Patent Application
20150360962
Not applicable.
Not applicable.
Recent developments in the biofuel industry have related to the use of genetically enhanced microorganisms to make products such as ethanol, typically in dilute solutions with water. Various efforts and different approaches have been undertaken to efficiently separate ethanol from water and enrich the ethanol product.
U.S. Pat. No. 8,163,066 to Eisenberger concerns selectively moving a vertically oriented carbon dioxide capture structure supporting an amine sorbent into and out of a regeneration enclosure in order to remove carbon dioxide from ambient air.
U.S. Pat. No. 8,491,705 to Choi et al. concerns capture of carbon dioxide from ambient air using solid amine adsorbents tethered to a silica, metal oxide or polymer resin substrate through covalent bonding.
Zhang et al., “Adsorption of Water and Ethanol in MFI-Type Zeolites”, Langmuir 2012, 28, 8664-8673 concerns water and ethanol vapor adsorption on MFI-type zeolites and discloses the preparation of silicalite-1(F″) in a fluoride-mediated route by hydrothermal synthesis adapted from literature procedures.
Gualtieri et al., “Seeded growth of TPA-MFI films using the fluoride route”, Microporous and Mesoporous Materials 111 (2008) 604-611 concerns the preparation of TPA-MFI films on dense amorphous silica glass supports using the fluoride route in combination with surface seeding.
A need exists for an improved sorbent that provides decreased water uptake and enhanced selectivity of ethanol over water.
An object of the present invention is a silicalite MFI particle having a mean height or b-dimension of about 0.2 microns to about 10 microns, a mean aspect ratio of about 5 to about 14, pore volume of less than about 0.0025 cm3 per gram, water uptake of about 0.20 mmol per gram or less at an activity of 0.98 and 35° C., and selectivity for ethanol over water of about 190 at an ethanol mole fraction of about 0.2 in a vapor-phase ethanol/water mixture.
Another object of the present invention is a method for making silicalite MFI particles having a mean height or b-dimension of about 0.2 microns to about 10 microns, a mean aspect ratio of about 5 to about 14, pore volume of less than about 0.0025 cm3 per gram, water uptake of about 0.20 mmol per gram or less at an activity of 0.98 and 35° C., and selectivity for ethanol over water of about 190 at an ethanol mole fraction of about 0.2 in a vapor-phase ethanol/water mixture.
Another object of the present invention is a system for separating ethanol from water comprising silicalite MFI particles having a mean height or b-dimension of about 0.2 microns to about 10 microns, a mean aspect ratio of about 5 to about 14, pore volume of less than about 0.0025 cm3 per gram, water uptake of about 0.20 mmol per gram or less at an activity of 0.98 and 35° C., and selectivity for ethanol over water of about 190 at an ethanol mole fraction of about 0.2 in a vapor-phase ethanol/water mixture.
Another object of the present invention is a method for separating ethanol from water using silicalite MFI particles having a mean height or b-dimension of about 0.2 microns to about 10 microns, a mean aspect ratio of about 5 to about 14, pore volume of less than about 0.0025 cm3 per gram, water uptake of about 0.20 mmol per gram or less at an activity of 0.98 and 35° C., and selectivity for ethanol over water of about 190 at an ethanol mole fraction of about 0.2 in a vapor-phase ethanol/water mixture.
The foregoing and other features and advantages of the invention will become further apparent from the following detailed description of the presently preferred embodiments, read in conjunction with the accompanying drawings. The detailed description and drawings are merely illustrative of the invention, rather than limiting the scope of the invention being defined by the appended claims and equivalents thereof.
Embodiments of the invention will be described below with reference to the following figures.
As used herein, the term “silicalite” means a polymorph of silica having a zeolite structure, but with no aluminum content detectable by energy-dispersive X-ray spectroscopy conducted using, for example, Oxford Instruments EDS analysis or similar suitable instrument.
As used herein, the term “silica” means silicon dioxide, a chemical compound that is an oxide of silicon with the chemical formula SiO2.
As used herein, the term “zeolite” means a microporous, aluminosilicate mineral commonly used as a commercial adsorbent.
As used herein, the term “microporous” means a material containing pores with diameters less than 0.002 microns, such as zeolites and metal-organic frameworks.
As used herein, the term “mesoporous” means a material containing pores with diameters between 0.002 and 0.050 microns.
As used herein, the term “aluminosilicate mineral” means a mineral composed of aluminium, silicon, and oxygen, plus countercations.
As used herein, the term “silicate” means a compound containing an anionic silicon compound.
As used herein, the term “mineral” means a naturally occurring substance that is solid and stable at room temperature, representable by a chemical formula, usually abiogenic, and has an ordered atomic structure.
As used herein, the term “abiogenic” means lacking carbon and hydrogen atoms.
As used herein, the term “sorbent” means a material used to absorb or adsorb liquids or gases.
As used herein, the term “adsorbent” means a material on which atoms, ions or molecules of a gas, liquid or dissolved solid can adhere.
As used herein, the term “MFI” means mordenite framework inverted.
As used herein, the term “mordenite” means a zeolite mineral with the chemical formula, (Ca, Na2, K2)Al2Si10O24.7H2O.
As used herein, the term “framework inverted” means a topology that is defined by the negative space, interstitial space or pore space, of another zeolite topology.
As used herein, the term “particle” means a solid material whose constituent atoms, molecules, or ions are arranged in an ordered pattern extending in the a, b and c spatial dimensions, as illustrated in
As used herein, the term “F-MFI” means MFI crystalline zeolites formed from fluoride-containing silicate gels.
As used herein, the term “defect-free” means amorphous defects less than about 0.1% as measured by X-ray diffraction conducted using, for example, a PANalytical X'Pert PRO Materials Research Diffractometer or similar suitable instrument; metal center defects less than about 0.001% as measured by energy-dispersive X-ray spectroscopy conducted using, for example, Oxford Instruments EDS analysis or similar suitable instrument; and silanol defects measured by water loading at unit activity of less than about 0.98 for a material with pore volume greater than about 0.15 cubic centimeters per gram, the measure of which is equivalent to less than about 0.1 silanol defects per unit cell of a MFI particle.
As used herein, the term “fiber” means a slender, elongated, threadlike object or structure.
As used herein, the term “monolith sorbent reactor” means inorganic rods or cylinders having surfaces coated with a sorbent, or alternatively honey-comb inorganic structures having inner surfaces coated with a sorbent.
As used herein, the term “interstice” means an empty space or gap between spaces full of structure or matter.
As used herein, the term “selectivity” means the ability of a sorbent to discriminate between an isolate in a mixture and the other components of the mixture and to retain the isolate exclusive of the other mixture components. Selectivity is a function of the chemical structure of the isolate, the properties of the sorbent, and the composition of the mixture, with maximum selectivity achieved when a sorbent is chosen that interacts through isolate functional groups that are not common to other mixture components.
As used herein, the term “isolate” means a chemical species or product of interest that is separated by a sorbent from a mixture.
As used herein, the term “water uptake” means water sorbed within a microporous material under exposure to water at certain relative pressures and temperatures.
As used herein, the term “non-wetting” means, in reference to a porous material exposed to 100% relative humidity water vapor or liquid water at 1 bar, the absence of liquid water in the pores.
As used herein, the term “hydrophobic” means uptake by a microporous material of less than 0.5 mmol/g water at 100% relative humidity water and 35° C.
As used herein, the term “space velocity” means the quotient of the entering volumetric flow rate of reactants divided by the reactor or catalyst bed volume, which indicates the number of reactor volumes of feed that can be treated in a unit time.
As used herein, the term “gel” means a substantially dilute cross-linked system present as a solid, jelly-like material that exhibits no flow when in steady-state.
As used herein, the term “homogeneous” means substances and mixtures that are in a single phase.
As used herein, the term “amorphous” means lacking the order characteristic of a crystal or micro-crystalline substance.
As used herein, the term “colloid” means a substance microscopically dispersed throughout another substance.
As used herein, the term “vacuum filtration” means a technique for separating a solid product from a solvent or liquid reaction mixture in which the mixture of solid and liquid is poured through a filter in, most commonly, a funnel.
As used herein, the term “sonication” means applying sound energy to agitate particles in a sample in order to initiate crystallization processes, control polymorphic crystallizations, and/or intervene in anti-solvent precipitations (crystallization) to aid mixing and isolate small crystals.
As used herein, the term “centrifugation” means the use of centrifugal force for the sedimentation of mixtures with a centrifuge.
As used herein, the term “decantation” means a process for the separation of mixtures, by removing a top layer of liquid from which a precipitate has settled.
As used herein, the term “drying” means a mass transfer process consisting of the removal of water or another solvent by evaporation from a solid, semi-solid or liquid.
As used herein, the term “calcination” means a thermal treatment process in presence of air applied to ores and other solid materials to bring about a thermal decomposition, phase transition, or removal of a volatile fraction.
As used herein, the term “ball-milling” means grinding materials into powder.
As used herein, the term “monoclinic” means a crystal described by three vectors of unequal length forming a rectangular prism with a parallelogram as its base, such that two pairs of vectors are perpendicular, while the third pair makes an angle other than 90°.
As used herein, the term “orthorhombic” means a crystal described by three vectors that remain mutually orthogonal to form a rectangular prism with a rectangular base and height, such that the length, width and height are distinct.
As used herein, the term “unit cell” means the space enclosed by the points of a lattice defining a crystal structure and is the simplest repeating unit that defines the crystal structure. The unit cell is specified by three vectors, a, b and c that form the edges of a parallelepiped. The lengths of a, b and c are called the unit cell dimensions, and their directions define the major crystallographic axes.
As used herein, the term “b-dimension” is illustrated in
As used herein, the term “pore volume” means a measure of void spaces in a porous material. Pore volume of materials such as silicalite and zeolites is commonly measured on the basis of nitrogen absorption capacity of the material at low temperature and high pressure. More specifically, pore volume can be determined using nitrogen as a probe gas at 77 K via, for example, a Micrometrics ASAP 2020 adsorption porosimeter or similar suitable instrument equipped with analysis functions for estimating BET pore volumes by the Horvath-Kawazoe method.
As used herein, the term “about” means approximately, in the region of, roughly, or around. When the term “about” is used in conjunction with a numerical value or range, it modifies that value or range by extending the boundaries above and below the numerical value(s) set forth. In general, the term “about” is used herein to modify a numerical value(s) above and below the stated value(s) within a confidence interval of 90% or 95%.
The present invention relates to improved silicalite particles having decreased water uptake, methods for making the improved silicalite particles, systems for separating ethanol from water comprising the improved silicalite particles and methods for separating ethanol from water using the improved silicalite particles. These and other aspects of the present invention significantly reduce energy consumption, and operating costs related thereto, vis-a-vis current ethanol/water separation processes.
Silicalite particles of the present invention are made from a mixture of tetrapropylammonium bromide and ammonium fluoride dissolved in water, to which amorphous, colloidal silicon dioxide is added, resulting in the formation of a homogeneous gel. The homogeneous gel is heated to produce the silicalite particles.
According to the present invention, the size and morphology of the silicalite particles can be altered by, in various embodiments, dispersing silicalite seeds in the mixture of tetrapropylammonium bromide and ammonium fluoride in order to impose structure on the formation of the homogenous gel, aging the homogenous gel before heating, and/or varying the duration of heating of the homogenous gel.
In some embodiments, silicalite particles of the present invention have a mean height, b, of about 0.2 microns to about 40 microns. In some embodiments, silicalite particles of the present invention have a mean height, b, of about 0.2 microns to about 10 microns. In some embodiments, silicalite particles of the present invention have a mean aspect ratio of about 5 to about 20. In some embodiments, silicalite particles of the present invention have a mean aspect ratio of about 5 to about 14.
According to the present invention, silicalite particles of the present invention are distinguishable from sorbents known in the art using, in some embodiments, X-ray diffraction, energy dispersive X-ray spectroscopy and 29Si MAS NMR to show the absence of amorphous defects, metal center defects and silanol defects, respectively, in silicalite particles of the present invention and the presence of such defects in sorbents known in the art. Silicalite particles of the present invention are also distinguishable from sorbents known in the art by their lack of defect-related water absorption and their unexpectedly large ethanol/water selectivities.
Silicalite particles of the present invention provide decreased water uptake and increased selectivity for ethanol over water, and corresponding improved energy efficiency of separation processes utilizing sorbents comprising silicalite particles of the present invention, in comparison with silicalite particles known in the art. As shown in
In some embodiments, as shown in
Low water uptake and high ethanol/water selectivity provided by silicalite particles of the present invention advantageously increase the efficiency and concomitantly reduce the energy requirements of separating ethanol from water. An adsorption process using silicalite particles of the present invention reduces the energy consumed in the process of separating ethanol from water by shifting the thermal energy requirement driving the separation from the heat of vaporization of water, which has a value known the art of about 2,260 kJ/kg, to the heat of sorption of ethanol, which has a value known the art of about 845 kJ/kg. Shifting the thermal energy requirement to ethanol, which is dilute at concentrations of about 1 wgt % or less in aqueous liquid or vapor streams of interest in the present invention, reduces energy requirements relative to traditional distillation techniques, since such techniques are directed to vaporization of water from a stream that contains primarily water. An approach utilizing silicalite particles of the present invention therefore is directed to a component of an aqueous stream that has a lower heat of vaporization and is present in smaller amounts in the dilute stream, thereby deleveraging the energy requirements for separating the components.
A gas delivery system can advantageously be paired with a system that uses silicalite particles of the present invention to recover ethanol from a dilute stream. In some embodiments, after the silicalite particles are washed with a mixture of ethanol and water in liquid or vapor form and the silicalite particles adsorb ethanol from the mixture, the silicalite particles subsequently are washed with carbon dioxide as a sweep gas and heated to a preselected temperature in a desorption step, during which ethanol desorbs from the silicalite particles into the carbon dioxide. The desorbed ethanol can then, for example, be condensed to a liquid product, optionally after passing through an ethanol dehydration membrane. Excess carbon dioxide from the gas delivery system can be sent to a photobioreactor containing an algae culture that requires carbon as a feedstock.
After desorption, the silicalite particles are washed with water, and carbon dioxide partitions into the water as dissolved carbon. The carbon dioxide-enriched aqueous stream can be sent to the photobioreactor for consumption by the algae culture as a carbon feedstock.
Silicalite particles of the present invention can be bound into a sorbent having a hollow fiber form using a hydrophobic, polymer binder in a spinning process and incorporated in a monolith sorbent reactor that is used in the ethanol/water processes described herein. One of ordinary skill in the art will appreciate that using the sorbent in this form will help reduce pressure losses as liquid and vapor streams are pumped through the fiber bed, which will reduce costs associated with pumping the streams.
A fiber sorbent bed of the present invention can be used to treat either liquid or vapor streams leaving a photobioreactor, or, for example, leaving a scrubber or other process operations used to capture ethanol product from the photobioreactor.
Silicalite particles identified as Samples I-V were synthesized by fluoride-mediated reaction routes with varying reaction conditions to achieve varying particle dimensions. Reagent quantities and other parameters for Samples I-V are specified in Table 1.
Reaction Routes:
1. For Sample I, disperse silica seed particles in deionized water in a polytetrafluoroethylene container using a sonication horn operated for three bursts of 30 seconds per burst.
2. For Samples I-V, dissolve tetrapropylammonium bromide (“TPABr”; 99% Sigma Aldrich) and ammonium fluoride (“NH4F”; >99.99% Sigma Aldrich) in the deionized water in the polytetrafluoroethylene container, covered and stirred for 10 minutes at room temperature.
3. For Samples I-V, add Cab-O-Sil® M-5 (untreated fumed silica; Cabot Corporation) to the mixture, stirring manually for 10 minutes to form a homogeneous gel.
4. For Sample III, age the gel covered with Parafilm® using an automated impeller.
5. For Samples I-V, seal the gel in a polytetrafluoroethylene sleeve in a stainless steel Parr reactor and react the gel in an oven preheated to 180° C.
6. For Samples I-V, cool the resulting solids for about 8 hours.
7. For Samples I-V, vacuum filter the resulting solids and wash with at least 200 mL of deionized water.
8. For Samples I-V, add 30 mL of deionized water to the solids and sonicate for 90 seconds to remove any un-reacted silica.
9. For Samples I-V, centrifuge the slurry and decant off the water.
10. For Samples I-V, repeat steps 8 and 9 at least twice.
11. For Samples I-V, dry the solids at 110° C. under vacuum.
12. For Samples I-V, calcine the solids according to the following profile: increase 5° C./min from 25° C. to 120° C., hold 120° C. for 2 hrs, ramp 5° C./min to 550° C., hold 550° C. for 12 hrs.
Silicalite seed particles used in step 1 above for Sample I were made according to the reaction route for Sample IV and were ball milled in about 1 mL of deionized water for 5 min in a Spex 8000M Mixer/Mill® using a hardened steel grinding vial with two 0.5 inch steel balls.
Scanning electron microscopy (SEM) was used to evaluate the particle size and morphology of Samples I-V. The samples were sputter-coated with a 10-20 nm thick gold coating (Model P-S1; ISI, Mountain View, Calif.), and transferred to a high-resolution field emission scanning electron microscope (Leo 1530, Leo Electron Microscopy, Cambridge, UK).
As shown in
Measurements of a, b and c dimensions in Table 2 are averages.
X-ray diffraction was conducted on the silicalite particles of Samples I-V to identify MFI topology and to investigate the particles' lattice systems. Powder x-ray diffraction was performed at room temperature on an X'Pert Pro PAnalytical X-ray Diffractometer using Cu—Kα radiation. Measurements were carried out from 5-400 2θ, using an X'celerator detector with low-background sample holders.
X-ray diffraction patterns shown in
29Si MAS NMR measurements of Samples I, II, IV and V were performed on a BSX300 spectrometer operating at 59.64 MHz with a spinning rate of 5 kHz. Spectra were acquired using a 7 mm probe with ZrO2 rotors and a 10-second recycle delay. Chemical shifts were referenced using 3-(trimethylsilyl)-1 propanesulfonic acid sodium salt.
The 29Si NMR spectra shown in
Nitrogen adsorption and desorption isotherms at 77K, Brunauer-Emmett-Teller (BET) surface areas and pore volumes (t-plot method) were calculated for Samples I-V from N2 physisorption measurements performed on an ASAP 2020 (Micrometrics). Samples I-V were degassed at 200° C. for 18 h within the N2 physisorption apparatus prior to taking measurements.
KBr pellets were prepared using equal amounts of Samples I-IV and analyzed using a Bruker Vertex 80v FT-IR with wavenumbers from 400 to 4000 cm−1. FT-IR spectra of Samples I-IV are shown in
Pore size distribution of Samples I, II, IV and V was determined using a simplified Broekoff-de Boer (BdB) pore size analysis method and the Frenkel-Halsey-Hill (FHH) theory for determining the statistical thickness of an adsorbed gas layer. As shown in
Pure vapor adsorption equilibrium experiments were performed on a VTI-SA vapor sorption analyzer from TA Instruments (New Castle, Del., United States) at 35° C. The vapor activity was controlled automatically by mixing a saturated vapor feed (using N2 as the carrier gas) with a dry N2 stream. The sample “dry mass” was measured under N2 and was at equilibrium before introduction of the vapor to the sample chamber.
According to
At the end of the adsorption step (Step II), the monolith sorbent reactor is then washed with 1-2 reactor volumes of product ethanol (Step III) to remove the interstitial ethanol/water solution.
After the product wash step (Step III), the monolith sorbent reactor is heated (Step IV), preferably to 70-110° C., in the presence of a gas such as carbon dioxide. A non-polar gas such as carbon dioxide, nitrogen, argon or helium can be selected for use in this step based on its high partition coefficient with an aqueous solution.
The adsorbed mixture of ethanol and water will desorb from the monolith sorbent reactor into the gas phase. The gas phase comprising ethanol can be transferred from the monolith sorbent reactor to a condensing unit in order to condense, capture and further treat the ethanol vapor as a liquid phase product, as shown in
Alternatively, the gas phase comprising ethanol can be further refined to remove water impurities using a high temperature ethanol dehydration membrane, for example, as shown in
The monolith sorbent reactor can then be refilled with an aqueous wash (Step I) in order to “pre-wet” the monolith sorbent reactor in preparation for the next sorption cycle and prevent bypass of the ethanol/water solution in Step II. During this step, gas that was sorbed by the monolith sorbent reactor during the heating step will partition into the aqueous wash. A non-polar gas selected for use in the heating step will have a high partition coefficient with the aqueous wash. Carbon dioxide that is used in the heating step and subsequently partitions into the aqueous wash can be recycled to the photobioreactor for consumption by cyanobacteria or other microorganisms contained in the photobioreactor.
Although the present disclosure has been described in considerable detail with reference to certain embodiments thereof, other embodiments are possible. Therefore, the spirit and scope of the appended claims should not be limited to the description of the embodiments contained herein, and all changes that come within the meaning and range of equivalents are intended to be embraced therein.
This application is a divisional of U.S. patent application Ser. No. 14/145,897, filed Dec. 31, 2013, the contents of which are incorporated herein by reference.