Patent Application
20070221005
The invention relates to a forged powder metal part and more particularly to a composite powder metal variable boundary part, including a method of manufacture thereof.
There is continuing demand for manufacturing processes that may lessen the cost, time or steps in producing a part. More often than not, the benefits resultantly associated with improving the manufacturing process are necessitated in the first instance by customer requirements to develop and improve products to have superior dimensional, mechanical and/or performance properties. For instance a typical differential side gear may have any or all of the following performance requirements such as: the spline area requiring dimensional precision, high shear strength and brinnelling resistance; the hub and thrust faces requiring dimensional precision, surface finish and case compatibility; the gear geometry requiring dimensional precision, surface finish and optimised profile; and the tooth and core strength may require impact resistance, wear resistance, spalling resistance, and different surface and core metallurgies. Different non-compatible manufacturing processes, i.e. casting, steel forging or powder metal forging, obtain different performance requirements for the same part, advantageously or otherwise.
Referring to
A manufacturing process to improve the performance requirements of powder metal parts is disclosed in U.S. Pat. No. 5,903,815 titled “Composite Powdered Metal Component.” The process teaches a component made from two or more discreet powder metals that are compacted and then sintered. Also, U.S. Pat. No. 6,148,685 titled “Duplex Sprocket/Gear Construction and Method of Making Same,” discloses a method of making a gear made from two or more discreet powder metals that are then also compacted and sintered to obtain the final part. These patents only teach composite powdered metal parts obtained by sintering, in general. No known processes exist which address applying composite powder processes to improve performance features such as improved load bearing upon the tooth flank of a gear while providing impact resistance and bending fatigue resistance in the tooth root; providing a composite variable boundary layer; or making a substantially fully dense part by compaction forging.
Therefore, there is a need for a composite powder metal variable boundary part exhibiting improved impact resistance and bending fatigue resistance in the tooth root. It would also be advantageous to provide a composite variable boundary layer or a substantially fully dense part by compaction forging. There is also a need for a method of producing a variable boundary in a composite powder metal part.
In accordance with the above-mentioned needs, a variable boundary composite powder metal gear exhibiting greater tooth wear resistance on its surface and greater impact resistance in its core is disclosed. The forged composite gear includes a plurality of teeth extending from a core, a first section having a first powder metal material, a second section having a second powder metal material and a variable boundary profile. The variable boundary profile is formed between the first section and the second section, whereby the variable boundary profile provides for greater tooth wear resistance on the teeth and greater impact resistance in the gear core.
For a more complete understanding of this invention, reference should now be made to the inventive aspects illustrated in greater detail in the accompanying drawings and described below.
In all figures, the same reference numerals are used to identify like parts in the various views. Thus, simultaneous reference to the various figures is appropriate. In some instances, for clarity, equivalent parts in different figures may have different reference numbers.
Optionally, a composite material may be strategically utilized for each material section. Also, additional or multiple material sections may be utilized in a preform in order to obtain multiple composite variable boundary profiles on select portions of a final forged part or gear, thereby obtaining select performance features.
The first surface 54 of the gear 50 includes a tip surface 64, a pitch line surface 66, a root fillet surface 68 and a root diameter or land surface 70. The variable boundary profile 58 is substantially represented by the effective boundary of: 2.4 mm at the tip surface; 1.9 mm at the pitch line surface; 0.4 mm at the root fillet surface; and 0.8 mm at the root land surface. While specific numbers are presented in the present embodiment, it is recognized that the variable boundary profile may have any non-constant effective boundary profile over a particular surface cross-section and is not limited to the specific profile here presented and is not intended to be limited by the example here given.
The variable boundary profile 58 may also be represented by a boundary ratio. The effective boundary ratio is given by comparing boundary depths measured at the tip surface 64 to the root fillet surface 68, the pitch line surface 66 to the root fillet surface 68, or the root land surface 70 to the root fillet surface 68. For example, the variable boundary ratio for the tip surface 64 to the root fillet surface 68 is 6:1, the pitch line surface 66 to the root fillet surface 68 is 19:4, and the root land surface 70 to the root fillet surface 68 is 2:1.
Advantageously, the boundary ratio may be 6:1 over the variable boundary profile 58 from the greatest depth to the shallower depth, thereby achieving greater mechanical properties such as tooth wear and impact resistance as desired.
Moreover, it is desirable to select a first powder metal material 55 for the first surface 54 of the teeth 52 achieving a surface hardness of at least 58 HRC in the forged gear. It also may be desirable to have a second powder metal material 57 in the gear core 56 having a hardness of not more than 43 HRC. In this regard, the second powder metal material is selected having effectively a non-hardening material such a low ferrous alloy steel having less than 0.2% carbon and the first powder metal material is a hardening material made from a different ferrous steel having a higher carbon content.
The variable boundary profile 58 advantageously provides a gear having greater tooth wear resistance on the first surface 54 while providing impact resistance in the tooth root 56 or improved shear resistance in the spline 62. The variable boundary profile 58 is representative of the effective boundary profile achieved by strategic compaction forging of a preform. The variable boundary profile 58 resultantly achieved by the forging process as discussed herein.
While the process is described with respect to a differential side gear 50, it is anticipated that the variable boundary profile 58 may be achieved on other parts or gears, including bevel, differential or pinion gears, without limitation.
The differential side gear 50 may be made from a low alloy, fully compacted, ferrous powder metal material for one of the material portions. However, it is anticipated that the gear may be made of various other types of forged powder metal steels.
Turning to the method of making the inventive variable boundary powder metal gear 50,
The mixing step 219, 220 readies each metal powder, including any needed binders or lubricants, by mixing the material until a nearly uniform mixture is achieved ready for filling into a compacting form during the filling step 221, 222. An optional step of separating 223 may be included during the filling steps 221, 222 thereby facilitating the material placement into the compaction form. While two mixing steps 219 and 220, and two filling steps 221 and 222 are shown, it is recognized that additional mixing or filling are necessary for each additional material desired. The filling steps 221, 222 can be sequentially such that the material 55 for the first surface 54 is strategically placed in the preform prior to the material 57 for the second surface 56, for example. In some cases, however, the filling steps 221, 222 may be simultaneous or nearly simultaneous.
The compacting step 224 includes the compaction of at least two different powder metal materials in a compaction form to obtain a preform. Before compacting, filling of a first portion of the compaction form with a first powdered metal material, then, with optional use of a separator 223, filling a second portion of the compaction form with a second powdered metal material. After the filling step of the die cavity is complete, the composite metal powders are compacted within the die cavity to form a preform. The preform includes at least one cross-sectional surface in which the final forged part resultantly obtains a variable boundary profile, as discussed herein. The process is then completed by sintering, forging and cooling steps to achieve a gear having a first section having the first powder metal material and a second section having the second powder metal material. It is noted that the first and second portions in the filling stage resulting in a preform, do not necessarily achieve the same boundary as a first and second sections of the final product.
The sintering step 226 may be accomplished as is known by a person of skill in the art. Optionally, if one of the composite materials is conducive to carburization or “sint-carb” processing, as is know in the art, then the material may include a carburization step to achiever further beneficial results prior to the forging process.
The variable forging or forging step 232 comprises forging the preform at a forge temperature and a forge pressure to obtain a substantially dense, net shape, part. The variable boundary profile for the gear results in nearly symmetrical profiles for each tooth because of the symmetrical nature of the forging process and the symmetrical nature of the preform. However, it is recognized that optional carburization steps or additional forging steps may be used to obtain multiple variable boundary profiles. The variable boundary profile is achieved by utilizing a die set of the forge to variably enhance critical flow of the different metal portions during the forging process. Essentially, the determined boundary of the composite powder metal preform is strategically compressed into the die sections, wherein portions of the preform are stretched and thinned during forging and other portions of the preform are thickened and deepened achieving the different powder metal zones from the composite preform.
In one aspect, the forging step used to obtain the composite variable boundary profile is further enhanced by strategically forming the material boundary layer in the preform to enhance critical flow of the composite powder metal preform during the forging process.
The cooling step 234 allows the forged part to obtain a particular metallurgy resulting in a gear having the desired variable boundary profile. Cooling of the forged part may be by quenching in oil, water, air or by other methods suitable to the powder metal forging process.
Prior to cooling, an optional dwelling step may be included, allowing the forged part to dwell for a period allowing for enhanced properties by allowing the material temperature to stabilize in the part.
Optionally, a preheating step may be included wherein the preform is heated to a pre-forge temperature prior to forging to enhance the desired metal flow during the forging process.
Further, optional post forging operations may include, turning, facing, surface grinding, splining, and broaching of the product depending upon final specification requirements, thereby being ready for washing, packing, or shipping. Because of the multi-material work piece, the finish class of these steps can be improved. For example, a higher spline class is achievable for the spline 62 of
With proper selection and combinations of powder metal, compaction forms, processing times, processing temperatures, processing pressures, forging dies, and cooling method a near-net shape, fully dense product may be obtained having the variable boundary profile, thereby requiring minimal if any machining operations facilitating cost savings and performance improvements.
While various process steps have been presented, they are intended only to be limited in scope or order as indicated in the claims of this invention. Further, while the invention has been described in connection with several embodiments, it should be understood that the invention is not limited to those embodiments. Thus, the invention covers all alternatives, modifications, and equivalents as may be included in the spirit and scope of the appended claims.