Patent Grant
8580082
This is a U.S. national phase of PCT Application No. PCT/IB2009/006777, filed Sep. 8, 2009, which claims priority to European Application No. 08015881.9, filed Sep. 9, 2008.
The present invention relates to mixtures of two distinct porous, stable aggregates and rather coarse PCCs (precipitated) calcium carbonate pigments with a coarser, third component, which may be a pigment or a filler such as natural calcium (ground) carbonate or (most preferably) a PCC (precipitated calcium carbonate), or optionally but far less preferred talc, kaolin, titanium oxide TiO2, clays and other pigments or charges used in the paper industry and generally known to the skilled man. Depending on the granulometry of the two PCCs the third, coarser component, may be omitted.
There is a definite need, in the paper-making industry, for a pigment composition comprising namely calcium carbonate(s), in specific combination, and possibly in combination with other pigments or fillers, in order to improve intricate, or finely tuned and delicate technical properties of the final paper sheet, such as “print show through” or “print strike through” in paper applications like Newsprint, light weight fine papers or wood free light papers, supercalendered magazines and so on.
Those properties are well known to the skilled man, and details will be found in attached ANNEX A in the domain of Newsprint.
In particular, it would be highly interesting to provide to the industry such a formulation which would improve those properties and if possible at a lower cost.
In a first embodiment, the invention consists of a composition comprising a blend or mix of one of the two porous, stable aggregates and rather coarse (2-10 μm) PCCs called Grade B or Grade C PCC, in combination with a second, specific S-PCC (S-PCC=scalenohedral type PCC) pigment as described here-below.
It might also be possible to use R- or A-PCC as well as third component.
According to the invention, the said ratio can be appropriately selected between 90/10 and 10/90 parts per hundred (percent) by dry weight, namely 80/20 and 20/80.
Best representative examples are, as exemplified here-below:
In the present application and claims, “comprising” means, except otherwise stated, that the composition, formulation, mixture or blend may contain usual additives having no noticeable effect on the function of the essential component used in the present invention.
Each inventive formulation may comprise the usual additives known and used in this paper-making industry, without noticeably affecting the results.
The list of such routine additives is well known to the skilled man.
In the most preferred mode, the invention consists of a composition comprising either a PCC Grade A or a PCC Grade B, in combination with the second pigment S-PCC, as mentioned above, in a ratio 90/10 to 10/90 by dry weight, and in combination with a third, coarser, specific pigment.
The percentage by dry weight of the total of the inventive blends of pigments is preferably chosen between 0.3 to 5%, most preferably between 0.5% to 3% by dry weight of the final paper product, and still more preferably between 1.0% to 2.0%. In the laboratory testings, the percentages have been selected at 2 and respectively 4% for practical reasons.
As to the proportion of the coarser pigment vs. the total of the three PCC Grade B or Grade C+S-PCC+coarser pigment, it must remain below 10 w % (w %=% by weight), and preferred ranges are from 0.1 to 10 w %, preferably from 0.5 to 7-10 w %, and most preferably between 2 to 7 w %.
The skilled man will be able to adapt those examples to other formulations.
In the following, and in particular in the Tables, the two or three components blend according to the invention will be named as “primary” since the examples have been performed with recycled paper based newsprint furnish and that they are the fresh used fillers.
The rest of the pigments, such as calcium carbonate of any kind, clay etc. . . . resulting from the recycled paper based newsprint furnish, will be named “secondary”.
The invention will be better understood in the following non-limiting examples, which are summarized in the accompanying Tables.
FIG 2: Figure showing optical density for “print strike through.” Results obtained with the formulations in the described paper-making test.
As will be explained here-below, the main criteria for selecting the said “coarser” pigment is that it should feature a granulometry which does not affect noticeably, when in admixture with the blend PCC Grade B (or PCC Grade C) with S-PCC (all being exemplified below and in the Table 1), the finest part of the granulometry data of the blend, and in particular that it should not contribute anything significant to the amount of particles <0.2 μm, preferably nothing <0.3 μm, more preferably nothing <0.5 μm and most preferably nothing <1 μm.
Any filler or pigment matching the above criteria are acceptable and can be routinely tested by the skilled man among those used in the paper industry or a similar industry, such as PCC, GCC (ground calcium carbonate, natural), clays, kaolin, dolomite, Titanium oxyde (TiO2) etc. . . .
Table 1 Shows the “Pigment Data” which are Referred to in the Experiments:
In the left-hand column, all the measures and properties are standard ones, well known to the skilled man, such as BET specific surface area measured according to the ISO standard 9277 or particle size distribution established in a Sedigraph™ 5100 equipment manufactured by Micromeritics™.
Viscosity B means Brookfield Viscosity, measured with a Brookfield viscometer at 25° C. and the appropriate spindle and speed.
The surface charge is measured according to a known method and is not particularly useful for the understanding of the present invention. However, the skilled man will appreciate that it could be very useful when considering water-based inks involving charged dyes, unless you do not wish to implicate water-based inkjet by default, though flexography (frequently used for newsprint today, can also apply such inks.
Brightness R-457 is known to the skilled man as well, and the said Brightness R-457 is measured according to the DIN standard 53140 using an equipment DATACOLOR ELREPHO™ 3300.
The dispersing agent is selected among the usual agents known and used in this paper-making industry, such as a polycarboxylate and so on. It is not particularly useful for the understanding of the present invention. However, if the polymer provides a certain surface charge that promotes adsorption of certain ink dyes, then it could be highly relevant for the understanding: again, the comments above apply.
Oil-absorption is measured according to a known method and is not particularly useful for the understanding of the present invention.
HYDREX™ P is a commercial product which is a Na silicate and which represents a well-known standard. When analysing the Tables, and namely Table 1, “Pigment Data”, it is surprising to notice that the inventive compositions feature a far lower BET value than the HYDREX P, with better or similar properties as can be seen in the Tables.
Experiments (Exp) 1 and 2 are experiments conducted according to this invention:
The conditions of the laboratory paper production tests are summarized in Table 2. DIP means de-inked pulp, as is known.
The retention aid(s) can be different from the used Polymin™ and can non-limitatively be either mono-component or so-called “dual” systems, such as inter alia acrylic (co)polymers (acrylamides) and a secondary retention aid like bentonite, or starches or starch derivatives, etc. . . . as is well known to the skilled man.
The secondary (that is, classical) pigment/filler blend is a mixture of 3.5% CaCO3 and of 7.5% of clay, by weight, forming an S-level of 11% regarded as the minimum acceptable.
In comparison, in addition to this 11 w % of classical fillers has been added 2 w % of the total blend (left-hand column) or respectively 4 w % (right-hand column) of the filler(s) indicated at the bottom of the Table, corresponding to the tests and experiments of Table 1.
The percentage in
As to the process for introducing the fillers into the fibre pulp or stock, the order of addition is not crucial; it is however preferred to introduce the inventive “primary” blend of two or three pigments in a pulp that already contains at least the minimum S-level of 11% or more. To be noted for completeness, impact of the primary filler is not related to the amount of secondary filler, it works also with 100% fresh pulp not carrying secondary pigment.
It is possible to add the inventive blend of pigments in one operation or injection, or in several injections at different points of the line. It is also possible to prepare premixes of the various fillers, including premixes of a part of the classical (“secondary”) fillers with a part or the total amount of the inventive (“primary”) fillers. Several such premixes may be introduced at different points along the line. Premixing the primary filler with secondary filler in the DIP is not really practical as the secondary pigment is within the DIP fiber furnish, but can be used.
It is well known in this industry that the skilled man can adapt those injection point(s) namely in view of the existing equipment, the desired degree of shear, contact time etc. . . .
This table shows the results obtained with the above formulations, in the described paper-making test.
“Print Strike Through” is a property whose measurement is detailed in ANNEX A and in EP 1 712 597.
This table shows the results obtained with the above formulations, in the described paper-making test.
“Print Show Through” is a known property whose measurement is made according to the method of ANNEX A.
The present invention also encompasses the fibres-containing pulps or stock for the fabrication of a sheet of paper, namely in a paper-making plant, characterized in that it contains an effective amount of the compositions of pigment blends of the invention, as described above, in an effective amount, namely that also described above.
The invention also encompasses the paper product produced from the above pulp or stock. as mentioned it works also with 100% mechanical fiber, blends of mech. fiber and DIP/DIP, most likely also with 100% fresh chemical pulp.
The cause of print through in newsprint is linked to opacity, porosity, ash content, roughness and surface weight of the paper.
Since newspaper printing inks dry through an entirely physical process, and not through oxidation as with curved offset printing, or evaporation of volatile substances as with roll offset/heat offset printing, migration of mobile substances such as mineral and plant oils into the paper occurs, and these are absorbed by the paper fibres and fillers. If the proportion of migrating oils becomes too great (too high a proportion of printing ink content), and the inner surface layer of the paper too thin, then a part of the oils will reach the other side of the paper and cause an increase in transparency.(1)
With this test method, production control of paper manufacture can be carried out. It is possible to obtain a good indication of variations in production, since the amount of ink and print pressure are so high, that a clear print through of the print must become visible, and thus weak or strong print through is also recognisable.
This method can not be used as a standard test in our test laboratory, because we are not looking to control production quality, but to compare various surface weight papers from different manufacturers with each other in the most objective way possible. In addition, we have to work with the most commonly practised ink amounts and printing pressures.(2)
Since we are looking to obtain an indication that is truest to common practice for the various newspapers, this method sets the amount of ink, in conformity with common practice printing pressure, to the required optical density.
In this way, any print through is a result of the paper used, and not of the amount of ink.
If too high a ink amount and too high a printing pressure are used, lower surface weight papers are automatically put at a disadvantage.
Sampling: after determining the individual weights of each sample paper (especially the laboratory sheets), this test only used those papers that came nearest to each other in surface weight. This was applicable for the whole range of papers to be tested.
If too high an ink amount and too high a printing pressure are used, lower surface weight papers are automatically put at a disadvantage.
Notes:
| Number | Date | Country | Kind |
|---|---|---|---|
| 08015881 | Sep 2008 | EP | regional |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/IB2009/006777 | 9/8/2009 | WO | 00 | 3/1/2011 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2010/029403 | 3/18/2010 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 6887351 | Lunden et al. | May 2005 | B1 |
| 20040108081 | Hughes | Jun 2004 | A1 |
| 20070202279 | Schultz et al. | Aug 2007 | A1 |
| 20070218222 | Campbell et al. | Sep 2007 | A1 |
| Number | Date | Country |
|---|---|---|
| WO 9961703 | Dec 1999 | WO |
| WO 03050355 | Jun 2003 | WO |
| WO 03054300 | Jul 2003 | WO |
| Entry |
|---|
| The International Search Report dated May 11, 2009 for PCT Application No. PCT/IB2009/006777. |
| The Written Opinion of the International Searching Authority for PCT Application No. PCT/IB2009/006777. |
| Number | Date | Country | |
|---|---|---|---|
| 20110146931 A1 | Jun 2011 | US |