This application claims the priority benefit of Taiwan application serial no. 110133235, filed on Sep. 7, 2021. The entirety of the above-mentioned patent application is hereby incorporated by reference herein and made a part of this specification.
The disclosure relates to a composite structure and a manufacturing method thereof, and more particularly relates to a composite structure with an aluminum-based alloy layer containing boron carbide and a manufacturing method thereof.
Pure aluminum materials or aluminum alloy materials have the characteristics of light weight and wear resistance, so the same have become common alloy materials in lightweight metals and may be used to repair various metal substrates. However, aluminum welding is different from welding steels substrates because of its high specific heat and enthalpy of fusion resulting in require high heat inputs to melt. The pure aluminum material or the aluminum alloy material is extremely easy to oxidize and generate air pores in welding and subsequent cooling. Besides, the aluminum oxide formed after oxidation has a high melting point, which far exceeds the melting point of the metal substrate that needs to be processed, so it is difficult to repair its substrate, especially for non-weldable aluminum alloy material.
In addition, during the process of repairing with the pure aluminum material or the aluminum alloy material, welding is usually used to fill the pure aluminum material or the aluminum alloy material into the defect of the metal substrate. However, at high welding temperatures, the pure aluminum material or the aluminum alloy material will have issues such as hot cracking, burning through, and collapse upon solidification from its clad surface, which will affect the repair quality.
The disclosure provides a composite structure with an aluminum-based alloy layer containing boron carbide. The aluminum-based alloy layer contains aluminum, boron, carbon, and oxygen.
The disclosure provides a manufacturing method of a composite structure with an aluminum-based alloy layer containing boron carbide. The aluminum-based alloy layer contains aluminum, boron, carbon, and oxygen.
The composite structure with the aluminum-based alloy layer containing boron carbide of the disclosure includes a substrate in its surface with a hole and the aluminum-based alloy layer containing boron carbide. The aluminum-based alloy layer is disposed in the hole and contains aluminum, boron, carbon, and oxygen. The content of aluminum is between 4 at. % and 55 at. %, the content of boron is between 9 at. % and 32 at. %, the content of carbon is between 13 at. % and 32 at. %, the content of oxygen is between 2 at. % and 38 at. %, and the ratio of the content of boron to carbon is between 0.3 and 2.7.
The manufacturing method of the composite structure with the aluminum-based alloy layer containing boron carbide of the disclosure includes the following steps. A substrate with a hole is provided. An aluminum-based alloy powder containing boron carbide is provided. The aluminum-based alloy powder contains aluminum, boron, carbon, and oxygen. A spray coating process is performed to melt and spray the aluminum-based alloy powder into the hole of the substrate surface to form the aluminum-based alloy layer. In the aluminum-based alloy layer, the content of aluminum is between 4 at. % and 55 at. %, the content of boron is between 9 at. % and 32 at. %, the content of carbon is between 13 at. % % and 32 at. %, the content of oxygen is between 2 at. % and 38 at. %, and the ratio of the content of boron to carbon is between 0.3 to 2.7.
The following embodiments are listed in conjunction with the accompanying drawings for detailed description, but the provided embodiments are not intended to limit the scope covered by the disclosure. In addition, the drawings are for illustrative purposes only and are not drawn according to the original dimensions. In order to facilitate understanding, the same elements will be described with the same reference numerals in the following description.
In the embodiment of the disclosure, a composite structure with an aluminum-based alloy layer includes a substrate with a hole in its surface and the aluminum-based alloy layer disposed in the open hole. The hole in the substrate may be a cavity, an air pore, or a crack, which is not limited by the disclosure. In addition, the aluminum-based alloy layer is configured to repair or fill the hole in the substrate, so that the substrate has a flat surface and the mechanical strength of the substrate is improved. Therefore, the composite structure with the aluminum-based alloy layer of the embodiment of the disclosure is a substrate repaired or filled by the aluminum-based alloy layer. In addition, in the method of the disclosure, a substrate with a thickness of not more than 2 mm may be repaired or filled, which can solve the issue of deformation of the substrate during the process of repairing or filling due to the thickness of the substrate being too thin in the prior art, which will be explained in detail below.
Then, please refer to
Then, a spray coating process 104 is performed to melt and spray the aluminum-based alloy powder 102 into the hole 100a of the substrate 100 surface to form an aluminum-based alloy layer 102a in the hole 100a. In detail, in the embodiment, by the spray coating process 104, the aluminum-based alloy powder 102 is first melted into a melt. At this time, boron carbide in the aluminum-based alloy powder 102 is alloyed with the aluminum-based alloy, so that the aluminum-based alloy melt contains boron carbide. Afterwards, the melt is sprayed into the hole 100a to form the aluminum-based alloy layer 102a containing boron carbide to repair or fill the hole 100a. In this way, the substrate 100 may have a flat surface, and can have a higher mechanical strength due to the hole 100a being repaired or filled. The spray coating process 104 may be laser spraying or thermal spraying. During the spray coating process 104, the aluminum-based alloy powder 102 is first heated by a laser or a heat source to form the melt, and then sprayed into the hole 100a. Generally speaking, when the size of the hole 100a is smaller or has a finer pattern, laser spraying may be adopted to precisely spray the molten aluminum-based alloy powder 102 into the hole 100a. In an embodiment, the rate of laser spraying is, for example, between 6 mm/min to 8 mm/min, and the aluminum-based alloy powder 102 is sprayed into the hole 100a in a slower but precise manner. In addition, when the size of the hole 100a is larger, thermal spraying may be adopted to quickly spray the molten aluminum-based alloy powder 102 into the hole 100a. In an embodiment, the rate of thermal spraying may be approximately 800 mm/sec, and the aluminum-based alloy powder 102 may be sprayed into the hole 100a in a faster and large-area manner. Through thermal spraying, the aluminum-based alloy powder 102 can even be quickly sprayed onto the surface of the substrate 100 in large area.
After the melt of the aluminum-based alloy powder 102 is sprayed into the hole 100a, the material of the aluminum-based alloy powder 102 reacts with the material of the substrate 100, and forms the aluminum-based alloy layer 102a after solidification. The aluminum-based alloy layer 102a repairs or fills the hole 100a and constitutes the composite structure with the aluminum-based alloy layer of the embodiment of the disclosure together with the substrate 100. Based on the material of the aluminum-based alloy powder 102, the aluminum-based alloy layer 102a contains aluminum, boron, carbon, and oxygen (which partially comes from the surrounding environment during the formation process). In addition, since the aluminum-based alloy layer 102a is formed by reacting the material of the aluminum-based alloy powder 102 with the material of the substrate 100, in the formed aluminum-based alloy layer 102a, the content of aluminum is between 4 at. % and 55 at. %, the content of boron is between 9 at. % and 32 at. %, the content of carbon is between 13 at. % and 32 at. %, the content of oxygen is between 2 at. % and 38 at. %, and the ratio of the content of boron to carbon is between 0.3 and 2.7. In addition, depending on the material of the aluminum-based alloy powder 102 and the material of the substrate 100, the aluminum-based alloy layer 102a may also contain silicon, iron, and/or other trace elements (such as magnesium, nickel, copper, zinc, manganese, titanium, bismuth, or a combination thereof). In an embodiment, when the aluminum-based alloy layer 102a contains silicon, the content of silicon is, for example, between 0.7 at. % and 2.1 at. %. In an embodiment, the aluminum-based alloy layer 102a may include iron either, and the content of iron does not exceed, for example, 32 at. %.
In the embodiment of the disclosure, the aluminum-based alloy layer 102a is formed from the aluminum-based alloy powder 102 with the content of boron carbide of not more than 10 wt. %, and the aluminum-based alloy layer 102a contains aluminum, boron, carbon, and oxygen, wherein the content of aluminum is between 4 at. % and 55 at. %, the content of boron is between 9 at. % and 32 at. %, the content of carbon is between 13 at. % and 32 at. %, and the content of oxygen is between 2 at. % and 38 at. %. Therefore, the aluminum-based alloy layer including boron carbide 102a may have a higher hardness than that aluminum-based alloy layer not including boron carbide. For example, compared to a general commercial aluminum-based alloy layer (not containing boron carbide) formed from the pure 4043 aluminum alloy powder, the Hv0.3 Vickers hardness (approximately 100) of the aluminum-based alloy layer 102a is significantly higher than that Vickers hardness (approximately 70) of the general commercial aluminum-based alloy layer.
In addition, in the aluminum-based alloy layer 102a, the ratio of the content of boron to the content of carbon is between 0.3 and 2.7. When the ratio of the content of boron to carbon is less than 0.3, the hardness of the aluminum-based alloy layer is reduced. When the ratio of the content of boron to carbon is greater than 2.7, the hardness of the aluminum-based alloy layer is significantly reduced to near the hardness range of a general commercial aluminum-based alloy layer.
In particular, once the aluminum-based alloy layer 102a is formed from the aluminum-based alloy powder 102 with the content of boron carbide of more than 10 wt. %, the hardness of the aluminum-based alloy layer 102a will be reduced. Therefore, in the aluminum-based alloy powder 102 forming the aluminum-based alloy layer 102a, based on the total weight of the aluminum-based alloy powder 102, the content of boron carbide is not more than 10 wt. %, preferably between 5 wt. % and 10 wt. %. Such boron carbide in the aluminum-based alloy 102a can have an enough high hardness to be used as a repairing layer and/or a strengthening layer of the substrate 100.
A 4043 aluminum alloy powder containing 5 wt. % of boron carbide was adopted as a material to fill a hole in a substrate (an aluminum 6061 substrate) surface.
A 4043 aluminum alloy powder containing 10 wt. % of boron carbide was adopted as a material to fill a hole in a substrate (an aluminum 6061 substrate) surface.
In addition, the structure of Example 1, the structure of Example 2, and the structure after filling the 4043 aluminum alloy powder into the hole in the substrate surface were subjected to an X-ray diffraction (XRD) analysis, and the results are shown in
A 4043 aluminum alloy powder containing 3 wt. % boron carbide was adopted as a material to fill a hole in a substrate (an aluminum 6061 substrate) surface.
A 4043 aluminum alloy powder containing 7 wt. % of boron carbide was adopted as a material to fill a hole in a substrate (an aluminum 6061 substrate) surface.
Although the disclosure has been disclosed in the above embodiments, the embodiments are not intended to limit the disclosure. Persons skilled in the art may make some changes and modifications without departing from the spirit and scope of the disclosure. Therefore, the protection scope of the disclosure shall be determined by the scope of the appended claims.
Number | Date | Country | Kind |
---|---|---|---|
110133235 | Sep 2021 | TW | national |
Number | Name | Date | Kind |
---|---|---|---|
5039633 | Pyzik et al. | Aug 1991 | A |
7550029 | Chen et al. | Jun 2009 | B2 |
9745648 | Olserius et al. | Aug 2017 | B2 |
9770787 | Anderson | Sep 2017 | B2 |
20100104843 | Pyzik et al. | Apr 2010 | A1 |
20100129683 | Lin et al. | May 2010 | A1 |
20180214991 | Yahata | Aug 2018 | A1 |
Number | Date | Country |
---|---|---|
103668382 | Mar 2014 | CN |
103890223 | Jun 2014 | CN |
104264201 | Jan 2015 | CN |
105256249 | Jan 2016 | CN |
109266992 | Jan 2019 | CN |
109536955 | Mar 2019 | CN |
110461535 | Nov 2019 | CN |
111715974 | Sep 2020 | CN |
1737993 | Jan 2007 | EP |
I244436 | Dec 2005 | TW |
Entry |
---|
Zewu Qi, et al., “Microstructure and mechanical properties of double-wire + arc additively manufactured Al—Cu—Mg alloys”,Journal of Materials Processing Technology, vol. 255, Dec. 13, 2017, pp. 347-353. |
Qiuyu Miao, et al., “Comparative study of microstructure evaluation and mechanical properties of 4043 aluminum alloy fabricated by wire-based additive manufacturing”, Materials and Design, vol. 186, Sep. 10, 2019, pp. 1-12. |
Zewu Qi, et al., “Microstructure and mechanical properties of wire + arc additively manufactured Al—Mg—Si aluminum alloy”,Materials Letters, vol. 233, Sep. 8, 2018, pp. 348-350. |
“Office Action of Taiwan Counterpart Application”, dated Mar. 4, 2022, p. 1-p. 22. |
Number | Date | Country | |
---|---|---|---|
20230074335 A1 | Mar 2023 | US |