Composite adsorbent

Abstract

Disclosed is a composite adsorbent consisting of a molded body of homogeneous mixture comprising powdery active carbon and hydrous alumina of the pseudoboehmite type. This composite adsorbent has high mechanical strength and abrasion resistance. This composite adsorbent is excellent in the capacity of adsorbing organic components such as gasoline, and the desorption of the adsorbed components can be easily accomplished at a high desorption ratio. These excellent capacities are retained even if the adsorption-desorption cycle is repeated. Accordingly, this composite adsorbent is especially valuable as the adsorbent for an automobile canister.

Description

BACKGROUND OF THE INVENTION

(1) Field of the Invention

The present invention relates to a composite adsorbent consisting of a composite molded body of active carbon and hydrous alumina. More particularly, the present invention relates to a composite adsorbent which is excellent in the combination of the propeRties of absorbing and desorbing organic components such as gasoline.

(2) Description of the Prior Art

Granular active carbon has been vigorously used for adsorbing various organic solvent vapors or various hydrocarbon vapors contained in air. This granular active carbon shows a high adsorbing capacity to organic components, but desorption of the adsorbed organic components is not satisfactorily easy. As the desorption means, there are adopted, for example, a method in which steam is passed through a packed layer of granular active carbon and a method in which a packed layer of granular active carbon is heated and a gas is passed through the heated packed layer.

However, if the adsorbent is heated for regeneration, there is a risk of combustion of the adsorbed component. Therefore, the desorption of the adsorbed component in ordinary air at room temperature is desired from the viewpoint of the operation efficiency and safety.

Moreover, granular active carbon is generally poor in the mechanical strength or abrasion resistance and there often arises a problem of dusting, and since granular active carbon has a black color, contamination of an apparatus or environment is often caused.

Summary of the Invention

It is therefore a primary object of the present invention to provide a novel composite adsorbent which is excellent in the properties of adsorbing and desorbing organic components, especially in the effective desorption quantity, is capable of easily desorbing adsorbed components in air at room temperature and is prominently excellent in the mechanical strength and abrasion resistance.

Another object of the present invention is to provide a composite adsorbent which has a high pack density and hence, a large adsorption treatment quantity per unit volume and in which even when the adsorptiondesorption cycle is repeated many times, the adsorbing and desorbing capacities are hardly reduced.

In accordance with one aspect of the present invention, there is provided a composite adsorbent which consists of a molded body of a homogeneous mixture comprising 30 to 70% by weight of powdery active carbon and 30 to 70% by weight of hydrous alumina of the pseudoboehmite type, and has a pack density of 500 to 700 g/l and an average pore radius of 13 to 20 .ANG..

In accordance with another aspect of the present invention, there is provided a composite adsorbent which consists of a molded body of a homogeneous mixture comprising 30 to 70% by weight of powdery active carbon, 5 to 70% by weight of hydrous alumina of the pseudoboehmite type and 5 to 60% by weight of a natural or synthetic smectite type clay mineral and has a pack density of 500 to 700 g/l and an average pore radius of 13 to 20 .ANG..

The composite adsorbent of the present invention is characterized in that it consists of a molded body of a homogeneous mixture of powdery active carbon and hydrous alumina of the pseudoboehmite type. The hydrous alumina of the pseudoboehmite type used in the present invention acts as an excellent excipient at the step of molding powdery active carbon, and at the heat treatment (calcination) of the molded body, the hydrous alumina gives a strong and dense molded body by the contraction of the hydrous alumina per se, and simultaneously, the hydrous alumina is converted to active alumina having an excellent adsorbing capacity.

This composite adsorbent has a smaller BET specific surface area and a smaller pore volume than granular active carbon, but the composite adsorbent shows such an excellent effective desorption quantity as 40% or more, though the effective desorption quantity of granular active carbon is only 20 to 30%. The fact that the composite adsorbent of the present invention shows an excellent effective desorption quantity was experimentally found, and the theoretical reason has not been sufficiently elucidated but it is presumed that the reason for attainment of the above-mentioned excellent effect is probably as follows.

The hydrous alumina of the pseudoboehmite type used in the present invention acts not only as a binder for powdery active carbon but also as an excellent adsorbent. The adsorbing capacity of the hydrous alumina to organic components is lower than that of active carbon but the adsorbing capacity to water is higher than that of active carbon. In the composite adsorbent of the present invention, it is believed that desorption of organic components is promoted by the adsorption of water contained in the desorption air by the hydrous alumina of the pseudoboehmite type. Furthermore, the average pore radius of the composite adsorbent per se is larger than that of powdery active carbon, and it is believed that this increased pore radius makes a contribution to increase of the effective desorption quantity of organic components. Moreover, the composite adsorbent has a large pack density, and it is believed that this increase of the pack density makes a contribution to increase of the adsorption quantity and desorption quantity per unit volume.

In the composite adsorbent of the present invention, powdery active carbon is present in an amount of 30 to 70% by weight, especially 40 to 60% by weight, and hydrous alumina of the pseudoboehmite type is present in an amount of 30 to 70% by weight, especially 40 to 60% by weight. If the amount of powdery active carbon is too small and below the above-mentioned range or the amount of the hydrous alumina exceeds the above-mentioned range, the effective desorption quantity is smaller than the effective desorption quantity attained in the present invention. If the amount of powdery active carbon exceeds the above-mentioned range or the amount of the hydrous alumina is below the above-mentioned range, reduction of the strength of the molded body or the effective desorption quantity is often caused.

The composite adsorbent of the present invention has a pack density of 400 to 700 g/l, especially 500 to 600 g/l, and an average pore radius of 13 to 20 .ANG., especially 14 to 18 .ANG.. Namely, the composite adsorbent of the present invention is characterized in that the pack density is higher than the pack density of granular active carbon, which is generally in the range of from 350 to 500 g/l. Increase of the pack density is effective for increasing the effective desorption quantity per unit volume. Furthermore, the composite adsorbent of the present invention is characterized in that the average pore radius is larger than the average pore radius of granular active carbon, which is generally in the range of from 9 to 13 .ANG.. It is presumed that this increase of the average pore radius results in increase of the effective desorption quantity.

Still further, the composite adsorbent of the present invention is excellent in the mechanical strength and abrasion resistance and has a crushing strength of at least 2 kg, especially at least 3 kg, as measured by a Kiya-type hardness meter. Accordingly, even if the adsorption-desorption cycle is repeated many times or under conditions where mechanical vibrations are applied, dusting is not caused and a composite adsorbent can be used stably for a long time. This is another characteristic of the composite adsorbent of the present invention.

If a natural or synthetic smectite clay mineral is added to the above-mentioned powdery active carbon and hydrous alumina of the psuedoboehmite type in an amount of 5 to 70% by weight, especially 10 to 40% by weight, based on the total mixture in the composite adsorbent of the present invention, the mechanical strength and abrasion resistance can be prominently improved without substantial degradation of the above-mentioned excellent adsorbing and desorbing capacities.

Brief Description of the Drawing

FIG. 1 shows X-ray diffraction patterns in which A indicates hydrous alumina of the pseudoboehmite type used in the present invention and B indicates the composite adsorbent obtained at Run No. 4 of Example 1.

Detailed Description of the Preferred Embodiments

Starting Materials

As pointed out hereinbefore, in the present invention, hydrous alumina of the psuedoboehmite type is used as the alumina adsorbent component. As the aluminum hydroxide or hydrous alumina, there are known gibbsite, bialite, boehmite, diaspore, and boehmite gel (pseudoboehmite). Among them, pseudoboehmite is used as the starting material in the present invention. In FIG. 1, A represents an X-ray diffraction pattern of hydrous alumina of the pseudoboehmite type.

The hydrous alumina used in the present invention has, in general, a particle size smaller than 5 .mu.m, especially smaller than 3 .mu.m, a BET specific surface area of 200 to 400 m.sup.2 /g and a pore volume of 0.2 to 0.6 ml/g, especially 0.3 to 0.5 ml/g. Hydrous alumina of the pseudoboehmite type is generally prepared by reacting sodium aluminate with a mineral acid such as sulfuric acid or by reacting an aluminum salt such as aluminum sulfate with an alkali such as caustic soda. Hydrous alumina prepared according to this known ordinary method, which satisfies the above-mentioned requirements, can be used in the present invention. Hydrous alumina which is advantageously used for attaining the objects of the present invention is disclosed in Japanese Patent Publication No. 13652/81 and is prepared according to the process disclosed in this patent publication. It is preferred that the hydrous alumina used as the starting material should have a composition represented by the following formula:

Al.sub.2 O.sub.3 .multidot.xH.sub.2 O

wherein x is a number of from 1.0 to 2.0, especially from 1.4 to 1.8.

Powdery active carbon used as the other starting material has preferably a particle size smaller than 10 .mu.m, especially smaller than 8 .mu.m, a BET specific surface area of at least 1000 m.sup.2 /g, especially at least 1200 m.sup.2 /g, and a pore volume of 0.8 to 1.5 ml/g, especially 1.0 to 1.3 ml/g. Powdery active carbon having an average pore radius of 12 to 20 .ANG., especially 14 to 18 .ANG., which is larger than that of ordinary active carbon, is advantageously used for attaining the objects of the present invention. The process for the preparation of active carbon is known. For example, powdery active carbon obtained by activating a starting material such as coconut husk by the chemical activation method using zinc chloride or the like is generally used.

As the natural or synthetic smectite type clay mineral optionally used as the third component, there can be mentioned dioctahedral smectites such as montmorillonite, beidellite and nontronite, and trioctahedral smectites such as saponite, hectorite, sauconite and stevensite. These smectite clay minerals have an adsorbing capacity, and they act as an inorganic binder and exert a function of improving the mechanical strength and abrasion resistance of the molded body. As preferred examples, there can be mentioned acid clay belonging to the montmorillonite group, activated acid clay, synthetic lamellar magnesium phyllosilicate disclosed in Japanese Patent Application Laid-Open Specification No. 10020/86, synthetic fraipontite disclosed in Japanese Patent Application Laid-Open Specification No. 10021/76, active bentonite disclosed in Japanese Patent Application Laid-Open Specification No. 50310/88 and synthetic stevensite disclosed in Japanese Patent Application No. 20476/87. The clay mineral used in the present invention has preferably a particle size smaller than 10 .mu.m, especially smaller than 3 .mu.m, and a BET specific surface area of 200 to 600 m.sup.2 /g, especially 200 to 500 m.sup.2 /g.

Composite Adsorbent and Preparation Process

According to the present invention, the above-mentioned starting materials are dry- or wet-mixed at the above-mentioned ratio so that the entire mixture becomes homogeneous. The mixture is kneaded in the presence of water for the homogenization and the kneaded mixture is molded into a predetermined shape. At the step of preparing the kneaded composition for molding, it is preferred that water be present in an amount of 30 to 60% by weight, especially 40 to 50% by weight, based on the solids, though the preferred amount of water differs to some extent according to the bulk specific gravity of the powder. A kneader, a super mixer or a single-screw or twin-screw extruder can be used for the kneading operation, and if necessary, a vacuum type soil kneader can be used.

A pelletizer, a tablet machine or the like can be used for molding the kneaded mixture into granules, and the rolling granulation method can be used for formation of spheres. The shape of the molded body is not particularly critical, and any of spherical, cylindrical, tablet-like, annular and honeycomb shapes can be optionally adopted. The particle size can be selected within a broad range of, for example, 0.3 mm to 5 mm. In order to impart a shape-retaining property to the kneaded composition, a known organic binder such as carboxymethyl cellulose, ethyl cellulose, polyvinyl alcohol, starch, cyanoethylated starch, tragacanth gum or a latex of a synthetic resin or synthetic rubber can be incorporated in the composition in an amount of 0.1 to 3% by weight based on the solids.

According to the present invention, the so-obtained molded body is heat-treated so that densification and enhancement of the strength can be attained by the firing contraction. The heat treatment is conducted at a temperature of 100 .degree. to 600.degree. C., especially 150.degree. to 350.degree. C., for 60 to 360 minutes, especially 120 to 240 minutes.

The composite adsorbent of the present invention has a BET specific surface area of 600 to 1200 m.sup.2 /g, especially 700 to 1000 m.sup.2 /g, and a pore volume of 0.5 to 1.0 ml/g, especially 0.6 to 0.8 ml/g. In general, the composite adsorbent has an adsorption capacity of 13 to 20 g/ml to an aliphatic hydrocarbon solvent, and the effective desorption quantity is at least 30%, especially at least 40%.

The composite adsorbent of the present invention is widely used for removing and recovering organic solvent vapors, hydrocarbon vapors, flon type halogenated hydrocarbons and the like from various atmospheres, and is also used for removing smell components and coloring components from various solutions and dispersions by the adsorption.

The composite adsorbent of the present invention consists of a molded body of a homogeneous mixture of powdery active carbon and hydrous alumina of the pseudoboehmite type, and the above-mentioned third component is optionally incorporated. The composite adsorbent of the present invention is excellent in the combination of the adsorbing and desorbing capacities to organic components to be adsorbed, for example, gasoline and especially excellent in the effective desorption quantity. Furthermore, the desorption of adsorbed components can be easily accomplished in air at room temperature, and the composite adsorbent is prominently excellent in the mechanical strength and abrasion resistance. Still further, the composite adsorbent has a high pack density and hence, the adsorption treatment quantity per unit volume is very large. Moreover, the composite adsorbent is advantageous in that even if the adsorption-desorption cycle is repeated many times, the adsorbing and desorbing capacities are hardly reduced.

The present invention will now be described in detail with reference to the following examples that by no means limit the scope of the invention.

Referential Example 1

Hydrous alumina of the pseudoboehmite type (hereinafter referred to as "hydrous alumina") was prepared according to the process described below.

A slightly acidic (pH=2 to 3) aqueous solution of aluminum nitrate having a concentration of 50 to 100 g/l as Al.sub.2 O.sub.3 was poured at a speed of 100 to 1000 ml/min into a slurry containing calcium carbonate at a concentration of 70.degree. to 300 g/l (hereinafter referred to as "calcium carbonate slurry"), which was heated and stirred at 70.degree. to 120.degree. C., and after completion of addition of the calcium carbonate slurry, the aging treatment was carried out with gentle stirring for about 1 hour at a temperature lower than 90.degree. C. so that the pH value of the reaction slurry was maintained at 6 to 8, whereby hydrous alumina was obtained.

The obtained hydrous alumina was recovered by filtration, washed with water and dried at a temperature of 110.degree. to 150.degree. C. to obtain a fine powder of hydrous alumina to be used in the present invention. The properties of the obtained fine powder are shown in Table 1.

TABLE 1______________________________________ Sample No. A-1 A-2 A-3 A-4 A-5______________________________________Bulk Density 0.32 0.52 0.45 0.42 0.39(g/ml)Average 2.6 3.5 2.8 3.2 3.2ParticleSize (.mu.m)Specific 310 250 294 286 302SurfaceArea (m.sup.2 /g)Pore Volume 0.412 0.352 0.380 0.373 0.384(ml/g)Average Pore 26.6 28.2 25.9 26.1 25.4Diameter (.ANG.)______________________________________

Referential Example 2

Commercially available products (supplied by Taiheiyo Kinzoku and Takeda Yakuhin Kogyo) having properties shown in Table 2 were used as the powdery active carbon according to the resent invention.

TABLE 2______________________________________ Sample No. B-1 B-2 B-3 B-4______________________________________Bulk Density 0.26 0.19 0.21 0.24(g/ml)Average Particle 8.4 7.2 8.3 8.4Size (.mu.m)Specific Surface 1200 1360 1290 1390Area (m.sup.2 /g)Pore Volume 0.87 1.05 0.99 1.45(ml/g)Average Pore 14.5 15.4 15.3 1.59Radius (.ANG.)______________________________________

Referential Example 3

Natural or synthetic smectite clay minerals having binder characteristics, the properties of which are shown in Table 3, were used as the third component according to the present invention.

TABLE 3______________________________________ Sample No. C-1 C-2 C-3 C-4______________________________________Clay Mineral acid clay synthetic synthetic synthetic lamellar hectorite stevensite magnesium phyllosilicateBulk Density 0.82 0.23 0.86 0.88(g/ml)Average Particle 5 3 0.01 0.01Size (.mu.m)Specific Surface 200 490 510 496Area (m.sup.2 /g)Pore Volume 0.30 0.33 0.35 0.30(ml/g)Average Pore 30 13.5 13.7 14.1Radius (.ANG.)______________________________________

Example 1

The starting materials shown in Tables 1, 2 and 3 were dried at 150.degree. C. for 6 hours and mixed at a ratio shown in Table 4.

Then, the mixture was kneaded for 1 hour by a kneader while adjusting the water content to 2% by weight by drying at 150.degree. C., and the kneaded mixture was extruded into columns having a diameter of 1.5 mm by a pelletizer (supplied by Fuji Powder)

The extruder was dried at 150.degree. C. for 20 hours and heat-treated at 300.degree. C. for 3 hours in air to obtain a composite adsorbent of the present invention. The properties were determined according to the following test methods. The obtained results are shown in Table 4.

Incidentally, Run Nos. 1 and 2 in Table 4 are comparative runs.

Test Methods

The properties referred to in the instant specification were determined according to the following test methods.

1. X-Ray Diffractometry

The X-ray diffractometry was carried out by using an X-ray diffraction apparatus supplied by Rigaku Denki (X-ray generator 4036Al, goniometer 2125Dl, counter 5071) under the following conditions.

Target: Cu Filter: Ni Detector: SC Voltage: 35 kV Current: 15 mA Full-Scale of Counting: 8000 c/s Time Constant: 1 sec Scanning Speed: 2/mm Chart Speed: 2 cm/mm Radiation Angle: 1 Slit Width: 0.3 mm

2. BET Specific Surface Area (SA)

The BET specific surface area was determined by using an automatic BET measuring apparatus (Sporptomatic Series 1800 supplied by Carlo-Erba).

3. Pore Volume (PV)

By using the above-mentioned BET measurement apparatus, the sample was deaerated at 250.degree. C. under 10.sup.-2 mmHg, and the N.sub.2 adsorption quantity (V1) in the normal state was calculated from the N.sub.2 adsorption quantity at the liquefied N.sub.2 saturation temperature under an N.sub.2 pressure of 735 mmHg and the pore volume was calculated according to the following formula:

Pore volume (PV)=V1.times.1.555.times.10.sup.-3 (ml/g)

4. Average Pore Radius (r)

Supposing that pores had a cylindrical shape, the average pore radius was calculated according to the following formula: ##EQU1##

5. Pack Density (BD)

A predetermined weight (W g) of a sample dried at 150.degree. C. for 3 hours was charged in a graduated cylinder having a capacity of 500 ml and sufficiently rammed into the cylinder, and the packed volume (V ml) of the sample was measured. The pack density (BD) was measured according to the following formula:

Pack density (BD)=(W/V).times.100 (g/l)

6. Particle Strength

The crushing strength was measured by using a Kiya-type hardness meter (10 kg meter) with respect to 20 columnar samples (1.5 mm in diameter and 3 mm in length) dried at 150.degree. C. for 2 hours, and the mean value was calculated and expressed as the particle strength.

7. Abrasion Resistance

A glass vessel (45 mm in diameter and 75 mm in height) set at a shaker (Model 5410 supplied by Red Devil) was charged with 40 g of a sample which had been used for the moisture-adsorbing treatment for 48 hours at a relative humidity of 75%, and the sample was shaken for 30 minutes and classified by using a 32-mesh sieve. The weight (W1, g) of the fraction passing through the sieve was measured and the abrasion resistance ratio was calculated according to the following formula:

Abrasion resistance ratio=[(40-W1)/40].times.100 (%)

8. Average Particle Size

The average particle size was the particle size at the point of 50% volume distribution in the accumulated particle size curve obtained according to the Coulter Counter method (Coulter Counter Model TA-II).

TABLE 4__________________________________________________________________________Composition Specific Average(parts by weight) Pack Surface Pore Pore Particle Abrasionof Adsorbent Density Area Volume Radius Strength ResistanceRun No. B A C (g/l) (m.sup.2 /g) (ml/g) (.ANG.) (kg) Ratio (%)__________________________________________________________________________ B-2 A-1 -- 1 100 0 0 280 1380 1.1 15.9 <0.1 2.0 2 80 20 0 440 117 0.97 16.5 1.2 99.0 3 70 30 0 506 1080 0.90 16.7 2.1 99.6 4 60 40 0 540 975 0.82 16.8 2.8 99.8 5 50 50 0 560 860 0.73 17.0 3.4 99.9 6 30 70 0 600 612 0.56 18.3 4.6 100 7 20 80 0 632 513 0.51 19.9 5.5 100 B-1 A-1 C-1 8 65 25 5 512 943 0.72 15.3 2.1 99.8 9 70 10 20 505 939 0.71 15.1 2.2 99.810 60 30 10 517 853 0.67 15.7 2.9 99.911 30 60 10 640 569 0.56 19.7 4.6 10012 30 50 20 632 557 0.55 19.7 4.6 100 B-2 A-2 C-113 30 40 30 628 546 0.54 19.8 4.8 99.914 30 30 40 620 536 0.53 19.8 4.4 99.915 30 20 50 614 523 0.52 19.9 4.2 99.916 30 10 60 609 512 0.52 20.3 4.0 99.817 30 5 65 596 508 0.51 20.1 4.0 99.8 B-2 A-1 C-218 70 20 10 508 970 0.73 15.1 2.2 99.719 70 10 20 503 997 0.72 14.4 2.1 99.720 60 30 10 517 908 0.65 14.3 2.5 99.921 30 60 10 632 604 0.55 18.2 4.5 10022 30 10 60 506 695 0.53 15.3 2.5 99.823 30 5 65 480 719 0.52 14.5 2.0 99.8 B-1 A-3 C-324 70 20 10 526 953 0.70 14.7 2.3 99.825 70 10 20 530 941 0.68 14.5 2.3 99.726 60 30 10 565 868 0.65 15.0 2.5 99.9 B-3 A-5 C-327 30 60 10 654 574 0.57 19.9 4.8 10028 30 10 60 596 551 0.53 19.2 4.5 99.929 35 5 60 570 529 0.51 19.3 4.8 99.9 B-2 A-2 C-430 70 20 10 594 945 0.72 15.2 3.0 99.831 70 10 20 605 940 0.71 15.1 3.3 99.932 60 30 10 620 856 0.65 15.2 2.8 100 B-4 A-4 C-433 30 60 10 672 569 0.52 18.3 4.8 10034 30 10 60 683 520 0.50 19.2 5.1 10035 30 5 65 689 512 0.47 18.4 5.2 100__________________________________________________________________________

Example 2

With respect to some of the composite adsorbents obtained in Example 1, the adsorption-desorption of organic components was examined, and the durability of this adsorption-desorption effect was evaluated by the cycle test. The obtained results are shown in Table 5.

More specifically, with respect to each of the composite adsorbents obtained at Run Nos. 4, 10, 20, 21, 26 and 32 of Example 1, 100 ml of the sample was charged in a beaker and the beaker was placed in a desiccator charged with an organic solvent shown in Table 5, and the saturated vapor of the organic sorbent was adsorbed in the sample. Then, the adsorbent was packed in a column (2.5 cm in diameter and 2.5 cm in length) and air having a relative humidity of 50% or 80% was circulated through the column at a flow rate of 500 ml/min for 25 minutes to desorb the adsorbed organic solvent. In some of these samples, this adsorption-desorption cycle test was repeated 20 times, and the adsorption quantity and desorption quantity at the 20th cycle were measured. The obtained results are shown in Table 5.

For comparison, the above test was carried out in the same manner as described above by using the active carbon component alone.

TABLE 5__________________________________________________________________________DesorptionCondition Adsorption-Desorption EffectOrganic (relative Active Carbon Composite AdsorbentSolvent humidity %) Adsorbent B-1 B-2 No. 4 No. 10 No. 20 No. 26 No. 32__________________________________________________________________________ethyl adsorption 13.9 15.7 29.6 21.7 26.3 25.6 26.9acetate quantity (g/100 cc) 80 desorption 3.98 4.62 12.82 9.31 12.22 10.85 11.30 quantity (g/100 cc) desorption 28.6 29.4 43.3 42.9 46.5 42.4 42.0 ratio (%) 50 desorption 4.25 4.89 12.92 9.42 12.35 11.00 11.52 quantity (g/100 cc) desorption 30.6 31.1 43.6 43.4 46.9 42.9 42.8 ratio (%)vinyl adsorption 19.3 15.95 30.64 22.69 27.28 26.70 28.06acetate quantity (g/100 cc) 80 desorption 5.49 4.63 13.18 9.71 12.69 11.35 11.95 quantity (g/100 cc) desorption 28.5 29.0 43.0 42.8 46.5 42.5 42.6 ratio (%) 50 desorption 6.25 5.15 13.25 10.1 12.82 11.42 12.1 quantity (g/100 cc) desorption 32.4 32.3 43.2 44.5 47.0 42.8 43.1 ratio (%)n-hexane adsorption 16.25 13.25 25.28 18.09 21.60 20.19 21.81 quantity (g/100 cc) 80 desorption 4.55 3.76 10.82 7.69 9.63 8.48 9.23 quantity (g/100 cc) desorption 28.0 28.4 42.8 42.5 44.6 42.0 42.3 ratio (%) 50 desorption 4.88 4.2 10.95 7.70 9.81 8.51 9.37 quantity (g/300 cc) desorption 30.0 31.7 43.3 42.6 45.4 42.1 43.0 ratio (%)__________________________________________________________________________ Desorption Condition Effect at Adsorption-Desorption EffectOrganic (relative Composite Adsorbent Active CarbonSolvent humidity %) No. 20 No. 21 B-2__________________________________________________________________________ethyl adsorption 26.1 28.5 12.9acetate quantity (g/100 cc) 80 desorption 12.93 11.40 3.72 quantity (g/100 cc) desorption 49.5 40.0 28.8 ratio (%) 50 desorption 12.89 12.15 4.15 quantity (g/100 cc) desorption 49.4 42.6 32.2 ratio (%)vinyl adsorptionacetate quantity (g/100 cc) 80 desorption quantity (g/100 cc) desorption ratio (%) 50 desorption quantity (g/100 cc) desorption ratio (%)n-hexane adsorption 22.10 23.50 12.35 quantity (g/100 cc) 80 desorption 9.86 8.84 2.48 quantity (g/100 cc) desorption 44.6 37.6 20.0 ratio (%) 50 desorption 10.15 9.35 3.76 quantity (g/100 cc) desorption 45.9 39.8 30.4 ratio (%)__________________________________________________________________________

Example 3

The composite absorbent obtained at Run No. 20 of Example 1 was subjected to the following adsorptiondesorption cycle test by using commercially available gasoline having an octane number (motor octane number) of 82.5 (80EM Gasoline supplied by Nippon Sekiyu).

Gasoline mixed with air fed at a flow rate of 1.6 l/min, which was heated at 65.degree. C., was passed through a layer packed with 300 ml of the molded body of the composite adsorbent prepared at Run No. 20 of Example 1, and when 2 g of the gasoline had been passed through the packed layer, the adsorption quantity was determined from the weight increase in the composite adsorbent.

Then, air having a relative humidity shown in Table 6 was passed through the packed layer at a flow rate of 5.3 l/min, and the desorption quantity was determined from the weight decrease in the composite adsorbent. This adsorption-desorption cycle test was repeated 20 times. After the 20th cycle, the desorption ratio (effective desorption ratio) was calculated according to the following formula:

Desorption ratio=[(desorption quantity)/ (desorption quantity accumulated residual gasoline quantity)].times.100

For comparison, the above test was carried out in the same manner by using a commercially available active carbon molded body (Run No. 3H-1).

The obtained results are shown in Table 6.

TABLE 6__________________________________________________________________________Run No. 3-1 Run No. 3-2description condition: desorption condition:relative humidity = 75% relative humidity = 65% residual residual adsorption desorption gasoline adsorption desorption gasolinecycle quantity quantity quantity quantity quantity quantitynumber (g/300 cc) (g/300 cc) (g/300 cc)* (g/300 cc) (g/300 cc) (g/300 cc)*__________________________________________________________________________ 1 28.3 16.6 11.7 11.7 26.5 15.6 10.9 10.9 2 23.0 19.0 4.0 15.7 21.6 18.1 3.5 14.4 3 22.8 19.7 3.1 18.8 21.7 19.2 2.5 16.9 4 22.3 20.2 2.1 20.9 21.2 19.4 1.8 18.7 5 22.4 20.4 2.0 22.9 21.0 19.5 1.5 20.2 6 22.2 20.5 1.7 24.6 21.0 19.6 1.4 21.6 7 22.2 20.9 1.3 25.9 21.1 19.9 1.2 22.8 8 22.5 21.4 1.1 27.0 21.2 20.0 1.2 24.0 9 22.8 21.3 1.5 28.5 21.2 20.1 1.1 25.110 23.3 21.9 1.4 29.9 21.3 20.3 1.0 26.111 22.8 22.1 0.7 30.6 21.3 20.3 1.0 27.112 22.8 22.4 0.4 31.0 21.0 20.4 0.6 27.713 22.8 22.4 0.4 31.4 21.5 20.6 0.9 28.614 22.9 22.5 0.4 31.8 21.3 20.8 0.5 29.115 23.1 22.6 0.5 32.3 21.5 21.0 0.5 29.616 23.0 22.6 0.4 32.7 21.6 21.2 0.4 30.017 23.1 22.6 0.5 33.2 21.8 21.3 0.5 30.518 23.2 22.7 0.5 33.7 22.2 21.6 0.6 31.119 23.2 22.7 0.5 34.2 22.0 21.5 0.5 31.620 23.0 22.7 0.3 34.5 22.1 21.6 0.5 32.1desorption ratio = 39.5% desorption ratio = 40.0%__________________________________________________________________________Run No. 3-3 Run No. 3H-1desorption condition: desorption condition:relative humidity = 80% relative humidity = 65% residual residual adsorption desorption gasoline adsorption desorption gasolinecycle quantity quantity quantity quantity quantity quantitynumber (g/300 cc) (g/300 cc) (g/300 cc)* (g/300 cc) (g/300 cc) (g/300 cc)*__________________________________________________________________________ 1 25.7 14.0 11.7 11.7 31.5 11.6 19.9 19.9 2 20.0 16.5 3.5 15.2 21.4 16.4 5.0 24.9 3 19.7 16.7 3.0 18.2 19.8 17.4 2.4 27.3 4 20.0 17.4 2.6 20.8 19.6 18.1 1.6 28.9 5 19.6 17.7 1.9 22.7 19.1 18.0 1.1 30.0 6 20.0 18.2 1.8 24.5 19.1 18.1 1.0 31.0 7 20.3 18.4 1.9 26.4 19.1 18.0 1.1 32.1 8 19.9 18.7 1.2 27.6 18.8 18.1 0.7 32.8 9 20.6 19.4 1.2 28.8 19.5 18.3 1.2 34.010 20.2 19.1 1.1 29.9 19.5 18.4 1.1 35.111 19.9 19.1 0.8 30.7 19.5 18.3 1.2 36.312 19.9 19.0 0.9 31.6 19.2 18.2 1.0 37.313 20.1 19.1 1.0 32.6 19.0 18.2 0.8 38.114 20.0 19.9 0.1 32.7 19.1 18.3 0.8 38.915 20.4 20.0 0.4 33.1 19.2 18.2 1.0 39.916 20.5 20.3 0.2 33.3 19.2 18.1 1.1 41.017 20.7 20.2 0.5 33.8 19.2 18.1 1.1 42.118 20.6 20.3 0.3 34.1 19.2 18.0 1.2 43.319 20.6 20.3 0.3 34.4 19.2 18.0 1.2 44.520 20.5 20.3 0.2 34.6 19.2 18.0 1.2 45.7desorption ratio = 36.9% desorption ratio = 28.3%__________________________________________________________________________ note: *accumulated residual gasoline quantity

Claims

1. A composite adsorbent which consists of a molded body of a homogeneous mixture comprising 40 to 60% by weight of a powdery active carbon and 40 to 60% by weight of hydrous alumina of the pseudoboehmite type, and has a pack density of 500 to 700 g/l and an average pore radius of 13 to 20 .ANG..

2. A composite adsorbent as set forth in claim 1, wherein the BET specific surface area is 500 to 1200 m.sup.2 /g and the pore volume is 0.4 to 1.0 ml/g.

3. A composite adsorbent as set forth in claim 1, wherein the powdery active carbon has a particle size smaller than 10 .mu.m, a specific surface area of at least 1000 m.sup.2 /g and a pore volume of 0.8 to 1.5 ml/g.

4. A composite adsorbent as set forth in claim 1, wherein the hydrous alumina of the pseudoboehmite type has a particle size smaller than 5 .mu.m, a BET specific surface area of 200 to 400 m.sup.2 /g and a pore volume of 0.3 to 0.6 ml/g.

5. A composite adsorbent as set forth in claim 1, wherein the crushing strength is at least 2 kg as measured by a Kiya-type hardness meter.

6. A composite adsorbent which consists of a molded body of a homogeneous mixture comprising 30 to 70% by weight of powdery active carbon, 5 to 70% by weight of hydrous alumina of the pseudoboehmite type and 5 to 60% by weight of a natural or synthetic smectite type clay mineral and has a pack density of 500 to 700 g/l and an average pore radius of 13 to 20 .ANG..

7. The composite adsorbent of claim 1 which has a pack density of from 500 to 600 g/l.

8. The composite adsorbent of from 14 to 18 .ANG..

9. The composite adsorbent of claim 8 having a pack density of from 500 to 600 g/l.

10. The composite adsorbent of claim 5 having a crushing strength of at least 3 kg as measured by Kiya=type hardness meter.

11. The composite adsorbent of claim 1 wherein the hydrous alumina of the pseudoboehmite type has the formula

Al.sub.2 O.sub.3 .multidot.xH.sub.2 O

wherein x is a number of from 1.0 to 2.0.

12. the composite adsorbent of claim 11 wherein x is a number of from 1.4 to 1.8.

13. The composite adsorbent of claim 3 wherein the powdery active carbon has a particle size smaller than 8 .mu.m, a specific surface area of at least 1200 m.sup.2 /g and a pore volume of 1.0 to 1.3 ml/g.

14. The composite adsorbent of claim 3 wherein the active carbon has an average pore radius of from 12 to 20 .ANG..

15. The composite adsorbent of claim 14 wherein the active carbon has an average pore radius of from 14 to 18 .ANG..

16. The composite adsorbent of claim 6 containing from 10 to 40% by weight of the natural or synthetic smectite type clay mineral.

17. The composite adsorbent of claim 6 wherein the clay mineral has a particle size smaller than 10 .mu.m, and a BET specific surface area of from 200 to 600 m.sup.2 /g.

18. The composite adsorbent of claim 6 wherein the clay mineral has a particle size less than 3 .mu.m and a BET specific surface area of from 200 to 500 m.sup.2 /g.

19. The composite adsorbent of claim 1 having a BET specific surface area of from 700 to 1000 m.sup.2 /g and a pore volume of from 0.6 to 0.8 ml/g.

20. A composite adsorbent molded body having an adsorption capacity for aliphatic hydrocarbon solvent of from about 13 to 20 g/ml and an effective desorption quantity when desorbed in a hydrocarbon-free air at room temperature of at least 30%, said molded body comprising a homogeneous mixture of from 30 to 70% by weight of powdery active carbon having an average particle size smaller than 10 .mu.m, and from 30 to 70% by weight of hydrous alumina of the pseudoboehmite type having a particle size smaller than 5 .mu.m, and having a pack density of from 500 to 700 g/l and an average pore radius of 13 to 20 .ANG..

21. A composite adsorbent molded body having an adsorption capacity for aliphatic hydrocarbon solvent of form about 13 to 20 g/ml and an effective desorption quantity when desorbed in a hydrocarbon-free air at room temperature of at least 30%, said molded body comprising a homogeneous mixture of from 30 to 70% by weight of powdery active carbon having an average particle size smaller than 10 .mu.m, from 5 to 60% by weight of hydrous alumina of the pseudoboehmite type having a particle size smaller than 5 .mu.m, and 5 to 60% by weight of natural or synthetic smectite type clay mineral having a particle size smaller than 10 .mu.m, and having a pack density of from 500 to 700 g/l and an average pore radius of 13 to 20 .ANG..