Patent Grant
11641865
This disclosure provides, e.g., coatings that are applied to agricultural products and methods of application and use thereof.
Common agricultural products are susceptible to degradation and decomposition (i.e., spoilage) when exposed to the environment. Such agricultural products can include, for example, eggs, fruits, vegetables, produce, seeds, nuts, flowers, and/or whole plants (including their processed and semi-processed forms). Edible non-agricultural products (e.g., vitamins, candy, etc.) can also be vulnerable to degradation when exposed to the ambient environment. The degradation of agricultural and other edible products can occur via abiotic means as a result of evaporative moisture loss from an external surface of the products to the atmosphere, oxidation by oxygen that diffuses into the products from the environment, mechanical damage to the surface, and/or light-induced degradation (i.e., photodegradation). Biotic stressors such as bacteria, fungi, viruses, and/or pests can also infest and decompose the products.
The cells that form the aerial surface of most plants (such as higher plants) include an outer envelope or cuticle, which provides varying degrees of protection against water loss, oxidation, mechanical damage, photodegradation, and/or biotic stressors, depending upon the plant species and the plant organ (e.g., fruit, seeds, bark, flowers, leaves, stems, etc.). Cutin, which is a biopolyester derived from cellular lipids, forms the major structural component of the cuticle and serves to provide protection to the plant against environmental stressors (both abiotic and biotic). The thickness, density, as well as the composition of the cutin (i.e., the different types of monomers that form the cutin and their relative proportions) can vary by plant species, by plant organ within the same or different plant species, and by stage of plant maturity. The cutin-containing portion of the plant can also contain additional compounds (e.g., epicuticular waxes, phenolics, antioxidants, colored compounds, proteins, polysaccharides, etc.). This variation in the cutin composition as well as the thickness and density of the cutin layer between plant species, plant organs and/or a given plant at different stages of maturation can lead to varying degrees of resistance between plant species or plant organs to attack by environmental stressors (i.e., water loss, oxidation, mechanical injury, and light) and/or biotic stressors (e.g., fungi, bacteria, viruses, insects, etc.).
Conventional approaches to preventing degradation, maintaining quality, and increasing the life of agricultural products include special packaging and/or refrigeration. Refrigeration requires capital-intensive equipment, demands constant energy expenditure, can cause damage or quality loss to the product if not carefully controlled, must be actively managed, and its benefits are lost upon interruption of a temperature-controlled supply chain. Produce mass loss (e.g. water loss) during storage increases humidity, which necessitates careful maintenance of relative humidity levels (e.g. using condensers) to avoid negative impacts (e.g. condensation, microbial proliferation, etc.) during storage. Moreover, respiration of agricultural products is an exothermic process which releases heat into the surrounding atmosphere. During transit and storage in shipping containers, heat generated by the respiration of the agricultural product, as well as external environmental conditions and heat generated from mechanical processes (e.g., motors) necessitates active cooling of the storage container in order to maintain the appropriate temperature for storage, which is a major cost driver for shipping companies. By reducing the rate of degradation, reducing the heat generation in storage and transit, and increasing the shelf life of agricultural products, there is a direct value to the key stakeholders throughout the supply chain.
There exists a need for new, more cost-effective approaches to prevent degradation, reduce the generation of heat and humidity, maintain quality, and increase the life of agricultural products. Such approaches may require less or no refrigeration, special packaging, etc.
Compositions and formulations for forming protective coatings and methods of making and using the coatings thereof are described herein. The components of the coatings form lamellar structures comprising one or more lamellae on the surface of the substrate (e.g., agricultural product) the coatings are disposed on, thus forming a protective barrier. In some embodiments, the protective barrier exhibits a low water and gas permeability. For example, the lattice formation that the molecules of the lamella adopt and the intermolecular forces between the lamellae can reduce loss of water or gas from the substrate. In some embodiments, the water and gas permeability of the coatings described herein can be modified by, e.g., (1) changing the components or amounts of the components in the composition (e.g., coating agent) applied to the substrate, as well as (2) modifying the method used to form the coating (e.g., the temperature or speed at which the mixture comprising the coating agent on the substrate is dried and/or the concentration of the coating agent in the mixture applied to the substrate). In some embodiments, the coating agents and/or coatings formed comprise lipid derivatives, such as fatty acids, fatty acid esters, or a combination thereof, and/or fatty acid salts. In some embodiments, the coatings described herein are a more effective barrier to water and gas than, e.g., conventional wax coatings. In some such embodiments, the thickness of the coating is less than the thickness of conventional wax coatings.
In one aspect, described herein is a coated agricultural product comprising a coating that forms a lamellar structure on the agricultural product, wherein the coating has a thickness of less than 20 microns.
In another aspect, described herein is a coated agricultural product comprising a coating that forms a lamellar structure on the agricultural product, wherein the coating comprises a plurality of grains.
In some embodiments, the coating comprises one or more fatty acids, fatty acid esters, or a combination thereof, and one or more fatty acid salts. In some embodiments, the coating comprises two or more fatty acids, fatty acid esters, or a combination thereof. In some embodiments, the coating comprises two or more fatty acid salts. In some embodiments, the coating comprises one to two fatty acids, fatty acid esters, or a combination thereof; and one to two fatty acid salts.
In some embodiments, the lamellar structure comprises a plurality of lamellae. In some embodiments, the interlayer spacing of the lamellae is from about 2 to about 13 nm. In some embodiments, the interlayer spacing of the lamellae is from about 3.0 to about 10 nm. In some embodiments, the interlayer spacing of the lamellae is from about 3.0 to about 6 nm. For example, the interlayer spacing of the lamellae is from about 5.0 to about 5.8 nm.
In some embodiments, the fatty acids, fatty acid esters, or a combination thereof are collectively 65% to 99% by weight of the coating. For example, the fatty acids, fatty acid esters, or a combination thereof are collectively 65% to 75% by weight of the coating. For example, the fatty acids, fatty acid esters, or a combination thereof are collectively 92% to 96% by weight of the coating. For example, the fatty acids, fatty acid esters, or a combination thereof are collectively 94% by weight of the coating.
In some embodiments, the fatty acid salts are collectively 1% to 35% by weight of the coating. For example, the fatty acid salts are collectively 25% to 35% by weight of the coating. For example, the fatty acid salts are collectively 4% to 8% by weight of the coating. For example, the fatty acid salts are collectively 6% by weight of the coating.
In some embodiments, the coating comprises a plurality of grains.
In some embodiments, the grain size is from about 6 nm to about 100 nm. For example, the grain size is from about 9 nm to about 22 nm. For example, the grain size is from about 13 nm to about 25 nm.
In some embodiments, the coating has a thickness of 100 nm to 20 microns. In some embodiments, the coating has a thickness of less than 2 microns. For example, the coating has a thickness of about 100 nm to about 2 microns. For example, the coating has a thickness of about 700 nm to about 1.5 microns. For example, the coating has a thickness of about 700 nm to about 1 micron.
In some embodiments, each fatty acid and/or ester thereof is an independently selected compound of Formula I, wherein Formula I is:
wherein:
R is selected from —H, -glyceryl, —C1-C6 alkyl, —C2-C6 alkenyl, —C2-C6 alkynyl, —C3-C1 cycloalkyl, aryl, or heteroaryl, wherein each alkyl, alkenyl, alkynyl, cycloalkyl, aryl or heteroaryl is optionally substituted with one or more groups selected from halogen (e.g., C1, Br, or I), hydroxyl, nitro, —CN, —NH2, —SH, —SR15, —OR14, —NR14R15, C1-C6 alkyl, C2-C6 alkenyl, or C2-C6 alkynyl;
R1, R2, R5, R6, R9, R10, R11, R12 and R13 are each independently, at each occurrence, —H, —(C═O)R14, —(C═O)H, —(C═O)OH, —(C═O)OR14, —(C═O)—O—(C═O)R14, —O(C═O)R14, —OR14, —NR14R15, —SR14, halogen, —C1-C6 alkyl, —C2-C6 alkenyl, —C2-C6 alkynyl, —C3-C1 cycloalkyl, aryl, or heteroaryl, wherein each alkyl, alkenyl, alkynyl, cycloalkyl, aryl, or heteroaryl is optionally substituted with one or more —OR14, —NR14R15, —SR14, or halogen;
R3, R4, R7, and R8 are each independently, at each occurrence, —H, —OR14, —NR14R15, —SR14, halogen, —C1-C6 alkyl, —C2-C6 alkenyl, —C2-C6 alkynyl, —C3-C1 cycloalkyl, aryl, or heteroaryl wherein each alkyl, alkynyl, cycloalkyl, aryl, or heteroaryl is optionally substituted with one or more —OR14, —NR14R15, —SR14, or halogen; or
R3 and R4 can combine with the carbon atoms to which they are attached to form a C3-C6 cycloalkyl, a C4-C6 cycloalkenyl, or 3- to 6-membered ring heterocycle; and/or
R7 and R8 can combine with the carbon atoms to which they are attached to form a C3-C6 cycloalkyl, a C4-C6 cycloalkenyl, or 3- to 6-membered ring heterocycle;
R14 and R15 are each independently, at each occurrence, —H, aryl, heteroaryl, —C1-C6 alkyl, —C2-C6 alkenyl, or —C2-C6 alkynyl;
the symbol represents a single bond or a cis or trans double bond;
n is 0, 1, 2, 3, 4, 5, 6, 7 or 8;
m is 0, 1, 2 or 3;
q is 0, 1, 2, 3, 4 or 5; and
r is 0, 1, 2, 3, 4, 5, 6, 7 or 8.
In some embodiments, R is -glyceryl.
In some embodiments, R1, R2, R5, R6, R9, R10, R11, R12 and R13 are each independently selected from —H, —C1-C6 alkyl, and —OH.
In some embodiments, R3, R4, R7, and R8 are each independently selected from —H, —C1-C6 alkyl, and —OH. In some embodiments, R3 and R4 combine with the carbon atoms to which they are attached to form a 3- to 6-membered ring heterocycle. In some embodiments, R7 and R8 combine with the carbon atoms to which they are attached to form a 3- to 6-membered ring heterocycle.
In some embodiments, q is 1 and the sum of n, m, and r is from 10 to 12.
In some embodiments, each fatty acid salt is an independently selected compound of Formula II or Formula III, wherein Formula II and Formula III are:
wherein for each formula:
X is a cationic moiety;
Xp+ is a cationic counter ion having a charge state p, and p is 1, 2, or 3;
R1, R2, R5, R6, R9, R10, R11, R12 and R13 are each independently, at each occurrence, —H, —(C═O)R14, —(C═O)H, —(C═O)OH, —(C═O)OR14, —(C═O)—O—(C═O)R14, —O(C═O)R14, —OR14, —NR14R15, —SR14, halogen, —C1-C6 alkyl, —C2-C6 alkenyl, —C2-C6 alkynyl, —C3-C1 cycloalkyl, aryl, or heteroaryl, wherein each alkyl, alkenyl, alkynyl, cycloalkyl, aryl, or heteroaryl is optionally substituted with one or more —OR14, —NR14R15, —SR14, or halogen;
R3, R4, R7, and R8 are each independently, at each occurrence, —H, —OR14, —NR14R15, —SR14, halogen, —C1-C6 alkyl, —C2-C6 alkenyl, —C2-C6 alkynyl, —C3-C1 cycloalkyl, aryl, or heteroaryl wherein each alkyl, alkynyl, cycloalkyl, aryl, or heteroaryl is optionally substituted with one or more —OR14, —NR14R15, —SR14, or halogen; or
R3 and R4 can combine with the carbon atoms to which they are attached to form a C3-C6 cycloalkyl, a C4-C6 cycloalkenyl, or 3- to 6-membered ring heterocycle; and/or
R7 and R8 can combine with the carbon atoms to which they are attached to form a C3-C6 cycloalkyl, a C4-C6 cycloalkenyl, or 3- to 6-membered ring heterocycle;
R14 and R15 are each independently, at each occurrence, —H, aryl, heteroaryl, —C1-C6 alkyl, —C2-C6 alkenyl, or —C2-C6 alkynyl;
the symbol represents a single bond or a cis or trans double bond;
n is 0, 1, 2, 3, 4, 5, 6, 7 or 8;
m is 0, 1, 2 or 3;
q is 0, 1, 2, 3, 4 or 5; and
r is 0, 1, 2, 3, 4, 5, 6, 7 or 8.
In some embodiments, the fatty acid salt is a compound of Formula II. In some embodiments, the fatty acid salt is a compound of Formula III.
In some embodiments, X is sodium.
In some embodiments, R1, R2, R5, R6, R9, R10, R11, R12 and R13 are each independently selected from —H, —C1-C6 alkyl, and —OH.
In some embodiments, R3, R4, R7, and R8 are each independently selected from —H, —C1-C6 alkyl, and —OH. In some embodiments, R3 and R4 combine with the carbon atoms to which they are attached to form a 3- to 6-membered ring heterocycle. In some embodiments, R7 and R8 combine with the carbon atoms to which they are attached to form a 3- to 6-membered ring heterocycle.
In some embodiments, q is 1 and the sum of n, m, and r is from 10 to 12.
In some embodiments, each fatty acid and/or ester thereof is an independently selected compound of Formula IA, wherein Formula IA is:
wherein:
R is selected from the group consisting of H and C1-C6 alkyl optionally substituted with one or more of OH and C1-C6 alkoxy;
R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
each occurrence of R10A, R10B, R11A, and R11B is independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
or any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a double bond, a 3- to 6-membered ring heterocycle, or a C3-C6 cycloalkyl; and
o is an integer from 0 to 17;
p is an integer from 0 to 17;
wherein the sum of o and p is from 0 to 17;
or a salt thereof when R is C1-C6 alkyl optionally substituted with one or more of OH and C1-C6 alkoxy.
In some embodiments, R is C1-C6 alkyl optionally substituted with one or more OH.
In some embodiments, the compound of Formula IA is a compound of Formula IA-A-i:
or a salt thereof,
wherein:
RA1 and RA2 are independently selected from H and C1-C6 alkyl;
R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
each occurrence of R10A, R10B, R11A, and R11B is independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
or any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a double bond, a 3- to 6-membered ring heterocycle, or a C3-C6 cycloalkyl;
o is an integer from 0 to 17;
p is an integer from 0 to 17; and
wherein the sum of o and p is from 0 to 17.
In some embodiments, RA1 and RA2 are H.
In some embodiments, R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of: H, OH, and C1-C6 alkyl. In some embodiments, R1, R2, R3, R4, R5, R6, R7, R8, and R9 are H.
In some embodiments, R10A, R10B, R11A, and R11B are independently selected from the group consisting of: H, OH, and C1-C6 alkyl. In some embodiments, R10A, R10B, R11A, and R11B are H.
In some embodiments, R4 is taken together with R6 and the carbon atoms to which they are attached to form a C3-C6 heterocyclyl. In some embodiments, R4 is taken together with R6 and the carbon atoms to which they are attached to form a double bond.
In some embodiments, the sum of o and p is from 11 to 13.
In some embodiments, each fatty acid salt is an independently selected compound of Formula IIA, wherein Formula IIA is:
wherein:
R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
each occurrence of R10A, R10B, R11A, and R11B is independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
or any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a double bond, a 3- to 6-membered ring heterocycle, or a C3-C6 cycloalkyl;
o is an integer from 0 to 17;
p is an integer from 0 to 17;
wherein the sum of o and p is from 0 to 17;
Xn+ is a cationic moiety having formal charge n; and
each occurrence of R′ is selected from H and C1-C6 alkyl.
In some embodiments, R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of: H, OH, and C1-C6 alkyl. In some embodiments, R1, R2, R3, R4, R5, R6, R7, R8, and R9 are H.
In some embodiments, R10A, R10B, R11A, and R11B are independently selected from the group consisting of: H, OH, and C1-C6 alkyl. In some embodiments, R10A, R10B, R11A, and R11B are H.
In some embodiments, R4 is taken together with R6 and the carbon atoms to which they are attached to form a C3-C6 heterocyclyl. In some embodiments, R4 is taken together with R6 and the carbon atoms to which they are attached to form a double bond.
In some embodiments, the sum of o and p is from 11 to 13.
In another aspect, described herein is a method of coating an agricultural product, comprising:
(i) applying a mixture comprising a coating agent and a solvent to the agricultural product;
(ii) drying the mixture at a temperature of greater than 50° C. to form a coating on the agricultural product;
wherein:
the coating forms a lamellar structure on the agricultural product; and
the coating has a thickness of less than 20 microns.
In another aspect, described herein is a method of coating an agricultural product, comprising:
(i) applying a mixture comprising a coating agent and a solvent to the agricultural product;
(ii) drying the mixture at a temperature of greater than 50° C. to form a coating on the agricultural product;
wherein:
the coating forms a lamellar structure on the agricultural product; and
the coating comprises a plurality of grains.
In another aspect, described herein is a method of coating an agricultural product, comprising:
(i) applying a mixture comprising a coating agent and a solvent to the agricultural product;
(ii) removing the solvent to form a coating on the agricultural product;
(iii) heating the coated agricultural product from a first temperature to a second temperature, wherein the second temperature is greater than the first temperature and less than the melting point of the coating; and
(iv) cooling the coated agricultural product from the second temperature to a third temperature, wherein the third temperature is less than the second temperature;
wherein:
the coating forms a lamellar structure on the agricultural product; and
the coating comprises a plurality of grains.
In some embodiments, the first temperature is from about 20° C. to about 30° C. For example, the first temperature is from about 23° C. to about 27° C. For example, the first temperature is about 25° C.
In some embodiments, the second temperature is from about 50° C. to about 65° C. For example, the second temperature is from about 57° C. to about 63° C. For example, the second temperature is about 60° C.
In some embodiments, the third temperature is from about 20° C. to about 30° C. or example, the third temperature is from about 23° C. to about 27° C. For example, the third temperature is about 25° C.
In some embodiments, the second temperature is maintained for about 5 minutes to about 60 minutes. For example, the second temperature is maintained for about 25 minutes to about 35 minutes.
In some embodiments, the grain size after cooling the coated agricultural product from the second temperature to the third temperature is larger than the grain size before heating the coated agricultural product from the first temperature to the second temperature. In some embodiments, the grain size of the coating before heating the coated agricultural product from the first temperature to the second temperature is from about 8 nm to about 10 nm. In some embodiments, the grain size of the coating after cooling the coated agricultural product from the second temperature to the third temperature is from about 11 nm to about 17 nm.
In another aspect, described herein is a method of reducing the mass loss rate of an agricultural product, comprising:
(i) applying a mixture comprising a coating agent and a solvent to the agricultural product;
(ii) drying the mixture at a temperature of greater than 50° C. to form a coating on the agricultural product;
wherein:
the coating forms a lamellar structure on the agricultural product; and
the coating has a thickness of less than 20 microns.
In another aspect, described herein is a method of reducing the respiration rate of an agricultural product, comprising:
(i) applying a mixture comprising a coating agent and a solvent to the agricultural product;
(ii) drying the mixture at a temperature of greater than 50° C. to form a coating on the agricultural product;
wherein:
the coating forms a lamellar structure on the agricultural product; and
the coating has a thickness of less than 20 microns.
In some embodiments, the coating agent comprises one or more fatty acids, fatty acid esters, or a combination thereof, and one or more fatty acid salts. In some embodiments, the coating agent comprises two or more fatty acids, fatty acid esters, or a combination thereof. In some embodiments, the coating agent comprises two or more fatty acid salts. In some embodiments, the coating agent comprises one to two fatty acids, fatty acid esters, or a combination thereof; and one to two fatty acid salts.
In some embodiments, the solvent comprises water. For example, the solvent is water.
In some embodiments, the concentration of the coating agent in the mixture is from about 25 g/L to about 60 g/L. For example, the concentration of the coating agent in the mixture is from about 30 g/L to about 50 g/L For example, the concentration of the coating agent in the mixture is about 30 g/L. For example, the concentration of the coating agent in the mixture is about 40 g/L. For example, the concentration of the coating agent in the mixture is about 50 g/L.
In some embodiments, the mixture is dried at a temperature of from about 55° C. to about 65° C. For example, the mixture is dried at a temperature of from about 60° C. to about 65° C.
For example, the mixture is dried at a temperature of about 65° C.
In some embodiments, the lamellar structure comprises a plurality of lamellae. In some embodiments, the interlayer spacing of the lamellae is from about 2 to about 13 nm. In some embodiments, the interlayer spacing of the lamellae is from about 3.0 to about 10 nm. In some embodiments, the interlayer spacing of the lamellae is from about 3.0 to about 6 nm. For example, the interlayer spacing of the lamellae is from about 5.0 to about 5.8 nm.
In some embodiments, the fatty acids, fatty acid esters, or a combination thereof are collectively 65% to 99% by weight of the coating agent. For example, the fatty acids, fatty acid esters, or a combination thereof are collectively 65% to 75% by weight of the coating agent. For example, the fatty acids, fatty acid esters, or a combination thereof are collectively 92% to 96% by weight of the coating agent. For example, the fatty acids, fatty acid esters, or a combination thereof are collectively 94% by weight of the coating agent.
In some embodiments, the fatty acid salts are collectively 1% to 35% by weight of the coating agent. For example, the fatty acid salts are collectively 25% to 35% by weight of the coating agent. For example, the fatty acid salts are collectively 4% to 8% by weight of the coating agent. For example, the fatty acid salts are collectively 6% by weight of the coating agent.
In some embodiments, the coating comprises a plurality of grains.
In some embodiments, the grain size is from about 6 nm to about 100 nm. For example, the grain size is from about 9 nm to about 22 nm. For example, the grain size is from about 13 nm to about 25 nm.
In another aspect, described herein is a method of reducing the mass loss rate of an agricultural product having a coating disposed thereon, comprising:
(i) heating the coated agricultural product from a first temperature to a second temperature; and
(ii) cooling the coated agricultural product from the second temperature to a third temperature, wherein the third temperature is less than the second temperature;
wherein:
the coating forms a lamellar structure on the agricultural product; and
the coating comprises a plurality of grains.
In another aspect, described herein is a method of reducing the respiration rate of an agricultural product having a coating disposed thereon, comprising:
(i) heating the coated agricultural product from a first temperature to a second temperature; and
(ii) cooling the coated agricultural product from the second temperature to a third temperature, wherein the third temperature is less than the second temperature;
wherein:
the coating forms a lamellar structure on the agricultural product; and
the coating comprises a plurality of grains.
In some embodiments, the first temperature is from about 20° C. to about 30° C. For example, the first temperature is from about 23° C. to about 27° C. For example, the first temperature is about 25° C.
In some embodiments, the second temperature is from about 50° C. to about 65° C. For example, the second temperature is from about 57° C. to about 63° C. For example, the second temperature is about 60° C.
In some embodiments, the third temperature is from about 20° C. to about 30° C. or example, the third temperature is from about 23° C. to about 27° C. For example, the third temperature is about 25° C.
In some embodiments, the second temperature is maintained for about 5 minutes to about 60 minutes. For example, the second temperature is maintained for about 25 minutes to about 35 minutes.
In some embodiments, the grain size after cooling the coated agricultural product from the second temperature to the third temperature is larger than the grain size before heating the coated agricultural product from the first temperature to the second temperature. In some embodiments, the grain size of the coating before heating the coated agricultural product from the first temperature to the second temperature is from about 8 nm to about 10 nm. For example, the grain size of the coating after cooling the coated agricultural product from the second temperature to the third temperature is from about 11 nm to about 17 nm.
In some embodiments, the coating comprises one or more fatty acids, fatty acid esters, or a combination thereof, and one or more fatty acid salts. In some embodiments, the coating comprises two or more fatty acids, fatty acid esters, or a combination thereof. In some embodiments, the coating comprises two or more fatty acid salts. In some embodiments, the coating comprises one to two fatty acids, fatty acid esters, or a combination thereof; and one to two fatty acid salts.
In some embodiments, the lamellar structure comprises a plurality of lamellae. In some embodiments, the interlayer spacing of the lamellae is from about 2 to about 13 nm. In some embodiments, the interlayer spacing of the lamellae is from about 3.0 to about 10 nm. In some embodiments, the interlayer spacing of the lamellae is from about 3.0 to about 6 nm. For example, the interlayer spacing of the lamellae is from about 5.0 to about 5.8 nm.
In some embodiments, the fatty acids, fatty acid esters, or a combination thereof are collectively 65% to 99% by weight of the coating. For example, the fatty acids, fatty acid esters, or a combination thereof are collectively 65% to 75% by weight of the coating. For example, the fatty acids, fatty acid esters, or a combination thereof are collectively 92% to 96% by weight of the coating. For example, the fatty acids, fatty acid esters, or a combination thereof are collectively 94% by weight of the coating.
In some embodiments, the fatty acid salts are collectively 1% to 35% by weight of the coating. For example, the fatty acid salts are collectively 25% to 35% by weight of the coating.
For example, the fatty acid salts are collectively 4% to 8% by weight of the coating. For example, the fatty acid salts are collectively 6% by weight of the coating.
In some embodiments, the coating has a thickness of 100 nm to 20 microns. In some embodiments, the coating has a thickness of less than 2 microns. For example, the coating has a thickness of about 100 nm to about 2 microns. For example, the coating has a thickness of about 700 nm to about 1.5 microns. For example, the coating has a thickness of about 700 nm to about 1 micron.
In some embodiments, each fatty acid and/or ester thereof is an independently selected compound of Formula I, wherein Formula I is:
wherein:
R is selected from —H, -glyceryl, —C1-C6 alkyl, —C2-C6 alkenyl, —C2-C6 alkynyl, —C3-C1 cycloalkyl, aryl, or heteroaryl, wherein each alkyl, alkenyl, alkynyl, cycloalkyl, aryl or heteroaryl is optionally substituted with one or more groups selected from halogen (e.g., C1, Br, or I), hydroxyl, nitro, —CN, —NH2, —SH, —SR15, —OR14, —NR14R15, C1-C6 alkyl, C2-C6 alkenyl, or C2-C6 alkynyl;
R1, R2, R5, R6, R9, R10, R11, R12 and R13 are each independently, at each occurrence, —H, —(C═O)R14, —(C═O)H, —(C═O)OH, —(C═O)OR14, —(C═O)—O—(C═O)R14, —O(C═O)R14, —OR14, —NR14R15, —SR14, halogen, —C1-C6 alkyl, —C2-C6 alkenyl, —C2-C6 alkynyl, —C3-C1 cycloalkyl, aryl, or heteroaryl, wherein each alkyl, alkenyl, alkynyl, cycloalkyl, aryl, or heteroaryl is optionally substituted with one or more —OR14, —NR14R15, —SR14, or halogen;
R3, R4, R7, and R8 are each independently, at each occurrence, —H, —OR14, —NR14R15, —SR14, halogen, —C1-C6 alkyl, —C2-C6 alkenyl, —C2-C6 alkynyl, —C3-C1 cycloalkyl, aryl, or heteroaryl wherein each alkyl, alkynyl, cycloalkyl, aryl, or heteroaryl is optionally substituted with one or more —OR14, —NR14R15, —SR14, or halogen; or
R3 and R4 can combine with the carbon atoms to which they are attached to form a C3-C6 cycloalkyl, a C4-C6 cycloalkenyl, or 3- to 6-membered ring heterocycle; and/or
R7 and R8 can combine with the carbon atoms to which they are attached to form a C3-C6 cycloalkyl, a C4-C6 cycloalkenyl, or 3- to 6-membered ring heterocycle;
R14 and R15 are each independently, at each occurrence, —H, aryl, heteroaryl, —C1-C6 alkyl, —C2-C6 alkenyl, or —C2-C6 alkynyl;
the symbol represents a single bond or a cis or trans double bond;
n is 0, 1, 2, 3, 4, 5, 6, 7 or 8;
m is 0, 1, 2 or 3;
q is 0, 1, 2, 3, 4 or 5; and
r is 0, 1, 2, 3, 4, 5, 6, 7 or 8.
In some embodiments, R is -glyceryl. In some embodiments, R1, R2, R5, R6, R9, R10, R11, R12 and R13 are each independently selected from —H, —C1-C6 alkyl, and —OH. In some embodiments, R3, R4, R7, and R8 are each independently selected from —H, —C1-C6 alkyl, and —OH. In some embodiments, R3 and R4 combine with the carbon atoms to which they are attached to form a 3- to 6-membered ring heterocycle. In some embodiments, R7 and R8 combine with the carbon atoms to which they are attached to form a 3- to 6-membered ring heterocycle. In some embodiments, q is 1 and the sum of n, m, and r is from 10 to 12.
In some embodiments, each fatty acid salt is an independently selected compound of Formula II or Formula III, wherein Formula II and Formula III are:
wherein for each formula:
X is a cationic moiety;
Xp+ is a cationic counter ion having a charge state p, and p is 1, 2, or 3;
R1, R2, R5, R6, R9, R10, R11, R12 and R13 are each independently, at each occurrence, —H, —(C═O)R14, —(C═O)H, —(C═O)OH, —(C═O)OR14, —(C═O)—O—(C═O)R14, —O(C═O)R14, —OR14, —NR14R15, —SR14, halogen, —C1-C6 alkyl, —C2-C6 alkenyl, —C2-C6 alkynyl, —C3-C1 cycloalkyl, aryl, or heteroaryl, wherein each alkyl, alkenyl, alkynyl, cycloalkyl, aryl, or heteroaryl is optionally substituted with one or more —OR14, —NR14R15, —SR14, or halogen;
R3, R4, R7, and R8 are each independently, at each occurrence, —H, —OR14, —NR14R15, —SR14, halogen, —C1-C6 alkyl, —C2-C6 alkenyl, —C2-C6 alkynyl, —C3-C1 cycloalkyl, aryl, or heteroaryl wherein each alkyl, alkynyl, cycloalkyl, aryl, or heteroaryl is optionally substituted with one or more —OR14, —NR14R15, —SR14, or halogen; or
R3 and R4 can combine with the carbon atoms to which they are attached to form a C3-C6 cycloalkyl, a C4-C6 cycloalkenyl, or 3- to 6-membered ring heterocycle; and/or
R7 and R8 can combine with the carbon atoms to which they are attached to form a C3-C6 cycloalkyl, a C4-C6 cycloalkenyl, or 3- to 6-membered ring heterocycle;
R14 and R15 are each independently, at each occurrence, —H, aryl, heteroaryl, —C1-C6 alkyl, —C2-C6 alkenyl, or —C2-C6 alkynyl;
the symbol represents a single bond or a cis or trans double bond;
n is 0, 1, 2, 3, 4, 5, 6, 7 or 8;
m is 0, 1, 2 or 3;
q is 0, 1, 2, 3, 4 or 5; and
r is 0, 1, 2, 3, 4, 5, 6, 7 or 8.
In some embodiments, the fatty acid salt is a compound of Formula II. In some embodiments, the fatty acid salt is a compound of Formula III.
In some embodiments, X is sodium.
In some embodiments, R1, R2, R5, R6, R9, R10, R11, R12 and R13 are each independently selected from —H, —C1-C6 alkyl, and —OH. In some embodiments, R3, R4, R7, and R8 are each independently selected from —H, —C1-C6 alkyl, and —OH.
In some embodiments, R3 and R4 combine with the carbon atoms to which they are attached to form a 3- to 6-membered ring heterocycle. In some embodiments, R7 and R8 combine with the carbon atoms to which they are attached to form a 3- to 6-membered ring heterocycle.
In some embodiments, q is 1 and the sum of n, m, and r is from 10 to 12.
In some embodiments, each fatty acid and/or ester thereof is an independently selected compound of Formula IA, wherein Formula IA is:
wherein:
R is selected from the group consisting of H and C1-C6 alkyl optionally substituted with one or more of OH and C1-C6 alkoxy;
R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
each occurrence of R10A, R10B, R11A, and R11B is independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
or any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a double bond, a 3- to 6-membered ring heterocycle, or a C3-C6 cycloalkyl; and
o is an integer from 0 to 17;
p is an integer from 0 to 17;
wherein the sum of o and p is from 0 to 17;
or a salt thereof when R is C1-C6 alkyl optionally substituted with one or more of OH and C1-C6 alkoxy.
In some embodiments, R is C1-C6 alkyl optionally substituted with one or more OH.
In some embodiments, the compound of Formula IA is a compound of Formula IA-A-i:
or a salt thereof,
wherein:
RA1 and RA2 are independently selected from H and C1-C6 alkyl;
R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
each occurrence of R10A, R10B, R11A, and R11B is independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
or any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a double bond, a 3- to 6-membered ring heterocycle, or a C3-C6 cycloalkyl;
o is an integer from 0 to 17;
p is an integer from 0 to 17; and
wherein the sum of o and p is from 0 to 17.
In some embodiments, RA1 and RA2 are H.
In some embodiments, R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of: H, OH, and C1-C6 alkyl. In some embodiments, R1, R2, R3, R4, R5, R6, R7, R8, and R9 are H.
In some embodiments, R10A, R10B, R11A, and R11B are independently selected from the group consisting of: H, OH, and C1-C6 alkyl. In some embodiments, R10A, R10B, R11A, and R11B are H.
In some embodiments, R4 is taken together with R6 and the carbon atoms to which they are attached to form a C3-C6 heterocyclyl. In some embodiments, R4 is taken together with R6 and the carbon atoms to which they are attached to form a double bond.
In some embodiments, the sum of o and p is from 11 to 13.
In some embodiments, each fatty acid salt is an independently selected compound of Formula IIA, wherein Formula IIA is:
wherein:
R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
each occurrence of R10A, R10B, R11A, and R11B is independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
or any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a double bond, a 3- to 6-membered ring heterocycle, or a C3-C6 cycloalkyl;
o is an integer from 0 to 17;
p is an integer from 0 to 17;
wherein the sum of o and p is from 0 to 17;
Xn+ is a cationic moiety having formal charge n; and
each occurrence of R′ is selected from H and C1-C6 alkyl.
In some embodiments, R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of: H, OH, and C1-C6 alkyl. In some embodiments, R1, R2, R3, R4, R5, R6, R7, R8, and R9 are H.
In some embodiments, R10A, R10B, R11A, and R11B are independently selected from the group consisting of: H, OH, and C1-C6 alkyl. In some embodiments, R10A, R10B, R11A, and R11B are H.
In some embodiments, R4 is taken together with R6 and the carbon atoms to which they are attached to form a C3-C6 heterocyclyl. In some embodiments, R4 is taken together with R6 and the carbon atoms to which they are attached to form a double bond.
In some embodiments, the sum of o and p is from 11 to 13.
In some embodiments, the compositions can include a first group of compounds, where each compound of the first group is selected from fatty acids, fatty acid esters, and fatty acid salts, and each compound of the first group has a carbon chain length of at least 14 carbons. The compositions can also include a second group of compounds selected from fatty acids, fatty acid esters, fatty acid salts, and combinations thereof, wherein each compound of the second group has a carbon chain length from 7 to 13 carbons. At least some of the compounds of the first group (e.g., fatty acid salts) can function as emulsifiers, allowing the composition to be dissolved, suspended, or dispersed in a solvent. At least some of the compounds of the second group can function as wetting agents or surfactants in order to improve the surface wetting of items to be coated when solutions, suspensions, or colloids that include the compositions are applied to the items. The fatty acid salts having a carbon chain length of less than 14 (e.g., from 7 to 13 carbons) can also (or alternatively) function as emulsifiers, allowing the composition to be dissolved, suspended, or dispersed in a solvent.
Accordingly, in a first aspect, a composition can include from about 50% to about 99.9% by mass of one or more first compounds selected from the group consisting of fatty acids, fatty acid esters, fatty acid salts, and combinations thereof, wherein each of the one or more first compounds has a carbon chain length of at least 14. The composition can further include from about 0.1% to about 35% by mass of one or more second compounds selected from the group consisting of fatty acids, fatty acid esters, fatty acid salts, and combinations thereof, wherein each of the one or more second compounds has a carbon chain length in a range of 7 to 13.
Any of the compositions or mixtures described herein can include one or more of the following features, either alone or in combination. The second compounds or wetting agents can have a carbon chain length of 8, 10, 11, or 12. Any of the compounds of the composition can be compounds of Formula I. The cationic moiety can be an organic or an inorganic ion. The cationic moiety can include sodium. Each of the one or more second compounds can be a wetting agent. The one or more first compounds can include monoacylglycerides and/or fatty acid salts. The fatty acid esters can include monacylglycerides. A mass ratio of the fatty acid esters (e.g., monoacylglycerides) to the fatty acid salts can be in a range of about 2 to 100 or about 2 to 99. Accordingly, a mass ratio of the first group of compounds to the second group of compounds can be in a range of 2 to 99 or 2 to 100. The composition can comprise less than 10% by mass of diglycerides. The composition can comprise less than 10% by mass of triglycerides. Each compound of the first and/or second group of compounds can have a carbon chain length of at least 14. In Formula I, R can -glyceryl. The second group of compounds can comprise SA-Na, PA-Na, MA-Na, SA-K, PA-K, or MA-K. The composition can comprise from 70% to 99% by mass of the first group of compounds and from 1% to 30% by mass of the second group of compounds. The solvent can be water, or can be at least 50% or at least 70% water by volume. A concentration of the composition in the mixture can be in a range of 0.5 to 200 mg/mL.
In another aspect, a mixture (e.g., a solution, suspension, or colloid) can include any of the compositions described herein in a solvent (e.g., dissolved, suspended, or dispersed in a solvent). Any of the mixtures described herein can include one or more of the following features. The solvent can be characterized as having a contact angle of at least about 70 degrees on carnauba wax. The solvent can be water or can be at least 70% water by volume. The solvent can include ethanol. The solvent can include water and ethanol. The mixture can include an antimicrobial agent, which can for example be citric acid. A concentration of the composition in the mixture can be in a range of 0.5 to 200 mg/mL. A concentration of the wetting agents in the mixture can be at least about 0.1 mg/mL.
In another aspect, a method of forming a mixture can include providing a solvent that is characterized as exhibiting a contact angle of at least about 70° (e.g., at least about 75°, at least about 80°, at least about 85°, or at least about 90°) when disposed on the surface of carnauba wax. The method can further include adding a composition to the solvent to form the mixture. The composition can include one or more fatty acids or salts or esters thereof, and/or can include compounds of Formula I, Formula II, and/or Formula III. The resulting mixture is characterized as exhibiting a contact angle less than about 85° (e.g., less than about 80°, less than about 75°, less than about 70°, or less than about 65°) when disposed on carnauba wax. The contact angle of the resulting mixture on carnauba wax can be less than the contact angle of the solvent (prior to the addition of the composition) on carnauba wax. Optionally, at least one of the fatty acids or salts or esters thereof of the composition can have a carbon chain length of 13 or less. Optionally, at least one of the fatty acids or salts or esters thereof of the composition can have a carbon chain length of 14 or greater. Optionally, the solvent can be water or can be at least 70% water by volume.
In another aspect, a method of forming a protective coating over a substrate (e.g., an agricultural product) can include applying a mixture (e.g., a solution, a suspension, or a colloid) to a surface of the substrate, the mixture comprising a composition in a solvent. The method can further include removing the solvent from the surface of the substrate, thereby causing the protective coating to be formed from the composition over the surface of the substrate.
As used herein, the term “alkyl” refers to saturated linear or branched-chain monovalent hydrocarbon radicals, containing the indicated number of carbon atoms. For example, “C1-6 alkyl” refers to saturated linear or branched-chain monovalent hydrocarbon radicals of one to six carbon atoms. Non-limiting examples of alkyl include methyl, ethyl, 1-propyl, isopropyl, 1-butyl, isobutyl, sec-butyl, tert-butyl, 2-methyl-2-propyl, pentyl, neopentyl, and hexyl.
As used herein, “fatty acid derivative” is a hydrocarbon chain comprising an ester, acid, or carboxylate group, collectively referred to as “oxycarbonyl moieties”, bonded to one terminus of the hydrocarbon chain, understood to be the “hydrophilic” end; while the opposite terminus is understood to be the “hydrophobic” end. Fatty acid derivatives include fatty acids, fatty acid esters (such as monoglycerides), and fatty acid salts. In some embodiments, the fatty acid derivatives have a chain length of from C5 to C22 (e.g., from C8 to C20. Fatty acid derivatives include compounds of Formula I, Formula II, Formula III, Formula IA, Formula IA-A, Formula IA-A-i, Formula IA-A-ii, Formula IA-B, and Formula IIA.
As used herein, the term “alkenyl” refers to a linear or branched mono-unsaturated hydrocarbon chain, containing the indicated number of carbon atoms. For example, “C2-6 alkenyl” refers a linear or branched mono unsaturated hydrocarbon chain of two to six carbon atoms. Non-limiting examples of alkenyl include ethenyl, propenyl, butenyl, or pentenyl.
As used herein, the term “alkynyl” refers to a linear or branched hydrocarbon chain containing a triple bond, and containing the indicated number of carbon atoms. For example, “C2-6 alkynyl” refers to a linear or branched hydrocarbon chain having a triple bond and two to six carbon atoms. Non-limiting examples of alkynyl include ethynyl, propynyl, butynyl, or pentynyl.
As used herein, the term “alkoxy” refers to an —O-alkyl radical, wherein the radical is on the oxygen atom. For example, “C1-6 alkoxy” refers to an —O—(C1-6 alkyl) radical, wherein the radical is on the oxygen atom. Examples of alkoxy include methoxy, ethoxy, propoxy, isopropoxy, butoxy and tert-butoxy.
As used herein, the term “cycloalkyl” refers to a saturated or partially saturated cyclic hydrocarbon, containing the indicated number of carbon atoms. For example, “C3-C6 cycloalkyl” refers to a saturated or partially saturated cyclic hydrocarbon having three to six ring carbon atoms. Non-limiting examples of cycloalkyl include cyclopropyl, cyclobutyl, cyclopentyl, and cyclohexyl.
As used herein, the term “heterocycle” refers to a monocyclic nonaromatic ring system containing indicated number of ring atoms (e.g., 3-6 membered heterocycle) having 1-3 heteroatoms, said heteroatoms selected from O, N, or S. Examples of heterocyclyl groups include oxiranyl, piperazinyl, pyrrolidinyl, dioxanyl, morpholinyl, and tetrahydrofuranyl.
As used herein, the term “aryl” refers to a mono-, bi-, tri- or polycyclic hydrocarbon group containing the indicated numbers of carbon atoms, wherein at least one ring in the system is aromatic (e.g., C6 monocyclic, C10 bicyclic, or C14 tricyclic aromatic ring system). Examples of aryl groups include phenyl, naphthyl, tetrahydronaphthyl, and the like.
As used herein, the term “heteroaryl” refers to a mono-, bi-, tri- or polycyclic group having indicated numbers of ring atoms (e.g., 5-6 ring atoms; e.g., 5, 6, 9, 10, or 14 ring atoms); wherein at least one ring in the system is aromatic (but does not have to be a ring which contains a heteroatom, e.g. tetrahydroisoquinolinyl, e.g., tetrahydroquinolinyl), and at least one ring in the system contains one or more heteroatoms independently selected from the group consisting of N, O, and S. Heteroaryl groups can either be unsubstituted or substituted with one or more substituents. Examples of heteroaryl include thienyl, pyridinyl, furyl, oxazolyl, oxadiazolyl, pyrrolyl, imidazolyl, triazolyl, thiodiazolyl, pyrazolyl, isoxazolyl, thiadiazolyl, pyranyl, pyrazinyl, pyrimidinyl, pyridazinyl, triazinyl, thiazolyl benzothienyl, benzoxadiazolyl, benzofuranyl, benzimidazolyl, benzotriazolyl, cinnolinyl, indazolyl, indolyl, isoquinolinyl, isothiazolyl, naphthyridinyl, purinyl, thienopyridinyl, pyrido[2,3-d]pyrimidinyl, pyrrolo[2,3-b]pyridinyl, quinazolinyl, quinolinyl, thieno[2,3-c]pyridinyl, pyrazolo[3,4-b]pyridinyl, pyrazolo[3,4-c]pyridinyl, pyrazolo[4,3-c]pyridine, pyrazolo[4,3-b]pyridinyl, tetrazolyl, chromane, 2,3-dihydrobenzo[b][1,4]dioxine, benzo[d][1,3]dioxole, 2,3-dihydrobenzofuran, tetrahydroquinoline, 2,3-dihydrobenzo[b][1,4]oxathiine, isoindoline, and others.
As used herein, the term “cycloalkenyl” means a monocyclic nonaromatic ring containing 3-6 carbon ring members and at least one double bond. Examples of cycloalkenyl groups include cyclohexenyl and cyclopentenyl.
As used herein, the term “halo” or “halogen” means fluoro, chloro, bromo, or iodo.
As used herein, the term “plant matter” refers to any portion of a plant, including, for example, fruits (in the botanical sense, including fruit peels and juice sacs), vegetables, leaves, stems, barks, seeds, flowers, peels, or roots. Plant matter includes pre-harvest plants or portions thereof as well as post-harvest plants or portions thereof, including, e.g., harvested fruits and vegetables, harvested roots and berries, and picked flowers.
As used herein, a “coating agent” refers to a composition including a compound or group of compounds from which a protective coating can be formed.
As used herein, “glyceryl” refers to a propyl radical substituted with a hydroxyl at each of the two carbon atoms that the radical is not centered on. In some embodiments, a glyceryl is 1-glyceryl (i.e., —CH2CH(OH)CH2OH). In some embodiments, a glyceryl is 2-glyceryl (i.e., —CH(CH2OH)CH2OH).
As used herein, the “mass loss rate” refers to the rate at which the product loses mass (e.g. by releasing water and other volatile compounds). The mass loss rate is typically expressed as a percentage of the original mass per unit time (e.g. percent per day).
As used herein, the term “mass loss factor” is defined as the ratio of the average mass loss rate of uncoated produce (measured for a control group) to the average mass loss rate of the corresponding tested produce (e.g., coated produce) over a given time. Hence a larger mass loss factor for a coated produce corresponds to a greater reduction in average mass loss rate for the coated produce.
As used herein, the term “respiration rate” refers to the rate at which the product releases gas, such as CO2. This rate can be determined from the volume of gas (e.g., CO2) (at standard temperature and pressure) released per unit time per unit mass of the product. The respiration rate can be expressed as ml gas/kg hour. The respiration rate of the product can be measured by placing the product in a closed container of known volume that is equipped with a sensor, such as a CO2 sensor, recording the gas concentration within the container as a function of time, and then calculating the rate of gas release required to obtain the measured concentration values.
As used herein, the term “respiration factor” is defined as the ratio of the average gas diffusion (e.g., CO2 release) of uncoated produce (measured for a control group) to the average gas diffusion of the corresponding tested produce (e.g., coated produce) over a given time.
Hence a larger respiration factor for a coated produce corresponds to a greater reduction in gas diffusion/respiration for the coated produce.
As used herein, the term “contact angle” of a liquid on a solid surface refers to an angle of the outer surface of a droplet of the liquid measured where the liquid-vapor interface meets the liquid-solid interface. For example, as shown in
As used herein, the terms “wetting agent” or “surfactant” each refer to a compound that, when added to a solvent, suspension, colloid, or solution, reduces the difference in surface energy between the solvent/suspension/colloid/solution and a solid surface on which the solvent/suspension/colloid/solution is disposed.
As used herein, the “carbon chain length” of a fatty acid or salt or ester thereof refers to the number of carbon atoms in the chain including the carbonyl carbon.
As used herein, a “long chain fatty acid”, a “long chain fatty acid ester”, or a “long chain fatty acid salt” refers to a fatty acid or ester or salt thereof, respectively, for which the carbon chain length is greater than 13 (i.e., is at least 14).
As used herein, a “medium chain fatty acid”, a “medium chain fatty acid ester”, or a “medium chain fatty acid salt” refers to a fatty acid or ester or salt thereof, respectively, for which the carbon chain length is in a range of 7 to 13 (inclusive of 7 and 13).
As used herein, a “cationic counter ion” is any organic or inorganic positively charged ion associated with a negatively charged ion. Examples of a cationic counter ion include, for example, sodium, potassium, calcium, and magnesium.
As used herein, a “cationic moiety” is any organic or inorganic positively charged ion.
The following abbreviations are used throughout. Hexadecanoic acid (i.e., palmitic acid) is abbreviated to “PA”. Octadecanoic acid (i.e., stearic acid) is abbreviated to “SA”. Tetradecanoic acid (i.e., myristic acid) is abbreviated to “MA”. (9Z)-Octadecenoic acid (i.e., oleic acid) is abbreviated to “OA”. Dodecanoic acid (e.g., lauric acid) is abbreviated to “LA”. Undecanoic acid (e.g., undecylic acid) is abbreviated to “UA”. Decanoic acid (e.g., capric acid) is abbreviated to “CA”. 1,3-dihydroxypropan-2-yl palmitate (i.e., 2-glyceryl palmitate) is abbreviated to “PA-2G”. 1,3-dihydroxypropan-2-yl octadecanoate (i.e., 2-glyceryl stearate) is abbreviated to “SA-2G”. 1,3-dihydroxypropan-2-yl tetradecanoic acid (i.e., 2-glyceryl myristate) is abbreviated to “MA-2G”. 1,3-dihydroxypropan-2-yl (9Z)-octadecenoate (i.e., 2-glyceryl oleate) is abbreviated to “OA-2G”. 2,3-dihydroxypropyl icosanoate is abbreviated to “IA-1G”. 2,3-dihydroxypropan-1-yl palmitate (i.e., 1-glyceryl palmitate) is abbreviated to “PA-1G”. 2,3-dihydroxypropan-1-yl octadecanoate (i.e., 1-glyceryl stearate) is abbreviated to “SA-1G”. 2,3-dihydroxypropan-1-yl tetradecanoate (i.e., 1-glyceryl myristate) is abbreviated to “MA-1G”. 2,3-dihydroxypropan-1-yl (9Z)-octadecenoate (i.e., 1-glyceryl oleate) is abbreviated to “OA-1G”. 2,3-dihydroxypropan-1-yl dodecanoate (i.e., 1-glyceryl laurate) is abbreviated to “LA-1G”. 2,3-dihydroxypropan-1-yl undecanoate (i.e., 1-glyceryl undecanoate) is abbreviated to “UA-1G”. 2,3-dihydroxypropan-1-yl decanoate (i.e., 1-glyceryl caprate) is abbreviated to “CA-1G”. Sodium salt of stearic acid is abbreviated to “SA-Na”. Sodium salt of myristic acid is abbreviated to “MA-Na”. Sodium salt of palmitic acid is abbreviated to “PA-Na”. Sodium salt of myristic acid is abbreviated to “MA-Na”. Sodium salt of lauric acid is abbreviated to “LA-Na”. Sodium salt of capric acid is abbreviated to “CA-Na”. Potassium salt of stearic acid is abbreviated to “SA-K”. Potassium salt of myristic acid is abbreviated to “MA-K”. Potassium salt of palmitic acid is abbreviated to “PA-K”. Calcium salt of stearic acid is abbreviated to “(SA)2-Ca”. Calcium salt of myristic acid is abbreviated to “(MA)2-Ca”. Calcium salt of palmitic acid is abbreviated to “(PA)2-Ca”. Magnesium salt of stearic acid is abbreviated to “(SA)2-Mg”. Magnesium salt of myristic acid is abbreviated to “(MA)2-Mg”. Magnesium salt of palmitic acid is abbreviated to “(PA)2-Mg”.
“Substituted” or “substituent”, as used herein, means an atom or group of atoms is replaced with another atom or group of atoms. Exemplary substituents include, but are not limited to, halogen, hydroxyl, nitro, cyano, alkyl, alkenyl, alkynyl, cycloalkyl, cycloalkenyl, formyl, acyl, ether, ester, keto, aryl, heteroaryl, etc.
As used herein, “lamellar structure” refers to a structure comprising one or more lamellae vertically stacked adjacent to each other and held together by intermolecular forces. As used herein, “lamella” or “lamellae” refer to a discrete layer of molecules arranged in a lattice formation. The distance between a surface of a lamella and the surface of an adjacent lamella that is facing the same direction is referred to herein as “interlayer spacing” or “periodic spacing”.
d=2π/qpeak
In some embodiments, a lamella is a “lipid bilayer”, which includes two contiguous sublayers, wherein each sublayer comprises molecules of fatty acid derivatives aligned adjacent to each other lengthwise such that the hydrophilic ends form a hydrophilic surface and the hydrophobic ends form a hydrophobic surface; and the molecular arrangement defines a repeating lattice structure. The hydrophobic surfaces of each sublayer in the lipid bilayer face each other, and the hydrophilic surfaces of each layer face away from each other. For purposes of illustration,
As used herein, “grain” refers to a domain within a lamellar structure wherein the lattice formation is continuous and has one orientation. The boundaries between the grains in a lamellar structure are defects in the lattice formation wherein the continuity of the lattice formation and/or orientation of the molecules forming the lattice formation are interrupted. For purposes of illustration,
D=2πb/FWHM
wherein b=about 0.95 for a 2-dimensional crystal.
Without being bound by any theory, grain size inversely correlates with grain boundaries. As such, the larger the grain size, the fewer the grain boundaries; and the smaller the grain size, the more grain boundaries there are. It is further understood that the fewer the grain boundaries in a coating, the lower the mass loss rate and/or respiration rate of the coated agricultural product since there are fewer pathways for water and/or gas to pass through the coating.
As used herein, “mosaicity” refers to the probabilities that the orientation of lamellae in a coating deviate from a plane that is substantially parallel with the plane of the substrate (e.g., agricultural product) surface. Deviation of a lamella from a plane that is substantially parallel with the plane of the substrate surface is understood to be a type of crystal defect that increases the permeability of a coating to air and water, thus increasing the mass loss rate and respiration rate when the coating is disposed over an agricultural product.
As used herein, “substrate” refers to an article that a coating is applied to. In some embodiments, the substrate is an agricultural product (e.g., produce), a silicon substrate, or a substrate comprising a polysaccharide (e.g., cellulose).
Protective Coatings
Described herein are solutions, suspensions, or colloids containing a composition (e.g., a coating agent) in a solvent that can be used to form protective coatings over substrates such as plant matter, agricultural products, or food products. The protective coatings can, for example, prevent or reduce water loss and gas diffusion from the substrates, oxidation of the substrates, and/or can shield the substrates from threats such as bacteria, fungi, viruses, and the like. The coatings can also protect the substrates from physical damage (e.g., bruising) and photodamage. Accordingly, the coating agents, solutions/suspensions/colloids, and the coatings formed thereof can be used to help store agricultural or other food products for extended periods of time without spoiling. In some instances, the coatings and the coating agents from which they are formed can allow for food to be kept fresh in the absence of refrigeration. The coating agents and coatings described herein can also be edible (i.e., the coating agents and coatings can be non-toxic for human consumption). In some particular implementations, the solutions/suspensions/colloids include a wetting agent or surfactant which cause the solution/suspension/colloid to better spread over the entire surface of the substrate during application, thereby improving surface coverage as well as overall performance of the resulting coating. In some particular implementations, the solutions/suspensions/colloids include an emulsifier which improves the solubility of the coating agent in the solvent and/or allows the coating agent to be suspended or dispersed in the solvent. The wetting agent and/or emulsifier can each be a component of the coating agent, or can be separately added to the solution/suspension/colloid. In some embodiments, the coatings are understood to form lamellar structures on the surface of the substrate (e.g., agricultural product) they are disposed over.
Plant matter (e.g., agricultural products) and other degradable items can be protected against degradation from biotic or abiotic stressors by forming a protective coating over the outer surface of the product. The coating can be formed by adding the constituents of the coating (herein collectively a “coating agent”) to a solvent (e.g., water and/or ethanol) to form a mixture (e.g., a solution, suspension, or colloid), applying the mixture to the outer surface of the product to be coated, e.g., by dipping the product in the mixture or by spraying the mixture over the surface of the product, and then removing the solvent from the surface of the product, e.g., by allowing the solvent to evaporate, thereby causing the coating to be formed from the coating agent over the surface of the product. The coating agent can be formulated such that the resulting coating provides a barrier to water and/or oxygen transfer, thereby preventing water loss from and/or oxidation of the coated product. The coating agent can additionally or alternatively be formulated such that the resulting coating provides a barrier to CO2, ethylene and/or other gas transfer.
Coating agents including long chain fatty acids (e.g., palmitic acid, stearic acid, myristic acid, and/or other fatty acids having a carbon chain length greater than 13) and/or esters or salts thereof can both be safe for human consumption and can be used as coating agents to form coatings that are effective at reducing mass loss and oxidation in a variety of produce. For example, coatings formed from coating agents that include various combinations of palmitic acid, myristic acid, stearic acid, 1-glyceryl esters of palmitic acid (i.e., 2,3-dihydroxypropan-1-yl palmitate, herein “PA-1G”), 2-glyceryl esters of palmitic acid (i.e., 1,3-dihydroxypropan-2-yl palmitate, herein “PA-2G”), 1-glyceryl esters of myristic acid (i.e., 2,3-dihydroxypropan-1-yl tetradecanoate, herein “MA-1G”), 1-glyceryl esters of stearic acid (i.e., 2,3-dihydroxypropan-1-yl octadecenoate, herein “SA-1G”), and/or other long chain fatty acids or salts or esters thereof have been shown to be effective at reducing mass loss rates in many types of produce, for example finger limes, avocados, blueberries, and lemons. Specific examples of a variety of coatings and their effects in reducing mass loss rates in various types of produce are provided in Examples 1-4 below.
Medium chain fatty acids (e.g., having a carbon chain length in a range of 7 to 13) and/or salts or esters thereof can also be used as coating agents to form coatings over produce or other plant matter or agricultural products using the methods described above. However, these compounds have typically been found to cause damage to the produce or plant matter, and also typically result in minimal to no reduction in mass loss rates. For example, treating avocados with a solution of 1-glyceryl esters of undecanoic acid (i.e., 2,3-dihydroxypropan-1-yl undecanoate, herein “UA-1G”) suspended in water at a concentration as low as 5 mg/mL (UA-1G has a carbon chain length of 11) was shown to cause the avocados' skins to change from being virtually entirely green to having a high density of black discolored regions as a result of skin damage caused by the UA-1G. As seen in
Coating and Coating Agent Compositions
In some embodiments, the compositions (e.g., the coating agents or coatings) herein are derived from cutin obtained from a plant cuticle. In some embodiments, the plant that the cutin is obtained from is selected from palm, rapeseed, grapeseed, pumpkin, and coconut.
In some embodiments, the compositions (e.g., the coating agents or coatings) comprise one or more fatty acid derivatives. In some embodiments, the one or more fatty acid derivatives comprise one or more fatty acids, fatty acid esters, or a combination thereof. In some embodiments, the one or more fatty acid derivatives comprise one or more fatty acid salts. In some embodiments, the one or more fatty acid derivatives comprise two or more fatty acids, fatty acid esters, or a combination thereof. In some embodiments, the one or more fatty acid derivatives comprise two or more fatty acid salts. In some embodiments, the one or more fatty acid derivatives comprise one or more fatty acids, fatty acid esters, or a combination thereof and one or more fatty acid salts. In some embodiments, the one or more fatty acid derivatives comprise two or more fatty acids, fatty acid esters, or a combination thereof and two or more fatty acid salts. In some embodiments, the one or more fatty acid derivatives comprise one fatty acid or ester thereof and one fatty acid salt. In some embodiments, the one or more fatty acid derivatives comprise one fatty acid thereof and one fatty acid salt. In some embodiments, the one or more fatty acid derivatives comprise one fatty acid ester and one fatty acid salt. In some embodiments, the one or more fatty acid derivatives comprise two fatty acids, fatty acid esters, or a combination thereof and two fatty acid salts. In some embodiments, the one or more fatty acid derivatives comprise two fatty acid esters and two fatty acid salts. In some embodiments, the one or more fatty acid derivatives comprise two fatty acid esters and one fatty acid salt. In some embodiments, the one or more fatty acid derivatives comprise one fatty acid ester, one fatty acid, and one fatty acid salts. In some embodiments, the one or more fatty acid derivatives comprise one fatty acid ester and one fatty acid salt.
In some embodiments, the one or more fatty acids, fatty acid esters, or a combination thereof comprise one or more fatty acid esters. In some embodiments, the one or more fatty acid esters is one fatty acid ester. In some embodiments, the one or more fatty acid esters is two fatty acid esters.
In some embodiments, the one or more fatty acid salts is one fatty acid salt. In some embodiments, the one or more fatty acid salts is two fatty acid salts.
In some embodiments, the one or more fatty acids, fatty acid esters, or a combination thereof comprise one monoglyceride (e.g., a 1-monoglyceride or a 2-monoglyceride). In some embodiments, the one or more fatty acids, fatty acid esters, or a combination thereof comprise two monoglycerides (e.g., two 1-monoglycerides, two 2-monoglycerides, or one 1-monoglyceride and one 2-monoglyceride).
In some embodiments, the composition (e.g., coating or coating agent) comprises from about 40% to about 100% by weight of the one or more fatty acids, fatty acid esters, or a combination thereof. For example, the composition comprises from about 40% to about 45%, from about 45% to about 50%, from about 50% to about 55%, from about 55% to about 60%, from about 60% to about 65%, from about 65% to about 70%, from about 70% to about 75%, from about 75% to about 80%, from about 80% to about 85%, from about 85% to about 90%, from about 90% to about 95%, from about 95% to about 100%, from about 40% to about 50%, from about 50% to about 60%, from about 60% to about 70%, from about 70% to about 80%, from about 80% to about 90%, from about 65% to about 99%, from about 90% to about 100%, from about 40% to about 60%, from about 60% to about 80%, from about 80% to about 100%, from about 60% to about 100%, from about 70% to about 100%, from about 40% to about 99%, from about 60% to about 99%, from about 70% to about 99%, from about 80% to about 99%, from about 85% to about 99%, from about 90% to about 99%, from about 92% to about 98%, from about 92% to about 96%, from about 93% to about 95%, from about 62% to about 78%, from about 65% to about 75%, from about 67% to about 73%, from about 69% to about 71%, about 68%, about 69%, about 70%, about 71%, about 72%, about 92%, about 93%, about 94%, about 95%, about 96%, about 97%, about 98%, or about 99% by weight of the one or more fatty acids, fatty acid esters, or a combination thereof. For example, the composition comprises from about 60% to about 80%, about 70%, from about 85% to about 99%, about 95%, or about 96% by weight of the one or more fatty acids, fatty acid esters, or a combination thereof.
In some embodiments, the composition (e.g., coating or coating agent) comprises from about 1% to about 50% by weight of the one or more fatty acid salts. For example, the composition comprises from about 1% to about 10%, from about 10% to about 20%, from about 20% to about 30%, from about 30% to about 40%, from about 40% to about 50%, from about 1% to about 40%, from about 1% to about 35%, from about 1% to about 30%, from about 1% to about 20%, from about 10% to about 50%, from about 20% to about 40%, from about 15% to about 45%, from about 25% to about 35%, from about 28% to about 32%, from about 1% to about 10%, from about 2% to about 10%, from about 3% to about 9%, from about 4% to about 8%, from about 4% to about 6%, about 3%, about 4%, about 5%, about 6%, about 7%, about 8%, about 29%, about 30%, or about 31% by weight of the one or more fatty acid salts. In some embodiments, when the composition comprises two fatty acid salts, the molar ratio or weight ratio of the two fatty acid salts is from about 1:20 to about 20:1. For example, from about 1:10 to about 10:1, from about 1:10 to about 2:1, from about 1:4 to about 1:2, from about 1:3 to about 3:1, from about 1:2 to about 2:1, or about 1:1.
In some embodiments, the composition (e.g., coating or coating agent) comprises from about 70% to about 99% by weight of the one or more fatty acids, fatty acid esters, or a combination thereof; and from about 1% to about 30% by weight of the one or more fatty acid salts. In some embodiments, the composition (e.g., coating or coating agent) comprises from about 70% to about 99% by weight of one fatty acid ester; and from about 1% to about 30% by weight of one fatty acid salt. In some embodiments, the composition (e.g., coating or coating agent) comprises from about 70% to about 99% by weight of two fatty acid esters; and from about 1% to about 30% by weight of one fatty acid salt. In some embodiments, the composition (e.g., coating or coating agent) comprises from about 70% to about 99% by weight of one fatty acid ester; and from about 1% to about 30% by weight of two fatty acid salts. In some embodiments, the composition (e.g., coating or coating agent) comprises from about 70% to about 99% by weight of two fatty acid esters; and from about 1% to about 30% by weight of two fatty acid salts. In some embodiments, the composition (e.g., coating or coating agent) comprises one fatty acid ester and one fatty acid salt in a weight ratio of about 70:30 to about 94:6 (e.g., about 70:30 or about 94:6). In some embodiments, the composition (e.g., coating or coating agent) comprises two fatty acid esters and one fatty acid salt in a weight ratio of about 70:30 to about 94:6 (e.g., about 70:30 or about 94:6). In some embodiments, the composition (e.g., coating or coating agent) comprises one fatty acid ester and two fatty acid salts in a weight ratio of about 70:30 to about 94:6 (e.g., about 70:30 or about 94:6). In some embodiments, the composition (e.g., coating or coating agent) comprises two fatty acid esters and two fatty acid salts in a weight ratio of about 70:30 to about 94:6 (e.g., about 70:30 or about 94:6).
In some embodiments, each fatty acid and/or ester thereof is an independently selected compound of Formula IA:
wherein:
R is selected from the group consisting of H and C1-C6 alkyl optionally substituted with one or more of OH and C1-C6 alkoxy;
R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of:
H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
each occurrence of R10A, R10B, R11A, and R11B is independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
or any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a double bond, a 3- to 6-membered ring heterocycle, or a C3-C6 cycloalkyl; and
o is an integer from 0 to 17;
p is an integer from 0 to 17;
wherein the sum of o and p is from 0 to 17;
or a salt thereof when R is C1-C6 alkyl optionally substituted with one or more of OH and C1-C6 alkoxy.
In some embodiments, R is H.
In some embodiments, R is C1-C6 alkyl optionally substituted with one or more OH or C1-C6 alkoxy. In some embodiments, R is C1-C6 alkyl optionally substituted with one or more OH. In some embodiments, R is C1-C6 alkyl optionally substituted with two OH. In some embodiments, R is C1-C3 alkyl optionally substituted with one or more OH. In some embodiments, R is C1-C3 alkyl optionally substituted with two OH. In some embodiments, R is propyl optionally substituted with one or more OH. In some embodiments, R is propyl optionally substituted with two OH. In some embodiments, R is 1,3-dihydroxy-2-propyl. In some embodiments, R is 1,2-dihydroxy-1-propyl.
In some embodiments, R is C1-C6 alkyl optionally substituted with one or more C1-C6 alkoxy. In some embodiments, R is C1-C6 alkyl optionally substituted with two C1-C6 alkoxy. In some embodiments, R is C1-C3 alkyl optionally substituted with one or more C1-C6 alkoxy. In some embodiments, R is C1-C3 alkyl optionally substituted with two C1-C6 alkoxy.
In some embodiments, the compound of Formula IA is a compound of Formula IA-A:
In some embodiments, RB1 is H and RB2 is —CH2ORA.
In some embodiments, RB1 is —CH2ORA and RB2 is H.
In some embodiments, each RA is H. In some embodiments, one RA is H and the other RA is C1-C6 alkyl. In some embodiments, each RA is C1-C6 alkyl. In some embodiments, each RA is C1-C6 alkyl.
In some embodiments, the compound of Formula IA-A is a compound of Formula IA-A-i:
In some embodiments, RA1 is H and RA2 is C1-C6 alkyl. In some embodiments, RA1 is C1-C6 alkyl and RA2 is H. In some embodiments, RA1 and RA2 are H.
In some embodiments, the compound of Formula IA-A is a compound of Formula IA-A-ii:
In some embodiments, RA1 is H and RA3 is C1-C6 alkyl. In some embodiments, RA1 is C1-C6 alkyl and RA3 is H. In some embodiments, RA1 and RA3 are H.
In some embodiments, the compound of Formula IA is a compound of Formula IA-B:
In some embodiments, each fatty acid salt is an independently selected compound of Formula II:
In some embodiments, Xn+ is selected from Na+, K+, Ag+, Ca2+, Mg2+, Zn2+, Cu2+, and (R′)4N+.
In some embodiments, each R′ is an independently selected C1-C6 alkyl. In some embodiments, one R′ is H and the other three R′ are independently selected C1-C6 alkyl. In some embodiments, two R′ are H and the other two R′ are independently selected C1-C6 alkyl.
In some embodiments, three R′ are H and the other R′ is C1-C6 alkyl. In some embodiments, each R′ is H.
In some embodiments, Xn+ is selected from Na+, K+, Ag+, Ca2+, Mg2+, and Zn2+. In some embodiments, Xn+ is selected from Na+, K+, Ca2+, Mg2+, and Zn2+. In some embodiments, Xn+ is Na+. In some embodiments, Xn+ is K+. In some embodiments, Xn+ is Ca2+. In some embodiments, Xn+ is Mg2+. In some embodiments, Xn+ is Zn2+.
In some embodiments, R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of: H, OH, C1-C6 alkyl, and C1-C6 alkoxy. In some embodiments, R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of: H, OH, and C1-C6 alkyl. In some embodiments, R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of: H and OH. In some embodiments, R1, R2, R3, R4, R5, R6, R7, R8, and R9 are each H. In some embodiments, one of R1, R2, R3, R4, R5, R6, R7, R8, and R9 is OH and the remaining R1, R2, R3, R4, R5, R6, R7, R8, and R9 are each H. In some embodiments, two of R1, R2, R3, R4, R5, R6, R7, R8, and R9 is OH and the remaining R1, R2, R3, R4, R5, R6, R7, R8, and R9 are each H.
In some embodiments, R4 is OH. In some embodiments, R5 is OH. In some embodiments, R6 is OH. In some embodiments, R7 is OH.
In some embodiments, each occurrence of R10A, R10B, R11A, and R11B is independently selected from the group consisting of: H, OH, C1-C6 alkyl, and C1-C6 alkoxy. In some embodiments, each occurrence of R10A, R10B, R11A, and R11B is independently selected from the group consisting of: H, OH, and C1-C6 alkyl. In some embodiments, each occurrence of R10A, R10B, R11A, and R11B is independently selected from the group consisting of: H and OH. In some embodiments, each occurrence of R10A, R10B, R11A, and R11B is each H. In some embodiments, one of each occurrence of R10A, R10B, R11A, and R11B is OH and the remaining occurrences of R10A, R10B, R11A, and R11B are each H. In some embodiments, two of each occurrence of R10A, R10B, R11A, and R11B is OH and the remaining occurrences of R10A, R10B, R11A, and R11B are each H.
In some embodiments, any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a double bond. In some embodiments, any two pairs of R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are each taken together with the carbon atoms to which they are attached to form two double bonds. In some embodiments, any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a 3- to 6-membered ring heterocycle. In some embodiments, any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a double bond, and any two remaining R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a 3- to 6-membered ring heterocycle. In some embodiments, the 3- to 6-membered ring heterocycle is oxiranyl.
In some embodiments, R4 is taken together with R6 and the carbon atoms to which they are attached to form a double bond. In some embodiments, R4 is taken together with R6 and the carbon atoms to which they are attached to form a 3- to 6-membered ring heterocycle.
In some embodiments, one of R1, R2, R3, R4, R5, R6, R7, R8, R9, and each occurrence of R10A, R10B, R11A, and R11B is OH; and the remaining R1, R2, R3, R4, R5, R6, R7, R8, R9, and each occurrence of R10A, R10B, R11A, and R11B are each H.
In some embodiments, one of R1, R2, R3, R4, R5, R6, R7, R8, R9, and each occurrence of R10A, R10B, R11A, and R11B is OH; any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a double bond; and the remaining R1, R2, R3, R4, R5, R6, R7, R8, R9, and each occurrence of R10A, R10B, R11A, and R11B are each H.
In some embodiments, one of R1, R2, R3, R4, R5, R6, R7, R8, R9, and each occurrence of R10A, R10B, R11A, and R11B is OH; any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a double bond; and the remaining R1, R2, R3, R4, R5, R6, R7, R8, R9, and each occurrence of R10A, R10B, R11A, and R11B are each H.
In some embodiments, one of R1, R2, R3, R4, R5, R6, R7, R8, R9, and each occurrence of R10A, R10B, R11A, and R11B is OH; any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form an oxiranyl; and the remaining R1, R2, R3, R4, R5, R6, R7, R8, R9, and each occurrence of R10A, R10B, R11A, and R11B are each H.
In some embodiments, R1, R2, R3, R4, R5, R6, R7, R8, R9, and each occurrence of R10A, R10B, R11A, and R11B are each H; and any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form an oxiranyl.
In some embodiments, R1, R2, R3, R4, R5, R6, R7, R8, R9, and each occurrence of R10A, R10B, R11A, and R11B are each H; and any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a double bond.
In some embodiments, the sum of o and p is from 0 to 13. In some embodiments, the sum of o and p is from 1 to 9. In some embodiments, the sum of o and p is from 0 to 13. In some embodiments, the sum of o and p is from 5 to 7. In some embodiments, the sum of o and p is from 10 to 13. In some embodiments, the sum of o and p is from 11 to 13. In some embodiments, the sum of o and p is 1. In some embodiments, the sum of o and p is from 10 to 13. In some embodiments, the sum of o and p is 1. In some embodiments, the sum of o and p is 2. In some embodiments, the sum of o and p is 3. In some embodiments, the sum of o and p is 4. In some embodiments, the sum of o and p is 5. In some embodiments, the sum of o and p is 6. In some embodiments, the sum of o and p is 7. In some embodiments, the sum of o and p is 8. In some embodiments, the sum of o and p is 9. In some embodiments, the sum of o and p is 10. In some embodiments, the sum of o and p is 11. In some embodiments, the sum of o and p is 12. In some embodiments, the sum of o and p is 13. In some embodiments, the sum of o and p is 14. In some embodiments, the sum of o and p is 15. In some embodiments, the sum of o and p is 16. In some embodiments, the sum of o and p is 17. Without wishing to be bound by theory, it is believed that compounds of Formula IA-A wherein the sum of o and p is 0 to 9 are able to function as wetting agents when included in the compositions (e.g., mixtures, coatings, and coating agents) described herein, thus increasing the aptitude of the compositions (e.g., mixtures, coatings, and coating agents) to spread over the surface of an agricultural product or plant to form a coating of substantially uniform thickness.
In some embodiments, the compound of Formula IA is selected from the group consisting of:
In some embodiments, the compound of Formula IIA is selected from the group consisting of:
In some embodiments, the composition (e.g., coating or coating agent) comprises one or more (e.g., 1, 2, or 3) compounds of Formula IA. In some embodiments, the composition comprises one or more (e.g., 1, 2, or 3) compounds of Formula IA-A. In some embodiments, the composition comprises one or more (e.g., 1, 2, or 3) compounds of Formula IA-A-i. In some embodiments, the composition comprises one or more (e.g., 1, 2, or 3) compounds of Formula IA-A-ii. In some embodiments, the composition comprises one or more (e.g., 1, 2, or 3) compounds of Formula IA-B. In some embodiments, the composition comprises one or more (e.g., 1, 2, or 3) compounds of Formula IIA.
In some embodiments, each compound of Formula IA is a compound of Formula IA-A. In some embodiments, each compound of Formula IA-A is independently selected from a compound of Formula IA-A-i and a compound of Formula IA-A-ii. In some embodiments, each compound of Formula IA-A is a compound of Formula IA-A-i. In some embodiments, each compound of Formula IA-A is a compound of Formula IA-A-ii. In some embodiments, at least one (e.g., 1 or 2) compounds of Formula IA-A is a compound of Formula IA-A-i and at least one (e.g., 1 or 2) compounds of Formula IA-A is a compound of Formula IA-A-ii.
In some embodiments, the composition (e.g., coating or coating agent) comprises one compound of Formula IA-A and one compound of Formula IA-B. In some embodiments, the composition comprises one compound of Formula IA-A-i and one compound of Formula IA-B. In some embodiments, the composition comprises one compound of Formula IA-A-ii and one compound of Formula IA-B. In some embodiments, the composition comprises one compound of Formula IA-A-i, one compound of Formula IA-A-ii, and one compound of Formula IA-B.
In some embodiments, the composition (e.g., coating or coating agent) comprises one compound of Formula IA-A-i and one compound of Formula IA-A-ii. In some embodiments, the composition comprises two compounds of Formula IA-A-i. In some embodiments, the composition comprises two compounds of Formula IA-A-ii.
In some embodiments, the composition (e.g., coating or coating agent) comprises one or more (e.g., 1, 2, or 3) compounds of Formula IA and one or more (e.g., 1, 2, or 3) compounds of Formula IIA. In some embodiments, the composition comprises one compound of Formula IA and one compound of Formula IIA. In some embodiments, the composition comprises two compounds of Formula IA and one compound of Formula IIA. In some embodiments, the composition comprises one compound of Formula IA and two compounds of Formula IIA. In some embodiments, the composition comprises two compounds of Formula IA and two compounds of Formula IIA.
In some embodiments, the composition (e.g., coating or coating agent) comprises one or more (e.g., 1, 2, or 3) compounds of Formula IA-A and one or more (e.g., 1, 2, or 3) compounds of Formula IIA. In some embodiments, the composition comprises one compound of Formula IA-A and one compound of Formula IIA. In some embodiments, the composition comprises two compounds of Formula IA-A and one compound of Formula IIA. In some embodiments, the composition comprises one compound of Formula IA-A and two compounds of Formula IIA. In some embodiments, the composition comprises two compounds of Formula IA-A and two compounds of Formula IIA.
In some embodiments, the composition (e.g., coating or coating agent) comprises one or more (e.g., 1, 2, or 3) compounds of Formula IA-A-i and one or more (e.g., 1, 2, or 3) compounds of Formula IIA. In some embodiments, the composition comprises one compound of Formula IA-A-i and one compound of Formula IIA. In some embodiments, the composition comprises two compounds of Formula IA-A-i and one compound of Formula IIA. In some embodiments, the composition comprises one compound of Formula IA-A-i and two compounds of Formula IIA. In some embodiments, the composition comprises two compounds of Formula IA-A-i and two compounds of Formula IIA.
In some embodiments, the composition (e.g., coating or coating agent) comprises a first compound of Formula IA-A-i wherein the sum of o and p is from 9 to 17 (e.g., from 11 to 13 (e.g., 13)); a second compound of Formula IA-A-i wherein the sum of o and p is from 0 to 8 (e.g., from 5 to 7 (e.g., 7)); and one compound of Formula IIA. In some embodiments, the composition comprises a first compound of Formula IA-A-i wherein the sum of o and p is from 9 to 17 (e.g., from 11 to 13); a second compound of Formula IA-A-i wherein the sum of o and p is from 0 to 8 (e.g., from 5 to 7); and two compounds of Formula IIA.
In some embodiments, the composition (e.g., coating or coating agent) comprises a first compound of Formula IA-A-i wherein the sum of o and p is from 9 to 17 (e.g., from 11 to 13 (e.g., 13)); a second compound of Formula IA-A-i wherein the sum of o and p is from 9 to 17 (e.g., from 11 to 13 (e.g., 11)); and one compound of Formula IIA. In some embodiments, the composition comprises a first compound of Formula IA-A-i wherein the sum of o and p is from 9 to 17 (e.g., from 11 to 13); a second compound of Formula IA-A-i wherein the sum of o and p is from 9 to 17 (e.g., from 11 to 13); and two compounds of Formula IIA.
In some embodiments, the composition (e.g., coating or coating agent) comprises one or more (e.g., 1, 2, or 3) compounds of Formula IA-A-ii and one or more (e.g., 1, 2, or 3) compounds of Formula IIA. In some embodiments, the composition comprises one compound of Formula IA-A-ii and one compound of Formula IIA. In some embodiments, the composition comprises two compounds of Formula IA-A-ii and one compound of Formula IIA. In some embodiments, the composition comprises one compound of Formula IA-A-ii and two compounds of Formula IIA. In some embodiments, the composition comprises two compounds of Formula IA-A-ii and two compounds of Formula IIA.
In some embodiments, the composition (e.g., coating or coating agent) comprises one or more (e.g., 1, 2, or 3) compounds of Formula IA-A-i, one or more (e.g., 1, 2, or 3) compounds of Formula IA-A-ii, and one or more (e.g., 1, 2, or 3) compounds of Formula IIA. In some embodiments, the composition comprises one compound of Formula IA-A-i, one compound of Formula IA-A-ii, and one compound of Formula IIA. In some embodiments, the composition comprises two compounds of Formula IA-A-i, one compound of Formula IA-A-ii, and one compound of Formula IIA. In some embodiments, the composition comprises one compound of Formula IA-A-i, two compounds of Formula IA-A-ii, and one compound of Formula IIA. In some embodiments, the composition comprises two compounds of Formula IA-A-i, two compounds of Formula IA-A-ii, and one compound of Formula IIA. In some embodiments, the composition comprises one compound of Formula IA-A-i, one compound of Formula IA-A-ii, and two compounds of Formula IIA. In some embodiments, the composition comprises two compounds of Formula IA-A-i, one compound of Formula IA-A-ii, and two compounds of Formula IIA. In some embodiments, the composition comprises one compound of Formula IA-A-i, two compounds of Formula IA-A-ii, and two compounds of Formula IIA. In some embodiments, the composition comprises two compounds of Formula IA-A-i, two compounds of Formula IA-A-ii, and two compounds of Formula IIA.
In some embodiments, when the composition (e.g., coating or coating agent) comprises two or more compounds of Formula IA, Formula IA-A, Formula IA-A-i, Formula IA-A-ii, Formula IA-B, and/or Formula IIA, the weight ratio of the two compounds is from about 1:1 to about 10:1. For example, from about 1:1 to about 8:1, from about 1:1 to about 6:1, from about 1:1 to about 4:1, from about 1:1 to about 3:1, from about 1:1 to about 2:1, from about 2:1 to about 4:1, from about 4:1 to about 6:1, from about 6:1 to about 8:1, from about 8:1 to about 10:1, about 1:1, about 1:2, about 1:4, about 1:6, about 1:8, or about 1:10.
In some embodiments, when the composition (e.g., coating or coating agent) comprises two or more compounds of Formula IA, Formula IA-A, Formula IA-A-i, Formula IA-A-ii, Formula IA-B, and/or Formula IIA, the sum of o and p of at least two compounds is different. In some embodiments, when the composition comprises two or more compounds of Formula IA, Formula IA-A, Formula IA-A-i, Formula IA-A-ii, Formula IA-B, and/or Formula IIA, the sum of o and p of at least two compounds is the same.
In some embodiments, the composition (e.g., coating or coating agent) comprises from about 40% to about 100% by weight of the one or more compounds of Formula IA, Formula IA-A, Formula IA-A-i, Formula IA-A-ii, and Formula IA-B. For example, the composition comprises from about 40% to about 45%, from about 45% to about 50%, from about 50% to about 55%, from about 55% to about 60%, from about 60% to about 65%, from about 65% to about 70%, from about 65% to about 99%, from about 70% to about 75%, from about 75% to about 80%, from about 80% to about 85%, from about 85% to about 90%, from about 90% to about 95%, from about 95% to about 100%, from about 40% to about 50%, from about 50% to about 60%, from about 60% to about 70%, from about 70% to about 80%, from about 80% to about 90%, from about 90% to about 100%, from about 40% to about 60%, from about 60% to about 80%, from about 80% to about 100%, from about 60% to about 100%, from about 70% to about 100%, from about 40% to about 99%, from about 60% to about 99%, from about 70% to about 99%, from about 80% to about 99%, from about 85% to about 99%, from about 90% to about 99%, from about 92% to about 98%, from about 92% to about 96%, from about 93% to about 95%, from about 62% to about 78%, from about 65% to about 75%, from about 67% to about 73%, from about 69% to about 71%, about 68%, about 69%, about 70%, about 71%, about 72%, about 92%, about 93%, about 94%, about 95%, about 96%, about 97%, about 98%, or about 99% by weight of the one or more compounds of Formula IA, Formula IA-A, Formula IA-A-i, Formula IA-A-ii, and Formula IA-B. For example, the composition comprises from about 60% to about 80%, about 70%, from about 85% to about 99%, about 95%, or about 96% by weight of the one or more compounds of Formula IA, Formula IA-A, Formula IA-A-i, Formula IA-A-ii, and Formula IA-B.
In some embodiments, when the composition (e.g., coating or coating agent) comprises two compounds of Formula IA, Formula IA-A, Formula IA-A-i, Formula IA-A-ii, and/or Formula IA-B (for example, two compounds of Formula IA-A-i, two compounds of Formula IA-A-ii, or one compound of Formula IA-A-i and one compound of Formula IA-A-ii), each compound is independently from about 0.1% to about 99% by weight of the composition. For example, one compound is from about 20% to about 70%, from about 60% to about 99%, from about 70% to about 99%, from about 80% to about 95%, 20% to about 25%, from about 25% to about 30%, from about 30% to about 35%, from about 35% to about 40%, from about 40% to about 45%, from about 45% to about 50%, from about 50% to about 55%, from about 55% to about 60%, from about 60% to about 65%, from about 65% to about 70%, from about 20% to about 30%, from about 30% to about 40%, from about 40% to about 50%, from about 50% to about 60%, from about 60% to about 70%, from about 20% to about 40%, from about 40% to about 60%, from about 20% to about 50%, from about 25% to about 45%, from about 30% to about 40%, from about 32% to about 38%, from about 33% to about 63%, from about 38% to about 58%, from about 43% to about 53%, from about 45% to about 51%, from about 0.1% to about 5%, from about 0.1% to about 3%, from about 0.1 to about 34%, about 35%, about 36%, about 47%, about 48%, or about 49% by weight of the composition; and the other compound is from about 20% to about 70%, from about 60% to about 99%, from about 70% to about 99%, from about 80% to about 95%, 20% to about 25%, from about 25% to about 30%, from about 30% to about 35%, from about 35% to about 40%, from about 40% to about 45%, from about 45% to about 50%, from about 50% to about 55%, from about 55% to about 60%, from about 60% to about 65%, from about 65% to about 70%, from about 20% to about 30%, from about 30% to about 40%, from about 40% to about 50%, from about 50% to about 60%, from about 60% to about 70%, from about 20% to about 40%, from about 40% to about 60%, from about 20% to about 50%, from about 25% to about 45%, from about 30% to about 40%, from about 32% to about 38%, from about 33% to about 63%, from about 38% to about 58%, from about 43% to about 53%, from about 45% to about 51%, from about 0.1% to about 5%, from about 0.1% to about 3%, from about 0.1 to about 34%, about 35%, about 36%, about 47%, about 48%, or about 49% by weight of the composition. In some embodiments, when the composition comprises two compounds of Formula IA, Formula IA-A, Formula IA-A-i, Formula IA-A-ii, and/or Formula IA-B (for example, two compounds of Formula IA-A-i, two compounds of Formula IA-A-ii, or one compound of Formula IA-A-i and one compound of Formula IA-A-ii), the molar ratio or weight ratio of the two compounds is from about 350:1 to about 1:10. For example, from about 330:1 to about 50:1, from about 50:1 to about 10:1, from about 10:1 to about 1:1, from about 1:1 to about 8:1, from about 1:1 to about 6:1, from about 1:1 to about 4:1, from about 1:1 to about 3:1, from about 1:1 to about 2:1, from about 2:1 to about 4:1, from about 4:1 to about 6:1, from about 6:1 to about 8:1, from about 8:1 to about 10:1, from about 10:1 to about 2:1, from about 3:1 to about 1:3, about 316:1, about 200:1, about 189:1, about 77:1, about 31:1, about 15:1, about 13:1, about 6:1, about 5:1, about 1:2, about 1:4, about 1:6, about 1:8, or about 1:10, or about 1:1. For example, about 1:1.
In some embodiments, the composition (e.g., coating or coating agent) comprises from about 1% to about 50% by weight of the one or more compounds of Formula IIA. For example, the composition comprises from about 1% to about 10%, from about 10% to about 20%, from about 20% to about 30%, from about 30% to about 40%, from about 40% to about 50%, from about 1% to about 40%, from about 1% to about 30%, from about 1% to about 35%, from about 1% to about 20%, from about 10% to about 50%, from about 20% to about 40%, from about 15% to about 45%, from about 25% to about 35%, from about 28% to about 32%, from about 1% to about 10%, from about 2% to about 10%, from about 3% to about 9%, from about 4% to about 8%, from about 4% to about 6%, about 3%, about 4%, about 5%, about 6%, about 7%, about 8%, about 29%, about 30%, or about 31% by weight of the one or more compounds of Formula IIA. In some embodiments, when the composition comprises two compounds of Formula IIA, the molar ratio or weight ratio of the two compounds is from about 1:20 to about 20:1. For example, from about 1:10 to about 10:1, from about 1:10 to about 2:1, from about 1:4 to about 1:2, from about 1:3 to about 3:1, from about 1:2 to about 2:1, or about 1:1. For example, about 1:1.
In some embodiments, when the composition (e.g., coating or coating agent) comprises two compounds of Formula IIA, each compound is independently from about 1% to about 49% by weight of the composition. For example, one compound is from about 1% to about 7%, from about 10% to about 20%, from about 20% to about 30%, from about 30% to about 40%, from about 40% to about 49%, from about 1% to about 15%, from about 1% to about 10%, from about 1% to about 20%, from about 10% to about 49%, from about 20% to about 40%, from about 7% to about 25%, from about 12% to about 18%, from about 13% to about 17%, from about 1% to about 10%, from about 2% to about 5%, from about 3% to about 4%, about 1%, about 2%, about 3%, about 4%, about 5%, about 6%, about 7%, about 8%, about 9%, about 10%, about 11%, about 12%, about 13%, about 14%, about 15%, about 16%, or about 17% by weight of the composition; and the other compound is from about 1% to about 7%, from about 10% to about 20%, from about 20% to about 30%, from about 30% to about 40%, from about 40% to about 49%, from about 1% to about 15%, from about 1% to about 10%, from about 1% to about 20%, from about 10% to about 49%, from about 20% to about 40%, from about 7% to about 25%, from about 12% to about 18%, from about 13% to about 17%, from about 1% to about 10%, from about 2% to about 5%, from about 3% to about 4%, about 1%, about 2%, about 3%, about 4%, about 5%, about 6%, about 7%, about 8%, about 9%, about 10%, about 11%, about 12%, about 13%, about 14%, about 15%, about 16%, or about 17% by weight of the composition.
In some embodiments, when the composition (e.g., coating or coating agent) comprises a compound of Formula IA-A-i and a compound of Formula IA-A-ii, the weight or molar ratio of the compound of Formula IA-A-i to the compound of Formula IA-A-ii is from about 1:10 to about 10:1. For example, from about 1:10 to about 2:1, from about 1:8 to about 2:1, from about 1:4 to about 2:1, from about 1:3 to about 2:1, from about 1:2 to about 2:1, from about 1:10 to about 1:1, from about 1:8 to about 1:1, from about 4:1 to about 1:1, from about 3:1 to about 1:1, from about 2:1 to about 1:1, about 3:1, about 2:1, or about 1:1. In some embodiments, the weight or molar ratio of the compound of Formula IA-A-ii to the compound of Formula IA-A-i is from about 1:10 to about 10:1. For example, from about 1:10 to about 2:1, from about 1:8 to about 2:1, from about 1:4 to about 2:1, from about 1:3 to about 2:1, from about 1:2 to about 2:1, from about 1:10 to about 1:1, from about 1:8 to about 1:1, from about 4:1 to about 1:1, from about 3:1 to about 1:1, from about 2:1 to about 1:1, about 3:1, about 2:1, or about 1:1.
In some embodiments, when the composition (e.g., coating or coating agent) comprises two compounds of Formula IA-A-i, the weight or molar ratio of one of the compounds of Formula IA-A-i to the other of the compounds of Formula IA-A-i is from about 1:10 to about 10:1. For example, from about 1:10 to about 2:1, from about 1:8 to about 2:1, from about 1:4 to about 2:1, from about 1:3 to about 2:1, from about 1:2 to about 2:1, from about 1:10 to about 1:1, from about 1:8 to about 1:1, from about 4:1 to about 1:1, from about 3:1 to about 1:1, from about 2:1 to about 1:1, about 3:1, about 2:1, or about 1:1. For example, about 1:1.
In some embodiments, when the composition (e.g., coating or coating agent) comprises two compounds of Formula IA-A-ii, the weight or molar ratio of one of the compounds of Formula IA-A-ii to the other of the compounds of Formula IA-A-ii is from about 1:10 to about 10:1. For example, from about 1:10 to about 2:1, from about 1:8 to about 2:1, from about 1:4 to about 2:1, from about 1:3 to about 2:1, from about 1:2 to about 2:1, from about 1:10 to about 1:1, from about 1:8 to about 1:1, from about 4:1 to about 1:1, from about 3:1 to about 1:1, from about 2:1 to about 1:1, about 3:1, about 2:1, or about 1:1.
In some embodiments, the composition (e.g., coating or coating agent) comprises a compound of Formula IA-A-i and a compound of Formula IIA. In some embodiments, the weight or molar ratio of the compound of Formula IA-A-i to the compound of Formula IIA is from about 30:1 to about 1:1. For example, from about 25:1 to about 2:1, from about 20:1 to about 2:1, from about 10:1 to about 3:1, from about 7:1 to about 3:1, from about 5:1 to about 2:1, from about 4:1 to about 2:1, from about 25:1 to about 15:1, from about 22:1 to about 18:1, from about 88:12 to about 99:1, from about 90:10 to about 97:3, from about 92:8 to about 96:4, from about 93:7 to about 95:5, about 20:1, about 4:1, about 94:6, or about 70:30. In some embodiments, the composition comprises about 40% to about 100% by weight of the compound of Formula IA-A-i. For example, the composition comprises from about 40% to about 45%, from about 45% to about 50%, from about 50% to about 55%, from about 55% to about 60%, from about 60% to about 65%, from about 65% to about 70%, from about 65% to about 99%, from about 70% to about 75%, from about 75% to about 80%, from about 80% to about 85%, from about 85% to about 90%, from about 90% to about 95%, from about 95% to about 100%, from about 40% to about 50%, from about 50% to about 60%, from about 60% to about 70%, from about 70% to about 80%, from about 80% to about 90%, from about 90% to about 100%, from about 40% to about 60%, from about 60% to about 80%, from about 80% to about 100%, from about 60% to about 100%, from about 70% to about 100%, from about 40% to about 99%, from about 60% to about 99%, from about 70% to about 99%, from about 70% to about 94%, from about 80% to about 99%, from about 85% to about 99%, from about 90% to about 99%, from about 92% to about 98%, from about 92% to about 96%, from about 93% to about 95%, from about 62% to about 78%, from about 65% to about 75%, from about 67% to about 73%, from about 69% to about 71%, about 68%, about 69%, about 70%, about 71%, about 72%, about 75%, about 80%, about 85%, about 90%, about 92%, about 93%, about 94%, about 95%, about 96%, about 97%, about 98%, or about 99% by weight of the compound of Formula IA-A-i. For example, the composition comprises from about 60% to about 80%, about 70%, from about 85% to about 99%, about 95%, or about 96% by weight of the compound of Formula IA-A-i. In some embodiments, the composition comprises about 1% to about 50% by weight of the compound of Formula IIA. For example, the composition comprises from about 1% to about 10%, from about 10% to about 20%, from about 20% to about 30%, from about 30% to about 40%, from about 40% to about 50%, from about 1% to about 40%, from about 1% to about 35%, from about 1% to about 30%, from about 1% to about 20%, from about 10% to about 50%, from about 20% to about 40%, from about 15% to about 45%, from about 10% to about 20%, from about 20% to about 30%, from about 25% to about 35%, from about 28% to about 32%, from about 6% to about 30%, from about 1% to about 10%, from about 2% to about 10%, from about 3% to about 9%, from about 4% to about 8%, from about 4% to about 6%, about 3%, about 4%, about 5%, about 6%, about 7%, about 8%, about 10%, about 15%, about 20%, about 25%, about 29%, about 30%, or about 31% by weight of the compound of Formula IIA. In some embodiments, in the compound of Formula IA-A-i, RA1 and RA2 are H; R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from H and OH; each occurrence of R10A, R10B, R11A, and R11B is H; and the sum of o and p is from 11 to 13. For example, the compound of Formula IA-A-i is 2,3-dihydroxypropan-1-yl octadecanoate. In some embodiments, in the compound of Formula IIA, RA1 and RA2 are H; R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from H and OH; each occurrence of R10A, R10B, R11A, and R11B is H; and the sum of o and p is from 11 to 13. For example, the compound of Formula IIA is sodium stearate. In some embodiments, the composition comprises about 70% 2,3-dihydroxypropan-1-yl octadecanoate and about 30% sodium stearate. In some embodiments, the composition comprises about 94% 2,3-dihydroxypropan-1-yl octadecanoate and about 6% sodium stearate. In some embodiments, the composition comprises 2,3-dihydroxypropan-1-yl octadecanoate and sodium stearate in a weight ratio of about 70:30 or about 94:6. In some embodiments, the composition further comprises citric acid, sodium bicarbonate, or both. In some embodiments, the composition comprises citric acid and sodium bicarbonate. In some embodiments, the molar ratio of the citric acid to sodium bicarbonate is from about 1:5 to about 1:1, for example, about 1:3 to about 1:1, about 1:3 to about 1:2, about 1:3, about 1:2, or about 1:1. In some embodiments, the weight percentage of citric acid in the composition is from about 0.2% to about 2%, for example, about 0.25% to about 1.5%, about 0.25%, about 0.5%, about 1%, or about 1.5%. In some embodiments, the weight percentage of sodium bicarbonate in the composition is from about 0.2% to about 2%, for example, about 0.25% to about 1.5%, about 0.25%, about 0.5%, about 1%, or about 1.5%. In some embodiments, the collective weight percentage of citric acid and sodium bicarbonate in the composition is from about 0.2% to about 2%, for example, about 0.25% to about 1.5%, about 0.25%, about 0.5%, about 1%, or about 1.5%.
In some embodiments, the composition (e.g., coating or coating agent) comprises a compound of Formula IA-A-i and two compounds of Formula IIA. In some embodiments, the weight or molar ratio of the compound of Formula IA-A-i to both compounds of Formula IIA is from about 30:1 to about 1:1. For example, from about 25:1 to about 2:1, from about 20:1 to about 2:1, from about 10:1 to about 3:1, from about 7:1 to about 3:1, from about 5:1 to about 2:1, from about 4:1 to about 2:1, from about 25:1 to about 15:1, from about 22:1 to about 18:1, from about 88:12 to about 99:1, from about 90:10 to about 97:3, from about 92:8 to about 96:4, from about 93:7 to about 95:5, about 20:1, about 4:1, about 94:6, or about 70:30. In some embodiments, the weight or molar ratio of one compound of Formula IIA to the other compound of Formula IIA is from about 1:20 to about 20:1. For example, from about 1:10 to about 10:1, from about 1:10 to about 2:1, from about 1:4 to about 1:2, from about 1:3 to about 3:1, from about 1:2 to about 2:1, or about 1:1. For example, about 1:1. In some embodiments, the composition comprises about 40% to about 100% by weight of the compound of Formula IA-A-i. For example, the composition comprises from about 40% to about 45%, from about 45% to about 50%, from about 50% to about 55%, from about 55% to about 60%, from about 60% to about 65%, from about 65% to about 70%, from about 65% to about 99%, from about 70% to about 75%, from about 75% to about 80%, from about 80% to about 85%, from about 85% to about 90%, from about 90% to about 95%, from about 95% to about 100%, from about 40% to about 50%, from about 50% to about 60%, from about 60% to about 70%, from about 70% to about 80%, from about 80% to about 90%, from about 90% to about 100%, from about 40% to about 60%, from about 60% to about 80%, from about 80% to about 100%, from about 60% to about 100%, from about 70% to about 100%, from about 40% to about 99%, from about 60% to about 99%, from about 70% to about 99%, from about 70% to about 94%, from about 80% to about 99%, from about 85% to about 99%, from about 90% to about 99%, from about 92% to about 98%, from about 92% to about 96%, from about 93% to about 95%, from about 62% to about 78%, from about 65% to about 75%, from about 67% to about 73%, from about 69% to about 71%, about 68%, about 69%, about 70%, about 71%, about 72%, about 75%, about 80%, about 85%, about 90%, about 92%, about 93%, about 94%, about 95%, about 96%, about 97%, about 98%, or about 99% by weight of the compound of Formula IA-A-i. For example, the composition comprises from about 60% to about 80%, about 70%, from about 85% to about 99%, about 95%, or about 96% by weight of the compound of Formula IA-A-i. In some embodiments, the composition comprises about 1% to about 50% by weight of both compounds of Formula IIA. For example, the composition comprises from about 1% to about 10%, from about 10% to about 20%, from about 20% to about 30%, from about 30% to about 40%, from about 40% to about 50%, from about 1% to about 40%, from about 1% to about 35%, from about 1% to about 30%, from about 1% to about 20%, from about 10% to about 50%, from about 20% to about 40%, from about 15% to about 45%, from about 10% to about 20%, from about 20% to about 30%, from about 25% to about 35%, from about 28% to about 32%, from about 6% to about 30%, from about 1% to about 10%, from about 2% to about 10%, from about 3% to about 9%, from about 4% to about 8%, from about 4% to about 6%, about 3%, about 4%, about 5%, about 6%, about 7%, about 8%, about 10%, about 15%, about 20%, about 25%, about 29%, about 30%, or about 31% by weight of both compounds of Formula IIA. In some embodiments, in the compound of Formula IA-A-i, RA1 and RA2 are H; R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from H and OH; each occurrence of R10A, R10B, R11A, and R11B is H; and the sum of o and p is from 11 to 13. For example, the compound of Formula IA-A-i is 2,3-dihydroxypropan-1-yl octadecanoate. In some embodiments, in each compound of Formula IIA, RA1 and RA2 are H; R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from H and OH; each occurrence of R10A, R10B, R11A, and R11B is H; and the sum of o and p is from 11 to 13. In some embodiments, the sum of o and p in one compound of Formula IIA is 13 and the sum of o and p in the other compound of Formula IIA is 11. For example, one compound of Formula IIA is sodium stearate and the other compound of Formula IIA is sodium palmitate. In some embodiments, the composition comprises about 70% 2,3-dihydroxypropan-1-yl octadecanoate and about 30% of sodium stearate and sodium palmitate in a 1:1 weight ratio.
In some embodiments, the composition comprises about 94% 2,3-dihydroxypropan-1-yl octadecanoate and about 6% sodium stearate and sodium palmitate in a 1:1 weight ratio. In some embodiments, the composition comprises 2,3-dihydroxypropan-1-yl octadecanoate, sodium stearate, and sodium palmitate in a weight ratio of about 70:15:15 or about 94:3:3. In some embodiments, the composition further comprises citric acid, sodium bicarbonate, or both.
In some embodiments, the molar ratio of the citric acid to sodium bicarbonate is from about 1:5 to about 1:1, for example, about 1:3 to about 1:1, about 1:3 to about 1:2, about 1:3, about 1:2, or about 1:1. In some embodiments, the weight percentage of citric acid in the composition is from about 0.2% to about 2%, for example, about 0.25% to about 1.5%, about 0.25%, about 0.5%, about 1%, or about 1.5%. In some embodiments, the weight percentage of sodium bicarbonate in the composition is from about 0.2% to about 2%, for example, about 0.25% to about 1.5%, about 0.25%, about 0.5%, about 1%, or about 1.5%. In some embodiments, the collective weight percentage of citric acid and sodium bicarbonate in the composition is from about 0.2% to about 2%, for example, about 0.25% to about 1.5%, about 0.25%, about 0.5%, about 1%, or about 1.5%.
In some embodiments, the composition (e.g., coating or coating agent) comprises a first compound of Formula IA-A-i, a second compound of Formula IA-A-i, and one compound of Formula IIA. In some embodiments, the weight or molar ratio of the compound of both compounds of Formula IA-A-i to the compound of Formula IIA is from about 30:1 to about 1:1.
For example, from about 25:1 to about 2:1, from about 20:1 to about 2:1, from about 10:1 to about 3:1, from about 7:1 to about 3:1, from about 5:1 to about 2:1, from about 4:1 to about 2:1, from about 25:1 to about 15:1, from about 22:1 to about 18:1, from about 88:12 to about 99:1, from about 90:10 to about 97:3, from about 92:8 to about 96:4, from about 93:7 to about 95:5, about 20:1, about 4:1, about 94:6, or about 70:30. In some embodiments, the weight or molar ratio of one compound of Formula IA-A-i to the other compound of Formula IA-A-i is from about 1:20 to about 20:1. For example, from about 1:10 to about 10:1, from about 1:10 to about 2:1, from about 1:1 to about 8:1, from about 1:1 to about 6:1, from about 1:1 to about 4:1, from about 1:1 to about 3:1, from about 1:1 to about 2:1, from about 2:1 to about 4:1, from about 4:1 to about 6:1, from about 6:1 to about 8:1, from about 8:1 to about 10:1, from about 1:4 to about 1:2, from about 1:3 to about 3:1, from about 1:2 to about 2:1, about 1:1, about 1:2, about 1:4, about 1:6, about 1:8, or about 1:10, or about 1:1. For example, about 1:1. In some embodiments, the composition comprises about 40% to about 100% by weight of both compounds of Formula IA-A-i. For example, the composition comprises from about 40% to about 45%, from about 45% to about 50%, from about 50% to about 55%, from about 55% to about 60%, from about 60% to about 65%, from about 65% to about 70%, from about 65% to about 99%, from about 70% to about 75%, from about 75% to about 80%, from about 80% to about 85%, from about 85% to about 90%, from about 90% to about 95%, from about 95% to about 100%, from about 40% to about 50%, from about 50% to about 60%, from about 60% to about 70%, from about 70% to about 80%, from about 80% to about 90%, from about 90% to about 100%, from about 40% to about 60%, from about 60% to about 80%, from about 80% to about 100%, from about 60% to about 100%, from about 70% to about 100%, from about 40% to about 99%, from about 60% to about 99%, from about 70% to about 99%, from about 70% to about 94%, from about 80% to about 99%, from about 85% to about 99%, from about 90% to about 99%, from about 92% to about 98%, from about 92% to about 96%, from about 93% to about 95%, from about 62% to about 78%, from about 65% to about 75%, from about 67% to about 73%, from about 69% to about 71%, about 68%, about 69%, about 70%, about 71%, about 72%, about 75%, about 80%, about 85%, about 90%, about 92%, about 93%, about 94%, about 95%, about 96%, about 97%, about 98%, or about 99% by weight of both compounds of Formula IA-A-i. For example, the composition comprises from about 60% to about 80%, about 70%, from about 85% to about 99%, about 95%, or about 96% by weight of both compounds of Formula IA-A-i. In some embodiments, the composition comprises about 1% to about 50% by weight of the compound of Formula IIA. For example, the composition comprises from about 1% to about 10%, from about 10% to about 20%, from about 20% to about 30%, from about 30% to about 40%, from about 40% to about 50%, from about 1% to about 40%, from about 1% to about 35%, from about 1% to about 30%, from about 1% to about 20%, from about 10% to about 50%, from about 20% to about 40%, from about 15% to about 45%, from about 10% to about 20%, from about 20% to about 30%, from about 25% to about 35%, from about 28% to about 32%, from about 6% to about 30%, from about 1% to about 10%, from about 2% to about 10%, from about 3% to about 9%, from about 4% to about 8%, from about 4% to about 6%, about 3%, about 4%, about 5%, about 6%, about 7%, about 8%, about 10%, about 15%, about 20%, about 25%, about 29%, about 30%, or about 31% by weight of the compound of Formula IIA. In some embodiments, the weight or molar ratio of the first compound of Formula IA-A-i to the second compound of Formula IA-A-i to the compound of Formula IIA is about 47:47:6 or about 35:35:30. In some embodiments, the weight or molar ratio of the first compound of Formula IA-A-i to the second compound of Formula IA-A-i to the compound of Formula IIA is about 190:1:10, about 316:1:17, about 20:4:1, about 78:1:5, about 13:1:1, about 31:1:2, about 20:4:1, about 20:3:1, or about 18:1:1. In some embodiments, the composition comprises from about 25% to about 75% (e.g., from about 35% to about 65%, from about 40% to about 60%, from about 25% to about 45%, from about 30% to about 40%, from about 32% to about 38%, from about 42% to about 55%, about 34%, about 35%, about 36%, about 45%, about 46%, about 47%, about 48%, about 49% or about 50%) of the first compound of Formula IA-A-i, from about 25% to about 75% (e.g., from about 35% to about 65%, from about 40% to about 60%, from about 25% to about 45%, from about 30% to about 40%, from about 32% to about 38%, from about 42% to about 55%, about 34%, about 35%, about 36%, about 45%, about 46%, about 47%, about 48%, about 49% or about 50%) of the second compound of Formula IA-A-i, and from about 1% to about 40% (e.g., from about 10% to about 40%, from about 20% to about 40%, from about 25% to about 35%, from about 27% to about 33%, from about 1% to about 10%, from about 3% to about 8%, about 29%, about 30%, about 31%, about 6%, about 5%, or about 4%) of the compound of Formula IIA. In some embodiments, the composition comprises from about 75% to about 99% (e.g., from about 78% to about 96%, from about 85% to about 96%, about 81%, about 87%, about 89%, about 92%, about 93%, about 94%, or about 95%) of the first compound of Formula IA-A-i, from about 0.1% to about 20% (e.g., from about 0.1% to about 5%, from about 0.1% to about 10%, from about 3% to about 20%, from about 5% to about 15%, from about 10% to about 20%, about 0.3%, about 0.5%, about 1%, about 3%, about 6%, about 7%, about 14%, or about 17%) of the second compound of Formula IA-A-i, and about 1% to about 10% (e.g., from about 3% to about 8%, about 4%, about 5%, or about 6%) of the compound of Formula IIA. In some embodiments, in one compound of Formula IA-A-i, RA1 and RA2 are H; R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from H and OH; each occurrence of R10A, R10B, R11A, and R11B is H; and the sum of o and p is from 11 to 13. In some embodiments, in the other compound of Formula IA-A-i, RA1 and RA2 are H; R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from H and OH; each occurrence of R10A, R10B, R11A, and R11B is H; and the sum of o and p is from 7 to 9. For example, one compound of Formula IA-A-i is 2,3-dihydroxypropan-1-yl octadecanoate and the other compound of Formula IA-A-i is 2,3-dihydroxypropan-1-yl dodecanoate. In some embodiments, in the compound of Formula IIA, RA1 and RA2 are H; R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from H and OH; each occurrence of R10A, R10B, R11A, and R11B is H; and the sum of o and p is from 11 to 13. For example, the compound of Formula IIA is sodium stearate. In some embodiments, the composition comprises about 70% 2,3-dihydroxypropan-1-yl octadecanoate and 2,3-dihydroxypropan-1-yl dodecanoate in a 1:1 weight ratio and about 30% of sodium stearate. In some embodiments, the composition comprises about 94% 2,3-dihydroxypropan-1-yl octadecanoate and 2,3-dihydroxypropan-1-yl dodecanoate in a 1:1 weight ratio and about 6% sodium stearate. In some embodiments, the composition comprises 2,3-dihydroxypropan-1-yl octadecanoate, 2,3-dihydroxypropan-1-yl dodecanoate, and sodium stearate in a weight ratio of about 35:35:30 or about 47:47:6. In some embodiments, the composition further comprises citric acid, sodium bicarbonate, or both. In some embodiments, the molar ratio of the citric acid to sodium bicarbonate is from about 1:5 to about 1:1, for example, about 1:3 to about 1:1, about 1:3 to about 1:2, about 1:3, about 1:2, or about 1:1. In some embodiments, the weight percentage of citric acid in the composition is from about 0.2% to about 2%, for example, about 0.25% to about 1.5%, about 0.25%, about 0.5%, about 1%, or about 1.5%. In some embodiments, the weight percentage of sodium bicarbonate in the composition is from about 0.2% to about 2%, for example, about 0.25% to about 1.5%, about 0.25%, about 0.5%, about 1%, or about 1.5%. In some embodiments, the collective weight percentage of citric acid and sodium bicarbonate in the composition is from about 0.2% to about 2%, for example, about 0.25% to about 1.5%, about 0.25%, about 0.5%, about 1%, or about 1.5%.
In some embodiments, the composition (e.g., coating or coating agent) comprises a first compound of Formula IA-A-i, a second compound of Formula IA-A-i, a first compound of Formula IIA, and a second compound of Formula IIA. In some embodiments, the weight or molar ratio of the compound of both compounds of Formula IA-A-i to both compounds of Formula IIA is from about 30:1 to about 1:1. For example, from about 25:1 to about 2:1, from about 20:1 to about 2:1, from about 10:1 to about 3:1, from about 7:1 to about 3:1, from about 5:1 to about 2:1, from about 4:1 to about 2:1, from about 25:1 to about 15:1, from about 22:1 to about 18:1, from about 88:12 to about 99:1, from about 90:10 to about 97:3, from about 92:8 to about 96:4, from about 93:7 to about 95:5, about 20:1, about 4:1, about 94:6, or about 70:30. In some embodiments, the weight or molar ratio of one compound of Formula IA-A-i to the other compound of Formula IA-A-i is from about 1:20 to about 20:1. For example, from about 1:10 to about 10:1, from about 1:10 to about 2:1, from about 1:1 to about 8:1, from about 1:1 to about 6:1, from about 1:1 to about 4:1, from about 1:1 to about 3:1, from about 1:1 to about 2:1, from about 2:1 to about 4:1, from about 4:1 to about 6:1, from about 6:1 to about 8:1, from about 8:1 to about 10:1, from about 1:4 to about 1:2, from about 1:3 to about 3:1, from about 1:2 to about 2:1, about 1:1, about 1:2, about 1:4, about 1:6, about 1:8, or about 1:10, or about 1:1. For example, about 1:1. In some embodiments, the weight or molar ratio of one compound of Formula IIA to the other compound of Formula IIA is from about 1:20 to about 20:1. For example, from about 1:10 to about 10:1, from about 1:10 to about 2:1, from about 1:4 to about 1:2, from about 1:3 to about 3:1, from about 1:2 to about 2:1, or about 1:1. For example, about 1:1. In some embodiments, the composition comprises about 40% to about 100% by weight of both compounds of Formula IA-A-i. For example, the composition comprises from about 40% to about 45%, from about 45% to about 50%, from about 50% to about 55%, from about 55% to about 60%, from about 60% to about 65%, from about 65% to about 70%, from about 65% to about 99%, from about 70% to about 75%, from about 75% to about 80%, from about 80% to about 85%, from about 85% to about 90%, from about 90% to about 95%, from about 95% to about 100%, from about 40% to about 50%, from about 50% to about 60%, from about 60% to about 70%, from about 70% to about 80%, from about 80% to about 90%, from about 90% to about 100%, from about 40% to about 60%, from about 60% to about 80%, from about 80% to about 100%, from about 60% to about 100%, from about 70% to about 100%, from about 40% to about 99%, from about 60% to about 99%, from about 70% to about 99%, from about 70% to about 94%, from about 80% to about 99%, from about 85% to about 99%, from about 90% to about 99%, from about 92% to about 98%, from about 92% to about 96%, from about 93% to about 95%, from about 62% to about 78%, from about 65% to about 75%, from about 67% to about 73%, from about 69% to about 71%, about 68%, about 69%, about 70%, about 71%, about 72%, about 75%, about 80%, about 85%, about 90%, about 92%, about 93%, about 94%, about 95%, about 96%, about 97%, about 98%, or about 99% by weight of both compounds of Formula IA-A-i. For example, the composition comprises from about 60% to about 80%, about 70%, from about 85% to about 99%, about 95%, or about 96% by weight of both compounds of Formula IA-A-i. In some embodiments, the composition comprises about 1% to about 50% by weight of both compounds of Formula IIA. For example, the composition comprises from about 1% to about 10%, from about 10% to about 20%, from about 20% to about 30%, from about 30% to about 40%, from about 40% to about 50%, from about 1% to about 40%, from about 1% to about 35%, from about 1% to about 30%, from about 1% to about 20%, from about 10% to about 50%, from about 20% to about 40%, from about 15% to about 45%, from about 10% to about 20%, from about 20% to about 30%, from about 25% to about 35%, from about 28% to about 32%, from about 6% to about 30%, from about 1% to about 10%, from about 2% to about 10%, from about 3% to about 9%, from about 4% to about 8%, from about 4% to about 6%, about 3%, about 4%, about 5%, about 6%, about 7%, about 8%, about 10%, about 15%, about 20%, about 25%, about 29%, about 30%, or about 31% by weight of both compounds of Formula IIA. In some embodiments, the weight or molar ratio of the first compound of Formula IA-A-i to the second compound of Formula IA-A-i to the first compound of Formula IIA to the second compound of Formula IIA is about 47:47:3:3 or about 35:35:15:15. In some embodiments, the composition comprises from about 25% to about 75% (e.g., from about 35% to about 65%, from about 40% to about 60%, from about 25% to about 45%, from about 30% to about 40%, from about 32% to about 38%, from about 42% to about 55%, about 34%, about 35%, about 36%, about 45%, about 46%, about 47%, about 48%, about 49% or about 50%) of the first compound of Formula IA-A-i, from about 25% to about 75% (e.g., from about 35% to about 65%, from about 40% to about 60%, from about 25% to about 45%, from about 30% to about 40%, from about 32% to about 38%, from about 42% to about 55%, about 34%, about 35%, about 36%, about 45%, about 46%, about 47%, about 48%, about 49% or about 50%) of the second compound of Formula IA-A-i, from about 1% to about 30% (e.g., from about 10% to about 30%, from about 20% to about 30%, from about 10% to about 20%, from about 5% to about 20%, from about 12% to about 18%, about 14%, about 15%, or about 16%) of the first compound of Formula IIA, and from about 1% to about 30% (e.g., from about 10% to about 30%, from about 20% to about 30%, from about 10% to about 20%, from about 5% to about 20%, from about 12% to about 18%, about 14%, about 15%, or about 16%) of the second compound of Formula IIA. In some embodiments, in each compound of Formula IA-A-i, RA1 and RA2 are H; R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from H and OH; each occurrence of R10A, R10B, R11A, and R11B is H; and the sum of o and p is from 11 to 13. For example, one compound of Formula IA-A-i is 2,3-dihydroxypropan-1-yl octadecanoate and the other compound of Formula IA-A-i is 2,3-dihydroxypropan-1-yl palmitate. In some embodiments, in each compound of Formula IIA, RA1 and RA2 are H; R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from H and OH; each occurrence of R10A, R10B, R11A, and R11B is H; and the sum of o and p is from 11 to 13. In some embodiments, the sum of o and p in one compound of Formula IIA is 13 and the sum of o and p in the other compound of Formula IIA is 11. For example, one compound of Formula IIA is sodium stearate and the other compound of Formula IIA is sodium palmitate. In some embodiments, the composition comprises about 70% 2,3-dihydroxypropan-1-yl octadecanoate and 2,3-dihydroxypropan-1-yl palmitate in an about 1:1 weight ratio and about 30% of sodium stearate and sodium palmitate in an about 1:1 weight ratio. In some embodiments, the composition comprises about 94% 2,3-dihydroxypropan-1-yl octadecanoate and 2,3-dihydroxypropan-1-yl palmitate in an about 1:1 weight ratio and about 6% of sodium stearate and sodium palmitate in an about 1:1 weight ratio. In some embodiments, the composition comprises 2,3-dihydroxypropan-1-yl octadecanoate, 2,3-dihydroxypropan-1-yl palmitate, sodium stearate, and sodium palmitate in a weight ratio of about 35:35:15:15 or about 47:47:3:3. In some embodiments, the composition further comprises citric acid, sodium bicarbonate, or both. In some embodiments, the molar ratio of the citric acid to sodium bicarbonate is from about 1:5 to about 1:1, for example, about 1:3 to about 1:1, about 1:3 to about 1:2, about 1:3, about 1:2, or about 1:1. In some embodiments, the weight percentage of citric acid in the composition is from about 0.2% to about 2%, for example, about 0.25% to about 1.5%, about 0.25%, about 0.5%, about 1%, or about 1.5%. In some embodiments, the weight percentage of sodium bicarbonate in the composition is from about 0.2% to about 2%, for example, about 0.25% to about 1.5%, about 0.25%, about 0.5%, about 1%, or about 1.5%. In some embodiments, the collective weight percentage of citric acid and sodium bicarbonate in the composition is from about 0.2% to about 2%, for example, about 0.25% to about 1.5%, about 0.25%, about 0.5%, about 1%, or about 1.5%.
In some embodiments, less than 10% (e.g., less than 5%, less than 2%, less than 1%) by weight of the composition is diglycerides. In some embodiments, less than 10% (e.g., less than 5%, less than 2%, less than 1%) by weight of the composition is triglycerides. In some embodiments, the composition does not comprise an acetylated monoglyceride (e.g., a monoglyceride wherein the hydroxyl groups of the glyceryl moiety are acetylated).
Coating agents formed from or containing a high percentage of long chain fatty acids and/or salts or esters thereof (e.g., having a carbon chain length of at least 14) have been found to be effective at forming protective coatings over a variety of substrates that can prevent water loss from and/or oxidation of the substrate. The addition of one or more medium chain fatty acids and/or salts or esters thereof (or other wetting agents) can further improve the performance of the coatings. Accordingly, the coating agents herein can include one or more compounds of Formula I, wherein Formula I is:
wherein:
R is selected from —H, -glyceryl, —C1-C6 alkyl, —C1-C6 alkenyl, —C1-C6 alkynyl, —C3-C1 cycloalkyl, aryl, or heteroaryl, wherein each alkyl, alkenyl, alkynyl, cycloalkyl, aryl or heteroaryl is optionally substituted with one or more groups selected from halogen (e.g., Cl, Br, or I), hydroxyl, nitro, —CN, —NH2, —SH, —SR15, —OR14, —NR14R15, C1-C6 alkyl, C2-C6 alkenyl, or C2-C6 alkynyl;
R1, R2, R5, R6, R9, R10, R11, R12 and R13 are each independently, at each occurrence, —H, —(C═O)R14, —(C═O)H, —(C═O)OH, —(C═O)OR14, —(C═O)—O—(C═O)R14, —O(C═O)R14, —OR14, —NR14R15, —SR14, halogen, —C1-C6 alkyl, —C2-C6 alkenyl, —C2-C6 alkynyl, —C3-C1 cycloalkyl, aryl, or heteroaryl, wherein each alkyl, alkenyl, alkynyl, cycloalkyl, aryl, or heteroaryl is optionally substituted with one or more —OR14, —NR14R15, —SR14, or halogen;
R3, R4, R7, and R8 are each independently, at each occurrence, —H, —OR14, —NR14R15, —SR14, halogen, —C1-C6 alkyl, —C2-C6 alkenyl, —C2-C6 alkynyl, —C3-C1 cycloalkyl, aryl, or heteroaryl wherein each alkyl, alkynyl, cycloalkyl, aryl, or heteroaryl is optionally substituted with one or more —OR14, —NR14R15, —SR14, or halogen; or
R3 and R4 can combine with the carbon atoms to which they are attached to form a C3-C6 cycloalkyl, a C4-C6 cycloalkenyl, or 3- to 6-membered ring heterocycle; and/or
R7 and R8 can combine with the carbon atoms to which they are attached to form a C3-C6 cycloalkyl, a C4-C6 cycloalkenyl, or 3- to 6-membered ring heterocycle;
R14 and R15 are each independently, at each occurrence, —H, aryl, heteroaryl, —C1-C6 alkyl, —C2-C6 alkenyl, or —C2-C6 alkynyl;
the symbol represents a single bond or a cis or trans double bond;
n is 0, 1, 2, 3, 4, 5, 6, 7 or 8;
m is 0, 1, 2 or 3;
q is 0, 1, 2, 3, 4 or 5; and
r is 0, 1, 2, 3, 4, 5, 6, 7 or 8.
In some embodiments, R is selected from —H, —CH3, or —CH2CH3. In some embodiments, R is selected from —H, -glyceryl, —C1-C6 alkyl, —C2-C6 alkenyl, —C2-C6 alkynyl, —C3-C1 cycloalkyl, aryl, or heteroaryl, wherein each alkyl, alkenyl, alkynyl, cycloalkyl, aryl or heteroaryl is optionally substituted with one or more C1-C6 alkyl or hydroxyl.
In some embodiments, R is -glyceryl. In some embodiments, R1, R2, R5, R6, R9, R10, R11, R12 and R13 are each independently selected from —H, —C1-C6 alkyl, and —OH. In some embodiments, R3, R4, R7, and R8 are each independently selected from —H, —C1-C6 alkyl, and —OH. In some embodiments, R3 and R4 combine with the carbon atoms to which they are attached to form a 3- to 6-membered ring heterocycle. In some embodiments, R7 and R8 combine with the carbon atoms to which they are attached to form a 3- to 6-membered ring heterocycle. In some embodiments, q is 1 and the sum of n, m, and r is from 10 to 12.
As further described herein, the coating agents can additionally or alternatively include fatty acid salts such as sodium salts (e.g., SA-Na, PA-Na, or MA-Na), potassium salts (e.g., SA-K, PA-K, MA-K), calcium salts (e.g., (SA)2-Ca, (PA)2-Ca, or (MA)2-Ca) or magnesium salts (e.g., (SA)2-Mg, (PA)2-Mg, or (MA)2-Mg). Accordingly, the coating agents herein can include one or more compounds of Formula II or Formula III, wherein Formula II and Formula III are:
wherein for each formula:
X is a cationic moiety;
Xp+ is a cationic counter ion having a charge state p, and p is 1, 2, or 3;
R1, R2, R5, R6, R9, R10, R11, R12 and R13 are each independently, at each occurrence, —H, —(C═O)R14, —(C═O)H, —(C═O)OH, —(C═O)OR14, —(C═O)—O—(C═O)R14, —O(C═O)R14, —OR14, —NR14R15, —SR14, halogen, —C1-C6 alkyl, —C2-C6 alkenyl, —C2-C6 alkynyl, —C3-C1 cycloalkyl, aryl, or heteroaryl, wherein each alkyl, alkenyl, alkynyl, cycloalkyl, aryl, or heteroaryl is optionally substituted with one or more —OR14, —NR14R15, —SR14, or halogen;
R3, R4, R7, and R8 are each independently, at each occurrence, —H, —OR14, —NR14R15, —SR14, halogen, —C1-C6 alkyl, —C2-C6 alkenyl, —C2-C6 alkynyl, —C3-C1 cycloalkyl, aryl, or heteroaryl wherein each alkyl, alkynyl, cycloalkyl, aryl, or heteroaryl is optionally substituted with one or more —OR14, —NR14R15, —SR14, or halogen; or
R3 and R4 can combine with the carbon atoms to which they are attached to form a C3-C6 cycloalkyl, a C4-C6 cycloalkenyl, or 3- to 6-membered ring heterocycle; and/or
R7 and R8 can combine with the carbon atoms to which they are attached to form a C3-C6 cycloalkyl, a C4-C6 cycloalkenyl, or 3- to 6-membered ring heterocycle;
R14 and R15 are each independently, at each occurrence, —H, aryl, heteroaryl, —C1-C6 alkyl, —C2-C6 alkenyl, or —C2-C6 alkynyl;
the symbol represents a single bond or a cis or trans double bond;
n is 0, 1, 2, 3, 4, 5, 6, 7 or 8;
m is 0, 1, 2 or 3;
q is 0, 1, 2, 3, 4 or 5; and
r is 0, 1, 2, 3, 4, 5, 6, 7 or 8.
In some embodiments, the fatty acid salt is a compound of Formula II. In some embodiments, the fatty acid salt is a compound of Formula III.
In some embodiments, X is sodium.
In some embodiments, R is -glyceryl. In some embodiments, R1, R2, R5, R6, R9, R10, R11, R12 and R13 are each independently selected from —H, —C1-C6 alkyl, and —OH. In some embodiments, R3, R4, R7, and R8 are each independently selected from —H, —C1-C6 alkyl, and —OH. In some embodiments, R3 and R4 combine with the carbon atoms to which they are attached to form a 3- to 6-membered ring heterocycle. In some embodiments, R7 and R8 combine with the carbon atoms to which they are attached to form a 3- to 6-membered ring heterocycle. In some embodiments, q is 1 and the sum of n, m, and r is from 10 to 12.
Any of the coating agents described herein can include one or more of the following medium chain fatty acid compounds (e.g., compounds of Formula I):
Any of the coating agents described herein can include one or more of the following long chain fatty acid compounds (e.g., compounds of Formula I):
The coating agents herein can include one or more of the following medium chain fatty acid methyl ester compounds (e.g., compounds of Formula I):
The coating agents herein can include one or more of the following long chain fatty acid methyl ester compounds (e.g., compounds of Formula I):
The coating agents herein can include one or more of the following medium chain fatty acid ethyl ester compounds (e.g., compounds of Formula I):
The coating agents herein can include one or more of the following long chain fatty acid ethyl ester compounds (e.g., compounds of Formula I):
The coating agents herein can include one or more of the following medium chain fatty acid 2-glyceryl ester compounds (e.g., compounds of Formula I):
The coating agents herein can include one or more of the following long chain fatty acid 2-glyceryl ester compounds (e.g., compounds of Formula I):
The coating agents herein can include one or more of the following medium chain fatty acid 1-glyceryl ester compounds (e.g., compounds of Formula I):
The coating agents herein can include one or more of the following long chain fatty acid 1-glyceryl ester compounds (e.g., compounds of Formula I):
The coating agents herein can include one or more of the following fatty acid salts (e.g., compounds of Formula II or Formula III), where X is a cationic counter ion and n represents the charge state (i.e., the number of proton-equivalent charges) of the cationic counter ion:
In some embodiments, n is 1, 2, or 3. In some embodiments, X is sodium, potassium, calcium, or magnesium.
Coating Agent Mixtures
In some embodiments, the composition (e.g., coating agent) can be dissolved, mixed, dispersed, or suspended in a solvent to form a mixture (e.g., solution, suspension, or colloid). Examples of solvents that can be used include water, methanol, ethanol, isopropanol, butanol, acetone, ethyl acetate, chloroform, acetonitrile, tetrahydrofuran, diethyl ether, methyl tert-butyl ether, or combinations thereof. For example, the solvent is water. For example, the solvent is ethanol.
In some embodiments, the concentration of the composition (e.g., coating agent) in the solution or mixture (e.g., solution, suspension, or colloid) is from about 1 mg/mL to about 200 mg/mL. For example, from about 1 to about 150 mg/mL, 1 to 100 mg/mL, from about 1 to about 90 mg/mL, from about 1 to about 80 mg/mL, from about 1 to about 75 mg/mL, from about 1 to about 70 mg/mL, from about 1 to about 65 mg/mL, from about 1 to about 60 mg/mL, from about 1 to about 55 mg/mL, from about 1 to about 50 mg/mL, from about 1 to about 45 mg/mL, from about 1 to about 40 mg/mL, from about 2 to about 200 mg/mL, from about 2 to about 150 mg/mL, from about 2 to about 100 mg/mL, from about 2 to about 90 mg/mL, from about 2 to about 80 mg/mL, from about 2 to about 75 mg/mL, from about 2 to about 70 mg/mL, from about 2 to about 65 mg/mL, from about 2 to about 60 mg/mL, from about 2 to about 55 mg/mL, from about 2 to about 50 mg/mL, from about 2 to about 45 mg/mL, from about 2 to about 40 mg/mL, from about 5 to about 200 mg/mL, from about 5 to about 150 mg/mL, from about 5 to about 100 mg/mL, from about 5 to about 90 mg/mL, from about 5 to about 80 mg/mL, from about 5 to about 75 mg/mL, from about 5 to about 70 mg/mL, from about 5 to about 65 mg/mL, from about 5 to about 60 mg/mL, from about 5 to about 55 mg/mL, from about 5 to about 50 mg/mL, from about 5 to about 45 mg/mL, from about 5 to about 40 mg/mL, from about 10 to about 200 mg/mL, from about 10 to about 150 mg/mL, from about 10 to about 100 mg/mL, from about 10 to about 90 mg/mL, from about 10 to about 80 mg/mL, from about 10 to about 75 mg/mL, from about 10 to about 70 mg/mL, from about 10 to about 65 mg/mL, from about 10 to about 60 mg/mL, from about 10 to about 55 mg/mL, from about 10 to about 50 mg/mL, from about 10 to about 45 mg/mL, from about 10 to about 40 mg/mL, from about 20 to about 50 mg/mL, from about 20 to about 40 mg/mL, from about 25 to about 35 mg/mL, from about 30 to about 50 mg/mL, or from about 35 to about 45 mg/mL. For example, the concentration of the composition (e.g., coating agent) in the mixture (e.g., solution, suspension, or colloid) is about 30 mg/mL or about 40 mg/mL.
As previously described, coating agents formed predominantly of various combinations of compounds of Formula I (e.g., coating agents that are at least 50% compounds of Formula I by mass or by molar composition) each having a carbon chain length of at least 14 have been shown to form protective coatings on produce and other agricultural products that are effective at reducing moisture loss and oxidation. As also previously described, the coatings can be formed over the outer surface of the agricultural product by dissolving, suspending, or dispersing the coating agent in a solvent to form a mixture, applying the mixture to the surface of the agricultural product (e.g., by spray coating the product, by dipping the product in the mixture, or by brushing the mixture onto the surface of the product), and then removing the solvent (e.g., by allowing the solvent to evaporate). The solvent can include any polar, non-polar, protic, or aprotic solvents, including any combinations thereof. Examples of solvents that can be used include water, methanol, ethanol, isopropanol, butanol, acetone, ethyl acetate, chloroform, acetonitrile, tetrahydrofuran, diethyl ether, methyl tert-butyl ether, any other suitable solvent or combinations thereof. In cases where the coating is going to be applied to plants or other edible products, it may be preferable to use a solvent that is safe for consumption, for example water, ethanol, or combinations thereof. Depending on the solvent that is used, the solubility limit of the coating agent in the solvent may be lower than desired for particular applications. For example, when compounds of Formula I are used as the coating agent and the solvent is water (or is predominantly water), the solubility limit of the coating agent may be relatively low. In these cases it may still be possible to add the desired concentration of coating agent to the solvent and form a suspension or colloid.
In order to improve the solubility of the coating agent in the solvent, or to allow the coating agent to be suspended or dispersed in the solvent, the coating agent can further include an emulsifier. When the coatings are to be formed over plants or other edible products, it may be preferable that the emulsifier be safe for consumption. Furthermore, it is also preferable that the emulsifier either not be incorporated into the coating or, if the emulsifier is incorporated into the coating, that it does not degrade the performance of the coating.
Through extensive experimentation, it has been shown that organic salts (e.g., compounds of Formula II or Formula III) added to the coating agent can increase the solubility of the coating agent or allow the coating agent to be suspended or dispersed in solvents having a substantial water content (e.g., solvents that are at least 50% water by volume), provided that the concentration of the salts is not too low (relative to the concentration of compounds of Formula I). Furthermore, the added salts do not substantially degrade the performance of subsequently formed coatings provided that the concentration of the salts (relative to the concentration of the compounds of Formula I) is not too high.
For example, coating agents including a first group of compounds of Formula I mixed with a second group of compounds of Formula II and/or III can be added to water to form a suspension by heating the water to about 70° C., adding the coating agent, and then cooling the resulting mixture to about room temperature (or a lower temperature). The cooled mixture can then be applied to substrates such as produce to form a protective coating, as described throughout. However, it has been found that when the compounds of Formula I make up at least 50% of the mass of the coating agent and the compounds of Formula II and/or III make up less than about 3% of the coating agent, the coating agent either cannot be suspended in the water at the elevated temperature, or the coating agent can be suspended in the water at the higher temperature but then crashes out as the temperature is reduced, thus preventing coatings from being able to be formed from the mixture.
Additionally, if the concentration of compounds of Formula II and/or III is too high, the performance of the resulting coatings can be degraded. For example, as shown in
In view of the above, compositions (e.g., coating agents) can include a first group of compounds that includes one or more compounds of Formula I (e.g., fatty acids or esters thereof) and a second group of compounds that includes one or more salts of Formula II or Formula III (e.g., fatty acid salts). The compound(s) of Formula I and/or the salt(s) of Formula II or III can optionally have a carbon chain length of at least 14. A mass ratio of the first group of compounds (e.g., compounds of Formula I such as fatty acids or esters, including monoacylglycerides) to the second group of compounds (salts of Formula II or III, e.g., fatty acid salts) can, for example, be in a range of about 2 to 200, for example about 2 to 100, 2 to 99, 2 to 90, 2 to 80, 2 to 70, 2 to 60, 2 to 50, 2 to 40, 2 to 30, 2 to 25, 2 to 20, 2 to 15, 2 to 10, 2.5 to 200, 2.5 to 100, 2.5 to 90, 2.5 to 80, 2.5 to 70, 2.5 to 60, 2.5 to 50, 2.5 to 40, 2.5 to 30, 2.5 to 25, 2.5 to 20, 2.5 to 15, 2.5 to 10, 3 to 200, 3 to 100, 3 to 90, 3 to 80, 3 to 70, 3 to 60, 3 to 50, 3 to 40, 3 to 30, 3 to 25, 3 to 20, 3 to 15, 3 to 10, 4 to 200, 4 to 100, 4 to 90, 4 to 80, 4 to 70, 4 to 60, 4 to 50, 4 to 40, 4 to 30, 4 to 25, 4 to 20, 4 to 15, 4 to 10, 5 to 200, 5 to 100, 5 to 90, 5 to 80, 5 to 70, 5 to 60, 5 to 50, 5 to 40, 5 to 30, 5 to 25, 5 to 20, 5 to 15, 5 to 10, 10 to 100, 10 to 99, 10 to 90, 10 to 80, 10 to 70, 10 to 60, 10 to 50, 10 to 40, 10 to 30, 10 to 25, 10 to 20, 10 to 15, 15 to 100, 15 to 99, 15 to 90, 15 to 80, 15 to 70, 15 to 60, 15 to 50, 15 to 40, 15 to 30, 15 to 25, or 15 to 20.
As described above, the coating agent can be added to or dissolved, suspended, or dispersed in a solvent to form a colloid, suspension, or solution. The various components of the coating agent (e.g., the compounds of Formula I and the salts) can be combined prior to being added to the solvent and then added to the solvent together. Alternatively, the components of the coating agent can be kept separate from one another and then be added to the solvent consecutively (or at separate times).
The concentration of the first group of compounds (compounds of Formula I) in the solvent/solution/suspension/colloid can, for example, be in a range of about 1 mg/mL to about 200 mg/mL, such as about 1 to 150 mg/mL, 1 to 100 mg/mL, 1 to 90 mg/mL, 1 to 80 mg/mL, 1 to 75 mg/mL, 1 to 70 mg/mL, 1 to 65 mg/mL, 1 to 60 mg/mL, 1 to 55 mg/mL, 1 to 50 mg/mL, 1 to 45 mg/mL, 1 to 40 mg/mL, 2 to 200 mg/mL, 2 to 150 mg/mL, 2 to 100 mg/mL, 2 to 90 mg/mL, 2 to 80 mg/mL, 2 to 75 mg/mL, 2 to 70 mg/mL, 2 to 65 mg/mL, 2 to 60 mg/mL, 2 to 55 mg/mL, 2 to 50 mg/mL, 2 to 45 mg/mL, 2 to 40 mg/mL, 5 to 200 mg/mL, 5 to 150 mg/mL, 5 to 100 mg/mL, 5 to 90 mg/mL, 5 to 80 mg/mL, 5 to 75 mg/mL, 5 to 70 mg/mL, 5 to 65 mg/mL, 5 to 60 mg/mL, 5 to 55 mg/mL, 5 to 50 mg/mL, 5 to 45 mg/mL, 5 to 40 mg/mL, 10 to 200 mg/mL, 10 to 150 mg/mL, 10 to 100 mg/mL, 10 to 90 mg/mL, 10 to 80 mg/mL, 10 to 75 mg/mL, 10 to 70 mg/mL, 10 to 65 mg/mL, 10 to 60 mg/mL, 10 to 55 mg/mL, 10 to 50 mg/mL, 10 to 45 mg/mL, or 10 to 40 mg/mL.
The concentration of the second group of compounds (salts of Formula II or Formula III, e.g., fatty acid salts) in the solvent/solution/suspension/colloid can, for example, be in a range of about 0.01 mg/mL to about 80 mg/mL, such as about 0.01 to 75 mg/mL, 0.01 to 70 mg/mL, 0.01 to 65 mg/mL, 0.01 to 60 mg/mL, 0.01 to 55 mg/mL, 0.01 to 50 mg/mL, 0.01 to 45 mg/mL, 0.01 to 40 mg/mL, 0.01 to 35 mg/mL, 0.01 to 30 mg/mL, 0.01 to 25 mg/mL, 0.01 to 20 mg/mL, 0.01 to 15 mg/mL, 0.01 to 10 mg/mL, 0.1 to 80 mg/mL, 0.1 to 75 mg/mL, 0.1 to 70 mg/mL, 0.1 to 65 mg/mL, 0.1 to 60 mg/mL, 0.1 to 55 mg/mL, 0.1 to 50 mg/mL, 0.1 to 45 mg/mL, 0.1 to 40 mg/mL, 0.1 to 35 mg/mL, 0.1 to 30 mg/mL, 0.1 to 25 mg/mL, 0.1 to 20 mg/mL, 0.1 to 15 mg/mL, 0.1 to 10 mg/mL, 1 to 80 mg/mL, 1 to 75 mg/mL, 1 to 70 mg/mL, 1 to 65 mg/mL, 1 to 60 mg/mL, 1 to 55 mg/mL, 1 to 50 mg/mL, 1 to 45 mg/mL, 1 to 40 mg/mL, 1 to 35 mg/mL, 1 to 30 mg/mL, 1 to 25 mg/mL, 1 to 20 mg/mL, 1 to 15 mg/mL, 1 to 10 mg/mL, 2 to 80 mg/mL, 2 to 75 mg/mL, 2 to 70 mg/mL, 2 to 65 mg/mL, 2 to 60 mg/mL, 2 to 55 mg/mL, 2 to 50 mg/mL, 2 to 45 mg/mL, 2 to 40 mg/mL, 2 to 35 mg/mL, 2 to 30 mg/mL, 2 to 25 mg/mL, 2 to 20 mg/mL, 2 to 15 mg/mL, or 2 to 10 mg/mL.
The concentration of the composition (e.g., the coating agent) in the solvent/solution/suspension/colloid can, for example, be in a range of about 1 mg/mL to about 200 mg/mL, such as about 1 to 150 mg/mL, 1 to 100 mg/mL, 1 to 90 mg/mL, 1 to 80 mg/mL, 1 to 75 mg/mL, 1 to 70 mg/mL, 1 to 65 mg/mL, 1 to 60 mg/mL, 1 to 55 mg/mL, 1 to 50 mg/mL, 1 to 45 mg/mL, 1 to 40 mg/mL, 2 to 200 mg/mL, 2 to 150 mg/mL, 2 to 100 mg/mL, 2 to 90 mg/mL, 2 to 80 mg/mL, 2 to 75 mg/mL, 2 to 70 mg/mL, 2 to 65 mg/mL, 2 to 60 mg/mL, 2 to 55 mg/mL, 2 to 50 mg/mL, 2 to 45 mg/mL, 2 to 40 mg/mL, 5 to 200 mg/mL, 5 to 150 mg/mL, 5 to 100 mg/mL, 5 to 90 mg/mL, 5 to 80 mg/mL, 5 to 75 mg/mL, 5 to 70 mg/mL, 5 to 65 mg/mL, 5 to 60 mg/mL, 5 to 55 mg/mL, 5 to 50 mg/mL, 5 to 45 mg/mL, 5 to 40 mg/mL, 10 to 200 mg/mL, 10 to 150 mg/mL, 10 to 100 mg/mL, 10 to 90 mg/mL, 10 to 80 mg/mL, 10 to 75 mg/mL, 10 to 70 mg/mL, 10 to 65 mg/mL, 10 to 60 mg/mL, 10 to 55 mg/mL, 10 to 50 mg/mL, 10 to 45 mg/mL, or 10 to 40 mg/mL.
As also described above and demonstrated in the examples below, the coating solutions/suspensions/colloids can further include a wetting agent that serves to reduce the contact angle between the solution/suspension/colloid and the surface of the substrate being coated. The wetting agent can be included as a component of the coating agent and therefore added to the solvent at the same time as other components of the coating agent. Alternatively, the wetting agent can be separate from the coating agent and can be added to the solvent either before, after, or at the same time as the coating agent. Alternatively, the wetting agent can be separate from the coating agent, and can be applied to a surface before the coating agent in order to prime the surface.
The wetting agent can be a fatty acid or salt or ester thereof. The wetting agent can be a compound or group of compounds of Formula I, II, or III, where Formulas I, II, and III are given above. In particular, the wetting agent compounds can each have a carbon chain length of 13 or less. For example, the carbon chain length can be, 7, 8, 9, 10, 11, 12, 13, in a range of 7 to 13, or in a range of 8 to 12. The wetting agent can also or alternatively be one or more of a phospholipid, a lysophospholipid, a glycoglycerolipid, a glycolipid (for example, sucrose esters of fatty acids), an ascorbyl ester of a fatty acid, an ester of lactic acid, an ester of tartaric acid, an ester of malic acid, an ester of fumaric acid, an ester of succinic acid, an ester of citric acid, an ester of pantothenic acid, or a fatty alcohol derivative (e.g., an alkyl sulfate). In some embodiments, the wetting agents included in the mixtures herein are edible and/or safe for consumption.
Prior to adding the wetting agent to the solvent (and either before or after adding the coating agent for cases where the wetting agent and coating agent are separate), the contact angle between the solvent/solution/suspension/colloid and carnauba, candelilla, or paraffin wax can be at least about 70°, for example at least about 75°, at least about 80°, at least about 85°, or at least about 90°. After adding the wetting agent to the solvent (and either before or after adding the coating agent for cases where the wetting agent and coating agent are separate), the contact angle between the resulting solution/suspension/colloid and carnauba, candelilla, or paraffin wax can be less than 85°, for example less than about 80°, less than about 75°, less than about 70°, less than about 65°, less than about 60°, less than about 55°, less than about 50°, less than about 45°, less than about 40°, less than about 35°, less than about 30°, less than about 25°, less than about 20°, less than about 15°, less than about 10°, less than about 5°, or about 0°.
Because the wetting agents can in many cases damage the substrate being coated, the concentration of the wetting agent compounds can be less than that of the other components of the coating agent. However, if the concentration of the wetting agents added to the solvent is too low, the surface energy of the resulting solution/suspension/colloid may not be substantially different from that of the solvent, in which case improved surface wetting of the substrate may not be achieved.
In some embodiments, compounds used as wetting agents can also (or alternatively) be used as emulsifiers. For example, in some embodiments, a medium chain fatty acid (e.g., having a carbon chain length of 7, 8, 9, 10, 11, 12, or 13) or salt or ester thereof is used as an emulsifier (and optionally also functions as a wetting agent) in the composition, thereby enabling the composition to be dissolved or suspended in the solvent. In some embodiments, a phospholipid, a lysophospholipid, a glycoglycerolipid, a glycolipid (for example, sucrose esters of fatty acids), an ascorbyl ester of a fatty acid, an ester of lactic acid, an ester of tartaric acid, an ester of malic acid, an ester of fumaric acid, an ester of succinic acid, an ester of citric acid, an ester of pantothenic acid, or a fatty alcohol derivative (e.g. an alkyl sulfate), is included in the composition and functions as an emulsifier (and optionally also functions as a wetting agent). In some embodiments, the emulsifier is cationic. In some embodiments, the emulsifier is anionic.
In some embodiments, the emulsifier is zwitterionic. In some embodiments, the emulsifier is uncharged.
In some embodiments, the composition (e.g., coating or coating agent) comprises one or more (e.g., 1, 2, or 3) wetting agents, surfactants, and/or emulsifiers. In some embodiments, the one or more wetting agents, surfactants, and/or emulsifiers comprise sodium bicarbonate, citric acid, cetyl trimethylammonium bromide, sodium lauryl sulfate, ammonium lauryl sulfate, sodium laureth sulfate, sodium myreth sulfate, docusate, sodium dodecyl sulfate, sodium stearate, sodium lauroyl sarcosinate, perfluorononanoate, perfluorooctanoate, perfluorooctanesulfonate (PFOS), perfluorobutanesulfonate, alkyl-aryl ether phosphates, alkyl ether phosphates, 2-[4-(2,4,4-trimethylpentan-2-yl)phenoxy]ethanol (Triton X-100), 3-[(3-Cholamidopropyl)dimethylammonio]-1-propanesulfonate (CHAPS), cholic acid, nonyl phenoxypolyethoxylethanol (NP-40), octyl thioglucoside, octyl glucoside, dodecyl maltoside, octenidine dihydrochloride, cetrimonium bromide (CTAB), cetylpyridinium chloride (CPC), benzalkonium chloride (BAC), benzethonium chloride (BZT), dimethyldioctadecylammonium chloride, and dioctadecyldimethylammonium bromide (DODAB), cocamidopropyl hydroxysultaine, cocamidopropyl betaine, phosphatidylserine, phosphatidylethanolamine, phosphatidylcholine, phosphatidylinositol, phosphatidic acid, lysophosphatidylserine, lysophosphatidylethanolamine, lysophosphatidylcholine, lysophosphatidylinositol, lysophosphatidic acid, sphingomyelins, lauryldimethylamine oxide, myristamine oxide, octaethylene glycol monododecyl ether, pentaethylene glycol monododecyl ether, polyethoxylated tallow amine, cocamide monoethanolamine, cocamide diethanolamine, poloxamers, fatty acid esters of polyhydroxy compounds, fatty acid esters of glycerol, glycerol monostearate, glycerol monolaurate, fatty acid esters of sorbitol, sorbitan monolaurate, sorbitan monostearate, sorbitan tristearate, Tween 20, Tween 40, Tween 60, Tween 80, fatty acid esters of sucrose, alkyl polyglucosides, alkyl polyglycoside, decyl glucoside, lauryl glucoside, octyl glucoside, fatty acid esters of sucrose, sucrose monostearate, sucrose distearate, sucrose tristearate, sucrose polystearate, sucrose monopalmitate, sucrose dipalmitate, sucrose tripalmitate, sucrose polypalmitate, sucrose monomyri state, sucrose dimyri state, sucrose trimyristate, sucrose polymyristate, sucrose monolaurate, sucrose dilaurate, sucrose trilaurate, or sucrose polylaurate. For example, the one or more wetting agents, surfactants, and/or emulsifiers comprises sodium lauryl sulfate. For example, the one or more wetting agents, surfactants, and/or emulsifiers comprises sodium bicarbonate. For example, the one or more wetting agents, surfactants, and/or emulsifiers comprises citric acid.
In some embodiments, the mixture or composition (e.g., coating or coating agent) comprises from about 0.1% to about 40% by weight of the one or more wetting agents, surfactants, and/or emulsifiers. For example, the mixture or composition (e.g., coating or coating agent) comprises from about 0.1% to about 35%, from about 0.1% to about 30%, from about 0.1% to about 25%, from about 0.1% to about 20%, from about 0.1% to about 15%, from about 0.1% to about 10%, from about 0.1% to about 8%, from about 0.1% to about 6%, from about 0.1% to about 5%, from about 0.1% to about 4%, from about 0.1% to about 3%, from about 0.1% to about 2%, from about 0.1% to about 1%, from about 0.1% to about 0.5%, from about 1% to about 40%, from about 1% to about 30%, from about 1% to about 20%, from about 1% to about 15%, from about 1% to about 10%, from about 1% to about 5%, from about 3% to about 9%, from about 5% to about 10%, from about 10% to about 20%, from about 20% to about 30%, from about 30% to about 40%, from about 20% to about 40%, from about 25% to about 35%, about 0.1%, about 1%, about 2%, about 3%, about 4%, about 5%, about 6%, about 7%, about 8%, about 9%, about 29%, about 30%, or about 31%.
In some embodiments, the mixture or composition (e.g., coating or coating agent) comprises one or more (e.g., 1, 2, or 3) preservatives. In some embodiments, the one or more preservatives comprise one or more antioxidants, one or more antimicrobial agents, one or more chelating agents, or any combination thereof. Exemplary preservatives include, but are not limited to, vitamin E, vitamin C, butylatedhydroxyanisole (BHA), butylatedhydroxytoluene (BHT), sodium benzoate, disodium ethylenediaminetetraacetic acid (EDTA), citric acid, benzyl alcohol, benzalkonium chloride, butyl paraben, chlorobutanol, meta cresol, chlorocresol, methyl paraben, phenyl ethyl alcohol, propyl paraben, phenol, benzonic acid, sorbic acid, methyl paraben, propyl paraben, bronidol, and propylene glycol.
In some embodiments, the mixture or composition (e.g., coating or coating agent) comprises from about 0.1% to about 40% by weight of the one or more preservatives. For example, the mixture or composition (e.g., coating or coating agent) comprises from about 0.1% to about 35%, from about 0.1% to about 30%, from about 0.1% to about 25%, from about 0.1% to about 20%, from about 0.1% to about 15%, from about 0.1% to about 10%, from about 0.1% to about 8%, from about 0.1% to about 6%, from about 0.1% to about 5%, from about 0.1% to about 4%, from about 0.1% to about 3%, from about 0.1% to about 2%, from about 0.1% to about 1%, from about 0.1% to about 0.5%, from about 1% to about 40%, from about 1% to about 30%, from about 1% to about 20%, from about 1% to about 15%, from about 1% to about 10%, from about 1% to about 5%, from about 3% to about 9%, from about 5% to about 10%, from about 10% to about 20%, from about 20% to about 30%, from about 30% to about 40%, about 0.1%, about 1%, about 2%, about 3%, about 4%, about 5%, about 6%, about 7%, about 8%, or about 9%.
In view of the above, any of the compositions (e.g., coating agents) described herein can include a first group of compounds of Formulas I, II, and/or III (e.g., fatty acids and/or salts or esters thereof) and a second group of compounds of Formulas I, II, and/or III (e.g., fatty acids and/or salts or esters thereof), where each compound of the first group of compounds has a carbon chain length of at least 14, and each compound of the second group of compounds has a carbon chain length of 13 or less, for example in a range of 7 to 13. The first and second groups of compounds can each, for example, include ethyl esters, methyl esters, glyceryl esters (e.g., monoacylglycerides such as 1-monoacylglycerides or 2-monoacylglycerides), sodium salts of fatty acids, potassium salts of fatty acids, calcium salts of fatty acids, magnesium salts of fatty acids, or combinations thereof. In some embodiments, any of the compositions described herein can include a first group of compounds of Formula I, (e.g., fatty acids and/or esters thereof) and a second group of compounds, where the second group of compounds function as an emulsifier (e.g. is a fatty acid salt, a phospholipid, a lysophospholipid, a glycoglyceroiipid, a giycolipid (for example, sucrose esters of fatty acids), an ascorbyl ester of a fatty acid, an ester of lactic acid, an ester of tartaric acid, an ester of malic acid, an ester of fumaric acid, an ester of succinic acid, an ester of citric acid, an ester of pantothenic acid, or a fatty alcohol derivative (e.g. an alkyl sulfate).
A mass ratio of the fatty acids and/or esters in the first group of compounds to the emulsifiers in the second group of compounds can be in any of the ranges given previously (e.g., a range such that the solubility of the coating agent in the solvent is sufficient to allow the desired coating agent concentration to be dissolved, suspended, or dispersed in the solvent). A mass ratio of the first group of compounds (carbon chain length of at least 14) to the second group of compounds (carbon chain length of 13 or less, or emulsifier) can be in a range of about 2 to 200, for example about 2 to 100, 2 to 90, 2 to 80, 2 to 70, 2 to 60, 2 to 50, 2 to 40, 2 to 30, 2 to 25, 2 to 20, 2 to 15, 2 to 10, 2.5 to 200, 2.5 to 100, 2.5 to 90, 2.5 to 80, 2.5 to 70, 2.5 to 60, 2.5 to 50, 2.5 to 40, 2.5 to 30, 2.5 to 25, 2.5 to 20, 2.5 to 15, 2.5 to 10, 3 to 200, 3 to 100, 3 to 90, 3 to 80, 3 to 70, 3 to 60, 3 to 50, 3 to 40, 3 to 30, 3 to 25, 3 to 20, 3 to 15, 3 to 10, 4 to 200, 4 to 100, 4 to 90, 4 to 80, 4 to 70, 4 to 60, 4 to 50, 4 to 40, 4 to 30, 4 to 25, 4 to 20, 4 to 15, 4 to 10, 5 to 200, 5 to 100, 5 to 90, 5 to 80, 5 to 70, 5 to 60, 5 to 50, 5 to 40, 5 to 30, 5 to 25, 5 to 20, 5 to 15, or 5 to 10.
As shown in
As shown in
As seen in
As described above, the coating agent can be added to or dissolved, suspended, or dispersed in a solvent to form a suspension, colloid, or solution. The various components of the coating agent (e.g., the compounds of Formula I, the salts of Formula II and/or III, and/or the wetting agents) can be combined prior to being added to the solvent and then added to the solvent together. Alternatively, at least some of the components of the coating agent can be kept separate from other components and can be added to the solvent consecutively (or at separate times).
The concentration of the first group of compounds (compounds of Formula I, II and/or III having a carbon chain length of at least 14) in the solvent/solution/suspension/colloid can, for example, be in a range of about 1 mg/mL to about 200 mg/mL, such as about 1 to 150 mg/mL, 1 to 100 mg/mL, 1 to 90 mg/mL, 1 to 80 mg/mL, 1 to 75 mg/mL, 1 to 70 mg/mL, 1 to 65 mg/mL, 1 to 60 mg/mL, 1 to 55 mg/mL, 1 to 50 mg/mL, 1 to 45 mg/mL, 1 to 40 mg/mL, 2 to 200 mg/mL, 2 to 150 mg/mL, 2 to 100 mg/mL, 2 to 90 mg/mL, 2 to 80 mg/mL, 2 to 75 mg/mL, 2 to 70 mg/mL, 2 to 65 mg/mL, 2 to 60 mg/mL, 2 to 55 mg/mL, 2 to 50 mg/mL, 2 to 45 mg/mL, 2 to 40 mg/mL, 5 to 200 mg/mL, 5 to 150 mg/mL, 5 to 100 mg/mL, 5 to 90 mg/mL, 5 to 80 mg/mL, 5 to 75 mg/mL, 5 to 70 mg/mL, 5 to 65 mg/mL, 5 to 60 mg/mL, 5 to 55 mg/mL, 5 to 50 mg/mL, 5 to 45 mg/mL, 5 to 40 mg/mL, 10 to 200 mg/mL, 10 to 150 mg/mL, 10 to 100 mg/mL, 10 to 90 mg/mL, 10 to 80 mg/mL, 10 to 75 mg/mL, 10 to 70 mg/mL, 10 to 65 mg/mL, 10 to 60 mg/mL, 10 to 55 mg/mL, 10 to 50 mg/mL, 10 to 45 mg/mL, or 10 to 40 mg/mL.
The concentration of wetting agents or second group of compounds of Formula I, II, and/or III (e.g., compounds of Formula I and/or salts of Formula II and/or III having a carbon chain length of 13 or less) in the solvent/solution/suspension/colloid can, for example, be about 0.01 mg/mL to about 20 mg/mL, such as about 0.01 mg/mL to 15 mg/mL, 0.01 mg/mL to 12 mg/mL, 0.01 mg/mL to 10 mg/mL, 0.01 mg/mL to 9 mg/mL, 0.01 mg/mL to 8 mg/mL, 0.01 mg/mL to 7 mg/mL, 0.01 mg/mL to 6 mg/mL, 0.01 mg/mL to 5 mg/mL, 0.1 mg/mL to 20 mg/mL, 0.1 mg/mL to 15 mg/mL, 0.1 mg/mL to 12 mg/mL, 0.1 mg/mL to 10 mg/mL, 0.1 mg/mL to 9 mg/mL, 0.1 mg/mL to 8 mg/mL, 0.1 mg/mL to 7 mg/mL, 0.1 mg/mL to 6 mg/mL, 0.1 mg/mL to 5 mg/mL, 0.5 mg/mL to 20 mg/mL, 0.5 mg/mL to 15 mg/mL, 0.5 mg/mL to 12 mg/mL, 0.5 mg/mL to 10 mg/mL, 0.5 mg/mL to 9 mg/mL, 0.5 mg/mL to 8 mg/mL, 0.5 mg/mL to 7 mg/mL, 0.5 mg/mL to 6 mg/mL, or 0.5 mg/mL to 5 mg/mL.
The composition that is added to the solvent (e.g., the coating agent) can be composed from about 50% to about 99.9% (e.g., about 60%-99.9%, 65%-99.9%, 70%-99.9%, 75%-99.9%, 80%-99.9%, 85%-99.9%, 90%-99.9%, 50%-99%, 60%-99%, 65%-99%, 70%-99%, 75%-99%, 80%-99%, 85%-99%, 90%-99%, 50%-98%, 60%-98%, 65%-98%, 70%-98%, 75%-98%, 80%-98%, 85%-98%, 90%-98%, 50%-96%, 60%-96%, 65%-96%, 70%-96%, 75%-96%, 80%-96%, 85%-96%, 90%-96%, 50%-94%, 60%-94%, 65%-94%, 70%-94%, 75%-94%, 80%-94%, 85%-94%, or 90%-94%) by mass of a first group of compounds of fatty acids, fatty acid esters, fatty acid salts, or combinations thereof (e.g., compounds of Formula I and/or salts of Formula II or Formula III), where optionally each compound of the first group optionally has a carbon chain length of at least 14. In some embodiments, the compounds of the first group are fatty acid esters, e.g., monoacylglycerides.
The composition that is added to the solvent (e.g., the coating agent) can be composed from about 0.1% to about 50% (e.g., about 0.1%-45%, 0.1%-40%, 0.1%-35%, 0.1%-30%, 0.1%-25%, 0.1%-20%, 0.1%-15%, 0.1%-10%, 0.1%-8%, 0.1%-6%, 0.1%-5%, 0.1%-4%, 0.4%-50%, 0.4%-45%, 0.4%-40%, 0.4%-35%, 0.4%-30%, 0.4%-25%, 0.4%-20%, 0.4%-15%, 0.4%-10%, 0.4%-8%, 0.4%-6%, 0.4%-5%, 0.4%-4%, 0.7%-50%, 0.7%-45%, 0.7%-40%, 0.7%-35%, 0.7%-30%, 0.7%-25%, 0.7%-20%, 0.7%-15%, 0.7%-10%, 0.7%-8%, 0.7%-6%, 0.7%-5%, 0.7%-4%, 1%-50%, 1%-45%, 1%-40%, 1%-35%, 1%-30%, 1%-25%, 1%-20%, 1%-15%, 1%-10%, 1%-8%, 1%-6%, 1%-5%, or 1%-4%) by mass of a second group of compounds of fatty acids, fatty acid esters, fatty acid salts, or combinations thereof (e.g., compounds of Formula I and/or salts of Formula II and/or III), where each compound of the second group optionally has a carbon chain length of 13 or less (e.g., a carbon chain length in a range of 7 to 13). The compounds of the second group can function as wetting agents, as previously described.
The composition that is added to the solvent (e.g., the coating agent) can be composed from about 0.1% to about 50% (e.g., about 0.1%-45%, 0.1%-40%, 0.1%-35%, 0.1%-30%, 0.1%-25%, 0.1%-20%, 0.1%-15%, 0.1%-10%, 0.1%-8%, 0.1%-6%, 0.1%-5%, 0.1%-4%, 0.4%-50%, 0.4%-45%, 0.4%-40%, 0.4%-35%, 0.4%-30%, 0.4%-25%, 0.4%-20%, 0.4%-15%, 0.4%-10%, 0.4%-8%, 0.4%-6%, 0.4%-5%, 0.4%-4%, 0.7%-50%, 0.7%-45%, 0.7%-40%, 0.7%-35%, 0.7%-30%, 0.7%-25%, 0.7%-20%, 0.7%-15%, 0.7%-10%, 0.7%-8%, 0.7%-6%, 0.7%-5%, 0.7%-4%, 1%-50%, 1%-45%, 1%-40%, 1%-35%, 1%-30%, 1%-25%, 1%-20%, 1%-15%, 1%-10%, 1%-8%, 1%-6%, 1%-5%, or 1%-4%) by mass of a third group of compounds comprised of salts of compounds of Formula II or Formula III, or fatty acid salts. Each compound of the third group can optionally have a carbon chain length greater than 13. The compounds of the third group can function as emulsifiers and, for example, increase the solubility of the coating agent, as previously described.
Any of the coating solutions/suspensions/colloids described herein can further include an antimicrobial agent, for example ethanol or citric acid. In some embodiments, the antimicrobial agent is part of or a component of the solvent. Any of the coating solutions described herein can further include other components or additives such as sodium bicarbonate.
Any of the coating agents described herein can further include additional materials that are also transported to the surface with the coating, or are deposited separately and are subsequently encapsulated by the coating (e.g., the coating is formed at least partially around the additional material), or are deposited separately and are subsequently supported by the coating (e.g., the additional material is anchored to the external surface of the coating). Examples of such additional materials can include cells, biological signaling molecules, vitamins, minerals, pigments, aromas, enzymes, catalysts, antifungals, antimicrobials, and/or time-released drugs. The additional materials can be non-reactive with surface of the coated product and/or coating, or alternatively can be reactive with the surface and/or coating.
In some embodiments, the coating can include an additive configured, for example, to modify the viscosity, vapor pressure, surface tension, or solubility of the coating. The additive can, for example, be configured to increase the chemical stability of the coating. For example, the additive can be an antioxidant configured to inhibit oxidation of the coating. In some embodiments, the additive can reduce or increase the melting temperature or the glass-transition temperature of the coating. In some embodiments, the additive is configured to reduce the diffusivity of water vapor, oxygen, CO2, or ethylene through the coating or enable the coating to absorb more ultra violet (UV) light, for example to protect the agricultural product (or any of the other products described herein). In some embodiments, the additive can be configured to provide an intentional odor, for example a fragrance (e.g., smell of flowers, fruits, plants, freshness, scents, etc.). In some embodiments, the additive can be configured to provide color and can include, for example, a dye or a US Food and Drug Administration (FDA) approved color additive.
Any of the coating agents or coatings formed thereof that are described herein can be flavorless or have high flavor thresholds, e.g. above 500 ppm, and can be odorless or have a high odor threshold. In some embodiments, the materials included in any of the coatings described herein can be substantially transparent. For example, the coating agent, the solvent, and/or any other additives included in the coating can be selected so that they have substantially the same or similar indices of refraction. By matching their indices of refraction, they may be optically matched to reduce light scattering and improve light transmission. For example, by utilizing materials that have similar indices of refraction and have a clear, transparent property, a coating having substantially transparent characteristics can be formed.
The compositions (e.g., coating agents) described herein can be of high purity. For example, the compositions can be substantially free (e.g., be less than 10% by mass, less than 9% by mass, less than 8% by mass, less than 7% by mass, less than 6% by mass, or less than 5%, 4%, 3%, 2%, or 1% by mass) of diglycerides, triglycerides, acetylated monoglycerides, proteins, polysaccharides, phenols, lignans, aromatic acids, terpenoids, flavonoids, carotenoids, alkaloids, alcohols, alkanes, and/or aldehydes. In some embodiments, the compositions comprise less than 10% (e.g., less than 9%, 8%, 7%, 6%, 5%, 4%, 3%, 2%, or 1%) by mass of diglycerides. In some embodiments, the compositions comprise less than 10% (e.g., less than 9%, 8%, 7%, 6%, 5%, 4%, 3%, 2%, or 1%) by mass of triglycerides. In some embodiments, the compositions comprise less than 10% (e.g., less than 9%, 8%, 7%, 6%, 5%, 4%, 3%, 2%, or 1%) by mass of acetylated monoglycerides.
Any of the coatings described herein can be disposed on the external surface of an agricultural product or other substrate using any suitable means. For example, the substrate can be dip-coated in a bath of the coating formulation (e.g., an aqueous or mixed aqueous-organic or organic solution). The deposited coating can form a thin layer on the surface of an agricultural product, which can protect the agricultural product from biotic stressors, water loss, respiration, and/or oxidation. In some embodiments, the deposited coating can have a thickness of less than 20 microns, less than 10 microns, less than 9 microns, less than 8 microns, less than 7 microns, less than 6 microns, less than 5 microns, less than 4 microns, less than 3 microns, less than 2 microns, less than about 1.5 microns, about 100 nm to about 20 microns, about 100 nm to about 2 microns, about 700 nm to about 1.5 microns, 700 nm to about 1 micron, about 1 micron to about 1.6 microns, about 1.2 microns to about 1.5 microns, and/or the coating can be transparent to the naked eye. For example, the deposited coating can have a thickness of about 10 nm, about 20 nm, about 30 nm, about 40 nm, about 50 nm, about 100 nm, about 150 nm, about 200 nm, about 250 nm, about 300 nm, about 350 nm, about 400 nm, about 450 nm, about 500 nm, about 550 nm, about 600 nm, about 650 nm, about 700 nm, about 750 nm, about 800 nm, about 850 nm, about 900 nm, about 950 nm, 1,000 nm, about 1,100 nm, about 1,200 nm, about 1,300 nm, about 1,350 nm, about 1,400 nm, about 1,500 nm, about 1,600 nm, about 1,700 nm, about 1,800 nm, about 1,900 nm, about 2,000 nm, about 2,100 nm, about 2,200 nm, about 2,300 nm, about 2,400 nm, about 2,500 nm, about 2,600 nm, about 2,700 nm, about 2,800 nm, about 2,900 nm, or about 3,000 nm, inclusive of all ranges therebetween.
In some embodiments, the deposited coating can be deposited substantially uniformly over the substrate and can be free of defects and/or pinholes. In some embodiments, the dip-coating process can include sequential coating of the agricultural product in baths of coating precursors that can undergo self-assembly or covalent bonding on the agricultural product to form the coating. In some embodiments, the coating can be deposited on agricultural products by passing the agricultural products under a stream of the coating solution/suspension/colloid (e.g., a waterfall of the coating solution/suspension/colloid). For example, the agricultural products can be disposed on a conveyor that passes through the stream of the coating solution/suspension/colloid. In some embodiments, the coating can be misted, vapor- or dry vapor-deposited on the surface of the agricultural product. In some embodiments, the coating solution/suspension/colloid can be mechanically applied to the surface of the product to be coated, for example by brushing it onto the surface. In some embodiments, the coating can be configured to be fixed on the surface of the agricultural product by UV crosslinking or by exposure to a reactive gas, for example oxygen.
In some embodiments, the coating solutions/suspensions/colloids can be spray-coated on the agricultural products. Commercially available sprayers can be used for spraying the coating solutions/suspensions/colloids onto the agricultural product. In some embodiments, the coating formulation can be electrically charged in the sprayer before spray-coating on to the agricultural product, such that the deposited coating electrostatically and/or covalently bonds to the exterior surface of the agricultural product.
In some embodiments, coatings formed from coating agents described herein over agricultural products can be configured to change the surface energy of the agricultural product. Various properties of coatings described herein can be adjusted by tuning the crosslink density of the coating, its thickness, or its chemical composition. This can, for example, be used to control the ripening of postharvest fruit or produce. For example, coatings formed from coating agents that primarily include bifunctional or polyfunctional monomer units can, for example, have higher crosslink densities than those that include monofunctional monomer units. Thus, coatings formed from bifunctional or polyfunctional monomer units can in some cases result in slower rates of ripening as compared to coatings formed from monofunctional monomer units.
In some embodiments, one or more wetting agents such as those described above are used to improve the wetting of the surfaces to which the coating solutions/suspensions/colloids are applied, but the wetting agent are not included in the coating solutions/suspensions/colloids. Instead, the wetting agents are added to a second solvent (which can be the same as or different than the solvent to which the coating agent is added) to form a second mixture, and the second mixture is applied to the surface to be coated prior to applying the coating solution/suspension/colloid to the surface. In this case, the second mixture can prime the surface to be coated such that the contact angle of the coating solution/suspension/colloid with the surface is less than it would have otherwise been, thereby improving surface wetting.
As previously described, the coatings formed from coating agents described herein can be configured to prevent water loss or other moisture loss from the coated portion of the plant, delay ripening, and/or prevent oxygen diffusion into the coated portion of the plant, for example, to reduce oxidation of the coated portion of the plant. The coatings can also serve as a barrier to diffusion of carbon dioxide and/or ethylene into or out of the plant or agricultural product. The coatings can also protect the coated portion of the plant against biotic stressors, such as, for example, bacteria, fungi, viruses, and/or pests that can infest and decompose the coated portion of the plant. Since bacteria, fungi and pests all identify food sources via recognition of specific molecules on the surface of the agricultural product, coating the agricultural products with the coating agent can deposit molecularly contrasting molecules on the surface of the portion of the plant, which can render the agricultural products unrecognizable. Furthermore, the coating can also alter the physical and/or chemical environment of the surface of the agricultural product making the surface unfavorable for bacteria, fungi or pests to grow. The coating can also be formulated to protect the surface of the portion of the plant from abrasion, bruising, or otherwise mechanical damage, and/or protect the portion of the plant from photodegradation. The portion of the plant can include, for example, a leaf, a stem, a shoot, a flower, a fruit, a root, etc.
Any of the coatings described herein can be used to reduce the humidity generated by agricultural products (e.g., fresh produce) via mass loss (e.g. water loss) during transportation and storage by reducing the mass loss rate of the agricultural products (e.g., fresh produce). For example, as seen in Example 16, the mass loss rate from a group of lemons coated with a 94:6 mixture of compounds of Formula I (SA-1G and PA-1G) and compounds of Formula II or Formula III (SA-Na) at 50 g/L in water was 0.37% per day, as compared to 1.61% per day for the untreated control group. This corresponded to a lower humidity in cold storage after 48 hours (i.e. 61% humidity) for the coated group as compared to the untreated group (i.e. 72% humidity).
In some embodiments, the agricultural product is coated with a composition that reduces the mass loss rate by at least 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90% or greater compared to untreated product measured. In some embodiments, treating an agricultural product using any of the coatings described herein can give a mass loss factor of at least 1.1, at least 1.2, at least 1.3, at least 1.4, at least 1.5, at least 1.6, at least 1.7, at least 1.8, at least 1.9, at least 2.0, at least 2.2, at least 2.4, at least 2.6, at least 2.8, at least 3.0. In some embodiments, treating an agricultural product using any of the coatings described herein can reduce the humidity generated during storage by at least 1%, 2%, 3%, 4%, 5%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90% or greater compared to untreated product. In some embodiments, the reduction in mass loss rate of the agricultural product can reduce the energy required to maintain a relative humidity at a predetermined level (e.g., at 90% relative humidity or less, at 85% relative humidity or less, at 80% relative humidity or less, at 75% relative humidity or less, at 70% relative humidity or less, at 65% relative humidity or less, at 60% relative humidity or less, at 55% relative humidity or less, at 50% relative humidity or less, or at 45% relative humidity or less) during storage or transportation. In some embodiments, the energy required to maintain a relative humidity at the predetermined level (e.g., any of the predetermined levels listed above) during storage or transportation can be reduced by at least 1%, 2%, 3%, 4%, 5%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90% or greater compared to untreated product.
Any of the coatings described herein can be used to reduce the heat generated by agricultural products (e.g., fresh produce) via respiration during transportation and storage by reducing the respiration rate of the agricultural products (e.g., fresh produce). As shown in Example 17, the energy usage to maintain a temperature (16° C.) of a group of avocados coated with a 94:6 mixture of compounds of Formula I (SA-1G and PA-1G) and compounds of Formula II or Formula III (SA-Na) at 50 g/L in water for 72 hours was 0.85 kWh, as compared to 1.19 kWh for the untreated control group. In some embodiments, the product is coated with a composition that reduces the respiration rate by at least 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90% or greater compared to untreated product (measured as described above). In some embodiments, the reduction in heat generated by the agricultural product can reduce the energy required to maintain a temperature (e.g., a predetermined temperature) during storage or transportation. In some embodiments, the heat generated can be reduced by at least 5%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90% or greater for coated products compared to untreated products. In some embodiments, the energy required to maintain the coated products at a predetermined temperature (e.g., at 25° C. or less, at 23° C. or less, at 20° C. or less, at 18° C. or less, at 15° C. or less, at 13° C. or less, at 10° C. or less, at 8° C. or less, at 5° C. or less, or at 3° C. or less) can be reduced by at least 1%, 2%, 3%, 4%, 5%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%, 90% or greater compared to untreated products.
Respiration rate approximations for various types of agricultural products (e.g., fresh produce) are shown below:
In some embodiments, the methods and compositions described herein are used to treat agricultural products (e.g., fresh produce) that are stored and/or transported in a refrigerated container or “reefer” 2400, illustrated schematically in
The methods and compositions described herein can also be used to minimize or reduce temperature or humidity gradients that arise from concentrating agricultural products (e.g., fresh produce) in stacks or pallets in order to prevent uneven ripening. The treated agricultural products (e.g., fresh produce) can be straight stacked during storage or can be stacked in an alternative fashion (e.g. cross stacked) to increase circulation around the agricultural products (e.g., fresh produce). Within the produce supply chain, boxes of agricultural products may be reoriented from a straight stack, which can be preferable during shipment, to a cross stack, which can be used during storage to increase air circulation and to prevent uneven ripening. As shown in
In some embodiments, treating an agricultural product with a coating that reduces the respiration rate can reduce the rate at which the temperature increases in a stack (e.g. upon removal from cold storage) by at least 0.5° C. per day, at least 1.0° C. per day, at least 1.5° C. per day, at least 2.0° C. per day, at least 2.5° C. per day, at least 3.0° C. per day, at least 3.5° C. per day, at least 4.0° C. per day, at least 4.5° C. per day, or at least 5° C. per day, as compared to an untreated stack. In some embodiments, treating an agricultural product with a coating that reduces the respiration rate can reduce the equilibrium temperature difference between the atmosphere and the average temperature of the stack by at least 0.5° C., at least 1.0° C., at least 1.5° C., at least 2.0° C., at least 2.5° C., at least 3.0° C., at least 3.5° C., at least 4.0° C., at least 4.5° C., or at least 5° C.
Any of the coatings described herein can be used to protect any agricultural product. In some embodiments, the coating can be coated on an edible agricultural product, for example, fruits, vegetables, edible seeds and nuts, herbs, spices, produce, meat, eggs, dairy products, seafood, grains, or any other consumable item. In such embodiments, the coating can include components that are non-toxic and safe for consumption by humans and/or animals. For example, the coating can include components that are U.S. Food and Drug Administration (FDA) approved direct or indirect food additives, FDA approved food contact substances, satisfy FDA regulatory requirements to be used as a food additive or food contact substance, and/or is an FDA Generally Recognized as Safe (GRAS) material. Examples of such materials can be found within the FDA Code of Federal Regulations Title 21, located at “www.accessdata.fda.gov/scripts/cdrh/cfdocs/cfcfr/cfrsearch.cfm”, the entire contents of which are hereby incorporated by reference herein. In some embodiments, the components of the coating can include a dietary supplement or ingredient of a dietary supplement. The components of the coating can also include an FDA approved food additive or color additive. In some embodiments, the coating can include components that are naturally derived, as described herein. In some embodiments, the coating can be flavorless or have a high flavor threshold of below 500 ppm, are odorless or have a high odor threshold, and/or are substantially transparent. In some embodiments, the coating can be configured to be washed off an edible agricultural product, for example, with water.
In some embodiments, the coatings described herein can be formed on an inedible agricultural product. Such inedible agricultural products can include, for example, inedible flowers, seeds, shoots, stems, leaves, whole plants, and the like. In such embodiments, the coating can include components that are non-toxic, but the threshold level for non-toxicity can be higher than that prescribed for edible products. In such embodiments, the coating can include an FDA approved food contact substance, an FDA approved food additive, or an FDA approved drug ingredient, for example, any ingredient included in the FDA's database of approved drugs, which can be found at “http://www.accessdata.fda.gov/scripts/cder/drugsatfda/index.cfm”, the entire contents of which are hereby incorporated herein by reference. In some embodiments, the coating can include materials that satisfy FDA requirements to be used in drugs or are listed within the FDA's National Drug Discovery Code Directory, “www.accessdata.fda.gov/scripts/cder/ndc/default.cfm”, the entire contents of which are hereby incorporated herein by reference. In some embodiments, the materials can include inactive drug ingredients of an approved drug product as listed within the FDA's database, “www.accessdata.fda.gov/scripts/cder/ndc/default.cfm”, the entire contents of which are hereby incorporated herein by reference.
Embodiments of the coatings described herein provide several advantages, including, for example: (1) the coatings can protect the agricultural products from biotic stressors, i.e. bacteria, viruses, fungi, or pests; (2) the coatings can prevent evaporation of water and/or diffusion of oxygen, carbon dioxide, and/or ethylene; (3) coating can help extend the shelf life of agricultural products, for example, post-harvest produce, without refrigeration; (4) the coatings can introduce mechanical stability to the surface of the agricultural products eliminating the need for expensive packaging designed to prevent the types of bruising which accelerate spoilage; (5) use of agricultural waste materials to obtain the coatings can help eliminate the breeding environments of bacteria, fungi, and pests; (6) the coatings can be used in place of pesticides to protect plants, thereby minimizing the harmful impact of pesticides to human health and the environment; (7) the coatings can be naturally derived and hence, safe for human consumption. Since in some cases the components of the coatings described herein can be obtained from agricultural waste, such coatings can be made at a relatively low cost. Therefore, the coatings can be particularly suited for small scale farmers, for example, by reducing the cost required to protect crops from pesticides and reducing post-harvest losses of agricultural products due to decomposition by biotic and/or environmental stressors.
Due to segmentation in the marketplace, the preparation/formation of coating agents or coating solutions/suspensions/colloids and the formation of coatings over substrates from the coating solutions/suspensions/colloids are often carried out by different parties or entities. For example, a manufacturer of compositions such as coating agents described herein (i.e., a first party) can form the compositions by one or more of the methods described herein. The manufacturer can then sell or otherwise provide the resulting composition to a second party, for example a farmer, shipper, distributor, or retailer of produce, and the second party can apply the composition to one or more agricultural products to form a protective coating over the products. Alternatively, the manufacturer can sell or otherwise provide the resulting composition to an intermediary party, for example a wholesaler, who then sells or otherwise provides the composition to a second party such as a farmer, shipper, distributor, or retailer of produce, and the second party can apply the composition to one or more agricultural products to form a protective coating over the products.
In some cases where multiple parties are involved, the first party may optionally provide instructions or recommendations about the composition (i.e., the coating agent), either written or oral, indicating one or more of the following: (i) that the composition is intended to be applied to a product for the purpose of coating or protecting the product, to extend the life of the product, to reduce spoilage of the product, or to modify or improve the aesthetic appearance of the product; (ii) conditions and/or methods that are suitable for applying the compositions to the surfaces of products; and/or (iii) potential benefits (e.g., extended shelf life, reduced rate of mass loss, reduced rate of molding and/or spoilage, etc.) that can result from the application of the composition to a product. While the instructions or recommendations may be supplied by the first party directly with the plant extract composition (e.g., on packaging in which the composition is sold or distributed), the instructions or recommendations may alternatively be supplied separately, for example on a website owned or controlled by the first party, or in advertising or marketing material provided by or on behalf of the first party.
In view of the above, it is recognized that in some cases, a party that manufactures compositions (i.e., coating agents) or coating solutions/suspensions/colloids according to one or more methods described herein (i.e., a first party) may not directly form a coating over a product from the composition, but can instead direct (e.g., can instruct or request) a second party to form a coating over a product from the composition. That is, even if the first party does not coat a product by the methods and compositions described herein, the first party may still cause the coating agent or solution to be applied to the product to form a protective coating over the product by providing instructions or recommendations as described above. Accordingly, as used herein, the act of applying a coating agent or solution/suspension/colloid to a product (e.g., a plant or agricultural product) also includes directing or instructing another party to apply the coating agent or solution to the product, thereby causing the coating agent or solution to be applied to the product.
Solvents
The solvent to which the coating agent and wetting agent (when separate from the coating agent) is added to form the solution/suspension/colloid can, for example, be water, methanol, ethanol, isopropanol, butanol, acetone, ethyl acetate, chloroform, acetonitrile, tetrahydrofuran, diethyl ether, methyl tert-butyl ether, an alcohol, any other suitable solvent, or a combination thereof. The resulting solutions, suspensions, or colloids can be suitable for forming coatings on agricultural products. For example, the solutions, suspensions, or colloids can be applied to the surface of the agricultural product, after which the solvent can be removed (e.g., by evaporation or convective drying), leaving a protective coating formed from the coating agent on the surface of the agricultural product.
While a number of the solvents above (particularly water and ethanol) can be safely and effectively used in solutions/suspensions/colloids that are applied to edible products such as produce or other agricultural products, in many cases it can be advantageous to use either water or otherwise a solvent which is at least about 40% (and in many cases higher) water by volume. This is because water is typically cheaper than other suitable solvents and can also be safer to work with than solvents that have a higher volatility and/or a lower flash point (e.g., acetone or alcohols such as isopropanol or ethanol). In some embodiments, the solvent comprises water. For example, the solvent is water. Accordingly, for any of the solutions/suspensions/colloids described herein, the solvent or solution/suspension/colloid can be at least about 40%, at least about 45%, at least about 50%, at least about 55%, at least about 60%, at least about 65%, at least about 70%, at least about 75%, at least about 80%, at least about 85%, at least about 90%, at least about 95%, or at least about 99% water by mass or by volume. In some embodiments, the solvent includes a combination of water and ethanol, and can optionally be at least about 40%, at least about 45%, at least about 50%, at least about 55%, at least about 60%, at least about 65%, at least about 70%, at least about 75%, at least about 80%, at least about 85%, at least about 90%, at least about 95%, or at least about 99% water by volume. In some embodiments, the solvent or solution/suspension/colloid can be about 40% to 100% water by mass or volume, about 40% to 99% water by mass or volume, about 40% to 95% water by mass or volume, about 40% to 90% water by mass or volume, about 40% to 85% water by mass or volume, about 40% to 80% water by mass or volume, about 50% to 100% water by mass or volume, about 50% to 99% water by mass or volume, about 50% to 95% water by mass or volume, about 50% to 90% water by mass or volume, about 50% to 85% water by mass or volume, about 50% to 80% water by mass or volume, about 60% to 100% water by mass or volume, about 60% to 99% water by mass or volume, about 60% to 95% water by mass or volume, about 60% to 90% water by mass or volume, about 60% to 85% water by mass or volume, about 60% to 80% water by mass or volume, about 70% to 100% water by mass or volume, about 70% to 99% water by mass or volume, about 70% to 95% water by mass or volume, about 70% to 90% water by mass or volume, about 70% to 85% water by mass or volume, about 80% to 100% water by mass or volume, about 80% to 99% water by mass or volume, about 80% to 97% water by mass or volume, about 80% to 95% water by mass or volume, about 80% to 93% water by mass or volume, about 80% to 90% water by mass or volume, about 85% to 100% water by mass or volume, about 85% to 99% water by mass or volume, about 85% to 97% water by mass or volume, about 85% to 95% water by mass or volume, about 90% to 100% water by mass or volume, about 90% to 99% water by mass or volume, about 90% to 98% water by mass or volume, or about 90% to 97% water by mass or volume.
In view of the above, for some applications the solvent can be a low wetting solvent (i.e., a solvent exhibiting a large contact angle with respect to the surface to which it is applied). For example, in the absence of any added wetting agents or other surfactants, the contact angle between the solvent and either (a) carnauba wax, (b) candelilla wax, (c) paraffin wax, or (d) the surface of a non-waxed lemon can be at least about 70°, for example at least about 75°, 80°, 85°, or 90°. Addition of any of the wetting agents described herein to the solvent, either alone or in combination with other compounds or coating agents, can cause the contact angle between the resulting solution/suspension/colloid and either (a) carnauba wax, (b) candelilla wax, (c) paraffin wax, or (d) the surface of a non-waxed lemon to be less than about 85°, for example less than about 80°, 75°, 70°, 65°, 60°, 55°, 50°, 45°, 40°, 35°, 30°, 25°, 20°, 15°, 10°, 5°, or 0°.
The coating agent that is added to or dissolved, suspended, or dispersed in the solvent to form the coating solution/suspension/colloid can be any compound or combination of compounds capable of forming a protective coating over the substrate to which the solution/suspension/colloid is applied. The coating agent can be formulated such that the resulting coating protects the substrate from biotic and/or abiotic stressors. For example, the coating can prevent or suppress the transfer of oxygen and/or water, thereby preventing the substrate from oxidizing and/or from losing water via transpiration/osmosis/evaporation. In cases where the substrate is perishable and/or edible, for example when the substrate is a plant, an agricultural product, or a piece of produce, the coating agent is preferably composed of non-toxic compounds that are safe for consumption. For example, the coating agent can be formed from or include fatty acids and/or salts or esters thereof. The fatty acid esters can, for example, be ethyl esters, methyl esters, or glyceryl esters (e.g., 1-glyceryl or 2-glyceryl esters).
Coated Agricultural Products and Methods of Preparation and Use Thereof
In some embodiments, when the components of the coating agent (e.g, fatty acids, fatty acid esters, or a combination thereof and/or fatty acid salts) are mixed with a solvent, they form microstructures, such as, for example, vesicles in the solvent. Referring to
In some embodiments, an advantage of the lamellar structure is its low permeability. Without being bound by any theory, when water passes through the coating, it travels through grain boundaries and between the lamellae if the outer surfaces of the lamellae are sufficiently hydrophilic (e.g., when the lamellae are lipid bilayers). In some embodiments, when the lamellar structure is composed of lipid bilayers formed from fatty acids, fatty acid esters, or a combination thereof and/or fatty acid salts, higher amounts of fatty acid salts in the coating increases the hydrophilicity of the outer surfaces of the lipid bilayers that make up the coating, thus allowing more water to intercalate between the lipid bilayers and therefore increasing the water permeability of the coating, resulting in an increased mass loss rate. In some embodiments, the mass loss rate of a coated agricultural product can be increased by increasing the fatty acid salt content of the coating, or, alternatively, the mass loss rate of the coated agricultural product can be decreased by decreasing the fatty acid salt content. In some such embodiments, the respiration rate changes less than the mass loss rate (e.g., remains nearly the same). This is illustrated in Example 26 and
In some embodiments, increasing the concentration of the coating agent in the mixture increases the thickness of the coating, which, for example, can reduce the water permeability (and can therefore reduce mass loss when the coating is disposed over an agricultural product) and can lower the gas diffusion ratio (and can therefore reduce the respiration rate when the coating is disposed over an agricultural product).
In some embodiments, the higher the temperature of drying, the larger the grain size and lower the mosaicity (which is a measure of the probabilities that the orientation of lamellae in a coating deviate from a plane that is substantially parallel with the plane of the substrate surface, recognized as a type of crystal defect) in the coating, which can result in fewer grain boundaries and defects for water and/or gas to travel through. In some embodiments, this can result in a lower water and gas permeability that can translate into a lower mass loss rate and lower respiration rate when, e.g., the coating is disposed on an agricultural product.
In some embodiments, heating the coating (or coated agricultural product) from a first temperature to a second temperature higher than the first temperature but below the melting point (i.e., the phase transition temperature) of the coating, then cooling the coating, can increase the grain size in the coating, which can result in a lower mass loss rate, lower gas diffusion ratio, and lower respiration rate.
Coated Agricultural Products
In one aspect, described herein is a coated substrate comprising a coating that forms a lamellar structure on the substrate, wherein the coating has a thickness of less than 20 microns.
In another aspect, described herein is a coated substrate comprising a coating that forms a lamellar structure on the substrate, wherein the coating comprises a plurality of grains.
In some embodiments, the substrate is an agricultural product, a silicon substrate, or a substrate comprising a polysaccharide (e.g., cellulose). For example, the substrate is an agricultural product.
In another aspect, described herein is a coated agricultural product comprising a coating that forms a lamellar structure on the agricultural product, wherein the coating has a thickness of less than 20 microns.
In another aspect, described herein is a coated agricultural product comprising a coating that forms a lamellar structure on the agricultural product, wherein the coating comprises a plurality of grains.
In some embodiments (e.g., when the lamella is a lipid bilayer (e.g., when the lamella is a lipid bilayer comprising one or more fatty acid derivatives)), the lattice formation is defined by a hexagonal unit cell such as, for example, the unit cell depicted in
In some embodiments, the lamellar structure comprises a plurality of lamellae. The distance between a surface of a lamella and the surface of an adjacent lamella that is facing the same direction is referred to herein as “interlayer spacing”. In some embodiments, the interlayer spacing of the lamellae is from about 1.0 to about 20 nm. For example, the interlayer spacing is from about 1 to about 20 nm, from about 2 to about 13 nm, from about 3 nm to about 10 nm, from about 3 to about 7 nm, from about 3 to about 6 nm, from about 3 to about 5 nm, from about 5 to about 7 nm, from about 4 to about 6 nm, from about 4 to about 5 nm, from about 5 to about 6 nm, from about 5.0 to about 5.8 nm, about 3.3 nm, about 3.7 nm, about 4.1 nm, about 4.5 nm, about 5.0 nm, about 5.2 nm, about 5.4 nm, about 5.5 nm, about 5.6 nm, or about 5.7 nm.
In some embodiments, the coating comprises a plurality of grains.
In some embodiments, the grain size is from about 2 nm to about 100 nm. For example, from about 4 nm to about 100 nm, from about 7 nm to about 100 nm, from about 6 nm to about 100 nm, from about 6 nm to about 80 nm, from about 6 nm to about 60 nm, from about 6 nm to about 40 nm, from about 6 nm to about 25 nm, from about 9 nm to about 22 nm, from about 9 nm to about 15 nm, from about 13 nm to about 25 nm, from about 8 nm to about 25 nm, from about 11 nm to about 17 nm, from about 11 nm to about 14 nm, from about 13 nm to about 17 nm, from about 12 nm to about 16 nm, from about 15 nm to about 17 nm, from about 9 nm to about 13 nm, from about 13 nm to about 17 nm, from about 17 nm to about 25 nm, from about 2 nm to about 10 nm, 5 nm to about 10 nm, from about 8 nm to about 9 nm, from about 8.5 nm to about 9.5 nm, from about 9 nm to about 10 nm, about 8 nm, about 9 nm, about 10 nm, about 11 nm, about 12 nm, about 13 nm, about 14 nm, about 15 nm, about 16 nm, about 17 nm, about 19 nm, about 21 nm, or about 22 nm.
In one aspect, described herein is a coated substrate comprising a coating that forms a lamellar structure on the substrate, wherein:
wherein:
R is selected from the group consisting of H and C1-C6 alkyl optionally substituted with one or more of OH and C1-C6 alkoxy;
R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
each occurrence of R10A, R10B, R11A, and R11B is independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
or any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a double bond, a 3- to 6-membered ring heterocycle, or a C3-C6 cycloalkyl; and
o is an integer from 0 to 17;
p is an integer from 0 to 17;
wherein the sum of o and p is from 0 to 17; and
wherein Formula IIA is:
wherein:
R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
each occurrence of R10A, R10B, R11A, and R11B is independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
or any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a double bond, a 3- to 6-membered ring heterocycle, or a C3-C6 cycloalkyl;
o is an integer from 0 to 17;
p is an integer from 0 to 17;
wherein the sum of o and p is from 0 to 17;
Xn+ is a cationic moiety having formal charge n; and
each occurrence of R′ is selected from H and C1-C6 alkyl.
In one aspect, described herein is a coated substrate comprising a coating that forms a lamellar structure on the substrate, wherein:
wherein:
R is selected from the group consisting of H and C1-C6 alkyl optionally substituted with one or more of OH and C1-C6 alkoxy;
R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
each occurrence of R10A, R10B, R11A, and R11B is independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
or any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a double bond, a 3- to 6-membered ring heterocycle, or a C3-C6 cycloalkyl; and
o is an integer from 0 to 17;
p is an integer from 0 to 17;
wherein the sum of o and p is from 0 to 17; and
wherein Formula IIA is:
wherein:
R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
each occurrence of R10A, R10B, R11A, and R11B is independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
or any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a double bond, a 3- to 6-membered ring heterocycle, or a C3-C6 cycloalkyl;
o is an integer from 0 to 17;
p is an integer from 0 to 17;
wherein the sum of o and p is from 0 to 17;
Xn+ is a cationic moiety having formal charge n; and
each occurrence of R′ is selected from H and C1-C6 alkyl.
In one aspect, described herein is a coated substrate comprising a coating that forms a lamellar structure on the substrate, wherein:
Methods of Use and Application
In another aspect, described herein is a method of coating a substrate, comprising:
(i) applying a mixture comprising a coating agent and a solvent to the agricultural product;
(ii) drying the mixture at a temperature of greater than 50° C. to form a coating on the agricultural product;
wherein:
the coating forms a lamellar structure on the substrate; and
the coating has a thickness of less than 20 microns.
In another aspect, described herein is a method of coating a substrate, comprising:
(i) applying a mixture comprising a coating agent and a solvent to the agricultural product;
(ii) drying the mixture at a temperature of greater than 50° C. to form a coating on the agricultural product;
wherein:
the coating forms a lamellar structure on the substrate; and
the coating comprises a plurality of grains.
In another aspect, described herein is a method of coating a substrate, comprising:
(i) applying a mixture comprising a coating agent and a solvent to the substrate;
(ii) removing the solvent to form a coating on the substrate;
(iii) heating the coated agricultural product from a first temperature to a second temperature, wherein the second temperature is greater than the first temperature and less than the melting point of the coating; and
(iv) cooling the coated substrate from the second temperature to a third temperature, wherein the third temperature is less than the second temperature;
wherein:
the coating forms a lamellar structure on the substrate; and
the coating comprises a plurality of grains.
In another aspect, described herein is a method of coating an agricultural product, comprising:
(i) applying a mixture comprising a coating agent and a solvent to the agricultural product;
(ii) drying the mixture at a temperature of greater than 50° C. to form a coating on the agricultural product;
wherein:
the coating forms a lamellar structure on the agricultural product; and
the coating has a thickness of less than 20 microns.
In another aspect, described herein is a method of coating an agricultural product, comprising:
(i) applying a mixture comprising a coating agent and a solvent to the agricultural product;
(ii) drying the mixture at a temperature of greater than 50° C. to form a coating on the agricultural product;
wherein:
the coating forms a lamellar structure on the agricultural product; and
the coating comprises a plurality of grains.
In another aspect, described herein is a method of coating an agricultural product, comprising:
(i) applying a mixture comprising a coating agent and a solvent to the agricultural product;
(ii) removing the solvent to form a coating on the agricultural product;
(iii) heating the coated agricultural product from a first temperature to a second temperature, wherein the second temperature is greater than the first temperature and less than the melting point of the coating; and
(iv) cooling the coated agricultural product from the second temperature to a third temperature, wherein the third temperature is less than the second temperature;
wherein:
the coating forms a lamellar structure on the agricultural product; and
the coating comprises a plurality of grains.
In some embodiments, the first temperature is from about 0° C. to about 50° C. For example, the first temperature is from about 10° C. to about 40° C., from about 20° C. to about 30° C., from about 23° C. to about 27° C., or about 25° C. In some embodiments, the first temperature is greater than the temperature of the surrounding atmosphere. In some embodiments, the first temperature is less than the temperature of the surrounding atmosphere.
In some embodiments, the second temperature is from about 40° C. to about 65° C. For example, the second temperature is from about 45° C. to about 65° C., from about 50° C. to about 65° C., from about 55° C. to about 65° C., from about 57° C. to about 63° C., or about 60° C. In some embodiments, the second temperature is greater than the temperature of the surrounding atmosphere. In some embodiments, the second temperature is less than the temperature of the surrounding atmosphere. In some embodiments, the coated agricultural product is heated with air having a temperature higher than the temperature of the agricultural product. In some embodiments, the air that the coated agricultural product is heated with is higher than the second temperature. In some embodiments, the air that the coated agricultural product is heated with is higher than the melting point of the coating.
In some embodiments, if the coating is heated at or above its melting temperature (about 65° C. to about 70° C., or about 70° C.), the lattice formation of the lamellae in the coating can be disrupted, the constituent molecules can adopt random orientations, and the coating can liquify.
In some embodiments, the third temperature is from about 0° C. to about 50° C. For example, the first temperature is from about 10° C. to about 40° C., from about 20° C. to about 30° C., from about 23° C. to about 27° C., or about 25° C. In some embodiments, the third temperature is greater than the temperature of the surrounding atmosphere. In some embodiments, the third temperature is less than the temperature of the surrounding atmosphere.
In some embodiments, the second temperature is maintained for about 5 seconds to about 10 hours. For example, the second temperature is maintained for about 5 seconds to about 7 hours, about 5 seconds to about 3 hours, about 5 seconds to about 1.5 hours, about 5 seconds to about 60 minutes, about 30 seconds to about 45 minutes, about 5 minutes to about 60 minutes, about 10 minutes to about 45 minutes, about 20 minutes to about 40 minutes, about 25 minutes to about 35 minutes, about 30 seconds to about 10 minutes, about 30 seconds to about 7 minutes, about 30 seconds to about 3 minutes, about 3 minutes to about 7 minutes, about 30 seconds to about 1 minute, about 1 minute to about 5 minutes, about 25 minutes, about 27 minutes, about 29 minutes, about 30 minutes, about 32 minutes, about 35 minutes, about 30 seconds, about 1 minute, about 2 minutes, about 3 minutes, about 4 minutes, about 5 minutes, about 6 minutes, or about 7 minutes.
In some embodiments, the grain size after cooling the coated agricultural product from the second temperature to the third temperature is larger than the grain size before heating the coated agricultural product from the first temperature to the second temperature. In some embodiments, the grain size of the coating before heating the coated agricultural product from the first temperature to the second temperature is from about 2 nm to about 10 nm. For example, from about 5 nm to about 10 nm, from about 8 nm to about 9 nm, from about 8.5 nm to about 9.5 nm, from about 9 nm to about 10 nm, about 8 nm, about 9 nm, or about 10 nm. For example, the grain size of the coating after cooling the coated agricultural product from the second temperature to the third temperature is from about 7 nm to about 100 nm. For example, from about 8 nm to about 25 nm, from about 11 nm to about 17 nm, from about 11 nm to about 14 nm, from about 13 nm to about 17 nm, from about 12 nm to about 16 nm, from about 15 nm to about 17 nm, about 11 nm, about 12 nm, about 13 nm, about 14 nm, about 15 nm, about 16 nm, or about 17 nm.
In another aspect, described herein is a method of reducing the mass loss rate of an agricultural product, comprising:
(i) applying a mixture comprising a coating agent and a solvent to the agricultural product;
(ii) drying the mixture at a temperature of greater than 50° C. to form a coating on the agricultural product;
wherein:
the coating forms a lamellar structure on the agricultural product; and
the coating has a thickness of less than 20 microns.
In another aspect, described herein is a method of reducing the respiration rate of an agricultural product, comprising:
(i) applying a mixture comprising a coating agent and a solvent to the agricultural product;
(ii) drying the mixture at a temperature of greater than 50° C. to form a coating on the agricultural product;
wherein:
the coating forms a lamellar structure on the agricultural product; and
the coating has a thickness of less than 20 microns.
In some embodiments, the concentration of the coating agent in the mixture is from about 1 g/L to about 200 g/L. For example, the concentration of the coating agent in the mixture is from about 1 g/L to about 150 g/L, from about 1 g/L to about 50 g/L, from about 50 g/L to about 100 g/L, from about 100 g/L to about 150 g/L, from about 150 g/L to about 200 g/L, from about 5 g/L to about 100 g/L, from about 5 g/L to about 80 g/L, from about 70 g/L to about 130 g/L, from about 10 g/L to about 80 g/L, from about 25 g/L to about 60 g/L, from about 30 g/L to about 60 g/L, from about 30 g/L to about 50 g/L, from about 40 g/L to about 60 g/L, from about 30 g/L to about 40 g/L, from about 40 g/L to about 50 g/L, from about 50 g/L to about 60 g/L, about 10 g/L, about 20 g/L, about 30 g/L, about 40 g/L, about 50 g/L, about 60 g/L, about 70 g/L, about 80 g/L, about 90 g/L, about 100 g/L, about 110 g/L, about 120 g/L, about 130 g/L or about 140 g/L.
In some embodiments, the mixture is dried at a temperature of from about 20° C. to about 100° C. For example, the mixture is dried at a temperature of from about from about 25° C. to about 80° C., from about 25° C. to about 70° C., from about 30° C. to about 65° C., from about 40° C. to about 65° C., 50° C. to about 65° C., from about 55° C. to about 65° C., from about 60° C. to about 65° C., about 55° C., about 60° C., or about 65° C. In some embodiments, the mixture is partially dried. In some embodiments, the drying removes greater than 5% of the solvent. For example, the drying removes greater than 10%, greater than 20%, greater than 30%, greater than 40%, greater than 50%, greater than 60%, greater than 70%, greater than 80%, greater than 90%, or greater than 95% of the solvent. In some embodiments, the lamellar structure forms when the mixture is partially dried. In some embodiments, the lamellar structure forms after at least 5% of the solvent has been removed. For example, the lamellar structure forms after at least 10%, at least 20%, at least 30%, at least 40%, at least 50%, at least 60%, at least 70%, at least 80%, at least 90%, or at least 95% of the solvent has been removed.
In some embodiments, faster solvent removal and/or drying can improve the performance of the coating. For example, faster solvent removal and/or drying can result in thicker and more homogeneous coatings. In some embodiments, removing the solvent or drying the mixture is performed in under 2 hours. For example, the solvent is removed or dried in under 1.5 hours, under 1 hour, under 45 minutes, under 30 minutes, under 25 minutes, under 20 minutes, under 15 minutes, under 10 minutes, under 5 minutes, under 4 minutes, under 2 minutes, under 1 minute, under 30 seconds, under 15 seconds, under 10 seconds, under 5 seconds, or under 3 seconds.
In another aspect, described herein is a method of coating an agricultural product, comprising:
(i) applying a mixture comprising a coating agent and a solvent to the agricultural product;
(ii) drying the mixture at a temperature of greater than 50° C. to form a coating on the agricultural product;
wherein:
the coating forms a lamellar structure on the agricultural product;
the coating has a thickness of less than 2 microns; and
the coating agent comprises one or more compounds of Formula IA and one or more compounds of Formula IIA, wherein Formula IA is
wherein:
R is selected from the group consisting of H and C1-C6 alkyl optionally substituted with one or more of OH and C1-C6 alkoxy;
R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
each occurrence of R10A, R10B, R11A, and R11B is independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
or any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a double bond, a 3- to 6-membered ring heterocycle, or a C3-C6 cycloalkyl; and
o is an integer from 0 to 17;
p is an integer from 0 to 17;
wherein the sum of o and p is from 0 to 17; and
wherein Formula IIA is:
wherein:
R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
each occurrence of R10A, R10B, R11A, and R11B is independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
or any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a double bond, a 3- to 6-membered ring heterocycle, or a C3-C6 cycloalkyl;
o is an integer from 0 to 17;
p is an integer from 0 to 17;
wherein the sum of o and p is from 0 to 17;
Xn+ is a cationic moiety having formal charge n; and
each occurrence of R′ is selected from H and C1-C6 alkyl.
In another aspect, described herein is a method of coating an agricultural product, comprising:
(i) applying a mixture comprising a coating agent and a solvent to the agricultural product;
(ii) drying the mixture at a temperature of greater than 50° C. to form a coating on the agricultural product;
wherein:
In another aspect, described herein is a method of coating an agricultural product, comprising:
(i) applying a mixture comprising a coating agent and a solvent to the agricultural product;
(ii) drying the mixture at a temperature of greater than 60° C. to form a coating on the agricultural product;
wherein:
the coating forms a lamellar structure on the agricultural product;
the grain size is from about 13 nm to about 25 nm;
the coating has a thickness of less than 2 microns; and
the coating agent comprises one or more compounds of Formula IA and one or more compounds of Formula IIA, wherein Formula IA is
wherein:
R is selected from the group consisting of H and C1-C6 alkyl optionally substituted with one or more of OH and C1-C6 alkoxy;
R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
each occurrence of R10A, R10B, R11A, and R11B is independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
or any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a double bond, a 3- to 6-membered ring heterocycle, or a C3-C6 cycloalkyl; and
o is an integer from 0 to 17;
p is an integer from 0 to 17;
wherein the sum of o and p is from 0 to 17; and
wherein Formula IIA is:
wherein:
R1, R2, R3, R4, R5, R6, R7, R8, and R9 are independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
each occurrence of R10A, R10B, R11A, and R11B is independently selected from the group consisting of: H, OH, C1-C6 alkyl, C2-C6 alkenyl, and C1-C6 alkoxy;
or any two R1, R2, R3, R4, R5, R6, R7, R8, R9, R10A, R10B, R11A, and R11B on adjacent carbon atoms are taken together with the carbon atoms to which they are attached to form a double bond, a 3- to 6-membered ring heterocycle, or a C3-C6 cycloalkyl;
o is an integer from 0 to 17;
p is an integer from 0 to 17;
wherein the sum of o and p is from 0 to 17;
Xn+ is a cationic moiety having formal charge n; and
each occurrence of R′ is selected from H and C1-C6 alkyl.
In another aspect, described herein is a method of reducing the water permeability of a coating on a substrate, comprising:
(i) heating the coated substrate from a first temperature to a second temperature; and
(ii) cooling the coated substrate from the second temperature to a third temperature, wherein the third temperature is less than the second temperature;
wherein:
the coating forms a lamellar structure on the substrate; and
the coating comprises a plurality of grains.
In another aspect, described herein is a method of reducing the gas diffusion ratio of a coating on a substrate, comprising:
(i) heating the coated substrate from a first temperature to a second temperature; and
(ii) cooling the coated substrate from the second temperature to a third temperature, wherein the third temperature is less than the second temperature;
wherein:
the coating forms a lamellar structure on the substrate; and
the coating comprises a plurality of grains.
In some embodiments, the substrate is an agricultural product, a silicon substrate, or a substrate comprising a polysaccharide (e.g., cellulose). For example, the substrate is an agricultural product.
In another aspect, described herein is a method of reducing the mass loss rate of an agricultural product having a coating disposed thereon, comprising:
(i) heating the coated agricultural product from a first temperature to a second temperature; and
(ii) cooling the coated agricultural product from the second temperature to a third temperature, wherein the third temperature is less than the second temperature;
wherein:
the coating forms a lamellar structure on the agricultural product; and
the coating comprises a plurality of grains.
In another aspect, described herein is a method of reducing the respiration rate of an agricultural product having a coating disposed thereon, comprising:
(i) heating the coated agricultural product from a first temperature to a second temperature; and
(ii) cooling the coated agricultural product from the second temperature to a third temperature, wherein the third temperature is less than the second temperature;
wherein:
the coating forms a lamellar structure on the agricultural product; and
the coating comprises a plurality of grains.
In some embodiments, the first temperature is from about 0° C. to about 50° C. For example, the first temperature is from about 10° C. to about 40° C., from about 20° C. to about 30° C., from about 23° C. to about 27° C., or about 25° C. In some embodiments, the first temperature is greater than the temperature of the surrounding atmosphere. In some embodiments, the first temperature is less than the temperature of the surrounding atmosphere.
In some embodiments, the second temperature is from about 40° C. to about 65° C. For example, the second temperature is from about 45° C. to about 65° C., from about 50° C. to about 65° C., from about 55° C. to about 65° C., from about 57° C. to about 63° C., or about 60° C. In some embodiments, the second temperature is greater than the temperature of the surrounding atmosphere. In some embodiments, the second temperature is less than the temperature of the surrounding atmosphere. In some embodiments, the agricultural product is heated with air having a temperature higher than the first temperature of the agricultural product. In some embodiments, the agricultural product is heated with air having a temperature higher than the second temperature of the agricultural product. In some embodiments, the air that the coated agricultural product is heated with is higher than the melting point of the coating.
In some embodiments, if the coating is heated at or above its melting temperature (about 65° C. to about 70° C., or about 70° C.), the lattice formation of the lamellae in the coating can be disrupted, the constituent molecules can adopt random orientations, and the coating can liquify.
In some embodiments, the third temperature is from about 0° C. to about 50° C. For example, the first temperature is from about 10° C. to about 40° C., from about 20° C. to about 30° C., from about 23° C. to about 27° C., or about 25° C. In some embodiments, the third temperature is greater than the temperature of the surrounding atmosphere. In some embodiments, the third temperature is less than the temperature of the surrounding atmosphere.
In some embodiments, the second temperature is maintained for about 5 seconds to about 10 hours. For example, the second temperature is maintained for about 5 seconds to about 7 hours, about 5 seconds to about 3 hours, about 5 seconds to about 1.5 hours, about 5 seconds to about 60 minutes, about 30 seconds to about 45 minutes, about 5 minutes to about 60 minutes, about 10 minutes to about 45 minutes, about 20 minutes to about 40 minutes, about 25 minutes to about 35 minutes, about 30 seconds to about 10 minutes, about 30 seconds to about 7 minutes, about 30 seconds to about 3 minutes, about 3 minutes to about 7 minutes, about 30 seconds to about 1 minute, about 1 minute to about 5 minutes, about 25 minutes, about 27 minutes, about 29 minutes, about 30 minutes, about 32 minutes, about 35 minutes, about 30 seconds, about 1 minute, about 2 minutes, about 3 minutes, about 4 minutes, about 5 minutes, about 6 minutes, or about 7 minutes.
In some embodiments, the grain size after cooling the coated agricultural product from the second temperature to the third temperature is larger than the grain size before heating the coated agricultural product from the first temperature to the second temperature. In some embodiments, the grain size of the coating before heating the coated agricultural product from the first temperature to the second temperature is from about 2 nm to about 10 nm. For example, from about 5 nm to about 10 nm, from about 8 nm to about 9 nm, from about 8.5 nm to about 9.5 nm, from about 9 nm to about 10 nm, about 8 nm, about 9 nm, or about 10 nm. For example, the grain size of the coating after cooling the coated agricultural product from the second temperature to the third temperature is from about 7 nm to about 100 nm. For example, from about 8 nm to about 25 nm, from about 11 nm to about 17 nm, from about 11 nm to about 14 nm, from about 13 nm to about 17 nm, from about 12 nm to about 16 nm, from about 15 nm to about 17 nm, about 11 nm, about 12 nm, about 13 nm, about 14 nm, about 15 nm, about 16 nm, or about 17 nm.
Coating Thickness and Mass Loss Factor/Rate
In some embodiments, for coatings that are formulated to prevent water loss from or oxidation of coated substrates such as produce, thicker coatings will be less permeable to water and oxygen as compared to thinner coatings formed from the same coating agent, and should therefore result in lower mass loss rates as compared to thinner coatings. Thicker coatings can be formed by increasing the concentration of the coating agent in the solution/suspension/colloid and applying a similar volume of solution/suspension/colloid to each piece of (similarly sized) produce. The effect of increasing the coating thickness on harvested produce is demonstrated in
For certain solutions/suspensions/colloids including long chain fatty acids and/or salts or esters thereof dissolved or suspended or dispersed in a solvent, protective coatings formed over certain types of produce by the methods described above were found to reduce the mass loss rate of the produce but did not result in lower mass loss rates as the thickness of the coating was increased, as in the blueberries described above. Instead, the mass loss rate in these cases was found to be lower than in uncoated produce but was approximately the same for thinner and thicker coatings. For example,
Surprisingly, for many cases in which the mass loss rate did not vary with coating thickness (as with the lemons in
The beneficial effects of adding small concentrations of medium chain fatty acids or salts or esters thereof to coating solutions/suspensions/colloids that include long chain fatty acids or salts/esters thereof are shown in
While treating the lemons with the coating agents that only included long chain fatty acid salts and esters (804 and 806) did reduce the average mass loss rate of the lemons, the mass loss factor did not substantially increase when the concentration of the coating agent compounds in the mixture was increased from 10 mg/mL (804) to 30 mg/mL (806). However, the mass loss factor did increase substantially when a small concentration of medium chain fatty acid esters (5 mg/mL of UA-1G) was added to each of the mixtures. Specifically, adding 5 mg/mL of medium chain esters to the mixture with 10 mg/mL of long chain fatty acid esters/salts caused the mass loss factor of the lemons due to the resulting coatings to increase from about 1.5 (bar 804) to about 1.9 (bar 808), corresponding to an increase in mass loss factor of over 25%. Adding 5 mg/mL of medium chain esters to the mixture with 30 mg/mL of long chain fatty acid esters/salts caused the mass loss factor of the lemons due to the resulting coatings to increase from about 1.7 (bar 806) to about 2.6 (bar 810), corresponding to an increase in mass loss factor of over 50%. The mass loss factor of the lemons corresponding to bar 810 was in fact substantially larger than that of groups of lemons coated with any of the concentrations of long chain fatty acid esters/salts in solution for which medium chain fatty acids or salts/esters thereof were not also added.
Contact Angle/Wetting Agent
Without wishing to be bound by theory, it is believed that many of the mixtures (i.e., solutions, suspensions, or colloids) that lacked the medium chain fatty acids or salts/esters thereof were not sufficiently wetting the entire surface of the produce to which they were applied due to a difference in surface energy of the mixture as compared to that of the surface of the produce. Consequently, the coatings formed from these mixtures did not completely cover the surface of the produce. As such, mass loss was dominated by water loss through the openings in the coating, and was relatively unaffected by increasing the coating thickness. Thus, in cases where this effect was believed to occur (e.g., in lemons coated from a water-based solution such as in
Without wishing to be bound by theory, it is believed that the medium chain fatty acids that were added to the mixtures acted as surfactants/wetting agents, reducing the contact angle of the mixture on the surface of the produce. In some embodiments, the addition of the wetting agents can improve coverage of the mixture over the surface of the produce, thereby allowing a substantially contiguous coating to be formed over the entire surface. Consequently, the mass loss rates of coated produce were found to decrease with increasing coating thickness, and overall mass loss rates were found to be substantially reduced as compared to produce coated with similar mixtures that lacked the wetting agents. Furthermore, the long chain fatty acids and/or salts or esters thereof appeared, for example, to suppress surface damage to the produce observed in cases where the wetting agent was dissolved, dispersed, or suspended in the mixture and applied on its own without also including the long chain fatty acids and/or salts or esters thereof. Additional evidence of these effects is provided below.
Through extensive experimentation, it was found that the contact angle of droplets of some solvents and coating solutions/suspensions on the surfaces of at least some types of produce was quite large, indicating a large difference in surface energy of the droplets as compared to the surface of the produce. This effect was particularly evident in cases where the coating solution/suspension was at least 70% water by volume, since the surfaces of many plants or other agricultural products often tend to be hydrophobic due to the presence of epicuticular waxes. This phenomenon was characterized as follows. Droplets of solvent or coating solution/suspension/colloid (i.e., solvent with coating agent dissolved, suspended or dispersed therein) were deposited either directly on produce surfaces or directly on carnauba, candellila, or paraffin wax (carnauba, candellila, and paraffin wax all tend to have similar native hydrophobicity to that of the surfaces of lemons as well as many other types of produce, see
In some embodiments, increasing the concentration of the wetting agent (e.g., the medium chain fatty acids and/or salts or esters thereof) in water-based or high water content coating mixtures decreased the contact angle of the solution/suspension/colloid on the produce or wax surface. For example, as shown in
It was further found that for some mixtures, the addition of medium chain fatty acids and/or salts or esters thereof having a smaller chain length caused a larger reduction in contact angle of droplets on produce than addition of similar concentrations of medium chain fatty acids and/or salts or esters thereof having a longer chain length. For example,
As seen in
As previously described, carnauba, candellila, and paraffin wax were all found to have similar native hydrophobicity to that of the surfaces of lemons (as well as other produce). Hence the wetting properties (e.g., contact angle) of mixtures characterized on carnauba, candellila, or paraffin wax surfaces are typically predictive of the wetting properties of the mixtures on produce. For example,
The effects of adding small concentrations of LA-1G and CA-1G to coating mixtures used to form coatings on avocados is shown in the graph of
The addition of the CA-1G (carbon chain length of 10) to the coating mixture increased the mass loss factor to about 2.35 for a CA-1G concentration of 1 mg/mL (bar 1303), to about 2.24 for a CA-1G concentration of 2.5 mg/mL (bar 1304), and to about 2.18 for a CA-1G concentration of 4 mg/mL (bar 1305). So while the mass loss factor was substantially larger for all concentrations of CA-1G in a range of 1 to 4 mg/mL as compared to mixtures lacking the medium chain fatty acid esters (bar 1302), the mass loss factor appeared to decrease slightly as the concentration of CA-1G was increased. Without wishing to be bound by theory, it is believed that the addition of CA-1G at all concentrations of at least 1 mg/mL was effective at improving the wetting of the solution on the surfaces of the avocados, but that increasing the concentration of the CA-1G began to cause some moderate damage to the avocados, thereby mitigating the beneficial surface wetting effects and causing a slight decrease in the mass loss factor.
Still referring to
The effects of adding small concentrations of CA-1G to coating mixtures used to form coatings on cherries is shown in
The effects of adding small concentrations of UA-1G to coating mixtures used to form coatings on finger limes is shown
As described throughout, wetting agents can be included in coating solutions/suspensions/colloids in order to, e.g., improve the surface wetting of substrates to which the solutions/suspensions/colloids are applied, thereby resulting in, e.g., improved surface coverage of the coatings that are formed thereover. The wetting agents can be included within or as part of the coating agent that is dissolved or suspended in the solvent to form the coating solution/suspension/colloid. That is, a sub-group of the compounds of the coating agent can cause a change in surface energy of the solvent to which the coating agent is added, thereby acting as a wetting agent. Alternatively, the wetting agent can be a separate compound (or group of compounds) from the coating agent, and can be added to the solvent either before, after, or at the same time as the coating agent.
Alternatively, the wetting agent can be a separate compound (or group of compounds) from the coating agent and can be applied to the surface prior to applying the coating agent. For example, the wetting agent can first be added to a separate solvent to form a wetting agent solution/suspension/colloid. The wetting agent solution/suspension/colloid can then be applied to the surface, after which the coating solution/suspension/colloid is applied to the surface to form the coating. Priming of the surface in this manner can improve the surface wetting of the coating solution/suspension/colloid with the surface.
An example of the surface priming effect described above is shown in
The following examples describe effects of various coating agents and solutions/suspensions/colloids on various substrates, as well as characterization of some of the various coating agents and solutions/suspensions/colloids. These examples are only for illustrative purposes and are not meant to limit the scope of the present disclosure. In each of the examples below, all reagents and solvents were purchased and used without further purification unless specified.
In order to form the coatings, the finger limes were placed in bags, and the solution containing the composition was poured into the bag. The bag was then sealed and lightly agitated until the entire surface of each finger lime was wet. The finger limes were then removed from the bag and allowed to dry on drying racks. The finger limes were kept under ambient room conditions at a temperature in the range of about 23° C.-27° C. and humidity in the range of about 40%-55% while they dried and for the entire duration of the time they were tested.
As shown in
Nine solutions using combinations of long chain fatty acid esters were prepared to examine the effects of various coating agent compositions on the mass loss rate of avocados treated with a solution composed of the coating agent dissolved in a solvent to form a coating over the avocados. Each solution was composed of the coating agents described below dissolved in ethanol at a concentration of 5 mg/mL.
The first solution contained MA-1G and PA-2G combined at a molar ratio of 1:3. The second solution contained MA-1G and PA-2G combined at a molar ratio of 1:1. The third solution contained MA-1G and PA-2G combined at a molar ratio of 3:1. The fourth solution contained PA-1G and PA-2G combined at a molar ratio of 3:1. The fifth solution contained PA-1G and PA-2G combined at a molar ratio of 1:1. The sixth solution contained PA-1G and PA-2G combined at a molar ratio of 1:3. The seventh solution contained SA-1G and PA-2G combined at a molar ratio of 1:3. The eighth solution contained SA-1G and PA-2G combined at a molar ratio of 1:1. The ninth solution contained SA-1G and PA-2G combined at a molar ratio of 3:1.
Avocados were harvested simultaneously and divided into nine groups of 30 avocados, each of the groups being qualitatively identical (i.e., all groups had avocados of approximately the same average size and quality). In order to form the coatings, the avocados were each individually dipped in one of the solutions, with each group of 30 avocados being treated with the same solution. The avocados were then placed on drying racks and allowed to dry under ambient room conditions at a temperature in the range of about 23° C.-27° C. and relative humidity in the range of about 40%-55%. The avocados were all held at these same temperature and humidity conditions for the entire duration of time they were tested.
As shown in
As shown, the mass loss factor tended to increase as the carbon chain length of the fatty acid ester was increased. For example, all mixtures for which the carbon chain length of the ester was greater than 13 resulted in a mass loss factor greater than 1.2, all mixtures for which the carbon chain length of the ester was greater than 15 resulted in a mass loss factor greater than 1.35, and all mixtures for which the carbon chain length of the ester was greater than 17 resulted in a mass loss factor great than 1.6.
Two solutions were prepared by dissolving a coating agent formed of PA-2G and PA-1G mixed at a mass ratio of 75:25 in substantially pure ethanol. For the first solution, the coating agent was dissolved in the ethanol at a concentration of 10 mg/mL, and for the second solution, the coating agent was dissolved in the ethanol at a concentration of 20 mg/mL.
Blueberries were harvested simultaneously and divided into three groups of 60 blueberries each, each of the groups being qualitatively identical (i.e., all groups had blueberries of approximately the same average size and quality). The first group was a control group of untreated blueberries, the second group was treated with the 10 mg/mL solution, and the third group was treated with the 20 mg/mL solution.
To treat the blueberries, each blueberry was picked up with a set of tweezers and individually dipped in the solution for approximately 1 second, after which the blueberry was placed on a drying rack and allowed to dry. The blueberries were kept under ambient room conditions at a temperature in the range of 23° C.-27° C. and humidity in the range of 40%-55% while they dried and for the entire duration of the time they were tested. Mass loss was measured by carefully weighing the blueberries each day, where the reported percent mass loss was equal to the ratio of mass reduction to initial mass.
Each bar in the graph represents a group of 90 lemons. All coatings were formed by dipping the lemons in their associated suspension, placing the lemons on drying racks, and allowing the lemons to dry under ambient room conditions at a temperature in the range of about 23° C.-27° C. and humidity in the range of about 40%-55%. The lemons were held at these same temperature and humidity conditions for the entire duration of the time they were tested. As seen in
Each bar in the graph represents a group of 60 lemons. All coatings were formed by dipping the lemons in their associated solution, placing the lemons on drying racks, and allowing the lemons to dry under ambient room conditions at a temperature in the range of about 23° C.-27° C. and humidity in the range of about 40%-55%. The lemons were held at these same temperature and humidity conditions for the entire duration of the time they were tested. As seen in
As seen in
As seen in
As seen in
As seen in
As seen in
As seen in
As seen in
As seen in
As seen in
As seen in
As seen in
The table above shows a comparison between mass loss rates and cold storage humidity for untreated lemons and lemons treated with a 94:6 mixture of fatty acid esters (an approximately 50/50 mix of SA-1G and PA-1G) and fatty acid salts (SA-Na) at 50 g/L in water. Each treatment group included 7 boxes of lemons with 60 lemons per box. Each treatment group was placed in a chest freezer equipped with a fan and a humidity sensor. As seen in the table above the untreated group had a mass loss rate of 1.61% per day, as compared to 0.37% per day for the lemons treated with the 50 g/L mixture. The higher mass loss rate of the untreated group corresponded to a higher humidity inside the chest freezer, with the freezer containing the untreated lemons having a humidity of 72%, as compared to 61% humidity in the freezer with the lemons treated with the 50 g/L mixture.
The table above shows a comparison between energy usage of untreated avocados and avocados treated with a 94:6 mixture of fatty acid esters (an approximately 50/50 mix of SA-1G and PA-1G) and fatty acid salts (SA-Na) at 50 g/L in water. Each treatment group included 7 boxes of avocados with 60 avocados per box. Each treatment group was placed in a chest freezer equipped with a fan and an energy usage meter. As seen in the table above, the freezer containing the untreated group consumed 1.19 kWh of energy after 72 hours, as compared to 0.85 kWh for the freezer containing the avocados treated with the 50 g/L mixture.
As shown in
Coating agents including a monoglyceride mixture and fatty acid salt mixture combined at a mass ratio of 94:6 were coated on the surface of a lemon. Mass loss and respiration rates were measured and compared with an uncoated lemon and a wax-coated lemon.
Specifically, a coating agent of 94% monoglyceride (thereof ˜50% glycerol monostearate (SA-1G) and 50% glycerol monopalmitate (PA-1G)) and 6% fatty acid salt (thereof 50% sodium stearate (SA-Na) and 50% sodium palmitate (PA-Na)) was prepared. Coatings were formed by adding each coating agent to water at a concentration of 10 g/L or 20 g/L to form a suspension, dipping the lemons in their associated suspension, placing the lemons on drying racks, and allowing the lemons to dry under ambient room conditions at a temperature in the range of about 23° C.-27° C. and humidity in the range of about 40%-55%. The lemons were held at these same temperature and humidity conditions for the entire duration of the time they were tested.
Mass loss and respiration rates of the coated lemons were measured and compared to uncoated lemons and lemons coated with a conventional wax coating. Mass loss factor was determined as the ratio of the average mass loss rate of uncoated produce (measured for a control group) to the average mass loss rate of the corresponding tested produce.
Coating agents were applied to the surface of a silicon substrate, which as a hydrophilic surface when expose to air. An X-ray scattering image of the applied coat was obtained to identify characteristics of the coating.
Specifically, a coating agent of 94% monoglyceride (thereof 50% SA-1G/50% PA-1G) and 6% fatty acid salt (thereof 50% SA-Na/50% PA-Na) was applied to the surface of a silicon substrate. An X-ray scattering image of the applied coat was obtained and analyzed to determine characteristics of the coating based on the scattering pattern.
As illustrated in
The molecular tilt of SA-1G and PA-1G in the lipid bilayer was estimated from q1 and q2 in
Thus, the coating composition comprising 94% monoglyceride (thereof 50% SA-1G/50% PA-1G) and 6% fatty acid salt (thereof 50% SA-Na/50% PA-Na) showed phase separation between PA-1G and SA-1G and tilt of molecules within the bilayers of about 25°.
A coating agent comprising 94% monoglyceride (thereof 50% SA-1G/50% PA-1G) and 6% fatty acid salt (thereof 50% SA-Na/50% PA-Na) was applied to the surface of a silicon substrate and allowed to dry at room temperature. Grazing incidence X-ray scattering images of the coating were obtained at the following time intervals after application—0 min, 6 min, 12 min, 18 min, 24 min, 35 min, 44 min, and 51 min (
A coating agent comprising 94% monoglyceride (thereof 50% SA-1G/50% PA-1G) and 6% fatty acid salt (thereof 50% SA-Na/50% PA-Na) was applied to the surface of an avocado. X-ray scattering images of the surface of a coated avocado and an uncoated avocado were obtained, as shown in
The surface of an avocado coated with i) 94% monoglyceride (thereof 50% SA-1G/50% PA-1G) and 6% fatty acid salt (thereof 50% SA-Na/50% PA-Na) or ii) conventional wax coating was imaged by scanning electron microscopy (
Even with a much thinner coating, the monoglyceride-based coating performed better as a gas and water barrier than the wax barrier. This performance may be due in part to the ordered structure of the lamellar structure on the axis extending orthogonal to the plane of the substrate or produce surface (
A coating agent comprising 94% monoglyceride (thereof 50% SA-1G/50% PA-1G) and 6% fatty acid salt (thereof 50% SA-Na/50% PA-Na) was prepared and mixed with water at a concentration of 10 g/L, 20 g/L, 30 g/L, and 40 g/L to form coating compositions of varying concentration. All coatings were formed by brushing the suspension onto the avocados on a brushbed, and drying the coated avocados.
As shown in
As described in Example 23, a coating agent of 94% monoglyceride (thereof 50% SA-1G/50% PA-1G) and 6% fatty acid salt (thereof 50% SA-Na/50% PA-Na) was coated on avocados at concentrations of 10 g/L, 20 g/L, 30 g/L, and 40 g/L. Mass loss and gas diffusion of the coated avocados and a set of uncoated avocados was measured to determine mass loss factor and gas diffusion ratio.
As shown in
Gas diffusion through the coating was measured for CO2, C2H4, and O2, and the gas diffusion was compared to the gas diffusion of an uncoated avocado under the same conditions to determine a gas diffusion ratio (R) (R=Diffusion (treated)/Diffusion (untreated). The gas diffusion cell depicted in
Two coating agents were prepared: i) a 94/6 coat comprising 94% monoglyceride (thereof 50% SA-1G/50% PA-1G) and 6% fatty acid salt (thereof 50% SA-Na/50% PA-Na), and ii) a 70/30 coat comprising 70% monoglyceride (thereof 50% SA-1G/50% PA-1G) and 30% fatty acid salt (thereof 50% SA-Na/50% PA-Na). Mixtures of 20 g/L, 30 g/L, and 40 g/L coating agent in water were prepared for each coating agent. Each coating mixture was applied to the surface of an avocado. Respiration and mass loss for the coated avocados and uncoated avocados was then measured under identical conditions.
Two coating agents were prepared: i) a 94/6 coat comprising 94% monoglyceride (thereof 50% SA-1G/50% PA-1G) and 6% fatty acid salt (thereof 50% SA-Na/50% PA-Na), and ii) a 70/30 coat comprising 70% monoglyceride (thereof 50% SA-1G/50% PA-1G) and 30% fatty acid salt (thereof 50% SA-Na/50% PA-Na).
The 94/6 coat was applied to avocado and silicon wafer.
A silicon wafer coated with a 94/6 coat was exposed to humidity for 4 hours, followed by re-drying to determine bilayer spacing changes due to hydration. X-ray scattering plots (
A comparison between hydration in the 94/6 coating and the 70/30 coating was then performed.
The 94/6 coat was then applied to dry avocado peel and fresh avocado peel. The 70/30 coat was applied to fresh avocado peel.
X-ray scattering images of the coating were obtained to identify out-of-plane diffraction peaks to determine bilayer spacing changes due to hydration (
Avocado coated with a 94/6 coat was also exposed to humidity for 4 hours, followed by re-drying to determine if the interlayer hydration induced swelling is reversible. X-ray scattering images of the coating were obtained under dry conditions before exposure to humidity, after exposure to humidity for 4 hours, and after re-exposing to drying conditions (“re-dry”) (
In view of the above results, the water permeability of a coating bilayer can be modulated by adjusting the fatty acid salt concentration (i.e., an increase in fatty acid salt concentration in the coating increases the water-permeability of the coating, and a decrease in the fatty acid salt concentration in the coating decreases the water permeability of the coating.) The thickness of the layer can also be tuned by hydration according to the fatty acid salt concentration of the bilayer.
A silicon wafer was then coated with the 94/6 coating in a dry state, exposed to 24 hours of humidity, then re-dried.
A 94/6 coating agent comprising 94% monoglyceride (thereof 50% SA-1G/50% PA-1G) and 6% fatty acid salt (thereof 50% SA-Na/50% PA-Na) was applied to the surface of a silicon substrate and allowed to dry at room temperature. The coating was heated and X-ray scattering images of the surface were obtained at 60° C., 65° C., and 70° C. A crystalline-to-noncrystalline phase transition was observed between 65° C. and 70° C. (
X-ray scattering images were obtained for the coating above at temperatures of 25° C., 40° C., and 60° C. Out-of plane scattering was analyzed to identify intensity peaks, which were used to determine interlayer spacing of the coating at each temperature. As shown in
Grain size of the coating was then analyzed based on the X-ray scattering images obtained. Grains are identified as domains within which the crystal lattice is continuous and has one orientation. A grain boundary is identified as an interface (or gap) between two adjacent grains, considered as defect in crystal structure (which can act as a pathway for water and gas diffusion). An increase in grain size corresponds to a decrease in the amount of grain boundary. To illustrate this concept,
Film coating applied to the surface of the silicon substrate was exposed to an air duct temperature of 20° C., 50° C., 70° C., or 100° C. for 100 seconds and cooled to room temperature. Mass loss factor was then determined for each coating. As shown in
In addition, films dried at different temperatures also have different grain sizes (
Drying temperature can impact the mosaicity (
Gas diffusion was then measured in coatings that were dried at 25° C. (
Aqueous dispersions of 95:5 IA-1G and SA-Na, 95:5 SA-1G and SA-Na, 95:5 PA-1G and PA-Na, 95:5 MA-1G and MA-Na, 95:5 LA-1G and LA-Na, and 95:5 CA-1G and CA-Na were each prepared in a Vitamix blender at concentrations of 30 g/L with hot water and mixed for 3 minutes. The dispersions were cast into films on plastic substrates in an oven at 50° C. for 12 h followed by characterization by grazing incidence small angle X-ray scattering (GISAXS). The 1D circularly averaged scattering profiles were plotted.
D=2π/q*
Wherein D is the periodic spacing and q* is the primary peak position identified by the black arrows in
The morphologies of the IA-1G, SA-1G, PA-1G, and MA-1G monoglyceride films were determined by obtaining the grazing incidence wide angle X-ray scattering plots, indexing the diffraction peaks to the primary scattering peaks (q*) of the plots, then cross-referencing to known morphologies.
The morphologies of the LA-1G and CA-1G monoglyceride films were determined by obtaining the grazing incidence wide angle X-ray scattering plots, indexing the diffraction peaks to the primary scattering peaks (q*) of the plots, then cross-referencing to known morphologies.
A polysaccharide cellulose was coated with a 94:3:3 SA-1G:SA-Na:PA-Na composition and dried at ambient conditions for 24 h, then characterized by grazing incidence small angle X-ray scattering.
While various compositions and methods have been described above, it should be understood that they have been presented by way of example only, and not limitation. Where methods and steps described above indicate certain events occurring in certain order, ordering of steps may be modified, and such modification are in accordance with the variations of the invention. Additionally, certain of the steps may be performed concurrently in a parallel process when possible, as well as performed sequentially as described above. The various implementations have been particularly shown and described, but it will be understood that various changes in form and details may be made. Accordingly, other implementations are within the scope of the following claims.
This application claims priority to U.S. Provisional Application No. 62/985,305, filed on Mar. 4, 2020, which is incorporated by reference herein in its entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 1016761 | Moore | Feb 1912 | A |
| 1943468 | Bridgeman | Jan 1934 | A |
| 2213557 | Tisdale | Sep 1940 | A |
| 2222000 | Schmidt | Nov 1940 | A |
| 2223168 | Dombrow | Nov 1940 | A |
| 2275659 | Steinle et al. | Mar 1942 | A |
| 2324448 | Wehrli | Jul 1943 | A |
| 2333887 | Redlinger | Nov 1943 | A |
| 2363232 | De Witt Cothran | Nov 1944 | A |
| 2424952 | Handy | Jul 1947 | A |
| 2472794 | Cothran | Jun 1949 | A |
| 2657282 | Winkel | Oct 1953 | A |
| 2697793 | Trump et al. | Dec 1954 | A |
| 2857282 | Jansen | Oct 1958 | A |
| 3189467 | Kalmar | Jun 1965 | A |
| 3208951 | Berger et al. | Sep 1965 | A |
| 3232765 | Rosenthal et al. | Feb 1966 | A |
| 3449108 | McConnell et al. | Jun 1969 | A |
| 3471303 | Hamdy et al. | Oct 1969 | A |
| 3715024 | Mumma | Feb 1973 | A |
| 3997674 | Ukai | Dec 1976 | A |
| 4002775 | Kabara | Jan 1977 | A |
| 4002777 | Juvinall et al. | Jan 1977 | A |
| 4115313 | Lyon et al. | Sep 1978 | A |
| 4421775 | Chan, Jr. | Dec 1983 | A |
| 4423071 | Chignac et al. | Dec 1983 | A |
| 4649057 | Thomson | Mar 1987 | A |
| 4654370 | Marriot et al. | Mar 1987 | A |
| 4661359 | Seaborne | Apr 1987 | A |
| 4710228 | Seaborne et al. | Dec 1987 | A |
| 4726898 | Mills et al. | Feb 1988 | A |
| 4732708 | Ekman et al. | Mar 1988 | A |
| 4820533 | Seaborne | Apr 1989 | A |
| 4857345 | Sardo | Aug 1989 | A |
| 4874618 | Seaborn | Oct 1989 | A |
| 4960600 | Kester et al. | Oct 1990 | A |
| 4962885 | Coffee | Oct 1990 | A |
| 5019403 | Krochta | May 1991 | A |
| 5051448 | Shashoua | Sep 1991 | A |
| 5110509 | Peter et al. | May 1992 | A |
| 5126153 | Beck | Jun 1992 | A |
| 5209410 | Wichmann et al. | May 1993 | A |
| 2342063 | Sells | Feb 1994 | A |
| 5354573 | Gross et al. | Oct 1994 | A |
| 5366995 | Savage | Nov 1994 | A |
| 5376391 | Nisperos-Carriedo | Dec 1994 | A |
| 5389389 | Beck | Feb 1995 | A |
| 5451266 | Kirk | Sep 1995 | A |
| 5498295 | Murch | Mar 1996 | A |
| 5543164 | Krochta et al. | Aug 1996 | A |
| H1591 | Fulcher | Sep 1996 | H |
| 5607970 | Ishihara | Mar 1997 | A |
| 5658768 | Quinlan | Aug 1997 | A |
| 5741505 | Beyer | Apr 1998 | A |
| 5827553 | Dimitroglou | Oct 1998 | A |
| 5832527 | Kawaguchi | Nov 1998 | A |
| 5906831 | Larsson et al. | May 1999 | A |
| 5925395 | Chen | Jul 1999 | A |
| 5939117 | Chen et al. | Aug 1999 | A |
| 6010726 | Evans et al. | Jan 2000 | A |
| 6033705 | Isaacs | Mar 2000 | A |
| 6136856 | Savage | Oct 2000 | A |
| 6162475 | Hagenmaier et al. | Dec 2000 | A |
| 6165529 | Yang | Dec 2000 | A |
| 6241971 | Fox et al. | Jun 2001 | B1 |
| 6254645 | Kellis et al. | Jul 2001 | B1 |
| 6255451 | Koch et al. | Jul 2001 | B1 |
| 6294186 | Beerse et al. | Sep 2001 | B1 |
| 6348217 | Santos et al. | Feb 2002 | B1 |
| 6503492 | McGlone et al. | Jan 2003 | B2 |
| 6723364 | Bompeix | Apr 2004 | B1 |
| 6783768 | Brown et al. | Aug 2004 | B1 |
| 6822105 | Luxem | Nov 2004 | B1 |
| 7373135 | Najib-Fruchart et al. | May 2008 | B2 |
| 7375135 | Naiib-Fruchart et al. | May 2008 | B2 |
| 7550617 | Imig et al. | Jun 2009 | B2 |
| 7708822 | Lahav et al. | May 2010 | B2 |
| 7732470 | Imig et al. | Jun 2010 | B2 |
| 7754766 | Awad | Jul 2010 | B2 |
| 7785897 | Agnes et al. | Aug 2010 | B2 |
| 7851002 | Hekal et al. | Dec 2010 | B2 |
| 7931926 | Lidster et al. | Apr 2011 | B2 |
| 7943336 | Viksoe-Nielsen et al. | May 2011 | B2 |
| 8101221 | Chen et al. | Jan 2012 | B2 |
| 8119178 | Lidster et al. | Feb 2012 | B2 |
| 8197870 | Krasutsky et al. | Jun 2012 | B2 |
| 8247609 | Roques et al. | Aug 2012 | B2 |
| 8263751 | Peterson | Sep 2012 | B2 |
| 8424243 | Narciso et al. | Apr 2013 | B1 |
| 8501445 | Yoshikawa et al. | Aug 2013 | B2 |
| 8546115 | Buchert et al. | Oct 2013 | B2 |
| 8586807 | Hatcher | Nov 2013 | B2 |
| 8609169 | Chen et al. | Dec 2013 | B2 |
| 8752328 | Kaiser et al. | Jun 2014 | B2 |
| 8846355 | Yoshikawa et al. | Sep 2014 | B2 |
| 9095152 | Munger | Aug 2015 | B2 |
| 9102125 | Battersby et al. | Aug 2015 | B2 |
| 9283173 | Lederman | Mar 2016 | B2 |
| 9284432 | Yoshikawa et al. | Mar 2016 | B2 |
| 9475643 | Odman et al. | Oct 2016 | B1 |
| 9714399 | Verkuiil | Jul 2017 | B2 |
| 9743670 | Grund | Aug 2017 | B2 |
| 9743679 | Perez et al. | Aug 2017 | B2 |
| 9770041 | Dong et al. | Sep 2017 | B2 |
| 10150132 | Hamamoto et al. | Dec 2018 | B2 |
| 20010042341 | Hamersky et al. | Nov 2001 | A1 |
| 20020043577 | Krasutsky et al. | Apr 2002 | A1 |
| 20020123546 | Bigg et al. | Sep 2002 | A1 |
| 20030044488 | Roskam | Mar 2003 | A1 |
| 20030124228 | Goto | Jul 2003 | A1 |
| 20030194445 | Kuhner et al. | Oct 2003 | A1 |
| 20040022906 | Petacvich | Feb 2004 | A1 |
| 20040120919 | Nguyen et al. | Jun 2004 | A1 |
| 20040220283 | Zhang et al. | Nov 2004 | A1 |
| 20050053593 | Wang et al. | Mar 2005 | A1 |
| 20050233039 | Wolfe | Oct 2005 | A1 |
| 20050249856 | Marangoni | Nov 2005 | A1 |
| 20060037892 | Blanc | Feb 2006 | A1 |
| 20060057187 | Eskuchen et al. | Mar 2006 | A1 |
| 20060057259 | Ripoll et al. | Mar 2006 | A1 |
| 20060153912 | Habich et al. | Jul 2006 | A1 |
| 20060198924 | Song et al. | Sep 2006 | A1 |
| 20060292281 | Kragh et al. | Dec 2006 | A1 |
| 20070278103 | Hoerr et al. | Dec 2007 | A1 |
| 20080026120 | Petcavich | Jan 2008 | A1 |
| 20080038471 | Boger et al. | Feb 2008 | A1 |
| 20080119772 | Coffee | May 2008 | A1 |
| 20080254987 | Liu et al. | Oct 2008 | A1 |
| 20080262190 | Koskimies et al. | Oct 2008 | A1 |
| 20080310991 | Webster | Dec 2008 | A1 |
| 20090035414 | Cheng et al. | Feb 2009 | A1 |
| 20090042985 | Bhaggan et al. | Feb 2009 | A1 |
| 20090104446 | Guillet et al. | Apr 2009 | A1 |
| 20090123632 | Klemann et al. | May 2009 | A1 |
| 20090142453 | Lobisser et al. | Jun 2009 | A1 |
| 20090163729 | Li | Jun 2009 | A1 |
| 20090224437 | Fukuoka et al. | Sep 2009 | A1 |
| 20090325240 | Daniell | Dec 2009 | A1 |
| 20100029778 | Bailey et al. | Feb 2010 | A1 |
| 20100092631 | Sardo | Apr 2010 | A1 |
| 20100210745 | McDaniel | Aug 2010 | A1 |
| 20100278784 | Pojasek et al. | Nov 2010 | A1 |
| 20100292426 | Hossainv | Nov 2010 | A1 |
| 20110000975 | Gartstein et al. | Jan 2011 | A1 |
| 20110003014 | Kulikowski | Jan 2011 | A1 |
| 20110240064 | Wales | Oct 2011 | A1 |
| 20110244095 | Sardo | Oct 2011 | A1 |
| 20110280942 | Schad | Nov 2011 | A1 |
| 20120003356 | Ekanayake et al. | Jan 2012 | A1 |
| 20120103790 | Krull et al. | May 2012 | A1 |
| 20120251675 | Sowa | Oct 2012 | A1 |
| 20130045246 | Edwards et al. | Feb 2013 | A1 |
| 20130095141 | Schad | Apr 2013 | A1 |
| 20130156970 | Crawford | Jun 2013 | A1 |
| 20130209617 | Lobisser et al. | Aug 2013 | A1 |
| 20130216488 | Hemandez-Brenes et al. | Aug 2013 | A1 |
| 20130323378 | Stark | Dec 2013 | A1 |
| 20140033926 | Passel et al. | Feb 2014 | A1 |
| 20140199449 | Hernandez et al. | Jul 2014 | A1 |
| 20140205722 | Quintanar Guerrero | Jul 2014 | A1 |
| 20140221308 | Baker et al. | Aug 2014 | A1 |
| 20140234921 | Nyyssola et al. | Aug 2014 | A1 |
| 20140348945 | Dong et al. | Nov 2014 | A1 |
| 20150021802 | Wakita | Jan 2015 | A1 |
| 20150030780 | Rogers | Jan 2015 | A1 |
| 20150079248 | Nussinovitch | Mar 2015 | A1 |
| 20150210855 | Firth | Jul 2015 | A1 |
| 20150359217 | Narita | Dec 2015 | A1 |
| 20150366230 | Malefyt et al. | Dec 2015 | A1 |
| 20160002483 | Zhao | Jan 2016 | A1 |
| 20160100597 | Immaraju | Apr 2016 | A1 |
| 20160213030 | Schad | Jul 2016 | A1 |
| 20160256429 | Spanova et al. | Sep 2016 | A1 |
| 20160304410 | Schultz | Oct 2016 | A1 |
| 20160324172 | Williams | Nov 2016 | A1 |
| 20170049119 | Perez et al. | Feb 2017 | A1 |
| 20170073532 | Perez et al. | Mar 2017 | A1 |
| 20170251673 | Cifuentes | Sep 2017 | A1 |
| 20170320077 | Rogers | Nov 2017 | A1 |
| 20180092811 | Klee | Apr 2018 | A1 |
| 20180303732 | Wehner et al. | Oct 2018 | A1 |
| 20180317509 | Van Velzen | Nov 2018 | A1 |
| 20180368427 | Rogers et al. | Dec 2018 | A1 |
| 20190104748 | Kann et al. | Apr 2019 | A1 |
| 20190269145 | Bakus, II et al. | Sep 2019 | A1 |
| 20200068912 | Hernandez | Mar 2020 | A1 |
| 20200352184 | Frazier et al. | Nov 2020 | A1 |
| 20200383343 | Rodriguez et al. | Dec 2020 | A1 |
| 20210337817 | Lee et al. | Nov 2021 | A1 |
| 20220039416 | Kaun et al. | Feb 2022 | A1 |
| 20220064859 | Hernandez et al. | Mar 2022 | A1 |
| 20220135510 | Bakus, II et al. | May 2022 | A1 |
| Number | Date | Country |
|---|---|---|
| 86104531 | Feb 1988 | CN |
| 1103548 | Jun 1995 | CN |
| 1215420 | Apr 1999 | CN |
| 1616561 | May 2005 | CN |
| 1817147 | Aug 2006 | CN |
| 1856261 | Nov 2006 | CN |
| 1870912 | Nov 2006 | CN |
| 101035926 | Sep 2007 | CN |
| 101356012 | Jan 2009 | CN |
| 101454406 | Jun 2009 | CN |
| 101708013 | May 2010 | CN |
| 102119719 | Jul 2011 | CN |
| 102291986 | Dec 2011 | CN |
| 102335142 | Feb 2012 | CN |
| 102349555 | Feb 2012 | CN |
| 103283830 | Sep 2013 | CN |
| 103478233 | Jan 2014 | CN |
| 103609670 | Mar 2014 | CN |
| 103719261 | Apr 2014 | CN |
| 103734280 | Apr 2014 | CN |
| 104606076 | May 2015 | CN |
| 104642528 | May 2015 | CN |
| 105341619 | Feb 2016 | CN |
| 105494615 | Apr 2016 | CN |
| 106280909 | Jan 2017 | CN |
| 107828560 | Mar 2018 | CN |
| 110255947 | Sep 2019 | CN |
| 112898630 | Jun 2021 | CN |
| 2505428 | Aug 1976 | DE |
| 3622191 | Jan 1988 | DE |
| 0104043 | Mar 1984 | EP |
| 0655201 | May 1995 | EP |
| 1020124 | Jul 2000 | EP |
| 1681281 | Jul 2006 | EP |
| 2389814 | Nov 2011 | EP |
| 2644185 | Oct 2013 | EP |
| 2684879 | Jan 2014 | EP |
| 3354264 | Aug 2018 | EP |
| 1041955 | Aug 1999 | ES |
| 421649 | Dec 1934 | GB |
| 192832 | May 2004 | IN |
| S54-139645 | Oct 1979 | JP |
| S58-034034 | Feb 1983 | JP |
| S58-89140 | May 1983 | JP |
| 62-126931 | Jun 1987 | JP |
| S63-062574 | Mar 1988 | JP |
| H04-016173 | Jan 1992 | JP |
| H04-507192 | Dec 1992 | JP |
| H06-506166 | Jul 1994 | JP |
| H07-075519 | Mar 1995 | JP |
| H08-056564 | Mar 1996 | JP |
| 2519455 | Jul 1996 | JP |
| H10-298003 | Nov 1998 | JP |
| 2002-531075 | Sep 2002 | JP |
| 2003-522130 | Jul 2003 | JP |
| 2007-502271 | Feb 2007 | JP |
| 2007-510014 | Apr 2007 | JP |
| 2008-504442 | Feb 2008 | JP |
| 2009-527357 | Jul 2009 | JP |
| 2010-530795 | Sep 2010 | JP |
| 2012-087072 | May 2012 | JP |
| 2012-515561 | Jul 2012 | JP |
| 2013-139433 | Jul 2013 | JP |
| 2014-231481 | Dec 2014 | JP |
| WO 9306735 | Apr 1993 | WO |
| WO 2001001980 | Jan 2001 | WO |
| WO 2004030455 | Apr 2004 | WO |
| WO 2007100654 | Sep 2007 | WO |
| WO 2008142393 | Nov 2008 | WO |
| WO 2009119730 | Oct 2009 | WO |
| 2010031929 | Mar 2010 | WO |
| WO 2011014831 | Feb 2011 | WO |
| WO 2012042404 | Apr 2012 | WO |
| WO 2012164561 | Dec 2012 | WO |
| WO 2012173262 | Dec 2012 | WO |
| 2014162238 | Oct 2014 | WO |
| WO 2014206911 | Dec 2014 | WO |
| WO 2015017450 | Feb 2015 | WO |
| WO 2015028299 | Mar 2015 | WO |
| WO 2015052433 | Apr 2015 | WO |
| WO 2015074144 | May 2015 | WO |
| WO 2015176020 | Nov 2015 | WO |
| WO 2016168319 | Oct 2016 | WO |
| WO 2016187581 | Nov 2016 | WO |
| WO 2017043972 | Mar 2017 | WO |
| WO 2017048951 | Mar 2017 | WO |
| WO 2017100636 | Jun 2017 | WO |
| WO 2017132281 | Aug 2017 | WO |
| WO 2017172951 | Oct 2017 | WO |
| WO 2018009846 | Jan 2018 | WO |
| WO 2018042435 | Mar 2018 | WO |
| WO 2018094269 | May 2018 | WO |
| 2019096844 | May 2019 | WO |
| Entry |
|---|
| Dinani et al., Optimization of Carboxymethyl Cellulose and Calcium Chloride Dip-Coating on Mushroom Slices Prior to Hot Air Drying Using Response Surface Methodology, Journal of Food Processing and Prevention, 38, 2014, pp. 1269-1278. |
| Rahman et al., The Effect of a New Coating on the Drying Performace of Fruit and Vegetables Products: Experimental Investigation and Artificial Neural Network Modeling, Foods, 2020, 9, 308, pp. 1-13. |
| Lin et al., “Innovations in the Development and Application of Edible Coatings for Fresh and Minimally Processed Fruits and Vegetables,” Compr. Rev. Food Sci. Food Saf., Jun. 2007, 6(3):60-75. |
| Alvaro, J. et al., “Effects of peracetic acid disinfectant on the postharvest of some fresh vegetables,” Journal of Food Engineering, 2009, vol. 95, pp. 11-15. |
| Alvira et al., “Pretreatment Technologies for an Efficient Bioethanol Production Process Based on Enzymatic Hydrolysis: A Review,” Bio resource Technology, 2010, 101(13):4851-4861. |
| Andrade, Ricardo D. et al., “Atomizing spray systems for application of edible coatings,” Comprehensive Reviews in Food Science and Food Safety, vol. 11, No. 3, 2012, p. 323-337. |
| Ayala-Zavala, J.F. et al., “High Relative Humidity In-Package of Fresh-Cut Fruits and Vegetables: Advantage or Disadvantage Considering Microbiological Problems and Antimicrobial Delivering Systems?,” J Food Science, 2008, vol. 73, p. R41-R47. |
| Baker et al., “Cutin Degradation by Plant Pathogenic Fungi,” The American Phytopathological Society, May 15, 1978, 68:1577-1584. |
| Banerjee, S. et al., “Review Article: Electrospray Ionization Mass Spectrometry: A Technique to Access the Information Beyond the Molecular Weight of the Analyte,” International Journal of Analytical Chemistry, Nov. 2011, vol. 2012, Article ID 282574, 40 pages. |
| Bateman, A. et al., “Supporting Information for Manuscript es-2008-01226w—The Effect of Solvent on the Analysis of Secondary Organic Aerosol Using Electrospray Ionization Mass Spectrometry,” [online] 2008; available from the Internet URL: http://aerosol.chem.uci.edu/publications/Irvine/2008.sub.--Bateman.sub.---EST.sub.--SOA.sub.--solvent.sub.--effects.sub.--supporting.sub.--info.pdf, 6 pages. |
| Bateman, A. et al., “The Effect of Solvent on the Analysis of Secondary Organic Aerosol Using Electrospray Ionization Mass Spectrometry,” Environ. Sci. Technol., 2008, vol. 42, No. 19, pp. 7341-7346. |
| Bell et al., “The activity of (S)-hydroprene space spray against three stored products pests in a simulated food production environment,” Journal of Stored Products Research, Apr. 1999,35(2):117-126. |
| Ben-Yehoshua, S. et al., “Modified-atmosphere packaging of fruits and vegetables: reducing condensation of water in bell peppers and mangoes,” Acta Hort (ISHS), 1998, vol. 464, 387-392. |
| Bewick, T. et al., “Evaluation of Epicuticular Wax Removal from Whole Leaves with Chloroform,” Weed Technology, Jul. 1993, vol. 7, No. 3, pp. 706-716. |
| Bourtoom, T., “Edible films and coatings: characteristics and properties,” International Food Research Journal, 2008, vol. 15, No. 3, pp. 237-248, 13 pages. |
| Cantwell, M., “Properties and recommended conditions for long-term storage of fresh fruits and vegetables,” Nov. 2001, 8 Pages. |
| Cech, N., et al., “Practical Implications of Some Recent Studies in Electrospray Ionization Fundamentals,” Mass Spectrometry Reviews, 2001, vol. 20, pp. 362-387. |
| Chen, D-R., et al., “Electrospraying of Conducting Liquids for Monodisperse Aerosol Generation in the 4 nm to 1.8 .mu.m Diameter Range,” J. Aerosol Sci., 1995, vol. 26, No. 6, pp. 963-977. |
| Cochran, H.D., “Solvation in supercritical water,” Fluid Phase Equilibria, 1992, vol. 71, pp. 1-16. |
| Deell JR et al., “Addition of sorbitol with KMnO4 improves broccoli quality retention in modified atmosphere packages,” J Food Oual, 2006, vol. 29, p. 65-75. |
| Dhall, “Advances in edible coatings for fresh fruits and vegetables: a review,” Crit. Rev. Food Sci. Nutr., 2013, 53(5), pp. 435-450. |
| Duoren et al., “Green Plasticizers,” Scientific and Technological Literature Publishing House, the 1st Edition, Oct. 2011, 339-340, 7 pages (with English translation). |
| Elgimabi and Ahmed, “Effects of Bactericides and Sucrose-Pulsing on Vase Life of Rose Cut Flowers (Rosa hybirida),” Botany Research International, 2009, 2(3) p. 164-168. |
| Enke, C., “A Predictive Model for Matrix and Analyte Effects in Electrospray Ionization of Singly-charged Ionic Analytes,” Analytical Chemistry, 1997, vol. 69, No. 23, pp. 4885-4893. |
| Extended European Search Report for European Patent Application No. EP 14831592.2, dated Mar. 2, 2017, 9 Pages. |
| Gabler, M., et al., “Impact of Postharvest Hot Water or Ethanol Treatment of Table Grapes on Gray Mold Incidence, Quality, and Ethanol Content,” Plant Disease, Mar. 2005, vol. 89, No. 3, pp. 309-316. |
| Gaskell, S., “Special Feature: Tutorial-Electrospray: Principles and Practice,” J. Mass Spectrom, 1997, vol. 32, pp. 677-688. |
| Gil, M. et al., “Fresh-cut product sanitation and wash water disinfection: Problems and solutions,” International Journal of Food Microbiology, 2009, vol. 134, pp. 37-45. |
| Graca, “Suberin: the biopolyester at the frontier of plants,” Frontiers in Chemistry, Oct. 2015, 3(62):1-11. |
| Graca, J. et al., “Glycerol and glyceryl esters of o-hydroxyacids in cutins,” Phytochemistry, 2002, vol. 61, pp. 205-215. |
| Graca, J. et al., “Linear and branched poly (omega-hydroxyacid) esters in plant cutins,” J. Agric. Food Chem., 2010, vol. 58, No. 17, pp. 9666-9674. |
| Hardenburg, R., et al., “The Commercial Storage of Fruits, Vegetables, and Florist and Nursery Stocks,” United States Department of Agriculture, Agriculture Handbook No. 66, Sep. 1986, pp. 6-7, 30, 50-51. |
| Hauff, S. et al., “Determination of hydroxylated fatty acids from the biopolymer of tomato cutin and their fate during incubation in soil,” Phytochemical Analysis, Aug. 26, 2010, vol. 21, No. 6, pp. 582-589. |
| He et al., “Stem end blockage in cut Grevillea ‘Crimson Yul-lo’ inflorescences,” Postharvest Biology and Technology, 2006, vol. 41, p. 78-84. |
| Herrero et al., “Compressed fluids for the extraction of bioactive compounds,” TrAC Trends in Analytical Chemistiy, 2013, 43(1):67-83. |
| Hojjati et al., “Chemical Treatments of Eustoma Cut Flower Cultivars for Enhanced Vase Life,” Journal of Awiculture and Social Sciences, 2007, vol. 3, No. 3, p. 75-78. |
| Holcroft, D., “Water Relations in Harvested Fresh Produce,” PEF White Paper No. 15-01, The Postharvest Education Foundation (PEF), May 2015, 16 Pages. |
| Hongyou, “Homemade Fruit and Vegetable Coating Preservative,” Vegetables, Nov. 30, 2005, p. 39, 2 pages (with English translation). |
| Huang et al., “Automation of a Fourier transform ion cyclotron resonance mass spectrometer for acquisition, analysis, and e-mailing of high-resolution exact-mass electrospray ionization mass spectral data,” Journal of the American Society for Mass Spectrometry, Nov. 1, 1999, 10(11):1166-1173. |
| Huang, T-Y., et al., “Electron Transfer Reagent Anion Formation via Electrospray Ionization and Collision-induced Dissociation,” Anal Chem., 2006, vol. 78, No. 21, pp. 7387-7391, 9 pages. |
| Hudson, B., “Fatty Acids,” Encyclopedia of Food Sciences and Nutrition (Second Edition), 2003, pp. 2297-2300. |
| Javad et al., “Effect of Cultivar on Water Relations and Postharvest Quality ofGerbera (Gerbera jamesonii bolus ex. Hook f.) Cut Flower,” World Applied Sciences Journal, 2012, vol. 18, No. 5, p. 698-703. |
| Javad et al., “Postharvest evaluation of vase life, stem bending and screening of cultivars ofcut gerbera (Gerberajamesonii bolux ex. Hook f.) flowers,” African Journal of Biotechnology 2011, 10(4), p. 560-566. |
| Jaworek, A., “Electrospray Droplet Sources for Thin Film Deposition,” J. Mater Sci, 2007, vol. 42, pp. 266-297. |
| Jenkin, S. et al., “Isolation and Compositional Analysis of Plant Cuticle Lipid Polyester Monomers,” Journal of Visualized Experiments, 105 e53386, 10 pages, URL: https://www.jove.com/video/53386. |
| Jensen et al., “Estimation of the Monoglyceride Content of Milk,” Journal of Dairy Science, 1959, 42(2):232-239. |
| Jerome, F., et al., “”One pot“ and selective synthesis of monoglycerides over homogeneous and heterogeneous guanidine catalysts,” Green Chem., 2004, vol. 6, pp. 72-74. |
| Jiabin, “Rubberized fabrics and products thereof,” World Rubber Industry, Dec. 2000, 6:27-32, 24 pages (with English translation). |
| Jingmei et al., “Preparation of modified starch/polylactic acid bleeds,” New Chemical Materials, Jun. 2011, 39(6)425-126 and 129 (with English abstract). |
| Jones et al., “Pulsing with Triton X-100 Improves Hydration and Vase Life of Cut Sunflowers (Helianthus annuus L.),” HortScience, 1993, vol. 28, No. 12, p. 1178-1179. |
| Karabulut, O. et al., “Postharvest ethanol and hot water treatments of table grapes to control gray mold,” Postharvest Biology and Technology, 2004, vol. 34, pp. 169-177. |
| Kebarle, P., “Special Feature: Commentary—A Brief Overview of the Present Status of the Mechanisms Involved in Electrospray Mass Spectrometry,” J. Mass Spectrom, 2000, vol. 35, pp. 804-817. |
| Keller, B., et al., “Review Article: Interferences and Contaminants Encountered in Modem Mass Spectrometry,” Analytica Chimica Acta, 2008, vol. 627, pp. 71-81. |
| Khan et al., “Application of Edible Coating for Improving Meat Quality: A Review,” Pakistan Journal of Food Sciences, 2013, 23(2):71-79. |
| Kolattukudy, P.E., “BiopolyesterMembranes of Plants: Cutin and Suberin,” Science, 1980, vol. 208, No. 4447, pp. 990-1000. |
| Kolattukudy, P.E., “Cutin from plants,” Biopolymers Online, 3a, 2005, 40 pages. |
| Krammer, P., et al., “Hydrolysis of esters in subcritical and supercritical water,” Journal of Supercritical Fluids, 2000, vol. 16, pp. 189-206. |
| Kroll, B., et al., “Review: Chemistry of Secondary Organic Aerosol: Formation and Evolution of Low-volatility Organics in the Atmosphere,” Atmospheric Environment, 2008, vol. 42, pp. 3593-3624. |
| Kubo et al., “Modes of antifungal action of alkanols against Saccharomyces cerevisiae,” Bioorganic & Medicinal Chemistiy, Mar. 2003, 11(6):1117-1122. |
| Kubo et al., “Structural functions of antimicrobial long-chain alcohols and phenols,” Bioorganic & Medicinal Chemistry, Jul. 1995, 3(7):873-880. |
| Kulkarni et al., “Natural Polymers—A comprehensive review,” International Journal of Research in Pharmaceutical and Biomedical Sciences, Dec. 2012, 3(4):1597-1613. |
| Li, M., et al., “Direct Quantification of Organic Acids in Aerosols by Desorption Electrospray Ionization Mass Spectrometiy,” Atmospheric Environment, 2009, vol. 43, pp. 2717-2720. |
| Loppinet-Serani, A. et al., “Supercritical water for environmental technologies,” J Chem Technol Biotechnol, Jan. 12, 2010, vol. 85, pp. 583-589. |
| Martin, “Preparation of Saturated and Unsaturated Symmetrical Monoglycerides,” Journal of American Chemical Society, Jun. 1953, 75(20):5482-5483. |
| Matic, M., “The chemistry of Plant Cuticles: a study of cutin form Agave americana L.,” Biochemical Journal, 1956, vol. 63, No. 1, pp. 168-176. |
| Mattson, F.H., et al., “Synthesis and properties of glycerides,” J Lipid Research, Jul. 1962, vol. 3, No. 3, pp. 281-296. |
| Meihu et al., “Research on Coating of Preserved Egg for Quality-keeping and Fresh-keeping,” Wan Fang, Aug. 2007, 17 pages (with English translation). |
| Morton, H., “The Relationship of Concentration and Germicidal Efficiency of Ethyl Alcohol,” Annals New York Academy of Sciences, 53(1), 1950, pp. 191-196. |
| Mukheijee et al., “Antibacterial activity of long-chain fatty alcohols against mycobacteria,” FEMS Microbiol. Lett, Jan. 2013, 338(2):177-183. |
| Nemoto et al., “Polyols of a cascade type as a water-solubilizing element of carborane derivatives for boron neutron capture therapy,” The Journal of Organic Chemistry, Jan. 1992, 57(2):435. |
| Nizkorodov, S et al., “Molecular Chemistry of Organic Aerosols through the Application of High Resolution Mass Spectrometry,” Phys. Chern, Chem., Phys, 2011, vol. 13, pp. 3612-3629. |
| Oh, D. et al., “Antimicrobial activity of ethanol, glycerol monolaurate or lactic acid against Listeria monocytogenes,” International Journal of Food Microbiology, 1993, vol. 20, pp. 239-246. |
| Olmez, H. et al., “Potential alternative disinfection methods for organic fresh-cut industry for minimizing water consumption and environmental impact,” LWT—Food Science and Technology, 2009, vol. 42, pp. 686-693. |
| Orts et al., “Edible Films and Coatings: Why, What, and How?,” Edible Films and Coatings for Food Applications, 2009, Chapter 1:1-23. |
| Osman, S.F. et al., “Preparation, Isolation, and Characterization of Cutin Monomers and oligomers from Tomato Peels,” J. Agric, Food Chem, 1999, vol. 47, No. 2, pp. 799-802. |
| PCT International Preliminary Report on Patentability in International Appln. No. PCT/US2016/051936, dated Mar. 29, 2018, 12 pages. |
| PCT International Search Report and Written Opinion for PCT/US2016/051936, dated Jan. 31, 2017, 18 Pages. |
| PCT International Search Report and Written Opinion for PCT/US2016/065917, dated Mar. 9, 2017, 10 Pages. |
| PCT International Search Report and Written Opinion for PCT/US2017/014978, dated Apr. 10, 2017, 13 Pages. |
| PCT International Search Report and Written Opinion in International Appln. No. PCT/US2019/042693, dated Oct. 2, 2019, 8 pages. |
| PCT International Search Report and Written Opinion in International Appln. No. PCT/US2019/045784, dated Oct. 22, 2019, 14 pages. |
| PCT International Search Report and Written Opinion in International Appln. No. PCT/US2019/049585, dated Jan. 13, 2020, 14 pages. |
| PCT International Search Report and Written Opinion in International Appln. No. PCT/US2020/036174, dated Sep. 7, 2020, 32 pages. |
| PCT International Search Report and Written Opinion in PCT/US18/46998, dated Dec. 27, 2018, 31 pages. |
| PCT International Search Report and Written Opinion in PCT/US2014/048707, dated Nov. 13, 2014, 14 pages. |
| PCT International Search Report and Written Opinion in PCT/US2017/024799, dated Jun. 8, 2017, 13 pages. |
| PCT International Search Report and Written Opinion in PCT/US2017/041167, dated Oct. 9, 2017, 16 pages. |
| PCT International Search Report and Written Opinion, PCT Application No. PCT/US16/33617, dated Aug. 26, 2016, 20 Pages. |
| PCT International Search Report and Written Opinion, PCT Application No. PCT/US17/62399, dated Feb. 16, 2018, 16 Pages. |
| PCT International Search Report and Written Opinion, PCT Application No. PCT/US2018/46994, dated Dec. 20, 2018, 28 pages. |
| PCT Invitation to Pay additional Fees and, Where Applicable, Protest Fee in International Appln. No. PCT/US2018/046994, dated Oct. 23, 2018, 2 pages. |
| Perkins et al., “Ultrasonic fog application of organic acids delays postharvest decay in red bayberry,” Postharvest Biology and Technology, Nov. 2017, 13:41-47. |
| Roy, S. et al., “Modified atmosphere and modified humidity packaging of fresh mushrooms,” J Food Sci., 1996, vol. 61, p. 391-397. |
| Rujun et al., “Surface Modification and Physical properties of Inorganic Nanomaterials,” University of Technology Press, 1st Edition, Oct. 2009, 43-45, 11 pages (with English translation). |
| Rutala, W. et al., “Guideline for Disinfection and Sterilization in Healthcare Facilities, 2008,” CPC, 2008, 158 Pages. |
| Sasaki, M. et al., “Cellulose hydrolysis in subcritical and supercritical water,” Journal of Supercritical Fluids, 1998, vol. 13, pp. 261-268. |
| Sasaki, M. et al., “Dissolution and Hydrolysis of Cellulose in Subcritical and Supercritical Water,” Ind. Eng. Chem. Res., 2000, vol. 39, pp. 2883-2890. |
| Savage, P., “Organic Chemical Reactions in Supercritical Water,” Chem. Rev., 1999, vol. 99, pp. 603-621. |
| Schreiber et al., “Transport bamers made of cutin, suberin and associated waxes,” Trends in Plant Science, 2010, vol. 15, No. 10, p. 546-553. |
| Schweizer, P. et al., “Perception of free cutin monomers by plant cells,” The Plant Journal, vol. 10, No. 2, 1996, p. 331-341. |
| Schweizer, P. et al., “Plant Protection by Free Cutin Monomers in Two Cereal Pathosystems,” Advances in Molecular Genetics of Plant-Microbe Interactions, 1994, p. 371-374. |
| Shirazi A, et al., “Controlling relative humidity in modified atmosphere packages of tomato fruit,” HortScience, 1992, vol. 27, p. 336-339. |
| Siekmann et al., “Preparation and structural investigations of colloidal dispersions prepared from cubic monoglyceride-water phases,” Int. J. Pharm., Sep. 2002, 244(1-2):33-43. |
| Spicer et al., “Novel Process for Producing Cubic Liquid Crystalline Nanoparticles (Cubosomes),” Langmuir, Aug. 2001, 17(19):5748-5756. |
| Steuter et al., “Water Potential of Aqueous Polyethylene Glycol,” Plant Physiol., 1981, vol. 67, p. 64-67. |
| Takats, Z., et al., “Special Feature: Perspective-Ambient Mass Spectrometry Using Desorption Electrospray Ionization (DESI): Instrumentation, Mechanisms and Applications in Forensics, Chemistry, and Biology,” J. Mass Spectrom, 2005, vol. 40, pp. 1261-1275. |
| Tanaka, M., et al., “Quantitative determination of isomeric glycerides, free fatty acids and triglycerides by thin layer chromatography-flame ionization detector system.” Lipids, 1980, vol. 15, No. 10, pp. 872-875. |
| Technical Evaluation Report, “Glycerides (mono and di) Handling/Processing,” Compiled by OMRI for the USDA National Organic Program, Jan. 27, 2015, 1-14. |
| Tegelaar, E.W. et al., “Some mechanisms of flash pyrolysis of naturally occurring higher plant polyesters,” Journal of Analytical and Applied Pyrosis, 1989, vol. 15, 2 pages (abstract only). |
| The Fountainhead Group, Inc., “Burgess Electric Professional Fogger,” Manual No. 161128, Revision D, Feb. 25, 2015, retrieved on Jan. 12, 2021, retrieved from URL <https://www.jondon.com/media/pdf/manuals/FG-EGF-EA_manual.pdf>, 8 pages. |
| TW Search Report in Taiwan Appln. No. 105130215, dated Aug. 6, 2020, 12 pages (with English translation). |
| Van Doorn et al., “Alkylethoxylate surfactants for rehydration of roses and Bouvardia flowers,” Postharvest Biology and Technology, 2002, vol. 24, p. 327-333. |
| Van Doorn et al., “Effects of surfactants on the longevity of dry-stored cut flowering stems of rose, Bouvardia, andAstilbe,” Postharvest Biology and Technology, 1993, vol. 3, pp. 69-76. |
| Van Meeteren, “Water Relations and Keeping-Quality of Cut Gerbera Flowers. I. The Cause of Stem Break,” Scientia Horticulturae, 1978, vol. 8, p. 65-74. |
| Vardar et al., “The application of various disinfectants by fogging for decreasing postharvest diseases of strawberry,” Postharvest Biology and Technology, Apr. 2012, 66:30-34. |
| Wang, R. et al., “Evolution of the Solvent Polarity in an Electrospray Plume,” J. Am Soc Mass Spectrom, 2010, vol. 21, pp. 378-385. |
| Weingartner, H. et al., “Supercritical water as a solvent,” Angewandte Chemie, 2005, vol. 44, Issue 18, pp. 2672-2692. |
| Wikipedia, Anonymous, “Paint-Wikipedia,” retrieved from URL <https://en.wikipedia.org/w/index.php?title=Paint&oldid=563291624>, retrieved Jul. 2013, 7 Pages. |
| Xizhong et al., “Spray drying,” the 2nd edition, Chemical Industry Press, Feb. 28, 2003, 147-151, 9 pages. |
| Yang et al., “Progress on Graft Polymerization of Cellulose,” Journal of Cellulose Science and Technology, Sep. 2009, 17(3), 6 pages (with English abstract). |
| Yeats, T. et al., “The identification of cutin synthase: formation of the plant polyester cutin,” Nat Chem Biol., Jul. 2012, vol. 8, No. 7, pp. 609-611, 10 pages. |
| Zhu, J. et al., “Focus: Electrospray-Formation and Decompositions of Chloride Adduct Ions, [M+CI], in Negative Ion Electrospray Ionization Mass Spectrometry,” J. Am Soc Mass Spectrom, 2000, vol. 11, pp. 932-941. |
| Zhu, J. et al., “Ranking of a Gas-phase Acidities and Chloride Affinities of Monosaccharides and Linkage Specificity in Collision-induced Decompositions of Negative Ion Electrospray-generated Chloride Adducts of Oligosaccharides,” J. Am Soc Mass Spectrom, 2001, vol. 12, pp. 1193-1204. |
| Berge et al., “Pharmaceutical Salts,” J. Pharm. Sci., Jan. 1977, 66(1):1-19. |
| PCT International Search Report and Written Opinion in International Appln. No. PCT/US2021/020692, dated Jun. 1, 2021, 13 pages. |
| PCT International Search Report and Written Opinion in International Appln. No PCT/US2021/044535, dated Nov. 17, 2021, 16 pages. |
| Vargas et al., “Development of Edible Coatings for Fresh Fruits and Vegetables: Possibilities and Limitations,” Fresh Produce, Jan. 2008, 2(2):32-40. |
| PCT International Preliminary Reporton Patentability in International Appln. No. PCT/US2020/036174, dated Dec. 16, 2021, 9 pages. |
| PCT International Search Report and Written Opinion in International Appln. No. PCT/US2021/048301, dated Dec. 7, 2021, 12 pages. |
| Adkins et al., “Manipulating Avocado Fruit Ripening with 1-Methylcyclopropene,” Postharvest Biol. Technol., Jan. 2005, 35(1):33-42. |
| Baldwin et al., “Edible Coatings for Lightly Processed Fruits and Vegetables,” HortScience, Feb. 1995, 30(1):35-3E. |
| Dao et al., “Control of Food Spoilage Fungi by Ethanol,” Food Control, Mar. 2011, 22(3-4):360-368. |
| kumitasu.com [online], “About fruit wax and chenpi,” Jul. 26, 2015, retrieved on Aug. 16, 2021, retrieved from URL <https://web.archive.org/web/20160409110129/https://www.kumitasu.com/contents/hyoji/806>, 5 pages (with machine translation). |
| postharvest.ucdavis.edu [online], “Fact Sheets,” available on or before Aug. 9, 2016, via Internet Archive: Wayback Machine URL <https://web.archive.org/web/20160809075048/http://postharvest.ucdavis.edu/Commodity_Resources/Fact_Sheets/>, retrieved on Aug. 16, 2021, URL <http://postharvest.ucdavis.edu/Commodity_Resources/Fact_Sheets/>, 3 pages. |
| Quiros-Sauceda et al., “Edible coatings as encapsulating matrices for bioactive compounds: a review,” Journal of Food Science and Technology, Jan. 2014, 51(9), pp. 1674-1685, 12 pages. |
| United States Environmental Protection Agency, “Containers and Packaging: Product-Specific Data,” Nov. 6, 2019, last updated Jan. 28, 2021, retrieved on Oct. 6, 2021, retrieved from URL <https://www.epa.gov/facts-and-figures-about-materials-waste-and-recycling/containers-and-packaging-product-specific-data>, 12 pages. |
| Watkins, “The Use of 1-Methylcyclopropene (1-MCP) on Fruits and Vegetables,” Biotech. Adv., Jul.-Aug. 2006, 24(4):389-409. |
| Extended European Search Report in European Patent Appln. No. EP 19857630.8, dated May 20, 2022, 9 pages. |
| International Search Report and Written Opinion in International Appln No. PCT/US2021/057448, dated Feb. 18, 2022, 17 pages. |
| Number | Date | Country | |
|---|---|---|---|
| 20210282432 A1 | Sep 2021 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62985305 | Mar 2020 | US |