Composite Metal Organic Framework Materials, Processes for Their Manufacture and Uses Thereof

Abstract

A monolithic metal-organic framework (MOF) composite body is disclosed, comprising: MOF crystallites adhered to each other via a binder comprising MOF; and at least 0.15 vol % nanoparticles encapsulated in the MOF body. The nanoparticles have an average particle size corresponding to an average particle diameter in the range 3-200 nm. The nanoparticles may have photocatalytic activity. The MOF composite body is of use for treating water containing an organic dye, the photocatalytic reaction supported by the photocatalytic nanoparticles being a degradation reaction of the organic dye.

Description

BACKGROUND TO THE INVENTION

Field of the Invention

The present invention relates to composite metal organic framework (MOF) materials, processes for the manufacture of such materials and to the uses of such materials. The invention has particular, but not exclusive, applicability to the deployment of photocatalytic materials for treatment of water.

Related Art

Metal-organic frameworks (MOFs) are porous crystalline materials prepared by the self-assembly of metal ions and organic ligands. MOFs can have large pore volumes and apparent surface areas as high as 8,000 m²/g. MOFs combine a structural and chemical diversity that make them attractive for many potential applications, including gas storage, gas separation and purification, sensing, catalysis and drug delivery. The most striking advantage of MOFs over more traditional porous materials is the possibility to tune the host/guest interaction by choosing the appropriate building blocks, i.e. the metal ions and organic ligands, from which the MOF is formed.

WO 2010/148463 discloses a method for synthesis of MOFs in which the synthesis conditions are mild—typically below 30° C.—and the synthesis proceeds relatively quickly—typically in less than 1 hour. The synthesis takes place in a mixture of water and ethanol. The material studied in WO 2010/148463 is Cu₃(BTC)₂-type MOF.

US 2010/0181212 discloses MOF materials supported on open cell polymer foam structures, for use in gas storage applications.

Related work from the present inventors' research group has been published as WO 2015/189599. In WO 2015/189599, there is disclosed a process for manufacturing a MOF body comprising MOF crystallites adhered to each other via a MOF binder, that it, a binder that is formed of MOF. In one embodiment, the body consists of: MOF crystallites; a MOF binder which binds the crystallites together in the body; optionally, residual solvent; and optionally, one or more additives, wherein the additives are present at a level of not more than 10% by mass. WO 2015/189599 has one embodiment in which the MOF binder has substantially the same composition as the MOF crystallites.

WO 2015/189599 has another embodiment in which the MOF binder has a different composition to the MOF crystallites.

SUMMARY OF THE INVENTION

The present inventors have realized that functional nanoparticles may benefit from encapsulation in a MOF material. This may allow the exploitation of the combined physico-chemical properties of both constituents [Ref. 10]. However, to the best of the inventors' knowledge, there are no reports of nanoparticle encapsulation that provides a suitable monolithic composite (NP@_monoMOF) by a cost-effective process. Previous attempts to exploit the properties of MOFs for environmental remediation, for example, have focused on powdered morphologies, with their ability to degrade toxic organic compounds being poor [Ref. 11].

The present invention has been devised in order to address at least one of the above problems. Preferably, the present invention reduces, ameliorates, avoids or overcomes at least one of the above problems.

Accordingly, in a first preferred aspect, the present invention provides a monolithic metal-organic framework (MOF) composite body comprising:

MOF crystallites adhered to each other via a binder comprising MOF;

at least 0.15 vol % nanoparticles encapsulated in the MOF body, the nanoparticles having an average particle size corresponding to an average particle diameter in the range 3-200 nm.

In a second preferred aspect, the present invention provides a monolithic metal-organic framework (MOF) composite body consisting of: MOF crystallites;

a binder formed of MOF which binds the MOF crystallites together in the body;

at least 0.15 vol % nanoparticles encapsulated in the MOF body, the nanoparticles having an average particle size corresponding to an average particle diameter in the range 3-200 nm;

optionally, residual solvent; and

optionally, one or more additives, wherein the additives are present in an amount of not more than 10% by mass of the composite body.

In a third preferred aspect, the present invention provides a population of MOF composite bodies according to the first or second aspect.

In a fourth preferred aspect, the present invention provides a process for manufacturing a monolithic metal-organic framework (MOF) composite body, the process comprising the steps:

providing MOF precursors;

providing nanoparticles having an average particle size corresponding to an average particle diameter in the range 3-200 nm;

providing at least one solvent;

allowing the reaction of the MOF precursors in the solvent in the presence of the nanoparticles;

carrying out a drying stage with a maximum temperature in the drying stage of not more than 80° C. to form a monolithic MOF composite body comprising MOF crystallites adhered to each other via a binder comprising MOF, and incorporating at least 0.15 vol % of the nanoparticles encapsulated in MOF.

In a fifth preferred aspect, the present invention provides a method for treating water, the method comprising:

contacting a MOF composite body according to the first or second aspect or a population of MOF composite bodies according to the third aspect with water to be treated, the nanoparticles being photocatalytic nanoparticles; and

allowing the MOF composite bodies in contact with the water to be treated to be subjected to electromagnetic radiation suitable for activating at least one photocatalytic reaction supported by the photocatalytic nanoparticles.

In a sixth preferred aspect, the present invention provides a method for treating fluid, the method comprising contacting a MOF composite body according to the first or second aspect or a population of MOF composite bodies according to the third aspect with fluid to be treated, the nanoparticles interacting with the fluid to be treated.

The first, second, third, fourth, fifth and/or sixth aspect of the invention may have any one or, to the extent that they are compatible, any combination of the following optional features.

Preferably, the binder comprising MOF is formed substantially only of MOF. Preferably, for example, the binder comprising MOF consists of 100% MOF.

In the composite body, the nanoparticles may be provided in an amount of at least 0.2 vol %, or at least 0.25 vol %, or at least 0.3 vol %, or at least 0.35 vol %, or at least 0.4 vol %, or at least 0.45 vol %, or at least 0.5 vol %, based on the volume of the composite.

The nanoparticles may be present in the composite in an amount of at most 1 vol %, based on the volume of the composite. Although it is preferred to include as much volume of nanoparticles in the composite as possible, typically to enhance a functional effect provided by the nanoparticles in the composite body, it is found that at higher concentrations, sedimentation of the nanoparticles may take place during synthesis of the composite body.

In the process for manufacturing the composite body, the maximum temperature in the drying stage may be not more than 70° C., more preferably not more than 60° C., more preferably not more than 50° C. The temperature during the drying stage is typically selected according to the MOF composition of interest. It is typically found that gentle conditions during the drying stage promote the formation of suitable monolithic composite bodies.

In some preferred embodiments, the nanoparticles are photocatalytic nanoparticles. Such nanoparticles are of interest in order to promote certain chemical reactions, in particular under illumination. Preferably, the relative photonic efficiency ξ_r of the nanoparticles is greater than 1. Further discussion of this feature is set out further below.

In some preferred embodiments, the nanoparticles comprise a composition selected from the group consisting of one or a combination of:

metal oxides, including SnO₂, ZnO, TiO₂, PdO

Pd, Au, Ru, Rh, Pt,

Bi-containing compositions, including BiFeO₃, Bi₂S₃, BiVO₄ and Bi₂Fe₃O₉

Cd-containing materials, including CdSe and CdS

transition metal dichalcogenides, including MoS₂ and WS₂.

The nanoparticles may comprise at least two different materials having a heterojunction interface between them.

In the case of photocatalytic nanoparticles, it may be preferred to use a material with a relatively narrow bands gap in order to utilize the solar spectrum more effectively.

Due to electron-hole recombination, it is understood that many of the materials listed rarely appear alone and typically form a heterojunction with a different material, extending excitation lifetime. 2 component and 3 component nanoparticles are of interest. Examples of 2 component systems include core@shell NPs like Bi₂S₃@MoS₂ or CdSe@MoS₂. Examples of 3 component systems include Bi₂S₃@MoS₂/TiO₂ or CdSe@MoS₂/TiO₂ or Au@PdO/TiO₂ nanocomposites.

Preferably, the smallest dimension of the composite body is at least 10 μm. It is considered that the composite body should be a self-supporting body, and therefore is typically not formed as a film or layer on a substrate. The smallest dimension of the composite body may be at least 50 μm, at least 100 μm, at least 200 μm, at least 500 μm, at least 1 mm, at least 2 mm, or at least 5 mm. The composite body preferably takes the form of a monolith.

The composite body may have a BET surface area of at least 500 m²g⁻¹. It is understood that this is still a substantial surface area compared with typical materials. However, it is relatively low for a MOF material. The incorporation of (typically non-porous) nanoparticles into the MOF reduces the available surface area per unit weight of the composite body. The composite body may have a BET surface area of at least 600 m²g⁻¹, at least 700 m²g⁻¹, or at least 800 m²g⁻¹. The MOF material itself (without the incorporation of nanoparticles) typically has a higher BET surface area than the composite body, e.g. at least 900 m²g⁻¹′.

The nanoparticles, when isolated from the MOF composite body, may have a BET surface area of at most 100 m²g⁻¹. Thus, the nanoparticles themselves are not microporous. Thus, the nanoparticles, when isolated from the MOF composite body, may alternatively have a BET surface area of at most 50 m² g⁻¹, or at most 10 m² g⁻¹.

In some preferred embodiments, the MOF comprises a zeolitic imidazolate framework (ZIF).

The MOF may, for example, comprise one or more materials selected from the group consisting of:

ZIF-8, HKUST-1, UiO-66, MOF-74, Al-fumarate, NU-1000, MIL-100, MIL-53.

For reference, the chemical compositions for these materials can be expressed as:

ZIF-8: C₈H₁₀N₄Zn

HKUST-1: C₁₈H₆Cu₃O₁₂

UiO-66: C₄₈H₂₈O₃₄Zr₆

MOF-74: C₈H₂O₆X₂(X=Zin, Co, Ni, Mg, Fe, Mn, Cu)

Al-fumarate: C₄H₁₀O_8.5A

NU-1000: C₈₈H₆₄O₃₂Zr₆

MIL-100:C₁₈O₁₄H₇Fe₃ (X═Al, Fe, Cr)

MIL-53: C₈H₅O₅X (X═Al, Fe, Cr)

In the process, the drying stage may be carried out in a mould so that the composite body is formed to conform to an internal shape of the mould.

In terms of the method of treatment of water using the composite body, the water to be treated may contain an organic dye. Preferably, the photocatalytic reaction supported by the photocatalytic nanoparticles is a degradation reaction of the organic dye. The organic dye may, for example, be one or a combination of organic dyes selected from the group consisting of:

eosin dyes, rhodamine dyes, xanthene dyes, fluorescein dyes, acridine dyes, anthraquinone dyes, azo dyes, diazonium dyes, fluorine dyes, fluorone dyes, phthalocyanine dyes.

For water treatment, it is preferred that the nanoparticles comprise, for example, a composition selected from the group consisting of one or a combination of:

metal oxides, including SnO₂, ZnO, TiO₂,

Bi-containing compositions, including BiFeO₃, Bi₂S₃, BiVO₄ and Bi₂Fe₃O₉

Cd-containing materials, including CdSe and CdS

transition metal dichalcogenides, including MoS₂ and WS₂.

Preferably, the electromagnetic radiation to which the composite bodies are subjected is natural sunlight or artificial sunlight.

Where the composite body is used to treat a fluid, the fluid to be treated may comprise CO. In that case, preferably the nanoparticles may comprise, for example, Au, the CO being treated by being oxidised.

Where the composite body is used to treat a fluid, the fluid to be treated may comprise hydrogen. In that case, preferably the nanoparticles may comprise, for example, one or more of:

Ru, Ru/Rh, Pt, Pd

resulting in a hydrogenation reaction.

Where the composite body is used to treat a fluid, the fluid to be treated may comprise water. In that case, the nanoparticles may comprise Ru, resulting in a hydration reaction.

Where the composite body is used to treat a fluid, the fluid to be treated may comprise methane. In that case, the nanoparticles may comprise, for example, one or more of:

PdO/Au/TiO₂ or Au@PdO/TiO₂

resulting in a methane oxidation reaction to form methanol.

Where the composite body is used to treat a fluid, the fluid to be treated may comprise water. In that case, the nanoparticles may comprise, for example, Pt, resulting in the formation of hydrogen and oxygen.

Further optional features of the invention are set out below.

BRIEF DESCRIPTION OF THE DRAWINGS

Embodiments of the invention will now be described by way of example with reference to the accompanying drawings in which:

FIG. 1 shows a representative image of _monoZIF-8, for reference.

FIG. 2 shows a representative image of SnO₂@_monoZIF-8, according to an embodiment of the invention.

FIGS. 3-6 show SEM micrographs of SnO₂@_monoZIF-8 upon FIB milling, with the sample at 52° tilt. Bright rectangular areas and vertical curtaining are due to localized charging under the electron beam and artefacts caused by milling, respectively. FIG. 6 reveals embedded SnO₂—NPs (f).

FIG. 7 shows FIB-XPS binding energy spectra for the 3d region of Sn(IV) in SnO₂@_monoZIF-8. The indicated peak energies are calculated as an average over the 10 spectra.

FIG. 8 shows PXRD patterns of simulated and experimental _monoZIF-8, SnO₂—NPs, and SnO₂@_monoZIF-8 fresh and after 1, 5 and 10 catalytic cycles.

FIG. 9 shows the degradation of aqueous MB (25 mL, 1.55×10⁻⁵ M) in the presence of 0.4 g (cycles 1, 5, 10) and 1.7 g of SnO₂@_monoZIF-8.

FIGS. 10 and 11 show representative bright field TEM (scale bar 50 nm in FIG. 10 and scale bar 20 nm in FIG. 11) micrographs of SnO₂ nanoparticles. The inset in FIG. 10 shows particle size distribution, the error for which is calculated using standard deviation over 100 values of particle diameters. The inset image in FIG. 11 shows an HRTEM image (scale bar 5 nm).

FIG. 12 shows an indexed X-ray powder diffraction pattern of SnO₂ nanoparticles prepared using a hydrothermal method.

FIG. 13 shows a Williamson-Hall plot of

$\frac{\mathrm{\beta cos\theta }}{\lambda }$

against

$\frac{\sin \theta }{\lambda }$

for SnO₂ nanoparticles prepared using a hydrothermal method.

FIGS. 14 and 15 show representative TEM micrographs of the mother liquors associated with the preparation of _monoZIF-8 (FIG. 14) and SnO₂@_monoZIF-8 (FIG. 15) taken at 15 minutes reaction time.

FIGS. 16 and 17 show representative STEM-HAADF images of SnO₂@_monoZIF-8 (scale bar 100 nm in FIG. 16 and scale bar 20 nm in FIG. 17).

FIG. 18 shows drift corrected EDX analysis of SnO₂@_monoZIF-8, scanned over Area 1 (blue) and Area 2 (red) as illustrated by the regions identified in FIG. 17.

FIG. 19 shows selected FIB-XPS data for Zn (marked as a), N (marked as b), O (marked as c) and C (marked as d) for etched layers of SnO₂@_monoZIF-8. The etching depth is indicated below the graphs of FIG. 19. The peak energies calculated as an average over the 10 spectra.

FIG. 20 shows FIB-XPS survey spectra for etched layers of SnO₂@_monoZIF-8 (etching depth indicated on left in graph).

FIG. 21 shows N₂ adsorption isotherms at 77 K on non-logarithmic axes for:

_monoZIF-8 (large filled diamonds)

SnO₂@_monoZIF-8 (filled squares)

SnO₂@_monoZIF-8 after 1 catalytic cycle (small filled diamonds)

SnO₂@_monoZIF-8 after 5 catalytic cycles (filled triangles)

SnO₂@_monoZIF-8 after 10 catalytic cycles (filled circles)

SnO₂@_monoZIF-8 after 1 water cycle (open diamonds)

SnO₂@_monoZIF-8 after 5 water cycles (open triangles)

SnO₂@_monoZIF-8 after 10 water cycles (open circles)

FIG. 22 shows the data of FIG. 21 on semi-logarithmic axes.

FIG. 23 shows a schematic representation of sample recovery by gravimetric filtration.

FIG. 24 shows photocatalytically induced spectral changes to aqueous MB dye (1.55×10⁻⁵M) highlighting degradation of the absorption maximum at 664 nm in the absence of composite (red) and presence of 1.7 g SnO₂@_monoZIF-8 (green) after 3 hours of simulated solar irradiation.

FIG. 25 shows the degradation of MB in the presence of 0.4 g (Cycles 1-5 and 10) and 1.7 g of SnO₂@_monoZIF-8. Error bars were calculated using the standard deviation in triplicated readings.

FIGS. 26 and 27 show optical microscopy images of the 3-faced pyramidal indents resulting from 2000 nm depth nanoindentation experiments. FIG. 26 shows _monoZIF-8 monolith. FIG. 27 shows SnO₂@_monoZIF-8 composite. The scale bar is 10 μm in each image.

FIGS. 28, 29 and 30 show load-displacement (P-h) nanoindentation data for a surface penetration depth of 2000 nm. In FIG. 28, the results for ZIF-8 monolith are shown on which 9 indentation tests were performed, where highly reproducible P-h data reflect the homogeneous nature of the sample tested. In FIG. 29, the results for SnO₂@_monoZIF-8 composite are shown, here showing a larger scatter in P-h data, therefore 48 indents were performed to better establish the sample variability. FIG. 30 shows combined P-h nanoindentation curves in which the red curve depicts the consistent data for _monoZIF-8, adjacent to the relatively more varied mechanical response of the SnO₂@_monoZIF-8 composite (blue).

FIGS. 31 and 32 show Young's modulus, E, of _monoZIF-8 (FIG. 31) and SnO₂@_monoZIF-8 (FIG. 32) plotted as a function of surface penetration depth, where each red error bar corresponds to the standard deviation in 9 and 48 indents, respectively. Averaged Young's moduli of _monoZIF-8 and the composite were determined using data collected over the 500-2000 nm indent range, yielding 3.0±0.1 GPa and 3.3±0.1 GPa, respectively.

FIGS. 33 and 34 show hardness of _monoZIF-8 (FIG. 31) and SnO₂@_monoZIF-8 (FIG. 32) plotted as a function of surface penetration depth. Each red error bar arises from the standard deviation in 9 and 48 indents, respectively. Averaged hardnesses of _monoZIF-8 and the composite were determined using data collected over the 500-2000 nm indent range, yielding 0.41±0.01 GPa and 0.44±0.01 GPa, respectively.

FIG. 35 shows thermogravimetric analysis of _monoZIF-8, SnO₂—NPs, methylene blue (MB), and SnO₂@_monoZIF-8.

FIGS. 36 and 37 show FT-IR spectra of SnO₂ nanoparticles and MB (FIG. 36) and _monoZIF-8, fresh SnO₂@_monoZIF-8 and SnO₂@_monoZIF-8 after 10 catalytic cycles of MB dye degradation (FIG. 37).

FIG. 38 shows fluorescence spectral changes measured under simulated solar illumination of 0.4 g of SnO₂@_monoZIF-8 in a basic solution of TA (excitation at 315 nm).

FIGS. 39 and 40 show TEM images for CdSe@ZIF-8_mono.

FIG. 41 shows powder XRD (PXRD) patterns for CdSe@ZIF-8_mono (upper line) and for ZIF-8_mono (lower line).

FIGS. 42 and 43 show TEM images for Au@ZIF-8_mono. The magnified image shown in FIG. 43 is of the area indicated in FIG. 42.

FIG. 44 shows the particle size distribution of Au nanoparticles in Au@ZIF-8_mono. The measured average particle size of Au nanoparticles was 2.60±0.96 nm (assessed over 200 particles). The largest Au particles (very rarely seen) were never more than about 7 nm in diameter.

FIGS. 45 and 46 show further TEM images for Au@ZIF-8_mono.

FIG. 47 shows a scanning transmission electron microscope—high-angle annular dark field (STEM-HAADF) image of (PdO/TiO₂)@ZIF-8_mono. FIGS. 48, 49 and 50 show elemental maps, for the particle imaged in FIG. 47, of Zn, Pd and Ti, respectively.

FIG. 51 shows powder XRD (PXRD) patterns for (PdO/TiO₂)@ZIF-8_mono (upper line) and for ZIF-8_mono (lower line). Specific peaks of interest in the (PdO/TiO₂)@ZIF-8_mono pattern are labelled.

FIGS. 52, 53, 54 and 55 show elemental maps for Zn, Ti, Au and Pd, respectively for a ((Au@PdO)/TiO₂)@ZIF-8_mono particle imaged via transmission electron microscope-high-angle annular dark field (STEM-HAADF).

FIG. 56 shows powder XRD (PXRD) patterns for ((Au@PdO)/TiO₂)@ZIF-8_mono (upper line) and for ZIF-8_mono (lower line). Specific peaks of interest in the ((Au@PdO)/TiO₂)@ZIF-8_mono pattern are labelled.

FIG. 57 shows a TEM image for Pd@HKUST-1_mono.

FIG. 58 shows the response of Pd@HKUST-1_mono to thermogravimetric analysis (TGA).

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS, AND FURTHER OPTIONAL FEATURES OF THE INVENTION

The photocatalytic degradation of toxic dye effluents has received considerable attention. Despite semiconducting nanoparticles being promising photocatalysts for the degradation of these compounds, their powder morphology has previously hindered applications due to poor catalyst retention and recyclability. Furthermore, applications development faces difficulties owing to particle toxicity and agglomeration. We disclose here, in one embodiment of the invention, a new type of composite material involving the in situ immobilization of tin oxide nanoparticles (SnO₂—NPs) within a monolithic metal-organic framework (MOF), the zeolitic imidazolate framework ZIF-8. SnO₂@_monoZIF-8 exploits the mechanical properties and structural resilience of a monolithic MOF, whilst leveraging the catalytic action of the nanoparticles. The composite displays outstanding photocatalytic properties with full retention of activity observed after 10 catalytic cycles and represents a substantial advance in the field of treating toxic effluents and a vital validation for commercial application.

Zeolitic imidazolate frameworks (ZIFs) are MOFs with zeolitic topologies based on large cages and narrow windows [Ref. 1]. ZIF-8 (Zn(2-mlm)₂, 2-mlm=C₄H₅N₂⁻) in particular, boasts both high porosity (1.16 nm cavity diameter; flexible 0.34 nm window diameter [Ref. 2]; total pore volume 0.485 cm³ g⁻¹) and high chemical and thermal stability [Ref. 3]. However, despite their industrial potential, MOFs and ZIFs are almost invariably synthesized in powdered or thin film morphologies [Ref. 4]. In a recent major advance in MOF shaping, we presented a novel sol-gel synthetic method for producing transparent, robust, monolithic ZIF-8 without the need for high pressures or binders [Ref. 5]. These monoliths retained the same porous texture and chemical stability of the powder [Ref. 6] but now in the form of a mechanically robust macrostructure with bulk densities and volumetric BET areas 3-4 times higher than those of the powder. Compared with other pelletization methods that can lead to up to 90% of pore collapse due to the use of high pressures [Ref. 7], this synthetic protocol and monolithic morphology introduces the possibility of creating mechanically stable supports based on porous MOFs that can incorporate highly active and potentially toxic species such as nanoparticles (NPs) [Refs. 8 and 9].

The incorporation of catalytically active NPs, in one embodiment, into a MOF represents a method of exploiting the combined physico-chemical properties of both constituents [Ref. 10]. However, to the best of the inventors' knowledge, there are no reports of nanoparticle encapsulation via a ‘bottom up’ synthesis involving MOF precursors resulting in a mechanically stable monolithic composite (NP@_monoMOF) recoverable by simple filtration. Previous attempts to exploit the properties of MOFs for environmental remediation have focused on powdered morphologies, with their ability to degrade toxic organic compounds being poor [Ref. 11]. In this work, we synthesize mechanically and chemically robust monolithic SnO₂@_monoZIF-8, in one embodiment. This composite combines excellent activity in the degradation of toxic industry effluent with straightforward catalyst recyclability.

We chose SnO₂—NPs for encapsulation due to their non-toxic nature and track record in detoxification [Refs. 12, 13]. This photocatalyst, however, is considered to present major problems of recovery and reuse owing to the small size of the NPs [Ref. 14]. The synthesis of SnO₂—NPs resulted in uniform, monocrystalline NPs with a mean size distribution of ca. 5.0±1.1 nm (FIGS. 10-13). These were incorporated into ZIF-8 monoliths during its sol-gel synthesis; whereas pure ZIF-8 monoliths (_monoZIF-8) were transparent (FIG. 1), SnO₂@_monoZIF-8 appears white (FIG. 2). Scanning electron microscopy (SEM) analysis of SnO₂@_monoZIF-8 revealed a similar flat surface morphology to that previously reported for _monoZIF-8 (FIG. 3) [Ref. 15]. Transmission electron microscopy (TEM) analysis of the mother liquor revealed a primary particle size for SnO₂@_monoZIF-8 (100-150 nm) larger than that for _monoZIF-8 (60-80 nm) (FIGS. 14 and 15); suggesting ZIF-8 exhibits slower nucleation in the presence of SnO₂—NPs [Ref. 15].

We confirmed the composition of SnO₂@_monoZIF-8 using energy-dispersive X-ray spectroscopy (EDX). FIGS. 16 and 17 show representative scanning transmission electron microscopy (STEM) images indicating the presence of bright spots within the monolithic matrix. These present some agglomeration at the local level but are well distributed through the monolith. By using EDX (FIG. 18) we confirmed the chemical nature of the SnO₂ bright spots, so demonstrating the successful encapsulation of SnO₂—NPs. We further investigated the sub-surface features of the monolith and the presence of the SnO₂—NPs using focused ion beam (FIB)-SEM. FIGS. 3-6 show images obtained during etching, revealing SnO₂ agglomerates dispersed throughout the monolithic matrix. By providing a solid surface to which nanoparticles with high interfacial energies can adhere, _monoZIF-8 has prevented the worst excesses of NP agglomeration (FIGS. 10 and 11). We found the level of SnO₂—NP loading to be 2.0±0.1 wt. % (Table S1).

X-ray photoelectron spectroscopy (XPS) confirmed the results of FIB-SEM. FIG. 7 shows the FIB-XPS analysis of the 3d region of Sn(IV). This revealed peaks attributable to Sn(3d_5/2) and Sn(3d_3/2) binding energies, centred at 486.7 and 495.5 eV, respectively, confirming the presence of SnO₂ [Ref. 16]. The high energy shoulder on the Sn(3d_3/2) peak is attributed to the presence of ZIF-8 [Ref. 17]. Encouragingly, we detected Sn consistently throughout the etched areas, whilst the external surface spectrum revealed a lower Sn presence. This supports the FIB-SEM micrographs and confirms that minimal SnO₂ is present at the monolith external surface. Discussion of the remaining XPS data is set out further below.

FIG. 8 compares the PXRD patterns of simulated ZIF-8 with experimental _monoZIF-8, SnO₂—NPs, and SnO₂@_monoZIF-8. Fresh SnO₂@_monoZIF-8 revealed minimal peak variation compared to _monoZIF-8, confirming that the SnO₂—NPs do not perturb the crystallinity of the MOF. FIG. 20 shows the N₂ adsorption isotherms for the composite; Table 1 compares the Brunauer-Emmett-Teller (BET) areas, and the micropore and total pore volumes. Both _monoZIF-8 and SnO₂@_monoZIF-8 display typical stepped ZIF-8 adsorption isotherms and an absence of mesoporosity [Ref. 2]. However, the adsorption capacity and BET area of the composite is about 25% lower than that of _monoZIF-8. This is attributed to pore blocking from non-porous phases. Mercury porosimetry revealed the bulk density (envelop or particle density) of SnO₂@_monoZIF-8 to be slightly higher than that of _monoZIF-8, i.e. 1.13 g cm⁻³ vs. 1.05 g cm⁻³.

TABLE 1
BET areas (SBET), micropore volumes (W0), and total
pore volumes (VTOT) for monoZIF-8 and SnO2@monoZIF-
8 before and after exposure to MB and H2O.
	SBET	W0[a|	VTOT[b]
Material	[m2g−1]	[cm3 g−1]	[cm3 g−1]
monoZIF-8	1423	0.543	0.546
SnO2@monoZIF-8	1055	0.413	0.417
SnO2@monoZIF-8 - 1 cycle (MB)	1068	0.421	0.427
SnO2@monoZIF-8 - 5 cycle (MB)	985	0.389	0.393
SnO2@monoZIF-8 - 10 cycle (MB)	1027	0.405	0.411
SnO2@monoZIF-8 - 1 cycle (H2O)	973	0.384	0.389
SnO2@monoZIF-8 - 5 cycle (H2O)	991	0.389	0.393
SnO2@monoZIF-8 - 10 cycle (H2O)	996	0.395	0.399
[a]Data obtained at P/P0 = 0.1
[b]P/P0 = 0.99.

We assessed the photocatalytic activity of SnO₂@_monoZIF-8 using aqueous methylene blue (MB) over multiple catalytic cycles. Each cycle lasted 3 hours, with the composite recovered each time by simple gravity filtration (FIG. 23) before being reused without washing. MB (dimensions: 7.9×16.3×4.0 Å) [Ref. 18] is widely used in the textile industry and represents a common toxic effluent in water supplies [Ref. 19]. By using a dye larger than the apertures of ZIF-8 (i.e. 3.4 Å) [Ref. 2], we have explored the accessibility of the SnO₂—NPs. FIG. 9 shows the degradation of MB in the presence of different amounts of SnO₂@_monoZIF-8 (see also FIG. 25). Low loading experiments utilizing 0.4 g of composite (i.e. 53 μmol of SnO₂—NP) proved SnO₂@_monoZIF-8 to be moderately photoactive, with an average of 41.5±3.0% MB degradation achieved in 3 hours. Importantly, the catalytic performance was sustained, with 39.4±0.6% MB degradation achieved in the 10^th cycle, providing compelling evidence for NP retention in the composite. When increasing the loading to 1.7 g of composite (i.e. 225 μmol catalyst), MB degradation increased to 93.6±2.7% in 3 hours. This is a substantial improvement on previously reported semiconducting nanoparticle-ZIF-8 hybrid materials [Ref. 11]. Previous studies suggest that to achieve appreciable degradation of a dye under comparable conditions, 150-300 μmol of powdered photocatalytic nanoparticles are typically required [Ref. 20].

Interestingly, although the narrow apertures of ZIF-8 preclude the passage of MB, this is not a barrier to photocatalysis. Houas et al. have proposed the following mechanism [Ref. 19], where intimate contact between SnO₂—NPs and dye is not necessary:

SnO2 + hv → e−CB + h+VB 1) Exciton production
O2 + e−CB → O2•−        2) Ionosorption and reduction of
                        O2 (0 to −0.5 eV)
H2O + h+VB → H+ + OH•   3) Production of hydroxyl radicals
O2•− + H+ → HO2•        4) Neutralisation of O2•−
2HO2• → H2O2 + O2       5) H2O2 formation
H2O2 + e−CB → OH• + OH− 6) H2O2 degradation
R + OH• → R′• + H2O     7) Oxidation of dye (R)

In this mechanism, the species active in dye degradation derive from adsorbed oxygen and water [Ref. 14]. In our case, we propose that water, with a 2.68 Å kinetic diameter [Ref. 21], diffuses through the ZIF-8 windows [Ref. 22] and interacts with SnO₂. Reaction with the photoinduced excitons (electrons, e⁻, and holes, h⁺) in the conduction (CB) and valence (VB) bands of the NPs then creates the hydroxyl and superoxide radicals required for dye degradation. The high levels of photocatalytic activity achieved using SnO₂@_monoZIF-8 suggest that SnO₂ far below the monolith surface, and not only that present at the external surface, must be intrinsically involved in the catalytic cycle.

We evaluated the chemical robustness of SnO₂@_monoZIF-8 by PXRD and N₂ adsorption. PXRD patterns of the composite after 1, 5 and 10 photocatalytic cycles showed no significant variations from that of fresh composite (FIG. 8). However, the adsorption isotherms of N₂ showed a decrease in the BET area (Table 1 and FIGS. 21 and 22). We obtained similar values of decrease in BET areas when measuring the adsorption properties of fresh composite after submersion in water for 3-hour cycles, strongly suggesting that the decrease is due to the decomposition of SnO₂@ZIF-8 in water rather than MB adsorption.

Industrial applications require that materials possess the mechanical strength and toughness to withstand the stresses of friction, cyclic compression or vibration within a container. We used the nanoindentation technique to establish that the magnitudes of both the Young's modulus, E, and Hardness, H, of SnO₂@_monoZIF-8 (3.30±0.01 GPa and 0.44±0.01 GPa, respectively) were about 10% greater than those of _monoZIF-8 (3.00±0.01 GPa and 0.41±0.01 GPa, respectively), thereby rendering the composite structurally stiffer and more resistant to permanent deformation (FIGS. 26-34). This is likely attributable to the incorporation of the SnO₂—NPs, leading to a greater packing efficiency of the primary particles [Ref. 23]. SnO₂@_monoZIF-8 was found by thermogravimetric analysis (FIG. 35) to decompose at a lower temperature (450-500° C.) than _monoZIF-8 (600° C.). Importantly, however, the thermal stability of the composite far exceeds the application temperature and is not reduced after recycling.

In summary, we report a chemically and mechanically robust composite in which SnO₂—NPs have been controllably integrated into a monolithic metal-organic framework without the need for binders, additives or high pressures, so avoiding structural amorphization and pore collapse. SnO₂@_monoZIF-8 has shown high levels of photocatalytic activity and extraordinary recyclability when compared to powdered nanoparticles or previously reported NP@MOF composites. Furthermore, the straightforward synthetic method used led to the immobilization of nanoparticles in a way that prevented high degrees of agglomeration. The outstanding level of recyclability coupled with the unprecedented degree of dye degradation seen under high loading of the composite has proven SnO₂@_monoZIF-8 to be a highly effective photocatalyst.

Synthesis of SnO₂ Nanoparticles

SnO₂—NPs were prepared following a modified literature synthesis [Ref. 24]. SnCl₄.5H₂O (0.787 g, 2.24 mmol) was dissolved in water (15 mL). Sodium hydroxide (0.7 g, 17.5 mmol) was dissolved in water (20 mL) and ethanol (20 mL). This was added dropwise to the stannic chloride solution until a pH of 12 was achieved. The mixture was transferred quantitatively (ca. 40 mL) to an autoclave and hydrothermally treated (200° C., 24 hours). After cooling, the resultant precipitate was separated and washed with water and 1:1 ethanol/water mix under centrifugation (7000 rcf). The washed sample was dried in a desiccator overnight, yielding SnO₂—NPs as a white powder.

Synthesis of SnO₂@_monoZIF-8 Monoliths

Zn(NO₃)₂.6H₂O (0.293 g, 0.985 mmol) was dissolved in ethanol (20 mL). 2-methylimidazole (C₄H₆N₂) (0.809 g, 9.85 mmol) was dissolved separately in ethanol (20 mL), and SnO₂—NPs were added (30 mg, 0.198 mmol). Both solutions were ultrasonicated for 20 minutes before being combined. The resulting mixture was stirred for 15 minutes at room temperature then centrifuged (4250 rcf, 10 minutes). The collected solid was washed in ethanol (20 mL, 3 times) and the pellet dried at room temperature overnight, yielding a solid monolith. This was ground into 1-5 mm pieces before activation at 110° C. in a vacuum oven overnight.

Characterization of Materials

Zn(NO₃)₂.6H₂O (98%) and 2-methylimidazole (97%) were purchased from Alfa Aesar; ethanol (>99.5%), SnCl₄.5H₂O and methylene blue were purchased from Sigma-Aldrich; NaOH pellets (>97%) were purchased from Fischer Scientific. Chemicals were used as received, without further purification. SnO₂@_monoZIF-8 was characterised utilising: focused ion beam-X-ray photoelectron spectroscopy (FIB-XPS), focused ion beam-scanning electron microscopy (FIB-SEM), transmission electron microscopy (TEM), scanning transmission electron microscopy-energy dispersive X-ray spectroscopy (STEM-EDX), thermogravimetric analysis (TGA), powder X-ray diffraction (PXRD), N₂ adsorption isotherms at 77 K, mercury porosimetry, nanoindentation studies, attenuated total reflectance FT infrared spectroscopy (FT-IR), inductively coupled plasma-optical emission spectroscopy (ICP-OES) and elemental analysis (EA) techniques.

Photocatalytic properties were explored by monitoring the degradation of model organic volatile methylene blue (MB) under simulated solar irradiation produced by a 150 W xenon lamp fitted with an air mass 1.5 global (AM 1.5 G) filter (Solar Simulator model LSO106, 1 sun illumination, 100 mW cm⁻²). The degradation of aqueous MB (25 mL, 1.55×10⁻⁵ M, pH 7.30) was recorded by monitoring the reduction in λ_max at 664 nm using a BOECO S-22 and a Perkin Elmer Lambda 750 UV/vis/NIR spectrometer for single and multi-wavelength measurements, respectively. An ice-cold water bath prevented dye evaporation under impeding light and thermal dye degradation. Control experiments were run (i) without irradiation in the presence of SnO₂@_monoZIF-8 and (ii) with irradiation in the absence of composite. Low loading experiments used 0.4 g of composite, whilst high loading sets used 1.7 g. Composite was collected under gravity filtration and dried under ambient conditions overnight before recycling. Each cycle under solar irradiation was performed parallel to a control in the dark, administering the same recycling procedure. All experiments were triplicated. Hydroxyl radicals produced during photocatalysis were detected using a terephthalic acid probe.

PXRD patterns were measured on a PANalytical Empyrean diffractometer fitted with an X'celerator detector and using a Cu-Kα₁ (λ=1.5406 Å) source with a step size of 0.002° and a scanning speed of 0.022° s⁻¹ at 40 kV and 40 mA. SEM images were obtained on a FEI Helios Nanolab with an accelerating voltage of 5 keV. TEM images were collected on a FEI Tecnai G2 and a FEI Osiris S/TEM operated in scanning mode with an accelerating voltage of 200 keV. For the TEM images of the mother liquor, a 1 mL sample of the reaction medium was withdrawn after 15 minutes and diluted 10 times in ethanol. 25 μL of the resulting solution was drop-coated onto a copper grid and the ethanol evaporated at room temperature. For high angle annular dark field (HAADF) images and EDX analysis the monolithic sample was pressed into a copper grid, with the EDX signal collected using a set of Bruker Super-X detectors. Thermogravimetric analyses were performed on TA Instruments TGA 500, ranging from room temperature to 750° C. in nitrogen, using a ramp rate of 10° C. min⁻¹. N₂ adsorption isotherms were obtained at 77 K using a Micrometrics 3 Flex instrument. All samples were degassed in situ at 110° C. for 6 hours before measurement. The recycled SnO₂@_monoZIF-8 samples were not washed after photocatalysis. Mercury porosimetry data was obtained using an AutoPore IV 9500 instrument employing pressures up to 2000 bar. An Exeter analytical CE 440 elemental analyser at a combustion temperature of 975° C. was utilised for C, H, and N analysis whilst Zn and Sn analysis was performed on a Thermo Scientific iCAP 7400 ICP-OES analyser against 1 ppm and 10 ppm standards. SnO₂@_monoZIF-8 was filtered, soaked in deionised water, and dried under conventional and vacuum oven environments before elemental analyses were performed again. FIB-XPS measurements were obtained using a Thermo Scientific K-Alpha system. The binding energy was calibrated internally based on the C(1s) line position. Each etch was conducted at full power (ion energy=3000 eV, current=‘high’) for 20 seconds. The estimated sputter rate of the Ta₂O₅ source was 0.68 nm sec⁻¹, leading to an estimated total etching depth of 122 nm, whilst the diameter of the area analysed was 400 μm. FT-IR spectra were collected on a Thermo Scientific Nicolet iS50 FT-IR spectrometer in ATR mode. Nanoindentation measurements were performed using an MTS Nano Indenter XP system equipped with a Berkovich diamond tip. The continuous stiffness method was employed and epoxy mounted monolithic samples were indented up to a maximum surface penetration depth of 2000 nm, in accordance with the established methodology for characterizing MOFs [Ref. S1], taking Poisson's ratio of 0.33 [Ref. S2], to determine the upper bounds of Young's modulus, E. In photocatalytic experiments, 3 mL aliquots taken at 15-minute intervals over three hours gave the concentration of dye as a function of time. Each aliquot was returned to the original dye solution immediately after analysis. Hydroxyl radicals (OH^⋅) produced during photocatalysis were detected by dispersing 0.4 g of SnO₂@_monoZIF-8 in a basic aqueous solution of terephthalic acid (10⁻⁴ M). The solution was exposed to simulated solar irradiation and the maximum fluorescence emission intensity of 2-hydroxyterephthalic acid measured after excitation at 315 nm.

The diffraction pattern (FIG. 12) was analyzed using the Scherrer (Equation S1) and Williamson-Hall (Equation S2) equations to give estimates of particle size by accounting for size and strain broadening.

$\begin{array}{cc}D=\frac{K\lambda }{\beta \cos \theta }& \left(\mathrm{Equation}\mathrm{S1}\right)\\ \beta \cos \theta =\frac{k\lambda }{D}+\eta \sin \theta & \left(\mathrm{Equation}S2\right)\end{array}$

where D is the mean crystallite size, β is the full-width-at-half-maximum (FWHM) in radians, θ is the angle in degrees, λ is the wavelength of incident radiation (1.5406 Å for the Cu-Kα₁ source), η is the strain in the crystallite lattice, K is the dimensionless shape factor and k is a constant, typically close to unity [Ref. S3].

The (110), (211), (112), (202) and (200) peaks were utilized in the Williamson-Hall analysis (Equation S2), assuming a constant of unity.

$\frac{\beta \cos \theta }{\lambda }$

was plotted against

$\frac{\sin \theta }{\lambda }$

to give an intercept of

$\frac{1}{D}$

and gradient η, which were used to determine crystallite size and lattice strain respectively.

Peak broadening in the PXRD pattern indicated small particle size, with the Scherrer formula (Equation S1) giving an average crystallite size of 5.03 nm, assuming a dimensionless shape factor of 0.89 (FIG. 12). It is important to note that this gives a lower limit for particle size. The value is in close agreement with results obtained from the Williamson-Hall plot [Ref. S4], which gives an average crystallite size of 5.17 nm and a strain of −0.0188 (FIG. 13). This negative strain value indicates a compressive lattice strain in the nanoparticles. Diffraction peaks were indexed to the tetragonal crystal structure known to be associated with SnO₂ using the (200) and (002) peaks, producing lattice parameters, a=4.729 Å and c=3.172 Å, in good agreement with reported values (JCPDS card no. 41-1445).

SnO₂ @_monoZIF-8 Analysis

TABLE S1
Chemical microanalyses of monoZIF-8 (simulated and experimental) and
fresh SnO2@monoZIF-8 based on nitrogen and tin contributions
acquired from elemental analysis and ICP-OES data. Errors were
determined using the standard deviation in triplicated Sn and N wt % values
with zero readings occurring due to numerical rounding.
Deviation from 100% total loading is attributed to residual
reagents and solvents trapped in the materials.
	Composition
	Wt. %
Materials	C	H	N	Sn	Zn	SnO2	ZIF-8
Sim. ZIF-8	42.2	4.4	24.6	—	28.7	—	100
Exp. monoZIF-8	41.7 ± 0.0	4.5 ± 0.0	24.4 ± 0.3	—	26.2 ± 0.4	—	99.0 ± 1.1
SnO2@monoZIF-8	40.5 ± 0.4	4.6 ± 0.1	23.1 ± 0.3	1.6 ± 0.1	24.5 ± 0.4	2.0 ± 0.1	93.9 ± 1.2

The O(1s) etched levels revealed a peak at 530.6 eV, characteristic of lattice oxygen in SnO₂ (FIG. 19c) [Ref. S5]. Individual spectra of the remaining elements of interest (FIGS. 19a, 19b and 19d for Zn, N and C spectra, respectively) as well as survey spectra (FIG. 20) showed similar homogeneity and consistent peak distribution throughout the etched areas of the composite. The O(1s) spectra (FIG. 19c) revealed a higher percentage of oxygen at the unetched MOF surface than at the subsequently etched levels. This is attributed to oxygen adsorption at the composite surface with a binding energy of 531.8 eV [Refs. S6, S7]. Asymmetric broadening in the O(1s) spectra represents oxygen physically adsorbed to the SnO₂—NPs [Ref. S8].

Inspection of the cavity dimensions of pure ZIF-8 (11.6 Å) indicates that the nanoparticles do not reside in the MOF pores, which are too small to accommodate them. Instead, the nanoparticles are encapsulated by the grown ZIF-8 matrix.

Control experiments for the photocatalytic degradation of MB were performed: (i) without solar irradiation in the presence of composite (SnO₂@_monoZIF-8) and (ii) with solar irradiation in the absence of composite (FIGS. 24 and 25). A final control experiment, (iii), was conducted to assess the photocatalytic properties of _monoZIF-8. Low loading and high loading experiments were performed using 0.4 and 1.7 g of composite or _monoZIF-8, respectively. The recyclability was demonstrated by reassessing catalytic activity with fresh dye solution for nine further cycles. Each cycle under solar irradiation was performed parallel to control (i), administering the same gravity filtration recycling procedure in each case.

The degree of degradation was calculated according to the reduction in absorption for the major MB absorption band at λ_max=664 nm over 3 hours:

$\begin{array}{cc}\mathrm{Degradation}\text{/}\%=100\times \left(1-\frac{C_t}{C_0}\right)& \left(\mathrm{Equation}\mathrm{S3}\right)\end{array}$

where C₀ is the starting concentration of MB and C_t is the concentration of MB after time t.

Triplicated data indicate an average degradation of 18.3±1.4% under simulated solar irradiation in the absence of composite. Error is calculated from the standard deviation in triplicated values. A number of MOFs are known to have photocatalytic properties of their own [Refs. S9 and S10], with the partial degradation of MB under nanoparticulate ZIF-8 previously attributed to the wide band gap of the semiconducting material. This was explained by the proposed ligand-to-metal-charge-transfer (LMCT) of a 2p HOMO electron from the nitrogen linker into the empty zinc LUMO orbital under stimulation from a UV source [Refs. S11 and S12]. For these reasons it was essential to establish whether _monoZIF-8 represented a source of potential dye degradation in the current work. Triplicated control experiment (iii) revealed that _monoZIF-8 presents no photocatalytic behavior under simulated solar irradiation, with measured dye degradation attributable to surface physisorption. This is consistent with literature solid-state UV-Vis data for powdered ZIF-8, which suggests that a large band gap of 4.9 eV prevents exciton formation under solar irradiation [Ref. S13]. However, inspection of the valence and conduction band potentials of SnO₂ reveals that they are positioned such that production of hydroxyl and superoxide radicals, the key species responsible for dye degradation [Refs. S14 and S15], is thermodynamically viable [Ref. S16].

The thermal stability of fresh and recycled SnO₂@_monoZIF-8 was measured by TGA. We found that the decomposition temperature for SnO₂@_monoZIF-8 (450-500° C.) is lower than that of _monoZIF-8 (600° C.). This is expected due to the nanoparticles disrupting the coordination bonds within the MOF, promoting thermal decomposition [Ref. S17]. FIG. 35 shows an initial weight loss of 2.5%, 4.0%, 4.5%, 4.5% and 5.5% at 250° C. for _monoZIF-8, fresh SnO₂@_monoZIF-8 and SnO₂@_monoZIF-8 after 1, 5 and 10 catalytic cycles, respectively. As SnO₂ is very thermally stable, the initial weight loss is attributed to ethanol and water adhered to the pure nanoparticles and trapped in the composite materials.

Even allowing for their flexibility, the narrowness of the 3.4 Å windows of ZIF-8 suggests that the dye cannot pass through its framework apertures. Dye adsorption is thought to occur predominantly via physisorption to the external surface of the monoliths rather than via chemisorption or coordination to zinc clusters [Refs. S6 and S18]. Spectra for SnO₂, _monoZIF-8, fresh SnO₂@_monoZIF-8 and SnO₂@_monoZIF-8 after 10 catalytic cycles were recorded in the range of 400-4000 cm⁻¹ (FIGS. 36 and 37). Whilst SnO₂ displays peaks at 1641 and 3337 cm⁻¹ corresponding to bending and stretching modes of adsorbed water [Refs. S19 and S20], respectively, the characteristic peaks of the stretching vibrations of Sn—O at 463 and 608 cm⁻¹ are not visible in the SnO₂@_monoZIF-8 spectrum [Refs, S21 and S22]. This is attributed to the relatively low loading of the nanoparticles. Importantly, the key peaks associated with the bending (1668 cm⁻¹) and stretching (1583 cm⁻¹) vibrations of N—H [Ref. S23] as well as the Zn—N stretching vibration [Ref. S24] (420 cm⁻¹) and ring stretch region [Ref. S25] (550-1500 cm⁻¹) in SnO₂@ZIF-8 do not differ in magnitude or frequency on going from the fresh to the cycled composite, suggesting no disruption of the composite bonding regime after exposure to MB dye. Furthermore, no evidence of a NH—O peak [Ref. S26] (3370 cm⁻¹), Zn—O peak [Ref. S6] (478 cm⁻¹) is observed in the spectrum of the cycled composite. These would be expected to be seen if the composite was exhibiting chemisorption to the degradation products of MB [Ref. S27]. This is consistent with there being no chemisorption of dye to the monolith surface.

A terephthalic acid (TA) probe was used to prove OH^⋅ radical production. Reaction of TA with OH^⋅ radicals generates the fluorescent species 2-hydroxyterephthalic acid. The formation of this molecule was monitored using the maximum intensity at 450 nm after excitation at 315 nm, and it was seen to increase with irradiation time (FIG. 38), indicating the photogeneration of OH^⋅. This strongly endorses the photocatalytic mechanism proposed above.

The vol % of nanoparticles in the composite is determined based on the density of the nanoparticles, the wt % of the nanoparticles and the density of the composite. In the example of SnO₂@_monoZIF-8, the nanoparticles of SnO₂ have density 6.95 g/cm³ and 2 wt % and the density of the composite is 1.13 g/cm³.

Relative Photonic Efficiency ξ_r

It is known in the art of photogenerated catalysis and catalysed photolysis that it can be important to provide for the reliable determination and comparison of the efficiency of a particular photocatalyst material to catalyse the degradation of a particular target molecule when subjected to a particular excitation radiation. Therefore in this disclosure the relative photonic efficiency ξ_r of the nanoparticles is considered. The relative photonic efficiency ξ_r of the nanoparticles can be represented as:

${\xi }_r=\frac{R^{\mathrm{in}}\left(\mathrm{nanoparticles}\right)}{R^{\mathrm{in}}\left(P25\right)}$

wherein:

Rⁱⁿ(P25) is the initial rate of degradation of 200 μM phenol in an air-equilibrated aqueous dispersion by standard titania particles (Degussa P-25 TiO₂) at 2 g/L under AM1 simulated sunlight radiation.

Rⁱⁿ(nanoparticles) is the initial rate of degradation of 200 μM phenol in an air-equilibrated aqueous dispersion by the nanoparticles (isolated from the MOF of the composite body) at 2 g/L under AM1 simulated sunlight radiation.

Other than the nature of the catalyst particles, the experiments to determine Rⁱⁿ(P25) and Rⁱⁿ(nanoparticles) are carried out in identical experimental conditions. This follows the guidance for the determination of relative photonic efficiency ξ_r given by Serpone and Salarino (1999) [Ref. S28], the entire content of which is hereby incorporated by reference.

In effect, therefore, r of the nanoparticles is determined relative to the corresponding photocatalytic efficiency of a standard catalyst (P-25 titania) to degrade a standard target molecule (phenol) under otherwise identical experimental conditions.

Degussa P-25 TiO₂ consists of two crystalline phases, with about 80% anatase and about 20% rutile and contains traces of SiO₂, Al₂O₃, HCl and Fe. It is nonporous with a BET specific surface area of about 55 m²/g. The particle diameter is in the range 25 to 35 nm.

Rⁱⁿ(P25) and Rⁱⁿ(nanoparticles) are tested using a method based on Kar et al. (2016) [Ref. S29]. The method is as follows. Composite containing 5.0 mg of catalyst (from ICP analysis) to be added to 25 mL of a 1.0×10⁻⁵ M aqueous solution of dye (pH 7), and the mixture stirred in the dark for 2 hours to allow adsorption on the composite surface. Determine the absorption of a 3.0 mL aliquot of the mixture by UV-Vis to obtain the dye concentration before photocatalysis (C0) then return the aliquot to the reaction. Irradiate with a 150 W xenon lamp fitted with an air mass 1.5 global (AM 1.5 G) filter (1 sun illumination, 100 mW cm⁻²). 3 mL aliquots to be taken at 15 minute intervals over 3 hrs to obtain the concentration of dye as a function of time by UV-Vis. Each aliquot to be returned to the original dye solution immediately after analysis. Use an ice cold water bath to prevent evaporation during catalysis and to avoid degradation due to heating. Two reference experiments, i) without light irradiation in the presence of catalyst, and ii) with light irradiation in the absence of catalyst should be done for comparison purposes. Composite to be collected under gravity filtration and dried under ambient conditions overnight before recycling for subsequent catalytic cycles. Each cycle under solar irradiation to be performed parallel to a control in the dark, administering the same recycling procedure. Hydroxyl radicals (OH*) produced during photocatalysis should be estimated using terephthalic acid as a probe molecule and an excitation wavelength of 315 nm. This method relies on the fluorescence signal at 425 nm of 2-hydroxyterephthalic acid.

In this method, the nanoparticles are tested in situ in the composite with the MOF. For strict adherence to the definition of the relative photonic efficiency r of the nanoparticles, the nanoparticles can be tested in an air-equilibriated aqueous dispersion, without MOF encapsulant. Where the nanoparticles are provided in the form of a composite with MOF, the nanoparticles can be isolated by digesting the MOF, e.g. at low pH. In the cases of the MOF being ZIF-8, a pH below 4-5 is suitable.

For further strict adherence to the definition of the relative photonic efficiency ξ_r of the nanoparticles, the 1.0×10⁻⁵ M aqueous solution of dye (pH 7) can be replaced with 200 μM phenol.

Further Experimental Work

We report here some additional experimental work that has been carried out to demonstrate further compositional embodiments. Specifically, the following materials were synthesised:

CdSe@ZIF-8_mono

Au@ZIF-8_mono

(PdO/TiO₂)@ZIF-8_mono

((Au@PdO)/TiO₂)@ZIF-8_mono

Pd@HKUST-1 _mono

CdSe@ZIF-8_mono was synthesised by adapting the synthesis method for SnO₂@ZIF-8_mono disclosed above, the adaptation being the use of CdSe nanoparticles. FIGS. 39 and 40 show TEM images for CdSe@ZIF-8_mono whereas FIG. 41 shows powder XRD (PXRD) patterns for CdSe@ZIF-8_mono (upper line) and for ZIF-8_mono (lower line), confirming that the crystalline structure of ZIF-8_mono is substantially unchanged by the incorporation of CdSe nanoparticles.

Au@ZIF-8_mono was synthesised by adapting the synthesis method for SnO₂@ZIF-8_monodisclosed above, the adaptations being the following: Synthesis of Au nanoparticles (NP): HAuCl₄.3H₂O (7.88 mg, 0.02 mmol) and trisodium citrate (5.88 mg, 0.02 mmol) were dissolved in DI water (80 mL) and mixed vigorously.

An ice-cold solution of NaBH₄ (9.08 mg, 0.24 mmol) in DI water (2.4 mL) was rapidly injected, causing the solution to turn from pale yellow to bright red/purple. The solution was mixed for 30 seconds at RT before PVP (10 k) (0.5 g) was added and mixed for a further 30 min. The water was removed under vacuum until 2 mL remained. The purple solution was diluted with distilled ethanol (18 mL).

For (PdO/TiO₂)@ZIF-8_mono, Pd/TiO₂ nanoparticles were synthesized as follows: Stearic acid (0.84 g, 2.95 mmol) was dissolved in a solution of ethanol (80 mL) and DI water (20 mL) at 85° C. under rapid stirring. Pd(acac)₂ (0.03 g, 0.1 mmol) was added and the resulting yellow solution was heated under reflux for 4 hours yielding a black solution. A solution of Ti(OBu)₄ (0.4 mL, 1.17 mmol) in ethanol (2 mL) was added dropwise to the rapidly mixing solution. The solution was maintained at reflux for a further 2 hours before being cooled to room temperature. The solution was collected under cebtrifugation (5.5 k RCF, 10 min) and washed in alternating water/ethanol (1:7, 2×40 mL) and ethanol (2×40 mL) solutions. The resulting NPs were suspended in ethanol (20 mL) and dried under vacuum overnight before being heated in a furnace at 500° C. for 3 hours, yielding a brown solid.

For ((Au@PdO)/TiO₂)@ZIF-8_mono, Au@PdO nanoparticles were first formed as follows: HAuCl₄.3H₂O (0.02 g, 0.05 mmol) was dissolved in DI water (2.5 mL) under sonication to give solution A. Na₂PdCl₄ (0.015 g, 0.05 mmol) was dissolved in DI water (2.5 mL) under sonication to give solution B. Solution A and B were mixed together and PVP(40 k) (0.067 g) was added. Under rapid stirring a solution of ascorbic acid (0.07 g, 0.04 mmol) in DI water (0.67 mL) was quickly injected, causing a colour change from bright orange to dark brown. The solution was sonicated for 5 mins before being left to rapidly mix for a further 6 hours at RT. The solution was centrifuged (5.5 k RCF, 20 min.) to obtain a black/brown solid which was washed with DI water (3×40 mL). The resulting NPs were dried under vacuum or re-suspended in DI water (20 mL) and sonicated for 30 mins.

Next, Au@PdO/TiO₂ nanoparticles were formed as follows: The Au@PdO NP aqueous suspension (20 mL) was added to a solution of stearic acid (0.84 g, 2.95 mmol) in ethanol (80 mL) at RT. Under rapid stirring a solution of Ti(Obu)₄ (0.4 mL, 1.17 mmol) in ethanol (2 mL) was added dropwise. The resulting grey mixture was heated to 115° C. over 10 mins and maintained at this temperature for 2 hours. The solution was cooled to RT and washed in alternating water/ethanol (1:7, 2×40 mL) and ethanol (2×40 mL) solutions before being dried under vacuum. The resulting grey powder was heated in a furnace at 500° C. for 3 hours.

FIGS. 42, 43, 45 and 46 show TEM images for Au@ZIF-8_mono. The magnified image shown in FIG. 43 is of the area indicated in FIG. 42. FIG. 44 shows the particle size distribution of Au nanoparticles in Au@ZIF-8_mono. The measured average particle size of Au nanoparticles was 2.60±0.96 nm (assessed over 200 particles). The largest Au particles (very rarely seen) were never more than about 7 nm in diameter.

FIG. 47 shows a scanning transmission electron microscope—high-angle annular dark field (STEM-HAADF) image of (PdO/TiO₂)@ZIF-8_mono. FIGS. 48, 49 and 50 show elemental maps, for the particle imaged in FIG. 47, of Zn, Pd and Ti, respectively. FIG. 51 shows powder XRD (PXRD) patterns for (PdO/TiO₂)@ZIF-8_mono (upper line) and for ZIF-8_mono (lower line). Specific peaks of interest in the (PdO/TiO₂)@ZIF-8_mono pattern are labelled. Via ICP-AES (Inductively Coupled Plasma Atomic Emission Spectroscopy), the proportions of Pd, Zn and N were found to be: Pd—0.7%, Zn—24.5%, N—21.1%. Via calculation, the amount of ZIF-8 was 85.3% and the amount of TiO₂ was 14%.

FIGS. 52, 53, 54 and 55 show elemental maps for Zn, Ti, Au and Pd, respectively for a ((Au@PdO)/TiO₂)@ZIF-8_mono particle imaged via scanning transmission electron microscopy—high-angle annular dark field (STEM-HAADF). FIG. 56 shows powder XRD (PXRD) patterns for ((Au@PdO)/TiO₂)@ZIF-8_mono (upper line) and for ZIF-8_mono (lower line). Specific peaks of interest in the ((Au@PdO)/TiO₂)@ZIF-8_mono pattern are labelled.

FIG. 57 shows a TEM image for Pd@HKUST-1_mono, whereas FIG. 58 shows the response of Pd@HKUST-1_mono to thermogravimetric analysis (TGA).

While the invention has been described in conjunction with the exemplary embodiments described above, many equivalent modifications and variations will be apparent to those skilled in the art when given this disclosure. Accordingly, the exemplary embodiments of the invention set forth above are considered to be illustrative and not limiting. Various changes to the described embodiments may be made without departing from the spirit and scope of the invention.

All references referred to above and/or listed below are hereby incorporated by reference.

LIST OF NON-PATENT DOCUMENT REFERENCES

• [1] Y. Liu, Y. Ma, Y. Zhao, X. Sun, F. Gándara, H. Furukawa, Z. Liu, H. Zhu, C. Zhu, K. Suenaga, P. Oleynikov, A. S. Alshammari, X. Zhang, O. Terasaki, O. M. Yaghil, Science 2016, 351, 365-369.
• [2] D. Fairen-Jimenez, S. A. Moggach, M. T. Wharmby, P. A. Wright, S. Parsons, T. Düren, J. Am. Chem. Soc. 2011, 133, 8900-8902.
• [3] D. Fairen-Jimenez, R. Galvelis, A. Torrisi, A. D. Gellan, M. T. Wharmby, P. A. Wright, C. Mellot-Draznieks, T. Düren, Dalton Trans. 2012, 41, 10752-10762.
• [4] M. Jian, B. Liu, G. Zhang, R. Liu, X. Zhang, Colloids Surfaces A Physicochem. Eng. Asp. 2015, 465, 67-76.
• [5] T. Tian, J. Velazquez-Garcia, T. D. Bennett, D. Fairen-Jimenez, J. Mater. Chem. A 2014, 3, 2999-3005.
• [6] Y. Gao, J. Wu, W. Zhang, Y. Tan, J. Zhao, B. Tang, Mater. Lett. 2014, 128, 208-211.
• [7] A. Ahmed, M. Forster, R. Clowes, P. Myers, H. Zhang, Chem. Commun. 2014, 50, 14314-14316.
• [8] T. Berger, O. Diwald, Photocatalysis: Fundamentals and Perspectives, Royal Society Of Chemistry, Cambridge, 2016, pp 185-217.
• [9] H. Fujii, M. Ohtaki, K. Eguchi, H. Arai, J. Mol. Catal. A Chem. 1998, 129, 61-68.
• [10] G. Lu, S. Li, Z. Guo, O. K. Farha, B. G. Hauser, X. Qi, Y. Wang, X. Wang, S. Han, X. Liu, J. S. DuChene, H. Zhang, Q. Zhang, X. Chen, J. Ma, S. C. J. Loo, W. D. Wei, Y. Yang, J. T. Hupp, F. Huo, Nat. Chem. 2012, 4, 310-316.
• [11] T. T. Isimjan, H. Kazemian, S. Rohani, A. K. Ray, J. Mater. Chem. 2010, 20, 10241-10245.
• [12] R. Vinu, G. Madras, J. Indian Inst. Sci. 2010, 90, 189-230.
• [13] A. Kar, A. Patra, J. Mater. Chem. C 2014, 2, 6706-6722.
• [14] A. Kar, S. Sain, D. Rossouw, B. R. Knappett, S. K. Pradhan, A. E. H. Wheatley, Nanoscale 2016, 8, 2727-2739.
• [15] J. Cravillon, R. Nayuk, S. Springer, A. Feldhoff, K. Huber, M. Wiebcke, Chem. Mater. 2011, 23, 2130-2141.
• [16] Y.-d. Wang, C.-I. Ma, X.-d. Sun, H.-d. Li, Nanotechnology 2002, 13, 565-569.
• [17] M. Zahmakiran, Dalton Trans. 2012, 41, 12690-12696.
• [18] X. Zhao, X. Bu, T. Wu, S.-T. Zheng, L. Wang, P. Feng, Nat. Commun. 2013, 4, 2344-2352.
• [19] A. Houas, H. Lachheb, M. Ksibi, E. Elalouui, C. Guillard, J.-M. Herrmann, Appl. Catal. B Environ. 2001, 31, 145-157.
• [20] C. Tian, Q. Zhang, A. Wu, M. Jiang, Z. Liang, B. Jiang, H. Fu, Chem. Commun. 2012, 48, 2858-2860.
• [21] T. Borjigin, F. Sun, J. Zhang, K. Cai, H. Ren, G. Zhu, Chem. Commun. 2012, 48, 7613-7615.
• [22] P. Horcajada, T. Chalati, C. Serre, B. Gillet, C. Sebrie, T. Baati, J. F. Eubank, D. Heurtaux, P. Clayette, C. Kreuz, J.-S. Chang, Y. K. Hwang, V. Marsaud, P.-N. Bories, L. Cynober, S. Gil, G. Ferey, P. Couvreur, R. Gref, Nat. Mater. 2010, 9, 172-178.
• [23] J. Silvestre, N. Silvestre, J. De Brito, J. Nanomater. 2015, 2015, 106494-106507.
• [24] A. Kar, S. Kundu, A. Patra, J. Phys. Chem. C, 2011, 115, 118-124.
• [S1] J. Tan, T. D. Bennett, A. K. Cheetham, Proc. Natl. Acad. Sci. U.S.A 2010, 107, 9938.
• [S2] J. C. Tan, B. Civalleri, C. C. Lin, L. Valenzano, R. Galvelis, P. F. Chen, T. D. Bennett, C. Mellot-Draznieks, C. M. Zicovich-Wilson, A. K. Cheetham, Phys. Rev. Lett. 2012, 108, 1.
• [S3] X. Xu, J. Zhuang, X. Wang, J. Am. Chem. Soc. 2008, 130, 12527.
• [S4] G. Williamson, W. Hall, Acta Metall. 1953, 1, 22.
• [S5] A. Kar, S. Sain, D. Rossouw, B. R. Knappett, S. K. Pradhan, A. E. H. Wheatley, Nanoscale 2016, 8, 2727.
• [S6] M. Jian, B. Liu, G. Zhang, R. Liu, X. Zhang, Colloids Surfaces A Physicochem. Eng. Asp. 2015, 465, 67.
• [S7] J.-C. Dupin, D. Gonbeau, P. Vinatier, A. Levasseur, Phys. Chem. Chem. Phys. 2000, 2, 1319.
• [S8] L. Cao, H. Wan, L. Huo, S. Xi, J. Colloid Interface Sci. 2001, 244, 97.
• [S9] M. Fuentes-Cabrera, D. M. Nicholson, B. G. Sumpter, M. Widom, J. Chem. Phys. 2005, 123, DOI 10.1063/1.2037587.
• [S10] M. A. Nasalevich, M. van der Veen, F. Kapteijn, J. Gascon, CrystEngComm 2014, 16, 4919.
• [S11] H.-P. Jing, C.-C. Wang, Y.-W. Zhang, P. Wang, R. Li, RSC Adv. 2014, 4, 54454.
• [S12] L. Sun, M. G. Campbell, M. Dince, Angew. Chemie—Int. Ed. 2016, 55, 3566.
• [S13] F. Wang, Z.-S. Liu, H. Yang, Y.-X. Tan, J. Zhang, Angew. Chemie 2011, 123, 470.
• [S14] S. Wu, H. Cao, S. Yin, X. Liu, X. Zhang, J. Phys. Chem. C 2009, 113, 17893.
• [S15] B. Esen, T. Yumak, A. Sinag, T. Yildiz, Photochem. Photobiol. 2011, 87, 267.
• [S16] R. Vinu, G. Madras, J. Indian Inst. Sci. 2010, 90, 189.
• [S17] B. K. Kandola, D. Deli, in Polym. Green Flame Retard. (Eds.: C.D. Papaspyrides, P. Kiliaris), Elsevier, Oxford, 2014, pp. 503-549.
• [S18] I. B. Vasconcelos, T. G. Da Silva, G. C. G. Militão, T. a. Soares, N. M. Rodrigues, M. O. Rodrigues, N. B. Da Costa, R. O. Freire, S. A. Junior, RSC Adv. 2012, 2, 9437.
• [S19] S. Blessi, M. M. L. Sonia, S. Vijayalakshmi, S. Pauline, Int. J. chem Tech Res. 2014, 6, 2153.
• [S20] Q. Li, X. Yuan, G. Zeng, Shiquan Xi, Mater. Chem. Phys. 1997, 47, 239.
• [S21] Y. Wang, L. Tan, L. Wang, J. Nanomater. 2011, 2011, DOI 10.1155/2011/529874.
• [S22] J. Zhang, L. Gao, J. Solid State Chem. 2004, 177, 1425.
• [S23] Y. Shen, Y. Zhang, Q. Zhang, L. Niu, T. You, A. Ivaska, Chem Commun 2005, 4193.
• [S24] M. He, J. Yao, Q. Liu, K. Wang, F. Chen, H. Wang, Microporous Mesoporous Mater. 2014, 184, 55.
• [S25] Y. Hu, H. Kazemian, S. Rohani, Y. Huang, Y. Song, Chem. Commun. (Camb). 2011, 47, 12694.
• [S26] C. H. Rochester, G. H. Yong, J. Chem. Soc., Faraday Trans. 1 1980, 76, 1158.
• [S27] R. Zuo, G. Du, W. Zhang, L. Liu, Y. Liu, L. Mei, Z. Li, 2014, 2014, 1.
• [S28] N. Serpone and A. Salarino, “TERMINOLOGY, RELATIVE PHOTONIC EFFICIENCIES AND QUANTUM YIELDS IN HETEROGENEOUS PHOTOCATALYSIS. PART I: SUGGESTED PROTOCOL” Pure & Appl. Chem., Vol. 71, No. 2, pp. 303-320, 1999.
• [S29] Kar et al. (2016), Nanoscale, 2016, 8, 2727-2739.

Claims

1. A monolithic metal-organic framework (MOF) composite body selected from the group consisting of: (i) a MOF composite body comprising: MOF crystallites adhered to each other via a binder comprising MOF;at least 0.15 vol % nanoparticles encapsulated in the MOF body, the nanoparticles having an average particle size corresponding to an average particle diameter in the range 3-200 nm; and(ii) a MOF composite body consisting of: MOF crystallites;a binder formed of MOF which binds the MOF crystallites together in the body;at least 0.15 vol % nanoparticles encapsulated in the MOF body, the nanoparticles having an average particle size corresponding to an average particle diameter in the range 3-200 nm;optionally, residual solvent; andoptionally, one or more additives, wherein the additives are present in an amount of not more than 10% by mass of the composite body.

2. (canceled)

3. The monolithic MOF composite body according to claim 1 wherein the nanoparticles are photocatalytic nanoparticles.

4. The monolithic MOF composite body according to claim 1 wherein the relative photonic efficiency ξr of the nanoparticles is greater than 1.

5. The monolithic MOF composite body according to claim 1 wherein the nanoparticles are present in the composite in an amount of at most 1 vol %, based on the volume of the composite.

6. The monolithic MOF composite body according to claim 1 wherein the nanoparticles comprise a composition selected from the group consisting of one or a combination of: metal oxides, including for example SnO2, ZnO, TiO2, PdO;Pd, Au, Ru, Rh, Pt;Bi-containing compositions, including for example BiFeO3, Bi2S3, BiVO4 and Bi2Fe3O9;Cd-containing materials, including for example CdSe and CdS;transition metal dichalcogenides, including for example MoS2 and WS2.

7. The monolithic MOF composite body according to claim 6 wherein the nanoparticles comprise at least two different materials having a heterojunction interface between them.

8. The monolithic MOF composite body according to claim 1 wherein the smallest dimension of the composite body is at least 2 mm.

9. The monolithic MOF composite body according to claim 1 having a BET surface area of at least 500 m2g−1.

10. The monolithic MOF composite body according to claim 9 wherein the nanoparticles, when isolated from the MOF composite body have a BET surface area of at most 100 m2 g−1.

11. The monolithic MOF composite body according to claim 1 wherein the MOF comprises a zeolitic imidazolate framework (ZIF).

12. The monolithic MOF composite body according to claim 1 wherein the MOF comprises one or more materials selected from the group consisting of: ZIF-8, HKUST-1, UiO-66, MOF-74, Al-fumarate, NU-1000, MIL-100, MIL-53.

13. (canceled)

14. A process for manufacturing a monolithic metal-organic framework (MOF) composite body, the process comprising the steps: providing MOF precursors;providing nanoparticles having an average particle size corresponding to an average particle diameter in the range 3-200 nm;providing at least one solvent;allowing the reaction of the MOF precursors in the solvent in the presence of the nanoparticles;carrying out a drying stage with a maximum temperature in the drying stage of not more than 80° C. to form a monolithic MOF composite body comprising MOF crystallites adhered to each other via a binder comprising MOF, and incorporating at least 0.15 vol % of the nanoparticles encapsulated in MOF.

15. The process according to claim 14 wherein the drying stage is carried out in a mould so that the composite body is formed to conform to an internal shape of the mould.

16. A method for treating fluid, the method comprising: providing a MOF composite body selected from the group consisting of:(i) a MOF composite body comprising: MOF crystallites adhered to each other via a binder comprising MOF;at least 0.15 vol % nanoparticles encapsulated in the MOF body, the nanoparticles having an average particle size corresponding to an average particle diameter in the range 3-200 nm; and(ii) a MOF composite body consisting of: MOF crystallites;a binder formed of MOF which binds the MOF crystallites together in the body;at least 0.15 vol % nanoparticles encapsulated in the MOF body, the nanoparticles having an average particle size corresponding to an average particle diameter in the range 3-200 nm;optionally, residual solvent; andoptionally, one or more additives, wherein the additives are present in an amount of not more than 10% by mass of the composite body; andcontacting the MOF composite body with a fluid to be treated, the nanoparticles interacting with the fluid to be treated.

17. The method according to claim 27 wherein the water to be treated contains an organic dye, the photocatalytic reaction supported by the photocatalytic nanoparticles being a degradation reaction of the organic dye.

18. The method according to claim 17 wherein the organic dye is one or a combination of organic dyes selected from the group consisting of: eosin dyes, rhodamine dyes, xanthene dyes, fluorescein dyes, acridine dyes, anthraquinone dyes, azo dyes, diazonium dyes, fluorine dyes, fluorone dyes, phthalocyanine dyes.

19. The method according to claim 27 wherein the nanoparticles comprise a composition selected from the group consisting of one or a combination of: metal oxides, including SnO2, ZnO, TiO2,Bi-containing compositions, including BiFeO3, Bi2S3, BiVO4 and Bi2Fe3O9Cd-containing materials, including CdSe and CdStransition metal dichalcogenides, including MoS2 and WS2.

20. The method according to claim 27 wherein the electromagnetic radiation is natural sunlight or artificial sunlight.

21. (canceled)

22. The method according to claim 16 wherein the fluid to be treated comprises CO and the nanoparticles comprise Au, the CO being treated by being oxidised.

23. The method according to claim 16 wherein the fluid to be treated comprises hydrogen and the nanoparticles comprising one or more of: Ru, Ru/Rh, Pt, Pdresulting in a hydrogenation reaction.

24. The method according to claim 16 wherein the fluid to be treated comprises water and the nanoparticles comprise Ru, resulting in a hydration reaction.

25. The method according to claim 16 wherein the fluid to be treated comprises methane and the nanoparticles comprising one or more of: PdO/Au/TiO2 or Au @ PdO/TiO2 resulting in a methane oxidation reaction to form methanol.

26. The method according to claim 16 wherein the fluid to be treated comprises water and the nanoparticles comprise Pt, resulting in the formation of hydrogen and oxygen.

27. The method for treating fluid according to claim 16, wherein the fluid is water, the nanoparticles being photocatalytic nanoparticles, the method comprising allowing the MOF composite bodies in contact with the water to be treated to be subjected to electromagnetic radiation suitable for activating at least one photocatalytic reaction supported by the photocatalytic nanoparticles.