Patent Application
20080277454
1. Field of the Invention
This invention relates to metal articles made from dissimilar metals. It also relates to improved methods of making saw blades, and in particular, composite saw blades.
2. Description of Related Art
Saw bands and saw blades must have high dimensional stability of their cutting edges as well as high wear resistance. They should also be able to withstand the high loading produced by compressive, flexural and shearing forces, even under the temperatures that result from the friction between the saw blade and the material being sawn. Since it is difficult to combine the properties mentioned above in a single material, saw blade nowadays usually comprise a relatively tough metal base with high bending fatigue strength and a cutting-edge band of a high-speed steel that is less tough but highly wear resistant. The cutting-edge band is of such a width that at least the teeth tips of the saw band or blade, or even the cutting teeth as a whole, can be cut out from it.
Composite saw blades, that is, saw blades made up of two or more dissimilar materials, have been prepared by welding a thin strip of cutting tool steel to an edge of a flexible alloy steel backer. A common welding technique is electron beam welding; however, the resulting weld, an alloy of the two metals and a heat-affected area adjacent to it, is materially weakened. In preparation for welding, and in particular for electron beam welding, the metal backer and the thin strip of cutting tool steel are rolled and annealed repeatedly to attain the desired dimensions for welding. When welding dimensions are achieved, both the metal backer and the strip still needs to be further conditioned to obtain sharp, square edges at the site of welding. This process can be very time consuming and costly.
Composite metal articles also have been prepared by casting molten cutting tool steel against a supporting metal strip. The molten cutting tool steel is fed into a space adjacent to the supporting metal strip, where it bonds.
Solid phase edge bonding has been used for side-by-side joining of metal strips by application of heat and pressure under a reducing atmosphere. Solid phase bonding is accomplished by heating the metal strips under sufficient pressure to form a metallurgical bond. Although solid state bonding can produce a metallurgical bond without deleterious effect to neighboring metal area, solid state edge bonding does not generate sufficient new bonding surfaces, heat and pressure to form a strong bond, and the joined strips often do not survive subsequent processing.
Hot rolling of metals is known, and the hot rolling of steel ingots has been in common practice for many years. Hot rolling is usually carried out at temperatures around 2000° F., and the hot rolled steel typically is cold-rolled to its final dimensions. It is often necessary when rolling high speed steel to anneal the steel after each 10% to 30% cold worked reduction due to damage, i.e., work hardening, resulting from cold working. Thus, cold working requires additional time-consuming and costly processing steps.
Hot bonding has been used to prepare composite metal articles such as copper clad steel by heating a steel core and two copper strips to hot rolling temperatures using electric resistance heating. The three components are introduced into a chamber with a reducing atmosphere and are then passed directly into a roll, where pressure and heat bond the materials. As with hot rolling, it is most often necessary to cold work the article to its final dimensions.
Thus, improved methods for providing composite articles having high bond strength between different metals are desired.
There remains a need for efficient manufacture of composite metal articles.
There remains a further need for composite metal articles having a strong bond between the component metals with minimal material damage to the bonding region.
These and other limitations of the prior art are addressed in the following invention.
The present invention provides a composite metal article that exhibits superior bonding between the dissimilar metals. The composite article is capable of being further processed into saw blades or other useful articles. A saw blade with superior cutting and wear-resistant properties is provided.
The present invention also provides a simple and effective method for forming a composite metal article. According to one aspect of the invention, a method of making a composite metal article from two dissimilar metals includes providing a metal base comprised of a first metal and having first and second opposing surfaces, said base having a least one longitudinally-positioned depression in at least one of said first and second opposing surfaces for receiving a wire; introducing an elongated metal element comprised of a second metal into said at least one first and second depressions of the metal base to form a composite assembly; and heating the composite assembly under pressure to urge the adjacent surfaces of the second metal elements and the depressions together to form a bonded article.
In one or more embodiments, the metal base is a sheet or strip. A sheet or strip has its conventional meaning and includes one dimension, e.g., thickness, that is significantly smaller than the other two dimensions, e.g., length and width. Exemplary dimensions include an aspect ratio (width:thickness) of greater than about 5.
In one or more embodiments, the metal base is a metal bar. Metal bar has its conventional meaning and includes one dimension, e.g., thickness, that is smaller than the other two dimensions, e.g., length and width; however, the aspect ratio (width:thickness) is not as great, e.g., 1:1 to about 4:1.
As used herein “transverse direction” is considered to be the direction perpendicular to the plane of the base, or in the direction of the applied pressure. The transverse direction typically is across the thickness of the article.
In one aspect of the invention, a method of making a composite metal article from two dissimilar metals includes providing a metal base comprised of a first metal and having first and second opposing surfaces, said base having at least one longitudinal depression in at least one of said first and second opposing surfaces for receiving a wire; introducing a wire comprised of a second metal into said at least one depression of the metal base to form a composite assembly; and heating the composite assembly under pressure to urge the adjacent surfaces of the second metal elements and the depressions together to form a bonded article.
In another aspect of the invention, a method of making a composite metal article from two dissimilar metals includes providing a metal base comprised of a first metal and having first and second opposing surfaces, positioning at least one wire comprised of a second metal at a location on at least one of said first and second surfaces; restricting the lateral movement of the wire relative to its location on said surface to form a composite assembly; and heating the composite assembly under pressure to urge the adjacent surfaces of the at least one wire and the metal together to form a bonded article.
In still another aspect of the invention, a method of making a composite wire includes providing a metal bar comprised of a first metal and having first and second opposing surfaces, said base having a least one longitudinal depression in at least one of said first and second opposing surfaces for receiving a wire; introducing a wire comprised of a second metal into said at least one depression of the metal base to form a composite assembly; and heating the composite assembly under pressure to urge the adjacent surfaces of the second metal elements and the depressions together to form a bonded article.
In another aspect of the invention, a composite metal article includes a base comprised of a first metal and having first and second opposing surfaces; and at least one elongated member comprised of a second metal, said at least one elongated member embedded in at least one of said first and second opposing surfaces and positioned along the length of the base, wherein the surface of the base containing the embedded elongated member and the opposing surface form planar surfaces, and wherein the base and the embedded, elongated member form a metallurgical bond along their interface.
In another aspect of the invention, a composite metal cutting tool includes a base comprised of a first metal and having a first thickness at a first edge and having a tapered region on the opposing edge of the base that tapers from said first thickness to a second, smaller thickness; and at least one edge member located adjacent to the tapered edge region of the base, the edge member comprised of a second metal and forming a metallurgical bond with a surface of the tapered region of the meal base, such that the thickness of the edge member and the tapered region of the metal base is the same as the first thickness of the metal base.
In still another aspect of the invention, a turks' head having improved restraint on lateral spread includes a first pair of horizontal rolls; and a second pair of vertical rolls located at the edges of the horizontal rolls, wherein the rotational axis of the vertical rolls is offset upstream of the rotational axis of the horizontal rolls, said offset being within the arc of contact of the horizontal roll with a material to be processed.
In yet another aspect of the invention, an apparatus of making a composite metal article includes:
means for introducing a metal base into a first controlled atmosphere;
means for introducing first and second elements into a first controlled atmosphere and for positioning the first and second elements adjacent to the metal base at a location where bonding is to occur;
means for heating the metal base and first and second wires;
at least one roll pair for applying pressure to the metal base and two wires; and
means for monitoring and controlling tension.
As used here and throughout the specification, the term “about” refers to ±10% of the stated value.
Various objects, features, and advantages of the present invention can be more fully appreciated with reference to the following detailed description of the invention when considered in connection with the following figures, in which like reference numerals identify like elements. The following drawings are for the purpose of illustration only and are not intended to be limiting of the invention, the scope of which is set forth in the claims that follow.
The present invention provides a composite metal article that exhibits superior bonding between the dissimilar metals. The composite metal article is formed between at least two dissimilar metals. As used herein, it is understood that the term “metals” includes metal alloys. The composite metal article is comprised of a metal base and one or more other metal elements that form a strong bond with the metal base. The bond is formed without deleteriously altering the chemical, metallurgical and/or mechanical properties of article adjacent to the bond.
In one or more embodiments, a metal edge member is bonded on both sides of a metal base along one side of the body of the base. An exemplary composite metal article according to one or more embodiments of the invention is shown in
Due to the highly effective metallurgical bonding of the two dissimilar materials at the atomic level, the interface is very clean with a discreet bond interface; however, there is no embrittled alloys formed in the bonding zone, as is typical of electron beam welded articles. The thickness of the thinned section 125 can vary according to the contemplated uses of the article of the invention, and can range from about 70% to an insignificant amount of the total thickness, as measured at the exposed surface 160 of the slit article or as measured at the narrowest point 150 between opposing elements (or adjacent to the metal element in those embodiments having only one elongated metal element). In one or more embodiments, the base metal thickness at point 150 or 160 can range to about 30%, or is about 5-15% of the total thickness. The edge members 128, 128′ (or the elongated metal elements 126, 126′) may have substantially equal thickness on either side of the tapered base section, however, it is recognized that manufacturing process may cause the edge members 128, 128′ (or the elongated metal elements 126, 126′) to vary somewhat in thickness. In one or more embodiments, the edge members 128, 128′ (or the elongated metal elements 126, 126′) may be of unequal shape, size and thickness. Improved cutting properties have been observed in blades prepared from the composite metal article of the invention.
In one or more embodiments, a composite metal sheet 200 includes an elongated metal element 210 embedded in and bonded to one side of a metal base 220, as is shown in
In one or more embodiments of the present invention, the first metal is tougher, e.g., has a higher hardness, than the second metal. In one or more embodiments, the base is a metal having desirable properties of mechanical and thermal stability, for example, under the conditions typically encountered in sawing or cutting operations. In general, the metal base can be any hot or cold rolled metal or metal alloy that is tough and spring-like. The metal base exhibits flexibility, and metals that exhibit flexibility, e.g., spring metals, can be used in the present invention.
In one or more embodiments of the invention, the second metal used as the cutting edge is harder or more wear-resistant than the first metal. In one or more embodiments, the edge member is a wear-resistant metal; for example, the edge member is made from a metal capable of withstanding the abrasive conditions typically encountered by the cutting edge under sawing or cutting operations. The edge member metal can be one or more high speed steels, including powdered metals. By way of example only, high speed steels include Matrix II, M2, M42, M51, M3 Type 1, M3 Type 2, and the like.
A feature of the present invention is that the article is not limited to any specific metal or metal alloy for use in either the metal base or the edge metal. Because bonding relies on the diffusion of metal across a dramatically increasing interface, almost any combination of metals can be used in the practice of the present invention. This versatility is in distinct contrast to conventional welding operations used in the fabrication of cutting tools, which often require specific alloy compositions for successful welding.
More complex articles are contemplated in accordance with the present invention. In one or more embodiments of the invention, a cutting edge 400 of a composite metal article 410 as shown in
The base and edge members of the composite article form a metallurgical bond using the method of the present invention as described herein below. The bond results from the atomic interaction and rearrangement at the interface of the two metals at moderate temperatures, i.e., below the temperature of any metallurgical transformation (Tm) of either metal. Unlike more conventional joining methods, such as electron beam welding or laser welding techniques, there is no significant area near the joint that is materially affected, i.e., weakened, by the joining process. The strength of the bond also arises from the differences in the shear line between a welded article and the bonded article of the present invention. A shear line 310 in conventionally welded article 320 is shown in
The resultant metallurgical bond strength varies according to the materials and methods used in its manufacture; however, the bond is at least strong enough to survive subsequent post-bonding fabrication steps. In the case of saw blade fabrication, the resultant metallurgical bond strength between the base metal and the edge metal is strong enough to withstand slitting, cutting and tooth setting, which are typical post-bonding fabrication steps. After fabrication, the resultant article is typically subjected to a heat treatment to harden the article.
The composite metal article of the invention is useful in the fabrication of cutting tools, i.e., blades. Any variation of a cutting tool is contemplated according to the present invention. A cutting edge of any geometry can be machined into the edge member of the composite article. In one or more embodiments of the present invention, the blade is a toothed blade, e.g., a saw blade such as hand and powered hacksaw, hole saw, jigsaw, reciprocating saw and band saw blades. In one or more embodiments, the blade is a toothless blade, e.g., a knife. By way of example only, a blade can be welded, e.g., butt-welded, to form a band saw blade, or the surface can be machined cut to form a smooth, toothless saw edge or a knife edge
Cutting teeth are machined into the cutting edge using conventional processes. The teeth can be of any geometry and orientation suitable for a particular cutting application. The cutting teeth can be arranged in any way desired along the cutting surface. The teeth can be in or out of plane from the base, as is needed by a particular cutting application. In short, one is free to design the cutting tool as is most appropriate for a particular cutting application.
In one or more embodiments of the present invention, the cutting teeth are formed from a combination of a hard cutting tool metal and a softer, supporting metal. The cutting edge presented to a surface to be cut includes alternating regions of hard cutting tool metal and softer metal. In one or more embodiments of the invention, the cutting edge is provided in the form of a composite metal. The cutting edge includes alternating regions or sections of hard and soft metal that have been solid state bonded to each other and include the edge members and tapered regions of the composite metal article shown in
In one or more embodiments, the cutting tool is a hybrid article including a composite metal cutting strip that is prepared in a separate step and that is welded, after fabrication, to a metal base.
The composite metal article of the present invention is prepared by heating an assembly of dissimilar metal components under pressure to form a bonded article, a process known as solid phase bonding. The composite assembly includes a metal base, such as a sheet or strip, having at least one depression or groove positioned longitudinally on one or both sides of the metal base that is capable of receiving an elongated metal element. The term “wire” or “insert wire” may be used as an alternative for “elongated metal element” without loss of any scope afforded the latter term. The wire can be of any shape, and is selected based upon any number of factors, including raw material availability, ease of manufacture, and the desire to complement the shape of the longitudinal depression of the metal base. An exemplary composite assembly 500 including a metal base 510 and elongated elements 520, 525 positioned in depressions 530, 535, respectively, of the metal base 510 is shown in cross-section in
The grooves and related elongated elements can be of any shape or geometry. In one or more embodiments, the elongate element is a rod, bar, wire. The elongated element or wire can have any cross-sectional geometry; for example, a cross-section that is round, oval, polygonal, square, rectangular or rhomboid, and the like, is contemplated. The elongated element can be used in the size and shape provided by the manufacturer. Alternatively, the wire can be processed to a particular size and shape by any conventional method, including by not limited to, drawing, turks head, or wire extrusion. The wire may be reduced from an initial dimension by warm or hot rolling (below Tm).
The elongated elements may be, but are not required to be, complementary to the groove in the metal base. A large amount of variability is possible in forming wire inserts-metal base combinations, so long as the shape of the depression is adapted to receive the wire insert. In one or more embodiments, the combination is selected to “lock” the wire into the groove of the metal base. This is typically accomplished by establishing at least two points of contact between the wire insert and the groove. Thus, by way of example only, a round wire in a v-groove or a trapezoidal wire in a round groove provides sufficient contact. In one or more embodiments of the present invention, the wire insert and the groove can be of complementary shapes so that elongated element matches the shape of the groove or depression of the metal base.
The composite assembly is then heated under pressure to bring the metal base and the elongated elements into intimate contact and to form a metallurgical bond between the component metals. In one or more embodiments, the composite assembly is first heated to a temperature that is above room temperature and below the temperature of any metallurgical transformation (Tm) of any of the metals of the composite assembly and then passed through a pair of rolls (a “mill roll”) to exert bonding pressure and to reduce the article thickness.
Although the actual temperatures used will vary depending upon the materials and pressing procedure used, temperatures can range from about 800 to about 1600° F., or in some embodiments from about 1000 to about 1550° F. Heating can be accomplished using any conventional method. By way of example, the composite assembly is heated using inductive or electrical resistance heating. In one or more embodiments, the heat is supplied by a form of radiation, for example, laser radiation.
Similarly, the actual pressures used in the practice of the method of the invention will vary greatly depending upon the materials and pressing procedure used. The pressure can be generated using any conventional method. By way of example, pressure is generated using a rolling mill or a turks head. Pressure is a function of many variables including, but not limited to, roll diameter, material deformation resistance (hardness), metal thickness, and the coefficient of friction between the roll and the metal being rolled, and the forces generated in rolling are well known in the industry. In one or more embodiments of the present invention, rolling occurs without lubrication of the rolls, which increases the rolling pressure. In one or more embodiments, the addition of a hard insert wire, and in particular the addition of two wires stacked one on top of the other above and below the metal base, causes higher pressure at the point of contact—the specific location where high pressures are desired to improve bonding. The additional thickness locally due to the presence of the elongated element provides additional pressure for improved bonding during the solid phase bonding operation.
The metal base has one or more grooves or depressions longitudinally-positioned on one or both sides of the metal base.
Thus, in a few simple (and rapid) steps, the method of one or more embodiments of the invention provides a bonded article of a desired thickness. The starting materials can be thicker than those used in conventional electron beam welding processes, yet final thickness is achieved in fewer steps and less time, resulting in a significant savings in cost and materials.
In one or more embodiments using insert wire above and below the metal base, it is desired to keep the wires registered in place. In instances where the wire can move laterally, the resultant bonded sections of the wire insert can shift during rolling so that the resultant bonded regions are offset from one another. Use of a wire insert and groove geometry that forms a multipoint contact is helpful in reducing lateral shift of the bonded second metal region.
In one or more embodiments of the present invention, the arrangement and geometry of the wire, metal base and rolls are selected to reduce the relative movement of the wire and base. If the wire shifts during processing, the resultant bonded metal element may be out of position for subsequent processing, e.g., slitting. In particular for the case where a wire pair are positioned above and below the metal base, it is desired to maintain accurate position of the components of the composite assembly. In one or more embodiments, the upper and lower depressions are kept in close alignment to the desired position.
In one or more embodiments of the present invention, the roll, metal base, or both, includes a groove that engages the wire insert to constrain the lateral movement of the insert wire. As is shown in
In one or more embodiments, the wire 1300 is engaged in a groove 1310 of a roll 1320 that runs in the rolling direction. When there is a deep groove in the rolls (shown in
In one or more embodiments, the wire is engaged in the depression of the metal base and no roll groove is employed to fix the component positions. As shown in
The composite metal article of the invention can be further processed to obtain the desired article. For example, in the manufacture of saw blades, the composite article is divided into two similar pieces by slitting the article through the center region 548 or center region 570 of the article. See
In one or more embodiments, the elongated metal element used as an insert wire also is a composite metal.
The final bonded articles can have varying thicknesses, for example, ranging from about 0.020″ to about 0.100″. Articles having small final thicknesses and/or relatively large percent reduction (e.g., large increases in the area of interface) tend to form very strong bonds. In instances where the final thickness is relatively large, e.g., 0.065″ or greater, or where the percent reduction in thickness is not very large, the bonding strength is not as high. In other instances where the overall article is very wide, one may not want to use rolling to attain the entire width as flow properties can vary over the greater distances. In these (and other) instances, a composite cutting edge can be welded to an edge of the metal base using conventional welding techniques to provide the cutting edge of the present invention. An example of such an article has been previously described (
A method of making a welded product having a composite metal edge is now described with reference to
Similarly, the article can be of any width, and can for example range from less than ¼″ to 3½″ or more.
In one or more operations, solid phase bonding of the dissimilar metals is accomplished using bonding rolls and/or turks head rolls for the application of heat and/or pressure. In one or more embodiments, bond rolling is carried out using a plurality of bonding rolls or “stands.” A stand is a component of a mill used for the bonding operation. Each stand includes a pair of bonding rolls that is independently motor driven and independent “screw down” gear assembly used to adjust the vertical position of the rolls for the application and release of pressure at the rolls and control of material thickness. A mill includes a plurality of independent rolling stands operating in tandem and in communication with one another through “bridges” or enclosures that span between the exit of one stand and the entrance of the next stand in order to keep the materials being bonded in a controlled, typically reducing, atmosphere. In one or more embodiments, the mill includes two or more rolling stands, and can include 3 to 6 stands, or more.
Many modifications and variations of the process are within the scope of the invention. It is appreciated that a pressing operation such as rolling will either elongate or widen the composite article. In the present invention, there is an additional cause for lateral spread due to the presence of additional material (the elongated elements) which are being forced into the center of the metal sheet directly over one another. Left unattended, the lateral spread causes the center of the rolled form to fracture. In one or more embodiments, the bonding cavity, i.e., the space between the bonding rolls, have the ability to restrain lateral spread. “Restraining lateral spread” as that term is used herein, means that the lateral spread is substantially reduced or eliminated (it is recognized that a small amount of lateral spread will occur despite steps taken to prevent it), or that the material is allowed to spread laterally to a predetermined width, at which point the material is constrained from further spreading. The materials being reduced in the bonding cavity are allowed to spread forward and to the rear along the axis of the metal sheet or strip. In addition to providing a product of uniform dimensions, constraining lateral spread has been found to maintain bonding pressures of the article to enhance the quality of the bond.
In one or more embodiments, lateral spread is restrained in a rolling operation by employing a male 1000/female 1005 bonding roll arrangement such as that shown in
In one or more embodiments, lateral spread is restrained using an edge roll system, e.g., a turks head. A “turks head” is a special configuration of a rolling mill, i.e., it is two mills set up to roll in the same plane. A rolling mill becomes a turks head when an additional roll pair is used whose rolling axis is positioned at 90° relative to the mill rolls rolling axis. The turks head rolling axis is coplanar with the plane of reduction. As the material passes through a bonding roll and material is spread laterally to the sides of the roll, the turks head rolls apply an opposing force to material at its edges. A turks head is employed in the initial rolling stages, for example, in the first two mill stands where significant lateral flow can otherwise cause the base metal to split at the groove. While all mill stands reduce the base (web) thickness to about the same degree, a large percentage of thickness reduction occurs at or around the insert wire in the initial stages when the wire is embedded into the metal base.
For the purposes of this invention, it is desirable that the side rolls do not produce a “flash” (a thin bead of metal that flows between the mill rolls and turks head rolls). The present invention has discovered that flashing can be avoided by locating the side rolls slightly ahead (upstream) of the rolling axis of the mill rolls. In one or more embodiments, the offset of the turks head roll is within the arc of contact of the bonding roll with the material to be rolled. The arc of contact 1400, as shown in
In one or more embodiments of the present invention, the offset is in the range of about ¼″ to about ¾″. As in the case using male/female roll assemblies, the turks head roll is not necessary once the thickness of the material is reduced by 2 or 3 passes. In one or more embodiments, the turks head roll is used in the first, second and optionally, third stands.
In one or more embodiments, a turks head is employed to limit the lateral spread to a predetermined value. In one or more embodiments, the turks head can be allowed to spread or can be located a distance from the edge of the mill roll. When the material enters the mill roll, the material will spread a predetermined amount up to the point where it meets the turks head. In one or more embodiments, the metal base is narrower than the mill roll width, and the turks head is positioned at the edge of the mill roll (or may be located a distance from the edge of the mill roll). Again, the material is able to spread laterally, but only to a point at which it contacts the turks head roll. Controlled lateral spread can result in the controlled thinning of the base, particularly in the bonding region where the insert wires and metal base are in contact. Controlled lateral spread can be used to thin the metal base in the bonding region to the point that is breaks or thins to a point that the base metal is effectively absent.
An exemplary process for the manufacture of a composite metal article according to one or more embodiments is described.
The insert wire 1500 is shaped to the desired dimension and cross-section, for example by cold or hot working. The shaped wire is cleaned using standard metals cleaning procedures to remove residual oils and oxides. Wires can be butt-welded into long lengths to increase run times. In an exemplary process a 0.095″ round wire, e.g., M2, is rolled to 0.080″ by 0.105″ rhomboid shape.
The metal base (6150) 1510 is initially obtained as 0.065-0.250″ thick and of a width necessary to provide the final desired width and is turks head rolled to form a v-shaped (inverse groove) depression on either side without changing the thickness and with very little change in the width. The turks head pull through technique is able to keep top and bottom grooves in alignment within 0.002″ and in the center of the strip within +/−0.005″ and also maintained the base thickness (although the base may widen slightly).
The materials (insert wire 1500 and metal base 1510) are fed off rolls and heated as they approach the mill stands using direct current heating. With reference to
The mill stands include rolling mills that are surrounded by a gas chamber 1555 that keeps the material in a reducing atmosphere, although they can be exposed to air for brief periods. A bridge retort 1560 spans between mill stands and maintains a reducing atmosphere for the heated strip as it passes from mill to mill. Exposure to atmosphere at these elevated temperatures would otherwise result in surface oxidation. The mill rolls are made from durable hard materials, such as high speed steed, e.g., H13, or tungsten carbide. The mill rolls are selected to minimize sticking of the rolled materials. The mill rolls are typically hollow; and they can be air- or water-cooled. For example, they are shell mill-type rolls that are supported on an arbor capable of being water-cooled.
Each mill rectifier operates on its own circuit so that it may be independently controlled. The temperature drop of the material as it exits one mill stand and enters a subsequent one is monitored and the rectifiers adjust heating (e.g. voltage) to compensate for temperature drop. A hybrid heating system using resistance and induction heating is also possible. In a hybrid system, the first mill stand is set up as a conventional bonding configuration with ground contact at the first stand. Re-heating the materials between successive hot rolling stands is accomplished with high frequency induction units. As the wire/base metal assembly enters the first mill stand at target temperature, mill load is increased to target mill load. A load cell at each stand monitors mill load. As each mill stand equilibrates to the target temperature and mill load, the subsequent mill rolls are engaged.
Typically the first mill stand roll speed is operator-controlled and subsequent roll speeds are set as a function of its predecessor's speed. As material is reduced in gauge, the percent reduction is proportional to the speed differential of the rolls. The web tension of the material between mill stands can be monitored using a tensiometer 1570 and mill speeds can be adjusted as needed to control web tension; however, many other conventional methods of monitoring speed and thickness may be used. Tension control is accomplished using a roll over which the hot strip passes at a shallow angle. An arrangement transmits the force to a load cell. The load cell feeds back to a controller, which monitors the tension and makes mill speed adjustments accordingly.
The bonded article exits the mill stands as a continuous bonded strip 1580 that is taken up at spool 1590. Slitting is done in a separate operation.
Although various embodiments that incorporate the teachings of the present invention have been shown and described in detail herein, those skilled in the art can readily devise many other varied embodiments that incorporate these teachings. All references mentioned herein are incorporated by reference.
This application is a continuation of and claims the benefit of priority under 35 U.S.C. § 120 of U.S. patent application Ser. No. 10/207,409, now U.S. Pat. No. 7,373,857, filed on Jul. 29, 2002, entitled “Composite Metal Article and Method of Making”, incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10207409 | Jul 2002 | US |
| Child | 12123026 | US |