.5	Inv. Ex.
	45	3.9	11	Yes	10.9	Inv. Ex.
	46	4.3	12	Yes	10.7	Inv. Ex.
	47	3.8	10	Yes	10.0	Inv. Ex.
	48	4.2	12	Yes	11.1	Inv. Ex.
	49	3.7	10	Yes	10.8	Inv. Ex.
	50	1.7	5	No	13.5	Inv. Ex.
	51	3.1	10	Yes	11.1	Inv. Ex.
	52	3.9	10	Yes	11.5	Inv. Ex.
	53	4.0	10	Yes	11.5	Inv. Ex.
	*6: If the value in the column is zero, the spline is formed by cutting. Otherwise, the spline is formed by rolling and the figure in the column indicates the processing ratio
	Rel. Ex.: Example of related art,
	Inv. Ex.: Example of the present invention
	Comp. Ex.: Comparative example

Tables 11-1 and 11-2 clearly show that every hub with a hardened structure in which the average former austenitic grain diameter was 12 μm or less and the maximum grain diameter did not exceed four times the average grain diameter exhibited a sliding rolling contact fatigue life at least 10 times that of the related-art sample.

In contrast, Comparative Examples with an average former austenitic grain diameter exceeding 12 μm and a maximum grain diameter exceeding four times the average grain diameter exhibited short sliding rolling contact fatigue life.

Example 7

A gear 25 shown in FIG. 20 was prepared as a component for machine structural use according to the present invention.

A gear 25 shown in FIG. 20 was a representative example of a gear and has many teeth 26 in the edge face. The gear of the present invention, as shown in FIG. 21, had many teeth 26 and bottoms 27 between the teeth 26, and a hardened structure layer 28 was formed in the surface layer of the teeth and the bottoms. In the illustrated example, the hardened structure layer 28 was formed in the surface portion of the teeth 26 and the bottoms 27; alternatively, it was possible to form a hardened structure layer in the inner surface of a shaft hole 29 into which a driving shaft of a variety of type was inserted.

Each of steel materials having compositions shown in Table 3 was melted in a converter and cast into a cast slab by continuous casting. The size of the cast slab was 300×400 [mm]. The cast slab was subjected to a breakdown step and rolled into a 150 mm square billet. The billet was then rolled under hot working conditions indicated in Tables 12-1 and 12-2 to prepare a steel bar having a diameter of 90 mm. The processing ratio here is defined as the ratio of reduction in the cross section in the individual temperature ranges.

A gear was prepared from this steel bar by cutting as follows:

small gear: outer diameter: 75 mm, module: 2.5, number of teeth: 28, reference diameter: 70 mm

large gear: outer diameter: 85 mm, module: 2.5, number of teeth: 32, reference diameter: 80 mm

This gear was hardened under the conditions set forth in Tables 12-1 and 12-2 using a 200 kHz high-frequency hardening apparatus and tempered at 180° C. for 2 hours in a heating furnace, followed by fatigue test of actual gears. The tempering was omitted for some of the gears.

The fatigue test of actual gears was conducted by meshing the small and large gears and rotating them at a speed of 3000 rpm and a load torque of 245 N·m. The number of torque application cycles until fracture of one of the gears was evaluated.

The results are set forth in Tables 12-1 and 12-2.

Gears prepared under same conditions were analyzed to determine the average diameter and the maximum diameter of the former austenitic grains in the hardened structure layer by the above-described process.

The results are also set forth in Tables 12-1 and 12-2.

	TABLE 12-1
	Hot-working conditions		Pre-hardening
	Total processing		structure	HF hardening conditions
		ratio (%) at	Processing ratio	Cooling rate	Proportion		Heating	Retention time
	Steel	800° C. to	(%) at 700° C. to	(° C./s) after	(vol. %) of bainite	Heating	temperature	(sec) at 800° C.
No.	type	1000° C.	less than 800° C.	working	structure	rate(° C./s)	(° C.)	or more
1	A	30	20	0.7	73	800	880	1
2	A	80	20	0.8	71	800	890	1
3	A	80	50	0.7	72	800	870	1
4	A	80	20	0.06	4	800	910	1
5	A	80	0	0.8	72	800	890	1
6	B	80	20	0.8	75	800	870	1
7	C	30	20	0.7	84	800	880	1
8	C	80	0	0.8	83	800	880	1
9	C	80	20	0.7	85	800	880	1
10	C	80	50	0.8	82	800	880	1
11	C	80	20	0.08	7	800	880	1
12	C	80	0	0.8	86	3000	880	1
13	C	80	10	0.8	84	200	900	1
14	C	80	20	0.8	85	800	700	0
15	C	80	20	0.8	86	800	1050	1
16	D	80	20	0.8	79	800	890	1
17	E	80	20	0.7	9	800	890	1
18	F	80	20	0.7	75	800	890	1
19	G	80	20	0.7	70	800	890	1
20	H	80	20	0.7	10	800	890	1
21	A	80	20	0.8	75	2000	800	1
22	I	80	20	0.8	68	800	890	1
23	J	80	20	0.8	82	800	890	1
	Hardened layer structure		Number of
		Average former	Maximum former		torque
		austenitic grain	austenitic grain		application
	No.	diameter (μm)	diameter (μm)	Tempering	(×104)	Reference
	1	6.5	35	Yes	36	Comp. Ex.
	2	4.8	9.5	Yes	1039	Inv. Ex.
	3	2.5	5.3	Yes	1691	Inv. Ex.
	4	13.5	40	Yes	36	Comp. Ex.
	5	7.5	48	Yes	39	Comp. Ex.
	6	4.8	11	Yes	1725	Inv. Ex.
	7	5.6	30	Yes	128	Comp. Ex.
	8	4.8	35	Yes	113	Comp. Ex.
	9	2.5	7	Yes	1621	Inv. Ex.
	10	1.7	5	Yes	1553	Inv. Ex.
	11	6.5	35	Yes	113	Comp. Ex.
	12	3.5	20	Yes	73	Comp. Ex.
	13	8.9	45	Yes	70	Comp. Ex.
	14	Undetectable	Undetectable	Yes	2	Comp. Ex.
		due to	due  to
		incomplete	incomplete
		hardening	hardening
	15	15.5	50	Yes	61	Comp. Ex.
	16	4.5	15	Yes	1745	Inv. Ex.
	17	7.5	45	Yes	29	Comp. Ex.
	18	4.5	35	Yes	65	Comp. Ex.
	19	4.8	32	Yes	99	Comp. Ex.
	20	4.2	35	Yes	22	Comp. Ex.
	21	2.8	9	Yes	61	Comp. Ex.
	22	4.2	12	Yes	1745	Inv. Ex.
	23	4.3	12	Yes	997	Inv. Ex.
	Rel. Ex.: Example of related art,
	Inv. Ex.: Example of the present invention
	Comp. Ex.: Comparative example

	TABLE 12-2
	Hot-working conditions		Pre-hardening
	Total processing		structure	HF hardening conditions
		ratio (%) at	Processing ratio	Cooling rate	Proportion		Heating	Retention time
	Steel	800° C. to	(%) at 700° C. to	(° C./s) after	(vol. %) of bainite	Heating	temperature	(sec) at 800° C.
No.	type	1000° C.	less than 800° C.	working	structure	rate(° C./s)	(° C.)	or more
24	K	80	20	0.8	79	800	890	1
25	L	80	20	0.8	79	800	890	1
26	M	80	20	0.8	79	800	890	1
27	N	80	20	0.8	79	800	890	1
28	O	80	20	0.8	72	800	890	1
29	P	80	20	0.8	79	800	890	1
30	Q	80	20	0.8	79	800	890	1
31	R	80	20	0.8	79	800	890	1
32	S	80	20	0.8	70	800	890	1
33	T	80	20	0.8	79	800	890	1
34	U	80	20	0.8	79	800	890	1
35	V	80	20	0.8	79	800	890	1
36	W	80	20	0.8	79	800	890	1
37	X	80	20	0.8	79	800	890	1
38	Y	80	20	0.8	79	800	890	1
39	Z	80	20	0.8	79	800	890	1
40	AA	80	20	0.8	85	800	890	1
41	AB	80	20	0.8	79	800	890	1
42	AC	80	20	0.8	80	800	890	1
43	AD	80	20	0.8	79	800	890	1
44	AE	80	20	0.8	79	800	890	1
45	AF	80	20	0.8	79	800	890	1
46	AG	80	20	0.8	79	800	890	1
47	AH	80	20	0.8	79	800	890	1
48	AI	80	20	0.8	85	800	890	1
49	C	80	50	0.8	82	800	880	1
50	AJ	80	20	0.8	83	800	930	2
51	AK	80	20	0.8	81	500	930	3
52	AL	80	20	0.8	81	500	930	3
	Hardened layer structure		Number of
		Average former	Maximum former		torque
		austenitic grain	austenitic grain		application
	No.	diameter (μm)	diameter (μm)	Tempering	(×104)	Reference
	24	3.9	11	Yes	1089	Inv. Ex.
	25	4.3	12	Yes	1115	Inv. Ex.
	26	4.2	12	Yes	1195	Inv. Ex.
	27	4.3	12	Yes	1169	Inv. Ex.
	28	3.9	11	Yes	1211	Inv. Ex.
	29	4.3	12	Yes	1254	Inv. Ex.
	30	3.8	10	Yes	1300	Inv. Ex.
	31	4.3	12	Yes	1364	Inv. Ex.
	32	4.2	12	Yes	1364	Inv. Ex.
	33	4.3	12	Yes	1445	Inv. Ex.
	34	4.5	13	Yes	1039	Inv. Ex.
	35	4.3	12	Yes	1195	Inv. Ex.
	36	3.8	10	Yes	1839	Inv. Ex.
	37	4.3	12	Yes	1169	Inv. Ex.
	38	4.2	12	Yes	1249	Inv. Ex.
	39	4.3	12	Yes	1254	Inv. Ex.
	40	3.9	11	Yes	1300	Inv. Ex.
	41	4.3	12	Yes	1425	Inv. Ex.
	42	3.8	10	Yes	1051	Inv. Ex.
	43	4.3	12	Yes	1445	Inv. Ex.
	44	3.9	11	Yes	1249	Inv. Ex.
	45	4.3	12	Yes	1211	Inv. Ex.
	46	3.8	10	Yes	1254	Inv. Ex.
	47	4.2	12	Yes	1300	Inv. Ex.
	48	3.7	10	Yes	1249	Inv. Ex.
	49	1.7	5	No	1700	Inv. Ex.
	50	3.1	10	Yes	1310	Inv. Ex.
	51	3.9	10	Yes	1350	Inv. Ex.
	52	4.0	10	Yes	1340	Inv. Ex.
	Rel. Ex.: Example of related art,
	Inv. Ex.: Example of the present invention
	Comp. Ex.: Comparative example

Tables 12-1 and 12-2 clearly show that when the hardened layer had an average former austenitic grain diameter of 12 μm or less and a maximum grain diameter not exceeding four times the average grain diameter, excellent fatigue properties, i.e., the number of torque load application cycles being about 1000×10⁴ or more, was achieved.

In contrast, gears having hardened structures with an average former austenitic grain diameter exceeding 12 μm and a maximum grain diameter exceeding four times the average grain diameter exhibited poor fatigue properties.

INDUSTRIAL APPLICABILITY

According to the present invention, a component for machine structural use that excels in all the fatigue properties, such as torsional fatigue property, the bending fatigue property, the rolling fatigue property, and the sliding rolling contact fatigue property, can be stably produced. Therefore, the invention has a significant effect on the demand of weight-reduction of automobile components and the like.

Claims

1. A component for machine structural use, comprising a steel material at least part of which is subjected to hardening, wherein the hardened structure has an average diameter of former austenitic grains of 12 mm or less and a maximum grain diameter not exceeding four times the average grain diameter.

2. The component for machine structural use according to claim 1, the steel material comprising a composition containing, in terms of percent by mass: C: 0.3% to 1.5%. Si: 0.05% to 3.0% and Mn: 0.2% to 2.0%, and satisfying a formula (1): C1/2(1+0.7Si)(1+3Mn)>2.0   (1) wherein the balance is Fe and inevitable impurities.

3. The component for machine structural use according to claim 2, the composition further containing, in terms of percent by mass: Al: 0.25% or less.

4. A component for machine structural use comprising a steel material at least tart of which is subjected to hardening, wherein the hardened structure has an average diameter of former austenitic grains of 12 μm or less and a maximum grain diameter not exceeding four times the average grain diameter, the steel material comprising, a composition containing in terms of percent by mass: C: 0.3% to 1.5%; Si: 0.05% to 3.0%; Mn: 0.2% to 2.0%; at least one element selected from the group consisting of Cr: 0.03% to 2.5%, Mo: 0.05% to 1.0%, Cu: 0.03% to 1.0%, Ni: 0.05% to 2.5%, Co: 0.01% to 1.0%, V: 0.01% to 0.5% and W: 0.005% to 1.0%, and satisfying a formula (2): C1/2(1+0.7Si)(1+3Mn)(1+2.1Cr)(1+3.0 Mo)(1+0.4 Cu)(1+0.3Ni)(1+5.0V)(1+0.5W)>2.0   (2) wherein the balance is Fe and inevitable impurities.

5. A component for machine structural use comprising a steel material at least part of which is subjected to hardening, wherein the hardened structure has an average diameter of former austenitic grains of 12 μm or less and a maximum grain diameter not exceeding four times the average grain diameter, the steel material comprising, a composition containing, in terms of percent by mass: C: 0.3% to 1.5%; Si: 0.05% to 3.0%; Mn: 0.2% to 2.0%; at least one element selected from the group consisting of Cr: 0,03% to 2.5%, Mo: 0.05% to 1.0%, Cu: 0.03 to 1.0%, Ni: 0.05% to 2.5%, Co: 0.01% to 1.0%, V: 0.01% to 0.5% and W: 0.005% to 1.0%; at least one element selected from the group consisting of Ti: 0.005% to 0.1%, Nb: 0.005% to 0.1%, Zr: 0.005% to 0.1%, B: 0.0003% to 0.01%, Ta: 0.02% to 0.5%, Hf: 0.02% to 0.5% and Sb: 0.005% to 0.015%, and satisfying a formula (3): C1/2(1+0.7Si)(1+3Mn)(1+2.1Cr)(1+3.0 Mo)(1+0.4 Cu)(1+0.3Ni)(1+5.0V)(1+1000B)(1+0.5W)>2.0   (3) wherein the balance is Fe and inevitable impurities.

6. The component for machine structural use according to claim 2 or 3, the composition further containing, in terms of percent by mass, at least one element selected from the group consisting of S: 0.1% or less, Pb: 0.01% to 0.1%, Bi: 0.01% to 0.1%, Se: 0.003% to 0.1%, Te: 0.003% to 0.1%, Ca: 0.0001% to 0.01%, Mg: 0.0001% to 0.01% and REM: 0.0001% to 0.1%.

7. A method for making a component for machine structural use, comprising subjecting at least part of a steel material to high-frequency heating at least once, the steel material containing one or both of a fine bainite structure and a fine martensite structure in a total of 10 percent by volume, wherein the high-frequency heating is conducted at a heating rate of at least 400° C./s and an ultimate temperature of 1,000° C. or less.

8. The method for making the component for machine structural use according to claim 7, wherein the steel material is worked through: a hot-working step in which a total processing ratio at 800° C. to 1,000° C. is 80% or more; a cooling step subsequent to the hot-working step, in which the cooling rate is 0.2° C./s or more in the temperature range of 700° C. to 500° C.; and a secondary working step of either effecting 20% or more of working in a temperature range of 700° C. to less than 800° C. before the cooling step or effecting 20% or more of working in a temperature range of up to the A1 transformation temperature subsequent to the cooling step.

9. The method for making the component for machine structural use according to claim 7 or 8, wherein a retention time at 800° C. or more in the high-frequency heating is 5 seconds or less at a time.

10. The method for making the component for machine structural use according to claim 7 or 8, wherein the steel material comprising, in terms of percent by mass, C: 0.3% to 1.5%; Si: 0.05% to 3.0% and Mn: 0.2% to 2.0%, and satisfying a formula (1): C1/2(1+0.7Si)(1+3Mn)>2.0   (1) wherein the balance is Fe and inevitable impurities.

11. The method for making the component for machine structural use according to claim 10, the steel material further comprising: Al: 0.25 mass % or less.

12. The method for making the component for machine structural use according to claim 10, wherein the steel material comprising, in terms of percent by mass, C: 0.3% to 1.5%; Si: O.005% to 3.0%; Mn: 0.2% to 2.0%; at least one element selected from the group consisting of Cr: 0.03% to 2.5%, Mo: 0.05% to 1.0%, Cu: 0.03% to 1.0%, Ni: 0.05% to 2.5%, Co: 0.01% to 1.0%, V: 0.01% to 0.5% and W: 0.005% to 1.0%, and satisfying a formula (2): C1/2(1+0.7Si)(1+3Mn)(1+2.1Cr)(1+3.0 Mo)(1+0.4 Cu)(1+0.3Ni)(1+5.0V)(1+0.5W)>2.0   (2) wherein the balance is Fe and inevitable imurities.

13. The method for making the component for machine structural use according to claim 10, wherein the steel material comprising, in terms of percent by mass, C: 0.3% to 1.5%; Si: 0.05% to 3.0%; Mn: 0.2% to 2.0%; at least one element selected from the group consisting of Cr; 0.03% to 2.5%, Mo: 0.05% to 1.0%, Cu: 0.03% to 1.0%, Ni: 0.05% to 2.5%, Co: 0.01% to 1.0%, V: 0.01% to 0.5% and W: 0.005% to 1.0%; at least one element selected from the group consisting of Ti: 0.005% to 0.1%, Nb: 0.005% to 0.1%, Zr: 0.005% to 0.1%, B: 0.0003% to 0.01%, Ta: 0.02% to 0.5%, Hf: 0.02% to 0.5% and Sb: 0.005% to 0.015%, and satisfying a formula (3): C1/2(1+0.7Si)(1+3Mn)(1+2.1Cr)(1+3.0 Mo)(1+0.4 Cu)(1+0.3Ni)(1+5.0V)(1+1000B)(1+0.5W)>2.0   (3) wherein the balance is Fe and inevitable impurities.

14. The method for making the component for machine structural use according to claim 10, wherein the steel material further comprising, in terms of percent by mass, at least one element selected from the groud consisting of S: 0.1% or less, Pb: 0.01% to 0.1%, Bi: 0.01% to 0.1%, Se: 0.003% to 0.1%, Te: 0.003% to 0.1%, Ca: 0.0001% to 0.01%, Mg: 0.0001% to 0.01% and REM: 0.0001% to 0.1%.

15. (canceled)

16. The component for machine structural use according to claim 4, the composition further containing, in terms of percent by mass, at least one element selected from among the group consisting of S: 0.1% or less Pb: 0.01% to 0.1% Bi: 0.01% to 0.1%, Se: 0.003% to 0.1%, Te: 0.003% to 0.1%, Ca: 0.0001% to 0.01%, Mg: 0.0001% to 0.01% and REM: 0.0001% to 0.1%.

17. The component for machine structural use according to claim 5, the composition further containing, in terms of percent by mass, at least one element selected from the group consisting of S: 0.1% or less, Pb: 0.01% to 0.1%, Bi: 0.01% to 0.1%, Se: 0.003% to 0.1%, Te: 0.003% to 0.1%, Ca: 0.0001% to 0.01%, Mg: 0.0001% to 0.01% and REM: 0.0001% to 0.1%.

18. (canceled)

19. The component for machine structural use according to claim 4, wherein the composition further comprises 0.25% by mass or less of Al.

20. The component for machine structural use according to claim 5, wherein the composition further comprises 0.25% by mass or less of Al.

21. The method for making the component for machine structural use according to claim 12, wherein the steel further comprises 0.25% by amss or less of Al.

22. The method for making the component for machine structural use according to claim 13, wherein the steel further comprises 0.25% by mass or less of Al.