The present invention relates to the assembly of nanoparticles, and, in particular, to a method of using electrostatic force to assemble nanoparticles onto nanostructures.
The manufacture of nanostructures from carbon nanotubes and nanoparticles may be useful in a broad range of applications including: nanoelectronics, chemical sensors, biosensors, catalysis, fuel cells, and hydrogen storage. Current methods for assembling these components are primarily based on “wet-chemical” techniques in which the components are created or manipulated with chemical reactions taking place in solution. These methods, however, are generally very slow and the associated interfacial chemistry is material dependent, limiting their ability to create nanostructures of arbitrary composition. Furthermore, although the size of the nanoparticles may be controlled in the solution prior to assembly, there is very limited control over the assembly process.
The present invention addresses the problem of conveniently and efficiently decorating both single-walled and multi-walled carbon nanotubes with nanoparticles by using electrostatic force directed assembly (“ESFDA”). Using ESFDA, the packing density, spacing, and size distribution of nanoparticles on nanotubes can be controlled during the assembly process. Due to the inherent material independent nature of electrostatic force, nanoparticle-nanotube structures can be produced from a variety of different materials and different combinations of materials.
Specifically then, the present invention provides a method of coating various nanostructures with a variety of nanoparticles in which a plurality of electrically conductive nanostructures is created. A plurality of charged aerosol nanoparticles is then produced, and an electrical field is applied to the nanostructures. The charged nanoparticles introduced to the electrical field are then attracted to the nanostructures and bond to the nanostructures.
Thus, it is an object of at least one embodiment of the present invention to provide a simple method of assembling nano-sized particles into structures without the need for a liquid environment.
It is another object of the invention to provide an assembly technique that is largely indifferent to the chemical composition of the nanoparticles and nanostructures and that thus may be used to assemble a variety of novel structures of arbitrary composition.
The nanostructures may be either single-walled or multi-walled in nature.
The bonding between the nanostructures and nanoparticles may be non-covalent in nature so as to preserve the sp2 hybridization of carbon atoms.
It is thus another object of the invention to preserve desirable electronic properties of carbon in the nanostructure.
The assembly time may be controlled so as to control the packing density of the nanoparticles on the nanostructures. In addition or alternatively, the aerosol flow rate and/or electrical field may also be controlled so as to control the size of the nanoparticles that attach to the nanostructures.
Thus, it is yet another object of at least one embodiment of the present invention to provide an assembly technique that allows multidimensional control of the assembly process.
The nanostructures used in the invention may be nanotubes.
Thus, it is another object of at least one embodiment of the present invention that the nanoparticles introduced to the electrical field may comprise a mixture of two different types of nanoparticles.
It is thus another object of the invention to provide an assembly method that may work with multiple nanoparticles of different chemical compositions.
Thus, it is another object of at least one embodiment of the present invention that the nanoparticles used are catalysts, photoelectric materials, or semiconductors.
It is thus another object of the invention to provide an assembly technique that by allowing great flexibility in the types and composition of nanoparticles being used is widely applicable to applications such as: filtration, sensing, purification, generation of materials, catalyzation, hydrogen storage, fuel cell components, discharge electrodes, spintronics, Raman scattering, wave guides, solar energy harvesting, nanometrology, and marking the nanostructure to study nanomechanics.
The assembled nanoparticles and nanostructure may be attached to a substrate and the nanostructure removed to transfer the nanoparticles to the substrate.
Thus, it is another object of the invention to provide a method of organizing nanoparticles on a microscopic scale for transfer to another object. A carbon nanotube used as the substrate organizes the nanoparticles along one dimension, while mutual electrostatic repulsion of the nanoparticles organizes them with a regular spacing defined by the number of nanoparticles deposited.
The above method may be used to produce a sensing electrode having a conductive nanowire extending between a first and second electrode to conduct electricity therethrough and nanoparticles of a different material than the conductive nanowire responsive to an environment of the conductive nanowire to change the properties of conduction of the conductive nanowire.
Thus, it is another object of at least one embodiment of the invention to provide a novel sensing device making use of the ability to attached materials of arbitrary composition, in a regular manner, to a conductive nanowire.
These particular objects and advantages may apply to only some embodiments falling within the claims and thus do not define the scope of the invention.
a and 5b are elevation fragmentary views of an assembled nanotube and nanoparticles showing steps of destroying the nanotube to transfer the ordered nanoparticles to a secondary substrate;
Referring to
The application of the arc 16 to the precursor material 22 creates an aerosol of nanoparticles 42 through physical vaporization of the solid precursor material 22. This generation of nanoparticles creates a relatively broad size distribution of nanoparticles 42. A significant fraction of the nanoparticles 42 are charged by the arc 16 or through plasma or thermionic emission, which makes ESFDA feasible without the use of further nanoparticle 42 charging device. The charging of the nanoparticles 42 may prevent their agglomeration. Alternatively, the nanoparticle 42 production means may use aerosol reactors or may aerosolize colloidal nanoparticles 42, in which case additional charging means may be required in such assemblies, or example using corona discharge electrodes.
Multiple precursor materials 22 may be used, for example, silver (Ag) and tin oxide (SnO2) for example from different arc assemblies or using a mixture of precursor materials 22. The gaseous aerosol may thus comprise a mixture different nanoparticles 42, including generally catalysts, photo-catalysts, or semiconductors. The nanoparticles 42 will typically be less than 100 nanometers in diameter and may have a mean diameter of less than 20 nanometers.
The ESFDA device 10 further provides a room temperature carrier gas source 28 that is connected to the plasma source chamber 18 by way of a first inlet tube 26 and a second inlet tube 24. The first and second inlet tubes are coupled together by a metering valve or flow meter 30 so that flow of the gas into the chamber 18 may be precisely controlled. The gas from the carrier gas source 28 is applied to the chamber 18 to carry the nanoparticles 42 created by the arc plasma source down a flow tube 38. The flow tube 38 generally acts as an electrode and may comprise grounded metal conductor. A bypass tube 25 branches from the flow tube to the flow out of the flow tube 38 independent of the flow of carrier gas into the chamber 18. The bypass tube 25 leads to a metering valve 34 and then connects to an exhaust tube 27 leading to a filter 32 disposed at the end of the exhaust tube 27 to catch any nanoparticles 42 that are diverted from the flow tube 38.
A substrate electrode 40 is provided beneath the flow tube 38 and a voltage source 36 is connected between the substrate electrode 40, and the flow tube 38 to provide an electrical field therebetween. The voltage source 36 may be either positive or negative in nature, depending on the charge of the nanoparticles, so as to attract the nanoparticles to the substrate electrode 40. Supported by the substrate electrode 40 and in electrical communication with the substrate electrode 40, are nanostructures 44 to which the nanoparticles will be assembled. In one embodiment, the nanostructures 44 are carbon nanotubes (CNT) coating a substrate electrode 40 that is a perforated copper grid. The holes in the grid appear to enhance the effect of the electrical field. A gap distance (e.g., 2-0.5 mm) is maintained between the metal flow tube 38 and the substrate electrode 40 using, for example, a precision-machined ceramic spacer. The larger the gap between the flow tube 38 and the substrate electrode 40, the higher applied voltage necessary to sufficiently attract the nanoparticles 42 to the nanostructures 44.
The presence of the voltage source 36 creates an electrical field in the neighborhood of the nanostructures 44 on the substrate electrode 40. Thus, after the nanoparticles 42 flow through the flow tube 38, they are preferentially attracted to the nanostructure 44 surfaces on the substrate electrode 40. This attraction results in nanoparticle 42 decoration of the nanostructures 44, which will be discussed further below. The voltage source may provide a voltage of 2 kV-500 V depending on the gap distance. The voltage is limited only by the breakdown voltage of the carrier gas (about 3×106 V/m for dry air). Calculation from experiments show the maximum electric field near the surface of a 20-nm carbon nanotube reaches 2.45×106 V/m for a voltage source 36 of 2 kV and a gap of 2 mm.
In the absence of an electrical field, it has been determined that the nanoparticles 42 are not appreciably attracted to the nanostructures 44 and do not bond to the surfaces of the nanostructures.
Various different nanostructures 44 such as carbon nanotubes, nanorings, nanorods, and nanowires may be used in the present invention. The nanostructures 44 are produced using known methods in the relevant technological field or, alternatively, may be bought from known commercial sources, e.g., Carbon Nanotechnologies, Inc. and Alfa Aesar.
Referring now to
The nanoparticles 42 are generally evenly spaced across the external surface of the nanostructure 44 because of the electrical charge carried on each of the nanoparticles 42 which cause them to mutually repel one another leading to a minimum energy configuration of substantially uniform distribution.
The average separation of the nanoparticles 42 bonded to the external surfaces of the nanostructures 44 can be controlled by adjusting the assembly conditions. For example, adjusting the duration of the flow of nanoparticles 42 over the substrate electrode 40 will control the packing density of the nanoparticles 42 on the nanostructures 44 as the packing density increases with increased assembly time. If the assembly time is sufficiently long, the entire surface of the nanostructure 44 may be coated with nanoparticles 42.
Referring now to
To the extent that the amount of charge can be controlled on different nanoparticles 42, this same effect may be used to sort nanoparticle materials or provide different size ratios among nanoparticles 42 of different materials.
Nanoparticles 42 reaching the nanostructures 44 are selected through their electrical mobility, the ability of a particle to move in an electrical field, characterized by the following equation: Zp=νp/E=neCc/3πμDp, wherein νp is the nanoparticle 42 velocity along electric field lines, E is the electrical field, n is the number of elementary charges carried by nanoparticles, e is the elementary charge, Cc is the Cunningham slip correction factor, Dp is the diameter of the nanoparticles, and μ is the flow viscosity. The electric field need not be homogenous but can be further altered to control the distribution of the particles for example with electrode shapes, shields or photoelectric dissipation.
Some size selection is also intrinsic to the process of generating and conveying the aerosolized nanoparticles 42.
Referring now to
As shown in
As shown in
Referring to
Referring now to
Referring now to
Various alternatives are contemplated as being within the scope of the following claims, particularly pointing out and distinctly claiming the subject matter regarded as the invention.
This application claims the benefit of U.S. provisional application 60/710,642 filed on Aug. 23, 2005, hereby incorporated by reference.
Number | Name | Date | Kind |
---|---|---|---|
5460701 | Parker et al. | Oct 1995 | A |
5514349 | Parker et al. | May 1996 | A |
5788738 | Pirzada et al. | Aug 1998 | A |
5851507 | Pirzada et al. | Dec 1998 | A |
5874684 | Parker et al. | Feb 1999 | A |
5905000 | Yadav et al. | May 1999 | A |
5939146 | Lavernia | Aug 1999 | A |
5952040 | Yadav et al. | Sep 1999 | A |
5984997 | Bickmore et al. | Nov 1999 | A |
5989648 | Phillips | Nov 1999 | A |
6113795 | Subramaniam et al. | Sep 2000 | A |
6228904 | Yadav et al. | May 2001 | B1 |
6254940 | Pratsinis et al. | Jul 2001 | B1 |
6268054 | Costantino et al. | Jul 2001 | B1 |
6379419 | Celik et al. | Apr 2002 | B1 |
6447848 | Chow et al. | Sep 2002 | B1 |
6528020 | Dai et al. | Mar 2003 | B1 |
6528029 | Dettling et al. | Mar 2003 | B1 |
6548171 | Barbera-Guillem et al. | Apr 2003 | B1 |
6623559 | Huang | Sep 2003 | B2 |
6652967 | Yadav et al. | Nov 2003 | B2 |
6726992 | Yadav et al. | Apr 2004 | B1 |
6730537 | Hutchison et al. | May 2004 | B2 |
6765949 | Chang | Jul 2004 | B2 |
6777639 | Schroder et al. | Aug 2004 | B2 |
6855426 | Yadav | Feb 2005 | B2 |
6872971 | Hutchinson et al. | Mar 2005 | B2 |
6933331 | Yadav et al. | Aug 2005 | B2 |
7012214 | Schroder et al. | Mar 2006 | B2 |
7126081 | Schroder et al. | Oct 2006 | B2 |
7172790 | Koulik et al. | Feb 2007 | B2 |
7223444 | Deppert et al. | May 2007 | B2 |
7232771 | Jacobs et al. | Jun 2007 | B2 |
7318908 | Dai | Jan 2008 | B1 |
7326954 | Wybourne et al. | Feb 2008 | B2 |
7335908 | Samuelson et al. | Feb 2008 | B2 |
7416699 | Dai et al. | Aug 2008 | B2 |
7442573 | Hutchison et al. | Oct 2008 | B2 |
7528002 | Samuelson et al. | May 2009 | B2 |
7531136 | Besnard et al. | May 2009 | B2 |
7955559 | Joshi et al. | Jun 2011 | B2 |
20020016306 | Hutchison et al. | Feb 2002 | A1 |
20020117659 | Lieber et al. | Aug 2002 | A1 |
20020146742 | Wybourne et al. | Oct 2002 | A1 |
20030077625 | Hutchison | Apr 2003 | A1 |
20030102444 | Deppert et al. | Jun 2003 | A1 |
20030147966 | Franzen et al. | Aug 2003 | A1 |
20030230554 | Schroder et al. | Dec 2003 | A1 |
20040018306 | Tenne et al. | Jan 2004 | A1 |
20040052289 | Chang | Mar 2004 | A1 |
20040057896 | Kronholm et al. | Mar 2004 | A1 |
20040065170 | Wu et al. | Apr 2004 | A1 |
20040075464 | Samuelson et al. | Apr 2004 | A1 |
20040105980 | Sudarshan et al. | Jun 2004 | A1 |
20040166673 | Hutchison et al. | Aug 2004 | A1 |
20040178530 | Yadav | Sep 2004 | A1 |
20040202682 | Emrick et al. | Oct 2004 | A1 |
20040221813 | Chang | Nov 2004 | A1 |
20050000950 | Schroder et al. | Jan 2005 | A1 |
20050008861 | Yadav et al. | Jan 2005 | A1 |
20050011431 | Samuelson et al. | Jan 2005 | A1 |
20050061785 | Schroder et al. | Mar 2005 | A1 |
20050147747 | Yadav | Jul 2005 | A1 |
20050181587 | Duan et al. | Aug 2005 | A1 |
20050199861 | Wu et al. | Sep 2005 | A1 |
20060019470 | Seifert et al. | Jan 2006 | A1 |
20060057360 | Samuelson et al. | Mar 2006 | A1 |
20060063299 | Hutchison et al. | Mar 2006 | A1 |
20060081835 | Hutchison et al. | Apr 2006 | A1 |
20060083694 | Kodas et al. | Apr 2006 | A1 |
20060125056 | Samuelson et al. | Jun 2006 | A1 |
20060159596 | De La Veaux et al. | Jul 2006 | A1 |
20060204441 | Atala et al. | Sep 2006 | A1 |
20060204445 | Atala et al. | Sep 2006 | A1 |
20060204539 | Atala et al. | Sep 2006 | A1 |
20070141163 | Vitaliano et al. | Jun 2007 | A1 |
20070193518 | Shiina et al. | Aug 2007 | A1 |
20070262482 | Halpap et al. | Nov 2007 | A1 |
20070272664 | Schroder et al. | Nov 2007 | A1 |
20080142361 | Han et al. | Jun 2008 | A1 |
20080142926 | Seifert et al. | Jun 2008 | A1 |
20090084163 | Chen et al. | Apr 2009 | A1 |
Number | Date | Country |
---|---|---|
0144796 | Jun 2001 | WO |
Number | Date | Country | |
---|---|---|---|
20120207938 A1 | Aug 2012 | US |
Number | Date | Country | |
---|---|---|---|
60710642 | Aug 2005 | US |