Patent Application
20210122454
This application claims priority to European Patent Application 19382922-3 filed Oct. 23, 2019, the entirety of which is incorporated by reference.
The present invention belongs to the field of manufacturing composite parts, and particularly, the invention provides a composite laminate for an airframe lifting surface and a method for manufacturing thereof. The invention may be embodied to provide an advanced composite laminate for an airframe lifting surface by means of high deposition pre-preg materials technology.
A composite airframe lifting surface is typically composed by a skin, such as a composite laminate skin which is stiffened, such as by a torsion box. The lifting surface may be wings, horizontal and/or vertical tail planes, rudders, elevator, ailerons, spoilers and flaps.
Typically, these composite airframe lifting surfaces are manufactured with standard pre-preg materials by means of Automated Fibre Placement (AFP) or Automated Tape Laying (ATL). In both methods, the lay-up process needs a high volume of labour hours even though the process is automated. Furthermore, according to a high production rate scenario, a big investment is needed in terms of machines and shop floor to compensate the large lead time involved in said lay-up processes.
High deposition pre-preg material formats are known in the aeronautical field whose formats and technology reduce substantially the lay-up time for the composite structures. These high deposition pre-preg materials are pre-impregnated composite fibres materials where a thermoset polymer matrix material or a thermoplastic resin is already present. The technology design of these material formats allow a quick lay up of tapes (tows) of pre-preg material that are provided in a wider format (width of 2 inch or 50.8 mm), and in some cases, also thicker than the conventional standard pre-preg material formats.
The use of thicker high deposition pre-preg material formats for current laminate designs for lifting surfaces may result in failures at the edges of the laminate. The failures are known as edge effects or delaminations, and are related to the increase of interlaminar stresses towards the edges of the laminate. The edge effect is a consequence of the accumulation or grouping of material fibres non-parallel to the edge of the laminate in combination with the strain level at the edge area. Particularly, the edge effect may be more critical for the high cured ply thickness laminates, such as laminates manufactured with thicker high deposition pre-preg material formats.
The present invention may be embodied as a composite laminate for an airframe lifting surface comprising a set of stacked plies of pre-preg material, the composite laminate being surrounded by at least an edge following an edge direction E along the composite laminate, the set of stacked plies comprising: (i) a first plurality of plies formed by tapes arranged parallel to the edge direction E, and (ii) a second plurality of plies formed by tapes arranged in a direction different to the edge direction E, wherein the thickness of at least one ply of the second plurality of plies is lower than the thickness of each ply of the first plurality of plies.
The composite laminate may be manufactured with high deposition pre-preg material formats that are laid up in the form of tapes in a same direction for each ply thus conforming such composite laminate. The lay-up of these pre-preg material formats may be performed by AFP.
The present composite laminate is surrounded or bounded on their lateral sides by edges at their ends, where at least one edge follows an edge direction E along the composite laminate that may include the total thickness of the set of stacked plies, defined between the ends of their lateral sides.
Unlike the conventional designs of composite airframe lifting surface laminate, the present invention provides a new laminate design for manufacturing composite airframe lifting surface with high deposition pre-preg material formats. So far, these materials have not been used to manufacture lifting surfaces due to the disadvantages caused by the edge effect. However, the present invention provides an improved design of a composite laminate which is compatible with the high deposition pre-preg material formats and avoids or reduces the edge effect.
Moreover, the decreased thickness of plies between both the first plurality of plies and the second plurality of plies, and compared with the prior art designs, advantageously reduces the edge effect on the composite laminate. That is, the edge effects due to thicker plies formed by the high deposition pre-preg material formats are prevented by the present design wherein the thickness of the plies the composite laminate are minimized between layers in comparison with the prior art laminate ply thickness. Further, this new design for composite laminate provides cost and lead time reduction thus allowing a high production rate.
The thickness of all the plies forming the second plurality of plies may be narrower than the thickness of each ply of the first plurality of plies. The thicknesses of each of first plurality of plies may be a uniform thickness; and the thickness of each of the second plurality of plies may be less than three-fourths of the uniform thickness.
Moreover, each of the directions of the tapes in the second plurality of plies is at an angle least twenty degrees from the edge direction.
The thickness of all the plies forming the first and the second plurality of plies may be, respectively, substantially the same.
The second plurality of plies of the composite laminate may be formed by tapes arranged in a direction orthogonal to the edge direction E. In this case, the first plurality of plies are formed by tapes arranged parallel to the edge direction E (which are referred to as 0° plies), and the second plurality of plies of the composite laminate are formed by tapes arranged in a direction orthogonal to the edge direction E (90° plies).
In a second embodiment, the first plurality of plies are formed by tapes arranged parallel to the edge direction E (0° plies), and the second plurality of plies of the composite laminate are formed by tapes arranged in a laying up direction of +45° with respect to the edge direction E.
In a third embodiment, the first plurality of plies are formed by tapes arranged parallel to the edge direction E (0°), and the second plurality of plies of the composite laminate are formed by tapes arranged in a laying up direction of −45° with respect to the edge direction E.
When using thinner plies, more quantity of plies have to be deposited to achieve the same total thickness of the laminate. The thinner plies may be distributed between the other plies to spread the interlaminar efforts through the entire laminate and reduce the criticality of border effects.
The second plurality of plies may distributed through the entire thickness (depth) of the composite laminate.
According to another embodiment, the first plurality of plies and the second plurality of plies are evenly (homogeneously) distributed through the thickness (depth) of the composite laminate.
In another particular embodiment, the set of stacked plies comprises: at least a first ply formed by tapes arranged parallel to the edge direction E, at least a second ply formed by tapes arranged in a direction orthogonal to the edge direction E, at least a third ply formed by tapes arranged in a laying up direction of +θ° with respect to the edge direction E, and at least a forth ply formed by tapes arranged in a laying up direction of −θ with respect to the edge direction E; wherein θ is in a range of 0 to 90 degrees.
Thus, the first ply is laid up in a laying up direction that is parallel to the edge direction E, the second ply is laid up in a laying up direction of 90° with respect to the edge direction E; the third ply is laid up in a laying up direction of +θ° with respect to the edge direction E; and the third ply is laid up in a laying up direction of −θ° direction with respect to the edge direction E. In a particular embodiment, θ is 45.
In another particular embodiment, the plies of both the first and second plurality of plies are interspersed through the thickness (depth) of the set of stacked plies. The expression “interspersed” will be understood, for example, as positioning, by order of stacking, first plies formed by tapes arranged parallel to a particular direction, the first plies being interposed between second plies formed by tapes arranged in a direction different to the particular direction.
In another particular embodiment, the thickness of the plies of the second plurality of plies is comprised between 0.184 mm and 1 mm.
In a more particular embodiment, wherein the 50% of the plies of the set of stacked plies corresponds to the first plurality of plies, the 33% of the plies of the set of stacked plies corresponds to the third and fourth plies of the second plurality of plies, and the 17% of plies of the stacked plies corresponds to the second plies of the second plurality of plies.
The invention may be embodied in an airframe lifting surface comprising a composite laminate according to the first inventive aspect. The airframe lifting surface may include stiffening elements, such as stringers, spars, beams, the stiffening elements being bonded to the composite laminate by an adhesive, such as an adhesive line. The airframe lifting surface may be one of a: torsion box, horizontal tail plane, vertical tail plane, rudder, elevator, aileron, spoiler or flap. Further, the invention may be embodied an aircraft comprising a composite airframe lifting surface.
The invention may be embodied as a method for manufacturing a composite laminate for an airframe lifting surface according to the first inventive aspect, the method comprising the steps of: laying up pre-preg material forming a set of stacked plies; curing the set of stacked plies, and obtaining a composite laminate for an airframe lifting surface in the form of a cured composite laminate; wherein the cured composite laminate is surrounded by at least an edge, the edge following an edge direction E along the composite laminate;
The step of laying up the pre-preg material may include: a first plurality of plies with tapes laid up in the edge direction E, and a second plurality of plies, each ply with tapes laid up in a laying up direction different to the edge direction E; and the thickness of at least one ply of the second plurality of plies is lower than the thickness of each ply of the first plurality of plies.
The present method provides a composite laminate with a reduced lamination effect at the edges of the composite laminate.
In a particular embodiment, the step of laying up pre preg material may be performed by an Automated Fibre Placement (AFP) wherein the fibre of the pre-preg material is laid up in a particular direction for each ply according to the present invention.
The step of laying up the pre preg material may provide a composite laminate in a fresh state in the form of fresh stack of plies.
The step of laying up the pre preg material may comprise laying up: tapes in a laying up direction parallel to the edge direction E for forming at least a first ply, tapes in a laying up direction orthogonal to the edge direction E for forming at least a second ply, tapes in a laying up direction of +0° with respect to the edge direction E for forming at least a third ply i, and tapes in a laying up direction of −θ° with respect to the edge direction E for forming at least a forth ply, wherein θ is in a range of 0 to 90 degrees.
In a fifth inventive aspect, the present invention provides a method for manufacturing an airframe lifting surface according the second inventive aspect, the method comprising the following steps: providing at least a composite laminate according to the first inventive aspect, providing stiffening elements, joining the stiffening elements to the composite laminate, and obtaining the airframe lifting surface.
In a particular embodiment, the step of joining the stiffening elements may comprise co-bonding the stiffening elements to the cured composite laminate by means of an adhesive line.
In a particular embodiment, the of joining the stiffening elements may comprise co-curing the set of stacked plies with stiffening elements or other structural components in a same curing cycle.
All the features described in this specification (including the claims, description and drawings) and/or all the steps of the described method can be combined in any combination, with the exception of combinations of such mutually exclusive features and/or steps.
These and other characteristics and advantages of the invention will become clearly understood in view of the detailed description of the invention which becomes apparent from the disclosed embodiments of the invention, given just as examples and not being limited thereto, with reference to the drawings.
The present invention provides an improved composite laminate design for an aircraft airframe lifting surface manufactured with high deposition pre-preg material formats.
Airframe Lifting Surface
As shown in
The airframe lifting surface shown in
Composite Laminate (2)
The above design, corresponding to the prior art, would experience the edge effect or delamination on the edges (30) of the composite laminate (20) since the application of high deposition material formats for manufacturing an airframe lifting surface.
To reduce or even avoid the edge effect or delamination of the composite laminate (2), the thickness of the plies that are laid up in a direction different to the edge direction E is reduced compared to the prior art laminate shown in
Therefore, in the composite laminate (2) design shown in this
In a particular example, the 50% of the plies of the set of stacked plies (10) corresponds to first plies (4.1) formed by tapes parallel to the edge direction E; the 33% of the plies corresponds to third and fourth plies (5.2, 5.3) formed by tapes in the laying up direction of ±45° with respect to the edge direction E; and the 17% of plies corresponds to the second plies (5.1) formed by tapes in a direction orthogonal to the edge direction E.
Method for Manufacturing a Composite Laminate (2)
The present invention may be embodied as a method for manufacturing a composite laminate (2) for an airframe lifting surface, the method comprising the steps of: (a) laying up pre-preg material forming a set of stacked plies (10), (b) curing the set of stacked plies (10) obtained in the step a), and (c) obtaining a composite laminate (2) for an airframe lifting surface in the form of a cured composite laminate (2); wherein the cured composite laminate (2) obtained in the step c) is surrounded by at least an edge (3), the edge (3) following an edge direction E along the composite laminate (2);
The step (a) of laying up pre-preg material may comprise laying up at least: (i) a first plurality (4) of plies (4.1) with tapes laid up in the edge direction E, and (ii) a second plurality (5) of plies (5.1, 5.2, 5.3), each ply (5) with tapes laid up in a laying up direction different to the edge direction E; and the thickness of each ply of the second plurality (5) of plies is lower than the thickness of each ply of the first plurality (4) of plies.
The step (a) of laying up the pre-preg material may comprise laying up high deposition pre-preg material formats in the form of tapes (4) that makes up each ply of a plurality of stacked plies (10). According to at least an edge (3) of the composite laminate (2), in the step of laying up, some plies are laid up in the edge direction E and other plies are laid up in a direction different to the edge direction E.
In a particular example, some plies are laid up in a laying up direction of ±45° direction with respect to the edge direction E; other plies are laid up in another laying up direction that is orthogonal to the edge direction E, and some other plies are laid up in a direction that is parallel to the edge direction E.
The thickness of the laid up plies is a particular thickness for each ply so that the thickness of the plies formed by tapes that are laid up in a direction different to the edge direction E is lower than the thickness of the plies formed by tapes that are laid up in the edge direction E. That is, according to the edge (3) of the composite laminate (2) and both its edge direction E and the laying up direction of each ply, the thickness of the laid up tapes varies for each ply respectively in view of the prior art solutions.
In a particular example, after a cured composite laminate (2) is obtained, the method further comprises trimming the composite laminate (2) at its edges (3) in order to obtain the desired form.
Method for Manufacturing an Airframe Lifting Surface
The present invention provides a method for manufacturing an airframe lifting surface comprising the following steps: (a) providing at least a composite laminate (2), (b) providing stiffening elements (6), (c) joining the stiffening elements (6) to the composite laminate (2), and (d) obtaining the airframe lifting surface.
The cured composite laminate (2), may be joined to at least a stiffening element (6) by a co-bonding process wherein the stiffening element (6) is bonded to the composite laminate (2) by an adhesive line.
In another particular example, the set of stacked plies (10), in the form of a fresh composite laminate, is joined to at least a stiffening element (6) and both components are cured together in a same curing cycle by means of a co-curing process.
Aircraft
While at least one exemplary embodiment of the present invention(s) is disclosed herein, it should be understood that modifications, substitutions and alternatives may be apparent to one of ordinary skill in the art and can be made without departing from the scope of this disclosure. This disclosure is intended to cover any adaptations or variations of the exemplary embodiment(s). In addition, in this disclosure, the terms “comprise” or “comprising” do not exclude other elements or steps, the terms “a” or “one” do not exclude a plural number, and the term “or” means either or both. Furthermore, characteristics or steps which have been described may also be used in combination with other characteristics or steps and in any order unless the disclosure or context suggests otherwise. This disclosure hereby incorporates by reference the complete disclosure of any patent or application from which it claims benefit or priority.
| Number | Date | Country | Kind |
|---|---|---|---|
| 19382922-3 | Oct 2019 | EP | regional |