The invention relates to a composite anti-restenosis drug for coronary drug-eluting stent and a controlled release system thereof.
Coronary stent is an interventional medical device primarily used to treat ischemic heart disease due to coronary artery stenosis or occlusion, such as heart attack. Due to the inevitable damage to the coronary vessels during stent expansion, the vascular smooth muscle cells are hyperproliferative, resulting in postoperative in-stent restenosis (ISR). Early coronary stents are made of stainless steel, and a bare stent made of stainless steel has a restenosis rate of up to 20% or more.
With the development of stenting techniques, some anti-restenosis drugs are coated on the stent to form a drug-eluting stent, also known as a drug-releasing stent, in which the drug is mainly carried by a polymer coated on the surface of the metal stent. After the stent is placed in the intravascular lesion, the drug is controlled released upon elution from the polymer coating into the vessel wall tissues to exert a biomedical effect, preventing restenosis and thrombus in the stent after stent implantation. Currently, Sirolimus is the most widely used in-stent anti-restenosis drug since the discovery of drug stents, and Sirolimus derivatives are used by a few companies, such as Everolimus or Paclitaxel, which all show significant superiority against restenosis. In China, arsenic trioxide (As2O3) anti-restenosis drugs developed by Beijing AmsinoMed Medical Co., Ltd. have also achieved good results (CN101161300A). Due to the effect of anti-restenosis drugs, restenosis rate can be controlled to 5% or below.
However, long-term clinical observations of Sirolimus-eluting stents for more than a decade have shown that although the use of Sirolimus has greatly reduced in-stent restenosis, the incidence of intravascular thrombosis in patients has also increased. The main reason lies in that, while Sirolimus inhibits the hyperproliferation of vascular smooth muscles, it also indiscriminately inhibits the growth and repair of vascular endothelial cells. Because of the inhibitory effect of Sirolimus on endothelial cells, coronary vascular endothelium recovery is slow after implantation of a Sirolimus-eluting stent. Some clinical data showed that 10% of stents were not completely covered by endothelium 10 months after stent implantation, and 5% of patients developed fatal late thrombosis. It is well known that incomplete endothelialization after stent implantation is the main cause of intravascular thrombosis. Drug-eluting stents using Sirolimus increases the risk of intravascular thrombosis while significantly reducing in-stent restenosis. In order to prevent thrombosis, patients who use Sirolimus-eluting stents often need long-term or even life-long administration of antithrombotic drugs.
Currently, it is a great challenge in the development of stent interventional therapy to solve the problem of the inhibition of the growth and repair of vascular endothelial cells and subsequent thrombosis caused by anti-restenosis drugs.
An objective of the present invention is to provide a composite drug for coronary drug-eluting stent, which functions to inhibit smooth muscle cell proliferation and facilitate endothelial cell recovery, so as to achieve an excellent in-stent anti-restenosis effect after stent implantation and lower the incidence of intravascular thrombosis.
Another objective of the present invention is to provide the use of the composite drug for coronary drug-eluting stent in the manufacture of a controlled release system of a composite drug for coronary drug-eluting stent for controlling restenosis and preventing thrombosis.
Still another objective of the present invention is to provide a composite drug controlled release system for coronary drug-eluting stent, which allows the composite drug to release in accordance with an optimal profile and achieve the optimal therapeutic efficacy of both controlling restenosis and preventing thrombosis.
In one aspect, the present invention provides a composite drug for coronary drug-eluting stent comprising As2O3 and Sirolimus.
The inventors found in the study that a composite drug prepared from Sirolimus and arsenic trioxide in a certain ratio can reduce or prevent the inhibition of vascular endothelial cell growth and repair, or even accelerate the vascular endothelialization, while achieving a good anti-restenosis effect.
Although it has been reported in the prior art that both Sirolimus and arsenic trioxide can inhibit smooth muscle proliferation and act on the G1 phase of the cell growth cycle, the mechanism of action is different. Sirolimus is a novel macrolide-type immunosuppressive agent that blocks signaling through different cytokine receptors and blocks the progression from the G1 to S phase of T lymphocytes and other cells, thereby exhibiting an inhibitory effect (“The mechanism of action and clinical application of Sirolimus”, Li Min, Zhao Ming, Department of Blood Purification and Kidney Transplantation, Zhujiang Hospital, First Military Medical University, Foreign Medicine and Pharmacy, June 2002, Vol. 29, No. 3). Mitochondria is the most arsenic trioxide-sensitive organelle, and a previous study, “Study on the Mechanisms of Arsenic Trioxide-induced Vascular Smooth Muscle Cells Apoptosis in vitro” (Li Hui et al., Journal of Medical Research, October 2010, Vol. 39, No. 10), found that As2O3 could induce a decrease of mitochondrial transmembrane potential (Δψm) in VSMCs, and the decrease of mitochondrial Δψm was significantly correlated to the apoptosis-inducing effect thereof. In the process of induced apoptosis, because the decrease of Δψm occurs earlier than morphological changes by apoptosis, it is a specific marker of apoptosis. Thus, it has been confirmed that arsenic trioxide induced a decrease of mitochondrial Δψm in VSMCs, which led to apoptosis in VSMCs. The use of Sirolimus in combination with arsenic trioxide as an anti-restenosis drug has not been reported in the prior art.
According to a specific embodiment of the present invention, in the composite drug for coronary drug-eluting stent according to the present invention, the weight ratio between Sirolimus and arsenic trioxide is 1:2 to 2:1.
According to a particular embodiment of the present invention, in the composite drug for coronary drug-eluting stent according to the present invention, based on a stent having an opened external diameter of 3.0 mm, the amount of As2O3used is 1 to 8 μg/mm and the amount of the Sirolimus used is 1 to 8 μg/mm.
According to a specific embodiment of the present invention, in the composite drug for coronary drug-eluting stent according to the present invention, a polymer material may be further combined, and the resultant composition may be used in the preparation of a composite drug controlled release system for coronary drug-eluting stent. Here, the polymer material may specifically include one or more of polyactide (PLA), Polyglycolide (PGA), Poly(lactic-co-glycolic acid) (PLGA), Polycaprolac(PCL), and Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV). The polymer material is primarily used as a drug carrier, and the ratio between the polymer material and the drug may be adjusted as necessary for the release of a specific drug. Preferably, the weight ratio between the polymer material and the drug used in the present invention is 1:0.3 to 1:10.
The present invention proves through experiments that arsenic trioxide at a certain concentration functions to promote endothelial cell proliferation to some extent. According to a specific embodiment of the present invention, in the composite drug for coronary drug eluting stent of the present invention, the use amount of Sirolimus which has an hindrance effect on endothelial recovery can be greatly reduced, and the amount of arsenic trioxide used can be increased, so as to accelerate the endothelialization process of blood vessels while achieving a good anti-restenosis effect. In addition, the composite drug for a coronary drug eluting stent according to the present invention acts on the coronary artery that is damaged upon stent implantation, and shows a stronger effect in inhibiting smooth muscle hyperproliferation and preventing in-stent restenosis than that by using a single drug.
In another aspect, the present invention provides the use of the composite drug for coronary drug-eluting stent in the manufacture of a composite drug controlled release system for coronary drug-eluting stent for controlling restenosis and preventing thrombosis.
In still another aspect, the present invention provides a composite drug controlled release system for coronary drug-eluting stent comprising:
According to a specific embodiment of the present invention, the composite drug controlled release system according to the present invention further comprises the above polymer material. The polymer material is used as a drug carrier and controls the release of the drug, which is preferably a degradable polymer material, for example, any one or more selected from polyactide, polyglycolide, poly(lactic-co-glycolic acid), polycaprolac, and poly(3-hydroxybutyrate-co-3-hydroxyvalerate). Preferably, the weight ratio between the degradable polymer material and the drug is between 1:0.3 to 1:10.
In the composite drug controlled release system according to the present invention, during the preparation of the composite drug controlled release system from the composite drug for coronary drug-eluting stent, As2O3and Sirolimus, or As2O3, Sirolimus and the degradable polymer material may be mixed in a designed ratio (e.g., by simple mixing).
In the present invention, by further changing the structure (monolayer or multilayer) of the drug release system (drug coating) and the ratio between the drug and the polymer material in each layer, a controlled release of the drug may be realized, allowing the composite drug to release in accordance with the optimal profile and achieve the optimal therapeutic efficacy of both controlling restenosis and preventing thrombosis.
According to a specific embodiment of the present invention, in the composite drug controlled release system of the present invention, the drug layer is a composite drug monolayer structure; that is, a layer of the composite drug or the composite drug and degradable polymer material that are proportionally and uniformly mixed is included in the composite drug controlled release system. In other words, the present invention provides a monolayer-structured composite drug release system. In this monolayer-structured composite drug release system, two anti-restenosis drugs (As2O3and Sirolimus) are included, or a polymer material is further included. By adjusting the ratio between the drugs and that between the drugs and the polymer material, a change in the drug release profile is attained, thereby achieving the goal of controlled drug release. Upon consideration for further optimization, in the formulation of the composite drug, the amount of As2O3used is 4 to 8 μg/mm, and the amount of the Sirolimus used is 1 to 5 μg/mm. These amounts are based on a stent having an opened external diameter of 3.0 mm, and the usage of drugs should be increased in proportion to the actual surface area of the stent for a stent having a larger opened external diameter. In such a structure, a layer of polymer material or other materials may be added between the single layer of the mixed drug layer and the stent surface, so as to increase the adhesion of the drug layer to the stent surface. A polymer material or other materials may be spray coated on the outer surface of the monolayer mixed drug layer in order to protect the mixed drug layer, preventing the mixed drug layer from rupture during stent implantation. It was observed in experiments that the release of Sirolimus did not change significantly upon mixing Sirolimus with arsenic trioxide but the releasing performance of arsenic trioxide was greatly improved. By appropriately adjusting the usage ratio between Sirolimus and arsenic trioxide, the release of both Sirolimus and arsenic trioxide may coincide with the release profile according to clinical requirements, to produce the optimal clinical results. Furthermore, since there is only one layer of mixed drug, the drug spraying process to the stent becomes simple and easy. Due to the liposoluble nature of Sirolimus, it may readily penetrate the cell wall to exert the pro-apoptotic effect of the drug on cells. The molecular weight of Sirolimus is four times that of arsenic trioxide. It is quite likely that this mixed drug delivery system allows large molecules of Sirolimus to “carry” small molecules of arsenic trioxide into the cell to help arsenic trioxide to have a better pharmaceutical effect. In this structure, a layer of polymeric material or other materials may be added between the drug layer and the stent surface to increase the adhesion of the drug layer to the stent surface. A polymer material or other materials may be spray coated on the outer surface of the drug layer in order to protect the drug layer, preventing the drug layer from rupture during stent implantation. Preferably, in the monolayer-structured composite drug release system, a degradable polymer material of poly(lactic-co-glycolic acid) (PLGA) is used as a drug carrier.
According to another specific embodiment of the present invention, in the composite drug controlled release system of the present invention, the drug layer is a composite drug multilayer structure; that is, a plurality of layers of the composite drug or the composite drug and degradable polymer material that are proportionally and uniformly mixed are included in the composite drug controlled release system. In the multilayer-structured controlled release system, each layer independently: comprises only one drug; comprises only the composite drug; comprises only the degradable polymer material; comprises only one drug and the degradable polymer material; comprises only the composite drug and the degradable polymer material. In other words, the present invention provides a multilayer-structured (each layer only comprising a single drug) composite drug release system. In this release system, there are a plurality of drug layers, with each layer comprising only a single drug and an optional polymer material, and at least one layer of arsenic trioxide drug layer and at least one layer of Sirolimus layer are included in the overall structure. By adjusting the number of drug layers, the ratio between the drugs and the polymer material in each layer and the relative position of each drug layer, an optimal drug release is achieved. With regard to the drug usage, the total amount of As2O3used in the overall system is 4 to 8 μg/mm and the total amount of the Sirolimus used in the overall system is 1 to 5 μg/mm. These amounts are based on a stent having an opened external diameter of 3.0 mm, and the usage of drugs should be increased in proportion to the actual surface area of the stent for a stent having a larger opened external diameter. In such a structure, a layer of polymer material or other materials may be added between the lowest drug layer and the stent surface, so as to increase the adhesion of the drug layer to the stent surface. A polymer material or other materials may be spray coated on the outer surface of the outermost drug layer in order to protect the drug layers, preventing the drug layers from rupture during stent implantation. Preferably, in the monolayer-structured composite drug release system, a degradable polymer material of poly(lactic-co-glycolic acid) (PLGA) is used as a drug carrier.
According to still another specific embodiment of the present invention, the present invention provides a multilayer-structured (each layer comprising a mixed drug of one or two or more drugs) composite drug release system. In this release system, there are a plurality of drug layers, with each layer comprising one or two or more drugs and an optional polymer material. By adjusting the number of drug layers, the ratio between the drugs and that between the drugs and the polymer material in each layer, as well as the relative position of each drug layer, an optimal drug release is achieved. With regard to the drug usage, the total amount of As2O3used in the overall system is 2 to 10 μg/mm and the total amount of the Sirolimus used in the overall system is 2 to 12 μg/mm. These amounts are based on a stent having an opened external diameter of 3.0 mm, and the usage of drugs should be increased in proportion to the actual surface area of the stent for a stent having a larger opened external diameter. In such a structure, a layer of polymer material or other materials may be added between the lowest drug layer and the stent surface, so as to increase the adhesion of the drug layer to the stent surface. A polymer material or other materials may be spray coated on the outer surface of the outermost drug layer in order to protect the drug layers, preventing the drug layers from rupture during stent implantation.
In another aspect, the present invention provides a method for controlling restenos is and preventing thrombosis with a coronary drug-eluting stent, comprising: implanting a stent having a drug layer into the coronary artery of an individual in need thereof, wherein the drug layer includes a drug layer formed by coating the composite drug for coronary drug-eluting stent according to the present invention.
The present invention has the following technical effects:
The composite drug for coronary drug-eluting stent according to the present invention has an inhibitory effect on smooth muscle cell proliferation and, due to the reduced amount of Sirolimus used, can reduce the damage of the drug to endothelial cells and further effect to facilitate endothelial cell recovery, thereby achieving excellent in-stent anti-restenosis effect after stent implantation and lowering the incidence of intravascular thrombosis. The composite drug controlled release system for coronary drug-eluting stent according to the present invention may allow the composite drug to release in accordance with an optimal profile and achieve the optimal therapeutic efficacy of both controlling restenosis and preventing thrombosis.
Sirolimus has been used for an anti-restenosis drug stent for a long time, and its pro-apoptotic effect on smooth muscle cells and endothelial cells in coronary vessels has been substantiated in tremendous studies and in clinic. As for arsenic trioxide, although it has been used as a drug for treating leukemia for a long time, there still lacks investigation of the mechanism of its in vivo and in vitro action on cells when used in a drug stent. In the present invention, in vitro experiments with arsenic trioxide on smooth muscle cells and endothelial cells of porcine coronary vessels are performed, and a series of significant experimental results are observed. These results confirm that arsenic trioxide has a strong pro-apoptotic effect on smooth muscle cells when it reaches a certain dose. However, for endothelial cells, the pro-apoptotic effect of arsenic trioxide is not obvious. On the contrary, on the first to the third day upon drug action, there even shows a stimulation of growth. This effect is completely different from the simple pro-apoptotic effect of Sirolimus on endothelial cells, and may have a positive impact on rapid endothelial repair.
The present invention also provides two configurations for the controlled release system of a composite drug of As2O3 and Sirolimus: a monolayer-structured composite drug release system and a multilayer-structured (each layer comprising one drug or a mixture of one or two or more drugs) composite drug release system. It is found in the experiments on these controlled release systems that Sirolimus may accelerate the release of As2O3from polymer materials, and further by intricately designing the controlled release system, it is possible for both As2O3 and Sirolimus to achieve optimal release and good clinical results in a controlled release system while substantially reducing the amount of Sirolimus used.
For better understanding of the technical features, purposes and beneficial effects of the present invention, the technical solutions of the present invention will now be set forth in details in connection with the specific examples and the accompanying drawings. It will be appreciated that these examples are merely illustrative of the present invention and are not intended to limit the scope of the present invention.
In designing a drug controlled release system for a drug-eluting stent, the drug and degradable polymer material must be mixed together in a certain manner to be sprayed on the stent, and the drug will be released from the polymer materials after the stent is implanted. Sirolimus can be dissolved in a variety of common organic solvents, and controlled release system can be easily designed by using Sirolimus as an anti-restenosis drug. Arsenic trioxide is an inorganic oxide, with only one crystal form thereof out of three slightly soluble in water, while it cannot be dissolved in common solvents such as ethanol. This makes the subsequent mixing with the polymer material difficult. In addition, it has shown in the experiments that even if arsenic trioxide was mixed in a polymer material in a particulate state, the release rate of the drug could not meet the requirement for clinically effective therapeutic effect until the arsenic trioxide reached a very high concentration. However, this high concentration state significantly reduces the total spraying amount (0.3 μg/mm2) of the polymer material and the drug, which not only makes it difficult to control the spraying process but affects the uniformity of the drug in clinical use as well.
After adding Sirolimus to the arsenic trioxide/polymer material mixture at the same ratio (
In this example, two implementation methods, which achieve controlled drug release by changing the structure (monolayer or multilayer) of the drug release system (drug coating) and the ratio between drug and polymer material in each layer, are exemplified.
In this monolayer-structured release system of mixed drugs, arsenic trioxide, Sirolimus, and a polymer material PLGA are included. By adjusting the ratio between drugs and that between the drug and the polymer material, the drug release profile is changed to achieve the objective of controlled drug release.
As long as there is no adverse interaction between the mixed drugs, a variety of anti-restenosis drugs such as arsenic trioxide, Sirolimus, paclitaxel or the like can be selected for drug mixing in theory. In consideration of clinical and manufacturing optimization, two drugs, arsenic trioxide and Sirolimus, may be selected for mixing. Upon consideration for further optimization, in the formulation of the composite drug, the amount of As2O3 used is 4 to 8 μg/mm, and the amount of the Sirolimus used is 1 to 5 μg/mm. These amounts are based on a stent having an opened external diameter of 3.0 mm, and the use amount of drugs should be increased in proportion to the actual surface area of the stent for a stent having a larger opened external diameter.
In such a structure, a layer of polymer material or other materials may be added between the single layer of the mixed drug layer and the stent surface, so as to increase the adhesion of the drug layer to the stent surface. A polymer material or other materials may be spray coated on the outer surface of the monolayer mixed drug layer in order to protect the mixed drug layer, preventing the mixed drug layer from rupture during stent implantation.
In the process of implementing the monolayer-structured composite drug release system, the ratio between Sirolimus and the degradable polymer material PLGA could be adjusted to allow the release of Sirolimus to reach an optimal profile (
With the mixing of Sirolimus and arsenic trioxide, the release property of arsenic trioxide is greatly improved, and it is thus possible to make the release of both Sirolimus and arsenic trioxide meet the release profile in accordance with clinical requirements by properly adjusting the usage ratio of Sirolimus to arsenic trioxide, thereby producing optimal clinical results. Also, since there is only one mixed drug layer, the drug spraying process for the stent becomes simple and easy.
In this release system, there are a plurality of drug layers, with each layer comprising only a single drug and an optional polymer material. By adjusting the number of drug layers, the ratio between the drugs and the polymer material in each layer and the relative position of each drug layer, an optimal drug release is achieved.
With regard to the use amount for the drug, the total amount of As2O3 used in the overall system is 4 to 8 μg/mm and the total amount of the Sirolimus used in the overall system is 1 to 5 μg/mm. These amounts are based on a stent having an opened external diameter of 3.0 mm, and the use amount of drugs should be increased in proportion to the actual surface area of the stent for a stent having a larger opened external diameter.
In such a structure, a layer of polymer material or other materials with good biocompatibility may be added between the lowest drug layer and the stent surface, for example, a layer of porous metal titanium may be plated on the metallic stent surface, so as to increase the adhesion of the drug layer to the stent surface. A polymer material or other materials may be spray coated on the outer surface of the outermost drug layer in order to protect the drug layers, preventing the drug layers from rupture during stent implantation.
In this release system, there are a plurality of drug layers, with each layer comprising one or two or more drugs and an optional polymer material. By adjusting the number of drug layers, the ratio between the drugs and that between the drugs and the polymer material in each layer, as well as the relative position of each drug layer, an optimal drug release is achieved.
With regard to the drug use amount, the total amount of As2O3used in the overall system is 2 to 10 μg/mm and the total amount of the Sirolimus used in the overall system is 2 to 12 μg/mm. These amounts are based on a stent having an opened external diameter of 3.0 mm, and the use amount of drugs should be increased in proportion to the actual surface area of the stent for a stent having a larger opened external diameter.
In such a structure, a layer of polymer material or other materials with good biocompatibility may be added between the lowest drug layer and the stent surface, so as to increase the adhesion of the drug layer to the stent surface. A polymer material or other materials may be spray coated on the outer surface of the outermost drug layer in order to protect the drug layers, preventing the drug layers from rupture during stent implantation.
Comparative experiments were conducted on porcine coronary animal models by using drug-eluting stents prepared by the implementation methods 1 and 2, respectively. Grouping is shown below:
Coronary angiography and OCT examination results from some stents after stent implantation are shown in the following table:
Groups 1 and 2 were stents with pure arsenic trioxide or Sirolimus respectively that were used as a control group. Groups 3, 4, and 5 were stents with a composite drug (arsenic trioxide and Sirolimus). As compared to those with pure anti-restenosis drugs (arsenic trioxide or Sirolimus as used in this experiment), stents with the composite drug (arsenic trioxide and Sirolimus) showed better in-stent anti-restenosis ability under coronary angiography conditions. The results from OCT observation showed that the coronary vascular endothelium completely covered the stent surface within 3 months when the stent with composite drug was used. Here,
Last but not least, it should be noted that the above examples are merely illustrative of the implementation processes and features of the present invention and not limiting the technical solutions of the present invention. Even though the present invention are described in details with reference to these examples, persons skilled in the art would recognize that modification or equivalent substitution can be made to the present invention and any modification or partial substitution made without departing from the spirit and scope of the present invention is intended to be encompassed within the scope of protection of the present invention.
Number | Date | Country | Kind |
---|---|---|---|
201710669568.6 | Aug 2017 | CN | national |
Filing Document | Filing Date | Country | Kind |
---|---|---|---|
PCT/CN2018/096393 | 7/20/2018 | WO | 00 |