Compositions comprising melt-processed inorganic fibers and methods of using such compositions

Information

  • Patent Grant
  • 7493968
  • Patent Number
    7,493,968
  • Date Filed
    Wednesday, November 14, 2007
    17 years ago
  • Date Issued
    Tuesday, February 24, 2009
    15 years ago
Abstract
Improved lost circulation compositions that include melt-processed inorganic fibers and methods for using such compositions in subterranean formations are provided. An example of a method of the present invention is a method comprising providing a drilling mud comprising a plurality of melt-processed inorganic fibers, wherein the melt-processed inorganic fibers have a length of less than about 10 millimeters, and comprise at least one melt-processed inorganic fiber selected from the group consisting of: a basalt fiber, a wollastonite fiber, and a ceramic fiber; and circulating the drilling mud in the subterranean formation.
Description
BACKGROUND

The present invention relates to subterranean well cementing operations, and more particularly, to cement compositions comprising melt-processed inorganic fibers and methods for using such cement compositions.


Hydraulic cement compositions commonly are utilized in subterranean operations, particularly subterranean well completion and remedial operations. For example, hydraulic cement compositions are used in primary cementing operations whereby pipe strings, such as casing and liners, are cemented in well bores. In performing primary cementing operations, usually a hydraulic cement composition is pumped into an annular space between the walls of a well bore and the exterior surface of the pipe string disposed therein. The cement composition sets in the annular space, forming therein an annular sheath of hardened, substantially impermeable cement that supports and positions the pipe string in the well bore and bonds the exterior surface of the pipe string to the walls of the well bore. Hydraulic cement compositions also are used in remedial cementing operations, such as plugging highly permeable zones or fractures in well bores, plugging cracks and holes in pipe strings, and the like.


When the cement compositions contact permeable subterranean formations, fluid (e.g., water) may be lost into the formation. Excessive fluid loss may cause the cement composition to become prematurely dehydrated, thereby potentially causing bridging in the annulus and limiting the time for which said slurry can remain pumpable, and/or reducing bond strength between the set cement composition and a subterranean zone, the walls of pipe and/or the walls of the well bore. Fluid loss control additives (e.g., polymers and copolymers) may be included in a cement composition, inter alia, to reduce fluid loss into the formation. When the permeability of the formation is high, for example, because of unconsolidated or depleted formations, or microfractures, the rate of fluid loss may increase to an extent that some conventional fluid loss control additives (e.g., polymer and copolymers) may not be effective in preventing fluid loss from cement compositions. In an extreme case, fluid loss may increase to the point where the cement composition no longer can be circulated back to the surface—in such case, the cementing operation being conducted may be said to have “lost circulation.” To help control fluid loss, and to prevent fluid loss from escalating to “lost circulation,” certain types of fluid loss control additives that sometimes are referred to as “lost circulation materials” may be included in cement compositions. Examples of conventional lost circulation materials include peanut shells, mica, cellophane, walnut shells, calcium carbonate, plant fibers, cottonseed hulls, ground rubber, and polymeric materials.


Lost circulation also can occur during drilling of subterranean well bores. For example, fluid may be lost into high-permeability zones (e.g., unconsolidated zones or depleted formations), vugular zones, and fractures (e.g., either pre-existing fractures or fractures created during the subterranean operation). Conventional attempts to prevent lost circulation during subterranean drilling operations have involved, for example, the addition of soluble additives (e.g., polymers) to drilling fluids. However, when circulation losses exceed 1 barrel per hour, these additives may not be as effective as desired.


In many cases when circulation losses have been encountered that exceed 1 barrel per hour, conventional insoluble particulate materials (e.g., fibers) have been added to the drilling fluid. Such conventional insoluble particulate materials may form a filter cake on the walls of the well bore. This filter cake may be less permeable than the well bore walls, and, accordingly the establishment of the filter cake may reduce circulation losses. However, the use of conventional insoluble particulate materials may be problematic. For example, if the conventional particulate materials are not chosen carefully, they may cause pumping problems or plug flow lines. In some circumstances, the conventional particulate materials may be screened out on shale shakers (and thus be prevented from remaining with the circulating fluid as it flows into the well bore). In some cases, the comparatively lighter density of the conventional particulate materials may cause them to tend to remain afloat within the comparatively denser drilling fluid. In other circumstances, the addition of conventional particulate materials may cause the drilling fluid to become excessively thick and viscous.


SUMMARY OF THE INVENTION

The present invention relates to subterranean well cementing operations, and more particularly, to cement compositions comprising melt-processed inorganic fibers and methods for using such cement compositions.


An example of a method of the present invention is a method of cementing in a subterranean formation, comprising: providing a cement composition comprising water, cement, and a plurality of melt-processed inorganic fibers having a mean aspect ratio of greater than about 25, a specific gravity of greater than about 1.2, and a length of less than about 10 millimeters; introducing the cement composition into a subterranean formation; and allowing the cement composition to set therein.


Another example of a method of the present invention is a method comprising: providing a cement composition that comprises cement, water, and a plurality of melt-processed inorganic fibers, the melt-processed inorganic fibers having a mean aspect ratio of greater than about 25, a specific gravity of greater than about 1.2, and a length of less than about 10 millimeters; introducing the cement composition into a well bore that penetrates a subterranean formation, and allowing the melt-processed inorganic fibers to at least partially prevent fluid loss from the cement composition into the subterranean formation.


Another example of a method of the present invention is a method of treating a subterranean formation comprising: providing a drilling mud comprising a plurality of melt-processed inorganic fibers, wherein the melt-processed inorganic fibers have a length of less than about 10 millimeters and comprise at least one melt-processed inorganic fiber selected from the group consisting of: a basalt fiber, a wollastonite fiber, and a ceramic fiber; and circulating the drilling mud in the subterranean formation.


Another example of a method of the present invention is a method of reducing fluid loss in a subterranean drilling operation comprising: providing a drilling mud comprising a plurality of melt-processed inorganic fibers, comprising at least one melt-processed inorganic fiber selected from the group consisting of: a basalt fiber, a wollastonite fiber, and a ceramic fiber; and using the melt-processed inorganic fibers to at least partially reduce fluid loss in the subterranean drilling operation.


Another example of a method of the present invention is a method of treating a subterranean formation comprising: providing a drilling mud comprising a plurality of melt-processed inorganic fibers, wherein the melt-processed inorganic fibers have a mean aspect ratio of grater than about 25, a length of less than about 10 millimeters, and comprise at least one melt-processed inorganic fiber selected from the group consisting of: a basalt fiber, a wollastonite fiber, and a ceramic fiber; and circulating the drilling mud in the subterranean formation.


An example of a composition of the present invention comprises: water; cement; and a plurality of melt-processed inorganic fibers having a mean aspect ratio of greater than about 25, a specific gravity of greater than about 1.2, and a length of less than about 10 millimeters.


The features and advantages of the present invention will be readily apparent to those skilled in the art. While numerous changes may be made by those skilled in the art, such changes are within the spirit of the invention.





BRIEF DESCRIPTION OF THE DRAWINGS

These drawings illustrate certain aspects of some of the embodiments of the present invention, and should not be used to limit or define the invention



FIG. 1 is a photograph of the test apparatus used in Example 2.



FIG. 2 is another photograph of the test apparatus used in Example 2.





DETAILED DESCRIPTION OF EMBODIMENTS

The present invention relates to subterranean well cementing operations, and more particularly, to cement compositions comprising melt-processed inorganic fibers and methods for using such cement compositions.


Certain embodiments of the cement compositions of the present invention comprise a hydraulic cement, water, and a plurality of melt-processed inorganic fibers having a mean aspect ratio of greater than about 25, a specific gravity of greater than about 1.2, and a length of less than about 10 millimeters. As referred to herein, the term “aspect ratio” will be understood to mean the ratio of a solid body's length to its width. As referred to herein, the term “melt-processed inorganic fibers” will be understood to mean fibers produced from inorganic materials using any suitable melt processing technique, such as melt blowing or melt spinning.


Any hydraulic cement suitable for use in subterranean cementing operations may be used in accordance with the present invention. A variety of hydraulic cements are suitable for use, including those comprising calcium, aluminum, silicon, oxygen, and/or sulfur, which set and harden by reaction with water. Such hydraulic cements include, but are not limited to, Portland cements, pozzolanic cements, gypsum cements, soil cements, calcium phosphate cements, high alumina content cements, silica cements, high alkalinity cements, and mixtures thereof. In certain embodiments, the cement compositions of the present invention may comprise a Portland cement. In certain embodiments, the Portland cement may be chosen from those classified as Class A, C, G, and H cements according to API Specification for Materials and Testing for Well Cements, API Specification 10, Fifth Ed., Jul. 1, 1990. Another cement that may be useful in certain embodiments of the present invention is commercially available under the trade name “THERMALOCK™” from Halliburton Energy Services, Inc., of Duncan, Okla. Other cements that may be suitable for use in accordance with the present invention include, inter alia, low-density cements. Such low-density cements may be, inter alia, foamed cements or cements comprising another means to reduce their density, such as hollow microspheres, low-density elastic beads, fly ashes, blast furnace slag, or other density-reducing additives known in the art.


Generally, the water utilized in the cement compositions of the present invention may be fresh water, salt water (e.g., water containing one or more salts dissolved therein), brine (e.g., saturated salt water), seawater, or any combination thereof. This water may be from any source, provided that the water does not contain an excess of compounds (e.g., dissolved organics) that may adversely affect other components in the cement composition. In some embodiments, the water may be present in the cement compositions of the present invention in an amount sufficient to form a pumpable slurry. In certain embodiments, the water is present in the cement compositions of the present invention in an amount in the range of from about 30% to about 180% by weight of cement (“bwoc”) therein. In certain embodiments, the water is present in the cement compositions of the present invention in an amount in the range of from about 40% to about 50% bwoc therein. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the appropriate amount of water for a chosen application.


The cement compositions of the present invention comprise melt-processed inorganic fibers. Among other things, inclusion of melt-processed inorganic fibers in the cement compositions of the present invention may aid in the prevention of lost circulation and/or enhance the compressive and tensile strengths of the set cement composition. Inclusion of melt-processed inorganic fibers in the cement compositions of the present invention may be particularly appropriate when fluid loss of about 1 barrel per hour, or more, is encountered.


Melt processing is a well-known procedure for the production of fibers. Suitable melt processing techniques are described in Encyclopedia of Polymer Science and Engineering: Fiber Manufacture, J. E. Mcintyre and M. J. Denton (J. I. Kroschwitz ed., John Wiley and Sons 2d ed.). Suitable examples of melt-processed fibers include melt-blown fibers and melt-spun fibers. In some embodiments, combinations of melt-blown and melt-spun fibers may be used. The melt spinning of fibers may include spinning the material into a continuous strand of single or multiple filaments and then cutting it into a desired length.


The melt-processed inorganic fibers suitable for use in the methods and compositions of the present invention generally have a mean length of less than about 10 millimeters. In certain embodiments, the melt-processed inorganic fibers may have a mean length in the range of from about 0.1 millimeters to about 10 millimeters. In certain embodiments, the melt-processed inorganic fibers may have a mean length of about 0.5 millimeters, or about 1 millimeter, or about 2 millimeters, or about 3 millimeters, or about 4 millimeters, or about 5 millimeters, or about 6 millimeters, or about 7 millimeters, or about 8 millimeters, or about 9 millimeters, or about 10 millimeters. The melt-processed inorganic fibers suitable for use in the methods and compositions of the present invention generally have a mean aspect ratio of greater than about 25. In certain embodiments, the melt-processed inorganic fibers suitable for use in the methods and compositions of the present invention may have a mean aspect ratio of greater than about 100. In certain embodiments, the melt-processed inorganic fibers may have a mean aspect ratio in the range of from about 130 to about 660. In certain embodiments, the melt-processed inorganic fibers may have a mean aspect ratio in the range of from about 130 to about 330. In certain embodiments, the melt-processed inorganic fibers may have a mean aspect ratio in the range of from about 260 to about 660. The melt-processed inorganic fibers may be cut to any desired length, e.g., by mechanically cutting the fiber strands, so as to produce strands having a desired length. As will be appreciated by one of ordinary skill in the art, with the benefit of this disclosure, the length and diameter of the melt-processed inorganic fibers may be adjusted to enhance properties such as their flexibility and ease of dispersion in the cement compositions of the present invention.


The melt-processed inorganic fibers should be present in the cement compositions of the present invention in an amount sufficient to provide the desired mechanical properties and/or fluid loss control. In some embodiments, the melt-processed inorganic fibers may be present in the cement compositions of the present invention in an amount in the range of from about 0.1% to about 20% bwoc. In some embodiments, the melt-processed inorganic fibers may be present in an amount in the range of from about 0.1% to about 10% bwoc. In some embodiments, the melt-processed inorganic fibers may be present in the cement compositions of the present invention in an amount in the range of from about 0.1% to about 3% bwoc.


Suitable melt-processed inorganic fibers may be produced from a variety of materials. Examples of suitable inorganic fibers that may be melt-processed to form suitable melt-processed inorganic fibers include basalt fibers, wollastonite fibers, non-amorphous metallic fibers, ceramic fibers, glass fibers (e.g., AR glass fibers and non-AR glass fibers), and combinations thereof. Basalt fibers generally are produced from basalt, which is an igneous rock that is generally comprised of microscopic grains, such as calcium-sodium (plagioclase) feldspar, pyroxene, and olivine. Suitable melt-processed basalt fibers are commercially available from Sudaglass Fiber Technology, Houston, Tex. Suitable melt-processed ceramic fibers may be processed from alumina-silica material. An example of suitable commercially available melt-processed ceramic fibers is “FIBERFRAX” ceramic fiber, available from Unifrax Corporation, Niagara Falls, N.Y.


As noted above, in certain embodiments of the present invention, the melt-processed inorganic fibers may comprise nonamorphous metallic fibers that have been melt-processed. In certain embodiments, the non-amorphous metallic fibers may be obtained by cold drawing low-carbon steel wires (e.g., steel wool). Suitable metallic fibers include, but are not limited to, chopped steel fibers, stainless steel fibers, brass fibers, bronze fibers, nickel fibers, and titanium fibers. In certain embodiments of the present invention, the non-amorphous metallic fibers are low-carbon chopped steel wool fibers. Examples of suitable metallic fibers include, inter alia, those that are commercially available from Global Material Technologies, of Palatine, Ill., under the trade names “GMT-2136,” “GMT-180,” and “GMT-380.” In certain embodiments wherein steel fibers are used, the steel fibers may comprise carbon present in an amount in the range of from about 0.06% to about 0.11% by weight. In certain embodiments of the present invention wherein the high aspect ratio material comprises non-amorphous metallic fibers, the non-amorphous metallic fibers generally have a mean diameter in the range of from about 0.025 millimeters to about 0.10 millimeters, and a mean length in the range of from about 0.1 millimeter to about 10 millimeters. As will be appreciated by one of ordinary skill in the art, with the benefit of this disclosure, the length and diameter of the non-amorphous metallic fibers may be adjusted to enhance properties such as their flexibility and ease of dispersion in the cement compositions of the present invention. In certain embodiments of the present invention wherein non-amorphous metallic fibers are included, the non-amorphous metallic fibers generally have an aspect ratio in the range of from about 1.25 to about 400. In certain embodiments, the non-amorphous metallic fibers may have an aspect ratio in the range of from about 15 to about 200, and in certain other embodiments, from about 25 to about 100. In certain embodiments of the present invention where non-amorphous metallic fibers are included, the metallic fibers may be present in the cement compositions of the present invention in an amount in the range of from about 0.5% to about 10% bwoc. Due to their density, certain metallic fibers may exhibit a propensity to settle out of the cement compositions of the present invention. Therefore, certain embodiments of the cement compositions of the present invention that comprise melt-processed non-amorphous metallic fibers also may comprise a settling-prevention additive, such as a viscosifier, that may eliminate, or at least reduce, settling. Suitable settling-prevention additives include, inter alia, hydroxyethylcellulose, and xanthan gum. A suitable settling-prevention additive is commercially available from Halliburton Energy Services, Inc., under the trade name “FWCA.” Where settling-prevention additives are included in the cement composition, they should be present in the cement composition in an amount that facilitates a uniform density throughout the cement composition. In certain embodiments, non-amorphous metallic fibers may be coated by, e.g., surfactants that may inhibit any reaction that may occur between the cement composition and the metallic fibers. Examples of suitable surfactants that may be used to coat the non-amorphous metallic fibers include, inter alia, hydrophobic organic materials such as sorbitol mono-oleate, sorbitol tri-oleate, and the like. Sorbitol mono-oleate is commercially available from Aldrich Chemical Company, of Milwaukee, Wis., under the trade name “SPAN 80,” while sorbitol tri-oleate is commercially available from Aldrich Chemical Company under the trade name “SPAN 85.” In certain embodiments of the present invention wherein the non-amorphous metallic fibers are coated, the coating may be present on the non-amorphous metallic fibers in an amount in the range of from about 0.5% to about 5% by weight of the fibers.


As noted above, in certain embodiments of the present invention, the melt-processed inorganic fibers may comprise glass fibers. In certain embodiments, the glass fibers are alkali-resistant (AR) glass fibers, although non-AR glass fibers also may be used in certain embodiments of the present invention. Examples of suitable non-AR glass fibers include general purpose E-glass fibers and specialty glass fibers, such as ECR glass fibers (high corrosion resistance), A-glass fibers, and C-glass fibers. These grades refer to ASTM Specification D 578-98. In certain embodiments of the present invention where non-AR glass fibers are used, the non-AR glass fibers may be made alkali-resistant through the application of a coating with an acrylic acid-based polymer, as will be understood by one of ordinary skill in the art, with the benefit of this disclosure. In certain embodiments wherein the cement compositions of the present invention comprise an alkaline cement, and the melt-processed inorganic fibers comprise glass fibers, AR glass fibers may be particularly suitable. However, when prepared using larger portions of pozzolanic or latent-hydraulic cement additives (e.g., coal, fly ash, or silica dust), or high aluminate cements, certain embodiments of the cement compositions of the present invention may have lower pH values, which may facilitate the use of non-AR glass fibers. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the amounts and mixtures of AR and non-AR resistant glass fibers to use depending on the alkalinity of the cement being used. In certain embodiments, the AR glass fibers may comprise zirconium oxide in an amount in the range of from about 0.01% to about 15% by weight; in certain other embodiments, the AR glass fibers may comprise zirconium oxide in an amount in the range of from about 10% to about 15% by weight. In certain embodiments of the present invention, the glass fibers have a length in the range of from 0.5 to about 10 millimeters, and a diameter in the range of from about 10 to about 400 microns. In certain embodiments, the glass fibers may have an aspect ratio in the range of from about 1.25 to about 5,000. In certain embodiments, the glass fibers may have an aspect ratio in the range of from about 10 to about 1,000, and in certain other embodiments, from about 20 to about 500. Examples of suitable glass fibers include, inter alia, “CEM-FIL® HD” chopped strands and “CEM-FIL® HP” chopped strands, available from Saint-Gobain Vetrotex America, Inc., of Valley Forge, Pa. Other examples of suitable glass fibers include, inter alia, “E” grade “FIBERGLAST,” available from Fiberglast Development Corp., of Brookville, Ohio. When included in the cement compositions of the present invention, the glass fibers may be present in an amount in the range of from about 0.1% to about 20% bwoc.


Optionally, the non-amorphous metallic fibers and the glass fibers described above may be added to the cement composition without having been melt-processed, as an additional component to the melt-processed inorganic fibers.


Optionally, certain embodiments of the cement compositions of the present invention also may include solid materials that may strengthen and reinforce the cement. These solid materials may include both natural and man-made materials, and may have any shape, including, but not limited to, beaded, cubic, bar-shaped, flake, fiber, platelets, cylindrical, or mixtures thereof. Suitable such solid materials include, but are not limited to, carbon fibers, plastic fibers (e.g., polypropylene and polyacrylic nitrile fibers), and combinations thereof. Where included, these additional solid materials may be added to the cement composition of the present invention individually or in combination. Additionally, the solid materials of the present invention may be present in the cement composition in a variety of lengths and aspect ratios. One of ordinary skill in the art, with the benefit of this disclosure, will recognize the mixtures of type, length, and aspect ratio to use to achieve the desired properties of a cement composition for a particular application.


Optionally, additional additives may be added to the cement compositions of the present invention as deemed appropriate by one skilled in the art with the benefit of this disclosure. Examples of such additives include, inter alia, fly ash, silica compounds, fluid loss control additives, lost circulation materials, a surfactant, a dispersant, an accelerator, a retarder, a salt, a formation conditioning agent, fumed silica, bentonite, microspheres, expanding additives, weighting materials, organic fibers, and the like. For example, the cement compositions of the present invention may be foamed cement compositions comprising an expanding additive that produces gas within the cement composition in order, inter alia, to reduce the cement composition's density. An example of a suitable expanding additive comprises a blend containing gypsum, and is commercially available under the trade name “MICROBOND” from Halliburton Energy Services, Inc., at various locations. One of ordinary skill in the art with the benefit of this disclosure will recognize the proper amount of an expanding additive to use in order to provide a foamed cement composition having a desired density. An example of a suitable sodium silicate is commercially available from Halliburton Energy Services, Inc., under the trade name ECONOLITE®. An example of a suitable additive that demonstrates free-water-reduction and solids-suspension properties is commercially available from Halliburton Energy Services, Inc., of Duncan, Okla., under the trade name “FWCA™.” An example of a suitable dispersant is commercially available from Halliburton Energy Services, Inc., under the trade name “CFR-3.” An example of a suitable fly ash is an ASTM class F fly ash that is commercially available from Halliburton Energy Services, Inc., under the trade name “POZMIX® A.” An example of a suitable silica flour is commercially available from Halliburton Energy Services, Inc., under the trade name “SSA-1.” An example of a suitable fumed silica is an aqueous suspension of fumed silica that is commercially available from Halliburton Energy Services, Inc., under the trade name “MICROBLOCK.” An example of a suitable foaming surfactant is commercially available from Halliburton Energy Services, Inc., under the trade name “ZONESEAL 3000.” An example of a suitable defoamer is commercially available from Halliburton Energy Services, Inc., under the trade name “D-AIR 3000L.”


The melt-processed inorganic fibers may be added to the cement composition at any suitable time, such as before, after, or simultaneously with combining the water and the cement.


To facilitate a better understanding of the present invention, the following examples of certain aspects of some embodiments are given. In no way should the following examples be read to limit, or define, the scope of the invention.


EXAMPLE 1

Sample compositions were prepared by mixing a base fluid with various amounts and grades of fibers. The base fluid comprised an aqueous suspension of 1.64% bentonite clay by weight. For some sample compositions, fibers were mixed into the base fluid. The fibers that were used were either (i) glass fibers, having a mean length of 3 millimeters, commercially available from Saint Gobain Vetrotex, of Madrid, Spain; or (ii) basalt fibers, having a mean length of 6 millimeters, commercially available from Sudaglass Fiber Technology. The AR glass fibers were strand cut to a length of about 3 millimeters with a diameter of about 20 microns, and thus had an aspect ratio of 150. The basalt fibers were strand cut to a length of about 6 millimeters and had a mean aspect ratio in the range of from about 230 to about 660. The sample compositions were charged into a cement fluid loss cell used for measurement of cement slurry losses as described in API Recommended Practice 10B, Twenty-Second Edition, December 1997. The volume of fluid loss for each sample composition was measured as a function of time, and was calculated for 30-minute fluid losses according to the equations provided in the aforementioned API manual.


Sample Composition No. 1 comprised 600 cubic centimeters of water and 10 grams of bentonite clay, with no fibers.


Sample Composition No. 2 comprised the base fluid and AR glass fibers in an amount of about 1.98 pounds per barrel.


Sample Composition No. 3 comprised the base fluid and AR glass fibers in an amount of about 4.95 pounds per barrel. Visual observation of Sample Composition No. 3 indicated that the glass fibers and the bentonite clay formed lumps of a gelatinous mass.


Sample Composition No. 4 comprised the base fluid and basalt fibers in an amount of about 1.98 pounds per barrel.


Sample Composition No. 5 comprised the base fluid and basalt fibers in an amount of about 4.95 pounds per barrel. Visual observation of Sample Composition No. 5 indicated that the basalt fibers and the bentonite clay formed lumps of a gelatinous mass.


The results of the testing are set forth in Table 1, below.
















TABLE 1










Total






Fiber
Fiber
Initial
Fluid

Calculated


Sample
Fiber
Length
Amount
Spurt
Collected
Time
Fluid Loss


Composition
Type
(mm)
(lb/bbl)
(ml)
(ml)
(min)
(cc/min)






















Sample
None
None
None
33
179
17
476


Composition


No. 1


Sample
AR
3
1.98
33
58
30
116


Composition
Glass


No. 2


Sample
AR
3
4.95
60
105
30
206


Composition
Glass


No. 3


Sample
Basalt
6
1.98
44
112
30
224


Composition


No. 4


Sample
Basalt
6
4.95
120
135
4.1
731


Composition


No. 5









Example 1 demonstrates, inter alia, that the lost circulation materials of the present invention reduce lost circulation.


EXAMPLE 2

A cement fluid loss cell, illustrated in FIGS. 1 and 2, was equipped on the bottom end with hemispherical plates that were attached (via screws) to a plate having an elliptical opening that was aligned to match with spacing of the hemispherical plates. The hemispherical plates were spaced apart to provide a slit having a predefined width. The bottom plate assembly was secured to the bottom of the pressure chamber with a set of threaded metal rings, and the top of the pressure vessel was equipped with a lid having an attachment for connection with a pressurized gas supply. The slot width was fixed at 0.01 inches, and the slot length was fixed at 1.75 inches. A fluid volume of 200 milliliters of a mud comprising about 6.25% bentonite by weight was used to charge the vessel for each run. After the vessel was charged, air pressure of 100 psi was applied, and the time of the run (e.g., the time until all fluid was lost through the slit) was monitored.


Sample Composition No. 6 comprised the base fluid, with no fibers added.


Sample Composition No. 7 comprised the base fluid, with 2 grams of AR glass fibers that had been strand cut to a length of 3 millimeters.


Sample Composition No. 8 comprised the base fluid, with 5 grams of AR glass fibers that had been strand cut to a length of 3 millimeters.


Sample Composition No. 9 comprised the base fluid, with 10 grams of AR glass fibers that had been strand cut to a length of 3 millimeters.


Sample Composition No. 10 comprised the base fluid, with 2 grams of basalt fibers that had been strand cut to a length of 6 millimeters.


Sample Composition No. 11 comprised the base fluid, with 5 grams of basalt fibers that had been strand cut to a length of 6 millimeters.


Sample Composition No. 12 comprised the base fluid, with 10 grams of basalt fibers that had been strand cut to a length of 6 millimeters.


Sample Composition No. 13 comprised the base fluid, with 2 grams of AR glass fibers that had been strand cut to a length of 6 millimeters.


Sample Composition No. 14 comprised the base fluid, with 5 grams of AR glass fibers that had been strand cut to a length of 6 millimeters.


Sample Composition No. 15 comprised the base fluid, with 10 grams of AR glass fibers that had been strand cut to a length of 6 millimeters.


The results of the testing are set forth in Table 2, below.













TABLE 2









Time to




Fiber
Fiber
Complete



Fiber
Length
Amount
Fluid Loss


Sample Composition
Type
(mm)
(grams)
(seconds)



















Sample Composition
None
None
None
1.64


No. 6


Sample Composition
AR Glass
3
2
3.64


No. 7


Sample Composition
AR Glass
3
5
6.21


No. 8


Sample Composition
AR Glass
3
10
5.00


No. 9



(plugged)


Sample Composition
Basalt
6
2
1.75


No. 10


Sample Composition
Basalt
6
5
3.72


No. 11


Sample Composition
Basalt
6
10
5.62


No. 12


Sample Composition
AR Glass
6
2
1.55


No. 13


Sample Composition
AR Glass
6
5
5.56


No. 14


Sample Composition
AR Glass
6
10
11.96


No. 15









Sample Composition No. 9 plugged, and the experiment was halted after 5 minutes had elapsed. About 100 grams of fluid remained in the chamber when the experiment was halted.


Example 2 demonstrates, inter alia, that the improved lost circulation compositions of the present invention desirably reduce the loss of circulation.


Therefore, the present invention is well adapted to attain the ends and advantages mentioned as well as those that are inherent therein. The particular embodiments disclosed above are illustrative only, as the present invention may be modified and practiced in different but equivalent manners apparent to those skilled in the art having the benefit of the teachings herein. Furthermore, no limitations are intended to the details of construction or design herein shown, other than as described in the claims below. It is therefore evident that the particular illustrative embodiments disclosed above may be altered or modified and all such variations are considered within the scope and spirit of the present invention. In particular, every range of values (of the form, “from about a to about b,” or, equivalently, “from approximately a to b,” or, equivalently, “from approximately a-b”) disclosed herein is to be understood as referring to the power set (the set of all subsets) of the respective range of values, and set forth every range encompassed within the broader range of values. Also, the terms in the claims have their plain, ordinary meaning unless otherwise explicitly and clearly defined by the patentee.

Claims
  • 1. A method of treating a subterranean formation comprising: providing a drilling mud comprising a plurality of melt-processed inorganic fibers, wherein the melt-processed inorganic fibers have a length of less than 10 millimeters and comprise at least one melt-processed inorganic fiber selected from the group consisting of: a basalt fiber and a ceramic fiber; andcirculating the drilling mud in the subterranean formation.
  • 2. The method of claim 1 wherein the drilling mud comprises an aqueous fluid and bentonite.
  • 3. The method of claim 1 wherein the melt-processed inorganic fibers have a specific gravity of greater than about 1.2.
  • 4. The method of claim 1 wherein the melt-processed inorganic fibers comprise at least one melt-processed inorganic fiber selected from the group consisting of: a melt-spun fiber and a melt-blown fiber.
  • 5. The method of claim 1 wherein the melt-processed inorganic fibers have a mean aspect ratio of greater than about 25.
  • 6. The method of claim 1 wherein the melt-processed inorganic fibers have a mean aspect ratio in the range of from about 130 to about 660.
  • 7. The method of claim 1 wherein the drilling mud further comprises non-amorphous metallic fibers having a mean aspect ratio of from about 1.25 to about 400.
  • 8. The method of claim 1 wherein the drilling mud further comprises glass fibers having a mean aspect ratio in the range of from about 1.25 to about 5,000.
  • 9. The method of claim 8 wherein the glass fibers have a mean length of from about 0.5 millimeters to about 6 millimeters.
  • 10. A method of reducing fluid loss in a subterranean drilling operation comprising: providing a drilling mud comprising a plurality of melt-processed inorganic fibers, the melt-processed inorganic fibers comprising at least one melt-processed inorganic fiber selected from the group consisting of: a basalt fiber, a wollastonite fiber, and a ceramic fiber; andusing the melt-processed inorganic fibers to at least partially reduce fluid loss in the subterranean drilling operation.
  • 11. The method of claim 10 wherein the melt-processed inorganic fibers have a mean aspect ratio of greater than about 25, a specific gravity of greater than about 1.2, and a length of less than about 10 millimeters.
  • 12. The method of claim 10 wherein the drilling mud comprises an aqueous fluid and bentonite.
  • 13. The method of claim 10 wherein the melt-processed inorganic fibers comprise at least one melt-processed inorganic fiber selected from the group consisting of: a melt-spun fiber and a melt-blown fiber.
  • 14. The method of claim 10 wherein the melt-processed inorganic fibers have a mean aspect ratio of greater than about 25.
  • 15. The method of claim 10 wherein the melt-processed inorganic fibers have a mean aspect ratio in the range of from about 130 to about 660.
  • 16. The method of claim 10 wherein the drilling mud further comprises non-amorphous metallic fibers having a mean aspect ratio of from about 1.25 to about 400.
  • 17. The method of claim 10 wherein the drilling mud further comprises glass fibers having a mean aspect ratio in the range of from about 1.25 to about 5,000.
  • 18. The method of claim 17 wherein the glass fibers have a mean length of from about 0.5 millimeters to about 6 millimeters.
  • 19. A method of treating a subterranean formation comprising: providing a drilling mud comprising a plurality of melt-processed inorganic fibers, wherein the melt-processed inorganic fibers have a mean aspect ratio of greater than about 25, a length of less than about 10 millimeters, and comprise at least one melt-processed inorganic fiber selected from the group consisting of: a basalt fiber and a ceramic fiber; andcirculating the drilling mud in the subterranean formation.
  • 20. The method of claim 19 wherein the drilling mud comprises an aqueous fluid and bentonite.
CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. patent application Ser. No. 11/272,951 entitled “Compositions Comprising Melt-Processed Inorganic Fibers and Methods of Using Such Compositions,” filed on Nov. 14, 2005, now abandoned which is a continuation-in-part of U.S. patent application Ser. No. 11/101,762, entitled “Cement Compositions Comprising High Aspect Ratio Materials, and Methods of Use in Subterranean Formations,” filed on Apr. 8, 2005, which is a continuation-in-part of U.S. patent application Ser. No. 10/884,756 filed on Jul. 2, 2004, now U.S. Pat. No. 7,178,597 the entirety of each of which are herein incorporated by reference, and from which priority is claimed pursuant to 35 U.S.C. § 120.

US Referenced Citations (138)
Number Name Date Kind
2463561 Riley Mar 1949 A
2738285 Biefeld et al. Mar 1956 A
2779417 Clark et al. Jan 1957 A
2805719 Anderson Sep 1957 A
3036633 Mayhew May 1962 A
3092505 Demaison Jun 1963 A
3146828 Mann Sep 1964 A
3220863 Mayhew Nov 1965 A
3363689 Smith et al. Jan 1968 A
3736162 Chvalovsky et al. May 1973 A
3774683 Smith et al. Nov 1973 A
3834916 Kesler Sep 1974 A
3844351 Sutton et al. Oct 1974 A
3852082 Majumdar et al. Dec 1974 A
3854986 Chvalovsky et al. Dec 1974 A
3861926 Irlam et al. Jan 1975 A
3861927 Kimura et al. Jan 1975 A
3904424 Aoki et al. Sep 1975 A
3953953 Marsden May 1976 A
4008094 Beall et al. Feb 1977 A
4030939 Mallow Jun 1977 A
4036654 Yale et al. Jul 1977 A
4062913 Miller et al. Dec 1977 A
4066465 Mohri et al. Jan 1978 A
4090884 Goeman May 1978 A
4140533 Ohtomo et al. Feb 1979 A
4142906 Iizawa Mar 1979 A
4199336 Rittler Apr 1980 A
4224377 Moens Sep 1980 A
4240840 Downing et al. Dec 1980 A
4289536 Dereser Sep 1981 A
4304604 Daerr et al. Dec 1981 A
4341835 MacDowell Jul 1982 A
4345037 Fyles et al. Aug 1982 A
4366255 Lankard Dec 1982 A
4474907 Genba et al. Oct 1984 A
4534796 Massol et al. Aug 1985 A
4565840 Kobayashi et al. Jan 1986 A
4585487 Destree et al. Apr 1986 A
4610926 Tezuka Sep 1986 A
4689084 Ambroise et al. Aug 1987 A
4780141 Double et al. Oct 1988 A
4793861 Sohm Dec 1988 A
4818288 Aignesberger et al. Apr 1989 A
4835122 Chopinet et al. May 1989 A
4836940 Alexander Jun 1989 A
4858487 Mercier Aug 1989 A
4871395 Sugama Oct 1989 A
4923517 Rerup et al. May 1990 A
4960649 Takata et al. Oct 1990 A
4968561 Mizobe et al. Nov 1990 A
4975396 Thiery Dec 1990 A
5064785 Kawamoto et al. Nov 1991 A
5118225 Koch et al. Jun 1992 A
5154955 Delvaux et al. Oct 1992 A
5167710 Leroux et al. Dec 1992 A
5225243 Bruck et al. Jul 1993 A
5298071 Vondran Mar 1994 A
5339902 Harris et al. Aug 1994 A
5358676 Jennings et al. Oct 1994 A
5421409 Mueller et al. Jun 1995 A
5443918 Banthia et al. Aug 1995 A
5447564 Xie et al. Sep 1995 A
5456752 Hogan Oct 1995 A
5489626 Takaki et al. Feb 1996 A
5588489 Chatterji et al. Dec 1996 A
5628822 Hogan May 1997 A
5641815 Fehlmann Jun 1997 A
5648568 Oharu et al. Jul 1997 A
5649568 Allen et al. Jul 1997 A
5690729 Jones Nov 1997 A
5711801 Chatterji et al. Jan 1998 A
5820670 Chatterji et al. Oct 1998 A
5865000 Nemegeer et al. Feb 1999 A
5875845 Chatterji et al. Mar 1999 A
5897699 Chatterji et al. Apr 1999 A
5900053 Brothers et al. May 1999 A
5916361 Molloy et al. Jun 1999 A
5948157 McKenney et al. Sep 1999 A
5981630 Banthia et al. Nov 1999 A
6016879 Burts Jan 2000 A
6060535 Villar et al. May 2000 A
6063738 Chatterji et al. May 2000 A
6080234 Clavaud et al. Jun 2000 A
6143069 Brothers et al. Nov 2000 A
6152227 Lawson et al. Nov 2000 A
6156808 Chatterji et al. Dec 2000 A
6220354 Chatterji et al. Apr 2001 B1
6230804 Mueller et al. May 2001 B1
6297202 Chatterji et al. Oct 2001 B1
6308777 Chatterji et al. Oct 2001 B2
6332921 Brothers et al. Dec 2001 B1
6367550 Chatterji et al. Apr 2002 B1
6457524 Roddy Oct 2002 B1
6458198 Baret et al. Oct 2002 B1
6488763 Brothers et al. Dec 2002 B2
6500252 Chatterji et al. Dec 2002 B1
6508305 Brannon et al. Jan 2003 B1
6547871 Chatterji et al. Apr 2003 B2
6550362 Galinat et al. Apr 2003 B1
6582511 Velpari Jun 2003 B1
6613424 Putt et al. Sep 2003 B1
6645288 Dargaud et al. Nov 2003 B1
6647747 Brik Nov 2003 B1
6689208 Brothers Feb 2004 B1
6702044 Reddy et al. Mar 2004 B2
6706380 Edwards et al. Mar 2004 B2
6723162 Cheyrezy et al. Apr 2004 B1
6729405 DiLullo et al. May 2004 B2
6823940 Reddy et al. Nov 2004 B2
6824847 Mariaggi et al. Nov 2004 B2
6832651 Ravi et al. Dec 2004 B2
6861392 Shaarpour Mar 2005 B2
6866712 Rossi et al. Mar 2005 B1
6907929 Leroy-Delage et al. Jun 2005 B2
6962201 Brothers Nov 2005 B2
7174961 Chatterji et al. Feb 2007 B2
7178597 Reddy et al. Feb 2007 B2
7284611 Reddy et al. Oct 2007 B2
20020069537 Wenzler et al. Jun 2002 A1
20020157575 DiLullo et al. Oct 2002 A1
20030010314 Brossear et al. Jan 2003 A1
20040040712 Ravi et al. Mar 2004 A1
20040045713 Bianchi et al. Mar 2004 A1
20040069537 Reddy et al. Apr 2004 A1
20040069538 Reddy et al. Apr 2004 A1
20040106704 Meyer et al. Jun 2004 A1
20040108141 Reddy et al. Jun 2004 A1
20040194960 DiLullo et al. Oct 2004 A1
20040206501 Brothers et al. Oct 2004 A1
20040211562 Brothers et al. Oct 2004 A1
20060000611 Reddy et al. Jan 2006 A1
20060000612 Reddy et al. Jan 2006 A1
20060096759 Reddy et al. May 2006 A1
20060157244 Reddy et al. Jul 2006 A1
20060174802 Bedel et al. Aug 2006 A1
20060213664 Chatterji et al. Sep 2006 A1
20070051516 Reddy et al. Mar 2007 A1
Foreign Referenced Citations (15)
Number Date Country
1284248 Feb 2003 EP
2 392 682 Mar 2004 GB
60016853 Jan 1985 JP
5339040 Dec 1993 JP
WO 0066878 Sep 2000 WO
WO 0218291 Mar 2002 WO
WO 03014040 Feb 2003 WO
WO 03048526 Jun 2003 WO
WO 2004022500 Mar 2004 WO
WO 2004022500 Mar 2004 WO
WO 2004101704 Nov 2004 WO
WO 2006003389 Jan 2006 WO
WO 2006100506 Sep 2006 WO
WO 2006106301 Oct 2006 WO
WO 2007054670 May 2007 WO
Related Publications (1)
Number Date Country
20080103065 A1 May 2008 US
Continuations (1)
Number Date Country
Parent 11272951 Nov 2005 US
Child 11940173 US
Continuation in Parts (2)
Number Date Country
Parent 11101762 Apr 2005 US
Child 11272951 US
Parent 10884756 Jul 2004 US
Child 11101762 US