FIELD OF THE INVENTION
The present invention is in the field of optics. In particular, it is in the area of optical diffusers.
BACKGROUND OF THE INVENTION
The prior art in holographic optical diffusers, which can be found in U.S. Pat. Nos. 6,675,863, 7,700,199, and 8,097,311, all of which are incorporated in their entirety by reference, comprises three-dimensional (3-D) surface relief patterns produced by optically recording laser speckle in thick (10 microns to 60 microns) photoresist material.
Referring to FIG. 1, an optical bench setup 100 capable of recording prior art holographic optical diffuser(s) in planar format, may be used as the starting point for improvements that comprise the present invention.
Referring to FIG. 2, an optical bench setup 200 capable of recording prior art holographic optical diffuser(s) in cylindrical (seamed and seamless) format, may be used as the starting point for improvements that comprise the present invention.
SUMMARY OF THE INVENTION
This invention describes a method to produce high frequency structures on top of classical holographic optical diffusers using modified holographic optical recording setups.
This innovation in optical diffuser mastering includes legacy microstructure surface relief patterns, along with smaller ones, overlaid on the larger ones. The characteristic features produced by the present invention will be found useful when viewers do not want to see visible structures in/on optical diffusers, such as those used in movie projection screens (utilizing either coherent (i.e., laser-generated) and non-coherent (e.g., lamp-generated) light), head-up displays (HUDs), liquid crystal displays (LCDs), non-motion picture laser projection viewing, etc., as the present invention produces much sharper images than those afforded by traditional holographic optical diffusers. Additionally, it can reduce glare, reduce Moiré artifacts, and add a specific, controllable amount of haze. As a result, it positively impacts the experience of end users.
Therefore, the present invention reduces the visibility of optical artifacts visible with the unaided human eye at working distances relevant to particular application of said optical diffuser. Alternately, a high-fidelity replica of said optical diffuser master may be used in any particular target application with substantially the same benefits as the optical diffuser master of the present invention.
BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 is an illustration of prior art equipment setup used to create planar (i.e., flat) optical holographic diffuser masters.
FIG. 2 is an illustration of prior art equipment setup used to create cylindrical (seamed and seamless) holographic optical diffuser masters.
FIG. 3 is an illustration of one preferred embodiment the present invention, as it would be used in practice, to produce composite holographic optical diffusers in a planar format.
FIG. 4 is an illustration of another preferred embodiment the present invention, as it would be used in practice, to produce composite holographic optical diffusers in a planar format.
FIG. 5 is an illustration of one preferred embodiment the present invention, as it would be used in practice, to produce composite holographic optical diffusers in a cylindrical (seamed and seamless) format.
FIG. 6 is an illustration of another preferred embodiment the present invention, as it would be used in practice, to produce composite holographic optical diffusers in a cylindrical (seamed and seamless) format.
FIG. 7 is a chart (plot) of the superposition of the lower-frequencies produced by the base recording and the higher-frequencies produced by the overlay recording.
FIG. 8 is a photomicrograph of a holographic optical diffuser with only the lower-frequency surface relief microstructures.
FIG. 9 is a photomicrograph of a preferred embodiment of the present invention with higher-frequency surface relief microstructures superimposed upon the lower-frequency surface relief structures shown in FIG. 7.
FIG. 10 is the photomicrograph of FIG. 9 without the individual surface relief structure callouts (for visual clarity).
DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS
The present invention, a composite holographic optical diffuser and method of fabrication thereof, comprises a composite surface relief structure, which acts as a suppressor to visible optical artifacts—in particular, undesirable ones.
The present invention does this by overlaying smaller (higher spatial frequency) microstructures on top of lower-frequency ones by either of the following:
Method 1
Performing a first exposure with larger microstructure projections (about 5-100 microns) upon a target substrate coated with photoresist recording media followed by a second exposure with smaller microstructures (about 0.5-3 microns) projected upon the same substrate (i.e., on top of the larger microstructures). The photoresist can be either developed or left undeveloped between these two exposures.
Method 2
Placing a partial mirror between the mid-diffuser and the target substrate coated with photoresist recording media, with the partial mirror close (less than 4 inches and preferably 0.25 inches to 3 inches) to the target substrate, so as to produce a substantial (i.e., recordable) re-reflection of the part of the original recording light that is reflected from the recording media.
Referring to FIG. 3, the present invention is retrofittable to existing equipment 300 used to fabricate planar holographic optical diffuser masters by introducing a fixture (Method 1) to move the mid-diffuser 305 much closer less than 4 inches (and preferably 0.25 inches to 3 inches, to the target recording media (and substrate) than is done in prior art setups and performing a second exposure. The setup comprises a laser 301, its raw laser beam 302, lensing 303, refracted laser beam 304, a mid-diffuser 305, an aperture 306, a patterned laser beam (307 for the first exposure and 314 for the second exposure), a target substrate 308 mounted to a support structure 309 and an x-y translation stage 310 mounted upon an optical bench 311 supported by vibration-isolation elements 312.
Referring to FIG. 4, the present invention is retrofittable to existing equipment 400 used to fabricate cylindrical optical holographic optical diffuser masters by introducing a partial mirror 413 between the mid-diffuser and the target substrate coated with photoresist recording media (Method 2), with the partial mirror 413 close (about preferably 3 inches) to the target substrate, so as to produce a substantial (i.e., recordable) re-reflection 415 of the part of the original recording light that is reflected from the recording media. The setup comprises a laser 401 its raw laser beam 402, lensing 403, refracted laser beam 404, a mid-diffuser 405, an aperture 406, a patterned laser beam 407 and 414, a target substrate 408 and an x-y translation stage 410 mounted upon an optical bench 411 supported by vibration-isolation elements 412.
Referring to FIG. 5, the present invention is retrofittable to existing equipment 500 used to fabricate seamed and seamless holographic optical diffuser masters by introducing a fixture (Method A) to move the mid-diffuser 505 much closer about 0.25 inches to 4 inches and preferably 3 inches, to the target recording media (and substrate) than is done in prior art setups and performing a second exposure. The setup comprises a laser 501 its raw laser beam 502, lensing 503, refracted laser beam 504, a mid-diffuser 505, an aperture 506, a patterned laser beam 507, a target substrate 508 and an x translation stage with rotation stage 510 mounted upon an optical bench 511 supported by vibration-isolation elements 512.
Referring to FIG. 6, the present invention is retrofittable to existing equipment 600 used to fabricate cylindrical optical holographic optical diffuser masters by introducing a partial mirror 613 between the mid-diffuser and the target substrate coated with photoresist recording media (Method 2), with the partial mirror 613 close (less than 4 inches and preferably 3 inches) to the target substrate, so as to produce a substantial (i.e., recordable) re-reflection 615 of the part of the original recording light that is reflected from the recording media. The setup comprises a laser 601 its raw laser beam 602, lensing 603, refracted laser beam 604, a mid-diffuser 605, an aperture 606, a patterned laser beam 607 and 614, a target substrate 608 and a rotating cylinder mounted on a x-axis translation stage 610 mounted upon an optical bench 611 supported by vibration-isolation elements 612. Mask 616 prevents undesired double exposure.
Referring to FIG. 7, a plot 700 of the composite structure 701 comprising the overlay of high spatial frequency signals 703 upon lower spatial frequency ones 702 is shown. In this example, the size of the higher optical frequency signal is about 1 micron, and the lower optical frequency signal is about 10 microns.
Referring to FIG. 8, a photomicrograph of a legacy (prior art) diffuser 800 produced with only the lower frequency structures (approx. 20 microns×10 microns in this example) 801.
Referring to FIG. 9, a photomicrograph of the composite diffuser of the present invention, one can see the higher spatial frequency (approx. 5 micron×8 micron) structures 902 superimposed upon the lower ones 901.
Referring to FIG. 10, the photomicrograph of FIG. 9 is shown without the individual microstructures called out (for visual clarity).
Method of Production
Basic Exposure Process to Produce Primary LSD Structure
Equipment
- 1) Optical table
- 2) Laser
- 3) Substrate with photo-resist material
- 4) Optical shutter
- 5) Lenses—Spherical, Aspherical and Cylindrical
- 6) Aperture
- 7) Mid Diffuser
- 8) Motion Stage
- 9) Lens holders, posts, post holders, rails, etc.
Procedure:
- 1) Layout the optical elements onto the optical table as shown in FIG. 1. Exact layout will depend upon angle desired.
- 2) Measure the spot size at the Substrate.
- 3) Calculate the amount of movement to get uniform angle.
- 4) Calculate exposure (time and laser power) per shot to form the correct angle.
- 5) Program the stage and shutter according to the calculations.
- 6) Run the program and leave the room to reduce noise in the recording.
- 7) When the program is finished, remove the substrate and develop the photo-resist.
Method for Overlaying Secondary High Frequency Structure
Method 1
- 1) Expose plate as previously explained.
- a. Method 1 can be applied prior to development step.
- b. Method 1 can be applied after development step.
- 2) Set up high frequency optical layout. The mid diffuser is set much closer to the recording substrate (0.1″ to 2″), the full width half maximum (fwhm) spot size on the mid diffuser ideally is the same or larger than the distance to the substrate. The diffraction features (minimum size) recorded will be approximately 1.3*wavelength*distance/(spot size on mid diffuser).
- a. If recording on a flat substrate, the mid-diffuser can be flat.
- b. If recording on a cylindrical substrate (as with seamless recording), the mid-diffuser can be cylindrical in order reduce the apparent distance to the substrate.
- 3) Develop normally.
Method 2
- 1) Set up the optics the same as the basic setup.
- 2) Once the basic set up is done, place an additional optic:
- a. Partial mirror that can also be a flat window (0.1″ to 5″) in front of the recording substrate for flat substrate.
- b. Cylindrical window (0.1″ to 5″) concentric to the recording substrate FIG. 2.
- 3) Follow the exposure process.
- 4) Develop normally.
This method will produce features that are smaller than 1 micron. The substructure tends to be fractal in nature. Method 2 can only be applied with a single exposure; i.e., optical tiling will not work since the high frequency tends to be blurred out in the process.
Patent Grant
9568885