Patent Application
20220183957
The present invention relates to the general technical field of substances and compounds used in the field of formulation of cosmetic and/or dermatological compositions, in particular of the kind of compounds including a functional agent, for example of the pigment type.
More particularly, the present invention concerns a compound comprising at least 50 weight % of a functional agent.
The present invention also concerns a method for producing such a compound. Finally, the present invention concerns a method for producing a cosmetic and/or dermatological composition.
The production of cosmetic and/or dermatological compositions usually require combining some substances and compounds to be mixed into a homogeneous material, that is to say which has a regular distribution of the different compounds and substances, and which is stable, namely in particular without separation of the phases over time, for example by sedimentation or creaming, or another undesirable phenomenon such as coalescence or flocculation.
To this end, it is known to resort to solid pigments which are ground into fine particles by grinding units, before being integrated into a cosmetic composition to color or enhance its matt or shiny appearance. Although it they are generally satisfactory in their final use, the implementation of these ground pigments still has some drawbacks.
One major drawback of the use of these ground pigments in making of a cosmetic composition lies in the pulverulent nature of these, which makes storage, transport and handling of these ground pigments complex, expensive, dirty, and even polluting, while featuring a non-negligible risk regarding the safety of living beings and installations, as well as major difficulties with regards to cleaning and/or elimination of these ground pigments. In general, the finer the grinding of the pigments and therefore the smaller the pigment particles, the more complex the management will be. Moreover, the powdery state of these pigments confers a large specific surface (actual surface/low mass) thereon resulting, in turn, in a considerable reactivity, and therefore in particular in an increased risk of degradation over time, and even a risk of accident, such as an explosion in particular.
In addition, grinding units are quite often specialized and very expensive, whereas the grinding process itself could turn out to be particularly long and complex depending on the nature and desired size of the ground pigment particles, which could vary for example according to aesthetics, organoleptic and/or qualitative requirements. In most cases, because of their cost and their complexity, these grinding units are not specifically dedicated to the specific grinding of a pigment, and therefore require settings to grind a pigment according to other specifications, such as a different grain-size, or to grind other types of pigments. Thus, these grinding units process different «batches» or sets of several types and sizes of ground pigments that shall be stored, transported and used afterwards at different cosmetic compositions production units.
This results, on the one hand, in a multiplication of batches of pulverulent pigments that are difficult to deal with (storage, transport, handling in particular during mixing with other substances to make the formulation of a cosmetic composition, avoiding mixing of different pigments), and, on the other hand, in the fact that the cosmetic compositions production units are almost always distinct and remote from the grinding units, which complicates even more the management (in particular the transport) of the ground pigments.
Ultimately, the integration of the ground pigments into the cosmetic compositions, as currently practiced, is insufficient in terms of ease of implementation, storage, transport, safety, and costs.
Consequently, the invention proposes overcoming the different drawbacks set out hereinbefore by providing a new compound which not only turns out to be capable of being easily integrated into a cosmetic and/or dermatological composition, but further has a great ease of implementation with regards to management thereof and in particular transport, storage and handling thereof.
Another object of the invention aims at providing a new compound with an extremely simple and cheap design. Another object of the invention aims at providing a new compound that is particularly easy to handle.
Another object of the invention aims at providing a new compound that is particularly easy to transport and to store.
Another object of the invention aims at providing a new compound that is easy to effectively integrate to cosmetic and/or dermatological compositions.
Another object of the invention aims at providing a new compound whose deign enables it to obtain a good repeatability as a component for the formulation of cosmetic and/or dermatological compositions.
Another object of the invention aims at providing a new compound whose design enables it to be used in a wide range of applications, in particular for a very wide variety of cosmetic and/or dermatological compositions.
Another object of the invention aims at providing a new compound having a minimal risk with regards to safety of living beings and which does not degrade the installations.
Another object of the invention aims at providing a new compound whose manufacture can be easily industrialized, implementing a minimum number of different substances.
Another object of the invention aims at providing a new compound that degrades only very little, or not at all, over time.
Another object of the invention aims at providing a method for producing a compound whose implementation is simple, easy and cost-effective, and has a good repeatability and a good safety for the user.
Another object of the invention aims at providing a method for producing a cosmetic and/or dermatological compound whose implementation is rapid, easy to monitor and easy, while guaranteeing optimum safety conditions.
The objects assigned to the invention are achieved by means of a compound comprising at least 50 weight % of a functional agent, characterized in that it also comprises a waxy matrix, comprising at least one organosilicon material, said organosilicon material forming most, preferably all, of the weight of said waxy matrix, within which said functional agent, formed by solid particles, is dispersed, said compound being solid at room temperature and intended to be dispersed by fluidification and/or solubilization within a cosmetic and/or dermatological composition to integrate said functional agent therein.
The objects assigned to the invention are also achieved by means of a method for producing a compound comprising at least 50 weight % of a functional agent, characterized in that it comprises at least:
said compound being solid at room temperature and intended to be dispersed by fluidification and/or solubilization within a cosmetic and/or dermatological composition to integrate said functional agent therein.
The objects assigned to the invention are further achieved by means of a method for producing a cosmetic and/or dermatological composition comprising a redispersion step during which a compound as mentioned hereinbefore is added and then mixed with one or several cosmetically and/or dermatologically acceptable component(s).
Other particularities and advantages of the invention will appear and come out in more detail upon reading the description made hereinafter, with reference to the appended drawings, provided as merely illustrative and non-limiting examples, wherein:
As illustrated in the figures, the invention concerns a compound 1. Hence, said compound 1 is preferably formed by several different elements, more specifically by a relatively homogeneous and stable mixture of several different substances, materials, matters together, advantageously all cosmetically and/or dermatologically acceptable, that is to say suited to be integrated within a cosmetic and/or dermatological composition. Hence, the compound 1 advantageously has a very low, and possibly zero, toxicity level with regards to the use of a cosmetic and/or dermatological composition.
According to the invention, the compound 1 comprises at least 50 weight % of a functional agent. According to a preferred embodiment, the compound 1 comprises (strictly) more than 50 weight %, preferably (strictly) more than 60 weight %, more preferably at least 70 weight %, still more preferably at least 80 weight %, even more preferably at least 85 weight %, still more preferably at least 90 weight %, of said functional agent. Advantageously, said functional agent is selected appropriately, so as to form an element suited to be integrated within a cosmetic and/or dermatological composition. Thus, a high proportion of the functional agent within the compound 1 is particularly advantageous when the latter constitutes an intermediate (or possibly almost finite) product intended to be redispersed with other compounds to form a finite cosmetic and/or dermatological product. Indeed, said compound 1 advantageously serves as an intermediate «support» or «vehicle» for the functional agent, and it is therefore preferable that the proportion of the functional agent within the compound 1 is as high as possible on the one hand for the final formulation (that is to say the finite cosmetic and/or dermatological product) not to depend or depend very little on the nature of the substances other than said functional agent within said compound 1, and on the other hand for obvious reasons relating to costs, storage and transport, an intermediate compound having a low content of the functional agent which, by definition, has to be used in a larger amount and therefore occupying a larger volume for a generally greater weight for a given amount of the functional agent, whereas the substances other than said functional agent within said compound 1, being in greater proportions, represent a high cost that what is more is not valued in the final formulation (and possibly «parasitize» said final, or finite cosmetic and/or dermatological, formulation). Preferably, said functional agent is intended to fill one or several very specific function(s) within a cosmetic and/or dermatological composition. For example, said functional agent is intended to form a physical sunscreen, in particular within a sun cream type cosmetic and/or dermatological composition, that is to say it is intended to form a physical, preferably opaque, barrier between the Sun's ultraviolet rays and the skin of a user of said cosmetic and/or dermatological composition.
According to the invention, said functional agent is formed by solid particles 2, that is to say which are preferably solid at least at room temperature, and even solid at higher temperatures, such as for example between 30 and 90° C. Preferably, said solid particles are insoluble in water. Preferably, said solid particles have an average size comprised between 10 nm and 500 μm, preferably between 100 nm and 100 μm. Hence, said average size preferably refers to the average grain-size of said particles 2, and in particular their average diameter or an average maximum dimension of said particles, which could be measured in particular using only one sample of said particles.
For example, said solid particles 2 comprise at least organic and/or mineral (that is to say inorganic) pigments, organic and/or mineral charges, composite and/or biocomposite materials, or a mixture of these. According to a particular embodiment, said solid particles 2 are primarily, or totally, formed by mineral pigments, which could be constituted for example by titanium dioxide, iron oxide(s), chromium oxide(s), ultramarine pigment(s) (for example ultramarine blue or violet), tin oxide(s) and/or zinc oxide. For example, said organic pigments are constituted by carbon black and/or organic lacquers. For example, said mineral charges are constituted by talc, mica, sericite, kaolin, silica, hydroxyapatite, barium sulfate, perlite, calcium carbonate, and/or borosilicates. For example, said organic charges are constitutes by starch, cellulose, natural or synthetic polymers, and/or silicone polymers and resins. For example, said composites and/or biocomposites include one or several mother-of-pearl(s). In the case where said solid particles consist of pigments, the functional agent is for example intended to color a cosmetic and/or dermatological formulation, or to protect the skin from the Sun (case of the aforementioned sun cream, the solid particles 2 forming in particular a sunscreen). In the case where said solid particles 2 consist of charges, the functional agent may for example be intended to modify the organoleptic properties of a cosmetic and/or dermatological formulation.
Still according to the invention, the compound 1 also comprises a waxy matrix 3 within which said functional agent is dispersed. In other words, said functional agent, and more specifically said solid particles 2, is/are advantageously mixed with said waxy matrix 3 and scattered within the latter, preferably homogeneously, that is to say according to a regular volumetric distribution. Advantageously, within the compound 1, the waxy matrix 3 and said solid particles 2 form, from a macroscopic perspective, one single phase, and it is impossible to differentiate the waxy matrix 3 from said solid particles 2 with the naked eye.
According to the invention, said waxy matrix 3 comprises at least one organosilicon (or organosilicic) material. It may also possibly comprise a plurality of different organosilicon materials.
According to the invention, said organosilicon material forms most, preferably all, of the weight of said waxy matrix 3. In other words, the organosilicon material forms at least 50 weight %, advantageously at least 75 weight %, preferably at least 90 weight %, even more preferably substantially 100 weight % of said waxy matrix 3. Alternatively, or complementarily with the configuration disclosed hereinbefore, said waxy matrix 3 is primarily, preferably totally, formed, in weight, by a plurality of different organosilicon materials, that is to say said organosilicon material is in this case formed by a plurality of different organosilicon compounds.
Besides said organosilicon material, said waxy matrix 3 may possibly comprise at least another waxy material such as a natural, mineral and/or synthetic, wax, a fatty body solid at room temperature derived from fractioning of one or several natural and/or synthetic oil(s), a natural and/or synthetic resin, a silicone or silicone polymer wax, an organosilicon (or organosilicic) material or a mixture of these.
Advantageously, said organosilicon material (or a plurality of different organosilicon materials) belongs to the family of silsesquioxanes, which have the general formula (RSiO3/2)n, R representing a carbonated group in particular of the alkane, alkene, aryl or arylene type, whereas as usual Si represents a silicon atom, and 0 represents an oxygen atom, n representing an integer generally greater than 1, for example comprised between 3 and 20, such as equal to 8. Even more advantageously, said organosilicon material is a silsesquioxane polymer. Preferably, said organosilicon material is an organosilicone material.
Thus, according to a particular embodiment of the invention, said organosilicon material consists of polymethylsilsesquioxane. In other words, in this embodiment, said waxy matrix 3 comprises polymethylsilsesquioxane, and, preferably, is for example primarily formed by the latter, and possibly almost totally or totally formed by the latter. Thus, advantageously, the polymethylsilsesquioxane is a type of organosilicon materials particularly effective when it is used as a waxy matrix 3, alone or possibly mixed with another waxy material such as another organosilicon material or one of the previously-described waxy materials (natural wax, resin, etc.). For example, the waxy matrix 3 further comprises, primarily (in weight) or not, cyclopentasiloxane, at least one (C30 to C45) alkyl methicone and/or hydrogenated esters such as hydrogenated esters of plant oils, for example an olive oil hydrogenated ester with the INCI name «Hydrogenated olive oil stearyl esters». Of course, said waxy matrix 3 may possibly be formed by a mixture of several substances, in particular among those mentioned hereinbefore, the polymethylsilsesquioxane advantageously remaining predominant in weight. Preferably, said waxy matrix 3 is substantially solid at room temperature, and in particular below 30° C., preferably below 45° C., more preferably below 55° C., even more preferably below 65° C. Conversely, said waxy matrix 3 is advantageously substantially fluid at a temperature higher than room temperature, and for example a temperature equal to or higher than 30° C., preferably 45° C., more preferably 55° C., and even more preferably 65° C. Thus, advantageously, said waxy matrix 3 has a melting point and/or a softening point comprised between 30 and 150° C. included, more preferably between 45 and 130° C. included, even more preferably between 55 and 130° C. included. In some embodiments of the invention, said waxy matrix 3 has a melting point and/or a softening point comprised between 55 and 150° C. included, for example between 55 and 95° C. included, or between 95 and 150° C. included. For example, said waxy matrix 3 has a density comprised approximately between 0.80 and 1.5, preferably between 0.9 and 1.3, for example about 1.24 in the case where the waxy matrix 3 is primarily, or totally, formed by polymethylsilsesquioxane. For example, in particular when said waxy matrix 3 is primarily, or totally, formed by polymethylsilsesquioxane, its softening point is advantageously comprised between 55 and 150° C., or between 75 and 90° C. Preferably, said waxy matrix 3 is formed by a material having general physical characteristics similar or equivalent to those of waxes, and in particular a material that significantly fluidize above a given temperature, that is to say a material that loses its solidity or switches from a very high viscosity to a much lower viscosity when it is heated up to a given temperature, or above. For example, said waxy matrix 3 is formed by a substantially heat-meltable and/or thermoplastic material, and significantly softens and/or melts when it is heated up or above a given temperature, for example 65° C. Hence, said waxy matrix 3 is preferably solid at room temperature and preferably becomes substantially fluid when it is brought to a given temperature above the room temperature, in particular above its melting and/or softening point. Advantageously, the waxy matrix 3 may be formed, at room temperature, by solids granulates distinct from each other, that is to say difficult to compact or non-compactable by mechanical pressure.
According to the invention, said compound 1 is solid at room temperature and intended to be dispersed by fluidification and/or solubilization within a cosmetic and/or dermatological composition to integrate said functional agent therein. Advantageously, the compound 1 has, at room temperature or below 30° C. or below 45° C. for example, a relatively firm, non-flabby, consistence, that is to say a minimum mechanical strength, substantially differentiating it from a fluid and in particular from a liquid. For example, said compound 1 is in the form of granulates, for examples pellets or sticks 4, obtained by extrusion, as illustrated in
Advantageously, said waxy matrix 3 is designed so as to be able to be solubilized at room temperature, that is to say advantageously at a temperature lower than 30° C., more advantageously lower than 25° C. (and optionally higher than 15° C.), for example about 20° C. (+/−2° C.), in a fatty phase (that is to say an oil phase) of said cosmetic and/or dermatological composition. Thus, said organosilicon material is advantageously easy to solubilize at room temperature within a fatty phase of a cosmetic and/or dermatological composition. Advantageously, said compound 1 (therefore integrating said waxy matrix 3) could be solubilized at room temperature, that is to say preferably at a temperature lower than 30° C., more advantageously lower than 25° C. (and optionally higher than 15° C.), for example approximately 20° C. (+/−2° C.), in a fatty phase (that is to say an oil phase) of said cosmetic and/or dermatological composition. Such a configuration allows solubilizing «at low temperature», that is to say at room temperature (in practice generally comprised between 18 and 25° C. approximately), the compound 1 in different oil types that could be integrated into a cosmetic and/or dermatological composition. Advantageously, this allows avoiding the need for heating the compound 1 and/or the fatty phase (oil) of the cosmetic and/or dermatological composition in order to disperse the compound 1 within a cosmetic and/or dermatological composition to integrate said functional agent therein, such a heating being not only energy-intensive (and therefore involving an additional cost), but also potentially a source of degradation of one or several component(s) of the oil phase of the cosmetic and/or dermatological composition.
Said cosmetic and/or dermatological composition may be intended directly to one user, or form an intermediate product which, in turn, is intended to integrate a cosmetic and/or dermatological product which, in turn, is a final one, intended to a user, or an intermediate one.
Said compound 1, advantageously resulting from mixing of the functional agent, that is to say the particles 2, and of the organosilicon waxy matrix 3 (such as polymethylsilsesquioxane in particular), is not preferably pulverulent, but cohesive and easy to «redisperse» within a cosmetic and/or dermatological composition during formulation in the fluid form. Hence, at low temperature, that is to say at room temperature, the compound 1 advantageously constitutes a solid dispersion, in the same manner as a set of solid particles 2 dispersed within the waxy matrix 3 which is also solid at low temperature. Preferably, such a configuration allows in particular getting rid of the constraints related to the nature, often naturally pulverulent, of said solid particles 2 alone. Thus, preferably, the compound 1 is substantially easier to manage, that is to say to store, transport and handle, than said particles 2 alone, in particular because the compound 1 is, for example, at room temperature, in the form of small solids (for example pellet or stick 4 type granulates), coherent, relatively inert, and easy to handle, whereas, on the contrary, said particles 2, when they are alone, often have an extremely fractioned, powdery nature, with a high reactivity and highly dispersible in air. Advantageously, the compound 1 is formed, at room temperature, by solids distinct from each other, preferably with a reduced size such as granulates, for example sticks, pellets 4, said distinct solids being preferably difficult to compact or non-compactible by mechanical pressure. Thus, said compound 1 is easy to store and easy to transport, in the form of said (small) distinct solids stockpiled in containers, for example bags, of several kilograms or several tens of kilograms (at least), without said distinct solids being detached from each other, for example by agglomeration, by coalescence, by squeezing, or by sedimentation. In other words, said compound 1 is preferably easy to store and transport in the form of said distinct solids, which remain distinct from each other during transport and/or storage, even when this/these is/are performed using containers such as bags each weighting, with their content (formed by said distinct solids, several kilograms or several tens of kilograms. Preferably, the distinct solids, formed by the compound 1 remain easy to handle even after having been stored and/or transported within said containers, and that being so thanks to the absence of attachment of said distinct solids even when they are stockpiled, said distinct solids preserving their respective unit nature despite stockpiling. Of course, the above-described transport is preferably carried out at room temperature or at a temperature slightly hotter than room temperature, but which advantageously remains below the melting and/or softening point of said waxy matrix 3. Thus, the compound 1 is practical not only to transport and store, but also to quantify when it should be dispersed within a cosmetic and/or dermatological composition, said distinct solids, and in particular the granulates (for example pellets or sticks 4). In particular, this allows quantifying easily the amount of functional agent to be obtained in the final cosmetic and/or dermatological composition, which implies an excellent repeatability when formulating the latter thanks to the compound 1.
Advantageously, said solid particles 2 have undergone a surface treatment causing a reduction of the capacity of absorption of the waxy matrix 3 by said treated solid particles 2, in comparison with non-treated solid particles of the same kind. In other words, said solid particles 2, which form the functional agent of the compound 1, have advantageously undergone a surface treatment allowing « saturating» them more rapidly with the waxy matrix 3, that is to say using a smaller amount of the waxy matrix 3 in comparison with a considered amount of solid particles 2. For example, the absorption limit (or « saturation») of the waxy matrix 3 with an amount of solid particles 2 (whether treated or not) is tested as follows: an amount (more than necessary) of the waxy matrix 2 (preferably formed by an organosilicon material and in particular polymethylsilsesquioxane) is heated up so as to fluidize, for example heated up to 65°, and its added drop-by-drop to a considered amount of solid particles 2 (whether treated or not), which hare preferably subjected at the same time to a mixing or trituration action; the mixed or triturated solid particles 2/drops of waxy matrix 3 mixture will firstly form an extremely viscous, and even solid or almost solid, paste, in the same manner as for example a plasticine, and then, upon the addition of an additional drop of waxy matrix 3, will have its viscosity drop significantly and/or switch from a solid or almost solid state into a fluid or almost fluid state (liquid or softened in particular). Hence, said surface treatment advantageously allows reducing the amount of fluidized waxy matrix 3 to be added to a considered amount of solid particles 2 for their mixture to loss its consistency, that is to say switches from a very viscous, solid or almost solid, state into a significantly less viscous, fluid or almost fluid, state. The surface treatments allowing causing a reduction of the capacity of absorption of the waxy matrix are known as such and vary according to multiple alternatives, the invention of course not being limited to a particular treatment. As a non-limiting example, the surface treatment of the solid particles 2 implemented in the context of the invention may be based on a treatment based on amino acids, for example N-acylamino acids such as the N-acyl-L-glutamic acid, and be advantageously in accordance with the teaching of the patent U.S. Pat. No. 4,606,914. For example, the surface treatment is based on a treatment based on amino acids in the form of metallic salts of N-acylamino acid, such as a salt made from sodium myristoyl glutamate and aluminum hydroxide. Of course, other surface treatments in accordance with the invention could be considered, and the surface treatment may for example be based on: a treatment implementing disodium myristoyl glutamate, advantageously as well as aluminum dimyristate and triethoxycaprylylsilane; a treatment implementing an alkoxysilane such as triethoxycaprylylsilane; a treatment in accordance with the teaching of the patent U.S. Pat. No. 6,482,441, a treatment implementing a fatty acid, a treatment implementing one or several phospholipid(s), a treatment implementing an olive oil hydrogenated ester, etc. For example, said solid particles 2 having undergone a surface treatment are formed by raw pigments (preferably more than 90 weight %), sodium myristoyl glutamate (preferably less than 10 weight %) and an aluminum hydroxide (preferably less than 10 weight %), according to a merely illustrative and non-limiting example. The surface treatment allowing causing a reduction of the capacity of absorption of the waxy matrix may further be formed by a combination of the different treatments listed hereinbefore. Advantageously, the surface treatments allowing causing a reduction of the capacity of absorption of the waxy matrix also allow increasing the hydrophobic nature of the treated solid particles 2, and/or improving their dispersability in an oil phase, in comparison with non-treated solid particles of the same kind. Advantageously, said functional agent forms (strictly) more than 50 weight %, preferably more than 60 weight %, more preferably at least 70 weight %, even more preferably at least 80 weight %, even more preferably at least 85 weight % or even at least 90 weight % of said compound 1. Thus, preferably, at least 70 weight %, preferably at least 80 weight %, or at least 85 weight % of said compound 1, is formed by said solid particles 2. Such a high weight proportion of the functional agent (and therefore of the particles) is advantageously made possible thanks to said surface treatment. In turn, said waxy matrix preferably forms between 5 and 25 weight %, preferably between 7 and 22 weight %, more preferably between 15 and 20 weight %, of the compound 1. To sum up, advantageously, thanks to the surface treatment, a relatively small amount of the waxy matrix 3 is sufficient to serve as a support to a relatively large amount of solid particles 2.
Preferably, when it is fluidized and/or solubilized, the compound 1, and by extension the functional agent contained thereby (and more specifically said solid particles 2), could be dispersed or mixed in a homogeneous and stable manner within a cosmetic and/or dermatological composition. To sum up, thanks to the general principle of the invention, and in particular to the surface treatment, it is advantageously possible not only to obtain a compound 1 that is easy to handle comprising a large amount of the functional agent (at least 50 weight % or at least 80 and even 85 weight %) and a small amount of the waxy matrix 3, but also to carry out, subsequently, an easy dispersion of the compound 1 within a cosmetic and/or dermatological composition during production to integrate said functional agent therein. Advantageously, the waxy matrix 3, and by extension the compound 1, serves as a support for the functional agent before redispersion thereof within a cosmetic and/or dermatological composition. Preferably, the redispersion of the compound 1 may be done by fluidification and therefore by heating of the compound 1 until making it fluid, to mix it more easily with cosmetically and/or dermatologically acceptable components which are themselves fluid, or by solubilization of the compound 1, preferably in the form of small solids (granulates in particles, for example pellets or sticks 4), possibly at low temperature (that is to say without heating), within cosmetically and/or dermatologically acceptable components which are fluid too.
In addition, the relatively small, or limited, amount of the waxy matrix 3 within said compound 1, as well as the nature of the organosilicon material (such as polymethylsilsesquioxane) of the latter, advantageously enables said compound 1 to be integrated to a wide range of cosmetic and/or dermatological compositions. In other words, the design of the compound 1 advantageously allows integrating said functional agent contained thereby within a cosmetic and/or dermatological composition, without, or almost without, any constraints with regards to the other compounds of the latter, that is to say without the need for modifying these other components forming said cosmetic and/or dermatological composition to adapt them to said compound 1. To sum up, the compound 1 of the invention could advantageously be integrated to a wide range of cosmetic and/or dermatological compositions. Advantageously, the waxy matrix 3, and in particular the organosilicon material that partially or totally forms it (preferably constituted by polymethylsilsesquioxane), has a significant filmogenic nature, which is particularly interesting in cosmetic and/or dermatological compositions intended to be used on the hair of a user. Thus, the compound 1 may be intended to be dispersed into a cosmetic and/or dermatological composition, not only to integrate the functional agent therein but also to integrate a nature inherent to the waxy matrix 3 thereon, for example the aforementioned filmogenic nature of the waxy matrix 3, in particular when the organosilicon material that partially or totally forms it is polymethylsilsesquioxane.
Preferably, said waxy matrix 3 is liposoluble and/or insoluble or almost insoluble in water. Thus, the waxy matrix 3, which advantageously has physical characteristics close or similar to those of natural or synthetic waxes (and in particular silicone waxes), preferably has a lipophilic, liposoluble and/or hydrophobic nature. In particular, the waxy matrix 3 is dissolved in oil phases commonly used in the production of cosmetic and/or dermatological compositions. Advantageously, because of its small relative amount within the compound 1, the waxy matrix 3 is intended to relatively easily integrate the cosmetic and/or dermatological composition in which the compound is, in turn, intended to be integrated, preferably without significantly modifying the physical and/or chemical properties of said composition, and that being even more easily when said composition has a fatty or oil (and/or lipophilic) phase possibly within a water-in-oil type, for example water-in-silicone type, or alternatively oil-in-water type, emulsion.
Said compound 1 may possibly be intended to be redispersed so as to be part of a cosmetic and/or dermatological composition comprising only but an anhydride phase, preferably of the fat/oil/silicone type, said composition being for example a balm, a lipstick, etc. Advantageously, said surface treatment also allows increasing the lipophilic and/or hydrophobic nature of the treated solid particles 2, in comparison with non-treated solid particles 2 of the same kind. Thus, the surface treatment confers on said solid particles 2 or reinforces in these a chemical affinity for fats and fatty matters and the same advantageously encompassing said waxy matrix 3. In particular, such a feature allows obtaining a better dispersion of the solid particles 2 within said waxy matrix 3 and/or a better dispersion of said compound 1 (and therefore of the solid particles 2 themselves) within a cosmetic and/or dermatological composition (in turn including in particular an oil phase or the same).
Preferably, said surface treatment involves grafting of molecules 5 to the respective surface of said particles 2, as illustrated in
Advantageously, said functional agent and said waxy matrix 3 form together at least 95 weight %, preferably at least 97 weight %, more preferably at least 99 weight %, even more preferably all, of said compound 1. Indeed, whether for making said compound 1 or for dispersing the latter within a cosmetic and/or dermatological composition, it is advantageously not necessary to integrate to the latter a component other than said waxy matrix 3 and said functional agent, although this still could be considered. Thus, preferably, the compound 1 does not comprise any surfactant, that is to say in particular it does not comprise any substance whose primary function is to lower the surface tension, or the compound 1 comprises such a substance but in a non-useful amount, negligible in weight with respect to the waxy matrix 3 and/or to the functional agent.
The invention also concerns, as such, according to a second aspect partially illustrated by an embodiment in
According to the invention, the production method comprises at least one step C of heating up a waxy matrix 3 comprising at least one organosilicon (or organosilicic) material in order to obtain a fluid matrix 3. Said organosilicon material forms most, preferably all, of the weight of said waxy matrix 3. In other words, the organosilicon material forms at least 50 weight %, advantageously at least 75 weight %, preferably at least 90 weight %, even more preferably substantially 100 weight % of said waxy matrix 3. Preferably, said waxy matrix 3 is that already mentioned hereinbefore, whereas said organosilicon material is also preferably as mentioned hereinbefore, and in particular consists of polymethylsilsesquioxane. In other words, during said heating step C, said waxy matrix 3 is heated up, for example using at least one resistance or by convection, until it is fluidized, that is to say molten or softened enough so as to no longer have the consistency of a solid, thereby forming a fluid waxy matrix 3. During said heating step, said waxy matrix 3 is advantageously heated up to a temperature equal to or higher than its melting and/or softening point. Thus, during the heating step, said waxy matrix 3 is heated for example up to a temperature comprised between 30 and 150° C. included, more preferably between 45 and 130° C. included, so as to be fluidized, or up to a temperature comprised between 55 and 95° C. included or between 55 and 150° C. included. Preferably, at low temperature, said waxy matrix 3 is thus substantially solid whereas at hot temperature, beyond a given temperature, it is substantially fluid. Preferably, the expression « fluid matrix» therefore refers to the waxy matrix 3 heated up until fluidification.
Still according to the invention, the method further comprises a step D of dispersing said functional agent, formed by solid particles 2, within said fluid matrix 3. Advantageously, said dispersion step D comprises at least one step M of mixing said treated particles 2 and of said waxy matrix 3, the latter could in particular be at low temperature, in a solid form, or at hot temperature, in a fluidized form. Preferably, said solid particles 2 are as mentioned hereinbefore.
Preferably, the method also comprises a step T (not illustrated) of treating said solid particles 2 during which these undergo a surface treatment causing a reduction of the capacity of absorption of the fluid matrix 3 by the treated solid particles 2, in comparison with non-treated solid particles 2 of the same kind, said treated solid particles 2 forming said functional agent. In particular, as disclosed hereinbefore, said treatment step T advantageously involves grafting of molecules 5 to the respective surface of said particles 2 and/or an increase of the lipophilic and/or hydrophobic nature of the treated solid particles 2, in comparison with non-treated solid particles of the same kind.
According to the invention, said compound 1 is solid at room temperature and intended to be dispersed by fluidification and/or solubilization within a cosmetic and/or dermatological composition to integrate said functional agent therein, advantageously as described before.
Advantageously, the method further comprises a step B of grinding said solid particles 2 intended to reduce their average size. For example, upon completion of said grinding step B, said solid particles 2 have an average size substantially comprised between 10 nm and 500 μm, preferably between 100 nm and 100 μm.
Preferably, as illustrated in
According to a particular embodiment of the invention, as illustrated in
Advantageously, after the dispersion step D, the method also comprises a cooling step F during which said compound 1 cools down to room temperature so as to form a solid.
According to an embodiment provided for illustrative and non-limiting purposes, illustrated in
Advantageously, in particular according to this embodiment, the method involves the use of a twin-screw heater extruder 7, within which the steps disclosed hereinafter are carried out.
The invention also concerns, as such, according to a third aspect, a method for producing a cosmetic and/or dermatological composition, comprising a redispersion step R during which a compound 1, as described before, is added and then mixed with one or several cosmetically and/or dermatologically acceptable components. Advantageously, the previous description concerning the compound 1 and the method for producing a compound 1 also applies to the method for producing a composition according to the invention.
According to a first variant, said redispersion step R further comprises a step of solubilizing said compound 1 by one or more of said cosmetically and/or dermatologically acceptable components. Advantageously, said solubilization step comprises at least the solubilization (that is to say in particular the dispersion) of the compound 1 within a fatty phase (in particular oil) or a portion of said fatty phase of said cosmetic and/or dermatological composition.
According to a second variant, compatible with the first one described hereinbefore, said redispersion step R further comprises a fluidification step, in which said added compound 1 is heated up at least until fluidification, for example at a temperature higher than 50° C., which may be comprised between 55 and 85° C. Said redispersion step R may also comprise said solubilization step and said fluidification step, for example one after another or, according to another example, concomitantly. Preferably, for the redispersion step R and in particular for the solubilization step and/or for the fluidification step, one or more of said cosmetically and/or dermatologically acceptable components is/are substantially fluid at room temperature, thereby facilitating the redispersion of said compound 1 whether through solubilization thereof and/or through fluidification thereof.
In particular, the fact that the waxy matrix 3 of the compound 1 of the invention is primarily, or totally, formed (in weight) by said organosilicon material allows obtaining an excellent dispersability of the compound 1 within a cosmetic and/or dermatological composition, and more specifically within a fatty (oil) phase of such a composition. Thus, in particular, the waxy matrix 3 of the compound 1 of the invention enables the solid particles 2 of the compound 1 to be effectively (re)dispersed, without any particular difficulty, and possibly with no heating, that is to say at room temperature, with other components to form a cosmetic and/or dermatological composition, and in particular to color it when said solid particles 2 consist of pigments.
Thus, according to a particular embodiment, said solubilization step is carried out (in particular within said fatty phase) at a temperature lower than 30° C., preferably lower than 25° C. (and optionally higher than 15° C.), for example about 20° C. (+/−2° C.). Hence, in this last particular embodiment, said redispersion step R does not advantageously include heating of the compound 1, and preferably neither heating of the cosmetic and/or dermatological composition, and in particular of the fatty (oil) phase of the latter. Hence, said solubilization step may advantageously be carried out «at low temperature», that is to say at room temperature (in practice generally between 18 and 25° C. approximately), thereby saving energy and avoiding the potential degradation due to heat of one or several component(s) of the cosmetic and/or dermatological composition, and in particular of the fatty phase of the latter. Thus, said redispersion step R does not comprise the step of fluidification of the compound 1 by heating, and that being so thanks to the properties of the organosilicon material selected to form the waxy matrix 3, in particular polymethylsilsesquioxane. In order to highlight the excellent «redispersability» of the compound 1, and therefore of the solid particles 2 contained thereby, different examples of compounds 1, referred to as C1 to C3, in accordance with the invention, that is to say each comprising a respective functional agent formed by respective solid particles 2 and dispersed in a waxy matrix 3 formed by an organosilicon material, have been made, only for illustrative and non-limiting purposes. Examples of control compounds C4 to C4 have also been made, in the same manner, respectively, as the examples of compounds C1 to C3 in accordance with the invention, with the exception of the fact that the respective waxy matrix of each example of control compounds C4 to C6 is not formed by an organosilicon material, but for example by an olive oil ester wax, which is a non-organosilicon material. In particular, the organosilicon material of the waxy matrices 3 of the examples of compounds C1 to C3 consists of polymethylsilsesquioxane.
The compounds C1 to C6 have been prepared according to Table 1, and each therefore results from a mixing of respective solid particles (pigments in this instance) and of a respective waxy matrix.
All of the examples of compounds C1 to C6 are in the form of granulates that are solid at room temperature (approximately 20 to 25° C.).
In these non-limiting examples, the solid particles 2 of the compounds C1 to C6 consist of treated pigments, that is to say (pigment type) solid particles 2 having undergone a surface treatment causing a reduction of the capacity of absorption of the waxy matrix. The respective commercial names (on the date of filing of the present patent application) of these treated pigments are reported in Table 1. These treated pigments are commercialized under their respective commercial names in particular by the company Miyoshi.
For example, the surface treatment of the pigments (which are solid particles) of the examples of compounds C1 to C6 may be carried out with a treatment based on amino acids, preferably in accordance with the teaching of the patent U.S. Pat. No. 4,606,914, the amino acids are in particular in the form of metallic salts of N-acylamino acid. Thus, for example, said surface treatment consists in coating raw, that is to say non-treated, solid particles (and in particular pigments) with 0.5 to 10 weight % of one or several metallic salts of N-acylamino acid, with respect to the weight of the raw solid particles. For example, the N-acylamino acid is a N-acyl-L-glutamic acid, whereas the metal consists for example of aluminum, magnesium, calcium, zinc or titanium. For example, the metallic salt of N-acylamino acid is made using sodium myristoyl glutamate and aluminum hydroxide. In particular, such a surface treatment may be used for the examples presented herein, for illustrative and non-limiting purposes, as well as in the rest of the description hereinbefore and hereinafter. Said surface treatment, in particular said treatment using metallic salts of N-acylamino acid, preferably increases the hydrophobic nature and the dispersability in oil of the treated solid particles 2 in comparison with the (non-treated) raw solid particles.
The examples of compounds C1 to C3 have been prepared according to the method for producing the compound 1 of the invention, whereas the examples of compounds C4 to C6 have been prepared according to an equivalent production method, except that the method for producing C4 to C6 includes the implementation of a non-organosilicon material (in particular, olive oil ester wax) instead of the organosilicon material (polymethylsilsesquioxane in this instance).
Afterwards, the dispersability of the examples of compounds C1 to C3 in accordance with the invention has been compared with that of the examples of compounds C4 to C6 not compliant with the invention, by dispersing each of the examples of compounds C1 to C6 within a respective liquid fatty body, always of the same nature and in the same proportions, the liquid fatty body being selected from the following components: dimethicone type linear silicone oil, cyclopentasiloxane type cyclic silicon oil, and methyl trimethicone type branched silicone oil. The ratio (in weight) of the example of compound (C1 to C6) and of the fatty body is 1:9. The dispersion (solubilization in this instance) of the examples of compounds C1 to C6 has been made under homogenization at 6000 rpm, for 5 to 15 min, at room temperature (between 20 and 25° C. approximately).
The dispersion of each example of compound C1 to C6 within their respective liquid fatty bodies allows obtaining respective mixtures M1 to M6 (Mx therefore corresponds to the solubilization of the example of compound Cx in a respective liquid fatty body, with x comprised between 1 and 6).
The dispersability of the examples of compounds C1 to C3 (with the organosilicon material matrix) and of the examples of compounds C4 to C6 (with the non-organosilicon material matrix) has been compared by observing the mixtures C1 to C6:
Thus, the invention allows obtaining a compound 1 including a large content of a functional agent and facilitating the transport, storage and handling of the latter.
| Number | Date | Country | Kind |
|---|---|---|---|
| 1904461 | Apr 2019 | FR | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/FR2020/050693 | 4/23/2020 | WO | 00 |