Patent Application
20140087325
The present invention generally relates to a composite material which is used for medical devices such as stents, guide wires, embolization coils, inferior vena cava filters, and wires for orthodontics, and particularly relates to a composite material for medical devices utilizing a superelastic shape memory alloy as a matrix and a method of manufacturing the same.
Various kinds of alloys have been used as the material for medical devices such as stents and guide wires. For example, Japanese Application Publication No. 2003-325655 discloses a stent consisting of NiTi shape memory alloys and Japanese Application Publication No. 9-182799 discloses a guide wire consisting of NiTi-based alloys, CuZnAl-based alloys, CuAlNi-based alloys, or the like.
NiTi-based alloys, FeMnSi-based alloys, CuAlNi-based alloys, CuZnAl-based alloys, or the like are generally called a shape memory alloy, and among these, there is an alloy showing superelasticity at human body temperature (around 37° C.). The superelastic shape memory alloys have a crystal structure in which stress-induced type martensitic transformation is generated and have characteristics of returning to their original shape after releasing the stress. The term, “superelasticity” herein means that even if the material is deformed (bent, stretched, compressed, and twisted) at service temperature to the region in which ordinary metals undergo plastic deformation, releasing the deformation stress results in recovery to nearly the original shape before deformation without heating. The superelastic shape memory alloys having such characteristics can be used with advantage in stents, guide wires, or the like which are used in the living body.
Since the superelastic shape memory alloys are generally a “soft” alloy, there were some cases where the stress value in the plateau region (the region in which the stress value shows nearly constant value with respect to an increase of strain in the stress-strain curve) is insufficient depending on the application. In particular, in medical devices such as stents and guide wires which are arranged or used in the living body, more reduction in size is desired. However, when the stress value in the plateau region (the strength) is insufficient, it is difficult to promote a reduction in size such as a reduction in wall thickness and a reduction in diameter.
According to one aspect disclosed here, a medical device composite material comprises a superelastic shape memory alloy constituting a matrix; and a metal oxide dispersed in the matrix.
According to another aspect, a medical device comprises: one of a stent, a guide wire, an embolization coil, an inferior vena cava filter, and an orthodontics wire made of a composite material comprising a superelastic shape memory alloy matrix in which a metal oxide is dispersed.
The medical device composite material exhibits improved stress value in the plateau region. A description will be set forth below of various Examples implementing the composite material disclosed here. Generally, speaking, the stress value in the plateau region is improved by containing the proper dose of the metal oxide in the matrix.
To contain the proper dose of the metal oxide in the matrix, the composite material for medical devices is preferably obtained by sintering to be subjected to extrusion processing after the superelastic shape memory alloy powder and the metal oxide particles are mixed. If the metal oxide particles are added into the dissolved superelastic shape memory alloys, it is difficult to maintain the proper dose of the metal oxide in the matrix. In contrast, if the metal oxide particles are added into and mixed with the superelastic shape memory alloy powder, it is possible to maintain the proper dose of the metal oxide in the matrix.
The additive amount of the metal oxide particles to the superelastic shape memory alloy powder is preferably from 0.10% by volume to 1.0% by volume. When the additive amount is less than 0.10% by volume, an improvement of the stress value in the plateau region is insufficient. When the additive amount is over 1.0% by volume, while the stress value in the plateau region is improved, it does not become appropriate for the application as medical devices used in the living body since a decrease in stretching becomes prominent.
Furthermore, “the additive amount of the metal oxide to the superelastic shape memory alloy powder” defined by % by volume is part by volume of the additive amount of the metal oxide to 100 part by volume of the superelastic shape memory alloy powder.
The superelastic shape memory alloy powder is, for example, one kind of alloy powder selected from a group consisting of TiNi-based alloy powder, Cu-based alloy powder, Fe-based alloy powder, and Ti-based alloy powder. As a material for medical devices such as stents and guide wires, TiNi-based alloys which have excellent biocompatibility are particularly preferable. TiNi-based alloys have excellent corrosion resistance in the blood, and there is no risk that the alloy constituents are eluted into the blood since the surface is stable. The metal oxide particles are, for example, one kind of oxide particles selected from a group consisting of TiO2, Al2O3, CeO2, MgO, CaO and ZrO2.
In a preferred embodiment, the superelastic shape memory alloy powder is TiNi-based alloy powder, and the metal oxide particles and the additive amount thereof are any one of 0.10% by volume to 1.0% by volume of TiO2 and 0.1% by volume to 1.0% by volume of Al2O3.
Another aspect involves a method of manufacturing a medical device composite material used to fabricate medical devices. The method comprises: producing an ingot consisting of a superelastic shape memory alloy using a dissolution method; crushing or cutting the superelastic shape memory alloy ingot to produce a superelastic shape memory alloy powder; mixing the superelastic shape memory alloy powder and metal oxide particles; and sintering a mixture of the superelastic shape memory alloy powder and the metal oxide particles to be subjected to extrusion processing.
In the method described above, it is preferable that the superelastic shape memory alloys be TiNi-based alloys, and the metal oxide and the additive amount thereof are any one of 0.10% by volume to 1.0% by volume of TiO2 and 0.1% by volume to 1.0% by volume of Al2O3.
According to the material and method disclosed here, in a composite material for medical devices utilizing a superelastic shape memory alloy as a matrix, it is possible to improve the stress value in the plateau region in the stress-strain curve by containing a metal oxide which is dispersed in the matrix. As a result, it is possible to realize a reduction in wall thickness and a reduction in diameter, of medical devices such as stents and guide wires.
A composite material disclosed here is used for medical devices such as stents, guide wires, embolization coils, inferior vena cava filters, and wires for orthodontics, and contains a metal oxide which is dispersed in the matrix, utilizing a superelastic shape memory alloy as a matrix.
The superelastic shape memory alloys have the alloy constituents which can exhibit superelastic shape memory characteristics, and for example, TiNi-based alloys, Cu-based alloys, Fe-based alloys, Ti-based alloys, and the like can be included. In a case of TiNi-based alloys, TiNi-based alloys contain 43% by mass to 57% by mass of Ni and the residue consists of Ti and unavoidable impurities. A small amount of other metals, for example, cobalt, iron, palladium, platinum, boron, aluminum, silicon, vanadium, niobium, copper, or the like may be added to such TiNi-based alloys.
As Cu-based alloys, for example, CuAlNi alloys, CuZn alloys, CuZnAl alloys, and the like can be included. As Fe-based alloys, for example, FeNi alloys, FeMnSi alloys, FePd alloys, FePt alloys, and the like can be included. As Ti-based alloys, for example, TiNb alloys, TiMo alloys, and the like can be included.
Among the various kinds of the superelastic shape memory alloys described above, the superelastic shape memory alloys which are particularly appropriate as a composite material for medical devices are TiNi-based alloys in which the strain recovery is large and which have excellent biocompatibility. An example of TiNi-based alloys is TiNi-based alloys, for example, in which TiNi-based alloys contain 54.5% by mass to 57% by mass of Ni and the residue consists of Ti and unavoidable impurities. As unavoidable impurities, 0.050% by mass or less of Co, 0.010% by mass or less of Cu, 0.010% by mass or less of Cr, 0.005% by mass or less of H, 0.050% by mass or less of Fe, or 0.050% by mass or less of Nb may be contained.
To improve the stress value in the plateau region in the stress-strain curve, it is important to disperse the metal oxide in the matrix of the superelastic shape memory alloys. Examples of the metal oxide include TiO2, Al2O3, CeO2, MgO, CaO and ZrO2, and the like. A preferred metal oxide is any one of TiO2 and Al2O3.
The proper dose of the metal oxide should be contained in the matrix, but it has been found that if the metal oxide particles such as TiO2 and Al2O3 are added into the dissolved superelastic shape memory alloy, it is difficult to maintain the proper dose of the metal oxide in the matrix.
The composite material disclosed here is manufactured through the following steps. The following description will be set forth using as an example a case where the superelastic shape memory alloys are TiNi-based alloys.
An ingot consisting of TiNi-based alloys is produced by a dissolution method. As an other method, it is considered that a sintered body of TiNi-based alloy is obtained by a powder metallurgy method in which Ti powder and Ni powder are mixed to be sintered.
TiNi-based alloy powder is obtained by crushing or cutting the TiNi-based alloy ingot.
Metal oxide particles such as TiO2 and Al2O3 are added to TiNi-based alloy powder to mix so that metal oxide particles are uniformly dispersed. The additive amount of metal oxide particles to TiNi-based alloy powder is preferably 0.10% by volume to 1.0% by volume. If the additive amount is less than 0.10% by volume, an improvement of the stress value in the plateau region is insufficient in the stress-strain curve in the composite material which is finally obtained. When the additive amount is over 1.0% by volume, while the stress value in the plateau region is improved, it is not appropriate for the application as medical devices used in the living body, since a decrease in stretching becomes prominent. Particularly, in a case of stents being arranged at a bending part of the blood vessel, the characteristic of stretching becomes an important factor, since a cyclic bending load acts.
The mixture of the TiNi-based alloy powder and the metal oxide particles is sintered to be subjected to extrusion processing. Sintering is preferably performed in a vacuum atmosphere or an inert gas atmosphere, and more preferably performed in a vacuum atmosphere. The sintering temperature is not particularly limited. However, by way of example, 700° C. to 1,200° C. is preferable, and 800° C. to 1,100° C. is more preferable. In addition, extrusion processing is preferably hot extrusion processing.
After steps described above, the composite material for medical devices according to the disclosure here is obtained. In the composite material which is finally obtained, for example, by dispersing Al2O3 as particles in the matrix of TiNi-based alloys, the strength of the composite material is enhanced. In this manner, if Al2O3 particles are added, it is possible to improve the stress value in the plateau region of the composite material which is finally obtained, by strengthening particle dispersion. However, there is a possibility that a particle dispersion strengthening type composite material may not be appropriate for applications in which a cyclic bending load acts. For example, in a case of manufacturing stents which are to be being arranged at a bending part of the blood vessel using a particle dispersion type composite material, the presence of particles dispersed in the matrix of a device which is to be subjected to cyclic loading is likely to be the starting point of fatigue failure.
In a case of the application described above, it is preferable that TiO2 particles be used as metal oxide particles. In a case where metal oxide particles which are added are TiO2, TiO2 are not finally present as particles but by decomposing, oxygen is dissolved in a parent phase to provide solid solution strengthening and the strength of the composite material for medical devices is improved. Particularly, by adding Tio2 particles not by a melting method (a dissolution method), but by a powder metallurgy method, it is possible to dissolve more oxygen content. Since oxygen which is dissolved does not become the starting point of fatigue failure, an oxygen solid solution strengthening type composite material is appropriate for the application in which a cyclic load is applied.
As a metal oxide where the solid solution strengthening of oxygen can be expected, CeO2, MgO, CaO, ZrO2, and the like in which it is considered that it is more difficult to decompose than TiO2, from an oxide standard production free energy diagram, can be included. In these metal oxides, without oxygen which has been decomposed once reacting to a metal element to generate a metal oxide again, oxygen is dissolved in a parent phase.
The applications of the composite material of the invention are medical devices such as stents, guide wires, embolization coils, inferior vena cava filters, and wires for orthodontics. While being described in Examples later, in a case of TiNi-based alloy composite material to which 0.5% by volume (0.33 wt %) of TiO2 particles are added, the stress value (the strength) in the plateau region increases from 600 MPa (no addition of TiO2) to 800 MPa. Therefore, considering an application for stents having a conventional material thickness (wall thickness) of the material forming the stent of 0.2 mm, the material thickness can be reduced to approximately three-quarter (about 1.5 mm) if the same degree of the strength is maintained. One benefit of reducing the material thickness is that the amount of the used alloys is decreased and as a result, it is possible to reduce elution of alloy constituents since it is possible to support a film of the blood vessel by a thin beam. In addition, when delivering to the blood vessel, it is possible to fold stents into a smaller diameter.
Considering that the stress value (the strength) in the plateau region increases form 600 MPa to 800 MPa, considering an application for guide wires, the outer diameter of 0.50 mm of the conventional wires can be reduced to 0.45 mm if the same degree of strength is maintained. One benefit of this reduction in diameter is that it is possible to achieve the reduction in diameter of the inner and outer diameter of other medical devices which can be laid along wires.
The following mixtures were prepared.
Sample 1: TiNi-based alloy powder (Comparative Example)
Sample 2: 0.5% by volume (0.33 wt %) of TiO2 particles are added to TiNi-based alloy powder (Example of the invention)
Sample 3: 1.0% by volume (0.66 wt %) of TiO2 particles are added to TiNi-based alloy powder (Example of the invention)
Sample 4: 0.2% by volume of Al2O3 particles are added to TiNi-based alloy powder (Example of the invention)
Sample 5: 1.0% by volume of Al2O3 particles are added to TiNi-based alloy powder (Example of the invention)
Sample 6: 0.15% by volume (0.10 wt %) of TiO2 particles are added to TiNi-based alloy powder (Example of the invention)
Sample 7: 0.38% by volume (0.25 wt %) of TiO2 particles are added to TiNi-based alloy powder (Example of the invention)
Each sample described above was sintered according to the following conditions to obtain a sintered body.
Temperature: 900° C.
Retention time: 30 minutes
Atmosphere: Vacuum
Pressure: 40 MPa
Rate of temperature elevation: 20° C./min
The sintered body obtained was subjected to hot extrusion processing according to the following conditions to obtain an extruded product.
Preheating temperature: 1,050° C.
Pre-overheating time: 10 minutes
Extrusion ratio: 6
Extrusion ram speed: 6 mm/sec
Tensile tests of the extruded products of Samples 1 to 7 were performed at ambient temperature under the following conditions, with tensile tests conducted on two products of each of the Samples 1 to 5, and on one product of each of Samples 6 and 7.
Shape of test piece: Round bar
Diameter of test piece: 3.5 mm
Length of test piece: 20 mm
Tension speed: Strain rate 5×10−4s−1
The graph illustrated in
Considering medical device applications such as stents and guide wires, since deteriorating elongation characteristics are typically not very much desired, the preferred upper limit value of the additive amount of TiO2 is 1.0% by volume.
The stress value of Sample 1 to which TiO2 was not added in the plateau region is about 600 MPa, whereas the stress value of Sample 2 to which 0.5% by volume (0.33 wt %) of TiO2 was added in the plateau region is about 800 MPa. Regarding elongation characteristics, a big difference between Sample 1 and Sample 2 is not recognized.
From the graph illustrated in
It is discovered that the preferred additive amount of TiO2 is from approximately 0.15% by volume (0.10 wt %) to 0.5% by volume (0.33 wt %), from the viewpoint of improving the stress value in the plateau region without deteriorating elongation characteristics. Considering that the stress value in the plateau region increases by about 120 MPa when the additive amount of TiO2 is 0.15% by volume (0.10 wt %), an increase in the stress value by about 100 MPa is expected even if 0.10% by volume is added. Therefore, the preferred lower limit value of the additive amount of TiO2 is 0.10% by volume.
The graph illustrated in
Considering medical device applications, since deteriorating elongation characteristics are typically not very much desired, the preferred upper limit value of the additive amount of Al2O3 is 1.0% by volume.
The stress value of Sample 1 to which Al2O3 was not added in the plateau region is about 600 MPa, whereas the stress value of Sample 4 to which 0.2% by volume of Al2O3 was added in the plateau region is about 750 MPa. Regarding elongation characteristics, a big difference between Sample 1 and Sample 4 is not recognized. It is thus discovered that the preferred additive amount of Al2O3 is approximately 0.2% by volume, from the viewpoint of improving the stress value in the plateau region without deteriorating elongation characteristics. Considering that the stress value in the plateau region increases by about 150 MPa when the additive amount of Al2O3 is 0.2% by volume, an increase in the stress value by about 100 MPa is expected even 0.1% by volume is added. Therefore, the preferred lower limit value of Al2O3 is 0.1% by volume.
Using a tensile test in which the stress is released after imparting a constant strain by stretching the extruded products of Sample 2, Sample 3, Sample 6 and Sample 7 to form a cycle, a hysteresis test in which three cycles are performed by changing the strain imparted was performed according to the following conditions. The strain amount of Sample 2 is set to 3% at cycle 1, 7% at cycle 2, and 15% at cycle 3. The strain amount of Sample 3 is set to 3% at cycle 1, 5% at cycle 2, and 10% at cycle 3. The strain amount of Sample 6 and Sample 7 is set to 4% at cycle 1, 10% at cycle 2, and 15% at cycle 3.
Shape of test piece: Round bar
Diameter of test piece: 3.5 mm
Length of test piece: 20 mm
Tension speed: Strain rate 5×10−4s−1
The result of Sample 2 is illustrated in
The composite material disclosed here has useful application as a material for medical devices such as stents and guide wires.
The detailed description above describes a composite material having useful application for medical devices. The invention is not limited, however, to the precise embodiment and variations described. Various changes, modifications and equivalents can be employed by one skilled in the art without departing from the spirit and scope of the invention as defined in the accompanying claims. It is expressly intended that all such changes, modifications and equivalents which fall within the scope of the claims are embraced by the claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2011-118434 | May 2011 | JP | national |
This application is a continuation of International Application No. PCT/JP2012/061712 filed on May 8, 2012, and claims priority to Japanese Application No. 2011-118434 filed on May 26, 2011, the entire content of both of which is incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/JP2012/061712 | May 2012 | US |
| Child | 14088937 | US |