This disclosure generally relates to a composite of metal and resin suitable for casings of electronic devices, housings of home electric appliances, structural components, machinery parts, for example, and also to a method for manufacturing the composite.
Composites of metal and resin are used in a variety of industrial fields. For example, a metal layer and a resin layer can be joined together by an adhesive material. Recently, a new method of injection joining for manufacturing composites of metal and resin has be introduced. In this method, a molten resin material is injected onto a metal piece that has been previously inserted into an injection molding mold. The surface of the metal combines with the resin. Before inserting the metal piece into the mold, a surface of the metal piece is treated by an etchant to form a number of micropores so that a stronger bond may be formed with the resin material.
The components in the drawings are not necessarily drawn to scale, the emphasis instead being placed upon clearly illustrating the principles of the present disclosure. Moreover, in the drawings, like reference numerals designate corresponding parts throughout several views.
This disclosure is illustrated by way of example and not by way of limitation in the figures of the accompanying drawings in which like reference numerals indicate similar elements. It should be noted that references to “an” or “one” embodiment in this disclosure are not necessarily to the same embodiment, and such references mean “at least one”.
The metal piece 20 can include a surface 21 defining a plurality of micropores 22. At least one of the micropores 22 can be in the shape of an inverted “V”. Each micropore 22 can include a first inclined hole 221 and a second inclined hole 222 which are both inclined with respect to the surface 21 of the metal piece 20. The first inclined hole 221 and the second inclined hole 222 can be symmetrical around line N shown in
In the illustrated embodiment, the first inclined hole 221 and the second inclined hole 222 can be each sloped at an angle θ in relation to the N-axis, and the angle θ can be in a range from about 15 degrees to about 45 degrees. The micropores 22 can be positioned in an array. In other exemplary embodiments, the micropores 22 can be positioned randomly.
The first inclined hole 221 and the second inclined hole 222 each have a diameter defined as t1, and a depth defined as t2. In one exemplary embodiment, t1 can be in a range from about 100 nanometers (nm) to about 300 nm, and a width-to-depth ratio (t1/t2) can be in a range from about 1:3 to about 1:5.
The resin piece 30 becomes bonded to the metal piece 20 when molten resin material is inserted into a mold holding the metal piece 20, wherein the molten resin material is embedded into the micropores 22. The resin material is a thermoplastic resin which crystallizes as it cools. The crystallized-type thermoplastic resin material can be selected from the group consisting of a composite of polyphenylene sulfide and glass fiber, polyamide, polyethylene terephthalate, and polybutylene terephthalate. When using the polyphenylene sulfide and glass fiber composite, the percentage composition of the glass fiber is in a range from 20 percent to 50 percent.
Each micropore 22 can include the first inclined hole 221 and the second inclined hole 222. When an external force is applied to separate the metal piece 20 and the resin piece 30, the external force is divided into a first force parallel to the bottom of the second inclined hole 222 and a second force vertical to the bottom of the first inclined hole 221. Therefore, the composite 10 of this disclosure has a larger sliding friction than the conventional composite of vertical micropores, allowing an increased bonding strength.
The metal piece 20 can be immersed in the degreasing agent solution having a temperature in an approximate range from 20° C. to 30° C. for 1 to 6 minutes. The concentration of degreasing agent contained in the solution can be in an approximate range of 90 grams/liter (g/l) to 150 grams/liter (g/l). The metal piece 20 is washed with distilled water after being removed from the solution.
In detail, the first inclined holes 221 can be formed by a first plasma etching process with the patterned photoresist layer 40 as a mask. The first plasma etching process can be an isometric plasma etching process applied to the surface 21. The first inclined holes 221 extend through the corresponding openings 41 into the metal piece 20. The plasma can be argon gas or other gases. An etching direction of the plasma can be sloped at an angle tilted from the N-axis, and an etching angle can be in a range from about 5 degrees to 75 degrees.
In one exemplary embodiment, the first inclined hole 221 can be sloped at the angle θ with the N-axis, and the angle θ can be in a range from about 15 degrees to about 45 degrees. The diameter of first inclined hole 221 is t1, and the depth of the first inclined hole 221 is t2. In one exemplary embodiment, t1 can be in a range of about 100 nm to about 300 nm, and a width-to-depth ratio of the first inclined hole 221 can be in a range of about 1:3 to about 1:5.
In detail, the second inclined holes 222 can be formed by a second plasma etching process with the patterned photoresist layer 40 as a mask. The second plasma etching process can be an isometric plasma etching process applied to the surface 21. The second inclined holes 222 extend through the corresponding openings 41 into the metal piece 20. The plasma can be argon gas or other gases. An etching direction of the plasma can be sloped at an angle tilted from the N axis, and an etching angle can be in a range from about 5 degrees to 75 degrees.
In one exemplary embodiment, the second inclined hole 222 can be sloped at the angle θ with the N axis, and the angle θ can be in a range of about 15 degrees to about 45 degrees. The diameter of second inclined hole 222 is t1, and the depth of the second inclined hole 222 is t2. In one exemplary embodiment, t1 can be in a range from about 100 nm to about 300 nm, and the width-to-depth ratio of the second inclined hole 222 can be in a range from about 1:3 to about 1:5. The second inclined hole 222 has a shape substantially similar to the shape of the first inclined hole 221.
When the resin material 30 is embedded in the micropores 22 on the surface 21 of the metal piece 20, the combination strength between the resin and the metal is increased. The method of manufacturing such composite of metal and resin does not need strong acids or alkalis, so the method is more environmentally friendly than the conventional method. Furthermore, normal pressures can be used in the process, and the difficulty of processing is reduced, therefore, the method is more suitable for mass production.
It is believed that the present exemplary embodiments and their advantages will be understood from the foregoing description, and it will be apparent that various changes can be made thereto without departing from the spirit and scope of the exemplary embodiments or sacrificing all of its material advantages.
Number | Date | Country | Kind |
---|---|---|---|
201310503354.3 | Oct 2013 | CN | national |
The present application is a divisional application of U.S. patent application Ser. No. 14/515,935, filed on Oct. 16, 2014, which claims priority to Chinese Application No. 201310503354.3 filed on Oct. 24, 2013, the contents of which are entirely incorporated by reference herein.
Number | Date | Country | |
---|---|---|---|
Parent | 14515935 | Oct 2014 | US |
Child | 15373875 | US |