Embodiments of this application relate to the field of flexible display technologies, and in particular, to a composite structure, a flexible display assembly, and a foldable terminal.
With development of flexible display technologies, flexible displays are increasingly used in terminal devices. To maintain flatness and rigidity of screens of flexible displays of foldable terminals, a metal layer is usually disposed under a screen as an under-screen support mechanical part. A material of the metal layer is mainly a stainless steel and a titanium alloy. The stainless steel is a widely used material, but the stainless steel is heavy, which is not conducive to overall weight reduction of a foldable terminal. The titanium alloy is lighter, but costs of the titanium alloy are much higher than those of the stainless steel. In addition, rigidity and strength of the titanium alloy are lower than those of the stainless steel. Consequently, a risk of bending reliability of the titanium alloy is higher than that of the stainless steel, and the titanium alloy has not been widely used currently. To overcome a disadvantage of an under-screen support mechanical part made of a stainless steel or a titanium alloy, it is necessary to provide a flexible display support structure that can simultaneously implement high structural strength, lightweight, and low costs.
In view of this, embodiments of this application provide a composite structure, including a substrate layer and a functional layer. The substrate layer is made of a hard rubber fiber composite material, which has higher strength, a smaller mass, and lower costs compared with a metal material such as a stainless steel. The functional layer may provide the composite structure with functions such as electrical conductivity, thermal conductivity, impact resistance, and the like. The composite structure is used for supporting a flexible display, may provide the flexible display with good rigid support, has a small mass and low costs, and in addition can effectively implement functions such as electrical conductivity, thermal conductivity, impact resistance, and the like, so that product competitiveness of a foldable terminal is improved.
Specifically, a first aspect of embodiments of this application provides a composite structure. The composite structure includes a substrate layer and a functional layer disposed on a surface of at least one side of the substrate layer, where the substrate layer includes a first support member and a second support member that are disposed side by side and a bendable connecting member that is disposed between the first support member and the second support member and that is connected to the first support member and the second support member, a material of the first support member and the second support member includes a hard rubber fiber composite material, and the functional layer includes one or more of an electrically conductive layer, a thermally conductive layer, and an impact-resistant layer. The first support member and the second support member are made of the hard rubber fiber composite material, in other words, a fiber-reinforced hard rubber material, which has a small mass and high strength, can provide good rigid support for a flexible display, has a high weight reduction benefit, and has low material costs, so that product competitiveness of a foldable terminal is improved. The functional layer may be disposed to provide the composite structure with performance such as electrical conductivity, thermal conductivity, impact resistance, and the like, to implement functions such as electrical connection, heat dissipation, and drop resistance of the entire flexible display and a terminal product, meet a multi-functional requirement for a flexible display support structure on the market, and further improve market competitiveness of a foldable terminal product.
In an implementation of this application, the electrically conductive layer includes electrically conductive metal, and the electrically conductive layer has a single-layer or multi-layer structure. The electrically conductive layer may be disposed to enable the composite structure to be effectively electrically connected to another component. The electrically conductive layer may be formed on the substrate layer in a manner of adhesive bonding, electroless plating, electroless plating bonded to electroplating, or metal sheet press-fitting.
In an implementation of this application, the electrically conductive metal includes one or more of copper, silver, gold, nickel, and tin. When the electrically conductive layer has a single-layer structure, the electrically conductive layer may be formed by one type of electrically conductive metal, for example, a single copper layer or a single nickel layer; or may be formed by two or more types of electrically conductive metal, for example, the electrically conductive layer is formed by nickel and gold. Specifically, a local region of the electrically conductive layer may be a gold layer, and another region other than the gold layer is a nickel layer. When the electrically conductive layer has a multi-layer structure, materials of different layers may be the same or different, and each layer may be formed by one type of electrically conductive metal, or may be formed by two or more different types of electrically conductive metal. For example, the electrically conductive layer includes an inner layer and an outer layer, the inner layer is disposed on the substrate layer, and the outer layer is disposed on a side of the inner layer away from the substrate layer. Specifically, the inner layer may include at least one of gold, silver, and copper, the outer layer includes at least one of nickel and tin, and the outer layer may protect the inner layer. Alternatively, the inner layer may be a nickel layer, and the gold layer is locally plated on the nickel layer.
In an implementation of this application, the thermally conductive layer includes one or more of a thermally conductive silicone sheet, a thermally conductive silicone grease, a thermally conductive double-sided tape, a thermally conductive graphite sheet, a graphene sheet, and a graphene oxide sheet. The thermally conductive layer may be disposed to provide the composite structure with a good thermal conductivity function, to provide an effective channel for heat dissipation of the flexible display and the entire terminal product. The thermally conductive layer may be formed on the substrate layer in a manner of adhesive bonding or thermal fusion.
In an implementation of this application, the impact-resistant layer includes one or more of silicone rubber, a thermoplastic elastomer (TPE), polyurethane acrylate (PUA), polyvinyl chloride (PVC) soft rubber, and polyurethane (PU). The impact-resistant layer may be disposed to improve capabilities of the composite structure and the flexible display to resist external impact, to help maintain stability of the composite structure and improve drop-resistant performance of the terminal product. The impact-resistant layer may be formed on the substrate layer in a manner of adhesive bonding or thermal fusion.
In an implementation of this application, the functional layer may be disposed on one side of the substrate layer, or may be disposed on two sides of the substrate layer. The functional layer may completely cover the substrate layer, or may partially cover the substrate layer. For example, the partially covering the substrate layer may be that the functional layer covers only surfaces of the first support member and the second support member of the substrate layer, and does not cover the bendable connecting member. When the functional layers are disposed on two sides of the substrate layer, materials, quantities of layers, thicknesses, and the like of the functional layers on the two sides may be the same, or may be different. The electrically conductive layer, the thermally conductive layer, and the impact-resistant layer may be disposed on the substrate layer in any sequence in a laminated manner.
In an implementation of this application, the hard rubber fiber composite material includes at least one fiber layer and a hard rubber material cured on the fiber layer.
In an implementation of this application, the fiber layer includes unidirectional fiber fabric and/or woven fiber fabric. In other words, a fiber weaving manner of each fiber layer may be unidirectional weaving, or may be multi-directional weaving.
In an implementation of this application, the hard rubber material includes rigid resin and/or rigid rubber. A support member used for supporting a main body of the flexible display needs to have high rigidity, and rigid resin and/or rigid rubber may be selected to meet a rigidity requirement.
In an implementation of this application, the hard rubber material includes one or more of epoxy resin, phenolic resin, amino resin, unsaturated polyester, silyl ether resin, polyolefin, polyamide, polyoxymethylene, polycarbonate, polyphenylene ether, and polysulfone.
In an implementation of this application, the fiber layer includes one or more of glass fiber, carbon fiber, aramid fiber, aluminum oxide fiber, ultra-high-molecular-weight polyethylene fiber, and poly(p-phenylene benzobisoxazole) fiber.
In an implementation of this application, a mass content of the fiber in the hard rubber fiber composite material is 10% to 80%. An increase in fiber content can improve strength of the hard rubber fiber composite material.
In an implementation of this application, the hard rubber fiber composite material includes a plurality of fiber layers, and the plurality of fiber layers and the hard rubber material form a composite laminate in which the fiber and hard rubber are alternately laminated; or the plurality of fiber layers are laminated to form a fiber stack, and the hard rubber material is cured on the fiber stack.
In an implementation of this application, a material of the bendable connecting member includes one or more of an organic flexible material, a soft rubber fiber composite material, a bendable hard rubber fiber composite material, and a bendable metal material. All the foregoing four materials can implement bending performance of the bendable connecting member, to cooperate with folding and unfolding of the flexible display. The soft rubber fiber composite material and the organic flexible material can further obtain a weight reduction benefit.
In an implementation of this application, the organic flexible material includes one or more of fluorine rubber, silicone rubber, a thermoplastic elastomer, polyvinyl chloride, polyimide, polyethylene terephthalate, a cyclic olefin polymer, a liquid crystal polymer, and polydimethylsiloxane.
In an implementation of this application, the soft rubber fiber composite material includes at least one fiber layer and a soft rubber material cured on the fiber layer; and the soft rubber material includes one or more of fluorine rubber, silicone rubber, and a thermoplastic elastomer.
In an implementation of this application, a mass content of the fiber in the soft rubber fiber composite material is 10% to 80%.
In an implementation of this application, the soft rubber fiber composite material includes a plurality of fiber layers, and the plurality of fiber layers and the soft rubber material form a composite laminate in which the fiber and soft rubber are alternately laminated; or the plurality of fiber layers are laminated to form a fiber stack, and the soft rubber material is cured on the fiber stack.
In an implementation of this application, the bendable metal material includes one or more of a stainless steel, a titanium alloy, and an aluminum alloy. Specifically, to better implement bending performance, the bendable metal material may be a porous stainless steel, a porous titanium alloy, or a porous aluminum alloy.
In an implementation of this application, when the bendable connecting member is made of the soft rubber fiber composite material, the composite structure includes an integrally woven fiber layer that continuously exists in the first support member, the second support member, and the bendable connecting member. The composite structure may be an integrally woven fiber layer including one or more layers.
In an implementation of this application, the bendable hard rubber fiber composite material has a porous structure. The bendable hard rubber fiber composite material may form a porous structure by performing laser hole-cutting on the hard rubber fiber composite material, to implement bending performance.
In an implementation of this application, when the bendable connecting member is made of the bendable hard rubber fiber composite material, the bendable connecting member and the first support member and/or the second support member may be an integrally formed structure. When the substrate layer is an integrally formed structure, the substrate layer includes an integrally woven fiber layer and a hard rubber layer that continuously exist in the first support member, the second support member, and the bendable connecting member. The substrate layer is an integrally formed structure, which helps to implement high structural stability of the substrate layer as a whole.
In an implementation of this application, a thickness of the composite structure is 0.1 mm to 5 mm. The thickness of the composite structure may be specifically designed according to performance of a material and an actual application requirement of the product. The composite structure has a plate or sheet form as a whole.
In an implementation of this application, the first support member, the bendable connecting member, and the second support member are combined in a manner of hot press-fitting, adhesive bonding, splicing, or embedding, or the bendable connecting member and the first support member and/or the second support member are an integrally formed structure.
The composite structure provided in the first aspect of embodiments of this application is characterized by high strength, high rigidity, small mass, low costs, and functionalization, and has bending performance. The composite structure may be used in a foldable terminal product, to implement lightweight and functionalization of a product while meeting requirements such as strength and rigidity, and improve competitiveness of a foldable terminal product.
A second aspect of embodiments of this application provides a terminal, including the composite structure according to the first aspect of embodiments of this application. The composite structure may be an under-screen support structure used as a flexible display, or may be used as another functional component. The terminal includes a flexible display and a composite structure disposed below the flexible display.
A third aspect of embodiments of this application provides a flexible display assembly, including a flexible display and a flexible display support structure used for supporting the flexible display. The flexible display support structure is made by using the composite structure according to the first aspect of embodiments of this application. The foregoing composite structure is used as the flexible display support structure, so that product lightweight and functionalization can be implemented while strength, rigidity, and bending performance of the flexible display support structure are met. Compared with a stainless steel flexible display support structure, a weight is reduced by more than 60%, and costs are low.
An embodiment of this application further provides a foldable terminal, including the flexible display assembly according to the third aspect of embodiments of this application. A flexible display includes a bending region and non-bending regions on two sides of the bending region, a flexible display support structure is disposed on an outer surface of the flexible display, the first support member and the second support member of the flexible display support structure respectively correspond to the non-bending regions on two sides of the flexible display, and the bendable connecting member corresponds to the bending region of the flexible display. According to the foldable terminal provided in this embodiment of this application, the flexible display support structure has high strength, can provide sufficient rigid support for the flexible display, and has small mass and low costs. In addition, the flexible display support structure can further implement functions such as electrical connection, heat dissipation, and drop resistance of the flexible display and the foldable terminal, to improve product competitiveness and user experience.
The following describes embodiments of this application with reference to accompanying drawings in embodiments of this application.
Refer to
Refer to
In an implementation of this application, the flexible display support structure 30 may be bonded to a surface of the side of the flexible display 20 away from the display surface through an adhesive, to support the flexible display 20. In other words, the substrate layer 100 or the functional layer 200 may be bonded to the flexible display 20 by an adhesive, and different regions of the flexible display support structure 30 may be tightly and firmly bonded to the flexible display 20 by a same adhesive or different adhesives. In an implementation of this application, a length and a width (in other words, sizes in the X direction and a Y direction in
Refer to
In an implementation of this application, the functional layer 200 may include one or more of an electrically conductive layer, a thermally conductive layer, and an impact-resistant layer, and may further include a functional layer having another function as required. In other words, the functional layer 200 includes at least one of an electrically conductive layer, a thermally conductive layer, and an impact-resistant layer. The functional layer 200 may include one or more electrically conductive layers. The functional layer 200 may include one or more thermally conductive layers. The functional layer 200 may include one or more impact-resistant layers. A thickness of the functional layer 200 may be 5 μm to 500 μm. The thickness of the functional layer 200 is 5 μm to 500 μm, and is a total thickness of the functional layer on one side of the substrate layer 100. In some embodiments, the thickness of the functional layer 200 may be 10 μm to 200 μm. In some embodiments, the thickness of the functional layer 200 may be 6 μm to 100 μm. The functional layer 200 may be disposed on one side of the substrate layer 100, or may be disposed on two sides of the substrate layer 100. The functional layer 200 may completely cover the substrate layer 100, or may partially cover the substrate layer 100. When the functional layers 200 are disposed on two sides of the substrate layer 100, materials, quantities of layers, thicknesses, and the like of the functional layers 200 on the two sides may be the same, or may be different. The electrically conductive layer, the thermally conductive layer, and the impact-resistant layer may be selectively disposed on one side or two sides of the substrate layer 100 according to an actual requirement. The functional layer 200 may include an electrically conductive layer, or may include a thermally conductive layer, or may include an impact-resistant layer, or may include an electrically conductive layer and a thermally conductive layer, or may include an electrically conductive layer and an impact-resistant layer, or may include a thermally conductive layer and an impact-resistant layer, or may include an electrically conductive layer, a thermally conductive layer, and an impact-resistant layer. Optionally, the functional layer 200 may further include a functional layer having another function. The electrically conductive layer, the thermally conductive layer, and the impact-resistant layer may be disposed on the substrate layer 100 in any sequence in a laminated manner. Optionally, the impact-resistant layer is located on the outermost side, and the impact-resistant layer is located on an outer side and may be closer to the flexible display, to better protect the flexible display. In an embodiment, the functional layer 200 includes an electrically conductive layer, a thermally conductive layer, and an impact-resistant layer that are sequentially disposed on the substrate layer 100. Such a lamination sequence facilitates process preparation, and facilitates functional implementation of each functional layer.
Refer to
Refer to
Refer to
In some other implementations of this application, when the functional layers 200 are disposed on two sides of the substrate layer 100, as shown in
In an implementation of this application, the electrically conductive layer includes electrically conductive metal, and the electrically conductive layer may have a single-layer or multi-layer structure. The electrically conductive layer may be disposed to provide the flexible display support structure 30 with an electrical conduction function, so that the flexible display support structure 30 is effectively electrically connected to another component of the terminal 10, to compensate for a problem that when the substrate layer 100 is made of a non-electrically conductive material as a whole, the flexible display support structure 30 cannot be electrically connected to the another component of the terminal 10.
In an implementation of this application, the electrically conductive metal may include one or more of copper, silver, gold, nickel, and tin. When the electrically conductive layer has a single-layer structure, the electrically conductive layer may be formed by one type of electrically conductive metal, for example, a single copper layer or a single nickel layer; or may be formed by two or more types of electrically conductive metal. For example, the electrically conductive layer is formed by nickel and gold. A local region of the electrically conductive layer may be a gold layer, and another region other than the gold layer is a nickel layer. In another example, the electrically conductive layer is formed by nickel and copper. A local region of the electrically conductive layer is a copper layer, and another region other than the copper layer is a nickel layer. Alternatively, copper and nickel are used in all regions of the electrically conductive layer. When the electrically conductive layer has a multi-layer structure, materials of different layers may be the same or different, and each layer may be formed by one type of electrically conductive metal, or may be formed by two or more types of electrically conductive metal. For example, the electrically conductive layer includes an inner layer and an outer layer, the inner layer is disposed on the substrate layer, and the outer layer is disposed on a side of the inner layer away from the substrate layer. Specifically, the inner layer may include at least one of gold, silver, and copper, the outer layer includes at least one of nickel and tin, and the outer layer may protect the inner layer. Alternatively, the inner layer may be a nickel layer, and the gold layer is locally plated on the nickel layer. The flexible display support structure 30 has an electrical conduction function, and can meet an electrical connection requirement.
The electrically conductive layer may be formed on the substrate layer 100 in a manner of adhesive bonding, electroless plating, electroless plating bonded to electroplating, or metal sheet press-fitting. In an implementation, the electrically conductive layer is formed on the substrate layer 100 in an electroless plating manner. A specific process may include:
In an implementation of this application, the thermally conductive layer may include one or more of a thermally conductive silicone sheet, a thermally conductive silicone grease, a thermally conductive double-sided tape, a thermally conductive graphite sheet, a graphene sheet, and a graphene oxide sheet. The thermally conductive layer may be a single-layer or multi-layer structure. The thermally conductive layer may be disposed to provide the flexible display support structure 30 with a good thermal conductivity function, to facilitate heat dissipation of the flexible display and the entire terminal product. Specifically, the flexible display support structure 30 has a thermal conduction function, and may transfer heat generated by a battery inside the terminal and the like to a side of the display, and finally dissipate the heat to the outside of the terminal. The thermally conductive layer may be formed on the substrate layer 100 in a manner of adhesive bonding or thermal fusion (hot press-fitting).
In an implementation of this application, the impact-resistant layer may include one or more of silicone rubber, a thermoplastic elastomer (TPE), polyurethane acrylate (PUA), polyvinyl chloride (PVC) soft rubber, and polyurethane (PU). The impact-resistant layer has a buffer function, and the impact-resistant layer may be a single-layer or multi-layer structure. The thermoplastic elastomer (TPE) may include, but is not limited to, one or more of thermoplastic polyurethane (TPU), a thermoplastic polyester elastomer (TPEE), a styrene-based thermoplastic elastomer, a polyolefin-based thermoplastic elastomer (POE), a polyether ester-based thermoplastic elastomer, and a polyamide-based thermoplastic elastomer. The impact-resistant layer may be disposed to provide the flexible display support structure 30 with a capability of resisting external impact, to help protect the display and improve drop-resistant performance of the terminal product. When the impact-resistant layer is disposed only on one side of the substrate layer 100, the impact-resistant layer is located on the side of the substrate layer facing the display, so that the impact-resistant layer can better protect the display from drop impact. The impact-resistant layer may be formed on the substrate layer 100 in a manner of adhesive bonding or thermal fusion.
Refer to
In an implementation of this application, the fiber in the fiber layer 111 is continuous fiber, and may specifically include, but is not limited to, one or more of glass fiber, carbon fiber, aramid fiber, aluminum oxide fiber, ultra-high-molecular-weight polyethylene fiber, and poly (p-phenylene benzobisoxazole) fiber. The ultra-high-molecular-weight polyethylene fiber is fiber spinning by using polyethylene with a molecular weight>1 million. The fiber layer 111 may be woven by one type of fiber, or may be woven by two or more types of fiber. Performance advantages of various types of fiber may be combined by weaving different types of fiber.
In an implementation of this application, a mass content of the fiber in the hard rubber fiber composite material may be 10% to 80%. Specifically, the mass content of the fiber in the hard rubber fiber composite material may be, for example, 10%, 20%, 30%, 40%, 50%, 60%, 70%, or 80%. Fiber content in the hard rubber fiber composite material may be adjusted according to a specific rigid support requirement and in combination with a mechanical property of the selected rigid resin or rigid rubber. Generally, when the fiber content is higher, the overall weight of the hard rubber fiber composite material is larger, and it is more beneficial to weight reduction. In some implementations, in combination with rigid support performance and a weight reduction requirement, the mass content of the fiber in the hard rubber fiber composite material is 30% to 70%.
In an implementation of this application, a fiber weaving manner of each fiber layer 111 may be unidirectional weaving, or may be multi-directional weaving. In other words, the fiber layer 111 may be unidirectional fiber fabric, or may be woven fiber fabric. The unidirectional fiber fabric, in other words, fiber single axial-direction weaving, is fabric that has a large number of textile yarns in one direction (usually warp or weft unidirectional fabric) and only a small number of usually fine yarns in another direction. Therefore, all strength of the fabric is in one direction. The woven fiber fabric is textile fabric in which fiber is woven in a plurality of axial directions, a large quantity of textile yarns exist in a plurality of directions, and the strength of the final fabric is distributed in a plurality of axial directions. For example, warp and weft biaxial weaving, in other words, 0°/90° weaving, means that fiber of fiber fabric is distributed in two axial directions, angles of the two axial directions are respectively 0° and 90°, and an angle between fiber in the two axial directions is 90°. In another example, 45° weaving (in other words, +45°/−45°) means that fiber of the fiber fabric is distributed in two axial directions, angles of the two axial directions are respectively +45° and −45°, and an included angle between the fiber in the two axial directions is 90 degrees.
In an implementation of this application, a specific weaving form of fiber multi-directional weaving is not limited. Specifically, a form of multi-directional weaving may be plain weaving shown in (a) in
In an implementation of this application, the hard rubber fiber composite material may include only one fiber layer 111, or may include a plurality of (two or more) fiber layers 111. For example, there is one fiber layer 111 in the hard rubber fiber composite material in
In some implementations of this application, as shown in
In an implementation of this application, a material of the bendable connecting member 103 may include one or more of a soft rubber fiber composite material, a bendable metal material, a bendable hard rubber fiber composite material, or an organic flexible material. The bendable connecting member 103 may have good bending performance by using the foregoing material, so that the first support member 101 and the second support member 102 can be folded or unfolded relative to each other.
In an implementation, the bendable connecting member 103 is a soft rubber fiber composite material, and is specifically a soft rubber fiber composite panel. Two sides of the soft rubber fiber composite panel are respectively connected to the first support member 101 and the second support member 102 that are formed by a hard rubber fiber composite panel. In this case, the substrate layer 100 is a composite panel structure of a hard rubber fiber composite material, a soft rubber fiber composite material, and a hard rubber fiber composite material in sequence. The soft rubber fiber composite material is used in a middle region to implement a flexible bending function, and the hard rubber fiber composite material is used on two sides to provide under-screen support for the flexible display. In an implementation of this application, the soft rubber fiber composite material includes at least one fiber layer, and a soft rubber material that is impregnated and cured on the fiber layer. In an implementation of this application, for fiber selection, a specific structure of the fiber layer, a structure of the soft rubber fiber composite material, a preparation manner, and the like in the soft rubber fiber composite material, refer to related descriptions of the hard rubber fiber composite material. Details are not described herein again. A difference between the soft rubber fiber composite material and the hard rubber fiber composite material in this application lies in that the soft rubber fiber composite material is a soft rubber material bonded to fiber, and the hard rubber fiber composite material is a hard rubber material bonded to fiber. The soft rubber fiber composite material is soft and bendable, and can be used as a bendable connecting member to match bending of the bending region of the flexible display. The hard rubber fiber composite material has high rigidity, and can effectively support the non-bending regions of the flexible display. The soft rubber material may include, but is not limited to, one or more of fluorine rubber, silicone rubber, and a thermoplastic elastomer. The thermoplastic elastomer, in other words, artificial rubber or synthetic rubber, may specifically include, but is not limited to, one or more of thermoplastic polyurethane (TPU), a thermoplastic polyester elastomer (TPEE), a styrene-based thermoplastic elastomer, a polyolefin-based thermoplastic elastomer (POE), a polyether ester-based thermoplastic elastomer, and a polyamide-based thermoplastic elastomer.
In an implementation of this application, a mass content of the fiber in the soft rubber fiber composite material is 10% to 80%. Specifically, the mass content of the fiber in the soft rubber fiber composite material may be, for example, 10%, 20%, 30%, 40%, 50%, 60%, 70%, or 80%. The fiber content in the soft rubber fiber composite material may be adjusted according to a specific bending performance requirement, a rigid support requirement, and performance of the selected soft rubber material. Generally, when the fiber content is higher, the overall strength of the soft rubber fiber composite material is increased, the bending property is reduced, and the weight is relatively reduced. In some implementations, in combination with bending performance, rigid support performance, and a weight reduction requirement, the mass content of the fiber in the soft rubber fiber composite material may be 10% to 50%.
In an implementation of this application, in the substrate layer 100, the fiber layer in the first support member 101 and the second support member 102 and the fiber layer in the bendable connecting member 103 may be designed to be independent of each other, or may be an integrally woven structure. Materials of the fiber layers may be the same or different. Quantities of layers of the fiber layers may be the same or different. Stacking manners of fiber layers may be the same or different. The fiber content may be the same or different. The fiber content in the hard rubber fiber composite material and the fiber content in the soft rubber fiber composite material may be selected according to specific conditions. Generally, the fiber content in the soft rubber fiber composite material is lower than the fiber content in the hard rubber fiber composite material.
In some implementations of this application, as shown in
In an implementation of this application, the soft rubber fiber composite material includes a plurality of fiber layers, the plurality of fiber layers and the soft rubber material may form a composite laminate in which the fiber and soft rubber are alternately laminated; or the plurality of fiber layers may be laminated to form a fiber stack, and the soft rubber material is impregnated and cured on the fiber stack.
In an implementation of this application, the bendable connecting member 103 may be formed by using single-layer woven fiber fabric, or may be formed by stacking a plurality of layers of unidirectional fiber fabric at a plurality of angles.
In an implementation of this application, a specific preparation manner of the substrate layer 100 that is formed by a hard rubber fiber composite material, a soft rubber fiber composite material, and a hard rubber fiber composite material in sequence is not limited. For example, the substrate layer 100 may be prepared in the following two manners:
Manner 1:
Step 101: Take a plurality of fiber layers, and stack the plurality of fiber layers at a plurality of angles, to form a fiber stack.
The plurality of fiber layers are usually a plurality of layers of unidirectional fiber fabric, and the plurality of fiber layers may be stacked at any angle in a range from 0° to 90°.
Step 102: Impregnate a hard rubber material on two sides of the fiber stack by using a solvent impregnation method or a hot melting method, impregnate a soft rubber material in the middle, and obtain the substrate layer 100 after hot press-fitting. The substrate layer 100 prepared in this manner is an integrally woven fiber layer that continuously exists in the first support member 101, the second support member 102, and the bendable connecting member 103.
Manner 2:
Step 201: Take a fiber layer, and impregnate a hard rubber material on two sides of the fiber layer by using a solvent impregnation method or a hot melting method, to form a hard rubber fiber single-layer prepreg; and perform multi-layer stacking on the hard rubber fiber single-layer prepreg at a plurality of angles, to obtain a hard rubber fiber laminated prepreg.
Step 202: Take a fiber layer, and impregnate a soft rubber material on two sides of the fiber layer by using a solvent impregnation method or a hot melting method to form a soft rubber fiber single-layer prepreg; and perform multi-layer stacking on the soft rubber fiber single-layer prepreg at a plurality of angles, and then perform hot press-fitting to obtain a soft rubber fiber composite panel. In this step, a single fiber layer of a target thickness may be directly selected, and multi-layer stacking is not used. The fiber layer on which a plurality of layers are stacked is usually unidirectional fiber fabric, and when a single fiber layer is directly selected, the fiber layer is usually woven fiber fabric.
Step 203: Arrange the hard rubber fiber laminated prepreg, the soft rubber fiber composite panel, and the hard rubber fiber laminated prepreg side by side, and then perform hot press-fitting to obtain the substrate layer 100.
In this implementation, the substrate layer 100 is a composite panel made of a hard rubber fiber composite material, a soft rubber fiber composite material, and a hard rubber fiber composite material in sequence. The substrate layer 100 has a flat plate or sheet structure as a whole.
To better bond the hard rubber fiber composite material and the soft rubber fiber composite material at a connection, when the two materials are arranged side by side, the hard rubber fiber laminated prepregs on the two sides may be partially cross-connected to the soft rubber fiber composite panel in the middle. Specifically, a width of a single-layer prepreg located in the middle several layers of the hard rubber fiber laminated prepreg may be reduced, in other words, the single-layer prepreg is indented to a specific width, to reserve a clamping space. The soft rubber fiber composite panel in the middle is partially clamped in the clamping space, and after the press-fitting, the composite panel made of the hard rubber fiber composite material, the soft rubber fiber composite material, and the hard rubber fiber composite material in sequence is prepared without a step difference. The hard rubber fiber laminated prepreg forms a hard rubber fiber composite panel, to be specific, the panel made of a hard rubber fiber composite material, after hot press-fitting.
In some other implementations of this application, multi-layer stacking may be performed on the soft rubber fiber single-layer prepregs at a plurality of angles to obtain the soft rubber fiber laminated prepreg, then the hard rubber fiber laminated prepreg, the soft rubber fiber laminated prepreg, and the hard rubber fiber laminated prepreg are arranged side by side, and then hot press-fitting is performed, to obtain the flexible display support structure. In some other implementations of this application, multi-layer stacking may be performed on the hard rubber fiber single-layer prepreg at a plurality of angles to obtain the hard rubber fiber laminated prepreg, then hot press-fitting is performed to obtain the hard rubber fiber composite panel, then the hard rubber fiber composite panel, the soft rubber fiber composite panel, and the hard rubber fiber composite panel are arranged side by side, and then hot press-fitting is performed, to obtain the flexible display support structure.
In an implementation of this application, the hard rubber fiber composite material and the soft rubber fiber composite material may be spliced and bonded in the foregoing hot press-fitting manner, or may be spliced and bonded in another manner that can implement good bonding, for example, gluing, fusion bonding, laser welding, or the like.
In another implementation of this application, the bendable connecting member 103 is a bendable metal connecting member, and two sides of the bendable metal connecting member are respectively connected to the first support member 101 and the second support member 102 that are formed by a hard rubber fiber composite panel. The bendable metal connecting member may be specifically made of a metal material such as a stainless steel, a titanium alloy, an aluminum alloy, or the like. The bendable metal connecting member 103 may be bonded to the first support member 101 and the second support member 102 in a manner of hot press-fitting, gluing, splicing, clamping, or the like, or may be connected by a connection mechanism.
In an implementation of this application, a specific preparation manner of the substrate layer 100 that is formed by a hard rubber fiber composite material, a metal material, and a hard rubber fiber composite material in sequence is not limited. For example, the substrate layer 100 may be prepared in the following manner:
Step 301: Take a fiber layer, and impregnate a hard rubber material on two sides of the fiber layer by using a solvent impregnation method or a hot melting method, to form a hard rubber fiber single-layer prepreg; and perform multi-layer stacking on the hard rubber fiber single-layer prepreg at a plurality of angles, to obtain a hard rubber fiber laminated prepreg.
Step 302: Take a metal sheet of a target thickness, arrange the hard rubber fiber laminated prepreg, the metal sheet, and the hard rubber fiber laminated prepreg side by side, and then perform hot press-fitting to obtain the substrate layer 100.
In this implementation, the substrate layer 100 is a composite panel made of a hard rubber fiber composite material, a metal material, and a hard rubber fiber composite material in sequence. The substrate layer 100 has a flat plate or sheet structure as a whole.
To better bond the hard rubber fiber composite material and the metal sheet at a connection, when the two materials are arranged side by side, the hard rubber fiber laminated prepregs on the two sides may be partially cross-connected to the metal sheet in the middle. Specifically, a width of a single-layer prepreg located in the middle several layers of the hard rubber fiber laminated prepreg may be reduced, in other words, the single-layer prepreg is indented to a specific width, to reserve a clamping space. Two ends of the metal sheet in the middle are reduced by a specific thickness, to form a clamping part (a step surface is formed due to a reduced surface) matching the clamping space, and the clamping part is clamped in the clamping space of the hard rubber fiber laminated prepreg. After the hot press-fitting, the composite panel made of the hard rubber fiber composite material, the metal material, and the hard rubber fiber composite material in sequence is prepared without a step difference. The clamping parts at both ends of the metal sheet may form an opening through etching, to enhance the bonding of the hard rubber fiber composite material and the metal sheet. Before the hot press-fitting, the surface of the metal sheet may be treated with plasma, to improve surface roughness and enhance the bonding between the hard rubber fiber composite material and the metal sheet.
In an implementation of this application, a metal sheet used as a bendable connecting member is required to have good bending performance, and is usually a porous metal sheet, and a porous hole extends vertically (in other words, in a Y direction).
In an implementation of this application, the hard rubber fiber composite material and the metal material may be spliced and bonded in the foregoing hot press-fitting manner, or may be spliced and bonded in another manner that can implement good bonding, for example, gluing, fusion bonding, laser welding, or the like.
In another implementation of this application, the bendable connecting member 103 is an organic flexible material film. Two sides of the organic flexible material film are respectively connected to the first support member 101 and the second support member 102 that are formed by the hard rubber fiber composite panel, and may be specifically bonded together through hot press-fitting, gluing, welding, or clamping, or may be connected by a connection mechanism. The organic flexible material film can implement a flexible and bending function. The organic flexible material may include one or more of fluorine rubber, silicone rubber, a thermoplastic elastomer, polyvinyl chloride (PVC), polyimide (PI), polyethylene terephthalate (PET), a cyclic olefin polymer (COP), a liquid crystal polymer (LCP), and polydimethylsiloxane (PDMS). The thermoplastic elastomer is, in other words, artificial rubber or synthetic rubber. The thermoplastic elastomer may specifically include one or more of thermoplastic polyurethane (TPU), a thermoplastic polyester elastomer (TPEE), a styrene-based thermoplastic elastomer, a polyolefin-based thermoplastic elastomer (POE), a polyether ester-based thermoplastic elastomer, and a polyamide-based thermoplastic elastomer.
In an implementation of this application, a specific preparation manner of the substrate layer 100 that is formed by a hard rubber fiber composite material, an organic flexible material, and a hard rubber fiber composite material in sequence is not limited. For example, the substrate layer 100 may be prepared in the following manner:
Step 301: Take a fiber layer, and impregnate a hard rubber material on two sides of the fiber layer by using a solvent impregnation method or a hot melting method, to form a hard rubber fiber single-layer prepreg; and perform multi-layer stacking on the hard rubber fiber single-layer prepreg at a plurality of angles, to obtain a hard rubber fiber laminated prepreg.
Step 302: Take an organic flexible material film of a target thickness, arrange the hard rubber fiber laminated prepreg, the organic flexible material film, and the hard rubber fiber laminated prepreg side by side, and then perform hot press-fitting to obtain the substrate layer 100.
In this implementation, the substrate layer 100 is a composite panel made of a hard rubber fiber composite material, an organic flexible material, and a hard rubber fiber composite material in sequence. The substrate layer 100 has a flat plate or sheet structure as a whole.
In this implementation, a structure of a joint between a hard rubber fiber composite panel 101 and an organic flexible material film 103 is not limited. The combination may be a combination of lines shown in
In another implementation of this application, the bendable connecting member 103 is a bendable hard rubber fiber composite material. To implement bending performance of the hard rubber fiber composite material in the region of the bendable connecting member 103, the hard rubber fiber composite material in the region of the bendable connecting member 103 may be formed into a porous structure in a manner such as laser hole-cutting. In other words, the bendable hard rubber fiber composite material is a hard rubber fiber composite material having the porous structure. To better obtain bending performance, the porous structure may be arranged in a longitudinal extension manner (in other words, in a Y direction in
In an implementation of this application, a specific preparation manner of the substrate layer 100 that is formed by a hard rubber fiber composite material, a bendable hard rubber fiber composite material, and a hard rubber fiber composite material in sequence is not limited. For example, the substrate layer 100 may be prepared in the following manner:
Step 401: Take a fiber layer, and impregnate a hard rubber material on two sides of the fiber layer by using a solvent impregnation method or a hot melting method, to form a hard rubber fiber single-layer prepreg; and perform multi-layer stacking on the hard rubber fiber single-layer prepreg at a plurality of angles, and then perform hot press-fitting to obtain a hard rubber fiber panel.
Step 402: Form a porous structure in a preset bendable connecting member region of the hard rubber fiber panel in a laser hole-cutting manner, so that the bendable connecting member region has bendable performance, to obtain the substrate layer 100.
In this implementation, the substrate layer 100 is a composite panel made of a hard rubber fiber composite material, a bendable hard rubber fiber composite material, and a hard rubber fiber composite material in sequence, and the substrate layer 100 is an integrally formed plate or sheet structure.
In an implementation of this application, a thickness of the substrate layer 100 may be approximately 0.1 mm to 5 mm. Specifically, the foldable terminal may be designed according to an actual requirement of the foldable terminal. When the thickness is larger, it indicates that support strength is larger. In some implementations, the thickness of the substrate layer 100 may be 0.15 mm to 0.2 mm. In some other implementations, the thickness of the substrate layer 100 may be 0.25 mm to 0.8 mm. In some other implementations, the thickness of the substrate layer 100 may be 1 mm to 2 mm, or may be 2 mm to 4 mm. A small thickness of the substrate layer 100 helps reduce a weight, and also helps reduce a total thickness of the foldable terminal, to improve user experience.
In an implementation of this application, a thickness of the flexible display support structure 30 may be 0.1 mm to 5 mm. In some implementations, the thickness of the flexible display support structure 30 may be 0.15 mm to 0.22 mm. In some other implementations, the thickness of the flexible display support structure 30 may be 0.25 mm to 0.8 mm. In some other implementations, the thickness of the flexible display support structure 30 may be 1 mm to 2 mm, or may be 2.5 mm to 4 mm. A total thickness of the flexible display support structure 30 mainly depends on a sum of the thicknesses of the substrate layer 100 and the functional layer 200.
In this application, “a plurality of” types of indicates two or more types. In this application, “-” represents a range value, including endpoint values at two ends. For example, if the thickness of the functional layer 200 is 5 μm to 500 μm, it indicates that the thickness of the functional layer 200 is between 5 μm and 500 and includes endpoint values 5 μm and 500 μm.
Embodiments of this application are further described below by using a plurality of embodiments.
Refer to
A preparation process of the flexible display support structure in this embodiment is as follows:
Compared with a flexible display support structure that is completely made of a stainless steel and that has a same size, a weight of the flexible display support structure prepared in this embodiment is reduced by more than 75%. In addition, the flexible display support structure prepared in this embodiment is bent 200,000 times for testing, and no cracking occurs. In addition, in a bending process, the carbon fiber in a bending region may be stretched and deformed. This is because the bending region is a 45° woven carbon fiber. Therefore, deformation may occur in the bending process, and a displacement difference between a folded state and an unfolded state is absorbed. The flexible display support structure prepared in this embodiment has an electrical conduction function, and can meet an electrical connection requirement.
Refer to
A preparation process of the flexible display support structure in this embodiment is as follows:
Compared with a flexible display support structure that is completely made of a stainless steel and that has a same size, a weight of the flexible display support structure prepared in this embodiment is reduced by more than 75%. In addition, the flexible display support structure prepared in this embodiment is bent 200,000 times for testing, no cracking occurs, and good flatness can still be maintained after testing. Compared with Embodiment 1, the bending region of the flexible display support structure in this embodiment has continuous carbon fiber in a 0° direction, and therefore it is relatively difficult to absorb a displacement difference between unfolding and bending. Compared with Embodiment 1, in this embodiment, a copper layer is added to the electrically conductive layer, and conductivity of copper is better than that of the nickel. Therefore, conductivity of the flexible display support structure in this embodiment is better than that in Embodiment 1.
Refer to
A preparation process of the flexible display support structure in this embodiment is as follows:
Compared with a flexible display support structure that is completely made of a stainless steel and that has a same size, a weight of the flexible display support structure prepared in this embodiment is reduced by more than 75%. In addition, the flexible display support structure prepared in this embodiment is bent 200,000 times for testing, no cracking occurs, and good flatness can still be maintained after testing. In the flexible display support structure in this embodiment, because the bending region is made of a pure PI material and has no fiber, the flexible display support structure has better bending performance than a soft rubber fiber composite material, but lacks a fiber net and has a slightly weak support strength. The flexible display support structure prepared in this embodiment has an impact resistance function, and can effectively protect a flexible display from drop impact.
Refer to
A preparation process of the flexible display support structure in this embodiment is as follows:
Compared with a flexible display support structure that is completely made of a stainless steel and that has a same size, a weight of the flexible display support structure prepared in this embodiment is reduced by more than 75%. In addition, the flexible display support structure prepared in this embodiment is bent 200,000 times for testing, no cracking occurs, and good flatness can still be maintained after testing. The flexible display support structure prepared in this embodiment has a thermal conduction function, and is conducive to transferring heat generated by a battery inside a terminal to a side of a flexible display.
Refer to
A preparation process of the flexible display support structure in this embodiment is as follows:
Compared with a flexible display support structure that is completely made of a stainless steel and that has a same size, a weight of the flexible display support structure prepared in this embodiment is reduced by more than 75%. In addition, the flexible display support structure prepared in this embodiment is bent 200,000 times for testing, no cracking occurs, and good flatness can still be maintained after testing. The flexible display support structure prepared in this embodiment has both an electrical conduction function and an impact resistance function.
Refer to
A preparation process of the flexible display support structure in this embodiment is as follows:
Compared with a flexible display support structure that is completely made of a stainless steel and that has a same size, a weight of the flexible display support structure prepared in this embodiment is reduced by more than 75%. In addition, the flexible display support structure prepared in this embodiment is bent 200,000 times for testing, no cracking occurs, and good flatness can still be maintained after testing. The flexible display support structure prepared in this embodiment has both an electrical conduction function and a thermal conduction function.
Refer to
A preparation process of the flexible display support structure in this embodiment is as follows:
Compared with a flexible display support structure that is completely made of a stainless steel and that has a same size, a weight of the flexible display support structure prepared in this embodiment is reduced by more than 75%. In addition, the flexible display support structure prepared in this embodiment is bent 200,000 times for testing, no cracking occurs, and good flatness can still be maintained after testing. The flexible display support structure prepared in this embodiment has both a thermal conduction function and an impact resistance function.
Refer to
A preparation process of the flexible display support structure in this embodiment is as follows:
Compared with a flexible display support structure that is completely made of a stainless steel and that has a same size, a weight of the flexible display support structure prepared in this embodiment is reduced by more than 62%. In addition, the flexible display support structure prepared in this embodiment is bent 200,000 times for testing, no cracking occurs, and good flatness can still be maintained after testing. The flexible display support structure prepared in this embodiment has both an electrical conduction function and an impact resistance function.
Refer to
A preparation process of the flexible display support structure in this embodiment is as follows:
Compared with a flexible display support structure that is completely made of a stainless steel and that has a same size, a weight of the flexible display support structure prepared in this embodiment is reduced by more than 70%. In addition, the flexible display support structure prepared in this embodiment is bent 200,000 times for testing, no cracking occurs, and good flatness can still be maintained after testing. The flexible display support structure prepared in this embodiment has both an electrical conduction function, a thermal conduction function, and an impact resistance function.
Refer to
A preparation process of the flexible display support structure in this embodiment is as follows:
The flexible display support structure prepared in this embodiment has both an electrical conduction function, a thermal conduction function, and an impact resistance function.
Refer to
A preparation process of the flexible display support structure in this embodiment is as follows:
The flexible display support structure prepared in this embodiment has an electrical conduction function, a thermal conduction function, and an impact resistance function.
According to the flexible display support structure in embodiments of this application, a composite material of an organic material and fiber is used as the main body material. Compared with an existing flexible display support structure that is completely made of a metal material such as a stainless steel, the weight of the flexible display support structure is greatly reduced, and good rigid support can be provided for a flexible display. In addition, the bending region may be made of a metal material, or may be made of an organic flexible material or a soft rubber fiber composite material, so that the total weight of the support structure is further reduced while bending reliability is ensured, to help reduce the weight of the foldable terminal product, improve product competitiveness, and improve user experience. In addition, the flexible display support structure in embodiments of this application has low preparation costs. In addition, the flexible display support structure in embodiments of this application further has functions such as electrical conduction, thermal conduction, impact resistance, and the like by arranging the functional layers, so that a functional requirement of the support structure can be met, and performance of a terminal product can be improved.
Number | Date | Country | Kind |
---|---|---|---|
202110606183.1 | May 2021 | CN | national |
This application is a continuation of International Application No. PCT/CN2022/095153, filed on May 26, 2022, which claims priority to Chinese Patent Application No. 202110606183.1, filed on May 31, 2021. The disclosures of the aforementioned applications are hereby incorporated by reference in their entireties.
Number | Date | Country | |
---|---|---|---|
Parent | PCT/CN2022/095153 | May 2022 | US |
Child | 18518020 | US |