Patent Grant
9174415
This application is the national phase application of PCT Application No. PCT/CN2012/080190, filed Aug. 15, 2012, which claims priority to and benefits of Chinese Patent Application Serial No. 201110237931.X, filed with the State Intellectual Property Office of P. R. China on Aug. 18, 2011, the entire content of both is incorporated herein by reference.
The present disclosure relates to material engineering, and more particularly to a method of joining an amorphous alloy material to a heterogeneous material and a composite formed by the same.
The statements in this section merely provide background information related to the present disclosure and may or may not constitute prior art.
Currently, there are more and more needs for products with precision and durability, high reliability and high strength, however, conventional materials and conventional forming and joining technologies may hardly meet design requirements for products. For example, although a magnesium alloy has light weight and may be precisely formed, the magnesium alloy may be poor in strength and easy to crack, and may not be corrosion resistant. Although an aluminum alloy may be precisely formed and may have corrosion resistance and colorful decoration property, however, the aluminum alloy may be low in hardness and may not be wear resistant. Although a zinc alloy may be low in price and easy to form, the zinc alloy may be low in strength, and may not be corrosion resistant. Although a stainless steel may have high strength and high corrosion resistance, the stainless steel may be difficult to precisely form. Even if the stainless steel may be precisely machined, the machining cost is very high, so the stainless steel may be difficult to popularize.
Due to the unordered and uniquely arranged structure of atoms constituting an alloy, an amorphous alloy material, also referred to as metallic glass, may have excellent physical and chemical properties different from those of common crystalline metal materials, for example, high yield strength, high hardness, superelasticity (i.e., high elastic limit), high wear resistance, and high corrosion resistance, so may have broad application prospects.
An amorphous alloy has been first reported in 1960s. Because the critical size (i.e., the largest size to form an amorphous alloy) of the initial amorphous alloy only may reach micron scale, the initial amorphous alloy may be difficult to practically use. In recent years, gradual increase of the critical size of the amorphous alloy makes possible industrial application of the amorphous alloy.
The amorphous alloy has excellent casting performance. For example, the amorphous alloy has low melting temperature like a magnesium alloy, an aluminum alloy, a zinc alloy or a copper alloy, for example, the melting temperature of a rare-earth-based amorphous alloy may be as low as about 300° C. Because the amorphous alloy retains the structural feature of a molten state without phase change, the shrinkage rate of the amorphous alloy may be lower than that of a conventional metal and a plastic. Like a plastic, the amorphous alloy not only has a melting temperature and a glass transition temperature, but also has a large supercooled liquid phase region, so the amorphous alloy may have high flowability and good replicating of the shape and surface of a cast. Meanwhile, without performance difference caused by composition segregation and grain coarsening, the amorphous alloy in a casting state may have excellent mechanical property. The above advantages enable the amorphous alloy to have broad application prospects. For example, the use of an amorphous alloy material to manufacture a frame for an electronic device may solve problems of scratching, destruction under force, and other defects caused by insufficient hardness and strength in a frame made of a conventional metal material. The amorphous alloy material may also be used for manufacturing a structural member with very complex structure and high strength, which may solve large-cutting-amount machining problems created when a steel is used for manufacturing a precise structural member with complex structure and high strength. Meanwhile, the amorphous alloy material may be used for forming a precise micro-gear, which may solve problems of forming difficulty and poor wear resistance of the micro-gear.
However, due to some inherent characteristics of the amorphous alloy, the application of the amorphous alloy material is largely affected. For example, because the hardness of the amorphous alloy is high, when machining, punching and drilling need to be performed on an amorphous alloy article, the process difficulty may be increased, and the life of a cutting tool may be significantly shortened, thus enhancing the production cost. In addition, for an article with very complex structure and a wall thickness not larger than about 0.3 mm, the amorphous alloy article may be difficult to form, which may enhance the production cost to a large extent or even cause the production of the amorphous alloy article not to be carried out. Meanwhile, because the plastic deformation of the amorphous alloy is carried out by forming and extending a low-viscosity region of a shear band, the amorphous alloy generally exhibits very low plastic deformation and appears as a brittle material, which may largely restrict the application of the amorphous alloy in a device for which high safety is required, for example, the application of the amorphous alloy in an article for which drop performance or impact performance are specially required. Meanwhile, the use of various amorphous alloy systems, especially amorphous alloy materials with low amorphous formation ability and low cost, may be largely restricted. In addition, currently, an amorphous alloy is generally constituted by a noble metal, which may be high in material cost; and when the structure of an article is being designed, excellent performance of the amorphous alloy is not required for all the structures of articles. Therefore, how to realize low-cost application of a high-cost material is one difficult problem which needs to be solved.
U.S. Pat. Nos. 5,482,580; 6,818,078 and 6,771,490 disclose methods of joining an amorphous alloy material to other materials. However, in the amorphous alloy composite articles manufactured by these conventional methods, the bonding strength between the amorphous alloy material and other materials is low; the impact resistance of the amorphous alloy composite articles is low; and in the methods disclosed in the above U.S. Patents, it is required that the melting temperature of a pre-formed piece is higher than that of a material to be joined to the pre-formed piece, or the elastic limit of the amorphous alloy material is larger than about 1.5%. Therefore, the use of the amorphous alloy to be joined to other materials may be largely restricted.
Meanwhile, in terms of joining technique, buckling, nut, welding, bonding and other conventional techniques are widely used, which may cause low strength and poor reliability or cause high cost due to process complexity. Even if the insert molding technique is used, due to huge difference of heterogenic materials, the bonding strength is still poor.
Embodiments of the present disclosure seek to solve at least one of the problems existing in the prior art to at least some extent. Accordingly, a method of joining an amorphous alloy material to a heterogeneous material is provided. By the method, high bonding strength and high reliability between the amorphous alloy material and the heterogeneous material may be ensured, a composite made of the amorphous alloy material and the heterogeneous material may have high impact toughness, and the method is simple in process and low in cost.
Further, a composite made of the amorphous alloy material and the heterogeneous material is also provided, which may have high strength, high impact toughness and high reliability. Therefore, the use requirements for the amorphous alloy material and the use amount of the amorphous alloy material may be reduced, the manufacturing process may be simplified, and the production cost may be reduced.
According to an aspect of the present disclosure, a method of joining an amorphous alloy material to a heterogeneous material is provided. The method comprises steps of:
placing a pre-formed piece made of one of the amorphous alloy material and the heterogeneous material into a mold;
heating the other of the amorphous alloy material and the heterogeneous material to a predetermined temperature, and then casting the other of the amorphous alloy material and the heterogeneous material into the mold to form a transition connection part joining the amorphous alloy material to the heterogeneous material and having one of a fusion welded structure, a microstructure reinforcing connection structure and a composite connection structure, in which the fusion welded structure is formed by the amorphous alloy material and the heterogeneous material via fusion welding, the microstructure reinforcing connection structure is formed by a microstructure on a surface of the pre-formed piece and the other of the amorphous alloy material and the heterogeneous material, and the composite connection structure comprises the fusion welded structure and the microstructure reinforcing connection structure; and
cooling the amorphous alloy material and the heterogeneous material at a rate higher than a critical cooling rate of the amorphous alloy material to obtain a composite formed by the amorphous alloy material to the heterogeneous material joined via the transition connection part.
With the method of joining the amorphous alloy material to the heterogeneous material according to an embodiment of the present disclosure, the amorphous alloy material is joined to the heterogeneous material by a fusion welded structure, a microstructure reinforcing connection structure and a composite connection structure comprising the fusion welded structure and the microstructure reinforcing connection structure which are formed by the amorphous alloy material and the heterogeneous material, thus enhancing the bonding strength between the amorphous alloy material and the heterogeneous material, reducing the requirements for the forming ability and the performance of the amorphous alloy material, reducing the requirements for the elastic deformation of the amorphous alloy material, and enhancing the applicability of the amorphous alloy material.
According to another aspect of the present disclosure, a composite made of an amorphous alloy material and a heterogeneous material is provided. The composite comprises: a first part made of the amorphous alloy material; a second part made of the heterogeneous material; and a transition connection part joining the first part to the second part and having one of a fusion welded structure, a microstructure reinforcing connection structure and a composite connection structure, in which the fusion welded structure is formed by the amorphous alloy material and the heterogeneous material via fusion welding, the microstructure reinforcing connection structure is formed by a microstructure on a surface of a pre-formed piece made of one of the amorphous alloy material and the heterogeneous material and the other of the amorphous alloy material and the heterogeneous material, and the composite connection structure comprises the fusion welded structure and the microstructure reinforcing connection structure.
With the composite made of the amorphous alloy material and the heterogeneous material according to an embodiment of the present disclosure, the bonding strength between the amorphous alloy material and the heterogeneous material may be enhanced, the requirements for the forming ability and the performance of the amorphous alloy material may be reduced, the composite may be used for manufacturing an article with high manufacturing precision and complex structure, the use amount of the amorphous alloy material may be decreased, and the cost may be reduced.
Additional aspects and advantages of embodiments of present disclosure will be given in part in the following descriptions, become apparent in part from the following descriptions, or be learned from the practice of the embodiments of the present disclosure.
These and other aspects and advantages of embodiments of the present disclosure will become apparent and more readily appreciated from the following descriptions made with reference to the accompanying drawings, in which:
Reference will be made in detail to embodiments of the present disclosure. The embodiments described herein with reference to drawings are explanatory, illustrative, and used to generally understand the present disclosure. The embodiments shall not be construed to limit the present disclosure. The same or similar elements and the elements having same or similar functions are denoted by like reference numerals throughout the descriptions.
In the description, term “heterogeneous material” refers to a material which has characteristics (such as material characteristics and/or chemical property) obviously different from those of an amorphous alloy material to be joined to the heterogeneous material. It would be appreciated that the heterogeneous material may comprise an amorphous alloy material having a composition different from that of the amorphous alloy material to be joined to the heterogeneous material. In one embodiment, the heterogeneous material may be a heterogeneous metal material.
As shown in
The inventors may achieve high bonding strength and high reliability between the amorphous alloy material and the heterogeneous material by combining respective characteristics of the amorphous alloy material and the heterogeneous material.
It has been found by the inventors that a fusion welded region (i.e., a transition connection part) may be formed by the amorphous alloy material and a conventional metal material. The fusion welded region has a structural feature of gradual transition from an amorphous state to a crystalline state, and the bonding force is present in the form of a metallic bond, so the fusion welded region may have high structural strength. Meanwhile, because the fusion welded region has a structural feature of gradual transition, the fusion welded region may have continuously gradually changed thermal expansion coefficient and heat capacity, so the fusion welded region may have high thermal stability and high anti-structural-deformation ability, as shown in
In the description herein, a bulk amorphous alloy material may refers to an amorphous alloy material with a critical size larger than about 1 mm and a critical cooling rate lower than about 500° C./s.
Because the amorphous alloy material has excellent flowability and strong replication ability, it has been further found by the inventors that the amorphous alloy material may be closely connected with a pre-formed piece made of the heterogeneous material, especially a pre-formed piece with large specific surface or a pre-formed piece having a microstructure, with increased connection area, which may increase the molecular force (e.g., van der Waals force) and produce strong mechanical force by the microstructure of the pre-formed piece so as to achieve reliable bonding strength. In some embodiments, the microstructure on a surface of the pre-formed piece may be shown in
It has been found by the inventors through research that, if the pre-formed piece is made of a heterogeneous metal material and a casting temperature of the melt of the amorphous alloy material is higher than a melting temperature of the heterogeneous metal material by a predetermined value, for example, the predetermined value is not less than about 15% of the melting temperature of the heterogeneous metal material, when the melt of the amorphous alloy material enters into a chamber of a mold and contacts with the heterogeneous metal material, the surface of the heterogeneous metal material will be softened or melted by the melt of the amorphous alloy material, and the amorphous alloy material and the heterogeneous metal material will be subjected to fusion melting. In the description, the term “casting temperature” refers to a temperature at which a melt of a material contacting with a wall of a chamber of a mold or another material in the chamber of the mold after the melt of the material enters into the chamber of the mold. It should be noted that in practical use, because the structure of an article to be manufactured is complex, when the melt of the amorphous alloy material enters into the mold, the temperature distribution of the melt of the amorphous alloy material is nonuniform, so that the temperatures at which the melt of the amorphous alloy material contacts with the pre-formed piece is different. Therefore, mold flow analysis or other temperature tests may be performed according to the structure of the article, the initial temperature of the melt of the amorphous alloy material, and the temperature distribution of the melt of the amorphous alloy material in the mold, to analyze the temperature distribution of the melt of the amorphous alloy material in the mold, so as to determine the casting temperature in each region of the mold or at each point of the mold. According to the welding theory, when a welding member and a member to be welded are both in a molten state and the chemical reaction between the welding member and the member to be welded take place, a fusion welded structure will be formed. The welding member needs latent heat of fusion during the melting process, and consequently may need enough energy. It has been found by the inventors through research that, because the amorphous alloy material has high chemical activity, when the temperature of the melt of the amorphous alloy material is higher than the melting temperature of the heterogeneous metal material by a predetermined value, the amorphous alloy material will supply latent heat of fusion to the heterogeneous metal material and chemically reacts with the heterogeneous metal material to form a stable fusion welded structure. In addition, the amorphous alloy material does not have a fixed melting point, and the amorphous alloy material will be softened and viscous flow will occur at a temperature higher than a glass transition temperature of the amorphous alloy material. Therefore, if the pre-formed piece made of the amorphous alloy material is placed into the mold, it has been found by the inventors through research that, when a casting temperature of the heterogeneous metal material is higher than a glass transition temperature of the amorphous alloy material by a predetermined value, for example, the predetermined value is not less than about 15% of the glass transition temperature of the amorphous alloy material, when the melt of the heterogeneous metal material enters into a chamber of a mold and contacts with the amorphous alloy material, the amorphous alloy material and the heterogeneous metal material will be subjected to fusion melting, and the chemical reaction between the amorphous alloy material and the heterogeneous metal material will take place so as to form a stable fusion melted structure.
When the structure of the article is more complex, the temperature distribution of a melt is nonuniform. If a microstructure is formed on a surface of the pre-formed piece, a fusion welded structure and a microstructure reinforcing connection structure will be formed between the amorphous alloy material and the heterogeneous material, thus further achieving high bonding strength.
It has been found by the inventors through research that achieving high bonding strength may give full play to unique properties of the amorphous alloy material and the heterogeneous material. For example, the amorphous alloy material has properties of high strength, high hardness and high brittleness, while the heterogeneous material has properties of low strength, high toughness and high plasticity. Therefore, when an external force is applied to a composite made of the amorphous alloy material and the heterogeneous material, the heterogeneous material will absorb the deformation energy, so that the composite may exhibit good impact resistance and high drop performance; because the amorphous alloy material has excellent elastic deformation property, the composite may not be deformed significantly. Even if a larger external force is applied to the composite and the amorphous alloy material cracks or breaks, because of high plastic deformation of the heterogeneous material and reliable bonding strength between the amorphous alloy material and the heterogeneous material, the breakage of and the damage to the composite, which may result in serious structural damage, may be avoided, thus achieving high reliability of the composite. Because the cost of a conventional material is usually lower than that of the amorphous alloy material, by reliable connection, the application cost of the amorphous alloy material may be reduced significantly while ensuring that a structural member with high performance is obtained.
In some embodiments, in consideration of practical production and application features of the amorphous alloy material, advantageously, the amorphous alloy material may be a bulk amorphous alloy material. In the description herein, the bulk amorphous alloy material may refers to an amorphous alloy material with a critical size larger than about 1 mm.
The method of joining the amorphous alloy material to the heterogeneous material and the composite formed by joining the amorphous alloy material to the heterogeneous material by the method according to an embodiment of the present disclosure will be described below with reference to the drawings.
It should be noted that the transition connection part 103 described herein means a transitional portion or area between the first part 101 and the second part 102, which should not be confined to a specific dimension or configuration. That is, the transition connection part 103 is a part composed of the amorphous alloy material and the non-amorphous material which are crossed, cross-linked, welded or joined at the interface therebetween.
In the process of joining the amorphous alloy material to the heterogeneous material, depending on different materials of the pre-formed piece, the joining processes are different.
The method of joining the amorphous alloy material to the heterogeneous material according to a first embodiment of the present disclosure will be described below with reference to
As shown in
In some embodiments, a casting temperature of the amorphous alloy material is higher than a melting temperature of the heterogeneous material by a predetermined value, for example, the predetermined value is not less than about 15% of the melting temperature of the heterogeneous material. As described above, because the casting temperature of the amorphous alloy material is higher than the melting temperature of the heterogeneous material by a predetermined value, the transition connection part formed by the amorphous alloy material and the heterogeneous material via fusion welding has a fusion welded structure.
As shown in
In this embodiment, the pre-formed piece made of the heterogeneous material is joined to the amorphous alloy material by the transition connection part, and the transition connection part has a fusion welded structure, thus enhancing the bonding strength between the amorphous alloy material and the heterogeneous material and reducing the requirements for the forming ability and the performance of the amorphous alloy material largely. Advantageously, the amorphous alloy material is a bulk amorphous alloy material with a critical size larger than about 1 mm. Meanwhile, because high bonding strength between the amorphous alloy material and the heterogeneous material is achieved, the elastic limit of the amorphous alloy material may be reduced to about 0.5%. However, in U.S. Pat. No. 6,771,490, it is required that the amorphous alloy material has an elastic limit of about 1.5% to ensure the safety of an article structure. Because the requirement for the performance of the amorphous alloy material is reduced, the amorphous alloy material may be a bulk amorphous alloy material, which has a crystalline phase produced during the casting process because of small critical size or is doped with inorganic substances. It has been found by the inventors through research that, as long as it is ensured that the amorphous alloy material has an elastic limit of about 0.5% or more in practical use, the application requirements may be met.
In some embodiments, during the cooling process, the fusion welded structure may have one of an amorphous structure, a crystalline structure, and any combination thereof.
More advantageously, the amorphous alloy material contains crystalline substances or is doped with inorganic substances. In some embodiments, the amorphous alloy material may be at least one material selected from a group consisting of a Fe-based amorphous alloy, a Zr-based amorphous alloy, a Cu-based amorphous alloy, a Ti-based amorphous alloy, and a Ni-based amorphous alloy.
Advantageously, the matrix elements or the major elements of the heterogeneous material may be similar to the major elements of the amorphous alloy material so as to achieve better welding effect, thus achieving higher bonding strength.
In the practical article application process, the amorphous alloy material may be flexibly selected according to practical requirements. In consideration of factors of the cost and the comprehensive performance, advantageously, the amorphous alloy material may be at least one material selected from a group consisting of a Fe-based amorphous alloy, a Zr-based amorphous alloy, a Cu-based amorphous alloy, a Ti-based amorphous alloy, and a Ni-based amorphous alloy. According to the current situation of the research on the amorphous alloy material and the requirement for the performance of the amorphous alloy material, advantageously, the amorphous alloy material may be represented by at least one of the following general formulas:
Zra1Alb1Cuc1Nid1Ye1, in which 40≦a1≦70; 5≦b1≦35; 5≦c1≦40; 5≦d1≦14; 0≦e1≦5; a1, b1, c1, d1 and e1 are each atomic percents; and the amorphous alloy may contain about 5 atomic percents or less of other elements or impurity elements;
Zra2Alb2Cuc2(M1)d2, in which 30≦a2≦70; 5≦b2≦35; 5≦c2≦40; 5≦d2≦30; M1 is at least one element selected from the group consisting of Nb, Sc, Ta, Ni, Co, Y, Ag, Fe, Sn, Hf, Ti and Be; a2, b2, c2 and d2 are each atomic percents; and the amorphous alloy may contain about 5 atomic percents or less of other elements or impurity elements;
(Zr,Ti)a3(Cu,Ni)b3Bec3(M2)d3, in which 40≦a3≦60; 15≦b3≦35; 0≦c3≦25; 5≦d3≦30; M2 is at least one element selected from the group consisting of Nb, Sc, Ta, Y, Ag, Fe, Sn, Al, Hf and rare earth elements; a3, b3, c3 and d3 are each atomic percents; and the amorphous alloy may contain about 5 atomic percents or less of other elements or impurity elements;
Tia4Cub4(M3)c4(M4)d4, in which M3 is at least one element selected from the group consisting of Ni, Fe, Co, Mn, Ru, Ag, Pd, Pt and Sn; M4 is at least one element selected from the group consisting of Al, Be, Y and Sc; a4, b4, c4 and d4 are each atomic percents; 40≦a4≦55; 25≦b4≦45; 0≦c4≦4; 1≦d4≦7; and the sum of a4, b4, c4 and d4 is 100;
Fea5Crb5Moc5(M5)d5Be5Yf5, in which 40≦a5≦70; 0<b5≦20; 0<c5≦20; 0<d5≦10; 0<e5≦30; 0<f5≦10; a5, b5, c5, d5, e5 and f5 are each atomic percents; the sum of a5, b5, c5, d5, e5 and f5 is 100; and M5 is at least one element selected from the group consisting of Zr, Al, Ti, Mn, W, Co, C, Si, Nd and Hf;
Nia6Zrb6(M6)c6, in which 40≦a6≦60, 10≦b6≦30, 5≦c6≦25, a6, b6 and c6 are each atomic percents; the sum of a6, b6 and c6 is 100; and M6 is at least one element selected from the group consisting of Nb, Ti, Co, Cu, Al, Hf, Si and rare earth elements; and
Cu(100-a7-b7-c7-d7)Zra7Alb7 (M7)c7 (M8)d7, in which 36≦a7≦49; 1≦b7≦10; 0≦c7≦10; 0≦d7≦5; a7, b7, c7 and d7 are each atomic percents; M7 is at least one element selected from the group consisting of Nb, Ti, Be, Ag and Y; M8 is at least one element selected from the group consisting of amphoteric elements, Sn and Si; and the amorphous alloy may contain about 5 atomic percents or less of other elements or impurity elements.
In addition, other amorphous alloy materials, for example, the bulk amorphous alloys disclosed in U.S. Pat. Nos. 5,288,344; 5,368,659; 5,618,359; 6,682,611; 5,735,975, may also be used in the present disclosure.
In some embodiments, the heterogeneous material may be a heterogeneous metal material; and the heterogeneous metal material may be selected from a group consisting of a steel, an aluminum alloy, a magnesium alloy, a nickel alloy, a copper alloy, a titanium alloy, a zinc alloy, a heterogeneous bulk amorphous alloy, and any combination thereof.
In practical production and application, in consideration of complementary advantages of the amorphous alloy material and the heterogeneous material, advantageously, the pre-formed piece made of the heterogeneous material may be a workpiece with a certain structural feature, for example, a structural piece such as at least one of a sheet, a shaft, a frame, a nut, and a buckle. Advantageously, the sheet has a thickness less than about 0.3 mm.
It should be noted that, when the transition connection part 103 has a fusion welded structure (as shown in
Because the amorphous alloy material has good casting performance and the nature of glass, advantageously, the casting step is performed by die casting, gravity casting or squeeze casting. Meanwhile, because the amorphous alloy material in a high-temperature state or a molten state has high chemical activity and the critical feature of the amorphous alloy material may be easily affected by nonmetal impurity elements, advantageously, the casting step is performed under vacuum or inert gas protection.
The method of joining the amorphous alloy material to the heterogeneous material according to a second embodiment of the present disclosure will be described below with reference to
As shown in
In some embodiments, a casting temperature of the heterogeneous material is higher than a glass transition temperature of the amorphous alloy material by a predetermined value, for example, the predetermined value is not less than about 15% of the glass transition temperature of the amorphous alloy material. As described above, because the casting temperature of the heterogeneous material is higher than the glass transition temperature of the amorphous alloy material by a predetermined value, the transition connection part is formed by the amorphous alloy material and the heterogeneous material via fusion welding. Advantageously, the casting temperature of the heterogeneous material is higher than a melting temperature of the amorphous alloy material.
Other aspects of the method of joining the amorphous alloy material to the heterogeneous material according to the second embodiment of the present disclosure are the same as those of the method of joining the amorphous alloy material to the heterogeneous material according to the first embodiment of the present disclosure, so a detailed description thereof will be omitted here.
The method of joining the amorphous alloy material to the heterogeneous material according to a third embodiment of the present disclosure will be described below with reference to
As shown in
In some embodiments, a casting temperature of the amorphous alloy material is lower than a melting temperature of the heterogeneous material, so that the transition connection part between the amorphous alloy material and the heterogeneous material has a microstructure reinforcing connection structure formed by the amorphous alloy material and the microstructure on the surface of the pre-formed piece. By forming the microstructure reinforcing connection structure, the bonding strength between the amorphous alloy material and the heterogeneous material may be enhanced.
Because the casting temperature of the amorphous alloy material is lower than the melting temperature of the heterogeneous material, the melt of the amorphous alloy material may not destroy the microstructure on the surface of the pre-formed piece, so that the microstructure reinforcing connection structure may be formed by the amorphous alloy material and the microstructure on the surface of the pre-formed piece to enhance the bonding strength between the amorphous alloy material and the heterogeneous material.
In consideration of the influence of excellent casting performance and strong replication characteristics of the amorphous alloy material on the microstructure reinforcing connection structure, it has been found by the inventors through research that, advantageously, the microstructure on the surface of the pre-formed piece is at least one of a hole, a closed or semi-closed honeycomb structure, and a surface structure with a roughness Ra between about 1 μm and about 250 μm, thus achieving excellent bonding strength. Advantageously, the minimum three-dimensional feature size of the hole and/or the honeycomb structure ranges from about 1 μm to about 3000 μm.
In consideration of the economical efficiency of the production, in some embodiments, advantageously, the microstructure may be formed by at least one of shot blasting, sand blasting, machining, chemical corrosion, laser machining, foaming, and molding.
It should be noted that, the term “feature size” should be understood in a broad sense. For example, when the microstructure is a hole, the feature size may refer to the diameter of the hole; and when the microstructure is a honeycomb structure, the feature size may refer to the diameter of a hole of the honeycomb structure.
In this embodiment, because the transition connection part between the amorphous alloy material and the heterogeneous material has a microstructure reinforcing connection structure, the heterogeneous material may be a material with a high melting temperature or a material with a low melting temperature, and may also be an amorphous alloy having characteristics different from those of an amorphous alloy material to be joined to the heterogeneous material. It has been found by the inventors through research that, advantageously, the heterogeneous material is selected from a group consisting of a steel, an aluminum alloy, a magnesium alloy, a nickel alloy, a copper alloy, a titanium alloy, a zinc alloy, a plastic material, ceramics, glass, a heterogeneous bulk amorphous alloy, and any combination thereof.
When the heterogeneous material is ceramics or glass, because the heterogeneous material needs to sustain high thermal shock during the casting process, advantageously, the heterogeneous material has low thermal expansion coefficient to resist the change of the temperature. It has been found by the inventors through research that, advantageously, the ceramics is selected from the group consisting of aluminum oxide ceramics, zirconium oxide ceramics, silicon nitride ceramics, boron carbide ceramics, silicon carbide ceramics, and any combination thereof, each of which has low thermal expansion coefficient; and advantageously, the glass is selected from the group consisting of glass ceramics and quartz glass, each of which has low thermal expansion coefficient.
When the heterogeneous material is a plastic material, advantageously, the plastic material is selected from a group consisting of polyethylene (PE), polyvinyl chloride, polystyrene, polyvinyl alcohol, polypropylene, polybutylene, polyisobutylene, polyformaldehyde, polyamide, polycarbonate, polytetrafluoroethylene, polyethylene terephthalate, an epoxy resin, phenolic resin, polyurethane, and a rubber.
In some embodiments, because the heterogeneous material may be a nonmetal heterogeneous material, the casting step may be performed by die casting, gravity casting or injection molding. When the heterogeneous material is a plastic material, advantageously, the casting step may be performed by injection molding.
It should be noted that, in some embodiments, the casting process is not limited to the above casting processes. For example, the casting process may be permanent molding, die casting, hot pressing or a continuous process such as planar flow casting. One such die-casting process is disclosed in U.S. Pat. No. 5,711,363, which is incorporated by reference. Other casting processes are disclosed in, for example, U.S. Pat. Nos. 6,027,586; 5,950,704; 5,896,642; 5,324,368; 5,306,463, each of which is incorporated by reference in its entirety. In some embodiments, because the amorphous alloy material has high strength and metastable structural characteristics, the obtained composite made of the amorphous alloy material and the heterogeneous material may not need to be subjected to heat treatment.
In the following, only the processes of die casting and hot pressing for joining the amorphous alloy material to the heterogeneous material will be described in detail.
Die Casting
The pre-formed piece made of the heterogeneous material and formed with a microstructure on a surface thereof is placed in a die-casting mold and fixed onto the die-casting mold. Then, the amorphous alloy material may be heated to the glass transition temperature to form a melt or a semisolid melt of the amorphous alloy material, which is cast into a casting chamber of the die-casting mold to perform die casting. A casting temperature of the amorphous alloy material is lower than a melting temperature of the heterogeneous material. In the die casting process, the temperature of the melt of the amorphous alloy material is higher than the melting temperature of the amorphous alloy material to facilitate the feeding operation. The entire die casting process only lasts for tens of seconds or less, for example, ten seconds or less if hot chamber die casting is used, thus increasing the yield dramatically. Due to the excellent flowability of the molten amorphous alloy material, the amorphous alloy materials may be tightly bonded to the pre-formed piece made of the heterogeneous material via the microstructure on the surface of the pre-formed piece to form a transition connection part having a microstructure reinforcing connection structure. Thereafter, the mold are cooled at a rate higher than a critical cooling rate of the amorphous alloy material to ensure that the amorphous alloy material remains substantially amorphous, so as to obtain a composite made of the amorphous alloy material and the heterogeneous material. Finally, the die-casting mold is opened to remove the composite.
It should be noted that when the transition connection part having a fusion welded structure is formed by the die casting process, it is only required that the casting temperature of the amorphous alloy material is higher than the melting temperature of the heterogeneous material, but it is not required that a microstructure is formed on the surface of the pre-formed piece made of the heterogeneous material, otherwise the microstructure may be destroyed.
Hot Pressing
The pre-formed piece made of the heterogeneous material and formed with a microstructure on a surface thereof is placed in a hot pressing chamber of a hot pressing mold of a hot press and fixed onto the hot pressing mold. Then, the amorphous alloy material is placed in the hot pressing chamber, heated to a temperature not lower than the glass transition temperature, and pressed under a predetermined shaping pressure at a certain rate into a predetermined shape. The amorphous alloy material may be joined to the pre-formed piece under the pressure. Accordingly, the amorphous alloy material is tightly filled in the microstructure to form the microstructure reinforcing connection structure, that is, to form the transition connection part 103 having the microstructure reinforcing connection structure. Due to the excellent flowability of the molten amorphous alloy material, the amorphous alloy materials may be tightly bonded to the pre-formed piece made of the heterogeneous material via the microstructure under the directly applied thermal pressure. Thereafter, the mold are cooled at a rate higher than a critical cooling rate of the amorphous alloy material to ensure that the amorphous alloy material remains substantially amorphous, so as to obtain a composite made of the amorphous alloy material and the heterogeneous material. Finally, the hot pressing mold is opened to remove the composite. The hot pressing is performed mainly by using the superplastic rheology or semisolid flow of a material, and in some embodiments, the hot pressing is performed mainly by using the semisolid flow of the amorphous alloy material due to the supercooled liquid phase region thereof, so that in the hot pressing, the casting temperature of the amorphous alloy material is higher than the glass transition temperature Tg of the amorphous alloy material, but lower than the melting temperature of the amorphous alloy material.
It should be noted that other casting processes, for example, injection casting or insert molding, may also be used to join the amorphous alloy material to the heterogeneous material via the microstructure. Therefore, the die casting and the hot pressing are illustrated for exemplary purpose rather than limitation.
The method of joining the amorphous alloy material to the heterogeneous material according to a fourth embodiment of the present disclosure will be described below with reference to
As shown in
In some embodiments, a casting temperature of the heterogeneous material is lower than a glass transition temperature of the amorphous alloy material, so that the transition connection part between the amorphous alloy material and the heterogeneous material may have a microstructure reinforcing connection structure formed by the heterogeneous material and the microstructure on the surface of the pre-formed piece. By forming the microstructure reinforcing connection structure, the bonding strength between the amorphous alloy material and the heterogeneous material may be enhanced.
Because the casting temperature of the heterogeneous material is lower than the glass transition temperature of the amorphous alloy material, the melt of the heterogeneous material may not destroy the microstructure on the surface of the pre-formed piece, so that the microstructure reinforcing connection structure may be formed by the heterogeneous material and the microstructure on the surface of the pre-formed piece to enhance the bonding strength between the amorphous alloy material and the heterogeneous material.
Other aspects of the method of joining the amorphous alloy material to the heterogeneous material according to the fourth embodiment of the present disclosure may be the same as those of the method of joining the amorphous alloy material to the heterogeneous material according to the third embodiment of the present disclosure, so a detailed description thereof will be omitted here.
The method of joining the amorphous alloy material to the heterogeneous material according to a fifth embodiment of the present disclosure will be described below with reference to
As shown in
In some embodiments, a casting temperature of the amorphous alloy material in a first partial region of the mold is lower than a melting temperature of the heterogeneous material, so that the transition connection part between the amorphous alloy material and the heterogeneous material may have a microstructure reinforcing connection structure formed by the amorphous alloy material and the microstructure on the surface of the pre-formed piece. By forming the microstructure reinforcing connection structure, the bonding strength between the amorphous alloy material and the heterogeneous material may be enhanced. In some embodiments, a casting temperature of the amorphous alloy material in a second partial region of the mold is higher than the melting temperature of the heterogeneous material by a predetermined value, and consequently the melt of the amorphous alloy material may destroy the microstructure on the surface of the pre-formed piece, so that the transition connection part having a fusion welded structure may be formed by the amorphous alloy material and the heterogeneous material via fusion welding.
In other words, the transition connection part between the amorphous alloy material and the heterogeneous material has a microstructure reinforcing connection structure and a fusion welded structure, which may be referred to as a composite connection structure.
In this embodiment, the transition connection part between the amorphous alloy material and the heterogeneous material has a microstructure reinforcing connection structure and a fusion welded structure, thus further enhancing the bonding strength between the amorphous alloy material and the heterogeneous material.
In an alternative embodiment, the pre-formed piece may be made of the amorphous alloy material, and the heterogeneous material is heated to a temperature not lower than a melting temperature of the heterogeneous material and cast into the mold, in which a casting temperature of the heterogeneous material in a first partial region of the mold is lower than a glass transition temperature of the amorphous alloy material, and a casting temperature of the heterogeneous material in a second partial region of the mold is higher than the glass transition temperature of the amorphous alloy material by a predetermined value. In this embodiment, the transition connection part between the amorphous alloy material and the heterogeneous material may also have a composite connection structure.
Examples of the present disclosure will be described below.
Amorphous alloy components were mixed according to a proportion shown in Table 1 and melted to obtain an ingot of a Zr-based amorphous alloy, which was called an amorphous alloy for short in the following. As determined by DSC (differential scanning calorimetry) analysis, the glass transition temperature and the melting temperature of the amorphous alloy were 420° C. and 835° C. respectively. It was proven by X-ray diffraction that the amorphous alloy was completely amorphous. A stainless steel, a magnesium alloy, an aluminum alloy, a zinc alloy, and the amorphous alloy were made into pre-formed pieces 12 shown in
In addition, the amorphous alloy was made into a pre-formed piece which was placed in a mold, the zinc alloy was heated to a temperature which is not lower than the melting temperature of the zinc alloy and not lower than the glass transition temperature Tg of the amorphous alloy, the melt of the zinc alloy was cast into the mold and joined to the pre-formed piece, and the mold was cooled and opened to obtain a composite workpiece shown in
After the composite workpieces were manufactured, free-drop strength testing was performed for the obtained 100 workpieces, and the test results were shown in Table 1. It may be seen from Table 1 that, due to the brittleness of the amorphous alloy, 90% of the workpieces merely made of the amorphous alloy breaks under the impact of 2.4 joules of energy; due to low strength and good plastic deformation of the stainless steel, 100% of the workpieces merely made of the stainless steel are bent; however, there are cracks on only a part of the workpieces made of the amorphous alloy and the heterogeneous material according to an embodiment of the present disclosure, and the integrity of the article reaches 100%, thus ensuring high strength and high use safety of the composite workpieces.
Amorphous alloy components were mixed according to a proportion shown in Table 2 and melted to obtain an ingot of a Zr-based amorphous alloy, which was called an amorphous alloy for short in the following. As determined by DSC analysis, the glass transition temperature and the melting temperature of the amorphous alloy were 420° C. and 835° C. respectively. It was proven by X-ray diffraction that the amorphous alloy was completely amorphous. A stainless steel, a magnesium alloy, an aluminum alloy, a zinc alloy, and the amorphous alloy were made into pre-formed pieces 12 shown in
In addition, a pre-formed piece made of the amorphous alloy was placed in an injection mold, the PE plastic was heated to a temperature not lower than the melting temperature thereof, the melt of the PE plastic was cast into the injection mold and joined to the pre-formed piece, and the injection mold was cooled and opened to obtain a composite workpiece shown in
After the composite workpieces were manufactured, the bonding strength and the impact toughness of the obtained workpieces were tested respectively. The bonding strength of the workpieces was determined by tensile tests on a universal mechanical testing machine. The toughness of the workpieces was obtained by Izod unnotched impact tests. The test results were shown in Table 2. In addition, the tensile curves of the amorphous alloy, the composite made of the amorphous alloy and the stainless steel, and the stainless steel were shown in
It may be seen from Table 2 that, compared with conventional physical joining ways, the bonding strength (for example, the microstructure reinforcing connection structure and/or the fusion welded structure) between the amorphous alloy material and the heterogeneous material according to an embodiment of the present disclosure may be enhanced significantly; and although the bonding strength between the amorphous alloy material and the heterogeneous material according to an embodiment of the present disclosure is lower than the strength of the amorphous alloy material, the impact toughness of the composite according to an embodiment of the present disclosure are enhanced significantly, and the bonding strength between the amorphous alloy material and the heterogeneous material according to an embodiment of the present disclosure is higher than the bonding strength between a conventional amorphous alloy and the stainless steel. It may be seen from
Meanwhile, when the amorphous alloy material wraps up the heterogeneous material or is partially joined to the heterogeneous material, high hardness, excellent wear resistance and corrosion resistance of the amorphous alloy material may be brought into play, and the use amount of the amorphous alloy material may be saved, thus saving the cost.
When the heterogeneous material wraps up the amorphous alloy material or is partially joined to the amorphous alloy material, low strength of the heterogeneous material may be compensated for, however, high plastic deformation and large impact toughness of the heterogeneous material may be brought into play, as shown by the example where the plastic is joined to the amorphous alloy in Table 2.
Data of the performance of the composite workpieces which were formed by the amorphous alloy to a heterogeneous material via fusion welding and which are not formed by fusion welding the amorphous alloy to a heterogeneous material were listed in Table 3. The composition, the melting temperature and the glass transition temperature of the amorphous alloy, the casting temperature of the melt of the amorphous alloy, the surface state of each pre-formed piece, the melting temperature and the casting temperature of the heterogeneous material, and the joining ways were all listed in Table 3. The bonding performance data of the composites formed by joining the amorphous alloy to a heterogeneous material were also listed in Table 3. The methods of joining the amorphous alloy to a heterogeneous material were the same as those in Example 1.
It may be seen from Table 3 that, the bonding strength and the impact toughness of the composites formed by the amorphous alloy to the heterogeneous material via fusion welding according to an embodiment of the present disclosure are significantly higher than those of the composites in the comparative examples, in which the bonding strength and the impact toughness of a part of the composites may be 2 times or more as high as those of the composites formed by a conventional physical joining way, thus enhancing the strength and the safety of the composite largely.
Therefore, the composite formed by the method of joining the amorphous alloy material to the heterogeneous material according to an embodiment of the present disclosure may have high strength and high use safety, thus enhancing the safety performance of the article largely. Meanwhile, high strength may be beneficial for the miniaturization of the article.
Data of the performance of the composite workpieces formed by joining different amorphous alloys to the heterogeneous material, i.e., a stainless steel, were listed in Table 4. The composition of each amorphous alloy, the content of the crystalline phase in each amorphous alloy, the critical size of each amorphous alloy, the elastic limit of each amorphous alloy, the surface state of each pre-formed piece, and the joining ways were listed in Table 4 in detail. The bonding performance data of the composites formed by joining two amorphous alloys, i.e., an amorphous alloy and a heterogeneous amorphous alloy, were also listed in Table 4. The methods of joining the amorphous alloys to the heterogeneous material were the same as those in Example 1.
It may be seen from Table 4 that, the bonding strength and the impact toughness of the composite formed by joining the amorphous alloy material to the heterogeneous material according to an embodiment of the present disclosure are significantly higher than those of the composites in the comparative examples, the composites formed by joining different amorphous alloys with a critical size larger than 1 mm and an elastic limit larger than 0.5% to the stainless steel may all have high strength and high toughness, and the composite having high strength may also be obtained by joining the amorphous alloy to a heterogeneous amorphous alloy. It may also be seen from Table 4 that, the bonding strength and the impact toughness of the composite formed by joining the amorphous alloy having a crystalline phase to the stainless steel are also higher than those of the composites in the comparative examples.
Therefore, the method of joining the amorphous alloy material to the heterogeneous material and the composite formed by the same according to an embodiment of the present disclosure may have wide applicability, thus supplying technical conditions to the application of the amorphous alloy material and the reduction of the cost.
A surface of the frame portion 1 is polished and decorated, and then the shell for the mobile phone is assembled with other members for the mobile phone to form the mobile phone. The obtained mobile phone has performances of wear resistance and corrosion resistance, and may pass the rigorous drop test for a mobile phone. Therefore, the composite made of the amorphous alloy and the stainless steel according to an embodiment of the present disclosure may protect functional members inside the mobile phone, and the mobile phone may have high safety and high reliability. Meanwhile, the pre-implantation of the stainless steel sheet stamped structure 2 with a thickness of 0.1 mm may reduce the amount of the amorphous alloy, reduce the forming difficulty of the amorphous alloy, enhance the production yield, and reduce the production cost of the composite, which reflects the significant advantages of the method of joining the amorphous alloy material to the heterogeneous material and the composite formed by the same according to an embodiment of the present disclosure.
Reference throughout this specification to “an embodiment,” “some embodiments,” “one embodiment”, “another example,” “an example,” “a specific example,” or “some examples,” means that a particular feature, structure, material, or characteristic described in connection with the embodiment or example is included in at least one embodiment or example of the present disclosure. Thus, the appearances of the phrases such as “in some embodiments,” “in one embodiment”, “in an embodiment”, “in another example,” “in an example,” “in a specific example,” or “in some examples,” in various places throughout this specification are not necessarily referring to the same embodiment or example of the present disclosure. Furthermore, the particular features, structures, materials, or characteristics may be combined in any suitable manner in one or more embodiments or examples.
Although explanatory embodiments have been shown and described, it would be appreciated by those skilled in the art that the above embodiments can not be construed to limit the present disclosure, and changes, alternatives, and modifications can be made in the embodiments without departing from spirit, principles and scope of the present disclosure.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2011 1 0237931 | Aug 2011 | CN | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/CN2012/080190 | 8/15/2012 | WO | 00 | 2/13/2014 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2013/023606 | 2/21/2013 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 3921701 | Cordone | Nov 1975 | A |
| 5482580 | Scruggs et al. | Jan 1996 | A |
| 5896911 | Gegel | Apr 1999 | A |
| 6652925 | Schwarz et al. | Nov 2003 | B1 |
| 6771490 | Peker et al. | Aug 2004 | B2 |
| 6818078 | Kim et al. | Nov 2004 | B2 |
| 20030024616 | Kim et al. | Feb 2003 | A1 |
| 20070111119 | Hu et al. | May 2007 | A1 |
| 20090239088 | Collier et al. | Sep 2009 | A1 |
| 20130040163 | Chiang et al. | Feb 2013 | A1 |
| Number | Date | Country |
|---|---|---|
| 101829844 | Sep 2010 | CN |
| 102152540 | Aug 2011 | CN |
| H07268597 | Oct 1995 | JP |
| 2009084613 | Apr 2009 | JP |
| 2009173964 | Aug 2009 | JP |
| WO 2012065323 | May 2012 | WO |
| Entry |
|---|
| International Search Report, International Application No. PCT/CN2012/080190, Nov. 22, 2012, 3 pages. |
| Bao, Jidong, “Research Development in Joining Amorphous Alloys,” Gansu Science and Technology, Jan. 2010, vol. 26, No. 1, pp. 108-110. |
| Number | Date | Country | |
|---|---|---|---|
| 20140199560 A1 | Jul 2014 | US |