Composite H2O absorber for sealed medical devices

Information

  • Patent Grant
  • 8673060
  • Patent Number
    8,673,060
  • Date Filed
    Thursday, July 9, 2009
    15 years ago
  • Date Issued
    Tuesday, March 18, 2014
    10 years ago
Abstract
There are described composite absorbers for sealed medical devices, which comprise an active species dispersed in a polymeric matrix having an H2O transmission comprised between 0.05 g mm −2 d−1 and 5.4 g mm m−2 d−1 at 25° C. and 100% RH, and a method for H2O removal from the sealed medical devices by means of said composite absorbers.
Description
CROSS REFERENCE TO RELATED APPLICATIONS

The present application is the U.S. national stage of International Application PCT/EP2009/058782 filed on Jul. 9, 2009 which, in turn, claims priority to Italian Patent Application MI2008A001374 filed on Jul. 25, 2008.


The present invention relates to a composite H2O absorber for sealed medical devices, with particular but not exclusive reference to medical devices that can be implanted in the human body.


Recent developments in the field of sealed medical devices, like e.g. pacemakers, neurostimulators, acoustic aids, defibrillators, electromechanical systems for the controlled release of medicines, implantable cardioverter defibrillator, cardiac resynchronization therapy led and lead to a continuous improvement of their characteristics, both in terms of performance and reliability.


In the following reference will be made to implantable devices, since they are those most benefiting from the invention.


These devices are usually sealed under an inert gas atmosphere, typically nitrogen or argon and helium although some particular manufacturing processes provide for their sealing in dry air.


Regardless of the fact of using or not an anhydrous gas for the sealing of the medical device, it can not be excluded that noxious species, initially in a gaseous phase, can accumulate inside the device over time and interfere with the correct operation of the device, or even damage it in an irreversible manner. Moisture is one of the mostly noxious species due both to its corrosiveness with respect to the components used inside the device and to its possible damage to the operation of electronic components.


The moisture present inside a sealed medical device may originate by three different manners. A first cause can derive from the manufacturing process itself, the outgassing of components of the medical device is a second possible cause, while a third one is related to the permeation through the walls of the sealed device. This latter permeation phenomenon from the outside to the inside of the device may sometimes be present also once the device is installed, whereas for other devices the greatest amount of water comes in during the time between the manufacturing of the device and its actual installation. In this regard, the junctions of the sealed medical device typically exhibit the greatest permeation from the external environment.


Major details concerning the effects of the ingress of H2O inside the medical device, as well as the maximum allowable permeation from the outside for several medical devices can be found on chapter 3 of the book “Neutral Prostheses for Restoration of Sensory and Motor Function”, by Chapin and Moxon, published in 2001 by CRC Press. This reference also refers to the possible and typical use of getter materials to remove H2O from the sealed devices.


Besides this functional need for removing H2O from the inside of the sealed medical device, typically obtained by using a getter material, there is another need of industrial nature, related to the manufacturing processes of the devices, according to which it should ideally be possible to handle the getter material in air without excessively compromising its capacity. This allows to avoid to use means and methods that make the manufacturing process more complex and expensive, such as for example the use of glove boxes through which an anhydrous gas flows, or allowing the use of manufacturing means being less performing from this point of view, or the reduction of the number of operations to be carried out in a glove box.


Therefore, there are two opposite requirements for the H2O absorber: on the one hand the absorber must be able to absorb water coming into or already present in the device and thus have such an absorbing speed to avoid the increase of water concentration inside the device, while on the other hand the absorber must not have excessive degradation due to the exposure to air or due to other manipulations made under conditions in which the absorber is exposed to a non-anhydrous atmosphere.


The generic use of composite absorbers made up of an active species useful for the removal of H2O and dispersed inside a polymeric matrix is described in patent U.S. Pat. No. 5,078,909, but in this patent no specific reference is made to the properties of the polymer in terms of water permeation or transmission.


Composite absorbers are also described in patent publications WO 2007/013118 and WO 2007/013119, both in the applicant's name, where WO 2007/013118 teaches the use of an absorber material arranged in the pores of a porous material that is in turn dispersed in a polymeric matrix, but does not teach any specific permeation value of the polymer, whereas WO 2007/013119 discloses active barriers, i.e. composite systems made of active materials dispersed in a polymer having a low permeability, i.e. a permeability lower than 0.00215 10−3 g mm m−2 d−1.


The problem of using polymers having a given permeability in order to protect medicines avoiding exposure to H2O is instead described in the international publication WO 99/61856, wherein this technical effect is obtained through the formation of micro-channels deriving from the removal of a suitable additive. This document describes the possibility that these channels keep in communication the noxious species with an absorber. Therefore, the function of the polymer as taught in this document is merely that of an agent suitable to contain and enclose the active species and to guarantee the communication between the inner atmosphere of the medicine container and the active species, without any shielding and protecting action of the active species by means of the polymer itself.







Object of the present invention is to provide a specific composite absorber for sealed medical devices, which is able to overcome the problems still present in the prior art, i.e. to provide a composite absorber that ensures a sufficient H2O absorbing speed from the housing of the medical device and that can be handled in air without any special caution for the time requested by the production process, in order to simplify the manufacturing of the device.


In a first aspect thereof, the invention relates to a composite H2O absorber for sealed medical devices comprising an active species dispersed in a polymeric matrix, characterized in that said polymeric matrix has a MVTR comprised between 0.05 g mm m−2 d−1 and 5.4 g mm m−2 d−1 at 25° C. and 100% RH.


MVTR indicates the coefficient of transmission of the polymer (Moisture Vapour Transmission Rate), which is measured according to ASTM E96 procedure at 25° C. and 100% relative humidity. In the following, the indication RH (Relative Humidity) will be used for this unit of measurement.


The wording “active species” indicates any material suitable to remove (i.e. to getter) H2O through physisorbing, chemisorbing mechanisms or both of them.


In particular, the inventors have found that by means of a composite absorber made according to the present invention it is possible to ensure an H2O absorption in the medical device comprised between 2.5% and 15.2%, expressed as a weight percentage with respect to the total weight of the composite absorber and not of the sole active species dispersed therein. Moreover, the composite absorber of the present invention may be handled in air under typical use conditions (22° C., 22% RH) without excessively jeopardizing its ability of removing H2O. In particular, for example, samples having a thickness of 0.2 mm are characterized by a 3% loss with respect to their initial capacity when exposed in air for one hour, whereas the exposure time increases up to ten hours when the thickness is 1 mm in order to have the same loss of capacity.


The use of polymeric barriers comprising an active species for use in solar panels is described in patent applications WO 2009/043776 and WO 2009/043817, both the applicant's name. These applications are characterised by using a polymeric material having a H2O transmission lower than 10 g mm m−2 d−1 measured at 25° C. and 100% RH. Considering the specific use as barriers, and thereby the technical effect desired, the transmission must be as low as possible. Therefore, no teaching can be found in these applications concerning composite absorbers for sealed medical devices, with particular reference to the minimum H2O transmission value allowing their use for removing H2O from sealed medical devices, thus avoiding its noxious collection inside the device.


Among the active species for the sorption of H2O zeolites, silica gel, alumina, alkaline metal oxides and alkaline-earth metal oxides can be used either alone or in combination.


In the field of sealed medical devices there are applications that operate at temperatures higher than the ambient temperature or that anyway cause a local overheating in proximity to the composite absorber. In particular, the use of calcium oxide is preferred at temperatures of 65° C. of higher.


Although water is the mostly undesirable species for the sealed medical device, the presence of other gaseous species, the most common of which are from this point of view hydrogen, carbon dioxide, carbon monoxide and hydrocarbons, is also noxious for some of these devices. In this case it is particularly useful that the composite absorber contains one or more getter materials suitable to absorb also these noxious species and not only H2O.


Concerning the polymeric matrix in which the active species is dispersed, useful materials for carrying out the invention are for example: Ethylene-Vinyl Acetate (EVA), Low Density PolyEthylenes (LDPE), Medium Density PolyEthylenes (MDPE) and High Density PolyEthylenes (HDPE), PolyEther-Block-Amide (PEBA), ionomeric resin such as Surlyn™ sold by DuPont, Ethylene-acrylic acid copolymers such as for example Lucalen® sold by Basell, PolyVinylidene Fluoride (PVDF), PolyVinylButyral (PVB) and PolyVinylidene Chloride (PVDC) such as Saran™ sold by DOW Chemicals, butyl rubbers, Ethylene-Propylene Rubber (EPR), Ethylene Propylene Diene Monomer Rubber (EPDM) rubbers and Sylossanic resins such as Sylgard™ sold by Dow Corning.


The previously mentioned materials may have different MVTRs according to the specific composition, whereby the choice of the polymeric matrix for the manufacturing of the composite absorber must be made on the basis of the correct transmission of H2O, i.e. a value comprised between 0.05 g mm m−2 d−1 and 5.4 g mm m−2 d−1 1. For example an EVA containing a 33% of vinyl-acetate has a MVTR of 5.4 g mm m−2 d−1 and thus it is suitable for carrying out the invention, whereas an EVA containing a 70% of vinyl-acetate has a transmission of 17.5 g mm m−2 d−1 and thus it is not suitable.


The transmission data are typically provided by the manufacturer or can be easily found in the literature on texts such as “Permeability and Other Film Properties of Plastic and Elastomer” published by Plastics Design Library, and therefore the choice of a polymer having a given H2O transmission value can be easily made by those skilled in the art.


The composite absorber object of the present invention contains an amount of material for H2O removal comprised between 10% and 50% by weight. This percentage is preferably comprised between 30% and 45%. It is important that the weight concentration of the absorber material is not lower than 10% in order to ensure a sufficient capacity.


Another advantage that can be obtained by means of the present invention is that the composite absorber may be easily manufactured with and adapted to different geometries. In particular, according to the present invention it is possible to obtain composite absorbers having a thickness comprised between 0.15 mm and 2 mm, the user being free to define the width and length by means of a simple cutting operation when inserting the absorber inside the medical device.


Typically, this level of adaptability and flexibility of the product in the medical device is obtained at present by using dispensable drying pastes, which have the disadvantage of requiring cautions during their handling and further also need a consolidation phase at temperature higher than ambient temperature inside the product, i.e. the medical device.


In a second aspect thereof, the invention relates to a method for H2O removal from sealed medical devices by using a composite absorber comprising an active species dispersed in a polymeric matrix, characterized in that the polymeric matrix has an MVTR comprised between 0.05 g mm m−2 d−1 and 5.4 g mm m−2 d−1 at 25° C. and 100% RH.

Claims
  • 1. A method for H2O removal from a sealed medical device, comprising: introducing in said device a composite absorber comprising one active species in the form of one or more among zeolites, silica gel, alumina, alkali metal oxides, alkaline-earth metal oxides dispersed in a polymeric matrix, wherein said polymeric matrix shows a Moisture Vapour Transmission Rate comprised between 0.05 g mm m−2 day−1 and 5.4 g mm m−2 day−1 at 25° C. and 100% relative humidity.
  • 2. The method of claim 1, wherein said alkaline-earth metal oxides compromise calcium oxide, barium oxide or combinations thereof.
  • 3. The method of claim 2, wherein said sealed medical device operates at temperatures of 65°C. or higher and the active species comprises calcium oxide.
  • 4. The method of claim 1, wherein introduction of the composite absorber inside the sealed medical device comprises cutting an absorber sheet with a length and width so that is able to be placed inside said medical device, and a thickness comprised between 0.15 and 2 mm.
  • 5. The method of claim 1, wherein said sealed medical device is selected from pacemakers, neurostimulators, acoustic aids, defibrillators, and electromechanical systems for controlled release of drugs.
Priority Claims (1)
Number Date Country Kind
MI2008A1374 Jul 2008 IT national
PCT Information
Filing Document Filing Date Country Kind 371c Date
PCT/EP2009/058782 7/9/2009 WO 00 12/22/2010
Publishing Document Publishing Date Country Kind
WO2010/009986 1/28/2010 WO A
US Referenced Citations (21)
Number Name Date Kind
4014346 Brownlee et al. Mar 1977 A
4036360 Deffeyes Jul 1977 A
4081397 Booe Mar 1978 A
4127134 Ushakoff Nov 1978 A
5078909 Shigeta et al. Jan 1992 A
5591379 Shores Jan 1997 A
6080350 Hekal Jun 2000 A
6226890 Boroson et al. May 2001 B1
6493960 Taylor et al. Dec 2002 B2
6596192 Himeshima et al. Jul 2003 B2
6681135 Davis et al. Jan 2004 B1
6740145 Boroson et al. May 2004 B2
6743524 Schaepkens Jun 2004 B2
8034739 Solovyov et al. Oct 2011 B2
20030037677 Boroson et al. Feb 2003 A1
20030079772 Gittings et al. May 2003 A1
20030109628 Bonfanti et al. Jun 2003 A1
20050000901 Campbell et al. Jan 2005 A1
20070135552 Wrosch et al. Jun 2007 A1
20090018633 Lindquist et al. Jan 2009 A1
20100314579 Rondena et al. Dec 2010 A1
Foreign Referenced Citations (15)
Number Date Country
101222977 Jul 2008 CN
S4-10-1978 Apr 1978 JP
2000-504773 Feb 1997 JP
2003-154227 May 2003 JP
9731069 Feb 1996 WO
WO 9731069 Aug 1997 WO
9961856 Dec 1999 WO
9962697 Dec 1999 WO
0009848 Feb 2000 WO
0166625 Sep 2001 WO
2007013118 Feb 2007 WO
2007013119 Feb 2007 WO
2007013119 Feb 2007 WO
2009043776 Apr 2009 WO
2009043817 Apr 2009 WO
Non-Patent Literature Citations (10)
Entry
http://www.perfomaxtech.com/know-how%20of%20L80-5000%20wvtr.PDF p. 3.
PCT International Search Report for PCT/EP2009/058782 filed Jul. 9, 2009 in the name of Antonio Bonucci et al.
PCT International Report on Preliminary Patentability for PCT/EP2009/058782 filed Jul. 9, 2009 in the name of Antonio Bonucci et al.
PCT Written Opinion for PCT/EP2009/058782 filed Jul. 9, 2009 in the name of Antonio Bonucci et al.
Gerald E. Loeb et al., “BION™ Implants for Therapeutic and Functional Electrical Stimulation”, CRC Press, 3; pp. 75-99 (2001).
William Andrew Publishing, “Permeability and Other Film Properties of Plastics and Elastomers” Plastics Design Library, (1995).
First Office Action issued for China's Patent Application No. 200980125858.8 filed on in the name of Saes Getters S.P.A.; mailing date: Sep. 18, 2012 (original and English translation).
Office Action issued for China's Patent Application No. 200980125858.8 filed in the name of Saes Getters S.P.A. mail date: Sep. 4, 2013 (English translation and original).
Japanese Office Action mailed on Oct. 29, 2013 for Japanese Application 2011-519109 filed on Jul. 9, 2009 in the name SAES GETTERS S.P.A.
Yasuda T., Test methods and evaluation results of dynamic characteristics of plastic materials, Plastics 2000, 51: 119-127 (Tables 3 & 4 translated into English).
Related Publications (1)
Number Date Country
20110113959 A1 May 2011 US