Patent Application
20130115414
The invention relates to a composite film, a method for producing a composite film as well as a method for producing a film composite consisting of at least one composite film. The invention further relates to an apparatus for producing a composite film.
A composite film of this kind is particularly known from the food or nutriment industry and hereby serves to produce packaging which in each case contains a certain quantity of food or nutriments. Such composite films are particularly known in the production of so-called tubular bag packages. Such tubular bag packages are produced by two opposing peripheral regions of a composite film, or even two separate composite films, being laid against each another, wherein the peripheral regions on the sealing layers of the composite film, which are laid against each other, weld with one another while being subjected to heat and pressure. The composite films thereby consist of a plurality of layers which are connected to one another and have different melting points. During the sealing process, the film layers having the lowest melting point melt initially. It is therefore customary when welding composite films on the inner side of the package for those layers having the lowest melting point to be disposed as the sealing layers.
Due to economic considerations, a sealing layer, which simultaneously forms the inner layer of the packaging is in this case worth considering, in particular polyethylene (PE). Other plastics having a higher melting point with respect to PE as, for example, polyamide (PA) or polyethylene terephthalate (PET), are not used as the sealing layer because these polymers have too high a melting point so that they can not be economically welded in the packaging field or the strength of the weld seam is not sufficient. In addition, the use of such plastics as PA or PET on the inner side of the package is not possible when plastics having a lower melting point in comparison thereto are simultaneously used. This is the case because the layer having the lower melting point would initially melt without melting of the layer on the inside of the package having the higher melting point in relation to the aforementioned layer occurring.
It should be additionally mentioned that the use of polyethylene (PE) in particular as the innermost packaging material layer, which in turn has contact with a bulk material, is not suitable as packaging for sensitive food as, for example, mineral water, due to the high migration capability thereof.
On the basis of the prior art, the task underlying the invention is to further develop a composite film, a method for producing a composite film as well as method for producing a film composite consisting of at least one composite film according to the preambles of the respective independent claims such that materials can be used as inner layers of the packaging, which do not necessarily have to have the lowest melting point with respect to the different layers. The use of alternative polymers instead of polyethylene should thereby be particularly made possible. This aim is met by a composite film according to the invention.
The invention is based on the idea of using a material, in particular polyethylene therephthalate, having with respect to the firstly melting (sealing) layer a higher melting point relative thereto as the inner layer which has contact to a bulk material, wherein said inner layer has at least one through-opening, which is covered by a sealing layer having a lower melting point relative thereto. The leak-tight connection in the region of the sealing or the weld seam is also particularly thereby achieved in that when melting the sealing layer, the material of the sealing layer penetrates through the through-opening of the PET inner layer and comes into operative connection with the opposing sealing layer. At the same time and depending on the welding parameters and the sealing tool, the through- openings in the innermost layer break open under the influence of the pressure of the sealing jaws; and therefore a preferably, in particular lineary, connection zone covering the whole surface is achieved in the region of the through-openings.
Advantageous modifications to the composite film according to the invention, to the method for producing the composite film as well as to the method for producing a film composite consisting of at least one composite film are specified in the respective dependent claims. All combinations from at least two of the features disclosed in the claims, the description and/or the figures fall within the scope of the invention.
The use of PET as the inner layer, in particular for packages, has the advantage that in the case of sensitive foods as, for example, water, a composite film of this kind is suitable for packaging sensitive food of this kind due to the very low migration capability of PET.
It is particularly preferred if at least one third layer acting as a barrier layer is arranged between the sealing layer and the first layer. Such a barrier layer can, for example, prevent the entry of UV radiation into a packaging and thus increase the shelf life of the nutriment or food item.
It is especially preferred if a plurality of through-openings are configured in the second layer, said through-openings being arranged evenly spaced in relation to each other. By means of this configuration, a composite film, in particular as a continuous packaging material web, according to the invention can be stockpiled and particularly easily processed.
Particularly in the forming of leak-proof tubular bag packages, in which the discharge of particularly liquid or pasty bulk material has to be reliably prevented, provision is furthermore made in a particularly preferred embodiment of the invention for at least two rows of through-openings to be provided, for a strip-like zone without through-openings to be configured between the rows and for the two rows of through-openings to be aligned relative to each other in such a way that when the composite film is folded over in the region of the strip-like zone and when the two sections are laid against each other to form a folded edge, the through-openings of the two second layers laid against each other are arranged in an overlapping manner relative to one another.
Satisfactory results with regard to the properties of the packaging of tubular bags are achieved if the sealing layer consists of polyethylene (PE) and has a layer thickness of 30 μm to 100 μm, preferably between 50 μm and 90 μm, and if the second layer has a thickness of 8 μm to 20 μm, preferably between 12 μm and 18 μm.
Further advantages, features and details of the invention ensue from the following description of preferred exemplary embodiments as well as from the drawings.
Said drawings show in:
In
The use of the composite film for packaging of sensory sensitive food as, for example, water is particularly preferred.
The packaging 1 is designed cushion-like in the exemplary embodiment and particularly has an upper strip-like weld seam 2 and a lower likewise strip-like weld seam 3. Such a packaging 1 is typically produced by means of so-called tubular bag machines in which at least one composite film stored as a continuous packaging material web is cyclically or continuously removed, folded, filled and welded. In so doing, tubular bag machines of this kind work either with a single packaging material web, wherein the two end regions, which are spaced in the longitudinal direction with respect to the preferential direction, are laid against each other, or else with two separate packaging material webs which are brought into superposition. In both cases, further so-called longitudinal weld seams not depicted in the illustration of
It deserves to be additionally mentioned that instead of the cushion-like packaging 1, packaging 1 shaped differently also, of course, falls within the scope of the invention. Such packaging 1, for example in the shape of standard bag packages, pyramid-like packages etc. can be provided or used. It is only essential that all such packaging 1 has weld seams 2, 3.
The production of weld seams 2 and 3 takes place by so-called sealing tools known from prior art. Said sealing tools comprise sealing jaws, between which the two opposing sections of the at least one packaging material web are welded together while being subjected to heat and pressure.
The packaging 1 is produced using an inventive composite film 10 depicted in
In practice, satisfactory results for packaging 1 were achieved if the layer thickness of the sealing layer 12 is between 30 μm and 100 μm, preferably between 50 μm and 90 μm, and wherein the inner layer 13 has a layer thickness from 8 μm to 20 μm , preferably between 12 μm and 18 μm.
Provision can also particularly be made for at least one additional barrier layer 15 to be arranged between the outer layer 11 and the sealing layer 13, as can be seen with the aid of
It is essential to the invention that the inner layer 13 is configured having at least one perforation or at least one through-opening 17. In
When forming the packaging 1 using the inventive composite film 10, it is essential that in accordance with
In the exemplary embodiment shown in
When forming the weld seams 2, 3 in the region of the through-openings 17, heat and pressure are introduced in the region of the weld seam 2 or 3 by means of the previously mentioned sealing or respectively welding tool. In so doing, the sealing layer 12 is melted according to the depiction of
The through-openings 17 are furthermore broken open or widened as a function of the welding parameters and the design of the sealing tool such that a strip-like connection zone is preferably formed, in which the two sealing layers 12 form a tight connection over the whole surface; and therefore, as the case may be, the composite film 10 does not have to be folded back to form an edge 18.
A device 20 for producing through-openings 17 in the inner layer 13 is depicted in a greatly simplified manner, said inner layer being part of an apparatus (not shown). In this case, the inner layer 13 is moved along in accordance with the arrow 21 cyclically or continuously beneath the device 20, wherein said device 20 forms the through-openings in the inner layer 13. A laser beam device, a punching device or a device 20 comprising at least one knife are particularly worthy of consideration for being said device 20. The inner layer 13 configured in this manner is subsequently connected in a known manner per se by means of the apparatus to the outer layer 11, the sealing layer 12 as well as, if applicable, to the barrier layer 15, wherein the sealing layer 12 covers at least the region of the through-openings. Other devices 20 are also conceivable. The through-openings 17 can, for example, be subsequently formed by means of a laser device in an already finished composite film 10; and if need be additional weak areas are thereby formed on the composite film, for example for the simplified mounting of a spout or for the simplified use of the same.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2010 031 362.9 | Jul 2010 | DE | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP11/59032 | 6/1/2010 | WO | 00 | 1/15/2013 |