Patent Grant
7635755
The present invention relates generally to methods for preparation of concentrated aqueous silk fibroin solutions and to the use of these solutions in the production of silk fibroin materials such as, fibers, films, sponge-like porous foams, 3-dimensional scaffolds, and hydrogels. In particular, an all-aqueous means for preparation of silk fibroin solutions is described.
Silk is a well described natural fiber produced by the silkworm, Bombyx mori, which has been used traditionally in the form of threads in textiles for thousands of years. This silk contains a fibrous protein termed fibroin (both heavy and light chains) that form the thread core, and glue-like proteins termed sericin that surround the fibroin fibers to cement them together. The fibroin is a highly insoluble protein containing up to 90% of the amino acids glycine, alanine and serine leading to β-pleated sheet formation in the fibers (Asakura, et al., Encylopedia of Agricultural Science, Arntzen, C. J., Ritter, E. M. Eds.; Academic Press: New York, N.Y., 1994; Vol. 4, pp 1-11).
The unique mechanical properties of reprocessed silk such as fibroin and its biocompatibility make the silk fibers especially attractive for use in biotechnological materials and medical applications. Silk provides an important set of material options for biomaterials and tissue engineering because of the impressive mechanical properties, biocompatibility and biodegradability (Altman, G. H., et al., Biomaterials 2003, 24, 401-416; Cappello, J., et al., J. Control. Release 1998, 53, 105-117; Foo, C. W. P., et al., Adv. Drug Deliver. Rev. 2002, 54, 1131-1143; Dinerman, A. A., et al., J. Control. Release 2002, 82, 277-287; Megeed, Z., et al., Adv. Drug Deliver. Rev. 2002, 54, 1075-1091; Petrini, P., et al., J. Mater. Sci-Mater. M. 2001, 12, 849-853; Altman, G. H., et al., Biomaterials 2002, 23, 4131-4141; Panilaitis, B., et al., Biomaterials 2003, 24, 3079-3085). For example, 3-dimensional porous silk scaffolds have been described for use in tissue engineering (Meinel et al., Ann Biomed Eng. 2004 Jan; 32(1):112-22; Nazarov, R., et al., Biomacromolecules in press). Further, regenerated silk fibroin films have been explored as oxygen- and drug-permeable membranes, supports for enzyme immobilization, and substrates for cell culture (Minoura, N., et al., Polymer 1990, 31, 265-269; Chen, J., et al., Minoura, N., Tanioka, A. 1994, 35, 2853-2856; Tsukada, M., et al., Polym. Sci. Part B Polym. Physics 1994, 32, 961-968). In addition, silk hydrogels have found numerous applications in tissue engineering, as well as in drug delivery (Megeed et al., Pharm Res. 2002 July; 19(7):954-9; Dinerman et al., J Control Release. 2002 Aug. 21;82(2-3):277-87).
However, in order to prepare silk based materials described above, chemical agents or organic solvents, such as hexafluoroisopropanol (HFIP), have been used for cross-linking or for the processing (Li, M., et al., J. Appl. Poly. Sci. 2001, 79, 2192-2199; Min, S., et al., Sen'i Gakkaishi 1997, 54, 85-92; Nazarov, R., et al., Biomacromolecules in press). For example, HFIP is used to optimize solubility of the silk and methanol is used to induce an amorphous to β-sheet conformation transition in the fibroin, in order to generate water-stable silk structures.
The use of organic solvents in the preparation of silk fibroin materials represents a significant drawback, as organic solvents pose biocompatibility problems when the processed materials are exposed to cells in vitro or in vivo. Organic solvents can also change the properties of fibroin material. For example, the immersion of silk fibroin films in organic solvents such as methanol causes dehydration of the hydrated or swollen structure, leading to crystallization and thus, loss of solubility in water. Further, with respect to tissue engineering scaffolds, the use of organic solvents can render the silk material to be less degradable. Thus, there is a need in the art for the development of silk based materials that can be formed in the absence of chemical cross-linking and/or organic solvents.
The present invention provides for concentrated aqueous silk fibroin solutions and an all-aqueous mode for preparation of concentrated aqueous fibroin solutions that avoids the use of organic solvents or harsh chemicals. The invention further provides for the use of these solutions in production of materials, e.g., fibers, films, foams, meshes, scaffolds and hydrogels.
In one embodiment, an aqueous silk fibroin solution is provided that has a fibroin concentration of at least 10 wt % and wherein said solution is free of organic solvents. Also provided for are aqueous silk fibroin solutions wherein the fibroin concentration is at least 15 wt %, at least 20 wt %, at least 25 wt %, or at least 30 wt %. If desired, the solution can be combined with a biocompatible polymer before processing.
The fibroin of the aqueous silk fibroin solution can be obtained from a solution containing a dissolved silkworm silk, e.g. from Bombyx mori, a dissolved spider silk, e.g. from Nephila clavipes, or from a solution containing a genetically engineered silk.
In one embodiment of the invention, the aqueous silk fibroin solutions described herein, further comprise a therapeutic agent. Therapeutic agents include, for example, proteins, peptides, nucleic acids and small molecule drugs.
In another embodiment, a method for the production of a concentrated aqueous fibroin solution is provided. The method comprises preparing an aqueous silk fibroin solution and dialyzing the solution against a hygroscopic polymer for a sufficient time to result in an aqueous fibroin solution of at least 10 wt %.
Hygroscopic polymers useful in the method of the present invention, include, for example, polyethylene glycol, amylase, or sericin. Preferably, the hygroscopic polymer is a polyethylene glycol (PEG) with a molecular weight of 8,000 to 10,000 g/mol. Most preferably, the PEG has a concentration of 25-50%.
In one embodiment, a method for the production of a fiber is provided. The method comprises processing the concentrated aqueous silk fibroin solution to form a fiber. Processing includes, for example electrospinning or wet spinning. Alternatively, a fiber can be pulled directly from the solution. If desired, the fiber can be treated with methanol, preferably by immersion, after processing. The fiber is then preferably washed with water.
A composition comprising a fiber that is produced by the method of the present invention and a therapeutic agent is also provided.
In another embodiment, a method of producing a silk foam is provided. The method comprises processing the concentrated aqueous silk solution of the invention to produce a foam. Processing methods include, for example, salt leaching, gas foaming, micropatterning, or by contacting solution with a salt particle. The salt is preferably monovalent, e.g. NaCl, KCl, KFl, or NaBr. Alternatively, divalent salts, e.g. CaCl2, MgSO4, or MgCl2, may also be used.
A composition comprising a foam produced by the method of the present invention and a therapeutic agent is also provided.
In another embodiment, a method of producing a film is provided. The method casting the concentrated aqueous salt solution to form a film. In certain embodiments, it is useful to contact the film with water vapor. In addition, the film can be stretched mono-axially and bi-axially.
A composition comprising a film that is produced by the method of the present invention and a therapeutic agent is also provided.
In another embodiment, a method of producing a silk hydrogel is provided. The method comprises inducing a sol-gel transition in the concentrated aqueous silk solution of the invention.
The sol-gel transition can be induced by an increase in the silk fibroin concentration, an increase in temperature, a decrease in pH, an increase in the concentration of salt (e.g. KCl, NaCl, or CaCl2.), or by addition of a polymer (e.g. polyethylene oxide (PEO).
A composition comprising a silk hydrogel that is produced by the method of the present invention and a therapeutic agent is also provided.
The accompanying drawings, which are incorporated in and constitute a part of this specification, illustrate embodiments of the invention and, together with the description, serve to explain the objects, advantages, and principles of the invention.
a and 3b show (
a and 4b shown the mass of scaffolds remaining over time when prepared from (
a and 5b illustrate one embodiment of the present invention for silk film preparation including (
a, 8b, and 8c show the gelation time of silk fibroin aqueous solutions with different Ca2+ (pH 5.6˜5.9) and K+(pH 6.2˜6.4) concentrations at (
a and 11b show the X-ray profiles of (
a, 12b, and 12c show the compressive strength (
Methods for preparation of concentrated aqueous silk fibroin solutions in the absence of organic solvents or harsh chemicals are described. The process comprises forming a solution comprising silk fibroin. Preferably, the solution is in an aqueous salt, such as lithium bromide. The solution is then dialyzed against a hygroscopic polymer for a sufficient time to result in an aqueous silk fibroin solution of between 10-30 wt % or greater. A preferred hyproscopic polymer is polyethylene glycol (PEG).
We have discovered that increasing the viscosity of the aqueous silk fibroin solution to at least 10 wt % allows for the formation of fibers by electrospinning, for the formation of porous 3-dimensional tissue engineering scaffolds, and for other applications, e.g., formation of foams and films, while avoiding the use of organic solvents that can pose problems when the processed materials are exposed to cells in vitro or in vivo. Dialysis of the solution against a hygroscopic polymer is also sufficient to control water content in the formation of silk hydrogels.
As used herein, the term “fibroin” includes silkworm fibroin and insect or spider silk protein (Lucas et al., Adv. Protein Chem 13: 107-242 (1958)). Preferably, fibroin is obtained from a solution containing a dissolved silkworm silk or spider silk. The silkworm silk protein is obtained, for example, from Bombyx mori, and the spider silk is obtained from Nephila clavipes. In the alternative, the silk proteins suitable for use in the present invention can be obtained from a solution containing a genetically engineered silk, such as from bacteria, yeast, mammalian cells, transgenic animals or transgenic plants. See, for example, WO 97/08315 and U.S. Pat. No. 5,245,012.
The silk fibroin solution to be concentrated can be prepared by any conventional method known to one skilled in the art. For example, B. mori cocoons are boiled for about 30 minutes in an aqueous solution. Preferably, the aqueous solution is about 0.02M Na2CO3. The cocoons are rinsed, for example, with water to extract the sericin proteins and the extracted silk is dissolved in an aqueous salt solution. Salts useful for this purpose include, lithium bromide, lithium thiocyanate, calcium nitrate or other chemicals capable of solubilizing silk. Preferably, the extracted silk is dissolved in about 9-12 M LiBr solution. The salt is consequently removed using, for example, dialysis.
The solution is then concentrated using, for example, dialysis against a hygroscopic polymer, for example, PEG, a polyethylene oxide, amylose or sericin.
Preferably, the PEG is of a molecular weight of 8,000-10,000 g/mol and has a concentration of 25-50%. A slide-a-lyzer dialysis cassette (Pierce, MW CO 3500) is preferably used. However, any dialysis system may be used. The dialysis is for a time period sufficient to result in a final concentration of aqueous silk solution between 10-30%. In most cases dialysis for 2-12 hours is sufficient.
The concentrated aqueous solution of the present invention can be processed into hydrogels, foams, films, threads, fibers, meshes, and scaffolds using processes known in the art. See, e.g., Altman, et al., Biomaterials 24:401, 2003.
Biocompatible polymers can be added to the silk solution to generate composite matrices in the process of the present invention.
Biocompatible polymers useful in the present invention include, for example, polyethylene oxide (PEO) (U.S. Pat. No. 6,302,848), polyethylene glycol (PEG) (U.S. Pat. No. 6,395,734), collagen (U.S. Pat. No. 6,127,143), fibronectin (U.S. Pat. No. 5,263,992), keratin (U.S. Pat. No. 6,379,690), polyaspartic acid (U.S. Pat. No. 5,015,476), polylysine (U.S. Pat. No. 4,806,355), alginate (U.S. Pat. No. 6,372,244), chitosan (U.S. Pat. No. 6,310,188), chitin (U.S. Pat. No. 5,093,489), hyaluronic acid (U.S. Pat. No. 387,413), pectin (U.S. Pat. No. 6,325,810), polycaprolactone (U.S. Pat. No. 6,337,198), polylactic acid (U.S. Pat. No. 6,267,776), polyglycolic acid (U.S. Pat. No. 5,576,881), polyhydroxyalkanoates (U.S. Pat. No. 6,245,537), dextrans (U.S. Pat. No. 5,902,800), and polyanhydrides (U.S. Pat. No. 5,270,419). Two or more biocompatible polymers can be used.
Silk films can be produced by preparing the concentrated aqueous silk fibroin solution and casting the solution. In one embodiment, the film is contacted with water or water vapor, in the absence of alcohol. The film can then be drawn or stretched mono-axially or biaxially. See, for example,
In one embodiment, the film comprises from about 50 to about 99.99 part by volume aqueous silk protein solution and from about 0.01 to about 50 part by volume biocompatible polymer e.g., polyethylene oxide (PEO). Preferably, the resulting silk blend film is from about 60 to about 240 μm thick, however, thicker samples can easily be formed by using larger volumes or by depositing multiple layers.
Foams may be made from methods known in the art, including, for example, freeze—drying and gas foaming in which water is the solvent or nitrogen or other gas is the blowing agent, respectively. Alternately the foam is made by contacting the silk fibroin solution with granular salt. The pore size of foams can be controlled, for example by adjusting the concentration of silk fibroin and the particle size of a granular salt (for example, the preferred diameter of the salt particle is between about 50 microns and about 1000 microns). The salts can be monovalent or divalent. Preferred salts are monovalent, such as NaCl and KCl. Divalent salts, such as CaCl2 can also be used. Contacting the concentrated silk fibroin solution with salt is sufficient to induce a conformational change of the amorphous silk to a β-sheet structure that is insoluble in the solution. After formation of the foam, the excess salt is then extracted, for example, by immersing in water. The resultant porous foam can then be dried and the foam can be used, for example, as a cell scaffold in biomedical application. See,
In one embodiment, the foam is a micropatterned foam. Micropatterned foams can be prepared using, for example, the method set forth in U.S. Pat. No. 6,423,252, the disclosure of which is incorporated herein by reference. The method comprises contacting the concentrated silk solution of the present invention with a surface of a mold, the mold comprising on at least one surface thereof a three-dimensional negative configuration of a predetermined micropattern to be disposed on and integral with at least one surface of the foam, lyophilizing the solution while in contact with the micropatterned surface of the mold, thereby providing a lyophilized, micropatterned foam, and removing the lyophilized, micropatterned foam from the mold. Foams prepared according this method comprise a predetermined and designed micropattern on at least one surface, which pattern is effective to facilitate tissue repair, ingrowth or regeneration.
Fibers may be produced using, for example, wet spinning or electrospinning. Alternatively, as the concentrated solution has a gel-like consistency, a fiber can be pulled directly from the solution.
Electrospinning can be performed by any means known in the art (see, for example, U.S. Pat. No. 6,110,590). Preferably, a steel capillary tube with a 1.0 mm internal diameter tip is mounted on an adjustable, electrically insulated stand. Preferably, the capillary tube is maintained at a high electric potential and mounted in the parallel plate geometry. The capillary tube is preferably connected to a syringe filled with silk solution. Preferably, a constant volume flow rate is maintained using a syringe pump, set to keep the solution at the tip of the tube without dripping. The electric potential, solution flow rate, and the distance between the capillary tip and the collection screen are adjusted so that a stable jet is obtained. Dry or wet fibers are collected by varying the distance between the capillary tip and the collection screen.
A collection screen suitable for collecting silk fibers can be a wire mesh, a polymeric mesh, or a water bath. Alternatively and preferably, the collection screen is an aluminum foil. The aluminum foil can be coated with Teflon fluid to make peeling off the silk fibers easier. One skilled in the art will be able to readily select other means of collecting the fiber solution as it travels through the electric field. As is described in more detail in the Examples section below, the electric potential difference between the capillary tip and the aluminum foil counter electrode is, preferably, gradually increased to about 12 kV, however, one skilled in the art should be able to adjust the electric potential to achieve suitable jet stream.
The present invention additionally provides a non-woven network of fibers comprising a fiber of the present invention. The fiber may also be formed into yarns and fabrics including for example, woven or weaved fabrics.
The fibroin silk solution of the present invention may also be coated onto various shaped articles including biomedical devices (e.g. stents), and silk or other fibers, including fragments of such fibers.
Silk hydrogels can be prepared by methods known in the art, and as exemplified herein. The sol-gel transition of the concentrated silk fibroin solution can be modified by changes in silk fibroin concentration, temperature, salt concentrations (e.g. CaCl2, NaCl, and KCl), pH, hydrophilic polymers, and the like. Before the sol-gel transition, the concentrated aqueous silk solution can be placed in a mold or form. The resulting hydrogel can then be cut into any shape, using, for example a laser.
The materials produced using the present invention, e.g., hydrogels, fibers, films, foams, or meshes, may be used in a variety of medical applications such as a drug (e.g, small molecule, protein, or nucleic acid) delivery device, including controlled release systems, wound closure systems, including vascular wound repair devices, hemostatic dressings, patches and glues, sutures, and in tissue engineering applications, such as, for example, scaffolds for tissue regeneration, ligament prosthetic devices and in products for long-term or bio-degradable implantation into the human body. Films may also be used for a wide range of materials science and engineering needs, such as controlled drug release systems, coatings, composites or as stand alone materials.
Additionally, these biomaterials can be used for organ repair replacement or regeneration strategies that may benefit from these unique scaffolds, including but are not limited to, spine disc, cranial tissue, dura, nerve tissue, liver, pancreas, kidney, bladder, spleen, cardiac muscle, skeletal muscle, tendons, ligaments and breast tissues.
In another embodiment of the present invention, silk biomaterials can contain therapeutic agents. To form these materials, the silk solution is mixed with a therapeutic agent prior to forming the material or loaded into the material after it is formed. The variety of different therapeutic agents that can be used in conjunction with the biomaterials of the present invention is vast and includes small molecules, proteins, peptides and nucleic acids. In general, therapeutic agents which may be administered via the invention include, without limitation: antiinfectives such as antibiotics and antiviral agents; chemotherapeutic agents (i.e. anticancer agents); anti-rejection agents; analgesics and analgesic combinations; anti-inflammatory agents; hormones such as steroids; growth factors (bone morphogenic proteins (i.e. BMP's 1-7), bone morphogenic-like proteins (i.e. GFD-5, GFD-7 and GFD-8), epidermal growth factor (EGF), fibroblast growth factor (i.e. FGF 1-9), platelet derived growth factor (PDGF), insulin like growth factor (IGF-I and IGF-II), transforming growth factors (i.e. TGF-β-III), vascular endothelial growth factor (VEGF)); anti-angiogenic proteins such as endostatin, and other naturally derived or genetically engineered proteins, polysaccharides, glycoproteins, or lipoproteins. Growth factors are described in The Cellular and Molecular Basis of Bone Formation and Repair by Vicki Rosen and R. Scott Thies, published by R. G. Landes Company, hereby incorporated herein by reference. Additionally, the silk biomaterials of the present invention can be used to deliver any type of molecular compound, such as, pharmacological materials, vitamins, sedatives, steroids, hypnotics, antibiotics, chemotherapeutic agents, prostaglandins, and radiopharmaceuticals. The delivery system of the present invention is suitable for delivery the above materials and others including but not limited to proteins, peptides, nucleotides, carbohydrates, simple sugars, cells, genes, anti-thrombotics, anti-metabolics, growth factor inhibitor, growth promoters, anticoagulants, antimitotics, fibrinolytics, anti-inflammatory steroids, and monoclonal antibodies.
Silk biomaterials containing bioactive materials may be formulated by mixing one or more therapeutic agents with the polymer used to make the material. Alternatively, a therapeutic agent could be coated on to the material preferably with a pharmaceutically acceptable carrier. Any pharmaceutical carrier can be used that does not dissolve the silk material. The therapeutic agents, may be present as a liquid, a finely divided solid, or any other appropriate physical form.
The biomaterials described herein can be further modified after fabrication. For example, the scaffolds can be coated with additives, such as bioactive substances that function as receptors or chemoattractors for a desired population of cells. The coating can be applied through absorption or chemical bonding.
Additives suitable for use with the present invention includes biologically or pharmaceutically active compounds. Examples of biologically active compounds include, but are not limited to: cell attachment mediators, such as collagen, elastin, fibronectin, vitronectin, laminin, proteoglycans, or peptides containing known integrin binding domains e.g. “RGD” integrin binding sequence, or variations thereof, that are known to affect cellular attachment (Schaffner P & Dard 2003 Cell Mol Life Sci. January;60(1):119-32; Hersel U. et al. 2003 Biomaterials. November;24(24):4385-415); biologically active ligands; and substances that enhance or exclude particular varieties of cellular or tissue ingrowth. For example, the steps of cellular repopulation of a 3-dimensional scaffold matrix preferably are conducted in the presence of growth factors effective to promote proliferation of the cultured cells employed to repopulate the matrix. Agents that promote proliferation will be dependent on the cell type employed. For example, when fibroblast cells are employed, a growth factor for use herein may be fibroblast growth factor (FGF), most preferably basic fibroblast growth factor (bFGF) (Human Recombinant bFGF, UPSTATE Biotechnology, Inc.). Other examples of additive agents that enhance proliferation or differentiation include, but are not limited to, osteoinductive substances, such as bone morphogenic proteins (BMP); cytokines, growth factors such as epidermal growth factor (EGF), platelet-derived growth factor (PDGF), insulin-like growth factor (IGF-I and II) TGF-β, and the like. As used herein, the term additive also encompasses antibodies, DNA, RNA, modified RNA/protein composites, glycogens or other sugars, and alcohols.
The biomaterials can be shaped into articles for tissue engineering and tissue guided regeneration applications, including reconstructive surgery. The structure of the scaffold allows generous cellular ingrowth, eliminating the need for cellular preseeding. The scaffolds may also be molded to form external scaffolding for the support of in vitro culturing of cells for the creation of external support organs.
The scaffold functions to mimic the extracellular matrices (ECM) of the body. The scaffold serves as both a physical support and an adhesive substrate for isolated cells during in vitro culture and subsequent implantation. As the transplanted cell populations grow and the cells function normally, they begin to secrete their own ECM support.
In the reconstruction of structural tissues like cartilage and bone, tissue shape is integral to function, requiring the molding of the scaffold into articles of varying thickness and shape. Any crevices, apertures or refinements desired in the three-dimensional structure can be created by removing portions of the matrix with scissors, a scalpel, a laser beam or any other cutting instrument. Scaffold applications include the regeneration of tissues such as nervous, musculoskeletal, cartilaginous, tendenous, hepatic, pancreatic, ocular, integumenary, arteriovenous, urinary or any other tissue forming solid or hollow organs.
The scaffold may also be used in transplantation as a matrix for dissociated cells, e.g., chondrocytes or hepatocytes, to create a three-dimensional tissue or organ. Tissues or organs can be produced by methods of the present invention for any species.
A number of different cell types or combinations thereof may be employed in the present invention, depending upon the intended function of the tissue engineered construct being produced. These cell types include, but are not limited to: smooth muscle cells, skeletal muscle cells, cardiac muscle cells, epithelial cells, endothelial cells, urothelial cells, fibroblasts, myoblasts, chondrocytes, chondroblasts, osteoblasts, osteoclasts, keratinocytes, hepatocytes, bile duct cells, pancreatic islet cells, thyroid, parathyroid, adrenal, hypothalamic, pituitary, ovarian, testicular, salivary gland cells, adipocytes, and precursor cells. For example, smooth muscle cells and endothelial cells may be employed for muscular, tubular constructs, e.g., constructs intended as vascular, esophageal, intestinal, rectal, or ureteral constructs; chondrocytes may be employed in cartilaginous constructs; cardiac muscle cells may be employed in heart constructs; hepatocytes and bile duct cells may be employed in liver constructs; epithelial, endothelial, fibroblast, and nerve cells may be employed in constructs intended to function as replacements or enhancements for any of the wide variety of tissue types that contain these cells. In general, any cells may be employed that are found in the natural tissue to which the construct is intended to correspond. In addition, progenitor cells, such as myoblasts or stem cells, may be employed to produce their corresponding differentiated cell types. In some instances it may be preferred to use neonatal cells or tumor cells.
Cells can be obtained from donors (allogenic) or from recipients (autologous). Cells can also be of established cell culture lines, or even cells that have undergone genetic engineering. Pieces of tissue can also be used, which may provide a number of different cell types in the same structure.
Appropriate growth conditions for mammalian cells are well known in the art (Freshney, R. I. (2000) Culture of Animal Cells, a Manual of Basic Technique. Hoboken N.J., John Wiley & Sons; Lanza et al. Principles of Tissue Engineering, Academic Press; 2nd edition May 15, 2000; and Lanza & Atala, Methods of Tissue Engineering Academic Press; 1st edition October 2001). Cell culture media generally include essential nutrients and, optionally, additional elements such as growth factors, salts, minerals, vitamins, etc., that may be selected according to the cell type(s) being cultured. Particular ingredients may be selected to enhance cell growth, differentiation, secretion of specific proteins, etc. In general, standard growth media include Dulbecco's Modified Eagle Medium, low glucose (DMEM), with 110 mg/L pyruvate and glutamine, supplemented with 10-20% fetal bovine serum (FBS) or calf serum and 100 U/mI penicillin are appropriate as are various other standard media well known to those in the art. Growth conditions will vary dependent on the type of mammalian cells in use and tissue desired.
In one embodiment, methods are provided for producing bone or cartilage tissue in vitro comprising culturing multipotent cells on a porous silk fibroin scaffold under conditions appropriate for inducing bone or cartilage formation. Suitable conditions for the generation of bone and cartilage are well known to those skilled in the art. For example, conditions for the growth of cartilage tissue often comprise nonessential amino acids, ascorbic acid-2-phosphate, dexamethasone, insulin, and TGF-β1. In one preferred embodiment, the nonessential amino acids are present at a concentration of 0.1 mM, ascorbic acid-2-phosphate is present at a concentration of 50 ug/ml, dexamethasone is present at a concentration of 10 nM, insulin is present at a concentration of 5 ug/ml and TGF-β1 is present at a concentration of 5 ng/ml. Suitable conditions for the growth of bone often include ascorbic acid-2-phosphate, dexamethasone, β-glycerolphoasphate and BMP-2. In a preferred embodiment, ascorbic acid-2-phosphate is present at a concentration of 50 ug/ml, dexamethasone is present at a concentration of 10 nM, β-glycerolphoasphate is present at a concentration of 7 mM and BMP-2 is present at a concentration of 1 ug/ml.
In general, the length of the growth period will depend on the particular tissue engineered construct being produced. The growth period can be continued until the construct has attained desired properties, e.g., until the construct has reached a particular thickness, size, strength, composition of proteinaceous components, and/or a particular cell density. Methods for assessing these parameters are known to those skilled in the art.
Following a first growth period the construct can be seeded with a second population of cells, which may comprise cells of the same type as used in the first seeding or cells of a different type. The construct can then be maintained for a second growth period which may be different in length from the first growth period and may employ different growth conditions. Multiple rounds of cell seeding with intervening growth periods may be employed.
In one preferred embodiment, tissues and organs are generated for humans. In other embodiments, tissues and organs are generated for animals such as, dogs, cats, horses, monkeys, or any other mammal.
The cells are obtained from any suitable donor, either human or animal, or from the subject into which they are to be implanted. As used herein, the term “host” or “subject” includes mammalian species, including, but not limited to, humans, monkeys, dogs, cows, horses, pigs, sheep, goats, cats, mice, rabbits, rats.
The cells that are used for methods of the present invention should be derived from a source that is compatible with the intended recipient. The cells are dissociated using standard techniques and seeded onto and into the scaffold. In vitro culturing optionally may be performed prior to implantation. Alternatively, the scaffold is implanted into the subject, allowed to vascularize, then cells are injected into the scaffold. Methods and reagents for culturing cells in vitro and implantation of a tissue scaffold are known to those skilled in the art.
Cells can be seeded within the matrix either pre- or post matrix formation, depending on the method of matrix formation. Uniform seeding is preferable. In theory, the number of cells seeded does not limit the final tissue produced, however optimal seeding may increase the rate of generation. The number of seeded cells can be optimized using dynamic seeding (Vunjak-Novakovic et al. Biotechnology Progress 1998; Radisic et al. Biotechnoloy and Bioengineering 2003).
It is another aspect of the invention that the 3-dimensional porous silk scaffold, described herein, can itself be implanted in vivo and serve as tissue substitute (e.g. to substitute for bone or cartilage). Such implants, would require no seeding of cells, but contain an addition e.g., RGD, that attracts cells.
In one embodiment, silk matrix scaffolds are seeded with multipotent cells in the presence of media that induces either bone or cartilage formation. Suitable media for the production of cartilage and bone are well known to those skilled in the art.
As used herein, “multipotent” cells have the ability to differentiate into more than one cell type in response to distinct differentiation signals. Examples of multipotent cells include, but are not limited to, bone marrow stromal cells (BMSC) and adult or embryonic stem cells. In a preferred embodiment BMSCs are used. BMSCs are multipotential cells of the bone marrow which can proliferate in an undifferentiated state and with the appropriate extrinsic signals, differentiate into cells of mesenchymal lineage, such as cartilage, bone, or fat (Friedenstein, A. J. 1976. Int Rev Cytol 47:327-359; Friedenstein et al. 1987. Cell Tissue Kinet 20:263-272; Caplan, A. I. 1994. Clin Plast Surg 21:429-435; Mackay et al. 1998. Tissue Eng 4:415-428; Herzog et al. Blood. 2003 Nov. 15;102(10):3483-93. Epub 2003 Jul. 31).
The formation of cartilaginous tissue or bone can be monitored by assays well known to those in the art including, but not limited to, histology, immunohistochemistry, and confocal or scanning electron microscopy (Holy et al., J. Biomed. Mater. Res (2003) 65A:447-453).
Using silk based scaffolds, organized tissue with a predetermined form and structure can be produced either in vitro or in vivo. For example, tissue that is produced ex vivo is functional from the start and can be used as an in vivo implant. Alternatively, the silk based structure can be seeded with cells capable of forming either bone or cartilage and then implanted as to promote growth in vivo. Thus, the scaffolds can be designed to form tissue with a “customized fit” that is specifically designed for implantation in a particular patient. For example, cartilaginous tissue or bone tissue produced by methods of the present invention can be used to replace large cartilage or bone defects found in musculoskeletal disorders and degenerative diseases such as osteoarthritis or rheumatism. Engineered bone and cartilage are also suitable for spine and joint replacements such as, elbow, knee, hip or finger joints or can be used in osteochondral implants.
All biomaterials of the present intention may be sterilized using conventional sterilization process such as radiation based sterilization (i.e. gamma-ray), chemical based sterilization (ethylene oxide), autoclaving, or other appropriate procedures. Preferably the sterilization process will be with ethylene oxide at a temperature between 52-55° C. for a time of 8 hours or less. After sterilization the biomaterials may be packaged in an appropriate sterilize moisture resistant package for shipment and use in hospitals and other health care facilities.
Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art. Although methods and materials similar or equivalent to those described herein can be used in the practice or testing of the invention, the preferred methods and materials are described below. All publications, patent applications, patents and other references mentioned herein are incorporated by reference. In addition, the materials, methods and examples are illustrative only and not intended to be limiting. In case of conflict, the present specification, including definitions, controls.
The invention will be further characterized by the following examples which are intended to be exemplary of the invention.
Methods
Preparation of a Regenerated B. mori Silk Fibroin Solution
B. mori silk fibroin was prepared as follows as a modification of our earlier procedure (Sofia, et al., Journal of Biomedical Materials Research 2001, 54, 139-148). Cocoons were boiled for 30 min in an aqueous solution of 0.02 M Na2CO3, then rinsed thoroughly with water to extract the glue-like sericin proteins. The extracted silk was then dissolved in 9.3 M LiBr solution at room temperature yielding a 20% (w/v) solution. This solution was dialyzed in water using a Slide-a-Lyzer dialysis cassette (Pierce, MWCO 2000) for 48 hours. The final concentration of aqueous silk solution was 8.0 wt %, which was determined by weighing the remaining solid after drying.
This solution was concentrated further by exposure to an aqueous polyethylene glycol (PEG) (MW 8,000 to 10,000) solution (25-50 wt %) on the outside of a Slide-a-Lyzer dialysis cassette (Pierce, MWCO 3500) for 2 to 12 hrs by osmotic pressure (
Electrospinning
In order to increase the viscosity of aqueous silk solution above 8 wt % for spinning, the solution was concentrated using the PEG solution method as described above. This was required since the viscosity and surface tension of the pure silk solution (8 wt %) was not high enough to maintain a stable drop at the end of the capillary tip. The increase of silk solutions generated a viscosity and surface tension suitable for electrospinning. With the new more concentrated pure silk solutions (10-30%), direct spinning is now feasible. The distance between the tip and the collector was 10-15 cm and flow rate of the fluid was 0.01 to 0.05 ml/min. As the potential difference between the capillary tip and the aluminum foil counter electrode was gradually increased 30 kV (E=2-3 kV/cm), the drop at the end of the capillary tip elongated from a hemispherical shape into a cone shape. The morphology and diameters of the electrospun fibers were examined using SEM. Silk/PEO blend solution produced microsize fibers with diameters 1.5 μm to 25 μm. The morphology of fiber surface and fracture surface in liquid nitrogen was well matched with native silk fiber.
Porous three-dimensional scaffolds were prepared from silk fibroin aqueous solutions by salt-leaching. By adjusting the concentration of silk fibroin and the particle size of granular NaCl, the morphological and functional properties of the scaffolds could be controlled. The scaffolds had highly homogeneous and interconnected pores and showed pore sizes ranging from 470 to 940 um depending on the mode of preparation. The scaffolds had porosities >90%. The compressive strength and modulus of scaffolds was up to 320±10 KPa and 3330±500 KPa, respectively. The scaffolds were fully degraded by protease during 21 days. These new silk-based 3-D matrices provide useful properties as biomaterial matrices for tissue engineering due to the all-aqueous mode of preparation, control of pore size, connectivity of pores, degradability and useful mechanical features.
Methods
Preparation of Silk Fibroin Aqueous Solution
Cocoons of B. mori were boiled for 20 min in an aqueous solution of 0.02 M Na2CO3, and then rinsed thoroughly with distilled water to extract the glue-like sericin proteins and wax. The extracted silk fibroin was then dissolved in 9.3 M LiBr solution at 60° C. for 4 hrs, yielding a 20 w/v % solution. This solution was dialyzed in distilled water using a Slide-a-Lyzer dialysis cassette (MWCO 3500, Pierce) for 2 days. The final concentration of silk fibroin aqueous solution was ca. 8 w/v %, which was determined by weighing the remaining solid after drying. To prepare concentrated silk fibroin solution, 10 ml of 8 w/v % silk fibroin solution was dialyzed against 1 liter of 25 wt % polyethylene glycol (PEG, 10,000 g/mol) solution at room temperature by using Slide-a-Lyzer dialysis cassettes (MWCO 3500). After the required time, the concentrated silk fibroin solution was slowly collected by syringe to avoid excessive shearing and the concentration was determined. Silk fibroin aqueous solutions with concentration less than 8 wt % were prepared by diluting with distilled water. All solutions were stored at 7° C. before use to avoid premature precipitation. Silk fibroin films prepared from 8 w/v % solutions were evaluated to verify the removal of Li+ ion by XPS; no residual Li+ ion was detected.
Preparation of Silk Fibroin Scaffolds
Four grams of granular NaCl (particle size; 300˜1180 um) were added to 2 ml of silk fibroin aqueous solution (4˜10 wt %) in disk-shaped Teflon containers (
X-Ray Diffraction
X-ray diffraction of freeze-dried samples of the scaffold were obtained with Ni-filterd Cu-Kα radiation (λ=0.15418 nm) from a Rigaku RU-200BH rotating-anode X-ray generator operating at 40 kV and 40 mA. X-ray diffraction patterns were recorded with a point collimated beam and a imaging plate (Fuji Film BAS-IP SR 127) in an evacuated camera. The camera length was calibrated with NaF (d=0.23166 nm).
FTIR Spectroscopy
Approximately 1 mg of freeze-dried sample was pressed into a pellet with 200 mg of potassium bromide and Fourier transform infrared (FTIR) spectrum was recorded with an accumulation of 64 scans and a resolution of 4 cm-1 by Nicolet Magna 860.
Scanning Electron Microscopy (SEM)
Silk scaffolds were cut into sections in distilled water using a razor blade and then freeze-dried. Samples were sputter coated with gold. The morphology of scaffolds was observed with a LEO Gemini 982 Field Emission Gun SEM. Pore size was obtained using ImageJ software developed at the US National Institutes of Health.
Porosity
The density and porosity of the silk scaffolds were measured by liquid displacement (Zhang, R. Y., et al., J. Biomed. Mater. Res. 1999, 44, 446-455). Hexane was used as the displacement liquid as it permeates through silk scaffolds without swelling or shrinking the matrix. The silk scaffold (dry weight, W) was immersed in a known volume (V1) of hexane in a graduated cylinder for 5 min. The total volume of hexane and the hexane-impregnated scaffold was recorded as V2. The hexane-impregnated scaffold was then removed from the cylinder and the residual hexane volume was recorded as V3. The total volume of the scaffold was:
V=(V2−V1)+(V1−V3)=V2−V3.
V2−V1 is the volume of the polymer scaffold and V1−V3 is the volume of hexane within the scaffold. The porosity of the scaffold (ε) was obtained by:
ε(%)=(V1−V3)/(V2−V3)×100
Swelling Properties
Silk fibroin scaffolds were immersed in distilled water at room temperature for 24 hrs. After excess water was removed, the wet weight of the scaffold (Ws) was determined. Samples were then dried in an oven at 65° C. under vacuum overnight and the dry weight of scaffolds (Wd) was determined. The swelling ratio of the scaffold and the water content in the scaffold were calculated as follows:
Swelling ratio=(Ws−Wd)/Wd
Water uptake (%)=[(Ws−Wd)/Ws]×100
Mechanical Properties
Resistance to mechanical compression of the scaffolds (12 mm diameter, 10 mm height, disks) were performed on an Instron 8511 equipped with a 0.1 KN load cell at room temperature. The crosshead speed was 10 mm/min. The compression tests were conducted conventionally as an open-sided/confined method. Four samples were evaluated for each composition. Cylinder-shaped samples measuring 12 mm in diameter and 10 mm in height were used, according to a modification based on the ASTM method F451-95. The compressive stress and strain were graphed and the average compressive strength as well as the compressive modulus and standard deviation determined. The elastic modulus was defined by the slope of the initial linear section of the stress-strain curve. The compressive strength was determined by drawing a line parallel to this, starting at 1% strain. The point at which this line crossed the stress-strain curve was defined as the compressive strength of the foam (Thomson R C et al., Biomaterials 1998, 19;1935-1943).
In Vitro Enzymatic Degradation
The degradation of the silk fibroin scaffolds was evaluated using protease XIV (EC 3.4.24.31, Sigma-Aldrich) with an activity of 5.6 U/mg. Samples (12 mm diameter, 5 mm height) were immersed in 5 ml of phosphate buffer saline (pH 7.4) containing protease (1 U) at 37° C. After the specific time samples were washed with phosphate buffer saline and distilled water, and freeze-dried. The enzyme solution was replaced with newly prepared solution every 24 hrs. For controls, samples were immersed in phosphate buffer saline without enzyme.
Results and Discussion
Preparation of Water-Based Scaffolds
Porous silk fibroin scaffolds were prepared using a salt-leaching method that has been previously used in the preparation of porous scaffolds from other polymers such as collagen and polylactic acid. The pore size and the porosity of the scaffolds were regulated by the addition of granular NaCl with particle sizes of diameter 300 to 180 μm to the silk fibroin aqueous solution. In this process, some of the surface of the NaCl particles dissolved in the silk fibroin aqueous solution, while most of the salt was retained as solid particles because of saturation of the solution. The silk fibroin aqueous solutions formed into hydrogels in the mixture after ˜24 hrs, which resulted in the formation of water-stable porous matrices. Table 1 shows the silk fibroin concentrations and particle sizes of NaCl used in the study. With an increase in silk fibroin concentration, matrices were homogeneously formed through the use of larger particle sizes of the NaCl. When NaCl with particle sizes of 500 to 600 μm were added to 8 wt % silk fibroin solution, the surface of the silk fibroin aqueous solutions rapidly formed a hydrogel.
In concentrated salt solutions, solvating forces are significantly altered from those in dilute electrolyte solutions because salt ions change the structure of the intervening water (Curtis R A et al., Biophys Chem 2002, 98:249-265). The effect of concentrated salt solutions with chloride ion, such as NaCl, KCl, CaCl2 and MgCl2, on silk fibroin was determined at salt concentrations up to 3 M at room temperature. When a drop of silk fibroin solution (8 wt %) was added to concentrated salt solutions of 3 M, silk hydrogels formed immediately in the NaCl and KCl solutions but not in the CaCl2 and MgCl2 solutions. Ions are classified as kosmotropic or chaotropic, based on their size and charge (Grigsby J J et al., Biophys Chem 2001, 91:231-243). Ions with high charge density such as Ca2+ and Mg2+ are highly kosmotropic, and ions with low charge density such as K+ are chaotropic. Na+ is weakly kosmotropic and Cl− is weakly chaotropic. Kosmotropic ions bind adjacent water molecules more strongly than chaotropic ions. In addition, kosmotropic ions strongly interact with oppositely charged residues on the protein surface due to their high charge density. At low salt concentration, the solution contains a sufficient number of water molecules to hydrate both the protein surface and the ions. At higher salt concentrations, more water molecules are needed to hydrate the increasing number of ions. Therefore water molecules are easily removed from the proteins as concentrations of salt solutions increase.
From the primary sequence of the silkworm silk fibroin heavy chain, seven internal hydrophobic blocks and seven much smaller internal hydrophilic blocks, with two large hydrophilic blocks at the chain ends are present (Zhou, C. Z., et al., Nucleic Acids Res. 2000, 28, 2413-2419). The percentage of hydrophobic residues in silk fibroin is 79% (Braun, F. N., et al., Int. J. Biol. Macromol. 2003, 32, 59-65) and the repetitive sequence in these hydrophobic blocks consists of GAGAGS (SEQ ID NO: 4) peptides that dominate the β-sheet structure that forms the crystalline regions in silk fibroin fibers and films (Mita, K., et al., J. Mol. Evol. 1994, 38, 583-592).
Since protein solubility typically decreases as salt concentration rises, interactions between proteins become favored (Curtis, R. A., et al., Biophys. Chem. 2002, 98, 249-265). It is well known that the hydrophobic interactions between non-polar residues increase with addition of salt, leading to the salting-out effect (Robinson, D. R., et al., J. Am. Chem. Soc. 1965, 87, 2470-2479). The behavior of the fibroin in the salt system described may be related to the role of the salt ions in extracting water that would otherwise coat the hydrophobic fibroin domains, promoting chain-chain interactions leading to the new more stable structure. These hydrophobic interactions induce protein folding, resulting in β-sheet formation (Li, G. Y., et al., Biochem. 2001, 268, 6600-6606).
Alginate or glass beads were examined to further clarify the ion effects on hydrogelation of silk fibroin (8 wt %). While gelation time of silk fibroin with glass beads showed a similar result as that observed over 30 days with silk fibroin in a previous study (Kim U J et al., Biomacromolecules, in press), the gelation time of the silk fibroin solution with alginate beads was ˜2 times faster due, presumably due to the removal of water molecules from the proteins associated with the swelling of the alginate beads. Compared with the gelation time (24 hrs) of silk fibroin in saturated NaCl solution, salt ions strongly induced protein-protein interactions.
Structural Analysis
Structural changes in the silk fibroin were determined by X-ray diffraction and FTIR (
Morphology
SEM images of freeze-dried scaffolds prepared from various silk fibroin concentrations and various sized particles of NaCl showed highly interconnected porous structures and the pore distribution was homogeneous in the whole scaffolds except for a thin layer formed on the top surface of the scaffolds, the air-water interface. The scaffolds showed rough pore surfaces highly interconnected by a number of smaller pores. Globular-like structures, 1˜3 μm in diameter, were observed on the surfaces of the pores. With an increase in silk fibroin concentration, the pore walls were thicker. Table 2 shows actual pore sizes in the scaffolds, ranging from 350 to 920 μm.
The actual pore sizes in the scaffolds were 80˜90 % smaller than the particle size of NaCl used in the process. The pore sizes in scaffolds prepared with the same particle size of NaCl, regardless of the concentration of silk fibroin used, resulted in similar sized pores.
Porosity and Swelling Properties
Silk fibroin scaffolds with >90% porosity were formed and porosities increased with a decrease in pore size and silk fibroin concentrations (Table 3). These values were similar as those (84˜98%) of HFIP-derived silk scaffolds prepared by salt leaching or gas forming (Nazarov R, et al., Biomacromolecules, in press). Swelling ratio and water uptake of the scaffolds are shown in Tables 4 and 5.
Swelling ratio decreased gradually with a decrease in pore size. However, swelling ratio decreased significantly with an increase in silk fibroin concentration due to the decrease in porosity. The swelling ratio of the scaffold prepared from 8 wt % silk fibroin was ˜8 times lower than that of collagen scaffolds, due to the differences in the hydrophilicities of proteins (Ma L. et al., Biomaterials 2003, 24:4833-4841). The value was similar to polylactic acid scaffolds (Maquet V. et al., Biomaterials 2004, 25:4185-4194). Water uptake of the scaffolds in distilled water was >93% during 24 hrs. The high water-binding ability of the scaffolds can be attributed to the highly porous structure of the protein network.
Mechanical Properties
The scaffolds exhibited a ductile and sponge-like behavior with different stiffness depending on the concentration of silk fibroin used in the process. An elastic region was observed at initial strain followed by a peak stress. Table 6 shows the mechanical properties of the silk fibroin scaffolds. The compressive strength and modulus of the scaffolds increased with an increase in silk fibroin concentration.
The improvement in mechanical properties was attributed to the increase in polymer concentration accompanied with the increase in the wall thickness of the pores. At the same silk fibroin concentration, scaffolds prepared with smaller particle sizes of NaCl showed higher compressive strength and modulus due to the decreased pore size. It is considered that the increased pore wall sites induced by the decreased pore size provided more paths to distribute the applied stress. The increased pore sites may functioned as a barrier, such as crack disipation, to reduce crack propagation. In addition, it has been reported that a more uniform pore distribution improved the mechanical properties of polymer matrices. Therefore, stress applied to porous materials is concentrated at the pore interface, and if the pore distribution is not uniform, polymer matrices typically deform at a lower stress (Harris L D. Et al., J Biomed Mater Res 1998, 42:396-402). For example, in our recent studies (Nazarov R. et al., Biomacromolecules, in press) three-dimensional silk fibroin scaffolds were developed using a salt leaching method with HFIP. While these scaffolds had smaller pore size and utilized a higher concentration of silk fibroin in processing, the compressive strengths (30 to 250 KPa) of the HFIP-derived silk scaffolds (17 wt % silk in HFIP) prepared by salt leaching were similar to those found for the aqueous-derived (8˜10 wt % silk in water) silk scaffolds in the present study. However, the compressive modulus of aqueous-derived silk scaffolds was 3˜4 times higher (100 to 790 kPa) for the HFIP-derived silk scaffolds.
Enzymatic Degradation
a shows the mass of the scaffolds over time prepared from 4 to 8 wt % silk fibroin with NaCl of 850-1000 μm diameter particle sizes during a degradation period of 21 days. The scaffolds in phosphate buffer without protease showed no degradation within 21 days. The scaffolds prepared with 4 wt % fibroin rapidly degraded and the mass remaining was only 2% after 10 days. The scaffolds prepared from 6 and 8 wt % fibroin gradually degraded with time and the mass was reduced to 30 and 20%, respectively, after 21 days.
Conclusions
Porous silk fibroin scaffolds were prepared directly from silk fibroin aqueous solutions by a salt leaching method, in the complete absence of any organic solvents or chemical crosslinking. The formation of the scaffolds included a structural transition from random coil to β-sheet. This transition provides a mechanistic basis for the transition, as the salt may promote water loss from the hydrophobic domains leading to enhanced chain-chain interactions and thus β-sheet formation. Functional and morphological properties of the scaffolds were controlled by the concentration of the silk fibroin solution used in the process and the particle size of NaCl.
Control of silk fibroin concentration in aqueous solutions via osmotic stress was studied to assess relationships to gel formation and structural, morphological and functional (mechanical) changes associated with this process. Environmental factors potentially important in the in vivo processing of aqueous silk fibroin were also studied to determine their contributions to this process. Gelation of silk fibroin aqueous solutions was affected by temperature, Ca2+, pH and polyethylene oxide (PEO). Gelation time decreased with increase in protein concentration, decrease in pH, increase in temperature, addition of Ca2+ and with the addition of PEO. No change of gelation time was observed with the addition of K+. Upon gelation, a random coil structure of the silk fibroin was transformed into β-sheet structure. Hydrogels with fibroin concentrations >4 weight percent exhibited network and sponge-like structures based on scanning electron microscopy. Pore sizes of the freeze-dried hydrogels were smaller as the silk fibroin concentration or gelation temperature were increased. Freeze-dried hydrogels formed in the presence of Ca2+ exhibited larger pores as the concentration of this ion was increased. Mechanical compressive strength and modulus of the hydrogels increased with increase in protein concentration and gelation temperature.
Methods
Preparation of Silk Fibroin Aqueous Solution
Cocoons of Bombyx mori, kindly provided by M. Tsukada (Institute of Sericulture, Tsukuba, Japan) and M. Goldsmith (U. Rhode Island), were boiled for 20 min in an aqueous solution of 0.02 M Na2CO3, and then rinsed thoroughly with distilled water to extract the glue-like sericin proteins and wax. The extracted silk fibroin was then dissolved in 9.3 M LiBr solution at 60° C. for 4 hrs, yielding a 20 w/v % solution. This solution was dialyzed in distilled water using a Slide-a-Lyzer dialysis cassette (MWCO 3500, Pierce) for 2 days. The final concentration of silk fibroin aqueous solution was ca. 8 wt %, which was determined by weighing the remaining solid after drying. Silk fibroin film prepared from 8 wt % solutions was evaluated to verify the removal of Li+ ion by XPS; no residual Li+ ion was detected.
Preparation of Concentrated Silk Fibroin Solution by Osmotic Stress
Silk fibroin aqueous solution (8 wt %, 10 ml) was dialyzed against 10˜25 wt % polyethylene glycol (PEG, 10,000 g/mol) solution at room temperature by using Slide-a-Lyzer dialysis cassettes (MWCO 3500). The volume ratio of PEG to silk fibroin solution was 100:1. By osmotic stress, water molecules in the silk fibroin solution moved into PEG solution through the dialysis membrane (Parsegian, V. A., et al., Methods in Enzymology, Packer, L., Ed.; Academic Press: 1986; Vol. 127, p 400). After the required time, concentrated silk fibroin solution was slowly collected by syringe to avoid excessive shearing and the concentration was determined. Silk fibroin aqueous solutions with concentration less than 8 wt % were prepared by diluting 8 wt % solutions with distilled water. All solutions were stored at 7° C. before use.
Sol-Gel Transitions
A 0.5 ml of silk fibroin aqueous solution was placed in 2.5 ml flat-bottomed vials (diameter: 10 mm). The vials were sealed and kept at room temperature, 37° C. and 60° C. Gelation time was determined when the sample had developed an opaque white color and did not fall from an inverted vial within 30 sec. To investigate the effect of ions and ion concentration on the process, CaCl2 or KCl solutions were added into the silk fibroin aqueous solution to generate a final salt concentration of 2.5 to 30 mM. The pH of the silk fibroin solution was adjusted with HCl or NaOH solution. For the preparation of silk fibroin-poly(ethylene) oxide (PEO, 900,000 g/mol) solution, the required amount of PEO solution (5 wt %) was added to silk fibroin solution with mild stirring for 5 minutes. The blend ratios of silk fibroin/PEO were 100/0, 95/5, 90/10, 80/20 and 70/30 (w/w).
Wide Angle X-Ray Scattering (WAXS)
X-ray profiles were recorded for freeze-dried silk fibroin solutions and hydrogels using a Brucker D8 X-ray Diffractometer at 40 kV and 20 mA, with Ni-filtered Cu-Kα radiation.
Scanning Electron Microscopy (SEM)
Silk fibroin solutions and hydrogels were frozen at −80° C. and then lyophilized. The samples were fractured in liquid nitrogen and examined using a LEO Gemini 982 Field Emission Gun SEM. To check for artifactual morphological changes due to freeze-drying, an alternative preparation used Karnovsky's fixative at room temperature for 4 hrs. Hydrogels with and without fixative treatment showed little morphological change upon freeze-drying. Pore size was obtained by using ImageJ software developed at the US National Institutes of Health.
Mechanical Properties
Compression tests of hydrogels were performed on an Instron 8511 equipped with a 2.5 kN load cell at room temperature. A crosshead speed was 10 mm/min. The cross-section of samples was 12 mm in diameter and 5 mm in height. The compression test was achieved conventionally as an open-sided method. The compression limit was 98% strain to protect the load cell. Five samples were evaluated for each composition.
Results
Concentrated Silk Fibroin Solutions
Silk fibroin aqueous solution with an initial concentration of 8 wt % was dialyzed against 10˜25 wt % PEG solution at room temperature. Silk fibroin aqueous solution was concentrated over time by osmotic stress and concentrations of ca. 21 wt % were obtained after 9 hrs dialysis against 25 wt % PEG solution (
Gelation of Silk Fibroin Aqueous Solution
The influence of temperature, Ca2+ and K+ concentrations, pH and PEO concentration was investigated on the gelation of silk fibroin aqueous solutions.
Structural Analysis of Hydrogels
Structural changes in the silk fibroin were determined by X-ray diffraction.
Morphology of Freeze-Dried Hydrogels
Morphological features of silk fibroin solutions and hydrogels were observed by SEM after freeze-drying at −80° C. Freeze-dried silk fibroin solutions of 4˜12 wt % showed leaf-like morphologies. Freeze-dried silk fibroin solutions of 16 wt % and 20 wt % exhibited network and sponge-like structures with pore sizes of 5.0±4.2 μm and 4.7±4.0 μm, respectively. By SEM imagery it was determined that freeze-dried hydrogels prepared from 4 wt % silk fibroin solution showed leaf-like morphologies and interconnected pores regardless of temperature and at higher fibroin concentrations than 4 wt % sponge-like structures were observed. The pore sizes of freeze-dried hydrogels (<1.1±0.8 μm) were smaller than those observed for the freeze-dried silk fibroin solution samples. Pore sizes in the freeze-dried hydrogels decreased with increase in silk fibroin concentration, and pore sizes decreased as temperature increased at the same silk fibroin concentration. The 4 wt % freeze-dried hydrogels with Ca2+ ions showed network and sponge-like structures, whereas the 4 wt % freeze-dried hydrogels with K+ ions had a leaf-like morphology. In freeze-dried hydrogels with fibroin concentrations >4 wt %, pore sizes of freeze-dried hydrogels with Ca2+ were larger than those of freeze-dried hydrogels prepared from silk fibroin aqueous solutions without Ca2+ ions. Interestingly, pore size was larger in freeze-dried hydrogels with the same silk fibroin concentration with an increase in Ca2+ concentrations. In contrast to freeze-dried hydrogels with Ca2+, pore sizes of freeze-dried hydrogels with K+ showed sizes similar to those of freeze-dried hydrogels prepared from silk fibroin aqueous solutions. These results imply that Ca2+ was more effective in inducing interactions among the silk fibroin chains than the K+. This result is also consistent with the earlier data wherein Ca2+ resulted in shorter gelation times than K+.
Mechanical Properties of Hydrogels
The compressive strength and modulus of hydrogels prepared from silk fibroin aqueous solutions increased with an increase in silk fibroin concentration (
Discussion
Gelation occurs due to the formation of inter- and intramolecular interactions among the protein chains, including hydrophobic interactions and hydrogen bonds (Ayub, Z. H., et al., Biosci. Biotech. Biochem. 1993, 57, 1910-1912; Hanawa, T., et al., Chem. Pharm. Bull. 1995, 43, 284-288; Kang, G. D., et al., Marcromol. Rapid Commun. 2000, 21, 788-.791). With an increase in fibroin content and temperature, interactions among the fibroin chains increases. Silk fibroin molecules are thereby able to interact more readily, leading to physical crosslinks.
The concentration of Ca2+ ion in the silkworm (Bombyx mori) increases from 5 mM to 15 mM as silk progresses toward the spinneret, while K+ ion is present at 5˜8 mM.3 Several calcium salts are known to dissolve silk fibroin because of strong interactions with the fibroin (Ajisawa, A. J. Seric. Sci. Jpn. 1998, 67, 91-94; Ha, S. W., et al., Biomacromolecules 2003, 4, 488-496). Rheological measurements of dilute solutions of silk fibroin from Bombyx mori revealed that the protein chains tend to form clusters by ionic interaction between COO− ions of amino acid side chains in the fibroin and divalent ions such as Ca2+ or Mg2+ (Ochi, A., et al., Biomacromolecules 2002, 3, 1187-1196). Through these interactions, the pH of silk fibroin solutions with Ca2+ ions was significantly lower than that of silk fibroin solutions in the absence of these ions, whereas the addition of monovalent ions such as K+ showed only a slight decrease of pH. With lower pH, repulsion among silk fibroin molecules decreases and interactions among the chains is easier, resulting in stronger potential for the formation of β-sheet structure through hydrophobic interactions. A pH near the isoelectric point (pI=3.8-3.9) (Ayub, Z. H., et al., Biosci. Biotech. Biochem. 1993, 57, 1910-1912; Kang, G. D., et al., Marcromol. Rapid Commun. 2000, 21, 788-791) of silk fibroin accelerated the sol-gel transition of silk fibroin aqueous solutions in a fashion similar to other proteins that aggregate near their isoelectric points.
These outcomes may reflect subtle differences in how different silk proteins from different organisms utilize physiologically relevant ions to facilitate sol-gel transitions. Divalent ions may induce aggregation of silk fibroin molecules by ionic interactions with negatively charged amino acids present particularly near the chain ends of the heavy chain fibroin. The lack of response to different concentrations of Ca2+ may suggest a broad window of response physiologically or perhaps a role for combinations of ions to fully control this process in vivo or in vitro. Additional studies will be required to elucidate these relationships, particularly when considered in concert with observations on domain mapping of silks related to processing environments (Bini, E., et al., J. Mol. Biol. 2004, 335, 27-40).
The movement of water from the silk fibroin molecules to the hydrophilic PEO facilitates inter- and intramolecular interactions among the protein molecules and the subsequent formation of the β-sheet structure. This transition is evident with silk based on our recent mechanistic understanding of the process (Jin, H. J., et al., Nature 2003, 424, 1057-1061). These transitions can be induced by direct addition of PEO into the fibroin aqueous solutions, or via separation from the aqueous solutions across a dialysis membrane (with PEG). Thus, direct contact between the protein and the PEO is not required, only the facilitation of water transport from the protein to the PEO/PEG to drive the sol-gel transition.
Conclusions
From the primary sequence, silkworm silk fibroin heavy chain is composed of seven internal hydrophobic blocks and seven much smaller internal hydrophilic blocks, with two large hydrophilic blocks at the chain ends (Zhou, C. Z., et al., Nucleic Acids Res. 2000, 28, 2413-2419; Jin, H. J., et al., Nature 2003, 424, 1057-1061). The percentage of hydrophobic residues in silk fibroin is 79% (Braun, F. N., et al., Int. J. Biol. Macromol. 2003, 32, 59-65) and the repetitive sequence in hydrophobic residues consists of GAGAGS peptides that dominate the β-sheet structure forming crystalline regions in silk fibroin fibers and films (Mita, K., et al., J. Mol. Evol. 1994, 38, 583-592). The formation of these β-sheets results in insolubility in water (Valluzzi, R., et al., J. Phys. Chem. B 1999, 103, 11382-11392). Hydrophobic regions of silk fibroin in aqueous solution assemble physically by hydrophobic interactions and eventually organize into hydrogels (Jin, H. J., et al., Nature 2003, 424, 1057-1061). Silk fibroin concentration, temperature, Ca2+, pH and PEO affected the gelation of the silk fibroin aqueous solutions. With increase in fibroin content and temperature, physical crosslinking among silk fibroin molecules formed more easily. Ca2+ ions accelerated these interactions, presumably through the hydrophilic blocks at the chain ends. The decrease in pH and the addition of a hydrophilic polymer decreased repulsion between silk fibroin molecules and promoted the desorption of water from the protein, resulting in shorter gelation times. Upon gelling, a conformational transition from random coil to β-sheet structure was induced and promoted the insolubility and stability of silk fibroin hydrogels in water. Silk fibroin hydrogels had network and sponge-like structures. Pore size was smaller with increased silk fibroin concentration and gelation temperature. Freeze-dried hydrogels showed larger pore sizes with increases in Ca2+ concentrations than freeze-dried hydrogels prepared from silk fibroin aqueous solutions at the same fibroin content. The compressive strength and modulus of hydrogels prepared from silk fibroin aqueous solution without ions increased with increase in protein concentration and gelation temperature.
Hydrogels from natural polymers, such as collagen, hyaluronate, fibrin, alginate and chotosan, have found numerous applications in tissue engineering as well as in drug delivery. However, they generally offer a limited range of mechanical properties (Lee, K. Y., et al., Chem. Rev. 2001, 101, 1869-1879). In contrast, silk fibroin provides an important set of material options in the fields of controlled release, biomaterials and scaffolds for tissue engineering because of combination with impressive mechanical properties, biocompatibility, biodegradability and cell interaction (Altman, G. H., et al., Biomaterials 2003, 24, 401-416; Cappello, J., et al., J. Control. Release 1998, 53, 105-117; Foo, C. W. P., et al., Adv. Drug Deliver. Rev. 2002, 54, 1131-1143; Dinerman, A. A., et al., J. Control. Release 2002, 82, 277-287; Megeed, Z., et al., Adv. Drug Deliver. Rev. 2002, 54, 1075-1091; Petrini, P., et al., J. Mater. Sci-Mater. M. 2001, 12, 849-853; Altman, G. H., et al., Biomaterials 2002, 23, 4131-4141; Panilaitis, B., et al., Biornaterials 2003, 24, 3079-3085).
We have examined the bone regeneration of human bon marrow stem cells on three-dimensional silk scaffolds from aqueous silk solutions of the invention. To study the ability of the silk scaffolds to support the growth and differentiation of the bone marrow stem cells, we have used the silk scaffolds without any decoration.
Methods
Materials
Bovine serum, Dulbecco's Modified Eagle Medium (DMEM), Minimal essential medium-a modification (αMEM), basic Fibroblast growth factor (bFGF), Penicillin-Streptomycin (Pen-Strep), Fungizone, non essential amino acids, trypsin were from Gibco (Carlsbad, Calif.). Ascorbic acid phosphate, Histopaque-1077, dexamethasone, and β-glycerolphosphate were from Sigma (St. Lois, Mo.). All other substances were of analytical or pharmaceutical grade and obtained from Sigma. Silkworm cocoons were kindly supplied by M. Tsukada (Institute of Sericulture, Tsukuba, Japan) and Marion Goldsmith (University of Rhode Island, Cranston, R.I.).
Preparation of Scaffolds
Aqueous-derived silk scaffolds were prepared by adding 4 g of granular NaCl (particle size; 1000˜1180 μm) into 2 ml of 8 wt % silk fibroin solution in disk-shaped Teflon containers. The container was covered and left at room temperature. After 24 hrs, the container was immersed in water and the NaCl was extracted for 2 days. HFIP-derived silk scaffolds were prepared by adding 4 g of granular NaCl (particle size; 850˜100 μm) into 2 ml of 8 wt % silk fibroin in HFIP. The containers were covered to reduce of HFIP and to provide the sufficient time for more homogeneous distribution of the solution. The solvent was evaporated at room temperature for 3 days. After the composite of silk/porogen was treated in methanol for 30 min to induce β-sheet structure and insolubility in aqueous solution, the composite was immersed in water to remove NaCl for 2 days. The porous silk scaffolds were air-dried.
Human Bone Marrow Stem Cell Isolation and Expansion
Total bone marrow (25 cm3, Clonetics, Santa Rosa, Calif.) was diluted in 100 ml of isolation medium (5% FBS in RPMI 1640 medium). Cells were separated by density gradient centrifugation. Briefly, 20 ml aliquots of bone marrow suspension were overlaid onto a poly-sucrose gradient (1,077 g/cm3, Histopaque, Sigma, St. Louis, Mo.) and centrifuged at 800×g for 30 min at room temperature. The cell layer was carefully removed, washed in 10 ml isolation media, pelleted and contaminating red blood cells were lysed in 5 ml of Pure-Gene Lysis solution. Cells were pelleted and suspended in expansion medium (DMEM, 10% FBS, 1 ng/ml bFGF, 100 U/ml penicillin, 100 μg/ml streptomycin, 0.25 μg/ml fungizone, nonessential amino acid) and seeded in 75 cm2 flasks at a density of 5×104 cells/cm2. The adherent cells were allowed to reach approximately 80% confluence (12-17 days for the first passage). Cells were trypsinized, replated and passage 2 (P2) cells (80% confluence after 6-8 days), were used for the experiments.
In Vitro Culture
For examination of cell growth and differentiation in vitro on silk scaffolds, BMSC (5×105 cells/scaffold, passage 2) was seeded onto prewetted (α-MEM, overnight) silk scaffolds. After 24 h, the medium was removed and cultures were maintained in individual wells of 6-well plates. Osteogenic media were α-MEM supplemented with 10% FBS, nonessential amino acid, 50 μg/ml ascorbic acid-2-phosphate, 10 nM dexamethasone, and 7 mM β-glycerolphosphate in the presence of penicillin and streptomycin and fungizone. Cultures were maintained at 37° C. in a humidified incubator supplemented with 5% CO2. Half of the medium was changed every 2-3 days.
Biochemical Analysis and Histology
Scaffolds were cultured for 2 and 4 weeks in osteogenic media and processed for biochemical analysis and histology. For DNA analysis, 3-4 scaffolds per group and time point were disintegrated. DNA content (n=3-4) was measured using the PicoGreen assay (Molecular Probes, Eugene, Oreg.), according to the protocol of the manufacturer. Samples were measured flurometrically at an excitation wavelength of 480 nm and an emission wavelength of 528 nm. For total calcium content, samples (n=4) were extracted twice with 0.5 ml 5% trichloroacetic acid. Calcium content was determined by a colorimetric assay using o-cresolphthalein complexone (Sigma, St. Louis, Mo.). The calcium complex was measured spectrophotometrically at 575 nm. Alkaline phosphatase activity was measured using a biochemical assay from Sigma (St. Louis, Mo.), based on conversion of p-nitrophenyl phosphate to p-nitrophenol, which was measured spectrophotometrically at 405 nm.
RNA Isolation, Real-Time-Reverse Transcription Polymerase Chain Reaction (Real Time RT-PCR)
Fresh scaffolds (n=3-4 per group) were transferred into 2 ml plastic tubes and 1.0 ml Trizol was added. Scaffolds were disintegrated using steel balls and a Microbeater. Tubes were centrifuged at 12000 g for 10 minutes and the supernatant was transferred to a new tube. Chloroform (200 μl) was added to the solution and incubated for 5 minutes at room temperature. Tubes were again centrifuged at 12000 g for 15 minutes and the upper aqueous phase was transferred to a new tube. One volume of 70% ethanol (v/v) was added and applied to an RNeasy mini spin column (Quiagen, Hilden, Germany). The RNA was washed and eluted according to the manufacturer's protocol. The RNA samples were reverse transcribed into cDNA using oligo (dT)-selection according to the manufacturer's protocol (Superscript Preamplification System, Life Technologies, Gaithersburg, Md.). Collagen type I, Collagen type II, Alkaline phosphatase, bone sialoprotein and Osteopontin gene expression were quantified using the ABI Prism 7000 Real Time PCR system (Applied Biosystems, Foster City, Calif.). PCR reaction conditions were 2 min at 50° C., 10 min at 95° C., and then 50 cycles at 95° C. for 15 s, and 1 min at 60° C. The expression data were normalized to the expression of the housekeeping gene, glyceraldehyde-3-phosphate-dehydrogenase (GAPDH). The GAPDH probe was labelled at the 5′ end with fluorescent dye VIC and with the quencher dye TAMRA at the 3′ end. Primer sequences for the human GAPDH gene were: Forward primer 5′-ATG GGG AAG GTG AAG GTC G-3′ (SEG ID NO: 1), reverse primer 5′-TAA AAG CCC TGG TGA CC-3′ (SEQ ID NO: 2), probe 5′-CGC CCA ATA CGA CCA AAT CCG TTG AC-3′(SEQ ID NO: 3). Primers and probes for alkaline phosphatase, bone sialoprotein (BSP), osteopontin and were purchased from Applied Biosciences (Assay on Demand #, Hs 00240993 ml (ALP), Hs 00173720 ml (BSP), Hs 00167093 ml (osteopontin)).
Western Blotting Analysis
For total protein extraction, cells were lysed in RIPA buffer [50 mM Tris-HCl, pH 8.0, 150 mM NaCl, 1% Nonidet P-40 (NP-40), 0.2% SDS, 5 mM NaF] containing protease inhibitors and phosphatase inhibitors. Protein content was measured by the Bradfod method. Proteins were resolved by 3-8% SDS-PAGE and transferred to membranes. Blots were probed with the primary antibody for 12 h at 4° C., washed, and incubated with the appropriate peroxidases labed secondary antibodies for 1 h at room temperature. Protein bands were revealed by ECL (Armersham-Pharmnacia,)
Scanning Electron Microscopy (SEM) Analysis
The polymeric surfaces prior to and after cell attachment were examined by scanning electron microscopy (SEM). Matrices were fixed using Karnovsky's fixative for 24 h, and washed three times in CMPBS to remove residual fixative. The samples were then dried using a graded series of ethanol (50˜100%) at 15 min intervals. After drying, the samples were sputter coated with gold and examined with a LEO Gemini 982 Field Emission Gun SEM.
Histological Evaluation
After fixation with 4% phosphate-buffered formaldehyde for at least 24 hours, specimens were embedded within paraffin and sectioned (4 μm). Using standard histochemical techniques, serial sections were stained with hematoxylin and eosin and alcian blue.
Results
SEM Analysis
Characterization of the 3D-silk scaffolds was determined by assessment of structurally by SEM for the analysis of pore size distribution and surface topography. SEM analysis showed the water-silk scaffold had the interconnected porous networks with an average pore size 920±50 μm. Pore surfaces had an appearance of a rough structure with nonhomogenous micropores. However, HFIP-silk scaffold had the poor interconnected porous networks with an average pore size 900±40 μm and showed the smooth surface structure. BMSCs (passage 2) were seeded in water-silk sponge and HFIP-silk sponge. More cells adhered to the water-silk sponge than to the HFIP-silk sponge. Water-silk sponge facilitated cell seeding. And BMSCs were homogeneously distributed throughout the water-silk sponge. In contrast, the distribution of BMSCs on HFIP-silk sponge was not homogenous. BMSCs growth was observed on water-silk sponge. SEM confirmed extensive growth of BMSCs on water-silk sponge, followed by growth for up to 4 weeks.
Gross Examination
The cell-scaffold constructs were cultured in osteogenic media under a 5% CO2 atmosphere at 37° C. Constructs were cultured for up to 28 days in 6 well plates. The BMSCs-water-silk constructs were became rounded after culturing but BMSCs-HFIP-silk constructs were originally flat and did not change after culturing. The tissue formed in the water-silk scaffold was whitish, hard to the touch and with surgical forceps. But the BMSCs seeded in the HFIP-silk scaffold did not form whitish tissue. No significant difference was noted 2- and 4-week specimens on gross examination. And homogenous cellular distribution of BMSCs within the water-silk scaffold was qualitatively demonstrated by the uniformity of matrix staining (indicative of MTT conversion by viable cells) on the surface and throughout the center of the scaffold. But HFIP-silk scaffold displayed intense staining along the surface of construct and regions of weak staining within the interior of the construct.
Biochemical Analysis
The porosity of the 3D matrices was ca 92% in both water- and HFIP-silk. The compressive strength and modulus water-silk scaffolds were 100±10 kPa and 1300±40 kPa. Those of HFIP-scaffolds were 50±5 kPa and 210±60 kPa.
The total number of cells cultured on the scaffolds was quantified using a DNA assay over the time course of the study. For water-silk scaffolds seeded with cells suspended in medium, there was an increase from 51,000±12,000 cells after initial seedings to 150,000±12,000 cells after 28 days of culture. HFIP-silk scaffolds seeded with cells suspended in medium did not show significant proliferation from the 8,000±3,400 cells after the initial cell seeding to 32,000±11,000 cells after 28 days of culture.
Alkaline phosphatase (ALPase) activity, an indicator of the osteoprogenitor cell's commitment to the osteoblastic phenotype, was measured on a per-scaffold. For water-silk scaffold, there was a significant increase in ALPase activity after 28 days in culture (9.7±0.3 mmol/scaffold) compared to 1 day (0.4±0.01 mmol/scaffold). After 28 days of culture for HFIP-silk scaffold, 2.9±0.12 mmol per scaffold was detected.
The total calcium content of each sample was measured on a per-scaffold. Significant calcium deposition (10.5±0.65 μg/scaffold)was found after 28 days of culture in osteogenic media for water-silk scaffold. After 28 days of culture for HFIP-silk scaffold, there was 1.4±0.1 μg of Ca2+ per scaffold.
Expression of Osteogenic Differentiation Associated Genes
To characterize the bone-like tissue produced by BMSC, the expression of several osteogenic differentiation and condrogenic differentiation marker genes were quantified using real-time RT-PCR assays. The genes analyzed included the osteogenic differentiation markers collagen type I (Col I), alkaline phosphatase (ALP), osteopontin (OP), bone sialoprotein (BSP), and the condrogenic differentiation marker collagen type II (Col II). The transcription level (normalized to GAPDH within the linear range of amplification) differences between scaffold types were significant. Col I, ALP, and OP transcription levels increased in water-silk scaffold when compared with HFIP-silk scaffold. After 28 days of culture, gene expression of Col I, ALP and BSP was significantly increased by 190%, 1100% and 10500%, respectively, in water-silk scaffolds when compared with after 1 days of culture. However, OP and Col II expression was significantly decreased. BSP expression was regulated similarly in water-silk scaffolds and HFIP-silk scaffolds. The differences between scaffold types were not statistically significant.
Expression of Osteogenic Differentiation Associated Proteins
In 3-D water-silk scaffold culture condition, human bone marrow stem cells expressed the osteoblast markers. In comparison to HFIP-silk constructs, the expression of Col I showed significant increase of protein levels under water-silk culture condition after 2 weeks. However the expression of Col I was decreased after 4 weeks culture under the both conditions. After 28 days of culture, the expression of OP was increased in water-silk constructs. The protein showed two bands, of which that at the highest molecular weight was assumed to be highly glycosilated, sulfated or phosphorylated (Singh et al., J. Biol Chem, 1990, 65:18696-18701). The other protein of bone, BSP was expressed in cells cultured both in water-silk scaffolds and in HFIP-silk scaffolds. However its expression was increased in HFIP-silk constructs after 28 days of culture.
We also analyzed the expression of matrix metalloproteinase 13 (MMP13) and Col II. MMP13 was expressed in only water-silk constructs. And the Col II was downregulated in both culture conditions after 4 weeks.
Histological Examination
Histological examination of these specimens using hematoxylin and eosin stains revealed that the percentage of osteoblast-like cells in their cuboidal or columnar morphology increased with an increase in the culture period in water-silk constructs. After 14 days of culture, almost all pores were filled with connective tissue, fibroblasts and cuboidal osteoblast-like cells. After 28 days, the pores were filled with extracellular matrix, osteoblast-like cells and few cells with fibroblast-like morphology. However, the histological sections of HFIP-silk scaffolds demonstrated that there was a sparse distribution of cells, with their majority forming a cell layer near the scaffold's surface. After 28 days of culture, the majority of cells within HFIP-silk constructs displayed a flat fibroblastic morphology.
After culture in osteogenic media, extracellular matrices of proteoglycan by alcian blue stains revealed that proteoglycans were detected in water-silk constructs. No proteoglycn was histologically detected in HFIP-silk constructs.
Discussion
The silk protein-based matrix scaffolds are of current interest for bone tissue engineering. These scaffolds exhibit higher mechanical properties than the other common biodegradable synthetic and natural polymers such as PGA-PLA copolymers and collagen. HFIP have been used to prepare porous silk fibroin materials. Although HFIP-silk scaffolds are known for their unique mechanical properties, these natural polymers lack cell-recognition signals, which results in insufficient cell adhesion. To overcome this problem, a number of approaches have been developed, including: surface modification with arginine-glycine-aspartic acid (RGD), and hybrid with naturally derived biodegradable polymers.
Cell adhesion is known as an important cellular process because it directly influences cell growth and differentiation. In the present example, used the silk scaffolds without any modification. We observed sufficient cell adhesion in water-silk scaffolds. More cells adhered to the water-silk scaffolds than to the HFIP-silk scaffolds. Variations in surface texture, or microtopography can affect the cellular response. It was found that a higher percentage of cells attached to the rougher surface. SEM analysis and histological analysis showed our water-silk scaffold had the rough structure with homogenous pores. However, HFIP-silk scaffold had the smooth surface structure.
With respect to the microstructures of the porous scaffolds, high porosity (>90%) and interconnected pore network are desirable. In addition, the preferred pore size is generally in the range of 50-500 μm to permit the ingrowth of cells and regeneration of tissue (Katoh K. et al., Biomaterials 2004, 25: 4255-4262; Thomson R, et al., In Principles of Tissue Engineering; Lanza R, Langer R and Vacanti J, eds. Academic Press: San Diego, pp. 251-262, 2000). The mitigation of nutrient transport limitations, external to three-dimensional cell/polymer constructs, influences the proliferation, differentiation, and expression of osteoblastic markers of MSCs seeded on three-dimensional scaffolds (Sikavitsas V I. Et al., J Biomed Mater Res 62: 136-148). The structural characterization showed that the pore size and the porosity of the water-silk sponge were controlled by the size of the NaCl particulates. We prepared the water-silk sponge with the regulated pore size (920±50 μm), which had more than 90% of the porosity. Furthermore, the pores were opened to the outside, interconnected and were uniformly distributed throughout the sponges. Porous silk scaffolds were seeded with human BMSCs, and BMSCs-silk constructs were cultured for an extended period of 28 days in two model silk scaffolds (water-silk scaffolds and HFIP-silk scaffolds). The BMSCs seeded in water-silk scaffolds demonstrated accelerated proliferation during the first 2 weeks of culture, and the strongest ALP activity and the highest calcium deposition at the end of the culture period. The onset of skeletogenesis, whether during fetal development or adult repair, begins with the condensation of mesenchymal stem cells. Shortly after the condensation stage, cells in the central region of the aggregation begin to adopt a cartilaginous phenotype (Ferguson C. et al., Mech. Dev. 1999, 87: 57-66). The expression of Col II showed this event in our silk scaffolds. Our investigation of Col II showed that despite the gene expression of Col II in early stage, differentiated BMSCs cultured in water-silk scaffolds maintained a differentiated phenotype to the end of the culture period. In early stage, we observed Col II expression expression in HFIP-silk constructs, too. But the Col II gene expression and protein expression were significantly reduced. Chondrocytes progress from a proliferative to a hypertrophic state. The majority of hypertrophic chondrocytes are ultimately fated to undergo programmed cell death, which is accompanied by remodeling of the extracellular matrix (ECM) and the subsequent deposition of new bone (Gerber H. et al., Nat. Med. 1999, 5: 623-628). MMP13 regulates remodeling of the hypertrophic cartilage matrix. The expression of MMP 13 observed in water-silk constructs, but not in HFIP-silk constructs, indicating that the cells in water-silk scaffold were mature and hypertrophic chondrocytes. The switch from a cartilage template to a bone during endochondral bone formation is not a mere switch of cell phenotypes. The cartilaginous ECM is then replaced by the bone ECM. Proteoglycan synthesis, the expression of ALP, and the expression of type I collagen, but very little type II collagen, were detected in water-silk constructs. Although the expression of ALP and type I collagen, the markers of osteoblastic differentiation, were significantly increased in water-silk constructs, the other protein of bone, BSP thought to comprise 8-12% of the total noncollagenous protein, was expressed similarly in water-silk scaffolds and HFIP-silk scaffolds. Coexpression of type I and type II collagen demonstrated in a study (Nakagawa T. et al., Oral Diseases 2003, 9: 255-263) showing that chondrocytes change their phenotype to produce the bone-like matrix and remain within the endochondral bone. One of the osteoblast markers, OP, appears to be highly expressed at two stages of osteogenesis: at an early, proliferative stage and at a later stage, subsequent to the initial formation of mineralized bone matrix (Yae, K L. et al., J Bone Miner. Res. 1994, 9: 231-240). Early in the culture, the expression of OP was upregurated in water-silk constructs. These studies point to the usefulness of water-silk scaffolds in the initial formation of bone tissue. Although type I collagen constitutes the largest portion (90%) of the organic matrix in bone, it is not unique to this tissue. Proteoglycan, or at least their component glycosaminoglaycan chains, have long been recognized as small but significant components of the mineralized bone matrix (Fisher L W. et al., J. Biol. Chem. 1982, 258: 6588-6594; Fedarko NS. Et al., J. Biol. Chem. 1990, 265: 12200-12209). After the culture in water-silk scaffolds, staining of sections with alcian blue stain clearly demonstrated the presence of proteoglycan in the ECM. Proteoglycan can be found in the cartilage. The origin and tissue specificity of these porteoglycans have not been determined. In our study, the proteoglycan was detected after 14 days of culture in water-silk constructs, but not in HFIP-silk constructs.
The references cited throughout the application are incorporated herein by reference.
This application is a continuation of International Application No. PCT/US2004/011199, filed on Apr. 12, 2004, which designated the U.S., and which claims the benefit under 35 U.S.C § 119(e) of U.S. Provisional Application No. 60/461,716 filed on Apr. 10, 2003, and U.S. Provisional Application No. 60/551,186 filed on Mar. 8, 2004.
This invention was supported by the NIH, the NSF and the Air Force (subcontract from Foster Miller) Grant No.(s) R01EB003210, R01DE13405-01A1, DMR-0090384, F49620-01-C-0064, and the government of the United States has certain rights thereto.
| Number | Name | Date | Kind |
|---|---|---|---|
| 1989005 | Fink et al. | Jan 1935 | A |
| 4233212 | Otoi et al. | Nov 1980 | A |
| 5047507 | Buchegger et al. | Sep 1991 | A |
| 6815427 | Tsubouchi et al. | Nov 2004 | B2 |
| 7057023 | Islam et al. | Jun 2006 | B2 |
| 7285637 | Armato et al. | Oct 2007 | B2 |
| 20040005363 | Tsukada et al. | Jan 2004 | A1 |
| 20040266992 | Migliaresi et al. | Dec 2004 | A1 |
| Number | Date | Country |
|---|---|---|
| WO 03022909 | Mar 2003 | WO |
| 2004041845 | May 2004 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20070187862 A1 | Aug 2007 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60461716 | Apr 2003 | US | |
| 60551186 | Mar 2004 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/US2004/011199 | Apr 2004 | US |
| Child | 11247358 | US |