Patent Application
20050103761
The present invention relates to a contact for a connector and a manufacturing method of an element to be soldered such as the contact.
Generally, in an element to be soldered such as a contact used in a connector, a foundation plating layer of nickel (Ni) is carried out on a metal material such as copper, and a gold plating is further carried out thereon. Owing to carrying out the gold plating on a surface of an element, not only the oxidization of the surface of the element can be prevented, but also a terminal of the element and a wiring pattern on a printed circuit board can easily be soldered owing to high wetting property between gold and solder.
On the other hand, a minute connector used in a mobile equipment such as a mobile phone or a digital still camera has a stacking height of the connector itself is about 1 mm when a socket and a header are coupled. Furthermore, a pitch of an arrangement of the contacts is about 0.4 mm and a height of the contact is about 0.7 mm. Thus, melted solder diffuses along a surface of the contact from the terminal portion due to the high wetting property between gold and solder, so that there is a possibility that the solder adheres at a portion such as a contacting portion to which the solder should not be adhered. Furthermore, there is a possibility that a sufficient connecting strength is not obtained due to deficiency of quantity of the solder adhered in the vicinity of the terminal portion and the wiring pattern on the printed circuit board which are to be soldered, according to the diffusion of the solder.
Therefore, as described in the publication gazettes of Japanese Patent Application 2-15662 and 6-204377, it is proposed to carry out partial plating for carrying gold plating only at the terminal portion and the contacting portion of the contact, surfaces of which are necessary to be plated with gold, so as not to be plated by gold at a portion between the terminal portion and the contacting portion. In this manner, when the foundation layer of nickel plating is unsheathed at the portion between the terminal portion and the contacting portion without plating gold, it is possible to prevent the diffusion of the solder from the terminal portion to the contacting portion due to low wetting property between nickel and solder.
The contact of the connector for mobile equipment, however, is much smaller, so that it is difficult to form the contact one by one and to carry out the plate on the contact entirely. Therefore, a side of a band metal plate is shaped like teeth of a comb, and the teeth portion is bend to have a predetermined shape, so that a semi-finished blank in which a lot of contacts are arranged at a predetermined pitch is formed. The semi-finished blank is dipped in a plating solution while it is conveyed in a lengthwise direction thereof, so that the nickel plating and the gold plating are carried out on entire surfaces of the contacts. Accordingly, it is very difficult to carry out the partial plating on the contacts. Even when the partial plating is forcibly carried out on the contacts, the processes and the plating machine for gold plating become very complex, and the conveying speed of the semi-finished blank becomes much slower, so that the productivity will be dropped.
A purpose of the present invention is to solve the above-mentioned problem and to provide a contact for a connector and a manufacturing method of an element to be soldered, by which the diffusion of the melted solder from the terminal portion to the contacting portion can be prevented, even though the gold plating is carried out on the entire surface of the contact.
For accomplishing the above-mentioned purpose, a contact for a connector in accordance with an aspect of the present invention comprises: a terminal portion provided in the vicinity of an end and a contacting portion provided in the vicinity of the other end, which are formed by shaping a metal material into a predetermined shape; a foundation plating layer and a gold plating layer or a metal alloy plating layer including gold formed substantially on entire surface of the contact including the terminal portion and the contacting portion; and a diffusion preventing area formed at a portion between the terminal portion and the contacting portion by processing on the gold plating layer or the metal alloy plating layer including gold in which melted solder rarely diffuses due to low wetting property with respect to the solder.
Furthermore, a manufacturing method of an element to be soldered in accordance with an aspect of the present invention comprises: a step of processing a metal material into a predetermined shape for forming a terminal portion in the vicinity of an end thereof; steps of plating a foundation plating layer and a gold plating layer or a metal alloy plating layer including gold on substantially entire surface of the element including the terminal portion and the contacting portion; and a step of irradiating laser beams on the gold plating layer or the metal alloy plating layer including gold at a position between the terminal portion and a portion not to be soldered for forming a diffusion preventing area in which melted solder rarely diffuses due to low wetting property with respect to the solder.
By such a configuration, the diffusion of the melted solder proceeding along the surface of the gold plating layer or the metal alloy plating layer including gold from the terminal portion stops at a boundary between the surface of the gold plating layer or the metal alloy plating layer including gold and the diffusion preventing area, so that the diffusion of the melted solder proceeds no more. Thus, the diffusion of the melted solder rarely reaches to the contacting portion. Furthermore, the diffusion of the melted solder stops at the boundary of the diffusion preventing area, so that it is secured that a predetermined quantity of the solder remains in the vicinity of the terminal portion, and it is assured that the terminal portion and a wiring pattern on a printed circuit board has a sufficient connecting strength. Still furthermore, it is no need to carry out the partial plating as the gold plating layer or the metal alloy plating layer including gold, so that the productivity can be maintained without reducing the conveying speed of the semi-finished blank in the manufacturing processes of the element to be soldered such as the contact.
The diffusion preventing area is formed by the irradiation of the laser beams to the surface of the gold plating layer or the metal alloy plating layer including gold. When a part of or all of the gold plating layer or the metal alloy plating layer including gold at a portion where the laser beam is irradiated is evaporated and removed, the foundation plating layer is unsheathed. Alternatively, when gold and a material of the foundation plating layer are alloyed, the metal alloy layer is unsheathed. Still alternatively, when a material except gold of the metal alloy including gold is diffused on the surface, the diffused layer is unsheathed. The foundation plating layer, the metal alloy layer and the diffused layer respectively have low wetting property with respect to the solder, so that the diffusion of the melted solder proceeding along the surface of the gold plating layer or the metal alloy plating layer including gold from the terminal portion stops at the boundary of the diffusion preventing area.
Description in Common with the Embodiments
Common portions in the embodiments of the present invention are described with reference to an example of a connector having a stacking height about 1 mm which is used in a mobile equipment such as a mobile phone or a digital still camera. A contact for the connector is described as an example of an element to be soldered. It, however, is not limited by this embodiment, and it is needless to say that it can be applied to another element to be soldered.
A configuration of a socket, which constitutes a connector, is shown in
A side face of the contact 1 is shown in
A state of mounting the socket 100 on a printed circuit board 110 is shown in
As mentioned above, since the contact 1 of the connector for mobile equipment is very small, a semi-finished blank 12, on which a lot of contacts 1 are arranged at a predetermined pitch, is manufactured in a manner so that a side of band metal plate is formed like teeth of a comb, and the teeth portion is bent to be a predetermined shape, as shown
After forming the gold plating layer on the entire surface of the contact 1 including the terminal portion 2 and the contacting portion 3, the diffusion preventing area 6 is formed when a process, which will be described in each embodiment, is carried out at a portion between the terminal portion 2 and the contacting portion 3. The position of the diffusion preventing area 6 is not limited, so that it can be positioned at any portion between the terminal portion 2 and the contacting portion 3. In consideration of connecting strength of the terminal portion 2 and the wiring pattern on the printed circuit board 110, the diffusion of the solder, however, should be made smaller. Thus, it is preferable to provide the diffusion preventing area 6 at a position near to the terminal portion 2.
After forming the diffusion preventing area 6 between the terminal portion 2 and the contacting portion 3, the semi-finished blank 12 is press fitted or inserted into the socket base 101 as it is. After each contact 1 is fixed on the socket base 101, the contact 1 is cut off from the semi-finished blank 12. As a result, the socket 100 is completed. Subsequently, the socket 100 is disposed on the printed circuit board 110, as shown in
Even though the melted solder diffuses on the surface of the gold plating area 4 of the terminal portion 2, the diffusion of the melted solder stops at the boundary between the diffusion preventing area 4 (SIC) and the gold plating area 4 due to low wetting property between the surface of the diffusion preventing area 6 and the solder. Consequently, it is possible to prevent not only the diffusion of the melted solder to the contacting portion 3, but also the reduction of the quantity of the solder remained at the terminal portion 2. Furthermore, the connecting strength of the terminal portion 2 on the printed circuit board 110 can be maintained higher.
Subsequently, a first embodiment of the present invention is described. In the first embodiment, laser beams are irradiated on the surface of the gold plating layer of the contact 1, so that the gold plating layer is partially removed.
As shown in
As shown in
Since the laser beams L are used for removing the gold plating layer 8, it is possible to concentrate the energy in a minute area. Thus, the diffusion preventing area 6 can be formed precisely, even when the contact 1 is much smaller. Furthermore, since the power of the laser beams L can be controlled, it is possible to form the diffusion preventing area 6 precisely in a short time period without removing the nickel plating layer 7 as the foundation plating when the energy condition is properly selected corresponding to the thickness of the gold plating layer 8, and so on.
As the laser beams L, it is preferable to use one, for example, having a wavelength equal to or shorter than 1100 nm, in a range from 0.5 to 5 mJ/pulse of the energy per one pulse and in a range from 100 to 2000 mJ/mm2 of the energy per a unit area. More preferably, it is preferable to use the laser beam in a range equal to or smaller than 3 mJ/pulse of the energy per one pulse and in a range equal to or smaller than 1200 mJ/mm2 of the energy per a unit area.
If the energy of the laser beams L is much larger, there are possibilities that the nickel plating layer 7 below the gold plating layer 8 is further removed, and the material of the contact 1 is melted. For example, when the material of the contact 1 is copper, the copper below the nickel plating layer 7 is unsheathes when the laser beams L having superfluous energy are irradiated. Since the wetting property between copper and solder is higher, it, however, is impossible to prevent the diffusion of the melted solder at the portions where the copper is unsheathed. Furthermore, since copper has low corrosion resistance, the corrosion resistance of the contact will be reduced due to the unsheathing of copper. Accordingly, it is preferable to unsheathe the nickel plating layer 7 owing to removing only the gold plating layer 8 with controlling the energy of the laser beams L, as mentioned above.
Subsequently, a method for irradiating the laser beams L is described. As mentioned above, the contacts 1 are arranged at a predetermined pitch on the side of the semi-finished blank 12. Accordingly, it is necessary to irradiate the laser beams L evenly along circumferences of all the contacts 1 without omission under the condition of the semi-finished blank 12. Thus, the laser beams L are simultaneously irradiated to two sides 1a and 1b which cross substantially at right angle among four sides 1a to 1d of substantially a rectangular section of the contact 1, while the laser beams L are scanned for taking a predetermined angle φ with respect to the conveying direction X of the semi-finished blank 12, as shown in
When the irradiation of the laser beams L with respect to two sides 1a and 1b from one side of the semi-finished blank 12 is completed, the semi-finished blank 12 is turned over or the laser beams L are scanned from the other side of the semi-finished blank 12, and the laser beams L are irradiated to two sides 1c and 1d on the opposite side of the semi-finished blank 12.
Furthermore, the direction for irradiating the laser beams L is slanted by a predetermined angle θ with respect to a plate portion of the semi-finished blank 12 so as not to occur any portion where the laser beams L are not irradiated due to hidden by another portion of the contact 1 such as a flexion 20 (SIC) corresponding to the shape of the contact 1, as shown in
By such the processes, the laser beams L can be irradiated to all the four sides 1a to 1d of each contact 1 of the semi-finished blank 12 evenly and without omission while the scanning of the laser beams L twice.
Subsequently, a width W of the diffusion preventing area 6 functional for preventing the diffusion of the melted solder (see
Various diameters of beam spots can be utilized as the laser beams L. When the laser beam having a diameter of the beam spot smaller than the width W necessary for serving as the diffusion preventing area 6 (for example, 0.05 mm in the example shown in
Subsequently, a relation between the shift quantity B of the laser beams L and a width (overlapping width) H of overlapped portion of the laser beams L irradiated continuously twice while the laser beams L are irradiated with scanning is considered. When it was assumed that the diameter of beam spot of the laser beams L was 0.15 mm, the nugget diameter to be formed would become substantially 0.15 mm, so that variation of the overlapping width H was obtained while the shit quantity B was varied by little and little. The variation is shown in
Hereupon, the overlapping width H is defined by the following equation when the nugget diameter is designated by a symbol D.
H={square root}{square root over (D2−B2)}
It is assumed that the gold plating layer can be removed by the irradiation of the laser beams L in one time. As can be seen from the table 1, it is possible to secure the width of 0/13 mm, which is necessary for functioning the diffusion preventing area 6, when the shift quantity B is made a half of the nugget diameter D, as shown in
Subsequently, a second embodiment of the present invention is described. In the second embodiment, the laser beams L having energy smaller than that of the laser beams L in the above-mentioned first embodiment are irradiated at a portion between the terminal portion 2 and the contacting portion 3 of the contact 1, so that the diffusion preventing area 6 is formed of alloying gold and nickel at the portion where the laser beams L are irradiated.
As shown in
As described in the first embodiment, the energy received from the laser beams L varies from place to place corresponding to the overlap of the laser beams L. Thus, it is possible to form the portions 9 where the nickel plating layer 7 is unsheathed by evaporating the gold plating layer 8 on the surface at the portions receiving higher energy from the laser beams L, and to form the metal alloy layer 8a of gold and nickel at the portions receiving lower energy from the laser beams L, as shown in
Subsequently, a third embodiment of the present invention is described. In the third embodiment, the diffusion preventing area 6 is formed by means of irradiation of the laser beam L after or before acting removing solution 40 of gold at a portion between the terminal portion 2 and the contacting portion 3 of the contact 1. Accordingly, the explanation of the common portion with the above-mentioned embodiments is omitted.
In the method for forming the diffusion preventing area in the third embodiment, the flexion 19 between the terminal portion 2 and the contacting portion 3 of the first (SIC) contact 1 is dipped in the removing solution 40 of gold so that the gold plating layer at the portion is removed, as shown in
The contact 1 to which the foundation plating and the gold plating are carried out is mounted on the jig 14 as a state of the semi-finished blank 12. Since a lot of guide holes 20 are formed on the semi-finished blank 12 at a predetermined interval, the semi-finished blank 12 is positioned and fixed on the jig 14 when the guide holes 20 is fitted to the positioning protrusions 16. The bathtub 15 is designed to have dimensions in a manner so that only the flexion 19 between the terminal portion 2 and the contacting portion 3 which is bent like U-shape is fitted but the contacting portion 3 never be fitted therein. When the terminal portion 2 of the contact 1 is disposed in the jig 14 under a state that the flexion 19 faces downward, the flexion 19 is dipped into the removing solution 40 in the bathtub 15.
When the flexion 19 between the terminal portion 2 and the contacting portion 3 of the contact 1 is dipped in the removing solution 40, gold in the gold plating layer is dissolved as complex owing to oxidative reaction. Accordingly, the gold plating layer of the contact 1 dipped in the removing solution 40 is removed, so that the foundation plating layer is unsheathed.
At that time, even when the removing solution 40 comes up along an inner wall of the bathtub 15 due to surface tension, the removing solution never reaches top the terminal portion 2 according to the opening of the cavity 21 adjoining the jig 14 (SIC). Consequently, it is possible to prevent the removing of the gold plating layer of the terminal portion 2. On the other hand, since the contacting portion 3 is not contacted with the jig 14, as shown in
Gold resolved in the removing solution 40 is collected as complexes state from the removing solution 40. The removing of the gold plating layer owing to the removing solution is carried out while the contacts 1 are on the semi-finished blank 12. It, however, is possible to remove the gold plating layer owing to the removing solution 40 after cutting off the contacts 1 from the semi-finished blank 12, depending on the circumstances.
The kind of the removing solution 40 is not limited, but it is possible to use one including potassium cyanide, nitro compound, lead oxide, or the like, as the major proportions. The time period for dipping the contact 1 in the removing solution 40 is selected in a range from several seconds to several minutes. Specifically, ENSTRIP Au-78M, Meltex Inc. is used as the removing solution 40, and the contact is dipped in about 15 sec.
After removing the gold plating layer of the flexion 19 between the terminal portion 2 and the contacting portion 3 of the contact 1 by this means, the laser beams L are irradiated at the portion where the gold plating layer 8 is removed owing to the method in accordance with the first or second embodiment, so that gold remained at the portion where the laser beams L are irradiated is evaporated or alloyed with nickel. According to the combination of the removing solution 40 and the irradiation of the laser beams L as just described, even if the gold plating layer 8 is not removed completely by the removing solution 40, the remained gold can be removed substantially completely or alloyed with nickel owing to the irradiation of the laser beams L, so that the diffusion preventing area 6 having low wetting property with respect to solder can be formed. Consequently, it is possible to prevent the diffusion of the melted solder from the terminal portion 2 to the contacting portion 3.
The energy of the laser beams L per one pulse and per a unit area can be selected at the discretion in a region by which the nickel plating layer 7 as the foundation plating and the material of the contact 1 (for example, copper) are not melted.
Alternatively to the above-mentioned description, it is possible to irradiate the laser beams L to a part of the flexion 19 between the terminal portion 2 and the contacting portion 3 of the contact 1 at first, and the portion irradiated by the laser beams L is dipped into the removing solution 40, subsequently. Specifically, the laser beams L are irradiated to the surface of the gold plating layer 8 formed on the surface of the contact 1 at a portion between the terminal portion 2 and the contacting portion 3 at first, so that the nickel plating layer 7 as the foundation plating is partially unsheathed by removing a part of gold at the portion or a part of gold at the portion is alloyed with nickel. Subsequently, the flexion 19 between the terminal portion 2 and the contacting portion 3 of the contact 1 is dipped into the removing solution 40 of gold, so that the remained gold after irradiating the laser beams L is removed. Since it is difficult to remove the gold which is alloyed with nickel by processing of removing solution 40, the metal alloy layer 8a of gold and nickel (see
As mentioned above, the gold plating layer 8 can remove substantially completely from the diffusion preventing area 6 by means of the combination of the removing solution 40 and the laser beams L, so that it is possible to prevent the diffusion of the melted solder along the remained gold plating layer 8.
Subsequently, a fourth embodiment of the present invention is described. In the above-mentioned first to third embodiment, the nickel plating layer 7 as the foundation plating and the gold plating layer 8 are formed on substantially entire surface of the contact. In the fourth embodiment, it is different that a gold-nickel (Au—Ni) alloy plating layer 80 is formed on the nickel plating layer 7 as the foundation plating, as shown in
The semi-finished blank 12, which is processed as shown in
The kind of the nickel plating solution is not limited. For example, when nickel sulfamic acid plating solution is used, it is possible to increase electric current density, so that the productivity can be increased. The nickel plating layer 7 is formed so that the thickness of the layer becomes in a range from 0.3 to 10 μm. Furthermore, the kind of the gold-nickel alloy plating solution is not limited. For example, it is preferable to use one having the eutectoid ratio of gold: nickel is in a range from 70:30 to 99.9˜0.1 (SIC). As an example of the gold-nickel alloy plating solution, the products of NIKKO metal plating Co. Ltd., can be used. The gold-nickel alloy plating layer 80 is formed in a manner so that the thickness of the layer becomes in a range from 0.01 to 0.5 μm.
After forming the nickel plating layer 7 and the gold-nickel alloy plating layer 80 are formed on substantially entire surface of the contact 1, the laser beams L are irradiated at a portion where the diffusion preventing area 6 of the melted solder is to be formed, as shown in
Since the nickel plating layer 7 has the wetting property much lower than that of the gold-nickel alloy plating layer 80, owing to the diffusion preventing area 6, where the nickel plating layer 7 is unsheathed, formed between the terminal portion 2 and the contacting portion 3 of the contact 1, the diffusion of the solder is stopped at the diffusion preventing area 6, that is, at the boundary between the unsheathed nickel plating layer 7 and the gold-nickel alloy plating layer 80, even when the melted solder diffuses along the surface of the gold-nickel alloy plating layer 80 from the terminal portion 2, and the solder diffuses no more. Consequently, it is possible to prevent the diffusion of the solder to the contacting portion 3 and insufficient quantity of the solder remains at the terminal portion 2. Furthermore, the connecting strength of the terminal portion 2 on the printed circuit board 110 can be maintained higher.
For example, in the above-mentioned second embodiment, the metal alloy layer 8a of gold and nickel is formed owing to irradiation of the laser beams L to the gold plating layer 8, as shown in
Furthermore, it is possible to form a diffusion layer 81, where nickel in the gold-nickel alloy plating layer 80 is diffused on a surface thereof, at a portion on the gold-nickel alloy plating layer 80 irradiated by the laser beams L owing to adjusting the power of the laser beam L, as shown in
Furthermore, it is possible to unsheathe the nickel plating layer 7 by evaporating the gold-nickel alloy plating layer 80 on the surface at portions 9 where the energy received from the laser beams L is higher, and to form diffusion layers 81 by diffusing nickel in the gold-nickel alloy at portions where the energy received from the laser beams L is smaller, as shown in
Subsequently, a fifth embodiment of the present invention is described. In the above-mentioned fourth embodiment, the nickel plating layer 7 as the foundation plating is formed on substantially entire surface of the contact 1, and the gold-nickel (Au—Ni) alloy plating layer 8 (SIC) is further formed on the nickel plating layer 7. In the fifth embodiment, a palladium-nickel (Pd—Ni) alloy plating layer 70 is further formed on the nickel plating layer 7 as the foundation plating, and the gold-nickel (Au—Ni) alloy plating layer 80 is formed on the palladium-nickel alloy plating layer 70.
The semi-finished blank 12, on which a lot of contacts 1 are arranged at a predetermined pitch, is dipped into nickel plating solution while it is conveyed in lengthwise direction, so that the nickel plating layer 7 as the foundation plating is formed on entire surface of the contact 1. Subsequently, the semi-finished blank 12 is dipped into palladium-nickel alloy plating solution while it is conveyed in lengthwise direction, so that the palladium-nickel alloy plating layer 70 is formed on the nickel plating layer 7. Furthermore, the semi-finished blank 12 is dipped into gold-nickel alloy plating solution while it is conveyed in lengthwise direction, so that the gold-nickel alloy plating layer 80 is formed on the palladium-nickel alloy plating layer 70 on the entire surface of the contact 1.
The kind of the nickel plating solution is not limited. For example, when nickel sulfamic acid plating solution is used, it is possible to increase electric current density, so that the productivity can be increased. The nickel plating layer 7 is formed so that the thickness of the layer becomes in a range from 0.3 to 10 μm. Furthermore, the kind of the palladium-nickel alloy plating solution is not limited, so that it is preferable to select one by which the electric current density can be increased and the productivity can be increased. The palladium-nickel alloy plating layer 70 is formed so that the thickness of the layer becomes ion a range from 0.01 to 1.0 μm. Still furthermore, the kind of the gold-nickel alloy plating solution is not limited. For example, it is preferable to use one having the eutectoid ratio of gold: nickel is in a range from 70:30 to 99.9˜0.1 (SIC). As an example of the gold-nickel alloy plating solution, the products of NIKKO metal plating Co. Ltd., can be used. The gold-nickel alloy plating layer 80 is formed in a manner so that the thickness of the layer becomes in a range from 0.01 to 0.5 μm.
After forming the nickel plating layer 7 (SIC) and the gold-nickel alloy plating layer 80 are formed on substantially entire surface of the contact 1, the laser beams L are irradiated at a portion where the diffusion preventing area 6 of the melted solder is to be formed, as shown in
Since the palladium-nickel alloy plating layer 70 has the wetting property much lower than that of the gold-nickel alloy plating layer 80, the diffusion preventing area 6 is formed by unsheathing the palladium-nickel alloy plating layer 70 at a portion between the terminal portion 2 and the contacting portion 3 of the contact 1. Even if the melted solder diffuses along the surface of the gold-nickel alloy plating layer 80 from the terminal portion 2, the diffusion of the solder is stopped at the diffusion preventing area 6, that is, at the boundary between the unsheathed palladium-nickel alloy plating layer 70 and the gold-nickel alloy plating layer 80, so that the solder diffuses no more. Consequently, it is possible to prevent the diffusion of the solder to the contacting portion 3 and insufficient quantity of the solder remains at the terminal portion 2. Furthermore, the connecting strength of the terminal portion 2 on the printed circuit board 110 can be maintained higher.
Furthermore, the palladium-nickel alloy layer 70 is superior to the nickel plating layer 7 as the foundation plating with respect to the corrosion resistance. It, however, is possible to increase the corrosion resistance than the case for unsheathing the nickel plating layer 7, even though the number of steps in the plating process is increased.
Furthermore, it is possible to form a diffusion layer 81, where nickel in the gold-nickel alloy plating layer 80 is diffused on a surface thereof, at a portion on the gold-nickel alloy plating layer 80 irradiated by the laser beams L owing to adjusting the power of the laser beam L, as shown in
Furthermore, it is possible to unsheathe the palladium-nickel alloy plating layer 70 by evaporating the gold-nickel alloy plating layer 80 on the surface at portions 9 where the energy received from the laser beams L is higher, and to form diffusion layers 81 by diffusing nickel in the gold-nickel alloy at portions where the energy received from the laser beams L is smaller, as shown in
In the above-mentioned embodiments including the irradiation process of the laser beams L, there might be the case that impurity such as carburet is adhered on the surface between the terminal portion 2 and the contacting portion 3 of the contact 1 after irradiating the laser beams L. When such the impurity is left as it is, it will cause the obstruction in after-treatment, so that it is difficult to obtain the contact 1 having high reliability. Thus, when the laser beams L are irradiated at a portion between the terminal portion 2 and the contacting portion 3, it is possible to dip the portion into cleaning fluid 23 with using, for example, the jig 14 shown in
Furthermore, the above-mentioned embodiments describe the cases for forming the diffusion preventing area of melted solder on the contact for a connector. The present invention, however, is not limited in this use, and it is possible to apply to, for example, electrically conductive leads provided on a package of a surface mounting semiconductor device. That is, the package of the surface mounting semiconductor device is used as an element to be mounted on the printed circuit board, similar to the connector. The mounting of the package of the surface mounting semiconductor device is carried out that the package is disposed above the printed circuit board, and the front ends of the leads provided on the package are soldered on the printed circuit board. In this case, it is possible to prevent the diffusion of the melted solder from the front ends of the leads to bases (roots) of the leads.
This application is based on Japanese patent applications 2002-297880, 2003-114759 and 2003-185748 filed in Japan, the contents of which are hereby incorporated by references.
Although the present invention has been fully described by way of example with reference to the accompanying drawings, it is to be understood that various changes and modifications will be apparent to those skilled in the art. Therefore, unless otherwise such changes and modifications depart from the scope of the present invention, they should be construed as being included therein.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2002-297880 | Oct 2002 | JP | national |
| 2003-114759 | Apr 2003 | JP | national |
| 2003-185748 | Jun 2003 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP03/13094 | 10/10/2003 | WO |