Patent Application
20140367249
Performance of electrochemical devices, such as solid oxide fuel cells and ceramic oxygen separation membranes, is typically limited by the electrical resistance of the solid electrolyte materials. Solid electrolyte materials with high ionic conductivity will not only increase the electrical performance of the electrochemical devices, but also allow the device to run at a lower temperature, which may enable use of cheaper metallic components. Yttria (Y2O3) stabilized zirconia (YSZ) has long been investigated for these applications. Over the last several years, scandium oxide (Sc2O3) stabilized zirconia (ScSZ) has emerged as a viable electrolyte material to replace YSZ for these devices. The stabilization of zirconia can be full or partial, depending on the type and amount of the dopants (such as yttria). For applications requiring high mechanical strength and toughness, such as Applicant's Ceramic Oxygen Generation Systems (COGS), a fully stabilized zirconia compound may not be the best candidate due to its relatively low strength and its lack of a toughening mechanism. Partially stabilized zirconia with lower dopant contents have excellent mechanical strength and toughness, but also have lower ionic conductivity.
Several zirconia based electrolyte materials were evaluated, both fully stabilized (such as 8YSZ and 10Sc1CeSZ) and partially stabilized (such as 3YSZ, 6Sc1 CeSZ and 6ScSZ). Ceramic Oxygen Generation System units with 6Sc1 CeSZ electrolyte have been manufactured and have proven their suitability for field applications under severe environmental conditions. However, the conductivity of 6Sc1CeSZ is far below that of 10Sc1CeSZ, resulting in lower performance at the same operation conditions.
There therefore remains a need for a solid electrolyte with optimized conductivity and mechanical strength suitable for use in solid state electrochemical devices such as Ceramic Oxygen Generation Systems.
The invention teaches composite electrolyte materials comprising at least one component from fully stabilized zirconia (such as 10Sc1CeSZ) and at least one component from partially stabilized zirconia (such as 6Sc1CeSZ) as the electrolyte material for solid state electrochemical devices.
This invention teaches composite electrolyte materials composed at least one component from fully stabilized zirconia (such as 10Sc1CeSZ, for example) and at least one component from partially stabilized zirconia (such as 6Sc1CeSZ, for example) as the electrolyte material for solid state electrochemical devices. The composite can be obtained through mixing electrolyte powders of fully stabilized zirconia and electrolyte powders from partially stabilized zirconia and following typical ceramic manufacturing processes. For example, 10Sc1CeSZ powder and 6Sc1CeSZ powder in a weight ratio between 1:10 to 10:1 can be mixed together. The mixture can then be processed to make components for solid state electrochemical devices. The preferred weight ratio of 10Sc1CeSZ to 6Sc1CeSZ in the mixture is 3:7 to 7:3.
Disks and bar samples with different 10Sc1CeSZ: 6Sc1CeSZ ratios were made to evaluate the ionic conductivity and the strength of the composite. Conductivity was measured using a DC method at a current density similar to a ceramic membrane under its typical intended operation conditions. Strength of bars was obtained via 4-point bending tests.
The 60% 10Sc1CeSZ-40% 6Sc1CeSZ composition was chosen for further evaluation as seen in Chart 1 below.
For electrolyte performance degradation, the voltage is evaluated as a function of time to generate a constant current (of oxygen ions). For Chart 1 above, the degradation rate (increase in voltage) was calculated for each 100 time period and reported as % degradation per 1000 hours. When this data was statistically analyzed using a t-test, there was a greater than 99% probability that the 10Sc1CeSZ degradation rate was lower than either of the other two, but there was only a 52% probability that the 6Sc1 CeSZ degradation rate could be distinguished from the composite electrolyte degradation rate.
In a preferred embodiment, the invention comprises an electrolyte formed by combining Zr(0.93)Sc(0.06)Ce(0.1)O(2) and Zr(0.89)Sc(0.10)Ce(0.1)O(2) powders and sintering the resulting powder compact to a sufficient density to elimination open porosity with a ratio of the first powder to the second powder ranging from 10:1 to 1:10 by weight. The mixing of the powders is performed thoroughly to the particle size using, for example, a wet ball milling process.
Sintering to acceptable densification was calculated using the “theoretical density” of the composite material as follows.
Made from Treibacher EA80/10.2 10Sc1CeSZ Cal 975C 12 hrs after processing, then it was mixed with EA81/10.2 6Sc1CeSZ AR and processed together
Pellets pressed in 13 mm die to indicated green density (assumed 5.93 g/cc for green density calculations)
Sintered in small CM 1475C 4 hrs
58% green density (1.7093 g of powder)
This average of the measurements gives a density of about 5.77 g/cc, which is shown in the Example 1 as only being 97.3% of theoretical; however, the theoretical density used (5.93 g/cc) is actually for 6Sc1CeSZ and not the composite. Using the rule of mixtures to calculate a theoretical density for the composite results in about 5.83 g/cc. Comparing this theoretical density to the measured values indicates approximately 99% of theoretical density was achieved for this sample which is considered to be very good and acceptable densification.
This application claims the benefit of Provisional Application U.S. Ser. No. 61/593,596 filed on Feb. 1, 2012.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/US13/24428 | 2/1/2013 | WO | 00 | 7/31/2014 |
| Number | Date | Country | |
|---|---|---|---|
| 61593596 | Feb 2012 | US |