Claims
- 1. A spin-orientation process for preparing a bundle of polyester continuous filaments that are hollow, having one or more longitudinal voids, and being of void content (VC) at least about 10%; wherein said hollow filaments are formed by a melt-spinning process comprising the steps of: i) melting polyester polymer of about 13 to about 23 LRV and with a zero-shear melting point (T.sub.M .degree.) of about 240 to about 265 C, and a glass transition temperature (T.sub.g) of about 40 C to about 80 C; (ii) extruding the resulting melt through a plurality of segmented orifices arranged so as to provide an extrusion void area (EVA) of about 0.2 mm.sup.2 to about 2 mm.sup.2, and so that the ratio of EVA to total extrusion area (EA) is about 0.6 to about 0.9 such that the ratio of EVA to spun filament denier (dpf).sub.s is about 0.2 to about 0.6, and post-coalescing the resulting plurality of extruded polyester melt streams to form uniform hollow filaments; (iii) quenching the extruded melt-streams using a protective delay shroud; (iv) converging the quenched hollow filaments into a multi-filament bundle while applying spin finish; and (v) withdrawing the multi-filament bundle at a withdrawal speed (V.sub.S) in a range of about 2000 to about 5000 m/min; such process conditions being selected to provide an as-spun filament bundle having: a residual elongation of about 40% to about 160%, tenacity-at-7% elongation (T.sub.7) of about 0.5 to about 1.75 g/d and a break tenacity (T.sub.B).sub.n, normalized to 20.8 polymer LRV, of at least 5g/d, a (1-S/S.sub.m)-ratio of at least 0.4 and differential shrinkage (DHS-S) less than about +2%, where S is the boil-off shrinkage, S.sub.m is the maximum shrinkage potential and DHS is the dry heat shrinkage (measured at 180 C), and a maximum shrinkage tension (ST.sub.max) of less than 0.2 g/d at a peak shrinkage tension temperature T(ST.sub.max) of about 5 to about 30 C greater than about the polymer glass transition temperature (T.sub.g).
- 2. A process according to claim 1, wherein spun filament denier (dpf).sub.s, polymer LRV, polymer zero-shear melting point (T.sub.M .degree.), polymer spin temperature (T.sub.p), orifice EVA, and withdrawal speed (V.sub.S) parameters are selected to provide as-spun yarn being characterized by a residual elongation of about 90% to about 120% and a tenacity-at-7% elongation (T.sub.7) of about 0.5 to about 1 g/d, such that the tenacity-at-7% elongation (T.sub.7) of about 0.5 to about 1 g/d, such that the tenacity-at-20% elongation (T.sub.20) is at least as high as the T.sub.7, and wherein said as-spun filament bundle is interlaced.
- 3. A process according to claim 1, wherein spun filament denier (dpf).sub.s, polymer LRV, polymer zero-shear melting point (T.sub.M .degree.), polymer spin temperature (T.sub.p), orifice EVA, and withdrawal speed (V.sub.S) parameters are selected to provide as-spun yarn having a residual elongation of about 40% to about 90%, a tenacity-at-7% elongation (T.sub.7) of about 1 to about 1.75 g/d, and a (1-S/S.sub.m)-ratio of at least about 0.85, and wherein said as-spun filament bundle is interlaced.
- 4. A process according to any one of claims 1 to 3, wherein spun filament denier (dpf).sub.s, polymer LRV, polymer zero-shear melting point (T.sub.M .degree.), polymer spin temperature (T.sub.p), orifice EVA, and withdrawal speed (V.sub.S) parameters are selected to provide a value of at least about 1 for the expression:
- {(k[LRV (T.sub.M .degree./T.sub.p).sup.6 ][V.sub.S.sup.2 (dpf).sub.s ][(EVA).sup.1/2).sup.n },
- where k has a value of about 10.sup.-7, and the exponent "n" is the product [(S/T)(L/W)] where S and T are inbound and outbound entrance angles, respectively, to slots forming the segmented orifices, and L and W are the orifice slot depth and slot width, respectively, and wherein the filament void content (V.sub.c) from said process is at least about 10% and at least about
- K.sub.p Log.sub.10 {(k[LRV(T.sub.M .degree./T.sub.p).sup.6 ][V.sub.S.sup.2 (dpf).sub.s ][(EVA).sup.1/2).sup.n },
- where Kp is a characteristic material constant for the selected polyester having a value of about 10 for poly(ethylene terephthalate)-based polymers.
- 5. A process according to claim 4, wherein the parameters are selected to provide a value of at least about 10 for the expression
- {(k[LRV(T.sub.M .degree./T.sub.p).sup.6 ][V.sub.S.sup.2 (dpf).sub.s ][(EVA).sup.1/2).sup.n }.
- 6. A process according to claim 1 or 2, wherein said as-spun filament bundle is interlaced, drawn and heat set to provide a uniform drawn yarn having a residual elongation of about 15% to about 40%, a tenacity-at-7% elongation (T.sub.7) at least about 1 g/d, and a (1-S/S.sub.m)-value at least about 0.85.
- 7. A process according to claim 3, wherein one or more uniform drawn polyester continuous hollow filament yarns of residual elongation about 15% to about 55%, of tenacity-at-7% elongation (T.sub.7) at least about 1 g/d, and of (1-S/S.sub.m)-value at least about 0.85, are prepared by cold or hot-drawing said as-spun filament bundles, with or without post heat treatment, under conditions selected whereby there is essentially no loss in filament void content (VC) during said drawing.
- 8. A process according to claim 1 or 2, wherein said as-spun filament bundle is drawn at a temperature between the glass-transition temperature (T.sub.g) and the temperature of onset of major crystallization of the polymer (T.sub.c .degree.), where T.sub.c .degree. is defined by [0.75(T.sub.M .degree.+273)-273], without heat setting, to provide a uniform drawn yarn having a residual elongation (E.sub.B) of about 15% to about 40%, a tenacity-at-7% elongation (T.sub.7) at least about 1 g/d, and a (1-S/S.sub.m)-value of about 0.4 to about 0.85.
- 9. A process according to claim 1, wherein the process conditions are selected to provide an interlaced mixed-filament yarn of as-spun filaments of two or more different types, whereby at least one such filament type has a shrinkage S such that the (1-S/S.sub.m)-value is greater than 0.85 and at least another such filament type has a shrinkage S such that the (1-S/S.sub.m)-value is in the range 0.4 to 0.85.
- 10. A process according to claim 9, wherein the resulting as-spun mixed-filament yarn is drawn to a residual elongation (E.sub.B) of about 15% to about 40% at a draw temperature (T.sub.D) between the glass transition temperature of the polymer (T.sub.g) and the temperature of onset of major crystallization of the polymer (T.sub.c .degree.) where T.sub.c .degree. is defined by [0.75(T.sub.M .degree.+273)-273], without heat setting, to provide a mixed-shrinkage drawn yarn comprised of two or more different types of filaments wherein at least one such filament type has a high shrinkage S such that the (1-S/S.sub.m)-value is at least about 0.85 and at least another such filament type has a low shrinkage S such that the (1-S/S.sub.m)-value is in the range 0.4 to 0.85 and such that the shrinkages of such filament types differ by at least about 5% and said drawn yarn has a maximum shrinkage tension (ST.sub.max) such that the product of the difference in shrinkages of the high and low shrinkage filament types and of the yarn maximum shrinkage tension (ST.sub.max) is at least about 1.50 (g/d)%, and wherein said drawn yarn has a tenacity-at-break (T.sub.B), normalized to 20.8 polymer LRV, of at least 5 g/d and a tenacity-at-7% elongation (T.sub.7) of at least about 1 g/d.
- 11. A process according to claim 9 or 10, wherein the resulting mixed-shrinkage yarn is heat-relaxed to provide a bulky yarn.
- 12. A process according to claim 6, wherein said as-spun filament bundle is drawn by a drawing process that incorporates air-jet texturing to provide a bulky drawn yarn.
- 13. A process according to claim 7, wherein said as-spun filament bundle is drawn by a drawing process that incorporates air-jet texturing to provide a bulky drawn yarn.
- 14. A process according to claim 6, wherein said as-spun filament bundle is drawn by a drawing process that incorporates false-twist texturing at a draw temperature between a maximum rate of crystallization of the polymer (T.sub.c,max) and 20 C less than the onset of melting (T.sub.M '), where T.sub.c,max is defined by [0.85(T.sub.M .degree.+273)-273] and T.sub.M ' is measured by conventional DSC at a heating rate of 20 C per minute, wherein filament voids partially or completely collapse during said texturing to produce filament cross-sections of different shape.
- 15. A process according to claim 7, wherein said as-spun filament bundle is drawn by a drawing process that incorporates false-twist texturing at a draw temperature between a maximum rate of crystallization of the polymer (T.sub.c,max) and 20 C less than the onset of melting (T.sub.M '), where T.sub.c,max is defined by [0.85(T.sub.M .degree.+273)-273] and T.sub.M ' is measured by conventional DSC at a heating rate of 20 C per minute, wherein filament voids are partially or completely collapsed during said texturing to produce filament cross-sections of different shape.
- 16. A process according to claim 9 or 10, comprising the step of air-jet texturing, without post heat treatment, to provide a bulky yarn.
- 17. A process according to claim 8, wherein the drawing step incorporates air-jet texturing to provide a bulky yarn of high shrinkage hollow filaments.
- 18. A process according to any one of the claims 1, 2, 3, 7, 9, 10, 13, or 15, wherein the as-spun hollow filaments are of denier about 1 to about 3, of elongation-to-break about 40% to about 120% and of shrinkage S such that the (1-S/S.sub.m)-value is at least about 0.6.
- 19. A process according to claim 12, wherein the as-spun hollow filaments are of denier about 1 to about 3, of elongation-to-break about 40% to about 120% and of shrinkage S such that the (1-S/S.sub.m)-value is at least about 0.6.
- 20. A process according to claim 17, wherein the as-spun hollow filaments are of denier about 1 to about 3, of elongation-to-break about 40% to about 120% and of shrinkage S such that the (1-S/S.sub.m)-value is at least about 0.6.
- 21. A process according to claim 14, wherein the as-spun hollow filaments are of denier about 1 to about 3, of elongation-to-break about 40% to about 120% and of shrinkage S such that the (1-S/S.sub.m)-value is at least about 0.6.
CROSS-REFERENCE TO RELATED APPLICATIONS
This is a continuation-in-part of copending applications 07/753,529 and 07/753,769, both filed by Knox et al., Sep. 3, 1991, now U.S. Pat. Nos. 5,261,472 and 5,229,060, respectively, and of the following four copending applications, that were all filed Nov. 1, 1991, Ser. No. 07/786,582, filed by Hendrix et al, and now U.S. Pat. No. 5,244,616, Ser. No. 07/786,583, filed by Hendrix et al, and now U.S. Pat. No. 5,145,623, Ser. No. 07/786,584, filed by Boles et al, now U.S. Pat. No. 5,223,197, Ser. No. 07/786,585, filed by Frankfort et al, now U.S. Pat. No. 5,223,198, all filed as continuations-in-part of application 07/338,251, filed Apr. 14, 1989, now U.S. Pat. No. 5,066,447, and which is sometimes referred to herein as the "parent application", being itself a continuation-in-part of abandoned application 07/053,309, filed May 22, 1987, itself a continuation-in-part of abandoned application 06/824,363, filed Jan. 30, 1986; and is also a continuation-in-part of copending applications 07/925,042, filed by Aneja et al, and 07/925,041 and 07/926,538 (all three now abandoned) filed by Bennie et al, all three filed Aug. 5, 1992 as continuations-in-part of abandoned application 07/647,381, filed by Collins et al, Jan. 29, 1991, and of abandoned application 07/860,776, filed by Collins et al, Mar. 27, 1992, as a continuation-in-part of abandoned application No. 07/647,371, also filed Jan. 29, 1991.
US Referenced Citations (2)
Number |
Name |
Date |
Kind |
5223198 |
Frankfort et al. |
Jun 1993 |
|
5250245 |
Collins et al. |
Oct 1993 |
|
Foreign Referenced Citations (1)
Number |
Date |
Country |
3011118 |
Oct 1981 |
DEX |
Related Publications (16)
|
Number |
Date |
Country |
|
753769 |
Sep 1991 |
|
|
786582 |
Nov 1991 |
|
|
786583 |
Nov 1991 |
|
|
786584 |
Nov 1991 |
|
|
786585 |
Nov 1991 |
|
|
925042 |
Aug 1992 |
|
|
925041 |
Aug 1992 |
|
|
926538 |
Aug 1992 |
|
|
925041 |
|
|
|
926538 |
|
|
|
860776 |
Mar 1992 |
|
|
753769 |
|
|
|
786582 |
|
|
|
786583 |
|
|
|
786584 |
|
|
|
786585 |
|
|
Continuation in Parts (6)
|
Number |
Date |
Country |
Parent |
753529 |
Sep 1991 |
|
Parent |
647381 |
Jan 1991 |
|
Parent |
647371 |
Jan 1991 |
|
Parent |
338251 |
Apr 1989 |
|
Parent |
53309 |
May 1987 |
|
Parent |
824363 |
Jan 1986 |
|