Patent Application
20050126481
The present invention relates to a process for retaining solid adsorbent particles such as carbon or APS silica gel in the micro-cavities of shaped fibers for subsequent use in filter applications such as cigarette filters that selectively remove or reduce certain components from mainstream tobacco smoke, for example.
Over the years a wide variety of fibrous materials have been employed in tobacco smoke filter elements. Cellulose acetate (“CA”) has long been considered the material of choice for this application. However, the choice of materials has been limited because of the need to balance various commercial requirements. A very important property is the filtration efficiency i.e. the ability to selectively remove or reduce certain components from mainstream tobacco smoke.
To achieve appropriate filtration efficiency, materials such as carbon and APS silica gel have been incorporated into cigarette filters. A current method for incorporating adsorbent materials in cigarette filters is the physical entrapment of adsorbent particles between CA fibers. The particle size of materials used is generally limited and in the range of 500 to about 1500 microns in diameter. In order to achieve reasonable product integrity and pressure drop, smaller particles could not be used in this design. In addition, the adsorbents were found to lose activity from exposure to triacetin, a plasticizer used as a binder for the CA fibers.
An improved and more expensive design is to put certain materials such as carbon in the cavity between CA plugs in a Plug/Space/Plug (P/S/P) filter configuration to limit the exposure of adsorbent to the binder. In order to keep the pressure drop through the filter within acceptable limits, coarse granulated materials in the size range of about 10 to about 60 mesh are generally used. A longer shelf life of the adsorbent is achieved, but the efficiency of the filters is limited by the relatively large particle size used. Finer size adsorbent particles with shorter internal diffusive paths and higher effective surface areas cannot be used directly in this configuration due to excessive pressure drop.
Smaller particle size adsorbent materials generally have enhanced kinetics of reaction with gas phase components because of their shorter diffusion paths to the interior surface area of such porous materials and the interior body of such adsorbent materials. It was known that employing smaller adsorbent particles with shorter diffusion paths can form filters with improved kinetics and capacity for gas phase filtration applications.
As explained in application Ser. No. 09/839,669, filed Apr. 20, 2001, and incorporated herein by reference in its entirety for all useful purposes, a fiber with open or semi-open micro-cavities is desirable for holding in place the adsorbent material such as carbon. The term “semi-open cavities” as used herein means cavities that possess openings smaller in dimension than the internal volume of the fiber in which they are formed, and that possess the ability to entrap solid fine particles in their internal volume. The term “open cavities” means the opening is the same or bigger in dimension than the internal volume of the fiber in which they are formed.
A primary object of the present invention is a continuous process for producing large quantities of shaped micro-cavity fibers with fine solid adsorbent particles such as carbon or APS silica gel on the fibers for subsequent filtration applications.
Another object of the present invention is a continuous process which is simple but highly efficient in adhering fine solid adsorbent particles such as carbon or APS silica gel onto shaped micro-cavity fibers by applying an electrostatic charge to the fibers.
In accordance with the present invention, a continuous process produces large quantities of micro-cavity fibers coated with adsorbent fine particles such as carbon or APS silica gel. The general concept of the process is to expose a continuous shaped fiber to an electrostatic charge and then draw the charged fiber through a reservoir that contains particles suitable for coating the fiber and impregnating into the micro-cavities thereof. Any excess particles on the fiber surface may be removed by vibrating the fiber over a free drawing distance or by exposing the fiber to an impact gas flow. The gas stream to remove the excess particles may be an air stream from a pressured or vacuum source.
In accordance with the present invention, a process of retaining fine adsorbent particles onto and in the micro-cavities of a shaped fiber comprises the steps of continuously conveying such shaped fiber to a charging arrangement where the fiber is electrostatically charged. The charged fiber is then drawn through a reservoir of fine adsorbent particles such as carbon or APS silica gel, for example. The shaped fiber passes through the reservoir thereby producing relative motion between the fiber and the particles, and such relative motion causes the particles to adhere to the micro-cavities of the charged fiber. Any excess particles are removed from the fiber outside the reservoir, and the shaped fiber loaded with the fine adsorbent particles is subsequently collected for use in filter applications such as cigarette filters.
Preferably the step of removing any excess particles from the fiber outside the reservoir includes directing an air stream onto the fiber from a pressurized or vacuum source. The excess particles so removed from the fiber are preferably recycled back to the reservoir. Moreover, the step of collecting the particle laden fiber may include winding the fiber onto a winding wheel thereby producing a generally circular bundle of fibers. Such circular bundle of fibers may be flattened and the end portions of the flattened bundle cut away so that the remaining fibers are aligned with one another in a particularly useful form for filter applications.
The charged fiber may be repeatedly passed through the reservoir to increase the amount of adsorbent particles adhering to the fiber. Also, it is preferred that the fiber be drawn through the reservoir of fine adsorbent particles at a speed in the range of 5 to 15 m/min, preferably 10 m/min.
Novel features and advantages of the present invention in addition to those mentioned above will become apparent to persons of ordinary skill in the art from a reading of the following detailed description in conjunction with the accompanying drawings wherein similar reference characters refer to similar parts and in which:
Referring in more particularity to the drawings,
Upon exit of the particle laden fibers from the reservoir any excess particles may be removed by directing an air stream 28 onto the fibers from a pressurized or vacuum source 30, 32. Mechanical vibration 34 may also be used for this purpose. The removed excess particles may be recycled via line 13. Ultimately, the particle laden fibers 12, 14 are collected and subsequently processed for use in filter applications such as cigarette filters.
Shaped fibers with micro-cavities are described in U.S. Pat. No. 5,057,368 which is incorporated by reference in its entirety for all useful purposes. This patent describes shaped micro-cavity fibers that are multilobal such as trilobal or quadrilobal. Other US patents which describe shaped micro-cavity fibers include U.S. Pat. Nos. 5,902,384; 5,744,236; 5,704,966 and 5,713,971, each of which is incorporated by reference in its entirety including the drawings thereof. In addition, U.S. Pat. Nos. 5,244,614 and 4,858,629 specifically disclose multilobal fibers, and these patents are incorporated by reference in their entirety for all useful purposes.
Suitable fine particles 14 include, but are not limited to, carbons, aluminas, silicates, molecular sieves, zeolites, and metal particles. The carbon used can be, but is not limited to, wood based, coal based or coconut shell based or derived from any other carbonaceous material such as petroleum pitch. Optionally, the material may be treated with desired chemical reagents, so as to modify the particle surfaces to include a particular functional group or functional structure. Coconut shell carbon powder available from Pica and a powdered Amino Propyl Silyl (APS) Silica Gel are particle examples. Carbon in spherical beaded form may also be utilized.
The charging voltage may be between 24 kV and 30 kV while the distance from the corona tip 64 to ground copper electrode plate 68 may be about 28 mm. This is high enough to produce corona without breakdown. A sample mat of fibers 12 is laid on top of the copper ground plate. The fiber sample is charged at room temperature for varying periods depending on the sample size and particle being used.
The retention capacity for APS silica gel powder in a micro-cavity fiber at various exposure times is summarized in Table 1 below.
The particle retention percentage is calculated by subtracting the initial weight of the fiber from the weight of the fiber loaded with APS silica gel, dividing by the initial weight of the fiber and multiplying by 100.
From the results shown in Table 1, it is clear that the retention capability of the fiber used (4-DG PP Fiber DPL-283) for APS powder was greatly enhanced by charging the fiber mat. Longer charging time produces increased static charge, and more charge produces higher particle retention. However, saturation occurs after 30 minutes charging time. The 4-DP PP Fiber DPL-283 is a deep groove polypropylene fiber available from Fiber Innovative Technologies. This fiber will be referred to hereafter as 4-DG PP.
The diagrammatic perspective view of a charged micro-cavity fiber retaining solid particles 14 is shown in
The shaped fibers laden with carbon may be directly transported to a plug maker (not shown) for producing cigarette filter plugs for attachment to tobacco rods in the manufacturing of cigarettes. Alternatively, as shown in
Curve 110 shows the delivery of a standard IR4F reference cigarette a while the remaining curves illustrate the delivery performance of other cigarette constructions. Curve 112 shows the performance of a cigarette having a filter constructed of 4-DG PP fiber without any particulate loading. The hydrogen cyanide delivery is slightly higher across all puffs. Curves 114 and 116 show the greatly reduced delivery of cigarette filters constructed with 4-DG PP micro-cavity fiber loaded with APS silica gel and carbon, respectively. Loading was done after the fiber was electrostatically charged.
It should be understood that the above detailed description while indicating preferred embodiments of the invention are given by way of illustration only since various changes and modifications within the spirit and scope of the invention will become apparent to those skilled in the art from the detailed description. For example, other shaped fibers with micro-cavities may be loaded with adsorbent material after initially being electrostatically charged.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 10336951 | Jan 2003 | US |
| Child | 11044518 | Jan 2005 | US |