composite magnetic compacts and their forming methods

BACKGROUND OF THE INVENTION
1. Field of the Invention
This invention relates to methods of forming composite magnetic compacts consisting essentially of a powder of superplastic Zn-22Al alloy, a magnetic powder and a powder of plastic, and more particularly to new composite magnetic compacts having good conductivity and excellent mechanical and magnetic properties and their forming methods.
2. Description of the Prior Art
Magnetic materials can generally be classified into hard magnetic materials having a coercive force of approximately 100 Oe or above and soft magnetic materials having a lower coercive force. The former includes ferrite magnet, sintered alnico magnet and rare-metal cobalt magnet which are known as magnet materials. They have wide applications in various kinds of electric appliances, measuring instruments, communications equipment, audio equipment, attracting magnets, toys and the like. Soft magnetic materials are used for transformers, magnetic heads, dampers, electromagnetic-wave absorbers and so on.
In recent years, general choices of market has shifted from heavy, thick, long and large products to lighter, thinner, shorter and smaller ones. The same applies to products made of magnetic materials. Demand for products smaller in size, higher in performance and more intricate in profile is increasing. Such demand can be satisfied, for example, by injection-moulding that is applied to such hard magnetic materials as plastic and rubber magnets.
In injection-moulding, a powder of hard magnetic material, such as a powder of ferrite, is mixed and stirred with molten thermoplastic or thermosetting plastic. The mixture is extruded into a mold placed in a magnetic field. After the profile of the mold has been transferred, the compact is cooled to room temperature, and then magnetized in a strong magnetic field. This method permits producing in a single process a compact of intricate profile that is very close to the desired final product in shape and dimension.
But injection-moulding and resins formed thereby have some drawbacks: (1) Serving as insulators, such resins do not prevent electromagnetic interference that has been at issue recently; (2) Losing plasticity on being formed, such resins are practically un-reformable; (3) Such resins must be kept above their melting point while they are being formed, as a consequence of which heating energy constitutes a large percentage of the total energy consumed in forming; (4) Compacts of such resins do not have high toughness; (5) Mold design must allow for the shrinkage of compacts and, therefore, require highly sophisticated skill; and (6) Compacts are likely to have flashes produced thereon as a result of injection-moulding.
Recently, more and more OA (office automation) machines and the like have come to be made of plastic, creating a serious social problem of electromagnetic interference. Therefore, development of effective electromagnetic shielding means has been expected. Another social problem coming up lately is vibration obstacle that also calls for the development of appropriate vibration absorbers and dampers.
SUMMARY OF THE INVENTION
An object of this invention is to provide a new highly conductive composite magnetic compact and its forming method that solve the problems with the conventional injection-moulding process, especially the problem of insulating magnet.
Another object of this invention is to provide a new composite magnetic compact that has not only high conductivity but also high vibration damping and electromagnetic shielding properties and its forming method.
Still another object of this invention is to provide a composite magnetic compact that has wide applications not only as hard magnetic material but also as soft magnetic material suited for electromagnetic absorbers.
Yet another object of this invention is to provide a composite magnetic compact and its forming method that solves the problems with the conventional injection-moulding process through the use of a powder of superplastic Zn-22Al alloy having good conductivity in the forming of magnetic powder.
A further object of this invention is to provide a method of forming a composite magnetic compact that ensures higher forming efficiency than the conventional injection-moulding process by employing pressure-forming that is applied in the production of common sintered powder products.
Still further object of this invention is to provide a composite magnetic compact that is made of a material mixture containing a higher percentage of magnetic powder but retains high enough strength, despite the fact that the use of such a material usually entails a drop in strength, and its forming method.
Another object of this invention is to provide a composite magnetic compact having excellent mechanical and magnetic properties and its forming method.
In order to achieve the above objects, composite magnetic compacts of this invention are made of mixed powders consisting essentially of 1 to 50 percent by weight of a magnetic powder and the remains consisting mainly of a superplastic Zn-22Al alloy powder.
A first method of forming such composite magnetic compact is to form a mixed powder consisting essentially of 1 to 50 percent by weight of a magnetic powder and the remains consisting mainly of a superplastic Zn-22Al alloy powder at a temperature between room temperature and 250.degree. C. and under a pressure of 3 to 60 kgf/mm.sup.2. A second method applies hot pressing on the above material powder at a temperature between 200.degree. C. and 250.degree. C. and under a pressure of 1 to 10 kgf/mm.sup.2, for a period of 10 to 60 minutes.
The strength of the compact decreases as the ratio of the magnetic powder increases in the mixture. On such occasions, the strength of the compact can be increased by adding prastics to the mixture of a magnetic powder and a powder of superplastic Zn-22Al alloy. Some examples of such plastics are phenol, epoxy, unsaturated polyester and polyurethane resins.
Such resins may be impregnated into a compact made by forming a mixture of a magnetic powder and a powder of superplastic Zn-22Al alloy at a temperature between room temperature and 250.degree. C. and under a pressure of 1 to 30 kgf/mm.sup.2. The appropriate amount of impregnated plastics is generally between 1 and 15 percent by weight.
While the above method requires two steps of forming and impregnating, the following methods are much simpler.
A first method is to form a mixture consisting of a powder of superplastic Zn-22Al alloy, a magnetic powder and a powder of plastics at a temperature between 100.degree. C. and 250.degree. C. and under a pressure of 1 to 30 kgf/mm.sup.2.
A second method is to hot-press the same mixture at a temperature between 100.degree. C. and 250.degree. C. and under a pressure of 1 to 20 kgf/mm.sup.2, for a period of 10 to 60 minutes.
A third method is to fire, at a temperature between 100.degree. C. and 250.degree. C., a compact made by forming the same mixture at room temperature and under a pressure of 1 to 50 kgf/mm.sup.2.
As was the case of impregnation mentioned before, such plastic powders as phenol, epoxy, unsaturated polyester and polyurethane resins can be used. The appropriate mixing ratio of such resins is generally between 1 and 15 percent by weight.
In any of the above cases, the formed compact must be magnetized in a strong magnetic field when the magnetic powder is a hard magnetic material.
The powder of superplastic Zn-22Al alloy used in the forming of composite magnetic compacts according to this invention is generally prepared by an air- or argon-atomizing method. The inventor found that the superplasticity of the powder of superplastic Zn-22Al alloy is effectively increased when the powder is quenched in iced water after being heated at a temperature of 380.degree. C. or thereabout for a period of 30 minutes. This knowledge was disclosed in Japanese Provisional Patent Publication No. 157201 of 1984. The strength and density of compacts according to this invention can also be effectively increased if the powder of superplastic Zn-22Al alloy thus quenched is used.
Superplasticity is a property whereby materials elongate extraordinarily under certain conditions, with a sharp drop in resistance to deformation. Metals having this property can be deformed as freely as starch syrup. So, such metals can be formed into products of intricate shapes with a small amount of working force and in a small number of processes. Superplasticity appears when (1) grain size is as fine as about 10 .mu.m and under, (2) grains are equiaxed, (3) grain-boundary slip is likely to occur, and (4) a material consists of a dual-phase structure. Thus a fine-grained microstructure is an important prerequisite for the attainment of superplasticity. Therefore, the starting material to reveal superplasticity must preferably be powder, rather than casting. This is because fine-grained microstructure cannot be obtained unless molten metal is cooled and solidified rapidly, and faster cooling is achieved with powders that occupy smaller cubic volumes than solid masses (castings). In addition, less segregation occurs in compacts made from powders that are cooled rapidly than in those made from castings.
Zn-22Al alloy is an example of superplastic material that exhibits excellent diffusing and joining properties, vibration damping and electromagnetic shielding effects where the conditions under which superplasticity appear exist.
This invention provides new composite magnetic compacts and their forming methods by taking advantage of the powder forming technique and the superplasticity of Zn-22Al alloy described above.

BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 is a schematic view illustrating an example of forming methods according to this invention.
FIG. 2 is a graphical representation of the relationship between the forming pressure and the density of compacts made of ferrite powder.
FIGS. 3 and 4 respectively show the forming and fracutre regions of cold- and hot-formed compacts.
FIG. 5 is a graphical representation of the results of rattler tests conducted on different compacts.
FIG. 6 is a schematic view illustrating another example of forming methods according to this invention.
FIG. 7 is a graphical representation of the relationship between the forming pressure and the density of compacts made from a material in which 30 percent by weight of ferrite powder is mixed.
FIG. 8 graphically shows the relationship between the strength of compacts and the mixing percentage of ferrite content.
FIG. 9 graphically shows, at (A) and (B), the relationship among the strength and density of compacts and the mixing percentage of ferrite content, proving the preferableness of hot-forming to cold-forming.
FIGS. 10 to 14 graphically show the relationship between the strength of compacts and the mixing percentage of ferrite content.
FIG. 10 shows the effectiveness of hot-pressing,
FIG. 11 shows the effectiveness of firing for cold-formed compacts, and
FIG. 12 proves the effectiveness of using a quenched powder of superplastic Zn-22Al alloy.
While FIG. 13 shows the influence of forming pressure,
FIG. 14 shows the influence of the mixing percentage of plastic content.

DESCRIPTION OF THE PREFERRED EMBODIMENTS
FIG. 1 schematically shows an example of an apparatus with which a forming method of this invention is carried out. As is illustrated, given amounts of a magnetic powder 1, a powder of superplastic Zn-22Al alloy 2 and a powder of plastic 3 that is added as needed are put in a die 6 and pressed to shape between upper and lower punches 4 and 5 at an appropriately controlled temperature.
Powders of ferrite and rare-earth minerals are good examples of the magnetic powder. Although this invention is applicable to either type, the following description is concerned with embodiments using ferrite powders.
The relationship between the quantities of powders of ferrite and superplastic Zn-22Al alloy mixed together (expressed in terms of percent by weight) is as follows: As the ratio of a ferrite powder increases, compacts will have better magnetic properties but lower strength and formability. Meanwhile, an increase in the ratio of a powder of superplastic Zn-22Al alloy enhances strength, conductivity and formability.
When a powder of plastic is added, compacts will be formed with greater ease and have greater strength as the percentage of the addition increases. But their conductivity and reformability will drop. Accordingly, the appropriate mixing ratio of a plastic powder may be between 1 and 15 percent by weight. The rest may consist of a magnetic powder and a powder of superplastic Zn-22Al alloy.
FIG. 2 shows the relationship between the forming pressure and the density of compacts made by use of a ferrite powder (the GP-500 made by Toda Kogyo Co., Ltd.), together with the density obtained after firing. While the true density of ferrite is approximately 5.2 g/ cm.sup.3, unfired compacts(green compacts)exhibit a substantially uniform density of 3.0 to 3.1 g/cm.sup.3 as indicated by the white dots in the figure. When the forming pressure is increased to about 15 kgf/mm.sup.2 or above, the compact fractures into pieces when taken out of the die as a result of the occurrence of lamination cracks. The black dots in FIG. 2 indicate the density of ferrite sinters obtained by sintering compacts in a vacuum at a temperature of 1100.degree. C. for 60 minutes. Cracks occur in some sintered compacts.
As is obvious from the above, magnetic powders, such as those of ferrite, do not have good compressibility and formability. In press-forming a ferrite powder by the closed-die forming method employing a metal die, the compact may fracture when taken out of the die because of the spring-back of the compact or the friction between it and the die. Even if the fracture at this point is avoided, the compact may still break while it is being delivered to firing, magnetizing and other subsequent processes or as a result of thermal expansion during firing.
This invention solves the above problems by making composite compacts through the use of a mixture of a magnetic powder and a powder of superplastic Zn-22Al alloy. The powder of superplastic Zn-22Al alloy is used like a binder. The resulting composite magnetic compacts have excellent plasticity, conductivity, vibration damping and electromagnetic shielding properties, and good formability and workability.
FIG. 3 shows the formed condition of compacts taken out of dies which are cold-formed under different pressures and with different percentages of ferrite addition. FIG. 4 shows the similar condition of hot-formed compacts (made at 250.degree. C.). FIG. 5 graphically shows the strength of compacts measured by the "Rattler Test on Compacts of Metal Powders" specified in JSPM (the Japan Powder Metal Association) Standard 4-69. Judging from the results shown in FIGS. 3 to 5, the maximum mixing percentage of a ferrite content that assures good formability and such compact strength as will keep the weight reduction under the Rattler test at 10 percent or under is 60 percent by weight. But, considering the strength of the compact and other requirements, the appropriate mixing percentage becomes 50 percent by weight or under. With soft magnetic materials, the mixing percentage of the magnetic powder may be 20 to 30 percent by weight maximum.
This invention is applicable to dispersed composite compacts obtained by mixing a ferrite powder with a powder of superplastic Zn-22Al alloy as shown in FIG. 1. It has also proved applicable to compacts in which a core of ferrite powder or casting (an ordinary material having a density of 100 percent) bulk 7 is buried in the center of said dispersed composite compacts or a compacts of a superplastic Zn-22Al alloy powder as shown in FIG. 6. In this instance, the magnetic material need not be a powder or casting of ferrite, but a powder or casting of rare-earth minerals.
With regard to the forming conditions, the forming temperature, forming pressure and duration of time in which such pressure is applied are the major factors. It is most important to choose an appropriate forming temperature because superplastic materials undergoes a larger ductility and a sharp drop in pressing force at certain temperatures. A temperature between 200.degree. C. and 250.degree. C., especially in the vicinity of 250.degree. C., is appropriate for the powders of superplastic Zn-22Al alloys, though they exhibit sufficient ductility even at room temperature. When the forming pressure is too low, the powder fails to solidify or, even when it solidifies, fails to form strong enough compacts.
FIG. 7 shows the relationship between the density and forming pressure of compacts formed cold and at a temperature of 250.degree. C. Here, 30 percent by weight of a ferrite powder is mixed with a powder of superplastic Zn-22Al alloy. A forming pressure of approximately 3 kgf/mm.sup.2 is sufficient when forming is done at a temperature of about 250.degree. C. using a mechanical or hydraulic press. Even if the forming pressure is increased beyond a required level, mechanical properties of compacts are not improved much because of the limited compressibility of the ferrite powder. Rather, there will arise the risk of breaking the forming die. As such, the higher limit of forming pressure may be about 60 kgf/mm.sup.2 even with cold-forming which needs a considerably large pressing force. The pressing force may be applied only momentarily as with forging on a mechanical press. But application of pressure over a longer period, which may be achieved by means of hot pressing, is effective in attaining higher densities as shown in Table 1 below.
TABLE 1______________________________________Forming Pressure Hot Pressing Hot Forming______________________________________1.0 kgf/mm.sup.2 3.59 g/cm.sup.3 3.41 g/cm.sup.32.1 kgf/mm.sup.2 3.86 g/cm.sup.3 3.65 g/cm.sup.33.2 kgf/mm.sup.2 4.07 g/cm.sup.3 3.87 g/cm.sup.3______________________________________ [Conditions Mixing ratio of ferrite powder: 30 percent by weight (constant) Hot pressing: 30 minutes at 250.degree. C. Hot forming(Hot forging): 1 minute at 250.degree. C.
As a consequence, the pressing force can be reduced to between 1 and 10 kgf/mm.sup.2. With superplastic Zn-22Al alloys, however, superplasticity drops as a result of the coasening of grain size when they are allowed to stand at a temperature of 250.degree. C. for a period longer than about 60 minutes.
Accordingly, the maximum duration of pressure application in hot pressing is set at 60 minutes.
When the magnetic powder is of the soft type, the products made under the above conditions are soft-magnetic composite compacts. When the magnetic powder is of the hard magnetic type, the products made under the above conditions are hard-magnetic composite compacts after magnetizing process. Still greater effect is obtained if a mixture of powders of hard ferrite and superplastic Zn-22Al alloy is formed in a magnetic field in which magnetism can be oriented.
Firing the formed compact at a temperature between 250.degree. C. and 350.degree. C. provides further enhancement of strength. But such firing can safely be dispensed with.
As is shown in FIG. 3, the strength of compacts decreases as the percentage of magnetic material in the mixture increases. With a view to improving the strength of such compacts, a compact made from a mixture of a ferrite powder and a powder of superplastic Zn-22Al alloy is placed in a hermetically sealed container. After evacuating the container with a rotary pump, thermosetting epoxy resin (the 27-770 made by Kasai Shoko Co., Ltd.) was impregnated in the compact. The obtained results are given in FIG. 8 which shows the relationship between the mixing ratio of ferrite and the strength of compacts formed under a pressure of 10 kgf/mm.sup.2. Obviously, the impregnation remarkably improves the strength of the compacts.
The forming conditions of pre-impregnated compacts are the same as those described before. But since plastic is to be impregnated later, the forming pressure need not be excessively large. A pressure of 2.5 to 5.0 kgf/mm.sup.2 is sufficient when forming is done at a temperature of 250.degree. C. or thereabout. The pressure may be between 1 and 30 kgf/mm.sup.2 in cold forming.
When the magnetic powder is of the hard magnetic type, the products formed under the above conditions are turned into strong composite magnetic compacts by the subsequent plastic impregnation and magnetization in a strong magnetic field. Still greater effect is obtained since the magnetism can be oriented by forming the mixture in a magnetic field.
Firing a pre-impregnated compact at a temperature between 200.degree. C. and 400.degree. C. brings about an improvement in strength. But such firing may safely be omitted since a remarkable improvement in strength can be achieved by impregnation.
Instead of impregnating plastic in formed compacts, a mixture of powders of ferrite, superplastic Zn-22Al alloy and plastic may be formed under such conditions as will be described in the following.
Of various factors involved in forming, such as the forming temperature and pressure and the duration of time over which such forming pressure is applied, the forming temperature is most important, especially when the plastic powder is of the thermosetting type as in the case of an example to be described later. The appropriate temperature range is between about 100.degree. C. at which the thermosetting property of plastic appears and about 250.degree. C. at which the superplasticity of Zn-22Al alloy appears. The appropriate forming pressure is 1 to 30 kgf/mm.sup.2 in hot forming (foring) at a temperature between 100.degree. C. and 250.degree. C., between 1 and 20 kgf/mm.sup.2 in hot pressing, and between 1 and 50 kgf/mm.sup.2 in cold forming(forging).
Although cold forming is generally not appropriate when the plastic powder is of the thermosetting type, the strength of such cold-formed compacts can be improved by heating at a temperature between 100.degree. C. and 250.degree. C. at which the thermosetting property of such plastic appears. But a choise of plastic suited for cold forming is preferable.
When the magnetic powder is of the hard magnetic type, the products formed under the above conditions turn into strong compacts on being magnetized in a strong magnetic field. Still greater effect is obtained if a mixture of powders of ferrite, superplastic Zn-22Al alloy and plastic is formed in a magnetic field in which magnetism can be oriented.
Now some examples of this invention will be given in the following.
EXAMPLE 1
Compacts were cold formed under a constant pressure of 44 kgf/mm.sup.2 from mixtures of a powder of ferrite (the GP-500 made by Toda Kogyo Co., Ltd.) and a powder of superplastic Zn-22Al alloy, with the mixing percentage of the ferrite powder varied between 10 and 40 percent by weight. Magnetic properties of the obtained compacts are shown in Table 2.
TABLE 2______________________________________Mixing Magnetic Properties of CompactsRatio of Residual Magnetic Coercive MaximumFerrite Flux Density Force EnergyPowder Br Hc Product (HB)______________________________________10 wt. % 230 G 220 Oe 0.0127 MGOe20 400 390 0.03930 600 560 0.08440 770 700 0.135______________________________________
EXAMPLE 2
Compacts were hot formed at a temperature of 250.degree. C. under a constant pressure of 44 kgf/mm.sup.2 from mixtures of a powder of ferrite (the GP-500 made by Toda Kogyo Co., Ltd.) and a powder of superplastic Zn-22Al alloy, with the mixing percentage of the ferrite powder varied between 10 and 60 percent by weight. Magnetic properties of the obtained compacts are shown in Table 3.
TABLE 3______________________________________Mixing Magnetic Properties of CompactsRatio of Residual Magnetic Coercive MaximumFerrite Flux Density Force EnergyPowder Br Hc Product (HB)______________________________________10 wt. % 200 G 200 Oe 0.010 MGOe20 410 390 0.04030 610 560 0.08540 780 700 0.13750 930 830 0.19360 1090 940 0.256______________________________________
EXAMPLE 3
Compacts were cold formed from a mixture of a powder of ferrite (the GP-500 made by Toda Kogyo Co., Ltd.) and a powder of superplastic Zn-22Al alloy, in which the mixing percentage of the ferrite powder was fixed at 30 percent by weight, with the forming pressure varied. Magnetic properties of the obtained compacts are shown in Table 4.
TABLE 4______________________________________ Magnetic Properties of Compacts Residual Magnetic Coercive MaximumForming Flux Density Force EnergyPressure Br Hc Product (HB)______________________________________75 kgf/mm.sup.2 610 G 560 Oe 0.085 MGOe60 610 560 0.08525 570 550 0.07815 540 520 0.0707.5 540 500 0.068______________________________________
EXAMPLE 4
In addition to the hard-magnetic compacts described so far, vibration damping effects of soft-magnetic composite compacts were also investigated. The SR-5 of Toda Kogyo Co., Ltd. was used as a magnetic powder, which was mixed with a quenched Zn-22Al superplastic powder. The mixing percentage of the magnetic powder was varied between 0 and 30 percent by weight. The compacts were formed at a temperature of 240.degree. C. and under a pressure of 20 kgf/mm.sup.2. Damping capacities of the obtained compacts are shown in Table 5.
TABLE 5______________________________________Forming ConditionsMixing Ratio Powder of Dampingof Ferrite Superplastic Forming CapacityPowder Zn-22Al alloy Temperature .eta. = Q.sup.-1______________________________________0 wt. % Quenched 240.degree. C. 0.008 .about. 0.0110 Quenched 240 0.008 .about. 0.0120 Quenched 240 0.008 .about. 0.0130 Quenched 240 0.008 .about. 0.01______________________________________
EXAMPLE 5
Compacts were cold-formed under a constant pressure of 10 kgf/mm.sup.2 from mixtures of a powder of ferrite (the GP-500 made by Toda Kogyo Co., Ltd.) and a powder of superplastic Zn-22Al alloy, with the mixing percentage of the ferrite powder varied between 10 and 100 percent by weight. Then, an epoxy resin (the 27-770 made by Kasai Shoko Co., Ltd.) was impregnated in the formed compacts. Magnetic properties of the obtained hard-magnetic composite compacts are shown in Table 6.
TABLE 6______________________________________ Magnetic Properties of CompactsMixing Ratio Residualof Ferrite Magnetic Flux Coercive MaximumPowder Density Br Force Hc Energy Product (HB)______________________________________10 wt. % 170 G 215 Oe 0.01 MGOe20 350 500 0.0430 520 480 0.0640 680 630 0.1050 830 730 0.1560 980 880 0.2270 1090 970 0.2680 1220 1050 0.3390 1340 1130 0.38100 1430 1210 0.45______________________________________
EXAMPLE 6
Mixtures of magnetic powders (the SR-5 and MZ-100 made by Toda Kogyo Co., Ltd.), 0 and 20 percent by weight, were mixed with a powder of superplastic Zn-22Al alloy and formed into compacts at room temperature under a constant pressure of 10 kgf/mm.sup.2. The same epoxy resin as was used in Example 5 was impregnated into the formed compacts. Damping capacities of the obtained soft-magnetic composite compacts for vibration damping services are shown in Table 7.
TABLE 7______________________________________Forming ConditionsMixing Ratio Type of Dampingof Magnetic Magnetic CapacityPowder Powder .eta. = Q.sup.-1______________________________________0 wt. % -- 0.0120 SR-5 0.0520 MZ-100 0.05______________________________________
EXAMPLE 7
In the following examples, an air-atomized powder of not larger than 44 .mu.m in grain size was used as a powder of superplastic Zn-22Al alloy, the GP-500 of Toda Kogyo Co., Ltd. as a powder of ferrite, and a powder of black phenol resin (the 21-111) of Kasai Shoko Co., Ltd., not larger than 840 .mu.m in grain size, as a powder of plastic.
The powders of superplastic Zn-22Al alloy, ferrite and plastic were mixed as shown in Table 8. While the percentage of the plastic powder was fixed at 10 percent by weight, the percentage of the powders of superplastic Zn-22Al alloy and ferrite were varied. Hot-forming was done at a constant temperature of 140.degree. C. under a constant pressure of 10 kgf/mm.sup.2. Some compacts were also cold-formed for the purpose of comparison. The strength of the formed compacts was measured by the radial crushing test according to JIS A1113 (testing conditions: temperature=room temperature, and testing speed=5 mm/min). The results are shown at (A) in FIG. 9. The density of the obtained compacts are shown at (B) in FIG. 9. The compacts formed at a temperature of 140.degree. C., at which the thermosetting property of the plastic appears, exhibiting higher strength and density, thus proving the advantage of hot-forming over cold-forming.
TABLE 8__________________________________________________________________________Mixing Ratio (Percent by Weight) Powder of Superplastic No. Alloy (SP)Zn-22Al Ferrite (FP)Powder of Plastic (PP)Powder of ##STR1##__________________________________________________________________________1 0 wt. % 90 wt. % 10 wt. % 80%2 10 80 10 803 20 70 10 704 30 60 10 605 40 50 10 506 50 40 10 407 60 30 10 308 70 20 10 209 80 10 10 1010 90 0 10 0__________________________________________________________________________
EXAMPLE 8
As in Example 7, the mixing ratio of the plastic powder and the forming pressure were fixed at 10 percent by weight and 10 kgf/mm.sup.2, respectively. Then, hot pressing was carried out at a temperature of 140.degree. C. for a period of 20 minutes. The strength of the formed compacts measured by the same method as that used in Example 7 is shown in FIG. 10. For the purpose of comparison, the results of cold-forming given at (A) of FIG. 9 are shown again. As is obvious from FIG. 10, hot-pressing is very effective in increasing the strength of compacts, as with the hot-forming shown in Example 7.
EXAMPLE 9
Compacts were cold-formed by fixing the mixing percentage of the plastic powder and forming pressure at 10 percent by weight and 10 kgf/mm.sup.2, respectively, as with the compacts for comparison prepared in Example 7. The formed compacts were then fired under three different conditions: (1) in a vacuum at a temperature of 200.degree. C. for a period of 3 minutes; (2) in the atmosphere at a temperature of 150.degree. C. for a period of 30 minutes; and (3) in the atmosphere at a temperature cf 250.degree. C. for a period of 30 minutes. The strength of the formed compacts and some cold-formed ones made for the purpose of comparison are shown in FIG. 11. Effectiveness of firing after cold-forming is obvious though the strength is not as high as that obtained from the hot-forming in Example 7 and hot-pressing in Example 8.
EXAMPLE 10
The powder of superplastic Zn-22Al alloy used in this example was heated at 380.degree. C. for 30 minutes and then quenched in iced water. The mixing percentage of the plastic powder and forming pressure were fixed at 10 percent by weight and 10 kgf/mm.sup.2, as in Examples 7 to 9. The strength of the compacts made by applying hot-forming at a temperature of 140.degree. C. is shown in FIG. 12. Effectiveness of quenching is obvious, as compared with the cold-formed compacts prepared for the purpose of comparison using an unquenched powder (as with the case of cold-forming shown at (A) of FIG. 9).
EXAMPLE 11
In the Examples 7 to 10, the forming pressure was fixed at 10 kgf/mm.sup.2. In this example, hot-forming was performed under three different pressures, i.e., 10, 20 and 30 kgf/mm.sup.2. The powder of superplastic Zn-22Al alloy was not quenched, the mixing percentage of the plastic powder was 10 percent by weight, and the forming temperature was 140.degree. C. As is shown in FIG. 13, the strength of the compacts formed under pressures of 10 to 30 kgf/mm.sup.2 varied little. This suggests that hot-forming can satisfactorily be achieved under a pressure of not more than about 10 kgf/mm.sup.2.
EXAMPLE 12
In Examples 7 to 11, the mixing percentage of the plastic powder was fixed at 10 percent by weight. In this example, the strength of the compacts made from mixtures containing 5 percent by weight and 15 percent by weight of the plastic powder, as shown in Tables 9 and 10, was also investigated. While the forming pressure and temperature were fixed at 10 kgf/mm.sup.2 and 140.degree. C., respectively, the powder of superplastic Zn-22Al alloy was not quenched. The results of the strength test are shown in FIG. 14. As is obvious, the strength was lower when the mixing percentage of the plastic powder was 5 percent by weight than in the cases in which the mixing percentage stood at 10 percent by weight and 15 percent by weight. Accordingly, the appropriate mixing percentage of the plastic powder is considered to be about 10 percent by weight.
TABLE 9__________________________________________________________________________Mixing Ratio (Percent by Weight) Powder of Superplastic No. Alloy (SP)Zn-22Al Ferrite (FP)Powder of Plastic (PP)Powder of ##STR2##__________________________________________________________________________1 5 wt. % 90 wt. % 5 wt. % 90%2 15 80 5 803 25 70 5 704 35 60 5 605 45 50 5 506 55 40 5 407 65 30 5 308 75 20 5 209 85 10 5 1010 95 0 5 0__________________________________________________________________________
TABLE 10__________________________________________________________________________Mixing Ratio (Percent by Weight) Powder of Superplastic No. Alloy (SP)Zn-22Al Ferrite (FP)Powder of Plastic (PP)Powder of ##STR3##__________________________________________________________________________1 5 wt. % 80 wt. % 15 wt. % 80%2 15 70 15 703 25 60 15 604 35 50 15 505 45 40 15 406 55 30 15 307 65 20 15 208 75 10 15 109 85 0 15 0__________________________________________________________________________

Number	Name	Date
4020236	Aonuma et al.	Apr 1977
4701301	Kuwahara et al.	Oct 1987
4892596	Chatterjee	Jan 1990

composite magnetic compacts and their forming methods

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Parent Case Info

US Referenced Citations (3)

Divisions (1)