Patent Application
20210108134
This disclosure is in the field of solid-state lighting. In particular, the disclosure relates to luminophoric compositions for use in methods of generating white light.
A wide variety of light emitting devices are known in the art including, for example, incandescent light bulbs, fluorescent lights, and semiconductor light emitting devices such as light emitting diodes (“LEDs”).
There are a variety of resources utilized to describe the light produced from a light emitting device, one commonly used resource is 1931 CIE (Commission Internationale de l'Éclairage) Chromaticity Diagram. The 1931 CIE Chromaticity Diagram maps out the human color perception in terms of two CIE parameters x and y. The spectral colors are distributed around the edge of the outlined space, which includes all of the hues perceived by the human eye. The boundary line represents maximum saturation for the spectral colors, and the interior portion represents less saturated colors including white light. The diagram also depicts the Planckian locus, also referred to as the black body locus (BBL), with correlated color temperatures, which represents the chromaticity coordinates (i.e., color points) that correspond to radiation from a black-body at different temperatures. Illuminants that produce light on or near the BBL can thus be described in terms of their correlated color temperatures (CCT). These illuminants yield pleasing “white light” to human observers, with general illumination typically utilizing CCT values between 1,800K and 10,000K.
Color rendering index (CRI) is described as an indication of the vibrancy of the color of light being produced by a light source. In practical terms, the CRI is a relative measure of the shift in surface color of an object when lit by a particular lamp as compared to a reference light source, typically either a black-body radiator or the daylight spectrum. The higher the CRI value for a particular light source, the better that the light source renders the colors of various objects it is used to illuminate.
LEDs have the potential to exhibit very high power efficiencies relative to conventional incandescent or fluorescent lights. Most LEDs are substantially monochromatic light sources that appear to emit light having a single color. Thus, the spectral power distribution of the light emitted by most LEDs is tightly centered about a “peak” wavelength, which is the single wavelength where the spectral power distribution or “emission spectrum” of the LED reaches its maximum as detected by a photo-detector. LEDs typically have a full-width half-maximum wavelength range of about 10 nm to 30 nm, comparatively narrow with respect to the broad range of visible light to the human eye, which ranges from approximately from 380 nm to 800 nm.
In order to use LEDs to generate white light, LED lamps have been provided that include two or more LEDs that each emit a light of a different color. The different colors combine to produce a desired intensity and/or color of white light. For example, by simultaneously energizing red, green and blue LEDs, the resulting combined light may appear white, or nearly white, depending on, for example, the relative intensities, peak wavelengths and spectral power distributions of the source red, green and blue LEDs. The aggregate emissions from red, green, and blue LEDs typically provide poor CRI for general illumination applications due to the gaps in the spectral power distribution in regions remote from the peak wavelengths of the LEDs.
White light may also be produced by utilizing one or more luminescent materials such as phosphors to convert some of the light emitted by one or more LEDs to light of one or more other colors. The combination of the light emitted by the LEDs that is not converted by the luminescent material(s) and the light of other colors that are emitted by the luminescent material(s) may produce a white or near-white light.
LED lamps have been provided that can emit white light with different CCT values within a range. Such lamps utilize two or more LEDs, with or without luminescent materials, with respective drive currents that are increased or decreased to increase or decrease the amount of light emitted by each LED. By controllably altering the power to the various LEDs in the lamp, the overall light emitted can be tuned to different CCT values. The range of CCT values that can be provided with adequate CRI values and efficiency is limited by the selection of LEDs.
The spectral profiles of light emitted by white artificial lighting can impact circadian physiology, alertness, and cognitive performance levels. Bright artificial light can be used in a number of therapeutic applications, such as in the treatment of seasonal affective disorder (SAD), certain sleep problems, depression, jet lag, sleep disturbances in those with Parkinson's disease, the health consequences associated with shift work, and the resetting of the human circadian clock. Artificial lighting may change natural processes, interfere with melatonin production, or disrupt the circadian rhythm. Blue light may have a greater tendency than other colored light to affect living organisms through the disruption of their biological processes which can rely upon natural cycles of daylight and darkness. Consequently, exposure to blue light late in the evening and at night may be detrimental to one's health.
Significant challenges remain in providing LED lamps that can provide white light across a range of CCT values while simultaneously achieving high efficiencies, high luminous flux, good color rendering, and acceptable color stability. It is also a challenge to provide lighting apparatuses that can provide desirable lighting performance while allowing for the control of circadian energy performance.
It is therefore a desideratum to provide compositions for converting light generated by LEDs into white light with desirable spectral characteristics.
Disclosed herein are aspects of compositions for use in generating white light, the compositions comprising a plurality of luminescent materials and a matrix material formed in a volumetric ratio. The plurality of luminescent materials can comprise one or more of a first type of luminescent material that emits light at a peak emission between about 515 nm and 590 nm in response to the associated LED string emission, and one or more of a second type of luminescent material that emits light at a peak emission between about 590 nm and about 700 nm in response to the associated LED string emission. In some implementations, the one or more of the first type of luminescent materials comprise BaMgAl10O17:Eu, Lu3Al5O12:Ce, (La,Y)3Si6N11:Ce, or Y3Al5O12:Ce. In some implementations, the one or more of the second type of luminescent materials comprise CaAlSiN3:Eu, (Sr,Ca)AlSiN3, or one or more semiconductor quantum dots. In some implementations the compositions are configured to be excited by LEDs that emit substantially saturated light at wavelengths between about 360 nm and about 535 nm to produce light having color points within the suitable blue color ranges 301A-C, red color ranges 302A-C, yellow/green color ranges 303A-C, and cyan color ranges 304A-C disclosed herein. In some instances the compositions are configured so that the light emitted by the LED(s) and associated compositions together have spectral power distributions (“SPD”) having spectral power with ratios of power across the visible wavelength spectrum that fall within the ranges disclosed herein in
Disclosed herein are aspects of methods of generating white light, the methods comprising passing light from a first LED string through a first luminophoric medium comprised of one or more luminescent materials and matrix in a first ratio for a first combined light in a blue color range on 1931 CIE diagram, passing light from a second LED string through a second luminophoric medium comprised of one or more luminescent materials and matrix in a second ratio for a second combined light in a red color range on 1931 CIE diagram, passing light from a third LED string through a third luminophoric medium comprised of one or more luminescent materials and matrix in a third ratio for a third combined light in a yellow/green color range on 1931 CIE diagram, passing light from a fourth LED string through a fourth luminophoric medium comprised of one or more luminescent materials and matrix in a fourth ratio for a fourth combined light in a cyan color range on 1931 CIE diagram, and mixing the first, second, third, and fourth combined light together. In some implementations the blue color range comprises one of regions 301A, 301B, or 301C, the red color range comprises one of regions 302A, 302B, or 302C, the yellow/green color range comprises one of regions 303A, 303B, or 303C, and the cyan color range comprises one of regions 304A, 304B, or 304C. In some instances, the first, second, third, and fourth combined lights can have spectral power distributions (“SPD”) having spectral power with ratios of power across the visible wavelength spectrum that fall within the ranges disclosed herein in
The general disclosure and the following further disclosure are exemplary and explanatory only and are not restrictive of the disclosure, as defined in the appended claims. Other aspects of the present disclosure will be apparent to those skilled in the art in view of the details as provided herein. In the figures, like reference numerals designate corresponding parts throughout the different views. All callouts and annotations are hereby incorporated by this reference as if fully set forth herein.
The disclosure, as well as the following further disclosure, is best understood when read in conjunction with the appended drawings. For the purpose of illustrating the disclosure, there are shown in the drawings exemplary implementations of the disclosure; however, the disclosure is not limited to the specific methods, compositions, and devices disclosed. In addition, the drawings are not necessarily drawn to scale. In the drawings:
The general disclosure and the following further disclosure are exemplary and explanatory only and are not restrictive of the disclosure, as defined in the appended claims. Other aspects of the present disclosure will be apparent to those skilled in the art in view of the details as provided herein. In the figures, like reference numerals designate corresponding parts throughout the different views. All callouts and annotations are hereby incorporated by this reference as if fully set forth herein.
Light emitting diode (LED) illumination has a plethora of advantages over incandescent to fluorescent illumination. Advantages include longevity, low energy consumption, and small size. White light is produced from a combination of LEDs utilizing phosphors to convert the wavelengths of light produced by the LED into a preselected wavelength or range of wavelengths.
In one aspect, the present disclosure provides semiconductor light emitting devices 100 that can have a plurality of light emitting diode (LED) strings. Each LED string can have one, or more than one, LED. As depicted schematically in
A recipient luminophoric medium 102A, 102B, 102C, or 102D includes one or more luminescent materials and is positioned to receive light that is emitted by an LED or other semiconductor light emitting device. In some implementations, recipient luminophoric mediums include layers having luminescent materials that are coated or sprayed directly onto a semiconductor light emitting device or on surfaces of the packaging thereof, and clear encapsulants that include luminescent materials that are arranged to partially or fully cover a semiconductor light emitting device. A recipient luminophoric medium may include one medium layer or the like in which one or more luminescent materials are mixed, multiple stacked layers or mediums, each of which may include one or more of the same or different luminescent materials, and/or multiple spaced apart layers or mediums, each of which may include the same or different luminescent materials. Suitable encapsulants are known by those skilled in the art and have suitable optical, mechanical, chemical, and thermal characteristics. In some implementations, encapsulants can include dimethyl silicone, phenyl silicone, epoxies, acrylics, and polycarbonates. In some implementations, a recipient luminophoric medium can be spatially separated (i.e., remotely located) from an LED or surfaces of the packaging thereof, with luminescent materials disposed within a matrix material. The matrix material can be any material capable of retaining luminescent materials and capable of allowing light to pass through it. In some implementations, such spatial segregation may involve separation of a distance of at least about 1 mm, at least about 2 mm, at least about 5 mm, or at least about 10 mm. In certain embodiments, conductive thermal communication between a spatially segregated luminophoric medium and one or more electrically activated emitters is not substantial. Luminescent materials can include phosphors, scintillators, day glow tapes, nanophosphors, inks that glow in visible spectrum upon illumination with light, semiconductor quantum dots, or combinations thereof.
As depicted schematically in
The light emitted by a light source may be represented by a point on a chromaticity diagram, such as the 1931 CIE chromaticity diagram, having color coordinates denoted (ccx, ccy) on the X-Y axes of the diagram. A region on a chromaticity diagram may represent light sources having similar chromaticity coordinates.
In some exemplary implementations, the present disclosure provides semiconductor light emitting devices 100 that include a plurality of LED strings, with each LED string having a recipient luminophoric medium that comprises a luminescent material. The LED(s) in each string and the luminophoric medium in each string together emit an unsaturated light having a color point within a color range in the 1931 CIE chromaticity diagram. A “color range” in the 1931 CIE chromaticity diagram refers to a bounded area defining a group of color coordinates (ccx, ccy).
In some implementations, four LED strings (101A/101B/101C/101D) are present in a device 100, and the LED strings can have recipient luminophoric mediums (102A/102B/102C/102D). A first LED string 101A and a first luminophoric medium 102A together can emit a first light having a first color point within a blue color range. The combination of the first LED string 101A and the first luminophoric medium 102A are also referred to herein as a “blue channel.” A second LED string 101B and a second luminophoric medium 102B together can emit a second light having a second color point within a red color range. The combination of the second LED string 101A and the second luminophoric medium 102A are also referred to herein as a “red channel.” A third LED string 101C and a third luminophoric medium 102C together can emit a third light having a third color point within a yellow/green color range. The combination of the third LED string 101A and the third luminophoric medium 102A are also referred to herein as a “yellow/green channel.” A fourth LED string 101D and a fourth luminophoric medium 102D together can emit a fourth light having a fourth color point within a cyan color range. The combination of the fourth LED string 101A and the fourth luminophoric medium 102A are also referred to herein as a “cyan channel.” The first, second, third, and fourth LED strings 101A/101B/101C/101D can be provided with independently applied on-state drive currents in order to tune the intensity of the first, second, third, and fourth unsaturated light produced by each string and luminophoric medium together. By varying the drive currents in a controlled manner, the color coordinate (ccx, ccy) of the total light that is emitted from the device 100 can be tuned. In some implementations, the device 100 can provide light at substantially the same color coordinate with different spectral power distribution profiles, which can result in different light characteristics at the same CCT. In some implementations, white light can be generated in modes that only produce light from two or three of the LED strings. In one implementation, white light is generated using only the first, second, and third LED strings, i.e. the blue, red, and yellow/green channels. In another implementation, white light is generated using only the first, second, and fourth LED strings, i.e., the blue, red, and cyan channels. In some implementations, only two of the LED strings are producing light during the generation of white light, as the other two LED strings are not necessary to generate white light at the desired color point with the desired color rendering performance.
In some implementations, suitable color ranges can be narrower than those depicted in
In some implementations, the LEDs in the first, second, third and fourth LED strings can be LEDs with peak emission wavelengths at or below about 535 nm. In some implementations, the LEDs emit light with peak emission wavelengths between about 360 nm and about 535 nm. In some implementations, the LEDs in the first, second, third and fourth LED strings can be formed from InGaN semiconductor materials. In some preferred implementations, the first, second, and third LED strings can have LEDs having a peak wavelength between about 405 nm and about 485 nm. In some implementations the fourth LED string can have LEDs having a peak wavelength between about 485 nm and about 520 nm. The LEDs used in the first, second, third, and fourth LED strings may have full-width half-maximum wavelength ranges of between about 10 nm and about 30 nm. In some preferred implementations, the first, second, and third LED strings can include one or more LUXEON Z Color Line royal blue LEDs (product code LXZ1-PR01) of color bin codes 3, 4, 5, or 6 or one or more LUXEON Z Color Line blue LEDs (LXZ1-PB01) of color bin code 1 or 2 (Lumileds Holding B.V., Amsterdam, Netherlands). In some preferred implementations, the fourth LED string can have one or more LUXEON Z Color Line blue LEDs (LXZ1-PB01) of color bin code 5 or one or more LUXEON Z Color Line cyan LEDs (LXZ1-PE01) color bin code 1, 2, 6, 7, 8, or 9 (Lumileds Holding B.V., Amsterdam, Netherlands). The wavelength information for these color bins is provided in the table in
In implementations utilizing LEDs that emit substantially saturated light at wavelengths between about 360 nm and about 535 nm, the device 100 can include suitable recipient luminophoric mediums for each LED in order to produce light having color points within the suitable blue color ranges 301A-C, red color ranges 302A-C, yellow/green color ranges 303A-C, and cyan color ranges 304A-C described herein. The light emitted by each LED string, i.e., the light emitted from the LED(s) and associated recipient luminophoric medium together, can have a spectral power distribution (“SPD”) having spectral power with ratios of power across the visible wavelength spectrum from about 380 nm to about 780 nm. While not wishing to be bound by any particular theory, it is speculated that the use of such LEDs in combination with recipient luminophoric mediums to create unsaturated light within the suitable color ranges 301A-C, 302A-C, 303A-C, and 304A-C provides for improved color rendering performance for white light across a predetermined range of CCTs from a single device 100. Some suitable ranges for spectral power distribution ratios of the light emitted by the four LED strings (101A/101B/101C/101D) and recipient luminophoric mediums (102A/102B/102C/102D) together are shown in
Blends of luminescent materials can be used in luminophoric mediums (102A/102B/102C/102D) to create luminophoric mediums having the desired saturated color points when excited by their respective LED strings (101A/101B/101C/101D). Traditionally, any desired combined output light can be generated along a tie line between the LED string output light color point and the saturated color point of the associated recipient luminophoric medium by utilizing different ratios of total luminescent material to the encapsulant material in which it is incorporated. Increasing the amount of luminescent material in the optical path will shift the output light color point towards the saturated color point of the luminophoric medium. In some instances, the desired saturated color point of a recipient luminophoric medium can be achieved by blending two or more luminescent materials in a ratio. The appropriate ratios to achieve the desired saturated color point can be determined via methods known in the art. Generally speaking, any blend of luminescent materials can be treated as if it were a single luminescent material, thus the ratio of luminescent materials in the blend can be adjusted to continue to meet a target CIE value for LED strings having different peak emission wavelengths. Luminescent materials can be tuned for the desired excitation in response to the selected LEDs used in the LED strings (101A/101B/101C/101D), which may have different peak emission wavelengths within the range of from about 360 nm to about 535 nm. Suitable methods for tuning the excitation and emission of luminescent materials are known in the art and may include altering the concentrations of dopants within a phosphor, for example.
In some implementations of the present disclosure, luminophoric mediums can be provided with combinations of two types of luminescent materials. The first type of luminescent material emits light at a peak emission between about 515 nm and about 590 nm in response to the associated LED string emission. The second type of luminescent material emits at a peak emission between about 590 nm and about 700 nm in response to the associated LED string emission. In some instances, the luminophoric mediums disclosed herein can be formed from a combination of at least one luminescent material of the first and second types described in this paragraph. In implementations, the luminescent materials of the first type can emit light at a peak emission at about 515 nm, 525 nm, 530 nm, 535 nm, 540 nm, 545 nm, 550 nm, 555 nm, 560 nm, 565 nm, 570 nm, 575 nm, 580 nm, 585 nm, or 590 nm in response to the associated LED string emission. In preferred implementations, the luminescent materials of the first type can emit light at a peak emission between about 520 nm to about 555 nm. In implementations, the luminescent materials of the second type can emit light at a peak emission at about 590 nm, about 595 nm, 600 nm, 605 nm, 610 nm, 615 nm, 620 nm, 625 nm, 630 nm, 635 nm, 640 nm, 645 nm, 650 nm, 655 nm, 670 nm, 675 nm, 680 nm, 685 nm, 690 nm, 695 nm, or 670 nm in response to the associated LED string emission. In preferred implementations, the luminescent materials of the first type can emit light at a peak emission between about 600 nm to about 670 nm. Some exemplary luminescent materials of the first and second type are disclosed elsewhere herein and referred to as Compositions A-F.
In some implementations, the luminescent materials of the present disclosure may comprise one or more phosphors comprising one or more of the following materials: BaMg2Al16O27:Eu2+, BaMg2Al16O27:Eu2+,Mn2+, CaSiO3:Pb,Mn, CaWO4:Pb, MgWO4, Sr5Cl(PO4)3:Eu2+, Sr2P2O7:Sn2+, Sr6P5BO20:Eu, Ca5F(PO4)3:Sb, (Ba,Ti)2P2O7:Ti, Sr5F(PO4)3:Sb,Mn, (La,Ce,Tb)PO4:Ce,Tb, (Ca,Zn,Mg)3(PO4)2:Sn, (Sr,Mg)3(PO4)2:Sn, Y2O3:Eu3+, Mg4(F)GeO6:Mn, LaMgAl11O19:Ce, LaPO4:Ce, SrAl12O19:Ce, BaSi2O5:Pb, SrB4O7:Eu, Sr2MgSi2O7:Pb, Gd2O2S:Tb, Gd2O2S:Eu, Gd2O2S:Pr, Gd2O2S:Pr,Ce,F, Y2O2S:Tb, Y2O2S:Eu, Y2O2S:Pr, Zn(0.5)Cd(0.4)S:Ag, Zn(0.4)Cd(0.6)S:Ag, Y2SiO5:Ce, YAlO3:Ce, Y3(Al,Ga)5O12:Ce, CdS:In, ZnO:Ga, ZnO:Zn, (Zn,Cd)S:Cu,Al, ZnCdS:Ag,Cu, ZnS:Ag, ZnS:Cu, NaI:Tl, CsI:Tl, 6LiF/ZnS:Ag, 6LiF/ZnS:Cu,Al,Au, ZnS:Cu,Al, ZnS:Cu,Au,Al, CaAlSiN3:Eu, (Sr,Ca)AlSiN3:Eu, (Ba,Ca,Sr,Mg)2SiO4:Eu, Lu3Al5O12:Ce, Eu3+(Gd0.9Y0.1)3Al5O12:Bi3+,Tb3+, Y3Al5O12:Ce, (La,Y)3Si6N11:Ce, Ca2AlSi3O2N5:Ce3+, Ca2AlSi3O2N5:Eu2+, BaMgAl10O17:Eu, Sr5(PO4)3Cl: Eu, (Ba,Ca,Sr,Mg)2SiO4:Eu, Si6-zAlzN8-zOz:Eu (wherein 0<z≤4.2); M3Si6O12N2:Eu (wherein M=alkaline earth metal element), (Mg,Ca,Sr,Ba)Si2O2N2:Eu, Sr4Al14O25:Eu, (Ba,Sr,Ca)Al2O4:Eu, (Sr,Ba)Al2Si2O8:Eu, (Ba,Mg)2SiO4:Eu, (Ba,Sr,Ca)2(Mg, Zn)Si2O7:Eu, (Ba,Ca,Sr,Mg)9(Sc,Y,Lu,Gd)2(Si,Ge)6O24: Eu, Y2SiO5:CeTb, Sr2P2O7—Sr2B2O5:Eu, Sr2Si3O8—2SrCl2:Eu, Zn2SiO4:Mn, CeMgAl11O19:Tb, Y3Al5O12:Tb, Ca2Y8(SiO4)6O2:Tb, La3Ga5SiO14:Tb, (Sr,Ba,Ca)Ga2S4:Eu,Tb,Sm, Y3(Al,Ga)5O12:Ce, (Y,Ga,Tb,La,Sm,Pau)3(Al,Ga)5O12:Ce, Ca3Sc2Si3O12:Ce, Ca3(Sc,Mg,Na,Li)2Si3O12:Ce, CaSc2O4:Ce, Eu-activated β-Sialon, SrAl2O4:Eu, (La,Gd,Y)2O2S:Tb, CeLaPO4:Tb, ZnS:Cu,Al, ZnS:Cu,Au,Al, (Y,Ga,Lu,Sc,La)BO3:Ce,Tb, Na2Gd2B2O7:Ce,Tb, (Ba,Sr)2(Ca,Mg,Zn)B2O6:K,Ce,Tb, Ca8Mg (SiO4)4Cl2:Eu,Mn, (Sr,Ca,Ba)(Al,Ga,In)2S4:Eu, (Ca,Sr)8 (Mg,Zn)(SiO4)4Cl2:Eu,Mn, M3Si6O9N4:Eu, Sr5Al5Si21O2N35:Eu, Sr3Si13Al3N21O2:Eu, (Mg,Ca,Sr,Ba)2Si5N8:Eu, (La,Y)2O2S:Eu, (Y,La,Gd,Lu)2O2S:Eu, Y(V,P)O4:Eu, (Ba,Mg)2SiO4:Eu,Mn, (Ba,Sr, Ca,Mg)25iO4:Eu,Mn, LiW2O8:Eu, LiW2O8:Eu,Sm, Eu2W2O9, Eu2W2O9:Nb and Eu2W2O9:Sm, (Ca,Sr)S:Eu, YAlO3:Eu, Ca2Y8(SiO4)6O2:Eu, LiY9(SiO4)6O2:Eu, (Y,Gd)3Al5O12:Ce, (Tb,Gd)3Al5O12:Ce, (Mg,Ca, Sr,Ba)2Si5(N,O)8:Eu, (Mg,Ca,Sr,Ba)Si(N,O)2:Eu, (Mg,Ca, Sr,Ba)AlSi(N,O)3:Eu, (Sr,Ca,Ba,Mg)10(PO4)6Cl2:Eu, Mn, Eu,Ba3MgSi2O8:Eu,Mn, (Ba,Sr,Ca,Mg)3(Zn,Mg)Si2O8:Eu,Mn, (k-x)MgO.xAF2.GeO2:yMn4+(wherein k=2.8 to 5, x=0.1 to 0.7, y=0.005 to 0.015, A=Ca, Sr, Ba, Zn or a mixture thereof), Eu-activated α-Sialon, (Gd,Y,Lu,La)2O3:Eu, Bi, (Gd,Y,Lu,La)2O2S:Eu,Bi, (Gd,Y, Lu,La)VO4:Eu,Bi, SrY2S4:Eu,Ce, CaLa2S4:Ce,Eu, (Ba,Sr,Ca)MgP2O7:Eu, Mn, (Sr,Ca,Ba,Mg,Zn)2P2O7:Eu,Mn, (Y,Lu)2WO6:Eu,Ma, (Ba,Sr,Ca)xSiyNz:Eu,Ce (wherein x, y and z are integers equal to or greater than 1),(Ca,Sr,Ba,Mg)10(PO4)6(F,Cl,Br,OH):Eu,Mn, ((Y,Lu,Gd,Tb)1-x-yScxCey)2(Ca,Mg)(Mg,Zn)2+rSiz-qGeqO12+δ, SrAlSi4N7, Sr2Al2Si9O2N14:Eu, M1aM2bM3cOd (wherein M1=activator element including at least Ce, M2=bivalent metal element, M3=trivalent metal element, 0.0001≤a≤0.2, 0.8≤b≤1.2, 1.6≤c≤2.4 and 3.2≤d≤4.8), A2+xMyMnzFn (wherein A=Na and/or K; M=Si and Al, and −1≤x≤1, 0.9≤y+z≤0.001≤z≤0.4 and 5≤n≤7), KSF/KSNAF, or (La1-x-y, Eux, Lny)2O2S (wherein 0.02≤x≤0.50 and 0≤y≤0.50, Ln=Y3+, Gd3+, Lu3+, Sc3+, Sm3+or Er3+). In some preferred implementations, the luminescent materials may comprise phosphors comprising one or more of the following materials: CaAlSiN3:Eu, (Sr,Ca)AlSiN3:Eu, BaMgAl10O17:Eu, (Ba,Ca,Sr,Mg)2SiO4:Eu, β-SiAlON, Lu3Al5O12:Ce, Eu3+(Cd0.9Y0.1)3Al5O12:Bi3+,Tb3+, Y3Al5O12:Ce, La3Si6N11:Ce, (La,Y)3Si6N11:Ce, Ca2AlSi3O2N5:Ce3+, Ca2AlSi3O2N5:Ce3+,Eu2+, Ca2AlSi3O2N5:Eu2+, BaMgAl10O17:Eu2+, Sr4.5Eu0.5(PO4)3Cl, or M1aM2bM3cOd (wherein M1=activator element comprising Ce, M2=bivalent metal element, M3=trivalent metal element, 0.0001≤a≤0.2, 0.8≤b≤1.2, 1.6≤c≤2.4 and 3.2≤d≤4.8). In further preferred implementations, the luminescent materials may comprise phosphors comprising one or more of the following materials: CaAlSiN3:Eu, BaMgAl10O17:Eu, Lu3Al5O12:Ce, or Y3Al5O12:Ce.
Luminescent materials can include an inorganic or organic phosphor; silicate-based phosphors; aluminate-based phosphors; aluminate-silicate phosphors; nitride phosphors; sulfate phosphor; oxy-nitrides and oxy-sulfate phosphors; or garnet materials. The phosphor materials are not limited to any specific examples and can include any phosphor material known in the art with the desired emission spectra in response to the selected excitation light source, i.e. the associated LED or LEDs that produce light that impacts the recipient luminophoric medium. The d50 (average diameter) value of the particle size of the phosphor luminescent materials can be between about 1 μm and about 50 μm, preferably between about 10 μm and about 20 μm, and more preferably between about 13.5 μm and about 18 μm. Quantum dots are also known in the art. The color of light produced is from the quantum confinement effect associated with the nano-crystal structure of the quantum dots. The energy level of each quantum dot relates directly to the size of the quantum dot. Suitable semiconductor materials for quantum dots are known in the art and may include materials formed from elements from groups II-V, II-VI, or IV-VI in particles having core, core/shell, or core/shells structures and with or without surface-modifying ligands.
Tables 1 and 2 shows aspects of some exemplary luminescent compositions and properties, referred to as Compositions “A”-“F”.
Blends of Compositions A-F can be used in luminophoric mediums (102A/102B/102C/102D) to create luminophoric mediums having the desired saturated color points when excited by their respective LED strings (101A/101B/101C/101D). In some implementations, one or more blends of one or more of Compositions A-F can be used to produce luminophoric mediums (102A/102B/102C/102D). In some preferred implementations, one or more of Compositions A, B, and D and one or more of Compositions C, E, and F can be combined to produce luminophoric mediums (102A/102B/102C/102D). In some preferred implementations, the encapsulant for luminophoric mediums (102A/102B/102C/102D) comprises a matrix material having density of about 1.1 mg/mm3 and refractive index of about 1.545. Other matrix materials having refractive indices of between about 1.4 and about 1.6 can also be used in some implementations. In some implementations, Composition A can have a refractive index of about 1.82 and a particle size from about 18 micrometers to about 40 micrometers. In some implementations, Composition B can have a refractive index of about 1.84 and a particle size from about 13 micrometers to about 30 micrometers. In some implementations, Composition C can have a refractive index of about 1.8 and a particle size from about 10 micrometers to about 15 micrometers. In some implementations, Composition D can have a refractive index of about 1.8 and a particle size from about 10 micrometers to about 15 micrometers. Suitable phosphor materials for Compositions A, B, C, and D are commercially available from phosphor manufacturers such as Mitsubishi Chemical Holdings Corporation (Tokyo, Japan), Intematix Corporation (Fremont, Calif.), EMD Performance Materials of Merck KGaA (Darmstadt, Germany), and PhosphorTech Corporation (Kennesaw, Ga.).
In some implementations, Composition A can be selected from the “BG-801” product series sold by Mitsubishi Chemical Corporation. The BG-801 series is provided as cerium doped lutetium aluminum garnet (Lu3Al5O12). For some implementations, other phosphor materials are also suitable and can have peak emission wavelengths of between about 530 nm and about 560 nm, FWHM of between about 90 nm and about 110 nm, and particle sizes (d50) of between about 10 μm and about 50 μm.
In some implementations, Composition B can be selected from the “BY-102” or “BY-202” product series sold by Mitsubishi Chemical Corporation. The BY-102 series is provided as cerium doped yttrium aluminum garnet (Y3Al5O12). The BY-202 series is provided as (La,Y)3Si6N11:Ce. For some implementations, other phosphor materials are also suitable and can have peak emission wavelengths of between about 545 nm and about 560 nm, FWHM of between about 90 nm and about 115 nm, and particle sizes (d50) of between about 10 μm and about 50 μm.
In some implementations, Composition C can be selected from the “BR-101”, “BR-102”, or “BR-103” product series sold by Mitsubishi Chemical Corporation. The BR-101 series is provided as europium doped calcium aluminum silica nitride (CaAlSiN3). The BR-102 series is provided as europium doped strontium substituted calcium aluminum silica nitride (Sr,Ca)AlSiN3. The BR-103 series is provided as europium doped strontium substituted calcium aluminum silica nitride (Sr,Ca)AlSiN3. For some implementations, other phosphor materials are also suitable and can have peak emission wavelengths of between about 610 nm and about 650 nm, FWHM of between about 80 nm and about 105 nm, and particle sizes (d50) of between about 5 μm and about 50 μm.
In some implementations, Composition D can be selected from the “VG-401” product series sold by Mitsubishi Chemical Corporation. The VG-401 series is provided as GBAM: BaMgAl10O17:Eu. For some implementations, other phosphor materials are also suitable and can have peak emission wavelengths of between about 510 nm and about 540 nm, FWHM of between about 45 nm and about 75 nm, and particle sizes (d50) of between about 5μm and about 50 μm.
Devices having four LED strings with particular color points were simulated. For each device, four LED strings and recipient luminophoric mediums with particular emissions were selected, and spectral power distributions for the resulting four channels (blue, red, yellow/green, and cyan) were calculated.
The calculations were performed with Scilab (Scilab Enterprises, Versailles, France), LightTools (Synopsis, Inc., Mountain View, Calif.), and custom software created using Python (Python Software Foundation, Beaverton, Oreg.). Each LED string was simulated with an LED emission spectrum and excitation and emission spectra of luminophoric medium(s). For luminophoric mediums comprising phosphors, the simulations also included the absorption spectrum and particle size of phosphor particles. The LED strings generating combined emissions within blue, red and yellow/green color regions were prepared using spectra of a LUXEON Z Color Line royal blue LED (product code LXZ1-PR01) of color bin codes 3, 4, 5, or 6 or a LUXEON Z Color Line blue LED (LXZ1-PB01) of color bin code 1 or 2 (Lumileds Holding B.V., Amsterdam, Netherlands). The LED strings generating combined emissions with color points within the cyan regions were prepared using spectra of a LUXEON Z Color Line blue LED (LXZ1-PB01) of color bin code 5 or LUXEON Z Color Line cyan LED (LXZ1-PE01) color bin code 1, 8, or 9 (Lumileds Holding B.V., Amsterdam, Netherlands). Similar LEDs from other manufacturers such as OSRAM GmbH and Cree, Inc. could also be used.
The luminophoric mediums used in the following examples were calculated as combinations of one or more of Compositions A, B, and D and one or more of Compositions C, E, and F as described more fully elsewhere herein. Those of skill in the art appreciate that various combinations of LEDs and luminophoric blends can be combined to generate combined emissions with desired color points on the 1931 CIE chromaticity diagram and the desired spectral power distributions.
A semiconductor light emitting device was simulated having four LED strings. A first LED string is driven by a blue LED having peak emission wavelength of approximately 450 nm to approximately 455 nm, utilizes a recipient luminophoric medium, and generates a combined emission of a blue color point with a 1931 CIE chromaticity diagram color point of (0.2625, 0.1763). A second LED string is driven by a blue LED having peak emission wavelength of approximately 450 nm to approximately 455 nm, utilizes a recipient luminophoric medium, and generates a combined emission of a red color point with a 1931 CIE chromaticity diagram color point of (0.5842, 0.3112). A third LED string is driven by a blue LED having peak emission wavelength of approximately 450 nm to approximately 455 nm, utilizes a recipient luminophoric medium, and generates a combined emission of a yellow/green color point with a 1931 CIE chromaticity diagram color point of (0.4482, 0.5258). A fourth LED string is driven by a cyan LED having a peak emission wavelength of approximately 505 nm, utilizes a recipient luminophoric medium, and generates a combined emission of a cyan color point with a 1931 CIE chromaticity diagram color point of (0.3258, 0.5407). Table 3 below shows the spectral power distributions for the blue, red, yellow-green, and cyan color points generated by the device of this Example, with spectral power shown within wavelength ranges in nanometers from 380 nm to 780 nm, with an arbitrary reference wavelength range selected for each color range and normalized to a value of 100.0:
Tables 4 and 5 show exemplary luminophoric mediums suitable for the recipient luminophoric mediums for the blue, red, yellow/green, and cyan channels of this Example, using the Compositions A-F from Implementation 1 or Implementation 2 as described in Tables 1 and 2 above.
A semiconductor light emitting device was simulated having four LED strings. A first LED string is driven by a blue LED having peak emission wavelength of approximately 450 nm to approximately 455 nm, utilizes a recipient luminophoric medium, and generates a combined emission of a blue color point with a 1931 CIE chromaticity diagram color point of (0.2625, 0.1763). A second LED string is driven by a blue LED having peak emission wavelength of approximately 450 nm to approximately 455 nm, utilizes a recipient luminophoric medium, and generates a combined emission of a red color point with a 1931 CIE chromaticity diagram color point of (0.5842, 0.3112). A third LED string is driven by a blue LED having peak emission wavelength of approximately 450 nm to approximately 455 nm, utilizes a recipient luminophoric medium, and generates a combined emission of a yellow/green color point with a 1931 CIE chromaticity diagram color point of (0.5108, 0.4708). A fourth LED string is driven by a cyan LED having a peak emission wavelength of approximately 505 nm, utilizes a recipient luminophoric medium, and generates a combined emission of a cyan color point with a 1931 CIE chromaticity diagram color point of (0.3258, 0.5407). Table 6 below shows the spectral power distributions for the blue, red, yellow-green, and cyan color points generated by the device of this Example, with spectral power shown within wavelength ranges in nanometers from 380 nm to 780 nm, with an arbitrary reference wavelength range selected for each color range and normalized to a value of 100.0:
Tables 7 and 8 show exemplary luminophoric mediums suitable for the recipient luminophoric mediums for the blue, red, yellow/green, and cyan channels of this Example, using the Compositions A-F from Implementation 1 or Implementation 2 as described in Tables 1 and 2 above.
A semiconductor light emitting device was simulated having four LED strings. A first LED string is driven by a blue LED having peak emission wavelength of approximately 450 nm to approximately 455 nm, utilizes a recipient luminophoric medium, and generates a combined emission of a blue color point with a 1931 CIE chromaticity diagram color point of (0.2219, 0.1755). A second LED string is driven by a blue LED having peak emission wavelength of approximately 450 nm to approximately 455 nm, utilizes a recipient luminophoric medium, and generates a combined emission of a red color point with a 1931 CIE chromaticity diagram color point of (0.5702, 0.3869). A third LED string is driven by a blue LED having peak emission wavelength of approximately 450 nm to approximately 455 nm, utilizes a recipient luminophoric medium, and generates a combined emission of a yellow/green color point with a 1931 CIE chromaticity diagram color point of (0.3722, 0.4232). A fourth LED string is driven by a cyan LED having a peak emission wavelength of approximately 505 nm, utilizes a recipient luminophoric medium, and generates a combined emission of a cyan color point with a 1931 CIE chromaticity diagram color point of (0.3704, 0.5083). Table 9 below shows the spectral power distributions for the blue, red, yellow-green, and cyan color points generated by the device of this Example, with spectral power shown within wavelength ranges in nanometers from 380 nm to 780 nm, with an arbitrary reference wavelength range selected for each color range and normalized to a value of 100.0:
Tables 10 and 11 show exemplary luminophoric mediums suitable for the recipient luminophoric mediums for the blue, red, yellow/green, and cyan channels of this Example, using the Compositions A-F from Implementation 1 or Implementation 2 as described in Tables 1 and 2 above.
A semiconductor light emitting device was simulated having four LED strings. A first LED string is driven by a blue LED having peak emission wavelength of approximately 450 nm to approximately 455 nm, utilizes a recipient luminophoric medium, and generates a combined emission of a blue color point with a 1931 CIE chromaticity diagram color point of (0.2387, 0.1692). A second LED string is driven by a blue LED having peak emission wavelength of approximately 450 nm to approximately 455 nm, utilizes a recipient luminophoric medium, and generates a combined emission of a red color point with a 1931 CIE chromaticity diagram color point of (0.5563, 0.3072). A third LED string is driven by a blue LED having peak emission wavelength of approximately 450 nm to approximately 455 nm, utilizes a recipient luminophoric medium, and generates a combined emission of a yellow/green color point with a 1931 CIE chromaticity diagram color point of (0.4494, 0.5161). A fourth LED string is driven by a cyan LED having a peak emission wavelength of approximately 505 nm, utilizes a recipient luminophoric medium, and generates a combined emission of a cyan color point with a 1931 CIE chromaticity diagram color point of (0.3548, 0.5484). Table 12 below shows the spectral power distributions for the blue, red, yellow-green, and cyan color points generated by the device of this Example, with spectral power shown within wavelength ranges in nanometers from 380 nm to 780 nm, with an arbitrary reference wavelength range selected for each color range and normalized to a value of 100.0:
Tables 13 and 14 show exemplary luminophoric mediums suitable for the recipient luminophoric mediums for the blue, red, yellow/green, and cyan channels of this Example, using the Compositions A-F from Implementation 1 or Implementation 2 as described in Tables 1 and 2 above.
A semiconductor light emitting device was simulated having four LED strings. A first LED string is driven by a blue LED having peak emission wavelength of approximately 450 nm to approximately 455 nm, utilizes a recipient luminophoric medium, and generates a combined emission of a blue color point with a 1931 CIE chromaticity diagram color point of (0.2524, 0.223). A second LED string is driven by a blue LED having peak emission wavelength of approximately 450 nm to approximately 455 nm, utilizes a recipient luminophoric medium, and generates a combined emission of a red color point with a 1931 CIE chromaticity diagram color point of (0.5941, 0.3215). A third LED string is driven by a blue LED having peak emission wavelength of approximately 450 nm to approximately 455 nm, utilizes a recipient luminophoric medium, and generates a combined emission of a yellow/green color point with a 1931 CIE chromaticity diagram color point of (0.4338, 0.5195). A fourth LED string is driven by a cyan LED having a peak emission wavelength of approximately 505 nm, utilizes a recipient luminophoric medium, and generates a combined emission of a cyan color point with a 1931 CIE chromaticity diagram color point of (0.3361, 0.5257). Table 15 below shows the spectral power distributions for the blue, red, yellow-green, and cyan color points generated by the device of this Example, with spectral power shown within wavelength ranges in nanometers from 380 nm to 780 nm, with an arbitrary reference wavelength range selected for each color range and normalized to a value of 100.0:
Tables 16 and 17 show exemplary luminophoric mediums suitable for the recipient luminophoric mediums for the blue, red, yellow/green, and cyan channels of this Example, using the Compositions A-F from Implementation 1 or Implementation 2 as described in Tables 1 and 2 above.
Those of ordinary skill in the art will appreciate that a variety of materials can be used in the manufacturing of the components in the devices and systems disclosed herein. Any suitable structure and/or material can be used for the various features described herein, and a skilled artisan will be able to select an appropriate structures and materials based on various considerations, including the intended use of the systems disclosed herein, the intended arena within which they will be used, and the equipment and/or accessories with which they are intended to be used, among other considerations. Conventional polymeric, metal-polymer composites, ceramics, and metal materials are suitable for use in the various components. Materials hereinafter discovered and/or developed that are determined to be suitable for use in the features and elements described herein would also be considered acceptable.
When ranges are used herein for physical properties, such as molecular weight, or chemical properties, such as chemical formulae, all combinations, and subcombinations of ranges for specific exemplar therein are intended to be included.
The disclosures of each patent, patent application, and publication cited or described in this document are hereby incorporated herein by reference, in its entirety.
Those of ordinary skill in the art will appreciate that numerous changes and modifications can be made to the exemplars of the disclosure and that such changes and modifications can be made without departing from the spirit of the disclosure. It is, therefore, intended that the appended claims cover all such equivalent variations as fall within the true spirit and scope of the disclosure.
This patent application is a continuation of U.S. patent application Ser. No. 15/176,083 filed Jun. 7, 2016 and issued as U.S. Pat. No. 9,719,660 on Aug. 1, 2017, which is a continuation of International Patent Application No.: PCT/US2016/015318 filed Jan. 28, 2016, the disclosures of which are incorporated by reference in their entirety.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16673891 | Nov 2019 | US |
| Child | 17000882 | US | |
| Parent | 15665269 | Jul 2017 | US |
| Child | 16673891 | US | |
| Parent | 15176083 | Jun 2016 | US |
| Child | 15665269 | US | |
| Parent | PCT/US2016/015318 | Jan 2016 | US |
| Child | 15176083 | US |