Claims
- 1. Blends of polystyrene with polymodal block copolymers in which the block copolymer contains from about 55 to about 95 weight percent of monovinylaromatic monomer based upon total weight of the copolymer and the copolymer is produced in accordance with a method comprising:
- (a) charging into a polymerization zone an initiator and a monovinylaromatic monomer in the presence of a randomizer and allowing polymerization to occur until essentially no free monomer is present; thereafter
- (b) charging into said polymerization zone a monovinylaromatic monomer and an initiator and allowing polymerization to occur until essentially no free monomer is present; thereafter
- (c) charging into said polymerization zone a mixture of monovinylaromatic monomer and conjugated diene monomer and allowing polymerization to occur until essentially no free monomer is present; thereafter
- (d) charging into said polymerization zone a mixture of monovinylaromatic monomer and conjugated diene monomer and allowing polymerization to occur until essentially no free monomer is present; thereafter
- (e) charging into said polymerization zone a monovinylaromatic monomer and an initiator and allowing polymerization to occur until essentially no free monomer is present; thereafter
- (f) charging into said polymerization zone a mixture of monovinylaromatic monomer and conjugated diene monomer and allowing polymerization to occur until essentially no free monomer is present; thereafter
- (g) charging into said polymerization zone a mixture of monovinylaromatic monomer and conjugated diene monomer and allowing polymerization to occur until essentially no free monomer is present; thereafter
- (h) charging into said polymerization zone a conjugated diene monomer and allowing polymerization to occur until essentially no free monomer is present; and thereafter
- (i) charging the reaction mixture with a coupling agent.
- 2. Blends as recited in claim 1 wherein said blends comprise from about 10 to about 95 weight percent, based upon total weight of the blend, of said polymodal copolymers produced in accordance with the method of claim 1.
- 3. Blends as recited in claim 1 wherein said blends comprise from about 20 to about 80 weight percent, based upon total weight of the blend, of said polymodal copolymers produced in accordance with the method of claim 1.
- 4. Blends as recited in claim 1 wherein said blends comprise from about 35 to about 65 weight percent, based upon total weight of the blend, of said polymodal copolymers produced in accordance with the method of claim 1.
- 5. A polymodal coupled resinous block copolymer of a monovinyl aromatic compound and a conjugated diene;
- said copolymer having from about 55 to about 95 weight percent polymerized monovinyl aromatic compound based on total weight of monomers in said copolymer;
- said copolymer having polymer chains which result from coupling
- S-S-B/S-B/S-S-B/S-B/S-B-Li
- S-B/S-B/S-S-B/S-B/S-B-Li
- S-B/S-B/S-B-Li
- wherein S=monovinylarene block
- B=conjugated diene block
- B/S=tapered block monovinylarene and conjugated diene
- Li=living polymer site or coupling site.
Parent Case Info
This application is a division of application Ser. No. 07/982,938, filed Nov. 30, 1992, now U.S. Pat. No. 5,290,875.