The present disclosure relates to a continuous production-type 3D printing method, and more particularly, to a continuous production-type 3D printing method includes repeatedly performing a printing process of installing a build platform on a conveyor belt made of a metallic material, such that the build platform is inclined at a predetermined angle with the top surface of the conveyor belt, applying a photocurable ink composition layer by layer onto the top surface of the build platform, and selectively curing the applied photocurable ink composition by emitting a light pattern thereto through a light emitting unit. During the printing process, a printed matter block stacked on the conveyor belt is transferred in one direction by the conveyor belt, according to the pace of the printing process, such that a printing space for a subsequent layer can be continuously secured through the transfer of the printed matter block. Thus, the 3D printing method can continuously output printed matters without a separate additional process such as a replacement operation of the build platform, and simultaneously change the shape of an output printed matter at any time through a simple operation of changing the light pattern emitted by the light emitting unit, during the printing process, thereby significantly improving the efficiency of the printing operation and the diversity of printed matters.
Recently, the 3D printing industry is rapidly settling down as a new industry, and actively widening its range of application in each industry. 3D printing is also referred to AM (Additive Manufacturing), and refers to a process of producing a 3D object by stacking materials using digital design data. Examples of 3D object producing technologies according to the related art may include a subtractive manufacturing method capable of manufacturing a 3D object by cutting and trimming a solid material through a machining process or the like. However, the 3D printing method includes a process of manufacturing a 3D object by stacking printing materials step by step.
As an example of such a 3D printing method, Korean Patent Application Publication No. 10-2018-0125910 has disclosed an SLA (Stereolithography) method. As illustrated in
However, the batch-type 3D printing method according to the related art arranges the printed matter on a virtual 3D block, having an area to which the printed matter is applied and a height at which the printed matter layers are stacked on the surface of the build platform, slices the printed matter into a plurality of layers, derives a light emitting pattern for each of the layers, and then repeatedly performs a process of applying the ink composition layer by layer according to the derived light emitting pattern and curing the ink composition through light emission, until the height of the layers reach a predetermined height, thereby producing a 3D printed matter. Therefore, such a batch-type 3D printing method has problems in that a printed matter cannot be changed during one batch of printing process once the batch of printing process is started, and printing can be started only after the above-described 3D virtual block is filled with sufficient printed matters to raise the efficiency of printing facilities. Furthermore, the batch-type 3D printing method inevitably requires a down time for printing facilities attributable to post processing. For example, after one batch of printing process is ended, the printed matter needs to be collected, and the build platform needs to be reorganized. Therefore, the entire producing speed of a 3D printed product may be delayed, and the batch-type 3D printing method may have many limitations in terms of the diversity of printed matters handled thereby.
Various embodiments are directed to a continuous production-type 3D printing method includes include repeatedly performing a printing process of installing a build platform on a conveyor belt made of a metallic material, such that the build platform is inclined at a predetermined angle with the top surface of the conveyor belt, applying a photocurable ink composition layer by layer onto the top surface of the build platform, and selectively curing the applied photocurable ink composition by emitting a light pattern thereto through a light emitting unit. During the printing process, a printed matter block stacked on the conveyor belt is transferred in one direction by the conveyor belt, according to the pace of the printing process, such that a printing space for a subsequent layer can be continuously secured through the transfer of the printed matter block. Thus, the 3D printing method can continuously output printed matters without a separate additional process such as a replacement operation of the build platform, and simultaneously change the shape of an output printed matter at any time through a simple operation of changing the light pattern emitted by the light emitting unit, during the printing process, thereby significantly improving the efficiency of the printing operation and the diversity of printed matters.
In an embodiment, there is provided a 3D printing method using a photocurable ink composition which exists as liquid at a predetermined phase-change temperature or higher, but hardens to a solid at a low temperature equal to or lower than the phase-change temperature. The 3D printing method may include: installing a build platform on one side of the top of a conveyor belt which is driven in one direction through a pulley, such that the build platform is inclined at a predetermined angle with the top surface of the conveyor belt; applying a photocurable ink composition layer by layer onto the top surface of the inclined build platform; selectively curing the applied photocurable ink composition layer by emitting a light pattern onto the ink composition layer through a light emitting unit; producing a 3D printed matter through printed matter layers which are repeatedly stacked in a direction indicated at the predetermined angle with the top surface of the conveyor belt, by repeated performing the steps of applying the photocurable ink composition layer by layer onto the ink composition layer onto which the light pattern has been completely emitted, and selectively curing the applied photocurable ink composition layer by emitting the light pattern onto the ink composition layer through the light emitting unit. The curing process through the application of the ink composition and the light emission may be performed in a low temperature chamber which is maintained at a low temperature equal to or lower than the phase change temperature of the ink composition, the conveyor belt may be driven in the one direction according to the progress speed of the printing process, and transfer a printed matter block stacked thereon in the one direction, and a printing space for a subsequent layer may be continuously secured by the transfer of the printed matter block through the conveyor belt.
The continuous production-type 3D printing method in accordance with the present disclosure may continuously secure a printing space for a subsequent layer by transferring a printed matter block during a printing process, and remove a down time for printing facilities, required for build platform rearrangement or equipment replacement, thereby producing continuous printed matters without stopping the printing facilities. Therefore, the continuous production-type 3D printing method may raise the productivity of a 3D printed matter, and continuously output various printed matters through one production line, thereby improving the diversity of the produced printed matters.
Hereafter, the above-described continuous production-type 3D printing method in accordance with the present disclosure will be described in more detail through preferred embodiments.
As illustrated in
When one printed matter layer is printed through such a process, the process of applying the photocurable ink composition layer by layer onto the printed matter layer, which is inclined at the predetermined angle with the top surface of the conveyor belt, through the slot die coater 400, and selectively curing the applied photocurable ink composition by emitting the light pattern onto the photocurable ink composition through the light emitting unit 500 is repeatedly performed to form printed matter layers 600 which are repeatedly stacked in such a direction that is diagonal at the predetermined angle with the top surface of the conveyor belt, and a 3D printed matter 700 is produced through the printed matter layers 600.
During this process, the printed matter block stacked on the conveyor belt may be transferred in one direction by the conveyor belt which is driven in the one direction according to the pace of the printing process, which makes it possible to easily and continuously secure the printing space for a subsequent layer.
At this time, the conveyor belt may be configured to be driven whenever the printing process for each layer is completed, or driven once in each printing period in which a plurality of layers with a preset thickness are printed.
As the printing space for a subsequent layer is continuously secured by transferring the printed matter block through the conveyor belt, it is possible to continuously manufacture 3D printed matters without a separate limitation, while the printing facilities are not stopped. Furthermore, it is possible to minimize the operation efficiency of the printing facilities, and to freely change the shape of the printed matter at any time during the printing process for a printed matter through a simple operation of changing the light pattern emitted by the light emitting unit, thereby significantly improving the efficiency of the printing operation and the diversity of printed matters.
In order to effectively perform the above-described continuous producing method in accordance wit the embodiment of the present disclosure, a process of collecting the output 3D printed matter by effectively processing the printed matter block transferred through the conveyor belt without delaying the printing process is necessarily required. This process will be described below in more detail with reference to
In the embodiment of the present disclosure, a photocurable resin composition which is cured by emitting a specific wavelength of light including ultraviolet light UV is used as the ink composition for 3D printing. At this time, the ink composition used in the present disclosure may have liquidus viscosity at a predetermined temperature or higher, such that one printed matter layer for 3D printing can be deposited on the surface of a printing plate such as the build platform. However, when the ink composition stays in a low temperature state below a predetermined temperature range of phase change temperature zone ΔT, the ink composition hardens to a solid while the viscosity thereof rapidly increases.
As illustrated in
The ink composition having a low-temperature phase change characteristic may be a resin composition which is composed of a monomer having a photocurable (meta)acrylic group with a molecular weight of 50 to 1,000 and an oligomer having a photocurable (meta)acrylic group with a molecular weight of 500 to 1,000,000, and can be photo-cured by a radical method, a resin composition which is composed of a monomer having a photocurable epoxy group with a molecular weight of 50 to 1,000 and an oligomer having a photocurable epoxy group with a molecular weight of 500 to 1,000,000, and can be photo-cured by a cationic method, or a hybrid composition obtained by combining the two resin compositions.
In the 3D printing method in accordance with the embodiment of the present disclosure, the process for 3D printing uses such phase-change temperature characteristics of the ink composition and is performed in a low-temperature chamber which is maintained at the environment of a low temperature ranging from 0° C. to 10° C., which is equal to or lower than the phase-change temperature of the ink composition. This process will be described below in detail with reference to
That is, in the present embodiment, through the above-described low-temperature printing environment, the liquid ink composition which is applied layer by layer onto the printing area by the slot die coater may be rapidly cooled and changed to a solid state, such that the fluidity thereof is removed. Furthermore, the printed matter block which has hardened but is not cured may support the 3D printed matter cured through light emission, and simultaneously form the printed surface of the ink composition layer which is subsequently applied. Therefore, even after the build platform which has initially formed the printed surface gets out of the printing space with the progress of the printing process, the continuous printing process is maintained through the inclined surface of an uncured printed matter block which is successively stacked in the printing space, by the conveyor belt driven in the one direction.
As illustrated in
The 3D printing method in accordance with the embodiment of the present disclosure includes providing the conveyor belt 200 which is made of a metallic material and driven in one direction through the pulley 100, installing the build platform 300 (see
At this time, a cooling unit (not illustrated) such as a cooling loop may be connected to the above-described conveyor belt 200 or the build platform, such that the surface temperature of the conveyor belt and the build platform can be always maintained at a predetermined temperature or lower. Furthermore, the inclination angle of the build platform 300 may be properly set according to the characteristic of the ink composition and the size of the 3D printed matter as a printing target. Desirably, it is effective to set the inclination angle to an angle of 10° C. to 60° C. with respect to the top surface of the conveyor belt.
When one printed matter layer is printed through such a process, the process of applying the photocurable ink composition layer by layer onto the printed matter layer, which is inclined at the predetermined angle with the top surface of the conveyor belt, through the slot die coater 400, and selectively curing the applied photocurable ink composition by emitting the light pattern onto the photocurable ink composition through the light emitting unit 500 is repeatedly performed to form the printed matter layers 600 which are repeatedly stacked in such a direction that is diagonal at the predetermined angle with the top surface of the conveyor belt, and the 3D printed matter 700 is produced through the printed matter layers 600.
During this process, the printed matter block stacked on the conveyor belt 200 may be transferred in one direction by the conveyor belt 200 which is driven in the one direction, according to the pace of the printing process, which makes it possible to easily and continuously secure a printing space for a subsequent layer.
At this time, the conveyor belt may be configured to be driven whenever the printing process for each layer is completed, or driven once in each printing period in which a plurality of layers with a preset thickness are printed.
Furthermore, a separation collection room 900 is connected to one outer wall of the low temperature chamber 800 to which the printed matter block is transferred by the conveyor belt 200, and serves to separate and collect the 3D printed matter 700 from the transferred printed matter block, and collect and reuse the ink composition, which has hardened but is not cured, by reducing the ink composition into liquid in the low temperature chamber 800. At this time, the operation environment of the separation collection room is maintained at a temperature higher than the phase-change temperature of the ink composition. Thus, the phase of the uncured ink composition constituting the transferred printed matter block changes to a liquid state again.
That is, as illustrated in
At the boundary wall between the low temperature chamber 800 and the separation collection room 900, a transfer path 910 is formed to transfer the printed matter block. On the transfer path 910, a heat insulating unit (not illustrated) such as an air curtain or curtain wall may be installed to prevent heat exchange caused by a temperature difference between the two spaces.
Through such a configuration, the ink composition which is not cured and constitutes the transferred printed matter block is changed again to liquid by the operation environment of the separation collection room 900, and naturally separated from the 3D printed matter cured in the printing process. Thus, the cured 3D printed matter may be separated and collected while the continuous 3D printing process is performed without stopping the printing process to separate the 3D printed matter. During this process, the liquid ink composition may be collected into an ink collection tub 920 installed under the conveyor belt 200 extended into the separation collection room 900, and then reused.
That is, the uncured ink composition constituting the transferred printed matter block may be changed again to liquid in the separation collection room 900, and collected by the ink collection tub 920 installed under the conveyor belt 200. The ink composition collected through the ink collection tub 920 may be filtered by a filter 940 through a collection line 930, transferred to an ink storage bath 950 in which the ink composition supplied to the slot die coater 400 is stored, and then supplied to the slot die coater 400 through a supply line 960 again. Thus, the ink composition which is not cured during the printing process may not be wasted, but be effectively reused.
Then, the uncured ink composition remaining on the surface of the 3D printed matter 700 separated from the phase-changed ink composition is completely removed through a cleaning process using a cleaning solution, and the 3D printed matter 700 is then dried and completely produced.
Furthermore, when the ink composition having the phase change characteristic, described with reference to
The above-described embodiment of the present disclosure only exemplifies a preferred aspect of the present disclosure, and the present disclosure is not limited thereto and the scope of the present disclosure is limited by the matters disclosed in the claims to be described below. Further, it is obvious that the person skilled in the art to which the present disclosure pertains can variously carry out the present disclosure without departing from the subject matter of the present disclosure claimed in the claims. Therefore, such modifications and improvements fall within the scope of the present disclosure as long as they are within the scope obvious to the person skilled in the art.
As described above, the continuous production-type 3D printing method in accordance with the present disclosure may include repeatedly performing the printing process of installing the build platform on the conveyor belt made of a metallic material, such that the built platform is inclined at the predetermined angle with the top surface of the conveyor belt, applying the photocurable ink composition layer by layer onto the top surface of the build platform, and selectively curing the applied photocurable ink composition by emitting a light pattern thereto through the light emitting unit. During the printing process, the printed matter block stacked on the conveyer block may be transferred in one direction by the conveyor belt, according to the pace of the printing process, such that the printing space for a subsequent layer can be continuously secured through the transfer of the printed matter block. Thus, the 3D printing method can continuously output printed matters without a separate additional process such as a replacement operation of the build platform, and simultaneously change the shape of an output printed matter at any time through a simple operation of changing the light pattern emitted by the light emitting unit, during the printing process, thereby significantly improving the efficiency of the printing operation and the diversity of printed matters.
Furthermore, when the ink composition which hardens to a solid matter at the predetermined temperature or lower but changes to liquid again at room temperature is used, the operation environment of the separation collection room for collecting the 3D printed matter, the collection and supply lines of the ink composition, and post-processing operations such as a cleaning operation of the collected 3D printed matter may be all performed at room temperature. Thus, the printing and post-processing facilities of the overall processes required for 3D printing may be easily constructed, which makes it possible to maximize the convenience and efficiency of the processing operations.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2019-0179633 | Dec 2019 | KR | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/KR2020/017450 | 12/2/2020 | WO | 00 |