Claims
- 1. The method of refining cement copper comprising:
- mixing cement copper with desired fluxes and preheating the mixture;
- injecting the mixture with a heated, pressurized gas into incandescent coke in an oxidizing shaft kiln at the level of highest temperature, to effect rapid melting of said mixture without significant dusting losses and the formation of molten metal and slag phases;
- injecting an oxidizing gas into said metal phase to drive impurities into said slag;
- removing said slag and covering said metal with a reductant;
- treating said metal with a reducing agent to produce a copper of high purity; and
- recovering said copper.
- 2. The method as claimed in claim 1, wherein said mixing and preheating are carried out in heat-exchange relation with said shaft kiln.
- 3. The method as claimed in claim 1, wherein said oxidizing step is carried out with a gas selected from the group consisting of air, oxygen-enriched air and substantially pure oxygen.
- 4. The method as claimed in claim 1, wherein said fluxes are selected from the group consisting of silica, sodium carbonate, glass, and mixtures thereof.
- 5. The method as claimed in claim 1, wherein said reductant is charcoal.
- 6. The method as claimed in claim 1, wherein said reducing agent is a heated hydrocarbon gas.
- 7. The method as claimed in claim 1, wherein said oxidizing, reducing and recovery steps are carried out in a vessel separate from said shaft kiln.
- 8. The method as claimed in claim 6, wherein said hydrocarbon is natural gas at about 800.degree. C.
- 9. The method as claimed in claim 1, wherein said preheated mixture is charged at a point between 45 and 50% of the height of said kiln.
- 10. The method of substantially continuously refining cement copper comprising:
- maintaining a column of incandescent coke in an oxidizing shaft kiln;
- continuously charging a preheated mixture of cement copper and desired fluxes into the hottest portion of said column by injection with a heated, pressurized gas;
- collecting molten metal and slag phases in a hearth of said kiln and transferring said phases to a forehearth;
- injecting an oxidizing gas into said metal to drive impurities into said slag;
- replacing said slag with a reductant;
- treating said metal with a heated hydrocarbon gas to produce a copper of high purity; and
- recovering said copper.
- 11. The method as claimed in claim 10, wherein a single shaft kiln is used in conjunction with a plurality of said forehearths.
- 12. The method as claimed in claim 10, wherein said oxidizing step is carried out with a free-oxygen containing gas, and said hydrocarbon is a natural gas at about 800.degree. C.
Parent Case Info
This is a division of application Ser. No. 700,217 filed June 28, 1976, now U.S. Pat. No. 4,056,262, issued Nov. 1, 1977 and titled "CUPOLA FURNACE TO ENABLE CONTINUOUS SMELTING AND REFINING OF CEMENT COPPER AND METHOD THEREFOR."