COMPOSITE STRUCTURAL COMPONENT AND METHOD OF MAKING SAME

Abstract

A composite includes a board. The board includes: a pair of corrugated layers, each corrugated layer being formed from two corrugated sheets bonded together; and a carboard honeycomb disposed between and bonded to the corrugated layers, the honeycomb being orientated such that the cells extend between the corrugated layers. The board can be cut using conventional machinery without fraying [thereby requiring little or no sanding] and can be edgetaped without being crushed using conventional edge taping machinery.

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present disclosure relates generally to a composite structural component.

2. Prior Art

Composite structural components including composite boards utilizing honeycomb centers have been disclosed in the art. However, known composite boards are either relatively difficult to machine, relatively difficult to edge band or relatively costly to produce.

SUMMARY OF THE INVENTION

Forming one aspect of the invention is a composite comprising a board. The board includes: a pair of corrugated layers, each corrugated layer being formed from two corrugated sheets bonded together; and a carboard honeycomb disposed between and bonded to the corrugated layers, the honeycomb being orientated such that the cells extend between the corrugated layers.

Further advantages and features will become evident upon a review of the detailed description with follows and the appended drawings, the latter being briefly described hereinafter.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a top perspective view of a finished composite component according to one exemplary embodiment of the invention; and

FIG. 2 is a view along 2-2 of FIG. 1.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

A composite component 20 which forms an exemplary embodiment of the present invention is hereinafter described with reference to FIGS. 1 and 2.

Composite component 20 will be seen to include a composite board 10 and an edge band 11.

Composite board 10 includes a honeycomb layer 12, a pair of corrugated layers 14 flanking the honeycomb layer 12, a backer layer 16 overlying each corrugated layer and a cover layer 18 overlying each backer layer 16.

Honeycomb layer 12 shown is formed from 0.5″ honeycomb sheet from Axxon Packaging.

Each corrugated layer 14 is formed from two EB corrugated sheets bonded together and to the honeycomb layer with PVA glue. [For greater certainty, layer 20 is an E flute layer with a thickness of approximately 0.06″ and layer 22 is a B flute layer with a thickness of approximately 0.11″]

Each backer layer 16 is formed from Polybak B90, with a thickness of 0.026″, and is bonded to the adjacent corrugated layer 14 with PVA glue.

Each cover layer 18 is a matte Renolit vinyl with a thickness of 0.008″ bonded to the corrugated layer with PVA glue.

The edge band 11 is made of polyvinyl chloride and surrounds the perimeter of the board 10.

The method of making composite board 10 is described as follows:

• • an EB sheet is put through a glue roller applicator to apply a layer of adhesive to produce a coated EB sheet and a further EB sheet is laid upon the coated EB sheet to form an EBBE combination;
  • the EBBE combination is passed through a pinch roller to form an EBBE sheet;
  • the honeycomb sheet is passed through a double roll glue applicator to apply adhesive on both sides of the honeycomb sheet and is laid upon an EBBE sheet, and a further EBBE is laid upon both, to form an EBBE-honeycomb-EBBE bundle;
  • the EBBE bundle is passed through a pinch roller to produce an EBBE sandwich and the EBBE sandwich is placed in a pneumatic pressure for 20 minutes to produce an EBBE board;
  • the backer and cover layers are applied in a manner analogous to the manner of application of the EBBE layers; and
  • the entire assembly is machined to size using a Homag WIKI Vantage 43 CNC cutting machine armed with the Solid Carbide UN-ruffer 67-445 (½″ dia) and the Solid Carbide Honeycomb Hogger.

Edge band 11 is applied using a Homag Edgebander and PUR glue to form the composite component 20.

Whereas a specific embodiment is herein shown and described, variations are possible. For example:

• • whereas a specific cutter is mentioned, other cutters, such as table saws, band saws and CNC routers can be utilized;
  • whereas EBBE sheets are mentioned, other combinations can be utilized, provided that the thickness of each corrugated layer is at least about ⅜″, which allows for edge banding;
  • whereas a honeycomb layer of 0.5″ is mentioned, thicknesses of up to 2.25″ can be utilized;
  • whereas a PVC edge band is specifically mentioned, ABS and polypropylene can also be used;
  • whereas PUR glue is taught for use in edge banding, hot-melt EVA can also be utilized;
  • whereas a pair of cover layers is shown, these are not essential;
  • whereas PolyBak is specifically mentioned, other strong polymer saturated Kraft papers can be used without sacrificing machinability; and
  • whereas Renolit vinyl is mentioned, other standard general purpose laminates can be used.

An advantageous PVA glue is Helmibond 816, but other glues can be used. Advantages of using PUR glue, for example, are that it sets quickly and can avoid or minimize the need for pressing. However, Helmibond 816 was found to provide a hard glass-like surface upon curing, which provided a board that did not require special handling, that cut using conventional machinery without fraying [thereby requiring little or no sanding] and that could be edgetaped without being crushed using conventional edge taping machinery.

In view of the above, it will be evident that the invention is limited only by the accompanying claims, purposively construed.

Claims

1. A composite comprising: a board includinga pair of corrugated layers, each corrugated layer being formed from two corrugated sheets bonded together;a carboard honeycomb disposed between and bonded to the corrugated layers, the honeycomb being orientated such that the cells extend between the corrugated layers.

2. A composite according to claim 1, wherein the corrugated layers are bonded to the honeycomb by PVA glue.

3. The composite according to claim 1, wherein each corrugated layer comprises a pair of B flute layers bonded together and a pair of E flute layers each bonded to one of the B flute layers.

4. The composite according to claim 3, wherein the E and B flute layers are bonded together with PVA glue.

5. The composite according to claim 3, wherein the E flute layer has a thickness of approximately 0.06″ and the B flute layer has a thickness of approximately 0.11″.

6. The composite according to claim 3, wherein the board further comprises, for each corrugated layer, a backer layer overlying and bonded to said each corrugated layer.

7. The composite according to claim 6, wherein each backer layer is formed from Polybak B90, with a thickness of 0.026″, and is bonded to the adjacent corrugated layer with PVA glue.

8. The composite according to claim 2, wherein the board further comprises, for each backer layer, a cover layer overlying and bonded to said each backer layer.

9. The composite according to claim 8, wherein each cover layer is a matte Renolit vinyl with a thickness of 0.008″ bonded to the corrugated layer with PVA glue.

10. The composite according to claim 2, further comprising an edge band surrounding the edge of the board.

11. The composite according to claim 10, wherein the edge band is PVC and is bonded to the board using PUR glue.