Patent Application
20210188715
The present application is based on, and claims priority from, EP Application Serial Number 19219135.1, filed on Dec. 20, 2019, the disclosure of which is hereby incorporated by reference herein in its entirety.
The technical field relates to method of removing fluoride ion from waste liquid, and in particular, it relates to the ceramic particles thereof.
Since hydrofluoric acid (HF) is widely used in cleaning waters or substrates, especially for semiconductors, optoelectronics panels, solar cells, etc., in Taiwan, for example, the usage amount of hydrofluoric acid is extremely high (at least 50,000 tons to 100,000 tons depending on the capacity utilization rate). In metric tons per year, the waste hydrofluoric acid discharged is a multiple of the amount used, because the cleaning process will be washed with ultrapure water, and naturally more hydrofluoric acid-containing waste liquid will be discharged. Waste water containing hydrofluoric acid must he recycled and treated, otherwise it will cause environmental pollution and damage.
In general, when hydrofluoric acid-containing waste is treated, a large amount of alkali must be used for neutralization treatment, and a lot of fine sludge is produced, which is very difficult and costly to handle. Moreover, if it is impossible to reproduce as industrially usable product such as calcium fluoride (CaF2), it can only be treated as sludge, which is very wasteful of resources and uneconomical.
One embodiment of the disclosure provides a composite material, including: a plurality of ceramic particles embedded in a calcium fluoride bulk, wherein the ceramic particles and the calcium fluoride bulk have a weight ratio of 1:4 to 1:20.
In some embodiments, the ceramic particles include oxides of 100 parts by weight of calcium, 30 to 95 parts by weight of iron, 15 to 50 parts by weight of silicon, 2 to 15 parts by weight of magnesium, 2 to 20 parts by weight of aluminum, and 2 to 10 parts by weight of manganese.
In some embodiments, the ceramic particles include a plurality of spinels distributed therein.
In some embodiments, the ceramic particles and the spinels have a weight ratio of 1:0.2 to 1:0.5.
In some embodiments, the ceramic particles have a diameter of 0.1 μm to 1000 μm.
In some embodiments, the density of the ceramic particles is between 3 g/cm3 to 6 g/cm3.
One embodiment of the disclosure provides a method of removing fluoride ion from waste liquid, including: providing a calcium source and a plurality of ceramic particles to a waste liquid containing fluoride ion for forming a plurality of calcium fluoride layers wrapping ceramic particles, wherein the calcium fluoride layers are connected to form a calcium fluoride bulk, and the ceramic particles are embedded in the calcium fluoride bulk, wherein the ceramic particles and the calcium fluoride bulk have a weight ratio of 1:4 to 1:20.
In some embodiments, the calcium source includes calcium chloride, calcium hydroxide, calcium carbonate, or a combination thereof.
In some embodiments, the ceramic particles include oxide of 100 parts by weight of calcium, 50 to 95 parts by weight of iron, 40 to 50 parts by weight of silicon, 2 to 15 parts by weight of magnesium, 2 to 20 parts by weight of aluminum, and 2 to 10 parts by weight of manganese.
In some embodiments, the ceramic particles include a plurality of spinels distributed therein.
In some embodiments, the ceramic particles and the spinels have a weight ratio of 1:0.2 to 1:0.5.
In some embodiments, the ceramic particles have a diameter of 0.1 μm to 1000 μm.
In some embodiments, the method further includes providing a pH adjuster to the waste liquid to adjust the pH value of the waste liquid to 7 to 10.
A detailed description is given in the following embodiments with reference to the accompanying drawings.
The disclosure can be more fully understood by reading the subsequent detailed description and examples with references made to the accompanying drawings, wherein:
In the following detailed description, for purposes of explanation, numerous specific details are set forth in order to provide a thorough understanding of the disclosed embodiments. It will be apparent, however, that one or more embodiments may be practiced without these specific details. In other instances, well-known structures and devices are schematically shown in order to simplify the drawing.
One embodiment of the disclosure provides a method of removing fluoride ion from waste liquid. First, providing a calcium source and a plurality of ceramic particles to a waste liquid containing fluoride ion, thereby forming a plurality of calcium fluoride layers 11 wrapping the ceramic particles 13, as shown in
In some embodiment, the waste liquid is aqueous solution. Alternatively, the waste liquid can be mainly composed of organic solvent, such as alcohol, acetone, and other polar solvent that is used in semiconductor industry and polluted by fluoride ion source (e.g. hydrofluoric acid). In the waste liquid containing fluoride ion, the fluoride ion concentration can be 100 mg/L to 10000 mg/L. If the fluoride ion concentration is too low, calcium fluoride layer cannot grow on the ceramic particles. If the fluoride ion concentration is too high, calcium fluoride layer will grow not only on the ceramic but also on the tank surface. However, the fluoride waste liquid should not be diluted before treatment, which may save water during the treatment. The calcium source should be added to fluoride ion-containing waste liquid, and the calcium source and the waste liquid have a weight ratio of 7:3 to save water. In some embodiments, the calcium source added to the waste liquid can be calcium chloride, calcium hydroxide, calcium carbonate, or a combination thereof.
The ceramic particles may serve as seeds to grow the calcium fluoride layer thereon. In some embodiments, the ceramic particles include oxide of 100 parts by weight of calcium, 50 to 95 parts by weight of iron, 40 to 50 parts by weight of silicon, 2 to 15 parts by weight of magnesium, 2 to 20 parts by weight of aluminum, and 2 to 10 parts by weight of manganese. If the iron ratio is too low, the density of ceramic particles will be lower than 3 g/cm3. If the iron ratio is too high, iron ion could be dissolved into the waste water. If the silicon ratio is too low, the strength of the ceramic powder will be not good enough. If the silicon ratio is too high, the fluoride ion resistance of the ceramic powder will be not enough, and the ceramic powder could be dissolved in the waste water. If the magnesium ratio is too low, the ratio of the spinel will be insufficient. If the magnesium ratio is too high, the expansion rate of the ceramic particles will increases. If the aluminum ratio is too low, the hardness of the ceramic particles will be insufficient. If the aluminum ratio is too high, fluoride ion resistance of the ceramic powder will be not enough, and the ceramic powder could be dissolved in the waste water. If the manganese ratio is too low, the ratio of the spinel will be insufficient and the density of the ceramic powder will be lower than 3 g/cm3. If the manganese ratio is too high, the cost of ceramic particles will increase. For example, calcium source (e.g. calcium carbonate, calcium hydroxide, or calcium oxide), iron source iron nitrate, ferric oxide, or ferrous oxide), silicon source (e.g. silicon oxide, or silica sand), magnesium source (e.g. magnesium carbonate, magnesium oxide, or magnesium acetate), aluminum source (e.g. aluminum nitrate, aluminum hydroxide, or aluminum oxide), and manganese (e.g. manganese nitrate, manganese dioxide, or manganese(III) oxide) of chemical stoichiometry are mixed, and sintered at 1000° C. to 1500° C. for 1.5 hours to 5 hours to obtain the ceramic particles. Alternatively, some raw materials of the elements may simultaneously contain at least two elements, such as calcium silicate (containing silicon and calcium). If the sintering temperature is too low or the sintering period is too short, the ratio of the spinel will be insufficient. If the sintering temperature is too high or the sintering period is too long, the crystal will be too large and the size of the powder will increase, or the ceramic powder will react with crucible and cause pollutant.
As shown in
In some embodiments, the ceramic particles include a plurality of spinels distributed therein. In some embodiments, the ceramic particles and the spinels have a weight ratio of 1:0.2 to 1:0.5. If the ratio of the spinels is too low, the density of the ceramic powder will be low and the fluoride ion resistance of the ceramic powder will be weak. If the ratio of the spinels is too high, the ceramic particles will have higher density as well as its weight. In some embodiments, the ceramic particles have a diameter of 0.1 μm to 1000 μm. If the diameters of the ceramic particles are too small, the thickness of the shell layer will be insufficient, therefore, the water resistance will be lower and result in the expansion of the ceramic particles. If the diameters of the ceramic particles are too large, the reactive surface of the ceramic particles will be too low, and calcium fluoride crystallization rate will be therefore slow. In some embodiments, the density of the ceramic particles 13 is between 3 g/cm3 to 6 g/cm3. If the density of the ceramic particles 13 is too low, the ceramic particles will easily float over the waste liquid, and it will be difficult to crystallize calcium fluoride. If the density of the ceramic particles 13 is too high, the ceramic particles will easily sink to the bottom of the waste liquid, and it will be also difficult to crystallize calcium fluoride.
In some embodiments, a pH adjuster is further provided to the waste liquid to adjust the pH value of the waste liquid to 7 to 10. If the pH value of the waste liquid is too low, the growth rate of calcium fluoride will be too slow. If the pH value of the waste liquid is too high, the calcium fluoride will become porous. In some embodiment, if the calcium source added to the waste liquid is alkaline Ca(OH)2), the step of providing the pH adjuster can be omitted. In addition, when the calcium of the calcium source and the fluoride ion of the waste liquid are reacted to form the calcium fluoride layer, and the acid and alkaline are neutralized, a large heat may be generated. As such, the temperature of the above method of removing fluoride ion in the waste liquid can be controlled (e.g. to 15° C. to 30° C.) by a cooler for safety.
The fluoride ion concentration of the waste liquid can be greatly reduced by the above method. For example, the original waste water may contain a hydrofluoric acid concentration of 100 mg/L to 10000 mg/L, and the treated waste water may contain a hydrofluoric acid concentration lower than 15 mg/L. The treated waste water can be recycled for other application. Moreover, the composite material of the calcium fluoride bulk with ceramic particles embedded therein can be easily dried due to its low water content (e.g. <15%), which can be used in other applications.
Note if only the calcium source is added to the waste liquid containing fluoride ion to form the calcium fluoride, it will form a sludge of the calcium fluoride rather than the calcium fluoride bulk (solid). The sludge is difficult to be collected and dried due to its large amount of water, and the sludge may suspend in the waste liquid and be difficult to remove. In other words, the ceramic powder may efficiently simplify the process of removing fluoride ion in waste liquid.
The above method of removing fluoride ion from waste liquid can be performed in batch-type or continuous-type. For a suitable apparatus of performing the method, the reader may refer to Taiwan Patent No. 310313, Taiwan Patent No. 1449668, or TW patent No. 1591022, or another suitable apparatus disclosed in the art.
Below, exemplary embodiments will be described in detail with reference to accompanying drawings so as to be easily realized by a person having ordinary knowledge in the art. The inventive concept may be embodied in various forms without being limited to the exemplary embodiments set forth herein. Descriptions of well-known parts are omitted for clarity, and like reference numerals refer to like elements throughout.
Calcium carbonate, iron oxide, silicon oxide, magnesium oxide, aluminum oxide, and manganese dioxide were mixed according to chemical stoichiometry, then heated to 1200° C. and sintered for 3 hours to form ceramic cores, which could include an oxide of 100 parts by weight of calcium, 75 parts by weight of iron, 19 parts by weight of silicon, 8 parts by weight of magnesium, 6 parts by weight of aluminum, and 6 parts by weight of manganese. The ceramic cores (particles) were analyzed by XRD and it showed diffraction peaks at 30.1 degrees and 35.4 degrees, as shown in
PH value of hydrofluoric acid-containing waste water (obtained from semiconductor manufacture) was first adjusted to 7.7 with NaOH solution, and the waste water had a fluoride ion concentration of 800 mg/L and a volume of 100 mL (determined by fluoride ion meter). 40 mL of CaCl2 solution (3000 mg/L), 30 g of the ceramic particles were added into the waste water and stirred at room temperature for 24 hours. The fluoride ion in the waste water and the calcium ions were bonded to form a CaF2 layer to wrap the ceramic powders, and the CaF2 layer was connected to form a CaF2 bulk, and the ceramic particles were embedded in the CaF2 bulk. The CaF2 bulk was a dense solid that was easily collected from the waste water. The waste water after the above treatment had a fluoride ion concentration of 6.4 mg/L (determined by fluoride ion meter). Accordingly, the ceramic particles could efficiently remove fluoride ion in the use water.
Calcium oxide, ferrous oxide, silicon oxide, magnesium acetate, aluminum hydroxide, and manganese acetate were mixed according to chemical stoichiometry, then heated to 1100° C. and sintered for 5 hours to form ceramic cores, which could include an oxide of 100 parts by weight of calcium, 81 parts by weight of iron, 19 parts by weight of silicon, 10 parts by weight of magnesium, 7 parts by weight of aluminum, and 7 parts by weight of manganese. The ceramic cores (particles) were analyzed by XRD and it showed diffraction peaks at 30.1 degrees and 35.4 degrees, which meant that the ceramic cores had spinets therein. The ceramic cores had a diameter of 1 μm to 50 μm.
PH value of hydrofluoric acid-containing waste water (obtained from semiconductor manufacture) was first adjusted to 7.7 with NaOH solution, and the waste water had a fluoride ion concentration of 800 mg/L and a volume of 100 mL (determined by fluoride ion meter). 40 mL of CaCl2 solution (3000 mg/L), 30 g of the ceramic particles were added into the waste water and stirred at room temperature for 24 hours. The fluoride ion in the waste water and the calcium ions were bonded to form a CaF2 layer to wrap the ceramic powders, and the CaF2 layer was connected to form a CaF2 bulk, and the ceramic particles were embedded in the CaF2 bulk. The CaF2 bulk was a dense solid that was easily collected from the waste water. The waste water after the above treatment had a fluoride ion concentration of 5.9 mg/L (determined by fluoride ion meter). Accordingly, the ceramic particles could efficiently remove fluoride ion in the waste water.
Calcium carbonate, iron powder, silicon oxide, magnesium hydroxide, aluminum nitrate, and manganic oxide were mixed according to chemical stoichiometry, then heated to 1300° C. and sintered for 1 hour to form ceramic cores, which could include an oxide of 100 parts by weight of calcium, 95 parts by weight of iron, 20 parts by weight of silicon, 8 parts by weight of magnesium, 19 parts by weight of aluminum, and 6 parts by weight of manganese. The ceramic cores (particles) were analyzed by XRD and it showed diffraction peaks at 30.1 degrees and 35.4 degrees, which meant that the ceramic cores had spinels therein. The ceramic cores had a diameter of 0.8 μm to 30 μm.
PH value of hydrofluoric acid-containing waste water (obtained from semiconductor manufacture) was first adjusted to 7.7 by adding NaOH solution, and the waste water had a fluoride ion concentration of 800 mg/L and a volume of 100 mL (determined by fluoride ion meter). 40 mL of CaCl2 solution (3000 mg/L), 30 g of the ceramic particles were added into the waste water and stirred at room temperature for 24 hours. The fluoride ion in the waste water and the calcium ions were bonded to form a CaF2 layer to wrap the ceramic powders, and the CaF2 layer was connected to form a CaF2 bulk, and the ceramic particles were embedded in the CaF2 bulk. The CaF2 bulk was a dense solid that was easily collected from the waste water. The waste water after the above treatment had a fluoride ion concentration of 6.2 mg/L (determined by fluoride ion meter). Accordingly, the ceramic particles could efficiently remove fluoride ion in the waste water.
PH value of hydrofluoric acid-containing waste water (obtained from semiconductor manufacture) was first adjusted to 7.7 with NaOH solution, and the waste water had a fluoride ion concentration of 800 mg/L and a volume of 100 mL (determined by fluoride ion meter). 40 mL of CaCl2 solution (3000 mg/L), 30 g of the 325 mesh silicon dioxide (Sigma-Aldrich 342890) were added into the waste water and stirred at room temperature for 24 hours. The silicon dioxide particles were dissolved in the waste water. As such, the fluoride ion in the waste water and the calcium ions were bonded to form CaF2 sludge. The CaF2 sludge was difficult to be collected from the waste water. For example, the CaF2 sludge contains at least 70 wt % of water, it consumed additional time and energy to dry the CaF2 sludge. In addition, the CaF2 sludge would remain (e.g. suspend) in the waste water, which is difficult to remove. Accordingly, the silicon oxide particles were not suitable to remove fluoride ion in the waste water.
PH value of hydrofluoric acid-containing waste water (obtained from semiconductor manufacture) was first adjusted to 7.7 by adding NaOH solution and the waste water had a fluoride ion concentration of 800 mg/L and a volume of 100 mL (determined by fluoride ion meter). 40 mL of CaCl2 solution (3000 mg/L), 30 g of the 325 mesh CaF2 (Sigma-Aldrich 01905) were added into the waste water and stirred at room temperature for 24 hours. The fluoride ion in the waste water and the calcium ions were bonded to form a CaF2 layer to wrap the CaF2 particles, and the CaF2 layer was connected to form CaF2 bulk, and the CaF2 particles were embedded in the CaF2 bulk. The CaF2 bulk was a dense solid that was easily collected from the waste water. The waste water after the above treatment had a fluoride ion concentration of 6 mg/L (determined by fluoride ion meter). Although the CaF2 particles could efficiently remove fluoride ion in the waste water, the cost of CaF2 is much higher than that of the ceramic particles. For example, the CaF2 costs 10 USD/kg, and the ceramic particles costs 1 USD/kg.
The compositions of Example 1, Example 2, Example 3, Comparative Example 1 and Comparative Example 2 were summarized as Table 1 to make it easy to understand this disclosure.
It will be apparent to those skilled in the art that various modifications and variations can be made to the disclosed methods and materials. It is intended that the specification and examples he considered as exemplary only, with the true scope of the disclosure being indicated by the following claims and their equivalents.