Composition structure for NOx sensors

Information

  • Patent Grant
  • 6379514
  • Patent Number
    6,379,514
  • Date Filed
    Thursday, September 28, 2000
    24 years ago
  • Date Issued
    Tuesday, April 30, 2002
    22 years ago
Abstract
A structural arrangement for NOx sensors including a first selectively oxygen ion-conductive layer and a second gas-permeable, nonconductive layer, the latter having a porous spinel structure or porous platinum. The oxygen ion-conductive layer made from a mixed-conductive ceramic can have an additional layer of a material which is catalytically inactive to NOx.
Description




FIELD OF THE INVENTION




The invention relates to a structural arrangement for NO


x


sensors including a first selectively oxygen ion-conductive layer and a second gas-permeable nonconductive layer.




BACKGROUND INFORMATION




It is known that exhaust gases of internal combustion engines, lean mixture engines in particular, contain nitrogen oxides and other gases in addition to unburned fuel components and oxygen. The composition of the exhaust gas is essentially determined by the setting of the air-fuel mixture with which the internal combustion engine is operated. If, for example, fuel is present in excess of a stoichiometric mixture, considerable amounts of unburned or only partially burned fuel are present in the exhaust gas while oxygen in excess of a stoichiometric mixture of the air in the air-fuel mixture results in a correspondingly higher concentration of oxygen in the exhaust gas. A known method for setting an optimum air-fuel mixture is to determine the composition of the exhaust gas in a proportional probe. In doing so, the limiting current probe has a solid electrolyte arranged between two electrodes, one electrode being exposed to the exhaust gas via a diffusion barrier. With a constant voltage applied to the electrodes, a limiting current occurs on both electrodes due to a difference in oxygen concentration, the limiting current being measured by a measuring device and analyzed, for example, for setting the air-fuel mixture with which the internal combustion engine is operated.




One possibility for determining oxygen and nitrogen oxides in particular in gas mixtures is described in the article by N. Kato, K. Nagakaki and N. Ina, SAE 1996, pages 137 to 142. The reactivity of the nitrogen oxides and other gas components with parts of the electrode is regarded as one of the disadvantages of the method described in that article.




Moreover, unpublished German Patent Application No. 196 35 494.3 (equivalent to German Published Patent Application No. 196 52 968) describes a measuring arrangement for the determination of gas components in gas mixtures with at least one electrochemical solid electrolyte measurement cell and at least one cathode exposed to the gas mixture to be measured, the cathode being spatially separated from a layer that selectively conducts oxygen ions by an electrically nonconductive layer which is gas-permeable at least in areas.




Consistent with this patent application, a mixed-conductive ceramic membrane with catalytic inactivity to nitrogen oxides and electrically insulated via a solid electrolyte pump cell must be provided for the structure of an amperometric NO


x


sensor. The ceramics used for this purpose may be composed of a metallic oxide, with perovskite ceramics being used frequently.




Previously, the mixed-conductive ceramics were imprinted onto a porous Al


2


O


3


structure as a support material. In this process, several components of the metallic oxide ceramic diffused into the Al


2


O


3


structure and formed phases with a spinel structure at the boundary surface of the membrane, with these phases being nonconductive to poorly conductive for ions.




An additional problem was that the ceramic materials known to be outstandingly mixed-conductive have as a rule, however, a highly catalytic activity toward NO


x


. On the other hand, the materials that are inactive to NO


x


, nickel catalyst materials, show only a slight resultant oxygen permeation rate.




SUMMARY OF THE INVENTION




An object of the present invention is to make a structural arrangement for NO


x


sensors available in which the supporting material does not substantially inhibit the exchange of oxygen into the gas phase and does not influence the structure of the mixed-conductive ceramic and accordingly the ionic conductivity. Moreover, the mixed-conductive membrane should have a high electron and ion conductivity, resulting in high oxygen permeability while at the same time, however, the catalytic activity to NO


x


should be as low as possible.




The object is achieved according to the present invention by a structural arrangement for NO


x


sensors which includes a first selectively oxygen ion-conductive layer and a second gas-permeable, nonconductive layer which has a porous spinel structure or porous platinum.




Spinels are understood to be a group of minerals and synthetically produced materials having the general formula AB


2


X


4


, A signifying a bivalent metal, B a trivalent or quadrivalent metal and X=O, S, Se. Al


2


O


3


. MgO and/or Co


3


O


4


may be used as particularly preferred spinels. The use of spinels according to the present invention possibly increases the standard reaction enthalpy for the formation of products from mixed-conductive perovskites and from the spinel substrate structure in relation to the previously used Al


2


O


3


substrates. It might thus be possible to inhibit the formation of nonconductive boundary phases.




Platinum substrates may be used in the production of the mixed-conductive layer. In doing so, no reaction takes place between the substrate and the ceramic. However, the porous platinum ensures a good bond between the substrate and the mixed-conductive layer.




In one embodiment of the present invention, the structural arrangement is characterized in that the selectively oxygen ion-conductive layer is made from a mixed-conductive ceramic having a layer on the side facing the exhaust gas which is made from a material that is catalytically inactive to NO


x


.




Examples of suitable materials that are catalytically inactive to NO


x


are Gd


0,7


Ca


0,3


CoO


3-δ


, Gd


0,7


Ca


0,3


FeO


3-δ


, composite materials of mixtures of Ce


0,8


Gd


0,2


O


2-δ


and Gd


0,7


Ca


0,3


CoO


3-δ


.




This layer can be applied to the layer composed of a mixed-conductive ceramic with the aid of thick-film technology or by a vapor deposition method.




In doing so, the layer is of a nickel catalyst material which is at least more than one layer of atoms thick, the nickel catalyst material rendering the mixed-conductive ceramic membrane inactive on its channel-side surface. The high ionic conductivity of the oxygen through the ceramic material is preserved in this manner.




In a preferred embodiment the mixed-conductive ceramic is composed of a perovskite or elpasolite, in particular having the composition Ca


0,7


Sr


0,7


CoO


3-δ


or SrFeCo


0,5


O


3-δ


.




According to the present invention, the range of variation of the mixed-conductive membrane materials suitable for use is now significantly and advantageously expanded by the modification of the substrate structure. Thus the elimination of the previous inactivation of the boundary surface distinctly reduces the permeability of the membrane with constant effective permeation quantity per surface area. Also, the entire membrane surface can be substantially reduced by the novel structural arrangement since the permeation through the ceramic material is substantially increased with continued catalytic inactivity of the surface.




Thus according to the present invention, the sensor diffusion distance is reduced and the response time of the sensor is reduced accordingly.




It is therefore now possible in an advantageous manner to extend the measuring range of the sensor with regard to the O


2


/NO


x


proportion with the same membrane surface.




Moreover, the contamination of the surface advantageously results in a reduction and inhibition of aging and drift phenomena, respectively, in the ceramic membrane.




With constant oversizing of the membrane surface, which is at least required for the complete oxygen removal, the total increased permeation per surface area now makes it possible for a larger proportion of surface area to be contaminated without disadvantageously influencing the characteristics of the sensor.











BRIEF DESCRIPTION OF THE DRAWING




The FIGURE shows a measuring arrangement and structural arrangement according to the present invention.











DETAILED DESCRIPTION




The FIGURE shows a measuring arrangement which is generally identified as


10


. This measuring arrangement


10


has a solid electrolyte


6


essentially in the form of a sheet on the side of which is arranged an electrode which is connected as an anode


7


. An electrode connected as a cathode


5


is arranged on the side of solid electrolyte


6


opposite anode


7


, the electrolyte being made from, for example, a zirconium dioxide-yttrium oxide ceramic. Cathode


5


is partially covered with a gastight layer


3


, for example of α- or γ-aluminum oxide or a layer of purely ion conductive material. It borders gas-permeable, nonconductive layer


2


which has a porous spinel structure. These electrically insulating layers


2


,


3


are covered with an additional layer


1


which is composed of a mixed-conductive metal oxide ceramic. This forms a selectively oxygen ion-conductive layer. The thickness of this layer varies between 5 and 200 μm. The boundary surface of mixed-conductive ceramic membrane


1


with nonconductive layer


2


is identified as


4


. Layer


11


which is catalytically inactive to NO


x


is present on mixed-conductive ceramic membrane


1


. Both anode


7


as well as the cathode are connected to measuring arrangement


10


via conductors with terminals, both of which are not shown here. Electrodes


5


,


7


are preferably made of platinum or another corrosion-resistant metal or metal alloy. A diffusion channel


8


is arranged beneath anode


7


, via which reference air can be directed to anode


7


. Diffusion channel


8


for the reference air is accommodated in a multilayer body


9


which is built up from multiple layers, multilayer body


9


being made from zirconium dioxide, for example.



Claims
  • 1. A structural arrangement for an NOx sensor, comprising:a first selectively oxygen ion-conductive layer made of a mixed-conductive ceramic including a layer on a side facing an exhaust gas and formed from a material that is catalytically inactive to NOx; and a second gas-permeable, nonconductive layer including a porous spinel structure.
  • 2. The structural arrangement according to claim 1, wherein:the mixed-conductive ceramic includes one of a perovskite and elpasolite.
  • 3. The structural arrangement according to claim 2, wherein:the mixed-conductive ceramic includes one of Ca0,7Sr0,7CoO3-δand SrFeCo0,5O3-δ.
  • 4. The structural arrangement according to claim 1, wherein:the porous spinel structure includes at least one of Al2O3.MgO and Co3O4.
  • 5. The structural arrangement according to claim 1, wherein:the material that is catalytically inactive to NOx is applied to the first selectively oxygen ion-conductive layer by an implementation of one of a thick-film technology and a vapor deposition operation.
  • 6. A measuring arrangement for a NOx sensor, comprising:a cathode; and a structural arrangement arranged over the cathode, the structural arrangement including: a first selectively oxygen ion-conductive layer made a mixed-conductive ceramic including a layer on a side facing an exhaust gas and formed from a material that is catalytically inactive to NOx, and a second gas-permeable, nonconductive layer including a porous spinel structure.
Priority Claims (1)
Number Date Country Kind
197 45 328 Oct 1997 DE
PCT Information
Filing Document Filing Date Country Kind
PCT/DE98/03005 WO 00
Publishing Document Publishing Date Country Kind
WO99/19721 4/22/1999 WO A
US Referenced Citations (6)
Number Name Date Kind
5543025 Garzon et al. Aug 1996 A
5681373 Taylor et al. Oct 1997 A
5723035 Mazanee et al. Mar 1998 A
5866799 Kato et al. Feb 1999 A
5902379 Phillips et al. May 1999 A
6143159 Bloomfield Nov 2000 A
Foreign Referenced Citations (3)
Number Date Country
44 39 901 May 1996 DE
196 52 968 Mar 1998 DE
0 468 500 Jan 1992 EP
Non-Patent Literature Citations (1)
Entry
“Thick Film ZrO2 NOx Sensor,” Kato et al., SAE, pp. 137-142 (1996), month unavailable.