The invention relates to a composite material for producing an acoustic membrane, a process for producing an acoustic membrane from the composite material as well as a method for preparing such a composite material.
Electromagnetic transducers are used for various types of loudspeakers and microphones, in particular also for miniature loudspeakers as applied in mobile phones, notebooks, tablets, gaming consoles, earphones, hands-free speakerphones, modern televisions and also in the automotive sector.
A general market trend shows that the structural shape of such loudspeakers does not allow a uniform design and demands great flexibility from manufacturers. In addition, smallest structural shapes with maximum performance are often demanded. Nevertheless, highest requirements are placed on the acoustic quality. All those requirements impose tremendous technological demands on the membrane, which functions as the centrepiece of a loudspeaker or microphone, respectively.
Silicone materials are preferred materials for acoustic membranes because of their desirable mechanical properties.
EP 2 268 058 discloses the use of a silicone elastomer in a membrane for a dynamic speaker, for example liquid silicone rubber (LSR), room temperature vulcanization rubber (RTV), and high temperature vulcanization rubber (HTV). The described membrane has a thickness of less than 0.3 mm. It may be produced by injection molding; said method is very preferred over deep drawing in this publication. However, injection molding is mainly suitable for producing large numbers of uniform membranes as this method does not easily allow design changes and requires a highest level of precision.
Moreover, elastic silicones were described to be desirable as damping layer or gluing layer in multi-layered membranes. For example in WO 2014/135620, silicones are suggested as material for a glue layer in a five-layered arrangement. Therein, the method suggested for producing the silicone layer is multi-roll coating, which may be considered as cumbersome.
WO 2016/091542 discloses the use of silicone based adhesives for a gluing layer as an inner layer in the context of multi-layered acoustic membranes. Therein, the adhesion material is preferably a pressure sensitive adhesive (PSA), which is a polymer material being sustainably sticky and permanently adhesive at application temperature (e.g. room temperature) and which adheres to various surfaces upon contact, particular adheres immediately. These properties, referred to as having a certain tack, are not present in standard silicone rubbers. US 2015/240141 discloses specific silicone PSA materials for acoustic membranes.
The thermal stability of the silicone elastomer is considered as an advantage in the application e.g. due to temperature variations occurring during service of the acoustic device. However, the thermal stability also may be considered as disadvantage for the production of multi-layer membranes with silicone materials. Injection molding is useful for producing a high number of pieces with identical shape and mono-layer arrangement, but is not easily adaptable for various shapes and for multi-layered membranes. Multi-roll coating may be applied to generate a multi-layer membrane with a silicone rubber layer. However, multi-layer membranes with a layer of silicone rubber are not preferred for subsequent thermoforming and may be exposed to high shear forces when those membranes are brought into a specific shape.
Thus, there is a need to provide alternative, more practicable ways for producing acoustic membranes with various shapes comprising elastomeric silicones.
The present invention provides a composite material for producing an acoustic membrane comprising
Such a composite material provides at least two layers forming a multi-layer film or foil. The support layer serves for support and protection of the uncured silicone or at least partially uncured silicone material (resin). In this arrangement, wherein the silicone layer is located adjacent to the support layer, it becomes possible to handle the (partially) uncured silicone in the form of a film layer of defined thickness. The silicone layer is provided in a state wherein it comprises at least a fraction of uncured silicone, i.e. the silicone layer is cross-linkable. The support layer adjacent to the silicone layer protects the underlying silicone layer against potential damages and allows for handling the composite material during packaging, e.g. winding, shipping, and processing, e.g. cutting. Due to the uncured character of the silicone rubber in the silicone layer, the composite allows the in situ curing of the silicone material during production of an acoustic membrane by thermal treatment or UV-light activation. Thus, the composite material allows to generate an acoustic membrane for an acoustic device from a pre-formed layered arrangement with predefined thickness.
This allows the production of an acoustic membrane with a specific three-dimensional form e.g. the formation of curvatures such as a torus region. Moreover, the composite material may include further layers that may become integral part of a multi-layered acoustic membrane. The composite material provides a valuable starting material for producing an acoustic membrane of various shapes and arrangements, wherein the silicone rubber maybe brought into shape upon curing the silicone rubber by e.g. application of heat or UV-light.
In the following, the term “partially uncured silicone rubber” is used both for a silicone rubber which is partially uncured as well as for a silicone rubber which is not cured at all.
The partially uncured silicone rubber that may form the silicone film preferably is an addition curing silicone rubber. The partially uncured silicone rubber may be provided as one-component or two-component system. Preferably, the partially uncured silicone rubber is a multi-component silicone rubber. In one embodiment, the silicone components comprise hydrogen-siloxane groups (Si—H) as well as vinyl groups (e.g. Si—CH═CH2). The partially uncured silicone rubber preferably includes a catalyst for addition curing. For example the catalyst may be platinum which may be thermally activated for cross-linking (i.e. curing) the silicone rubber. The silicone may be a high-temperature vulcanizing (HTV) silicone rubber. Generally, platinum-catalyzed, addition-curing silicone rubber may be provided as liquid silicone rubber or as solid silicone rubber. For the present invention solid silicone rubbers are preferred. Alternatively, peroxide curing can be temperature controlled and also specific catalysts being sensitive to ultra-violet (UV) light are available for addition curing silicone rubbers.
Exemplarily, a schematic mechanism of cross-linking of a platinum cured HTV silicone resin, as it may be comprised in a silicone layer of a composite material according to the invention, is shown in the following reaction scheme:
In this scheme, terminal methyl groups are indicated with CH3, whereas the unspecified bonds indicate that the polymeric starting material is continued and that the shown chemical structure only represents a substructure of a silicone polymer.
Preferably, a high temperature vulcanizing silicone rubber as used according to the invention has a vulcanizing temperature of above 50° C., more preferably between 70° C. and 200° C., for example 130° C. The vulcanizing temperature may also be understood as a synonym to the temperature at which a curing process may be completed.
An uncured or partially uncured silicone rubber according to the invention is characterized in that it has a substantial fraction of reactive groups which allow cross-linking. In one embodiment the silicone layer comprising the partially uncured silicone rubber may also comprise a fraction of already cured silicone rubber. This may be achieved in that the uncured silicone rubber is provided in a partially cured state. The partially uncured silicone rubber is a uniform mass and comprises reactive groups as well as a fraction that is already cured.
Preferably, the partially uncured silicone rubber comprises a substantial fraction, e.g. above 50%, preferably above 70%, more preferably above 80%, of reactive groups (e.g. vinyl groups and/or Si—H groups) in relation to the completely uncured silicone rubber. Thus, the silicone layer may comprise an uncured silicone rubber or a partially uncured silicone rubber, preferably a largely uncured silicone rubber. The presence of reactive groups, i.e. the degree of uncured character of the silicone rubber, may be characterized by investigation of relative solvent resistance. Relative solvent resistance may be easily determined by a solvent rub resistance test. The test is inspired by the standard ASTM D4752 and determines the maximum number of rubs with cheesecloth soaked with a solvent until failure or breakthrough of the film occurs. Preferably, the test is performed with an aprotic solvent, e.g. toluene, cyclohexane, n-heptane, low boiling spirits fraction or a mixture thereof, preferably toluene.
In order to quantify the degree of curing, the solvent resistance of a test object is compared with a reference sample, wherein the reference sample comprises a comparable silicone layer in fully cured state, i.e. after heating the silicone layer to a temperature well above the vulcanizing temperature; for example after heating to above 130° C.
Thus, in one embodiment, the silicone layer comprising a partially uncured silicone layer has a relative solvent resistance of below 80%, preferably below 50%, wherein the relative solvent resistance is determined by a solvent rub test and defined by A/B, wherein A is the maximum number of rubs until breakthrough or failure of the investigated silicone layer, and wherein B is a reference value of the maximum number of rubs until failure of the reference sample.
In the present invention, the uncured silicone rubber after curing results in a silicone rubber having essentially no tack, wherein having a tack is understood as previously defined. Accordingly, the resulting cured silicone rubber, for example the reference sample mentioned above, shows no stickiness. With other words, the uncured silicone rubber is selected such that it does not form a pressure sensitive adhesive (PSA).
The partially uncured silicone rubber may also be characterized by the ultimate tensile strength (UTS) of the material, as the UTS of the partially uncured silicone rubber is above the UTS of the completely uncured silicone rubber and below the UTS of the cured silicone rubber. Thus, the partially uncured silicone rubber allows the silicone layer to be less fragile. Partial curing of the silicone rubber may be achieved during preparation of a composite material according to the invention (s. below).
The silicone film may additionally comprise an aprotic solvent. The aprotic solvent may be selected out the group consisting of toluene, cyclohexane, n-heptane, low boiling spirits fraction and a mixture thereof. Such aprotic solvents may be used to provide the components of the uncured silicone rubber as solution or dispersion. This allows the preparation of a fluid which enables the formation of uniform, thin layers of the uncured silicone, e.g. for roll-coating or curtain coating. Thus, in one embodiment the silicone layer may be formed by the component(s) of the silicone rubber, the catalyst and the aprotic solvent. However, the aprotic solvent preferably is removed from the silicone layer, so that the silicone layer essentially consists of the components of the silicone rubber, the catalyst and only residual fraction of solvent.
Moreover, in a preferred embodiment, the silicone layer may be provided without the use of a solvent. In these cases, the silicone layer may consist of the cross-linkable components of the silicone rubber and the catalyst, optionally without any further elements. Embodiments without any solvent may be provided in that a partially uncured silicone is shaped by calendering or extrusion (s. below). In these embodiments the silicone layer comprising a partially uncured silicone has a viscosity of above 0.001 MPa*s preferably above 0.01 MPa*s, wherein the viscosity is measured at room temperature and with a shear rate of about 1 Hz. The viscosity of the partially uncured silicone may be determined for example according to DIN EN ISO 2884-1.
Furthermore, the silicone layer may comprise polymer fibers selected from of the group consisting of PAEK (polyaryletherketone), e.g. PEEK (polyetheretherketone), PA (polyamide), PET (polyethylene terephthalate), PEN (polyethylene naphthalate), preferably PEEK. These fibers may be mixed into the uncured silicone during manufacturing of the composite material and result in reinforcement of the acoustic membrane.
According to one embodiment of the invention the silicone layer has a thickness of from 10 μm to 1000 μm or from 10 μm to 500 μm. In a further embodiment, the silicone layer has a thickness of from 10 μm to 300 μm, preferably from 20 μm to 200 μm, more preferably from 30 μm to 100 μm.
It is an advantage of the present invention that such a thin layer comprising uncured silicone may be provided. Consequently, the composite material according the invention allows for production of an acoustic membrane with a layer of cured silicone rubber in the desired dimensions of below 1000 μm, preferably below 500 μm or more preferably below 300 μm, such as around 30 μm.
Thin layers are especially useful when the acoustic membrane is formed by multiple layers of different materials. Different multi-layer arrangements for acoustic membranes have been described previously. Various arrangements may be produced from the composite material according to the invention. The composite material according to the invention comprises at least two layers, however multiple-layers may be preferred and various layer arrangements for composite materials according to the invention are depicted in
In general, two different embodiments of the composite material may be distinguished: the support layer may be either a release layer or a structure layer.
In each of the above embodiments the at least one support layer should be sufficiently stable, i.e. self-supported while still providing enough flexibility that the composite material may be rolled-up. The support layer may be characterized in that it has a higher ultimate tensile strength than the silicone layer comprising a partially cured silicone layer. The desired mechanical properties of a material suitable for a support layer may be determined following DIN EN ISO 527-1, wherein the obtained stress-strain diagram allows to determine tensile strength as well as Young's modulus. Young's modulus may be considered relevant to characterize a suitable material for a support layer. Preferably, the support layer comprises or consists of a material having a Young's modulus above 3 MPa. Preferably, the support layer has a Young's modulus above 3 MPa.
The composite material according to the invention has two outer layers and it is preferred that at least one of the outer layers is a support layer.
Preferably, the support layer is a release layer. A support layer being a release layer must be an outer layer which is removable without damaging the partially uncured silicone rubber layer. The support layer being a release layer preferably is removed before cross-linking of the silicone rubber i.e. before forming an acoustic membrane. Said release layer should be easily detachable from the remaining composite material, e.g. peeled off from the silicone layer comprising a partially uncured silicone rubber. Upon removal the composite material is converted to a precursor defined as the composite material minus the release layer. Thus, a release layer may be characterized in that a) the release layer is arranged as outer layer in a composite material according to the invention and b) the force for peeling off the release layer is lower than the lowest internal strength of the remaining material. For example the needed peel strength should be lower than the ultimate tensile strength of the partially uncured silicone layer, because this likely is the most vulnerable part of the remaining material.
Preferred materials for the support layer being a release layer may be selected by economic factors and the ability to be easily removed from the silicone layer. In general, any film or flat structure of various materials with the desired properties including polymers, biopolymers, or even inorganic materials might be suitable as a release layer. For example, suitable materials comprised in the release layer can be a polyethylene terephthalate (PET) film or a paper. Preferably the release layer is provided with surface modification e.g. by coating or impregnation, e.g. siliconised or olefin-coated, said surface modification may be present on only one or both sides, and a both-sided modification may be symmetric (i.e. the same on both surfaces) or differentiated for both sides. A differentiated modification means that the two surfaces of the layer differ from each other in their release properties. Suitable release layers may comprise a material selected from the group consisting of PET film with one-sided siliconization, PET film with symmetric siliconization, PET film with differentiated siliconization on both sides, paper with one-sided olefin coating, paper with symmetric olefin coating, and paper with differentiated olefin coating on both sides.
Preferably the release layer may have a thickness in the same range as the silicone layer, i.e. from 10 μm to 1000 μm, preferably from 10 μm to 500 μm or more preferably from 10 μm to 300 μm. For example a PET film may have a thickness of 50 μm or a release liner paper a thickness of 100 μm.
Alternatively, the support layer of the composite material is a structure layer. In contrast to the release layer, a structure layer is not removable from the composite material without damaging the silicone layer comprising partially uncured silicone rubber. Thus, it becomes integral part of the acoustic membrane. The support layer being a structure layer should still have the desired higher mechanical stability than the silicone layer in order to allow protection. Exemplarily, a structure layer may comprise a material selected from the group consisting of a polymeric film or a fabric, i.e. a non-woven fabric or a woven fabric. Preferably, the structure layer comprises a material that has been used in the preparation of acoustic membranes. For example thermoplastic materials, elastomers, fabrics such as woven fabrics or non-woven fabrics (e.g. fleece).
On the other side it is preferred that a structure layer provides enough flexibility/formability during further processing to an acoustic membrane, so that various shapes may be obtained without introducing relevant shear forces. Thermoplastic materials have the advantage that during production of an acoustic membrane by means of thermoforming the structure layer may be shaped while the silicone layer is cured by heat.
It is preferred that a structure layer comprises a thermoplastic material, such as a material selected from the group consisting of PAEK (polyaryletherketone), e.g. PEEK (polyetheretherketone), perforated PEEK (with punched holes), PEI (polyether imide), PAR (polyarylate), modified PAR types, PC (polycarbonate), PA (polyamide), PET (polyethylene terephthalate), PEN (polyethylene naphthalate), PPSU (polyphenylsulfone), PES (polyethersulfone) and PSU (polysulfone), preferably PEEK or the structure layer comprises a thermoplastic elastomer such as thermoplastic polyurethanes (TPU), polyester elastomers, co-polyester elastomers, styrene block copolymers like SBS (styrene-butadiene block copolymer) or SEBS (styrene-ethylene-butylene-styrene block copolymer), elastic co-polyamides, thermoplastic silicones, and elastomeric polyolefins.
In a further embodiment the structure layer comprises a fully cured silicone, e.g. the structure layer is another silicone layer that has a relative solvent resistance of above 80%, or even above 90%. Preferably, the structure layer comprises a fully cured silicone, wherein the fully cured silicone is formed by the same material as comprised in the silicone layer. This embodiment allows for producing an acoustic material made from uniform silicone material. Preferably, the other silicone layer forming the structure layer is a thinner layer than the silicone layer comprising a partially uncured silicone. With large parts of the silicone in the composite being a cross-linkable silicone rubber, the composite material still exhibits the desirable formability.
Any further layer of the composite material becoming integral part of the acoustic membrane may be termed performance layer as it will contribute to the acoustic and mechanical properties of the acoustic membrane. The performance layers comprise or may consist of various materials known to be suitable in acoustic membranes, e.g. thermoplastic materials, elastomers such as cured silicones, adhesives, but also fabrics such as woven fabrics or non-woven fabrics (e.g. fleece).
For example the performance layer may be a soft material such as a silicone material, acrylic material, thermoplastic elastomers said materials being known as suitable materials for providing acoustic damping and adhesion (damping or gluing layer).
Moreover, it is preferred that one performance layer becoming integral part of the membrane preferably is formed by a material which has a higher mechanical stability, i.e. stiffness, or higher elastic modulus, as the silicone rubber in uncured state. In case that the performance layer has a higher elastic modulus than the silicone material of the silicone layer after being cured it may also be termed reinforcement layer. In these cases, the reinforcement layer preferably comprises or consists of a material selected from materials which are as also preferred for the structure layer (s. above).
Preferably the reinforcement layer consists of a thermoplastic material, preferably a material selected from the group consisting of PAEK (polyaryletherketone), e.g. PEEK (polyetheretherketone), perforated PEEK, PEI (polyether imide), PAR (polyarylate), modified PAR types, PC (polycarbonate), PA (polyamide), PET (polyethylene terephthalate), PEN (polyethylene naphthalate), PPSU (polyphenylsulfone), PES (polyethersulfone) and PSU (polysulfone), thermoplastic polyurethanes (TPU), polyester elastomers, co-polyester elastomers, styrene block copolymers like SBS (styrene-butadiene block copolymer) or SEBS (styrene-ethylene-butylene-styrene block copolymer), elastic co-polyamides, thermoplastic silicones, and elastomeric polyolefins.
In one aspect, the present invention also provides a method for preparing a composite material according to the invention selected from the group consisting of
In a first method, the silicone layer is prepared by solution coating. The method may be conducted as a continuous, in-line process with the steps of
In one embodiment, the solution coating method may include a step wherein the temperature is raised to a temperature in the range of the vulcanizing temperature of a high-temperature vulcanizing silicone rubber in order to allow partial curing, while it is essential that the silicone rubber at least partially remains uncured. Optionally, one or more further layer(s) may be introduced e.g. by covering the partially uncured silicone layer with a support layer or any further layer, before the composite material may be wound up.
In a second and preferred method of preparing a composite material according to the invention the partially uncured silicone rubber is directly deposited on a support layer. In order to achieve the desired thin layers of uncured silicone rubber the method may comprise a step of calendering or a step of extrusion through a slot die.
In one embodiment the method is conducted as an in-line process and includes the steps of
Alternatively, the uncured silicone rubber is brought into the desired thickness by extrusion. In this case the transport is also achieved by force conveyance.
During extrusion it must be controlled that the silicone rubber is not fully cured. Preferably the processing system is cooled, especially the die is cooled to maintain a processing temperature of well below the vulcanizing temperature of the silicone rubber, e.g. below 70° C. In an extrusion setup the use of a multilayer die may enable that a silicone layer and another layer, e.g. a thermoplastic material are co-extruded. For example a silicone layer and a reinforcement layer may be co-extruded and simultaneously deposited on a release layer to obtain an arrangement according to
In another aspect, the invention provides a process for producing an acoustic membrane comprising the steps of
The precursor is prepared in that the film is tailored to an appropriate size for the subsequent forming and curing step. The precursor may be a composite material or optionally—in case the composite material is an embodiment with the support layer being a release layer—derived from a composite material by removing the release layer.
For producing an acoustic membrane from the preferred composite material arrangements including a release layer, the release layer is removed before curing the silicone layer. Thus, in a preferred embodiment the method comprises a step of removing the release layer(s) to obtain the remaining silicone layer or the silicone layer in a multi-layer arrangement with one or more further layer(s) before the step of shaping and curing the precursor. In a subsequent step the composite material or the material remaining after removal of the release layer, i.e. the precursor, is formed and the silicone layer cured.
Forming, i.e. providing the material in the appropriate three-dimensional arrangement for the intended shape of the membrane, may be achieved by one or more forming tools.
Additionally, a pressure chamber may be used to allow forming by vacuuming or pressurizing.
Suitable conditions for curing depend on the partially uncured silicone rubber comprised in the silicone layer. Input of heat may be achieved by heating of the forming tool(s) or by thermal radiation, e.g. by using an infra-red (IR) source. Alternatively, silicone layers with a UV-curing silicone rubber may be exposed to a source of UV-light. In case of thermoforming, suitable conditions to achieve curing of an uncured or partially uncured silicone layer may be exposed to 130° C. to 250° C. for a time period of 1 min to 5 min, thus allowing the uncured silicone rubber to cure. However, heating conditions will vary with the used silicone rubber and the thickness of the membrane. Moreover, the reaction time may be reduced with increased temperature, e.g. for curing thin films 3 min at 150° C. may be as sufficient as 1 min at 180° C.
The process for producing an acoustic membrane, especially when using IR-initiated cross-linking allows for a time efficient production process in comparison to injection molding or deep drawing.
In the following aspects of the invention are described in figures and examples to illustrate embodiments of the invention. These embodiments should be understood as exemplary non-limiting examples.
In the preferred arrangements of Fig. A to L a support layer is the bottom outer layer of the arrangement. Words such as “top” and “bottom” are not meant to indicate a certain orientation of the membrane, but are merely used to describe the figures in a pictorial way. Here, the support layer is a release layer 1 and said release layer 1 may be removed from the composite material. In the arrangements of Fig. H to L, the top outer layer is also a support layer being a release layer 1. Preferred materials for the release layer designated with 1 are for example PET film with one-sided siliconized surface, PET film with symmetric siliconized surfaces, PET film with differentiated siliconized surfaces, paper with one-sided olefin coating, paper with symmetrically olefin-coated surfaces, and paper with differentiated olefin coating on both sides. These layers preferably have a thickness in the range of 30 μm to 200 μm, for example around 100 μm.
Moreover, the preferred embodiments of
The silicone layer in a composite material according to the invention preferably is a high-temperature vulcanizing silicone rubber, preferably a solid, two component material including a catalyst. Suitable silicone rubbers are commercially available. The silicone layer in the preferred embodiments has a thickness of below 100 μm, for example around 30 μm.
Furthermore, the multilayered arrangements with three or more layers may comprise a performance layer wherein the reference sign 3 indicates one or more damping layer(s) and the reference sign 4 indicates a reinforcement layer. Preferred materials for a damping layer 3 are soft materials. In the embodiments of
Preferred materials for the reinforcement layer 4 in embodiments of
In the embodiments of
In the elongated state the support layer may be subjected to a surface treatment. For example the support layer may be exposed to plasma or corona treatment as indicated with L in
Essential step of the coating process is the coating itself as indicated with C in
The large part of the solvent may be removed in a flotation dryer. In
After flotation drying, schematically depicted with a second arrow in
After calendering, the uncured silicone rubber is deposited on a support layer. The support layer, e.g. a thermoplastic film or paper, is provided from an unwind station 3 and processed in the running direction as indicated by the arrow. Immediately, after depositing of the silicone on the support layer, the lamination process is continued by two calibrating rolls 4′ and 4″. Subsequently, the composite material 5 may be moved over several rolls along the running direction. Here, optionally different parameters may be selected for smoothening of the surface and controlling the thickness of the silicone layer. Also temperature gradients or irradiation may be applied to allow controlled pre-curing of the silicone rubber. Finally, the composite material is rolled up on the rewind station 6.
In a preferred variation, the method may be performed as indicated in
In a process of producing an acoustic membrane with a composite material according to the invention, the composite material first has to be prepared. The material should be cut into an appropriate size, said size being for example marginally larger than the intended dimension of the acoustic membrane for lateral allowance during forming. Additionally, the removal of one or more release layers may be a step in preparation of composite material. Thus, the precursor may preferably comprise the silicone layer as outer layer.
In a second step, curing of the silicone rubber is achieved to shape the precursor into the desired form of the acoustic membrane. Exemplary, suitable tools are schematically shown in
UV-radiation is the method of choice for curing UV-sensitive silicone rubbers. However, also thermo-sensitive silicone rubbers may be cured by radiation, e.g. by use of an infrared (IR) source. In
A solvent resistance rub test was performed in order to characterize the partially uncured silicone layer in composite materials according to the invention. The rub test is performed on basis of the standard ASTM D4752 and involves rubbing the surface of the silicone layer with cheesecloth soaked with toluene until failure or breakthrough of the film occurs. The type of cheesecloth, stroke distance, stroke rate, and approximately applied pressure of the rub should be identical for all tests. The higher the number of rubs, said rubs being counted as double rubs, the higher is the solvent resistance of the investigated layer.
Heating to 140° C. results in a completely cured silicone layer, i.e. further curing for higher temperature or longer time did not result in increased solvent resistance. Thus, the composite material heated to 140° C. is a reference sample representing a cured state. The two embodiments heated to 100° C. or 120° C. are composite materials according to the invention with a partially uncured silicone rubber. The relative solvent resistance may be determined by dividing the achieved number of double rubs by the number of double rubs achieved with the completely cured reference material. The embodiment pre-treated at 100° C. has a relative solvent resistance of 9.8% and the embodiment pre-treated at 120° C. has a relative solvent resistance of 22.5%.
Number | Date | Country | Kind |
---|---|---|---|
16178183.6 | Jul 2016 | EP | regional |
Filing Document | Filing Date | Country | Kind |
---|---|---|---|
PCT/EP2017/066610 | 7/4/2017 | WO | 00 |