The present invention relates to materials and methods for use in connection with combustion fuels. More particularly, the present invention relates to catalyst particulates and methods of making such particulates, which provide catalytic effect and fuel value to various fuels. Accordingly, the present invention involves the fields of chemistry, combustion, metallurgy, and materials science.
Combustion of various chemical species involves a number of important considerations which can vary from one application to another. One recent area of interest in combustion chemistry is the enhancement of fuels for use in hypersonic jets and other high performance propulsion systems. In such applications, very fast fuel combustion is required for efficient propulsion. For example, in a ramjet or scramjet engine, the high volumetric air flow through the engine requires that combustion takes place on the millisecond or sub-millisecond time frame. This short combustion time frame is important so that combustion is substantially complete before the fuel-air mixture exits the engine. Unfortunately, much of the residence time is required for fuel-air mixing, making combustion on a substantially shorter time scale desirable. Another example of a high performance propulsion system is pulse-detonation engines (PDEs), where the fuel-air mixture combusts as a detonation wave propagates through the engine combustion chamber. Successful propagation of a detonation wave typically requires a sufficiently high rate of combustion to feed the combustion energy into driving the shock wave. The combustion time can depend on the engine tube diameter, but a typical value for the desired combustion time can be less than 100 microseconds. Further, current fuels have a limited energy density, especially when combined with materials having heats of combustion significantly below that of the fuel.
For high speed propulsion systems, the fuel and gas flow should be unimpeded. Thus, fixed catalyst beds are generally not suitable for use in such systems. Further, combustion rates must be increased, while ignition delays should be decreased. Any attempt to improve these aspects should also avoid substantial degradation of the energy density of the fuel.
In order to solve these and other problems, metallized propellants have become known in the art. These metallized propellants typically disperse aluminum or boron particles in a solid or liquid fuel, often as a gelled propellant. Aluminum and boron have high volumetric heats of combustion, relative to typical hydrocarbon fuels. As such, metallized propellants potentially have improved energy content relative to pure hydrocarbons. However, these metallized propellants can also present difficulties with respect to combustion times and efficiencies. These difficulties can reduce their usefulness for many combustion applications and particularly for applications requiring short combustion time scales. As such, materials and methods for improved high speed propulsion fuels and methods continue to be sought.
Accordingly, the present invention provides composite combustion catalyst particles which are suitable for use in various fuels with decreased ignition delays and increased combustion rates. In one aspect, a composite combustion catalyst particle can include a metal core including a combustible metal. The metal core can include a metal oxide coating at least partially surrounding the metal core. Additionally, a catalyst coating can at least partially surround the metal oxide coating or metal core.
In one detailed aspect of the present invention, the combustible metal can be aluminum, boron, magnesium, silicon, titanium, lithium, sodium, potassium, or alloys or composites thereof. In a more detailed aspect, the combustible metal can be aluminum.
Typically, the metal oxide coating can be a metal oxide of the combustible metal, i.e. a native oxide layer. Such metal oxide coatings can vary in thickness, and tend to have a thickness of about 2 nm to about 10 nm.
In yet another aspect of the present invention, the catalyst coating can include a metal which exhibits a catalytic effect for combustion of a fuel. Examples of suitable metals are palladium, platinum, and other noble metals which are known to be effective combustion catalysts. Many such metals can react exothermically with the combustible metal comprising the core of the particle to form intermetallic compounds, such as PdxAly in the case of a palladium catalyst reacting with an aluminum metal core.
In yet another aspect of the present invention, the catalyst coating can include a metal oxide or other metal compound which exhibits a catalytic effect for combustion of a fuel. Examples of suitable metal compounds are rare earth metal oxides, transition metal oxides, and mixtures thereof or multi-metal compounds such as NxMyOz, where N and M represent metallic elements, and O represents oxygen. Typically, such compounds can have a weaker affinity for oxygen than the combustible metal comprising the core of the particle, and thus can react exothermically with the metal core during the combustion process. Regardless of the specific catalyst material, the catalyst coating can have a thickness from about 0.5 nm to about 20 nm.
The composite combustion catalyst particle can be formed in a wide variety of sizes ranging from micron to nanosize particles. In one preferred aspect, the composite combustion catalyst particle is a nanoparticle. For example, composite nanoparticles can have a diameter from about 10 nm to about 500 nm, and in some cases from about 20 nm to about 100 nm. In some cases, such nanoparticles can be further aggregated to form particles in the micron size range.
In still another aspect of the present invention, the composite combustion catalyst particles can be dispersed in a fuel to produce an enhanced fuel. In this way, thorough dispersal can enhance intimate mixing of the hydrocarbon fuel with the composite combustion catalyst particles, and can disperse aggregated particles. Such dispersal can be obtained by mixing, stirring, ultrasonication, or other suitable methods. The hydrocarbon fuel can be either liquid or solid fuel. Liquid fuels such as jet propellant fuels, ramjet fuels, rocket fuels, kerosene, paraffin, and mixtures thereof can be used. Currently, of particular interest is the liquid fuel JP-10.
In order to maintain the volumetric energy density of the enhanced fuel, the composite combustion catalyst particles can have a volumetric heat of combustion ranging from about 80% to 250% of the volumetric heat of combustion of the hydrocarbon fuel. In terms of gravimetric energy density, the gravimetric heat of combustion of the composite combustion catalyst can range from about 50% to 150% relative to the gravimetric heat of combustion of the fuel. Further, although specific compositions can vary, the composite combustion catalyst particles can comprise from about 2 wt % to about 25 wt % of the enhanced fuel.
In accordance with another aspect of the present invention, the composite combustion catalyst particles can be produced by providing metal core particulates and forming a metal oxide coating substantially surrounding the metal core. A catalyst coating can then be formed on at least a portion of the metal oxide coating. The catalyst coating can be formed by a process such as chemical vapor deposition, physical vapor deposition, solution phase deposition, and other known coating techniques.
Advantageously, the composite combustion catalysts of the present invention provide both catalytic enhancement of combustion of the fuel, as well as combustion of the composite particle. More specifically, as the fuel is combusted, the metal core heats. The composition and configuration of the composite particles can provide for additional thermite-type reactions which are highly exothermic, enhance the combustion rate of the metal core, and contribute to the energy released during combustion of the enhanced fuel.
There has thus been outlined, rather broadly, the more important features of the invention so that the detailed description thereof that follows may be better understood, and so that the present contribution to the art may be better appreciated. Other features of the present invention will become clearer from the following detailed description of the invention, taken with the accompanying drawings and claims, or may be learned by the practice of the invention.
Before the present invention is disclosed and described, it is to be understood that this invention is not limited to the particular structures, process steps, or materials disclosed herein, but is extended to equivalents thereof as would be recognized by those ordinarily skilled in the relevant arts. It should also be understood that terminology employed herein is used for the purpose of describing particular embodiments only and is not intended to be limiting.
It must be noted that, as used in this specification and the appended claims, the singular forms “a” and “the” include plural referents unless the context clearly dictates otherwise. Thus, for example, reference to “a composite combustion catalyst particle” includes one or more of such particles, reference to “a coating” includes reference to one or more of such structures, and reference to “a coating process” includes reference to one or more of such processes.
Definitions
In describing and claiming the present invention, the following terminology will be used in accordance with the definitions set forth below.
As used herein, “combustible metal” refers to any metal which has a capacity for oxidation and release of heat and energy.
As used herein, “nanoparticle” refers to a particle having a diameter in the nanometer range, i.e. less than 1 μm. Typically, nanoparticles of the present invention can have a diameter less than about 500 nm, and more particularly from about 4 nm to about 500 nm.
As used herein with respect to an identified property or circumstance, “substantially” refers to a degree of deviation that is sufficient so as to not measurably detract from the identified property or circumstance. The exact degree of deviation allowable may in some cases depend on the specific context. Thus, for example, a composition which is “substantially different” from another composition will measurably deviate in combustion properties. Most often, one or more elements will be completely absent from the composition of interest, rather than a mere change in compositional percentages. Similarly, a coating which “substantially covers” a particle covers the entire particle surface, although a small percentage of the surface may be exposed, i.e. less than 5%, due to non-wetting or surface defects which may interfere with formation of the coating.
Concentrations, amounts, and other numerical data may be expressed or presented herein in a range format. It is to be understood that such a range format is used merely for convenience and brevity and thus should be interpreted flexibly to include not only the numerical values explicitly recited as the limits of the range, but also to include all the individual numerical values or sub-ranges encompassed within that range as if each numerical value and sub-range is explicitly recited.
As an illustration, a numerical range of “about 10 nm to about 500 nm” should be interpreted to include not only the explicitly recited values of about 10 nm to about 500 nm, but also include individual values and sub-ranges within the indicated range. Thus, included in this numerical range are individual values such as 20, 30, and 40 and sub-ranges such as from 10-30, from 200-400, and from 20-50, etc. This same principle applies to ranges reciting only one numerical value. Furthermore, such an interpretation should apply regardless of the breadth of the range or the characteristics being described.
Invention
In accordance with the present invention, a composite combustion catalyst particle can include a metal core, a metal oxide coating at least partially surrounding the metal core, and a catalyst coating at least partially surrounding the metal oxide coating. The metal core can be formed of a combustible metal having a relatively high heat of combustion. The composite combustion catalyst particles of the present invention are designed to provide catalytic activity to combustion of a fuel, while also acting as a fuel additive for increased energy density.
The composite combustion catalyst particles can be used in a variety of applications. For example, the composite particles can be added to liquid or solid fuels for use in propulsion systems, explosives, munitions, turbines, or the like to form an enhanced fuel. Several exemplary applications will be discussed in more detail below. However, current preferred applications include dispersing the composite particles in a liquid fuel for use in jet fuels such as JP-10 and other similar high performance fuels.
Suitable materials for use as the combustible metal can include any metal which can be oxidized under standard combustion conditions to release an amount of energy comparable to the fuel in which it is used. Non-limiting examples of suitable combustible metals includes aluminum, boron, magnesium, silicon, titanium, lithium, sodium, potassium, and alloys or composites thereof. In one aspect of the present invention, the combustible metal can be aluminum, boron, magnesium, and alloys or composites thereof. Currently, the preferred combustible metal is aluminum. In an alternative aspect, the metal core can further comprise a second combustible metal. As an example of the typical ranges of heats of combustion, aluminum (having a native oxide layer of about 3 nm) has a volumetric heat of combustion of about 81,000 kJ/liter, while JP-10 liquid fuel has a volumetric heat of combustion of about 39,500 kJ/liter. Typically, suitable materials for use as the metal core have a heat of combustion greater than about 30,000 kJ/liter, although this can vary depending on the fuel with which the composite particles are used, and the application.
In order to maintain the volumetric energy density of the enhanced fuel, the composite combustion catalyst particles can have a volumetric heat of combustion ranging from about 80% to 250% of the volumetric heat of combustion of the hydrocarbon fuel. In terms of gravimetric energy density, the gravimetric heat of combustion of the composite combustion catalyst can range from about 50% to 150% relative to the gravimetric heat of combustion of the fuel. Further, although specific compositions can vary, the composite combustion catalyst particles can comprise from about 2 wt % to about 25 wt % of the enhanced fuel. As a general guideline, energy density of a fuel can be measured with reference to either gravimetric or volumetric bases. Gravimetric energy content (i.e., energy/mass) is an important property in applications which are weight-limited. Similarly, volumetric energy content (energy/unit volume) is an important property in applications that are limited by allowable volumes of fuel. For high performance propulsion systems, volume energy content is often a dominant factor, although gravimetric energy content can also affect flight distance and performance.
Metal core particles can be produced using known methods, e.g., physical vapor deposition (PVD), chemical vapor deposition (CVD), low vapor pressure condensation, explosion synthesis, shock wave synthesis, and decomposition of organo-metallic compounds, or obtained from commercial sources. The metal core particles can have an average particle diameter which allows the composite particles produced therewith to combust within a designed time frame. For example, high performance propulsion applications such as pulse detonation engines (PDE), scramjet, and ramjet require time frames for ignition delay and combustion of less than about 1 millisecond. However, as a general guideline, particles ranging from about 4 nm to about 500 μm can be suitable for various applications. In high performance applications, the metal core can typically have an average diameter from about 5 nm to about 500 nm, and preferably from about 20 nm to about 100 nm. Suitable metal core particles can be obtained from a variety of commercial sources such as nanoparticles from Argonide Corp., Nanotechnologies Corp., and other commercial suppliers.
In another aspect of the invention, a metal oxide coating can be present over at least a portion of the metal core. Most frequently, the metal oxide coating forms naturally around substantially the entire metal core upon exposure to air or other oxygen-containing environment. Thus, in some embodiments, the metal oxide coating can be a metal oxide of the combustible metal, e.g., a native oxide coating. However, in some embodiments, the native oxide layer can be avoided by maintaining an oxygen-free environment. In this way, a coating can be formed on the metal core which has a predetermined composition. For example, a metal oxide of a metal which is different than the combustible metal can be formed on the metal core particles. Alternatively, the catalyst coating can be formed directly on the metal core without an intermediate metal oxide coating, as discussed in more detail below. Depending on the specific metal, the metal oxide coating can have a thickness of about 2 nm to about 10 nm. In the case of aluminum, the metal oxide coating can be about 2 to 5 nm, and preferably about 2.9 nm. The metal oxide coating can provide a barrier between the metal core and the catalyst coating. However, a relatively thin native oxide coating can allow for improved overall heats of combustion, i.e. excessively thick metal oxide coatings can reduce the energy density of the composite combustion catalyst particles.
In another aspect of the present invention, the composite catalyst particles can include a catalyst coating. Generally, the catalyst coating can include any metal or metal compound which exhibits a catalytic effect for combustion of a fuel. Two broad classes of catalyst coating materials include catalytically active metals and catalytically active compounds. In one aspect, the catalyst coating can comprise a catalytically active metal, such as palladium, platinum, nickel, noble metals, or other transition metal or binary or ternary combination of such metals known to be effective combustion catalysts. Many such metals can react exothermically with the combustible metal comprising the core of the particle to form intermetallic compounds, such as PdxAly in the case of palladium catalyst reacting with an aluminum metal core. Other suitable catalytically active metals include, but are not limited to, iridium, rhodium, ruthenium, and alloys or composites of these metals. In one preferred aspect, the catalyst coating can comprise palladium.
In yet another aspect of the present invention, the catalyst coating can comprise a metal oxide or other metal compound which exhibits a catalytic effect for combustion of a fuel. More specifically, the catalyst coating can comprise a catalytically active compound such as an inorganic oxide, or sulfide, of an alkaline-earth metal, a transition metal, a boron family element (boron, aluminum, gallium, indium, and thallium), rare-earth metals (atomic numbers 57 to 71, inclusive), and mixtures or alloys thereof. In one detailed aspect, suitable metal compounds can include rare earth metal oxides, transition metal oxides, and mixtures thereof. Several examples of suitable catalyst coating materials can include, but are not limited to, cerium oxide, palladium oxide, tin oxide, manganese oxide, yttrium oxide, iron oxide, cobalt oxide, and mixed oxides containing two or more metals, e.g., mixtures or multi-element oxides thereof such as NxMyOz where N and M are a metal and O represents oxygen. Typically, suitable catalyst materials can have a weaker affinity for oxygen than the combustible metal comprising the metal core of the particle, and thus can react exothermically with the metal core during the combustion process. Depending on the specific composition, the catalyst coating can have a thickness from about 0.5 nm to about 20 nm, although thicknesses outside this range can also be suitable depending on required combustion properties, particle size, fuel, etc.
In addition, the catalyst coating can be chosen to enhance combustion of the fuel. Particularly, catalyst coatings can help to reduce ignition delay times and provide increased combustion rates of the fuel. In some cases, the catalyst coating can also provide additional heat value. The currently preferred catalyst coating material is cerium oxide. Frequently, the native metal oxide layer on the metal core particle can also have a catalytic effect; however, the present invention covers coatings which are distinct from one another. Specifically, the native metal oxide coating and catalyst coatings have substantially different compositions.
The catalyst coating can be formed using known techniques or techniques to be developed in the future. Suitable coating techniques can form the catalyst coating on at least a portion of the metal oxide coating, and/or the metal core. Currently available techniques include chemical vapor deposition, solution phase deposition, physical vapor deposition, and combinations thereof. Typically, it can be desirable to avoid agglomeration of the particles during the coating process. Therefore, the particles can be dispersed in a fluid, e.g., solution phase deposition, or suspended in a fluidized bed reactor or other similar techniques to prevent agglomeration during the coating process. Methods for coating aluminum particles which can be used involve a fluidized bed reactor and are described in U.S. Pat. Nos. 6,613,383 and 6,713,177, which are incorporated herein by reference in their entireties. An additional example of a suitable coating process includes solution phase deposition. This type of deposition typically involves mixing a solution of catalyst metal salt (e.g., PdCl2 or CeCl3) with a slurry of metal core particles. The slurry can then be dried and then heated under a hydrogen atmosphere to reduce the salt to the catalytic metal (e.g., Pd). The metal may be present as a continuous film, or in the form of small nanoparticles dispersed on the metal core particle surface. In the case of a metal oxide catalyst (e.g., CeO2), the reduced Ce film can be carefully oxidized prior to use, or can be allowed to oxidize in the initial stages of combustion.
The catalyst coating thickness and particle coverage can be sufficient to provide a measurable improvement in combustion properties of the fuel. The catalyst coating can therefore vary significantly in thickness and coverage, depending on the specific catalyst used and the coating technique employed. However, as a general guideline, the catalyst coating can have a thickness from about 0.5 nm to about 20 nm, and preferably from about 1 nm to about 5 nm. Alternatively, the catalyst can be in the form of small nanoparticles, e.g., about 0.5 to about 5 nm. Depending on the coating process used, the catalyst coating can cover substantially the entire particle. However, in many cases, the catalyst coating can be present over only portions of the particle, e.g., several catalyst islands. Therefore, in some embodiments, the catalyst coating can cover from about 10% to about 100% of the particle, and often from about 20% to about 50%.
The composite combustion catalyst particles of the present invention can be formed in almost any size which is suitable for a particular application. Generally, the particles can range from about 5 nm to about 1 mm, although sizes outside this range may also be suitable. Of particular interest are applications which involve high performance jet fuels where combustion rates are extremely short. In such applications, it can be desirable to use smaller particles in order to increase catalyst surface area. It should be kept in mind that smaller particles also decrease the volume of the metal core. As such, the heat of combustion of the composite catalyst particles is also reduced, i.e. a fuel mixed with such composite particles would have a decreased energy density. Thus, there is generally an optimal particle size which balances the increase in combustion rates and decrease in ignition delay times with the decrease in energy density of the fuel mixed with the composite particles.
In one aspect of the present invention, the composite combustion catalyst particle can be a nanoparticle. Composite combustion catalyst nanoparticles having a diameter from about 10 nm to about 500 nm can be useful for a variety of high performance applications. Further, composite combustion catalyst nanoparticles having a diameter less than about 100 nm, and in some cases, particles having diameters from about 20 nm to about 100 nm can be particularly useful.
The composite combustion particles of the present invention can be used in a variety of applications. Several non-limiting examples of suitable applications include additives for liquid or solid propulsion fuels, explosives, munitions, or fuels for stationary power generation. In one preferred embodiment, the composite combustion catalyst particles can be used in fuels for high performance propulsion. Thus, in one aspect, an enhanced fuel can include a fuel and a plurality of composite combustion catalyst particles dispersed within the fuel.
In one aspect, the fuel can be a liquid fuel such as, but not limited to, jet propellant fuels, ramjet fuels, kerosene, and mixtures thereof. Suitable liquid fuels can include any fuel for which combustion thereof is catalyzed by the catalyst coatings of the present invention. Non-limiting examples of suitable liquid fuels can include jet propellant fuels (JP series), e.g., JP-4, JP-5, JP-7, JP-8, JP-9, and JP-10 (exotetrahydrodicyclopentadiene); ramjet fuels (RJ series), e.g., RJ1, RJ4 (tetrahydro-dimethycyclopentadiene), RJ5 (perhydrodi-norbomadiene), RJ6 (blend RJ5-JP10), and RJ9; KP-1, Jet-A, Jet-A1, Jet-B fuels, rocket propellants such as RP-1, kerosene, methylacetylene-propadiene, and other hydrocarbon based fuels. Currently, preferred liquid fuels include JP-10, kerosene, and Jet A fuel. In one aspect, the liquid fuel can be JP-10. Although the composition can vary considerably depending on the specific fuel, generally, the composite combustion catalyst particles can comprise from about 4 wt % to about 60 wt % of the enhanced liquid fuel. Typically, this composition also corresponds to a composite combustion catalyst particle content from about 1% to about 30% by volume. As an example, when using aluminum as the metal core, the preferred composition can be from about 5% to about 15% by volume, i.e. about 15 wt % to about 40 wt %.
Additionally, these liquid fuel systems can be part of bipropellants wherein the liquid fuel system is stored separately from an oxidizing agent and the two are mixed during operation. However, in the case of ramjets, scramjets, pulse-detonation engines, and other designs, the oxidizer can be provided by using oxygen from the air. Non-limiting examples of oxidizing agents can include oxygen, liquid oxygen, hydrogen peroxide, hydroxyl ammonium perchlorate (HAP), hydroxyl ammonium nitrate (HAN), ammonium perchlorate, ammonium nitrate, ammonium dinitramide (ADN), nitrogen tetroxide, nitric acid, liquid fluorine, and combinations thereof. Currently, oxygen is the most common oxidizer used. Other oxidizers and fuel compositions can be designed and prepared by those skilled in the art.
Alternatively, the enhanced fuel can include a solid fuel with the composite catalyst particles dispersed therein. A wide variety of solid rocket fuels are known and typically include a polymer or combustible metal with oxidizers and other additives. For example, polymers such as polymethyl methacrylate, high density polyethylene, hydroxyl terminated polybutadiene, and the like. Typical oxidizers that can be used in solid rocket fuels are ammonium perchlorate, potassium perchlorate, ammonium nitrate, liquid oxygen, hydrogen peroxide, nitrogen tetroxide, nitrous oxide, and occasionally fluorine. Composite fuels used for solid rocket fuels contain a high proportion of an oxidizing agent, e.g., 60% to 80%, and powdered aluminum, e.g., 5% to 10%. In accordance with the present invention, the composite catalyst particles can partially or wholly replace the powdered aluminum (or other metal). As a general guideline, the composite combustion catalyst particles can comprise from about 5 wt % to about 70 wt % of the enhanced solid fuel. Alternatively, the composite combustion catalyst particles can comprise from about 2 vol % to about 30 vol % of the enhanced solid fuel. Further, the composite catalyst particles of the present invention can be added to gelled fuels, e.g., RP-1 (aluminum metallized gelled kerosene), etc. Gelled fuels can be particularly desirable in that handling is easier and can be used in a wide variety of propulsion configurations. It will be understood that the above discussion is intended to be illustrative rather than exhaustive of potential fuel compositions to which the inventive catalyst particles can be added.
The presence of the catalyst coating can measurably decrease the ignition delay of enhanced fuels over those fuels which include uncoated metal particles of the same size. The enhanced fuels of the present invention can have an ignition delay of less than about 1 millisecond, and in some cases, from about 1 microsecond to about 200 microseconds.
An additional consideration in designing composite catalyst particles is the heat of combustion of the particles. As mentioned earlier, the metal core can enhance the energy density, while decreasing particle sizes decreases the effective volume of combustible metal. As a general guideline, the composite catalyst particles of the present invention can have a heat of combustion which is at least 80% of the volumetric heat of combustion of the fuel, and preferably at least about 90% of the volumetric heat of combustion of the fuel. Typically, the composite combustion catalyst particles can have a volumetric heat of combustion from about 80% to about 300% of the volumetric heat of combustion of the hydrocarbon fuel, and preferably from about 100% to about 250%. This effect of energy density can be balanced against the particle size. Specifically, as the particle size decreases, energy density decreases; however, catalytic effect per volume of composite particles increases due to a higher surface area. Regardless of the particular fuel, the composite combustion catalyst particles can comprise from about 5 wt % to about 70 wt % of the enhanced fuel.
The enhanced fuels of the present invention can be combusted using known configurations and systems, the performance of which can be improved by incorporation of the composite combustion catalyst particles described herein. Generally, combustion can be initiated in the presence of an oxidizing environment suitable for a particular fuel. Without being bound to a particular theory, it appears that the catalyst coating provides a catalytic effect to enhance combustion of the fuel. As the metal core begins to heat, the metal core begins to expand, which expansion results in stress cracks in the coatings of the composite particles. The exposed metal then contacts the oxidizer and combusts. Additionally, the metal core material and catalyst coating can react in a highly exothermic reaction, e.g., thermite-type reactions (in the case of an oxide catalytic coating), formation of intermetallics (in the case of a metallic catalytic coating), and the like. Specifically, the metal core can be formed of a metal having a higher affinity for oxygen than the catalyst metal. Thus, as the metal oxide coating cracks or is otherwise removed, the metal core and catalyst coating exothermically react to form metal oxides of the combustible metal and intermetallic compositions. Thus, the metal oxide layer also acts as a barrier which prevents the catalyst coating and metal core from reacting upon contact. This is at least one reason why aluminum is a preferred material for the metal core, i.e. aluminum is highly reactive with most metals and also has a higher affinity for oxygen than most metals.
Thus, the fuel and composite combustion catalyst particle are combusted such that the catalyst particles are single use and can be considered a catalyst and a fuel additive. The enhanced fuels of the present invention can be used in a variety of applications such as, but not limited to, propulsion, explosives, munitions, etc. These enhanced fuels can be particularly suited to use in pulse detonation engines, scramjet engines, and ramjet engines.
The following example illustrates a catalytic aspect of the invention. However, it is to be understood that the following is only exemplary or illustrative of certain aspects of the application of the principles of the present invention. Numerous modifications and alternative compositions, methods, and systems may be devised by those skilled in the art without departing from the spirit and scope of the present invention. The appended claims are intended to cover such modifications and arrangements. Thus, while the present invention has been described above with particularity, the following example provides further detail in connection with one aspect of the present invention.
A mass spectrum of JP-10 ˜5% in helium was obtained by electron impact (EI) ionization after passage through a room temperature flow tube reactor and was used as a reference point for JP-10 without decomposition. Similar EI mass spectra were obtained on JP-10 at 830 K, 920 K, and 1150 K. Additionally, an enhanced fuel mixture of JP-10 and cerium oxide particles as a catalyst, was subjected to ionization after passage through a flow tube reactor at the identified temperatures.
For these tests, a flow tube reactor was used having a 3 mm inside diameter alumina tube, the final 20 cm length can be heated by an external heater jacket. The average residence time of the flow in the hot zone of the reactor is on the order of 1 millisecond, and the pressure is low enough (˜15 mbar at the upstream end of the tube) that diffusion mixes the gas during the flow, and ensures that the average JP-10 reactant molecule will collide at least several times with the tube walls. Gas exiting the tube is sampled through a skimmer orifice and then detected and analyzed using electron impact ionization mass spectrometry.
For the purpose of illustration, pure cerium oxide nanoparticles were used. By eliminating the combustible metal core that would be present in a combustion, propulsion, or explosives application, purely catalytic effects of the particle surfaces can be isolated and measured. When cerium oxide nanoparticles are added, JP-10 molecules may collide with cerium oxide particles in the heated gas stream. However, cerium oxide particles also tend to coat the tube walls, and collisions between the fuel and catalyst particles can occur at the walls as well. The gas and wall temperatures are similar, thus either type of particle collision can serve to illustrate catalytic effects.
At a temperature of 830 K, the results with no cerium oxide particles show relatively insubstantial changes from the reference spectrum obtained at 300 K. However, addition of the cerium oxide particles significantly decreased the high mass peaks, indicting that JP-10 reacted at 830 K. Furthermore, new peaks appear at low masses corresponding to 18 (water), 28 (CO), 30 (H2CO or C2H6), 44 (CO2), for example. The spectrum clearly shows that oxygen is being incorporated into the products, and the only source of oxygen in this system is cerium oxide. Under similar conditions, no oxygen-containing products were observed even for JP-10/O2/helium flows containing up to equimolar amounts of JP-10 and oxygen.
At a temperature of 920 K, some JP-10 decomposition occurs in the absence of cerium oxide, i.e. about half of the JP-10. Under these conditions, the lower mass hydrocarbon peaks in the spectrum come from electron impact ionization of the products of thermal decomposition of JP-10, and electron-ionization-induced fragmentation of the residual JP-10 surviving passage through the hot flow tube. When cerium oxide was added, a significant reduction in the high mass peaks indicated reaction of JP-10, and increases in low mass peaks, from ionization of reaction products.
These results indicate that substantial catalytic effects can result from a few collisions of JP-10 with cerium oxide nanoparticles, including lowering of the minimum temperature required for a given extent of decomposition, increased extent of decomposition at a given temperature, and appearance of unique products derived from reaction with cerium oxide surfaces.
Of course, it is to be understood that the above-described arrangements are only illustrative of the application of the principles of the present invention. Numerous modifications and alternative arrangements may be devised by those skilled in the art without departing from the spirit and scope of the present invention and the appended claims are intended to cover such modifications and arrangements. Thus, while the present invention has been described above with particularity and detail in connection with what is presently deemed to be the most practical and preferred embodiments of the invention, it will be apparent to those of ordinary skill in the art that numerous modifications, including, but not limited to, variations in size, materials, shape, form, function and manner of operation, assembly and use may be made without departing from the principles and concepts set forth herein.
This application claims priority to U.S. Provisional Application No. 60/476,343, filed Jun. 6, 2003, which is incorporated by reference herein in its entirety.
This invention was made with support from the United States Government, and the United States Government may have certain rights in this invention pursuant to ONR Grant No. N00014-01-1-0541.
Number | Name | Date | Kind |
---|---|---|---|
3479276 | Becker et al. | Nov 1969 | A |
3503783 | Evans | Mar 1970 | A |
3511683 | Heilwell et al. | May 1970 | A |
3615166 | Hindin et al. | Oct 1971 | A |
3745077 | Jones | Jul 1973 | A |
3861138 | Bridgeforth, Jr. et al. | Jan 1975 | A |
4017527 | Merkl | Apr 1977 | A |
4440874 | Thompson | Apr 1984 | A |
4797329 | Kilbane et al. | Jan 1989 | A |
5170624 | Cornelison et al. | Dec 1992 | A |
5174968 | Whittenberger | Dec 1992 | A |
5179059 | Domesle et al. | Jan 1993 | A |
5258349 | Dalla Betta et al. | Nov 1993 | A |
5441706 | Whittenberger | Aug 1995 | A |
5451277 | Katzakian et al. | Sep 1995 | A |
5693207 | Fromson et al. | Dec 1997 | A |
5771679 | Taylor, Jr. et al. | Jun 1998 | A |
5846495 | Whittenberger et al. | Dec 1998 | A |
5935889 | Murrell et al. | Aug 1999 | A |
6071850 | Friedman et al. | Jun 2000 | A |
6107239 | Qin et al. | Aug 2000 | A |
6140266 | Corrigan et al. | Oct 2000 | A |
6177381 | Jensen et al. | Jan 2001 | B1 |
6179899 | Higa et al. | Jan 2001 | B1 |
6214765 | Fromson et al. | Apr 2001 | B1 |
6299654 | Thompson | Oct 2001 | B1 |
6454886 | Martin et al. | Sep 2002 | B1 |
6503350 | Martin et al. | Jan 2003 | B2 |
6528683 | Heidemann et al. | Mar 2003 | B1 |
6576199 | Liu et al. | Jun 2003 | B1 |
6596249 | Lin et al. | Jul 2003 | B2 |
6613168 | Reed, Jr. et al. | Sep 2003 | B2 |
6613383 | George et al. | Sep 2003 | B1 |
6627013 | Carter, Jr. et al. | Sep 2003 | B2 |
6652682 | Fawls et al. | Nov 2003 | B1 |
6676727 | Pozarnsky | Jan 2004 | B2 |
6679960 | Jones | Jan 2004 | B2 |
6710003 | Jan et al. | Mar 2004 | B2 |
6713177 | George et al. | Mar 2004 | B2 |
6737463 | Yadav et al. | May 2004 | B2 |
6858769 | Woodle et al. | Feb 2005 | B2 |
20020049132 | Jan et al. | Apr 2002 | A1 |
20040175313 | Foor et al. | Sep 2004 | A1 |
Number | Date | Country | |
---|---|---|---|
20040265214 A1 | Dec 2004 | US |
Number | Date | Country | |
---|---|---|---|
60476343 | Jun 2003 | US |