Patent Grant
9247590
The present invention relates to a control unit of an induction heating unit, an induction heating system, and a method of controlling the induction heating unit. Particularly, the present invention is suitable for being used to make an alternating magnetic field intersect a conductive sheet in a substantially orthogonal manner so as to inductively heat the conductive sheet.
Priority is claimed on Japanese Patent Application No. 2009-283255, filed Dec. 14, 2009, the content of which is incorporated herein by reference.
In the conventional techniques, for example, an induction heating unit has been used when heating a conductive sheet such as a steel sheet that is conveyed through a manufacturing line. The induction heating unit is provided with a heating coil, and heats the conductive sheet using an eddy current induced by the heating coil. In this induction heating unit, the eddy current is caused to the conductive sheet by an alternating magnetic field (AC magnetic field) generated by the heating coil, Joule heat is generated in the conductive sheet due to the eddy current. As an example of the induction heating unit, a transverse type induction heating unit is disclosed. In the transverse type induction heating unit, the alternating magnetic field is applied to the conductive sheet in a manner that intersects a sheet surface of the conductive sheet, which is an object to be heated, to be substantially orthogonal thereto.
As a method of controlling the transverse type induction heating unit, a technique disclosed in Patent Citation 1 may be exemplified. In Patent Citation 1, a capacitor is provided in parallel to the heating coil that makes up the induction heating unit, the heating coil and the capacitor make up a parallel resonance circuit, and power is supplied to the heating coil by a parallel resonance type inverter.
[Patent Citation 1] Japanese Unexamined Patent Application, First Publication No. 2002-313547
However, when the heating coil of the induction heating unit is seen from a power supply unit (power supply circuit) of the induction heating unit, the inductance varies in response to the sheet conveyance speed of the conductive sheet that is an object to be heated by the induction heating unit (in the following description, this inductance is referred to as apparent inductance as necessary). Specifically, when the sheet conveyance speed of the conductive sheet becomes fast (or slow), the apparent inductance becomes small (or large).
However, in the technique disclosed in Patent Citation 1, the heating coil and the capacitor make up the parallel resonance circuit. Therefore, when the apparent inductance varies, the power frequency, which is supplied to the heating coil, also varies. For example, when the sheet conveyance speed of the conductive sheet becomes fast and thereby the apparent inductance becomes small, the frequency of the power supplied to the heating coil increases. In this manner, when the frequency of the power supplied to the heating coil increases, the temperature in the vicinity of an end portion (edge) of the conductive sheet in the sheet width direction becomes higher than that in the vicinity of the central portion of the conductive sheet in the sheet width direction. Therefore, there is a concern in that a temperature distribution of the conductive sheet in the sheet width direction may be non-uniform.
As described above, in the conventional techniques, in a case where the conductive sheet is heated by using the transverse type induction heating unit, there is a problem in that as the sheet conveyance speed of the conductive sheet varies, the temperature distribution of the conductive sheet in the sheet width direction becomes non-uniform.
The present invention has been made in consideration of this problem, and an object of the present invention is to realize a temperature distribution that is more uniform than that in the conventional techniques by preventing the temperature distribution of the conductive sheet in the sheet width direction from being non-uniform even when the sheet conveyance speed of the conductive sheet varies in a case where the conductive sheet is heated using a transverse type induction heating unit.
(1) A control unit of an induction heating unit according to an aspect of the present invention controls AC power output to a heating coil of a transverse type induction heating unit allowing an alternating magnetic field to intersect a sheet surface of a conductive sheet that is being conveyed to inductively heat the conductive sheet. The control unit includes: a magnetic energy recovery switch that outputs AC power to the heating coil, a frequency setting unit that sets the output frequency in response to at least one of the relative permeability, resistivity, and sheet thickness of the conductive sheet; and a gate control unit that controls a switching operation of the magnetic energy recovery switch on the basis of the output frequency set by the frequency setting unit.
(2) In the control unit of an induction heating unit according to (1), the frequency setting unit may acquire attribute information that specifies the relative permeability, resistivity, and sheet thickness of the conductive sheet, and may select a frequency corresponding to the acquired attribute information as the output frequency with reference to a table in which the relative permeability, resistivity, and sheet thickness of the conductive sheet, and the frequency are correlated with each other and are registered in advance.
(3) The control unit of an induction heating unit according to (1) or (2) may further include: an output current setting unit that sets an output current value in response to at least one of the relative permeability, resistivity, and sheet thickness of the conductive sheet; a current measuring unit that measures an alternating current that flows to the induction heating unit; and a power supply unit that supplies DC power to the magnetic energy recovery switch and adjusts an alternating current that is measured by the current measuring unit to the output current value that is set by the output current setting unit, wherein the magnetic energy recovery switch may be supplied with the DC power by the power supply unit and may output the AC power to the heating coil.
(4) In the control unit of an induction heating unit according to (3), the output current setting unit may acquire attribute information that specifies the relative permeability, resistivity, and sheet thickness of the conductive sheet, and may select a current value corresponding to the acquired attribute information as the output current value with reference to a table in which the relative permeability, resistivity, and sheet thickness of the conductive sheet, and the current value are correlated with each other and are registered in advance.
(5) The control unit of an induction heating unit according to (1) or (2) may further include an output transformer that is disposed between the magnetic energy recovery switch and the induction heating unit, lowers the AC voltage that is output from the magnetic energy recovery switch, and outputs the lowered AC voltage to the heating coil.
(6) In the control unit of an induction heating unit according to (1) or (2), the magnetic energy recovery switch may include first and second AC terminals that are connected to one end and the other end of the heating coil, respectively, first and second DC terminals that are connected to an output terminal of the power supply unit, a first reverse conductivity type semiconductor switch that is connected between the first AC terminal and the first DC terminal, a second reverse conductivity type semiconductor switch that is connected between the first AC terminal and the second DC terminal, a third reverse conductivity type semiconductor switch that is connected between the second AC terminal and the second DC terminal, a fourth reverse conductivity type semiconductor switch that is connected between the second AC terminal and the first DC terminal, and a capacitor that is connected between the first and second DC terminals, the first reverse conductivity type semiconductor switch and the fourth reverse conductivity type semiconductor switch may be connected in series in such a manner that conduction directions at the time of a switch-off become opposite to each other, the second reverse conductivity type semiconductor switch and the third reverse conductivity type semiconductor switch may be connected in series in such a manner that conduction directions at the time of the switch-off become opposite to each other, the first reverse conductivity type semiconductor switch and the third reverse conductivity type semiconductor switch may have the same conduction direction at the time of the switch-off as each other, the second reverse conductivity type semiconductor switch and the fourth reverse conductivity type semiconductor switch may have the same conduction direction at the time of the switch-off as each other, and the gate control unit may control a switching operation time of the first and third reverse conductivity type semiconductor switches and a switching operation time of the second and fourth reverse conductivity type semiconductor switches on the basis of the output frequency that is set by the frequency setting unit.
(7) An induction heating system according to another aspect of the present invention allows an alternating magnetic field to intersect a sheet surface of a conductive sheet that is being conveyed to inductively heat the conductive sheet. The induction heating system includes: the control unit of an induction heating unit according to (1) or (2); a heating coil that is disposed to face the sheet surface of the conductive sheet; a core around which the heating coil is wound; and a shielding plate which is disposed to face a region including an edge of the conductive sheet in the width direction and is formed from a conductor having a relative permeability of 1.
(8) In the induction heating system according to (7), the shielding plate may have a depressed portion.
(9) In the induction heating system according to (8), the shielding plate may be disposed in such a manner that a region, which is closer to the edge of the conductive sheet than a region in which an eddy current flowing to the conductive sheet becomes the maximum, and the depressed portion face each other.
(10) A method of controlling an induction heating unit according to still another aspect of the present invention controls AC power, which is output to a heating coil of a transverse type induction heating unit allowing an alternating magnetic field to intersect a sheet surface of a conductive sheet that is being conveyed to inductively heat the conductive sheet. The method includes: outputting AC power to the heating coil by a magnetic energy recovery switch; setting an output frequency in response to at least one of a relative permeability, resistivity, and sheet thickness of the conductive sheet; and controlling a switching operation of the magnetic energy recovery switch on the basis of the output frequency that is set.
(11) In the method of controlling an induction heating unit according to (10), the output frequency may be set by acquiring attribute information that specifies the relative permeability, resistivity, and sheet thickness of the conductive sheet, and by selecting a frequency corresponding to the acquired attribute information as the output frequency with reference to a table in which the relative permeability, resistivity, and sheet thickness of the conductive sheet, and the frequency are correlated with each other and are registered in advance.
(12) The method of controlling an induction heating unit according to (10) or (11) may further include: setting an output current value in response to at least one of the relative permeability, resistivity, and sheet thickness of the conductive sheet; measuring an alternating current that flows to the induction heating unit; and supplying DC power, which is necessary for adjusting an alternating current that is measured to the output current value that is set, to the magnetic energy recovery switch.
(13) In the method of controlling an induction heating unit according to (12), the output current value may be set by acquiring attribute information that specifies the relative permeability, resistivity, and sheet thickness of the conductive sheet, and by selecting a current value corresponding to the acquired attribute information as the output current value with reference to a table in which the relative permeability, resistivity, and sheet thickness of the conductive sheet, and the current value are correlated with each other and are registered in advance.
(14) In the method of controlling an induction heating unit according to (10) or (11), an AC voltage that is output from the magnetic energy recovery switch may be lowered by an output transformer, and the lowered AC voltage may be output to the heating coil.
(15) In the method of controlling an induction heating unit according to (10) or (11), the magnetic energy recovery switch may include first and second AC terminals that are connected to one end and the other end of the heating coil, respectively, first and second DC terminals that are connected to an output terminal of the power supply unit, a first reverse conductivity type semiconductor switch that is connected between the first AC terminal and the first DC terminal, a second reverse conductivity type semiconductor switch that is connected between the first AC terminal and the second DC terminal, a third reverse conductivity type semiconductor switch that is connected between the second AC terminal and the second DC terminal, a fourth reverse conductivity type semiconductor switch that is connected between the second AC terminal and the first DC terminal, and a capacitor that is connected between the first and second DC terminals, the first reverse conductivity type semiconductor switch and the fourth reverse conductivity type semiconductor switch may be connected in series in such a manner that conduction directions at the time of a switch-off become opposite to each other, the second reverse conductivity type semiconductor switch and the third reverse conductivity type semiconductor switch may be connected in series in such a manner that conduction directions at the time of the switch-off become opposite to each other, the first reverse conductivity type semiconductor switch and the third reverse conductivity type semiconductor switch may have the same conduction direction at the time of the switch-off as each other, the second reverse conductivity type semiconductor switch and the fourth reverse conductivity type semiconductor switch may have the same conduction direction at the time of the switch-off as each other, and the AC power may be output to the heating coil by controlling a switching operation time of the first and third reverse conductivity type semiconductor switches and a switching operation time of the second and fourth reverse conductivity type semiconductor switches on the basis of the output frequency that is set.
According to the control unit of an induction heating unit according to the aspect of the present invention, the switching operation of the magnetic energy recovery switch is controlled on the basis of the frequency in response to at least one of the relative permeability, resistivity, and sheet thickness of the conductive sheet that is being conveyed, and the AC power of this frequency is output from the magnetic energy recovery switch. Therefore, the AC power of the frequency corresponding to the attribute of the conductive sheet that is being conveyed can be applied to the heating coil without being subjected to a restriction in regard to an operation with a resonant frequency. Therefore, it is possible to prevent the temperature distribution of the conductive sheet in the sheet width direction from being non-uniform even when a sheet conveyance speed of the conductive sheet varies in a case where the conductive sheet is heated using a transverse type induction heating unit. In addition, the AC power with the frequency in response to the attribute of the conductive sheet that is being conveyed can be supplied to the heating coil independently from operational conditions, such that the induction heating control can be performed in a relatively simple and reliable manner.
Hereinafter, embodiments of the present invention will be described with reference to the attached drawings. In each of the following embodiments, a description will be made with respect to an example in which a transverse type induction heating unit and a control unit thereof are applied to a continuous annealing line of a steel sheet in a manufacturing line. In addition, in the following description, “transverse type induction heating unit” will be simply referred to as “induction heating unit” as necessary. In addition, unless particularly specified, in regard to attributes of the steel sheet (steel strip), values at room temperature (for example, 25° C.) will be used.
(First Embodiment)
First, a first embodiment of the present invention will be described.
<Schematic Configuration of Continuous Annealing Line>
In
The first sealing roller assembly 14 conveys (feeds) a steel strip 10 into the first container 11 while shielding the first container 11 from external air. The steel strip 10 conveyed into the first container 11 by the first sealing roller assembly 14 is conveyed into the second container 12 by the rollers 19a and 19b in the first container 11. The steel strip 10 conveyed into the second container 12 is again conveyed into the first container 11 by the rollers 19g and 19h while being heated by the induction heating unit 20 which is disposed at both an upper side and a lower side of a horizontal portion of the second container 12 (of the steel strip 10 that is being conveyed). Here, the induction heating unit 20 (heating coil thereof) is electrically connected to the control unit 100 of the induction heating units, and AC power is supplied to the induction heating unit 20 from the control unit 100 of the induction heating unit. An alternating magnetic field, which intersects a sheet surface of the steel strip 10 in a substantially orthogonal manner, is generated by the AC power, and thereby the steel strip 10 is inductively heated. In addition, details of a configuration of the induction heating unit 20 will be described later. In addition, in the following description, “electrical connection” will be simply referred to as “connection” as necessary.
The steel strip 10 that is returned into the first container 11 is conveyed to the conveyance unit 15 by the rollers 19c to 19f after passing through a soaking and slow cooling stage. The steel strip 10 conveyed to the conveyance unit 15 is conveyed to the third container 13 by the rollers 19i and 19j. The steel strip 10 conveyed to the third container 13 is conveyed while being made to move in a vertically up and down manner by the rollers 19k to 19u and is rapidly cooled in the third container 13.
The second sealing roller assembly 16 forwards the steel strip 10, which is rapidly cooled in this manner, to a subsequent process while shielding the third container 13 from external air.
To the “first container 11, the second container 12, the third container 13, and the conveyance unit 15” that make up a “conveying path of the steel strip 10” described above, non-oxidation gas is supplied by the gas supply unit 17. In addition, the first container 11, the second container 12, the third container 13, and the conveyance unit 15 are maintained in a non-oxidation gas atmosphere by the “first sealing roller assembly 14 and the second sealing roller assembly 16” that shield the outside (external air) and the inside (the inside of the continuous annealing line 1).
<Configuration of Induction Heating Unit 20>
Specifically,
In
The upper side inductor 21 includes a core (magnetic core) 23, an upper side heating coil 24, and shielding plates 31a and 31c. The core 23 may be configured by stacking a plurality of electrical steel sheets.
The upper side heating coil 24 is a conductor that is wound on the core 23 through a slot (here, a depressed portion of the core 23) of the core 23, and is a coil in which the number of turns is “1” (so-called single turn). In addition, as shown in
Similarly to the upper side inductor 21, the lower side inductor 22 is also provided with a core (magnetic core) 27, a lower side heating coil 28, and shielding plates 31b and 31d.
Similarly to the upper side heating coil 24, the lower side heating coil 28 is a conductor that passes through a slot of the core 27 and is wound on the core 27, and is a coil in which the number of turns is “1” (so-called single turn). Furthermore, similarly to the upper side heating coil 24, the lower side heating coil 28 has a portion in which a shape of a longitudinal cross-section thereof is a hollow rectangle. A water-cooling pipe is connected to an end face of the hollow portion of the hollow rectangle, and cooling water can be made to flow to the hollow portion of the hollow rectangle. In addition, the shielding plates 31b and 31d are installed on the upper surface (slot side) of the core 27.
In addition, a coil face (face on which a loop is formed and through which a line of magnetic force penetrates) of the upper side heating coil 24 of the upper side inductor 21, and a coil face of the lower side heating coil 28 of the lower side inductor 22 face each other with the steel strip 10 interposed therebetween. Furthermore, sheet surfaces of the shielding plates 31a to 31d face end portions (edges) of the steel strip 10 in the sheet width direction. To satisfy this positional relationship, the upper side inductor 21 is provided at an upper side (in the vicinity of the upper surface of a horizontal portion of the second container 12) compared to the steel strip 10, and the lower side inductor 22 is provided at a lower side (in the vicinity of the lower surface of the horizontal portion of the second container 12) compared to the steel strip 10. In this embodiment, the shielding plates 31a to 31d are copper plates that have a flat surface (refer to
In this manner, the upper side inductor 21 and the lower side inductor 22 are different from each other in the position to be disposed, but have the same configuration as each other. In addition, in this configuration, since an alternating magnetic field generated from the heating coils intersects the conductive sheet 10 over the entire width thereof, the entire width of the conductive sheet 10 may be heated.
As shown in
One output terminal of the control unit 100 of the induction heating unit is connected to one end (front-end side of the copper pipe 41a) of the upper side heating coil 24 through the copper bus bar 42a. On the other hand, one end (front-end side of the copper pipe 41c) of the lower side heating coil 28 is connected to the other end (front-end side of the copper pipe 41b) of the upper side heating coil 24 through the copper bus bars 42c to 42e. In addition, the other output terminal of the control unit 100 of the induction heating unit is connected to the other end (front-end side of the copper pipe 41d) of the lower side heating coil 28 through copper bus bars 42i, 42h, and 42g.
As described above, the upper side heating coil 24 and the lower side heating coil 28 are connected in series to the control unit 100 of the induction heating unit by combining the copper pipes 41a to 41d and the copper bus bars 42a to 42i, thereby forming coils in which the number of turns is “1”. Here, the direction (in
In addition, as described later, the control unit 100 of the induction heating unit supplies AC power to the upper side heating coil 24 and the lower side heating coil 28 of the induction heating unit 20. Therefore, in
In addition, here, for illustrating a configuration of the upper side heating coil 24 and the lower side heating coil 28 in an easy manner, the copper pipes 41a to 41d and the copper bus bars 42a to 42i are connected in a manner as shown in
<Configuration of Control Unit 100 of Induction Heating Unit>
In
In
[Configuration of MERS 130]
Hereinafter, an example of a configuration of the MERS 130 will be described.
The MERS 130 converts DC power, which is input from the rectifying circuit 110 through the reactor 120, to AC power according to a method described later, and outputs the AC power to the induction heating unit 20.
In
The other end of the reactor 120 is connected to the DC terminal b, and the other end of the rectifying circuit 110 on the output side is connected to the DC terminal c. In addition, one end (copper bus bar 42a) and the other end (copper bus bar 42g) of the induction heating unit 20 are connected to the AC terminals a and d (refer to
The bridge circuit of the MERS 130 includes a first path L1 reaching the AC terminal d from the AC terminal a through the DC terminal b, and a second path L2 reaching the AC terminal d from the AC terminal a through the DC terminal c. The first reverse conductivity type semiconductor switch 131 is connected between the AC terminal d and the DC terminal b, and the fourth reverse conductivity type semiconductor switch 134 is connected between the DC terminal b and the AC terminal a. In addition, the second reverse conductivity type semiconductor switch 132 is connected between the AC terminal d and the DC terminal c, and the third reverse conductivity type semiconductor switch 133 is connected between the DC terminal c and the AC terminal a. In this manner, the first and second reverse conductivity type semiconductor switches 131 and 132 are connected in parallel, and the third and fourth reverse conductivity type semiconductor switches 133 and 134 are connected in parallel. In addition, the first and fourth reverse conductivity type semiconductor switches 131 and 134 are connected in series, and the second and third reverse conductivity type semiconductor switches 132 and 133 are connected in series.
Each of the first to fourth reverse conductivity type semiconductor switches 131 to 134 allows a current to flow in one direction at the time of a switch-off in which an on-signal is not input to a gate terminal thereof, and allows a current to flow in both directions at the time of a switch-on in which the on-signal is input to the gate terminal. That is, the reverse conductivity type semiconductor switches 131 to 134 allows a current to flow only in one direction between a source terminal and a drain terminal at the time of the switch-off but allows a current to flow in both directions between the source terminal and the drain terminal at the time of the switch-on. In addition, in the following description, “a direction toward which each of the reverse conductivity type semiconductor switches 131 to 134 allows a current to flow at the time of the switch-off” is also referred to as “a switch forward direction” as necessary. In addition, “a direction toward which each of the reverse conductivity type semiconductor switches 131 to 134 does not allow a current to flow at the time of the switch-off” is also referred to as “a switch reverse direction” as necessary. Furthermore, in the following description, “a connection direction with respect to the bridge circuit in the switch forward direction and the switch reverse direction” is also referred to as “a switch polarity” as necessary.
In addition, each of the reverse conductivity type semiconductor switches 131 to 134 is disposed to satisfy the switch polarity as described below. The first reverse conductivity type semiconductor switch 131 and the second reverse conductivity type semiconductor switch 132, which are connected in parallel, have switch polarities opposite to each other. Similarly, the third reverse conductivity type semiconductor switch 133 and the fourth reverse conductivity type semiconductor switch 134, which are connected in parallel, have switch polarities opposite to each other. In addition, the first reverse conductivity type semiconductor switch 131 and the fourth reverse conductivity type semiconductor switch 134, which are connected in series, have switch polarities opposite to each other. Similarly, the second reverse conductivity type semiconductor switch 132 and the third reverse conductivity type semiconductor switch 133, which are connected in series, have switch polarities opposite to each other. Therefore, the first reverse conductivity type semiconductor switch 131 and the third reverse conductivity type semiconductor switch 133 have the same switch polarity as each other. Similarly, the second reverse conductivity type semiconductor switch 132 and the fourth reverse conductivity type semiconductor switch 134 have the same switch polarity as each other. In addition, the switch polarity of the first and third reverse conductivity type semiconductor switches 131 and 133 is opposite to that of the second and fourth reverse conductivity type semiconductor switches 132 and 134.
In addition, in regard to the switch polarities shown in
In addition, various configurations may be considered with respect to the first to fourth reverse conductivity type semiconductor switches 131 to 134, but in this embodiment, the first to fourth reverse conductivity type semiconductor switches 131 to 134 are configured by a parallel connection between semiconductor switches S1 to S4 and diodes D1 to D4, respectively. That is, each of the first to fourth reverse conductivity type semiconductor switches 131 to 134 includes one diode (corresponding one among diodes D1 to D4) and one semiconductor switch (corresponding one among semiconductor switches S1 to S4) that is connected to the diode in parallel.
In addition, respective gate terminals G1 to G4 of the semiconductor switches S1 to S4 are connected to the gate control unit 140. An on-signal, which allows the semiconductor switches S1 to S4 to be turned on, is input to the gate terminals G1 to G4 from the gate control unit 140 as a control signal to the MERS 130. In a case where the on-signal is input, the semiconductor switches S1 to S4 enter an on-state, and may allow a current to flow in a both direction. However, in a case where the on-signal is not input, the semiconductor switches S1 to S4 enter an off-state, and can not allow a current to flow in any direction. Therefore, when the semiconductor switches S1 to S4 are turned off, a current can flow only in the conduction direction (forward direction) of the diodes D1 to D4 that are connected in parallel to the semiconductor switches S1 to S4.
In addition, the reverse conductivity type semiconductor switches included in the MERS 130 are not limited to the first to fourth reverse conductivity type semiconductor switches 131 to 134. That is, any reverse conductivity type semiconductor switch is preferable as long as this switch has a configuration capable of showing the above-described operation. For example, the reverse conductivity type semiconductor switches may have a configuration using a switching element such as a power MOSFET and a reverse conducting GTO thyristor, or may have a configuration in which a semiconductor switch such as an IGBT and a diode are connected in parallel.
In addition, hereinafter, a description will be made by substituting the switch polarity of the first to fourth reverse conductivity type semiconductor switches 131 to 134 with the polarity of the diodes D1 to D4. A switch forward direction (direction toward which a current flows at the time of a switch-off) is a conduction direction (forward direction) of each of the diodes D1 to D4, and a switch reverse direction (direction toward which a current does not flow at the time of the switch-off) is a non-conduction direction (reverse direction) of each of the diodes D1 to D4. In addition, conduction directions between diodes (D1 and D2, or D3 and D4) connected in parallel are opposite to each other, and conduction direction between diode (D1 and D4, or D2 and D3) connected in series are opposite to each other. In addition, conduction directions of the diodes D1 and D3 are the same as each other. Similarly, conduction directions of the diodes D2 and D4 are the same as each other. Therefore, the conduction direction of the diode D1 and D3 and the conduction direction of the diodes D2 and D4 are opposite to each other. In addition, the conduction directions of the semiconductor switches S1 to S4 and the diodes D1 to D4 are set with a direction of a
[Operation of MERS 130]
In
As shown in
When the charging of the capacitor C is completed, the current IL flowing to the induction heating unit 20 becomes zero. When the semiconductor switches S2 and S4 are turned on until the charging of the capacitor C is completed, and then the charging of the capacitor C is completed, the energy (charge) charged in the capacitor C is output (discharged) through the semiconductor switches S4 and S2. As a result, the current IL flows through a path of the semiconductor switch S4→the induction heating unit 20→the semiconductor switch S2 (period B). That is, in this period B, the voltage Vc at both ends of the capacitor C is lowered, and therefore the current IL (absolute value thereof) flowing to the induction heating unit 20 increases.
When the discharging of the capacitor C is completed, the voltage Vc at both ends of the capacitor C becomes zero, and therefore a reverse voltage is not applied to the diodes D1 and D3. Therefore, the diodes D1 and D3 enter a conduction state, and the current IL flows through a path of the semiconductor switch S4→the induction heating unit 20→the diode D1 and a path of the diode D3→the induction heating unit 20→the semiconductor switch S2 in parallel (period C). The current IL circulates between the induction heating unit 20 and the MERS 130. Therefore, in the period C, the absolute value of the current IL is attenuated in response to a time constant that is determined by impedance of the upper side heating coil 24, the lower side heating coil 28, and the steel strip 10 that is an object to be heated.
Then, in the dead time, not only the semiconductor switches S1 and S3, but also the semiconductor switches S2 and S4 are turned off. For the dead time, a current flows through a path of the diode D1→the capacitor C→the diode D3, and therefore the charging of the capacitor C is initiated (period D). As a result, the voltage Vc at both ends of the capacitor C is raised, and therefore the current IL (absolute value thereof) flowing to the induction heating unit 20 decreases. When the semiconductor switches S1 and S3 are turned on (while the semiconductor switches S2 and S4 are turned off) before the charging of the capacitor C is completed, a current flows through the path of the semiconductor switch S1 and the diode D1→the capacitor C→the semiconductor switch S3 and the diode D3, and therefore the capacitor C is charged (period D). That is, in this period D, the voltage Vc at both ends of the capacitor C is raised, and therefore the current IL (absolute value thereof) flowing to the induction heating unit 20 decreases.
When the charging of the capacitor C is completed, the current IL flowing to the induction heating unit 20 becomes zero. When the semiconductor switches S1 and S3 are turned on until the charging of the capacitor C is completed, and then the charging of the capacitor C is completed, the energy (charge) charged in the capacitor C is output (discharged) through the semiconductor switches S1 and S3. As a result, the current IL flows through a path of the semiconductor switch S1→the induction heating unit 20→the semiconductor switch S3 (period E). That is, in this period E, the voltage Vc at both ends of the capacitor C is lowered, and therefore the current IL (absolute value thereof) flowing to the induction heating unit 20 increases.
When the discharging of the capacitor C is completed, the voltage Vc at both ends of the capacitor C becomes zero, and therefore a reverse voltage is not applied to the diodes D2 and D4. Therefore, the diodes D2 and D4 enter a conduction state, and the current IL flows through a path of the semiconductor switch S1→the induction heating unit 20→the diode D4 and a path of the diode D2→the induction heating unit 20→the semiconductor switch S3 in parallel (period F). The current IL circulates between the induction heating unit 20 and the MERS 130. Therefore, in the period F, the absolute value of the current IL is attenuated in response to a time constant that is determined by impedance of the upper side heating coil 24, the lower side heating coil 28, and the steel strip 10 that is an object to be heated. Then, it returns to the operation for the period A, and the operations for the periods A to F are repetitively performed.
As described above, when turn-on and turn-off (switching operation) timings (times) of the respective gate terminals G1 to G4 (G1 and G3, and G2 and G4) of the semiconductor switches S1 to S4 (S1 and S3, and S2 and S4) are adjusted, a current of a desired frequency can be made to flow through the induction heating unit 20 (the upper side heating coil 24 and the lower side heating coil 28), thereby realizing frequency control type induction heating. That is, due to the gate control unit 140 that adjusts the conduction timing of the semiconductor switches S1 to S4, a frequency of the current IL that flows to the induction heating unit 20 that is a load can be controlled to an arbitrary value. In addition, when capacitance Cp of the capacitor C is determined according to Equation (1) described below, the period in which the voltage Vc at both ends of the capacitor C is zero can be adjusted.
Cp=1/[(2×π×ft)2×L] (1)
Here, Cp represents capacitance (F) of the capacitor C, and L represents inductance (H) of loads including the induction heating unit 20. In addition, ft represents an apparent frequency (Hz) with respect to the capacitor C, which is expressed by Equation (2) described below.
ft=1/(2×t+1/f) (2)
Here, t represents a period (sec) in which the voltage Vc at both ends of the capacitor C is zero, and f represents a frequency (Hz) of the voltage Vc and the current IL in a case where a period in which the voltage Vc at both ends of the capacitor C is zero is not present. When a capacitor C, which has capacitance Cp that is obtained by substituting ft (that is, f) when t is zero in Equation (2) into Equation (1), is selected, a period in which the voltage Vc at both ends of the capacitor C is zero is not present.
[Configuration of Frequency Setting Unit 180]
Returning to the description of
The object-to-be-heated information acquiring unit 181 acquires attribute information of the steel strip 10 that is an object to be heated. For example, the object-to-be-heated information acquiring unit 181 acquires (receives) the attribute information from an external computer that is an input unit through a network, or acquires (input) the attribute information on the basis of information that is input by a user with respect to a user interface (one of input units) provided for the control unit 100. Here, the attribute information of the steel strip 10 is information that is capable of specifying a relative permeability, a resistance, and a sheet thickness of the steel strip 10. For example, the relative permeability, the resistance, and the sheet thickness itself of the steel strip 10 may be set as the attribute information, or in a case where the relative permeability, the resistance, and the sheet thickness itself of the steel strip 10 are determined according to specifications, a name (a trade name or the like) of the steel strip 10 having the specifications may be set as the attribute information.
The frequency selector 183 uses the attribute information acquired by the object-to-be-heated information acquiring unit 181 as a key and selects one frequency among frequencies registered in the frequency setting table 182. In the frequency setting table 182, the attribute information and the frequency are correlated with each other and are registered in advance.
Information of a frequency (output frequency) selected by the frequency selector 183 is transmitted to the gate control unit 140. The gate control unit 140 determines turn-on and turn-off (switching operation) timings of the respective gate terminals G1 to G4 of the semiconductor switches S1 to S4 of the MERS 130 so that AC power of the selected frequency is generated, and outputs an on-signal to a gate terminal of a semiconductor switch to be turned on. In this manner, the MERS 130 outputs the AC power of the frequency (the output frequency) that is set to the gate control unit 140 by the frequency setting unit 180 to the induction heating unit 20 as described above.
As described above, in this embodiment, the frequency (the output frequency) of the AC power to be supplied to the induction heating unit 20 is automatically determined in response to the relative permeability, the resistance, and the sheet thickness of the steel strip 10. This is based on a finding obtained through various experiments performed by the inventors, specifically, a finding that the temperature distribution (particularly, the temperature in the vicinity of an edge) of the steel strip 10 is affected by the frequency of the AC power supplied to the induction heating unit 20, the attribute information (the relative permeability, the resistance, and the sheet thickness) of the steel strip 10 that is an object to be heated, and a gap (distance between the upper side heating coil 24 and the lower side heating coil 28).
Hereinafter, the reason why this phenomenon occurs will be described.
First, a description will be made with respect to a case where the temperature of the steel strip 10 is equal to or higher than the Curie temperature.
When the steel strip 10 is at a temperature that is equal to or higher than the Curie temperature, a main magnetic field that is generated from the induction heating unit 20 penetrates through the steel strip 10, and an eddy current within the steel strip 10 (within a plane orthogonal to the sheet thickness) increases. This eddy current is repelled from a main magnetic field and is apt to be biased to the vicinity of the edge of the steel strip 10. Therefore, a high-temperature region is apt to occur in the vicinity of the edge of the steel strip 10.
Here, the eddy current within the steel strip 10 is proportional to a cross-sectional area (cross-sectional area including a sheet thickness direction) of the steel strip 10, such that in a case where the sheet thickness of the steel strip 10 is large, the cross-sectional area of the steel strip 10 becomes large and therefore the eddy current within the steel strip 10 increases.
In addition, the eddy current of the steel strip 10 is inversely proportional to a resistance of the steel strip 10, such that in a case where the resistance of the steel strip 10 is small, the eddy current within the steel strip 10 increases.
In addition, a frequency of AC power supplied to the induction heating unit 20 is proportional to an induced electromotive force that is generated within the steel strip 10 due to the main magnetic field generated from the induction heating unit 20. The eddy current of the steel strip 10 is proportional to the induced electromotive force, such that in a case where the frequency of the AC power supplied to the induction heating unit 20 is high, the eddy current within the steel strip 10 increases.
In addition, in a case where the gap is small, the main magnetic field generated from the induction heating unit 20 becomes large, such that the induced electromotive force generated within the steel strip 10 due to the main magnetic field becomes large and therefore the eddy current within the steel strip 10 increases.
Next, a description will be made with respect to a case where the temperature of the steel strip 10 is less than Curie temperature.
In a case where the temperature of the steel strip 10 is less than Curie temperature, a relative permeability of the steel strip 10 is large, such that the main magnetic field generated from the induction heating unit 20 is difficult to penetrate through the steel strip 10 and therefore bypasses the edge portion of the steel strip 10. As a result, in the vicinity of the edge of the steel strip 10 in the sheet width direction, the current density of the eddy current becomes large, and therefore a high temperature region occurs in the vicinity of the edge of the steel strip 10 in the sheet width direction.
As described above, factors (the frequency of the AC power supplied to the induction heating unit 20, the relative permeability, resistance, and sheet thickness of the steel strip 10 that is an object to be heated, and the gap), which have an effect on the temperature of the steel strip 10, are independent from each other. Among these factors, the relative permeability, resistance, and sheet thickness of the steel strip 10, and the gap are determined by operational conditions (hardware restrictions on a material that is an object to be heated and a facility). Therefore, in this embodiment, among these factors, “the frequency (the output frequency) of the AC power supplied to the induction heating unit 20” that can be controlled through on-line is changed using the frequency setting unit 180 to adjust the temperature of the steel strip 10.
In addition, as is the case with this embodiment, when all of the relative permeability, the resistance, and the sheet thickness of the steel strip 10, and the frequency are correlated with each other and are registered in the frequency setting table 182, the temperature distribution of the steel strip 10 in the sheet width direction can be adjusted in a relatively uniform manner. Therefore, it is preferable that all of the relative permeability, resistance, and sheet thickness of the steel strip 10, and the frequency be correlated with each other. However, it is not necessary to correlate all of the relative permeability, resistance, and sheet thickness of the steel strip 10, and the frequency, and at least one of the relative permeability, resistance, and sheet thickness of the steel strip 10 may be correlated with the frequency in the frequency setting unit 180. In addition, at least one of the relative permeability, resistance, and sheet thickness of the steel strip 10, and the gap may be correlated with the frequency.
[Configuration of Output Current Setting Unit 150]
The output current setting unit 150 is a unit that sets a magnitude (output current value) of the AC current IL supplied to the induction heating unit 20. To realize this function, the output current setting unit 150 includes an object-to-be-heated information acquiring unit 151, an output current setting table 152, and an output current selector 153.
The object-to-be-heated information acquiring unit 151 acquires attribute information of the steel strip 10 that is an object to be heated, similarly to the object-to-be-heated information acquiring unit 181.
The output current selector 153 uses the attribute information acquired by the object-to-be-heated information acquiring unit 151 as a key and selects one current value among current values registered in the output current setting table 152. In the output current setting table 152, the attribute information and the current value are correlated with each other and are registered in advance. In addition, a control angle of the rectifying unit 110 is set in response to a difference between the current value (the output current value) selected by the output current selector 153 and a current value measured by the current transformer 170. In the case of adopting a thyristor rectifying device as the rectifying unit 110, a gate firing angle of the thyristor is set. In this manner, the value of the current flowing to the induction heating unit 20 is fed back and the control angle (the gate firing angle) of the rectifying unit 110 is controlled, such that the value of the current flowing to the induction heating unit 20 may be constantly controlled to be the current value (output current value) selected by the output current selector 153. As a result, the power supply unit (the AC power supply 160 and the rectifying unit 110) supplies DC power to the MFRS 130, and therefore the alternating current measured by the current transformer 170 can be adjusted to the current value (the output current value) set by the output current setting unit.
As described above, in this embodiment, the current value (the output current value) of the AC power supplied to the induction heating unit 20 is automatically determined in response to the relative permeability, resistance, and sheet thickness of the steel strip 10. This is because the current value corresponding to a target temperature can be determined by the relative permeability, the resistance, and the sheet thickness of the steel strip 10.
In addition, similarly to this embodiment, when all of the relative permeability, resistance, and sheet thickness of the steel strip 10, and the current value are correlated with each other and are registered in the output current setting table 152, a temperature distribution and an average temperature of the steel strip 10 in the sheet width direction may be set in a relatively appropriate manner. Therefore, it is preferable that all of the relative permeability, the resistance, and the sheet thickness of the steel strip 10, and the current value be correlated with each other. However, it is not necessary to correlate all of the relative permeability, resistance, and sheet thickness of the steel strip 10 with the current value, and at least one of the relative permeability, resistance, and sheet thickness of the steel strip 10 and the current value may be correlated with each other in the output current setting unit 150. In addition, at least one of the relative permeability, resistance, and sheet thickness of the steel strip 10, and the gap may be correlated with the current value.
<Effect of This Embodiment>
<Specifications of Steel Strip>
•Material: Stainless steel sheet •Sheet Thickness: 0.3 mm •Width: 500 mm
As shown in
On the other hand, when the sheet conveyance speed varies, the impedance of the load varies, such that in a case where the parallel resonance type inverter in the conventional technique is used, the inverter of the voltage source controls the output frequency of the inverter in such a manner that a resonance condition of the load is maintained. Therefore, as shown in
As described above, according to this embodiment, the current IL of the frequency (the output frequency) corresponding to the attribute (attribute information) of the steel strip 10 is supplied to the induction heating unit 20 using the MERS 130. Therefore, the control unit according to this embodiment is not subjected to a restriction in regard to an operation with a resonant frequency like the conventional technique, such that even when the sheet conveyance speed of the steel strip 10 varies, the frequency of the current IL that is supplied to the induction heating unit 20 may be set to a desired value in response to the attribute of the steel strip 10. Therefore, when the conductive sheet is heated using the transverse type induction heating unit, even when the sheet conveyance speed of the conductive sheet varies, it is possible to prevent the temperature distribution of the conductive sheet in the sheet width direction from being nonuniform. In addition, the current IL of a frequency, which is appropriate to the steel strip 10 that is an object to be heated (particularly, which makes the temperature distribution in the sheet width direction as uniform as possible), may be set to the induction heating unit 20.
In addition, in this embodiment, the control angle of the rectifying unit 110 is changed in response to the attribute of the steel strip 10, and therefore the current IL having a magnitude corresponding to the attribute of the steel strip 10 is supplied to the induction heating unit 20. As a result, the current IL having a magnitude appropriate to the steel strip 10 that is an object to be heated can flow through the induction heating unit 20. In addition, since the frequency is controlled to be constant, the temperature distribution of the conductive sheet in the sheet width direction can be uniformly controlled without actually measuring the variation in temperature with the passage of time at various positions of the steel strip 10.
Furthermore, in regard to the induction heating system provided with the control unit 100 and the induction heating unit 20 having the shielding plates 31a to 31d, since even when the sheet conveyance speed varies, the frequency of the AC power does not vary, it is not necessary to consider a variation (variation with the passage of time) in the eddy current generated at the edge portion of the steel strip 10. Therefore, when the control unit 100 is used in the induction heating system, even when the operational conditions vary, a heating amount in the vicinity of the edge can be appropriately controlled by the shielding plates 31a to 31d.
(Second Embodiment)
Next, a second embodiment of the present invention will be described. In the above-described first embodiment, the alternating current IL is made to flow to the induction heating unit 20 directly from the MERS 130. Conversely, according to this embodiment, the alternating current IL is made to flow to the induction heating unit 20 from the MERS 130 through a transformer. In this manner, in a configuration of this embodiment, the transformer is added to the above-described configuration of the first embodiment. Therefore, in this embodiment, the same reference symbols as those given in
As shown in
A primary side (input side) terminal of the output transformer 210 is connected to the AC terminals a and d of the MERS 130. A secondary side (output side) terminal of the output transformer 210 is connected to the induction heating unit 20 (the copper bus bars 42a and 42g). The transformation ratio (input:output) of the output transformer 210 is N:1 (N>1).
As described above, in this embodiment, since the output transformer 210 having the transformation ratio of N:1 (N>1) is disposed between the MERS 130 and the induction heating unit 20, substantially N times current of the current flowing through the MERS 130 can be made to flow to the induction heating unit 20. Therefore, in this embodiment, a large current can be made to flow to the induction heating unit 20 without making a large current flow to the “semiconductor switches S1 to S4 and the diodes D1 to D4” that make up the MERS 130.
In addition, a plurality of taps may be provided on the primary side or the secondary side of the output transformer 210 in such a manner that the transformation ratio of the output transformer 210 can be changed, and the tap to be used may be properly used in response to the steel strip 10 that is an object to be heated.
(Third Embodiment)
Next, a third embodiment of the present invention will be described. In the above-described first and second embodiments, a flat plate is used as the shielding plates 31a to 31d provided for the induction heating unit 20. Conversely, in this embodiment, a depressed portion is formed in the shielding plates provided for the induction heating unit 20. In this manner, this embodiment and the above-described first and second embodiments are different in a part of a configuration of the shielding plates. Therefore, in this embodiment, the same reference symbols as those given in
In addition,
As shown in
The width and length of the main shielding plate 50a are the same as those of the rear plate 50b. However, the rear plate 50b is formed of a copper plate in which a longitudinal cross-section and a transverse cross-section are uniform, and conversely, the main shielding plate 50a is formed of a copper plate in which two rhombic holes are formed in the longitudinal direction thereof. The shielding plate 301 is formed by close contact between the main shielding plate 50a and the rear plate 50b, and has two rhombic depressed portions (non-penetration holes) 51 and 52 in the longitudinal direction. In addition, in
As shown in
In this embodiment, as shown in
Particularly, in this embodiment, inner-side edges 51a and 52a of the depressed portions 51 and 52 of the shielding plate 301 (301d) are disposed on the edge 10a side compared to the maximum current passing region 56, and outer-side edges 51b and 52b of the depressed portions 51 and 52 are disposed on the edge side 10a compared to an edge current passing region 57 that is a region through which an eddy current flowing to the vicinity of the edge 10a of the steel strip 10 passes. Here, among edges of the depressed portions 51 and 52, the inner-side edges 51a and 52a are edges that are closest to a central portion in the width direction of the steel strip 10 and that are closer to the corresponding depressed portions 52 and 51 (or the central portion of the shielding plate 301d in the sheet conveyance direction). In addition, among edges of the depressed portions 51 and 52, outer-side edges 51b and 52b are edges that are farther from the central portion of the steel strip 10 in the width direction and that are farthest from the corresponding depressed portions 52 and 51 (or the central portion of the shielding plate 301d in the sheet conveyance direction).
In this embodiment, due to the shielding plate 301 disposed as described above, a decrease in the temperature of the steel strip 10 in the vicinity of the edge 10a is suppressed. Hereinafter, a mechanism, which suppresses a decrease in temperature of the steel strip 10 in the vicinity of the edge 10a due to the shielding plate 301, will be described.
As shown in
As a result, as shown in
Conversely, in a case the depressed portion is not present in the shielding plate 31 like the first embodiment, the eddy currents 53 and 54 do not flow through the shielding plate 31 as shown in
As described above, the inventors found that when the depressed portions 51 and 52 are formed in the shielding plate 301 made of copper, and the shielding plate 301 is disposed in such a manner that the depressed portions 51 and 52 are opposite to the vicinity of the edge of the steel strip 10, a decrease in temperature in the vicinity of the edge of the steel strip 10 can be suppressed. To confirm this finding, the inventors measured the temperature distribution in the sheet width direction of a conductive sheet (corresponding to the steel strip 10) in a case where the shielding plate 301 according to this embodiment is used and in a case where the shielding plate 31 according to the first embodiment is used, respectively.
Specifically,
Width of heating coil: 250 [mm] (length in a sheet conveyance direction)
Core: Ferrite core
Heating material: Non-magnetic SUS (stainless) sheet (a width of 500 [mm], and a thickness of 0.3 [mm])
Sheet conveyance speed: 8 [mpm (m/minute)]
Heating temperature: 30 to 130 [° C.] (a temperature increase at a central portion is set to 100 [° C.])
Frequency of power source: 29 [kHz], 21 [kHz], and 10 [kHz]
Material of shielding plate: Copper
In addition, the closer the relative permeability of a material approaches 1, the more easily the temperature in the vicinity of an edge decreases. In addition, when the temperature of the conductive sheet (material to be heated) is equal to or higher than the Curie temperature, the relative permeability of the conductive sheet becomes 1. Therefore, the non-magnetic SUS (stainless) sheet was used as the heating material having the relative permeability of 1.
As shown in
On the other hand, as shown in
In addition, in a case where the shielding plate is not provided, the temperature in the vicinity of the edge (here, at a position of “50” to “100” in the horizontal axis) does not decrease. However, since the temperature increase in the edge becomes substantially 500 [° C.], the edge was over-heated.
As described above, according to this embodiment, the depressed portions 51 and 52 are formed in the shielding plate 301 made of copper, the shielding plate 301 is disposed between the upper and lower side heating coils 24 and 28 and the steel strip 10 in such a manner that the depressed portions 51 and 52 face the vicinity of the edge of the steel strip 10. Therefore, even when the steel strip 10 is exposed to high temperatures, a decrease in temperature of the steel strip 10 in the vicinity of the edge thereof can be suppressed.
Furthermore, in the induction heating system provided with the control unit 100 and the induction heating unit having the shielding plate 301, even when the sheet conveyance speed varies, since the frequency of the AC power does not vary, it is not necessary to consider a variation (temporal variation) of the eddy current that is generated in the edge portion of the steel strip 10. Therefore, when the control unit 100 is used in the induction heating system, even when operational conditions vary, a temperature increase in the vicinity of the edge can be appropriately controlled by the shielding plate 301. Furthermore, since the depressed portions 51 and 52 are formed in the shielding plate 301, even when the relative permeability varies in response to a heated state of the steel sheet, the temperature distribution in the vicinity of the edge can be appropriately controlled due to the depressed portions 51 and 52. Therefore, in the configuration according to this embodiment, it is possible to cope with a change in heating speed in a relatively flexible manner.
In addition, in the above-described embodiments (the first embodiment to the third embodiment), the shielding plates 31 and 301 are not limited to a plate made of copper. That is, the shielding plates 31 and 301 may be formed by any material as long as this material is a conductor having a relative permeability of 1 (for example, metal that is a paramagnetic substance or a diamagnetic substance). For example, the shielding plate 31 may be formed of aluminum.
In addition, in this embodiment, the positional relationship between the steel strip 10 and the shielding plate 301 is not particularly limited as long as the depressed portions of the shielding plate 301 and the steel strip 10 (also including a plane extended from the steel strip 10) are opposite to each other in a region that is present on the edge 10a side compared to the maximum current passing region 56. However, it is preferable that a region between the maximum current passing region 56 and the edge 10a of the steel strip 10, and at least a part of the depressed portions of the shielding plate be opposite to each other as shown in
In addition, in this embodiment, a description has been made with respect to a case in which the two depressed portions are formed in the shielding plate as an example, but the number of the depressed portion formed in the shielding plate is not limited.
In addition, in this embodiment, an illustration has been made with respect to a case in which the shape of the depressed portions 51 and 52 is a rhombic shape as an example. However, the shape of the depressed portions 51 and 52 may be any shape as long as the eddy current may be made to flow through the steel strip 10 along the edge portion of the depressed portions 51 and 52. The shape of the depressed portions 51 and 52 may be, for example, an ellipse, a rectangle other than a rhombic shape, or other square shapes. At this time, when a depressed portion in which the length in the sheet conveyance direction is longer than that in a direction orthogonal to the sheet conveyance direction is formed, the eddy current can be easily made to flow along an edge portion of the depressed portion. Therefore, it is preferable to form a depressed portion in which the length in the sheet conveyance direction is longer than that in the direction orthogonal to the sheet conveyance direction. In addition, the shape of the depressed portion in the shielding plate is not necessary to have a closed shape. For example, the depressed portion may be formed in an end portion of the shielding plate.
Furthermore, copper is normally used for the upper side heating coil 24 and the lower side heating coil 28, but a conductor (metal) other than copper may be used. In addition, an induction heating system other than the continuous annealing line may be adopted. In addition, the dimensions of the cores 23 and 27 shown in
In addition, in the above-described embodiments, both of the upper side inductor 21 and the lower side inductor 22 are provided as an example, but either the upper side inductor 21 or the lower side inductor 22 may be provided. Furthermore, the size of the gap is not particularly limited.
In addition, all of the above-described embodiments of the present invention illustrate only a specific example for executing the present invention, and a technical scope of the present invention is not limited to the embodiments. That is, the present invention may be executed with various forms without departing from the technical scope or critical features thereof.
It is possible to provide a control unit of an induction heating unit, an induction heating system, and a control method of the induction heating unit, in which a temperature distribution in the sheet width direction of a conductive sheet is made more uniform compared to that in the conventional techniques, even when the sheet conveyance speed of the conductive sheet varies in a case where the conductive sheet is heated using a transverse type induction heating unit.
10: Steel strip (Conductive sheet)
20: Induction heating unit
23, 27: Core (Magnetic core)
24: Upper side heating coil (Heating coil)
28: Lower side heating coil (Heating coil)
31
a to 31d: Shielding plate
51, 52: Depressed portion (Valley portion)
100, 200: Control unit of induction heating unit
110: Rectifying unit
120: Reactor
130: Magnetic energy recovery switch (MERS)
131 to 134: First to fourth reverse conductivity type semiconductor switches
140: Gate control unit
150: Output current setting unit
160: AC power supply
170: Current transformer (Current measuring unit)
180: Frequency setting unit
210: Output transformer
301: Shielding plate
S1 to S4: Semiconductor switches
D1 to D4: Diodes
| Number | Date | Country | Kind |
|---|---|---|---|
| P2009-283255 | Dec 2009 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2010/070800 | 11/22/2010 | WO | 00 | 6/8/2012 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2011/074383 | 6/23/2011 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 2448008 | Baker | Aug 1948 | A |
| 2448012 | Baker | Aug 1948 | A |
| 3444346 | Cable et al. | May 1969 | A |
| 4317188 | Ushikoshi | Feb 1982 | A |
| 4357512 | Nishimoto et al. | Nov 1982 | A |
| 4678883 | Saitoh et al. | Jul 1987 | A |
| 4708325 | Georges | Nov 1987 | A |
| 4795872 | Hagisawa et al. | Jan 1989 | A |
| 4824536 | Kim et al. | Apr 1989 | A |
| 5034586 | Havas et al. | Jul 1991 | A |
| 5055647 | Heyes et al. | Oct 1991 | A |
| 5126522 | Katayama et al. | Jun 1992 | A |
| 5157233 | Inokuma et al. | Oct 1992 | A |
| 5378879 | Monovoukas | Jan 1995 | A |
| 5397877 | Couffet et al. | Mar 1995 | A |
| 5510600 | Jackson | Apr 1996 | A |
| 5739506 | Hanton et al. | Apr 1998 | A |
| 5770838 | Rohrbaugh et al. | Jun 1998 | A |
| 5827056 | Rohrbaugh et al. | Oct 1998 | A |
| 5911094 | Tsujimoto | Jun 1999 | A |
| 6154629 | Kinouchi et al. | Nov 2000 | A |
| 6262402 | Isoyama et al. | Jul 2001 | B1 |
| 6498328 | Anderhuber et al. | Dec 2002 | B2 |
| 6570141 | Ross | May 2003 | B2 |
| 6576877 | Dabelstein et al. | Jun 2003 | B2 |
| 6576878 | Thorpe et al. | Jun 2003 | B2 |
| 6710314 | Reiss et al. | Mar 2004 | B2 |
| 6849837 | Riess et al. | Feb 2005 | B2 |
| 6930293 | Matsuo et al. | Aug 2005 | B2 |
| 6930891 | Hama et al. | Aug 2005 | B1 |
| 6969833 | Suzuki | Nov 2005 | B2 |
| 7057485 | Preusse et al. | Jun 2006 | B2 |
| 7183526 | Yoshino et al. | Feb 2007 | B2 |
| 7525073 | Lovens et al. | Apr 2009 | B2 |
| 20030155349 | Matsuo et al. | Aug 2003 | A1 |
| 20050006120 | Lovens | Jan 2005 | A1 |
| 20050061803 | Sivasubramaniam et al. | Mar 2005 | A1 |
| 20050274717 | Kataoka et al. | Dec 2005 | A1 |
| 20080203088 | Kinouchi et al. | Aug 2008 | A1 |
| 20080296290 | Cao et al. | Dec 2008 | A1 |
| 20090057301 | Lovens | Mar 2009 | A1 |
| 20100258535 | Fukutani et al. | Oct 2010 | A1 |
| Number | Date | Country |
|---|---|---|
| 2 703 992 | May 2009 | CA |
| 2 073 368 | Jun 2009 | EP |
| 2001-6862 | Jan 2001 | JP |
| 2001-6863 | Jan 2001 | JP |
| 2002-313547 | Oct 2002 | JP |
| 2003-73746 | Mar 2003 | JP |
| 2004-114092 | Apr 2004 | JP |
| 2005-49815 | Feb 2005 | JP |
| 2006-244763 | Sep 2006 | JP |
| 2008-159505 | Jul 2008 | JP |
| 2008-159572 | Jul 2008 | JP |
| 2009-93805 | Apr 2009 | JP |
| 2009-289458 | Dec 2009 | JP |
| 2032996 | Apr 1995 | RU |
| 2150796 | Jun 2000 | RU |
| 2357383 | May 2009 | RU |
| 2372753 | Nov 2009 | RU |
| WO 2009139079 | Nov 2009 | WO |
| Entry |
|---|
| Microwaves101—High Permeability Materials.pdf. |
| International Search Report issued in PCT/JP2010/070800, mailed Feb. 15, 2011. |
| Office Action issued in Japanese Patent Application No. 2011-171344, mailed Oct. 4, 2011. |
| Office Action issued in Japanese Patent Application No. 2011-512742, mailed Aug. 30, 2011. |
| Notice of Allowance dated Sep. 19, 2013 issued in Russian Patent Application No. 2012125958. |
| Extended European Search Report dated Nov. 3, 2014, issued in European Patent Application No. 10837412.5. |
| Number | Date | Country | |
|---|---|---|---|
| 20120305547 A1 | Dec 2012 | US |