Patent Grant
7892800
This application is a 35 U.S.C. §371 filing of International Application Number PCT/EP2004/014627 filed Dec. 22, 2004, which claims priority to German Application 103 60 465.0, filed Dec. 22, 2003 in Germany. The contents of these applications are hereby incorporated by reference in their entireties.
The present invention relates to a composite material made of non-metallic inorganic grains and plastics particles, which is particularly suitable as a carrier material for bacteria. A preferred field of application for such carrier materials is in the biological stages of sewage treatment plants.
In most biological processes used today for sewage treatment, it is primarily the ability of microorganisms to oxidise organic toxins with oxygen of which use is made. For the operation of sewage treatment plants, therefore, the provision of a carrier material which offers bacteria favourable conditions for life in such plants is of great interest. In this regard, it is of decisive importance, on the one hand, that the largest possible surface be provided on which the bacteria can form colonies whilst, on the other hand, it is advantageous if the carrier material has a specific density which corresponds to that of the liquid to be treated, so that the carrier material becomes suspended in the liquid and can be circulated by existing currents. A further criterion for an advantageous bacteria carrier is the presence of a sufficiently smooth surface which enables the sludge containing the saturated bacteria building up on the material to fall off the carrier from time to time, providing room for new bacterial growth and thus for regeneration of the treatment unit.
It is known to use larva and/or shingle as carriers for bacteria in a fixed bed filter. This variant, however, is distinguished by the disadvantage that the carrier is denser than water and is therefore not capable of becoming suspended. A further disadvantage is that a high level of pressure loss occurs. Also disadvantageous for the use of these materials as bacteria carriers in sewage treatment plants is the fact that the contamination problem is not satisfactorily solved in this case, and that carrier materials of this type have too small a surface area.
Furthermore, the use of plastics carriers, particularly based on moulded bodies, in sewage treatment plants is known. These are distinguished, however, by a small surface area of up to a maximum of 600 m2/m3, and their partial tendency to float.
Carriers based on ceramics are also used, although these are also unsatisfactory, since on the one hand they are not capable of becoming suspended and, on the other hand, they are too expensive to produce.
With regard to the aforementioned prior art, the present invention is based on the aim of providing a carrier material for bacteria for use in sewage treatment plants and having a high specific surface area for colonisation by bacteria, and which is able to become suspended in the aqueous medium in a treatment plant and which, by means of a sufficiently smooth surface, enables sludge and saturated bacteria to fall off during operation.
This aim is fulfilled according to the invention by the composite material according to claim 1. Preferred embodiments of the composite material are described in the dependent claims 2 and 3.
The present invention also relates to the use of the composite material according to the invention as a carrier material for bacteria. This aspect of the present invention is described in claims 4 to 6.
The present invention further relates to a method for manufacturing the composite material according to the invention. This method is described in claims 7 and 8.
The non-metallic inorganic material used in the composite material according to the invention has the task of providing a sufficiently large surface area for colonisation by bacteria. Of decisive importance to the suitability for colonisation by bacteria, apart from the size of the specific surface area, is its structure. It is, in particular, preferable for colonisation by bacteria if the non-metallic inorganic material has pores that are accessible from outside and are not too small, in order that a good degree of material exchange with the surrounding medium is ensured.
According to the invention, the requirements set out above are met by an inert material having the following characteristics:
Preferred are materials whose specific surface area is in the range of 25,000 m2/m3 and 500,000 m2/m3. Particularly preferred are materials with specific surface areas in the range of 100,000 m2/m3 to 500,000 m2/m3. Similarly, materials are advantageously used in which at least 80% of the pores lie within a size range of 0.5 μm and 100 μm, and preferably between 5 μm and 50 μm. It is also preferable that 70% of the material has a grain size in the range of 0.1 mm to 50 mm and particularly preferably between 1 mm and 20 mm. Also preferable is the use of a material whose (open) porosity is in the range of 40% to 80% and preferably in the range of 50% to 70%.
The non-metallic inorganic material (similarly to the plastics material described below) also distinguishes itself in that it is inert in the surrounding medium in which it is used as a carrier material for bacteria (i.e. typically in an aqueous medium), that is that it is neither soluble nor does it undergo chemical reactions.
The chemical composition of the non-metallic inorganic material is not stipulated in greater detail, provided it fulfils the above requirements. The following non-metallic inorganic materials may, for instance, be used in accordance with the present invention: zeolites, activated charcoal, clay granulates, porous silicate materials.
A particularly preferred material is disclosed in DE 100 22 798.
Manufacturing of the non-metallic inorganic materials according to the invention takes place using conventional techniques.
Suitable grain sizes for the non-metallic inorganic material are obtained by grinding and/or sieving.
The plastics particles to be used according to the present invention have the purpose, on the one hand, through their combination with the non-metallic inorganic material of enabling a specific density of the composite material which corresponds to that of the surrounding medium, such that the composite material is capable of being suspended in this medium.
On the other hand, the plastics material with its surface which is smooth compared to the non-metallic inorganic material, enables detachment of the sludge and saturated bacteria from the surface of the composite material.
In order to fulfil this aim, it is advantageous if the plastics particles have a specific density in the range of 0.6 g/cm3 to 1.2 g/cm3, preferably 0.9 g/cm3 to 1.1 g/cm3, and a specific surface area in the range of 50 m2/m3 to 1000 m2/m3, preferably 100 m2/m3 to 500 m2/m3, and that, of the plastics particles, more than 50% have a particle size in the range of 5 mm to 100 mm, and preferably 8 mm to 60 mm.
Essentially every plastics material is suitable for use according to the present invention, provided that particles which fulfil the above criteria may be made from such material. Typical plastics that are suitable for use according to the present invention are PE (polyethylene), PP (polypropylene), PS (polystyrene), PU (polyurethane), ABS (acrylonitrile-butadiene-styrene) and PVC (polyvinyl chloride).
The shape of the plastics particles is not specified, and sphere, disk, lens or cube-shaped particles may be used, as well as mixed shapes and entirely irregularly-shaped particles.
The size and shape of the particles is determined by the manufacturing process.
An essential aspect of the composite material is the presence both of grains of the non-metallic inorganic material and of plastics particles. The relative mass ratio of these components lies typically in the range (non-metallic inorganic material: plastics particles) of 85:15 to 15:85. The exact mass ratio of the components is readily determined from the desired specific density of the composite material and from the specific density of the components, and may be easily determined by a person skilled in the art.
The desired specific density of the composite material is determined, when used as a bacterial carrier material in sewage treatment plants, by the specific density of the medium in the treatment plant. With regard to the ability of the particles to become suspended, it may be advantageous to select the specific density of the composite material such that it deviates by no more than 20% from the specific density of the medium. Still further preferred are composite materials whose specific densities deviate by no more than 10% from that of the medium. Particularly preferable are composite materials with a specific density which lies in the range of ±15% of the specific density of the medium. This means, for instance, for media with a specific density of 1 g/cm3, that the specific density of the composite material lies in the range of 0.8 g/cm3 to 1.2 g/cm3, preferably 0.9 g/cm3 to 1.1 g/cm3 and particularly preferably in the range of 0.95 g/cm3 to 1.05 g/cm3.
The components of the composite material are advantageously bound to each other such that on use (e.g. for operation of a sewage treatment plant), they are able to withstand the mechanical loads arising there. The manner of binding of the components is not specified in greater detail and may include both pressing during melting of the plastics particles, and cementing of the components.
The spatial arrangement of the components within the composite material is also not specified in greater detail. Thus, in the composite material according to the invention, apart from contact sites between grains of non-metallic inorganic material and plastics particles, contact sites between non-metallic inorganic grains among themselves and/or between plastics particles among themselves may exist.
It is also preferable that the components of the composite material are selected and combined with each other such that the specific surface area of the composite material lies in the range of 500 m2/m3 to 750,000 m2/m3, and particularly preferably 10,000 m2/m3 to 700,000 m2/m3. The size and shape of the particles of composite material is fundamentally not specified. However, disk-shaped particles with a circular base surface, a diameter in the range of 1 cm to 10 cm, preferably 2 cm to 6 cm, and a thickness in the range of 2 mm to 20 mm, preferably 5 mm to 10 mm, have proved to be advantageous, whereby these disk-shaped particles may relatively have large hollow spaces.
The composite material according to the invention is particularly suitable as a carrier material for bacteria for use in the biological treatment stage of sewage treatment plants. It is typically used in a quantity corresponding to between 5% and 50% by volume, and preferably between 10% and 40% of the reaction vessel.
When the material is put into use, the carrier material may be inoculated with suitable bacteria, although this is not necessarily required.
The use of the composite material according to the invention is not restricted to sewage treatment plants. It is also suitable as a carrier for bacteria for other uses, such as bioreactors in the chemical industry, fermentation reactors in the food industry, etc. With these uses, it may be necessary to adapt to components to be used to the prevailing conditions and requirements with respect to stability, specific density, toxicity, etc. This adaptation may readily be carried out with the aid of routine experiments and may take place based upon the general specialist knowledge of the relevant person skilled in the art.
The composite material according to the invention may be manufactured from the components by
The melting in step (3) takes place by heating the plastics particles at a temperature above the melting point of the plastics over a period in the range of 5 min. to 60 min. Preferably, only the edge regions of the particles should be melted, such that the structure and form of the particles are maintained by its core. Slight deformation of the particles is not harmful, however.
The manufacturing process typically includes mixing of the non-metallic inorganic material with the plastics material, filling into a suitable sintering mould and possibly, pressing. Then follows the sintering of the mixture in the sintering device according to a predetermined sintering programme with the parameters of temperature and dwell time. During the dwell time in the sintering device, sintering of the plastics particles takes place, enclosing the non-metallic inorganic material.
In a preferred embodiment, the connection between the plastics particles and the non-metallic inorganic material is achieved using a plastics powder. The plastics powder may be added at any desired time point before the melting. Preferred grain sizes for the plastics powder are in the range of 0.2 mm to 1.5 mm, and particularly preferably in the range of 0.2 mm to 1.0 mm. Due to these small grain sizes, the melting and therefore the binding of the components is facilitated. The plastics powder therefore acts as a mediator.
A suitable material for the plastics powder is the material of the plastics particles, although similar materials may be used. To be understood as “similar materials” in this connection are those having a specific density in the range of 0.6 g/cm3 to 1.2 g/cm3, preferably 0.9 g/cm3 to 1.1 g/cm3. In addition, the melting point of the plastics powder should be similar to that of the plastics particles. Preferably, the melting point should lie not more than 10% above that of the plastics particles and not more than 30% below that of the plastics particles.
The quantity of plastics powder that is favourably to be used depends on the other materials used and may be determined by means of simple preliminary tests. In any event, the quantity of plastics powder should advantageously at least be high enough such that detachment of components from the composite material is prevented. On the other hand, it is not advantageous to increase the relative quantity of plastics powder so much that the quantity required for simple covering of all surfaces is exceeded.
A composite material was manufactured by binding a ceramic material having the following properties.
Starting Materials:
Silicate material
Pore size: 0.1 μm to 100 μm
Material density: 2.2 g/cm3
Porosity: 60%
Specific surface area: 350,000 m2/m3
Plastics Material:
HDPE
Density: 1.035 g/cm3
Plastics Powder:
HDPE
Density: 0.951 g/cm3
Softening temperature: 84° C. (Vicat B50 to ISO 306)
Process temperature: 230° C. Dwell time: 20 min.
Specific density: ca. 1 g/cm3
Particle size: 20 mm to 50 mm
Specific surface area: ca. 175,000
The binding material was capable of becoming suspended in a sewage treatment plant medium and it was capable of colonisation by bacteria. During test operation of a treatment plant, it was found that the carriers colonised by bacteria were readily capable of regeneration, since bacteria and sludge could be removed from the carrier.
| Number | Date | Country | Kind |
|---|---|---|---|
| 103 60 465 | Dec 2003 | DE | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2004/014627 | 12/22/2004 | WO | 00 | 4/23/2007 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2005/061594 | 7/7/2005 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4620931 | Hirata et al. | Nov 1986 | A |
| 4664803 | Fuchs et al. | May 1987 | A |
| 5019311 | Koslow | May 1991 | A |
| 6043067 | Lihme et al. | Mar 2000 | A |
| 6818579 | Giangrasso | Nov 2004 | B2 |
| 7195233 | Giangrasso | Mar 2007 | B2 |
| Number | Date | Country |
|---|---|---|
| 3032869 | Apr 1982 | DE |
| 69024984 | Mar 1996 | DE |
| 69122393 | Oct 1996 | DE |
| 10022798 | Nov 2001 | DE |
| 1160206 | Dec 2001 | EP |
| 1412589 | Nov 1975 | GB |
| WO-0185644 | Nov 2001 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20070202176 A1 | Aug 2007 | US |