Patent Application
20100021721
1. Field of the Invention
The invention relates to a composite material as well as to a method for the production of a composite material.
2. The Prior Art
Composite materials are combinations of at least two different materials, with the goal of improving the material properties of the individual substances by means of the combination of materials.
It is known to produce composite bodies of ceramic and metal, in order to combine the properties of the materials, such as the hardness of the ceramic and the deformability of the metal, with one another. In this connection, a molten metal is embedded into a ceramic body (see German Publication Nos. DD 301 900 A9, DD 285 774 A5, and International Application Publication No. WO 92/00256 A2). German Patent No. DE 37 86 163 T2 describes a method for the production of ceramic/metal composite materials, in which the starting substances, in powder form, pass through a sintering process.
A metal/ceramic composite material is described in German Patent No. DE 10 2004 012 990 A1, which consists of an open-pore metal foam, and whose pores are completely or partially filled with a ceramic material. The composite material has a great hardness and great impact resistance, at a comparatively low weight.
From German Patent No. DE 10 2004 063 489 B3, it is known to form light-construction elements on the basis of hollow spheres, in which the hollow spheres are precisely placed in accordance with the part to be produced, by means of a feed device, and connected with one another by means of pressing or heating (see also German Patent No. DE 100 18 501 C1). In accordance with German Patent No. DE 199 29 760 C2, the metallic or ceramic hollow spheres consist of different material layers.
The disadvantage of the known methods consists in the fact that the production of a composite material that has low weight and great hardness and impact resistance is very complicated. It is true that the weight of the material is reduced by means of the use of hollow spheres or metal foam, but the hardness and impact resistance of the material, on the whole, are not satisfactory.
It is therefore an object of the invention to provide a composite material and a method for the production of a composite material, in which the composite material has steel-like properties, at an increased modulus of elasticity, and a lower weight, and which can be produced in cost-advantageous manner.
This task is accomplished, according to the invention, by a composite material consisting of a ceramic material made of ceramic particles, which is completely or partially sheathed with a metallic material, and partially or completely embedded in a metallic casting material.
The material according to the invention has steel-like properties but with an increased modulus of elasticity. The pressure forces that act on the material are absorbed by the brittle and solid ceramic material, while the steel matrix that surrounds the ceramic material absorbs the tensile forces that act on the material.
In one embodiment, the casting material can be a casting steel or casting iron, and/or the material that sheathes the ceramic particles can be steel. The embedded ceramic particles preferably possess a material grain size of 0.1 mm to 10 mm.
In one embodiment, the ceramic material is Al2O3. In another embodiment, the steel coating of the ceramic particles amounts to a thickness of 2 μm to 3 mm.
In another embodiment, the proportion of the ceramic material in the composite material amounts to 30% to 90 M-%, preferably 55% to 65-%. The ceramic particles to be sheathed are preferably almost spherical.
According to the method according to the invention, ceramic particles are sheathed with a metallic material, and the ceramic particles sheathed in this manner are either embedded in a metallic casting material or sintered to form a steel matrix, which can also be embedded in a metallic casting material, if necessary.
The small-grain ceramic particles are preferably sheathed with a metallic material by means of a spraying method or by means of granulation in a fluidized bed. In one embodiment, the ceramic particles, which preferably consist of Al2O3 and have a material grain size of 0.1 mm to 10 mm, are sheathed with a metallic material.
In another embodiment, the ceramic particles are completely or partially sheathed with a steel layer. In another embodiment, the sheathed ceramic particles are sintered together to form a steel matrix, which has a thickness of preferably 2 μm to 3 mm. The sheathed ceramic particles or the parts sintered together to form a steel matrix can have a metallic casting material such as casting steel or casting iron cast around them.
Preferably, the ceramic particles have a metallic casting material cast around them in such a manner that the proportion of the ceramic material in the composite material amounts to 30% to 90 M-%, preferably 55% to 65 M-%.
Another significant advantage of the solution according to the invention is that the material is lighter, on the whole, than a comparable steel material, and furthermore has an increased modulus of elasticity.
Other objects and features of the present invention will become apparent from the following detailed description considered in connection with the accompanying drawings. It is to be understood, however, that the drawings are designed as an illustration only and not as a definition of the limits of the invention.
In the drawings, wherein similar reference characters denote similar elements throughout the several views:
The composite material according to
Furthermore, when sheathing the ceramic particles 1, attention must be paid to ensure that the casting material, the sheathing material, and the ceramic material possess approximately the same heat expansion coefficient.
According to the invention, sintering of steel sheathings 2 of ceramic particles 1 with one another takes place in a further step, at appropriate temperatures, whereby the steel matrix formed in this manner already corresponds to the basic shape of the parts to be produced. The steel matrix that is sintered together, with the enclosed ceramic particles 1, is brought into its final shape by means of casting a metallic casting material 3 around it, whereby this molded piece can certainly be mechanically processed further. In this connection, the mechanical processing represents a significant advantage of the composite material according to the invention. Casting steel or casting iron is used as the casting material 3, for example.
The material produced in this manner has steel-like properties, but possesses an increased modulus of elasticity and is lighter as compared with pure steel material. As a result, there is an increased area of use in technology, particularly in motor vehicle technology.
A variant of the solution according to the invention provides for providing the ceramic particles 1 sheathed with a steel layer 2 with a surrounding casting structure by means of a casting material 3, without first sintering them with one another.
Another possibility consists in producing the final shape only by means of sintering together the sheathed ceramic particles 1. In this connection, casting a casting material 3 around the steel-sheathed ceramic particles 1 that have been sintered to one another is not required.
Accordingly, while only a few embodiments of the present invention have been shown and described, it is obvious that many changes and modifications may be made thereunto without departing from the spirit and scope of the invention.